JP3232381B2 - Building materials - Google Patents
Building materialsInfo
- Publication number
- JP3232381B2 JP3232381B2 JP35979092A JP35979092A JP3232381B2 JP 3232381 B2 JP3232381 B2 JP 3232381B2 JP 35979092 A JP35979092 A JP 35979092A JP 35979092 A JP35979092 A JP 35979092A JP 3232381 B2 JP3232381 B2 JP 3232381B2
- Authority
- JP
- Japan
- Prior art keywords
- polypropylene resin
- reactive
- building material
- light stabilizer
- absorber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、ポリプロピレン樹脂よ
り成る耐紫外線性の良好な建材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a building material made of polypropylene resin and having good ultraviolet resistance.
【０００２】[0002]
【従来の技術】従来より、テラスや車庫の屋根材その他
の外装用建材として、ポリ塩化ビニル樹脂板やポリカー
ボネート樹脂板等が使用されている。2. Description of the Related Art Conventionally, polyvinyl chloride resin plates, polycarbonate resin plates and the like have been used as roofing materials for terraces and garages and other exterior building materials.
【０００３】これらの樹脂板は強度や耐熱性が良好であ
るが、次のような問題があった。[0003] These resin plates have good strength and heat resistance, but have the following problems.
【０００４】[0004]
【発明が解決しようとする課題】即ち、上記の樹脂板
は、地球環境保護の観点から廃棄物として安全に焼却し
難いという問題があり、しかも耐紫外線性に劣るため、
外装用建材として使用すると短期間で劣化しやすいとい
う問題があった。That is, the above-mentioned resin plate has a problem that it is difficult to incinerate it safely as a waste from the viewpoint of protection of the global environment, and is inferior in UV resistance.
When used as an exterior building material, there is a problem that it is easily deteriorated in a short period of time.
【０００５】また、上記の樹脂板は表面滑性が乏しいた
め、例えば積雪地域の屋根材として使用すると雪下ろし
作業がし辛いという問題があり、気温が低下すると脆く
なって雪の重みや外部からの衝撃力で割れやすいという
問題があった。Further, since the above-mentioned resin plate has poor surface lubricity, there is a problem that it is difficult to remove snow when used as a roofing material in a snowy area, for example. There was a problem that it was easily broken by an impact force.
【０００６】[0006]
【課題を解決するための手段】上記の問題を解決するた
め、第一の発明はポリプロピレン樹脂より成る建材であ
って、そのポリプロピレン樹脂中に、ラジカル反応開始
剤として、過酸化ベンゾイル、ｔ−ブチルヒドロパーオ
キサイド、オクタノイルパーオキサイドのいずれかが含
有され、不飽和結合を有する反応型紫外線吸収剤及び反
応型光安定剤のいずれか一方又は双方が、上記のラジカ
ル反応開始剤によってポリプロピレン樹脂のポリマー分
子の側鎖として化学結合していることを要旨とするもの
である。そして、第二の発明はポリプロピレン樹脂より
成る建材であって、その表層部分のポリプロピレン樹脂
中に、ラジカル反応開始剤として、過酸化ベンゾイル、
ｔ−ブチルヒドロパーオキサイド、オクタノイルパーオ
キサイドのいずれかが含有され、不飽和結合を有する反
応型紫外線吸収剤及び反応型光安定剤のいずれか一方又
は双方が、上記のラジカル反応開始剤によって表層部分
のポリプロピレン樹脂のポリマー分子の側鎖として化学
結合していることを要旨とするものである。Means for Solving the Problems In order to solve the above problems, a first invention is a building material made of a polypropylene resin, wherein the polypropylene resin contains benzoyl peroxide and t-butyl as a radical reaction initiator. Any one or both of a reactive ultraviolet absorber and a reactive light stabilizer having an unsaturated bond, which contains any of hydroperoxide and octanoyl peroxide, is a polymer of a polypropylene resin by the above radical reaction initiator. The gist is that they are chemically bonded as side chains of the molecule. The second invention is a building material made of a polypropylene resin, wherein benzoyl peroxide, as a radical reaction initiator,
Any one or both of a reactive ultraviolet absorber and a reactive light stabilizer having an unsaturated bond, which contains any of t-butyl hydroperoxide and octanoyl peroxide, is surfaced by the above radical reaction initiator. The gist is that a part of the polypropylene resin is chemically bonded as a side chain of the polymer molecule.
【０００７】[0007]
【作用】第一発明及び第二発明の建材はいずれも、ポリ
プロピレン樹脂中に含まれる反応型紫外線吸収剤によっ
て紫外線が吸収され、また、反応型光安定剤によって劣
化時に発生するラジカルが捕捉されるので、耐紫外線性
が良好である。従って、外装用建材として使用しても、
紫外線による強度劣化や黄変化を生じることは殆どな
い。しかも、この建材に含まれる紫外線吸収剤や光安定
剤は、従来から汎用されている非反応型のものではな
く、反応型の紫外線吸収剤と光安定剤であり、ポリプロ
ピレン樹脂のポリマー分子との反応により化学結合して
固定化されているため、非反応型の紫外線吸収剤や光安
定剤のように経時的に揮散することがなく、長期に亘っ
てその効果を持続することができる。特に、第二発明の
建材のように、少なくとも表層部分のポリプロピレン樹
脂中に反応型紫外線吸収剤や反応型光安定剤が含有され
て化学結合していると、建材全体に含有させる場合に比
べて、反応型紫外線吸収剤や反応型光安定剤の含有量を
節約することができる。The building materials of the first and second inventions both absorb ultraviolet rays by the reactive ultraviolet absorber contained in the polypropylene resin, and capture the radicals generated during the degradation by the reactive light stabilizer. Therefore, the UV resistance is good. Therefore, even when used as exterior building materials,
There is almost no intensity deterioration or yellowing caused by ultraviolet rays. Moreover, the UV absorbers and light stabilizers contained in this building material are not reactive non-reactive ones, but are reactive UV absorbers and light stabilizers. Since it is chemically bonded and immobilized by the reaction, it does not volatilize over time unlike a non-reactive ultraviolet absorber or light stabilizer, and its effect can be maintained for a long time. In particular, as in the building material of the second invention, when a reactive UV absorber or a reactive light stabilizer is contained and chemically bonded in at least the surface layer of the polypropylene resin, compared with the case where the entire building material is contained. In addition, the content of the reactive ultraviolet absorber and the reactive light stabilizer can be saved.
