JP3386925B2 - Hot rolling material descaling equipment - Google Patents
Hot rolling material descaling equipmentInfo
- Publication number
- JP3386925B2 JP3386925B2 JP12544795A JP12544795A JP3386925B2 JP 3386925 B2 JP3386925 B2 JP 3386925B2 JP 12544795 A JP12544795 A JP 12544795A JP 12544795 A JP12544795 A JP 12544795A JP 3386925 B2 JP3386925 B2 JP 3386925B2
- Authority
- JP
- Japan
- Prior art keywords
- descaling
- nozzle
- scale
- spray angle
- hot rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】
【０００１】
【産業上の利用分野】本発明は、熱間圧延ラインのデス
ケーリング装置に関し、特にスケール剥離性不良により
圧延材表面に生じるスケール疵を防ぐため、デスケーリ
ングを完全に行なうデスケーリング装置に関する。
【０００２】
【従来の技術】従来周知の鋼材の熱間圧延ラインにおい
ては、加熱炉で発生する鋼材表面のスケールを除去する
ために約１００〜１５０ｋｇ／ｃｍ2のジェットデスケ
ーリング装置を設置し、水ジェットの吹きつけによって
スケールを剥離、除去しながら粗圧延を行なっている。
【０００３】前記デスケーリング装置によって剥離でき
ないスケールについては、スラブを複数回リバースさせ
て複数回デスケーリングを繰り返したり、あるいは水圧
をアップさせることによってスケールの剥離性を上げて
いる。
【０００４】前記のデスケーリングにおいては、複数回
スラブをリバースしてデスケーリングを行なうことは生
産性が悪くなり、また、水圧力をアップさせることは電
力原単位が上がるという欠点、問題点が生じる。
【０００５】そこで、前記問題点を解決するために、特
開昭５７ー１０３７３１号公報には、デスケーリングノ
ズルの前で鋼材表面のスケールを冷却し、熱収縮により
スケールにクラックを入れ、その後デスケーリングを行
なってスケールを除去する方法が開示されている。
【０００６】また、従来、水ジェットによりデスケーリ
ングを完全に行なうために、デスケーリングの回数ある
いは水ジェットの圧力の指定はあったが、水ジェットの
吹きつけ角度については特に考慮されることなく、ほと
んどのノズルを従前どおり約１５°に固定しているのが
現状である。
【０００７】
【発明が解決しようとする課題】しかしながら、前記公
報に開示されている方法では、表面を冷却することによ
り熱ロスが大きくなるため、予めスラブ温度を上げてお
かなくてはならないという欠点がある。
【０００８】そこで、本発明は、従来のデスケーリング
に比べて剥離性が向上し、１パスでスケールがほぼ剥離
され、生産性が向上し、熱ロスも低減できるデスケーリ
ング装置を提供するものである。
【０００９】
【課題を解決するための手段】本発明は、熱間圧延鋼板
のデスケーリング装置において、粗圧延機前に通板方向
とは逆方向に水ジェットを吹き付けるデスケーリングノ
ズルを２段設置し、各ノズルの吹き付け角度を、前段ノ
ズルの吹き付け角度θ １ においては、０゜≧θ １ ≧１５
゜、後段ノズルの吹き付け角度θ ２ においては、２０゜
≦θ ２ ≦４０゜としたことを特徴とする。
【００１０】
【００１１】図２は、各ノズルの角度を変化させてデス
ケーリングの状態について試験した結果を示すグラフ
で、前段ノズルの吹きつけ角（θ1）を０°≦θ1≦１５
°、後段ノズルの吹きつけ角度（θ2）を２０°≦θ2≦
４０°の範囲とすることによりデスケーリングが完全に
行なわれることが分かる。なお、水圧は従来から採用さ
れているとおりの１００〜１５０ｋｇ／ｃｍ2の範囲で
ある。
【００１２】
【作用】本発明によれば、前段ノズルの吹きつけ角度
（θ1）≦後段ノズルの吹きつけ角度（θ2）としたこと
により、前段ノズルの吹きつけによりスケールにクラッ
クが入り、後段ノズルの吹きつけによりクラックの入っ
たスケールを剥離することができる。
【００１３】
【実施例】図１により本発明の実施例について説明す
る。
【００１４】熱間圧延する鋼材４は加熱炉で１２００〜
１３００°Ｃに加熱されるが、鋼材の表面は炉内の空気
で酸化され、厚さ数ｍｍのスケール５が生成する。粗圧
延設備１の前には前段のデスケーリングノズル２及び後
段のデスケーリングノズル３の２段からなるデスケーリ
ングノズルが設置され、前段ノズルの吹きつけ角度（θ
1）≦後段ノズルの吹きつけ角度（θ2）に設定されてお
り、前段ノズルの吹きつけによりスケールにクラックを
入れ、次いで後段ノズルの吹きつけによりスケールを剥
離する。
【００１５】前段ノズル２の吹きつけ角度（θ1）を０
≦θ１≦１５°とし、後段ノズルの吹きつけ角度
（θ2）を２０°≦θ２≦４０°にすることによりスケ
ールを確実に剥離することができる。
【００１６】なお、本発明によれば、水ジェット６の圧
力は、従来のデスケーリングで採用されている１００〜
１５０ｋｇ／ｃｍ2で、なんら変更する必要はない。
【００１７】
【発明の効果】本発明の効果は、次のとおりである。
【００１８】（１） 本発明によれば、従来のデスケー
リングに比べ、完全にスケールを剥離することができる
ため、圧延材表面にスケールに起因するスケール疵がな
くなる。
【００１９】（２） 本発明によれば、従来のデスケー
リングに比べ、剥離性が向上するために、１パスでスケ
ールがほぼ剥離されるので、生産性が向上し、従来の複
