JP3986071B2 - Rooftop greening structure and manufacturing method of rooftop greening block material - Google Patents

Rooftop greening structure and manufacturing method of rooftop greening block material Download PDF

Info

Publication number
JP3986071B2
JP3986071B2 JP2003305854A JP2003305854A JP3986071B2 JP 3986071 B2 JP3986071 B2 JP 3986071B2 JP 2003305854 A JP2003305854 A JP 2003305854A JP 2003305854 A JP2003305854 A JP 2003305854A JP 3986071 B2 JP3986071 B2 JP 3986071B2
Authority
JP
Japan
Prior art keywords
block material
soil
wood
block
amount
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2003305854A
Other languages
Japanese (ja)
Other versions
JP2005073538A (en
Inventor
美紀夫 村中
Original Assignee
村中建設株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 村中建設株式会社 filed Critical 村中建設株式会社
Priority to JP2003305854A priority Critical patent/JP3986071B2/en
Publication of JP2005073538A publication Critical patent/JP2005073538A/en
Application granted granted Critical
Publication of JP3986071B2 publication Critical patent/JP3986071B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

本発明は、ビル又は家屋等の屋上を緑化するための屋上緑化用ブロック材及びその製造方法に関する。   The present invention relates to a roof greening block material for greening a roof of a building or a house and a manufacturing method thereof.

近年、都市部における温暖化やヒートアイランド現象に対応するため都市環境での緑化事業が活発に行われており、特にビルや家屋等の屋上を緑化することで、建物の温度上昇を防ぎ、さらに遮熱効果を高めて建物内の冷暖房を効率化することが期待できる。   In recent years, greening projects in urban environments have been actively carried out in order to cope with global warming and heat island phenomena in urban areas, and in particular, greening the rooftops of buildings, houses, etc., prevents temperature rise of buildings and further blocks them. It can be expected to increase the efficiency of the air conditioning in the building by increasing the thermal effect.

屋上に緑化用の植物を植生させる場合に通常の土壌を屋上に搬入することは、土壌の重量が付加されるためその分建物の強度を高める必要があり、また雨による土壌流出や屋上表面が傷みやすくなるといった欠点を有する。   When planting plants for greening on the roof, bringing ordinary soil into the roof adds to the weight of the soil, so it is necessary to increase the strength of the building. It has the disadvantage of being easily damaged.

そこで、こうした問題点に対処するために、特許文献１では、植栽装置として、装置底部に設けられる防水層と、植物の毛根等の装置外への侵出を防止するために防水層上に張設されるルートガードと、このルートガード上に張設される保水層と、保水層上に設けられ、上方から浸透する雨水等を保持・排水しあるいは保水層から水分を植物の根部に供給するための保水給排水手段と、保水給排水手段上に張設され、客土層からの土砂等の侵入を防止するためのフィルター層とで構成した点が記載されている。   Therefore, in order to deal with such problems, in Patent Document 1, as a planting device, a waterproof layer provided at the bottom of the device and a waterproof layer to prevent the hair roots of plants from escaping outside the device. A root guard that is stretched, a water retention layer that is stretched on the root guard, and is provided on the water retention layer to retain and drain rainwater that permeates from above or to supply moisture from the water retention layer to the root of the plant. The water retention / drainage means for carrying out and the filter layer stretched on the water retention / drainage means for preventing intrusion of earth and sand from the guest soil layer are described.

また、植物の植生用培地をブロック化することも提案されている。例えば、特許文献２では、植生用培地基材として、炭化物粉粒体と、予め水硬性の固結化材に粘土系鉱物の粉粒体をプレー混合させた強化固結化材の粉粒体と、木質チップ材と、天然及び／又は合成の繊維質材と、保水材とを主培地配合材として含有している点が記載されている。また、特許文献３には、緑化板として、有形骨材とバインダーとしての樹脂からなり芽や根の通過しうる大きさの連通空隙を有するポーラス版からなる表面側の植生孔を有する第１層及び底部側の第３層の間に種子又は木本系植物と培土とからなる第２層を挟持一体化し、骨材としてもみがら、ウッドチップ、廃プラスチック、下水汚泥の溶融スラグの少なくとも一つを使用した点が記載されている。また、特許文献４には、成形ブロックを根の侵入を許容すると共に多孔質で弾力を備えた成形体に形成して、その成形ブロックの複数を、隣接させる成形ブロック同士の間に空隙を形成自在にして栽培容器内に配置し、成形ブロックに植えた植物を生育させる点が記載されている。
特開平４−９９４１１号公報 特開２００３−５２２４１号公報 特開２００３−３８０２８号公報 特開２００３−１０２２６４号公報 It has also been proposed to block the plant vegetation medium. For example, in Patent Document 2, as a vegetation medium base material, carbide powder particles and powder particles of a reinforced consolidated material obtained by pre-mixing a clay-based mineral powder material with a hydraulic consolidated material. And a wood chip material, a natural and / or synthetic fiber material, and a water retention material are contained as a main medium compounding material. Patent Document 3 discloses a first layer having a vegetation hole on the surface side made of a porous plate made of a tangible aggregate and a resin as a binder and having a communicating gap of a size through which buds and roots can pass. And a second layer composed of seeds or woody plants and cultivated soil is sandwiched and integrated between the third layer on the bottom side and at least one of slag, wood chips, waste plastic, and molten slag of sewage sludge as an aggregate The point using is described. Further, in Patent Document 4, a molding block is formed into a porous and elastic molded body that allows root intrusion, and a plurality of molding blocks are formed between adjacent molding blocks. The point which freely arrange | positions in a cultivation container and grows the plant planted in the shaping | molding block is described.
Japanese Patent Laid-Open No. 4-99411 JP 2003-52241 A JP 2003-38028 A JP 2003-102264 A

