JP3349140B2 - Rayon fiber containing far-infrared radioactive particles and underwear containing the fiber - Google Patents
Rayon fiber containing far-infrared radioactive particles and underwear containing the fiberInfo
- Publication number
- JP3349140B2 JP3349140B2 JP2000357892A JP2000357892A JP3349140B2 JP 3349140 B2 JP3349140 B2 JP 3349140B2 JP 2000357892 A JP2000357892 A JP 2000357892A JP 2000357892 A JP2000357892 A JP 2000357892A JP 3349140 B2 JP3349140 B2 JP 3349140B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- far
- rayon
- fiber
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は遠赤外線放射性粒子
含有レーヨン系繊維及びその繊維を含有した下着に係
り、その目的は、人体に対して最も効果的とされる波長
の遠赤外線を良好に放射することができ、保温性に優れ
た遠赤外線放射性粒子含有レーヨン系繊維及びその繊維
を含有した下着を提供することにある。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a rayon fiber containing far-infrared ray radiating particles and an undergarment containing the fiber, and an object of the present invention is to satisfactorily radiate far-infrared rays having a wavelength most effective for the human body. It is an object of the present invention to provide a rayon-based fiber containing far-infrared radiation particles excellent in heat retention and an undergarment containing the fiber.
【０００２】[0002]
【従来の技術】３〜１０００μｍ程度の波長を有する遠
赤外線は、物体と接触するとその物体の分子や結晶を振
動させて、物体を温める温熱効果を有することが知られ
ている。しかも、遠赤外線は物体内部に浸透することが
できるために、物体表面を必要以上に加熱することなく
物体内部の温度を上昇させることが可能である。従来か
ら、このような遠赤外線の温熱効果を利用することによ
り保温性に優れた繊維及び衣服の開発が行われている。
この繊維及び衣服においては、遠赤外線を放射する特性
を有する成分を繊維に予め配合しておくことにより、保
温性を高めようと試みられている。2. Description of the Related Art It is known that far-infrared rays having a wavelength of about 3 to 1000 [mu] m have a heating effect of warming an object by vibrating molecules and crystals of the object when it comes into contact with the object. Moreover, since far-infrared rays can penetrate inside the object, it is possible to raise the temperature inside the object without heating the object surface more than necessary. Hitherto, development of fibers and clothes excellent in heat retention by utilizing such a thermal effect of far-infrared rays has been performed.
In these fibers and clothes, attempts have been made to increase the heat retention by preliminarily blending a component having the property of emitting far-infrared rays into the fibers.
【０００３】例えば、遠赤外線を放射する特性を有する
成分が配合された繊維に関する技術として、特開平３−
５１３０１号公報には、３０℃における遠赤外線放射率
が平均６５％以上である粒子を含有した遠赤外線放射層
を有することを特徴とする肌着が開示されている。ま
た、特開平３−１９０９９０号公報には、アルミナ、チ
タン、プラチナからなる遠赤外線放射性粒子が配合され
てなることを特徴とする合成繊維が開示されている。[0003] For example, Japanese Patent Application Laid-Open Publication No. Hei.
No. 51301 discloses an underwear characterized by having a far-infrared radiation layer containing particles having an average of 65% or more of far-infrared emissivity at 30 ° C. JP-A-3-190990 discloses a synthetic fiber characterized by mixing far-infrared radiating particles comprising alumina, titanium and platinum.
【０００４】[0004]
【発明が解決しようとする課題】上記のいずれの技術に
おいても、遠赤外線放射性粒子が含有される合成繊維と
しては、ポリエチレン系繊維やポリアミド系繊維等が用
いられていた。この理由は、ポリエチレン系繊維やポリ
アミド系繊維は、この他の合成繊維に比べて、遠赤外線
の透過性に優れるからであり、この他の合成繊維を使用
した場合、遠赤外線放射性粒子から放射された遠赤外線
が合成繊維に吸収されてしまい、このために、実質的な
遠赤外線の放射量が減少して保温効果を発揮することが
できないからである。また、従来の遠赤外線放射性粒子
は、十分満足できる効果を得ることができるほど遠赤外
線が放射されているとは言えず、この面からも遠赤外線
の透過性に優れた繊維を使用する必要があった。In any of the above techniques, polyethylene fibers, polyamide fibers, and the like have been used as synthetic fibers containing far-infrared radiation particles. The reason is that polyethylene fibers and polyamide fibers are more excellent in the transmission of far-infrared rays than other synthetic fibers, and when other synthetic fibers are used, they are radiated from far-infrared radiation particles. This is because the far infrared rays are absorbed by the synthetic fibers, and the radiation amount of the far infrared rays is substantially reduced, so that the heat retaining effect cannot be exhibited. In addition, conventional far-infrared radiating particles cannot be said to emit far-infrared rays so as to obtain a sufficiently satisfactory effect, and it is necessary to use fibers having excellent far-infrared transmittance from this aspect. there were.
【０００５】一方、近年、レーヨン系繊維の消費量が増
加している。この理由としては、ＡＶ加工、Ｒ加工、形
態安定加工等の各種加工技術が創出されたこと、またレ
ーヨン系繊維の持つ風合いの良さや、原材料としてパル
プ等の天然の素材を使用するといった面が消費者に見直
されたこと、さらには、他の繊維との混紡に適している
こと等を挙げることができる。On the other hand, in recent years, the consumption of rayon-based fibers has increased. The reasons for this are the creation of various processing technologies such as AV processing, R processing and morphological stability processing, the good texture of rayon-based fibers, and the use of natural materials such as pulp as raw materials. It can be mentioned that it has been reviewed by consumers and that it is suitable for blending with other fibers.