【０００８】また、これらの建材はポリプロピレン樹脂
より成るものであるから、廃棄物として焼却するとき有
害物質を発生せず、安全に焼却することができる。しか
も、このポリプロピレン樹脂は表面滑性が大きく、低温
でも脆弱化しにくい樹脂であるから、これらの建材を例
えば積雪地域の屋根材等として使用すると、雪下ろし作
業がしやすくなり、雪の重みや外部からの衝撃力で簡単
に割れる心配もない。Further, since these building materials are made of polypropylene resin, they can be safely incinerated without generating harmful substances when incinerated as waste. Moreover, since this polypropylene resin has a high surface lubricity and is not easily fragile even at low temperatures, if these building materials are used, for example, as roofing materials in snowy areas, it will be easier to remove snow, and the weight of the snow and external There is no need to worry about cracking easily with the impact force.
【０００９】[0009]
【実施例】以下、図面を参照して本発明の実施例を説明
する。Embodiments of the present invention will be described below with reference to the drawings.
【００１０】図１は第一発明の一実施例の断面図で、ポ
リプロピレン樹脂を平板状に溶融押出成形した建材１を
示している。建材１の形状は、実施例のような平板状の
他、波板状、シート状、柱状、異形状など、使用箇所に
応じた種々の形状とすることができ、例えば波板状の建
材とする場合は、平板状に押出成形したものを波付けロ
ールで波状に賦形すればよい。FIG. 1 is a sectional view of an embodiment of the first invention, and shows a building material 1 obtained by melt-extruding a polypropylene resin into a flat plate shape. The shape of the building material 1 can be various shapes depending on the place of use, such as a corrugated plate, a sheet, a column, and an irregular shape, in addition to the flat plate shape as in the embodiment. In this case, what is extruded into a flat plate may be shaped into a wave by a corrugating roll.
【００１１】この建材１のポリプロピレン樹脂中には、
紫外線吸収剤及び光安定剤のいずれか一方又は双方を含
有させてある。従って、この建材１に太陽光が当たって
も、紫外線吸収剤によって紫外線が吸収され、また、光
安定剤によって劣化時に発生するラジカルが捕捉される
ので、紫外線による強度劣化や黄変化を生じることは少
ない。[0011] In the polypropylene resin of the building material 1,
One or both of an ultraviolet absorber and a light stabilizer are contained. Therefore, even if the building material 1 is exposed to sunlight, ultraviolet rays are absorbed by the ultraviolet absorber, and radicals generated at the time of deterioration are captured by the light stabilizer. Few.
【００１２】ポリプロピレン樹脂に含有させる紫外線吸
収剤や光安定剤は非反応型のものでも反応型のものでも
よい。非反応型紫外線吸収剤としては、例えば２−
（２′−ヒドロキシ−３′−ｔ−ブチル−５′−メチル
フェニル−５−クロロベンゾトリアゾール、メチル−３
−［３−ｔ−ブチル−５−（２−ベンゾトリアゾール−
２−イル）−４−ヒドロキシフェニル］プロピオネート
−ポリエチレングリコール、２−（２′−ヒドロキシ−
３′，５′−ジ−ｔ−ブチルフェニル）−５−クロロベ
ンゾトリアゾール、２−ヒドロキシ−４−ｎ−オクトキ
シベンゾフェノン等が使用され、反応型紫外線吸収剤と
しては、分子中に不飽和結合を一つ以上有するベンゾフ
ェノン系又はベンゾトリアゾール系の紫外線吸収剤、例
えば２−ヒドロキシ−４−（２′−メタクリロイルオキ
シエトキシ）ベンゾフェノン、２−ヒドロキシ−４−
（２′−アクリロイルオキシエトキシ）ベンゾフェノ
ン、２−（２′−ヒドロキシ−３′−アリル−５′−ｔ
−ブチルフェニル）ベンゾトリアゾール、２−（２′−
ヒドロキシ−３′−アリル−５′−ｔ−オクチルフェニ
ル）ベンゾトリアゾール、２−（２′−ヒドロキシ−
３′−イソプロペニル−５′−ｔ−ブチルフェニル）ベ
ンゾトリアゾール、２−（２′−ヒドロキシ−３′−イ
ソプロペニル−５′−ｔ−オクチルフェニル）ベンゾト
リアゾール、２−（２′−アクリロイルオキシ−５′−
メチル）ベンゾトリアゾール等が使用される。The ultraviolet absorber and light stabilizer contained in the polypropylene resin may be of a non-reactive type or a reactive type. As the non-reactive ultraviolet absorber, for example, 2-
(2'-hydroxy-3'-t-butyl-5'-methylphenyl-5-chlorobenzotriazole, methyl-3
-[3-t-butyl-5- (2-benzotriazole-
2-yl) -4-hydroxyphenyl] propionate-polyethylene glycol, 2- (2'-hydroxy-
3 ', 5'-di-t-butylphenyl) -5-chlorobenzotriazole, 2-hydroxy-4-n-octoxybenzophenone and the like are used. As a reactive ultraviolet absorber, an unsaturated bond in the molecule is used. Benzophenone-based or benzotriazole-based ultraviolet absorbers having one or more of, for example, 2-hydroxy-4- (2'-methacryloyloxyethoxy) benzophenone, 2-hydroxy-4-
(2'-acryloyloxyethoxy) benzophenone, 2- (2'-hydroxy-3'-allyl-5'-t
-Butylphenyl) benzotriazole, 2- (2'-
Hydroxy-3'-allyl-5'-t-octylphenyl) benzotriazole, 2- (2'-hydroxy-
3'-isopropenyl-5'-t-butylphenyl) benzotriazole, 2- (2'-hydroxy-3'-isopropenyl-5'-t-octylphenyl) benzotriazole, 2- (2'-acryloyloxy -5'-
Methyl) benzotriazole and the like are used.