しかしながら、特許文献１では、砂利層や客土層を用いているため、重量としてはそれほど低減されることがなく、そのため砂利層や客土層を薄くする必要があり、植栽が平面的で限られた植物しか用いることができない。また、施工を行う場合に手間がかかる。また、特許文献２から４のブロック材は、いずれも植生用の保水材や肥料をブロック全体に混合しているため、保水性が全体に高まり湿潤状態での重量が大きくなる傾向がある。また、ブロック全体に肥料等を混合するためブロック内部の空隙を大きくすることはできず、その分全体重量の低減を大きくすることができない。   However, in Patent Document 1, since a gravel layer and a soil layer are used, the weight is not reduced so much. Therefore, it is necessary to make the gravel layer and the soil layer thin, and planting is flat. Only limited plants can be used. In addition, it takes time to perform the construction. Moreover, since the block material of patent documents 2 to 4 has mixed the water retention material and fertilizer for vegetation in the whole block, there exists a tendency for water retention to increase to the whole and to increase the weight in a moist state. Moreover, since fertilizer etc. are mixed in the whole block, the space | gap inside a block cannot be enlarged, and the reduction | decrease of the whole weight cannot be enlarged correspondingly.

そこで、本発明は、従来技術において上記のような課題があることにかんがみ、湿潤状態でも重量の増大を抑えることができ、施工も簡単に行うことができる屋上緑化用のブロック材及びその製造方法を提供することを目的とするものである。   Therefore, in view of the above-described problems in the prior art, the present invention can suppress an increase in weight even in a wet state, and can easily perform a rooftop greening block material and a method for manufacturing the same. Is intended to provide.

本発明に係る屋上緑化構造は、屋上表面に積層される防水層と、前記防水層上に積層される排水層と、前記排水層上に複数配列されるとともに、木材チップ又はおがくずからなる木質材と粒状のパーライトが所定容量単位に収容される量を基準とした比率で１：９〜１：１の割合で配合され、固化剤によりブロック状に成形固結されており、湿潤状態での比重が０．５〜１．０であるブロック材と、前記ブロック材に形成された凹部に収容された土壌に植生された植物と、山砂にセメント及び混和剤を混合して水を加えて混練して形成されるとともに前記ブロック材及び前記土壌の露出表面を少なくとも被覆するように積層された土舗装層とを備えていることを特徴とする。 The roof greening structure according to the present invention includes a waterproof layer laminated on the roof surface, a drainage layer laminated on the waterproof layer, and a plurality of wooden materials arranged on the drainage layer and made of wood chips or sawdust. And granular pearlite are blended at a ratio of 1: 9 to 1: 1 based on the amount stored in a predetermined volume unit, molded and consolidated into a block shape with a solidifying agent, and in a wet state specific gravity Kneaded by mixing water with cement and admixture mixed with block material having a thickness of 0.5 to 1.0, plants vegetated in soil housed in recesses formed in the block material, and mountain sand And a soil pavement layer formed to cover at least the exposed surface of the block material and the soil.

本発明に係る屋上緑化構造は、屋根材の上面形状に合わせて成形された底面を有するとともに、木材チップ又はおがくずからなる木質材と粒状のパーライトが所定容量単位に収容される量を基準とした比率で１：９〜１：１の割合で配合され、固化剤によりブロック状に成形固結されており、湿潤状態での比重が０．５〜１．０であるブロック材を屋根の上面に複数配列し、該ブロック材の凹部に収容された土壌に植物を植生し、山砂にセメント及び混和剤を混合して水を加えて混練して形成される土舗装層を前記ブロック材及び前記土壌の露出表面を少なくとも被覆するように積層していることを特徴とする。 The rooftop greening structure according to the present invention has a bottom surface formed in accordance with the top surface shape of the roofing material, and is based on the amount of wooden material made of wood chips or sawdust and granular pearlite accommodated in a predetermined capacity unit. A block material having a ratio of 1: 9 to 1: 1 in a ratio, molded and consolidated into a block shape by a solidifying agent, and having a specific gravity in a wet state of 0.5 to 1.0 is applied to the upper surface of the roof. A plurality of arrangements, planting plants in the soil accommodated in the recesses of the block material, mixing the cement and admixture into mountain sand, adding water and kneading the soil pavement layer formed the block material and the block It is characterized by being laminated so as to cover at least the exposed surface of the soil.

本発明に係る屋上緑化用ブロック材の製造方法は、木材チップ又はおがくずからなる木質材を水により十分湿潤させ、粒状のパーライトを前記木質材に対して所定容量単位に収容される量を基準とした比率で９：１〜１：１の割合で混合した後、前記パーライト及び前記木質材の所定容量単位に収容される量を基準としたそれぞれの配合量を加算した量に対して、所定容量単位に収容される量を基準とした比率で、セメントを３〜１０％、ゼオライトを１．５〜１０％、混和剤０．３〜１．０％及び水８〜１５％を混合した固化剤を混練して圧縮されない状態でブロック状に成形固結させたことを特徴とする。 The method for manufacturing a roof greening block material according to the present invention is based on the amount that a wooden material made of wood chips or sawdust is sufficiently wetted with water and granular pearlite is accommodated in a predetermined capacity unit with respect to the wooden material. After mixing at a ratio of 9: 1 to 1: 1 in the ratio, the predetermined volume with respect to the amount obtained by adding the respective blending amounts based on the amount accommodated in the predetermined volume unit of the pearlite and the wood material A solidifying agent in which 3 to 10% of cement, 1.5 to 10% of zeolite, 0.3 to 1.0% of an admixture and 8 to 15% of water are mixed in a ratio based on the amount contained in the unit. Is molded and consolidated into a block shape without being compressed.