【０００６】本発明者らは、このように優れた特性を有
するレーヨン系繊維に、遠赤外線放射性粒子を含有させ
て、優れた保温特性を有するレーヨン系繊維を開発する
べく鋭意研究を行った結果、特定の製造段階において遠
赤外線放射性粒子を配合することにより、紡糸した後も
繊維から遠赤外線放射性粒子が脱落することなく、しっ
かりと繊維に含有されるとともに、遠赤外線が十分放射
されて満足できる保温効果が得られることを見いだし本
発明の完成に至った。The present inventors have conducted intensive studies to develop rayon-based fibers having excellent heat retention properties by incorporating far-infrared radiation particles into rayon-based fibers having such excellent properties. By blending the far-infrared radiation particles at a specific manufacturing stage, the far-infrared radiation particles do not fall off from the fiber even after spinning, are firmly contained in the fiber, and the far-infrared ray is sufficiently radiated and satisfactory. The inventors have found that a heat retaining effect can be obtained, and have completed the present invention.
【０００７】[0007]
【課題を解決するための手段】即ち、請求項１に係る発
明は、１０〜３０重量％のアルミナ（Ａｌ２Ｏ３）と、
４５〜７０重量％のシリカ（ＳｉＯ２）と、５〜２０重
量％のマグネシア（ＭｇＯ）と、５〜２０重量％の酸化
カルシウム（ＣａＯ）と、０．８〜２重量％のプラチナ
（Ｐｔ）とからなる遠赤外線放射性粒子が含有されてな
ることを特徴とするレーヨン系繊維に関する。請求項２
に係る発明は、１０〜２０重量％のアルミナ（Ａｌ ２ Ｏ
３ ）と、４５〜６０重量％のシリカ（ＳｉＯ ２ ）と、１
０〜２０重量％のマグネシア（ＭｇＯ）と、１０〜２０
重量％の酸化カルシウム（ＣａＯ）と、８〜１５重量％
の二酸化チタン（ＴｉＯ ２ ）と、０．８〜２重量％のプ
ラチナ（Ｐｔ）とからなる遠赤外線放射性粒子が含有さ
れてなることを特徴とするレーヨン系繊維に関する。請
求項３に係る発明は、ジルコニア、酸化クロム、フェラ
イト、スピネル、セリウム、バリウム、炭化ホウ素、炭
化ケイ素、炭化チタン、炭化モリブデン、炭化タングス
テン、窒化ホウ素、窒化アルミニウム、窒化ケイ素、窒
化ジルコニウム、炭素、グラファイト、タングステン、
モリブデン、バナジウム、タンタル、マンガン、ニッケ
ル、酸化銅、酸化鉄から選択される任意の成分が１〜１
５重量％配合されてなることを特徴とする請求項１又は
２に記載のレーヨン系繊維に関する。請求項４に係る発
明は、請求項１乃至３のいずれかに記載のレーヨン系繊
維が含有されてなることを特徴とする下着に関する。請
求項５に係る発明は、天然繊維及び／又は合成繊維が混
紡されてなることを特徴とする請求項４に記載の下着に
関する。請求項６に係る発明は、天然繊維及び／又は合
成繊維が人体との接面側に配置するように混紡されてな
ることを特徴とする請求項５に記載の下着に関する。請
求項７に係る発明は、天然繊維及び／又は合成繊維が人
体との反接面側に配置するように混紡されてなることを
特徴とする請求項５に記載の下着に関する。 SUMMARY OF THE INVENTION That is, the invention according to claim 1, 10 to 30 wt% of alumina (Al 2 O 3),
45-70 wt% silica and (SiO 2), 5~20 double
Amount% of magnesia (MgO), and 5 to 20 wt% of calcium oxide (CaO), and characterized in that the far-infrared radiation particles consisting the 0.8 to 2 wt% of platinum (Pt) is formed by containing Rayon fiber. Claim 2
The present invention relates to 10 to 20% by weight of alumina (Al 2 O).
3 ), 45-60% by weight of silica (SiO 2 ), 1
0-20% by weight of magnesia (MgO);
Weight percent calcium oxide (CaO) and 8 to 15 weight percent
Titanium dioxide (TiO 2 ) and 0.8 to 2 wt%
Contains far-infrared radioactive particles consisting of platinum (Pt)
The present invention relates to a rayon-based fiber characterized by the fact that Contract
The invention according to claim 3 comprises zirconia, chromium oxide, ferrous
Light, spinel, cerium, barium, boron carbide, charcoal
Silicon carbide, titanium carbide, molybdenum carbide, tungsten carbide
Ten, boron nitride, aluminum nitride, silicon nitride, nitride
Zirconium oxide, carbon, graphite, tungsten,
Molybdenum, vanadium, tantalum, manganese, nickel
, An arbitrary component selected from copper oxide and iron oxide is 1 to 1
5. The composition according to claim 1, wherein 5% by weight is blended.
2. The rayon-based fiber according to item 2. Claim 4
Akira is a rayon-based fiber according to any one of claims 1 to 3.
The present invention relates to underwear characterized by containing fibers. Contract
The invention according to claim 5 is characterized in that natural fibers and / or synthetic fibers are mixed.
