JP3789513B2 - Easy-open packaging material, easy-open packaging bag and easy-open packaging using the same - Google Patents
Easy-open packaging material, easy-open packaging bag and easy-open packaging using the same Download PDFInfo
- Publication number
- JP3789513B2 JP3789513B2 JP15711595A JP15711595A JP3789513B2 JP 3789513 B2 JP3789513 B2 JP 3789513B2 JP 15711595 A JP15711595 A JP 15711595A JP 15711595 A JP15711595 A JP 15711595A JP 3789513 B2 JP3789513 B2 JP 3789513B2
- Authority
- JP
- Japan
- Prior art keywords
- easy
- resin film
- opening
- film
- packaging bag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】
【産業上の利用分野】
本発明は、易開封用包装材料、それを使用した易開封性包装用袋および易開封性包装体に関するものであり、更に詳しくは、詰め替え用洗剤等の充填包装に適する易開封用包装材料、それを使用した易開封性包装用袋および易開封性包装体に関するものである。
【0002】
【従来の技術】
従来、詰め替え用洗剤等の充填包装に適する包装用袋としては、種々のものが提案されているが、それらの一つに、最内層が線状低密度ポリエチレンとエチレン−ブテン−1共重合体のブレンド物フィルムであり、中間層が二軸延伸ポリオレフィンフィルムであり、最外層が二軸延伸ナイロンフィルムである三層積層フィルムから製造した包装用袋が提案されている(特開平5−193079号公報、特開平5−245990号公報、特開平5−278747号公報等)。
このものは、耐衝撃性と、耐環境ストレスクラッキング性に優れ、更に易開封性の良好なものであるとして提案されている。
【0003】
【発明が解決しようとする課題】
しかしながら、上記で提案されている包装用袋においては、開封時に包装用袋を引き裂いて易開封性を保持するためにのみ中間層が存在するものと思われるが、その中間層として使用されている二軸延伸ポリオレフィンフィルムは、赤外二色法による流れ方向の配向度MDと流れ方向と交叉する方向の配向度TDの比MD/TDが2以上であることが必要であり、このために最内層および最外層を構成するフィルムとの接着強度が弱く、時間の経過と共に層間で剥離し易くなるという問題点が存在するものである。
また、上記で提案されている包装用袋においては、包装用袋を引き裂いて易開封性を付与するためにのみ中間層が存在するものと思われるが、そのためにその分だけ製造コスト等の増加につながるものである。
ところで、詰め替え用洗剤等の充填包装に適する包装用袋としては、耐衝撃性、耐環境ストレスクラッキング性、シ−ルの安定性、保香性等の各種の重要な性能が要求され、保存安定性等に富むものでなければならず、これは逆に包装用袋の開封に際しては、その易開封性を困難にし兼ねないものである。
また、詰め替え用洗剤等の充填包装に適する包装用袋としては、その使用時に内容物を洗剤容器に移し替えなければならないものであり、そのために、包装用袋には、適度の強度、剛性等を有してその取り扱いに便利なものでなければならず、またその開封に際しては、易開封性であることが要求されるものである。
そこで本発明は、耐衝撃性、、耐環境ストレスクラッキング性、シ−ルの安定性、保香性、保存安定性、易開封性等の諸機能を充足し、その取り扱いが便利な詰め替え用洗剤等の充填包装に適する包装用袋を提供することである。
【0004】
【課題を解決するための手段】
本発明者は、上記のような問題点を解決し、その目的を達成すべく鋭意研究した結果、外層として、剛性等を有する強度に優れた樹脂のフィルムを使用し、他方、内層として、ヒ−トシ−ル性を有する樹脂のフィルムを使用し、而して、その両者を積層して二層からなる積層体を製造し、更に、上記の剛性等を有する強度に優れた樹脂のフィルムに、包装体になったときの最適開封位置に相当する箇所に開封用切れ目を刻設し、しかる後該積層体を使用して、その積層体のヒ−トシ−ル性を有する樹脂のフィルム面を対向させて重ね合わせてその周辺端部をヒ−トシ−ルして包装用袋を製造し、次いで該包装用袋の開口部から詰め替え用洗剤を充填し、更にその開口部をシ−ルして密閉して包装体を製造したところ、上記の技術的課題を解決し、その目的を達成することができることを見出して本発明を完成したものである。
【0005】
すなわち、本発明は、内層がヒ−トシ−ル性を有する樹脂のフィルムであり、外層が強度に優れた樹脂のフィルムである二層の積層体からなり、かつ該強度に優れた樹脂のフィルムに、包装体になったときの最適開封位置に相当する箇所に開封用切れ目を刻設してなることを特徴とする易開封用包装材料である。
【0006】
また、本発明は、内層がヒ−トシ−ル性を有する樹脂のフィルムであり、外層が強度に優れた樹脂のフィルムである二層の積層体からなり、かつ該強度に優れた樹脂のフィルムに、包装体になったときの最適開封位置に相当する箇所に開封用切れ目を刻設してなる易開封用包装材料であって、その内層の面を対向させて重ね合わせ、更にその周辺端部をヒ−トシ−ルしてシ−ル部を設けてなることを特徴とする易開封性包装用袋である。
【0007】
更にまた、本発明は、内層がヒ−トシ−ル性を有する樹脂のフィルムであり、外層が強度に優れた樹脂のフィルムである二層の積層体からなり、かつ該強度に優れた樹脂のフィルムに、包装体になったときの最適開封位置に相当する箇所に開封用切れ目を刻設してなる易開封用包装材料を、その内層の面を対向させて重ね合わせ、更にその周辺端部をヒ−トシ−ルしてシ−ル部を設けた易開封性包装用袋からなり、更にその開口部から内容物を充填包装し、その開口部をシ−ルしてなることを特徴とする易開封性包装体である。