【００１３】また、非反応型光安定剤としては、例えば
４−４′−チオビス−（２−メチル−６−ｔ−ブチルフ
ェノール）、テトラキス（１，２，２，６，６−ペンタ
メチル−４−ピペリジル）１，２，３，４ブタンテトラ
カルボキシラート、１，３，５−トリメチル−２，４，
６−トリス（３，５−ジ−ｔ−ブチル−４−ヒドロキシ
ベンジル）ベンゼン等が使用され、反応型光安定剤とし
ては、例えば１，２，２，６，６−ペンタメチル−４−
ピペリジルメタクリレート、１，２，２，６，６−ペン
タメチル−４−ピペリジルアクリレート、２，２，６，
６−テトラメチル−４−ピペリジルメタクリレート、
２，２，６，６−テトラメチル−４−ピペリジルアクリ
レート等が使用される。Examples of non-reactive light stabilizers include, for example, 4-4'-thiobis- (2-methyl-6-t-butylphenol) and tetrakis (1,2,2,6,6-pentamethyl-4-). Piperidyl) 1,2,3,4 butanetetracarboxylate, 1,3,5-trimethyl-2,4
6-tris (3,5-di-t-butyl-4-hydroxybenzyl) benzene and the like are used, and as a reactive light stabilizer, for example, 1,2,2,6,6-pentamethyl-4-
Piperidyl methacrylate, 1,2,2,6,6-pentamethyl-4-piperidyl acrylate, 2,2,6
6-tetramethyl-4-piperidyl methacrylate,
2,2,6,6-tetramethyl-4-piperidyl acrylate and the like are used.
【００１４】非反応型の紫外線吸収剤や光安定剤を含ん
だポリプロピレン樹脂より成る建材１を製造する場合
は、例えばポリプロピレン樹脂のペレットに紫外線吸収
剤や光安定剤をドライブレンドしたものを押出成形機に
投入し、成形機内部でポリプロピレン樹脂の融点以上
（但し熱分解温度以下）に加熱しながら溶融混練して、
成形機先端の押出口から板状に押出成形すればよい。こ
のようにして得られる建材１は、そのポリプロピレン樹
脂中に紫外線吸収剤や光安定剤が均一に分散した状態で
含有されており、紫外線吸収剤等がポリプロピレン樹脂
のポリマー分子と反応していない。この紫外線吸収剤や
光安定剤は揮散しやすいため、多量に含有させると該紫
外線吸収剤等が建材１の表面に移行、析出して外観が低
下する恐れがある。かといって含有量をあまり少なくす
ると、耐紫外線性を十分向上させることが困難となる。
従って、紫外線吸収剤や光安定剤の含有量は、ポリプロ
ピレン樹脂に対してそれぞれ単独で又は合計して０．０
１〜５重量％、好ましくは０．０５〜３重量％程度とす
るのがよい。In the case of manufacturing a building material 1 made of a polypropylene resin containing a non-reactive UV absorber or a light stabilizer, for example, a pellet obtained by dry blending a UV absorber or a light stabilizer with polypropylene resin pellets is extrusion-molded. Into the molding machine and melt-knead while heating to above the melting point of the polypropylene resin (but below the thermal decomposition temperature) inside the molding machine,
What is necessary is just to extrusion-mold into a plate shape from the extrusion port at the tip of a molding machine. The building material 1 thus obtained contains the UV absorber and the light stabilizer in the polypropylene resin in a state of being uniformly dispersed, and the UV absorber and the like do not react with the polymer molecules of the polypropylene resin. Since the ultraviolet absorber and the light stabilizer are easy to volatilize, if the ultraviolet absorber and the like are contained in a large amount, the ultraviolet absorber and the like may migrate and precipitate on the surface of the building material 1 to deteriorate the appearance. On the other hand, if the content is too small, it becomes difficult to sufficiently improve the ultraviolet resistance.
Accordingly, the content of the ultraviolet absorber and the light stabilizer is 0.04
It is good to be about 1 to 5% by weight, preferably about 0.05 to 3% by weight.
