JP3305488B2 - Lithographic printing plate - Google Patents
Lithographic printing plateInfo
- Publication number
- JP3305488B2 JP3305488B2 JP6379694A JP6379694A JP3305488B2 JP 3305488 B2 JP3305488 B2 JP 3305488B2 JP 6379694 A JP6379694 A JP 6379694A JP 6379694 A JP6379694 A JP 6379694A JP 3305488 B2 JP3305488 B2 JP 3305488B2
- Authority
- JP
- Japan
- Prior art keywords
- lithographic printing
- printing plate
- silver
- plate
- silver halide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】[0001]
【産業上の利用分野】本発明は、アルミニウム板を支持
体とする平版印刷版、特に実質的に明室環境下で取り扱
い可能な銀錯塩拡散転写法を用いる平版印刷版に関する
ものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a lithographic printing plate using an aluminum plate as a support, and more particularly to a lithographic printing plate using a silver complex salt diffusion transfer method which can be handled substantially in a bright room environment.
【0002】[0002]
【従来の技術】銀錯塩拡散転写法(DTR法)を用いた
平版印刷版については、フォーカル・プレス、ロンドン
ニューヨーク(1972年)発行、アンドレ ロット
及びエディス ワイデ著、「フォトグラフィック・シル
バー・ハライド・ディヒュージョン・プロセシズ」、第
101頁〜第130頁に幾つかの例が記載されている。2. Description of the Related Art A lithographic printing plate using a silver complex salt diffusion transfer method (DTR method) is described in "Photographic Silver Halide." Some examples are described in "Diffusion Processes", pp. 101-130.
【0003】その中で述べられているように、DTR法
を用いた平版印刷版には、転写材料と受像材料を別々に
したツーシートタイプ、あるいはそれらを一枚の支持体
上に設けたモノシートタイプの二方式が知られている。
ツーシートタイプの平版印刷版については、特開昭57
−158844号公報に詳しく記載されている。又、モ
ノシートタイプについては、特公昭48−30562
号、同51−15765号、特開昭51−111103
号、同52−150105号などの各公報に詳しく記載
されている。As described therein, a lithographic printing plate using the DTR method includes a two-sheet type in which a transfer material and an image receiving material are separated, or a monolithic type in which they are provided on a single support. Two types of sheet type are known.
A two-sheet type lithographic printing plate is disclosed in
This is described in detail in JP-A-158844. For the mono-sheet type, see JP-B-48-30562.
No. 51-15765, JP-A-51-111103
And JP-A Nos. 52-150105.
【0004】紙を支持体とした平版印刷版は、印刷中の
版伸びや水分のしみ込みなどのため耐刷性を含め高品質
の印刷は困難である。これらの問題点を改良し印刷性能
を向上する目的でフィルム支持体が用いられる。例え
ば、酢酸セルロースフィルム、ポリビニルアセタールフ
ィルム、ポリスチレンフィルム、ポリプロピレンフィル
ム、ポリエチレンテレフタレートフィルム、或はポリエ
ステル、ポリプロピレン、又はポリスチレンフィルムな
どをポリエチレンフィルムで被覆した複合フィルム等が
支持体として利用できる。[0004] A lithographic printing plate using paper as a support is difficult to print with high quality including printing durability due to plate elongation during printing and penetration of moisture. A film support is used for the purpose of improving these problems and improving printing performance. For example, a cellulose acetate film, a polyvinyl acetal film, a polystyrene film, a polypropylene film, a polyethylene terephthalate film, or a composite film obtained by coating a polyester, polypropylene, or polystyrene film with a polyethylene film can be used as the support.
【0005】しかしながら、フィルムを支持体とした平
版印刷版は紙ベースの印刷版と比べ、版伸び性や水分の
しみ込みなどの点で改良されたものの、耐刷性、保水
性、更には印刷機への版掛け性等の点で問題を残してい
る。[0005] However, lithographic printing plates using a film as a support are improved in terms of plate elongation and moisture penetration, as compared with paper-based printing plates, but they have improved printing durability, water retention and printing. The problem remains in terms of the ability to hang the plate on the machine.
【0006】そこで、上に述べた紙やフィルムを支持体
とした平版印刷版の種々の問題点を解決するために、金
属特にアルミニウム板を支持体とした銀塩方式の平版印
刷版が知られており、特開昭57−118244号、同
57−158844号、同63−260491号、特開
平3−116151号、同4−282295号などの各
公報に詳しく記載されている。In order to solve the above-mentioned various problems of the lithographic printing plate using a paper or a film as a support, a lithographic printing plate of a silver salt type using a metal, particularly an aluminum plate as a support has been known. These are described in detail in JP-A-57-118244, JP-A-57-158844, JP-A-63-260491, JP-A-3-116151, and JP-A-4-282295.
【0007】特開昭63−260491号、特開平3−
116151号、同4−282295号などの各公報に
は、粗面化され陽極酸化されたアルミニウム板を支持体
とし、その上に物理現像核を担持し、更にその上に感光
性ハロゲン化銀乳剤層を設けたモノシートタイプでDT
R法を利用する平版印刷版が詳述されている。それによ
れば、上記平版印刷版を像露光し、DTR現像した後、
ハロゲン化銀乳剤層を温水で洗浄して除去し印刷版を作
製する。しかしこれらの特許は、ハロゲン化銀乳剤とア
ルミニウム板とが接触することにより生じるアルミニウ
ム板の腐食を防止することに向けられた技術であり、転
写銀画像の画質、インキ受理性、耐刷力の点では十分と
はいえないものであった。JP-A-63-260491, JP-A-3-26049
JP-A-116151 and JP-A-4-282295 disclose that a roughened and anodized aluminum plate is used as a support, a physical development nucleus is supported thereon, and a photosensitive silver halide emulsion is further provided thereon. DT with mono-sheet type with layer
A lithographic printing plate utilizing the R method is described in detail. According to the method, after the lithographic printing plate is subjected to image exposure and DTR development,
The silver halide emulsion layer is removed by washing with warm water to prepare a printing plate. However, these patents are directed to preventing the corrosion of the aluminum plate caused by the contact between the silver halide emulsion and the aluminum plate, and are intended to improve the image quality of the transferred silver image, ink receptivity, and printing durability. It was not enough in point.