The underwear according to claim 4, which is spun.
Related. The invention according to claim 6 relates to natural fibers and / or synthetic fibers.
Make sure that the synthetic fibers are not blended so that they are placed on the surface in contact with the human body.
The undergarment according to claim 5, characterized in that: Contract
The invention according to claim 7 is characterized in that natural fibers and / or synthetic fibers are human.
Being blended so that it is placed on the side opposite to the body
An undergarment according to claim 5, characterized in that:
【０００８】[0008]
【発明の実施の形態】以下、本発明について詳細に説明
する。本発明に係る遠赤外線放射性粒子含有レーヨン系
繊維には、遠赤外線放射性粒子が含有されている。遠赤
外線放射性粒子とは、常温において遠赤外線を放射する
ことができる粒子、より好ましくは常温において人体に
有効な波長とされる４〜１２μｍ程度の遠赤外線を放射
することができる粒子のことである。本発明では遠赤外
線放射性粒子として、アルミナ（Ａｌ2 Ｏ3 ）、シリカ
（ＳｉＯ2 ）、マグネシア（ＭｇＯ）、酸化カルシウム
（ＣａＯ）、二酸化チタン（ＴｉＯ2 ）のうちから選択
された一種以上の金属酸化物と、プラチナ（Ｐｔ）が配
合されている。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail. The far-infrared radiation-containing fiber according to the present invention contains far-infrared radiation particles. The far-infrared radiation particles are particles capable of emitting far-infrared rays at room temperature, more preferably particles capable of emitting far-infrared rays of about 4 to 12 μm which are effective wavelengths for the human body at room temperature. . In the present invention, as the far-infrared radiation particles, at least one metal selected from alumina (Al 2 O 3 ), silica (SiO 2 ), magnesia (MgO), calcium oxide (CaO), and titanium dioxide (TiO 2 ) Oxide and platinum (Pt) are blended.
【０００９】配合されるアルミナ、シリカ、二酸化チタ
ン、マグネシア、酸化カルシウムの粒径は、レーヨン系
繊維の太さに応じて任意に設定することができるが、通
常の場合、それぞれ、０．１〜１５μｍ、好ましくは
０．１〜５μｍ、より好ましくは０．２〜１．５μｍと
される。The particle size of the alumina, silica, titanium dioxide, magnesia and calcium oxide to be blended can be arbitrarily set according to the thickness of the rayon-based fiber. It is 15 μm, preferably 0.1 to 5 μm, and more preferably 0.2 to 1.5 μm.
【００１０】また、配合されるプラチナの粒径は特に限
定されないが、０．１〜５μｍ、より好ましくは０．３
〜０．５μｍとされる。また、プラチナの配合量は特に
限定されないが、遠赤外線放射性粒子全量中、０．５〜
３重量％、好ましくは０．８〜２重量％とされる。[0010] The particle size of platinum to be compounded is not particularly limited, but is preferably 0.1 to 5 µm, more preferably 0.3 to 5 µm.
０．５0.5 μm. Further, the amount of platinum is not particularly limited, but in the total amount of far-infrared radiation particles, 0.5 to
The content is 3% by weight, preferably 0.8 to 2% by weight.
【００１１】尚、本発明においては、１０〜３０重量％
のアルミナと、４５〜７０重量％のシリカと、５〜２０
重量％のマグネシアと、５〜２０重量％の酸化カルシウ
ムと、０．８〜２重量％のプラチナとからなる遠赤外線
放射性粒子を用いることが好ましく、更には、１０〜２
０重量％のアルミナと、４５〜６０重量％のシリカと、
１０〜２０重量％のマグネシアと、１０〜２０重量％の
酸化カルシウムと、８〜１５重量％の二酸化チタンと、
０．８〜２重量％のプラチナとからなる遠赤外線放射性
粒子を用いることが好ましい。この理由は、各成分の配
合量を前述の通りに調整することにより、常温において
遠赤外線が十分放射されて保温効果を十分に発揮するこ
とができるからである。In the present invention, 10 to 30% by weight is used.
Of alumina, 45-70% by weight of silica and 5-20
It is preferable to use far-infrared radiation particles composed of magnesia by weight, 5 to 20% by weight of calcium oxide, and 0.8 to 2% by weight of platinum.
0% by weight alumina, 45-60% by weight silica,
10-20% by weight of magnesia, 10-20% by weight of calcium oxide, 8-15% by weight of titanium dioxide,
It is preferable to use far-infrared radiation particles composed of 0.8 to 2% by weight of platinum. The reason for this is that by adjusting the amount of each component as described above, far infrared rays can be sufficiently emitted at room temperature and the heat retaining effect can be sufficiently exhibited.
