JP3269154B2 - Polyester film for magnetic card - Google Patents
Polyester film for magnetic cardInfo
- Publication number
- JP3269154B2 JP3269154B2 JP00081793A JP81793A JP3269154B2 JP 3269154 B2 JP3269154 B2 JP 3269154B2 JP 00081793 A JP00081793 A JP 00081793A JP 81793 A JP81793 A JP 81793A JP 3269154 B2 JP3269154 B2 JP 3269154B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- polyester film
- polyester
- resin
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】[0001]
【産業上の利用分野】本発明は、磁性層を設けて磁気カ
ードとして使用されるポリエステルフィルムに関し、詳
しくは、帯電防止性、磁性層や印刷層との接着性等の特
性に優れた磁気カード用ポリエステルフィルムに関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyester film provided with a magnetic layer and used as a magnetic card, and more particularly, to a magnetic card having excellent characteristics such as antistatic properties and adhesion to a magnetic layer and a printing layer. The present invention relates to a polyester film for use.
【0002】[0002]
【従来の技術】磁気カードはいわゆるキャッシュレスの
便利さから、キャッシュカード、クレジットカードとし
て広く使用され、現金の自動入金・引出等の利用が金融
機関で実施されている。その他、IDカード、プリペイ
ドカード、電話カードや乗車カードとして様々な分野で
広く使用されており、今後ますます磁気カードの用途は
拡大するものと考えられる。2. Description of the Related Art Magnetic cards are widely used as cash cards and credit cards because of their so-called cashless convenience, and financial institutions use automatic payment and withdrawal of cash. In addition, the magnetic card is widely used in various fields as an ID card, a prepaid card, a telephone card, and a boarding card, and the use of the magnetic card is expected to further expand in the future.
【0003】磁気カードは、光線透過を少なくしたプラ
スチックシート表面に、磁性層と種々の情報を表示した
印刷層とが設けられたものである。基材となるプラスチ
ックシートには、耐水性、耐薬品性、機械的強度、寸法
安定性等の特性が要求されることから、これらの特性に
優れているポリエチレンテレフタレートを中心とするポ
リエステルフィルムが主に用いられている。このポリエ
ステルフィルムを磁気カードの基材として用いる時に最
も大きな問題となっているのが、静電気障害である。す
なわち、ポリエステルフィルムは絶縁体であるので静電
気が発生・蓄積し易いため、例えば、磁性層を塗布する
工程や印刷工程におけるロールへの巻き付き、人体への
電気ショック、取扱いの困難さといった作業能率の低下
につながるトラブルを初め、印刷ヒゲの発生、フィルム
表面の汚れ等の商品価値を低下させるトラブル等が多く
起こっていた。A magnetic card is provided with a magnetic layer and a printed layer displaying various information on a plastic sheet surface with reduced light transmission. Since the plastic sheet used as the base material is required to have properties such as water resistance, chemical resistance, mechanical strength, and dimensional stability, polyester films mainly made of polyethylene terephthalate, which excel in these properties, are mainly used. It is used for The biggest problem when using this polyester film as a base material of a magnetic card is electrostatic damage. That is, since the polyester film is an insulator, static electricity is likely to be generated and accumulated because it is an insulator. For example, it is difficult to handle such as winding on a roll in a process of applying a magnetic layer or a printing process, electric shock to a human body, and difficulty in handling. Many troubles such as the occurrence of print mustaches and stains on the film surface and the like which lower the commercial value have occurred, including the troubles leading to the reduction.
【0004】一方、磁気カードの耐久性向上の観点か
ら、ポリエステルフィルムと磁性層および印刷層との接
着性をさらに向上させることが要求されている。このた
め、種々の方法でポリエステルフィルムの接着性を向上
させたり、帯電防止性を付与する検討が行なわれてい
る。接着性を向上させる方法としては、フィルム表面を
コロナ放電、紫外線、プラズマ等の活性線で処理する方
法や、ポリエステル、ポリアクリル酸エステル、ポリウ
レタン等の易接着性樹脂を塗布する方法等がある。ま
た、帯電防止性を付与する方法としては、帯電防止性を
有する界面活性剤、イオン性化合物等の帯電防止剤や、
金属粉や金属酸化物等の導電性物質をポリエステル中に
練込んだり、塗布したりする方法がある。On the other hand, from the viewpoint of improving the durability of a magnetic card, it is required to further improve the adhesion between the polyester film and the magnetic layer and the printing layer. For this reason, various methods have been studied to improve the adhesiveness of the polyester film and to impart antistatic properties. Examples of the method for improving the adhesiveness include a method of treating the film surface with an actinic ray such as corona discharge, ultraviolet light, or plasma, and a method of applying an easily adhesive resin such as polyester, polyacrylate, or polyurethane. Further, as a method of imparting antistatic properties, surfactants having antistatic properties, antistatic agents such as ionic compounds,
There is a method of kneading or applying a conductive substance such as metal powder or metal oxide into polyester.
【0005】これらの方法の中でも、易接着性樹脂を塗
布する際に帯電防止剤や導電性物質を添加することによ
って、塗布層に接着性と帯電防止性を同時に付与する方
法が容易である。ただし導電性物質を添加する方法は、
低湿度の環境下で帯電防止性が低下するといった界面活
性剤やイオン性化合物等の帯電防止剤が有する問題は起
きないが、塗布層中に大量の導電性物質を添加しなけれ
ば帯電防止性効果が発現しないために接着性の付与効果
が低減するという問題があった。また、導電性物質は高
価であるためコストが上がるという問題も持っていた。
これらのことから、帯電防止剤を用いる方法がどちらか
というと一般的である。[0005] Among these methods, it is easy to add an antistatic agent or a conductive substance at the time of applying the easily-adhesive resin to simultaneously impart adhesiveness and antistatic property to the coating layer. However, the method of adding a conductive substance is
It does not cause the problems of antistatic agents such as surfactants and ionic compounds that lower the antistatic properties in a low humidity environment, but the antistatic properties must be added unless a large amount of conductive material is added to the coating layer. There is a problem that the effect of imparting adhesiveness is reduced because the effect is not exhibited. In addition, there is also a problem that the cost increases because the conductive material is expensive.
For these reasons, the method using an antistatic agent is rather common.