【0008】
【作用】
本発明においては、剛性等を有する強度に優れた樹脂のフィルムを包装用袋を構成する基本素材とし、これに前述の詰め替え用洗剤等を充填包装する包装用袋として要求される諸機能をできるだけ保持させ、更に、これに開封用切れ目を刻設してこれを易開封の手段として採用し、他方、これにヒ−トシ−ル性を有する樹脂のフィルムを積層して製袋時のヒ−トシ−ル性を付与すると共にその切れ目による開口孔を塞ぐことによって、詰め替え用洗剤等の充填包装に適する易開封用包装材料、易開封性包装用袋および易開封性包装体を製造するものである。
【0009】
【本発明の詳細な説明】
上記の本発明について以下に更に詳しく説明する。
まず、上記の本発明において、内層として使用するヒ−トシ−ル性を有する樹脂のフィルムについて説明すると、かかる樹脂のフィルムとしては、熱によって溶融し相互に融着し得るものであればよく、例えば、低密度ポリエチレン、中密度ポリエチレン、高密度ポリエチレン、線状低密度ポリエチレン、ポリプロピレ、エチレン−酢酸ビニル共重合体、アイオノマ−樹脂、エチレン−アクリル酸エチル共重合体、エチレン−アクリル酸共重合体、エチレン−プロピレン共重合体、メチルペンテンポリマ−、その他等の樹脂の一種ないしそれ以上からなる樹脂のフィルムないしシ−トを使用することができる。
そのフィルムの厚さとしては、100μm以上、好ましくは、130μmないし500μm位が望ましい。
特に、本発明において、ヒ−トシ−ル性を有する樹脂のフィルムは、強度を有する樹脂のフィルムに対して、約2ないし20倍位の厚さ、好ましくは、4ないし10倍位の厚さを有することが望ましい。
本発明においては、上記のような厚さのフィルムを使用することによって、フィルムの剛性、強度等を増し、強度に優れた樹脂のフィルムが有する物性等と相まって、包装用袋を構成したときに袋としての姿勢維持性が良好となり、消費者の詰め替え作業等が容易となり、更に流通過程で店頭での取り扱い等が便利になるという利点を有し、更には内容物の保香性等も保持するものである。
ところで、本発明においては、上記のような樹脂のフィルムの中でも、特に、内層として使用するヒ−トシ−ル性を有する樹脂のフィルムとしては、線状低密度ポリエチレンまたはエチレン−酢酸ビニル共重合体を主体とするフィルムないしシ−トを使用することが最も好ましいものである。
すなわち、上記の線状低密度ポリエチレンまたはエチレン−酢酸ビニル共重合体を主体とするフィルムは、粘着性を有することから破断の伝搬が少なく耐衝撃性を向上させるという利点があるものであり、また、内層は常時洗剤に接触していることから、耐環境ストレスクラッキング性の劣化を防止するためにも有効なものである。
また、本発明においては、線状低密度ポリエチレンまたはエチレン−酢酸ビニル共重合体に、他の樹脂をブレンドすることもでき、例えば、エチレン−ブテン共重合体等をブレンドすることにより、若干、耐熱性に劣り高温環境下ではシ−ル安定性が劣化する傾向があるものの、引き裂き性が向上し、易開封性に寄与するという利点がある。
【0010】
次にまた、上記の本発明において、外層として使用する剛性を有し、強度に優れた樹脂のフィルムについて説明すると、かかる樹脂のフィルムとしては、包装用袋を構成する基本素材となることから、機械的、物理的、化学的、その他等において優れた性質を有する樹脂のフィルムないしシ−トを使用することができ、具体的には、例えば、ポリエステル系樹脂、ポリアミド系樹脂、ポリアラミド系樹脂、ポリプロピレン系樹脂、ポリカ−ボネ−ト系樹脂、ポリアセタ−ル系樹脂、フッ素系樹脂、その他等の強靱な樹脂のフィルムないしシ−トを使用することができる。
而して、上記の樹脂のフィルムないしシ−トとしては、未延伸フィルム、あるいは一軸方向または二軸方向に延伸した延伸フィルム等のいずれのものでも使用することができる。
また、本発明において、その樹脂のフィルムの厚さとしては、強度、剛性等について必要最低限に保持され得る厚さであればよく、厚すぎると、レ−ザ加工不良等を発生して引き裂き性が低下し、またコストを上昇するとい欠点もあり、逆に、薄すぎると、強度、剛性等が低下して好ましくないものである。
本発明においては、上記のような理由から、約10μmないし50μm位、好ましくは、約12μmないし25μm位が最も望ましい。
ところで、本発明においては、上記のような樹脂のフィルムの中でも、外層としての樹脂のフィルムとしては、剛性を有し、機械的強靱性、耐屈曲性、耐突き刺し性、耐衝撃性、耐磨耗性、耐寒性、耐熱性、耐薬品性等の諸物性に優れ、かつ印刷適性も有している二軸延伸ポリアミドフィルムを使用することが最も好ましいものである。
また、上記の二軸延伸ポリアミドフィルムは、その配向がフィルムの流れ方向に近く、重ね合わせたときも引き裂きずれが非常に小さく、かつ後述するように、炭酸ガスレ−ザの発振波長に吸収があることから、開封用切れ目を設けるときのレ−ザ加工を容易に行うことができるという利点を有するものである。
かかる二軸延伸ポリアミドフィルムとしては、例えば、ナイロン−6、ナイロン−66、ナイロン−11、ナイロン−12、ナイロン−6、10等のナイロンフィルムであって、NONコ−ト二軸延伸フィルム、ポリ塩化ビニリデンコ−ト二軸延伸フィルム等を使用することができる。
【0011】
次に、上記の本発明において、上記の内層としてのヒ−トシ−ル性を有する樹脂のフィルムと、外層としての強度に優れた樹脂のフィルムとを積層して二層からなる積層体を製造する方法について説明すると、かかる方法としては、通常の包装材料をラミネ−トする方法、例えば、ウエットラミネ−ション法、ドライラミネ−ション法、無溶剤型ドライラミネ−ション法、押し出しラミネ−ション法、Tダイ共押し出し成形法、共押し出しラミネ−ション法、その他等で行うことができる。
而して、本発明においては、上記の積層を行う際に、必要ならば、例えば、コロナ処理、オゾン処理等の前処理をフィルムに施すことができ、また、例えば、イソシアネ−ト系(ウレタン系)、ポリエチレンイミン系、ポリブタジェン系、有機チタン系等のアンカ−コ−ティング剤、あるいはポリウレタン系、ポリアクリル系、ポリエステル系、エポキシ系、ポリ酢酸ビニル系、セルロ−ス系、その他等のラミネ−ト用接着剤等の公知のアンカ−コ−ト剤、接着剤等を使用することができる。
【0012】
次にまた、上記の本発明において、上記の外層として使用する強度に優れた樹脂のフィルムに、包装体になったときの最適開封位置に相当する箇所に開封用切れ目を刻設する方法等について説明すると、かかる方法としては、例えば、加熱した針を押し付けるニ−ドルパンチ法、エンボスロ−ル、研磨ロ−ル、砥石、研磨テ−プ等を使用してフィルムを溶融し、穿孔する熱溶融穿孔法、ナイフ、カッタ−等を使用する物理的穿孔法、レ−ザ−ビ−ム加工、コロナ放電、プラズマ放電等の加工法、その他等の方法によって行うことができる。
而して、本発明において、強度に優れた樹脂のフィルムに開封用切れ目を刻設するに当たっては、該強度に優れた樹脂のフィルムの単体の状態、あるいは上記のように、内層としてのヒ−トシ−ル性を有する樹脂のフィルムと、外層としての強度に優れた樹脂のフィルムとを積層した二層からなる積層体の状態、更には該積層体を使用してなる包装用袋の状態、また該包装用袋を使用してなる包装体の状態等のいずれの状態において刻設してもよく、これによって、該強度に優れた樹脂のフィルムに開封用切れ目を設けることができる。
本発明において、開封用切れ目の形状としては、直線状、曲線状、ミシン目線状、破線状、その他等の任意の形状でよく、その本数は、一本ないしそれ以上でよく、また連続状あるいは不連続状等のいずれでもよい。
また、その切れ目の構造は、貫通孔ないし透過孔の状態、あるいはハ−フカットの状態、あるいはそれらが混在するような状態のいずれの状態でもよく、本発明においては、その部分が弱体化して袋の開封用の切れ目として作用すればよいものである。
ところで、本発明においては、強度に優れた樹脂のフィルムに開封用切れ目を設ける方法としては、パルス発振タイプのレ−ザの照射を用いてミシン目状の開封用切れ目を刻設する方法が最も好ましい方法である。
特に、レ−ザ加工で樹脂のフィルムに開封用切れ目を刻設する場合、樹脂のフィルムにレ−ザ発振波長の吸収があることが必要となることから、炭酸ガスレ−ザを用いて開封用切れ目を刻設することが最適である。
更に、本発明においては、炭酸ガスレ−ザ光の10.6ミクロンの波長は、ナイロンフィルムに選択的に吸収されやすく、また線状低密度ポリエチレンまたはエチレン−酢酸ビニル共重合体を主体とするフィルムではそのほとんどが透過されることから、本発明において、内層としてのヒ−トシ−ル性を有する樹脂のフィルムとして、線状低密度ポリエチレンまたはエチレン−酢酸ビニル共重合体を主体とするフィルムを使用し、外層としての強度に優れた樹脂のフィルムとして、二軸延伸ナイロンフィルムを使用し、その両者を組み合わせて積層してなる二層からなる積層体を使用し、これに炭酸ガスレ−ザを照射してレ−ザ加工を行うと、上記の二軸延伸ナイロンフィルムのみに開封用切れ目を刻設することができ、かつ該開封用切れ目は、線状低密度ポリエチレンまたはエチレン−酢酸ビニル共重合体を主体とするフィルムが溶融してその孔を閉塞することがなく、開封に際しては、極めて良好に袋を引き裂いて開封することができるという利点があって好ましいものである。
なお、上記において、積層体の状態で炭酸ガスレ−ザを照射してレ−ザ加工を行う代わりに、該積層体を使用してなる包装用袋または包装体の状態で上記と同様に炭酸ガスレ−ザを照射してレ−ザ加工をを行っても、上記と全く同様な結果を得ることができた。
本発明においては、上記のようにレ−ザ加工によって、その波長を選択することにより、外層を構成するフィルムのみに開封用切れ目を刻設することができるものである。
また、本発明においては、レ−ザ加工であれば、前述のように、包装用袋あるいは包装体を構成した状態においても開封用切れ目を刻設することができる。
【0013】
次に本発明において、上記の二層からなる積層体を使用して易開封性包装用袋について説明すると、かかる易開封性包装用袋は、内層がヒ−トシ−ル性を有する樹脂のフィルムであり、外層が強度に優れた樹脂のフィルムである二層の積層体からなり、かつ該強度に優れた樹脂のフィルムに、包装体になったときの最適開封位置に相当する箇所に開封用切れ目を刻設してなる易開封用包装材料であって、その内層の面を対向させて重ね合わせ、更にその周辺端部をヒ−トシ−ルしてシ−ル部を設けた構成からなるものである。
而して、その製袋方法としては、上記の易開封用包装材料を、折り曲げるかあるいは重ね合わせて、その内層の面を対向させ、更にその周辺端部を、例えば、側面シ−ル型、二方シ−ル型、三方シ−ル型、四方シ−ル型、封筒貼りシ−ル型、合掌貼りシ−ル型(ピロ−シ−ル型)、ひだ付シ−ル型、平底シ−ル型、角底シ−ル型、その他等のヒ−トシ−ル形態によりヒ−トシ−ルして、本発明にかかる種々の易開封性包装用袋を製造することができる。
その他、例えば、自立性包装用袋(スタンディングパウチ)等も可能である。
上記において、ヒ−トシ−ルの方法としては、例えば、バ−シ−ル、回転ロ−ルシ−ル、ベルトシ−ル、インパルスシ−ル、高周波シ−ル、超音波シ−ル等の公知の方法で行うことができる。
【0014】
次に、本発明においては、上記で製造した易開封性包装用袋の開口部から、例えば、詰め替え用洗剤(溶液または粉末)等を充填し、しかる後その開口部をヒ−トシ−ルしてシ−ル部を形成して、本発明にかかる易開封性包装体を製造することができる。
而して、上記の易開封性包装体は、耐衝撃性、、耐環境ストレスクラッキング性、シ−ルの安定性、保香性、保存安定性等の諸機能を充足し、流通段階等において包装上のトラブルがなく、また、その袋は、剛性を有してその取り扱いに便利であり、特に、開封に際しては、開封用切れ目から袋を簡単に引き裂いて開封することができ、その取り扱い易いものである。
【0015】
【実施例】
次に本発明について実施例を挙げて更に詳しく本発明を説明する。
実施例1
厚さ15μmの二軸延伸ナイロンフィルムと厚さ130μmの線状低密度ポリエチレンフィルムとを用意し、これらを使用して従来公知の方法であるドライラミネ−ション法で積層して二層からなる積層体を製造した。
次に該積層体を使用し、前壁と後壁と逆V字型の底壁とを用意し、それらの線状低密度ポリエチレンフィルム面を対向させ、その周辺端部をヒ−トシ−ルしてスタンディングパウチ(自立性袋)を製造した。
次いで上記で製造したスタンディングパウチ(自立性袋)の前壁と後壁との表裏に、その最適開封位置に相当する箇所に、発振波長10.6ミクロンの炭酸ガスレ−ザ照射機(米国、シンラッド社製、機種名、48−1−28W)の2機を使用して、出力を4Wとし搬送速度30m/分でレ−ザ照射し、その表裏に同時に連続線の開封用切れ目を刻設した。
しかる後上記で開封用切れ目を刻設したスタンディングパウチを使用し、その開口部から500mlの詰め替え用液体洗剤を充填し、次いでその開口部をヒ−トシ−ルし、密閉して包装体を製造した。
上記と同様にして、包装体10袋を製造した。
【0016】
実施例2
上記の実施例1において、レ−ザ照射の出力を8Wとし、また、刻設する開封用切れ目として、加工間隔0.2mmでミシン目状の不連続の開封用切れ目を刻設し、それ以外はすべて上記の実施例1と同様に行って、本発明にかかる包装体を10袋を製造した。
【0017】
比較例
上記の実施例1において、レ−ザ加工を行わない以外は、該実施例1と同様に行って、包装体を10袋を製造した。
【0018】
実験例
上記の実施例1ないし2および比較例で製造した包装体を使用して、下記に示す各比較試験を行った。
(比較試験)
試験1 開封試験:上記で製造した包装体各10袋について、その開封用切れ目を利用して開封し、その時切り口が開封用切れ目からずれた数を確認した。
試験2 落下衝撃試験:上記で製造した包装体各10袋について、120cmの高さからコンクリ−ト面に垂直に各包装体を20回落とし、その袋のトップおよびボトム等における袋の破れを調べた。
試験3 耐圧強度試験:上記で製造した包装体各10袋について、50Kgの加重を10分間かけた時の破袋数および加工部分のフィルムの伸びを調べた。
試験4 耐環境ストレスクラッキング試験:
上記で製造した包装体各10袋について、温度50℃の状態に4週間保存した時のクラック、液漏れの発生を調べた。
【0019】
上記の実験の結果、下記の表1に示す結果を得た。
【表1】
【0020】
上記において、開封性の数字は、(切り口が開封用切れ目からずれた数)/(テスト数)を意味し、また、落下衝撃強度の数は、(破袋数)/(テスト数)を意味する。
上記の表から明らかなように、本発明にかかる包装体は、開封性、耐衝撃性、耐圧強度、耐環境ストレスクラッキング性等において、極めて優れているものであった。
【0021】
【発明の効果】
以上の説明で明らかなように、本発明は、外層として、剛性等を有する強度に優れた樹脂のフィルムを使用し、他方、内層として、ヒ−トシ−ル性を有する樹脂のフィルムを使用し、而して、その両者を積層して二層からなる積層体を製造し、更に、上記の剛性等を有する強度に優れた樹脂のフィルムに、包装体になったときの最適開封位置に相当する箇所に開封用切れ目を刻設し、しかる後該積層体を使用して、その積層体のヒ−トシ−ル性を有する樹脂のフィルム面を対向させて重ね合わせてその周辺端部をヒ−トシ−ルして包装用袋を製造し、次いで該包装用袋の開口部から詰め替え用洗剤を充填し、更にその開口部をシ−ルして密閉して包装体を製造することを特徴とするものである。
而して、かかる本発明によって、耐衝撃性、、耐環境ストレスクラッキング性、シ−ルの安定性、保香性、保存安定性等の諸機能を充足し、流通段階等において包装上のトラブルがなく、また、その袋は、剛性を有してその取り扱いに便利であり、特に、開封に際しては、開封用切れ目から袋を簡単に引き裂いて開封することができ、その取り扱いが簡便な易開封性包装体を製造することができるものである。[0001]
[Industrial application fields]
The present invention relates to an easy-open packaging material, an easy-open packaging bag using the same, and an easy-open packaging body. More specifically, the easy-open packaging material suitable for filling packaging such as a refill detergent, The present invention relates to an easy-open packaging bag and an easy-open packaging body using the same.
[0002]
[Prior art]
Conventionally, various types of packaging bags suitable for filling packaging such as detergent for refilling have been proposed, and one of them is a linear low density polyethylene and an ethylene-butene-1 copolymer. A packaging bag manufactured from a three-layer laminated film in which the intermediate layer is a biaxially stretched polyolefin film and the outermost layer is a biaxially stretched nylon film has been proposed (Japanese Patent Laid-Open No. 5-193079). Publication, JP-A-5-245990, JP-A-5-278747, etc.).
This has been proposed as being excellent in impact resistance and environmental stress cracking resistance, and having good easy-openability.
[0003]
[Problems to be solved by the invention]
However, in the packaging bag proposed above, an intermediate layer seems to exist only for tearing the packaging bag at the time of opening to maintain easy opening, but it is used as the intermediate layer. The biaxially stretched polyolefin film must have a ratio MD / TD of the orientation degree MD in the flow direction by the infrared dichroism method and the orientation degree TD in the direction crossing the flow direction of 2 or more. There is a problem that the adhesive strength with the film constituting the inner layer and the outermost layer is weak, and it becomes easy to peel off between layers as time passes.
In addition, in the packaging bag proposed above, it seems that an intermediate layer exists only for tearing the packaging bag and imparting easy-opening properties. It leads to
By the way, as a packaging bag suitable for filling packaging such as a refill detergent, various important performances such as impact resistance, environmental stress cracking resistance, seal stability, and fragrance retention are required, and storage stability is ensured. It must be rich in properties and the like, and conversely, when opening a packaging bag, its easy-openability may be difficult.
In addition, as a packaging bag suitable for filling and packaging such as a refill detergent, the contents must be transferred to a detergent container at the time of use. For this reason, the packaging bag has appropriate strength, rigidity, etc. It must be easy to handle and must be easy to open when opening.
Therefore, the present invention satisfies various functions such as impact resistance, environmental stress cracking resistance, seal stability, aroma retention, storage stability, and easy-openability, and is a refilling detergent that is easy to handle. It is to provide a packaging bag suitable for filling and packaging.
[0004]
[Means for Solving the Problems]
As a result of diligent research to solve the above-mentioned problems and to achieve the object, the present inventor used a resin film having rigidity and the like as the outer layer and the inner layer as the inner layer. -Using a resin film having a tosyl property, and then laminating both to produce a two-layer laminate, and further to a resin film excellent in strength having the above-mentioned rigidity and the like. The film surface of the resin having the heat sealing property of the laminate is formed by engraving the opening for cutting at a position corresponding to the optimum opening position when the package is formed, and then using the laminate. And the peripheral edges thereof are heat sealed to produce a packaging bag, and then a refill detergent is filled from the opening of the packaging bag, and the opening is sealed. And sealed to produce a package, which resolves the above technical issues , And completed the present invention have found that it is possible to achieve the purpose.
[0005]
That is, the present invention is a resin film having a two-layer laminate in which the inner layer is a resin film having a heat seal property and the outer layer is a resin film having an excellent strength, and the resin layer has an excellent strength. In addition, the easy-open packaging material is characterized in that an opening cut is formed at a position corresponding to the optimum opening position when the package is formed.
[0006]
Further, the present invention is a resin film having an inner layer made of a resin film having a heat-seal property and an outer layer made of a resin film having an excellent strength, and having an excellent strength. In addition, it is an easy-open packaging material in which an opening cut is engraved at a location corresponding to the optimal opening position when it becomes a package, and the inner layer faces are overlapped, and the peripheral edge thereof is further overlapped. A bag for easy-open packaging characterized in that a part is heat sealed and a seal part is provided.
[0007]
Furthermore, the present invention is a resin film having an inner layer which is a resin film having heat sealability and an outer layer which is a resin film having an excellent strength, and the resin having an excellent strength. An easy-open packaging material in which an opening cut is engraved at a position corresponding to the optimum opening position when it becomes a package on the film, with its inner layer faces facing each other, and its peripheral edge It is characterized by comprising an easy-open packaging bag having a seal portion provided with a heat seal, and filling and packaging the contents from the opening portion, and sealing the opening portion. It is an easy-open packaging body.
[0008]
[Action]
In the present invention, a resin film having rigidity and the like and having a high strength is used as a basic material for constituting a packaging bag, and various functions required as a packaging bag for filling and packaging the above-described refill detergent and the like are possible as much as possible. In addition, this is used as an easy-opening means by engraving on the opening cut, and on the other hand, a heat-sealable resin film is laminated on this to make the heat at the time of bag making. Providing easy-to-open packaging materials, easy-open packaging bags, and easy-open packaging bodies suitable for filling packaging such as detergents for refilling, by providing toseal properties and closing the opening holes due to the cuts. is there.
[0009]
[Detailed Description of the Invention]
The above-described present invention will be described in more detail below.
First, in the present invention described above, a resin film having a heat seal property used as an inner layer will be described as long as the resin film can be melted by heat and fused to each other. For example, low density polyethylene, medium density polyethylene, high density polyethylene, linear low density polyethylene, polypropylene, ethylene-vinyl acetate copolymer, ionomer resin, ethylene-ethyl acrylate copolymer, ethylene-acrylic acid copolymer A resin film or sheet made of one or more resins such as ethylene-propylene copolymer, methylpentene polymer, and the like can be used.
The thickness of the film is 100 μm or more, preferably about 130 μm to 500 μm.
In particular, in the present invention, the resin film having heat sealability is about 2 to 20 times thicker, preferably 4 to 10 times thicker than the resin film having strength. It is desirable to have
In the present invention, by using the film having the thickness as described above, the rigidity, strength, etc. of the film is increased, and when the packaging bag is configured in combination with the physical properties of the resin film having excellent strength, etc. Good posture maintenance as a bag, making it easier for consumers to refill, making it easier to handle at the store during the distribution process, etc. To do.
By the way, in the present invention, among the resin films as described above, in particular, as a resin film having a heat seal property used as an inner layer, linear low density polyethylene or ethylene-vinyl acetate copolymer is used. It is most preferable to use a film or sheet mainly composed of
That is, the film mainly composed of the above-described linear low density polyethylene or ethylene-vinyl acetate copolymer has an advantage of improving impact resistance with less propagation of breakage because of having adhesiveness. Since the inner layer is always in contact with the detergent, it is also effective for preventing deterioration of environmental stress cracking resistance.
In the present invention, other resins can be blended with the linear low density polyethylene or the ethylene-vinyl acetate copolymer. For example, by blending the ethylene-butene copolymer or the like, the resin is slightly heat resistant. However, the seal stability tends to deteriorate in a high temperature environment, but there is an advantage that the tearability is improved and it contributes to easy opening.
[0010]
Next, in the present invention described above, a resin film having rigidity and excellent strength used as an outer layer will be described as a resin film, which is a basic material constituting a packaging bag. A resin film or sheet having excellent properties in mechanical, physical, chemical, etc. can be used. Specifically, for example, polyester resin, polyamide resin, polyaramid resin, A tough resin film or sheet such as a polypropylene resin, a polycarbonate resin, a polyacetal resin, a fluorine resin, or the like can be used.
Thus, as the resin film or sheet, any of an unstretched film or a stretched film stretched in a uniaxial direction or a biaxial direction can be used.
Further, in the present invention, the thickness of the resin film may be a thickness that can be held to the minimum necessary for strength, rigidity, etc. If it is too thick, a laser processing defect or the like occurs and tears. However, if it is too thin, strength, rigidity and the like are lowered, which is not preferable.
In the present invention, for the reasons described above, about 10 to 50 μm, preferably about 12 to 25 μm is most desirable.
By the way, in the present invention, among the resin films as described above, the resin film as the outer layer has rigidity, mechanical toughness, bending resistance, puncture resistance, impact resistance, abrasion resistance. It is most preferable to use a biaxially stretched polyamide film that is excellent in various physical properties such as wear resistance, cold resistance, heat resistance, and chemical resistance and also has printability.
