JP3400616B2 - Liquid permeable opening plastic film - Google Patents

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】この発明は、生理用ナプキンや使
い捨ておむつなどの体液吸収性着用物品の表面シートと
して使用するのに好適な透液性の開口プラスチックフィ
ルムに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a liquid permeable open plastic film suitable for use as a surface sheet of a body fluid absorbent wearing article such as a sanitary napkin or a disposable diaper.

【０００２】[0002]

【従来の技術】従来、この種プラスチックフィルムは公
知である。例えば、特公昭５７−１７０８１号公報に
は、前記表面シートとして使用するための先細の導液管
を有するプラスチックフィルムが開示されている。この
導液管は、フィルムの上面から下面へ向かう方向に延び
ているから、このフィルムを使用するときには導液管の
下端部を吸液性コアに接触させ、フィルム上面に***さ
れた体液を導液管の毛管現象によってコアへ導く。2. Description of the Related Art Conventionally, this kind of plastic film is known. For example, Japanese Patent Publication No. 57-17081 discloses a plastic film having a tapered liquid guiding tube for use as the surface sheet. Since the liquid guiding tube extends in the direction from the upper surface to the lower surface of the film, when the film is used, the lower end of the liquid guiding tube is brought into contact with the liquid absorbing core to guide the body fluid excreted on the upper surface of the film. It leads to the core by the capillary action of the liquid tube.

【０００３】米国特許第４，３４２，３４１号公報に
は、表面シートとして使用する導液管つきの開口プラス
チックフィルムとその製造方法が開示されている。この
方法では、プラスチックフィルムに導液管つきの開口を
形成するために、フォトエッチング加工による多数の微
細孔を有する金属プレートを成形型として使用する。US Pat. No. 4,342,341 discloses an open plastic film with a liquid guiding tube used as a surface sheet and a method for producing the same. In this method, a metal plate having a large number of fine holes formed by photo-etching is used as a mold to form an opening with a liquid guiding tube in a plastic film.

【０００４】特開平５−１７７６９６号公報には、金網
を成形型として使うことにより、比較的簡単かつ低コス
トで導液管をプラスチックフィルムに形成する発明が記
載されている。Japanese Unexamined Patent Publication (Kokai) No. 5-177696 discloses an invention in which a metal conduit is used as a mold to form a liquid guiding tube on a plastic film relatively easily and at low cost.

【０００５】[0005]

【発明が解決しようとする課題】前記各公報に開示され
た開口プラスチックフィルムは、導液管の高さだけ着用
者の肌を湿ったコアから離間することができるから、コ
アと肌が接触したり、コアから逆流した体液が肌に触れ
たりする虞が少なくなる。したがって、このフィルムを
使用することにより着用物品の湿潤感を軽微にするとい
う効果が得られる。しかしながら、これらの開口プラス
チックフィルムは、体圧を受けて導液管が圧潰すると、
その効果を挙げることが難しくなる。Since the open plastic film disclosed in each of the above publications can separate the wearer's skin from the damp core by the height of the liquid guiding tube, the core and the skin contact each other. There is less risk of body fluid flowing back from the core touching the skin. Therefore, by using this film, the effect of reducing the wet feeling of the worn article can be obtained. However, these open plastic films, when the liquid guiding tube is crushed due to body pressure,
It is difficult to achieve that effect.

【０００６】また、前記特開昭５７−１７０８１３号公
報に開示された導液管つきの開口プラスチックフィルム
を前記米国特許第４，３４２，３１４号公報に開示の方
法によって製造しようとすると、エッチング加工でつく
る成形型の製作費がかさむ傾向にある。特にフィルムの
開口を微細にするほど型の製作費がかさみ、それがフィ
ルムのコスト上昇を招く。一方、特開平５−１７７６９
６号公報に開示の方法を利用すると、型の製作費を低く
抑えることはできるが、多数の微細な開口を互いに接近
させるには金網の線径を小さくしなければならなず、そ
うすることが成形型の耐久性を損ねるという結果をもた
らす。Further, when an attempt is made to manufacture the open plastic film with a liquid conducting tube disclosed in the above-mentioned Japanese Patent Laid-Open No. 170813/1982 by the method disclosed in the above-mentioned US Pat. No. 4,342,314, etching processing is performed. The cost of producing the forming mold tends to be high. In particular, the finer the opening of the film, the more expensive the cost of manufacturing the mold, which increases the cost of the film. On the other hand, JP-A-5-17769
If the method disclosed in Japanese Patent No. 6 is used, the cost of manufacturing the mold can be kept low, but the wire diameter of the wire mesh must be reduced in order to bring many fine openings close to each other. Results in impairing the durability of the mold.

