JP3484685B2 - Curing accelerator for aqueous resin - Google Patents

Curing accelerator for aqueous resin

Info

Publication number
JP3484685B2
JP3484685B2 JP02389195A JP2389195A JP3484685B2 JP 3484685 B2 JP3484685 B2 JP 3484685B2 JP 02389195 A JP02389195 A JP 02389195A JP 2389195 A JP2389195 A JP 2389195A JP 3484685 B2 JP3484685 B2 JP 3484685B2
Authority
JP
Japan
Prior art keywords
water
curing accelerator
cobalt
dipyridyl
ether sulfate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP02389195A
Other languages
Japanese (ja)
Other versions
JPH08217915A (en
Inventor
茂樹 松永
恭二 高橋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DIC Corp
Original Assignee
Dainippon Ink and Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dainippon Ink and Chemicals Co Ltd filed Critical Dainippon Ink and Chemicals Co Ltd
Priority to JP02389195A priority Critical patent/JP3484685B2/en
Publication of JPH08217915A publication Critical patent/JPH08217915A/en
Application granted granted Critical
Publication of JP3484685B2 publication Critical patent/JP3484685B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【産業上の利用分野】本発明は、分子内に不飽和脂肪酸
基を有する水分散性又は水可溶性の樹脂に適用する硬化
促進剤に関するものである。
FIELD OF THE INVENTION The present invention relates to a curing accelerator applied to a water-dispersible or water-soluble resin having an unsaturated fatty acid group in the molecule.

【0002】[0002]

【従来の技術】一般に、アルキッド樹脂等、乾性油の如
き分子内に不飽和脂肪酸基を有する樹脂を含有する塗料
等には、補助剤として硬化促進剤(ドライヤー)が添加
される。従来、硬化促進剤としては、コバルト、鉛等の
金属石鹸が用いられてきた。しかしながら、近年、低公
害化あるいは作業者に対する安全衛生上の改善の目的か
ら、塗料の水系化や硬化促進剤の脱鉛化が進んでいる。
また、コバルト地金の供給不安定等によって、硬化促進
剤の省コバルト化も進んでおり、コバルト及び鉛の使用
量を抑えた水系樹脂用硬化促進剤を開発することが必要
となってきた。
2. Description of the Related Art Generally, a curing accelerator (dryer) is added as an auxiliary agent to paints containing a resin having an unsaturated fatty acid group in the molecule such as a drying oil, such as an alkyd resin. Conventionally, metal soaps such as cobalt and lead have been used as the curing accelerator. However, in recent years, for the purpose of reducing pollution or improving safety and health for workers, water-based paints and lead-free curing accelerators have been advanced.
Further, due to unstable supply of cobalt ingots, etc., the use of cobalt in curing accelerators has been promoted, and it has become necessary to develop a curing accelerator for water-based resins that suppresses the amount of cobalt and lead used.

【0003】鉛石鹸を使用しない代わりに、コバルト石
鹸の使用量を多くすれば、硬化性能が向上するが、皮膜
の表面硬化が早く進むため、しわや縮みを生じ易く、ま
た、コバルト石鹸を多く使用すると、樹脂のコストアッ
プになり、実用的ではない。
When lead cobalt is not used, but the amount of cobalt soap is increased, the curing performance is improved, but the surface of the film accelerates hardening, so wrinkles and shrinkage tend to occur, and more cobalt soap is used. If used, the cost of the resin increases and it is not practical.