【００１５】更に、耐紫外線性を持続させる方法とし
て、反応型の紫外線吸収剤や光安定剤を含んだポリプロ
ピレン樹脂より成る建材１を製造する場合は、ポリプロ
ピレン樹脂のペレットに反応型の紫外線吸収剤や光安定
剤とラジカル反応開始剤とをドライブレンドし、これを
押出成形機に投入して成形機内部でポリプロピレン樹脂
の融点以上（但し熱分解温度以下）に加熱しながら溶融
混練し、成形機先端の押出口から板状に押出成形すれば
よい。このようにすると、成形機内部での溶融混練時に
反応型の紫外線吸収剤や光安定剤がポリプロピレン樹脂
のポリマー分子とラジカル反応し、該紫外線吸収剤等が
側鎖としてポリマー分子に結合して固定化されるので、
紫外線吸収剤等が揮散することなく長期に亘って効果を
発揮できる。従って、この場合は反応型の紫外線吸収剤
や光安定剤の含有量をポリプロピレン樹脂に対してそれ
ぞれ単独で又は合計して０．０１〜１０重量％、好まし
くは０．０５〜５重量％程度とするのがよい。このよう
に、反応型の紫外線吸収剤や光安定剤を含んだ建材１
は、該紫外線吸収剤等の含有量が同じでも、析出や揮散
による含有量の減少がないため、長期間に亘って優れた
耐紫外線性を発揮することができる。尚、ラジカル反応
開始剤としては過酸化ベンゾイル、アゾ−ｂｉｓ−イソ
ブチロニトリル、ｔ−ブチルヒドロパーオキサイド、
２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキ
シ）ヘキサン、オクタノイルパーオキサイド等が使用さ
れる。Further, as a method of maintaining the UV resistance, when manufacturing a building material 1 made of a polypropylene resin containing a reactive UV absorber or a light stabilizer, the reactive UV absorber is added to the polypropylene resin pellets. And a light stabilizer and a radical reaction initiator are dry-blended, and the mixture is put into an extruder and melt-kneaded in the molding machine while being heated to a temperature higher than the melting point of the polypropylene resin (but lower than the thermal decomposition temperature). What is necessary is just to extrusion-mold in plate shape from the extrusion port of the front end. In this way, the reactive UV absorber or light stabilizer reacts radically with the polymer molecules of the polypropylene resin during melt-kneading inside the molding machine, and the UV absorbers and the like are bonded to the polymer molecules as side chains and fixed. So that
The effect can be exhibited for a long period of time without volatilization of the ultraviolet absorber or the like. Therefore, in this case, the content of the reactive ultraviolet absorber or light stabilizer is about 0.01 to 10% by weight, preferably about 0.05 to 5% by weight, respectively, alone or in total with respect to the polypropylene resin. Good to do. Thus, the building material 1 containing the reactive UV absorber and the light stabilizer
Can exhibit excellent ultraviolet resistance over a long period of time because the content thereof does not decrease due to precipitation or volatilization even if the content of the ultraviolet absorber or the like is the same. In addition, as a radical reaction initiator, benzoyl peroxide, azo-bis-isobutyronitrile, t-butyl hydroperoxide,
2,5-dimethyl-2,5-di (t-butylperoxy) hexane, octanoyl peroxide and the like are used.
【００１６】上記の製造法はいずれも、非反応型又は反
応型の紫外線吸収剤や光安定剤を含んだポリプロピレン
樹脂を単層で押出成形しているが、例えば共押出成形機
を用いて、反応型の紫外線吸収剤や光安定剤を含んだポ
リプロピレン樹脂を上層とし、この上層よりも紫外線吸
収剤等が少ないか又は全く含まないポリプロピレン樹脂
を中間層又は下層として共押出成形すれば、少なくとも
表層部分に反応型の紫外線吸収剤や光安定剤が含有され
てポリプロピレン樹脂のポリマーと化学結合した二層な
いし三層構造の第二発明の建材が得られる。In each of the above production methods, a single layer of a polypropylene resin containing a non-reactive or reactive ultraviolet absorber or a light stabilizer is extruded. For example, using a co-extrusion molding machine, If a polypropylene resin containing a reactive UV absorber or a light stabilizer is used as the upper layer, and the polypropylene resin containing less or no UV absorber than the upper layer is co-extruded as an intermediate layer or a lower layer, at least the surface layer A building material of the second invention having a two-layer or three-layer structure in which a reactive ultraviolet absorber or a light stabilizer is contained in a portion and chemically bonded to a polypropylene resin polymer is obtained.
【００１７】図２は他の実施例を示す断面図で、前述の
ごとき紫外線吸収剤及び光安定剤のいずれか一方又は双
方を含有したポリプロピレン樹脂から成る建材１の内部
に補強繊維２を埋入したものである。補強繊維２として
は、ガラス繊維、炭素繊維、有機繊維等のネット、マッ
トあるいは短繊維等が好適に使用される。このように補
強繊維２を埋入すると、建材１の合成や耐衝撃強度が向
上するため割れにくくなり、成形時や賦形時の保形性も
向上する。FIG. 2 is a sectional view showing another embodiment, in which a reinforcing fiber 2 is embedded in a building material 1 made of a polypropylene resin containing one or both of an ultraviolet absorber and a light stabilizer as described above. It was done. As the reinforcing fibers 2, nets such as glass fibers, carbon fibers, and organic fibers, mats, short fibers, and the like are preferably used. When the reinforcing fiber 2 is embedded in this way, the composition and impact resistance of the building material 1 are improved, so that the material is less likely to break, and the shape retention during molding and shaping is also improved.