【０００７】そこで、この発明は、開口プラスチックフ
ィルムの表面に圧潰することのない***部を形成し、こ
のフィルムを着用物品の表面シートとして使用すること
によって、コアと着用者の肌とを確実に離間できるよう
にすることを課題にしている。Therefore, according to the present invention, a bulge which does not collapse is formed on the surface of an open plastic film, and by using this film as a surface sheet of a wearing article, the core and the wearer's skin are surely secured. The challenge is to be able to separate them.

【０００８】[0008]

【課題を解決するための手段】この発明は、前記課題を
解決するために、体液吸収性着用物品の表面シートに使
用する透液性開口プラスチックフィルムを前提にしてい
る。In order to solve the above problems, the present invention is premised on a liquid-permeable open plastic film used as a surface sheet of a body fluid absorbent wearing article.

【０００９】かかる前提において、この発明が特徴とす
るところは、前記フィルムを下記ａ〜ｄからなる工程に
よって得ることにある。 ａ．厚み０．００５〜０．０５ｍｍの熱可塑性プラスチ
ックフィルム原反をその長手方向に走行させ、 ｂ．幅０．０５〜１．５ｍｍの熱可塑性プラスチックの
ストランドを同時に多数押出成形し、 ｃ．前記ストランドを前記フィルム原反片面の長手方向
に所要の並行間隔で融着して複合フィルムとなし、 ｄ．表面部に開口形成用の多数の通気性凹部を有し、該
凹部の開口径が前記ストランドの幅よりも大きい成形型
の上に前記複合フィルムを前記片面を上にして供給し、
該複合フィルムにその加熱軟化状態下で厚み方向の流体
圧を作用させて該複合フィルムの前記フィルム原反部分
を前記凹部内に向けて局部的に開裂し、前記ストランド
幅よりも大きい開口径を有する多数の透液性開口を形成
する、ことからなる工程。Under such a premise, the feature of the present invention resides in that the film is obtained by the following steps a to d. a. Running a thermoplastic plastic film stock having a thickness of 0.005 to 0.05 mm in its longitudinal direction, b. Simultaneously extruding a large number of thermoplastic strands having a width of 0.05 to 1.5 mm, c. Forming a composite film by fusing the strands in the longitudinal direction of the one side of the original film at a required parallel interval; d. The surface portion has a large number of air-permeable recesses for forming openings, the opening diameter of the recesses is supplied with the one side of the composite film on a mold having a larger width than the width of the strand,
A fluid pressure in the thickness direction is applied to the composite film under its heat-softened state to locally cleave the original film portion of the composite film into the concave portion, and the strand
Forming a number of liquid permeable openings having an opening diameter greater than the width .

【００１０】また、この発明が特徴とするところの他の
一つは、前記開口プラスチックフィルムを下記ａ’〜
ｂ’からなる工程によって得ることにある。 ａ’．孔径が少なくとも０．０５ｍｍの多数の開口を有
する厚み０．００５〜０．０５ｍｍの熱可塑性プラスチ
ックフィルム原反をその長手方向に走行させ、 ｂ’．前記フィルム原反の開口径の寸法よりも小さい幅
を有する熱可塑性プラスチックのストランドを同時に多
数押出成形し、該ストランドが前記フィルム原反の開口
を横切るように該ストランドを前記フィルム原反片面の
長手方向に所要の並行間隔で供給して該片面に融着し、
前記ストランドとフィルム原反とからなる複合フィルム
を形成する、ことからなる工程。Another feature of the present invention is that the opening plastic film has the following a '.
b '. a '. A raw thermoplastic film having a thickness of 0.005 to 0.05 mm having a large number of openings having a pore size of at least 0.05 mm is run in the longitudinal direction thereof, and b ′. A large number of thermoplastic strands having a width smaller than the opening diameter of the film raw material are simultaneously extruded, and the strands are arranged so that the strands cross the opening of the film raw material and the length of one side of the film raw material is increased. Direction is supplied at the required parallel spacing and fused to the one side,
Forming a composite film consisting of the strands and the original film.

【００１１】この発明が特徴とするさらに他の一つは、
前記開口プラスチックフィルムにおいて、熱可塑性プラ
スチックフィルムの長手および短手方向に所要の間隔で
配列した多数の透液性開口を有し、前記フィルムの片面
の長手方向に前記開口の径よりも小さい幅を有する多数
の熱可塑性ストランドが所要の並列間隔で延在して融着
するとともに、少なくとも一条の前記ストランドが前記
開口を横切っていることにある。Still another feature of the present invention is that
In the opening plastic film, having a large number of liquid-permeable openings arranged at required intervals in the longitudinal and lateral directions of the thermoplastic film, a width smaller than the diameter of the opening in the longitudinal direction of one side of the film. A large number of the thermoplastic strands that are present extend at the required side-by-side spacing and fuse together, and at least one strand of the strands crosses the opening.

【００１２】[0012]

【実施例】添付の図面を参照してこの発明の詳細を説明
すると、以下のとおりである。DESCRIPTION OF THE PREFERRED EMBODIMENTS The details of the present invention will be described below with reference to the accompanying drawings.

