JP3232073U - Cold feeling wearing product and combination of cold feeling wearing product and fan wear - Google Patents
Cold feeling wearing product and combination of cold feeling wearing product and fan wear Download PDFInfo
- Publication number
- JP3232073U JP3232073U JP2021000763U JP2021000763U JP3232073U JP 3232073 U JP3232073 U JP 3232073U JP 2021000763 U JP2021000763 U JP 2021000763U JP 2021000763 U JP2021000763 U JP 2021000763U JP 3232073 U JP3232073 U JP 3232073U
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- cooling sensation
- cold
- wearing
- wearing product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】有効な冷感効果（人が着用して冷たいと感じる性能）を発揮することに加えて、着用開始後、相当な時間が経過した後でも振ることによって冷たさが回復することができる身体操着品を提供する。【解決手段】吸水性ならびに保水性が高い冷感生地１を備えたアンダーウェア、スポーツウェア、フェイスガード、アームカバー、手袋などの身体操着品であって、冷感生地１は、滴下法による吸水性試験結果が２秒未満の吸水性であり、保水性試験結果が１８０％〜２１０％の保水率である。冷感生地１を構成する構成糸の接触冷感値（ＱＭＡ×値）が０．２８Ｗ／ｃｍ２以上のポリエステル繊維糸である。冷感生地１は着用者の皮膚を覆う領域に配置されている。さらに、メッシュ生地２などの通気性の高い生地を併用する。【選択図】図１PROBLEM TO BE SOLVED: To recover coldness by shaking even after a considerable time has passed after the start of wearing, in addition to exhibiting an effective cooling sensation effect (performance that a person wears and feels cold). Provide gym clothes. SOLUTION: The cold sensation fabric 1 is a gym suit such as underwear, sportswear, face guard, arm cover, gloves, etc. The water absorption test result is water absorption of less than 2 seconds, and the water retention test result is 180% to 210% water retention rate. It is a polyester fiber yarn having a contact cold sensation value (QMA × value) of 0.28 W / cm2 or more of the constituent yarns constituting the cool sensation fabric 1. The cooling sensation fabric 1 is arranged in an area covering the wearer's skin. Further, a highly breathable fabric such as mesh fabric 2 is used in combination. [Selection diagram] Fig. 1
Description
本考案は、冷感装着品及び冷感装着品とファンウエアの組み合わせに関するものである。 The present invention relates to a cooling sensation wearing product and a combination of a cooling sensation wearing product and fan wear.
今日、熱中症対策の一つの手段として、冷感性能を持った衣服などの冷感装着品の開発が進められている。 Today, as one of the measures against heat stroke, the development of cooling sensation wearing products such as clothes having a cooling sensation performance is underway.
特許文献１では、肌側面に配される編地において、構成単糸の横断面の外周部が１個以上の凸部を有する扁平断面形状を有し、捲縮率が実質的に０％である合成繊維を使用する気化熱冷却編地であり、好ましくは、扁平断面形状の合成繊維の横断面の扁平度が１ ． ０ 〜 ５ であり、好ましくは、肌側面とは反対側の面に、ポリエステル捲縮糸が配されているダブルニットである気化熱冷却編地によって優れたクーリング効果を奏する気化熱冷却編地によって、アンダーウェアやスポーツウェアを構成することが開示されている。
ところが、衣服、特に上衣において、気化熱冷却編地を配置する位置に関しては十分な検討がなされていない。また、繰り返し気化熱を有効に利用するには保水性と吸水性のバランスを必要とするものの、かかる観点からの十分な考察がなされていない。
In
However, sufficient studies have not been made on the position of the heat of vaporization cooling knitted fabric for garments, especially upper garments. Further, although it is necessary to balance water retention and water absorption in order to effectively utilize the heat of vaporization repeatedly, sufficient consideration has not been made from this point of view.