【0008】一般に、平版印刷版に用いられるアルミニ
ウム支持体は、印刷時における湿し水に対する濡れ(保
水性)を良くするため、また感光層との密着を良くする
ため、その表面を粗面化することが行われる。この粗面
化処理(いわゆるグレイニング)には、ボールグレイニ
ング、ワイヤグレイニング、ブラシグレイニング等の機
械的粗面化処理、塩化物、フッ化物等で化学的にアルミ
ニウムを溶解することにより行う化学的粗面化処理、及
び電気化学的にアルミニウムを溶解することにより行う
電解粗面化処理、及びこれらの方法を併用した粗面化方
法が知られている。例えば特開昭48−28123号、
同53−123204号、同54−146234号、同
55−25381、同55−132294号、同56−
55291号、同56−150593号、同56−28
893号、同58−167196号、米国特許第2,3
44,510号、同第3,861,917号、同第4,
301,229号などがある。アルミ板の表面形状につ
いても、米国特許第2,344,510号は機械的粗面
化と電解粗面化を行い重畳的に複合した砂目構造、米国
特許第4,301,229号はピット径の累積度数分布
と中心線平均粗さ、米国特許第3,861,917号は
粗面の深さ、カナダ特許第955449号は粗面の山の
高さと直径、西ドイツ特許第1,813,443号は粗
面の高低差についてそれぞれ記載されている。In general, the surface of an aluminum support used for a lithographic printing plate is roughened in order to improve wettability (water retention) with a fountain solution during printing and to improve adhesion to a photosensitive layer. Is done. The surface roughening (so-called graining) is performed by mechanically roughening such as ball graining, wire graining, and brush graining, or by chemically dissolving aluminum with chloride, fluoride, or the like. There are known a chemical surface roughening treatment, an electrolytic surface roughening treatment performed by dissolving aluminum electrochemically, and a surface roughening method using these methods in combination. For example, JP-A-48-28123,
No. 53-123204, No. 54-146234, No. 55-25381, No. 55-132294, No. 56-
No. 55291, No. 56-150593, No. 56-28
Nos. 893 and 58-167196, U.S. Pat.
No. 44,510, No. 3,861,917, No. 4,
Nos. 301 and 229. Regarding the surface shape of an aluminum plate, U.S. Pat. No. 2,344,510 discloses a grain structure in which mechanical roughening and electrolytic surface roughening are performed in an overlapping manner, and U.S. Pat. No. 4,301,229 discloses pits. Cumulative frequency distribution and center line average roughness of diameter, U.S. Pat. No. 3,861,917, Roughness Depth, Canadian Patent No. 954,449, Roughness Crest Height and Diameter, West German Patent 1,813, No. 443 describes a difference in elevation of a rough surface.
【0009】このような粗面化処理を行なった後、硫
酸、燐酸、硝酸あるいはそれらの混合液などの電解液中
で陽極酸化処理が施される。After performing such a surface roughening treatment, an anodic oxidation treatment is performed in an electrolytic solution such as sulfuric acid, phosphoric acid, nitric acid or a mixture thereof.
【0010】このように印刷版用アルミニウム板の表面
処理は、平版印刷版の種類、印刷用途などによって、粗
面の形状、構造等の異なる極めて多くの粗面化アルミ板
が提案されている。しかし、本発明が対象とする平版印
刷版では、上記の印刷時における湿し水に対する濡れ
(保水性)を良くするため、また感光層との密着を良く
するためという機能に加えて、ハロゲン化銀の拡散転写
現像により、該アルミ表面上に形成される銀膜の印刷機
能に影響を与えること、具体的には、どのような表面形
状のアルミ板がインキ受理性、耐刷力の点で好ましいの
かについては知られていなかった。また、ハロゲン化銀
の拡散転写現像をコントロールして、高画質で、耐刷力
の点で好ましい銀画像を該アルミ表面上に形成させるた
めの諸因子についても、明らかにされていなかった。As described above, for the surface treatment of an aluminum plate for a printing plate, an extremely large number of surface-roughened aluminum plates having different shapes and structures of the roughened surface have been proposed depending on the type of lithographic printing plate, printing application and the like. However, in the lithographic printing plate targeted by the present invention, in addition to the function of improving the wetting (water retention) with a fountain solution at the time of printing and improving the adhesion to the photosensitive layer, the lithographic printing plate has a halogenated Influence the printing function of the silver film formed on the aluminum surface by the diffusion transfer development of silver, and specifically, the aluminum plate of any surface shape has a problem in terms of ink receptivity and printing durability. There was no known preference. Further, there are no known factors for controlling the diffusion transfer development of silver halide so as to form a silver image having high image quality and favorable printing durability on the aluminum surface.
【0011】現在、平版印刷分野で広く使用されている
アルミニウム板の上にフォトポリマーなどの感光性物質
層を設けたPS(Pre−Sensitized)版は
実質的に明室環境下で取り扱うことが出来る。At present, a PS (Pre-Sensitized) plate in which a photosensitive material layer such as a photopolymer is provided on an aluminum plate widely used in the field of lithographic printing can be handled substantially in a bright room environment. .
【0012】PS版は粗面化処理、陽極酸化処理などの
表面処理を施したアルミニウム板上にフォトポリマーな
どの感光性物質を塗布、乾燥して製造される。PS版は
紫外線領域に感度を持つため実質的に紫外線を含まない
安全光下、すなわち実質的な明室で取り扱いができ、紫
外線を多量に含んだ光源で露光される。紫外線による画
像露光後、現像、水洗、ガム引きなどの製版処理が施さ
れて印刷版が出来上がる。現像処理による未溶解の感光
層は画像部を形成し、感光層が除去されアルミニウム表
面が露出した部分は親水性となり非画像部が形成され
る。The PS plate is manufactured by applying a photosensitive material such as a photopolymer on an aluminum plate which has been subjected to a surface treatment such as a surface roughening treatment and an anodic oxidation treatment and drying. Since the PS plate has sensitivity in the ultraviolet region, it can be handled in safe light substantially free of ultraviolet light, that is, in a substantially bright room, and is exposed to a light source containing a large amount of ultraviolet light. After image exposure with ultraviolet rays, plate making processes such as development, washing, and gumming are performed to complete a printing plate. The undissolved photosensitive layer formed by the developing process forms an image portion, and the portion where the photosensitive layer is removed and the aluminum surface is exposed becomes hydrophilic and a non-image portion is formed.
