JP3275540B2 - How to paint a car body - Google Patents
How to paint a car bodyInfo
- Publication number
- JP3275540B2 JP3275540B2 JP13332694A JP13332694A JP3275540B2 JP 3275540 B2 JP3275540 B2 JP 3275540B2 JP 13332694 A JP13332694 A JP 13332694A JP 13332694 A JP13332694 A JP 13332694A JP 3275540 B2 JP3275540 B2 JP 3275540B2
- Authority
- JP
- Japan
- Prior art keywords
- coating
- organic solvent
- foreign matter
- boiling organic
- painting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は自動車車体の塗装方法に
関するものであり、塗膜にゴミ、ホコリ等の異物が混入
することによる塗膜外観品質の低下を防止する技術に関
するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for coating an automobile body, and more particularly to a technique for preventing a coating film from deteriorating in appearance quality due to foreign matter such as dust or dust entering the coating film.
【０００２】[0002]
【従来の技術】自動車の車体には、その防錆と美観付与
を主目的として塗装が施されている。一般に、塗料は１
つの材料により諸性能をすべて満足することはできず、
自動車車体の塗膜構成としては、従来、前処理した鋼板
基地表面上に、順に下塗り（電着）塗膜、中塗り塗膜、
上塗り塗膜を積層してなるものが一般的である。さら
に、上塗り塗膜の構成としては、ソリッド塗装における
ような一層のもの、あるいは、メタリック塗装、パール
トーン塗装におけるようなベースコートとその上部に設
けられるクリアコートからなる二層のものがある。この
ような自動車車体の塗装において自動車の商品価値を高
める上で外観品質は極めて重要であり、例えば、塗膜中
にゴミ、ホコリ等の異物が混入し外観不良が生じてしま
うといったことは極力防止する必要がある。2. Description of the Related Art A vehicle body is coated with a coating mainly for the purpose of preventing rust and imparting an aesthetic appearance. Generally, 1 paint
One material cannot satisfy all the performances,
Conventionally, as a coating composition of an automobile body, an undercoating (electrodeposition) coating, an intermediate coating,
The thing which laminates a top coat is common. Further, as the structure of the top coat, there are a single layer as in solid coating, and a two-layer structure composed of a base coat and a clear coat provided on the base coat as in metallic coating and pearl tone coating. Appearance quality is extremely important in increasing the commercial value of automobiles in coating such automobile bodies. For example, foreign matter such as dirt and dust in the paint film is prevented from causing poor appearance as much as possible. There is a need to.
【０００３】図４は、代表的な自動車車体の塗装工程の
一例を示すものであるが、各塗料塗装工程間において
は、塗膜品質を高めるために次のような工程が設けられ
ている。すなわち、図４に示すように、中塗り塗装５５
を行なう前には、下塗り塗装（電着塗装）５２において
形成された下塗り塗面の品質不良箇所をサンドペーパー
等での研ぎにより修正する研ぎ工程５３、および、車体
内外表面及び鋼板の合せ目に付着しているゴミ、研ぎカ
ス等の異物をエアブロー等により除去する中塗り準備工
程５４が設けられている。また同様に、上塗り塗装５８
を行なう前には、中塗り塗装５５において形成された中
塗り塗面の品質不良箇所をサンドペーパー等での研ぎに
より修正する研ぎ工程５６、および自動車ボデー内外表
面及び鋼板の合せ目に付着しているゴミ、研ぎカス等の
異物をエアブロー等により除去する上塗り準備工程５７
が設けられている。FIG. 4 shows an example of a typical painting process for a vehicle body. The following processes are provided between the respective painting processes in order to improve the quality of the coating film. That is, as shown in FIG.
Before performing the polishing, a poor quality portion of the undercoating surface formed in the undercoating (electrodeposition coating) 52 is corrected by sharpening with sandpaper or the like, and a sharpening process 53 is performed. An intermediate coating preparation step 54 is provided for removing foreign substances such as adhering dust and sharpened chips by air blow or the like. Similarly, the top coat 58
Before performing the polishing step 56, a poor quality portion of the intermediate coating surface formed in the intermediate coating 55 is corrected by sharpening with sandpaper or the like, Top coating preparation step 57 for removing foreign matter such as dust and sharpened chips by air blow or the like.
Is provided.
【０００４】しかしながら、前述のように中塗り準備工
程５４および上塗り準備工程５７においてエアブローを
行なった場合、圧縮空気によって舞い上がった異物がボ
デー外部に完全に運び去られることなく、複雑な形状を
有しかつ十分な開口部を有しないボデーフロア部（ボデ
ー内部）に再付着してしまうものであった。However, when air blowing is performed in the intermediate coating preparation step 54 and the top coating preparation step 57 as described above, foreign matters soared by the compressed air are not completely carried out of the body and have a complicated shape. Moreover, it re-adheres to the body floor (the inside of the body) which does not have a sufficient opening.
【０００５】この状態のまま、中塗り塗装５５あるいは
上塗り塗装５８を行なうと、塗装の際あるいはオーブン
内における塗膜の熱風乾燥の際に、ボデーフロア部の中
塗りあるいは上塗りの非塗装部位に付着しているこの除
去しきれなかった異物が再度舞い上がり、中塗り塗膜あ
るいは上塗り塗膜に付着してしまうこととなり、塗膜外
観品質の低下させる虞れがあった。In this state, if the intermediate coating 55 or the top coating 58 is applied, the coating adheres to the non-coated part of the middle or top coating of the body floor during coating or hot air drying of the coating in an oven. The foreign matter that could not be removed is sowed again and adheres to the intermediate coating film or the top coating film, and there is a possibility that the appearance quality of the coating film may be deteriorated.