また特許文献２では、「芯鞘構造を有する混繊糸であって、ポリエチレンを主たる構成成分とする繊維を鞘糸、ポリエステル、ポリアミド、ポリオレフィンから選択される少なくとも１種以上の繊維形成性重合体を主たる構成成分とする繊維を芯糸とすることを特徴とする冷感に優れた混繊糸」が提案されている。
ところが、使用開始にあたっては冷感効果（ヒヤリとする感覚を着用者に与える性能）を発揮することができるものの、使用を開始した後、時間が経つに従って冷感効果が低下することを避けることができず、生暖かい感覚を着用者に与えていた。
Further, in Patent Document 2, "a mixed fiber having a core-sheath structure, at least one or more fiber-forming polymers in which a fiber containing polyethylene as a main component is selected from a sheath yarn, polyester, polyamide, and polyolefin. A "mixed fiber yarn having an excellent cold feeling" has been proposed, which is characterized in that the core yarn is a fiber whose main component is.
However, although it is possible to exert a cooling sensation effect (performance that gives the wearer a feeling of tingling) at the start of use, it is possible to avoid a decrease in the cooling sensation effect over time after the start of use. I couldn't do it, giving the wearer a warm feeling.
また今日、特許文献３に示すような空調ファンを備えたファンウエアが実用化されているが、特許文献１〜３では、アンダーウェアやスポーツウェアの上衣とファンウエアの組み合わせによって良好な冷却効果を得ると言う観点からの考察がなされていない。
Further, today, fan wear provided with an air-conditioning fan as shown in
本考案は、有効な冷感効果（人が着用して冷たいと感じる性能）を発揮することに加えて、着用開始後、相当な時間が経過した後でも振ることによって冷たさが回復することができる身体操着品の提供を課題とする。
また本考案は、空調ファンを備えたファンウエアとアンダーウェアやスポーツウェアの上衣との効果的な組み合わせの提供を課題とする。
In addition to exerting an effective cooling sensation effect (performance that a person wears and feels cold), the present invention can recover the coldness by shaking even after a considerable amount of time has passed after the start of wearing. The challenge is to provide gym clothes that can be used.
Another object of the present invention is to provide an effective combination of fan wear equipped with an air-conditioning fan and an underwear or sportswear top.
本考案は、吸水性ならびに保水性が高い冷感生地を備え、前記冷感生地は、滴下法による吸水性試験結果が２秒未満の吸水性であり、保水性試験結果が１８０％〜２１０％の保水率であり、前記冷感生地を構成する構成糸の接触冷感値（ＱＭＡ×値）が０．２８W/cm２以上のポリエステル繊維糸であり、前記冷感生地が着用者の皮膚を覆う領域に配置されたことを特徴とする冷感装着品を提供することによって上記の課題を解決する。
前記冷感装着品としては、様々なものを挙げることができるが、アンダーウェア、スポーツウェア、フェイスガード、アームカバー、手袋、動物用衣料品、動物用ハーネスなどを例示することができる。
本考案の冷感装着品の開発に際して鋭意研究したところ、着用開始後、時間が経つに従って冷感効果が低下することを避けることはできないものの、を生地をつまんで振るなど人の装着部位から浮かせて動かすことによって、気化熱を利用して、冷感効果を回復させることが可能であることを知見した。
従来の繊維製品では、十分な水を素早く吸い込むように吸水性を高めのことを主眼としたものであったが、保水性が低い場合には気化熱を発生させる水分が早期に蒸発してしまい、身体操着品を振ったとしても冷感効果を回復させることが困難であった。
そこで本考案は、吸水性と保水性とのバランスをとることによって着用開始後、相当時間が経ったとしても気化熱を有効利用することで、冷感効果を回復させることが可能であることを知見し、さらに、糸についても熱伝導率が高くて接触冷感を発揮するとともに、気化熱を効率的に発揮させることに有効な毛細管現象が起こりやすい糸を用いることによって、本考案を完成させたものである。
The present invention comprises a cooling sensation fabric having high water absorption and water retention, and the cooling sensation fabric has a water absorption test result of less than 2 seconds by the dropping method, and the water retention test result is 180% to 210%. It is a polyester fiber yarn having a water retention rate of 0.28 W / cm 2 or more in contact cold sensation value (QMA × value) of the constituent yarns constituting the cool sensation fabric, and the cool sensation fabric touches the wearer's skin. The above problem is solved by providing a cooling sensation wearing product characterized in that it is arranged in an area to be covered.
Various examples of the cooling sensation wearing product can be mentioned, and examples thereof include underwear, sportswear, face guards, arm covers, gloves, animal clothing, and animal harnesses.