【００１３】図１に示す生理用ナプキンは、体液吸収性
着用物品の一例であって、この発明に係る開口プラスチ
ックフィルム１が表面シート２として使用されている。
かかるナプキンは、透液性の表面シート２と、不透液性
の裏面シート３と、それら両シート２，３間に介在する
吸液性コア４とによって構成されている。表裏面シート
２，３は、コア４の周縁から延出する部分の内面で互い
に接合している。The sanitary napkin shown in FIG. 1 is an example of a body fluid absorbent wearing article, and an open plastic film 1 according to the present invention is used as a topsheet 2.
The napkin is composed of a liquid-permeable top sheet 2, a liquid-impermeable back sheet 3, and a liquid-absorbent core 4 interposed between the two sheets 2 and 3. The front and back sheets 2 and 3 are joined to each other on the inner surfaces of the portions extending from the peripheral edge of the core 4.

【００１４】図２に示す表面シート２の部分拡大斜視図
において、シート２は、基材フィルム５と、基材フィル
ム５の上面に熱融着で接合し、ナプキンの前後方向に互
いに並行して延びる多数の糸状のストランド部６とで構
成されている。基材フィルム５は、その下面から下方へ
延出する多数の導液管１０を有し、この導液管１０は、
上部開口１０Ａと、下部開口１０Ｂと、上下開口部１０
Ａ，１０Ｂ間に位置する周壁１０Ｃとを有する。ストラ
ンド部６は、基材フィルム５の上面に接合している***
部６Ａと、***部６Ａの延長上にあって導液管１０の上
部開口１０Ａを横切る延長部６Ｂとで構成されている。
***部６Ａは、基材フィルム５の上面から***した状態
にある。多数の導液管１０において、上部開口１０Ａ
が、延長部６Ｂによって二分またはそれ以上に細分化さ
れている。ストランド部６は、その長さ方向が基材フィ
ルム５の上面に連続的または、間欠的に剥離不能に接合
している。In the partially enlarged perspective view of the surface sheet 2 shown in FIG. 2, the sheet 2 is joined to the base film 5 and the upper surface of the base film 5 by heat fusion, and is parallel to each other in the front-back direction of the napkin. It is composed of a large number of thread-shaped strands 6 that extend. The base film 5 has a large number of liquid guiding tubes 10 extending downward from the lower surface thereof.
Upper opening 10A, lower opening 10B, upper and lower openings 10
It has a peripheral wall 10C located between A and 10B. The strand portion 6 is composed of a raised portion 6A joined to the upper surface of the base film 5 and an extended portion 6B which is an extension of the raised portion 6A and which crosses the upper opening 10A of the liquid guiding tube 10.
The raised portion 6A is in a state of being raised from the upper surface of the base film 5. In a large number of liquid guiding tubes 10, an upper opening 10A
Is subdivided into two or more parts by the extension portion 6B. The lengthwise direction of the strand portion 6 is continuously or intermittently joined to the upper surface of the base material film 5 in a non-separable manner.

【００１５】図３は、図２のＩＩＩ−ＩＩＩ線端面図で
ある。ストランド部６の***部６Ａとその延長部６Ｂと
は、実線で示すように導液管１０の上部開口１０Ａをほ
ぼ水平に横切る場合の他に、延長部６Ｂが鎖線で示すよ
うに垂れ下がり、その一部１１が下部開口１０Ｂから下
にのぞく場合がある。図の***部６Ａは、その長手方向
が基材フィルム５の上面に連続的に接合している。FIG. 3 is an end view taken along line III-III in FIG. The ridge 6A of the strand portion 6 and its extension 6B extend substantially horizontally across the upper opening 10A of the liquid guiding tube 10 as shown by the solid line, and the extension 6B hangs down as shown by the chain line. A part 11 may look downward from the lower opening 10B. The ridge 6A in the figure has its longitudinal direction continuously joined to the upper surface of the base film 5.

【００１６】図４は、図３と同様な図面であるが、この
図では、ストランド部６が基材フィルム５に対して接合
部位１３で間欠的に接合し、部位１３間では***部６Ａ
と延長部６Ｂとが上向きに湾曲している。FIG. 4 is a drawing similar to FIG. 3, but in this figure, the strand portion 6 is intermittently joined to the base material film 5 at the joining portion 13, and the raised portion 6A is provided between the portions 13.
And the extension 6B are curved upward.

【００１７】図５は、表面シート２を連続的に製造する
工程の模式図である。この工程は左から右へと進み、左
から順に第１，２，３押出機１０１，１０２Ａ，１０２
Ｂが並び、第２，３押出機１０２Ａ，１０２Ｂの間には
真空成形用回転ドラム１３４が位置し、さらに、工程の
所要部位には案内用または加圧用のローラ１３０が配置
されている。第２，３押出機１０２Ａ，１０２Ｂは、後
記するように択一的に使用される。FIG. 5 is a schematic view of a process for continuously producing the topsheet 2. This process proceeds from left to right, and from the left, the first, second and third extruders 101, 102A, 102
B is lined up, a vacuum forming rotary drum 134 is located between the second and third extruders 102A and 102B, and a guide or pressure roller 130 is arranged at a required portion of the process. The second and third extruders 102A and 102B are alternatively used as described later.