【０００６】また、特開平３−１３７９６９号公報にお
いては、上塗りベースコートとして水性塗料を用いる場
合において、このベースコートの熱風乾燥工程において
ベースコート上にゴミ等の異物が付着し、ベースコート
とクリアコートの間に異物が存在することによる外観不
良の発生を防止するために、ベースコート塗布に先立ち
ボデー内板部に付着している異物を粘着性のある合成お
よび／または天然の樹脂により固定し、該異物が熱風乾
燥によって舞い上がり水性塗膜上に付着しないようにす
る技術が提唱されている。In Japanese Unexamined Patent Publication (Kokai) No. 3-137969, when a water-based paint is used as a base coat, foreign matter such as dust adheres to the base coat in a hot-air drying step of the base coat, and a gap between the base coat and the clear coat occurs. In order to prevent appearance defects due to the presence of foreign matter, foreign matter adhering to the inner plate of the body is fixed with an adhesive synthetic and / or natural resin before applying the base coat, and the foreign matter is heated with hot air. A technique has been proposed to prevent the particles from rising by drying and adhering to the aqueous coating film.
【０００７】[0007]
【発明が解決しようとする課題】しかしながら、このよ
うに樹脂材料を含有する粘着剤を用いる場合、当該粘着
剤の粘度が高いゆえに、圧縮空気を用いて塗布を行なう
必要があり、この塗布の際に異物の舞い上がりが発生す
る虞れが高いものであった。However, when an adhesive containing a resin material is used as described above, it is necessary to perform application using compressed air because the viscosity of the adhesive is high. Therefore, there is a high possibility that the foreign matter may be raised.
【０００８】また樹脂が含まれているために、塗布の際
の微粒化が悪いと、上塗り塗装部位に飛散付着した液滴
によって、塗膜に凸状欠陥が発生する虞れが大きいもの
であった。[0008] In addition, if resin is contained, and if atomization at the time of coating is poor, droplets scattered and attached to the topcoating portion are likely to cause convex defects in the coating film. Was.
【０００９】さらに、非塗装部位に塗布する粘着剤とし
て樹脂材料を含むために材料費が高くなり、特に、水系
塗料をベースコートとする態様以外の前記したような一
般的な中塗りないし上塗り塗装において適用すること
は、コスト的に問題が大きいものであった。Further, since the resin material is contained as an adhesive applied to the non-coating portion, the material cost is high. In particular, in the above-mentioned general intermediate coating or top coating other than the embodiment using a water-based coating as a base coat. The application was problematic in terms of cost.
【００１０】従って本発明は、自動車塗装において、よ
り安価にかつ簡便な施工により、塗膜にゴミ、ホコリ等
の異物が混入することを防止する技術を提供することを
課題とするものである。[0010] Accordingly, an object of the present invention is to provide a technique for preventing foreign substances such as dust and dirt from being mixed into a coating film by using a cheaper and simpler construction method in automotive coating.
【００１１】[0011]
【課題を解決するための手段】上記課題を解決する本発
明は、中塗り塗装工程および上塗り塗装工程の少なくと
もいずれかにおける塗料塗布に先立ち、当該塗装工程に
おける非塗装部位のうち、塗装部位に比較的近接する領
域には高沸点有機溶剤を塗布し、塗装部位より比較的離
れた領域には水または水を主成分とする水系溶媒を塗布
し、塗料塗布ないし乾燥時における当該非塗装部位から
の異物の飛散を抑制することを特徴とする自動車車体の
塗装方法である。Means for Solving the Problems] This onset <br/> bright to solve the above problems, prior to paint application at least one of intermediate coating step and finish coating step, of the unpainted parts of the painting process A high-boiling organic solvent is applied to a region relatively close to the coating site, and water or an aqueous solvent containing water as a main component is applied to a region relatively far from the coating site. A coating method for an automobile body, characterized in that scattering of foreign matter from a non-painted part is suppressed.
【００１２】上記発明において、前記高沸点有機溶剤
は、パターンノズルによるエアレス霧化により塗布され
るものであることが望ましい。[0012] In the above SL onset bright, the high-boiling organic solvent is preferably intended to be applied by airless atomization by the pattern nozzles.
【００１３】上記発明において、前記高沸点有機溶剤の
塗布は、当該塗装工程における塗装部位の清浄（ダステ
ィング）作業前に行なわれ得るものである。また、前記
高沸点有機溶剤の塗布は、当該塗装工程における非塗装
部位の手作業による清浄操作時に行なわれ得るものであ
る。[0013] In the above SL onset bright, the application of the high-boiling organic solvents are those that may be performed before cleaning (dusting) the work of painting site in the painting process. The application of the high-boiling organic solvent can be performed during a manual cleaning operation of a non-painted portion in the painting process.
【００１４】上記発明において、前記高沸点有機溶剤
は、リターダーシンナー、あるいは当該塗装工程におい
て使用される塗料に含有されている溶剤を１種以上含む
溶剤であることが望ましい。[0014] In the above SL onset bright, the high-boiling organic solvents, retarders thinners, or it is desirable that the solvent containing one or more solvents contained in the coating used in the painting process.
【００１５】[0015]
【作用】本発明によれば、ボデーフロア部等の非塗装部
分を、塗布された高沸点有機溶剤によって湿潤状態と
し、当該非塗装部分に付着しているゴミ、研りカス等の
異物を固定化することができる。このため、中塗り塗装
ないしは上塗り塗装工程において、スプレー塗装に使用
される圧縮空気あるいは熱風乾燥における熱風の影響に
より当該非塗装部から異物が舞い上がり塗装部位に付着
して塗装不良を起すといった問題が抑制される。また、
この非塗装部分に塗布するのは、リターダーシンナー、
あるいは当該塗装工程において使用される塗料に含有さ
れている溶剤を１種以上含む溶剤といった高沸点有機溶
剤であるために、塗布する際に塗装部分にその飛沫がか
かったとしても塗装にハジキ等の不具合が発生すること
もないため、塗装部の近傍まで塗布可能である。According to the present invention, an unpainted portion such as a body floor portion is wetted by the applied high-boiling organic solvent, and foreign matter such as dust and grinding chips adhered to the unpainted portion is fixed. Can be For this reason, in the middle coat or top coat process, the problem that foreign matter soars from the non-coating part and adheres to the coating part due to the influence of the compressed air used for spray coating or the hot air in hot air drying and causes a coating defect is suppressed. Is done. Also,
Applying to this unpainted part is retarder thinner,
Or, because it is a high-boiling organic solvent such as a solvent containing one or more solvents contained in the paint used in the painting process, even if the paint is sprayed on the painted portion when the paint is applied, cissing or the like may occur. Since no trouble occurs, it can be applied to the vicinity of the painted portion.
