JP3409086B2 - Filled OA floor panel - Google Patents
Filled OA floor panelInfo
- Publication number
- JP3409086B2 JP3409086B2 JP21759099A JP21759099A JP3409086B2 JP 3409086 B2 JP3409086 B2 JP 3409086B2 JP 21759099 A JP21759099 A JP 21759099A JP 21759099 A JP21759099 A JP 21759099A JP 3409086 B2 JP3409086 B2 JP 3409086B2
- Authority
- JP
- Japan
- Prior art keywords
- floor panel
- cement
- filled
- filler
- styrofoam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ＯＡ機器やコンピ
ュータ等を設置する床に於いて、電力線や通信線等を合
理的に配設することの出来るＯＡ床パネルに関するもの
で、中空の剛性体から成る床パネルの該中空部に充填材
を充填したＯＡ床パネルを提供するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an OA floor panel in which a power line, a communication line and the like can be rationally arranged on a floor on which OA equipment, a computer and the like are installed, and a hollow rigid body. The present invention provides an OA floor panel in which a filling material is filled in the hollow portion of the floor panel.
【０００２】[0002]
【従来の技術】従来より、ＯＡ床パネルには、コンクリ
ート製等の窯業系、アルミダイキャスト製、鋼板製等の
金属系、合成樹脂系、木製系或いはそれらを組み合わせ
たもの等の様々な材質によるものが使用されている。そ
の各々には利点も有るが欠点も有った。本発明に係るＯ
Ａ床パネルは、中空剛性体から成り、該中空部に充填材
を充填したものに係り、従来のこの種類のＯＡ床パネル
の充填材としては、当該中空部に通常の砂、砂利等より
成る骨材を混合したモルタル或いはコンクリート等を充
填するのが一般的で有った。また骨材として上記以外の
天然骨材、人工骨材等の各種他の材料を混合することも
有った。例えば、骨材としてシラスバルーンやパーライ
ト等の軽量骨材を混合していた。更に、近年、骨材とし
てガラス廃材を粉砕して形成した材料を混合している。
その場合、セメントとガラス廃材との混合比はその容積
比で約１；１の割合で混合している。2. Description of the Related Art Conventionally, OA floor panels are made of various materials such as ceramics such as concrete, aluminum die cast, metal such as steel plate, synthetic resin, wood or a combination thereof. Is used by. Each of them has its advantages but also its drawbacks. O according to the present invention
The A floor panel is composed of a hollow rigid body, and relates to a hollow portion filled with a filler. As a filler of a conventional OA floor panel of this type, the hollow portion is composed of ordinary sand, gravel or the like. It was common to fill mortar or concrete mixed with aggregate. In addition, various other materials such as natural aggregates and artificial aggregates other than the above may be mixed as the aggregate. For example, lightweight aggregates such as shirasu balloon and perlite have been mixed as aggregates. Further, in recent years, materials formed by crushing glass waste materials as aggregates have been mixed.
In that case, the mixing ratio of cement and waste glass is about 1: 1 in terms of volume ratio.
【０００３】[0003]
【発明が解決しようとする課題】上記従来より使用され
ているＯＡ床パネルは，窯業系のものにあっては骨材と
して砂や砂利を多量に使用しているので重量があり、運
搬上、施工上及びメンテナンス上問題が有った。また、
金属系のものは当該金属と接触した時に生じる金属音や
中空部での音の反射による反響音等により歩行感が悪か
った。更に、合成樹脂系のものは上記歩行感の問題の他
に、強度上の問題、材料確保の問題及び不燃性とは成り
得ない問題等が有った。また、金属系のものと窯業系の
ものとを組み合わせたＯＡ床パネルは、パネル単体の重
量が、約５０ｃｍ角、厚さ約２５ｍｍのパネルで約１０
Ｋｇ以上もあり、必要以上に重量があり、運搬上、施工
上或いはメンテナンス上問題点が有ったので、上記した
ように、中空金属製のパネルの中空部に軽量骨材を混合
したものが採用されてきている。しかし、それらシラス
バルーン、パーライト、セビオライト等の軽量骨材は、
天然材であり、近年それらの材料を国内で調達すること
は困難に成って来ており、地球環境の観点から、それら
材料の使用には大きな問題点があった。The above-mentioned conventional OA floor panels are heavy in weight because they use a large amount of sand or gravel as an aggregate in the ceramics type, so that they are easy to transport. There was a problem in construction and maintenance. Also,
The metal-based material had a bad walking feeling due to a metallic sound generated when it came into contact with the metal or an echo sound due to reflection of sound in the hollow portion. Further, in addition to the above-mentioned problem of walking feeling, the synthetic resin system has problems of strength, problems of securing materials, and problems that cannot be nonflammable. In addition, an OA floor panel that is a combination of a metal-based one and a ceramic-based one has a weight of about 50 cm square and a thickness of about 25 mm.
Since it weighed more than Kg and was unnecessarily heavy, and had problems in terms of transportation, construction, and maintenance, as described above, a mixture of lightweight aggregate in the hollow part of the hollow metal panel was used. Has been adopted. However, the lightweight aggregates such as Shirasu balloon, perlite, and ceviolite are
It is a natural material, and it has become difficult to procure these materials domestically in recent years, and there is a big problem in using these materials from the viewpoint of the global environment.
【０００４】更に、ガラス廃材を粉砕して形成した骨材
は、上記環境問題の上では良いが、約５０ｃｍ角、厚さ
約２５ｍｍの床パネルで、上記通常のこの種のパネルよ
りは軽量と成るもののそれでも約９、５Ｋｇの重量が有
り、重量の点及びコストが高いという欠点が有った。ま
た、中空金属製パネルの中空部に詰められた従来の充填
材は、それらコンクリート系充填材が硬化し強度を増加
させて行く過程、或いは硬化後の温度変化による収縮等
に於いて、内部応力の蓄積等が行われ、且つその充填材
がその周囲を金属板によって拘束されているので、それ
ら蓄積応力の逃げ道が無く、それらエネルギーが音とし
て発生する音鳴りの原因と成っていた。Further, the aggregate formed by crushing the waste glass material is good in view of the above environmental problems, but it is a floor panel of about 50 cm square and about 25 mm in thickness, which is lighter than the usual panel of this kind. However, it still has a weight of about 9,5 kg, and has a drawback of high weight and high cost. In addition, the conventional filler packed in the hollow part of the hollow metal panel has an internal stress in the process of hardening and increasing the strength of the concrete filler, or the shrinkage due to the temperature change after hardening. And the like, and the filling material is constrained by a metal plate around it, there is no escape route for those accumulated stresses, and this is a cause of the squealing of energy generated as sound.
