JP3356825B2 - Processing of plastic products - Google Patents

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【産業上の利用分野】本発明は分解性ポリマー組成物の
処理方法に関する。さらに詳しくは、ヒドロキシカルボ
ン酸ポリマーを主体とする熱可塑性ポリマー組成物を分
解処理し、回収し、得られたヒドロキシカルボン酸を必
要によりポリマー原料として用いる方法に関するもので
ある。The present invention relates to a method for treating a degradable polymer composition. More specifically, the present invention relates to a method for decomposing and recovering a thermoplastic polymer composition mainly containing a hydroxycarboxylic acid polymer, and using the obtained hydroxycarboxylic acid as a polymer raw material if necessary.

【０００２】[0002]

【従来の技術】従来、包装材料としてはポリエチレン、
ポリプロピレン、ポリエチレンテレフタレート、ポリ塩
化ビニル、紙、アルミニウム、またはそれらの複合材料
が用いられている。しかしこの中で上記の樹脂から製造
された包装材料は、廃棄する際、ゴミの量を増すうえ
に、従来の物は自然環境下での分解速度がきわめて遅い
ため、埋設処理された場合、半永久的に地中に残留す
る。また投棄されたプラスチック類により、景観が損な
われ海洋生物の生活環境が破壊されるなどの問題も起こ
っている。2. Description of the Related Art Conventionally, polyethylene,
Polypropylene, polyethylene terephthalate, polyvinyl chloride, paper, aluminum, or composites thereof have been used. However, among these, packaging materials manufactured from the above-mentioned resins increase the amount of garbage when discarded, and conventional products have a very low decomposition rate in the natural environment. Will remain in the ground. Discarded plastics also cause problems such as spoiling the landscape and destroying the living environment of marine life.

【０００３】一方、熱可塑性樹脂で生分解性のあるポリ
マーとして、ヒドロキシカルボン酸のポリマーまたはコ
ポリマー（以下ヒドロキシカルボン酸系ポリマーと略称
する）が知られている。特に、ポリ乳酸または乳酸とそ
の他のヒドロキシカルボン酸のコポリマーは、動物の体
内で数カ月から１年で１００％生分解し、又、土壌や海
水中に置かれた場合、湿った環境下では数週間で分解を
始め１年から数年で消滅し、さらに分解生成物は、人体
に無害な乳酸と二酸化炭素と水になるという特性を有し
ている。On the other hand, as a biodegradable polymer of a thermoplastic resin, a hydroxycarboxylic acid polymer or copolymer (hereinafter abbreviated as hydroxycarboxylic acid polymer) is known. In particular, polylactic acid or copolymers of lactic acid and other hydroxycarboxylic acids are 100% biodegradable in the body of animals in months to a year, and when exposed to soil or seawater for several weeks in moist environments. The decomposition product disappears in one to several years after being decomposed, and the decomposed product has the property of being harmless to the human body, such as lactic acid, carbon dioxide, and water.

【０００４】ポリ乳酸は、通常ラクタイドと呼ばれる乳
酸の環状２量体から合成され、その製造法に関してはＵ
ＳＰ１，９９５，９７０、ＵＳＰ２，３６２，５１１、
ＵＳＰ２，６８３，１３６に開示されている。また乳酸
とその他のヒドロキシカルボン酸のコポリマーは、通常
乳酸の環状２量体であるラクタイドとヒドロキシカルボ
ン酸の環状エステル中間体（例えばグリコール酸の２量
体であるグリコライド）から合成され、その製造方法に
関しては、ＵＳＰ３，６３６，９５６とＵＳＰ３，７９
７，４９９に開示されている。Polylactic acid is synthesized from a cyclic dimer of lactic acid, usually called lactide.
SP1,995,970, USP2,362,511,
No. 2,683,136. In addition, copolymers of lactic acid and other hydroxycarboxylic acids are usually synthesized from lactide, which is a cyclic dimer of lactic acid, and a cyclic ester intermediate of hydroxycarboxylic acid (eg, glycolide, which is a dimer of glycolic acid). Regarding the method, USP 3,636,956 and USP 3,795
7,499.

【０００５】しかし、上記分解性ポリマーを廃棄する際
に土中に埋設するためには、一般に遠隔の埋め立て地ま
で運ぶ必要があり、また埋め立てた場合でも分解するま
でにかなりの時間を要し、埋め立てる場所が不足すると
いう問題を直ちに解決することはできない。焼却により
処理する場合でも処理施設までの移送が必要があった
り、特別な焼却炉を廃棄物の発生源近くに備える必要が
ある。さらに、これらのポリマーが腐敗した有機物や病
原性微生物等で汚染されている場合には、廃棄する施設
に運搬するために、臭気や感染を防ぐための特別な配慮
を必要とする。特に、汚染物質が病原性微生物である場
合には、通常の埋め立て処理を行うと汚染の拡大につな
がるため、焼却処理が必須となるが、この場合にはポリ
マーの構成成分であるモノマーを回収することができ
ず、原料が無駄に廃棄されることになる。However, in order to bury the degradable polymer in the soil when discarding it, it is generally necessary to carry it to a remote landfill, and even if it is landfilled, it takes a considerable amount of time to decompose it. There is no immediate solution to the problem of lack of landfills. Even in the case of treatment by incineration, it is necessary to transfer to a treatment facility, or it is necessary to provide a special incinerator near the source of waste. Furthermore, if these polymers are contaminated with spoiled organic matter or pathogenic microorganisms, special care must be taken to prevent odors and infection in order to transport them to a disposal facility. In particular, if the contaminant is a pathogenic microorganism, incineration is essential because normal landfill treatment will lead to an increase in contamination, but in this case, the monomer that is a component of the polymer is recovered. And the raw material is wasted.

【０００６】[0006]

【発明を解決しようとする課題】本発明は、ポリヒドロ
キシカルボン酸系ポリマー、特に、ポリ乳酸系ポリマー
を主成分とする熱可塑性ポリマー組成物を簡単な設備で
安全にヒドロキシカルボン酸モノマーに分解処理して溶
液となし、この溶液中からヒドロキシカルボン酸を回収
し、これを必要により再びポリマー原料として用いる方
法を提供することにある。DISCLOSURE OF THE INVENTION The present invention provides a method for safely decomposing a thermoplastic polymer composition containing a polyhydroxycarboxylic acid-based polymer, particularly a polylactic acid-based polymer as a main component, into a hydroxycarboxylic acid monomer with simple equipment. To provide a method for recovering the hydroxycarboxylic acid from the solution and, if necessary, reusing it as a polymer raw material.