ここで、所定容量単位に収容される量とは、所定容量を有する容器等に材料を入れて圧縮することのない状態でその所定容量を満たす収容量を意味する。例えば、木材チップの場合、容器内に収容されて圧縮されない状態では多くの間隙が存在しているが、そのままの状態でその容器の容量を満たしたときに容器内に収容された量がそれに相当する。   Here, the amount accommodated in the predetermined capacity unit means an accommodation amount that satisfies the predetermined capacity without putting a material into a container or the like having a predetermined capacity and compressing it. For example, in the case of wood chips, there are many gaps in a state where they are accommodated in a container and are not compressed, but the amount accommodated in the container when the capacity of the container is filled as it is corresponds to that. To do.

本発明に係る屋上緑化用ブロック材は、上記のような構成を有することで、木材チップ又はおがくずからなる木質材及び粒状のパーライトを所定容量単位に収容される量を基準とした比率で１：９〜１：１の割合で配合するので、木質材同士の間に生じた多くの間隙に粒状のパーライトが入り込んで木質材表面に付着し、固化剤によってパーライト同士が固結され木質材同士も固結されてブロック状に成形される。したがって、多くの間隙が存在するブロック材とすることができ、木質材及びパーライト自体も軽量な材料であるため、格段に軽量化することが可能となる。また、湿潤状態でも間隙が多いため排水性がよく重量が増大することを抑えることができ、湿潤状態での比重を０．５〜１．０に抑えることができる。このように間隙が多い構造では強度の点で問題が生じるおそれがあるが、屋上では、人間が歩く程度の荷重が加わることを想定すればよく、こうした荷重条件には十分耐久力を有するものとなっている。   The block material for rooftop greening according to the present invention has the above-described configuration, and the ratio is based on the amount based on the amount of wood material or granular pearlite made of wood chips or sawdust in a predetermined volume unit. Since it is blended at a ratio of 9 to 1: 1, granular pearlite enters and adheres to the surface of the wooden material in many gaps formed between the wooden materials, and the pearlite is consolidated by a solidifying agent, and the wooden materials are also Consolidated into a block shape. Therefore, it can be set as the block material in which many gaps exist, and since the wood material and the pearlite itself are light materials, the weight can be remarkably reduced. Moreover, since there are many gaps even in a wet state, drainage is good and it is possible to suppress an increase in weight, and the specific gravity in a wet state can be suppressed to 0.5 to 1.0. In such a structure with many gaps, there may be a problem in strength, but on the roof, it is only necessary to assume that a load that humans can walk is applied, and such load conditions are sufficiently durable. It has become.

また、ブロック材を配列していくことで簡単に施工することができ、一部補修が必要な場合にもその部分のブロック材を取り換えればよい。さらに、現場において取り付ける形状に合わせてブロック成形したりすることも可能である。そして、解体する場合も簡単に行うことができ、ブロック材自体も粉砕して再利用することも可能である。以上のような施工の容易性は、屋上での施工作業に多大の利便性をもたらす。すなわち、ブロック化され軽量化されているため屋上への運搬作業が容易になり、現場においてもミキサー以外に特段の施工設備は不要で、ほとんどの作業を人力で行うことができる。   In addition, it can be easily constructed by arranging the block materials, and if a partial repair is required, the block material at that portion may be replaced. Furthermore, it is also possible to perform block molding according to the shape to be installed on site. And when disassembling, it can be performed easily, and the block material itself can also be crushed and reused. The ease of construction as described above brings great convenience to construction work on the roof. In other words, the work is transported to the roof easily because it is blocked and reduced in weight, and no special construction equipment other than the mixer is required on site, and most of the work can be performed manually.

さらに、植生を行う場合には、ブロック材に土壌収容用の凹部を形成すればよく、土壌中に必要な肥料成分を植生する植物毎に含有させておけば、ブロック材には特に肥料成分を混合しておく必要はなくなる。また、ブロック材には木質材が混合されているため次第に腐敗が進み、植物が生長してブロック材内部に根を張るようになれば、木質材自体が肥料となり、さらに木質材が腐敗して消滅することでさらに間隙が多くなって植物の根に空気が触れるようになり、植物にとってより好ましい生育環境が実現されるようになる。なお、木質材が腐敗して消滅してもパーライトが固化剤により強固に固結されているため、強度の劣化は抑えられる。   Furthermore, when vegetation is performed, it is only necessary to form a recess for accommodating soil in the block material. If the fertilizer component necessary for the vegetation is contained in each plant to be vegetated, the block material particularly includes the fertilizer component. There is no need to mix. In addition, because the wood material is mixed in the block material, it will gradually decay, and if the plant grows and roots inside the block material, the wood material itself becomes a fertilizer, and the wood material also decays. By disappearing, there will be more gaps and air will come into contact with the roots of the plant, and a more favorable growth environment for the plant will be realized. Even if the wood material decays and disappears, the pearlite is firmly consolidated by the solidifying agent, so that the strength deterioration can be suppressed.