【0013】平版印刷版としてPS版は広範囲で使用さ
れているものの、幾つかの問題点を抱えている。画像露
光時にはPS版をフィルムと密着して紫外線で露光する
が、PS版の感度が低いため強力な紫外線で長時間の露
光が必要である。強力な紫外線は目に悪く作業環境とし
て好ましいものではない。又、現像処理には高アルカリ
剤、有機溶剤などを含有した現像液を多量に使用する。
このような現像液を使用することは作業環境上好ましく
なく、更に多量に発生する廃液は地球環境保全上大きな
問題となっている。これ以外にも品質の安定化、処理の
迅速化などの改良が続けられている。Although the PS plate is widely used as a lithographic printing plate, it has some problems. At the time of image exposure, the PS plate is exposed to ultraviolet light in close contact with the film. However, since the sensitivity of the PS plate is low, long exposure with strong ultraviolet light is required. Strong ultraviolet light is bad for eyes and is not preferable as a working environment. Further, a large amount of a developing solution containing a high alkali agent, an organic solvent or the like is used in the developing treatment.
The use of such a developing solution is not preferable in the working environment, and the waste liquid generated in a larger amount is a major problem in global environmental conservation. In addition, improvements such as stabilization of quality and rapid processing have been continued.
【0014】以上のような状況の中で、銀錯塩拡散転写
法を用いたアルミニウム板を支持体とする平版印刷版に
関して、アルミニウム表面の腐食防止、現像処理方法な
どに係わる技術は前述した特許明細書等で開示されてい
るものの、明室環境下で取扱い可能でしかも高画質、高
耐刷力の銀錯塩拡散転写法を用いたアルミニウム板を支
持体とする平版印刷版については何等言及されていな
い。Under the circumstances described above, with regard to a lithographic printing plate using an aluminum plate as a support by a silver complex salt diffusion transfer method, techniques relating to corrosion prevention on an aluminum surface, a developing method, and the like are described in the above-mentioned patent specification. Although it is disclosed in a book or the like, there is no mention of a lithographic printing plate that can be handled in a bright room environment and has a high image quality and a high printing durability and uses an aluminum plate as a support using a silver complex salt diffusion transfer method. Absent.
【0015】[0015]
【発明が解決しようとする課題】本発明の目的は、上記
課題を解決するために、実質的に明室環境下で取扱い可
能で高画質、高耐刷力の銀錯塩拡散転写法を用いたアル
ミニウム板を支持体とする新規な平版印刷版を提供する
ことである。SUMMARY OF THE INVENTION In order to solve the above-mentioned problems, an object of the present invention is to use a silver complex salt diffusion transfer method which can be handled in a substantially bright room environment and has high image quality and high printing durability. An object of the present invention is to provide a novel lithographic printing plate using an aluminum plate as a support.
【0016】[0016]
【課題を解決するための手段】本発明の上記目的は、粗
面化され陽極酸化されたアルミニウム支持体とハロゲン
化銀乳剤層の間に物理現像核層を有する平版印刷版にお
いて、該ハロゲン化銀乳剤中にハロゲン化銀1モル当た
り10 -8 〜10 -3 モルの水溶性ロジウム塩、及びハロゲ
ン化銀1モル当たり0.2〜200mgの有機減感剤を
含んだことを特徴とする平版印刷版によって達成され
る。SUMMARY OF THE INVENTION The above object of the present invention, crude
Planarized and anodized aluminum support and halogen
A lithographic printing plate having a physical development nucleus layer between silver halide emulsion layers
1 mole of silver halide in the silver halide emulsion.
10 -8 to 10 -3 mol of a water-soluble rhodium salt and halogen
0.2 to 200 mg of organic desensitizer per mole of silver halide
Achieved by a lithographic printing plate characterized by including.
【0017】本発明に使用する水溶性ロジウム塩は、従
来知られているものが用いられるが、代表的にはロジウ
ムモノクロライド、ロジウムジクロライド、ロジウムト
リクロライド、ロジウムアンモニウムクロライドなどが
用いられる。添加量はハロゲン化銀1モル当り10-8〜
10-3モルの範囲でよい。ロジウム塩は、一般的にはハ
ロゲン化銀の沈澱もしくは物理熟成時に用いることが好
ましいが、その後の任意の時期であってもよい。As the water-soluble rhodium salt used in the present invention, conventionally known ones are used. Typically, rhodium monochloride, rhodium dichloride, rhodium trichloride, rhodium ammonium chloride and the like are used. The amount of addition is 10 @ -8 to 1 mol per mol of silver halide.
It may be in the range of 10-3 mol. The rhodium salt is generally preferably used at the time of silver halide precipitation or physical ripening, but may be at any time thereafter.
【0018】有機減感剤としては、一般に直接ポジ用ハ
ロゲン化銀乳剤に用いることが知られているものであ
る。そのような有機減感剤の具体例は、数多くの特許明
細書、文献に記載されており、それらはいずれも本発明
において同じ作用をもっているものであって、例えば特
公昭36−17595、同昭39−20261、同昭4
0−26751、同昭43−13167、同昭45−8
833、同昭47−8746、同昭47−10197、
同昭50−37530、特開昭48−24734、同昭
49−84639、同昭56−142525、米国特許
第2271229号、同第2541472号、同第30
35917号、同第3062651号、同第31244
58号、同第3326687号、同第3671254号
などの明細書に記載されている化合物が使用できる。以
下にその具体例を示す。 (A) 1、3ージエチルー1’ーメチルー2’ーフェ
ニルイミダゾ[4、5ーb]ーキノキサリノー3’ーイ
ンドロカルボシアニン・アイオダイド (B) ピナクリプトール・イエロー (C) 1、1’、3、3、3’、3’ーヘキサメチル
ー5、5’ージニトロインドカルボシアニン・Pートル
エンスルホネート (D) 5、5ージクロロー3、3’ージエチルー6、
6’ージニトロチアカルボシアニン・アイオダイド (E) 1、1’ージメチルー2、2’ージフェニルー
3、3’ーインドロカルボシアニン・ブロマイド (F) 1、1’、3、3’ーテトラエチルイミダゾ
[4、5ーb]キノキサノカルボシアニン・クロライド (G) 5ーm−ニトロベンジリデンローダニン (H) 6ークロロー4ーニトローニトロベンゾトリア
ゾール (I) 1、1’ージブチルー4、4’ービピリジニウ
ム・ジブロマイド (J) 1、1’ーエチレンー2、2’ービピリジニウ
ム・ジブロマイド (K) 4ー(Pーnーアミロキシフェニル)ー2、6
ージ(Pーエチルフェニル)チアピリウム・パークロレ
ート (L) 2ーメルカプトー4ーメチルー5ーニトロチア
ゾール (M) 2ー(Oーニトロスチリル)ー3ーエチルベン
ゾチアゾリウム・Pートルエンスルホネート (N) 2ー(Pーニトロスチリル)ーキノリン・Pー
トルエンスルホネート (O) フェノサフラン (P) ピナクリプトール・グリーン (Q) 2、3ージメチルー6ーニトローベンゾチアゾ
リウム・PートルエンスルホネートThe organic desensitizer is generally known to be directly used in a positive silver halide emulsion. Specific examples of such organic desensitizers are described in a number of patent specifications and literatures, all of which have the same action in the present invention. 39-20261, 4
0-26751, 43-13167, 45-8
833, 47-8746, 47-10197,
50-37530, JP-A-48-24734, 49-84639, 56-142525, U.S. Pat. Nos. 2,271,229, 2,541,472, and 30.