【００１２】さらに、本発明においては、以上説明した
成分のほか、ジルコニア、酸化クロム、フェライト、ス
ピネル、セリウム、バリウム、炭化ホウ素、炭化ケイ
素、炭化チタン、炭化モリブデン、炭化タングステン、
窒化ホウ素、窒化アルミニウム、窒化ケイ素、窒化ジル
コニウム、炭素、グラファイト、タングステン、モリブ
デン、バナジウム、タンタル、マンガン、ニッケル、酸
化銅、酸化鉄等を適宜任意に配合することができる。こ
れらの任意の成分の配合量は特に限定されないが、遠赤
外線放射性粒子全量中、１〜１５重量％、好ましくは２
〜１０重量％とされる。また、その粒径も特に限定され
ず、レーヨン系繊維の太さに応じて任意に設定すること
ができるが、通常の場合、０．１〜１５μｍ、好ましく
は０．１〜５μｍ、より好ましくは０．２〜１．５μｍ
とされる。Further, in the present invention, in addition to the components described above, zirconia, chromium oxide, ferrite, spinel, cerium, barium, boron carbide, silicon carbide, titanium carbide, molybdenum carbide, tungsten carbide,
Boron nitride, aluminum nitride, silicon nitride, zirconium nitride, carbon, graphite, tungsten, molybdenum, vanadium, tantalum, manganese, nickel, copper oxide, iron oxide, and the like can be appropriately compounded. The mixing amount of these optional components is not particularly limited, but is 1 to 15% by weight, preferably 2
To 10% by weight. In addition, the particle size is not particularly limited, and can be arbitrarily set according to the thickness of the rayon-based fiber, but is usually 0.1 to 15 μm, preferably 0.1 to 5 μm, more preferably 0.2-1.5 μm
It is said.
【００１３】以上説明した構成からなる遠赤外線放射性
粒子は、人体に対して有効な波長とされる４〜１２μｍ
前後の遠赤外線を常温において安定して、しかも人体に
対して十分な効果が発現される程度に放射される。The far-infrared radiating particles having the above-described structure have a wavelength of 4 to 12 μm which is effective for the human body.
The front and rear far infrared rays are radiated stably at room temperature and to such an extent that a sufficient effect is exerted on the human body.
【００１４】以上説明した遠赤外線放射性粒子をレーヨ
ン系繊維に含有させることにより、本発明に係る遠赤外
線放射性粒子含有レーヨン系繊維とすることができる。
尚、本発明におけるレーヨン系繊維とは、レーヨン、銅
アンモニアレーヨン（キュプラ）、精製セルロースのこ
とである。本発明においてレーヨン系繊維に遠赤外線放
射性粒子が含有される理由は、レーヨン系繊維は、この
他のあらゆる繊維材料との混紡に適しており、遠赤外線
放射性粒子含有レーヨン系繊維を他の繊維材料に混紡す
ることにより、あらゆる繊維材料に容易に保温性を保持
させることができるからである。また、この他の繊維の
場合、遠赤外線放射性粒子の必須成分であるプラチナが
繊維中に含有されずに、紡糸する際に脱落することがあ
るが、レーヨン系繊維の場合、脱落することなく、繊維
中にしっかりと含有されるからである。The rayon-based fibers according to the present invention can be obtained by incorporating the far-infrared radiation particles described above into rayon-based fibers.
The rayon-based fibers in the present invention are rayon, cuprammonium rayon (cupra), and purified cellulose. The reason that the rayon-based fiber contains far-infrared ray-emitting particles in the present invention is that rayon-based fiber is suitable for blending with any other fiber material, and that the rayon-based fiber containing far-infrared ray-emitting particles is mixed with another fiber material. This is because, by blending the fibers, heat retention can be easily maintained in any fiber material. In addition, in the case of other fibers, platinum, which is an essential component of far-infrared radiation particles, is not contained in the fibers and may fall off during spinning, but in the case of rayon-based fibers, without falling off, This is because it is firmly contained in the fiber.
【００１５】以下、レーヨン系繊維に遠赤外線放射性粒
子を含有させる方法について具体的に説明する。まず、
遠赤外線放射性粒子をレーヨンに含有させる場合につい
て説明する。レーヨンに遠赤外線放射性粒子を含有させ
るには、湿式紡糸する前の紡糸原液中に遠赤外線放射性
粒子を分散状態で混合した後に、常法に従いこの原液を
紡糸してレーヨンとすればよい。即ち、レーヨンの原材
料である木材パルプ等から製造されるアルカリセルロー
スを二硫化炭素と反応させた後に、得られる繊維素キサ
ントゲン酸ソーダを水酸化ナトリウム水溶液に溶解させ
てビスコース液を製造する硫化溶解工程において遠赤外
線放射性粒子を配合すればよい。また、前記の硫化溶解
工程により得られたビスコース液を熟成させる際に行わ
れる脱泡工程において添加することもできる。Hereinafter, a method for incorporating far-infrared radiation particles into rayon-based fibers will be specifically described. First,
The case where far-infrared radiation particles are contained in rayon will be described. In order to make the rayon contain far-infrared ray-emitting particles, the far-infrared ray-emitting particles are mixed in a dispersion state in a spinning solution before wet spinning, and then the stock solution is spun according to a conventional method to form rayon. That is, after reacting alkali cellulose produced from wood pulp or the like, which is a raw material of rayon, with carbon disulfide, the obtained cellulose xanthate is dissolved in an aqueous sodium hydroxide solution to produce a viscose solution. In the process, far-infrared radiation particles may be blended. Further, it can also be added in a defoaming step performed when the viscose liquid obtained in the above-mentioned sulfide dissolution step is aged.
