JP3417836B2 - Method of bonding non-slip made of silicone resin to piece and non-slip member manufactured by the method - Google Patents
Method of bonding non-slip made of silicone resin to piece and non-slip member manufactured by the methodInfo
- Publication number
- JP3417836B2 JP3417836B2 JP10557598A JP10557598A JP3417836B2 JP 3417836 B2 JP3417836 B2 JP 3417836B2 JP 10557598 A JP10557598 A JP 10557598A JP 10557598 A JP10557598 A JP 10557598A JP 3417836 B2 JP3417836 B2 JP 3417836B2
- Authority
- JP
- Japan
- Prior art keywords
- heat
- attachment piece
- resin layer
- slip
- piece
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、添片にシリコン樹
脂からなるすべり止め用の突起を接合させる方法及びそ
の方法により製造されたすべり止め部材の改良に関する
ものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of joining a non-slip projection made of a silicone resin to an attachment piece and an improvement of a non-slip member manufactured by the method.
【０００２】[0002]
【従来の技術】ズボン又はスカートの腰の裏側やこの部
分に装着する腰裏、あるいは、カバンの肩紐、ベルト、
玄関マット、座蒲団、コースター等各種物品の裏側に取
り付けることにより、すべり止め効果を発揮させるもの
としてすべり止め部材がある。このすべり止め部材は、
溶融状態のシリコン樹脂を型を用いて成型することによ
り、すべり止め用の複数個の突起４、４を添片１に形成
したものである。2. Description of the Related Art The back of the waist of trousers or skirts, the back of the waist worn on this part, or the shoulder straps and belts of bags.
There is a non-slip member that exerts a non-slip effect by being attached to the back side of various articles such as a doormat, a seating team, and a coaster. This non-slip member,
A plurality of protrusions 4 and 4 for slip prevention are formed on the attachment piece 1 by molding a molten silicon resin using a mold.
【０００３】[0003]
【発明が解決しようとする課題】ところで、溶融状態の
シリコン樹脂を型を用いて成型することによりすべり止
め用の複数個の突起４、４を添片１に形成する場合、溶
融状態のシリコン樹脂が添片１に含浸し、図５(a) にお
いて矢印で示すように反対側の面に達する。型を用いた
成型では添片１に圧力が掛かるから、添片１の材質にか
かわらずこの含浸は大なり小なり起こり得る。添片１が
織布からなる場合、溶融状態のシリコン樹脂が添片１に
特に含浸しやすい。When a plurality of anti-slip projections 4, 4 are formed on the attachment piece 1 by molding a molten silicon resin using a mold, the molten silicon resin is used. Impregnates the attachment piece 1 and reaches the opposite surface as shown by the arrow in FIG. In the case of molding using a mold, pressure is applied to the attachment piece 1, so this impregnation can occur to a greater or lesser extent regardless of the material of the attachment piece 1. When the piece 1 is made of a woven fabric, the silicon resin in a molten state is particularly likely to be impregnated into the piece 1.
【０００４】ところが、近年のすべり止め部材において
は、添片１の両面のうちすべり止め用の突起４、４が形
成される面と反対側の面（図５(a) における左側の面）
に、熱溶融性樹脂層1aが配置される場合が多い。この熱
溶融性樹脂層1aはアイロン、プレス機その他の器具です
べり止め部材を加熱することによりそれを溶融状態と
し、ズボン又はスカートの腰の裏側やこの部分に装着す
る腰裏、あるいは、カバンの肩紐等にすべり止め部材を
簡単に装着することができるようにするためのものであ
るが、上述したように溶融状態のシリコン樹脂が添片１
に含浸し、反対側の面にまで達していると、この熱溶融
性樹脂層1aを添片１に接合させることができないという
欠点がある。すなわち、溶融状態のシリコン樹脂が添片
１に含浸して反対側の面からにじみ出ていると、シリコ
ン樹脂と添片１に接合させるべき熱溶融性樹脂層1aとが
互いに反発し合って熱溶融性樹脂層1aが添片１にくっつ
かない。However, in the recent anti-slip member, the surface opposite to the surface on which the anti-slip projections 4 and 4 are formed on both surfaces of the attachment piece 1 (the surface on the left side in FIG. 5A).
In many cases, the heat-fusible resin layer 1a is arranged. This heat-fusible resin layer 1a is made into a molten state by heating an anti-slip member with an iron, a press machine or other equipment, and the back side of the waist of pants or skirt or the back of the waist worn on this part, or the bag The purpose of this is to make it possible to easily attach the anti-slip member to the shoulder strap or the like.
If the heat-fusible resin layer 1a is impregnated with the resin and reaches the opposite surface, the heat-meltable resin layer 1a cannot be bonded to the attachment piece 1. That is, when the silicon resin in a molten state is impregnated into the attachment piece 1 and oozes out from the opposite surface, the silicon resin and the heat-meltable resin layer 1a to be bonded to the attachment piece 1 repel each other and heat-melt. The resin layer 1a does not stick to the attachment piece 1.
【０００５】これを解決するために、本出願人は、図５
(b) に示すように、添片１の両面のうち、シリコン樹脂
からなるすべり止め用の突起４、４を接合すべき面と反
対側の面（図５(b) における左側の面）にプライマーを
塗布しておき、このプライマー層1b形成後プライマー層
1bが形成されていない面において、溶融状態のシリコン
樹脂を成型することによりすべり止め用の突起４、４を
添片１に形成することを提案した（特願平９−１３７５
５７号）。In order to solve this, the applicant of the present invention has shown in FIG.