本発明に係る屋上緑化構造は、上記のような構成を有することで、雨水等の水分は土壌、木質材及びパーライトにある程度は保水されるものの速やかに下部の排水層から外部に排出される。その際防水層により屋上表面に水が入り込むことは防止される。また、土壌流出防止層がブロック材及び前記土壌の露出表面を被覆しているため、表面の流水による土壌の流出が防止されるとともに、保水された水分の蒸発を抑制して表面温度の上昇を抑制する。また、土壌流出防止層を土舗装層とすることで透水性、保水性及び通気性を有し、景観上からみても優れたものとなる。また、屋根用の屋上緑化構造は、予め屋根材の上面形状に合わせてブロック材の底面を成形しておくので、屋根の上面にブロック材を容易に配列することができ、簡単に施工することが可能となる。   The rooftop greening structure according to the present invention has the above-described configuration, so that moisture such as rainwater is quickly discharged to the outside from the lower drainage layer although it is retained to some extent by the soil, the wood material and the pearlite. At that time, the waterproof layer prevents water from entering the roof surface. In addition, since the soil runoff prevention layer covers the block material and the exposed surface of the soil, the runoff of the soil due to running water on the surface is prevented, and evaporation of the retained water is suppressed to increase the surface temperature. Suppress. Moreover, it has water permeability, water retention, and air permeability by making the soil runoff prevention layer a soil pavement layer, and it is excellent even when viewed from the landscape. In addition, the rooftop greening structure for the roof is formed in advance according to the shape of the top surface of the roof material, so that the block material can be easily arranged on the top surface of the roof and installed easily. Is possible.

本発明に係る屋上緑化用ブロック材の製造方法は、上記のような構成を有することで、木材チップ又はおがくずからなる木質材を予め湿潤させておくので、粒状のパーライトを混合させると木質材表面にパーライトが十分に付着した状態となり、この状態で固化剤により混錬すれば固化剤はパーライト同士を強固に接着するため木質材同士も固結されて成形される。その際に圧縮されない状態で固結されるため、木質材の間には多くの間隙が存在した状態で成形固結されるようになる。   The method for manufacturing a roof greening block material according to the present invention has the above-described configuration, so that the wood material made of wood chips or sawdust is wetted in advance, so that the surface of the wood material when mixed with granular pearlite When the pearlite is sufficiently adhered to the pearlite and kneaded with the solidifying agent in this state, the solidifying agent firmly bonds the pearlite to each other so that the wooden materials are also solidified and molded. At that time, since it is consolidated in a state where it is not compressed, it is molded and consolidated in a state where there are many gaps between the wood materials.

また、固化剤として、パーライト及び木質材の所定容量単位に収容される量を基準としたそれぞれの配合量を加算した量に対して、所定容量単位に収容される量を基準とした比率で、セメントを３〜１０％、ゼオライトを１．５〜１０％、混和剤０．３〜１．０％及び水８〜１５％を混合したものを用いることで、セメントと混和剤により短時間で固化することができるとともに強度を高めることができる。また、ゼオライトを加えることでセメントのアクを取り除くように作用すると共に保水性が改善されて植物の根腐れを抑えることができる。そして、それぞれの材料を上記の範囲内の割合で用いることで、ブロック材の内部に間隙を十分存在させた状態固結するとともに上述した屋上での荷重条件に十分耐えることのできる強度を与えることが可能となる。   In addition, as a solidifying agent, a ratio based on the amount accommodated in the predetermined volume unit with respect to the amount obtained by adding the respective blending amounts based on the amount accommodated in the predetermined volume unit of the pearlite and the wood material, Solidified with cement and admixture in a short time by using 3-10% cement, 1.5-10% zeolite, 0.3-1.0% admixture and 8-15% water. It is possible to increase strength. In addition, the addition of zeolite acts to remove cement scum and improves water retention, thereby suppressing plant root rot. And by using each material in a ratio within the above range, the block material is solidified in a state where there is a sufficient gap and gives strength sufficient to withstand the above-mentioned roof load conditions. Is possible.

以下、本発明を添付図面に示す実施形態に基づいて詳しく説明する。なお、以下に説明する実施形態は、本発明を実施するにあたって好ましい具体例であるから、技術的に種々の限定がなされているが、本発明は、以下の説明において特に本発明を限定する旨明記されていない限り、これらの形態に限定されるものではない。   Hereinafter, the present invention will be described in detail based on embodiments shown in the accompanying drawings. The embodiments described below are preferable specific examples for carrying out the present invention, and thus various technical limitations are made. However, the present invention is particularly limited in the following description. Unless otherwise specified, the present invention is not limited to these forms.

図１は、本発明に係る屋上緑化用ブロック材の実施形態に関する斜視図である。この例では、ブロック材１は、平面視正方形の直方体状に成形されており、上面中央部には円筒状の凹部２が設けられている。凹部２には、後述するように土壌が収容されて植物が植生される。ブロック材１は、固化剤により固結したパーライトが木質材である木材チップ表面を被覆するように成形されており、そのため表面は木材チップの凹凸がそのまま表出している。そして、木材チップの間には多くの間隙が形成されている。   FIG. 1 is a perspective view of an embodiment of a roof greening block material according to the present invention. In this example, the block material 1 is formed in a rectangular parallelepiped shape in a plan view, and a cylindrical recess 2 is provided at the center of the upper surface. As will be described later, the recess 2 accommodates soil and vegetation. The block material 1 is formed so that the pearlite solidified by the solidifying agent covers the surface of the wood chip, which is a wood material, and therefore, the unevenness of the wood chip is exposed as it is on the surface. And many gaps are formed between the wood chips.