数パスによる熱ロスも低減できる。Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a descaling apparatus for a hot rolling line, and more particularly to a descaling apparatus for preventing scale flaws generated on the surface of a rolled material due to poor scale releasability. To a descaling device that completely performs 2. Description of the Related Art In a conventionally known hot rolling line for steel materials, a jet descaling device of about 100 to 150 kg / cm 2 is installed in order to remove scale on the surface of steel material generated in a heating furnace. Rough rolling is performed while removing and removing scale by spraying a water jet. [0003] For scales that cannot be peeled off by the descaling device, the slab is reversed a plurality of times to repeat the descaling a plurality of times, or the water pressure is increased to increase the peelability of the scales. In the above descaling, performing the descaling by reversing the slab a plurality of times degrades the productivity, and increasing the water pressure causes a drawback and a problem that the power consumption increases. . In order to solve the above problem, Japanese Patent Laid-Open No. 57-103731 discloses that a scale on a steel material surface is cooled in front of a descaling nozzle, cracks are formed in the scale by heat shrinkage, and then the scale is decomposed. A method for performing scaling and removing scale is disclosed. Conventionally, in order to completely perform descaling using a water jet, the number of times of descaling or the pressure of the water jet has been designated, but the blowing angle of the water jet is not particularly taken into consideration. At present, most nozzles are fixed at about 15 ° as before. However, in the method disclosed in the above publication, the heat loss is increased by cooling the surface, so that the slab temperature must be raised in advance. There is. Accordingly, the present invention provides a descaling apparatus which can improve the peeling property as compared with the conventional descaling, almost peels off the scale in one pass, improves the productivity and reduces the heat loss. is there. According to the present invention, in a descaling apparatus for a hot-rolled steel sheet, a two-stage descaling nozzle for spraying a water jet in a direction opposite to a sheet passing direction is provided before a rough rolling mill. And adjust the spray angle of each nozzle
At the blasting angle θ 1 , 0 ° ≧ θ 1 ≧ 15
゜, at the spray angle θ 2 of the subsequent nozzle , 20 °
≦ θ 2 ≦ 40 ° . FIG. 2 is a graph showing the result of a test on the descaling state by changing the angle of each nozzle. The blowing angle (θ 1 ) of the front nozzle is set to 0 ° ≦ θ 1 ≦ 15.
°, the spray angle (θ 2 ) of the subsequent nozzle is 20 ° ≦ θ 2 ≦
It can be seen that descaling is completely performed by setting the range to 40 °. The water pressure is in the range of 100 to 150 kg / cm 2 as conventionally used. According to the present invention, since the blowing angle of the front nozzle (θ 1 ) ≦ the blowing angle of the rear nozzle (θ 2 ), the scale is cracked by the blowing of the front nozzle, The cracked scale can be peeled off by spraying the latter nozzle. An embodiment of the present invention will be described with reference to FIG. The steel material 4 to be hot-rolled is heated to 1200
Although heated to 1300 ° C., the surface of the steel material is oxidized by air in the furnace, and a scale 5 having a thickness of several mm is generated. In front of the rough rolling equipment 1, a descaling nozzle composed of two stages, a former descaling nozzle 2 and a latter descaling nozzle 3, is installed, and the spray angle (θ
1 ) ≦ The spray angle of the subsequent nozzle (θ 2 ) is set, and the scale is cracked by spraying the former nozzle, and then the scale is peeled by spraying the latter nozzle. The spray angle (θ 1 ) of the front nozzle 2 is set to 0
By setting ≦ θ1 ≦ 15 ° and setting the spray angle (θ 2 ) of the subsequent nozzle to 20 ° ≦ θ2 ≦ 40 °, the scale can be reliably peeled. According to the present invention, the pressure of the water jet 6 ranges from 100 to 100 which is employed in the conventional descaling.
At 150 kg / cm 2 , there is no need to change anything. The effects of the present invention are as follows. (1) According to the present invention, the scale can be completely peeled off as compared with the conventional descaling, so that there is no scale flaw caused by the scale on the rolled material surface. (2) According to the present invention, compared to the conventional descaling, the scale is substantially peeled off in one pass because the peelability is improved, so that the productivity is improved and the heat generated by the conventional multiple passes is improved. Loss can also be reduced.
【図面の簡単な説明】
【図１】本発明によるデスケーリング装置の説明図。
【図２】ノズルの角度を変化させた時のデスケーリング
状態を示すグラフ。
【符号の説明】
１ 粗圧延機、 ２ 前段ノズル、 ３ 後段ノズル、
４ スラブ、 ５スケール、 ６ 水ジェットBRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is an explanatory diagram of a descaling device according to the present invention. FIG. 2 is a graph showing a descaling state when a nozzle angle is changed. [Description of Signs] 1 Rough rolling mill, 2 Pre-stage nozzle, 3 Post-stage nozzle,
4 slabs, 5 scales, 6 water jets
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) B21B 45/08 ──────────────────────────────────────────────────の Continued on front page (58) Field surveyed (Int. Cl. 7 , DB name) B21B 45/08
Claims (1)
いて、粗圧延機前に通板方向とは逆方向に水ジェットを
吹き付けるデスケーリングノズルを２段設置し、各ノズルの吹き付け角度を、前段ノズルの吹き付け角度
θ １ においては、０゜≧θ １ ≧１５゜、 後段ノズルの吹き付け角度θ ２ においては、２０゜≦θ
２ ≦４０゜としたこと を特徴とする熱間圧延素材のデス
ケーリング装置。(57) [Claims 1] In a descaling apparatus for a hot-rolled steel sheet, two stages of descaling nozzles for spraying a water jet in a direction opposite to a sheet passing direction are provided before a rough rolling mill, The spray angle of each nozzle is determined by the spray angle of the preceding nozzle.
In theta 1, 0 degree ≧ θ 1 ≧ 15 °, in the spray angle theta 2 in the subsequent stage nozzle, 20 ° ≦ theta
An apparatus for descaling a hot-rolled material, wherein 2 ≦ 40 ° .