JP3440337B2 - Easy release paper container blank - Google Patents
Easy release paper container blankInfo
- Publication number
- JP3440337B2 JP3440337B2 JP31287093A JP31287093A JP3440337B2 JP 3440337 B2 JP3440337 B2 JP 3440337B2 JP 31287093 A JP31287093 A JP 31287093A JP 31287093 A JP31287093 A JP 31287093A JP 3440337 B2 JP3440337 B2 JP 3440337B2
- Authority
- JP
- Japan
- Prior art keywords
- heat
- paper container
- peeling
- resin layer
- container blank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、熱封緘で成形され、易
剥離性あるいは易解体性のある紙容器ブランクに関し、
特に好適にはバー付きアイスクリーム用紙容器ブランク
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a paper container blank which is molded by heat-sealing and is easily peelable or easily disassembled.
Particularly preferably, it relates to an ice cream paper container blank with a bar.
【０００２】[0002]
【従来の技術】従来より、板紙を基材とする紙容器の熱
封緘部の剥離性を得るために凝集破壊を起こしやすいホ
ットメルト層を介して熱封緘する方法が一般的である。
ホットメルトには種々のものが使われているが、一例を
あげれば酢酸ビニル含有率１０〜４０％のエチレン・酢
酸ビニル共重合体を２０〜４０％，粘着付与剤２０〜４
０％，ワックス剤を２０〜４０％の範囲で混合したもの
がある。また、両面にポリオレフィン系樹脂層を有する
牛乳、果汁等用の液体紙容器ブランクの熱封緘された開
口部における剥離を容易にするための方法としては、レ
シチン等を含む抗ヒートシール剤を熱封緘部のポリオレ
フィン系樹脂層の表面にコートする方法が知られてい
る。この方法は対向するポリオレフィン系樹脂層間の剥
離を容易にするものである。一方で、対向するポリオレ
フィン系樹脂層のどちらか一方の層の内面に剥離層を設
ける方法が知られている。実公昭６０−２８５９２号公
報では熱封緘部の対向するポリオレフィン系樹脂層のど
ちらかの内面にメチルメタアクリレート１０〜５０重量
部、塩化ビニル−酢酸ビニル共重合体０〜２０重量部か
ら成る剥離層を設けることが提案されている。これは対
向するポリオレフィン系樹脂層は溶着され一体化されて
いるが、そのいずれか一方側にある剥離層と一体化した
ポリオレフィン系樹脂層との界面で剥離させることを狙
ったものである。従って剥離層のある方のポリオレフィ
ン系樹脂層が剥離時に容易に切断されるよう、２本の破
線状切込が粘着部に設けられている。さらにまた、実公
昭６２−３８９５４号公報でも、ブランク側辺に設けら
れた帯状の剥離層内に２本の破線状切込を設けている。2. Description of the Related Art Conventionally, in order to obtain the peelability of a heat-sealed portion of a paper container having a paperboard as a base material, a method of heat-sealing via a hot melt layer which is prone to cohesive failure has been generally used.
Various types of hot melts are used. As an example, 20-40% of an ethylene / vinyl acetate copolymer having a vinyl acetate content of 10-40% and a tackifier of 20-4 are given.