【0004】[0004]

【発明が解決しようとする課題】硬化促進剤の活性を増
大させる添加剤として、特開平6−172689号公報
には、ジピリジルとコバルト石鹸との組み合わせが開示
されているが、この組み合わせでは、コバルト石鹸や鉛
石鹸を、分子内に不飽和脂肪酸基を有する水分散性又は
水可溶性の樹脂に分散させるために一般的に使用される
アルキルベンゼンスルフォン酸塩及びポリオキシアルキ
レンアルキルフェニルエーテルを界面活性剤として使用
しても、分子内に不飽和脂肪酸基を有する水分散性又は
水可溶性の樹脂への分散性能に劣り、十分な硬化性能が
発揮できないという問題点があった。
JP-A-6-172689 discloses a combination of dipyridyl and cobalt soap as an additive for increasing the activity of a curing accelerator. In this combination, cobalt is used. Alkylbenzene sulfonates and polyoxyalkylene alkylphenyl ethers, which are commonly used to disperse soaps and lead soaps in water-dispersible or water-soluble resins having unsaturated fatty acid groups in the molecule, are used as surfactants. Even if it is used, there is a problem in that the dispersibility in a water-dispersible or water-soluble resin having an unsaturated fatty acid group in the molecule is poor and sufficient curing performance cannot be exhibited.

【0005】本発明が解決しようとする課題は、鉛を使
用せず、しかも鉛がもたらす硬化性能に匹敵し、更には
それを凌駕する性能を有し、かつ、分子内に不飽和脂肪
酸基を有する水分散性又は水可溶性の樹脂に対する分散
性に優れ、コバルト石鹸の使用量をできるだけ少なくす
ることが可能な硬化促進剤を提供することにある。
The problem to be solved by the present invention is that it does not use lead, has a performance comparable to, and exceeds, the curing performance provided by lead, and has an unsaturated fatty acid group in the molecule. An object of the present invention is to provide a curing accelerator which has excellent water dispersibility or dispersibility in a water-soluble resin and which can reduce the amount of cobalt soap used as much as possible.

【0006】[0006]

【課題を解決するための手段】本発明者等は、上記課題
を解決するために鋭意研究を行った結果、分子内に不飽
和脂肪酸基を有する水分散性又は水可溶性の樹脂への硬
化促進剤の分散性を向上させるために、アルキルベンゼ
ンスルフォン酸塩及びポリオキシアルキレンアルキルフ
ェニルエーテルを用いた場合には、樹脂への分散性が悪
く、硬化促進効果が得られなかったが、非イオン性界面
活性剤とポリオキシアルキレンアルキルアリールエーテ
ル硫酸塩又はポリオキシアルキレンアルキルエーテル硫
酸塩とから成る界面活性剤と、ジピリジルとコバルト石
鹸とを組み合わせて分子内に不飽和脂肪酸基を有する水
分散性又は水可溶性の樹脂に配合した場合には、樹脂に
対する分散性が良く、コバルト石鹸の活性を高め、鉛石
鹸を使用しなくとも、コバルト石鹸及び鉛石鹸を配合し
た従来の分子内に不飽和脂肪酸基を有する水分散性又は
水可溶性の樹脂に比べ、乾燥時間を大幅に短縮し、塗料
に使用した際の塗膜の光沢、付着性を向上させ、かつ、
コバルトの添加量を減らしても乾燥時間を短縮すること
を見い出し、本発明を完成するに至った。
Means for Solving the Problems As a result of intensive studies to solve the above problems, the inventors of the present invention have accelerated curing to a water-dispersible or water-soluble resin having an unsaturated fatty acid group in the molecule. When an alkylbenzene sulfonate and a polyoxyalkylene alkylphenyl ether were used to improve the dispersibility of the agent, the dispersibility in the resin was poor and the curing acceleration effect was not obtained, but the nonionic interface A water-dispersible or water-soluble surfactant having an unsaturated fatty acid group in the molecule by combining a surfactant consisting of an activator and a polyoxyalkylene alkylaryl ether sulfate or a polyoxyalkylene alkyl ether sulfate with dipyridyl and cobalt soap. When mixed with the above resin, the dispersibility in the resin is good, the activity of cobalt soap is increased, and lead soap is used. Compared to conventional water-dispersible or water-soluble resins having unsaturated fatty acid groups in the molecule, which are mixed with cobalt soap and lead soap, the drying time is greatly shortened, and the gloss of the coating film when used in a paint, Improves adhesion, and
It has been found that the drying time can be shortened even if the amount of cobalt added is reduced, and the present invention has been completed.

