JP3344029B2 - Surface cleaner for aluminum products - Google Patents
Surface cleaner for aluminum productsInfo
- Publication number
- JP3344029B2 JP3344029B2 JP24061893A JP24061893A JP3344029B2 JP 3344029 B2 JP3344029 B2 JP 3344029B2 JP 24061893 A JP24061893 A JP 24061893A JP 24061893 A JP24061893 A JP 24061893A JP 3344029 B2 JP3344029 B2 JP 3344029B2
- Authority
- JP
- Japan
- Prior art keywords
- cleaning
- aluminum
- present
- examples
- cleaning effect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は新規なアルミニウム製品
用表面洗浄剤に関するものである。さらに詳しくいえ
ば、本発明は、良好な洗浄効果を示し、かつアルミニウ
ム母材に対して腐食性が小さい上、洗浄作業における危
険性の少ないアルミニウム製品用表面洗浄剤に関するも
のである。The present invention relates to a novel surface cleaner for aluminum products. More specifically, the present invention relates to a surface cleaning agent for aluminum products, which exhibits a good cleaning effect, has low corrosiveness to an aluminum base material, and has a low risk in a cleaning operation.
【０００２】[0002]
【従来の技術】電気集塵機や空調用熱交換器は、使用に
よりその集塵板やフインなどに汚れが付着し、集塵効率
や熱交換効率が低下することから、一定期間使用後に分
解し、集塵板や熱交換フインを洗浄して使用している。
該集塵板やフインは、通常アルミニウム製であり、そし
て洗浄にはアルカリ性の薬剤が広く用いられている。し
かしながら、アルカリ性洗浄剤は、洗浄効果自体は良好
であるものの、腐食によりアルミニウム母材に損傷を与
えるとともに、眼など洗浄作業者の人体に対して危険性
を有するなどの問題がある。このような問題を解決する
ために、例えば有機酸、アルカリビルダー、界面活性剤
などを含有する酸性洗浄剤（特開平４−２０２７８９号
公報）、多価金属イオン封鎖剤、界面活性剤、アルカリ
ビルダーを含有する洗浄剤（特開平２−９９５９９号公
報）、エタノールアミン、有機カルボン酸などを含有す
る洗浄剤（特開昭６２−１１６６９７号公報）などが提
案されている。しかしながら、これらの洗浄剤において
は、洗浄力が必ずしも十分であるとはいえない。2. Description of the Related Art Electric dust collectors and air-conditioning heat exchangers are subject to disintegration after being used for a certain period of time because dust adheres to the dust collecting plates and fins due to use, and the dust collecting efficiency and heat exchange efficiency decrease. The dust collection plate and heat exchange fins are cleaned and used.
The dust collecting plates and fins are usually made of aluminum, and alkaline chemicals are widely used for washing. However, although the alkaline cleaning agent has a good cleaning effect itself, it has a problem that it damages the aluminum base material by corrosion and has a danger to the human body of a cleaning worker such as eyes. In order to solve such a problem, for example, an acidic detergent containing an organic acid, an alkali builder, a surfactant and the like (Japanese Patent Application Laid-Open No. 4-202789), a polyvalent metal ion sequestering agent, a surfactant, an alkali builder (JP-A-2-99599), a detergent containing ethanolamine, organic carboxylic acid and the like (JP-A-62-116697). However, these cleaning agents do not always have sufficient detergency.
【０００３】[0003]
【発明が解決しようとする課題】本発明はこのような事
情のもとで、良好な洗浄効果を示し、かつアルミニウム
母材に対して腐食性が小さい上、洗浄作業における危険
性の少ないアルミニウム製品用表面洗浄剤を提供するこ
とを目的としてなされたものである。SUMMARY OF THE INVENTION Under such circumstances, the present invention provides an aluminum product which exhibits a good cleaning effect, has a low corrosiveness to an aluminum base material, and has a low danger in a cleaning operation. The purpose of the present invention is to provide a surface cleaning agent for use.