【0006】一方、帯電防止性と易接着性を付与するた
めの塗布層を有する二軸延伸ポリエステルフィルムの製
造方法として、塗布液を塗布後フィルムを延伸、熱処理
する塗布延伸法(インラインコート法)といわれるもの
がある。この方法は、二軸延伸後のポリエステルフィル
ムに塗布液を塗布して塗布層を形成する方法と比較する
と、フィルムの製膜と塗布を同時に実施するため幅広の
製品が比較的安価に得られるだけでなく、塗布層と基材
のポリエステルフィルムの密着性が良いものが得られる
等の特徴を有しており有用な方法である。On the other hand, as a method for producing a biaxially stretched polyester film having a coating layer for imparting antistatic properties and easy adhesion, a coating and stretching method in which a coating solution is applied and then the film is stretched and heat-treated (in-line coating method). There is something called. Compared with the method of applying a coating solution to a polyester film after biaxial stretching and forming a coating layer, this method can obtain a wide product relatively inexpensively because the film is formed and applied simultaneously. However, it is a useful method because it has characteristics such as obtaining a film having good adhesion between the coating layer and the polyester film of the substrate.
【0007】しかしながら、インラインコート法により
帯電防止性ポリエステルフィルムを製造する場合には、
一般に帯電防止剤が熱的に不安定なため延伸等の熱処理
工程で揮散あるいは熱分解が生じて期待された帯電防止
効果が発揮されない場合が多い。従って、従来は熱安定
性の良好なアニオン型やノニオン型の化合物をバインダ
ー樹脂と混ぜて塗布する方法が採用されてきた。しか
し、アニオン型やノニオン型の帯電防止剤は高湿度下で
は実用的な帯電防止性を発現するが、帯電防止性に対す
る環境の湿度の影響が大きく、低湿度下では帯電防止性
が低下するという問題があった。However, when producing an antistatic polyester film by an in-line coating method,
In general, since an antistatic agent is thermally unstable, volatilization or thermal decomposition occurs in a heat treatment step such as stretching, so that an expected antistatic effect is often not exhibited. Therefore, conventionally, a method has been adopted in which an anionic or nonionic compound having good thermal stability is mixed with a binder resin and applied. However, anionic or nonionic antistatic agents exhibit practical antistatic properties under high humidity, but the effect of environmental humidity on the antistatic properties is large, and the antistatic properties decrease under low humidity. There was a problem.
【0008】また、帯電防止剤の添加のために接着性が
低下したり、塗布層の耐水性や耐溶剤性が低下するとい
う問題も発生しており、磁気カード用基材として良好な
接着性と帯電防止性を合わせ持つポリエステルフィルム
は得られていないのが現状である。[0008] In addition, the addition of an antistatic agent causes problems such as a decrease in adhesiveness and a decrease in water resistance and solvent resistance of the coating layer. At present, a polyester film having both antistatic properties and antistatic properties has not been obtained.
【0009】[0009]
【発明が解決しようとする課題】本発明は、上記のよう
な従来技術の問題点を解決し、静電気の発生、蓄積によ
る静電気障害を起こさず、磁性層や印刷層との接着性に
優れた磁気カード用ポリエステルフィルムを提供するこ
とを目的とする。The present invention solves the above-mentioned problems of the prior art, does not cause static electricity damage due to generation and accumulation of static electricity, and has excellent adhesion to a magnetic layer or a printed layer. An object of the present invention is to provide a polyester film for a magnetic card.
【0010】[0010]
【課題を解決するための手段】上記目的を解決すること
ができた本発明の磁気カード用ポリエステルフィルム
は、白色顔料を含有するポリエステルフィルムの少なく
とも片面に、側鎖にカチオン型の第4級アンモニウム塩
基を有し、かつ末端に重合性の二重結合を有する単官能
ビニル単量体(X)、水酸基を有する単官能ビニル単量
体(Y)、およびこれらの単量体と共重合可能な他の重
合性ビニル単量体(Z)を共重合して得られる水溶性イ
オン導電性樹脂(A)および熱架橋性単量体(B)を主
成分とする塗膜形成用樹脂組成物を塗布したものである
ところに要旨を有する。すなわち本発明は、上記樹脂組
成物をポリエステルフィルムに塗布することによって、
帯電防止性付与と接着性改善を同時に達成することに成
功したものである。The polyester film for a magnetic card according to the present invention, which can solve the above-mentioned object, comprises a polyester film containing a white pigment and at least one side chain of a cationic quaternary ammonium. Monofunctional vinyl monomer (X) having a base and having a polymerizable double bond at a terminal, monofunctional vinyl monomer (Y) having a hydroxyl group, and copolymerizable with these monomers A water-soluble ionic conductive resin (A) obtained by copolymerizing another polymerizable vinyl monomer (Z) and a resin composition for forming a coating film containing a thermally crosslinkable monomer (B) as main components. It has a gist where it is applied. That is, the present invention, by applying the resin composition to a polyester film,
It has succeeded in simultaneously providing the antistatic property and improving the adhesive property.
【0011】[0011]
【作用】本発明におけるポリエステルとは、テレフタル
酸、イソフタル酸、ナフタレンジカルボン酸等の芳香族
ジカルボン酸またはそのエステルと、エチレングリコー
ル、ジエチレングリコール、1,4-ブタンジオール、ネオ
ペンチルグリコール等のグリコールとを重縮合させて製
造されるポリエステルである。これらのポリエステルは
芳香族ジカルボン酸とグリコールを直接反応させる方法
や、芳香族ジカルボン酸のアルキルエステルとグリコー
ルをエステル交換反応させた後重縮合させる方法や、あ
るいは芳香族ジカルボン酸のジグリコールエステルを重
縮合させる方法等によって製造される。このようなポリ
エステルの代表例としては、ポリエチレンテレフタレー
ト、ポリブチレンテレフタレートあるいはポリエチレン
-2,6−ナフタレート等が挙げられる。これらのポリエス
テルはホモポリマーであっても、また第三成分を共重合
したものであってもよいが、エチレンテレフタレート単
位、ブチレンテレフタレート単位あるいはエチレン-2,6
- ナフタレート単位が70モル%以上、このましくは8
0モル%以上、さらに好ましくは90モル%以上である
ポリエステルが用いられる。The polyester in the present invention is an aromatic dicarboxylic acid such as terephthalic acid, isophthalic acid or naphthalenedicarboxylic acid or an ester thereof, and a glycol such as ethylene glycol, diethylene glycol, 1,4-butanediol or neopentyl glycol. Polyester produced by polycondensation. These polyesters can be prepared by a method of directly reacting an aromatic dicarboxylic acid and a glycol, a method of subjecting an alkyl ester of an aromatic dicarboxylic acid to a transesterification reaction with a glycol and then a polycondensation, or a method of polymerizing a diglycol ester of an aromatic dicarboxylic acid. It is produced by a method of condensation and the like. Representative examples of such polyesters include polyethylene terephthalate, polybutylene terephthalate and polyethylene.