【0007】即ち、本発明は上記課題を解決するため
に、(1)コバルト金属石鹸、(2)ジピリジル誘導体
(3)非イオン性界面活性剤及び(4)(a)ポリオキ
シアルキレンアルキルアリールエーテル硫酸塩又は
(b)ポリオキシアルキレンアルキルエーテル硫酸塩を
含有する硬化促進剤を提供する。
That is, in order to solve the above problems, the present invention provides (1) cobalt metal soap, (2) dipyridyl derivative (3) nonionic surfactant, and (4) (a) polyoxyalkylene alkylaryl ether. Provided is a curing accelerator containing a sulfate or (b) a polyoxyalkylene alkyl ether sulfate.

【0008】本発明で使用するコバルト石鹸としては、
例えば、オクチル酸塩の如き炭素原子数7〜10の脂肪
族モノカルボン酸のコバルト塩、トール油脂肪酸のコバ
ルト塩、ナフテン酸コバルト塩等が挙げられる。
As the cobalt soap used in the present invention,
Examples thereof include cobalt salts of aliphatic monocarboxylic acids having 7 to 10 carbon atoms such as octylates, cobalt salts of tall oil fatty acids, cobalt salts of naphthenic acid, and the like.

【0009】本発明で使用するジピリジル誘導体として
は、例えば、2、2’−ジピリジル、2,4’−ジピリ
ジル、4,4’−ジピリジル、4,4’−ジメチル−
2,2’−ジピリジル、6,6’−ジメチル−2,2’
−ジピリジル等が挙げられるが、これらの中でも2,
2’−ジピリジルが好ましい。
Examples of the dipyridyl derivative used in the present invention include 2,2'-dipyridyl, 2,4'-dipyridyl, 4,4'-dipyridyl and 4,4'-dimethyl-.
2,2'-dipyridyl, 6,6'-dimethyl-2,2 '
-Dipyridyl and the like, but among these, 2,
2'-dipyridyl is preferred.

【0010】ジピリジルとコバルト石鹸の使用割合は、
コバルト金属のモル数に対してジピリジルのモル数が
0.2〜5倍となる範囲が好ましく、0.5〜2倍とな
る範囲が特に好ましい。
The use ratio of dipyridyl and cobalt soap is
The range in which the number of moles of dipyridyl is 0.2 to 5 times the number of moles of cobalt metal is preferable, and the range of 0.5 to 2 times is particularly preferable.

【0011】本発明の硬化促進剤は、コバルト石鹸、界
面活性剤及びジピリジルを分子内に不飽和脂肪酸基を有
する水分散性又は水可溶性の樹脂に配合して用いるが、
コバルト石鹸、界面活性剤及びジピリジルを溶剤に溶解
させた溶液として用いると好ましく、当該溶剤として
は、例えば、トルエン、キシレン、ヘプタン、ヘキサ
ン、シクロヘキサン、ミネラルスピリットなどの炭化水
素系溶媒、メタノール、エタノール、プロパノール、シ
クロヘキサノールなどのアルコール系溶媒、メチルエチ
ルケトン、メチルイソブチルケトン、シクロヘキサノン
などのケトン系溶媒、プロピルエーテル、メチルセロソ
ルブ、セロソルブ、ブチルセロソルブ、メチルカルビト
ール、ブチルカルビトールなどのエーテル系溶媒、水な
どが挙げられ、これらから選ばれた1種もしくは2種以
上が使用できる。
The curing accelerator of the present invention is prepared by blending cobalt soap, a surfactant and dipyridyl in a water-dispersible or water-soluble resin having an unsaturated fatty acid group in the molecule.
Cobalt soap, surfactant and dipyridyl are preferably used as a solution dissolved in a solvent, as the solvent, for example, toluene, xylene, heptane, hexane, cyclohexane, hydrocarbon solvents such as mineral spirits, methanol, ethanol, Propanol, alcohol solvent such as cyclohexanol, methyl ethyl ketone, methyl isobutyl ketone, ketone solvent such as cyclohexanone, propyl ether, methyl cellosolve, cellosolve, butyl cellosolve, methyl carbitol, ether solvent such as butyl carbitol, water and the like. One or two or more selected from these can be used.

【0012】本発明で使用する非イオン性界面活性剤と
しては、例えば、ポリオキシエチレンセチルエーテル、
ポリオキシエチレンラウリルエーテルなどのポリオキシ
アルキレンアルキルエーテル、ポリオキシエチレンノニ
ルフェニルエーテル、ポリオキシエチレオクチルフェニ
ルエーテルの如きポリオキシアルキレンアルキルアリー
ルエーテル;ポリエチレングリコールモノラウレート、
ポリエチレングリコールジステアレートなどのポリアル
キレングリコール脂肪酸エステル、ソルビタンモノラウ
レート、ソルビタンモノステアレート、ソルビタンセス
キオレエートの如きソルビタン脂肪酸エステル;ポリオ
キシエチレンソルビタンモノラウレート、ポリオキシエ
チレンソルビタンモノステアレートの如きポリオキシア
ルキレンソルビタン脂肪酸エステル;グリセロールモノ
ステアレート、グリセロールモノオレエートの如きグリ
セリン脂肪酸エステル;ポリオキシアルキレンアルキル
アミンなどが挙げられる。これらの非イオン系界面活性
剤は、単独で、或いは2種以上を併用して本発明の水系
樹脂用硬化促進剤に使用することができる。
Examples of the nonionic surfactant used in the present invention include polyoxyethylene cetyl ether,
Polyoxyalkylene alkylaryl ethers such as polyoxyalkylene alkyl ethers such as polyoxyethylene lauryl ether, polyoxyethylene nonyl phenyl ethers, polyoxyethylene octyl phenyl ethers; polyethylene glycol monolaurate,
Polyalkylene glycol fatty acid ester such as polyethylene glycol distearate, sorbitan monolaurate, sorbitan monostearate, sorbitan fatty acid ester such as sorbitan sesquioleate; polyoxyethylene sorbitan monolaurate, polyoxyethylene sorbitan monostearate Examples thereof include polyoxyalkylene sorbitan fatty acid ester; glycerol monostearate, glycerol fatty acid ester such as glycerol monooleate; polyoxyalkylene alkylamine and the like. These nonionic surfactants can be used alone or in combination of two or more kinds for the curing accelerator for the water-based resin of the present invention.

【0013】本発明で使用するポリオキシアルキレンア
ルキルアリールエーテル硫酸塩としては、例えば、ポリ
オキシエチレンラウリルフェニルエーテル硫酸ナトリウ
ム、ポリオキシエチレンラウリルフェニルエーテル硫酸
カリウム、ポリオキシエチレンノニルフェニルエーテル
硫酸ナトリウム、ポリオキシエチレンオレイルフェニル
エーテル硫酸ナトリウム、ポリオキシエチレンセチルフ
ェニルエーテル硫酸ナトリウム、ポリオキシエチレンラ
ウリルフェニルエーテル硫酸アンモニウム、ポリオキシ
エチレンノニルフェニルエーテル硫酸アンモニウム、ポ
リオキシエチレンオレイルフェニルエーテル硫酸アンモ
ニウムなどが挙げられる。これらのポリオキシアルキレ
ンアルキルアリールエーテル硫酸塩は、単独で、或いは
2種以上を併用して本発明の水系樹脂用硬化促進剤に使
用することができる。
Examples of the polyoxyalkylene alkyl aryl ether sulfate used in the present invention include sodium polyoxyethylene lauryl phenyl ether sulfate, potassium polyoxyethylene lauryl phenyl ether sulfate, sodium polyoxyethylene nonyl phenyl ether sulfate and polyoxy. Examples thereof include sodium ethylene oleyl phenyl ether sulfate, sodium polyoxyethylene cetyl phenyl ether sulfate, ammonium polyoxyethylene lauryl phenyl ether sulfate, ammonium polyoxyethylene nonyl phenyl ether sulfate, and ammonium polyoxyethylene oleyl phenyl ether sulfate. These polyoxyalkylene alkylaryl ether sulfates can be used alone or in combination of two or more kinds for the curing accelerator for the water-based resin of the present invention.