【０００４】[0004]
【課題を解決するための手段】本発明者は前記目的を達
成するために鋭意研究を重ねた結果、クエン酸塩及び所
望により用いられる界面活性剤を所定の割合で含有し、
かつpHが特定の範囲にある水溶液から成る洗浄剤によ
り、その目的を達成しうることを見い出し、この知見に
基づいて本発明を完成するに至った。すなわち、本発明
は、クエン酸塩を３５〜３００ｇ／リットル及び所望に
より用いられる界面活性剤を１〜１００ｇ／リットル含
有するpH８.５〜１２の水溶液から成るアルミニウム製
品用表面洗浄剤を提供するものである。Means for Solving the Problems As a result of intensive studies conducted by the present inventor to achieve the above-mentioned object, the present inventor contains citrate and optionally used surfactant in a predetermined ratio,
It has been found that a cleaning agent comprising an aqueous solution having a pH in a specific range can achieve the object, and based on this finding, the present invention has been completed. That is, the present invention provides a surface cleaning agent for aluminum products comprising an aqueous solution having a pH of 8.5 to 12 containing 35 to 300 g / liter of a citrate salt and 1 to 100 g / liter of a surfactant used as desired. It is.
【０００５】以下、本発明を詳細に説明する。本発明の
洗浄剤においては、必須成分としてクエン酸塩が用いら
れる。該クエン酸塩を構成する陽イオンについては、そ
の塩が水溶性を示すものであればよく、特に制限され
ず、いかなるものであってもよい。該塩としては、例え
ばナトリウム塩、カリウム塩、アンモニウム塩、アルキ
ル基置換アンモニウム塩などが挙げられるが、これらの
中でナトリウム塩が好適である。また、該クエン酸塩は
３個のカルボン酸がすべて中和された完全中和型のもの
であってもよいし、一部中和された不完全中和型のもの
（例えばクエン酸ニナトリウム）であってもよく、ある
いは中和されていない完全遊離型のクエン酸を含んでい
てもよい。本発明の洗浄剤においては、前記クエン酸塩
は３５〜３００ｇ／リットル、好ましくは５０〜１５０
ｇ／リットルの割合で含有することが必要である。この
含有量が３５ｇ／リットル未満では洗浄効果が不十分で
あるし、３００ｇ／リットルを超えると洗浄効果自体に
は問題はないが、洗浄コストが高くなる。Hereinafter, the present invention will be described in detail. In the cleaning agent of the present invention, citrate is used as an essential component. The cation constituting the citrate is not particularly limited as long as the salt exhibits water solubility, and any cation may be used. Examples of the salt include a sodium salt, a potassium salt, an ammonium salt, an alkyl group-substituted ammonium salt and the like. Among them, a sodium salt is preferable. The citrate may be a completely neutralized type in which all three carboxylic acids are neutralized, or a partially neutralized incompletely neutralized type (for example, disodium citrate). ) Or may contain completely free citric acid which has not been neutralized. In the cleaning agent of the present invention, the citrate is 35 to 300 g / liter, preferably 50 to 150 g / l.
It must be contained at a rate of g / liter. When the content is less than 35 g / liter, the cleaning effect is insufficient, and when it exceeds 300 g / liter, there is no problem in the cleaning effect itself, but the cleaning cost increases.
【０００６】本発明の洗浄剤は、pHが８.５〜１２、好
ましくは９〜１０の範囲にあることが必要である。この
pHが８.５未満では洗浄効果が不十分であるし、１２を
超えると洗浄効果自体には問題はないが、人体に対する
安全性やアルミニウム母材に対する腐食性の問題が生じ
る。本発明の洗浄剤には、洗浄効果をさらに改善する目
的で、必要に応じ界面活性剤を含有させることができ
る。該界面活性剤としては、アニオン性界面活性剤及び
ノニオン性界面活性剤が好ましく用いられる。アニオン
性界面活性剤としては、例えばアルキル硫酸塩やアルキ
ルスルホン酸塩などが好適である。また、ノニオン性界
面活性剤としては、例えばポリオキシエチレンアルキル
エーテル、ポリオキシエチレンアルキルフェニルエーテ
ルなどが挙げられるが、特にＨＬＢが１０〜１７の範囲
にあるものが好適である。該界面活性剤の含有量は１〜
１００ｇリットルの範囲で選ばれる。この量が１ｇ／リ
ットル未満では添加効果が十分に発揮されないし、１０
０ｇ／リットルを超えると効果上は問題はないが、洗浄
コストが高くなったり、洗浄液に沈殿が生じることがあ
る。[0006] The cleaning agent of the present invention must have a pH in the range of 8.5 to 12, preferably 9 to 10. this
If the pH is less than 8.5, the cleaning effect is insufficient, and if it exceeds 12, there is no problem in the cleaning effect itself, but there is a problem of safety to the human body and corrosiveness to the aluminum base material. The cleaning agent of the present invention can contain a surfactant, if necessary, for the purpose of further improving the cleaning effect. As the surfactant, an anionic surfactant and a nonionic surfactant are preferably used. As the anionic surfactant, for example, an alkyl sulfate or an alkyl sulfonate is suitable. Examples of the nonionic surfactant include, for example, polyoxyethylene alkyl ether and polyoxyethylene alkyl phenyl ether, and those having an HLB in the range of 10 to 17 are particularly preferable. The content of the surfactant is 1 to
It is selected in the range of 100 gl. When the amount is less than 1 g / liter, the effect of addition is not sufficiently exhibited, and
If it exceeds 0 g / liter, there is no problem in the effect, but the washing cost may be increased or the washing solution may precipitate.