【０００７】[0007]

【課題を解決するための手段】本発明者らは、ヒドロキ
シカルボン酸系ポリマーを主成分とするポリマーの処理
方法を鋭意検討した結果、ヒドロキシカルボン酸系ポリ
マーがｐＨ１０以上のアルカリ溶液中で容易にモノマー
単位にまで分解し、この際にポリマー中のヒドロキシカ
ルボン酸が不斉炭素を持つ場合にはその立体配置を保っ
たまま分解され、この溶液中からヒドロキシカルボン酸
を回収し、それを必要により再びポリマー原料として用
いることができることを見いだし本発明を完成したもの
である。本発明により、ヒドロキシカルボン酸系熱可塑
性ポリマー組成物をアルカリ性溶液中で処理、分解し、
この溶液中からヒドロキシカルボン酸を回収して必要に
より再びポリマー原料として用いる、効率の良い工業的
に有用な方法を提供することができる。また、ポリマー
中のヒドロキシカルボン酸が不斉炭素を持つ場合にはそ
の立体配置を保ったまま回収することができ、再びポリ
マー原料として用いてもポリマー中の光学活性体の割合
を容易に制御することができる。Means for Solving the Problems The present inventors diligently studied a method for treating a polymer containing a hydroxycarboxylic acid-based polymer as a main component. As a result, the hydroxycarboxylic acid-based polymer was easily prepared in an alkaline solution having a pH of 10 or more. When the hydroxycarboxylic acid in the polymer has an asymmetric carbon, it is decomposed while maintaining its configuration, and the hydroxycarboxylic acid is recovered from the solution, and if necessary, it is decomposed into monomer units. The present inventors have found that they can be used again as a polymer raw material, and have completed the present invention. According to the present invention, the hydroxycarboxylic acid-based thermoplastic polymer composition is treated and decomposed in an alkaline solution,
An efficient and industrially useful method of recovering hydroxycarboxylic acid from this solution and using it again as a polymer raw material if necessary can be provided. When the hydroxycarboxylic acid in the polymer has an asymmetric carbon, it can be recovered while maintaining its steric configuration, and the ratio of the optically active substance in the polymer can be easily controlled even when used again as a polymer raw material. be able to.

【０００８】即ち、本発明は、ヒドロキシカルボン酸の
ポリマーまたはコポリマーを主成分とする熱可塑性ポリ
マー組成物をｐＨ１０以上のアルカリ性溶液中でモノマ
ー単位に分解し、この際にポリマー中のヒドロキシカル
ボン酸が不斉炭素を持つ場合にはその立体配置を保った
まま分解され、この溶液中からヒドロキシカルボン酸を
回収し、得られたヒドロキシカルボン酸を必要により再
びポリマー原料として用いる方法である。That is, the present invention decomposes a thermoplastic polymer composition containing a polymer or copolymer of hydroxycarboxylic acid as a main component into monomer units in an alkaline solution having a pH of 10 or more. When the compound has an asymmetric carbon, it is decomposed while maintaining its steric configuration, the hydroxycarboxylic acid is recovered from the solution, and the obtained hydroxycarboxylic acid is used again as a polymer raw material if necessary.

【０００９】本発明に用いられるポリマーは、ヒドロキ
シカルボン酸系ポリマーが主成分として用いられ、ヒド
ロキシカルボン酸としては、乳酸、グリコール酸、３−
ヒドロキシ酪酸、４−ヒドロキシ酪酸、４−ヒドロキシ
吉草酸、５−ヒドロキシ吉草酸、６−ヒドロキシカプロ
ン酸等が用いられる。ヒドロキシカルボン酸系ポリマー
は、（１）ヒドロキシカルボン酸から直接脱水重縮合す
る方法、（２）乳酸の環状２量体であるラクタイドまた
はグリコール酸の環状２量体であるグリコライド（ＧＬ
Ｄ）のような環状２量体を開環重合する方法、（３）ポ
リカプロラクトンのように６−ヒドロキシカプロン酸の
環状エステルであるε−カプロラクトン（ＣＬ）を開環
重合する方法、または（４）それらを混合して開環重合
する方法により得られる。なお、反応原料に環状体を使
用する場合には、回収されたヒドロキシカルボン酸を再
び環状体にする必要がある。The polymer used in the present invention is mainly composed of a hydroxycarboxylic acid-based polymer, and the hydroxycarboxylic acids include lactic acid, glycolic acid, and 3-hydroxycarboxylic acid.
Hydroxybutyric acid, 4-hydroxybutyric acid, 4-hydroxyvaleric acid, 5-hydroxyvaleric acid, 6-hydroxycaproic acid and the like are used. Hydroxycarboxylic acid-based polymers can be obtained by (1) a method of directly dehydrating polycondensation from hydroxycarboxylic acid, (2) lactide which is a cyclic dimer of lactic acid, or glycolide (GL) which is a cyclic dimer of glycolic acid.
Ring-opening polymerization of a cyclic dimer such as D), (3) ring-opening polymerization of ε-caprolactone (CL) which is a cyclic ester of 6-hydroxycaproic acid such as polycaprolactone, or (4) ) They are obtained by a method of mixing and ring-opening polymerization. When a cyclic material is used as a reaction raw material, it is necessary to convert the recovered hydroxycarboxylic acid into a cyclic material again.

【００１０】本発明のヒドロキシカルボン酸系ポリマー
の平均分子量は特に限定されない。強度を必要とする用
途には通常１万〜１００万程度のものが用いられる。１
万以下の分子量ではフィルムや成形物とするには強度が
小さい。また、分子量が１００万より高いと、溶融状態
での粘度が高く成型加工性に劣る。ヒドロキシカルボン
酸系ポリマーは、通常公知の熱可塑性ポリマーまたは可
塑剤、さらに各種の改質剤をが加えられ、熱可塑性ポリ
マー組成物とされる。熱可塑性ポリマー組成物中のヒド
ロキシカルボン酸系ポリマーの占める割合は、目的とす
る分解性により決められるが、一般的には５０％以上が
好ましい。The average molecular weight of the hydroxycarboxylic acid polymer of the present invention is not particularly limited. For applications requiring strength, those having about 10,000 to 1,000,000 are usually used. 1
With a molecular weight of 10,000 or less, the strength is low for forming a film or molded product. On the other hand, when the molecular weight is higher than 1,000,000, the viscosity in the molten state is high and the moldability is poor. The hydroxycarboxylic acid-based polymer is generally added with a known thermoplastic polymer or plasticizer, and further various modifiers, to obtain a thermoplastic polymer composition. The proportion of the hydroxycarboxylic acid-based polymer in the thermoplastic polymer composition is determined by the intended degradability, but is generally preferably 50% or more.