【0014】本発明で使用するポリオキシアルキレンア
ルキルエーテル硫酸塩としては、例えば、ポリオキシエ
チレンラウリルエーテル硫酸ナトリウム、ポリオキシエ
チレンラウリルエーテル硫酸カリウム、ポリオキシエチ
レンオレイルエーテル硫酸ナトリウム、ポリオキシエチ
レンセチルエーテル硫酸ナトリウム、ポリオキシエチレ
ンラウリルエーテル硫酸アンモニウム、ポリオキシエチ
レンオレイルエーテル硫酸アンモニウムなどが挙げられ
る。これらのポリオキシアルキレンアルキルエーテル硫
酸塩は、単独で、或いは2種以上を併用して本発明の水
系樹脂用硬化促進剤に使用することができる。
Examples of the polyoxyalkylene alkyl ether sulfate used in the present invention include sodium polyoxyethylene lauryl ether sulfate, potassium polyoxyethylene lauryl ether sulfate, sodium polyoxyethylene oleyl ether sulfate, and polyoxyethylene cetyl ether sulfate. Examples thereof include sodium, ammonium polyoxyethylene lauryl ether sulfate, and ammonium polyoxyethylene oleyl ether sulfate. These polyoxyalkylene alkyl ether sulfates can be used alone or in combination of two or more kinds for the curing accelerator for the water-based resin of the present invention.

【0015】本発明で使用する界面活性剤の配合量は、
コバルト石鹸及びジピリジルを配合した溶液100重量
部に対し、0.1〜50重量部の範囲が好ましく、1〜
20重量部の範囲が特に好ましい。また、非イオン性界
面活性剤に対するポリオキシアルキレンアルキルアリー
ルエーテル硫酸塩またはポリオキシアルキレンアルキル
エーテル硫酸塩の割合は、非イオン性界面活性剤100
重量部に対して、1〜10000重量部の範囲が好まし
く、10〜1000重量部の範囲が特に好ましい。
The amount of the surfactant used in the present invention is
The range of 0.1 to 50 parts by weight is preferable to 100 parts by weight of the solution containing cobalt soap and dipyridyl,
A range of 20 parts by weight is especially preferred. Further, the ratio of the polyoxyalkylene alkyl aryl ether sulfate or the polyoxyalkylene alkyl ether sulfate to the nonionic surfactant is 100% of the nonionic surfactant.
The range of 1 to 10000 parts by weight is preferable, and the range of 10 to 1000 parts by weight is particularly preferable.

【0016】本発明の硬化促進剤を配合する分子内に不
飽和脂肪酸基を有する水分散性又は水可溶性の樹脂とし
ては、当該コバルト石鹸により酸化重合を起こして硬化
が促進される樹脂成分を主成分とするものなどが挙げら
れ、樹脂成分としては、分子内に不飽和脂肪酸基を含む
水分散性または水可溶性のアルキッド系樹脂や各種の油
変性樹脂などが挙げられる。
The water-dispersible or water-soluble resin having an unsaturated fatty acid group in the molecule to which the curing accelerator of the present invention is added is mainly a resin component which is oxidatively polymerized by the cobalt soap to accelerate the curing. Examples of the resin component include water-dispersible or water-soluble alkyd-based resins containing unsaturated fatty acid groups in the molecule, and various oil-modified resins.

【0017】また、この硬化促進剤の配合量は、分子内
に不飽和脂肪酸基を有する水分散性又は水可溶性の樹脂
中の樹脂不揮発分100部に対して、コバルト分とし
て、0.001〜1重量部、好ましくは0.01〜0.
2重量部の範囲、ジピリジル分として0.001〜5重
量部、好ましくは0.01〜0.5重量部である。な
お、樹脂には、必要に応じて各種の顔料やタレ止め剤そ
の他の塗料添加剤などを配合することができる。
The amount of the curing accelerator blended is 0.001 to 0.001 as the cobalt content based on 100 parts of the resin non-volatile content in the water-dispersible or water-soluble resin having an unsaturated fatty acid group in the molecule. 1 part by weight, preferably 0.01-0.
The amount of dipyridyl is 0.001 to 5 parts by weight, preferably 0.01 to 0.5 parts by weight, in the range of 2 parts by weight. It should be noted that various kinds of pigments, anti-sagging agents and other paint additives may be added to the resin, if necessary.

【0018】[0018]

【実施例】以下、実施例及び比較例により本発明を更に
具体的に説明する。なお、例中の部はすべて重量基準で
ある。
EXAMPLES The present invention will be described in more detail with reference to Examples and Comparative Examples. All parts in the examples are based on weight.

【0019】(実施例1〜5)ジピリジル、ナフテン酸
コバルト、溶剤及び界面活性剤を、表1に示した割合で
混合した添加剤2部を、水系アルキッド樹脂「ウオータ
ーゾールCD−520」(大日本インキ化学工業株式会
社製)100部と共に十分に混合した後、その分散状態
を観察した。その結果を表1にまとめて示した。
(Examples 1 to 5) 2 parts of an additive obtained by mixing dipyridyl, cobalt naphthenate, a solvent and a surfactant in a ratio shown in Table 1 was mixed with an aqueous alkyd resin "Waterzol CD-520" (large). After thoroughly mixing with 100 parts of Nippon Ink Chemical Co., Ltd., the dispersion state was observed. The results are summarized in Table 1.

【0020】[0020]

【表1】 [Table 1]

【0021】次に、チタンホワイト顔料(石原産業株式
会社製R−820)1500g、上記の水系アルキッド
樹脂ウオーターゾールCD−520、3500g、皮張
防止剤(メチルエチルケトオキシム)15gを3本ロー
ルで混練して得た塗料40gに、ジピリジル、ナフテン
酸コバルト、溶剤及び界面活性剤を表1に示した割合で
混合した添加剤を、表2に示した割合(樹脂不揮発分1
00部に対するコバルト分の割合)で添加して得られた
塗料を調製し、これをガラス板上にアプリケータを用い
て厚さ76μmの塗膜をひき、RCI(米国ライヒホー
ルド・ケミカル社(REICHHOLD CHEMICALS INC.)の商
標)型乾燥時間測定機により乾燥時間を測定すると共
に、得られた塗膜の物性を測定した。これらの結果を表
2にまとめて示した。
Next, 1500 g of titanium white pigment (R-820 manufactured by Ishihara Sangyo Co., Ltd.), 3500 g of the above water-based alkyd resin Waterzol CD-520, and 15 g of anti-skinning agent (methyl ethyl ketoxime) were kneaded with a three-roll mill. 40 g of the obtained paint was mixed with dipyridyl, cobalt naphthenate, a solvent and a surfactant in the proportions shown in Table 1, and the proportions shown in Table 2 (resin non-volatile content 1
A coating material having a thickness of 76 μm was drawn on a glass plate using an applicator to prepare a paint obtained by adding the cobalt content to the 00 parts, and the RCI (Reichhold Chemical Co. CHEMICALS INC.) (Trademark) type drying time measuring device was used to measure the drying time and the physical properties of the resulting coating film. The results are summarized in Table 2.

【0022】(比較例1)従来技術における硬化促進剤
の平均水準的性能を示す目的で、上記塗料40gに、ナ
フテン酸コバルト5%W(商品名:大日本インキ化学工
業株式会社製)、ナフテン酸鉛20%W(商品名:大日
本インキ化学工業株式会社製)を、表2に示す割合(樹
脂不揮発分100部に対するコバルト分または鉛分の割
合)で添加して、得られた塗料の乾燥時間と塗膜の物性
を測定した。得られた結果を表2に示した。
(Comparative Example 1) For the purpose of showing the average level performance of the curing accelerator in the prior art, 40 g of the above paint was added to 5 g of cobalt naphthenate 5% W (trade name: manufactured by Dainippon Ink and Chemicals, Inc.) and naphthene. 20% W of lead acid (trade name: manufactured by Dainippon Ink and Chemicals, Inc.) was added at a ratio shown in Table 2 (a ratio of cobalt or lead to 100 parts of resin nonvolatile content) to obtain a coating composition. The drying time and the physical properties of the coating film were measured. The obtained results are shown in Table 2.