No. 35917, No. 3062651, No. 31244
No. 58, No. 3,326,687 and No. 3,671,254 can be used. Specific examples are shown below. (A) 1,3-diethyl-1′-methyl-2′-phenylimidazo [4,5-b] -quinoxalinol 3′-indolocarbocyanine iodide (B) pinacryptol yellow (C) 1,1 ′, 3,3, 3 ', 3'-hexamethyl-5,5'-dinitroindocarbocyanine-P-toluenesulfonate (D) 5,5-dichloro-3,3'-diethyl-6,
6 'dinitrothiacarbocyanine iodide (E) 1,1'-dimethyl-2,2'diphenyl-3,3'-indolocarbocyanine bromide (F) 1,1', 3,3'-tetraethylimidazo [4 5,5-b] quinoxanocarbocyanine chloride (G) 5-m-nitrobenzylidene rhodanine (H) 6-chloro-4-nitro-nitrobenzotriazole (I) 1,1'-dibutyl-4,4'-bipyridinium. Dibromide (J) 1,1'-Ethylene-2,2'-Bipyridinium dibromide (K) 4- (Pn-amyloxyphenyl) -2,6
Di (P-ethylphenyl) thiapyrium perchlorate (L) 2-mercapto-4-methyl-5-nitrothiazole (M) 2- (O-nitrostyryl) -3-ethylbenzothiazolium P-toluenesulfonate (N) 2- (P -Nitrostyryl) -quinoline / P-toluenesulfonate (O) phenosafuran (P) pinacryptol green (Q) 2,3-dimethyl-6-nitro-benzothiazolium / P-toluenesulfonate
【0019】有機減感剤の使用量は、ハロゲン化銀1モ
ル当り0.2〜200mg、好ましくは1〜50mgの
範囲で選択される。添加時期は、熟成終了後に添加する
のが一般的である。The amount of the organic desensitizer to be used is selected in the range of 0.2 to 200 mg, preferably 1 to 50 mg, per mol of silver halide. The time of addition is generally added after aging.
【0020】本発明に用いられるアルミニウム支持体
は、印刷用として用いられる表面処理されたアルミニウ
ム板であり、一般的に行われる粗面化処理(いわゆるグ
レイニング)がなされたものである。その粗面化には、
前述のごとく、機械的粗面化処理、化学的粗面化処理、
及び電解粗面化処理、及びこれらの方法を併用した粗面
化方法が用いられる。本発明においては、直径0.03
〜0.30μmのピットを100μm2,当たり500個
以上有し、且つそれらのピットの平均直径が0.05〜
0.20μmである粗面のアルミニウム板が好ましい。The aluminum support used in the present invention is a surface-treated aluminum plate used for printing, which has been subjected to a general surface roughening treatment (so-called graining). In the roughening,
As mentioned above, mechanical surface roughening, chemical surface roughening,
And an electrolytic surface roughening treatment, and a surface roughening method using these methods in combination. In the present invention, a diameter of 0.03
Have at least 500 pits of 0.30 μm per 100 μm 2 , and the average diameter of those pits is 0.05 to
A rough aluminum plate of 0.20 μm is preferred.
【0021】本発明者等は、本発明が対象とする平版印
刷版において、画質、インキ受理性、耐刷力を支配する
転写現像銀の出来方がアルミ板の粗面状態に関係してい
るのではないかとの考えに基づいて鋭意検討した結果、
極めて微小なピット(孔)が多数存在する粗面化され陽
極酸化されたアルミ板を用いることにより、画質に優
れ、印刷に対して非常に強固な転写銀を形成することを
見出だした。即ち、前述した特定の粗面アルミニウム板
を用いている本発明の平版印刷版は、ハロゲン化銀乳剤
層中で、拡散転写現像液に含まれるハロゲン化銀溶剤に
より、速やかに溶解され、該アルミ表面上に拡散され、
多数の微小ピットの存在により好ましい拡散コントロー
ルが生じ、高画質につながるものと推定している。ま
た、好ましい拡散転写現像により、転写銀が多数の微小
ピットの中に形成されて投錨的効果を有し、しかもその
転写銀が連続した緻密な親油性の層を形成してアルミ板
に接着しているため、長い印刷でも転写銀が欠落せず、
高耐刷力を示すものと考えられる。The inventors of the present invention have found that in a lithographic printing plate to which the present invention is directed, the quality of transfer developed silver which governs image quality, ink receptivity, and printing durability is related to the rough surface state of the aluminum plate. As a result of intensive studies based on the idea that
It has been found that by using a roughened and anodized aluminum plate having a large number of extremely small pits (holes), transfer silver excellent in image quality and very strong for printing is formed. That is, the lithographic printing plate of the present invention using the specific roughened aluminum plate described above is rapidly dissolved in a silver halide emulsion layer by a silver halide solvent contained in a diffusion transfer developer, and Diffused on the surface,
It is presumed that the presence of a large number of small pits produces favorable diffusion control, leading to high image quality. Further, by the preferred diffusion transfer development, transfer silver is formed in a large number of fine pits and has an anchoring effect, and the transfer silver forms a continuous dense lipophilic layer and adheres to the aluminum plate. Transfer silver is not lost even in long printing,
It is considered to show high printing durability.
【0022】本発明に用いられる粗面化され陽極酸化さ
れたアルミ板は、走査型電子顕微鏡を用い50,000
倍位の拡大倍率の写真により、容易に確認することがで
きる。ピットは0.03〜0.30μmの直径を有する
ものが100μm2,当たり500個、好ましくは約1,
000個以上存在する。上限は約15,000個までが
好ましい。0.03〜0.30μmの直径を有するピッ
トの平均直径は0.05〜0.20μm、好ましくは
0.05〜0.15μmである。ピットの直径は、円形
以外の形状のものについてはその直径は円形と見做した
ときの寸法である。このピットの中心深さは、ピットの
直径に対して1/3(0.01〜0.10μm)以上、
好ましくは1/2(0.015〜0.15μm)〜3
(0.03〜0.90μm)くらいが望ましい。The roughened and anodized aluminum plate used in the present invention was obtained by using a scanning electron microscope at 50,000.
The photograph can be easily confirmed by a photograph of a magnification of about twice. The pits have a diameter of 0.03 to 0.30 μm, and 500 pits per 100 μm 2 , preferably about 1,
There are 000 or more. The upper limit is preferably up to about 15,000. The average diameter of the pits having a diameter of 0.03 to 0.30 μm is 0.05 to 0.20 μm, preferably 0.05 to 0.15 μm. The pit diameter is a dimension when the diameter of a pit having a shape other than a circle is regarded as a circle. The center depth of this pit is 1/3 (0.01 to 0.10 μm) or more of the pit diameter,
Preferably 1 / (0.015 to 0.15 μm) to 3
(0.03 to 0.90 μm) is desirable.
【0023】前記の特開昭56−28893号公報には
機械的粗面化と化学的エッチングおよび電解粗面化を併
用することによりアルミニウム表面にプラトー(第1次
構造)とピット(プラトーの表面に出来る第2次構造)
からなる複合構造の砂目が記載されている。本発明の微
小ピットは、平均直径3〜15μmの大きなピット(プ
ラトー)の上に存在する複合構造を有するものが好まし
い。微小ピットの投影面積は5〜40%程度が好まし
く、前記の大きなピット(プラトー)の投影面積は50
〜95%程度が好ましい。中心線平均粗さ(Ra)は
0.3〜1.0μmの範囲が好ましい。このような本発
明の表面形状を有するアルミ板は、機械的粗面化処理、
化学的粗面化処理、電解粗面化処理の条件、陽極酸化処
理する方法によって比較的容易に見出すことができる。
前記の微小ピットが500個より少いか若しくは前記の
微小ピットが無く大きなピット(プラトー)のみの場
合、さらに平均直径0.30μmのピットが100μm
2,当たり500個以上の場合であっても本発明の平版印
刷版に比べて劣ったインキ受理性と耐刷力しか得られな
い。Japanese Unexamined Patent Publication No. Sho 56-28893 discloses that a plateau (primary structure) and a pit (surface of a plateau) are formed on an aluminum surface by using both mechanical roughening, chemical etching and electrolytic surface roughening. Secondary structure)
The grain of a composite structure consisting of The micro pit of the present invention preferably has a composite structure existing on a large pit (plateau) having an average diameter of 3 to 15 μm. The projected area of the small pit is preferably about 5 to 40%, and the projected area of the large pit (plateau) is 50%.
About 95% is preferable. The center line average roughness (Ra) is preferably in the range of 0.3 to 1.0 μm. The aluminum plate having such a surface shape of the present invention is subjected to mechanical roughening treatment,
It can be relatively easily found by the conditions of the chemical surface roughening treatment, the electrolytic surface roughening treatment, and the anodic oxidation method.
In the case where the number of the small pits is less than 500 or only the large pits without the small pits (plateaus), the pits having an average diameter of 0.30 μm are further 100 μm.
2 , Even if the number is 500 or more, only poor ink acceptability and printing durability can be obtained as compared with the lithographic printing plate of the present invention.
【0024】本発明に用いられる粗面化され陽極酸化さ
れたアルミ板の陽極酸化層の厚みは約0.3〜3.0μ
mの範囲が好ましい。尚、陽極酸化処理に先立ってデス
マット処理を施すことが好ましい。すなわち、粗面化処
理したアルミニウム基板を、10〜50%の熱硫酸(4
0〜60℃)や希薄なアルカリ(水酸化ナトリウム等)
で処理することにより表面に付着したスマットが除去さ
れる。The thickness of the anodized layer of the roughened and anodized aluminum plate used in the present invention is about 0.3 to 3.0 μm.
The range of m is preferred. Note that desmutting is preferably performed prior to the anodizing. That is, the surface-roughened aluminum substrate is replaced with 10 to 50% hot sulfuric acid (4%).
0-60 ° C) or dilute alkali (such as sodium hydroxide)
The smut adhered to the surface is removed by the treatment.
【0025】また、陽極酸化処理を行なった後、必要に
応じて後処理を行うことが出来る。例えば、英国特許第
1,230,447号に開示されたポリビニルホスホン
酸の水溶液中に浸漬処理する方法が用いられる。また、
必要に応じて、親水性高分子の下塗層を設けることも可
能であるが、その上に設ける感光層の性質により取捨選
択される。After the anodic oxidation treatment, a post-treatment can be performed if necessary. For example, a method of dipping in an aqueous solution of polyvinylphosphonic acid disclosed in British Patent No. 1,230,447 is used. Also,
If necessary, an undercoat layer of a hydrophilic polymer can be provided, but it is selected depending on the properties of the photosensitive layer provided thereon.
【0026】アルミニウム支持体の上に設けられる物理
現像核層の物理現像核としては、銀錯塩拡散転写法で通
常用いられる公知のものでよく、例えば金、銀等のコロ
イド、更にはパラジウム、亜鉛等の水溶性塩と硫化物を
混合した金属硫化物などが使用できる。これらの詳細及
びその製法については、特公昭48−30562号、特
開昭49−55402号、同53−21602号等の各
公報に記載されている技術が利用できる。The physical development nucleus of the physical development nucleus layer provided on the aluminum support may be a known one usually used in a silver complex salt diffusion transfer method, for example, a colloid of gold, silver or the like, furthermore, palladium, zinc or the like. A metal sulfide obtained by mixing a water-soluble salt such as sulfide with a sulfide can be used. With respect to these details and the production method thereof, techniques described in JP-B-48-30562, JP-A-49-55402, and JP-B-53-21602 can be used.
【0027】物理現像核層の上に設ける感光性ハロゲン
化銀乳剤に用いられるハロゲン化銀としては塩化銀、塩
臭化銀、塩沃臭化銀、塩沃化銀が用いられるが、いずれ
も塩化銀が80モル%以上、好ましくは90モル%以上
含まれるハロゲン化銀である。The silver halide used in the photosensitive silver halide emulsion provided on the physical development nucleus layer includes silver chloride, silver chlorobromide, silver chloroiodobromide and silver chloroiodide. It is a silver halide containing 80 mol% or more, preferably 90 mol% or more of silver chloride.
【0028】本発明では感光性ハロゲン化銀乳剤とし
て、直接ポジ用ハロゲン化銀乳剤を使用してネガ型の平
版印刷版とすることもできる。直接ポジ用ハロゲン化銀
乳剤については、米国特許第3,501,307号明細
書などに開示されている。In the present invention, a negative-type lithographic printing plate can be prepared by using a direct positive silver halide emulsion as the photosensitive silver halide emulsion. The direct positive silver halide emulsion is disclosed in U.S. Pat. No. 3,501,307.
【0029】乳剤の混合法としては順混合、逆混合、同
時混合など公知の方法のいずれであってもよい。また乳
剤の調製方法としてはアンモニア法、中性法、酸性法い
ずれの方法であってもよい。ハロゲン化銀粒子のサイズ
分布は単分散、ヘテロ分散のいずれでもよいが、粒子感
度の均一性のために単分散が好ましい。また粒子の晶癖
は立方体、八面体、その他どんなものであってもよい。
粒子サイズは1μm以下、好ましくは0.5μm以下が
よい。更に好ましくは0.3μm以下がよい。これは現
像銀粒子の荒れを防止するとともに、省銀のために微粒
子化が必要なためである。The method of mixing the emulsion may be any of known methods such as forward mixing, reverse mixing, and simultaneous mixing. The emulsion may be prepared by any of the ammonia method, neutral method and acidic method. The size distribution of the silver halide grains may be either monodisperse or heterodisperse, but monodisperse is preferred for uniformity of grain sensitivity. The crystal habit of the particles may be cubic, octahedral, or any other.
The particle size is 1 μm or less, preferably 0.5 μm or less. More preferably, it is 0.3 μm or less. This is because it is necessary to prevent the developed silver particles from being roughened and to make them finer for saving silver.
【0030】感光性ハロゲン化銀乳剤の保護コロイドと
して、酸処理ゼラチン、アルカリ処理ゼラチン、ゼラチ
ン誘導体、グラフト化ゼラチン等の各種ゼラチンを用い
ることが出来る他、ポリビニルピロリドン、各種でんぷ
ん、アルブミン、ポリビニルアルコール、アラビアゴ
ム、ヒドロキシエチルセルロース等の親水性高分子化合
物を含有することができる。As the protective colloid of the photosensitive silver halide emulsion, various gelatins such as acid-treated gelatin, alkali-treated gelatin, gelatin derivatives, and grafted gelatin can be used. In addition, polyvinylpyrrolidone, various starches, albumin, polyvinyl alcohol, It may contain a hydrophilic polymer compound such as gum arabic and hydroxyethyl cellulose.
【0031】このようにして調製された乳剤は、化学増
感剤によって化学増感(硫黄増感、金増感、還元増感な
ど)を施すことができる。しかし全く化学増感をしなく
てもよい。The emulsion thus prepared can be subjected to chemical sensitization (sulfur sensitization, gold sensitization, reduction sensitization, etc.) with a chemical sensitizer. However, no chemical sensitization is required.
【0032】本発明により得られるハロゲン化銀乳剤は
安定剤、カブリ防止剤、イラジエーション防止剤、膜物
性改質剤、界面活性剤、硬膜剤、マット剤、現像主薬な
どの一般の写真用に用いられる添加剤を含むことができ
る。The silver halide emulsion obtained according to the present invention can be used for general photographic purposes such as stabilizers, antifoggants, irradiation inhibitors, film physical property modifiers, surfactants, hardeners, matting agents and developing agents. Can be included.
【0033】このようにして調製したハロゲン化銀乳剤
層は、物理現像核層の上に直接塗設することができる
が、剥離性を容易にするためにゼラチン等の中間層を設
けてもよい。又、感光材料の表面を保護するためのゼラ
チンなどの親水性コロイド層を有していてもよい。The silver halide emulsion layer thus prepared can be coated directly on the physical development nucleus layer, but an intermediate layer of gelatin or the like may be provided for facilitating peelability. . Further, the material may have a hydrophilic colloid layer such as gelatin for protecting the surface of the photosensitive material.
【0034】本発明の平版印刷版は、主として印刷分野
で用いられる紫外光に富んだ光源、例えば水銀灯、超高
圧水銀灯、メタルハライド、あるいは紫外線アルゴンレ
ーザーなどの紫外線レーザー光源により露光される。
又、上記露光を施す前および施した後のいずれであって
も、明るい明室光下での長時間の安全な取扱いが出来
る。The lithographic printing plate of the present invention is exposed by an ultraviolet laser light source such as a mercury lamp, an ultra-high pressure mercury lamp, a metal halide, or an ultraviolet argon laser used mainly in the printing field.
In addition, before and after the exposure, long-time safe handling under bright light can be performed.
【0035】本発明の平版印刷版は、一般に像様露光後
アルカリ現像液で拡散転写現像処理され、残留乳剤被膜
を除去した後、引続き必要ならば、中和液、定着液、感
脂化液、給湿液等の製版及び印刷処理が施される。現像
液は、ハイドロキノンなどの現像主薬を含む通常の写真
用アルカリ現像液、或はそれらを材料中に含ませて現像
液中には実質的に現像主薬を含まない、いわゆるアルカ
リ性活性化現像液等いかなるものでも使用できる。ま
た、これら現像液の中には各種目的に応じて、特公昭5
1−486号、特開昭52−150105号等に記載さ
れている化合物が添加される。The lithographic printing plate of the present invention is generally subjected to diffusion transfer development with an alkali developing solution after imagewise exposure to remove a residual emulsion film, and if necessary, if necessary, a neutralizing solution, a fixing solution, and a sensitizing solution. And a plate making and printing process with a humidifying liquid or the like. The developer may be an ordinary photographic alkali developer containing a developing agent such as hydroquinone, or a so-called alkaline activated developer in which the material is contained in the material and the developer is substantially free of the developing agent. Anything can be used. Some of these developing solutions are used for various purposes.
Compounds described in JP-A-1-486 and JP-A-52-150105 are added.
【0036】本発明に用いられる中和液、定着液、感脂
化液、給湿液等の組成その他は、それぞれの目的に応じ
て当該技術者の知る組成のものが使用できる。As the composition of the neutralizing solution, fixing solution, sensitizing solution, humidifying solution and the like used in the present invention, those having compositions known to those skilled in the art can be used according to the respective purposes.
【0037】[0037]
【実施例】以下、本発明を実施例によって説明するが、
勿論本発明はこれだけに限定されるものではない。The present invention will be described below with reference to examples.
Of course, the present invention is not limited to this.
【0038】実施例1 電解粗面化処理と陽極酸化によって、平均直径約5μm
のプラトー上に直径0.03〜0.30μmのピットを
100μm2,当たり約5,600個有し、且つそれらの
ピットの平均直径が0.08μmである厚さ0.3mm
のアルミニウム板(A)を得た。このアルミ板は粗面化
処理後に陽極酸化したものであり、平均粗さ(Ra)は
0.5〜0.6μmであった。Example 1 An average diameter of about 5 μm was obtained by electrolytic surface roughening treatment and anodic oxidation.
0.3 mm thick having about 5,600 pits having a diameter of 0.03 to 0.30 μm per 100 μm 2 on the plateau and having an average diameter of 0.08 μm for the pits
An aluminum plate (A) was obtained. This aluminum plate was anodized after the surface roughening treatment, and had an average roughness (Ra) of 0.5 to 0.6 μm.
【0039】上記前処理を施したアルミニウム支持体上
に、カーレー・リー(Carey,Lea)法で調製した
銀ゾルを、銀量が10mg/m2になるように塗設し
た。On the pretreated aluminum support, a silver sol prepared by the Carey, Lea method was applied so that the silver amount was 10 mg / m 2 .
【0040】続いて、塩化銀95モル%を含む塩臭化銀
1モル当り塩化ロジウム塩を10-5モル使用して通常の
方法でハロゲン化銀の沈澱を行い、物理熟成を施して平
均粒径0.2μmの乳剤を得た。この乳剤を脱塩し、再
溶解したあとに有機減感剤としてピナクリプトール・イ
エローをハロゲン化銀1モル当り7mgを加え、更に安
定剤、界面活性剤を加えて調製をした。Subsequently, silver halide was precipitated by a conventional method using 10-5 mol of a rhodium chloride salt per mol of silver chlorobromide containing 95 mol% of silver chloride, and subjected to physical ripening to obtain an average grain size. An emulsion having a diameter of 0.2 μm was obtained. This emulsion was desalted and redissolved. Then, 7 mg per mol of silver halide of pinacritol yellow was added as an organic desensitizer, and a stabilizer and a surfactant were further added.
【0041】この乳剤を銀量が1.5g/m2、ゼラチ
ン量が1.0g/m2になるように、銀ゾルを塗設した
上記アルミニウム支持体の上に塗布し、乾燥した。This emulsion was coated on the aluminum support coated with silver sol and dried so that the silver content was 1.5 g / m 2 and the gelatin content was 1.0 g / m 2 .
【0042】以上のようにして作製した平版印刷版を、
明室プリンターを用いて像様露光した後、下記に示すア
ルカリ現像液中で20℃、30秒間拡散転写現像を行っ
た。 フェニドンB=4ーメチルー1ーフェニルー3ーピラゾ
リドンThe lithographic printing plate produced as described above is
After imagewise exposure using a bright room printer, diffusion transfer development was performed at 20 ° C. for 30 seconds in the following alkaline developer. Phenidone B = 4-methyl-1-phenyl-3-pyrazolidone
【0043】拡散転写現像後、乳剤層を剥離することに
よって、拡散転写銀画像の形成された平版印刷版が作製
できた。After the development by diffusion transfer, the emulsion layer was peeled off, whereby a lithographic printing plate on which a diffusion transfer silver image was formed was produced.
【0044】また、この試料を約500ルックスの明室
で1時間照射した後に上記と同様に露光、現像処理した
場合、感度、調子の変化はなく、拡散転写銀画像の形成
された平版印刷版を作製できた。更に、この試料に像様
露光を与えた後、上記の明室で15分間照射して同様に
現像処理した場合、やはり感度、調子の変化はなかっ
た。When this sample was irradiated in a bright room of about 500 lux for 1 hour and then exposed and developed in the same manner as above, there was no change in sensitivity and tone, and a lithographic printing plate having a diffusion-transferred silver image formed thereon. Could be produced. Further, when the sample was exposed to light in the above-mentioned light room for 15 minutes after being subjected to imagewise exposure and then developed similarly, there was no change in sensitivity or tone.
【0045】実施例2 上記実施例1において、ピナクリプトール・イエローの
代わりに前述した有機減感剤(A)、(E)、(O)、
(P)の夫々を再溶解後の乳剤に添加する以外はまった
く同様のやり方で四種類の平版印刷版を作製した。実施
例1と同様に明室環境適正を試験したところ、感度、調
子ともに良好な平版印刷版が得られた。Example 2 In the above-mentioned Example 1, the organic desensitizers (A), (E), (O), and
Four types of lithographic printing plates were prepared in exactly the same manner except that each of (P) was added to the re-dissolved emulsion. When the suitability for the light room environment was tested in the same manner as in Example 1, a lithographic printing plate having good sensitivity and tone was obtained.
【0046】比較例 ハロゲン化銀乳剤沈殿時には塩化ロジウム塩を添加せ
ず、しかも再溶解後の乳剤にピナクリプトール・イエロ
ーをハロゲン化銀1モル当り0.15mg加える以外
は、実施例1と同様にして平版印刷版を作製した。この
試料を約300ルックスの明室で30分照射した後で露
光、現像処理した場合、拡散転写銀画像は極めて薄い画
像であった。COMPARATIVE EXAMPLE The procedure of Example 1 was repeated, except that no rhodium chloride salt was added during the precipitation of the silver halide emulsion, and that 0.15 mg of pinakryptol yellow was added per mol of silver halide to the re-dissolved emulsion. A lithographic printing plate was prepared. When this sample was exposed and developed after irradiating it in a bright room of about 300 lux for 30 minutes, the diffusion transfer silver image was an extremely thin image.
【0047】実施例3 実施例1と実施例2で作製した平版印刷版を、アグファ
(Agfa)社製のコピーラピッド定着液(Fixe
r)で版面処理した後、印刷機ハイデルベルグTOK
(Heidelberg社製オフセット印刷機の商標)にかけ印刷
したところ、10万枚の印刷ができ、印刷画質も良好で
あった。比較例の試料も同様に印刷試験をしたが、イン
キが殆ど乗らず平版印刷版として機能しなかった。Example 3 The lithographic printing plates prepared in Examples 1 and 2 were applied to a copy rapid fixer (Fixe) manufactured by Agfa.
r), after the surface treatment, the printing press Heidelberg TOK
(Heidelberg's offset printing machine trademark), printing was performed on 100,000 sheets, and the print quality was good. The sample of the comparative example was also subjected to a printing test in the same manner, but hardly covered with ink and did not function as a lithographic printing plate.