【００１１】本発明において、熱可塑性ポリマー組成物
の分解に用いられるアルカリ性溶液は、無機塩基を水性
溶媒に加えて作ることができる。無機塩基としては、ナ
トリウム、カリウム等のアルカリ金属の水酸化物、酸化
物、炭酸塩等が、また、カルシウム、マグネシウム、バ
リウム等のアルカリ土類金属の水酸化物、酸化物等の水
溶液または懸濁液が使用できる。しかし通常は、経済的
な面及びヒドロキシカルボン酸の回収の面から水酸化ナ
トリウムまたは水酸化カルシウムが好ましい。本発明の
アルカリ水溶液のｐＨは１０以上である。ｐＨ９以下で
はポリマーが完全にモノマーまで加水分解されるまでに
非常に時間がかかり、実用的ではない。アルカリ溶液の
濃度は特に限定されないが、濃度が高い方が分解が速く
好ましい。通常１％以上の濃度で用いられる。溶液はポ
リマーの分解処理に繰り返し用いることができるが、処
理によりアルカリ溶液中のアルカリ成分が消費された場
合には、アルカリ成分を追加して液のアルカリ性をｐＨ
１０以上に保持する必要がある。処理を行う温度は、高
い方がポリマーの分解が速く通常４０℃以上で行われる
が特に限定されない。In the present invention, the alkaline solution used for decomposing the thermoplastic polymer composition can be prepared by adding an inorganic base to an aqueous solvent. Examples of the inorganic base include hydroxides, oxides and carbonates of alkali metals such as sodium and potassium, and aqueous solutions or suspensions of hydroxides and oxides of alkaline earth metals such as calcium, magnesium and barium. Suspensions can be used. However, usually, sodium hydroxide or calcium hydroxide is preferred from the economical viewpoint and the recovery of hydroxycarboxylic acid. The pH of the alkaline aqueous solution of the present invention is 10 or more. At a pH of 9 or less, it takes a very long time until the polymer is completely hydrolyzed to a monomer, which is not practical. The concentration of the alkaline solution is not particularly limited, but the higher the concentration, the faster the decomposition is preferable. Usually, it is used at a concentration of 1% or more. The solution can be used repeatedly to decompose the polymer, but if the alkali component in the alkaline solution is consumed by the treatment, the alkali component is added to increase the pH of the solution to pH.
Must be kept at 10 or more. The higher the temperature at which the treatment is performed, the faster the polymer is decomposed, and the temperature is usually 40 ° C. or higher, but is not particularly limited.

【００１２】本発明のアルカリ水溶液は、アルコール等
の有機溶剤を含んでいても構わない。このようにしてヒ
ドロキシカルボン酸系ポリマーをアルカリ処理して得ら
れた溶液中のヒドロキシカルボン酸は、不斉炭素を持つ
場合にもポリマー中での立体配置を保持している。病院
で用いられるヒドロキシカルボン酸系ポリマーを主成分
とする熱可塑性ポリマー組成物からなる医療用の器具
や、人や動物の***物と接触する用途に用いられるヒド
ロキシカルボン酸系ポリマーを主成分とする熱可塑性ポ
リマー組成物からなる物は病原性物質で汚染されている
可能性があり、廃棄する場合にも特別の配慮が必要であ
るが、本発明の処理方法では、病原性微生物等の汚染物
質で汚染されている場合でも、ポリマーが分解すると同
時に病原性微生物が死滅して汚染が広がるおそれがない
ために好適な処理方法として用いられる。The alkaline aqueous solution of the present invention may contain an organic solvent such as alcohol. The hydroxycarboxylic acid in the solution obtained by subjecting the hydroxycarboxylic acid-based polymer to alkali treatment retains the configuration in the polymer even when it has an asymmetric carbon. Medical equipment consisting of a thermoplastic polymer composition mainly composed of hydroxycarboxylic acid polymer used in hospitals, and hydroxycarboxylic acid polymer mainly used for contact with human and animal excrement The substance comprising the thermoplastic polymer composition may be contaminated with a pathogenic substance, and special consideration is required when disposing the substance. However, in the treatment method of the present invention, a contaminant such as a pathogenic microorganism is used. Is used as a suitable treatment method because there is no possibility that the pathogenic microorganisms will be killed and the contamination spread at the same time as the polymer is decomposed.

【００１３】本発明の処理は、通常のタンク、または攪
拌槽等にアルカリ性溶液を入れ加温しながら、またはそ
のままポリマーの成型物を投入し所定時間保持すること
により行うことができる。投入するポリマー成型物はそ
のままでも細かく破砕あるいは粉砕したものでもよい。The treatment of the present invention can be carried out by placing an alkaline solution in an ordinary tank or a stirring tank or the like while heating, or by charging a polymer molding as it is and keeping it for a predetermined time. The polymer molded product to be charged may be as it is or may be finely crushed or pulverized.