As shown in (b), on both surfaces of the attachment piece 1 on the surface opposite to the surface to which the non-slip projections 4 and 4 made of silicon resin are to be joined (the surface on the left side in FIG. 5B). After applying the primer and forming this primer layer 1b, the primer layer
It was proposed that the anti-slip projections 4 and 4 be formed on the attachment piece 1 by molding a molten silicon resin on the surface where the 1b is not formed (Japanese Patent Application No. 9-1375).
57).
【０００６】このプライマー層1bはいわゆる目止め材と
しての機能を有し、熱溶融性樹脂層1aの添片１への接着
性を増大させるのみならず、熱溶融性樹脂層1aがこのプ
ライマー層1bに強固に接着して両者の接着性を増大さ
せ、熱溶融性樹脂層1aが添片１から剥離することを防止
するためのものである。このプライマー中には、シラン
カップリング剤とともに種々の樹脂オリゴマーや溶剤な
どが配合されており、プライマー自体相当高価なもので
ある。また、プライマーを塗布しなければならない分、
製造工程に手間が掛かるという欠点がある。そこで、本
発明者は、このプライマーを用いないで熱溶融性樹脂層
が添片から剥離することを防止することができないか、
鋭意研究した結果、本発明を完成させるに至った。The primer layer 1b has a function as a so-called sealing material, and not only increases the adhesiveness of the heat-meltable resin layer 1a to the attachment piece 1, but the heat-meltable resin layer 1a also serves as the primer layer. This is to firmly adhere to 1b to increase the adhesiveness between them and prevent the heat-meltable resin layer 1a from peeling off from the attachment piece 1. In this primer, various resin oligomers, solvents and the like are mixed together with the silane coupling agent, and the primer itself is considerably expensive. Also, because the primer must be applied,
There is a drawback that the manufacturing process is troublesome. Therefore, the present inventor can prevent the heat-meltable resin layer from peeling from the attachment without using this primer,
As a result of earnest research, the present invention has been completed.
【０００７】[0007]
【課題を解決するための手段】すなわち、本発明では、
添片１を織物もしくは編物からなるものとし、その片面
に、所定の加熱温度では溶融しないか、あるいは、溶融
しにくい熱溶融性樹脂層２を形成し、次に、それとは反
対側の面において、溶融状態のシリコン樹脂を成型する
ことにより添片１にすべり止め用の突起４、４を形成
し、しかる後、前記熱溶融性樹脂層２の外面に、所定の
加熱温度で溶融する熱溶融性樹脂層３を形成する。この
場合において、熱溶融性樹脂層２となる溶融状態の熱溶
融性樹脂を添片１に形成する際、溶融状態の熱溶融性樹
脂が添片１の生地目に浸透して熱溶融性樹脂層２の添片
１への付着性が増大する。また、この樹脂層２が存在す
るために、その外面に重ね合わせた熱溶融性樹脂層３の
添片１への接着性が増大するのみならず、熱溶融性樹脂
層３が熱溶融性樹脂層２に強固に接着して両者の接着性
が増大し、熱溶融性樹脂層３が添片１から剥離すること
がない。That is, according to the present invention,
The attachment piece 1 is made of a woven or knitted material, and a thermofusible resin layer 2 that does not melt or is difficult to melt at a predetermined heating temperature is formed on one surface thereof, and then on the surface opposite to that. , The anti-slip projections 4, 4 are formed on the attachment piece 1 by molding a molten silicon resin, and then the outer surface of the heat-fusible resin layer 2 is melted at a predetermined heating temperature. The resin layer 3 is formed. In this case, when the melted heat-meltable resin that becomes the heat-meltable resin layer 2 is formed on the attachment piece 1, the melted heat-meltable resin permeates into the texture of the attachment piece 1 to form the heat-meltable resin. The adhesion of the layer 2 to the attachment piece 1 is increased. Further, since the resin layer 2 is present, not only the adhesiveness of the heat-melting resin layer 3 superposed on the outer surface of the resin layer 2 to the attachment piece 1 is increased, but also the heat-melting resin layer 3 is formed by the heat-melting resin layer 3. It strongly adheres to the layer 2 to increase the adhesiveness between them, and the heat-fusible resin layer 3 does not separate from the attachment piece 1.
【０００８】一方、熱溶融性樹脂層２形成後、その層２
が形成されていない面において、溶融状態のシリコン樹
脂を成型することにより添片１にすべり止め用の突起
４、４が形成されるが、その際、織物もしくは編物から
なる添片１の生地目に溶融状態のシリコン樹脂が浸透す
るとともに、添片１の生地目に含浸せしめられた溶融状
態のシリコン樹脂が裏側の熱溶融性樹脂層２と協働して
シリコン樹脂からなるすべり止め用の突起４、４の添片
１への付着性も増大する。なお、添片１の片面には予め
熱溶融性樹脂層２が形成されているから、すべり止め用
の突起４、４を形成するべく溶融状態のシリコン樹脂を
添片１に成型する際、溶融状態のこの樹脂が添片１の生
地目に浸透しても裏側からはみ出ることがない。On the other hand, after forming the heat-meltable resin layer 2, the layer 2
The non-slip protrusions 4 and 4 are formed on the attachment piece 1 by molding a molten silicon resin on the surface where the ridges are not formed. While the molten silicon resin permeates the silicon, the molten silicon resin impregnated into the texture of the attachment piece 1 cooperates with the heat-meltable resin layer 2 on the back side to form a non-slip protrusion made of the silicone resin. The adhesion of Nos. 4 and 4 to the attachment piece 1 is also increased. In addition, since the heat-meltable resin layer 2 is formed on one surface of the attachment piece 1 in advance, when the molten silicon resin is molded into the attachment piece 1 so as to form the projections 4 and 4 for preventing slippage, it is melted. Even if this resin in the state of permeation penetrates into the texture of the attachment piece 1, it does not protrude from the back side.
【０００９】織物もしくは編物の少なくとも表面が起毛
せしめられているものを添片１として用いるのが好まし
い。このようなものを用いると、すべり止め用の突起４
となる溶融状態のシリコン樹脂が、織物もしくは編物か
らなる添片１の生地目に浸透するとともに添片１の起毛
部分を抱持することになるので、熱溶融性樹脂層２の添
片１への付着性ならびに突起４の添片１への付着性がさ
らに増大し、その結果、熱溶融性樹脂層３ならびに突起
４が添片１から剥離することが一層なくなる。It is preferable to use a woven or knitted fabric having at least the surface thereof raised as the attachment piece 1. When such a thing is used, the projection 4 for slip prevention
Since the molten silicone resin that will penetrate into the texture of the attachment piece 1 made of woven or knitted material will hold the raised portion of the attachment piece 1, the addition to the attachment piece 1 of the heat-meltable resin layer 2 And the adhesion of the protrusions 4 to the attachment piece 1 are further increased, and as a result, the heat-meltable resin layer 3 and the protrusions 4 are further prevented from peeling from the attachment piece 1.
【００１０】また、本発明におけるすべり止め部材は、
織物もしくは編物からなる添片１の片面に、所定の加熱
温度では溶融しないか、あるいは、溶融しにくい熱溶融
性樹脂層２と、所定の加熱温度で溶融する熱溶融性樹脂
層３とが順次形成されており、それと反対側の面には、
溶融状態のシリコン樹脂を成型することによりすべり止
め用の突起４、４が形成されたものである。このすべり
止め部材における突起４、４は、溶融状態のシリコン樹
脂が織物もしくは編物からなる添片１の生地目に含浸せ
しめられるとともに、裏側の熱溶融性樹脂層２と協働し
て添片１に対して強固に接合されているところから、こ
のすべり止め部材を例えば、ズボン又はスカートの腰の
裏側やこの部分に装着する腰裏、カバンの肩紐、ベル
ト、玄関マット、座蒲団、コースター等各種物品の裏側
に取り付けることにより、きわめて良好なすべり止め効
果を長く維持することができる。しかも、水洗いやドラ
イクリーニングしてもすべり止め部材が剥離しない。Further, the non-slip member according to the present invention is
A heat-meltable resin layer 2 that does not melt or is difficult to melt at a predetermined heating temperature and a heat-meltable resin layer 3 that melts at a predetermined heating temperature are sequentially formed on one surface of an attachment piece 1 made of a woven or knitted material. Is formed, and on the opposite side,
The projections 4 and 4 for slip prevention are formed by molding a molten silicon resin. The protrusions 4 and 4 of the non-slip member are impregnated with a melted silicone resin in the texture of the additive piece 1 made of woven or knitted material, and in cooperation with the heat-meltable resin layer 2 on the back side. Since it is firmly joined to, the anti-slip member can be attached to, for example, the back of the waist of trousers or skirts, or the back of the waist worn on this part, bag shoulder straps, belts, entrance mats, seats, coasters, etc. By attaching to the back side of the article, a very good anti-skid effect can be maintained for a long time. Moreover, the non-slip member does not peel off even after washing with water or dry cleaning.
【００１１】ところで、添片１の片面に形成されている
溶融温度の異なる２つの熱溶融性樹脂層２、３のうち、
添片１から遠い熱溶融性樹脂層３は所定の温度に加熱す
ることにより、すなわち、アイロン、プレス機その他の
器具ですべり止め部材を加熱することにより溶融状態と
なるものであって、アイロン、プレス機その他の器具で
この層３を溶融状態とすることにより、すべり止め部材
を例えば、ズボン又はスカートの腰の裏側やこの部分に
装着する腰裏、カバンの肩紐、ベルト、玄関マット、座
蒲団、コースター等各種物品の裏側に取り付けることが
できる。一方、添片１に近い熱溶融性樹脂層２は前記熱
溶融性樹脂層３より溶融温度が高く、所定の温度に加熱
した程度では、すなわち、アイロン、プレス機その他の
器具で加熱した程度では溶融状態にならないか、あるい
は、溶融状態にはなりにくいものである。従って、アイ
ロン、プレス機その他の器具ですべり止め部材を加熱し
たとき、添片１から遠い熱溶融性樹脂層３は溶融状態と
なっても、添片１に近い熱溶融性樹脂層２は溶融状態に
ならないか、あるいは、溶融状態にはなりにくい。By the way, of the two heat-meltable resin layers 2 and 3 formed on one surface of the attachment piece 1 and having different melting temperatures,
The heat-meltable resin layer 3 far from the attachment piece 1 is brought into a molten state by heating it to a predetermined temperature, that is, by heating an anti-slip member with an iron, a press machine or other equipment. By making this layer 3 in a molten state with a press machine or other device, a non-slip member is attached to, for example, the back side of the waist of pants or skirts or the back of the waist to be attached to this part, shoulder straps of bags, belts, entrance mats, seating groups. It can be attached to the back side of various articles such as coasters. On the other hand, the heat-meltable resin layer 2 near the attachment piece 1 has a higher melting temperature than the heat-meltable resin layer 3 and is heated to a predetermined temperature, that is, to the extent that it is heated by an iron, a press machine or other equipment. It does not go into a molten state, or it does not go into a molten state easily. Therefore, when the anti-slip member is heated with an iron, a press, or other equipment, even if the heat-meltable resin layer 3 far from the attachment piece 1 is in a molten state, the heat-meltable resin layer 2 close to the attachment piece 1 is melted. It does not go into a state, or it does not easily go into a molten state.
【００１２】このように、本発明においては、溶融温度
に差のある２つの熱溶融性樹脂層２と３とを用い、織物
もしくは編物からなる添片１の片面に、溶融温度の高い
熱溶融性樹脂層を形成し、次に、それとは反対側の面に
おいて、溶融状態のシリコン樹脂を成型することにより
添片１にすべり止め用の突起４、４を形成し、しかる
後、前記熱溶融性樹脂層２の外面に熱溶融性樹脂層３を
形成する工程を経ることにより、熱溶融性樹脂層２を添
片１に、また、すべり止め用の突起４、４を添片１に、
さらに、熱溶融性樹脂層３を熱溶融性樹脂層２にいずれ
も強固に接合させることができる。従って、このすべり
止め部材を例えば、ズボン又はスカートの腰の裏側やこ
の部分に装着する腰裏、カバンの肩紐、ベルト、玄関マ
ット、座蒲団、コースター等各種物品の裏側に取り付け
ることにより、きわめて良好なすべり止め効果を長く維
持することができる。しかも、水洗いやドライクリーニ
ングしてもすべり止め部材が剥離しない。As described above, in the present invention, the two heat-meltable resin layers 2 and 3 having different melting temperatures are used, and one side of the additive 1 made of a woven or knitted fabric is melted at a high melting temperature. Of the conductive resin layer, and then, on the surface opposite to the resin layer, a silicon resin in a molten state is molded to form the projections 4 and 4 for preventing slippage on the attachment piece 1. By performing the step of forming the heat-meltable resin layer 3 on the outer surface of the heat-resistant resin layer 2, the heat-meltable resin layer 2 is attached to the attachment piece 1, and the non-slip projections 4 and 4 are attached to the attachment piece 1.
Further, any of the heat-melting resin layer 3 can be firmly bonded to the heat-melting resin layer 2. Therefore, by attaching this non-slip member to the back of the waist of trousers or skirts, the back of the waist worn on this part, the shoulder straps of bags, belts, entrance mats, seats, coasters, etc. The anti-slip effect can be maintained for a long time. Moreover, the non-slip member does not peel off even after washing with water or dry cleaning.
【００１３】この場合においても、織物もしくは編物の
少なくとも表面が起毛せしめられているものを用いるの
が好ましい。このようなものを用いると、すべり止め用
の突起４となる溶融状態のシリコン樹脂が、織物もしく
は編物からなる添片１の生地目に浸透するとともに添片
１の起毛部分を抱持することになるので、熱溶融性樹脂
層２の添片１への付着性ならびに突起４の添片１への付
着性がさらに増大し、その結果、熱溶融性樹脂層３なら
びに突起４が添片１から剥離することが一層なくなる。Also in this case, it is preferable to use a woven or knitted fabric having at least the surface raised. When such a material is used, the molten silicon resin which becomes the anti-slip projections 4 penetrates into the material of the piece 1 made of a woven or knitted fabric and holds the raised portion of the piece 1. Therefore, the adhesion of the heat-meltable resin layer 2 to the attachment piece 1 and the adhesion of the protrusions 4 to the attachment piece 1 are further increased, and as a result, the heat-meltable resin layer 3 and the protrusions 4 are removed from the attachment piece 1. It is even less likely to peel off.
【００１４】なお、すべり止め用の突起４、４は溶融さ
せたシリコン樹脂を加熱しながら、すなわち、溶融状態
のシリコン樹脂を型を用いて添片１に接合させ、しかる
後、それを硬化させることにより突起状にするものであ
る。The anti-slip projections 4 and 4 are heated while the molten silicon resin is being heated, that is, the molten silicon resin is bonded to the attachment piece 1 by using a mold, and thereafter, it is cured. By doing so, the projection is formed.
【００１５】[0015]
【発明の実施の形態】本発明の好ましい実施の形態を、
添付の図１〜図３に基いて詳細に説明する。図１(a) 、
図１(b) に、添片１の片面に、熱溶融性樹脂層２を形成
した状態を示す。添片１は織物もしくは編物からなるも
のである。従来はこれを人工皮革としたものもあるが、
人工皮革は織物もしくは編物に比べて高価であるから、
本発明では、添片１を織物もしくは編物からなるものと
する。そして、この添片１の片面（図１(a) の左側の
面、図１(b) の下側の面）には、所定の温度に加熱、す
なわち、アイロン、プレス機その他の器具ですべり止め
部材を加熱した程度の熱では溶融しないか、あるいは、
溶融しにくい熱溶融性樹脂層２が形成されている。BEST MODE FOR CARRYING OUT THE INVENTION
A detailed description will be given with reference to the attached FIGS. Figure 1 (a),
FIG. 1B shows a state in which the heat-meltable resin layer 2 is formed on one surface of the attachment piece 1. The attachment piece 1 is made of a woven or knitted fabric. Conventionally, there are some made of artificial leather,
Artificial leather is more expensive than woven or knitted fabrics,
In the present invention, the attachment piece 1 is made of a woven or knitted fabric. Then, on one surface of the attachment piece 1 (the surface on the left side of FIG. 1 (a), the surface on the lower side of FIG. 1 (b)), it is heated to a predetermined temperature, that is, it is slipped with an iron, a press machine or other equipment. Doesn't melt with the heat of heating the stopper, or
A heat-fusible resin layer 2 that is difficult to melt is formed.
【００１６】この熱溶融性樹脂層２が形成されている面
と反対側の面において、溶融状態のシリコン樹脂を成型
することにより添片１にすべり止め用の突起４、４を形
成する。図１(c) 図１(d) に、添片１にすべり止め用の
突起４、４を形成した状態を示す。すべり止め用の突起
４、４は溶融させたシリコン樹脂を加熱しながら、すな
わち、溶融状態のシリコン樹脂を型を用いて添片１に接
合させ、しかる後、それを硬化させることにより突起状
となる。なお、添片１の片面には予め熱溶融性樹脂層２
が形成されているから、すべり止め用の突起４、４を形
成するべく溶融状態のシリコン樹脂を添片１に成型する
際、溶融状態のこの樹脂が添片１の生地目に浸透しても
裏側からはみ出ることがない。すべり止め用の突起４、
４の形状は、図１(c) に示すように截頭円錐形とした
り、図１(d) に示すように略半円径とすることができ
る。その形状は何ら特定されるものではない。On the surface opposite to the surface on which the heat-meltable resin layer 2 is formed, a non-slip projection 4 or 4 is formed on the attachment piece 1 by molding a molten silicon resin. FIG. 1 (c) FIG. 1 (d) shows a state in which the non-slip projections 4 and 4 are formed on the attachment piece 1. The anti-slip protrusions 4 and 4 are formed into protrusions by heating the molten silicon resin, that is, by bonding the molten silicon resin to the attachment piece 1 using a mold, and then curing it. Become. In addition, the heat-meltable resin layer 2 is previously formed on one surface of the attachment piece 1.
Therefore, when the molten silicon resin is molded into the additive 1 to form the anti-slip projections 4 and 4, even if the molten resin penetrates into the texture of the additive 1. It does not stick out from the back side. Anti-slip protrusion 4,
The shape of 4 can be a frusto-conical shape as shown in FIG. 1 (c) or a substantially semi-circular diameter as shown in FIG. 1 (d). The shape is not specified at all.
【００１７】すべり止め用のこの突起４、４を形成した
後、図１(e) に示すように、前記熱溶融性樹脂層２の外
面に、所定の温度に加熱、すなわち、アイロン、プレス
機その他の器具ですべり止め部材を加熱したときの熱で
溶融する熱溶融性樹脂層３を形成する。熱溶融性樹脂か
らなる２つの層形態をさらに詳しく述べると、添片１の
片面において、添片１に近い方に、所定の温度に加熱、
すなわち、アイロン、プレス機その他の器具ですべり止
め部材を加熱した程度の熱では溶融しないか、あるい
は、溶融しにくい熱溶融性樹脂層２が、この熱溶融性樹
脂層２の外面であって添片１から遠い方に、所定の温度
に加熱、すなわち、アイロンなどですべり止め部材を加
熱したときの熱で溶融する熱溶融性樹脂層３が形成され
ている。なお、熱溶融性樹脂層２は織物もしくは編物か
らなる添片１の片面に熱溶融性樹脂フィルムをラミネー
トするだけで、その層２をきわめて簡単に形成すること
ができる。また、熱溶融性樹脂層３も熱溶融性樹脂層２
に熱溶融性樹脂フィルムをラミネートするだけで、その
層３をきわめて簡単に形成することができる。After forming the projections 4 and 4 for slip prevention, as shown in FIG. 1 (e), the outer surface of the heat-meltable resin layer 2 is heated to a predetermined temperature, that is, an iron, a press machine. The heat-fusible resin layer 3 that is melted by the heat when the anti-slip member is heated is formed by another device. To describe the two-layer form of the heat-fusible resin in more detail, one side of the attachment piece 1 is heated to a predetermined temperature closer to the attachment piece 1,
That is, the heat-meltable resin layer 2 which is not melted or is hardly melted by the heat of the anti-slip member with an iron, a press machine or other equipment is the outer surface of the heat-meltable resin layer 2 and is added thereto. A heat-fusible resin layer 3 that is heated to a predetermined temperature, that is, melted by heat when the anti-slip member is heated with an iron or the like, is formed on the side remote from the piece 1. The heat-meltable resin layer 2 can be formed very simply by laminating the heat-meltable resin film on one surface of the attachment piece 1 made of a woven or knitted material. Further, the heat-meltable resin layer 3 is also the heat-meltable resin layer 2
The layer 3 can be formed extremely simply by laminating a heat-meltable resin film on.
【００１８】アイロンやプレス機その他の器具ですべり
止め部材を加熱したとき溶融する温度、すなわち、熱溶
融性樹脂層３の溶融温度を、９０〜１００℃程度の範囲
に設定することができる。一方、この程度の温度ですべ
り止め部材を加熱しても溶融しないか、あるいは、溶融
しにくい温度、すなわち、熱溶融性樹脂層２の溶融温度
を、１２０〜１５０℃程度の範囲に設定することができ
る。なお、溶融温度に応じた熱溶融性樹脂を二種類適宜
選択することによって、上記設定温度をそれぞれ適宜変
更することが可能である。The temperature at which the non-slip member is melted with an iron, a press machine or other equipment, that is, the melting temperature of the heat-meltable resin layer 3 can be set in the range of about 90 to 100 ° C. On the other hand, even if the anti-slip member is heated at such a temperature, it does not melt, or the temperature at which it does not melt easily, that is, the melting temperature of the heat-meltable resin layer 2 is set in the range of about 120 to 150 ° C. You can The above set temperatures can be appropriately changed by appropriately selecting two kinds of heat-meltable resins according to the melting temperature.
【００１９】アイロン、プレス機その他の器具ですべり
止め部材を９０〜１００℃程度に加熱すると、熱溶融性
樹脂層３が溶融せしめられてホットメルト層となり、例
えば、図２、図３に示すようにズボン又はスカートの腰
の裏側に取り付ける帯体５にすべり止め部材をきわめて
簡単に接着することができる。この帯状物を腰裏という
（図２において、図面符号Ａで示す）。一方、熱溶融性
樹脂層２はこの程度の温度では溶融せしめられないか、
あるいは、溶融状態とはなりにくいものであり、少なく
とも層状態が保たれている。When the non-slip member is heated to about 90 to 100 ° C. with an iron, a press, or other equipment, the heat-meltable resin layer 3 is melted into a hot-melt layer, for example, as shown in FIGS. 2 and 3. The non-slip member can be bonded very easily to the strip 5 attached to the back of the waist of the pants or skirt. This strip is called the back of the waist (indicated by reference numeral A in FIG. 2). On the other hand, is the thermofusible resin layer 2 melted at this temperature?
Alternatively, it is unlikely to be in a molten state, and at least the layer state is maintained.
【００２０】上記腰裏Ａは、例えば、図３に示すよう
に、ズボン又はスカートの腰の裏側に取り付けられる。
図３では、ズボン又はスカートの表地６の裏側であって
腰の裏側に相当する部分に、縫着７により腰裏Ａが取り
付けられている。なお、図３において、図面符号８は芯
地、９はバイヤス裏地である。添片１にシリコン樹脂か
らなるすべり止め用の突起４、４を所定の間隔を置いて
接合させたすべり止め部材を、ズボン又はスカートの腰
の裏側に取り付ける帯体５に装着することにより、１つ
の腰裏Ａを作製することができ、図３に示すように、こ
の腰裏Ａをズボン又はスカートの腰の裏側に取り付けた
場合には、きわめて良好なすべり止め効果が得られる。
また、本発明によるすべり止め部材は、図４に示すよう
に、ズボン又はスカートの表地６の裏側であって腰の裏
側に相当する部分に直接取り付けたり、あるいは、カバ
ンの肩紐、ベルト、玄関マット、座蒲団、コースター等
各種物品の裏側その他様々な部分に取り付けることがで
き、いずれもそれらのすべり止め効果を発揮させること
ができる。The waist back A is attached to the back of the waist of pants or skirt, for example, as shown in FIG.
In FIG. 3, the back of the waist A is attached by sewing 7 to the back of the outer material 6 of the pants or skirt and corresponding to the back of the waist. In FIG. 3, reference numeral 8 is an interlining, and 9 is a vias lining. By attaching a non-slip member in which the non-slip projections 4 and 4 made of silicone resin are joined to the attachment piece 1 at a predetermined interval, the strip 5 is attached to the back side of the waist of the pants or skirt. Three backs A can be produced, and as shown in FIG. 3, when this back A is attached to the back of the waist of pants or skirt, a very good anti-skid effect is obtained.
Further, as shown in FIG. 4, the anti-slip member according to the present invention may be directly attached to the back side of the outer material 6 of the pants or skirt and corresponding to the back side of the waist, or the shoulder straps, belts, and entrances of the bag. It can be attached to various parts such as the back side of various articles such as mats, seats, and coasters, and any of them can exert their anti-slip effect.
【００２１】添片１を構成する織物もしくは編物の少な
くとも表面、換言すると、すべり止め用の突起４、４を
形成するべく溶融状態のシリコン樹脂を接合させる面
は、起毛せしめられているのが好ましい。このような添
片１を用いると、すべり止め用の突起４、４となる溶融
状態のシリコン樹脂が、織物もしくは編物からなる添片
１の生地目に浸透するとともに添片１の起毛部分を抱持
することになり、上述したような利点を有する。もっと
も、添片１を構成する織物もしくは編物の裏面、換言す
ると、熱溶融性樹脂層２を形成する面も起毛せしめられ
ていてもよい。織物もしくは編物の表面だけでなくこの
面も起毛せしめられていると、熱溶融性樹脂層２となる
溶融状態の樹脂が織物もしくは編物からなる添片１の生
地目に浸透するとともに添片１の裏面の起毛部分を抱持
することになり、熱溶融性樹脂層２自体の添片１への付
着性がさらに増大し、突起４の添片１への付着性もより
一層増大し、その結果、熱溶融性樹脂層３ならびに突起
４が添片１から剥離することがより一層なくなるという
利点を有することになる。At least the surface of the woven or knitted material that composes the attachment piece 1, in other words, the surface to which the molten silicon resin is bonded so as to form the projections 4 and 4 for preventing slippage is preferably raised. . When such an attachment piece 1 is used, the molten silicone resin that becomes the anti-slip projections 4 and 4 penetrates into the cloth of the attachment piece 1 made of a woven or knitted fabric and holds the raised portion of the attachment piece 1. It has the advantages described above. However, the back surface of the woven or knitted material that composes the attachment piece 1, in other words, the surface that forms the heat-meltable resin layer 2 may also be raised. When not only the surface of the woven or knitted fabric but also this surface is raised, the resin in a molten state which becomes the heat-meltable resin layer 2 penetrates into the texture of the added piece 1 made of the woven or knitted material and Since the raised portion on the back side is held, the adhesion of the heat-meltable resin layer 2 itself to the attachment piece 1 is further increased, and the adhesion of the protrusion 4 to the attachment piece 1 is further increased. Therefore, the heat-fusible resin layer 3 and the protrusions 4 have an advantage that they are further prevented from peeling off from the attachment piece 1.
【００２２】なお、従来のゴム又はビニール製のすべり
止め部材では通気性がないから、これに蒸気や熱を加え
てズボン又はスカートの腰の裏側などに接合しようとし
ても完全に接合させることはむつかしく、周囲を縫い付
ける等の補助作業が必要であるが、本発明によるすべり
止め部材を用いれば、添片１の表側から熱を加えるだけ
でズボン又はスカートの腰の裏側などに容易に接合する
ことができるのみならず、その接合状態はきわめて強固
であり、水洗いやドライクリーニングしてもすべり止め
部材が剥離しない。Since conventional rubber or vinyl non-slip members do not have air permeability, it is difficult to completely join them even if steam or heat is applied to them to join them to the underside of the waist of the pants or skirt. However, auxiliary work such as sewing around is required, but by using the non-slip member according to the present invention, it is possible to easily join to the back side of the waist of the pants or the skirt simply by applying heat from the front side of the accessory piece 1. Not only that, but the joining state is extremely strong, and the anti-slip member does not peel off even after washing with water or dry cleaning.
【００２３】[0023]
【発明の効果】請求項１記載の接合方法を用いれば、熱
溶融性樹脂層２の添片１への付着性、熱溶融性樹脂層３
と熱溶融性樹脂層２との接着性、及び、シリコン樹脂か
らなるすべり止め用の突起４、４の添片１への付着性が
いずれも増大し、熱溶融性樹脂層３とシリコン樹脂から
なるすべり止め用の突起４、４とが添片１から剥離する
ことがないという効果がある。According to the joining method of the first aspect, the adhesiveness of the heat-meltable resin layer 2 to the attachment piece 1 and the heat-meltable resin layer 3 are used.
The adhesiveness between the heat-fusible resin layer 2 and the heat-fusible resin layer 2 and the adhesion of the non-slip projections 4 and 4 made of silicon resin to the attachment piece 1 are both increased. The resulting anti-slip projections 4 and 4 are not separated from the attachment piece 1.
【００２４】請求項２記載の接合方法を用いれば、熱溶
融性樹脂層２の添片１への付着性、及び、シリコン樹脂
からなるすべり止め用の突起４、４の添片１への付着性
がさらに増大するという効果がある。If the joining method according to claim 2 is used, the adhesion of the heat-meltable resin layer 2 to the attachment piece 1 and the adhesion of the non-slip projections 4 and 4 made of silicone resin to the attachment piece 1 are used. This has the effect of further increasing the sex.
【００２５】請求項３記載のすべり止め部材を用いた場
合には、きわめて良好なすべり止め効果を長く維持する
ことができるのみならず、水洗いやドライクリーニング
してもすべり止め部材が剥離しないという効果がある。When the non-slip member according to the third aspect is used, not only the very good anti-slip effect can be maintained for a long time, but also the anti-slip member does not peel off even after washing with water or dry cleaning. There is.
【００２６】請求項４記載のすべり止め部材を用いた場
合には、熱溶融性樹脂層２の添片１への付着性、及び、
シリコン樹脂からなるすべり止め用の突起４、４の添片
１への付着性がさらに増大し、きわめて良好なすべり止
め効果を半永久的に維持することができるのみならず、
水洗いやドライクリーニングしてもすべり止め部材が全
く剥離しないという効果がある。When the non-slip member according to claim 4 is used, the adhesiveness of the heat-meltable resin layer 2 to the attachment piece 1 and
The adhesion of the non-slip projections 4 and 4 made of silicon resin to the attachment piece 1 is further increased, and not only a very good anti-slip effect can be maintained semipermanently,
Even if it is washed with water or dry-cleaned, the non-slip member does not peel off at all.
【図１】本発明の方法の一例を工程順に示す図で、(a)
は添片の片面に１つの熱溶融性樹脂層を形成した状態を
示す断面図、(b) はその一部を示す斜視図、(c) 、(d)
はすべり止め用の突起を接合した状態を示す断面図、
(e) は（c)に示す突起接合後の熱溶融性樹脂層の外面に
さらに熱溶融性樹脂層を形成した完成後のすべり止め部
材を示す断面図である。FIG. 1 is a diagram showing an example of a method of the present invention in the order of steps, (a)
Is a cross-sectional view showing a state in which one heat-meltable resin layer is formed on one surface of the attachment piece, (b) is a perspective view showing a part thereof, (c), (d)
Sectional view showing a state in which projections for slip prevention are joined,
(e) is a cross-sectional view showing a non-slip member after completion, in which a heat-meltable resin layer is further formed on the outer surface of the heat-meltable resin layer after the protrusion bonding shown in (c).
【図２】図１(e) に示すすべり止め部材を腰裏に適用し
た場合の一例を示す正面図で、その一部のみを示す。FIG. 2 is a front view showing an example of the case where the non-slip member shown in FIG. 1 (e) is applied to the back of the waist, and only a part thereof is shown.
【図３】図２に示す腰裏を、ズボン又はスカートの腰の
裏側に取り付けた状態を示す拡大断面図である。FIG. 3 is an enlarged cross-sectional view showing a state in which the back of the waist shown in FIG. 2 is attached to the back of the waist of pants or a skirt.
【図４】図１(e) に示すすべり止め部材を、ズボン又は
スカートの腰の裏側に相当する部分に直接取り付けた状
態を示す拡大断面図である。FIG. 4 is an enlarged cross-sectional view showing a state in which the anti-slip member shown in FIG. 1 (e) is directly attached to a portion of the pants or skirt corresponding to the back side of the waist.
【図５】従来のすべり止め部材の一例を示す断面図で、
(a) は溶融状態のシリコン樹脂を型を用いて成型し、添
片にすべり止め用の突起を接合するとき、溶融状態のシ
リコン樹脂が添片に含浸せしめられて行く様子を示す断
面図、(b) は添片の裏側にプライマーを塗布し、さら
に、その裏側にねじ溶融性樹脂層を形成した状態を示す
断面図である。FIG. 5 is a sectional view showing an example of a conventional non-slip member,
(a) is a cross-sectional view showing a state in which a molten silicon resin is impregnated into a splicing piece when a molten silicon resin is molded using a mold and a protrusion for slip prevention is joined to the splicing piece. (b) is a cross-sectional view showing a state in which a primer is applied to the back side of the attachment piece and a screw-meltable resin layer is further formed on the back side.
１─添片、２，３─熱溶融性樹脂層、４─突起、５─帯
体、Ａ─腰裏。1-Attachment, 2,3-Heat-meltable resin layer, 4-Protrusion, 5-Band, A-Back of the waist.
フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ Ａ４７Ｇ 27/04 Ａ４７Ｇ 27/04 Ａ (58)調査した分野(Int.Cl.7，ＤＢ名) A41D 27/00 A41D 1/06 A41D 1/14 Front page continuation (51) Int.Cl. 7 identification code FI A47G 27/04 A47G 27/04 A (58) Fields investigated (Int.Cl. 7 , DB name) A41D 27/00 A41D 1/06 A41D 1 /14
Claims (4)
し、その片面に、所定の加熱温度では溶融しないか、あ
るいは、溶融しにくい熱溶融性樹脂層２を形成し、次
に、それとは反対側の面において、溶融状態のシリコン
樹脂を成型することにより添片１にすべり止め用の突起
４、４を形成し、しかる後、前記熱溶融性樹脂層２の外
面に、所定の加熱温度で溶融する熱溶融性樹脂層３を形
成することを特徴とする添片にシリコン樹脂からなるす
べり止めを接合させる方法。1. An additive piece 1 is made of a woven or knitted material, and a thermofusible resin layer 2 which is not melted or is difficult to melt at a predetermined heating temperature is formed on one surface thereof. On the surface on the opposite side, projections 4 and 4 for slip prevention are formed on the attachment piece 1 by molding a molten silicon resin, and thereafter, a predetermined heating temperature is applied to the outer surface of the heat-meltable resin layer 2. A method of joining a non-slip made of a silicone resin to an attachment piece, characterized in that the heat-fusible resin layer 3 which is melted in (1) is formed.
せしめられている請求項１記載の添片にシリコン樹脂か
らなるすべり止めを接合させる方法。2. A method of joining a non-slip made of a silicone resin to the attachment piece according to claim 1, wherein at least the surface of the woven or knitted fabric is raised.
に、所定の加熱温度では溶融しないか、あるいは、溶融
しにくい熱溶融性樹脂層２と、所定の加熱温度で溶融す
る熱溶融性樹脂層３とが順次形成されており、それと反
対側の面には、溶融状態のシリコン樹脂を成型すること
によりすべり止め用の突起４、４が形成されていること
を特徴とするすべり止め部材。3. A heat-meltable resin layer 2 which is not melted at a predetermined heating temperature or is hardly melted at a predetermined heating temperature, and a heat-meltable resin which is melted at a predetermined heating temperature, on one surface of a piece of woven or knitted fabric. A non-slip member, characterized in that a layer (3) is sequentially formed, and anti-slip projections (4, 4) are formed on a surface opposite to the layer (3) by molding a molten silicon resin.
せしめられている請求項３記載のすべり止め部材。4. The non-slip member according to claim 3, wherein at least the surface of the woven or knitted fabric is raised.