【００１６】遠赤外線放射性粒子の配合量は特に限定さ
れず、常温において人体に有効な波長であるとされる４
〜１２μｍ前後の遠赤外線を放射して良好な保温性を発
揮できる配合量であって、下着の構成繊維材料として紡
糸可能な範囲内であれば、任意の配合量が採用される。
具体的には、１〜１５重量％、好ましくは５〜１０重量
％とされる。尚、前記の遠赤外線放射性粒子が配合され
たビスコース液からビスコースレーヨンを紡糸すること
も、またレーヨンステープルを紡糸することも可能であ
る。即ち、ビスコース液を紡糸口から押し出し、硫酸、
硫酸ソーダ等からなる凝固浴を通過させて固化して繊維
状に再生させた後に、得られた繊維を精製、洗浄、漂
白、乾燥等することによりビスコースレーヨンを得るこ
とができる。また、ビスコース液を紡糸口から押し出し
た後に、集束、切断して精錬することによりレーヨンス
テープルとすることもできる。The amount of the far-infrared radiation particles is not particularly limited, and is considered to be a wavelength effective for the human body at normal temperature.
Any compounding amount can be used as long as it is a compounding amount capable of radiating far-infrared rays of about 12 μm and exhibiting good heat retention and within a range in which spinning is possible as a constituent fiber material of underwear.
Specifically, the content is 1 to 15% by weight, preferably 5 to 10% by weight. The viscose rayon can be spun from the viscose liquid containing the above-mentioned far-infrared radiation particles, and the rayon staple can be spun. That is, the viscose liquid is extruded from the spinning port, sulfuric acid,
Viscose rayon can be obtained by passing through a coagulation bath made of sodium sulfate or the like, solidifying and regenerating into a fibrous form, and then purifying, washing, bleaching, and drying the obtained fiber. Rayon staples can also be obtained by extruding the viscose liquid from the spinning port, then bundling, cutting and refining.
【００１７】次に、遠赤外線放射性粒子を銅アンモニア
レーヨンに含有させる場合について説明する。銅アンモ
ニアレーヨンに遠赤外線放射性粒子を含有させるには、
湿式紡糸する前の紡糸原液中に遠赤外線放射性粒子を分
散状態で混合した後に、常法に従いこの原液を紡糸して
銅アンモニアレーヨンとすればよい。即ち、銅アンモニ
アレーヨンの原材料である綿やリンターから製造される
精製リンターを、酸化銅アンモニア溶液に溶解して紡糸
原液とする際に、遠赤外線放射性粒子を添加すればよ
い。また、前記得られた紡糸原液を紡糸する前に行われ
る脱泡工程において添加することも可能である。尚、前
記の遠赤外線放射性粒子が含有された紡糸原液からキュ
プラステープル及びキュプラフィラメントのいずれも製
造することができる。以上説明した以外の構成について
は、上記のレーヨンに遠赤外線放射性粒子を含有させる
場合と同様であり説明を省略する。Next, the case where far-infrared radiation particles are contained in copper ammonia rayon will be described. To include far-infrared radioactive particles in copper ammonia rayon,
After the far-infrared radiation particles are mixed in a dispersed state in the spinning solution before wet spinning, the stock solution may be spun according to a conventional method to obtain copper ammonia rayon. That is, far-infrared radiation particles may be added when a purified linter manufactured from cotton or linter, which is a raw material of copper ammonia rayon, is dissolved in a copper oxide ammonia solution to form a spinning solution. Further, it can be added in a defoaming step performed before spinning the obtained spinning stock solution. In addition, both cupless staples and cupra filaments can be manufactured from the spinning dope containing the far-infrared radiation particles. The configuration other than that described above is the same as the case where the above-described rayon contains far-infrared ray-emitting particles, and the description is omitted.
【００１８】次に、遠赤外線放射性粒子を精製セルロー
スに含有させる場合について説明する。精製セルロース
に遠赤外線放射性粒子を含有させるには、湿式紡糸する
前の紡糸原液中に遠赤外線放射性粒子を分散状態で混合
した後に、常法に従いこの原液を紡糸して精製セルロー
スとすればよい。即ち、精製セルロースの原材料である
木材パルプ等を直接溶剤に溶解させて紡糸原液を製造す
る際に遠赤外線放射性粒子を配合すればよい。また、前
記得られた紡糸原液を紡糸する前に行われる脱泡工程に
おいて添加することも可能である。尚、前記の遠赤外線
放射性粒子が含有された紡糸原液からステープル及びフ
ィラメントのいずれも製造することができる。以上説明
した以外の構成については、上記のレーヨンに遠赤外線
放射性粒子を含有させる場合と同様であり説明を省略す
る。Next, the case where far-infrared radiation particles are contained in purified cellulose will be described. In order to make the purified cellulose contain far-infrared radiation particles, the far-infrared radiation particles are mixed in a dispersion state in a spinning solution before wet spinning, and then the stock solution is spun according to a conventional method to obtain purified cellulose. That is, far-infrared radiation particles may be blended when a raw spinning solution is produced by directly dissolving wood pulp or the like, which is a raw material of purified cellulose, in a solvent. Further, it can be added in a defoaming step performed before spinning the obtained spinning stock solution. Both staples and filaments can be produced from the spinning dope containing the far-infrared radiation particles. The configuration other than that described above is the same as the case where the above-described rayon contains far-infrared ray-emitting particles, and the description is omitted.