【０００７】本発明の洗浄剤には、前記成分以外に、本
発明の目的が損なわれない範囲で、必要に応じ各種添加
成分、例えばアルカリビルダー、洗浄助剤、溶解補助
剤、腐食防止剤などを添加することができる。アルカリ
ビルダーとしては、例えばポリリン酸塩やケイ酸塩など
が、洗浄助剤としては、例えばカルビトール類などの有
機溶剤が、溶解補助剤としては、例えばエタノール、エ
チレングリコール、プロピレングリコールなどが、腐食
防止剤としては、例えばベンゾトリアゾール、亜硝酸ナ
トリウムなどが挙げられる。本発明はまた、前記洗浄剤
を用いてアルミニウム製品を洗浄する方法をも提供する
ものである。洗浄の方法については特に制限はなく、常
法に従ってアルミニウム製品を洗浄すればよい。[0007] In addition to the above-mentioned components, the cleaning agent of the present invention may contain various additional components, such as alkali builders, cleaning aids, dissolution aids, and corrosion inhibitors, as long as the object of the present invention is not impaired. Can be added. Examples of the alkali builder include polyphosphates and silicates, examples of the cleaning aid include organic solvents such as carbitols, and examples of the dissolution aid include ethanol, ethylene glycol, and propylene glycol. Examples of the inhibitor include benzotriazole and sodium nitrite. The present invention also provides a method for cleaning an aluminum product using the cleaning agent. The washing method is not particularly limited, and the aluminum product may be washed according to a conventional method.
【０００８】[0008]
【作用】従来のアルカリ洗浄剤は短時間で良好な洗浄効
果を示すが、これは次のように考えられる。洗浄効果は
一般に乳化・分散作用を含めた汚れの溶出作用及び母材
の腐食に起因する剥離作用によって発揮される。水酸化
ナトリウムなどのいわゆる苛性アルカリを主剤とするア
ルカリ洗浄剤は、激しいガス発生を伴いながらアルミニ
ウムを強く腐食させる。このため、溶出作用と剥離作用
のうち、主として剥離作用が洗浄効果発揮の要因とな
り、短時間で良好な洗浄効果を示すと考えられる。しか
し、その結果として母材は腐食され損傷することにな
る。母材を損傷させない洗浄方法として、乳化・分散作
用を含む汚れの溶出作用を主体にした洗浄剤が工夫され
ているが、剥離作用を欠いた溶出作用だけでは汚れの除
去力が弱く、汚れの激しい場合や母材が平滑でない場合
には、汚れを除去しきれなくなる。また、洗浄作業は短
時間で終了することが望まれるが、汚れが取れにくいた
め、要望を満たすことができない。The conventional alkaline cleaner shows a good cleaning effect in a short time, which is considered as follows. The cleaning effect is generally exhibited by the action of dissolving dirt including the action of emulsification / dispersion and the peeling action caused by corrosion of the base material. Alkaline cleaners based on so-called caustic, such as sodium hydroxide, strongly corrode aluminum with intense gas generation. For this reason, it is considered that, of the elution action and the stripping action, the stripping action is mainly a factor of exhibiting the cleaning effect, and a good cleaning effect is exhibited in a short time. However, as a result, the base material is corroded and damaged. As a cleaning method that does not damage the base material, a cleaning agent that mainly decontaminates dirt including emulsification / dispersion is devised. If it is severe or the base material is not smooth, it will not be possible to remove dirt. In addition, although it is desired that the cleaning operation be completed in a short time, it is difficult to remove dirt, so that the request cannot be satisfied.