【0048】実施例4 電解粗面化処理の違いと陽極酸化によって、以下の表1
に示す表面形状の厚さ0.3mmのアルミニウム板を得
た。Example 4 The following Table 1 shows the difference between the electrolytic surface roughening treatment and the anodic oxidation.
An aluminum plate having a surface shape shown in FIG.
【0049】[0049]
【表1】 [Table 1]
【0050】表1において、ピット数は平均直径約5μ
mのプラトー上に存在する直径0.03〜0.30μm
のピットを100μm2当たりの個数であり、平均直径
はそれらのピットの直径の平均値である。これらのアル
ミ板の平均粗さ(Ra)は0.5〜0.6μmであっ
た。In Table 1, the number of pits is about 5 μm on average.
0.03 to 0.30 μm on the plateau of m
Are the number of pits per 100 μm 2 , and the average diameter is the average value of the diameters of those pits. The average roughness (Ra) of these aluminum plates was 0.5 to 0.6 μm.
【0051】これらのアルミ支持体上に、実施例1と同
様にして、平版印刷版A−1、B−1、C−1、D−
1、及びE−1を作製した。On these aluminum supports, in the same manner as in Example 1, planographic printing plates A-1, B-1, C-1, D-
1 and E-1 were produced.
【0052】このようにして得られた平版印刷版に像露
光を行ない、実施例1に記載の拡散転写現像液で現像を
行なった後、直ちに流水でゼラチン層を洗い流し(ウォ
ッシュオフ)した。版面が乾かないうちに版面保護液を
脱脂綿等で塗布し乾燥させる。この様にして作成した平
版印刷版を、印刷機ハイデルベルグTOK(Heidelberg
社製オフセット印刷機の商標)にかけ、画質及び耐刷力
を評価した。The lithographic printing plate thus obtained was subjected to image exposure, developed with the diffusion transfer developer described in Example 1, and immediately washed (washed off) with a running water. Before the plate surface dries, apply a plate surface protection solution with absorbent cotton or the like and dry. The lithographic printing plate created in this way is used as a printing press Heidelberg TOK (Heidelberg
Image quality and printing durability.
【0053】画質については、密着原稿を通して露光さ
れ、現像された印刷版面上で、10μmのネガ罫線及び
ポジ罫線が同時に再現できるものを○とし、15μmの
ネガ罫線及びポジ罫線が同時に再現できるものを△と
し、20μmのネガ罫線及びポジ罫線が同時に再現でき
るものを×とした。インキは、大日本インキ社製ニュー
チャンピオンFグロス墨Nを用い、耐刷力は版圧を5ミ
リに設定して画像部のインキ乗りの不良、あるいは線飛
びが生じる時のいずれかにより印刷が不可能となったと
きの印刷枚数で評価した。結果を表2に示す。Regarding the image quality, a mark that can simultaneously reproduce a negative ruled line and a positive ruled line of 10 μm on the printing plate surface exposed and developed through a contact original is indicated by a circle, and a pattern that can be simultaneously reproduced by a negative ruled line and a positive ruled line of 15 μm. The symbol Δ indicates that a negative ruled line and a positive ruled line of 20 μm can be simultaneously reproduced. The ink used is New Champion F Gloss Black N manufactured by Dainippon Ink and the printing durability is set to 5 mm. The printing pressure is set to 5 mm. Evaluation was made based on the number of printed sheets when it became impossible. Table 2 shows the results.
【0054】[0054]
【表2】 [Table 2]
【0055】表2の結果より明かなように、直径0.0
3〜0.30μmのピットを100μm2当たり500
個以上有し、 且つそれらのピットの平均直径が0.0
5〜0.20μmであるアルミ板を用いた平版印刷版A
−1、B−1、及び、C−1は画質、及び、耐刷力に優
れたものであることが判った。一方、ピットの平均直径
が0.20μm以上のアルミ板を用いた平版印刷版D−
1、及びE−1の結果をみると、A−1、B−1、及び
C−1の方が、より好ましい事がわかる。As is clear from the results in Table 2, the diameter 0.0
3 to 0.30 μm pits of 500 per 100 μm 2
And the average diameter of those pits is 0.0
Lithographic printing plate A using aluminum plate of 5 to 0.20 μm
-1, B-1 and C-1 were found to be excellent in image quality and printing durability. On the other hand, a lithographic printing plate D- using an aluminum plate having an average pit diameter of 0.20 μm or more.
From the results of E-1 and E-1, it can be seen that A-1, B-1, and C-1 are more preferable.
【0056】[0056]
【発明の効果】本発明により、実質的な明室環境下で取
扱い可能で、高画質、高耐刷力の銀錯塩拡散転写方式を
用いたアルミニウム平版印刷版が製造できる。According to the present invention, it is possible to manufacture an aluminum lithographic printing plate which can be handled in a substantially bright room environment, uses a silver complex salt diffusion transfer system, and has high image quality and high printing durability.
フロントページの続き (58)調査した分野(Int.Cl.7,DB名) G03F 7/07 B41N 1/08 G03F 7/09 Continuation of the front page (58) Field surveyed (Int.Cl. 7 , DB name) G03F 7/07 B41N 1/08 G03F 7/09
Claims (2)
支持体とハロゲン化銀乳剤層の間に物理現像核層を有す
る平版印刷版において、該ハロゲン化銀乳剤中にハロゲ
ン化銀1モル当たり10 -8 〜10 -3 モルの水溶性ロジウ
ム塩、及びハロゲン化銀1モル当たり0.2〜200m
gの有機減感剤を含んだことを特徴とする平版印刷版。In a lithographic printing plate having a physical development nucleus layer between a roughened and anodized aluminum support and a silver halide emulsion layer, the lithographic printing plate contains 10 per mole of silver halide in the silver halide emulsion. -8 to 10 -3 mol of water-soluble rhodium
0.2 to 200 m per mole of silver salt and silver halide
A lithographic printing plate comprising g of an organic desensitizer.
100μm2当たり500個以上有し、且つそれらのピッ
トの平均直径が0.05〜0.20μmである粗面のア
ルミニウム板を支持体とする請求項1記載の平版印刷
版。2. A rough aluminum plate having at least 500 pits having a diameter of 0.03 to 0.30 μm per 100 μm 2 and having an average diameter of the pits of 0.05 to 0.20 μm. The lithographic printing plate according to claim 1, wherein