次に、ブロック材１を製造する方法を説明する。木質材として木材チップを用いる場合は、杉等の木材を数センチ角に切断したものを用いる。厚さは０．５〜１ｃｍのものが好ましい。この程度の厚さのものであれば、木材チップが重なるように固結されるため、強度を大きくする効果が期待できる。また、腐敗した後も強度の劣化を抑えることが可能となる。また、木質材としておがくずを用いる場合は、木材加工の際に生じる切削屑をそのまま用いればよい。   Next, a method for manufacturing the block material 1 will be described. When wood chips are used as the woody material, wood such as cedar cut into several centimeters is used. The thickness is preferably 0.5 to 1 cm. If the thickness is about this level, the wood chips are consolidated so as to overlap, so that an effect of increasing the strength can be expected. In addition, it is possible to suppress deterioration in strength even after decay. In addition, when sawdust is used as the wood material, cutting waste generated during wood processing may be used as it is.

パーライトは、白色の真珠系のもの（粒度範囲５．０ｍｍ以下；比重０．１７）及び黒色の黒曜石系のもの（粒度範囲３〜１５ｍｍ；比重０．１）を適宜配合して用いる。白色のものは保水性に優れ、黒色にものは排水性に優れており、用途に合わせて配合すれば、保水性及び排水性を調整することができる。   The pearlite is used by appropriately blending a white pearl type (particle size range 5.0 mm or less; specific gravity 0.17) and a black obsidian type (particle size range 3 to 15 mm; specific gravity 0.1). The white one is excellent in water retention, the black one is excellent in drainage, and the water retention and drainage can be adjusted if blended according to the application.

固化剤としては、木質材とパーライトとが成形固結されるものであればよく、一例を挙げれば、通常用いられているポルトランド系のセメントと混和剤を用いるのが経済的で好適である。混和剤としては、従来よりセメントの固化に用いられているものであれば採用可能である。混和剤によりセメントの固化が促進され強度も増すので、ブロック材の内部に間隙をより多く形成できる。これ以外にも接着効果がある樹脂材を固化剤として用いてもよい。そして、セメントを用いる場合には、アクを取り除く作用がある粉末又は粒状のゼオライトを加えておくとよい。配合割合としては、木質材及びパーライトを所定容量の容器に圧縮しない状態で満たし、その収容量を基準に算出する。木質材の収容量を１とすれば、パーライトは１〜９の割合で混合するとよい。また、固化剤については、パーライトの配合量と木質材の配合量を加算した量に対して、セメントを用いた場合で、セメントを３〜１０％、ゼオライトを１．５〜１０％、混和剤０．３〜１．０％の割合で加える。そして、セメントとともに混錬する水は８〜１５％の割合で加える。なお、ゼオライトの代わりに瓦屑を用いることもできる。   Any solidifying agent may be used as long as the wood material and pearlite are molded and consolidated. For example, it is economical and preferable to use a commonly used Portland cement and an admixture. . Any admixture that has been conventionally used for solidifying cement can be used. Since the solidification of the cement is promoted and the strength is increased by the admixture, more gaps can be formed inside the block material. In addition to this, a resin material having an adhesive effect may be used as a solidifying agent. And when using cement, it is good to add the powder or granular zeolite which has the effect | action which removes ax. The blending ratio is calculated based on the amount of wood and pearlite that are filled in a container of a predetermined capacity without being compressed and the amount contained. If the amount of wood material is 1, the pearlite may be mixed at a rate of 1-9. As for the solidifying agent, when cement is used relative to the sum of the amount of pearlite and the amount of wood, 3-10% of cement, 1.5-10% of zeolite, admixture Add at a rate of 0.3-1.0%. And the water kneaded with cement is added at a rate of 8 to 15%. In addition, debris can be used instead of zeolite.

まず、所定容量の容器を用いて圧縮しない状態で木質材を所定量計量し、一旦水槽に浸漬したり水を撒布することで十分湿潤した状態にする。湿潤状態の木質材と所定量計量したパーライトとをミキサー等により混合する。この際にゼオライトを併せて混合してもよい。そして、十分混合すると湿潤した木質材の周囲に粒状のパーライト及びゼオライトが付着し、周囲が被覆された状態となる。このような状態になると、セメント及び混和剤を投入しながら水を加えて混練する。均一に混練された状態になったら、所定量を矩形の型に入れる。型内を満たした状態になったら、圧縮することなくそのままの状態で固化させる。型から溢れる場合には手で軽く押さえてもよい。ブロック材に凹部を形成する場合には、まず型内の底面に所定の厚さだけ混練物を入れた後円筒状の内枠を型内の中央部分に設置して内枠の外周囲に混練物を入れて型内を満たした状態にする。混練物が固結した後内枠を取り外せば、凹部が形成される。   First, a predetermined amount of a wooden material is weighed in a state where it is not compressed using a container of a predetermined capacity, and is sufficiently dampened by being immersed in a water tank or spraying water. A wet wood material and a predetermined amount of perlite are mixed with a mixer or the like. At this time, zeolite may be mixed together. When sufficiently mixed, granular pearlite and zeolite adhere to the periphery of the wet wood material, and the periphery is covered. In such a state, water is added and kneaded while adding cement and admixture. When the mixture is uniformly kneaded, a predetermined amount is put into a rectangular mold. When the mold is filled, it is solidified as it is without being compressed. If it overflows from the mold, it may be lightly pressed by hand. When forming a recess in the block material, first put the kneaded material by a predetermined thickness on the bottom surface in the mold, then install the cylindrical inner frame in the center part of the mold and knead it around the outer periphery of the inner frame Put things in and fill the mold. If the inner frame is removed after the kneaded product is consolidated, a recess is formed.