As a result of diligent research during the development of the cooling sensation wearing product of the present invention, although it is unavoidable that the cooling sensation effect decreases with time after the start of wearing, the fabric is pinched and shaken to float it from the wearing part of a person. It was found that it is possible to recover the cooling sensation effect by utilizing the heat of vaporization.
Conventional textile products have been aimed at increasing water absorption so that sufficient water can be absorbed quickly, but if the water retention is low, the water that generates heat of vaporization evaporates early. However, it was difficult to recover the cooling effect even if the gym suit was shaken.
Therefore, according to the present invention, it is possible to recover the cooling sensation effect by effectively utilizing the heat of vaporization even if a considerable time has passed after the start of wearing by balancing water absorption and water retention. Furthermore, we have completed the present invention by using a thread that has a high thermal conductivity and exhibits a cool contact feeling, and is prone to capillarity, which is effective in efficiently exerting the heat of vaporization. It is a thing.
本考案は、編糸から構成された編地を冷感生地として用いることができるが、前記編糸として繊維断面が凹凸を備えたポリエステル繊維製の異形糸を用いることが適当である。これによって糸自体が毛細管現象の生じやすい構造を備えている。
また、前記編地は表面側に凸部を備え、この凸部は３本以上の前記編糸が密接する部分を備えると共に平面視において環状部が並べられた並列形態を備えているものであることが望ましい。多くの前記編糸が密接していることによって、一般的には保水性の低い編糸であったとしても、編地全体として比較的多くの水分を保持しておくことができる。従って、冷感生地の部分を振ることによって水分循環が生じて、水分の蒸発によって気化熱が奪われて糸及び編地自体の温度を低下させることができる。
In the present invention, a knitted fabric composed of knitted yarn can be used as a cooling sensation fabric, but it is appropriate to use a deformed yarn made of polyester fiber having an uneven fiber cross section as the knitted yarn. As a result, the thread itself has a structure in which a capillary phenomenon is likely to occur.
Further, the knitted fabric has a convex portion on the surface side, and this convex portion has a portion in which three or more of the knitting yarns are in close contact with each other and has a parallel form in which annular portions are arranged in a plan view. Is desirable. Due to the close contact of many of the knitted yarns, a relatively large amount of water can be retained in the knitted fabric as a whole, even if the knitted yarn generally has low water retention. Therefore, the water circulation is generated by shaking the portion of the cooling sensation fabric, and the heat of vaporization is taken away by the evaporation of the water, and the temperature of the yarn and the knitted fabric itself can be lowered.
この冷感生地は、ＪＩＳ Ｌ １９０７＿２０１０に準拠する繊維製品の吸水性試験験方法（滴下法）による吸水性試験結果が２秒未満であり、ＱＴＥＣ ＴＭ１１Ｂ法準用による保水性試験結果が保水率１８０％〜２１０％であることも望ましい。この吸水性と保水性とのバランスによって着用開始後、相当時間が経ったとしても気化熱を有効利用することで、冷感効果を回復させることが可能である。 For this cooling sensation fabric, the water absorption test result by the water absorption test test method (dropping method) of the textile product conforming to JIS L 1907_2010 is less than 2 seconds, and the water retention test result by applying the QTEC TM11B method is 180%. It is also desirable that it is ~ 210%. Due to this balance between water absorption and water retention, it is possible to recover the cooling sensation effect by effectively utilizing the heat of vaporization even if a considerable amount of time has passed after the start of wearing.
前記編糸は、繊維断面が略放射状の複数の繊維凸部を備えた異形糸として実施することができる。これによって、気化熱による温度低下を実現するために有効な毛細管現象を促進することができるし、前記の編地の構造と共に人の肌に対する接触面積をいたずらに大きくすることを抑制することができる。 The knitting yarn can be carried out as a deformed yarn having a plurality of fiber protrusions having substantially radial fiber cross sections. Thereby, it is possible to promote the capillary phenomenon effective for realizing the temperature decrease due to the heat of vaporization, and it is possible to suppress unnecessarily increasing the contact area with the human skin together with the structure of the knitted fabric. ..