【００１８】このような補強繊維入りの建材１を製造す
る場合は、例えば図３に示すように補強繊維２を供給ロ
ール３から連続供給すると共に、両側の押出成形機４，
４から紫外線吸収剤や光安定剤を含むポリプロピレン樹
脂１ａ，１ａを連続して押出し、これを一対のロール
５，５で両側から挟圧して融着一体化すればよい。In the case of manufacturing such a building material 1 containing reinforcing fibers, for example, as shown in FIG. 3, reinforcing fibers 2 are continuously supplied from a supply roll 3 and extruders 4 on both sides.
4, the polypropylene resin 1 a containing an ultraviolet absorber or a light stabilizer is continuously extruded, and this is pressed and fused by a pair of rolls 5 and 5 from both sides.
【００１９】この実施例では、ポリプロピレン樹脂より
成る建材１の厚み方向中間部に補強繊維２を単層状に埋
入しているが、補強繊維２を多層状に埋入させてもよ
い。また、補強繊維２としてガラス短繊維等を使用し、
建材１の内部全体に均一に埋入させてもよい。In this embodiment, the reinforcing fibers 2 are embedded in a single layer in the middle of the building material 1 made of polypropylene resin in the thickness direction. However, the reinforcing fibers 2 may be embedded in a multilayer. Also, using short glass fiber or the like as the reinforcing fiber 2,
It may be uniformly embedded in the entire inside of the building material 1.
【００２０】次に、具体的な実施例と比較例を説明す
る。 （実施例１）Next, specific examples and comparative examples will be described. (Example 1)
【００２１】ポリプロピレン樹脂１００重量部に対し、
非反応型紫外線吸収剤として１−ヒドロキシ−４−ｎ−
オクトキシベンゾフェノンを１．５重量部加えてドライ
ブレンドし、これを押出成形機に投入して２３０℃で溶
融混練し、成形機先端の押出口から押出して薄板状の建
材を製造した。そして、この建材を切断して試験片（５
０×１００×１ｍｍ）を作成した。For 100 parts by weight of the polypropylene resin,
1-hydroxy-4-n- as a non-reactive UV absorber
1.5 parts by weight of octoxybenzophenone was added and dry-blended, put into an extruder, melt-kneaded at 230 ° C., and extruded from an extrusion port at the tip of the extruder to produce a thin plate-like building material. Then, this building material was cut and a test piece (5
0 × 100 × 1 mm).
【００２２】この試験片について促進耐候性試験を行
い、照射時間と黄変度（ΔＹＩ）、紫外線吸収剤の残存
率との関係を調べた。その結果を表１に示す。The test pieces were subjected to an accelerated weather resistance test to examine the relationship between the irradiation time, the degree of yellowing (ΔYI), and the residual ratio of the ultraviolet absorbent. Table 1 shows the results.
【００２３】尚、促進耐候試験はキセノンウェザオメー
ター（アトラス社製）を用いて１００ｈｒ，５００ｈ
ｒ，１０００ｈｒ照射による促進試験を行い、ΔＹＩは
Σ９０カラーメジャーリングシステム（日本電色株式会
社製）により測定して求めたものである。また、残存率
は、可視紫外分光光度計ＵＶ−３１００（株式会社島津
製作所製）を用いて、それぞれの照射時間における試験
片の紫外線吸光度を測定し、それぞれの紫外線吸収剤の
最大吸収波長の吸光度変化を、照射時間０ｈｒのときの
残存率を１００として計算した値である。 （実施例２）The accelerated weathering test was performed for 100 hours and 500 hours using a xenon weatherometer (manufactured by Atlas).