成形固結されたブロック材は、多くの間隙が木質材の間に形成されており、木質材及びパーライト自体も軽量な材料のため格段に軽量化することができる。また、湿潤状態での比重も０．５〜１．０に抑えることができ、屋上に加わる重量を低減することが可能となる。湿潤状態の比重は、雨水が十分浸透した状態を想定して求めればよい。具体的な計測方法としては、まず、ブロック材を外形からみて所定の容積になるように形状を整える。次に、１日水槽に浸漬状態した後水槽から取り出して水を切り、重量を計測して容積から比重を計算する。以後同じように浸漬状態にして比重を計算することを繰り返して、定常状態になるまで行う。定常状態になれば、既にブロック材の内部が十分湿潤した状態となったと考えられるため、定常状態の比重を湿潤状態の比重とすればよい。   In the block material formed and consolidated, many gaps are formed between the wood materials, and the wood material and the perlite itself can be significantly reduced in weight because they are light materials. Moreover, the specific gravity in a wet state can also be suppressed to 0.5 to 1.0, and the weight applied to the rooftop can be reduced. The specific gravity in the wet state may be determined on the assumption that rainwater has sufficiently penetrated. As a specific measuring method, first, the shape of the block material is adjusted so as to have a predetermined volume as seen from the outer shape. Next, after being immersed in the water tank for one day, it is taken out from the water tank and drained, and the weight is measured to calculate the specific gravity from the volume. Thereafter, the calculation of specific gravity in the dipped state is repeated until the steady state is reached. If it becomes a steady state, it is considered that the inside of the block material has already been sufficiently wetted. Therefore, the specific gravity in the steady state may be set as the specific gravity in the wet state.

図２は、屋上緑化の施工を行う際に、ブロック材１を複数配列した状態の外観図である。ガーデニングのレイアウトに従って、コンクリート製の仕切り３や木製の柵が配置されており、盛土する部分にはブロック材１が配列されている。盛土を高くする部分はブロック材１の高さを高く成形したものを用いており、また草木を植える部分のブロック材１には図１に示したような凹部が形成されている。大きい木を植える部分にはブロック材１は配置せず空いた状態としておく。また、柵がループ状に形成されてブロック材１との間に隙間６が生じる場合には、現場において材料をポットミキサ等に投入して混錬し固化する前に隙間６に充填する。このように、レイアウトに沿って盛土する部分にベースとしてブロック材１を配列するので、簡単な作業で短時間に行うことができる。   FIG. 2 is an external view of a state in which a plurality of block members 1 are arranged when rooftop greening is performed. According to the gardening layout, concrete partitions 3 and wooden fences are arranged, and block materials 1 are arranged on the embankment. The part which raises embankment uses what shape | molded the height of the block material 1, and the recessed part as shown in FIG. 1 is formed in the block material 1 of the part which plants a plant. The block material 1 is not arranged in a portion where a large tree is to be planted, and is left empty. Further, when the fence is formed in a loop shape and a gap 6 is formed between the block material 1, the material is charged into the gap 6 before being put into a pot mixer or the like at the site and kneaded and solidified. Thus, since the block materials 1 are arranged as a base in the portion embanked along the layout, it can be performed in a short time with a simple operation.

図３は、屋上緑化構造における植物を植生した状態の概略断面図を示している。配列されたブロック材１に形成された凹部２には、土壌８が収容されて草木７が植生される。また、ブロック材１と屋上９の表面との間には、屋上９の表面から防水シート１０、耐根シート１１、排水シート１２及びフィルターシート１３が敷設される。防水シート１０は、屋上９への水の侵入を防止する。耐根シート１１は、防水シート１０への根の侵入を防止する。排水シート１２は、上方から流下する水を外部に排出する。フィルターシート１３は、土壌が流出するのを防止する。これらのシートは、いずれも従来より使用されているものである。フィルターシート１３の上面にブロック材１が配列されている。土壌８が露出する上面は必要に応じて防草シート１４で被覆しておくと、雑草等が生えることを確実に防止できる。そして、ブロック材１の上面には土舗装層１５が積層されると共に植物の根元部分には、人工の粒状物１６が敷設されている。土舗装層１５及び粒状物１６は、土壌が雨水により上面に流出するのを防止する。粒状物１６としては、例えば、軽量骨材を砕石したものに水性顔料で着色したものを用いることができる。   FIG. 3: has shown schematic sectional drawing of the state which planted the plant in a rooftop greening structure. In the recesses 2 formed in the arranged block members 1, soil 8 is accommodated and plants 7 are vegetated. Further, between the block material 1 and the surface of the rooftop 9, a waterproof sheet 10, a root-resistant sheet 11, a drainage sheet 12 and a filter sheet 13 are laid from the surface of the rooftop 9. The waterproof sheet 10 prevents water from entering the rooftop 9. The root-resistant sheet 11 prevents roots from entering the waterproof sheet 10. The drainage sheet 12 discharges water flowing down from above. The filter sheet 13 prevents the soil from flowing out. All of these sheets are conventionally used. The block material 1 is arranged on the upper surface of the filter sheet 13. If the upper surface where the soil 8 is exposed is covered with a weedproof sheet 14 as necessary, weeds and the like can be reliably prevented from growing. And the soil paving layer 15 is laminated | stacked on the upper surface of the block material 1, and the artificial granular material 16 is laid in the root part of the plant. The soil pavement layer 15 and the granular material 16 prevent the soil from flowing out to the upper surface by rainwater. As the granular material 16, for example, a material obtained by pulverizing a lightweight aggregate and coloring it with an aqueous pigment can be used.

図４は、屋根に緑化構造を施工した場合の概略図を示している。この例では、金属板を山形及び谷形が連続してジグザグ状に成形した屋根材２０の上面にブロック材２１を敷設してブロック材２１の上面に土舗装層を積層している。ブロック材２１の底面は、成形する際に屋根材２０のジグザグ形状に合致した型を用いて成形されているため、施工する際にはブロック材２１を屋根材２０の形状に合わせて敷設していけばよく、施工作業を効率化することができる。また、ブロック材２１は、できるだけ軽量化するために厚さを薄くすると共に木質材としておがくずを用いたり、パーライトの配合比率を高めて製造する。ブロック材２１の上面には、所定の厚さで土舗装層２２を積層しておくと、景観上優れたものになるとともに防草効果を発揮する。ブロック材２１には、予め植栽用の凹部２３を形成しておき、土壌を充填して蔦等の蔓状植物を植生する。なお、屋根材２０の谷状部分にパーライトを敷設した排水層２４を設けてブロック材２１を施工すれば、排水効果を高めることができる。   FIG. 4 shows a schematic view when a greening structure is constructed on the roof. In this example, a block material 21 is laid on the upper surface of a roof material 20 in which a mountain shape and a valley shape are formed in a zigzag shape continuously, and a soil pavement layer is laminated on the upper surface of the block material 21. Since the bottom surface of the block material 21 is formed using a mold that matches the zigzag shape of the roof material 20 when forming, the block material 21 is laid in accordance with the shape of the roof material 20 when performing construction. It is only necessary to make the construction work more efficient. The block material 21 is manufactured by reducing the thickness in order to reduce the weight as much as possible, using sawdust as a wood material, or increasing the blending ratio of pearlite. If the earth pavement layer 22 is laminated | stacked on the upper surface of the block material 21 by predetermined thickness, it will become the thing excellent on a landscape and will exhibit a herbicidal effect. A recess 23 for planting is formed in the block material 21 in advance, and the soil is filled with vines such as vines. In addition, if the drainage layer 24 which laid the pearlite in the valley-shaped part of the roofing material 20 is provided and the block material 21 is constructed, the drainage effect can be enhanced.

このように、ブロック材の厚さや底面の形状を容易に変更できるので、屋根の上面にも緑化構造を簡単に施工することができる。   Thus, since the thickness of a block material and the shape of a bottom face can be changed easily, a greening structure can be easily constructed also on the upper surface of a roof.

土舗装層は、山砂にセメント及び混和剤を混合して水を加えてミキサーで混練したものを練り込みでブロック材１の上面に積層する。山砂の他に人工軽量骨材、瓦等を粉砕したものを混合してもよい。また、顔料を添加して着色してもよい。練り込みで積層できるので、展圧しなくてもよく、展圧による屋上への影響を避けることができる。また、植物を植栽した後に積層できるので、施工を容易に行うことが可能となる。こうして積層された土舗装層は、透水性、通気性に優れ、また光を遮断するので防草効果も有する。   The soil pavement layer is laminated on the upper surface of the block material 1 by kneading a mixture of cement and admixture into mountain sand, adding water and kneading with a mixer. You may mix the thing which grind | pulverized the artificial lightweight aggregate, the roof tile, etc. besides the mountain sand. Moreover, you may add and color a pigment. Since it can be laminated by kneading, it is not necessary to apply pressure, and the influence of the pressure on the roof can be avoided. Moreover, since it can laminate | stack after planting a plant, it becomes possible to perform construction easily. The laminated soil pavement layer is excellent in water permeability and air permeability, and also has a herbicidal effect because it blocks light.

そして、土舗装層の表面に降雨があると、速やかに吸水されてブロック材１と土壌８に吸収される。ブロック材１に吸収された雨水はある程度保水されるものの排水シート１２に排出されて、外部に排水される。したがって、雨水により重量が増加することが抑えられ、屋上への荷重負担を増加を防ぐことができる。   And if there is rainfall on the surface of the soil pavement layer, it is quickly absorbed and absorbed by the block material 1 and the soil 8. Although rainwater absorbed by the block material 1 is retained to some extent, it is discharged to the drainage sheet 12 and drained to the outside. Therefore, an increase in weight due to rainwater is suppressed, and an increase in load burden on the roof can be prevented.

杉の木材チップを１０リットル、パーライトとして白色のもの１０リットル及び黒色のもの１０リットルを上述の製造方法により混合し、ポルトランド系セメント１．２リットル（約１．４ｋｇ）、ゼオライト３．２リットル（約３．３ｋｇ）、混和剤０．１リットル（約０．１ｋｇ）及び水３．５リットル（３．５ｋｇ）を混練して、型内に入れて圧縮させることなく成形固結させた。上述した計測方法により湿潤状態で比重を計測したところ０．８であった。   10 liters of cedar wood chips, 10 liters of white pearlite and 10 liters of black are mixed by the above manufacturing method, 1.2 liters of Portland cement (about 1.4 kg), 3.2 liters of zeolite (About 3.3 kg), 0.1 liter (about 0.1 kg) of the admixture and 3.5 liter (3.5 kg) of water were kneaded, put into a mold, and molded and consolidated without being compressed. It was 0.8 when specific gravity was measured in the wet state with the measuring method mentioned above.