【0023】(塗膜物性の評価方法) 「光沢」 :JIS K5400中の60度鏡面光沢度
試験に準じ、試験を行った。 「スオードロッカー」 :スオードロッカー試験器(テ
スター産業製)を用い、ガラス板での値を100とした
時の測定値で示した。 「クロスカット」 :JIS K5400中の碁盤目試
験に準じ試験を行い、セロテープを塗布方向に粘着剥離
させた時、100個の碁盤目中何個接着していたかで示
した。 「鉛筆硬度」 :JIS K5400中の鉛筆引っかき
試験に準じ、試験を行った。
(Evaluation method of physical properties of coating film) "Gloss": The test was conducted according to the 60-degree specular gloss test in JIS K5400. "Sword rocker": A suede rocker tester (manufactured by Tester Sangyo Co., Ltd.) was used and the measured value was shown when the value on the glass plate was 100. "Cross cut": A test was conducted according to the cross-cut test in JIS K5400, and it was shown by how many of the 100 cross-cuts were adhered when the cellophane tape was adhesively peeled in the coating direction. "Pencil hardness": The test was performed according to the pencil scratch test in JIS K5400.

【0024】[0024]

【表2】 [Table 2]

【0025】*1)添加量:樹脂不揮発分100部に対
するコバルト分またはジピリジルの添加量。 *2)乾燥時間:温度25℃,湿度60%で測定。
* 1) Addition amount: The addition amount of cobalt content or dipyridyl to 100 parts of resin non-volatile content. * 2) Drying time: Measured at a temperature of 25 ° C and a humidity of 60%.

【0026】(比較例2)従来技術における界面活性剤
の性能を示す目的で、ジピリジル、ナフテン酸コバルト
5%W(商品名:大日本インキ化学工業株式会社製)及
び溶剤を表3に示した割合で混合した添加剤2部を、水
系アルキッド樹脂「ウオーターゾールCD−520」1
00部と共に十分に混合し、その安定性を観察した。結
果を表3に示した。
Comparative Example 2 Table 3 shows dipyridyl, 5% W cobalt naphthenate (trade name: manufactured by Dainippon Ink and Chemicals, Inc.) and solvents for the purpose of showing the performance of the surfactant in the prior art. 2 parts of the additive mixed in a ratio of water-based alkyd resin "Watersol CD-520" 1
Mix well with 00 parts and observe its stability. The results are shown in Table 3.

【0027】(比較例3〜4)ジピリジル、ナフテン酸
コバルト、溶剤及び界面活性剤を、表3に示した割合で
混合した添加剤2部を、水系アルキッド樹脂「ウオータ
ーゾールCD−520」100部と共に十分に混合し、
その安定性を観察した。結果を表3にまとめて示した。
(Comparative Examples 3 to 4) Dipyridyl, cobalt naphthenate, a solvent and a surfactant were mixed in the proportions shown in Table 3 and 2 parts of the additive was mixed with 100 parts of an aqueous alkyd resin "Waterzol CD-520". Mix well with
Its stability was observed. The results are summarized in Table 3.

【0028】[0028]

【表3】 [Table 3]

【0029】なお、実施例1〜5及び比較例3〜4にお
いて使用した界面活性剤は次の市販品を用いた。
The following commercial products were used as the surfactants used in Examples 1-5 and Comparative Examples 3-4.

【0030】ポリオキシエチレンノニルフェニルエーテ
ル:松本油脂製薬株式会社製の「ペネロールNP−1
0」 ポリオキシエチレンラウリルエーテル:松本油脂製薬株
式会社製の「アクチノールL−3」 ポリオキシエチレンノニルフェニルエーテル硫酸ナトリ
ウム:松本油脂製薬株式会社製の「ペネロールSN」 ポリオキシエチレンアルキルフェニルエーテル硫酸アン
モニウム:松本油脂製薬株式会社製の「RY−321」 ポリオキシエチレンラウリルエーテル硫酸ナトリウム:
松本油脂製薬株式会社製の「アクチノールSL−3」
Polyoxyethylene nonyl phenyl ether: "Penerol NP-1" manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.
0 "Polyoxyethylene lauryl ether:" Actinol L-3 "manufactured by Matsumoto Yushi-Seiyaku Co., Ltd. Sodium polyoxyethylene nonylphenyl ether sulfate:" Penerol SN "manufactured by Matsumoto Yushi-Seiyaku Co., Ltd. Ammonium polyoxyethylene alkylphenyl ether sulfate: Matsumoto "RY-321" manufactured by Yushi-Seiyaku Co., Ltd. Sodium polyoxyethylene lauryl ether sulfate:
"Actinol SL-3" manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.

【0031】[0031]

【発明の効果】コバルト石鹸、ジピリジル誘導体、非イ
オン性界面活性剤及びポリオキシアルキレンアルキルア
リールエーテル硫酸塩またはポリオキシアルキレンアル
キルエーテル硫酸塩を含有する硬化促進剤は、分子内に
不飽和脂肪酸基を有する水分散性又は水可溶性の樹脂に
対する分散性に優れ、また、鉛石鹸を使用せず、かつ、
コバルト添加量を減らしても、樹脂の乾燥時間を短縮
し、塗膜の光沢、付着性を向上させるもので、本発明に
係る硬化促進剤は、産業上重要な価値を有する。
The curing accelerator containing cobalt soap, dipyridyl derivative, nonionic surfactant and polyoxyalkylene alkyl aryl ether sulfate or polyoxyalkylene alkyl ether sulfate has an unsaturated fatty acid group in the molecule. Excellent dispersibility in water-soluble or water-soluble resin having, also, without using lead soap, and
Even if the amount of cobalt added is reduced, the drying time of the resin is shortened and the gloss and adhesion of the coating film are improved. The curing accelerator according to the present invention has industrially important value.

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 FI C09D 167/08 C09D 167/08 (58)調査した分野(Int.Cl.7,DB名) C08L 1/00 - 101/16 C09D 1/00 - 201/10 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI C09D 167/08 C09D 167/08 (58) Fields investigated (Int.Cl. 7 , DB name) C08L 1/00-101/16 C09D 1/00-201/10

Claims (3)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】 分子内に不飽和脂肪酸基を有する水分散
性又は水可溶性の樹脂に適用する硬化促進剤であって、
(1)コバルト金属石鹸、(2)ジピリジル誘導体
(3)非イオン性界面活性剤及び(4)(a)ポリオキ
シアルキレンアルキルアリールエーテル硫酸塩又は
(b)ポリオキシアルキレンアルキルエーテル硫酸塩を
含有する硬化促進剤。
1. A curing accelerator applied to a water-dispersible or water-soluble resin having an unsaturated fatty acid group in the molecule, comprising:
Containing (1) cobalt metal soap, (2) dipyridyl derivative (3) nonionic surfactant, and (4) (a) polyoxyalkylene alkyl aryl ether sulfate or (b) polyoxyalkylene alkyl ether sulfate. Curing accelerator.
【請求項2】 ジピリジル誘導体が2,2’−ジピリジ
ル誘導体である請求項1記載の硬化促進剤。
2. The curing accelerator according to claim 1, wherein the dipyridyl derivative is a 2,2′-dipyridyl derivative.
【請求項3】 ジピリジル誘導体が2,2’−ジピリジ
ルである請求項1記載の硬化促進剤。
3. The curing accelerator according to claim 1, wherein the dipyridyl derivative is 2,2′-dipyridyl.
JP02389195A 1995-02-13 1995-02-13 Curing accelerator for aqueous resin Expired - Fee Related JP3484685B2 (en)