An acceleration test was performed by irradiation at r and 1000 hours, and ΔYI was determined by measuring with a # 90 color measuring system (manufactured by Nippon Denshoku Co., Ltd.). The residual ratio was determined by measuring the ultraviolet absorbance of the test piece at each irradiation time using a visible ultraviolet spectrophotometer UV-3100 (manufactured by Shimadzu Corporation), and measuring the absorbance at the maximum absorption wavelength of each ultraviolet absorber. The change is a value calculated by assuming that the residual rate when the irradiation time is 0 hr is 100. (Example 2)
【００２４】ポリプロピレン樹脂１００重量部に対し、
非反応型光安定剤として４−４′−チオビス−（２−メ
チル−６−ｔ−ブチルフェノールを１．０重量部加えて
ドライブレンドし、これを押出成形機に投入して実施例
１と同様に薄板状の建材を製造し、試験片（５０×１０
０×１ｍｍ）を作成した。この試験片について実施例１
と同様に促進耐候性試験を行い、照射時間と黄変度（Δ
ＹＩ）との関係を調べた結果を表１に示す。 （実施例３）For 100 parts by weight of the polypropylene resin,
1.0 part by weight of 4-4'-thiobis- (2-methyl-6-t-butylphenol) was added as a non-reactive light stabilizer and dry-blended. A thin plate-like building material is manufactured on a test piece (50 × 10
0 × 1 mm). Example 1 of this test piece
The accelerated weathering test was performed in the same manner as in
Table 1 shows the results of examining the relationship with YI). (Example 3)
【００２５】ポリプロピレン樹脂１００重量部に対し、
非反応型紫外線吸収剤として２−（２′−ヒドロキシ−
３，５′−ジ−ｔ−ブチルフェニル）−５−クロロベン
ゾトリアゾールを１．５重量部と、非反応型光安定剤と
して４−４′−チオビス−（２−メチル−６−ｔ−ブチ
ルフェノール）を１．０重量部加えてドライブレンド
し、これを押出成形機に投入して実施例１と同様に薄板
状の建材を製造し、試験片（５０×１００×１ｍｍ）を
作成した。この試験片について実施例１と同様に促進耐
候性試験を行い、照射時間と黄変度（ΔＹＩ）、紫外線
吸収剤の残存率との関係を調べた結果を表１に示す。 （実施例４）For 100 parts by weight of the polypropylene resin,
2- (2'-hydroxy-) as a non-reactive UV absorber
1.5 parts by weight of 3,5'-di-t-butylphenyl) -5-chlorobenzotriazole and 4-4'-thiobis- (2-methyl-6-t-butylphenol as a non-reactive light stabilizer ) Was added to 1.0 part by weight and dry-blended, and the mixture was put into an extruder to produce a thin plate-like building material in the same manner as in Example 1 to prepare a test piece (50 × 100 × 1 mm). Table 1 shows the results of an accelerated weathering test conducted on this test piece in the same manner as in Example 1 to examine the relationship between the irradiation time, the degree of yellowing (ΔYI), and the residual ratio of the ultraviolet absorbent. (Example 4)
【００２６】ポリプロピレン樹脂１００重量部に対し、
反応型紫外線吸収剤として２−ヒドロキシ−４−（２′
−メタクリロイルオキシエトキシ）ベンゾフェノンを
１．５重量部と、ラジカル反応開始剤として過酸化ブン
ゾイルを１．０重量部加えてドライブレンドした。この
ブレンド物を押出成形機に投入し、２３０℃に加熱して
溶融混練しながら５分間反応させ、成形機先端の押出口
から押出して薄板状の建材を製造した。そして、この建
材を切断して試験片（５０×１００×１ｍｍ）を作成し
た。この試験片について実施例１と同様に促進耐候性試
験を行い、照射時間と黄変度（ΔＹＩ）、紫外線吸収剤
の残存率との関係を調べた結果を表１に示す。 （実施例５）For 100 parts by weight of the polypropylene resin,
2-hydroxy-4- (2 'as a reactive UV absorber
-(Methacryloyloxyethoxy) benzophenone (1.5 parts by weight) and bunzoyl peroxide (1.0 part by weight) as a radical reaction initiator were added and dry blended. This blend was put into an extruder, heated to 230 ° C., melt-kneaded and reacted for 5 minutes, and extruded from an extruding port at the tip of the extruder to produce a thin plate-like building material. Then, this building material was cut to prepare a test piece (50 × 100 × 1 mm). Table 1 shows the results of an accelerated weathering test conducted on this test piece in the same manner as in Example 1 to examine the relationship between the irradiation time, the degree of yellowing (ΔYI), and the residual ratio of the ultraviolet absorbent. (Example 5)
【００２７】ポリプロピレン樹脂１００重量部に対し、
反応型光安定剤として１，２，２，６，６−ペンタメチ
ル−４−ピペリジルメタクリレートを２．０重量部と、
ラジカル反応開始剤として過酸化ベンゾイルを１．０重
量部加えてドライブレンドし、これを押出成形機に投入
して実施例４と同様に薄板状の建材を製造し、試験片
（５０×１００×１ｍｍ）を作成した。この試験片につ
いて実施例１と同様に促進耐候性試験を行い、照射時間
と黄変度（ΔＹＩ）との関係を調べた結果を表１に示
す。 （実施例６）For 100 parts by weight of the polypropylene resin,
2.0 parts by weight of 1,2,2,6,6-pentamethyl-4-piperidyl methacrylate as a reactive light stabilizer;
As a radical reaction initiator, 1.0 part by weight of benzoyl peroxide was added and dry-blended, and the mixture was put into an extruder to produce a thin plate-like building material in the same manner as in Example 4, and a test piece (50 × 100 × 1 mm). Table 1 shows the results of an accelerated weathering resistance test performed on this test piece in the same manner as in Example 1 to examine the relationship between the irradiation time and the yellowing degree (ΔYI). (Example 6)
【００２８】ポリプロピレン樹脂１００重量部に対し、
反応型紫外線吸収剤として２−ヒドロキシ−４−（２′
−アクリロイルオキシエトキシ）ベンゾフェノンを１．
５重量部と、反応型光安定剤として１，２，２，６，６
−ペンタメチル−４−ピペリジルアクリレートを１．０
重量部と、ラジカル反応開始剤として過酸化ベンゾイル
を１．０重量部加えてドライブレンドし、これを押出成
形機に投入して実施例４と同様に薄板状の建材を製造
し、試験片X（５０×１００×１ｍｍ）Yを作成した。こ
の試験片について実施例１と同様に促進耐候性試験を行
い、照射時間と黄変度（ΔＹＩ）、紫外線吸収剤の残存
率との関係を調べた結果を表１に示す。 （比較例１）For 100 parts by weight of the polypropylene resin,
2-hydroxy-4- (2 'as a reactive UV absorber
-Acryloyloxyethoxy) benzophenone.