【００１４】本発明の方法において、分解された溶液中
からヒドロキシカルボン酸を回収するには、次の方法が
ある。 （１）水酸化ナトリウム分解−電気透析方法 アルカリ溶液として、水酸化ナトリウム水溶液を用いた
場合には、電気透析を用いると効率よくヒドロキシカル
ボン酸の水溶液が得られる。電気透析はイオン交換膜と
電極を備えた装置により行われる。装置としてはＡｌｌ
ｉｅｄ社のＡｑｕａｔｅｃｈ等が、イオン交換膜として
はナフィオン膜（Ｄｕ Ｐｏｎｔ社商品名）、Ｓｅｌｅ
ｍｉｏｎ膜（旭ガラス社商品名）等が例示される。この
場合に、電気透析装置に供給されるヒドロキシカルボン
酸塩溶液の濃度はできるだけ高い方が効率がよく、アル
カリ溶液で処理した溶液が低い濃度である場合には、あ
らかじめ濃縮してから用いた方がよい。好ましくは、ア
ルカリ溶液での処理をあらかじめヒドロキシカルボン酸
塩の濃度が高くなるように行う。 （２）水酸化カルシウム分解−晶析方法 本発明のヒドロキシカルボン酸が乳酸である場合には、
アルカリ溶液として水酸化カルシウム水溶液または、懸
濁液が用いられる。水酸化カルシウムを用いると、分解
後の溶液からの乳酸カルシウムの単離を効率的に行うこ
とができる。例えば、水酸化カルシウムの水懸濁液にポ
リマーを加えて、撹拌下に５０〜１００℃でポリマーを
完全に分解する。分解後の溶液から未反応の水酸化カル
シウムを濾過等で除く。濾液を冷却することにより析出
した乳酸カルシウムを一旦分離する。次に、この乳酸カ
ルシウムを再び水に溶解した後、水溶液にカルシウムと
当量の硫酸を加えて乳酸を遊離させ、析出した硫酸カル
シウムを濾過して除く。このようにしてカルシウムをほ
とんど含まない乳酸水溶液を得ることができる。得られ
たヒドロキシカルボン酸溶液または乳酸水溶液が、微量
のナトリウム、カルシウム等のカチオンや、硫酸イオン
等のアニオンを含んでおり、高純度の製品が必要な場合
にはさらにイオン交換樹脂等で精製することもできる。In the method of the present invention, the following method can be used to recover the hydroxycarboxylic acid from the decomposed solution. (1) Sodium hydroxide decomposition-electrodialysis method When an aqueous solution of sodium hydroxide is used as the alkaline solution, an aqueous solution of hydroxycarboxylic acid can be efficiently obtained by using electrodialysis. Electrodialysis is performed by a device equipped with an ion exchange membrane and electrodes. The device is All
Aquatech etc. of ied company, Nafion membrane (Du Pont company name), Cell as ion exchange membrane
Mion film (trade name of Asahi Glass Co., Ltd.) is exemplified. In this case, the higher the concentration of the hydroxycarboxylate solution supplied to the electrodialysis device is, the higher the efficiency is. If the concentration of the solution treated with the alkaline solution is low, the concentration should be increased beforehand. Is good. Preferably, the treatment with the alkaline solution is performed in advance so that the concentration of the hydroxycarboxylate is increased. (2) Calcium hydroxide decomposition-crystallization method When the hydroxycarboxylic acid of the present invention is lactic acid,
An aqueous calcium hydroxide solution or suspension is used as the alkaline solution. When calcium hydroxide is used, calcium lactate can be efficiently isolated from the solution after decomposition. For example, the polymer is added to an aqueous suspension of calcium hydroxide and the polymer is completely decomposed at 50-100 ° C. under stirring. Unreacted calcium hydroxide is removed from the solution after decomposition by filtration or the like. The precipitated calcium lactate is once separated by cooling the filtrate. Next, after dissolving the calcium lactate in water again, sulfuric acid equivalent to calcium is added to the aqueous solution to release lactic acid, and the precipitated calcium sulfate is removed by filtration. Thus, an aqueous lactic acid solution containing almost no calcium can be obtained. The obtained hydroxycarboxylic acid solution or lactic acid aqueous solution contains trace amounts of cations such as sodium and calcium, and anions such as sulfate ions. If a high-purity product is required, the product is further purified with an ion exchange resin or the like. You can also.

【００１５】しかし、通常本発明の方法は比較的低温で
行われるため、分解、回収工程での副生物が少なく、ヒ
ドロキシカルボン酸を高純度で回収することができる。
従って、得られたヒドロキシカルボン酸を特に精製する
ことなく再びポリマー原料として用いることができる。
さらに、ヒドロキシカルボン酸が不斉炭素を持つ場合に
は、ポリマー中での立体配置を保持したままヒドロキシ
カルボン酸モノマーとして回収できるために、回収され
たヒドロキシカルボン酸を用いて合成したポリマー中の
光学活性体の割合をコントロールすることが容易であ
る。例えば、Ｌ−乳酸のポリマーからほとんど純粋なＬ
−乳酸が得られ、このＬ−乳酸を用いて合成したポリ乳
酸はほとんどＤ−乳酸を含まない。However, since the method of the present invention is usually carried out at a relatively low temperature, there are few by-products in the decomposition and recovery steps, and the hydroxycarboxylic acid can be recovered with high purity.
Therefore, the obtained hydroxycarboxylic acid can be used again as a polymer raw material without particular purification.
Furthermore, when the hydroxycarboxylic acid has an asymmetric carbon, it can be recovered as a hydroxycarboxylic acid monomer while maintaining the steric configuration in the polymer. It is easy to control the ratio of the active form. For example, from a polymer of L-lactic acid, almost pure L
-Lactic acid is obtained, and the polylactic acid synthesized using this L-lactic acid contains almost no D-lactic acid.

【００１６】[0016]

【実施例】本発明における分子量測定及びＤＬ組成の分
析方法を以下に示す。 （１）分子量の測定方法。 ポリマーの重量平均分子量はポリスチレンを標準として
ゲルパーミエーションクロマトグラフィーにより以下の
条件で測定した。 装置 ：島津ＬＣ−１０ＡＤ 検出器：島津ＲＩＤ−６Ａ カラム：日立化成ＧＬ−Ｓ３５０ＤＴ−５、ＧＬ−Ｓ３
７０ＤＴ−５ 溶媒 ：クロロホルム 濃度 ：１％ 注入量：２０μｌ 流速 ：１．０ｍｌ／ｍｉｎ （２）乳酸のＤＬ組成の分析方法。 ポリマーを５Ｎ水酸化ナトリウム溶液中６０℃で１０時
間保持して加水分解し、得られた溶液中のＬ−乳酸をＬ
−乳酸デヒドロゲナーゼとニコチンアミドアデニンジヌ
クレオチド（以下ＮＡＤと略記する）を作用させ、乳酸
がピルビン酸に酸化される際に生成した、ＮＡＤの還元
型であるＮＡＤＨの量を吸光分析により定量してＬ−乳
酸を定量し、一方、Ｄ−乳酸についても同様にＤ−乳酸
デヒドロゲナーゼとＮＡＤを作用させてＤ−乳酸の量を
求め、Ｌ−乳酸とＤ−乳酸の比を計算することにより求
めた。また、Ｌ−乳酸自体を５Ｎ水酸化ナトリウム溶液
中で１０時間保持して、加水分解条件下で乳酸のラセミ
化がおこらないことを確認した。初めに、実施例で使用
するポリマー及びそのフィルムの製造方法をしめす。The method of measuring the molecular weight and analyzing the DL composition according to the present invention will be described below. (1) Method for measuring molecular weight. The weight average molecular weight of the polymer was measured by gel permeation chromatography using polystyrene as a standard under the following conditions. Apparatus: Shimadzu LC-10AD Detector: Shimadzu RID-6A Column: Hitachi Chemical GL-S350DT-5, GL-S3
70DT-5 Solvent: chloroform Concentration: 1% Injection volume: 20 μl Flow rate: 1.0 ml / min (2) Method for analyzing DL composition of lactic acid. The polymer was hydrolyzed by holding the polymer in a 5N sodium hydroxide solution at 60 ° C. for 10 hours, and L-lactic acid in the obtained solution was converted to L-lactic acid.
Lactate dehydrogenase and nicotinamide adenine dinucleotide (hereinafter abbreviated as NAD) are acted on, and the amount of NADH, which is a reduced form of NAD, produced when lactic acid is oxidized to pyruvate is quantified by absorption spectrometry. -Lactic acid was quantified, and D-lactic acid was similarly treated with D-lactate dehydrogenase and NAD to determine the amount of D-lactic acid, and the ratio of L-lactic acid to D-lactic acid was calculated. In addition, it was confirmed that L-lactic acid itself was kept in a 5N sodium hydroxide solution for 10 hours and racemicization of lactic acid did not occur under hydrolysis conditions. First, the polymer used in the examples and the method for producing the film thereof will be described.

【００１７】製造例１ Ｌ−ラクタイド２１６ｇ（１．５モル）およびオクタン
酸スズ０．０１重量％と、ラウリルアルコール０．０３
重量％を、攪拌機を備えた肉厚の円筒型ステンレス製重
合器へ装入し、真空で２時間脱気した後窒素ガスで置換
した。この混合物を窒素雰囲気下で攪拌しつつ２００℃
で３時間加熱した。温度をそのまま保ちながら、排気管
及びガラス製受器を介して真空ポンプにより徐々に脱気
し反応容器内を３ｍｍＨｇまで減圧にし、脱気開始から
１時間反応させ、モノマーや低分子量揮発分の留出がな
くなった。容器内を窒素置換し、容器下部から得られた
ポリＬ−乳酸を紐状に抜き出し、これをカットしてペレ
ットとした。このペレット化したポリマーの平均分子量
はＭｗ＝１００，０００であり、そのＬ−乳酸とＤ−乳
酸の組成比は９９．５：０．５であった。Production Example 1 216 g (1.5 mol) of L-lactide, 0.01% by weight of tin octoate and 0.03% of lauryl alcohol
% By weight was charged into a thick cylindrical stainless steel polymerization vessel equipped with a stirrer, degassed under vacuum for 2 hours, and then replaced with nitrogen gas. The mixture was stirred at 200 ° C. under a nitrogen atmosphere.
For 3 hours. While maintaining the temperature as it is, slowly deaerate with a vacuum pump through an exhaust pipe and a glass receiver, reduce the pressure in the reaction vessel to 3 mmHg, react for 1 hour from the start of deaeration, and distill monomer and low molecular weight volatile components. I went out. The inside of the container was replaced with nitrogen, and the poly-L-lactic acid obtained from the lower portion of the container was extracted in a string form, and cut into pellets. The average molecular weight of the pelletized polymer was Mw = 100,000, and the composition ratio of L-lactic acid and D-lactic acid was 99.5: 0.5.

【００１８】製造例２ Ｌ−ラクタイド２１６ｇをＬ−ラクタイド１７２ｇとＤ
Ｌ−ラクタイド４４ｇに変えたほかは製造例１と同様に
してペレット化し、ポリ乳酸を得た。このポリマーの平
均分子量はＭｗ＝１００，０００であった。Production Example 2 216 g of L-lactide was added to 172 g of L-lactide and D
Pelletization was performed in the same manner as in Production Example 1 except that L-lactide was changed to 44 g to obtain polylactic acid. The average molecular weight of this polymer was Mw = 100,000.

【００１９】製造例３ Ｌ−ラクタイド２１６ｇをＬ−ラクタイド１０８ｇとグ
リコライド１０８ｇに変えた他は製造例１と同様にして
L-ラクタイド−グリコライド共重合体のペレットを得
た。得られたペレットの平均分子量はＭｗ＝１００，０
００であった。Production Example 3 The procedure of Production Example 1 was repeated except that 216 g of L-lactide was changed to 108 g of L-lactide and 108 g of glycolide.
A pellet of the L-lactide-glycolide copolymer was obtained. The average molecular weight of the obtained pellet was Mw = 100,0.
00.

【００２０】製造例４ Ｌ−ラクタイド２１６ｇをＬ−ラクタイド１０８ｇとε
−カプロラクトン１０８ｇに変えた他は製造例１と同様
にしてL-ラクタイド−ε−カプロラクトン共重合体のペ
レットを得た。得られたペレットの平均分子量はＭｗ＝
７０，０００であった。Production Example 4 216 g of L-lactide was combined with 108 g of L-lactide and ε.
-A pellet of L-lactide-ε-caprolactone copolymer was obtained in the same manner as in Production Example 1 except that the amount was changed to 108 g of caprolactone. The average molecular weight of the obtained pellet was Mw =
70,000.

【００２１】製造例５ ９０％Ｌ−乳酸１０．０ｋｇを１５０℃／５０ｍｍＨｇ
で３時間攪拌しながら水を留出させた後、錫末６．２ｇ
を加え、１５０℃／３０ｍｍＨｇでさらに２時間攪拌し
てオリゴマー化した。このオリゴマーに錫末２８．８ｇ
とジフェニルエーテル２１．１ｋｇを加え、１５０℃／
３５ｍｍＨｇで共沸脱水反応を行い留出した水と溶媒を
水分離器で分離して溶媒のみを反応機に戻した。２時間
後、反応機に戻す有機溶媒を４．６ｋｇのモレキュラシ
ーブ３Ａを充填したカラムに通してから反応機に戻るよ
うにして、１５０℃／３５ｍｍＨｇで４０時間反応を行
い平均分子量Ｍｗ＝１１０，０００のポリ乳酸溶液を得
た。この溶液に脱水したジフェニルエーテル４４ｋｇを
加え希釈した後４０℃まで冷却して、析出した結晶を濾
過し、１０ｋｇのｎ−ヘキサンで３回洗浄して６０℃／
５０ｍｍＨｇで乾燥した。この粉末を０．５Ｎ−ＨＣｌ
１２．ｋｇとエタノール１２．０ｋｇを加え、３５℃で
１時間攪拌した後濾過し、６０℃／５０ｍｍＨｇで乾燥
して、ポリ乳酸粉末６．１ｋｇ（収率８５％）を得た。
この粉末をペレット化機で処理しペレット状にして以下
の試験に用いた。得られたポリマーの平均分子量はＭｗ
＝１１０，０００であり、そのＬ−乳酸とＤ−乳酸の組
成比は９８．５：１．５であった。Production Example 5 10.0 kg of 90% L-lactic acid was added at 150 ° C./50 mmHg.
After distilling water while stirring for 3 hours, 6.2 g of tin powder was obtained.
Was added, and the mixture was further stirred at 150 ° C./30 mmHg for 2 hours to oligomerize. 28.8 g of tin powder was added to this oligomer.
And 21.1 kg of diphenyl ether,
An azeotropic dehydration reaction was performed at 35 mmHg, and distilled water and the solvent were separated by a water separator, and only the solvent was returned to the reactor. After 2 hours, the organic solvent to be returned to the reactor was passed through a column filled with 4.6 kg of molecular sieve 3A, and then returned to the reactor. The reaction was carried out at 150 ° C./35 mmHg for 40 hours, and the average molecular weight Mw = 110,000 Was obtained. The solution was diluted by adding 44 kg of dehydrated diphenyl ether, cooled to 40 ° C., and the precipitated crystals were filtered, washed three times with 10 kg of n-hexane, and washed at 60 ° C. /
Dry at 50 mmHg. This powder is mixed with 0.5N-HCl
12. After adding 1 kg of ethanol and 12.0 kg of ethanol, the mixture was stirred at 35 ° C. for 1 hour, filtered, and dried at 60 ° C./50 mmHg to obtain 6.1 kg of polylactic acid powder (yield: 85%).
This powder was processed by a pelletizer to form a pellet and used in the following tests. The average molecular weight of the obtained polymer is Mw
= 110,000, and the composition ratio of L-lactic acid to D-lactic acid was 98.5: 1.5.

【００２２】製造例６ ９０％Ｌ−乳酸１０．０ｋｇを９０％Ｌ−乳酸９．０ｋ
ｇと７０％グリコール酸１．３ｋｇに変えた他は製造例
５と同様にして重合、ペレット化し、Ｌ−乳酸とグリコ
ール酸の共重合体を得た。このポリマーの平均分子量は
Ｍｗ＝１００，０００であった。以下の実施例で用いた
フィルムは、製造例１〜６で得られたポリマーを濃度約
１０〜２０％になるようにクロロホルムに溶解してガラ
ス板上に塗布し、６０℃減圧下で乾燥することにより得
られた厚さ２５〜３０μのフィルムである。Production Example 6 10.0 kg of 90% L-lactic acid was replaced with 9.0 kg of 90% L-lactic acid.
g and 70% glycolic acid were changed to 1.3 kg, and polymerization and pelletization were carried out in the same manner as in Production Example 5 to obtain a copolymer of L-lactic acid and glycolic acid. The average molecular weight of this polymer was Mw = 100,000. The film used in the following examples was prepared by dissolving the polymers obtained in Production Examples 1 to 6 in chloroform so as to have a concentration of about 10 to 20%, coating the solution on a glass plate, and drying at 60 ° C. under reduced pressure. This is a film having a thickness of 25 to 30 μ obtained as described above.

【００２３】実施例１ 製造例１のポリマーから得られた縦１５０ｍｍ、横１５
０ｍｍ、厚さ３０μｍのフィルムを５０ｍｌの４％水酸
化ナトリウム水溶液に入れ、６０℃で１時間保持した。
フィルムは完全に溶解消滅した。この溶液のｐＨは１２
以上であり、反応液のＨＬＣによる分析の結果、ポリマ
ー中の乳酸単位とほぼ当量の乳酸が生成していた。Example 1 The polymer obtained in Production Example 1 was 150 mm long and 15 mm wide.
A film having a thickness of 0 mm and a thickness of 30 μm was placed in 50 ml of a 4% aqueous sodium hydroxide solution and kept at 60 ° C. for 1 hour.
The film completely dissolved and disappeared. The pH of this solution is 12
As described above, as a result of analysis of the reaction solution by HLC, it was found that lactic acid was produced in an amount equivalent to the lactic acid unit in the polymer.

【００２４】実施例２ 製造例１のポリマーの代わりに製造例２のポリマーを用
いた以外は実施例１と同様の操作を行った。フィルムは
完全に溶解消滅した。この溶液のｐＨは１２以上であ
り、反応液のＨＬＣによる分析の結果、ポリマー中の乳
酸単位とほぼ当量の乳酸が生成していた。Example 2 The same operation as in Example 1 was performed except that the polymer of Production Example 2 was used instead of the polymer of Production Example 1. The film completely dissolved and disappeared. The pH of this solution was 12 or more, and as a result of analysis of the reaction solution by HLC, it was found that lactic acid units were produced in an amount substantially equivalent to the lactic acid units in the polymer.

【００２５】実施例３ ４％水酸化ナトリウムの代わりに５％水酸化カルシウム
を用いた以外は実施例１と同様の操作を行った。１０メ
ッシュのふるいで濾過したところ形状をとどめているフ
ィルムは認められなかった。この溶液のｐＨは１２以上
であり、反応液のＨＬＣによる分析の結果、ポリマー中
の乳酸単位とほぼ当量の乳酸が生成していた。Example 3 The same operation as in Example 1 was performed except that 5% calcium hydroxide was used instead of 4% sodium hydroxide. When the mixture was filtered through a 10-mesh sieve, no film retaining its shape was found. The pH of this solution was 12 or more, and as a result of analysis of the reaction solution by HLC, it was found that lactic acid units were produced in an amount substantially equivalent to the lactic acid units in the polymer.

【００２６】実施例４ 製造例３のポリマーから得られた縦１５０ｍｍ、横１５
０ｍｍ、厚さ２５μｍのフィルムを５０ｍｌの５％アン
モニア水に入れ、４０℃で５時間保持した。フィルムは
完全に溶解消滅した。この溶液のｐＨは１２以上であ
り、反応液のＨＬＣによる分析の結果、ポリマー中の乳
酸単位およびグリコール酸とほぼ当量の乳酸およびグリ
コール酸が生成していた。Example 4 150 mm in length and 15 in width obtained from the polymer of Production Example 3
A film having a thickness of 0 mm and a thickness of 25 μm was placed in 50 ml of 5% aqueous ammonia and kept at 40 ° C. for 5 hours. The film completely dissolved and disappeared. The pH of this solution was 12 or more, and as a result of analysis of the reaction solution by HLC, lactic acid and glycolic acid were formed in approximately equivalent amounts to lactic acid units and glycolic acid in the polymer.

【００２７】実施例５ １５０ｍｍ×１５０ｍｍの製造例４のポリマーから得ら
れた厚さ２５μｍのフィルムを５０ｍｌの１０％水酸化
カリウムに入れ、６０℃で５時間保持した。フィルムは
完全に溶解消滅した。この溶液のｐＨは１２以上であ
り、反応液のＨＬＣによる分析の結果、ポリマー中の乳
酸単位およびε−カプロン酸とほぼ当量の乳酸およびε
−カプロン酸が生成していた。Example 5 A film having a thickness of 25 μm obtained from the polymer of Production Example 4 and measuring 150 mm × 150 mm was placed in 50 ml of 10% potassium hydroxide and kept at 60 ° C. for 5 hours. The film completely dissolved and disappeared. The pH of this solution was 12 or more. As a result of analysis of the reaction solution by HLC, lactic acid units and ε-caproic acid almost equivalent to lactic acid units and
-Caproic acid had formed.

【００２８】実施例６ １５０ｍｍ×１５０ｍｍの製造例１のポリマーから得ら
れた厚さ３０μｍのフィルムに大腸菌を付着させたもの
を５０ｍｌの４％水酸化ナトリウム水溶液に入れ、６０
℃で５時間保持した。フィルムは完全に溶解消滅した。
この溶液のｐＨは１２以上であり、反応液のＨＬＣによ
る分析の結果、ポリマー中の乳酸単位とほぼ当量の乳酸
が生成していた。また、処理後の溶液中に大腸菌は検出
されなかった。Example 6 Escherichia coli adhered to a 30 μm thick film obtained from the polymer of Production Example 1 having a size of 150 mm × 150 mm was placed in 50 ml of a 4% aqueous sodium hydroxide solution.
C. for 5 hours. The film completely dissolved and disappeared.
The pH of this solution was 12 or more. As a result of analysis of the reaction solution by HLC, it was found that lactic acid units were produced in an amount equivalent to the lactic acid units in the polymer. Escherichia coli was not detected in the solution after the treatment.

【００２９】実施例７ 製造例５ のポリマーのペレット２００ｇを５Ｎ水酸化
ナトリウム水溶液１ｌ中、８０℃で２時間保持した。溶
液のｐＨは終始１２以上であり、ペレットは完全に溶解
消滅した。この溶液の一部をとりＨＬＣで分析したとこ
ろ、ポリマー中の乳酸単位とほぼ当量の乳酸が生成して
いた。また、溶液中のＬ−乳酸とＤ−乳酸の比は９８．
５：１．５であり、ポリマー中の乳酸の不斉炭素の立体
配置を保持していた。Example 7 200 g of the polymer pellets of Production Example 5 were kept in 1 liter of a 5N aqueous sodium hydroxide solution at 80 ° C. for 2 hours. The pH of the solution was always 12 or more, and the pellet completely dissolved and disappeared. When a part of this solution was analyzed by HLC, it was found that lactic acid units were formed in an amount equivalent to lactic acid units in the polymer. The ratio of L-lactic acid to D-lactic acid in the solution was 98.
5: 1.5, and the configuration of the asymmetric carbon of lactic acid in the polymer was retained.

【００３０】次に、得られた加水分解溶液を６００ｍｌ
に濃縮し、透析膜に有効面積９ｃｍ ² のＳｅｌｅｍｉｏ
ｎ型ＣＭＲカチオン交換膜（旭硝子製）を使用し、陽
極、陰極を備えたセルを用いて、陽極室にポリマーの加
水分解溶液を入れ、陰極室に水酸化ナトリウムを加え
て、液を循環しながら電気透析することにより、濃度４
３％のＬ−乳酸溶液５５２ｇを得た。収率は９５％（用
いたポリマー換算）であった。この溶液を濃縮し重合用
の乳酸とした。このようにして回収された乳酸モノマー
を使用して、製造例６と同様の方法で重合を行った結
果、平均分子量Ｍｗ＝１００，０００のポリマーを得
た。Next, 600 ml of the obtained hydrolysis solution was used.
Dialysis membrane, effective area 9cm ^Two Sellemio
Using an n-type CMR cation exchange membrane (made by Asahi Glass),
Using a cell with poles and cathodes, add polymer to the anode compartment.
Add the water splitting solution and add sodium hydroxide to the cathode compartment
And electrodialysis while circulating the solution to obtain a concentration of 4
552 g of a 3% L-lactic acid solution was obtained. The yield is 95% (for
Polymer equivalent). Concentrate this solution for polymerization
Lactic acid. Lactic acid monomer recovered in this way
And the polymerization was performed in the same manner as in Production Example 6.
As a result, a polymer having an average molecular weight Mw = 100,000 was obtained.
Was.

【００３１】比較例１ 製造例５のポリマーペレット２０ｇを１Ｎ水酸化ナトリ
ウム溶液と１Ｎ塩酸でｐＨを９に調整した溶液１００ｍ
ｌ中に８０℃で２時間保持した。１５ｇのペレットの殆
どがその形状を保持したままであった。溶液を一部とり
ＨＬＣにより定量した結果、１ｇの乳酸が含まれてい
た。溶液中のＬ−乳酸とＤ−乳酸の比は９８．６：１．
４であった。Comparative Example 1 20 g of the polymer pellets of Production Example 5 were adjusted to a pH of 9 with a 1N sodium hydroxide solution and 1N hydrochloric acid to obtain a 100 m solution.
and kept at 80 ° C. for 2 hours. Most of the 15 g pellets retained their shape. A portion of the solution was quantified by HLC and found to contain 1 g of lactic acid. The ratio of L-lactic acid to D-lactic acid in the solution was 98.6: 1.
It was 4.

【００３２】実施例８ 製造例６のポリマーペレット２００ｇを５Ｎ水酸化ナト
リウム水溶液１ｌ中、８０℃で２時間保持した。ペレッ
トは完全に溶解した。この溶液を６００ｍｌまで濃縮
し、実施例７と同様の装置で分解電気透析し、Ｌ−乳酸
２１７ｇとグリコール酸２４ｇを含んだ５４０ｇの溶液
を得た。この溶液を濃縮し、製造例６と同様の方法で重
合を行った結果、平均分子量９０，０００のポリマーを
得た。Example 8 200 g of the polymer pellets of Production Example 6 were kept at 80 ° C. for 2 hours in 1 L of a 5N aqueous sodium hydroxide solution. The pellet was completely dissolved. This solution was concentrated to 600 ml, and subjected to decomposition electrodialysis with the same device as in Example 7, to obtain a solution of 540 g containing 217 g of L-lactic acid and 24 g of glycolic acid. The solution was concentrated and polymerized in the same manner as in Production Example 6 to obtain a polymer having an average molecular weight of 90,000.

【００３３】実施例９ 製造例１のポリマーペレット１００ｇを、１０％水酸化
カルシウム懸濁液１ｌに加え８０℃で２時間保持した。
溶液のｐＨは終始１２以上であり、ペレットは完全に溶
解消滅した。水酸化カルシウムの不溶分を濾過して除い
た濾液のＨＬＣによる分析の結果、ポリマー中の乳酸単
位にほぼ当量の乳酸が生成しており、また、Ｌ−乳酸と
Ｄ−乳酸の比は９９．５：０．５でポリマー中の乳酸の
立体配置を保持していた。この溶液を濃縮して１０℃で
一晩放置し、析出した乳酸カルシウム結晶を濾過により
単離した。得られた結晶に同量の水を加え６５℃で溶解
し、その溶液に９８％硫酸をカルシウムと等量加えて乳
酸を遊離させ、析出した硫酸カルシウムを濾過した。濾
液を減圧濃縮することにより８８％Ｌ−乳酸水溶液を得
た。収率は８４％であった。この溶液を濃縮し、製造例
６と同様の方法で重合を行った結果、平均分子量１０
０，０００のポリマーを得た。Example 9 100 g of the polymer pellets of Production Example 1 were added to 1 liter of a 10% calcium hydroxide suspension and kept at 80 ° C. for 2 hours.
The pH of the solution was always 12 or more, and the pellet completely dissolved and disappeared. As a result of HLC analysis of the filtrate from which the insolubles of calcium hydroxide were removed by filtration, almost equivalent lactic acid was generated in the lactic acid unit in the polymer, and the ratio of L-lactic acid to D-lactic acid was 99. At 5: 0.5, the configuration of lactic acid in the polymer was retained. The solution was concentrated and allowed to stand at 10 ° C. overnight, and the precipitated calcium lactate crystals were isolated by filtration. The same amount of water was added to the obtained crystals and dissolved at 65 ° C., and 98% sulfuric acid was added in the same amount as calcium to the solution to release lactic acid, and the precipitated calcium sulfate was filtered. The filtrate was concentrated under reduced pressure to obtain an 88% L-lactic acid aqueous solution. The yield was 84%. The solution was concentrated and polymerized in the same manner as in Production Example 6, resulting in an average molecular weight of 10
000 polymer was obtained.

【００３４】[0034]

【発明の効果】本発明の処理方法によれば、分解、回収
工程での副生物が少なく、ヒドロキシカルボン酸を高純
度で回収することができる。従って、得られたヒドロキ
シカルボン酸を特に精製することなく再びポリマー原料
として用いることができる。さらに、ヒドロキシカルボ
ン酸が不斉炭素を持つ場合には、ポリマー中での立体配
置を保持したままヒドロキシカルボン酸モノマーとして
回収できるために、回収されたヒドロキシカルボン酸を
用いて合成したポリマー中の光学活性体の割合をコント
ロールすることができる。According to the treatment method of the present invention, by-products in the decomposition and recovery steps are small, and hydroxycarboxylic acid can be recovered with high purity. Therefore, the obtained hydroxycarboxylic acid can be used again as a polymer raw material without particular purification. Furthermore, when the hydroxycarboxylic acid has an asymmetric carbon, it can be recovered as a hydroxycarboxylic acid monomer while maintaining the steric configuration in the polymer. The proportion of actives can be controlled.

───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平４−313377（ＪＰ，Ａ) 特開 昭63−115845（ＪＰ，Ａ) 米国特許4885387（ＵＳ，Ａ) (58)調査した分野(Int.Cl.⁷，ＤＢ名) C08J 11/10 - 11/16 C07C 51/09 C07C 59/01 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-4-313377 (JP, A) JP-A-63-115845 (JP, A) US Patent 4,853,387 (US, A) (58) Fields studied (Int .Cl. ⁷ , DB name) C08J 11/10-11/16 C07C 51/09 C07C 59/01

Claims (7)

(57)【特許請求の範囲】(57) [Claims] 【請求項１】 ヒドロキシカルボン酸のポリマーまたは
コポリマーを主成分とする熱可塑性ポリマー組成物を、
ｐＨ１０以上のアルカリ性溶液中で分解し、この溶液中
からヒドロキシカルボン酸を回収することを特徴とする
方法。1. A thermoplastic polymer composition based on a polymer or copolymer of a hydroxycarboxylic acid,
A method comprising decomposing in an alkaline solution having a pH of 10 or more and recovering hydroxycarboxylic acid from the solution. 【請求項２】 ヒドロキシカルボン酸が不斉炭素を持つ
場合にポリマー中での立体配置を保持したまま分解し、
回収することを特徴とする請求項１記載の方法。2. When the hydroxycarboxylic acid has an asymmetric carbon, it decomposes while maintaining the configuration in the polymer,
2. The method according to claim 1, wherein the method comprises recovering. 【請求項３】 ヒドロキシカルボン酸が乳酸であること
を特徴とする請求項２記載の方法。3. The method according to claim 2, wherein the hydroxycarboxylic acid is lactic acid. 【請求項４】 熱可塑性ポリマー組成物が汚染物質で汚
染された物であることを特徴とする請求項１記載の方
法。4. The method of claim 1, wherein the thermoplastic polymer composition is contaminated with contaminants. 【請求項５】 ヒドロキシカルボン酸のポリマーまたは
コポリマーを主成分とする熱可塑性ポリマー組成物を、
ｐＨ１０以上の水酸化ナトリウム溶液で分解し、この溶
液中からヒドロキシカルボン酸を電気透析により回収す
ることを特徴とする請求項１記載のヒドロキシカルボン
酸の回収方法。5. A thermoplastic polymer composition based on a hydroxycarboxylic acid polymer or copolymer,
pH10 was decomposed with more sodium hydroxide solution, a method for recovering a hydroxycarboxylic acid of claim 1, wherein the recovered by electrodialysis hydroxycarboxylic acid from the solution. 【請求項６】 乳酸のポリマーを主成分とする熱可塑性
ポリマー組成物を、ｐＨ１０以上の水酸化カルシウム溶
液中で分解し、この溶液中から乳酸カルシウムを分離
し、該乳酸カルシウムに硫酸を加えることにより乳酸に
変換して回収することを特徴とする請求項１記載の乳酸
の回収方法。6. Decomposing a thermoplastic polymer composition containing a lactic acid polymer as a main component in a calcium hydroxide solution having a pH of 10 or more, separating calcium lactate from the solution, and adding sulfuric acid to the calcium lactate. method of recovering lactic acid of claim 1, wherein the recovering is converted to lactic acid by. 【請求項７】 ヒドロキシカルボン酸のポリマーまたは
コポリマーを主成分とする熱可塑性ポリマー組成物を、
ｐＨ１０以上のアルカリ性溶液中で分解し、この溶液中
からヒドロキシカルボン酸を回収し、得られたヒドロキ
シカルボン酸をポリマー原料として用いることを特徴と
する請求項１記載の方法。7. A thermoplastic polymer composition based on a hydroxycarboxylic acid polymer or copolymer,
decomposes at pH10 or more alkaline solution, the solution hydroxycarboxylic acid is recovered from the in process of claim 1 wherein the resulting hydroxycarboxylic acid is characterized by using as the polymeric material.