There is a mixture of 0% and a wax agent in the range of 20 to 40%. Further, as a method for facilitating peeling at the heat-sealed opening of a liquid paper container blank for milk, fruit juice, etc. having a polyolefin resin layer on both sides, an anti-heat-sealing agent containing lecithin or the like is heat-sealed. There is known a method of coating the surface of the polyolefin-based resin layer in some parts. This method facilitates peeling between the opposing polyolefin resin layers. On the other hand, a method is known in which a release layer is provided on the inner surface of either one of the opposing polyolefin resin layers. According to Japanese Utility Model Publication No. 60-28592, a release layer composed of 10 to 50 parts by weight of methyl methacrylate and 0 to 20 parts by weight of vinyl chloride-vinyl acetate copolymer on the inner surface of either of the opposing polyolefin resin layers in the heat sealing part. Is proposed. This is aimed at peeling at the interface with the polyolefin resin layer integrated with the peeling layer on either side, although the opposing polyolefin resin layers are welded and integrated. Therefore, two broken line notches are provided in the adhesive portion so that the polyolefin resin layer having the release layer can be easily cut at the time of peeling. Further, also in Japanese Utility Model Publication No. 62-38954, two broken line notches are provided in a strip-shaped peeling layer provided on the side of the blank.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら熱封緘部
にホットメルト層を部分的に設ける方法は、封緘時にホ
ットメルトアプリケーターによる部分的な塗布作業が必
要となり煩わしく、剥離された跡が汚らしいという問題
がある。またアイスクリームや冷凍食品のように低温で
扱われる商品の場合に、接着力が落ち僅かな力で剥離し
てしまうという問題が起きることがある。また抗ヒート
シール剤による方法は、ポリオレフィン系樹脂コート済
の積層材へのカラー印刷と同時に抗ヒートシール剤を所
定の熱封緘部に部分コートする手法が採られるが、ポリ
オレフィン系樹脂の積層の後からポリオレフィン系樹脂
層の上に印刷する牛乳カートン等には適用できるが、印
刷加工が先行し、最後にポリオレフィン系樹脂コートを
行う紙容器の場合には、最後にまた剥離層だけ部分コー
トしなければならず、手間が掛かりすぎるので適用しに
くい。また、インキ層、剥離層を積層ブランクの最上層
に設けたくない場合は当然適用できない。さらに、実公
昭６０−２８５９２号公報による提案では、剥離に若干
力がかかりすぎ、剥離面が綺麗でないという問題があ
り、また低温での剥離の安定性に欠けるという問題があ
る。一般に、開封すべき熱封緘部の剥離強度が強すぎる
と、消費者が開封するのに大きな力を要し、さらに強く
なると、ブランク熱封緘部で紙間剥離等の破壊が起こ
り、開封孔が現れずに開封不能となったり、あるいは逆
に内容物が飛び出す等の不測の事態が伴い、消費者クレ
ームとなる。逆に、剥離強度が弱すぎると、紙容器の後
加工時あるいは物流時に外からかかる力で簡単に剥離し
てしまい、包装容器としての機能を果たさなくなるとい
う問題がある。本発明は、前述の問題点に鑑みてなされ
たもので、常温、低温を問わず、熱封緘部を適度な力
で、綺麗に剥離することができる剥離安定性のある易剥
離性紙容器ブランクを提供することを目的とする。However, the method of partially providing the hot-melt layer on the heat-sealing portion requires a partial coating operation by the hot-melt applicator at the time of sealing, which is troublesome, and there is a problem that the peeled marks are messy. is there. In addition, in the case of products such as ice cream and frozen foods that are handled at low temperatures, there is a problem that the adhesive strength is reduced and peeling occurs with a slight force. In addition, the method using an anti-heat sealing agent is a method in which the anti-heat sealing agent is partially coated on a predetermined heat-sealing portion at the same time as color printing on a laminated material coated with a polyolefin-based resin. Although it can be applied to milk cartons, etc. that are printed on the polyolefin resin layer from the above, in the case of a paper container where the printing process precedes and the polyolefin resin coating is the last, only the release layer must be partially coated at the end. It is difficult to apply because it takes too much time and effort. In addition, if the ink layer and the peeling layer are not desired to be provided on the uppermost layer of the laminated blank, it cannot be applied. Further, in the proposal of Japanese Utility Model Publication No. 60-28592, there is a problem that the peeling surface is not clean because the peeling force is excessively applied, and the peeling stability at low temperature is insufficient. Generally, if the peel strength of the heat-sealing part to be opened is too strong, the consumer needs a large force to open the opening, and if it becomes stronger, the blank heat-sealing part is broken such as peeling between papers, and the opening hole is opened. It becomes a consumer complaint because of an unforeseen situation such as unopening without opening or conversely the contents pop out. On the other hand, if the peel strength is too weak, there is a problem that the paper container is easily peeled off by an external force during post-processing or distribution, and the function as a packaging container cannot be achieved. The present invention has been made in view of the above-mentioned problems, and at room temperature and low temperature, the heat-sealed portion can be peeled off neatly with an appropriate force, and is easily peelable. The purpose is to provide.