-2,6-naphthalate and the like. These polyesters may be homopolymers, or may be those obtained by copolymerizing a third component, and include ethylene terephthalate units, butylene terephthalate units or ethylene-2,6.
-Naphthalate units are at least 70 mol%, preferably 8
A polyester having 0 mol% or more, more preferably 90 mol% or more is used.
【0012】本発明では、上記ポリエステルフィルム中
に白色顔料が混入される。白色顔料はポリエステルフィ
ルムを磁気カード化した場合に光線の透過を防いで印刷
層が裏面から見えないようにするために使用するもので
ある。白色顔料としては、ポリエステルに不溶性の熱可
塑性樹脂を海島状に分散させて光を散乱させるような熱
可塑性樹脂を用いてもよいし、ポリエステルに不溶性の
架橋型高分子等の有機粒子やあるいは無機粒子を用いて
もよい。In the present invention, a white pigment is mixed in the polyester film. The white pigment is used to prevent the transmission of light rays when the polyester film is formed into a magnetic card so that the printed layer cannot be seen from the back surface. As the white pigment, a thermoplastic resin that disperses a thermoplastic resin insoluble in polyester in a sea-island manner and scatters light may be used, or organic particles such as a cross-linked polymer insoluble in polyester or inorganic particles may be used. Particles may be used.
【0013】ポリエステルに不溶性の熱可塑性樹脂とし
ては、上記ポリエステルに不溶性のものであれば制限な
く用いることができるが、300℃以下で溶解するもの
であり、かつ押出し温度において安定性の良好なものが
好ましい。具体的には、ポリエチレン、ポリプロピレ
ン、ポリメチルペンテン等のポリオレフィン系樹脂;ア
イオノマー樹脂、EPラバー等の共重合ポリオレフィン
樹脂;ポリスチレン、スチレン−アクリロニトリル共重
合体、スチレン−ブタジエン−アクリロニトリル共重合
体等のポリスチレン系樹脂;ポリアリレート樹脂;ポリ
カーボネート樹脂;ポリアクリロニトリル系樹脂等を挙
げることができる。これらの中で、ポリオレフィン系樹
脂およびポリスチレン系樹脂が特に好適である。As the thermoplastic resin insoluble in polyester, any thermoplastic resin which is insoluble in the above-mentioned polyester can be used without any limitation. It is a resin which is soluble at 300 ° C. or less and has good stability at the extrusion temperature. Is preferred. Specifically, polyolefin resins such as polyethylene, polypropylene and polymethylpentene; copolymerized polyolefin resins such as ionomer resin and EP rubber; polystyrene such as polystyrene, styrene-acrylonitrile copolymer and styrene-butadiene-acrylonitrile copolymer Resin; polyarylate resin; polycarbonate resin; polyacrylonitrile resin, and the like. Among these, polyolefin-based resins and polystyrene-based resins are particularly preferred.
【0014】架橋型高分子等の有機粒子としては、ポリ
スチレン系粒子、ポリアクリル酸系粒子、ポリシロキサ
ン系粒子等を挙げることができる。また、無機粒子とし
ては、タルク、カオリン、硫酸バリウム、炭酸カルシウ
ム、酸化チタン、ゼオライト等を挙げることができ、酸
化チタンおよび炭酸カルシウムが好ましく使用できる。Examples of the organic particles such as a crosslinked polymer include polystyrene particles, polyacrylic acid particles, and polysiloxane particles. Examples of the inorganic particles include talc, kaolin, barium sulfate, calcium carbonate, titanium oxide, and zeolite. Titanium oxide and calcium carbonate are preferably used.
【0015】これらの熱可塑性樹脂、有機粒子および無
機粒子は単独で用いてもよいし、2種以上を併用しても
よい。特に無機粒子単独系かまたは熱可塑性樹脂と無機
粒子の併用系が好ましい。These thermoplastic resins, organic particles and inorganic particles may be used alone or in combination of two or more. In particular, a single inorganic particle system or a combination of a thermoplastic resin and inorganic particles is preferred.
【0016】ポリエステルフィルム中の上記白色顔料の
含有量は、白色顔料の種類、分散法、磁気カード基材と
しての厚さ、磁気カードの種類等に応じて適宜決められ
るが、磁性層および印刷層を設ける前のポリエステルフ
ィルムとして、JIS K6714 に準じ、ポイック積分球式
H.T.R. メーター(日本精密光学製)を用いて測定した
場合の光線透過率が50%以下、好ましくは40%以
下、さらに好ましくは20%以下となるように含有させ
ることが推奨される。The content of the above white pigment in the polyester film is appropriately determined according to the type of the white pigment, the dispersion method, the thickness as a magnetic card substrate, the type of a magnetic card, and the like. As a polyester film before the installation, a Poic integrating sphere type according to JIS K6714
It is recommended that the light transmittance be 50% or less, preferably 40% or less, more preferably 20% or less when measured using an HTR meter (manufactured by Nippon Seimitsu Optical).
【0017】白色顔料をポリエステルフィルムに含有さ
せるには、ポリエステルの重合工程中に添加する方法、
ポリエステル重合体に押出機等を用いて白色顔料を予め
練込む方法、フィルム製造工程における押出工程で白色
顔料を混合する方法等を採用することができる。本発明
のポリエステル中には上記白色顔料の他に、用途に応じ
て着色剤、耐光剤、蛍光剤、帯電防止剤等を添加するこ
とも可能である。In order to incorporate a white pigment into a polyester film, a method of adding the white pigment during a polyester polymerization step is provided.
A method in which a white pigment is previously kneaded into the polyester polymer using an extruder or the like, a method in which the white pigment is mixed in the extrusion step in the film production step, and the like can be adopted. In addition to the above-mentioned white pigment, a coloring agent, a light-fast agent, a fluorescent agent, an antistatic agent and the like can be added to the polyester of the present invention depending on the use.
【0018】こうして得られたポリエステルは、公知の
溶融押出し法でフィルム化された後、さらに速度差をも
ったロール間での延伸(ロール延伸)や、クリップに把
持して拡げていくことによる延伸(テンター延伸)や、
空気圧によって拡げることによる延伸(インフレーショ
ン延伸)等によって、少なくとも1軸に配向処理される
ことが好ましい。The polyester thus obtained is formed into a film by a known melt extrusion method, and then stretched between rolls having a further difference in speed (roll stretching), or stretched by being gripped and spread by clips. (Tenter stretching),
It is preferable that the film is at least uniaxially oriented by stretching (inflation stretching) by expanding by air pressure.
