JP3269122B2 - Reflective projection screen - Google Patents
Reflective projection screenInfo
- Publication number
- JP3269122B2 JP3269122B2 JP18711292A JP18711292A JP3269122B2 JP 3269122 B2 JP3269122 B2 JP 3269122B2 JP 18711292 A JP18711292 A JP 18711292A JP 18711292 A JP18711292 A JP 18711292A JP 3269122 B2 JP3269122 B2 JP 3269122B2
- Authority
- JP
- Japan
- Prior art keywords
- projection screen
- screen
- reflection type
- sheet
- type projection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、映写スクリーン、とく
に映画などの動画を映写するための反射型映写スクリー
ンに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a projection screen, and more particularly to a reflection type projection screen for projecting a moving image such as a movie.
【０００２】[0002]
【従来の技術】反射型映写スクリーンは、液晶プロジェ
クターなどの投影装置の普及にともなって、より鮮明な
画像を得るための種々の改善が提案されている。 出願
人も、映写スクリーンとして適切な拡散性と反射率をも
ち、しかもシワがつきにくく取扱いの容易な反射型映写
スクリーンをいくつか提案した（たとえば実願平３−２
４６２号）。2. Description of the Related Art With the spread of projection devices such as a liquid crystal projector, various improvements for obtaining a clearer image have been proposed for a reflection type projection screen. The applicant has also proposed some reflection-type projection screens which have appropriate diffusivity and reflectance as projection screens, are hardly wrinkled, and are easy to handle (for example, Jpn.
462).
【０００３】最近では、映写装置と音響装置とを組み合
わせて、臨場感のある映像を楽しむ傾向が強くなってき
ている。 出願人は、音響効果を高めた反射型映写スク
リーンとして、上記の映写スクリーンにおいて、スクリ
ーンの背後に配置したスピーカーからの音が通過できる
ように、少なくともスピーカーの位置に多数の小孔を設
けた映写スクリーンを提案した（特願平３−１３１３９
８号）。In recent years, there has been a strong tendency to enjoy a realistic image by combining a projection device and an audio device. The applicant has proposed a projection screen having a large number of small holes at least at the position of the speaker so as to allow sound from a speaker arranged behind the screen to pass therethrough as a reflection type projection screen having an enhanced sound effect. The screen was proposed (Japanese Patent Application No. Hei 3-13139).
No. 8).
【０００４】ところが、一定のパターンで小孔を設けた
スクリーンは、小孔の周期と投影画素の周期とが同調す
ることが多く、その場合、モアレが発生して映像が見に
くくなることが経験された。However, in a screen provided with small holes in a fixed pattern, the cycle of the small holes and the cycle of the projected pixels are often synchronized, and in that case, moiré is generated, making it difficult to see the image. Was.
【０００５】[0005]
【発明が解決しようとする課題】本発明の目的は、スク
リーンの背後に配置したスピーカーの音を通過させるこ
とができ、従って音響効果を高めることのできる反射型
映写スクリーンであって、モアレの発生がなく、画像が
美麗なものを提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to provide a reflection type projection screen capable of transmitting sound of a speaker arranged behind the screen and thus enhancing the sound effect. Without providing a beautiful image.