5 parts by weight and 1,2,2,6,6 as a reactive light stabilizer
-Pentamethyl-4-piperidyl acrylate in 1.0
Parts by weight and benzoyl peroxide as a radical reaction initiator in an amount of 1.0 part by weight were dry-blended, and the mixture was put into an extruder to produce a thin building material in the same manner as in Example 4. (50 × 100 × 1 mm) Y was prepared. Table 1 shows the results of an accelerated weathering test conducted on this test piece in the same manner as in Example 1 to examine the relationship between the irradiation time, the degree of yellowing (ΔYI), and the residual ratio of the ultraviolet absorbent. (Comparative Example 1)
【００２９】ポリプロピレン樹脂を押出成形して薄板状
の建材を製造し、これを切断して試験片（５０×１００
×１ｍｍ）を作製した。この試験片について実施例１と
同様に促進耐候性試験を行い、照射時間と黄変度（ΔＹ
Ｉ）との関係を調べた結果を表１に示す。A thin plate-like building material is manufactured by extrusion molding of a polypropylene resin, which is cut and cut into test pieces (50 × 100).
× 1 mm). This test piece was subjected to an accelerated weathering test in the same manner as in Example 1, and the irradiation time and the yellowing degree (ΔY
Table 1 shows the results of examining the relationship with I).
【００３０】[0030]
【表１】 [Table 1]
【００３１】この表１から、実施例１〜６のポリプロピ
レン樹脂製建材はいずれも、紫外線吸収剤を含まないポ
リプロピレン樹脂製建材（比較例１）に比べて、１００
０時間の紫外線照射後の黄変度（ΔＹＩ）が少なく、良
好な耐紫外線性を発揮することが判る。特に、実施例４
〜６のポリプロピレン樹脂製建材は、含有される紫外線
吸収剤等の大部分がポリマー分子と結合して固定化され
た状態で含有されているため、長時間照射における黄変
度が極めて小さく、紫外線吸収剤の残存率が大であり、
極めて優れた耐紫外線性を維持することが判る。 （実施例７〜１２）From Table 1, it can be seen that all of the polypropylene resin building materials of Examples 1 to 6 are 100% less than the polypropylene resin building material containing no ultraviolet absorber (Comparative Example 1).
It can be seen that the yellowing degree (ΔYI) after irradiating ultraviolet rays for 0 hour is small and good ultraviolet resistance is exhibited. In particular, Example 4
Since the building materials made of polypropylene resin of No. 6 to 6 are contained in a state where most of the contained ultraviolet absorbers and the like are bonded and fixed to polymer molecules, the yellowing degree in long-time irradiation is extremely small, The residual rate of the absorbent is large,
It can be seen that extremely excellent UV resistance is maintained. (Examples 7 to 12)
【００３２】実施例１〜６のドライブレンド物をそれぞ
れ左右の押出成形機に投入し、２３０°で溶融混練して
先端の押出口から０．５ｍｍのシート状に押出すと共
に、その間にガラス繊維ネット（繊維の太さ：０．１５
ｍｍ、網目の大きさ：４×４ｍｍ）を供給して一対のロ
ーラで圧着一体化し、中間にガラス繊維ネットが埋入さ
れた６種類の建材を製造した。そして、各建材を切断し
て６種類の試験片（５０×１００×１ｍｍ）を作製し、
実施例１と同様に促進耐候性試験を行なって照射時間と
黄変度（ΔＹＩ）、紫外線吸収剤の残存率との関係を調
べたところ、実施例１〜６の試験片と略同様の結果が得
られた。The dry blends of Examples 1 to 6 were respectively charged into the left and right extruders, melt-kneaded at 230 ° and extruded into a sheet of 0.5 mm from the extruding port at the tip, and the glass fiber was interposed therebetween. Net (fiber thickness: 0.15
mm, mesh size: 4 × 4 mm), and pressure-bonded and integrated with a pair of rollers to produce six types of building materials in which a glass fiber net was embedded in the middle. Then, each building material is cut to produce six types of test pieces (50 × 100 × 1 mm),
The accelerated weathering test was performed in the same manner as in Example 1 to examine the relationship between the irradiation time, the degree of yellowing (ΔYI), and the residual ratio of the ultraviolet absorber. The results were almost the same as those of the test pieces of Examples 1 to 6. was gotten.
【００３３】更に、実施例７〜１２の各試験片と比較例
１の試験片について、ＪＩＳ Ａ５７０２に準じて耐衝
撃試験を行ったところ、実施例７〜１２の試験片はいず
れも１ｋｇの剛球で１８００ｍｍ以上の耐衝撃強度を有
し、比較例１の試験片よりも遥かに優れていた。Further, the test pieces of Examples 7 to 12 and the test piece of Comparative Example 1 were subjected to an impact resistance test according to JIS A5702, and the test pieces of Examples 7 to 12 were all 1 kg hard spheres. At 1800 mm or more, and was far superior to the test piece of Comparative Example 1.