【0019】本発明では、ポリエステルフィルムの少な
くとも片面に、側鎖にカチオン型の第4級アンモニウム
塩基を有し、かつ末端に重合性二重結合を有する単官能
ビニル単量体(X)と、水酸基を有する単官能ビニル単
量体(Y)と、XおよびYとの共重合可能な他の重合性
ビニル単量体(Z)を共重合して得られる水溶性イオン
導電性樹脂(A)および熱架橋性単量体(B)を主成分
とする塗膜形成用樹脂組成物が塗布されていることが必
須要件である。この塗膜形成用樹脂組成物をポリエステ
ルフィルム表面に塗布することにより、接着性と帯電防
止性を同時に付与することが可能である。In the present invention, a monofunctional vinyl monomer (X) having a cationic quaternary ammonium base in a side chain and having a polymerizable double bond at a terminal is provided on at least one surface of the polyester film; Water-soluble ionic conductive resin (A) obtained by copolymerizing monofunctional vinyl monomer (Y) having a hydroxyl group with another polymerizable vinyl monomer (Z) copolymerizable with X and Y In addition, it is an essential requirement that a resin composition for forming a coating film containing a thermally crosslinkable monomer (B) as a main component is applied. By applying the resin composition for forming a coating film on the surface of a polyester film, it is possible to simultaneously impart adhesiveness and antistatic properties.
【0020】上記イオン導電性樹脂(A)中の、側鎖に
カチオン型の第4級アンモニウム塩基および末端に重合
性の二重結合を有する単官能ビニル単量体(X)として
は、例えばジメチルアミノエチルアクリレート4級化
物、ジメチルアミノエチルメタクリレート4級化物、ジ
エチルアミノエチルアクリレート4級化物、ジエチルア
ミノエチルメタクリレート4級化物、メチルエチルアミ
ノエチルアクリレート4級化物、メチルエチルアミノエ
チルメタクリレート4級化物、ジメチルアミノスチレン
4級化物、メチルエチルアミノスチレン4級化物等が挙
げられ、これらの1種または2種以上を使用することが
できる。The monofunctional vinyl monomer (X) having a cationic quaternary ammonium base in the side chain and a polymerizable double bond at the terminal in the ionic conductive resin (A) is, for example, dimethyl Quaternary aminoethyl acrylate, quaternary dimethylaminoethyl methacrylate, quaternary diethylaminoethyl acrylate, quaternary diethylaminoethyl methacrylate, quaternary methylethylaminoethyl acrylate, quaternary methylethylaminoethyl methacrylate, dimethylaminostyrene A quaternary compound, a quaternary compound of methylethylaminostyrene, and the like, and one or more of these can be used.
【0021】また、水酸基を有する単官能ビニル単量体
(Y)としては、例えば2−ヒドロキシエチルアクリレ
ート、2−ヒドロキシエチルメタクリレート等が挙げら
れ、上記(X)および(Y)と共重合可能な他の重合性
ビニル単量体(Z)としては、アクリル酸メチル、アク
リル酸エチル等のアクリル酸アルキルエステル、メタク
リル酸メチル、メタクリル酸エチル等のメタクリル酸ア
ルキルエステル、スチレン、ビニルトルエン、酢酸ビニ
ル等のビニル単量体が挙げられる。Examples of the monofunctional vinyl monomer having a hydroxyl group (Y) include 2-hydroxyethyl acrylate and 2-hydroxyethyl methacrylate, which are copolymerizable with the above (X) and (Y). Other polymerizable vinyl monomers (Z) include alkyl acrylates such as methyl acrylate and ethyl acrylate, alkyl methacrylates such as methyl methacrylate and ethyl methacrylate, styrene, vinyl toluene, vinyl acetate and the like. Vinyl monomer.
【0022】上記単官能ビニル単量体(X)と、単官能
ビニル単量体(Y)と、他の重合性ビニル単量体(Z)
を従来公知のラジカル重合で共重合することによりイオ
ン導電性樹脂(A)が得られるが、これらの共重合割合
は、(Y+Z)/Xの重合比率として5/1〜2/1の
範囲が好ましい。この重合比が5/1を超えるとイオン
導電性樹脂(A)の水溶性が低下したり、イオン導電性
樹脂(A)中にカチオン型の第4級アンモニウム塩基を
導入するための単官能ビニル単量体(X)の比率が結果
的に少なくなるため、帯電防止性に優れた塗膜が得られ
ない。一方、上記共重合比率が2/1未満の場合には塗
膜の耐水性が低下する傾向となり、得られた塗膜のべた
つきやブロッキング性が増加する。The above monofunctional vinyl monomer (X), monofunctional vinyl monomer (Y), and another polymerizable vinyl monomer (Z)
Is copolymerized by a conventionally known radical polymerization to obtain an ion-conductive resin (A), and the copolymerization ratio thereof is in a range of 5/1 to 2/1 as a polymerization ratio of (Y + Z) / X. preferable. When the polymerization ratio exceeds 5/1, the water solubility of the ionic conductive resin (A) decreases, or a monofunctional vinyl for introducing a cationic quaternary ammonium base into the ionic conductive resin (A). Since the ratio of the monomer (X) is consequently reduced, a coating film having excellent antistatic properties cannot be obtained. On the other hand, when the copolymerization ratio is less than 2/1, the water resistance of the coating film tends to decrease, and the resulting coating film has increased tackiness and blocking property.
【0023】また、(X+Z)/Yの重合比率は、10
/1〜15/1の範囲が好ましく、この重合比率が15
/1を超えると、水酸基を有する単官能ビニル単量体
(Y)が少なくなって後述の熱架橋性単量体(B)との
架橋点となる水酸基が少なくなり結果的に架橋性が不足
するため、塗膜の耐水性および耐溶剤性が低下する。一
方、重合比率が10/1未満の場合には、水酸基が多く
なり過ぎて、やはり塗膜の耐水性および耐溶剤性が低下
する。The polymerization ratio of (X + Z) / Y is 10
/ 1 to 15/1 are preferable, and the polymerization ratio is 15
When the ratio exceeds / 1, the amount of the hydroxyl group-containing monofunctional vinyl monomer (Y) decreases, and the number of hydroxyl groups serving as crosslinking points with the thermally crosslinkable monomer (B) described below decreases, resulting in insufficient crosslinkability. Therefore, the water resistance and solvent resistance of the coating film decrease. On the other hand, when the polymerization ratio is less than 10/1, the number of hydroxyl groups becomes too large, and the water resistance and solvent resistance of the coating film also decrease.