【００１９】さらに、以上説明した方法により製造され
た遠赤外線放射性粒子含有レーヨン系繊維は、他の繊維
材料と混紡されて、常法に従って下着とされる。遠赤外
線放射性粒子含有レーヨン系繊維と混紡される他の繊維
材料としては、綿、麻、絹、ウール等の天然繊維、蛋白
繊維、アクリル、ポリエステル、ナイロン、アセテー
ト、ビニロン、ポリプロピレン、ポリ塩化ビニル、ポリ
エチレン等の合成繊維を例示することができるが、特に
限定されない。また、遠赤外線放射性粒子含有レーヨン
系繊維を他の繊維材料と混紡する場合、遠赤外線放射性
粒子含有レーヨン系繊維の配合量は特に限定されない
が、通常の場合、２重量％以上、好ましくは２〜５０重
量％となるように用いることが好ましい。この理由は、
遠赤外線放射性粒子含有レーヨン系繊維の配合量が２重
量％未満の場合、遠赤外線放射性粒子含有レーヨン系繊
維から放射される遠赤外線の量が少なく、保温性が発揮
されないために、好ましくないからである。Further, the rayon-based fiber containing far-infrared ray-emitting particles produced by the above-described method is blended with another fiber material and made into an undergarment according to a conventional method. Other fiber materials blended with far-infrared radioactive particle-containing rayon fibers include cotton, hemp, silk, wool and other natural fibers, protein fibers, acrylic, polyester, nylon, acetate, vinylon, polypropylene, polyvinyl chloride, Synthetic fibers such as polyethylene can be exemplified, but are not particularly limited. Further, when the rayon-based fiber containing far-infrared radiation particles is blended with another fiber material, the amount of the rayon-based fiber containing far-infrared radiation particles is not particularly limited, but is usually 2% by weight or more, preferably 2 to 2% by weight. It is preferable to use 50% by weight. The reason for this is
If the content of the rayon-based fiber containing far-infrared ray-emitting particles is less than 2% by weight, the amount of far-infrared ray emitted from the rayon-based fiber containing far-infrared ray-emitting particles is small, and heat retention is not exhibited. is there.
【００２０】遠赤外線放射性粒子を配合したレーヨン系
繊維とこの他の繊維を混紡する場合、レーヨン系繊維を
着用者の皮膚と直接接触することができるように、即
ち、着用者の接面側となるように混紡することもでき
る。また、遠赤外線放射性粒子を配合したレーヨン系繊
維とこの他の繊維を混紡する場合、レーヨン系繊維を着
用者の皮膚と直接接触することないように、着用者の反
接面側となるように混紡することもできる。レーヨン系
繊維を着用者の皮膚の接面側に配置するように混紡する
ことにより、遠赤外線放射性粒子から放射された遠赤外
線を効果的に着用者の皮膚に放射されることとなる。こ
のために、遠赤外線の温熱効果を効率的に得ることがで
き、特に、冬用の下着に好適に用いることができる。ま
た、レーヨン系繊維を着用者の皮膚の反接面側に配置す
るように混紡することにより、着用者の皮膚とレーヨン
系繊維が直接接触することを避けることができる。こう
することにより、特にアレルギー症状を呈する人が安心
して着用することができる。また、夏用の下着に好適に
用いることができる。製造される下着としては特に限定
されず、アンダーシャツ、ランニングシャツ、ブリー
フ、パンツ、ズボン下、ショーツ、タンクトップ、パン
ティーホース、７分袖、フレンチ袖、ボディスーツ、ガ
ードル、腹巻、靴下等の通常の男性用下着、女性用肌着
を例示することができる。When a rayon-based fiber containing far-infrared radiation particles is blended with another fiber, the rayon-based fiber can be brought into direct contact with the wearer's skin, that is, the rayon-based fiber is in contact with the wearer's contact surface. It is also possible to make a blend. In addition, when blending rayon-based fibers containing far-infrared radiation particles and other fibers, so that the rayon-based fibers do not come into direct contact with the wearer's skin, so as to be on the non-contact side of the wearer. It can be blended. By blending the rayon-based fibers so as to be arranged on the contact surface side of the wearer's skin, far-infrared rays emitted from the far-infrared radiating particles are effectively radiated to the wearer's skin. For this reason, the thermal effect of far-infrared rays can be efficiently obtained, and particularly, it can be suitably used for winter underwear. In addition, by blending the rayon-based fibers so as to be arranged on the non-contact side of the skin of the wearer, direct contact between the skin of the wearer and the rayon-based fibers can be avoided. By doing so, a person exhibiting allergic symptoms can wear it with confidence. Further, it can be suitably used for summer underwear. The undergarments to be manufactured are not particularly limited, and include ordinary undershirts, running shirts, briefs, pants, pants, shorts, tank tops, panty hoses, seven-quarter sleeves, French sleeves, body suits, girdle, belly bands, socks, and the like. Men's underwear and women's underwear can be exemplified.
【００２１】[0021]
【実施例】以下、本発明を実施例を示してより詳細に説
明する。但し、本発明は以下の実施例により何ら限定さ
れるものではない。 （実施例の試料の調製）アルミナ２０重量％、シリカ５
０重量％、マグネシア１０重量％、酸化カルシウム１０
重量％、二酸化チタン８重量％、プラチナ２重量％から
なる金属を１０重量％配合したレーヨン系繊維２０重量
％と、綿・ナイロン・ポリウレタン８０重量％を混紡し
て通常の方法により製造した女性用肌着を実施例１の試
料とした。また、アルミナ２０重量％、シリカ５０重量
％、マグネシア１０重量％、酸化カルシウム１０重量
％、二酸化チタン８重量％、プラチナ２重量％からなる
金属を１０重量％配合したレーヨン系繊維２０重量％
と、ナイロン・ポリウレタン８０重量％を混紡して通常
の方法により製造したボディスーツを実施例２の試料と
した。 （比較例の試料の調製）前記実施例１の試料の調製に使
用したレーヨン系繊維（金属は配合せず）と綿・ナイロ
ン・ポリウレタンを混紡して通常の方法により製造した
女性用肌着を比較例１の試料とした。また、実施例２の
試料の調製に使用したレーヨン系繊維（金属は配合せ
ず）とナイロン・ポリウレタンを混紡して通常の方法に
より製造したボディスーツを比較例２の試料とした。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in more detail with reference to embodiments. However, the present invention is not limited at all by the following examples. (Preparation of Samples in Examples) Alumina 20% by weight, silica 5
0% by weight, magnesia 10% by weight, calcium oxide 10
20% by weight of rayon fiber blended with 10% by weight of a metal consisting of 8% by weight of titanium dioxide, 8% by weight of titanium dioxide and 2% by weight of platinum, and 80% by weight of cotton, nylon and polyurethane for a woman manufactured by a usual method. Underwear was used as the sample of Example 1. 20% by weight of rayon-based fiber containing 10% by weight of a metal consisting of 20% by weight of alumina, 50% by weight of silica, 10% by weight of magnesia, 10% by weight of calcium oxide, 8% by weight of titanium dioxide and 2% by weight of platinum
And a body suit manufactured by blending 80% by weight of nylon and polyurethane with a conventional method. (Preparation of Samples of Comparative Example) A comparison is made between women's underwear produced by blending rayon-based fibers (without mixing of metal) and cotton, nylon and polyurethane used in the preparation of the samples of Example 1 according to a conventional method. The sample of Example 1 was used. Further, a bodysuit manufactured by blending the rayon-based fiber (without blending metal) and nylon / polyurethane used in the preparation of the sample of Example 2 by a usual method was used as a sample of Comparative Example 2.
【００２２】（試験例１；皮膚血流量の変化）二名の健
常女性被験者（被験者Ａ；２０歳、被験者Ｂ；２３歳）
に上記の各試料を着用してもらい、被験者の指部皮膚血
流量の変化をレーザードップラー法により測定した。測
定方法は、まず、被験者二名を少なくとも試験開始３０
分前から安静状態にし、外部刺激の影響を受けないよう
にした。実施例又は比較例の各試料を着用する前及び着
用後にわたってレーザードップラー血流計ＦＬＯ−１
（オメガウェーブ社製）、生体信号処理装置ＤＰ−１１
００Ａ（日本電気三栄社製）を用いて、動静脈吻合の組
織血流量を計測し、６０００ポイント／ｍｉｎ．を平均
して１分間のデータ値として血流変化率を算出した。被
験者Ａが実施例１及び比較例１を着用した場合の結果を
図１に、被験者Ｂが実施例１及び比較例１を着用した場
合の結果を図２に、被験者Ａが実施例２及び比較例２を
着用した場合の結果を図３に、被験者Ｂが実施例２及び
比較例２を着用した場合の結果を図４に、それぞれ示
す。(Test Example 1; change in skin blood flow) Two healthy female subjects (Subject A; 20 years old; Subject B; 23 years old)
Each sample was worn by the subject, and the change in finger blood flow of the subject was measured by the laser Doppler method. The measurement method is as follows.
Minutes ago, they were not affected by external stimuli. Laser Doppler blood flow meter FLO-1 before and after wearing each sample of Example or Comparative Example
(Manufactured by Omega Wave), biological signal processor DP-11
00A (manufactured by NEC Corporation), the tissue blood flow rate for arteriovenous anastomosis was measured, and 6000 points / min. Were averaged to calculate a blood flow change rate as a data value for one minute. FIG. 1 shows the results when Subject A wears Example 1 and Comparative Example 1, and FIG. 2 shows the results when Subject B wears Example 1 and Comparative Example 1. FIG. FIG. 3 shows the results when Example 2 is worn, and FIG. 4 shows the results when Subject B wears Example 2 and Comparative Example 2.
【００２３】図１〜４に示される結果の通り、本発明に
係る金属含有レーヨン系繊維は、人体に対して遠赤外線
を放射することにより、着用者の血流量を増大させて、
高い保温効果を発揮することが分かる。As shown in FIGS. 1 to 4, the metal-containing rayon fiber according to the present invention emits far-infrared rays to the human body, thereby increasing the blood flow of the wearer.
It turns out that a high heat retention effect is exhibited.
【００２４】[0024]
【発明の効果】請求項１乃至３に記載のレーヨン系繊維
は、人体に特に有効な波長とされる遠赤外線を放射する
ことができる。請求項４又は５に記載の下着は、請求項
１乃至３に記載のレーヨン系繊維が含有されているか
ら、繊維から遠赤外線が着用者の皮膚に放射されて、着
用者の血流量を増大させることができ、保温性に優れた
下着とされる。請求項６に記載の下着は、請求項１乃至
３に記載のレーヨン系繊維が人体との接面側に配置され
るように混紡されているから、レーヨン系繊維から遠赤
外線が直接皮膚に放射されることにより、効果的に着用
者の血流量を増大させることことができ、特に保温性に
優れた下着とされる。請求項７に記載の下着は、請求項
１乃至３に記載のレーヨン系繊維が人体との反接面側に
配置されるように混紡されているから、着用者の皮膚と
遠赤外線放射性粒子とが直接接触することがなく、この
ために、アレルギー症状を有する人であっても安心して
着用することができる。The rayon-based fiber according to any one of claims 1 to 3 can emit far-infrared rays, which have a wavelength particularly effective for the human body. The underwear according to claim 4 or 5 is a claim.