【０００４】[0004]
【課題を解決するための手段】上記目的を達成するた
め、本発明による易剥離性紙容器ブランクの第１の解決
手段は、基材の両面にポリオレフィン系樹脂層が積層さ
れ、両側辺同士が重ね合わされて帯状に熱封緘される紙
容器胴部ブランクにおいて、熱封緘部で対向するポリオ
レフィン系樹脂層のどちらか一方の基材面上に接して、
アクリル系樹脂１００重量部に対して炭素数８〜３０個
のアルキル基またはアルキルフェニール基を有するポリ
オキシエチレンアルキル（またはアルキルアリル）エー
テルのりん酸エステル０．１〜５．０重量部からなる剥
離性樹脂層が、該熱封緘部より広い範囲に帯状に設けら
れていることを特徴とする。易剥離性紙容器ブランクの
第２の解決手段は、前記剥離性樹脂層が帯状に設けられ
ている剥離領域に、２本の半切れ２重線と１本の半切れ
線が前記熱封緘部を挟んで長手方向に設けられているこ
とを特徴とする。易剥離性紙容器ブランクの第３の解決
手段は、前記熱封緘部の両端部に前記剥離性樹脂層のな
い部分があることを特徴とする。易剥離性紙容器ブラン
クの第４の解決手段は、前記両側辺上部に段差の異なる
切欠が設けられていることを特徴とする。In order to achieve the above object, the first means for solving an easily peelable paper container blank according to the present invention is to laminate a polyolefin resin layer on both sides of a base material so that both sides are In a paper container body blank that is heat-sealed in a band-like manner by being superposed, in contact with either one of the base material surfaces of the polyolefin-based resin layers facing each other in the heat-sealing portion,
Peeling consisting of 0.1 to 5.0 parts by weight of phosphoric acid ester of polyoxyethylene alkyl (or alkylallyl) ether having an alkyl group or an alkylphenyl group having 8 to 30 carbon atoms with respect to 100 parts by weight of acrylic resin The characteristic resin layer is provided in a band shape in a range wider than the heat-sealing portion. A second solving means of the easily peelable paper container blank is that the heat-sealing portion has two half-cut double lines and one half-cut line in a peeling region where the peelable resin layer is provided in a strip shape. It is characterized in that it is provided in the longitudinal direction with the pinch in between. A third means for solving the easily peelable paper container blank is characterized in that there are portions without the peelable resin layer at both ends of the heat-sealed portion. A fourth solution means of the easily peelable paper container blank is characterized in that notches having different steps are provided at the upper portions of both side edges.
【０００５】[0005]
【作用】上記のように構成された易剥離性紙容器ブラン
クによれば、剥離性樹脂層のりん酸エステルの含有量を
適宜調整することにより、適宜な力で熱封緘部の開封が
可能となるよう剥離性をコントロールし易くなり、開封
面が綺麗になり、さらに広い温度範囲、とくに低温にお
いても安定した剥離性を示すようになった。According to the easily peelable paper container blank configured as described above, the heat sealing portion can be opened with an appropriate force by appropriately adjusting the content of the phosphate ester in the peelable resin layer. As a result, it becomes easier to control the peelability, the unsealed surface becomes clean, and stable peelability is exhibited even in a wider temperature range, especially at low temperatures.
【０００６】[0006]
【構成】本発明について、図面等を用いて更に詳しく説
明する。図１は本発明による易剥離性紙容器ブランクか
ら成形されたバー付きアイスクリーム紙容器の斜視図で
ある。図２は、本発明による易剥離性紙容器ブランクの
平面図であり、ブランクの一側辺寄りの基材面上には剥
離性樹脂層が形成されているとともに、ブランクの両面
にはポリオレフィン系樹脂層が積層されている。そし
て、略扇状ブランク１の両側辺は重ね合わされ、対向す
るポリオレフィン系樹脂層が斜線で示す熱封緘部６で熱
融着され、図１に示すように円錐状となり、トップ部は
外方向にカールされてトップカール２を形成し、下部は
内側に折り返されて凸溝５でバー４付き底板が係止され
る。本容器は、中身を包んで保護するのに十分な封緘強
度を具備し、アイスクリーム充填後フィルムでトップシ
ールされて冷凍され、低温流通される。内容物を取り出
す時には、突起部３から引き剥がすことにより胴部を熱
封緘部６において、適度な力で容易に綺麗に剥離あるい
は解体することができる。[Structure] The present invention will be described in more detail with reference to the drawings. FIG. 1 is a perspective view of an ice cream paper container with a bar formed from an easily peelable paper container blank according to the present invention. FIG. 2 is a plan view of an easily peelable paper container blank according to the present invention, in which a peelable resin layer is formed on a base material surface near one side of the blank, and a polyolefin-based material is formed on both surfaces of the blank. A resin layer is laminated. Then, both sides of the substantially fan-shaped blank 1 are overlapped with each other, and the opposing polyolefin-based resin layers are heat-sealed at the heat-sealing portion 6 shown by diagonal lines to form a conical shape as shown in FIG. 1, and the top portion curls outward. Thus, the top curl 2 is formed, the lower part is folded back inward, and the bottom plate with the bar 4 is locked by the convex groove 5. This container has sufficient sealing strength to wrap and protect the contents, and after being filled with ice cream, it is top-sealed with a film, frozen, and circulated at a low temperature. When the contents are taken out, the body portion can be easily and neatly peeled off or disassembled in the heat-sealing portion 6 by peeling it off from the protruding portion 3 with an appropriate force.
【０００７】図２に示すように、ブランク１の一端は開
封時の引張りが容易なように突起部３が、他側辺には剥
離部７がそれぞれ設けられている。剥離部７には、斜線
で示す熱封緘部６とその左側には２本の半切れ線８、
８’が熱封緘部６に接近して、また右側には一本の切り
込み線８”が熱封緘部６より若干離れて設けられてい
る。最側辺は剥離層のない部分９がある。これは、若し
側辺のエッジまで剥離層があると、僅かの衝撃で側辺の
エッジから剥離が起きる可能性が大きいためである。As shown in FIG. 2, one end of the blank 1 is provided with a protrusion 3 for easy pulling at the time of opening, and a peeling portion 7 is provided on the other side. The peeling portion 7 includes a heat-sealing portion 6 indicated by diagonal lines and two half-break lines 8 on the left side thereof.
8'is close to the heat-sealing portion 6 and a cut line 8 '' is provided on the right side, slightly apart from the heat-sealing portion 6. The outermost side has a portion 9 without a peeling layer. This is because if there is a peeling layer up to the side edge, peeling from the side edge is likely to occur with a slight impact.
【０００８】図３は、図２における一側辺Ａ−Ａ’の断
面を模式的に表現したものである。板紙を基材１１とし
て、その両面にポリオレフィン系樹脂層１２を有し、剥
離層１０が、ブランク表面のポリオレフィン系樹脂層の
内面に接して設けられている。基材１１は必ずしも板紙
単体である必要は無くアルミ箔をラミネートしてあって
もよい。通常アルミ箔の表面には酢酸ビニル系のプライ
マー層が設けられる。従って、アルミ箔を用いる場合
は、外層から、剥離層／プライマー層／アルミ層／接着
層／板紙の層構成となる。半切れ線８、８’、８”はポ
リオレフィン系樹脂層１２を切断していて、熱封緘部１
４の剥離性を一層高めるためのものである。半切れ線は
半切れミシン目であっても良い。ここで重要なのは８、
８’と熱封緘部６との相互位置関係である。図４
（ａ）、（ｂ）はこの両者が一つの正常な関係に有る状
態例を示している。すなわち熱封緘部６の剥離の始まる
左端の直前に半切れ線８’があり、８’と８”間のポリ
オレフィン系樹脂層は対向するポリオレフィン系樹脂層
側に綺麗に移行している。ここで半切れ線８”は、剥離
を綺麗に終わらせるためのものであり、若し８”がない
と側辺末端のポリオレフィン系樹脂層を無理に切断する
こととなり汚い剥離状態を呈する。前記熱封緘部の左端
は、図４のような位置にあれば理想的であるが、８−
８’の間に入れば適度な力での剥離が可能である。熱封
緘部６の位置の胴部円周方向のバラツキは避けられない
ので、８、８’の２本の半切れ線が熱封緘部６の位置精
度に許容範囲を与え、剥離性の安定化を図っている。図
５（ａ）、（ｂ）は、従来行われていた２本だけの半切
れ線の場合の剥離不良の１例を示す模式図である。剥離
が始まる側の左の半切れ線と熱封緘部６の左端が開き過
ぎた場合であり、この場合の半切れ線は役に立たず、突
起部３側のポリオレフィン系樹脂層が熱封緘部で一体化
したポリオレフィン系樹脂層の直前部から図５（ｂ）の
ように破壊され、さらに紙層にも及び、結果として開封
不能であることを示している。図６は切れ目線８、８’
と熱封緘部との相対位置関係の優劣を示したもので、下
段の○×は剥離性の良否を示している。図７（ａ）は、
剥離部７のあるブランク側辺のトップカールの巻き込み
代２３に相当する部分に剥離層が設けられていないこと
を示している。それは、次に述べるように、２重巻き込
みでブランクエッジを綺麗に揃えても、剥離層があると
外からの力で剥離することが起きるからであり、剥離層
のない方がカールは安定する。図７（ａ）は、また両側
辺のトップ部に段差の異なる切欠２１、２２を設けれい
ることを示している。ここで突起部３のある側辺の方の
切欠２２が内側にくる側辺の切欠２１よりやや深い段差
を有している。これは、図７（ｂ）２４で示すように、
カール部の曲率が内外ブランクによって異なるので、段
差があった方が成形後にエッジが揃うからである。若し
同一段差では、図７（ｃ）２４に示すように、成形後エ
ッジが揃わず、見た目が悪いし、充填機のカップ供給部
で引っ掛かる可能性がある。FIG. 3 is a schematic representation of a cross section of one side AA 'in FIG. A board 11 is made of paperboard, and a polyolefin-based resin layer 12 is provided on both sides thereof, and a release layer 10 is provided in contact with the inner surface of the polyolefin-based resin layer on the blank surface. The base material 11 does not necessarily have to be a single paperboard, and may be laminated with aluminum foil. Usually, a vinyl acetate-based primer layer is provided on the surface of the aluminum foil. Therefore, when the aluminum foil is used, the outer layer has a layer structure of peeling layer / primer layer / aluminum layer / adhesive layer / paperboard. Half cut lines 8, 8 ′, 8 ″ cut the polyolefin resin layer 12, and the heat sealing part 1
It is for further enhancing the peelability of No. 4. The half-cut line may be a half-cut perforation. The important thing here is 8,
It is a mutual positional relationship between 8'and the heat sealing part 6. Figure 4
(A), (b) has shown the example of the state where these both have one normal relationship. That is, there is a half-break line 8'immediately before the left end where the heat-sealing portion 6 begins to peel, and the polyolefin-based resin layer between 8'and 8 "moves cleanly to the opposing polyolefin-based resin layer side. The half-break line 8 "is to end the peeling neatly, and if there is no 8", the polyolefin resin layer at the end of the side edge is forcibly cut and a dirty peeled state is exhibited. The left end of the section is ideal if it is in the position as shown in FIG.