【0024】イオン導電性樹脂(A)と共に塗膜形成用
樹脂組成物を構成する熱架橋性単量体(B)は、上記単
量体(Y)中の水酸基との反応性を有する単量体であれ
ば特に限定されないが、2〜4個のグリシジル基を有す
るエポキシ化合物が好ましく用いられる。このようなエ
ポキシ化合物の具体例としては、例えばエチレングリコ
ールグリシジルエーテル、ポリエチレングリコールジグ
リシジルエーテル、プロピレングリコールジグリシジル
エーテル、ポリプロピレングリコールジグリシジルエー
テル、ネオペンチルグリコールジグリシジルエーテル、
グリセロールポリグリシジルエーテル、トリメチロール
プロパンポリグリシジルエーテル、ジグリセロールポリ
グリシジルエーテル等が挙げられ、これらの1種または
2種以上を使用することができる。The thermally crosslinkable monomer (B) constituting the resin composition for forming a coating film together with the ionic conductive resin (A) is a monomer having a reactivity with a hydroxyl group in the monomer (Y). Although it is not particularly limited as long as it is a body, an epoxy compound having 2 to 4 glycidyl groups is preferably used. Specific examples of such an epoxy compound include, for example, ethylene glycol glycidyl ether, polyethylene glycol diglycidyl ether, propylene glycol diglycidyl ether, polypropylene glycol diglycidyl ether, neopentyl glycol diglycidyl ether,
Glycerol polyglycidyl ether, trimethylolpropane polyglycidyl ether, diglycerol polyglycidyl ether and the like can be mentioned, and one or more of these can be used.
【0025】本発明の塗膜形成用樹脂組成物中の、イオ
ン導電性樹脂(A)と熱架橋性単量体(B)との配合比
率は、重量比でA/Bが70/30〜97/3の範囲が
好ましい。配合比率が70/30未満の場合、熱架橋性
単量体(B)が過剰になるため得られる塗膜の耐水・耐
溶剤性は向上するが、帯電防止性が悪化したり、塗膜の
延展性が低下する。配合比率が97/3を超えると、熱
架橋性単量体(B)の量が減少して架橋反応性が低下す
ることにより塗膜の耐水・耐溶剤性が悪化したり、やは
り塗膜の延展性が低下し帯電防止性が悪化するため好ま
しくない。The mixing ratio of the ionic conductive resin (A) and the thermally crosslinkable monomer (B) in the resin composition for forming a coating film of the present invention is such that A / B is 70/30 to 70% by weight. A range of 97/3 is preferred. When the compounding ratio is less than 70/30, the heat-crosslinkable monomer (B) becomes excessive, so that the water resistance and solvent resistance of the obtained coating film are improved, but the antistatic property is deteriorated, The spreadability decreases. When the compounding ratio exceeds 97/3, the amount of the thermo-crosslinkable monomer (B) decreases and the crosslinking reactivity decreases, thereby deteriorating the water resistance and solvent resistance of the coating film. It is not preferable because the spreadability decreases and the antistatic property deteriorates.
【0026】なお本発明では、上記塗膜形成用樹脂組成
物を使用して塗膜を形成する場合、熱架橋性単量体
(B)を構成しているエポキシ化合物の架橋反応を促進
させるために、架橋促進剤として有機もしくは無機の水
溶性アルカリ化合物、例えば、アミン、ポリアミン、ア
ミドアミン、ポリアミドアミン、イミダゾール、アルカ
リ金属炭酸塩、およびこれらの誘導体を少量使用するこ
とが望ましい。In the present invention, when a coating film is formed using the above-mentioned resin composition for forming a coating film, the crosslinking reaction of the epoxy compound constituting the thermally crosslinkable monomer (B) is promoted. In addition, it is desirable to use a small amount of an organic or inorganic water-soluble alkali compound as a crosslinking accelerator, for example, amine, polyamine, amidoamine, polyamidoamine, imidazole, alkali metal carbonate, and derivatives thereof.
【0027】本発明では、イオン導電性樹脂(A)が水
溶性であるので、塗膜形成用樹脂組成物を水溶液で用い
ることが好ましいが、ポリエステルとの濡れ性を改良す
る等の目的でアルコール等の有機溶剤を併用しても良
い。また、塗膜形成用樹脂組成物中には、必要に応じて
他の架橋剤、触媒、濡れ剤等や本発明の目的を阻害しな
い範囲で紫外線吸収剤、顔料、有機フィラー、無機フィ
ラー、潤滑剤、ブロッキング防止剤等を添加してもよ
い。また他のバインダー樹脂を併用し、接着性やブロッ
キング性等の特性の改良を行なうこともできる。In the present invention, since the ion-conductive resin (A) is water-soluble, it is preferable to use the resin composition for forming a coating film in an aqueous solution, but it is preferable to use an alcohol for the purpose of improving the wettability with the polyester. May be used in combination. Further, in the resin composition for forming a coating film, if necessary, other crosslinking agents, catalysts, wetting agents, etc. and ultraviolet absorbers, pigments, organic fillers, inorganic fillers, lubricating agents, etc. within a range not to impair the object of the present invention. Agents, anti-blocking agents and the like may be added. Further, properties such as adhesion and blocking properties can be improved by using another binder resin in combination.
【0028】本発明の磁気カード用ポリエステルフィル
ムは、上記塗膜形成用樹脂組成物の溶液を、前記した白
色顔料を含有するポリエステルの少なくとも片面に塗布
することにより製造される。塗布層を設ける方法として
は、グラビアコート方式、キスコート方式、ディップ方
式、スプレイコート方式、カーテンコート方式、エアー
ナイフコート方式、プレードコート方式、リバースロー
ルコート方式等通常用いられている方法が適用できる。
塗布する段階としては、配向処理を行なう前のフィルム
表面に予め塗布する方法、1軸方向に配向したフィルム
表面に塗布し、それをさらに直角方向に配向させる方法
(インラインコート法)、配向処理の終了したフィルム
表面に塗布する方法等が採用できる。中でも、配向処理
を行なう前のフィルム表面に予め塗布する方法やインラ
インコート法が、その後の配向処理時の熱固定で同時に
熱架橋も行なえるため特に推奨される。The polyester film for a magnetic card of the present invention is produced by applying a solution of the resin composition for forming a coating film to at least one surface of the polyester containing the white pigment. As a method of providing the coating layer, a commonly used method such as a gravure coat method, a kiss coat method, a dip method, a spray coat method, a curtain coat method, an air knife coat method, a spread coat method, and a reverse roll coat method can be applied.
As a step of applying, a method of applying in advance to a film surface before performing an orientation treatment, a method of applying the film to a film surface oriented in an axial direction and further orienting it in a perpendicular direction (in-line coating method), A method of coating the finished film surface or the like can be adopted. Among them, a method of applying the film to the surface of the film before the orientation treatment or an in-line coating method is particularly recommended because heat crosslinking at the time of the subsequent orientation treatment can simultaneously perform thermal crosslinking.
【0029】本発明に係る塗膜形成用樹脂組成物は、ポ
リエステルフィルムの片面に塗布しただけで塗布面のみ
でなく非塗布面にも帯電防止性が発現するため、ポリエ
ステルフィルムの片面に塗布されれば該フィルムの帯電
防止性能は充分優れたものとなるが、両面に塗布すれば
両面共に磁性層や印刷層との接着性が向上する。また、
片面に上記塗膜形成用樹脂組成物を塗布し、この塗布面
の反対側の面に接着性を向上させる特性を有した他のバ
インダー樹脂層を塗布する方法を採用してもかまわな
い。The resin composition for forming a coating film according to the present invention exhibits antistatic properties not only on the coated surface but also on the non-coated surface only by being coated on one surface of the polyester film. If this is the case, the antistatic performance of the film will be sufficiently excellent, but if it is applied to both sides, the adhesion to the magnetic layer and the print layer will improve on both sides. Also,
A method of applying the above-mentioned resin composition for forming a coating film on one surface and applying another binder resin layer having a property of improving adhesiveness to the surface opposite to the application surface may be adopted.
【0030】ポリエステルフィルムに塗布される塗膜形
成用樹脂組成物の溶液の塗布量は、二軸延伸後のフィル
ム上に存在する固形分量として0.01〜5g/m2 が
好ましい。塗布量が0.01g/m2 未満の場合は、充
分な帯電防止性が得られず、5g/m2 以上塗布すると
ブロッキングが問題となる。本発明に用いられるポリエ
ステルフィルム自体の厚さは、磁気カードの用途に応じ
て決定されるが一般的には100〜500μmのものが
好ましく用いられる。The amount of the solution of the resin composition for forming a coating film applied to the polyester film is preferably 0.01 to 5 g / m 2 as a solid content present on the film after biaxial stretching. If the coating amount is less than 0.01 g / m 2 , sufficient antistatic properties cannot be obtained, and if the coating amount is 5 g / m 2 or more, blocking becomes a problem. The thickness of the polyester film itself used in the present invention is determined according to the use of the magnetic card, but generally 100 to 500 μm is preferably used.
【0031】上記塗膜形成用樹脂組成物の溶液を塗布す
る前に、例えばフィルムにコロナ放電処理を施す等、溶
液の塗布性を改良したりフィルムと塗膜との間の接着性
を改善しても構わない。また塗布層にさらにコロナ放電
処理、窒素雰囲気下でのコロナ放電処理、紫外線照射処
理等を施すことによってフィルム表面の濡れ性や接着性
を向上させることもできる。Before applying the solution of the resin composition for forming a coating film, the coatability of the solution can be improved by, for example, subjecting the film to a corona discharge treatment, or the adhesiveness between the film and the coating film can be improved. It does not matter. The wettability and adhesion of the film surface can be improved by subjecting the coating layer to a corona discharge treatment, a corona discharge treatment in a nitrogen atmosphere, an ultraviolet irradiation treatment, or the like.
【0032】[0032]
【実施例】以下に実施例を挙げて本発明をより具体的に
説明するが、本発明はこれらの実施例に限定されるもの
ではなく、本発明の前・後記の趣旨を逸脱しない範囲で
変更・実施することは本発明に含まれる。なお、実施例
で行なった測定方法および評価方法は次の通りである。EXAMPLES The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples and it does not depart from the gist of the present invention. Changes and implementations are included in the present invention. In addition, the measuring method and the evaluation method performed in the Example are as follows.
【0033】光線透過率 JIS K6714 に準じ、ポイック積分球式H.T.R.メーター
(日本精密光学製)を用いて測定した。 磁性塗料との接着性 試料フィルムに下記磁性塗料を所定の条件でコーティン
グした後、塗布面に幅10mm、長さ10cmのスコッ
チテープNo.610(3M社製)を気泡が入らないよ
うに貼り付けてロールでならし、23℃、50%RH下
で東洋ボールドウィン社製テンシロンを用い引張速度1
000cm/分で360°剥離試験を行なって剥離強度
を求めた。接着部分は5cmとし、チャック間距離は8
cmとした。Light transmittance was measured using a Poic integrating sphere HTR meter (manufactured by Nippon Seimitsu Kogaku) in accordance with JIS K6714. Adhesiveness to magnetic paint After coating the sample film with the following magnetic paint under predetermined conditions, a scotch tape No. 10 mm wide and 10 cm long was applied to the coated surface. 610 (manufactured by 3M) was stuck with a roll so that air bubbles did not enter, and a tensile speed of 1 was used at 23 ° C. and 50% RH using Tensilon manufactured by Toyo Baldwin.
Peel strength was determined by performing a 360 ° peel test at 000 cm / min. The bonding area is 5 cm, and the distance between chucks is 8
cm.
【0034】(評価用磁性塗料の調製および塗布方法) Co−γ−Fe2 O3 100重量部 塩化ビニル−酢酸ビニル共重合体 15重量部 ウレタン変性飽和ポリエステル樹脂 15重量部 α−アルミナ 3重量部 カーボンブラック 1重量部 トルエン 105重量部 メチルエチルケトン 105重量部 シクロヘキサノン 105重量部(Preparation and method of application of magnetic paint for evaluation) Co-γ-Fe 2 O 3 100 parts by weight Vinyl chloride-vinyl acetate copolymer 15 parts by weight Urethane-modified saturated polyester resin 15 parts by weight α-alumina 3 parts by weight Carbon black 1 part by weight Toluene 105 parts by weight Methyl ethyl ketone 105 parts by weight Cyclohexanone 105 parts by weight
【0035】上記評価様磁性塗料組成物をボールミルで
約12時間混合分散した後、パルミチン酸1重量部、ド
デシルステアレート2重量部、オレイン酸2重量部を加
えてさらに30分混合分散した。次いで、トリイソシア
ネート化合物の酢酸エチル溶液(固形分75重量%)を
10重量部加え、1時間混合分散し、磁性塗料を調製し
た。この磁性塗料を乾燥後の厚さで3μmとなるように
試料フィルム上に塗布し、磁場配向処理を施した後、6
0℃で乾燥し、次いでカレンダー処理を行ない、さらに
60℃で72時間エージングし硬化反応させた。After mixing and dispersing the magnetic coating composition for evaluation for about 12 hours in a ball mill, 1 part by weight of palmitic acid, 2 parts by weight of dodecyl stearate and 2 parts by weight of oleic acid were added and mixed and dispersed for another 30 minutes. Then, 10 parts by weight of an ethyl acetate solution of a triisocyanate compound (solid content: 75% by weight) was added and mixed and dispersed for 1 hour to prepare a magnetic paint. This magnetic paint is applied on a sample film so as to have a thickness after drying of 3 μm, and is subjected to a magnetic field orientation treatment.