Further, the above-mentioned biaxially stretched polyamide film has an orientation close to the flow direction of the film, so that the tearing deviation is very small even when they are overlapped with each other, and the oscillation wavelength of the carbon dioxide laser is absorbed as will be described later. For this reason, it has an advantage that the laser processing can be easily performed when the opening cut is provided.
Examples of the biaxially stretched polyamide film include nylon films such as nylon-6, nylon-66, nylon-11, nylon-12, nylon-6, 10 and the like, including NON-coated biaxially stretched films, poly A vinylidene chloride biaxially stretched film or the like can be used.
[0011]
Next, in the present invention, a laminate composed of two layers is produced by laminating a resin film having heat sealability as the inner layer and a resin film having excellent strength as the outer layer. This method is described as a method of laminating a normal packaging material, for example, a wet lamination method, a dry lamination method, a solventless dry lamination method, an extrusion lamination method, T A die co-extrusion molding method, a co-extrusion lamination method, and the like can be used.
Thus, in the present invention, when performing the above-mentioned lamination, if necessary, pretreatment such as corona treatment and ozone treatment can be applied to the film, and for example, isocyanate (urethane) Type), polyethyleneimine type, polybutadiene type, organic titanium type anchor coating agent, or polyurethane type, polyacrylic type, polyester type, epoxy type, polyvinyl acetate type, cellulose type, etc. -A well-known anchor coat agent, adhesives, etc., such as adhesive for adhesives, can be used.
[0012]
Next, in the above-mentioned present invention, a method of engraving a break for opening at a position corresponding to the optimum opening position when it becomes a package on the resin film having excellent strength used as the outer layer, etc. For example, as such a method, for example, a hot punching method in which a film is melted and punched using a needle punch method in which a heated needle is pressed, an embossing roll, a polishing roll, a grindstone, a polishing tape or the like. It can be carried out by a method such as a physical drilling method using a method, a knife, a cutter or the like, a laser beam machining, a machining method such as a corona discharge, a plasma discharge, or the like.
Thus, in the present invention, when the opening cut is engraved on the resin film having excellent strength, the resin film having excellent strength is in a single state or as described above, A state of a laminate composed of two layers of a resin film having a tosyl property and a resin film excellent in strength as an outer layer, and further a state of a packaging bag using the laminate, Moreover, you may cut | engrave in any states, such as the state of the package which uses this packaging bag, and this can provide the cut line for opening in the resin film excellent in this intensity | strength.
In the present invention, the shape of the opening cut line may be any shape such as a straight line, a curved line, a perforated line, a broken line, and the like, and the number thereof may be one or more, or may be continuous or Any of discontinuous shape etc. may be sufficient.
Further, the structure of the cut may be any state of a through hole or a perforation hole, a half cut state, or a state in which they are mixed. In the present invention, the portion is weakened and the bag is weakened. It only has to act as a break for opening.
By the way, in the present invention, the most preferable method for providing an opening cut on a resin film having excellent strength is to cut a perforated opening cut using irradiation of a pulse oscillation type laser. This is the preferred method.
In particular, when engraving on the opening of a resin film by laser processing, it is necessary to absorb the laser oscillation wavelength in the resin film. It is best to engrave the cut.
Furthermore, in the present invention, the 10.6 micron wavelength of carbon dioxide laser light is easily absorbed selectively by the nylon film, and is a film mainly composed of linear low density polyethylene or ethylene-vinyl acetate copolymer. In the present invention, a film mainly composed of linear low-density polyethylene or ethylene-vinyl acetate copolymer is used as the resin film having heat sealing properties as the inner layer. As a film of resin with excellent strength as the outer layer, a biaxially stretched nylon film is used, and a laminate consisting of two layers laminated together is used, and this is irradiated with a carbon dioxide laser. Then, when laser processing is performed, only the biaxially stretched nylon film can be engraved with an opening break, and the opening break The film mainly composed of linear low density polyethylene or ethylene-vinyl acetate copolymer does not melt and clog the hole, and can be opened by tearing the bag very well. This is preferable.
In the above, instead of performing laser processing by irradiating the carbon dioxide laser in the state of the laminated body, the carbon dioxide gas level in the state of the packaging bag or the packaging body using the laminated body is the same as described above. -Even when laser processing was performed by irradiating a laser beam, the same result as above could be obtained.
In the present invention, by selecting the wavelength by laser processing as described above, it is possible to engrave the opening cut only on the film constituting the outer layer.
In the present invention, as long as the laser processing is performed, the opening cut can be engraved even in the state where the packaging bag or the package is configured.
[0013]
Next, in the present invention, the easy-open packaging bag will be described using the above two-layer laminate. The easy-open packaging bag is a resin film whose inner layer has heat sealability. The outer layer is made of a two-layer laminate that is a resin film with excellent strength, and the resin film with excellent strength is used for opening at a location corresponding to the optimal opening position when it becomes a package. It is a packaging material for easy opening formed by engraving a cut, and has a structure in which the inner layer faces are overlapped to overlap each other, and the peripheral edge is heat sealed to provide a seal part. Is.
Thus, as the bag making method, the above easy-open packaging material is folded or overlapped so that the inner layer faces each other, and the peripheral edge thereof is, for example, a side seal type, Two-way seal type, three-way seal type, four-way seal type, envelope-attached seal type, joint-attached seal type (pill seal type), pleated seal type, flat bottom case -Various types of easy-open packaging bags according to the present invention can be manufactured by heat sealing in the form of a heat seal such as a seal type, a square bottom seal type, or the like.
In addition, for example, a self-supporting packaging bag (standing pouch) is also possible.
In the above, as the heat seal method, for example, a bar seal, a rotary roll seal, a belt seal, an impulse seal, a high frequency seal, an ultrasonic seal and the like are known. It can be done by the method.
[0014]
Next, in the present invention, for example, a refill detergent (solution or powder) is filled from the opening of the easy-open packaging bag produced above, and then the opening is heat sealed. By forming the seal part, the easy-open packaging body according to the present invention can be manufactured.
Thus, the above easy-open packaging body satisfies various functions such as impact resistance, environmental stress cracking resistance, seal stability, fragrance retention, storage stability, etc. There are no packaging problems, and the bag has rigidity and is convenient for handling. In particular, when opening the bag, the bag can be easily torn and opened from the opening cut, and the bag is easy to handle. Is.
[0015]
【Example】
Next, the present invention will be described in more detail with reference to examples.
Example 1
A laminate comprising a biaxially stretched nylon film having a thickness of 15 μm and a linear low density polyethylene film having a thickness of 130 μm, which are laminated by a dry lamination method which is a conventionally known method. Manufactured.
Next, using the laminate, a front wall, a rear wall, and an inverted V-shaped bottom wall are prepared, their linear low-density polyethylene film faces are opposed, and the peripheral ends thereof are heat sealed. A standing pouch was produced.
Next, on the front and back of the standing pouch (self-supporting bag) manufactured above, a carbon dioxide laser irradiator with an oscillation wavelength of 10.6 microns (Sinrad, USA) 2 machines manufactured by the company, model name 48-1-28W), laser output was performed at a transfer speed of 30m / min with an output of 4W, and continuous lines were opened on the front and back at the same time. .
After that, using the above-mentioned standing pouch with the opening cut engraved, the opening is filled with 500 ml of liquid detergent for refilling, and then the opening is heat sealed and sealed to produce a package. did.
In the same manner as described above, 10 bags of the package were produced.
[0016]
Example 2
In Example 1 above, the laser irradiation output is 8 W, and the opening cuts to be engraved are engraved perforated discontinuous opening cuts with a processing interval of 0.2 mm. Were all carried out in the same manner as in Example 1 to produce 10 bags of the package according to the present invention.
[0017]
Comparative Example 10 bags were produced in the same manner as in Example 1 except that laser processing was not performed in Example 1 described above.
[0018]
Experimental Examples The following comparative tests were conducted using the packaging bodies produced in Examples 1 to 2 and the comparative examples.
(Comparative test)
Test 1 Opening test: Each of the 10 bags manufactured as described above was opened using the opening cuts, and the number of cuts deviated from the opening cuts was confirmed.
Test 2 Drop impact test: For each of the 10 bags manufactured as described above, each package was dropped 20 times perpendicularly to the concrete surface from a height of 120 cm, and the bags were torn at the top and bottom of the bag. It was.
Test 3 Pressure-resistant strength test: For each of the 10 bags produced as described above, the number of broken bags and the elongation of the film of the processed part when a weight of 50 kg was applied for 10 minutes were examined.
Test 4 Environmental stress cracking test:
Each of the 10 bags produced as described above was examined for occurrence of cracks and liquid leakage when stored at a temperature of 50 ° C. for 4 weeks.
[0019]
As a result of the above experiment, the results shown in Table 1 below were obtained.
[Table 1]
[0020]
In the above, the number of openability means (number of cuts deviated from the opening cut) / (number of tests), and the number of drop impact strength means (number of broken bags) / (number of tests). To do.
As is apparent from the above table, the package according to the present invention was extremely excellent in terms of opening properties, impact resistance, pressure resistance, environmental stress cracking resistance, and the like.
[0021]
【The invention's effect】
As is apparent from the above description, the present invention uses a resin film having rigidity and the like as the outer layer and a resin film having heat sealability as the inner layer. Thus, the two layers are laminated to produce a two-layer laminate, and furthermore, the above-mentioned resin film with excellent strength having rigidity and the like corresponds to the optimum opening position when it becomes a package. An opening cut is formed in the area to be opened, and then the laminated body is used so that the film surfaces of the heat-sealable resin layer of the laminated body face each other and overlap each other, and the peripheral edge portion thereof is heated. -Toseal to produce a packaging bag, and then fill with a refill detergent from the opening of the packaging bag, and further seal and seal the opening to produce a package. It is what.
Thus, according to the present invention, various functions such as impact resistance, environmental stress cracking resistance, seal stability, fragrance retention, storage stability, etc. are satisfied, and packaging troubles in the distribution stage etc. In addition, the bag has rigidity and is convenient for handling. In particular, when opening the bag, the bag can be easily torn from the opening cut, and the bag can be easily opened. It is possible to manufacture a packaging material.
Claims (1)