【０００５】[0005]
【課題を解決するための手段】本発明は、上記欠点を解
決したもので、パネル単体の重量を軽くし、天然材を採
取すること無く且つコスト削減を図ったＯＡ床パネルを
提供するもので、剛性体より成る中空床パネルの、該中
空部に軽量弾性骨材とセメントとの混合物を充填して成
ることを特徴とする充填材入りＯＡ床パネルとしたもの
である。また、剛性体より成る中空床パネルの、該中空
部に軽量弾性骨材、ガラス粉砕骨材及びセメントとの混
合物を充填して成ることを特徴とする充填材入りＯＡ床
パネルとしたものである。更に、上記剛性体を鋼板製と
した充填材入りＯＡ床パネルである。また、上記軽量弾
性骨材として、発泡スチロールを選択した充填材入りＯ
Ａ床パネルである。更に、上記発泡スチロールの外周面
に予めコーティングした充填材入りＯＡ床パネルであ
る。また、ガラス粉砕骨材を、瓶等を粉砕した再生品を
成形したものとした充填材入りＯＡ床パネルである。更
に、セメントを、フライアッシュセメントとした充填材
入りＯＡ床パネルである。また、セメントを、エコセメ
ントとした充填材入りＯＡ床パネルである。SUMMARY OF THE INVENTION The present invention solves the above-mentioned drawbacks and provides an OA floor panel in which the weight of the panel itself is reduced, natural materials are not collected, and the cost is reduced. A filler-filled OA floor panel, characterized in that the hollow portion of a rigid body is filled with a mixture of lightweight elastic aggregate and cement. Further, the present invention provides a filled OA floor panel, characterized in that the hollow portion of a rigid body is filled with a mixture of lightweight elastic aggregate, crushed glass aggregate and cement. . Furthermore, it is an OA floor panel containing a filler in which the rigid body is made of a steel plate. In addition, as the above-mentioned lightweight elastic aggregate, O containing a filler in which Styrofoam is selected
A floor panel. Further, it is an OA floor panel containing a filler, which is pre-coated on the outer peripheral surface of the polystyrene foam. Further, it is an OA floor panel containing a filler, which is made by molding glass crushed aggregate into a recycled product obtained by crushing a bottle or the like. Furthermore, it is an OA floor panel containing a filler in which the cement is fly ash cement. Further, it is an OA floor panel containing a filler in which cement is eco-cement.
【０００６】[0006]
【発明の実施の形態】本発明に係る充填材入りＯＡ床パ
ネルは、剛性体より成る中空パネルの該中空部に軽量弾
性骨材を混合したコンクリート等を充填したもので、以
下にその実施例について説明する。
実施例１
充填材入りＯＡ床パネル１は、外側外形形状を形成する
周囲の金属板２と、当該金属板２で囲まれた中空部に充
填された充填材３とより構成している。金属板２として
は、溶融亜鉛メッキ鋼板製のものが使用され、表面板４
及び裏面板５とを接合して形成している。表面板４は略
四角形状の平板状とされ、その裏面側の裏面板５をカシ
メ手段によって両者をカシメ接合している。当該裏面板
５は、その底面側から表面側に向けてお椀形状に突出形
成された多数のディンプル形状の突起６を形成してい
る。ディンプル状突起６は、約５０ｃｍ角のパネルに於
いて３６ヶ所形成している。ディンプル状突起６の頂部
７は表面板４の裏面に接触し、ディンプル状突起６の基
端部は表面板４と所定間隔を有して底面側を形成し、デ
ィンプル間連結部８としている。また、裏面板５の周縁
部も表面板４と所定間隔を有して底面側を形成した周縁
部平坦部９としている。上記ディンプル間連結部８と周
縁部平坦部９の面とは略面一としている。上記裏面板５
の周縁部の外側端部１０は、折り曲げて表面板４の裏面
と接触し、また、ディンプル状突起６の頂部７も表面板
４の裏面と接触し、当該接触ヶ所で相互をカシメ接合し
ている。BEST MODE FOR CARRYING OUT THE INVENTION An OA floor panel containing a filler according to the present invention is a hollow panel made of a rigid body filled with concrete or the like mixed with lightweight elastic aggregate in the hollow portion thereof. Will be described. Example 1 An OA floor panel 1 with a filler is composed of a surrounding metal plate 2 forming an outer shape and a filler 3 filled in a hollow portion surrounded by the metal plate 2. As the metal plate 2, a hot-dip galvanized steel plate is used.
And the back plate 5 are joined together. The surface plate 4 has a substantially rectangular flat plate shape, and the rear surface plate 5 on the back surface side thereof is caulked by caulking means. The back plate 5 has a large number of dimple-shaped projections 6 projecting in a bowl shape from the bottom surface side toward the front surface side. The dimple-shaped projections 6 are formed at 36 places on a panel of about 50 cm square. The top portion 7 of the dimple-shaped projection 6 contacts the back surface of the surface plate 4, and the base end portion of the dimple-shaped projection 6 forms a bottom surface side with a predetermined distance from the surface plate 4 to form an inter-dimple connection portion 8. Further, the peripheral portion of the back plate 5 is also a peripheral flat portion 9 having a bottom face formed with a predetermined distance from the front plate 4. The surfaces of the inter-dimple connection portion 8 and the peripheral flat portion 9 are substantially flush with each other. The back plate 5
The outer end portion 10 of the peripheral edge portion is bent to make contact with the back surface of the surface plate 4, and the top portion 7 of the dimple-shaped projection 6 also makes contact with the back surface of the surface plate 4 and is caulked to each other at the contact point. There is.
【０００７】中空部に充填する充填材料は、使用済みの
瓶等を粉砕し成形したガラス廃材のリサイクル材料、発
泡スチロールを粉砕した材料及びセメントとの混合物が
使用される。ガラスは、砂、ソーダ灰、石灰岩等の原料
から作られるので、新しい材料でガラス製品を製造する
と成ると、当然それら材料の採石を行う必要があり、運
搬手段と併せて、その周辺環境に多大な影響を及ぼして
いた。また、ガラスは生物分解出来ない材料なので、使
用後の再利用されないガラスは、埋立処分等を行う必要
があった。本発明では、上記ガラスの内、ガラス廃材を
利用するもので、自然環境に与える影響を回避すること
が出来る。従来より、ガラス食器、板ガラス、使用済み
の各種瓶等はガラス廃材としてカレット（割れガラス）
して再利用していたが、色分けの困難なカレットについ
てはその使用用途が制限されており、多くのこの種のガ
ラス廃材はそのまま廃棄されていた。本発明は、カレッ
トの色について特に仕分けの必要の無い使用用途と成る
ので骨材としての利用は最適である。本発明のものはカ
レットをさらに粉砕して成形したものを骨材として使用
する。As a filling material for filling the hollow portion, a mixture of a recycled material of glass waste material obtained by crushing and molding used bottles, a material obtained by crushing styrofoam, and cement is used. Since glass is made from raw materials such as sand, soda ash, and limestone, when it comes to manufacturing glass products with new materials, it is of course necessary to quarry those materials, and in addition to the transportation means, it greatly affects the surrounding environment. Had a great influence. Further, since glass is a material that cannot be biodegraded, glass that is not reused after use needs to be landfilled. In the present invention, a waste glass material is used among the above-mentioned glasses, and the influence on the natural environment can be avoided. Traditionally, glass tableware, plate glass, various used bottles, etc. are cullet (broken glass) as glass waste materials.
However, the use of cullet, which is difficult to color-code, is limited, and many glass wastes of this type were discarded as they were. The present invention is most suitable for use as an aggregate because it is a use application in which the color of cullet is not particularly required to be sorted. In the present invention, the cullet obtained by further crushing is used as an aggregate.
【０００８】また、発泡スチロールとしては、各種緩衝
材、包装材、魚箱、食品用トレー、建築用断熱材等で使
用された使用済みの発泡スチロール成形品を粉砕機等で
粉砕したものを採用する。その粉砕粒径は１〜３ｍｍ程
度まで粉砕したものを利用する。粒径は上記に限定する
こと無く、更に大径のものでも良い。上記発泡スチロー
ルは極めて軽量なのでセメントと混合したとき浮き上が
る心配がある。また、混合作業時に舞い上がる心配も有
った。そこでその浮き上がりの防止等を図るために発泡
スチロールの周囲を予めコーティングする。コーティン
グ手段として、発泡スチロール粉砕粒の表面を予めセメ
ントペーストで被覆する。セメントの粉末度は約３００
０〜３５００ｃｍ２／ｇなので、発泡スチロール粉砕粒
子にセメント、水を混入し、ミキサー等で混合すること
により、セメントペーストで発泡スチロールの外周面全
体を被覆することが出来る。他のコーティング材として
は、砂、石粉、石膏、水ガラス等の材料を採用すること
も出来る。上記発泡スチロールの外周面全体がコーティ
ングされても、その比重は約０、３〜０、５程度であ
る。As the Styrofoam, used Styrofoam molded products used for various cushioning materials, packaging materials, fish boxes, food trays, heat insulating materials for construction, etc. are crushed by a crusher or the like. The crushed particle size is about 1 to 3 mm. The particle size is not limited to the above and may be larger. Since the styrofoam is extremely lightweight, it may rise when mixed with cement. Also, there was a concern that it would rise up during the mixing work. Therefore, in order to prevent the floating and the like, the periphery of the styrofoam is coated in advance. As a coating means, the surface of styrofoam crushed particles is previously coated with cement paste. The fineness of cement is about 300
Since it is 0 to 3500 cm 2 / g, it is possible to coat the entire outer peripheral surface of the Styrofoam with the cement paste by mixing cement and water into the Styrofoam crushed particles and mixing them with a mixer or the like. As the other coating material, materials such as sand, stone powder, gypsum, and water glass can be adopted. Even if the entire outer peripheral surface of the Styrofoam is coated, its specific gravity is about 0, 3 to 0, 5.
【０００９】セメントは、通常はポルトランドセメント
が使用されるが、フライアッシュセメントを使用するこ
とが最適である。フライアッシュセメントは、火力発電
所等の微粉炭燃焼ボイラーから出る排ガス中に含まれて
いる灰の微粉粒子をコットレル集塵機で捕集した微粉末
状のもので、表面が滑らかな球形粒子から成るフライア
ッシュを原料としているので、ワーカビリティーが良
く、長期強度は大きく、水和熱が低く乾燥収縮も小さ
く、本発明のように、中空金属製材料の該中空部に充填
する材料として適している。上記ガラス廃材、使用済み
の発泡スチロール粉砕粒及びセメントに水を混合するこ
とにより中空金属製ＯＡ床パネルの充填材を得ることが
出来る。上記材料の具体的な混合比は容積比で、ガラス
廃材約５０％、発泡スチロール約３０％及びセメント約
２０％の混合物である。上記充填材を充填したＯＡ床パ
ネルは、約５０ｃｍ角、厚さ約２５ｍｍのパネル単体で
約７、０Ｋｇの重量と成る。また、従来のＯＡ床パネル
のものと比較してセメントの量を少なくすることが可能
と成った。更に、中空部への充填時の流動性を良好とす
るために、ＡＥ剤等の界面活性剤を混入することも有効
である。Portland cement is usually used as the cement, but fly ash cement is most preferably used. Fly ash cement is a fine powder that collects fine particles of ash contained in the exhaust gas from a pulverized coal combustion boiler of a thermal power plant with a Cottrell dust collector, and a fly with a smooth surface. Since ash is used as a raw material, the workability is good, the long-term strength is large, the heat of hydration is low, and the drying shrinkage is small, and it is suitable as a material for filling the hollow portion of the hollow metal material as in the present invention. A filler for a hollow metal OA floor panel can be obtained by mixing water with the above glass waste material, used styrofoam crushed particles, and cement. A specific mixing ratio of the above materials is, by volume, a mixture of about 50% glass waste material, about 30% styrofoam and about 20% cement. The OA floor panel filled with the above-mentioned filler has a weight of about 7.0 kg in a panel unit of about 50 cm square and about 25 mm thick. Further, it has become possible to reduce the amount of cement as compared with the conventional OA floor panel. Further, it is also effective to mix a surfactant such as an AE agent in order to improve the fluidity when filling the hollow portion.
【００１０】実施例２
上記実施例１では、セメントとしてフライアッシュセメ
ントを使用したが、本実施例では、当該セメントに換え
て都市ごみ焼却灰をセメントの原料としたエコセメント
を使用する。都市焼却灰は塩素を約２％含んでいるの
で、鉄筋を腐食させ易いので、その用途に制限を受けて
いる。本発明ではこのエコセメントを採用することがで
きる。この塩素を含んだ場合は、金属板にコーティング
することにより、金属板が腐食されることは無い。ま
た、近年、破砕した都市ごみを硫酸酸性にして、セメン
トキルンの廃熱（２００〜３００度Ｃ）等で脱塩素した
技術も開発されている。この場合は、塩素が除去される
ので、セメントと金属板が直接接触しても金属板が腐食
することは無い。上記実施例１で示したガラス廃材と発
泡スチロールに上記エコセメントと水を混合することに
より、中空金属製ＯＡ床パネルの充填材を得ることが出
来る。上記材料の具体的な混合比は容積比で、ガラス廃
材約５０％、使用済み発泡スチロール約３０％及びエコ
セメント約２０％の混合物である。従って、本実施例２
のものは、充填材としてすべての材料をリサイクル材料
から得ることが出来ることに成る。Example 2 In Example 1 above, fly ash cement was used as cement, but in this Example, ecocement using municipal waste incineration ash as a raw material for cement is used instead of the cement. Since the municipal incineration ash contains about 2% of chlorine, it easily corrodes the reinforcing bar, so its use is limited. This eco-cement can be adopted in the present invention. When this chlorine is contained, the metal plate is not corroded by coating the metal plate. Further, in recent years, a technique has been developed in which crushed municipal waste is acidified with sulfuric acid and dechlorinated by waste heat (200 to 300 ° C) of a cement kiln. In this case, since chlorine is removed, the metal plate will not be corroded even if the cement and the metal plate come into direct contact with each other. The hollow metal OA floor panel filler can be obtained by mixing the eco-cement and water in the waste glass material and the styrofoam shown in Example 1 above. A specific mixing ratio of the above materials is, by volume ratio, a mixture of about 50% of waste glass material, about 30% of used styrofoam and about 20% of ecocement. Therefore, the second embodiment
In this case, all materials can be obtained from recycled materials as fillers.
【００１１】実施例３
この実施例では、使用済み発泡スチロールとセメントと
を混合したものである。 骨材としての発泡スチロール
は、実施例１と同様、使用済みの発泡スチロール成形品
を粉砕機等で粉砕したものを採用する。その粉砕粒径は
１〜３ｍｍ程度まで粉砕したものを利用する。また、当
該発泡スチロールの周囲全体をコーティングする。セメ
ントは、通常のポルトランドセメントの他、フライアッ
シュセメント或いはエコセメントを使用することが出来
る。上記材料の具体的な混合比は容積比で、使用済み発
泡スチロール約６０％〜７０％、セメント約３０％〜４
０％混合したものが使用される。Example 3 In this example, used styrofoam and cement were mixed. As the styrofoam as the aggregate, a used styrofoam molded product is crushed by a crusher or the like as in the first embodiment. The crushed particle size is about 1 to 3 mm. Further, the entire periphery of the styrofoam is coated. As the cement, in addition to ordinary Portland cement, fly ash cement or ecocement can be used. The specific mixing ratio of the above materials is, by volume, about 60% to 70% of used Styrofoam and about 30% to 4 of cement.
A mixture of 0% is used.
【００１２】上記各実施例で示した充填材３を中空金属
板２の該中空部に充填することに成るが、その充填方法
としては、金属板２の裏面板５の周縁部平坦部９に形成
された充填材挿入孔１１よりポンプ等による強制注入に
より充填することに成る。挿入孔１１は約３０ｍｍ径に
形成されている。充填材の充填を良好とさせるために、
当該挿入孔１１とは略対向する位置に空気抜きのための
空気抜き孔１２を形成する。The filling material 3 shown in each of the above embodiments is filled in the hollow portion of the hollow metal plate 2. The filling method is as follows: Filling is performed by forced injection from the formed filler insertion hole 11 by a pump or the like. The insertion hole 11 has a diameter of about 30 mm. In order to make the filling of the filling material good,
An air vent hole 12 for venting air is formed at a position substantially opposite to the insertion hole 11.
【００１３】[0013]
【発明の効果】以上詳述したように、本発明の充填材入
りＯＡ床パネル１は、今まで再利用の用途が限られてい
た廃材を利用しているので天然材料の枯渇の問題が無
く、自然環境保護の面で優れたＯＡ床パネルを提供出来
るものである。また、ＯＡ床パネル１は、従来の同一タ
イプの充填材入り金属製ＯＡ床パネルと比較して軽量と
成り、運搬上、施工上或いはＯＡ床パネルの敷設後のメ
ンテナンス上、取り扱い易い部材を提供することが可能
と成った。更に、従来のＯＡ床パネルと比較して軽量と
成ったが、中空金属板とその中空部へ充填される骨材と
セメントとの混合物とでＯＡ床パネルが構成されるの
で、所定の重量は確保でき、且つ中空内を充填材により
詰めているので、歩行感に優れたＯＡ床パネルを得るこ
とが出来る。As described above in detail, since the filled OA floor panel 1 of the present invention uses the waste material which has been limited in the reuse, there is no problem of depletion of natural materials. It is possible to provide an OA floor panel which is excellent in terms of protection of the natural environment. In addition, the OA floor panel 1 is lighter than the conventional metal OA floor panel containing the same type of filler, and provides a member that is easy to handle for transportation, construction, or maintenance after laying the OA floor panel. It became possible to do. Further, it is lighter than the conventional OA floor panel, but since the OA floor panel is composed of the hollow metal plate and the mixture of the aggregate and the cement filled in the hollow portion, the predetermined weight is Since the space can be secured and the inside of the hollow is filled with the filling material, it is possible to obtain an OA floor panel excellent in walking feeling.
【００１４】また、従来の同一タイプの充填材入りＯＡ
床パネルは、金属板の中空部に密封されているコンクリ
ート系の充填材に起因する発生音が生じていたが、本発
明のものは、骨材として弾力性のある発泡スチロールを
採用したこと及び充填材全体に占めるセメントの割合を
削減したこと等により、コンクリートの乾燥或いは温度
変化等による収縮等によって生じる歪等の変位量の発生
を少なくさせたこと、並びに当該歪等を弾力性のある発
泡スチロールにより吸収させること等により、音の発生
が無くなった。更に、発泡スチロール粒体は、中に空気
層を有しているので、断熱性、防音・防振性に優れてお
り、その結果、充填材入りＯＡ床パネル１全体も断熱
性、各種機器類から発生する音或いは歩行音等に対して
の防音・防振性に優れている。また、本発明の充填材入
りＯＡ床パネル１は、不燃性と剛性とを兼ね備えている
ことは言うまでも無い。The conventional OA containing the same type of filler
The floor panel generated noise due to the concrete-based filler sealed in the hollow part of the metal plate, but the one of the present invention adopts elastic Styrofoam as the aggregate and the filling. By reducing the proportion of cement in the total material, the amount of displacement such as strain caused by shrinkage of concrete due to drying or temperature change etc. was reduced, and the strain etc. was expanded by styrofoam. The sound was eliminated by absorbing it. Furthermore, since the expanded polystyrene particles have an air layer inside, they are excellent in heat insulating properties, soundproofing, and vibration damping properties, and as a result, the entire OA floor panel 1 containing the filler is also heat insulating properties, and from various devices. It has excellent soundproofing / vibrationproofing against generated sounds or walking sounds. Needless to say, the filled OA floor panel 1 of the present invention has both noncombustibility and rigidity.
【図１】本発明の充填材入りＯＡ床パネルの断面図。FIG. 1 is a cross-sectional view of a filled OA floor panel of the present invention.
【図２】本発明の充填材入りＯＡ床パネルの表面側平面
図。FIG. 2 is a front surface side plan view of an OA floor panel containing a filler of the present invention.
【図３】本発明の充填材入りＯＡ床パネルの裏面側平面
図。FIG. 3 is a back side plan view of an OA floor panel containing a filler of the present invention.
１・・ＯＡ床パネル ２・・金属板 ３・・充填材 ４・・表面板 ５・・裏面板 ６・・ディンプル状突起 ７・・頂部 ８・・ディンプル間連結部 ９・・周縁部平坦部 １０・・外側端部 １１・・挿入孔 １２・・空気抜き孔 1 ... OA floor panel 2 ... Metal plate 3 ... Filling material 4 ... Surface plate 5 ... Back plate 6 ... Dimple-shaped protrusion 7 ... top Connection between dimples 9 ... Flat part on peripheral edge 10 ... Outer end 11 ... Insertion hole 12-Air vent holes
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平７−139137（ＪＰ，Ａ) 特開 平５−148986（ＪＰ，Ａ) 特開 平11−147278（ＪＰ，Ａ) 特開 昭64−71969（ＪＰ，Ａ) 特開 平８−326275（ＪＰ，Ａ) 特許2742980（ＪＰ，Ｂ２) (58)調査した分野(Int.Cl.7，ＤＢ名) E04F 15/024 601 ─────────────────────────────────────────────────── --Continued from the front page (56) Reference JP-A-7-139137 (JP, A) JP-A-5-148986 (JP, A) JP-A-11-147278 (JP, A) JP-A-64- 71969 (JP, A) JP 8-326275 (JP, A) Patent 2742980 (JP, B2) (58) Fields investigated (Int. Cl. 7 , DB name) E04F 15/024 601
Claims (8)
に外周面に予めコーティングした発泡スチロールとセメ
ントとの混合物を充填して成ることを特徴とする充填材
入りＯＡ床パネル。1. An OA floor panel containing a filler, characterized in that a hollow floor panel made of a rigid body is filled with a mixture of styrofoam and cement whose outer peripheral surface is pre-coated on the hollow portion.
〜７０％、セメント約３０％〜４０％として成ることを
特徴とする請求項１に記載の充填材入りＯＡ床パネル。2. A styrene foam mixing ratio is about 60% by volume.
The filled OA floor panel of claim 1, wherein the OA floor panel comprises ˜70% and about 30% to 40% cement.
に外周面に予めコーティングした発泡スチロール、ガラ
ス粉砕骨材及びセメントとの混合物を充填して成ること
を特徴とする充填材入りＯＡ床パネル。3. A filler-filled OA floor, characterized in that a hollow floor panel made of a rigid body is filled with a mixture of styrofoam, glass crushed aggregate and cement, the outer surface of which is pre-coated on the hollow portion. panel.
％、ガラス粉砕骨材約５０％、セメント約２０％として
成ることを特徴とする請求項３に記載の充填材入りＯＡ
床パネル。4. The volume ratio of the polystyrene foam is about 30.
%, Crushed glass aggregate about 50%, cement about 20%, filled OA according to claim 3, characterized in that
Floor panel.
た再生品としたことを特徴とする請求項３又は４に記載
の充填材入りＯＡ床パネル。5. The filler-filled OA floor panel according to claim 3, wherein the crushed glass aggregate is a recycled product formed by crushing a bottle or the like.
ことを特徴とする請求項１〜５のいずれか１に記載の充
填材入りＯＡ床パネル。6. A filler-filled OA floor panel according to claim 1, wherein the coating material is cement paste.
たことを特徴とする請求項１〜６のいずれか１に記載の
充填材入りＯＡ床パネル。7. The filler-filled OA floor panel according to claim 1, wherein the cement is fly ash cement.
徴とする請求項１〜６のいずれか１に記載の充填材入り
ＯＡ床パネル。8. The filler-filled OA floor panel according to claim 1, wherein the cement is ecocement.