本発明に係るブロック材に関する実施形態を示す概略斜視図である。It is a schematic perspective view which shows embodiment regarding the block material which concerns on this invention. 本発明に係る屋上緑化構造の施工時の外観図である。It is an external view at the time of construction of the rooftop greening structure which concerns on this invention. 本発明に係る屋上緑化構造に関する概略断面図である。It is a schematic sectional drawing regarding the rooftop greening structure which concerns on this invention. 本発明に係る屋根用の屋上緑化構造に関する概略図である。It is the schematic regarding the rooftop greening structure for roofs concerning this invention.

符号の説明Explanation of symbols

１ ブロック材
２ 凹部
３ 仕切り
４ 柵
７ 植物
８ 土壌
14 防草シート
15 土舗装層
16 粒状物
20 屋根材 1 Block material 2 Recess 3 Partition 4 Fence 7 Plant 8 Soil
14 Weedproof sheet
15 dirt pavement layer
16 Granules
20 Roofing material

Claims (3)

屋上表面に積層される防水層と、A waterproof layer laminated on the rooftop surface;
前記防水層上に積層される排水層と、  A drainage layer laminated on the waterproof layer;
前記排水層上に複数配列されるとともに、木材チップ又はおがくずからなる木質材と粒状のパーライトが所定容量単位に収容される量を基準とした比率で１：９〜１：１の割合で配合され、固化剤によりブロック状に成形固結されており、湿潤状態での比重が０．５〜１．０であるブロック材と、  A plurality of the drainage layers are arranged and blended at a ratio of 1: 9 to 1: 1 based on an amount of wood chips or sawdust from wood chips and granular pearlite stored in a predetermined volume unit. A block material that is molded and consolidated into a block shape by a solidifying agent and has a specific gravity in a wet state of 0.5 to 1.0;
前記ブロック材に形成された凹部に収容された土壌に植生された植物と、  A plant vegetated in soil housed in a recess formed in the block material;
山砂にセメント及び混和剤を混合して水を加えて混練して形成されるとともに前記ブロック材及び前記土壌の露出表面を少なくとも被覆するように積層された土舗装層と  A soil pavement layer formed by mixing cement and an admixture with mountain sand, adding water and kneading and laminating so as to cover at least the exposed surface of the block material and the soil;
を備えていることを特徴とする屋上緑化構造。A rooftop greening structure characterized by comprising: 屋根材の上面形状に合わせて成形された底面を有するとともに、木材チップ又はおがくずからなる木質材と粒状のパーライトが所定容量単位に収容される量を基準とした比率で１：９〜１：１の割合で配合され、固化剤によりブロック状に成形固結されており、湿潤状態での比重が０．５〜１．０であるブロック材を屋根の上面に複数配列し、It has a bottom surface formed in accordance with the shape of the top surface of the roofing material, and is a ratio of 1: 9 to 1: 1 based on the amount by which the wood material made of wood chips or sawdust and granular pearlite are accommodated in a predetermined capacity unit. The block material having a specific gravity of 0.5 to 1.0 in a wet state is arrayed on the top surface of the roof,
該ブロック材の凹部に収容された土壌に植物を植生し、  Planting the plant in the soil contained in the recess of the block material,
山砂にセメント及び混和剤を混合して水を加えて混練して形成される土舗装層を前記ブロック材及び前記土壌の露出表面を少なくとも被覆するように積層していることを特徴とする屋根用の屋上緑化構造。  A roof comprising a soil pavement layer formed by mixing cement and an admixture with mountain sand, kneading and adding water so as to cover at least the block material and the exposed surface of the soil. Rooftop greening structure. 木材チップ又はおがくずからなる木質材を水により十分湿潤させ、粒状のパーライトを前記木質材に対して所定容量単位に収容される量を基準とした比率で９：１〜１：１の割合で混合した後、前記パーライト及び前記木質材の所定容量単位に収容される量を基準としたそれぞれの配合量を加算した量に対して、所定容量単位に収容される量を基準とした比率で、セメントを３〜１０％、ゼオライトを１．５〜１０％、混和剤０．３〜１．０％及び水８〜１５％を混合した固化剤を混練して圧縮されない状態でブロック状に成形固結させたことを特徴とする屋上緑化用ブロック材の製造方法。A wood material made of wood chips or sawdust is sufficiently moistened with water, and granular pearlite is mixed at a ratio of 9: 1 to 1: 1 based on the amount accommodated in a predetermined volume unit with respect to the wood material. After that, the ratio of the amount contained in the predetermined volume unit to the amount obtained by adding the respective blending amounts based on the amount contained in the predetermined volume unit of the pearlite and the wood material as a reference, the cement 3 to 10%, zeolite 1.5 to 10%, admixture 0.3 to 1.0% and water 8 to 15% mixed with a solidifying agent kneaded and molded into blocks in a compressed state A method for producing a roof greening block material characterized by having been made.
JP2003305854A 2003-08-29 2003-08-29 Rooftop greening structure and manufacturing method of rooftop greening block material Expired - Fee Related JP3986071B2 (en)