【００１８】図６に示すように、ドラム１３４は、その
表面に表面シート２の上部開口１０Ａの開口形状に対応
する多数の凹部１３５Ａを有する。凹部１３５Ａの底面
１３５Ｂには、ドラム１３４の図示しない真空吸引系統
につながる微細な透孔１３５Ｃが形成されている。As shown in FIG. 6, the drum 134 has a large number of recesses 135A corresponding to the opening shape of the upper opening 10A of the topsheet 2 on its surface. On the bottom surface 135B of the recess 135A, a minute through hole 135C connected to a vacuum suction system (not shown) of the drum 134 is formed.

【００１９】図５の製造工程では、まず、第１押出機１
０１から基材フィルム５となるべき原反としてのフィル
ム１０５が押し出され、続いて第２押出機１０２Ａから
***部６Ａとその延長部６Ｂとなるべき複数条の断面中
実のストランド１０６が押し出され、それが軟化状態に
ある間にフィルム１０５の上面に融着して接合し、複合
フィルム１０５Ａが形成される。必要なら、ローラ１３
０で基材フィルム１０５とストランド１０６とを加圧
し、両者を確実に接合する。複合フィルム１０５Ａは、
ドラム１３４に密着して進み、必要ならヒーター１３１
による加熱軟化の工程を経て、ドラム１３４の真空サク
ションゾーン１３２においてドラム表面の凹部１３５Ａ
内に吸引され、その先端部が破裂する。そのときに、フ
ィルム１０５がよく延びるものであれば、吸引された部
分が管状を呈し、導液管１０が形成される。フィルム１
０５がよく延びないものであれば、開口だけが形成され
る。複合フィルム１０５Ａは、冷却ゾーン１３５のファ
ン１３６で冷却された後、ドラム１３４から離脱して表
面シート２の連続体である開口プラスチックフィルム１
となりロール１３７として巻き取られる。このように、
この発明の開口プラスチックフィルム１には、導液管１
０がある場合と、ない場合とがある。In the manufacturing process of FIG. 5, first, the first extruder 1
01, the film 105 as an original fabric to be the base film 5 is extruded, and subsequently the second extruder 102A extrudes the ridge 6A and the plurality of solid strands 106 having a cross section to be the extension 6B. While it is in the softened state, it is fused and bonded to the upper surface of the film 105 to form the composite film 105A. Roller 13 if needed
At 0, the base film 105 and the strand 106 are pressed to securely bond them. The composite film 105A is
Proceed in close contact with the drum 134, and if necessary, heater 131
In the vacuum suction zone 132 of the drum 134, the concave portion 135A on the drum surface is subjected to the heating and softening process by
It is sucked in and its tip ruptures. At that time, if the film 105 extends well, the sucked portion has a tubular shape, and the liquid guiding tube 10 is formed. Film 1
If 05 does not extend well, only openings are formed. The composite film 105A is cooled by the fan 136 in the cooling zone 135 and then separated from the drum 134 to form the open plastic film 1 which is a continuous body of the topsheet 2.
Next, it is wound up as a roll 137. in this way,
The opening plastic film 1 of the present invention includes a liquid guiding tube 1
There are cases where there is 0 and cases where there is no.

【００２０】複合フィルム１０５Ａにおいて、導液管１
０が形成される過程の詳細は次のとおりである。複合フ
ィルム１０５Ａは、ストランド１０６の接合している部
位が特に厚く、ストランド１０６どうしの間のフィルム
１０５の部分が薄いから、加熱温度等の吸引条件の選択
によってその薄い部分だけが相対的に高倍率で延伸され
て破裂する。その間にストランド１０６は殆ど変形しな
いか、フィルム１０５とともに吸引されて撓む。ストラ
ンド１０６がドラム１３４の凹部１３５Ａを横切ってい
ると、ストランド１０６の両側でフィルム１０５が破裂
し、図２，３の実線で示すように凹部１３５Ａにおいて
形成される開口部をストランド１０６で細分化すること
になる。もし、ストランド１０６の軟化温度がフィルム
１０５のそれと異なると、真空吸引のときのストランド
１０６の撓み量は図３の鎖線のように様々に変化する。
ストランド１０６のフィルム１０５の上面に対する接合
が連続的であるか間欠的であるかは、ストランド１０６
を融着するときのローラ１３０による加圧が連続的であ
るか間欠的であるかによって決まる。In the composite film 105A, the liquid guiding tube 1
The details of the process of forming 0 are as follows. In the composite film 105A, the portion where the strands 106 are joined is particularly thick, and the portion of the film 105 between the strands 106 is thin, so that only the thin portion has a relatively high magnification by selecting suction conditions such as heating temperature. Is stretched and bursts. In the meantime, the strand 106 is hardly deformed or is sucked and flexed together with the film 105. When the strands 106 cross the recesses 135A of the drum 134, the film 105 ruptures on both sides of the strands 106, and the openings formed in the recesses 135A are subdivided by the strands 106 as shown by the solid lines in FIGS. It will be. If the softening temperature of the strand 106 is different from that of the film 105, the amount of bending of the strand 106 during vacuum suction changes variously as shown by the chain line in FIG.
Whether the joining of the strand 106 to the upper surface of the film 105 is continuous or intermittent is determined by the strand 106.
Is determined by whether the pressure applied by the roller 130 at the time of fusing is continuous or intermittent.

【００２１】第２押出機１０２Ａは、それを第３押出機
１０２Ｂに代えることができる。第３押出機１０２Ｂ
は、ドラム１３４の後方にあり、導液管１０となるべき
管状部が既に形成されている基材フィルム１０５の上面
にストランド１０６を供給する。基材フィルム１０５の
走行速度に対し、ストランド１０６の供給速度が同じ程
度であるか、または遅ければストランド１０６は図３の
実線で示すようにほぼ水平な状態となり、その速度が速
ければ仮想線で示すように導液管１０の中で撓む。The second extruder 102A can be replaced with the third extruder 102B. Third extruder 102B
Is provided behind the drum 134 and supplies the strands 106 to the upper surface of the base film 105 on which the tubular portion to be the liquid guiding tube 10 is already formed. If the supply speed of the strands 106 is about the same as or slower than the traveling speed of the base film 105, the strands 106 are in a substantially horizontal state as shown by the solid line in FIG. It bends in the liquid guide tube 10 as shown.

【００２２】複合フィルム１０５Ａにおけるフィルム１
０５やストランド１０６の原料には、ＰＰ，ＰＥ，ＥＶ
Ａ，ＳＥＢＳ等の熱可塑性合成樹脂を利用することが可
能であり、必要ならそれらにＴｉＯ2 やＣａＣＯ3 等の
フィラーを１〜１０重量％の範囲で混合することができ
る。フィルム１０５の厚みは０．００５〜０．０５ｍｍ
であることが好ましく、導液管１０の上部開口１０Ａの
径は０．４〜７ｍｍ，下部開口１０Ｂの径は０．２〜７
ｍｍ、管の長さ（高さ）は０．２〜３ｍｍであることが
好ましい。また、フィルム１０５に融着している状態で
見たときのストランド１０６は、その厚みが０．００５
〜１ｍｍ、その幅が０．０５〜１．５ｍｍ、隣接するス
トランド１０６どうしの間隔が０．１〜１．５ｍｍであ
ることが好ましい。ただしストランド１０６の寸法や配
列間隔は、導液管１０の上部開口１０Ａを実質的に塞ぐ
ことがないように定めることが必要である。Film 1 in composite film 105A
The raw materials for 05 and strand 106 include PP, PE, EV
A thermoplastic synthetic resin such as A or SEBS can be used, and if necessary, a filler such as TiO2 or CaCO3 can be mixed in the range of 1 to 10% by weight. The thickness of the film 105 is 0.005 to 0.05 mm
The diameter of the upper opening 10A of the liquid guiding tube 10 is 0.4 to 7 mm, and the diameter of the lower opening 10B is 0.2 to 7
mm, and the length (height) of the tube is preferably 0.2 to 3 mm. The thickness of the strand 106 when viewed in a state of being fused to the film 105 is 0.005.
It is preferable that the width is 0.05 to 1 mm, the width is 0.05 to 1.5 mm, and the interval between the adjacent strands 106 is 0.1 to 1.5 mm. However, it is necessary to determine the dimensions and arrangement intervals of the strands 106 so that the upper opening 10A of the liquid guiding tube 10 is not substantially blocked.

【００２３】フィルム１０５とストランド１０６とは、
それらに使用する原料の熱軟化特性や、熱溶融特性に差
をもたせたり、親水性（または疎水性）、光沢、色調な
どの特性に差を持たせたりすることができる。そのよう
な差のある複合フィルム１０５Ａを表面シート２に使用
した生理用ナプキンでは、例えば、フィルム１０５が疎
水性であり、ストランド１０６が親水性であると、表面
シート２の上面に***された体液をストランド１０６、
すなわち***部６Ａと延長部６Ｂとに沿って一方向へ拡
散させることができる。かかるナプキンでは、その中央
部に限らず、前後の両端部でも体液を吸収することが可
能になるから、コア４の全体を有効に利用することによ
るナプキンの実質的吸液量の向上が実現する。また、ス
トランド１０６が太いほど、すなわち、***部６Ａの丈
が高いほど、コア４を着用者の肌から遠く離間させるこ
とができるから、湿潤状態のコア４と肌との直接的な接
触や、コア４から逆流した体液と肌との接触の機会が少
なくなり、ナプキンを使用しているときの湿潤感が軽微
になる。丈の低い***部６Ａが必要なときには、ストラ
ンド１０６をローラ１３０で圧縮して扁平にすればよ
い。隣接する***部６Ａどうしは前後に延びる溝を画成
しているから、ナプキンを着用したときにそこに空気が
ながれて肌と表面シート２との間の通気性がよい。ま
た、導液管１０の上部開口１０Ａを細分化する延長部６
Ｂは、コア４に吸収された経血が上部開口１０Ａから直
視されるのを妨げ、使用済みナプキン１を廃棄するとき
の不快感を柔げることができる。延長部６Ｂが下部開口
１０Ｂから下にのぞく部位１１は、コア４を構成する繊
維と絡み合い、表面シート２とコア４とを密着させる効
果を奏する。The film 105 and the strand 106 are
The raw materials used for them may have different heat softening properties and heat melting properties, or may have different properties such as hydrophilicity (or hydrophobicity), gloss, and color tone. In the sanitary napkin in which the composite film 105A having such a difference is used for the topsheet 2, for example, when the film 105 is hydrophobic and the strands 106 are hydrophilic, the body fluid excreted on the upper surface of the topsheet 2 The strand 106,
That is, it can be diffused in one direction along the raised portion 6A and the extended portion 6B. With such a napkin, not only the central portion but also the front and rear end portions can absorb the body fluid, so that the effective absorption of the napkin can be realized by effectively utilizing the entire core 4. . Further, the thicker the strand 106 is, that is, the higher the height of the raised portion 6A is, the farther the core 4 can be separated from the wearer's skin, and thus the direct contact between the wet core 4 and the skin, The chance of contact between the body fluid flowing back from the core 4 and the skin is reduced, and the wet feeling when using the napkin is reduced. When the ridge 6A having a low height is required, the strand 106 may be compressed by the roller 130 to be flat. Since the adjacent raised portions 6A define a groove extending in the front-rear direction, air is blown into the napkin when the napkin is worn, so that the air permeability between the skin and the surface sheet 2 is good. In addition, an extension portion 6 that subdivides the upper opening 10A of the liquid guide tube 10
B can prevent menstrual blood absorbed in the core 4 from being directly viewed from the upper opening 10A, and reduce discomfort when discarding the used napkin 1. The portion 11 where the extension portion 6B looks downward from the lower opening 10B is entangled with the fibers forming the core 4 and has an effect of bringing the surface sheet 2 and the core 4 into close contact with each other.

【００２４】[0024]

【発明の効果】この発明に係る開口プラスチックフィル
ムは、その表面に***部とその延長部とからなるストラ
ンド部を有するから、このフィルムを体液吸収性着用物
品の表面シートとして使用すると、着用者の肌と吸液性
コアとの離間距離が大きくなり、湿潤状態のコアが肌に
接触したり、コアから逆流した体液が肌に接触したりす
る虞が少なくなる。また、隣接する***部とそれらの間
に介在する基材フィルムとは、一方向に延びる溝を形成
しているから、体液がこの溝に沿って物品の前後方向へ
拡散することが可能になる。この溝には空気が流れるこ
とも可能であり、それによって肌と表面シートとの間の
通気性がよくなる。したがって、このフィルムを使用し
た着用物品は、使用時の湿潤感が軽微になる。EFFECTS OF THE INVENTION Since the open plastic film according to the present invention has a strand portion consisting of a raised portion and an extended portion on the surface thereof, when this film is used as a surface sheet of a body fluid absorbent wearing article, The separation distance between the skin and the liquid-absorbent core becomes large, and the risk of the wet core coming into contact with the skin or the body fluid flowing back from the core coming into contact with the skin is reduced. Further, since the adjacent ridges and the base film interposed therebetween form a groove extending in one direction, it becomes possible for body fluid to diffuse along the groove in the front-back direction of the article. . It is also possible for air to flow in this groove, which improves the breathability between the skin and the topsheet. Therefore, a worn article using this film has a slight wet feeling during use.

【００２５】フィルム表面のストランド部は、断面が中
実であるから、体圧を受けても潰れて偏平になることが
なく、肌とコアとの離間距離を確実に維持することがで
きる。Since the strand portion on the film surface has a solid cross section, it does not crush and become flat even when subjected to body pressure, and the distance between the skin and the core can be reliably maintained.

【図面の簡単な説明】[Brief description of drawings]

【図１】生理用ナプキンの部分破断斜視図。FIG. 1 is a partially cutaway perspective view of a sanitary napkin.

【図２】表面シートの部分拡大斜視図。FIG. 2 is a partially enlarged perspective view of a topsheet.

【図３】図２のＩＩＩ−ＩＩＩ線端面図。3 is an end view taken along line III-III in FIG.

【図４】図３と異なる態様の端面図。FIG. 4 is an end view of a mode different from FIG.

【図５】開口プラスチックフィルムの模式製造工程図。FIG. 5 is a schematic manufacturing process diagram of an open plastic film.

【図６】ドラム表面の部分拡大斜視図。FIG. 6 is a partially enlarged perspective view of a drum surface.

【符号の説明】[Explanation of symbols]

１ 開口プラスチックフィルム ２ 表面シート（複合フィルム） ５ 基材フィルム（熱可塑性プラスチックフィルム
原反） ６ ストランド部（ストランド） １０ 導液管（透液性開口） １０Ａ 上部開口（透液性開口） １０Ｂ 下部開口（透液性開口） １０Ｃ 周壁 １０５ フィルム（熱可塑性プラスチックフィルム原
反） １０５Ａ 複合フィルム １０６ ストランド １３４ ドラム（成形型） １３５Ａ 凹部（通気性凹部） 1 Open plastic film 2 Top sheet(Composite film) 5 Base film(Thermoplastic film
Original fabric) 6 Strand part(Strand) 10 Liquid transfer tube(Liquid-permeable opening) 10AUpper opening (liquid-permeable opening) 10BLower opening (liquid-permeable opening) 10C peripheral wall 105Film (thermoplastic film raw
Anti) 105AComposite film 106 Strand 134Drum (molding die) 135A recess(Breathable recess)

───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平５−49659（ＪＰ，Ａ) 特開 昭62−57975（ＪＰ，Ａ) 特開 昭58−1517（ＪＰ，Ａ) 実開 昭64−43915（ＪＰ，Ｕ) (58)調査した分野(Int.Cl.⁷，ＤＢ名) B29C 47/30 A61F 13/00 - 13/84 ─────────────────────────────────────────────────── ─── Continuation of the front page (56) Reference JP-A-5-49659 (JP, A) JP-A-62-57975 (JP, A) JP-A-58-1517 (JP, A) Actual development Sho-64- 43915 (JP, U) (58) Fields surveyed (Int.Cl. ⁷ , DB name) B29C 47/30 A61F 13/00-13/84

Claims (10)