【００３４】[0034]
【発明の効果】以上の説明から明らかなように、ポリプ
ロピレン樹脂中に反応型紫外線吸収剤や反応型光安定剤
を含む本発明の建材は耐紫外線性が良好で、外装用建材
として使用しても黄変化や強度劣化が少ないという効果
を奏し、これらの反応型紫外線吸収剤や反応型光安定剤
はポリプロピレン樹脂のポリマー分子と化学結合して固
定化されているため、経時的に揮散することがなく、長
期間に亘って優れた耐紫外線性を持続することができ
る。そして、少なくとも表層部分のポリプロピレン樹脂
中に反応型紫外線吸収剤や反応化光安定剤を含有させた
建材は、その含有量を節約することができる。しかも、
本発明の建材はポリプロピレン樹脂より成るものである
から、廃棄物として焼却するとき有害物質を発生せず安
全に焼却することができ、また、ポリプロピレン樹脂は
表面滑性が大きく低温でも脆弱化しにくい樹脂であるか
ら、本発明の建材を例えば積雪地域の屋根材等として使
用すると、雪下ろし作業がしやすくなり、雪の重みや外
部からの衝撃力で簡単に割れる心配もないといった効果
を奏する。As is apparent from the above description, the building material of the present invention containing a reactive UV absorber or a reactive light stabilizer in a polypropylene resin has excellent UV resistance and is used as an exterior building material. The reactive UV absorbers and reactive light stabilizers are chemically bonded to the polymer molecules of the polypropylene resin and are immobilized. And excellent UV resistance can be maintained for a long period of time. And the building material which made the reactive type ultraviolet absorber and the reactive light stabilizer contain at least the polypropylene resin of the surface layer part can save the content. Moreover,
Since the building material of the present invention is made of polypropylene resin, it can be safely incinerated without generating harmful substances when incinerated as waste, and the polypropylene resin has a large surface lubricity and is hardly brittle even at low temperatures. Therefore, when the building material of the present invention is used, for example, as a roofing material in a snow-covered area, there is an effect that the snow-removing work becomes easy, and there is no fear of easily being broken by the weight of snow or an external impact.
【図１】本発明の建材の一実施例を示す断面図である。FIG. 1 is a sectional view showing one embodiment of a building material of the present invention.
【図２】本発明の建材の他の実施例を示す断面図であ
る。FIG. 2 is a sectional view showing another embodiment of the building material of the present invention.
【図３】同実施例の建材の一製法例を示す説明図であ
る。FIG. 3 is an explanatory diagram showing an example of a manufacturing method of the building material of the embodiment.
１ 反応型紫外線吸収剤及び反応型光安定剤のいずれか
一方又は双方を反応させたポリプロピレン樹脂より成る
平板状の建材 ２ 補強繊維DESCRIPTION OF REFERENCE NUMERALS 1 A plate-shaped building material made of a polypropylene resin obtained by reacting one or both of a reactive UV absorber and a reactive light stabilizer
───────────────────────────────────────────────────── フロントページの続き (72)発明者 加藤 隆明 大阪市中央区安土町２丁目３番13号 タ キロン株式会社内 (56)参考文献 特開 昭63−146949（ＪＰ，Ａ) 特開 平４−298505（ＪＰ，Ａ) 特開 平２−281009（ＪＰ，Ａ) 特開 平２−49767（ＪＰ，Ａ) 特開 昭63−99247（ＪＰ，Ａ) 特開 平４−226552（ＪＰ，Ａ) 特開 平３−139590（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) E04D 3/00 - 3/40 C08J 7/04 - 7/06 ──────────────────────────────────────────────────続 き Continuation of the front page (72) Takaaki Kato 2-3-1-13 Azuchicho, Chuo-ku, Osaka City Inside Takiron Co., Ltd. (56) References JP-A-63-146949 (JP, A) JP-A-Hei JP-A-4-298505 (JP, A) JP-A-2-281008 (JP, A) JP-A-2-49767 (JP, A) JP-A-63-99247 (JP, A) JP-A-4-226552 (JP, A A) JP-A-3-139590 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) E04D 3/00-3/40 C08J 7 /04-7/06
Claims (2)
て、そのポリプロピレン樹脂中に、ラジカル反応開始剤
として、過酸化ベンゾイル、ｔ−ブチルヒドロパーオキ
サイド、オクタノイルパーオキサイドのいずれかが含有
され、不飽和結合を有する反応型紫外線吸収剤及び反応
型光安定剤のいずれか一方又は双方が、上記のラジカル
反応開始剤によってポリプロピレン樹脂のポリマー分子
の側鎖として化学結合していることを特長とする建材。1. A building material comprising a polypropylene resin, wherein the polypropylene resin contains any one of benzoyl peroxide, t-butyl hydroperoxide and octanoyl peroxide as a radical reaction initiator, and is unsaturated. A building material characterized in that one or both of a reactive ultraviolet absorber and a reactive light stabilizer having a bond are chemically bonded as side chains of polymer molecules of a polypropylene resin by the above-mentioned radical reaction initiator.
て、その表層部分のポリプロピレン樹脂中に、ラジカル
反応開始剤として、過酸化ベンゾイル、ｔ−ブチルヒド
ロパーオキサイド、オクタノイルパーオキサイドのいず
れかが含有され、不飽和結合を有する反応型紫外線吸収
剤及び反応型光安定剤のいずれか一方又は双方が、上記
のラジカル反応開始剤によって表層部分のポリプロピレ
ン樹脂のポリマー分子の側鎖として化学結合しているこ
とを特長とする建材。2. A building material comprising a polypropylene resin, wherein the surface layer of the polypropylene resin contains any one of benzoyl peroxide, t-butyl hydroperoxide and octanoyl peroxide as a radical reaction initiator. One or both of the reactive UV absorber and the reactive light stabilizer having an unsaturated bond are chemically bonded as side chains of the polymer molecules of the polypropylene resin in the surface layer by the above radical reaction initiator. Building materials characterized by: