JP3297590B2 - Neon tube for display - Google Patents
Neon tube for displayInfo
- Publication number
- JP3297590B2 JP3297590B2 JP09401296A JP9401296A JP3297590B2 JP 3297590 B2 JP3297590 B2 JP 3297590B2 JP 09401296 A JP09401296 A JP 09401296A JP 9401296 A JP9401296 A JP 9401296A JP 3297590 B2 JP3297590 B2 JP 3297590B2
- Authority
- JP
- Japan
- Prior art keywords
- glass
- metal
- display
- neon tube
- bead
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、電気機器の電圧表
示に用いられる表示用ネオン管に関し、特に使用される
明るさの雰囲気によっても点灯電圧が影響されない表示
用ネオン管に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a display neon tube used for displaying voltage of electric equipment, and more particularly to a display neon tube whose lighting voltage is not affected by an atmosphere of brightness used.
【０００２】[0002]
【従来の技術】従来より電気機器の電圧表示のためにネ
オン管が広く用いられており、その構成は図４に示すよ
うに、主電極１０、１１を相対向してビードガラス２を
挿通させて設け、このビードガラス２でガラス管１の開
口端を封止、さらにガラスバルブ１の内部にネオンガス
を封入したものである。2. Description of the Related Art Conventionally, a neon tube has been widely used for indicating the voltage of electric equipment, and as shown in FIG. 4, the main electrodes 10 and 11 are opposed to each other and a bead glass 2 is inserted therethrough. The bead glass 2 seals the open end of the glass tube 1, and the glass bulb 1 is filled with neon gas.
【０００３】かかる構成のネオン管は、例えば図５に示
すようにコンデンサ１２の充電電圧を表示するために、
コンデンサ１２に抵抗を介して並列に接続され、そして
コンデンサ１２の充電電圧が所定の電圧に充電された時
点でネオン管１３を点灯するように使用される。[0005] The neon tube having such a configuration is used to display the charging voltage of the capacitor 12 as shown in FIG.
The capacitor 12 is connected in parallel via a resistor, and is used to turn on the neon tube 13 when the charged voltage of the capacitor 12 is charged to a predetermined voltage.
【０００４】[0004]
【発明が解決しようとする課題】ネオン管は、その製作
に際しては、表示する電圧の大きさに応じて、電極間
隔、封入ガス圧等を考慮して設定しているが、使用され
る明るさの雰囲気、即ち明るい所と暗い所とでは、点灯
電圧に大きな差異を生じる問題点を有している。When a neon tube is manufactured, the neon tube is set in consideration of the electrode spacing, the gas pressure, etc., according to the magnitude of the voltage to be displayed. Atmosphere, that is, a bright place and a dark place, have a problem that a large difference occurs in the lighting voltage.
【０００５】したがって本発明は、かかる問題点を改善
すべく成したものであり、明・暗の使用条件下でも点灯
電圧に差異を生じない表示用ネオン管を提供することを
目的とする。SUMMARY OF THE INVENTION Accordingly, the present invention has been made to solve such a problem, and an object of the present invention is to provide a display neon tube which does not cause a difference in lighting voltage even under bright and dark use conditions.
【０００６】[0006]
【課題を解決するための手段】かかる目的を達成するた
めに、本発明はガラスバルブ内に挿通した一対の金属線
に焼結金属体を取り付けてなる。According to the present invention, a sintered metal body is attached to a pair of metal wires inserted into a glass bulb.
【０００７】本発明の請求項１に記載の発明は、ビード
ガラスと、このビードガラスを挿通して相対向して前記
ビードガラスに設けられる一対の金属線と、前記ビード
ガラスで開口端が封止されるガラスバルブと、前記ビー
ドガラスを挿通した金属線のうち前記ガラスバルブに位
置する方の金属線に取り付けられる焼結金属体と、前記
ガラスバルブに封入されるネオンガスとからなり、前記
焼結金属体は、高融点基体金属粉末と低融点の金属粉末
を溶剤に混練した混濁液に前記金属線先端部を浸漬塗布
し乾燥した後に、前記金属線が前記ガラスバルブに封止
される前に高温で焼結されて形成されたものである表示
用ネオン管である。焼結金属体の金属線への取り付け
は、金属線のガラスバルブへの封止前に、金属粉末と溶
剤の混濁液中に金属線を浸漬し、乾燥後に高温にて焼結
するので、強固に金属線に形成することができる。また
焼結金属体は、上記混濁液中に浸漬塗布し乾燥、高温焼
結するだけなので、大掛かりな装置を要せず、また作業
性良く形成することができる。そして、このような焼結
金属体を取り付けることによって明・暗の点灯電圧差が
著しく改善できる。 According to the first aspect of the present invention, there is provided a bead.
The glass and this bead glass are inserted and
A pair of metal wires provided on a bead glass;
A glass bulb having an open end sealed with glass;
Out of the metal wire through which the glass is inserted
A sintered metal body attached to the metal wire to be placed,
Consisting of neon gas sealed in a glass bulb,
Sintered metal body consists of high melting point base metal powder and low melting point metal powder
The tip of the metal wire is immersed and applied to a turbid liquid kneaded with a solvent.
After drying, the metal wire is sealed in the glass bulb
Indication that is formed by sintering at high temperature before
Neon tube. Attach sintered metal body to metal wire
Melts the metal wire before sealing the metal wire to the glass bulb.
The metal wire is immersed in the turbid liquid of the agent, dried and sintered at high temperature.
Therefore, it can be formed firmly on the metal wire. Also
The sintered metal body is immersed in the above turbid solution, dried, and fired at high temperature.
No need for large-scale equipment,
It can be formed well. And such sintering
By attaching a metal body, the lighting voltage difference between bright and dark
It can be significantly improved.
【０００８】[0008]
【０００９】[0009]
【００１０】以下本発明の実施の形態について説明す
る。図１は本発明の実施の形態を示す表示用ネオン管の
断面図であり、図において１は鉛ガラス、ソーダガラス
等で作成されるガラスバルブ、２はガラスバルブ１の開
口端を封止するビードガラス、３、４は電極、５、６は
電極を形成する焼結金属体、７、８はビードガラス２を
挿通してこのビードガラスに取り付けられるニッケル、
鉄、銅等の金属線であり、ガラスバルブ１内には放電電
圧を考慮した圧力のネオンガスが封入される。電極３、
４は、図２に示すように金属線７、８とこれに取り付け
られる焼結金属体５、６とで構成されており、この焼結
金属体５、６は、図３に示すように例えば基体金属であ
るバナジウムの高融点金属粉末の９０重量％と、低融点
の鉛、アルミニウム、インジウム等の金属粉末１０重量
％との混合粉末を水とで混練した混濁液中に金属線７、
８のバルブ内に位置される側を浸漬し、乾燥させた後、
４００〜５００℃の高温で焼成して作られる。なお、こ
の焼結金属体５、６の焼成は、最終工程であるガラスバ
ルブ１にネオンガスを封入、ビードガラスの溶融により
ガラスバルブ１を封止する際の加熱処理時の温度で焼成
しても良いし、ネオンガス封入、ガラスバルブの封止に
より先に、高温炉を用いて焼成しても良い。斯くの構成
よりなる本発明の表示用ネオン管の点灯電圧特性を確認
するために、ガラスバルブ１には外径４．２ｍｍφ、肉
厚０．５ｍｍ、金属線７、８には０．２ｍｍφの銅線に
ニッケルメッキを施したものを用い、金属焼結体５、６
には、バナジウム９０重量％とインジウム１０重量％の
混合金属粉末体の水溶混濁液９に金属線７、８を浸漬、
塗布、焼成したもの、ガラスバルブ１の内部にネオンガ
スを５０Ｔｏｒｒ封入して本発明の表示用ネオン管を５
個作成した。また図４にかかる構成の従来のものとし
て、ガラスバルブ、金属線、封入ガス等を本発明の表示
用ネオン管と同寸法、同素材にして５個作成して、図５
に示す表示回路で点灯電圧を確認し、次の結果を得た。An embodiment of the present invention will be described below. FIG. 1 is a cross-sectional view of a display neon tube showing an embodiment of the present invention. In FIG. 1, reference numeral 1 denotes a glass bulb made of lead glass, soda glass, or the like, and reference numeral 2 denotes an open end of the glass bulb 1. Bead glass, 3, 4 are electrodes, 5 and 6 are sintered metal bodies forming electrodes, 7, 8 are nickel that is inserted through the bead glass 2 and attached to the bead glass,
The glass bulb 1 is filled with a neon gas at a pressure in consideration of a discharge voltage. Electrode 3,
4 includes metal wires 7 and 8 and sintered metal bodies 5 and 6 attached thereto as shown in FIG. 2, and these sintered metal bodies 5 and 6 are, for example, as shown in FIG. The metal wire 7 was mixed in a turbid liquid obtained by kneading 90% by weight of a high melting point metal powder of vanadium as a base metal and 10% by weight of a low melting point metal powder such as lead, aluminum, and indium with water.
After immersing the side located in the valve of No. 8 and drying,
It is made by firing at a high temperature of 400 to 500 ° C. The firing of the sintered metal bodies 5 and 6 may be performed by filling a neon gas into the glass bulb 1 as a final step, and firing at a temperature at the time of a heat treatment when the glass bulb 1 is sealed by melting the bead glass. Alternatively, baking using a high-temperature furnace may be performed first by filling neon gas and sealing a glass bulb. In order to confirm the lighting voltage characteristics of the display neon tube of the present invention having such a configuration, the glass bulb 1 has an outer diameter of 4.2 mmφ, a wall thickness of 0.5 mm, and the metal wires 7 and 8 have a diameter of 0.2 mmφ. Using a copper wire plated with nickel, metal sintered bodies 5, 6
The metal wires 7 and 8 are immersed in an aqueous turbid solution 9 of a mixed metal powder body of 90% by weight of vanadium and 10% by weight of indium.
The neon gas for display according to the present invention is filled with 50 Torr of neon gas inside the glass bulb 1 after coating and firing.
Created. In addition, as a conventional one having the configuration shown in FIG. 4, five glass bulbs, metal wires, filled gas, etc. are formed in the same size and the same material as the display neon tube of the present invention.
The lighting voltage was confirmed by the display circuit shown in (1), and the following results were obtained.
【００１１】 本発明品（ｎ＝５） 従来品（ｎ＝５） 点灯雰囲気 平均値 （範 囲） 平均値（範 囲） 明 285Ｖ（290〜275Ｖ） 290Ｖ（300〜285Ｖ） 暗 290Ｖ（300〜285Ｖ） 310Ｖ（315〜295Ｖ） 以上の結果より明らかなように、本発明品は暗い雰囲気
での点灯電圧は明るい時に比べてやや高いものの差異は
少ない。これに比して従来品は明と暗との差異は２０Ｖ
とその電圧差は大きく、本発明品が明・暗の雰囲気での
点灯電圧差を著しく改善していることを明白に示してい
る。Product of the present invention (n = 5) Conventional product (n = 5) Lighting atmosphere Average value (range) Average value (range) Lighting 285 V (290 to 275 V) 290 V (300 to 285 V) Dark 290 V (300 to 285 V) 285 V) 310 V (315 to 295 V) As is clear from the above results, the lighting voltage of the present invention is slightly higher in a dark atmosphere than in a bright environment, but the difference is small. Compared with this, the difference between light and dark is 20 V for the conventional product
And the voltage difference is large, which clearly shows that the present invention significantly improves the lighting voltage difference in a bright and dark atmosphere.
【００１２】[0012]
【００１３】[0013]
【発明の効果】以上述べたように、本発明の表示用ネオ
ン管は、ビードガラスに設けられた一対の金属線に焼結
金属体を取り付けて電極を形成したことにより、明・暗
による点灯電圧の差を非常に少なくすることができ、安
定した電圧の表示に供することができるものである。As described above, the neon tube for display of the present invention is formed by sintering a pair of metal wires provided on a bead glass to form electrodes by forming electrodes, thereby providing light / dark lighting. The voltage difference can be made very small, and a stable voltage can be displayed.
【図１】本発明の実施の形態の表示用ネオン管を示す断
面図FIG. 1 is a sectional view showing a display neon tube according to an embodiment of the present invention.
【図２】図１にかかる表示用ネオン管の金属線に焼結金
属体を取り付けてなる拡大断面図FIG. 2 is an enlarged sectional view of the neon tube for display according to FIG. 1 in which a sintered metal body is attached to a metal wire.
【図３】金属粉末の混濁液を金属線に塗布している状態
図FIG. 3 is a diagram showing a state in which a turbid liquid of a metal powder is applied to a metal wire.
【図４】従来の表示用ネオン管の断面図FIG. 4 is a cross-sectional view of a conventional display neon tube.
【図５】表示用ネオン管を使用した電圧表示回路図FIG. 5 is a voltage display circuit diagram using a display neon tube.
１ ガラスバルブ ２ ビードガラス ３ 電極 ５ 焼結金属体 ６ 焼結金属体 ７ 金属線 ８ 金属線 DESCRIPTION OF SYMBOLS 1 Glass bulb 2 Bead glass 3 Electrode 5 Sintered metal body 6 Sintered metal body 7 Metal wire 8 Metal wire
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭60−77343（ＪＰ，Ａ) 実開 昭50−133780（ＪＰ，Ｕ) 実開 昭56−9667（ＪＰ，Ｕ) (58)調査した分野(Int.Cl.7，ＤＢ名) H01J 61/067 H01J 9/04 H01J 61/36 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-60-77343 (JP, A) JP-A-50-133780 (JP, U) JP-A-56-9667 (JP, U) Field (Int.Cl. 7 , DB name) H01J 61/067 H01J 9/04 H01J 61/36
Claims (1)
通して相対向して前記ビードガラスに設けられる一対の
金属線と、前記ビードガラスで開口端が封止されるガラ
スバルブと、前記ビードガラスを挿通した金属線のうち
前記ガラスバルブに位置する方の金属線に取り付けられ
る焼結金属体と、前記ガラスバルブに封入されるネオン
ガスとからなり、前記焼結金属体は、高融点基体金属粉
末と低融点の金属粉末を溶剤に混練した混濁液に前記金
属線先端部を浸漬塗布し乾燥した後に、前記金属線が前
記ガラスバルブに封止される前に高温で焼結されて形成
されたものである表示用ネオン管。1. A bead glass, a pair of metal wires provided in the bead glass so as to face each other through the bead glass, a glass bulb whose opening end is sealed by the bead glass, and the bead glass. And a neon gas sealed in the glass bulb, wherein the sintered metal body is a high melting point base metal powder.
Powder and a low melting point metal powder kneaded in a solvent
After dip coating and drying the tip of the metal wire, the metal wire
Formed by sintering at high temperature before sealing in glass bulb
Display for the neon tube is one that is.