Since the rayon-based fibers described in 1 to 3 are contained, far-infrared rays are radiated from the fibers to the skin of the wearer, thereby increasing the blood flow rate of the wearer and making the underwear excellent in heat retention. You. Undergarment according to claim 6, to claim 1
Since the rayon-based fiber described in No. 3 is blended so as to be disposed on the surface in contact with the human body, far-infrared rays are directly emitted from the rayon-based fiber to the skin, so that the blood flow of the wearer is effectively increased. Can be increased, and the underwear is particularly excellent in heat retention. Undergarment according to claim 7, since rayon fiber according to claims 1 to 3 is blended so as to be arranged in a counter-contact surface side of the human body, and the skin of the wearer and far-infrared radiation particles Does not come into direct contact, so that even a person with allergic symptoms can wear it with confidence.
【図１】図１は、試験例１において、被験者Ａが実施例
１及び比較例１の試料を着用した場合の結果を示したグ
ラフである。FIG. 1 is a graph showing the results when Test A wears the samples of Example 1 and Comparative Example 1 in Test Example 1.
【図２】図２は、試験例１において、被験者Ｂが実施例
１及び比較例１の試料を着用した場合の結果を示したグ
ラフである。FIG. 2 is a graph showing the results when the subject B wears the samples of Example 1 and Comparative Example 1 in Test Example 1.
【図３】図３は、試験例１において、被験者Ａが実施例
２及び比較例２の試料を着用した場合の結果を示したグ
ラフである。FIG. 3 is a graph showing the results when Test A wears the samples of Example 2 and Comparative Example 2 in Test Example 1.
【図４】図４は、試験例１において、被験者Ｂが実施例
２及び比較例２の試料を着用した場合の結果を示したグ
ラフである。FIG. 4 is a graph showing the results when the subject B wears the samples of Example 2 and Comparative Example 2 in Test Example 1.
フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) D01F 1/00 - 8/18 D02G 3/02 A41B 9/00 A41B 17/00 Continuation of the front page (58) Field surveyed (Int. Cl. 7 , DB name) D01F 1/00-8/18 D02G 3/02 A41B 9/00 A41B 17/00
Claims (7)
３）と、４５〜７０重量％のシリカ（ＳｉＯ２）と、５
〜２０重量％のマグネシア（ＭｇＯ）と、５〜２０重量
％の酸化カルシウム（ＣａＯ）と、０．８〜２重量％の
プラチナ（Ｐｔ）とからなる遠赤外線放射性粒子が含有
されてなることを特徴とするレーヨン系繊維。1. A method according to claim 1, wherein 10 to 30% by weight of alumina (Al 2 O
And 3), and 45 to 70 wt% silica (SiO 2), 5
And 20% by weight of magnesia (MgO), and 5 to 20 wt% of calcium oxide (CaO), far-infrared radioactive particles consisting the 0.8 to 2% by weight of <br/> platinum (Pt) is contained A rayon-based fiber characterized by comprising:
３3 ）と、４５〜６０重量％のシリカ（ＳｉＯ) And 45-60% by weight of silica (SiO ２2 ）と、１) And 1
０〜２０重量％のマグネシア（ＭｇＯ）と、１０〜２０0-20% by weight of magnesia (MgO);
重量％の酸化カルシウム（ＣａＯ）と、８〜１５重量％Weight percent calcium oxide (CaO) and 8 to 15 weight percent
の二酸化チタン（ＴｉＯTitanium dioxide (TiO2) ２2 ）と、０．８〜２重量％のプ) And 0.8 to 2% by weight
ラチナ（Ｐｔ）とからなる遠赤外線放射性粒子が含有さContains far-infrared radioactive particles consisting of platinum (Pt)
れてなることを特徴とするレーヨン系繊維。A rayon-based fiber, characterized by being obtained.
スピネル、セリウム、バリウム、炭化ホウ素、炭化ケイSpinel, cerium, barium, boron carbide, silicon carbide
素、炭化チタン、炭化モリブデン、炭化タングステン、Element, titanium carbide, molybdenum carbide, tungsten carbide,
窒化ホウ素、窒化アルミニウム、窒化ケイ素、窒化ジルBoron nitride, aluminum nitride, silicon nitride, jill nitride
コニウム、炭素、グラファイト、タングステン、モリブConium, carbon, graphite, tungsten, molybdenum
デン、バナジウム、タンタル、マンガン、ニッケル、酸Den, vanadium, tantalum, manganese, nickel, acid
化銅、酸化鉄から選択される任意の成分が１〜１５重量Any component selected from copper oxide and iron oxide is 1 to 15 weight
％配合されてなることを特徴とする請求項１又は２に記% Or more.
載のレーヨン系繊維。Rayon-based fiber.
ヨン系繊維が含有されてなることを特徴とする下着。Underwear characterized by containing a Yong fiber.
てなることを特徴とする請求項４に記載の下着。The undergarment according to claim 4, wherein the undergarment comprises:
接面側に配置するように混紡されてなることを特徴とすCharacterized by being blended so as to be arranged on the contact side
る請求項５に記載の下着。The underwear according to claim 5.
反接面側に配置するように混紡されてなることを特徴とIt is characterized by being blended so that it is arranged on the opposite contact side
する請求項５に記載の下着。6. The undergarment of claim 5, wherein