【００１６】なお、前記発明の一実施態様においては、
高沸点有機溶剤は、当該塗装工程における非塗装部位の
うち、塗装部位に比較的近接する領域のみに塗布され
る。中塗り塗装ないしは上塗り塗装工程において、スプ
レー塗装の圧縮空気の影響を大きく受け、異物の舞い上
がりが生じやすいのは、非塗装部分のうち塗装部分に比
較的近接する領域、具体的には、例えば塗装部分末端か
ら該末端より１００〜４００ｍｍ程度離れた位置までの
領域であるため、この領域にのみに塗布することによっ
ても異物の舞い上がりを有効に抑制することができ、当
該高沸点有機溶剤の使用量を抑えて製造コストを削減で
きる。[0016] It should be noted that, in the previous Symbol onset Akira of one embodiment,
The high-boiling organic solvent is applied only to a region relatively close to the coating site among the non-coating sites in the coating process. In the intermediate coating or top coating process, the influence of the compressed air of the spray coating is greatly affected, and foreign matter is likely to rise in the non-painted area that is relatively close to the painted part, specifically, for example, painting Since it is a region from the partial end to a position about 100 to 400 mm away from the end, it is possible to effectively suppress the sowing of foreign matter even by applying only to this region, and the amount of the high boiling organic solvent used And the manufacturing cost can be reduced.
【００１７】さらに、本発明によれば、非塗装部分のう
ち塗装部分に比較的近接する位置には前記と同様に高沸
点有機溶剤を塗布し、塗装部位より比較的離れた位置に
は水または水を主成分とする水系溶媒を塗布するため
に、より低い材料コストにおいて、前記のように非塗装
部分の実質的全領域にわたり高沸点有機溶剤を塗布した
場合とほぼ同様の効果をもって、非塗装部からの異物の
舞い上がりを抑制することができる。なお、水系溶媒が
塗布されるのは塗装部位より比較的離れた領域のみであ
るために、水系溶媒塗布の際に塗装部分にその飛沫がか
かる虞れは実質的にないものである。Furthermore, according to the present invention, the non-high-boiling organic solvent relatively to adjacent positions before Symbol the same way to the paintwork of the paintwork is applied, a position relatively distant from the coating site In order to apply water or an aqueous solvent containing water as a main component, at a lower material cost, with substantially the same effect as when applying a high-boiling organic solvent over substantially the entire area of the unpainted portion as described above, It is possible to suppress the sowing of foreign matter from the unpainted portion. It should be noted that since the aqueous solvent is applied only to a region relatively far from the coating site, there is substantially no danger that the applied portion will be splashed when the aqueous solvent is applied.
【００１８】また上記発明の好ましい実施態様において
は、前記高沸点有機溶剤はパターンノズルでのエアレス
霧化により塗布されるが、この場合、当該有機溶剤塗布
の際に噴霧圧によって非塗装部位に付着していた異物が
舞い上がる虞れも小さくなり、異物に起因する塗装不良
の発生の確率がより低減される。このようにエアレス霧
化により塗布可能であるのは、前記高沸点有機溶剤は樹
脂材料などと比較して低粘度のものであるためである。[0018] In a preferred embodiment of a light above Symbol onset Moreover, the high boiling organic solvent but is applied by airless atomization pattern nozzles, in this case, unpainted site by spraying pressure when the organic solvent coating The possibility that the foreign matter adhering to the surface will soar is also reduced, and the probability of occurrence of a coating defect caused by the foreign matter is further reduced. The reason why the coating can be performed by airless atomization is that the high-boiling organic solvent has a lower viscosity than a resin material or the like.
【００１９】さらに、上記発明において、前記高沸点有
機溶剤の塗布が、当該塗装工程における塗装部位の清浄
操作前に行なわれると、例えばエアブローなどによる清
浄操作において非塗装部位へと飛散してくる異物を固定
できるものである。また前記高沸点有機溶剤の塗布が、
当該塗装工程における非塗装部位の手作業による清浄操
作時に行なわれると、その後に自動ワイプ・エアブロー
装置を用いて塗装部位の清浄操作を行なう際に非塗装部
位へと飛散してくる異物を固定できるものである。Furthermore, in the above Symbol onset Ming, application of the high-boiling organic solvent, when performed before cleaning operation painting site in the painting process, for example, scattered to the non-painted portion in the cleaning operation by the air blow It can fix incoming foreign matter. Also, the application of the high boiling organic solvent,
When performed during a manual cleaning operation of a non-painting part in the painting process, foreign matter scattered to the non-painting part when performing a cleaning operation of the painting part using an automatic wipe and air blow device can be fixed thereafter. Things.
【００２０】[0020]
【実施例】以下、本発明を実施例によりさらに具体的に
説明する。EXAMPLES Hereinafter, the present invention will be described more specifically with reference to examples.
【００２１】図１は、本発明の自動車車体塗装方法の一
実施例における工程図であり、また図２は、自動車車体
において本発明に係る異物飛散防止処理を施す領域を示
す概略平面図、図３は図２のＡ−Ａ矢視図である。FIG. 1 is a flow chart showing an embodiment of a method for coating an automobile body according to the present invention, and FIG. 2 is a schematic plan view showing a region where the foreign matter scattering prevention processing according to the present invention is applied to the automobile body. FIG. 3 is a view on arrow AA of FIG. 2.
【００２２】図１に示すように本発明の自動車車体塗装
方法においては、まず、常法と同様に、自動車ボデー
は、脱錆、脱脂、化成皮膜処理などを含む前処理工程１
へ、次いで、電着塗装法による下塗り塗装工程２へ、さ
らに、下塗り塗膜の品質不良箇所の確認、サンドペーパ
ー、研磨ブラシ等を用いた不良箇所の研ぎによる修正、
および研ぎカスのワイプによる除去を行なう下塗り研ぎ
工程３へとかけられる。なお、必要に応じて、この後
に、シーリング塗装、アンダーコート塗装、ストーンガ
ードコート塗装、ヒュージブルインシュレータ取付けな
どといった工程を付加することも可能である。[0022] In the automotive body painting process of the present invention as shown in FIG. 1, first, similarly to the conventional method, an automobile Bode chromatography
Is a pretreatment process 1 including derusting, degreasing, chemical conversion coating, etc.
Next, to the undercoating process 2 by the electrodeposition coating method, further confirmation of the poor quality of the undercoat coating, sanding, correction of the defective portion using a polishing brush, etc.,
Then, it is subjected to an undercoat sharpening step 3 for removing the shavings by wiping. If necessary, steps such as sealing painting, undercoat painting, stone guard coat painting, and mounting of a fusible insulator can be added after this.
【００２３】その後、下塗り塗膜を形成された自動車ボ
デーは、下塗り塗膜上に付着しているゴミ、研ぎカス等
の異物を除去し、清浄な表面として中塗り塗装を行なう
ための中塗り準備工程４へと送られるが、本実施例にお
いては、この中塗り準備工程４へと入る前、すなわち、
図１で符号ａで示す時期に、中塗り塗装を行なわない自
動車ボデーの部位（非塗装部位）に、高沸点有機溶剤を
塗布する異物飛散防止処理を施す。[0023] Then, the undercoating film automotive Bo <br/> de chromatography formed a is dust attached onto the undercoating film, sharpening to remove foreign matters such as scrap, the intermediate coating as clean surface It is sent to the intermediate coating preparation step 4 for performing, but in this embodiment, before entering the intermediate coating preparation step 4, that is,
The time indicated by the by symbol a 1, the automotive Bode over is not carried out intermediate coating site (uncoated portion) is subjected to a foreign matter scattering prevention process of applying the high-boiling organic solvent.
【００２４】高沸点有機溶剤としては、少なくとも、そ
の塗布から後続する塗装工程（この場合、中塗り塗装工
程５）において塗料塗布を行なうまでの間、より具体的
には、例えば塗布後約５分以上（約２５℃±５℃条件
下）、乾燥ないし揮発しないものであれば使用可能であ
り、好ましくは、７６０Ｔｏｒｒ下における沸点が１５
０℃以上、より好ましくは２００〜２２０℃程度の有機
溶剤が用いられる。また、この高沸点有機溶剤の粘度と
しては、約２０℃±１℃条件下において、フォードカッ
プＮｏ．４で２５秒以下、より好ましくは１５〜２０秒
程度であることが望ましい。すなわち、その粘度が２５
秒を越えるものであると、その塗布が困難となり高い圧
力を使用して塗布することによって、その塗布時におけ
る異物の舞い上がりが発生する虞れがあるためである。The high-boiling organic solvent is used at least from the time of its application to the time of the subsequent coating step (in this case, the intermediate coating step 5), and more specifically, for example, about 5 minutes after the application. Above (under conditions of about 25 ° C. ± 5 ° C.), any substance which does not dry or volatilize can be used, and preferably has a boiling point under 760 Torr of 15 ° C.
An organic solvent of 0 ° C. or higher, more preferably about 200 to 220 ° C., is used. The viscosity of the high boiling point organic solvent is about 20 ° C. ± 1 ° C., and Ford Cup No. 4 and 25 seconds or less, more preferably about 15 to 20 seconds. That is, its viscosity is 25
If the time is longer than a second, the application becomes difficult, and the application is performed using a high pressure.
【００２５】具体的には、例えば、シクロヘキサノン、
高沸点酢酸エステル、ソルベントナフサ、キシロールな
どから構成されるいわゆるリターダーシンナーや、例え
ば、エチレングリコールジアセテートなどといった当該
塗装工程で使用する塗料に含有されている溶剤を１種以
上含んでなる溶剤組成物などが使用可能である。Specifically, for example, cyclohexanone,
A solvent composition comprising at least one solvent contained in a paint used in the coating step, such as a so-called retarder thinner composed of a high boiling point acetate, solvent naphtha, xylol, etc., for example, ethylene glycol diacetate, etc. Etc. can be used.
【００２６】このような高沸点有機溶剤の非塗装部位へ
の塗布は、パターンノズルを用いたエアレス霧化による
スプレー、エアスプレーガンによるスプレー、あるいは
ハケ、ローラー、ウェス等の塗布媒体を用いた方法にて
行なわれ得るが、好ましくはパターンノズルでのエアレ
ス霧化により塗布することが望ましい。この場合、当該
有機溶剤塗布の際に噴霧圧によって非塗装部位に付着し
ていた異物が舞い上がる虞れも小さくなり、異物に起因
する塗装不良の発生の確率がより低減される。エアレス
霧化による噴霧圧は、０．２〜５ｋｇｆ／ｃｍ2 程度が
適当である。さらに、上記のような高沸点有機溶剤は、
塗装部分にその飛沫が若干かかったとしても塗装にハジ
キ等の不具合が発生することもないため、ボデーフロア
部への高沸点有機溶剤の塗布は、例えば、ドア上部の開
口部よりノズルを挿入して塗布する簡易自動機などを用
いることにより、自動塗布することも可能である。The application of such a high-boiling organic solvent to a non-coating portion is performed by spraying by airless atomization using a pattern nozzle, spraying by an air spray gun, or a method using a coating medium such as a brush, a roller, and a rag. However, it is preferable to apply by airless atomization with a pattern nozzle. In this case, the risk of foreign matter adhering to the non-painted portion rising due to the spray pressure during the application of the organic solvent is reduced, and the probability of occurrence of coating failure due to the foreign matter is further reduced. The appropriate spray pressure by airless atomization is about 0.2 to 5 kgf / cm 2 . Further, the high boiling organic solvent as described above,
Even if the spray is slightly applied to the painted part, there will be no problems such as repelling in the paint.Therefore, when applying a high boiling organic solvent to the body floor, insert a nozzle from the opening at the top of the door, for example. It is also possible to perform automatic application by using a simple automatic machine or the like that performs application.
【００２７】また、高沸点有機溶剤は、非塗装部位の実
質的全面に塗装することが最も望ましいが、図２および
図３に示すように、非塗装部位のうち、塗装部位に比較
的近接する領域のみ、具体的には、自動車ボデーフロア
部（非塗装部位）のうち、ドアオープニング（塗装部
位）部分末端から該末端より１００〜４００ｍｍ程度離
れた位置までの領域Ｉ（ホイルハウス部を含む）のみに
塗布するものであっても十分である。すなわち、このよ
うな領域Ｉが中塗り塗装ないしは上塗り塗装工程におい
て、スプレー塗装の圧縮空気の影響を大きく受け、異物
の舞い上がりが生じやすい部位であるためである。It is most preferable that the high boiling point organic solvent be applied to substantially the entire surface of the non-painted portion. However, as shown in FIGS. 2 and 3, the non-painted portion is relatively close to the painted portion. Region I, specifically, region I (including the wheelhouse portion) from the end of the door opening (painted portion) to a position about 100 to 400 mm away from the end of the car body floor portion (non-painted portion) It is sufficient to apply it only to the surface. That is, such a region I is a portion that is greatly affected by the compressed air of the spray coating in the intermediate coating or the top coating process, and is likely to cause foreign matter to fly.
【００２８】中塗り準備工程４においては、最初に手作
業にて主としてボデーフロア部および狭窄部等のエアブ
ロー、ワイプによる清浄操作を行ない、これらの部位に
おいて下塗り塗膜上に付着しているゴミ、研ぎカス等の
異物を除去し、次いで、自動ワイプ・エアブロー装置を
通過させ、ボデーアウター部に付着しているゴミ、研ぎ
カス等の異物を除去する自動清浄操作を行なう。前記し
たように中塗り準備工程４に先立ち、ボデーフロア部に
は異物飛散防止処理が施されており高沸点有機溶剤によ
って湿潤状態とされているので、上記のような清浄操作
時にボデーフロア部に飛散してきた異物も捕捉される。In the intermediate coating preparation step 4, first, a cleaning operation is mainly performed by hand, mainly by air blowing and wiping of a body floor portion and a constricted portion, and dust adhering to the undercoat coating film in these portions is removed. After removing foreign matter such as grinding chips, an automatic cleaning operation is performed to remove foreign matter such as dust and grinding chips attached to the body outer portion by passing through an automatic wipe air blow device. As described above, prior to the intermediate coating preparation step 4, the body floor portion has been subjected to a foreign matter scattering prevention treatment and is in a wet state with a high-boiling organic solvent. The scattered foreign matter is also captured.
【００２９】中塗り準備工程４においては、必要に応じ
て、このような清浄操作に続いて、静電塗装の安全対策
として、ボデーと塗装台車（図示せず）とのアース状態
の点検が行なわれる。[0029] In intermediate preparation step 4 is optionally Following such cleaning operation, as a safety measure for electrostatic coating, the inspection of the ground state of the Bode over and painted carriage (not shown) Done.
【００３０】次いで、中塗り塗装工程５において、中塗
り塗料をボデー塗装部位に塗装し、熱風乾燥炉において
焼付け乾燥するが、前記したようにボデーフロア部には
異物飛散防止処理が施されており高沸点有機溶剤によっ
て湿潤状態とされているので、スプレー塗装に使用され
る圧縮空気あるいは熱風乾燥における熱風の影響により
当該ボデーフロア部から異物が舞い上がり中塗り塗膜に
異物が付着する虞れが小さくなる。Next, in the intermediate coating step 5, the intermediate coating is applied to the body coating portion and baked and dried in a hot-air drying oven. As described above, the body floor has been subjected to the foreign matter scattering prevention treatment. Since it is in a wet state by the high boiling point organic solvent, there is a small possibility that foreign matter soars from the body floor due to the influence of compressed air used for spray coating or hot air in hot air drying, and the foreign matter adheres to the intermediate coating film. Become.
【００３１】本発明においては、中塗り塗装としては特
に限定されるわけではなく、常法に従い行なうことが可
能であり、例えば、スプレー塗装法あるいは静電スプレ
ー塗装法によって、メラミン−アルキド樹脂系中塗り塗
料を塗装し、その後、１３０〜１５０℃で、２０〜２５
分間という条件で焼付け乾燥を行なう。さらに、必要に
応じて、中塗り塗装工程においては、周知のごとく、チ
ッピングコート塗装、導電性付与プライマー塗装、黒色
塗装といった工程を付加することも可能である。In the present invention, the intermediate coating is not particularly limited, and can be performed according to a conventional method. For example, a spray coating method or an electrostatic spray coating method may be used to prepare a melamine-alkyd resin system. Apply paint and then, at 130-150 ° C, 20-25
Bake and dry under the condition of minutes. Further, if necessary, in the intermediate coating step, it is possible to add a step such as chipping coating, primer coating for imparting conductivity, and black coating, as is well known.
【００３２】中塗り塗装工程５の後、自動車ボデーは、
中塗り塗膜の品質不良箇所の確認、サンドペーパー、研
磨ブラシ等を用いた不良箇所の研ぎによる修正、および
研ぎカスのワイプによる除去を行なう中塗り研ぎ工程６
へとかけられる。なお、必要に応じて、この後に、黒色
塗装マスキングなどといった工程を付加することも可能
である。After the intermediate coating step 5, the car body is
An intermediate coating sharpening process 6 for confirming a defective portion of the intermediate coating film, correcting the defective portion by sanding with a sandpaper, a polishing brush, or the like, and removing a sharpening residue by wiping.
Be called. If necessary, a step such as black coating masking can be added after this.
【００３３】その後、上記中塗り塗装を行なう場合と同
様に、中塗り塗膜を形成された自動車ボデーは、中塗り
塗膜上に付着しているゴミ、研ぎカス等の異物を除去
し、清浄な表面として上塗り塗装を行なうための上塗り
準備工程７へと送られるが、本実施例においては、この
上塗り準備工程７へと入る前、すなわち、図１で符号ｃ
で示す時期に、上塗り塗装を行なわない自動車ボデーの
部位（非塗装部位）に、高沸点有機溶剤を塗布する異物
飛散防止処理を施す。使用される高沸点有機溶剤として
は、前記したものと同様なものが用いられ得、またその
塗布方法、塗布範囲としても前記したものと同様なもの
である。After that, as in the case of the above-mentioned intermediate coating, the automobile body having the intermediate coating formed thereon is free of foreign matter such as dust and swarf adhering to the intermediate coating and is cleaned. The surface is sent to the overcoat preparation step 7 for performing the overcoat coating as a suitable surface, but in this embodiment, before entering the overcoat preparation step 7, that is, in FIG.
The time indicated by, in <br/> site of automobile Bode over is not performed finish coating (uncoated portion) is subjected to a foreign matter scattering prevention process of applying the high-boiling organic solvent. As the high-boiling organic solvent to be used, the same ones as described above can be used, and the application method and the application range are the same as those described above.
【００３４】上塗り準備工程７においては、前記中塗り
準備工程４におけると同様に、最初に手作業にて主とし
てボデーフロア部および狭窄部等のエアブロー、ワイプ
による清浄操作を行ない、これらの部位において中塗り
塗膜上に付着しているゴミ、研ぎカス等の異物を除去
し、次いで、自動ワイプ・エアブロー装置を通過させ、
ボデーアウター部に付着しているゴミ、研ぎカス等の異
物を除去する自動清浄操作を行なう。前記したように上
塗り準備工程７に先立ち、ボデーフロア部には異物飛散
防止処理が施されており高沸点有機溶剤によって湿潤状
態とされているので、上記のような清浄操作時にボデー
フロア部に飛散してきた異物も捕捉される。In the top coat preparation step 7, as in the intermediate coat preparation step 4, first, a cleaning operation is mainly performed manually by air blow and wipe on the body floor portion and the constricted portion. Remove foreign matter such as dust and sharpened chips attached to the coating film, and then pass through an automatic wipe air blow device,
An automatic cleaning operation is performed to remove foreign substances such as dirt and grinding chips attached to the body outer portion. As described above, prior to the top coating preparation step 7, the body floor has been subjected to a foreign matter scattering prevention treatment and is wetted by the high boiling point organic solvent. The foreign matter that has been captured is also captured.
【００３５】上塗り準備工程７においては、必要に応じ
て、このような清浄操作に続いて、静電塗装の安全対策
として、ボデーと塗装台車とのアース状態の点検が行な
われる。[0035] In overcoating preparation step 7, if necessary, subsequent to such cleaning operation, as a safety measure for electrostatic coating, inspection of the ground state of the Bode over and painted carriage is performed.
【００３６】次いで、上塗り塗装工程８において、上塗
り塗料をボデー塗装部位に塗装し、熱風乾燥炉において
焼付け乾燥するが、前記したようにボデーフロア部には
異物飛散防止処理が施されており高沸点有機溶剤によっ
て湿潤状態とされているので、スプレー塗装に使用され
る圧縮空気あるいは熱風乾燥における熱風の影響により
当該ボデーフロア部から異物が舞い上がり上塗り塗膜に
異物が付着する虞れが小さくなる。Next, in the top coat coating step 8, the top coat is applied to the body coating portion and baked and dried in a hot air drying oven. As described above, the body floor has been subjected to the foreign matter scattering prevention treatment and has a high boiling point. Since it is in a wet state by the organic solvent, foreign matter soars from the body floor due to the influence of compressed air used for spray coating or hot air in hot air drying, and the possibility that the foreign matter adheres to the top coat is reduced.
【００３７】なお、本発明においては、上塗り塗装とし
ては特に限定されるわけではなく、常法に従い行なうこ
とが可能であり、例えば、スプレー塗装法あるいは静電
スプレー塗装法によって、メラミン−アルキド樹脂系等
の上塗りソリッド塗料を塗装し、その後、１３０〜１５
０℃で、２０〜２５分間という条件で焼付け乾燥を行な
う。あるいは、アクリル樹脂系等の上塗りベースコート
塗料を塗装し、さらにウェット・オン・ウェットにてア
クリル樹脂系等の上塗りクリアコート塗料を塗装し、上
記と同様の条件で焼付け乾燥を行なう。もちろん、これ
以外にも、パールトーン塗装、あるいは２コート２ベー
クなどといった態様も取り得るものである。In the present invention, the top coat is not particularly limited, and can be applied according to a conventional method. For example, a melamine-alkyd resin system can be applied by a spray coating method or an electrostatic spray coating method. Paint the top coating solid paint, etc., then 130 ~ 15
Bake and dry at 0 ° C. for 20 to 25 minutes. Alternatively, a top coat base coat paint of acrylic resin or the like is applied, and a top coat clear coat paint of acrylic resin or the like is further applied on a wet-on-wet basis, and baked and dried under the same conditions as described above. Of course, in addition to this, it is possible to adopt a mode such as pearl tone painting or 2 coats 2 bake.
【００３８】上記実施例においては、非塗装部位に高沸
点有機溶剤を塗布する異物飛散防止処理は、中塗り準備
工程４直前（ａ時期）および上塗り準備工程７直前（ｃ
時期）において行なわれたが、これらはそれぞれ中塗り
準備工程４における手作業による清浄操作と同時期、す
なわち図１における符号ｂで示す時期、および上塗り準
備工程７における手作業による清浄操作と同時期、すな
わち図１における符号ｄで示す時期において行なうこと
も可能である。このように、手作業による清浄操作と同
時期に行なえば、その後の自動ワイプ・エアブロー装置
を用いての清浄操作を行なう際に非塗装部位へと飛散し
てくる異物を固定でき、また前記と同様に中塗り塗装工
程ないし上塗り塗装工程における異物飛散防止効果が期
待できる。さらに本発明においては、上記のごとき異物
飛散防止処理は、前記ａ，ｂ，ｃ，ｄ時期の少なくとも
いずれかにおいて行なえばよく、また複数の時期に行な
う場合における組合せも任意である。In the above embodiment, the foreign matter scattering prevention treatment for applying the high boiling point organic solvent to the non-coating portion is performed immediately before the intermediate coating preparation step 4 (time a) and immediately before the top coating preparation step 7 (c).
These are performed at the same time as the manual cleaning operation in the intermediate coating preparation step 4, that is, at the same time as the manual cleaning operation in the top coating preparation step 7 at the time indicated by reference numeral b in FIG. That is, it is also possible to carry out at the time indicated by the symbol d in FIG. As described above, if the cleaning operation is performed at the same time as the manual cleaning operation, the foreign matter scattered to the non-painting portion when performing the cleaning operation using the automatic wipe / air blow device can be fixed. Similarly, the effect of preventing foreign matter scattering in the intermediate coating process or the top coating process can be expected. Further, in the present invention, the foreign matter scattering prevention processing as described above may be performed at least in any one of the a, b, c, and d timings, and a combination in a case where the processing is performed at a plurality of timings is also arbitrary.
【００３９】また、本発明においては、図２および図３
に示すように、非塗装部位のうち、塗装部位に比較的近
接する領域のみ、具体的には、自動車ボデーフロア部
（非塗装部位）のうち、ドアオープニング（塗装部位）
部分末端から該末端より１００〜４００ｍｍ程度離れた
位置までの領域Ｉ（ホイルハウス部を含む）のみに高沸
点有機溶剤を塗布し、塗装部位より比較的離れた領域、
具体的には、ボデーフロア部のうち、前記領域Ｉよりも
さらに内方に位置する領域IIには水または水を主成分と
する水系溶媒を塗布する。[0039] Also, in the present invention, FIGS. 2 and 3
As shown in the figure, only the area relatively close to the painted part in the non-painted part, specifically, the door opening (painted part) in the car body floor part (non-painted part)
Applying a high-boiling organic solvent only to the region I (including the foil house portion) from the partial end to a position about 100 to 400 mm away from the end, and a region relatively far from the coating site;
Specifically, water or a water-based solvent containing water as a main component is applied to a region II located further inward than the region I in the body floor portion.
【００４０】領域IIは、塗装部位より離れており、該領
域にスプレー等により液状媒体を塗布した場合において
も、その飛沫が塗装部位にかかる虞れはなく、前記した
ような高沸点有機溶剤に代えて、水または水を主成分と
する水系溶媒を塗布しても塗装に不具合が発生する虞れ
はない。これにより、より低い材料コストにおいて、前
記発明において非塗装部分の実質的全領域にわたり高沸
点有機溶剤を塗布した場合とほぼ同様の効果をもって、
非塗装部からの異物の舞い上がりを抑制することができ
る。The region II is far from the coating site. Even when a liquid medium is applied to the region by spraying or the like, there is no possibility that the droplets may be applied to the coating site. Alternatively, even if water or an aqueous solvent containing water as a main component is applied, there is no fear that a problem occurs in the coating. This allows for lower material costs,
Have substantially the same effect as in the serial onset bright coated with high boiling point organic solvent over substantially an entire area of the uncoated portion,
It is possible to suppress the sowing of foreign matter from the unpainted portion.
【００４１】なお、本発明において用いられる水を主成
分とする水系溶媒としては、例えば、水１００重量部に
対し、２０〜２５重量部程度の親水性溶媒、例えば、ア
ルコールもしくはグリコールエーテル等を添加したもの
などが用いられ得る。また、水としては、純水であるこ
とが望ましいが、水道水、工水であっても十分使用可能
である。さらに、領域Ｉへの高沸点有機溶剤の塗布と領
域IIへの水または水を主成分とする水系溶媒の塗布は、
いずれを先に行なっても、また同時に行なってもよい。As the aqueous solvent containing water as a main component used in the present invention, for example, about 20 to 25 parts by weight of a hydrophilic solvent such as alcohol or glycol ether is added to 100 parts by weight of water. And the like can be used. As the water, it is desirable to use pure water, but tap water and industrial water can also be used satisfactorily. Further, the application of a high boiling point organic solvent to the region I and the application of water or an aqueous solvent mainly containing water to the region II are as follows.
Either of them may be performed first or may be performed simultaneously.
【００４２】また、本発明において用いられる高沸点有
機溶剤の種類および塗布方法については前記のとおりで
あり、また、本発明において上記したような水または水
を主成分とする水系溶媒と高沸点有機溶剤とを用いる異
物飛散防止処理を行なう時期についても、前記における
異物飛散防止処理を行なう時期（ａ，ｂ，ｃ，ｄ時期）
と同様である。Further, the type and coating method of the high-boiling organic solvent used in the present invention are as defined above, also a water-based solvent and a high boiling organic to water or water as described above in the present invention as a main component about when performing foreign matter scattering prevention treatment with a solvent is also time to perform the foreign matter scattering prevention processing definitive prior Symbol (a, b, c, d timing)
Is the same as
【００４３】[0043]
【発明の効果】さらに、本発明は、自動車車体の塗装方
法において、中塗り塗装工程および上塗り塗装工程の少
なくともいずれかにおける塗料塗布に先立ち、当該塗装
工程における非塗装部位のうち、塗装部位に比較的近接
する領域には高沸点有機溶剤を塗布し、塗装部位より比
較的離れた領域には水または水を主成分とする水系溶媒
を塗布するものであるので、より低い材料コストにおい
て、中塗り塗装工程および上塗り塗装工程の少なくとも
いずれかにおける塗料塗布に先立ち、当該塗装工程にお
ける非塗装部位に高沸点有機溶剤を塗布するものである
ので、これらの塗装工程における非塗装部分からの異物
の舞い上がりを抑制することができ、かつこの高沸点有
機溶剤の飛沫が塗装部分に付着したとしても塗装にハジ
キ等の不具合が発生することもないため、高品質の自動
車車体塗装を達成することができるものである。なお、
水または水系溶媒が塗布されるのは塗装部位より比較的
離れた領域のみであるために、塗装部分にその飛沫がか
かり塗装のハジキ等の不具合が発生する虞れは実質的に
ないものである。Further, the present invention relates to a method for coating an automobile body, which comprises comparing a non-painted portion in the coating process with a painted portion prior to the application of the paint in at least one of the intermediate coating process and the top coating process. A high-boiling organic solvent is applied to areas that are close to each other, and water or an aqueous solvent containing water as a main component is applied to areas that are relatively far away from the coating area. Prior to the application of the paint in at least one of the painting step and the topcoating step, a high-boiling organic solvent is applied to a non-painting part in the painting step. Even if the high-boiling organic solvent droplets adhere to the painted part, problems such as cissing may occur. For nor does it, is capable of achieving an automobile body painting quality. In addition,
Since the water or the water-based solvent is applied only to the region relatively far away from the coating portion, there is substantially no danger that the coating portion will be sprayed and a problem such as repelling of the coating will occur. .
【００４４】また、高沸点有機溶剤を、当該塗装工程に
おける非塗装部位のうち、塗装部位に比較的近接する領
域のみに塗布した場合であっても、塗装工程における異
物の舞い上がりを有効に抑制することができ、当該高沸
点有機溶剤の使用量を抑えて 製造コストを削減できる。 Further , a high boiling organic solvent is used in the coating step.
Area that is relatively close to the painted part
Even in the coating process,
It is possible to effectively suppress soaring of objects,
The production cost can be reduced by reducing the amount of the organic solvent used .
【００４５】また上記発明において、前記高沸点有機溶
剤をパターンノズルでのエアレス霧化により塗布すれ
ば、当該有機溶剤塗布の際に噴霧圧によって非塗装部位
に付着していた異物が舞い上がる虞れも小さくなり、異
物に起因する塗装不良の発生の確率がより低減される。Further in the above Symbol onset bright, the high if boiling organic solvent applied by airless atomization pattern nozzle, a fear that foreign substances adhered to the unpainted site by spraying pressure when the organic solvent coating soar Therefore, the probability of occurrence of coating failure due to foreign matter is further reduced.
【図１】 本発明の自動車車体塗装方法の一実施例にお
ける工程図、FIG. 1 is a process diagram in one embodiment of a method of painting an automobile body according to the present invention;
【図２】 自動車車体において本発明に係る異物飛散防
止処理を施す領域を示す概略平面図、FIG. 2 is a schematic plan view showing a region on a vehicle body where a foreign matter scattering prevention process according to the present invention is performed;
【図３】 図２のＡ−Ａ矢視図、FIG. 3 is a view taken in the direction of arrows AA in FIG. 2;
【図４】 従来の自動車車体塗装方法の一例における工
程図。FIG. 4 is a process chart in an example of a conventional method of painting a vehicle body.
１ 前処理工程、 ２ 下塗り塗装工程、３
下塗り研ぎ工程、４ 中塗り準備工程、５
中塗り塗装工程、６ 中塗り研ぎ工程、７
上塗り準備工程、８ 上塗り塗装工程、ａ，ｂ，
ｃ，ｄ 異物飛散防止処理時期、Ｉ 非塗装部
位のうち塗装部位に比較的近接する領域、II 非塗
装部位のうち塗装部位より比較的離れた領域。1 Pretreatment process, 2 Undercoating process, 3
Undercoat sharpening process, 4 Intermediate coating preparation process, 5
Intermediate coating process, 6 Intermediate coating sharpening process, 7
Top coating preparation process, 8 Top coating process, a, b,
c, d Foreign matter scattering prevention processing time, a region relatively close to the painted portion among the I non-painted portions, and a region relatively far from the painted portion among the II non-painted portions.
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) B05D 3/10 B05D 1/02,1/32 B05D 7/14 B05B 15/04 ──────────────────────────────────────────────────続 き Continued on the front page (58) Field surveyed (Int. Cl. 7 , DB name) B05D 3/10 B05D 1 / 02,1 / 32 B05D 7/14 B05B 15/04
Claims (5)
少なくともいずれかにおける塗料塗布に先立ち、当該塗
装工程における非塗装部位のうち、塗装部位に比較的近
接する領域には高沸点有機溶剤を塗布し、塗装部位より
比較的離れた領域には水または水を主成分とする水系溶
媒を塗布し、塗料塗布ないし乾燥時における当該非塗装
部位からの異物の飛散を抑制することを特徴とする自動
車車体の塗装方法。1. A high-boiling organic solvent is applied to a region relatively close to a coating portion among non-coating portions in the coating process prior to coating in at least one of an intermediate coating process and a top coating process. A vehicle body characterized by applying water or an aqueous solvent containing water as a main component to a region relatively distant from a painted portion to suppress scattering of foreign matter from the non-painted portion when the paint is applied or dried. Painting method.
によるエアレス霧化により塗布されるものである請求項
１に記載の自動車車体の塗装方法。2. The high-boiling organic solvent is applied by airless atomization using a pattern nozzle.
2. The method for coating an automobile body according to claim 1 .
工程における塗装部位の清浄作業前に行なわれるもので
ある請求項１または２に記載の自動車車体の塗装方法。Wherein the coating of the high-boiling organic solvent, automotive body coating method of according to claim 1 or 2 is intended to be performed before the cleaning work of painting site in the painting process.
工程における非塗装部位の手作業による清浄操作時に行
なわれるものである請求項１〜３のいずれか記載の自動
車車体の塗装方法。Wherein the coating of the high-boiling organic solvent, claim 1 or automobile body coating method of description of 3 is intended to be performed during the cleaning operation by manual unpainted sites in the painting process.
ナー、あるいは当該塗装工程において使用される塗料に
含有されている溶剤を１種以上含む溶剤である請求項１
〜４のいずれかに記載の自動車車体の塗装方法。5. The high-boiling organic solvent is a retarder thinner or a solvent containing at least one solvent contained in a paint used in the coating step.
The method for coating an automobile body according to any one of claims 1 to 4 , wherein