If it enters between 8 ', it can be peeled off with an appropriate force. Since the position of the heat-sealing part 6 is inevitable in the circumferential direction of the body, the two half-cut lines 8 and 8'provide an allowable range for the position accuracy of the heat-sealing part 6 and stabilize the peelability. I am trying to FIG. 5A and FIG. 5B are schematic diagrams showing an example of peeling failure in the case of only two half-cut lines, which has been conventionally performed. This is the case where the left half-cut line on the side where peeling begins and the left end of the heat-sealing part 6 are too open. In this case, the half-cut line is not useful and the polyolefin resin layer on the protrusion 3 side is integrated in the heat-sealing part. As shown in FIG. 5 (b), the portion immediately before the liquefied polyolefin-based resin layer was destroyed, and the paper layer was also destroyed. As a result, it is impossible to open. Figure 6 shows the break lines 8 and 8 '
The relative positional relationship between the heat-sealed part and the heat-sealed part is superior or inferior. FIG. 7A shows
It shows that the peeling layer is not provided in the portion corresponding to the winding margin 23 of the top curl on the side of the blank where the peeling portion 7 is present. This is because, as will be described next, even if the blank edges are neatly aligned by double wrapping, the peeling layer causes peeling due to the force from the outside, and the curl is more stable without the peeling layer. . FIG. 7A also shows that notches 21 and 22 having different steps are provided in the top portions on both sides. Here, the notch 22 on the side with the protrusion 3 has a slightly deeper step than the notch 21 on the side that comes inside. This is as shown in FIG.
This is because the curl portion has different curvatures depending on the inner and outer blanks, and thus the edge having a step is aligned after molding. At the same step, as shown in FIG. 7 (c) 24, the edges after molding are not aligned, resulting in unsightly appearance, and there is a possibility of being caught by the cup supply part of the filling machine.
【０００９】本発明による易剥離性紙容器ブランクに使
用する剥離剤はアクリル性樹脂１００重量部に対して炭
素数８〜３０個のアルキル基またはアルキルフェニール
基を有するポリオキシエチレンアルキル（またはアルキ
ルアリル）エーテルのりん酸エステル０．１〜５．０重
量部からなる固形分４０％とトルエン６０％からなるも
ので、グラビアインキのワニス状に仕立てている。溶剤
は、りん酸エステルの溶解性のよい酢酸エチルを混ぜて
使用してもよい。上記の範囲で、りん酸エステル量を適
宜変更して剥離強度の最適条件を見つけ使用することが
できる。本発明の要旨の一つはりん酸エステルを剥離剤
として使用していることである。剥離剤はシリコーン樹
脂を使用する方が一般的であるが、シリコーン樹脂は剥
離性がありすぎ、剥離力のコントロールがやりにくいこ
とが、本発明に至った一つの理由である。The release agent used in the easily peelable paper container blank according to the present invention is a polyoxyethylene alkyl (or alkylallyl) having an alkyl group or an alkylphenyl group having 8 to 30 carbon atoms per 100 parts by weight of an acrylic resin. ) A varnish of gravure ink, which is composed of 40% solids consisting of 0.1 to 5.0 parts by weight of phosphoric ester of ether and 60% toluene. The solvent may be a mixture of ethyl acetate, which has a high solubility of phosphoric acid ester. Within the above range, the amount of phosphate ester can be appropriately changed to find and use the optimum condition of the peel strength. One of the gist of the present invention is to use a phosphate ester as a stripping agent. Silicone resin is generally used as a release agent, but one reason for the present invention is that the silicone resin has too much releasability and it is difficult to control the release force.
【００１０】[0010]
【実施例】以下、本発明の易剥離性紙容器ブランクの実
施例について説明する。基材として１６０ｇ／ｍ2 のカ
ップ原紙と、カップ原紙１６０ｇ／ｍ2 ／接着層／アル
ミ箔７μｍ／プライマー層の積層体の巻き取り紙を準備
した。先ず、グラビア多色印刷機を用いて図柄の印刷と
図２で示す剥離層コート部の部分コートをインラインで
行った。つぎに、ポリオレフィン系樹脂（低密度ポリエ
チレン）をエクストルジョンコーティングにより表裏と
も２０μｍの厚みでコートした。最後に高さ１００ｍ
ｍ，トップ外径５５ｍｍ，底部外径３４ｍｍの円錐状の
紙容器胴部を形成する図２で示すような扇形ブランクに
打ち抜いた。この場合、半切れ線８、８’、８”を同時
に加工した。８−８’間は２ｍｍ，８’−８”間は３ｍ
ｍとした。また、打ち抜き時の両側辺上部の図７で示す
切欠の段差ａ，ｂをそれぞれ４ｍｍ，３ｍｍとした。で
きあがったブランクをカップ成形機によって図１のよう
に熱封緘により円錐状に胴貼りした。熱封緘用にもちい
たヒートバー（シールヘッド）の厚みは１〜２ｍｍのも
のを使用した。これをユーザーへ送付し、底部にバー４
を嵌合させ、アイスクリーム充填後、蓋材フィルムをト
ップカール部２に封止し、マイナス４０℃に保冷した。
保冷したサンプルを取り出し、取り出した直後と、室温
で１分、５分放置した場合で剥離官能テストを行い、い
づれの場合も安定した、優れた剥離効果を示した。以上
により、本発明の有効性が確認された。本発明の実施例
はバー付きアイスクリーム用ブランクについて説明した
が、他のカートンブランクにおいても、本発明の利用は
可能でありる。EXAMPLES Examples of the easily peelable paper container blank of the present invention will be described below. And cup base paper 160 g / m 2 as a substrate was prepared paper web of the laminate of the cup base paper 160 g / m 2 / adhesive layer / aluminum foil 7 [mu] m / primer layer. First, a gravure multicolor printer was used to print a design and partially coat the release layer coating portion shown in FIG. 2 in-line. Next, a polyolefin resin (low density polyethylene) was coated by extrusion coating to a thickness of 20 μm on both front and back sides. Finally height 100m
m, a top outer diameter 55 mm, and a bottom outer diameter 34 mm to form a conical paper container body, which was punched into a fan-shaped blank as shown in FIG. In this case, the half cut lines 8, 8 ', 8 "were processed simultaneously. 2 mm between 8-8' and 3 m between 8'-8".
m. Further, the steps a and b of the notches shown in FIG. 7 at the upper sides of both sides at the time of punching were 4 mm and 3 mm, respectively. The resulting blank was conically bonded by heat sealing as shown in FIG. 1 using a cup molding machine. The heat bar (seal head) used for heat sealing had a thickness of 1 to 2 mm. Send this to the user and have a bar 4 on the bottom
After fitting, and filling with ice cream, the lid material film was sealed in the top curl portion 2 and kept cool to -40 ° C.
A sample which was kept cold was taken out, and a peeling sensory test was conducted immediately after taking it out and when it was left at room temperature for 1 minute and 5 minutes, and a stable and excellent peeling effect was shown in any case. From the above, the effectiveness of the present invention was confirmed. Although the embodiments of the present invention have been described with respect to the ice cream blank with a bar, the present invention can be applied to other carton blanks.
【００１１】[0011]
【発明の効果】本発明は、以上説明したような構成とな
っているので、紙容器の熱封緘部を適度な力で、容易
に、綺麗に、安定して剥離あるいは解体でき、内容物を
容易に取り出すことができる。一般に熱封緘による成形
容器は強固に成形されていて、使用後もその形態を保持
するものが多く、ゴミの容積を増大させる要因ともなっ
ているが、本発明の易剥離性、解体性はゴミの減容化に
も効果を発揮するものである。EFFECTS OF THE INVENTION Since the present invention has the constitution as described above, the heat-sealing portion of a paper container can be peeled or disassembled easily, neatly and stably with an appropriate force, and the contents can be removed. It can be taken out easily. In general, a heat-sealed molded container is strongly molded, and often retains its shape even after use, which is also a factor for increasing the volume of dust. It is also effective for volume reduction.
【図１】本発明の易剥離性紙容器ブランク成形品斜視図FIG. 1 is a perspective view of an easily peelable paper container blank molded product of the present invention.
【図２】本発明の易剥離性紙容器ブランク展開図FIG. 2 is a development view of an easily peelable paper container blank according to the present invention.
【図３】熱封緘部断面図FIG. 3 is a sectional view of the heat-sealing part
【図４】正常な剥離状態図[Figure 4] Normal peeling state diagram
【図５】異常な剥離状態図FIG. 5: Abnormal peeling state diagram
【図６】切れ目線と熱封緘部の位置関係図FIG. 6 is a positional relationship diagram between the cut line and the heat sealing part.
【図７】ブランク切欠部説明図FIG. 7 is an explanatory view of a blank cutout portion.
【００１２】[0012]
１ ブランク ２ トップカール部 ３ 突起部 ４ バー ５ 凸溝 ６ 熱封緘部 ７ 剥離部 ８ 半切れ線 ８’半切れ線 ８”半切れ線 ９ 剥離層のないブランク側辺 １０ 剥離層 １１ 紙層 １２ ポリオレフィン系樹脂層 ２１ 切欠 ２２ 切欠 ２３ 巻き込み代 ２４ 成形後の切欠部 1 blank 2 Top curl part 3 protrusions 4 bars 5 convex groove 6 heat seal part 7 Peeling part 8 half-break line 8'half line 8 "half line 9 Blank side without peeling layer 10 Release layer 11 paper layers 12 Polyolefin resin layer 21 notches 22 notches 23 Involvement fee 24 Notch after molding
フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ Ｂ６５Ｄ 5/56 Ｂ６５Ｄ 5/56 Ｚ 85/78 85/78 Ａ (58)調査した分野(Int.Cl.7，ＤＢ名) B65D 3/26 B65D 5/06 B65D 85/78 B65D 5/54 B65D 5/56 B32B 27/32 B32B 27/10 Continuation of front page (51) Int.Cl. 7 identification code FI B65D 5/56 B65D 5/56 Z 85/78 85/78 A (58) Fields investigated (Int.Cl. 7 , DB name) B65D 3 / 26 B65D 5/06 B65D 85/78 B65D 5/54 B65D 5/56 B32B 27/32 B32B 27/10
Claims (4)
積層され、両側辺同士が重ね合わされて帯状に熱封緘さ
れる紙容器胴部ブランクにおいて、熱封緘部で対向する
ポリオレフィン系樹脂層のどちらか一方の基材面上に、
アクリル系樹脂１００重量部に対して炭素数８〜３０個
のアルキル基またはアルキルフェニール基を有するポリ
オキシエチレンアルキル（またはアルキルアリル）エー
テルのりん酸エステル０．１〜５．０重量部からなる剥
離性樹脂層が、該熱封緘部より広い範囲に帯状に設けら
れていることを特徴とする易剥離性紙容器ブランク。1. In a paper container body blank in which a polyolefin resin layer is laminated on both sides of a substrate and both sides are superposed on each other and heat-sealed in a strip shape, which one of the polyolefin resin layers is opposed to each other at the heat-sealing portion. On one side of the substrate,
Peeling consisting of 0.1 to 5.0 parts by weight of phosphoric acid ester of polyoxyethylene alkyl (or alkylallyl) ether having an alkyl group or an alkylphenyl group having 8 to 30 carbon atoms with respect to 100 parts by weight of acrylic resin An easily peelable paper container blank, in which the flexible resin layer is provided in a band shape in a range wider than the heat-sealing portion.
る剥離領域に、２本の半切れ線と１本の半切れ線が前記
熱封緘部を挟んで長手方向に設けられていることを特徴
とする請求項１記載の易剥離性紙容器ブランク。2. In the peeling area where the peelable resin layer is provided in a strip shape, two half-cut lines and one half-cut line are provided in the longitudinal direction with the heat-sealing portion sandwiched therebetween. The easily peelable paper container blank according to claim 1.
層のない部分があることを特徴とする請求項１記載の易
剥離性紙容器ブランク。3. The easily peelable paper container blank according to claim 1, wherein both ends of the heat-sealed portion have portions without the peelable resin layer.
けられていることを特徴とする請求項１記載の易剥離性
紙容器ブランク。4. The easily peelable paper container blank according to claim 1, wherein notches having different steps are provided at upper portions of both side edges.