【０００９】アルミニウムは、本来腐食されやすい金属
にもかかわらず、中性の水系では強い耐食性を示す。こ
れは、アルミニウム表面に母材の保護皮膜として酸化ア
ルミニウム層が形成されているためと考えられている。
したがって、汚れは母材自体ではなく、酸化アルミニウ
ム層に付着すると考えられるため、酸化アルミニウム層
を溶解させれば、汚れは剥離されることとなり、汚れの
溶出作用のみに基づく洗浄剤と比べて、洗浄効果は飛躍
的に向上し、しかもアルミニウム母材の損傷が少ない。
本発明の洗浄剤に用いられるクエン酸塩は、中性に近い
弱アルカリ性でこのような作用を有しているものであ
る。[0009] Aluminum exhibits strong corrosion resistance in neutral aqueous systems despite its inherently susceptible metals. This is considered to be because an aluminum oxide layer was formed as a protective film of the base material on the aluminum surface.
Therefore, the dirt is considered to adhere to the aluminum oxide layer, not to the base material itself, so if the aluminum oxide layer is dissolved, the dirt will be peeled off, compared to a cleaning agent based solely on the elution action of the dirt. The cleaning effect is greatly improved, and the aluminum base material is less damaged.
The citrate used in the cleaning agent of the present invention has such an action at a weak alkaline property close to neutrality.
【００１０】[0010]
【実施例】次に、実施例により本発明をさらに詳細に説
明するが、本発明はこれらの例によってなんら限定され
るものではない。 実施例１〜５、比較例１〜８ たばこ煙汚れが付着した空気清浄機の集塵板（材質：ア
ルミニウム）を３５×４５mmに切断して重量測定した試
験片を、第１表及び第２表に示す４５℃の試験液５００
mlに３０分間浸漬した。その後、軽く水洗し、一夜風乾
した。重量測定後、アセトンで残存汚れを除去して再度
重量測定し、次式により洗浄効果を求めた。Next, the present invention will be described in more detail by way of examples, but the present invention is not limited to these examples. Examples 1 to 5 and Comparative Examples 1 to 8 Test pieces obtained by cutting a dust collecting plate (material: aluminum) of an air purifier to which tobacco smoke stain adhered into a piece of 35 × 45 mm and weighing the same are shown in Tables 1 and 2. Test liquid 500 at 45 ° C. shown in the table
The sample was immersed in ml for 30 minutes. Then, it was lightly washed with water and air-dried overnight. After the measurement of the weight, the remaining dirt was removed with acetone, and the weight was measured again.
【００１１】[0011]
【数１】 (Equation 1)
【００１２】なお、Ｗ1は試験前の重量、Ｗ2は風乾後の
重量、Ｗ3はアセトン洗浄後の重量である。洗浄効果が
１００％の場合を◎、９０％以上１００％未満の場合を
○、６０％以上９０％未満の場合を△、６０％未満の場
合を×として、結果を第１表及び第２表に示す。なお、
比較例１では激しい腐食のため、目視で判定したが、５
分程度の短時間で汚れは完全に除去されていた。W 1 is the weight before the test, W 2 is the weight after air drying, and W 3 is the weight after washing with acetone. The results are shown in Tables 1 and 2, with ◎ when the cleaning effect is 100%, ○ when 90% or more and less than 100%, Δ when 60% or more and less than 90%, and X when less than 60%. Shown in In addition,
In Comparative Example 1, because of severe corrosion, it was visually determined.
The dirt was completely removed in a short time of about a minute.
【００１３】[0013]
【表１】 [Table 1]
【００１４】注）アニオン性界面活性剤：ラウリル硫酸
ナトリウム ノニオン性界面活性剤：ポリオキシエチレンノニル フェニルエーテル（ＨＬＢ１３）Note: Anionic surfactant: sodium lauryl sulfate Nonionic surfactant: polyoxyethylene nonyl phenyl ether (HLB13)
【００１５】[0015]
【表２】 [Table 2]
【００１６】注）ＥＤＴＡ：エチレンジアミンテトラ酢
酸ナトリウム ＡＢＳ：ドデシルベンゼンスルホン酸ナトリウムNote) EDTA: sodium ethylenediaminetetraacetate ABS: sodium dodecylbenzenesulfonate
【００１７】第１表及び第２表から、次のことが分か
る。すなわち、（１）代表的な錯化剤のＥＤＴＡは不良
であるが（比較例２）、クエン酸ナトリウムは洗浄効果
が良好である（実施例１〜３）、（２）汚れの溶解作用
のみのラウリル硫酸ナトリウム単独では洗浄効果が不良
である（比較例３）、（３）クエン酸ナトリウム濃度が
２０ｇ／リットルでは洗浄効果が不足する（比較例
４）、（４）クエン酸ナトリウム濃度が十分でも、pHが
８.０では洗浄効果が不良である（比較例５）、（５）
特開平４−２０２７８９号公報の実施例は効果が不良で
ある（比較例６）、（６）特開平２−９９５９９号公報
の実施例は効果が不足する（比較例７）、（７）特開昭
６２−１１６６９７号公報の実施例は効果が不良である
（比較例８）、（８）水酸化ナトリウムは洗浄効果が良
好である（比較例１）（９）クエン酸ナトリウムに界面
活性剤を併用すると効果はさらに改善される（実施例
４、５）また、実施例２、３及び比較例１についてアル
ミニウムに対する腐食速度（２５℃）を調べた。その結
果を第３表に示す。The following can be seen from Tables 1 and 2. That is, (1) EDTA as a typical complexing agent is poor (Comparative Example 2), but sodium citrate has a good cleaning effect (Examples 1 to 3), and (2) only the action of dissolving dirt Of sodium lauryl sulfate alone has a poor cleaning effect (Comparative Example 3), (3) a sodium citrate concentration of 20 g / liter results in insufficient cleaning effect (Comparative Example 4), and (4) a sufficient sodium citrate concentration However, when the pH was 8.0, the cleaning effect was poor (Comparative Example 5), (5)
The embodiment of JP-A-4-202789 has a poor effect (Comparative Example 6), and (6) the embodiment of JP-A-2-99599 has an insufficient effect (Comparative Example 7). The examples of JP-A-62-116697 have poor effects (Comparative Example 8), and (8) sodium hydroxide has a good cleaning effect (Comparative Example 1). (9) Surfactant added to sodium citrate The effect is further improved by the combination of (Examples 4 and 5). Further, the corrosion rates (25 ° C.) of aluminum in Examples 2 and 3 and Comparative Example 1 were examined. Table 3 shows the results.
【００１８】[0018]
【表３】 [Table 3]
【００１９】第３表から、実施例２及び３は比較例１に
比べて、アルミニウム母材の腐食速度が大幅に軽減され
ることが分かる。From Table 3, it can be seen that Examples 2 and 3 significantly reduce the corrosion rate of the aluminum base material as compared with Comparative Example 1.
【００２０】[0020]
【発明の効果】本発明のアルミニウム製品用表面洗浄剤
は、良好な洗浄効果を示し、かつアルミニウム母材に対
して腐食性が小さい上、洗浄作業における危険性が少な
く、電気集塵機の集塵板や空調用熱交換器のフインなど
のアルミニウム製品の汚れ付着の洗浄に好適に用いられ
る。Industrial Applicability The surface cleaner for aluminum products of the present invention exhibits a good cleaning effect, is less corrosive to an aluminum base material, has less danger in cleaning work, and has a dust collecting plate for an electric dust collector. It is suitably used for cleaning dirt attached to aluminum products such as fins of air conditioners and heat exchangers for air conditioning.
Claims (2)
有するpH８.５〜１２の水溶液から成るアルミニウム製
品用表面洗浄剤。1. A surface cleaning agent for aluminum products comprising an aqueous solution containing 35 to 300 g / l of citrate and having a pH of 8.5 to 12.
び界面活性剤を１〜１００ｇ／リットル含有するpH８.
５〜１２の水溶液から成るアルミニウム製品用表面洗浄
剤。2. The pH 8. containing 35 to 300 g / l of citrate and 1 to 100 g / l of a surfactant.
A surface cleaner for aluminum products comprising an aqueous solution of 5 to 12.