(57)【特許請求の範囲】(57) [Claims] 【請求項１】体液吸収性着用物品の表面シートに使用す
る透液性開口プラスチックフィルムであって、 ａ．厚み０．００５〜０．０５ｍｍの熱可塑性プラスチ
ックフィルム原反をその長手方向に走行させ、 ｂ．幅０．０５〜１．５ｍｍの熱可塑性プラスチックの
ストランドを同時に多数押出成形し、 ｃ．前記ストランドを前記フィルム原反片面の長手方向
に所要の並行間隔で融着して複合フィルムとなし、 ｄ．表面部に開口形成用の多数の通気性凹部を有し、該
凹部の開口径が前記ストランドの幅よりも大きい成形型
の上に前記複合フィルムを前記片面を上にして供給し、
該複合フィルムにその加熱軟化状態下で厚み方向の流体
圧を作用させて該複合フィルムの前記フィルム原反部分
を前記凹部内に向けて局部的に開裂し、前記ストランド
幅よりも大きい開口径を有する多数の透液性開口を形成
する、 工程によって得られることを特徴とする前記開口プラス
チックフィルム。1. A liquid-permeable open plastic film for use as a surface sheet of a body fluid absorbent wearing article, comprising: a. Running a thermoplastic plastic film stock having a thickness of 0.005 to 0.05 mm in its longitudinal direction, b. Simultaneously extruding a large number of thermoplastic strands having a width of 0.05 to 1.5 mm, c. Forming a composite film by fusing the strands in the longitudinal direction of the one side of the original film at a required parallel interval; d. The surface portion has a large number of air-permeable recesses for forming openings, the opening diameter of the recesses is supplied with the one side of the composite film on a mold having a larger width than the width of the strand,
A fluid pressure in the thickness direction is applied to the composite film under its heat-softened state to locally cleave the original film portion of the composite film into the concave portion, and the strand
The apertured plastic film obtained by the step of forming a large number of liquid-permeable apertures having an aperture diameter larger than the width . 【請求項２】前記開口プラスチックフィルムにおいて、
前記ストランドは、その長手方向が前記フィルム原反片
面に連続的に融着している請求項１記載の開口プラスチ
ックフィルム。2. In the opening plastic film,
The open plastic film according to claim 1, wherein the strands are continuously fused to one side of the raw film in the longitudinal direction. 【請求項３】前記開口プラスチックフィルムにおいて、
前記ストランドは、その長手方向が前記フィルム原反片
面に間欠的に融着している請求項１記載の開口プラスチ
ックフィルム。3. The opening plastic film,
The open plastic film according to claim 1, wherein the strands are intermittently fused to one side of the film original fabric in the longitudinal direction. 【請求項４】体液吸収性物品の表面シートに使用する透
液性開口プラスチックフィルムであって、ａ．口径が少
なくとも０．０５ｍｍの多数の開口を有する厚み０．０
０５〜０．０５ｍｍの熱可塑性プラスチックフィルム原
反をその長手方向に走行させ、 ｂ．前記フィルム原反の開口径の寸法よりも小さい幅を
有する熱可塑性プラスチックのストランドを同時に多数
押出成形し、該ストランドが前記フィルム原反の開口を
横切るように該ストランドを前記フィルム原反片面の長
手方向に所要の並行間隔で供給して該片面に融着し、前
記ストランドとフィルム原反とからなる複合フィルムを
形成する、 工程によって得られることを特徴とする前記開口プラス
チックフィルム。4. A liquid-permeable plastic film for use in a surface sheet of a body fluid absorbent article, comprising: a. Thickness 0.0 with multiple openings with a diameter of at least 0.05 mm
A thermoplastic resin film stock of 05 to 0.05 mm is run in its longitudinal direction, b. A large number of thermoplastic strands having a width smaller than the opening diameter of the film raw material are simultaneously extruded, and the strands are arranged so that the strands cross the opening of the film raw material and the length of one side of the film raw material is increased. The open plastic film obtained by the step of forming a composite film composed of the strand and the original film by supplying the film at a predetermined parallel interval in the direction and fusion-bonding to the one surface. 【請求項５】前記ストランドを融着する相手のフィルム
原反は、その開口周縁に前記片面からもう一方の面へ向
かう方向に延びる管状部を有する請求項４記載の開口プ
ラスチックフィルム。5. A perforated plastic film according to claim 4, wherein the raw material film to which the strands are fused has a tubular portion extending in the direction from the one surface to the other surface at the peripheral edge of the opening. 【請求項６】前記複合フィルムにおいて、前記ストラン
ドは、その長手方向が前記フィルム原反片面に連続的に
融着している請求項４記載の開口プラスチックフィル
ム。6. The apertured plastic film according to claim 4, wherein, in the composite film, the strands are continuously fused to one side of the film original fabric in the longitudinal direction. 【請求項７】前記複合フィルムにおいて、前記ストラン
ドは、その長手方向が前記フィルム原反片面に間欠的に
融着している請求項４記載の開口プラスチックフィル
ム。7. The open plastic film according to claim 4, wherein in the composite film, the longitudinal direction of the strand is intermittently fused to one side of the original film. 【請求項８】8. 前記透液性開口を、その上部開口の径がThe diameter of the upper opening of the liquid-permeable opening is
０．４〜７ｍｍになるように形成し、前記多数のストラIt is formed to have a thickness of 0.4 to 7 mm, and
ンドは、それらの隣接するストランドどうしの間隔がThe spacing between adjacent strands is
０．１〜１．５ｍｍになるように押出成形する請求項１Extrusion molding is carried out so that it may become 0.1-1.5 mm.
ないし７いずれかに記載の開口プラスチックフィルム。8. An open plastic film according to any one of 1 to 7. 【請求項９】熱可塑性プラスチックフィルムの長手およ
び短手方向に所要の間隔で配列した多数の透液性開口を
有し、前記フィルムの片面の長手方向に前記開口の径よ
りも小さい幅を有する多数の熱可塑性ストランドが所要
の並列間隔で延在して融着するとともに、少なくとも一
条の前記ストランドが前記開口を横切っていることを特
徴とする、体液吸収性物品の表面シートに使用する透液
性開口プラスチックフィルム。9. A thermoplastic film having a large number of liquid-permeable openings arranged at required intervals in the longitudinal and lateral directions, and having a width smaller than the diameter of the opening in the longitudinal direction on one side of the film. A liquid-permeable liquid for use in a surface sheet of a body fluid-absorbing article, characterized in that a large number of thermoplastic strands are extended and fused at required parallel intervals and at least one of the strands crosses the opening. Open plastic film. 【請求項１０】10. 前記熱可塑性プラスチックフィルムは、The thermoplastic film is
厚み０．００５〜０．０５ｍｍであり、前記透液性開口The liquid-permeable opening has a thickness of 0.005 to 0.05 mm.
は、その上部開口の径が０．４〜７ｍｍであり、前記多Has a diameter of the upper opening of 0.4 to 7 mm,
数のストランドは、親水性であり、その幅が０．０５〜Some strands are hydrophilic and their width ranges from 0.05 to
１．５ｍｍであるとともにそれらの隣接するストランド1.5 mm and their adjacent strands
どうしの間隔が０．１〜１．５ｍｍであり、かつ、該スThe distance between them is 0.1 to 1.5 mm, and
トランドが前記透液性開口の上部開口を塞ぐことがないThe land does not block the upper opening of the liquid permeable opening.
ように該ストランドの前記寸法および間隔が定められてThe dimensions and spacing of the strands are
いる請求項９記載の開口プラスチックフィルム。The open plastic film according to claim 9.