It was dried at 0 ° C., then calendered, and aged at 60 ° C. for 72 hours to effect a curing reaction.
【0036】印刷インキとの接着性 セロハン用印刷インキとしてセロラーCCST 390藍(東洋
インキ製造社製)をグラビアコーターで乾燥後の厚さが
3μmになるように試料フィルム上に塗布し、乾燥後イ
ンキとフィルムの接着性をセロハンテープ剥離テストに
よって調べた。印刷面にセロハンテープを貼付した後、
フィルムを平面に保ちセロハンテープを約150°の方
向に剥離し、試料フィルムの印刷面におけるインキの残
存面積を画像処理装置ルーゼックスIID(ニレコ社製)
で測定し、%で表示した。残存面積が多いほど接着性が
良好である。Adhesiveness with printing ink Cellophane CCST 390 indigo (manufactured by Toyo Ink Mfg. Co., Ltd.) is applied as a printing ink for cellophane onto a sample film so as to have a thickness of 3 μm after drying with a gravure coater. The adhesiveness of the film and the film was examined by a cellophane tape peel test. After sticking cellophane tape on the printing surface,
The cellophane tape is peeled in a direction of about 150 ° while the film is kept flat, and the remaining area of the ink on the printed surface of the sample film is measured using an image processing device Luzex IID (manufactured by Nireco).
And measured in%. The larger the remaining area, the better the adhesion.
【0037】表面固有抵抗 タケダ理研社製固有抵抗測定器で印加電圧500V、2
3℃、50%RHの条件下で測定した。 帯電減衰性 米国のETS社製スタティックディケイメーターを用い
て、23℃、35%RHの条件下で電極間に試料フィル
ムをはさみ5.0KVの電圧を印加し、荷電圧が5.0
KVになったところで電極をアースし、アースしてから
荷電圧が0.05KVになるまでの減衰時間t99を測定
した。Surface resistivity: 500 V applied by a resistivity measurement device manufactured by Takeda Riken Co., Ltd.
The measurement was performed at 3 ° C. and 50% RH. Using a static decay meter manufactured by ETS in the United States, a sample film was sandwiched between the electrodes under a condition of 23 ° C. and 35% RH, a voltage of 5.0 KV was applied, and the charged voltage was 5.0.
Grounding the electrode was turned KV, it was measured decay time t 99 from the Ground until the load voltage becomes 0.05KV.
【0038】実施例1 常法によりメチルメタクリレート(MMA)/エチルア
クリレート(EA)/2−ヒドロキシエチルメタクリレ
ート(HEMA)/ジメチルアミノエチルメタクリレー
ト4級化物(DM)を、重量組成比として47/21/
7/25の割合で共重合して水溶性イオン導電性樹脂の
水溶液を得た。この水溶液に、エポキシ化合物としてグ
リセロールポリグリシジルエーテル(GPGE)をイオ
ン導電性樹脂固形分に対して4重量%添加し、さらに架
橋促進剤として2−メチルイミダゾールを前記グリセロ
ールポリグリシジルエーテルに対して2.5重量%添加
混合して固形分7重量%の塗膜形成用樹脂組成物の水溶
液を得た。 Example 1 Methyl methacrylate (MMA) / ethyl acrylate (EA) / 2-hydroxyethyl methacrylate (HEMA) / dimethylaminoethyl methacrylate quaternary product (DM) was prepared by a conventional method at a weight composition ratio of 47/21 /
An aqueous solution of a water-soluble ionic conductive resin was obtained by copolymerization at a ratio of 7/25. To this aqueous solution, glycerol polyglycidyl ether (GPGE) as an epoxy compound was added at 4% by weight based on the solid content of the ion conductive resin, and 2-methylimidazole was added as a crosslinking accelerator to the glycerol polyglycidyl ether. An aqueous solution of the resin composition for forming a coating film having a solid content of 7% by weight was obtained by adding and mixing 5% by weight.
【0039】一方、酸化チタンを5重量%含有するポリ
エチレンテレフタレートを溶融押出しし、縦方向に3.
0倍延伸した後、前記塗膜形成用樹脂組成物の水溶液
を、キスコート法で乾燥後10g/m2 となる様に塗布
し、70℃の熱風で乾燥した。次いで横方向に3.0倍
延伸し、さらに200〜210℃で熱固定を行なって、
厚さ250μmの2軸延伸後の試料フィルムを得た。こ
の試料フィルムの光線透過率は6%であった。試料フィ
ルムのその他の特性を表2に示した。On the other hand, polyethylene terephthalate containing 5% by weight of titanium oxide is melt-extruded, and 3.
After stretching 0 times, an aqueous solution of the resin composition for forming a coating film was applied by a kiss coat method so as to be 10 g / m 2 after drying, and dried with hot air at 70 ° C. Then stretched 3.0 times in the transverse direction, and heat-set at 200 to 210 ° C.
A sample film having a thickness of 250 μm after biaxial stretching was obtained. The light transmittance of this sample film was 6%. Table 2 shows other characteristics of the sample film.
【0040】実施例2〜5 塗膜形成用組成物の組成を表1に記載したように変更す
る以外は実施例1と同様にして試料フィルムを作成し、
特性の評価結果を表2に示した。なお、これらの試料フ
ィルムの光線透過率はいずれも6%であった。実施例6 実施例1において、酸化チタンを4重量%とし、さらに
ポリスチレン樹脂10重量%を含有するポリエチレンテ
レフタレートを溶融押出する以外は実施例1と同様の方
法によって、独立気泡を含有した見掛比重が1.23で
光線透過率が8%の試料フィルムを得た。この試料フィ
ルムの特性を表2に示した。 Examples 2 to 5 Sample films were prepared in the same manner as in Example 1 except that the composition of the coating film forming composition was changed as shown in Table 1.
Table 2 shows the evaluation results of the characteristics. The light transmittance of each of these sample films was 6%. Example 6 An apparent specific gravity containing closed cells was obtained in the same manner as in Example 1 except that 4% by weight of titanium oxide and polyethylene terephthalate containing 10% by weight of a polystyrene resin were melt-extruded. Was 1.23, and a sample film having a light transmittance of 8% was obtained. Table 2 shows the properties of this sample film.
【0041】比較例1〜3 塗膜形成用樹脂組成物の組成を表1に記載のように変更
する以外は実施例1と同様にして試料フィルムを作成し
た。特性評価結果を表2に示した。比較例4 表1の比較例2の樹脂(A)およびスルホン酸ナトリウ
ム塩を含む市販のアニオン系帯電防止剤を8/2の割合
で混合した溶液を塗布液とする以外は実施例1と同様に
して行ない試料フィルムを作成した。特性評価結果は表
2に示した。比較例5 塗膜形成用樹脂組成物の水溶性を塗布しない以外は実施
例1と同様にして試料フィルムを得た。特性評価結果は
表2に示した。 Comparative Examples 1 to 3 Sample films were prepared in the same manner as in Example 1 except that the composition of the resin composition for forming a coating film was changed as shown in Table 1. Table 2 shows the characteristic evaluation results. Comparative Example 4 Same as Example 1 except that a solution obtained by mixing a resin (A) of Comparative Example 2 in Table 1 and a commercially available anionic antistatic agent containing sodium sulfonate at a ratio of 8/2 was used as a coating solution. To prepare a sample film. The characteristics evaluation results are shown in Table 2. Comparative Example 5 A sample film was obtained in the same manner as in Example 1, except that the water solubility of the resin composition for forming a coating film was not applied. The characteristics evaluation results are shown in Table 2.
【0042】[0042]
【表1】 [Table 1]
【0043】MMA :メチルメタクリレート EA :エチルアクリレート HEMA :2−ヒドロキシエチルメタクリレート DM :ジメチルアミノエチルメタクリレート4級
化物 GPGE :グリセロールポリグリシジルエーテル DGPGE:ジグリセロールポリグリシジルエーテル *実施例6は酸化チタン4重量%およびポリエスチレン
10重量% 含有したポリエチレンテレフタレートをベースフィルム
とした。MMA: methyl methacrylate EA: ethyl acrylate HEMA: 2-hydroxyethyl methacrylate DM: dimethylaminoethyl methacrylate quaternary product GPGE: glycerol polyglycidyl ether DGPGE: diglycerol polyglycidyl ether * In Example 6, 4% by weight of titanium oxide And polyethylene terephthalate containing 10% by weight of polystyrene as a base film.
【0044】[0044]
【表2】 [Table 2]
【0045】本実施例1〜6で得られた試料フィルムは
いずれも光線透過率が低く、磁性塗料や印刷インクとの
接着性に優れており、かつ、帯電防止性に優れたもので
あった。一方、比較例1では塗膜の延展性が乏しく不均
一な塗布となった。また得られたフィルムは接着性およ
び帯電防止性共に劣っている。比較例2の試料フィルム
は接着性は良好であるが帯電防止性が劣っており、比較
例3の試料フィルムは帯電性は良好であるが接着性が劣
っていた。市販の帯電防止剤を混合して用いた比較例4
の試料フィルム、および比較例5の非コーティングフィ
ルムはいずれも接着性、帯電防止性の劣ったものであっ
た。Each of the sample films obtained in Examples 1 to 6 had a low light transmittance, was excellent in adhesion to magnetic paints and printing inks, and was excellent in antistatic properties. . On the other hand, in Comparative Example 1, the spreadability of the coating film was poor and the coating was uneven. Further, the obtained film is inferior in both adhesiveness and antistatic property. The sample film of Comparative Example 2 had good adhesion but poor antistatic properties, and the sample film of Comparative Example 3 had good charging properties but poor adhesion. Comparative Example 4 using a commercially available antistatic agent
Each of the sample film and the uncoated film of Comparative Example 5 were inferior in adhesion and antistatic properties.
【0046】[0046]
【発明の効果】本発明のポリエステルフィルムは、白色
顔料を含有しているため光透過が防止されて磁気カード
とした時の印刷の効果が発揮できる。また特定の塗膜形
成用樹脂組成物を塗布してあるので磁性層や印刷層との
接着性が改良され、かつ静電気の発生や蓄積による静電
気障害を起こさない帯電防止性に優れたポリエステルフ
ィルムを提供することができた。このポリエステルフィ
ルムは磁気カード用の基体フィルムとして好適である。Since the polyester film of the present invention contains a white pigment, light transmission is prevented and the effect of printing when a magnetic card is formed can be exhibited. In addition, since a specific coating film forming resin composition has been applied, the adhesion to the magnetic layer and the printing layer is improved, and a polyester film with excellent antistatic properties that does not cause static electricity damage due to generation or accumulation of static electricity. Could be provided. This polyester film is suitable as a base film for a magnetic card.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭60−248745(JP,A) 特開 平5−1164(JP,A) (58)調査した分野(Int.Cl.7,DB名) C08J 7/04 - 7/06 B32B 27/00 - 27/42 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-60-248745 (JP, A) JP-A-5-1164 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) C08J 7/04-7/06 B32B 27/00-27/42
Claims (1)
ムの少なくとも片面に、側鎖にカチオン型の第4級アン
モニウム塩基を有し、かつ末端に重合性の二重結合を有
する単官能ビニル単量体(X)、水酸基を有する単官能
ビニル単量体(Y)、およびこれらの単量体と共重合可
能な他の重合性ビニル単量体(Z)を共重合して得られ
る水溶性イオン導電性樹脂(A)および熱架橋性単量体
(B)を主成分とする塗膜形成用樹脂組成物を塗布して
なることを特徴とする磁気カード用ポリエステルフィル
ム。1. A monofunctional vinyl monomer having a cationic quaternary ammonium base in a side chain and a polymerizable double bond at a terminal on at least one side of a polyester film containing a white pigment. X), a monofunctional vinyl monomer having a hydroxyl group (Y), and a water-soluble ionic conductive compound obtained by copolymerizing another polymerizable vinyl monomer (Z) copolymerizable with these monomers. A polyester film for a magnetic card, which is obtained by applying a resin composition for forming a coating film containing a resin (A) and a thermally crosslinkable monomer (B) as main components.