【０００６】[0006]
【課題を解決するための手段】本発明の反射型映写スク
リーンは、図１に示すように、スクリーン（１）の背後
に配置したスピーカーからの音が通過できるように、少
なくともスピーカーの位置に多数の小孔（２）を設けた
反射型映写スクリーンにおいて、小孔の配置が周期性を
有していて、その周期が、 １）図２に示すように、小孔の配置の周期の方向がスク
リーンに投影される画素の周期の方向に対して１５〜７
５°の傾きをもっているか、または ２）図３に示すように、小孔の水平方向ピッチをＴｘ、
垂直方向のピッチをＴｙとし、投影される画素の水平方
向のピッチをｔｘ、垂直方向のピッチをｔｙとすると
き、 Ｔｘ／ｔｘ＝ｒ１， Ｔｙ／ｔｙ＝ｒ２ のｒ１およびｒ２がともに非整数であることを特徴とす
る。As shown in FIG. 1, the reflection type projection screen of the present invention has a large number of speakers at least at the positions of the speakers so that sound from speakers located behind the screen (1) can pass therethrough. In the reflection type projection screen provided with the small holes (2), the arrangement of the small holes has a periodicity, and the period of the small holes is: 1) As shown in FIG. 15 to 7 with respect to the direction of the period of the pixel projected on the screen
2) As shown in FIG. 3, the horizontal pitch of the small holes is Tx,
The pitch in the vertical direction and Ty, tx the horizontal pitch of the pixels to be projected, when the pitch of the vertical direction and ty, r 1 and r 2 of the Tx / tx = r 1, Ty / ty = r 2 is Both are non-integer.
【０００７】上記の２）の場合、ｒ１およびｒ２が、
（Ｎ＋０．３５）〜（Ｎ＋０．４３）の範囲（Ｎは１〜
１２の整数）にあることが望ましい。In case 2) above, r 1 and r 2 are:
The range of (N + 0.35) to (N + 0.43) (N is 1 to
(An integer of 12).
【０００８】スクリーンに設ける小孔の大きさは、直径
が０．５〜２．０mmの範囲が適当であり、その開口比
は、大きすぎると孔が目立つ上にスクリーンの裏側が見
えてしまい、小さすぎると音が通過しにくくなるので、
１〜２０％、とくに３〜１０％の範囲にすることが好ま
しい。 ここで「開口比」の語は、スクリーンの総面積
に対する、小孔の面積の合計の割合を意味する。 小孔
の形状は円または楕円にすると、スクリーンが引張られ
たときにも裂けにくくて好ましい。 小孔はスクリーン
の全面に設けてもよいが、固定式スクリーンのようにそ
の背後に配置するスピーカーの位置が定まっている場合
は、スピーカーに対向する部分にのみ小孔を設ければよ
い。The size of the small holes provided in the screen is suitably in the range of 0.5 to 2.0 mm in diameter. If the aperture ratio is too large, the holes are conspicuous and the back side of the screen is visible. If it is too small, the sound will not pass easily,
The content is preferably in the range of 1 to 20%, particularly 3 to 10%. Here, the term "aperture ratio" means the ratio of the total area of the small holes to the total area of the screen. The shape of the small holes is preferably a circle or an ellipse because the screen is less likely to tear when the screen is pulled. The small holes may be provided on the entire surface of the screen. However, when the position of the speaker disposed behind the fixed screen is fixed, as in the case of a fixed screen, the small holes may be provided only in the portion facing the speakers.
【０００９】スクリーンの穿孔は、刃型による打抜き、
ドリル穿孔、ＣＯ2 レーザによる溶融などの手段で行な
う。[0009] The perforation of the screen is performed by punching with a blade mold,
This is performed by means such as drilling and melting with a CO 2 laser.
【００１０】小孔を設けるスクリーンには、種々のタイ
プのものがある。 穿孔が可能であれば、どのタイプの
スクリーンをえらんでもよいが、その中でも映像が鮮明
なスクリーンの例をあげれば、次のとおりである。There are various types of screens provided with small holes. Any type of screen may be selected as long as perforation is possible. Among them, an example of a screen having a clear image is as follows.
【００１１】可撓性を有する基布または剛性を有する基
板の一方の面に暗色のプラスチックシートからなる光吸
収層を設け、他方の面に、白色不透明で柔軟なプラスチ
ックの基板シートの上面に光輝性顔料または方解石の粉
末を含有するインキで印刷した反射層を有する反射シー
ト、および光輝性顔料または方解石の粉末を含有する半
透明で柔軟なプラスチックの光拡散層をこの順に積層
し、表面にエンボスを施したもの（実願平３−２４６２
号）。A light-absorbing layer made of a dark plastic sheet is provided on one surface of a flexible base cloth or a rigid substrate, and a bright, opaque and flexible plastic substrate sheet is provided on the other surface. Sheet with a reflective layer printed with an ink containing a pigment or calcite powder, and a light-transmissive layer of a translucent and flexible plastic containing a glitter pigment or calcite powder in this order, embossed on the surface (Application 3-2462)
issue).
【００１２】可撓性を有する基布または剛性を有する基
板の一方の面に白色不透明で柔軟なプラスチックの基材
シートに暗色インキのベタ印刷を行なって光吸収層とし
たものを設け、他方の面に光輝性顔料または方解石の粉
末を練り込んだ光拡散層となる半透明で柔軟なプラスチ
ックシートの下面に光輝性顔料または方解石の粉末を含
有するインキで印刷した反射層を有するシートをこの順
に積層し、表面にエンボスを施したもの（実願平３−２
４６２号）。On one surface of a flexible base cloth or a rigid substrate, a white, opaque and flexible plastic base sheet is solid-printed with dark ink to form a light absorbing layer, and the other is provided. A sheet having a reflective layer printed with an ink containing a glitter pigment or calcite powder on the lower surface of a translucent and flexible plastic sheet that becomes a light diffusion layer kneaded with glitter pigment or calcite powder on the surface in this order Laminated and embossed on the surface (Jpn.
462).
【００１３】両面が暗色の基材の上に、鱗片状の光輝性
顔料を練り込んだ半透明なプラスチックシート製の光拡
散層を設け、必要により表面にエンボスを施したもの
（特願平４−９６３７６号）。A light-diffusing layer made of a translucent plastic sheet into which scaly glittering pigments are kneaded is provided on a base material having a dark color on both sides, and the surface is embossed as required (Japanese Patent Application No. Hei 4 (1994) -1992). -96376).
【００１４】表面に施すエンボスは、凹凸パターンが周
期性を有しないものであるか、または周期性を有すると
きも、凹凸パターンの周期の方向が投影画素の周期の方
向に対して１５〜７５°の傾きをもっているものが好ま
しい。The embossing applied to the surface is such that the uneven pattern does not have periodicity, or even when it has periodicity, the direction of the period of the uneven pattern is 15 to 75 ° with respect to the direction of the period of the projection pixel. Is preferred.
【００１５】光拡散層の表面の周囲に、暗色のインキで
外枠を印刷してもよい。The outer frame may be printed around the surface of the light diffusion layer with dark ink.
【００１６】[0016]
【作用】本発明の反射型映写スクリーンは、その背後に
あるスピーカーからの音を通過させるための小孔を、投
影される画素の周期と同調しないように設けたので、モ
アレ縞の発生がなく、鮮明な画像を確保した上に高い音
響効果を享受できる。In the reflection type projection screen of the present invention, the small holes for passing the sound from the speaker behind it are provided so as not to be synchronized with the period of the projected pixels, so that moire fringes do not occur. In addition, a clear image can be secured and a high sound effect can be enjoyed.
【００１７】[0017]
【実施例】［参考例］ 厚さ０．１３mmの白色塩ビ樹脂カレンダーシート（ＤＯ
Ｐ：６０phr)を基材シートとし、その上に下記組成の光
輝性インキを、 ビヒクル（ＰＶＣ） １００重量部 顔料（チタンコーテッド雲母） ２０重量部 乾燥時の厚さが３μｍとなるようにグラビア印刷して反
射シートを得た。EXAMPLES Reference Example 0.13 mm thick white PVC resin calender sheet (DO
P: 60 phr) as a base sheet, and a glitter ink having the following composition on the base sheet: 100 parts by weight of vehicle (PVC) 20 parts by weight of pigment (titanium-coated mica) 20 parts by weight Gravure printing so that the thickness when dried becomes 3 μm Thus, a reflection sheet was obtained.
【００１８】ガラス繊維の織布を可撓性を有する基布と
して用い、その一方の面に厚さ０．２８mmの黒色塩ビ樹
脂シート（ＤＯＰ：６０phr)の光吸収層を重ね、他方の
面に、上記の反射シート、パール顔料（チタンコーテッ
ド雲母）約２重量％を混練し押出し成形した厚さ０．１
５mmの半透明な塩ビ樹脂シート（ＤＯＰ：６０phr)、お
よび砂目調のエンボス版を順に重ね、熱圧ダブリングに
より一体化するとともにエンボス加工した。A glass fiber woven fabric is used as a flexible base fabric, and a light-absorbing layer of a 0.28-mm-thick black PVC resin sheet (DOP: 60 phr) is laminated on one surface, and on the other surface. The above reflection sheet, about 2% by weight of pearl pigment (titanium coated mica) were kneaded and extruded to a thickness of 0.1.
A 5 mm translucent polyvinyl chloride resin sheet (DOP: 60 phr) and a grained embossing plate were sequentially stacked, integrated by hot-press doubling, and embossed.
【００１９】この積層体をプレス加工で打ち抜き、直径
が０．５mmの円形の断面をもった小孔を開口比５％で全
面にランダムに配置するように設けて、映写スクリーン
を得た。This laminate was punched out by press working, and small holes having a circular cross section with a diameter of 0.5 mm were provided so as to be randomly arranged over the entire surface at an aperture ratio of 5% to obtain a projection screen.
【００２０】［実施例１］ 積層後は基材となる裏打ちシートとして、カーボンブラ
ック顔料を練り込んだ厚さ２００μｍの黒色塩ビ樹脂シ
ート（ＤＯＰ：６０phr)を用意し、あわせてガラス繊維
織布の基布、および中間シートとしてカーボンブラック
顔料を練り込んだ厚さ１３０μｍの黒色塩ビ樹脂カレン
ダーシート（ＤＯＰ：６０phr）を用意した。Example 1 A 200 μm-thick black vinyl chloride resin sheet (DOP: 60 phr) into which carbon black pigment was kneaded was prepared as a backing sheet serving as a substrate after lamination. A 130 μm-thick black PVC resin calendar sheet (DOP: 60 phr) into which a carbon black pigment was kneaded was prepared as a base cloth and an intermediate sheet.
【００２１】上記の裏打ちシート上に基布および中間シ
ートを順に重ね、さらにその上に、光拡散層としてパー
ル顔料（平均粒径１７μｍの鱗片状チタンコーテッド雲
母）約２重量％を混練して押出し成形した、厚さ１２０
μｍの半透明な塩ビ樹脂シート（ＤＯＰ：６０phr)、お
よび砂目調の艶消しエンボス版を順に重ね、熱プレスに
より積層一体化するとともにエンボス加工した。A base cloth and an intermediate sheet are sequentially stacked on the backing sheet, and about 2% by weight of a pearl pigment (flaky titanium-coated mica having an average particle size of 17 μm) is kneaded and extruded thereon as a light diffusion layer. Molded, thickness 120
A translucent polyvinyl chloride resin sheet (DOP: 60 phr) having a thickness of μm and a matte embossing plate having a grain-grained pattern were sequentially stacked, laminated and integrated by a hot press, and embossed.
【００２２】この積層体をプレス加工で打ち抜き、スク
リーンの右端および左端からそれぞれ４０cmまでの部分
に、直径０．８mmの円形断面の小孔を、開口比３％とな
るように設けた。 小孔の配置は、その周期の方向が投
影画素の周期の方向に対して４５°の傾きをもつように
した。This laminate was punched out by press working, and small holes having a circular cross section with a diameter of 0.8 mm were provided in portions of the screen up to 40 cm from the right and left ends, respectively, so as to have an opening ratio of 3%. The arrangement of the small holes was such that the direction of the period had an inclination of 45 ° with respect to the direction of the period of the projection pixels.
【００２３】得られたスクリーン表面に黒色インキをシ
ルクスクリーン印刷して幅３cmの黒い外枠を設け、対角
線の長さが１００インチの長方形状に囲われた、本発明
の反射型映写スクリーンを製造した。The reflection type projection screen of the present invention, in which a black outer frame having a width of 3 cm was provided by silk-screen printing of black ink on the obtained screen surface and surrounded by a rectangle having a diagonal length of 100 inches. did.
【００２４】[0024]
【発明の効果】本発明の映写スクリーンは、周期性をも
って繰り返される画素の集まりである画像を投影したと
きも、モアレ縞などに悩まされることなく、常に鮮明な
画像を見ることのできるスクリーンである。 もちろ
ん、本発明の映写スクリーンは、スクリーンの後の適切
な位置に置いたスピーカーの音を、スクリーンの前にい
る観者によく聞かせて臨場感を高めることができる。
従ってこの映写スクリーンは、液晶プロジェクターをは
じめとする各種の映写手段と、ステレオなどの音響装置
を組み合わせて使用する場合に好適である。The projection screen of the present invention is a screen that can always display a clear image without being bothered by moire fringes, even when projecting an image which is a group of pixels repeated periodically. . Of course, the projection screen of the present invention can make the sound of the speaker placed at an appropriate position after the screen well heard by a viewer in front of the screen to enhance the sense of reality.
Therefore, this projection screen is suitable when various projection means such as a liquid crystal projector are used in combination with an audio device such as a stereo.
【図１】 本発明の反射型映写スクリーンの全体の構成
を示す平面図であって、破線の円内の一部を拡大したも
のが図２および図３。FIG. 1 is a plan view showing the entire configuration of a reflection type projection screen according to the present invention, and FIGS.
【図２】 本発明の反射型映写スクリーンにおける、小
孔と投影された画素とのひとつの位置関係を示す、図１
の一部の拡大図。FIG. 2 shows one positional relationship between a small hole and a projected pixel in the reflection type projection screen of the present invention.
FIG.
【図３】 本発明の反射型映写スクリーンにおける、小
孔と投影された画素との別の位置関係を示す、図１の一
部の拡大図。FIG. 3 is an enlarged view of a part of FIG. 1 showing another positional relationship between a small hole and a projected pixel in the reflection type projection screen of the present invention.
１ 反射型映写スクリーン ２ 小孔 ３ 投影された画素 1 reflection type projection screen 2 small hole 3 projected pixel
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) G03B 21/56 G03B 21/60 ──────────────────────────────────────────────────続 き Continued on the front page (58) Field surveyed (Int.Cl. 7 , DB name) G03B 21/56 G03B 21/60
Claims (7)
からの音が通過できるように、少なくともスピーカーの
位置に多数の小孔を設けた反射型映写スクリーンにおい
て、 小孔の配置が周期性を有していて、その周期が、 １）小孔の配置の周期の方向がスクリーンに投影される
画素の周期の方向に対して１５〜７５°の傾きをもって
いるか、または２）小孔の水平方向ピッチをＴｘ、垂直
方向のピッチをＴｙとし、投影される画素の水平方向の
ピッチをｔｘ、垂直方向のピッチをｔｙとするとき、 Ｔｘ／ｔｘ＝ｒ１， Ｔｙ／ｔｙ＝ｒ２ のｒ１およびｒ２が、ともに非整数であることを特徴と
する反射型映写スクリーン。1. A reflection type projection screen having a large number of small holes at least at the position of a speaker so that sound from a speaker arranged behind the screen can pass therethrough. The period is 1) the direction of the period of the arrangement of the small holes is inclined by 15 to 75 ° with respect to the direction of the period of the pixels projected on the screen, or 2) the horizontal pitch of the small holes is Tx. , and the pitch of the vertical direction and Ty, tx the horizontal pitch of the pixels to be projected, when the pitch of the vertical direction and ty, Tx / tx = r 1 , Ty / ty = r 1 and r 2 of the r 2 Wherein both are non-integers.
ｒ1およびｒ2が（Ｎ＋０．３５）〜（Ｎ＋０．４３）の
範囲（Ｎは１〜１２の整数）にある請求項１の反射型映
写スクリーン。2. In the case of claim 1 b) -2),
reflective projection screen according to claim 1 range (N is the integer of 1 to 12) in the r 1 and r 2 are (N + 0.35) ~ (N + 0.43).
または剛性を有する基板の一方の面に暗色のプラスチッ
クシートからなる光吸収層を設け、他方の面に、白色不
透明で柔軟なプラスチックの基材シートの上面に光輝性
顔料または方解石の粉末を含有するインキで印刷した反
射層を有する反射シート、および光輝性顔料または方解
石の粉末を含有する半透明で柔軟なプラスチックの光拡
散層をこの順に積層し、表面にエンボスを施したものを
使用した請求項１の反射型映写スクリーン。3. A light-absorbing layer made of a dark plastic sheet is provided on one surface of a flexible base cloth or a rigid substrate as a screen, and a white opaque flexible plastic base is provided on the other surface. A reflection sheet having a reflection layer printed with an ink containing a glitter pigment or calcite powder on the upper surface of a material sheet, and a light diffusion layer of a translucent and flexible plastic containing a glitter pigment or calcite powder in this order. 2. The reflection type projection screen according to claim 1, wherein said reflection type projection screen is laminated and embossed.
または剛性を有する基板の一方の面に、白色不透明で柔
軟なプラスチックの基材シートに暗色インキのベタ印刷
を行なって光吸収層としたものを設け、他方の面に、光
輝性顔料または方解石の粉末を練り込んだ光拡散層とな
る半透明で柔軟なプラスチックシートの下面に光輝性顔
料または方解石の粉末を含有するインキで印刷した反射
層を有するシートをこの順に積層し、表面にエンボスを
施したものを使用した請求項１の反射型映写スクリー
ン。4. A light-absorbing layer obtained by performing solid printing of a dark ink on a white opaque and flexible plastic base sheet on one surface of a flexible base cloth or a rigid substrate as a screen. Reflection printed on the lower surface of a translucent and flexible plastic sheet that becomes a light diffusion layer kneaded with brilliant pigment or calcite powder on the other surface with ink containing brilliant pigment or calcite powder 2. The reflection type projection screen according to claim 1, wherein sheets having layers are laminated in this order, and the surface is embossed.
上に、鱗片状の光輝性顔料を練り込んだ半透明なプラス
チックシート製の光拡散層を設け、必要により表面にエ
ンボスを施したものを使用した請求項１の反射型映写ス
クリーン。5. A screen in which a light-diffusing layer made of a translucent plastic sheet kneaded with scaly brilliant pigment is provided on a dark-colored base material on both sides, and the surface is embossed as required. 2. The reflection type projection screen according to claim 1, wherein
ないものであるか、または周期性を有するときも、凹凸
パターンの周期の方向が投影画素の周期の方向に対して
１５〜７５°の傾きをもっている請求項３ないし５のい
ずれかの反射型映写スクリーン。6. When the embossed concavo-convex pattern has no periodicity, or when the embossed concavo-convex pattern has a periodicity, the direction of the period of the concavo-convex pattern is inclined by 15 to 75 ° with respect to the direction of the period of the projection pixel. The reflective projection screen according to any one of claims 3 to 5, further comprising:
で外枠を印刷した請求項１ないし６のいずれかの反射型
映写スクリーン。7. The reflection type projection screen according to claim 1, wherein an outer frame is printed with a dark ink around the surface of the light diffusion layer.