前記編糸には熱伝導率が高いものが適しており、接触冷感値（ＱＭＡ×値）が０．２８W/cm２以上の編糸を好適に用いることができる。熱伝導率が高い糸を用いるこれによって、糸自体の温度は同じであっても、人が触った時に冷たく感じることができる接触冷感性を発揮することができる。
前記編糸は、鉱物からなる冷感結晶体のナノ粒子を含有するものとして実施することによって、熱伝導性を高めて接触冷感値（ＱＭＡ×値）が０．２８W/cm２以上を実現することができる。
A knitting yarn having a high thermal conductivity is suitable for the knitting yarn, and a knitting yarn having a cool contact feeling value (QMA × value) of 0.28 W / cm 2 or more can be preferably used. By using a yarn having a high thermal conductivity, even if the temperature of the yarn itself is the same, it is possible to exhibit a cold contact feeling that a person can feel cold when touched.
By carrying out the knitting yarn on the assumption that it contains nanoparticles of a cooling sensation crystal made of minerals, the thermal conductivity is enhanced and a contact cooling sensation value (QMA × value) of 0.28 W / cm 2 or more is realized. can do.
本考案の前記冷感装着品は、アンダーウェア又はスポーツウェアの上衣として実施することもできる。
前記上衣の前身頃は、首回りから胸にかけて前記冷感生地が配置され、前記アンダーウェアの後身頃は、首回りから肩甲骨の間にかけて前記冷感生地が配置され、且つ、この後身頃の前記冷感生地の下から下方に向けて前記冷感生地よりも通気性の高いメッシュ生地が配置されているものとすることができる。
前記冷感装着品の上（外側）に、ファンウエアを着用することも好ましい。前記ファンウエアは、左右の両脇に外部の空気を内部に送る空調ファンを備え、前記空調ファンの間に前記メッシュ生地が位置するものとすることができる。これによって、前記空調ファンによって送られた空気が、前記メッシュ生地から前記冷感生地を通って前記首回りから外部に抜けるように導くことができる。
The cooling sensation wearing product of the present invention can also be implemented as an underwear or sportswear top.
The cooling sensation fabric is arranged from the neck to the chest on the front body of the upper garment, and the cooling sensation fabric is arranged from the neck to the shoulder blades on the back body of the underwear. It can be assumed that a mesh fabric having a higher breathability than the cooling sensation fabric is arranged from the bottom to the bottom of the cooling sensation fabric.
It is also preferable to wear fan wear on (outside) the cooling sensation wearing product. The fan wear may be provided with an air-conditioning fan that sends external air to the inside on both the left and right sides, and the mesh fabric may be located between the air-conditioning fans. As a result, the air sent by the air-conditioning fan can be guided from the mesh cloth to the outside through the cold feeling cloth and from the neck circumference.
本考案は、有効な冷感効果を発揮することに加えて、着用開始後、相当な時間が経過した後でも振ることによって冷たさが回復することができる身体操着品の提供をなすことができたものである。
また本考案は、空調ファンを備えたファンウエアとアンダーウェアやスポーツウェアの上衣との効果的な組み合わせを提供することができたものである。
The present invention is to provide a gym suit that can recover the coldness by shaking even after a considerable time has passed after the start of wearing, in addition to exerting an effective cooling sensation effect. It was made.
Further, the present invention has been able to provide an effective combination of fan wear equipped with an air-conditioning fan and an underwear or sportswear top.
以下、図面を参照しつつ本考案の実施の形態を説明する。
この実施の形態に係る冷感装着品について図１を参照して説明するが、これに用いられる冷感生地１については図５以降を参照して後述する。
Hereinafter, embodiments of the present invention will be described with reference to the drawings.
The cooling sensation-mounted product according to this embodiment will be described with reference to FIG. 1, but the
（アンダーウェアの上衣）
図１に示す冷感装着品は、アンダーウエアとして実施されている。アンダーウエアは、上半身に直に着用される上衣であって、袖なしのタンクトップ型やＴシャツや前びらきのシャツ型など様々な形態をとることができる。この実施の形態では左右の袖を備えた前身頃と後身頃と備えているが、襟は備えていない。前身頃は、首回りから胸にかけて冷感生地１が配置されており、その他の部分には一般的な身頃生地３が用いられている。身頃生地３には、ポリエステルやナイロンなどの合成繊維などによる吸汗速乾素材や綿布などの天然繊維など、肌着に用いられる種々の生地を採用することができる。後身頃には、首回りから肩甲骨の間の脊椎対応部位にかけて冷感生地１が配置されているものである。そしてこの冷感生地１に隣接してメッシュ生地２が配置され、このメッシュ生地２は下方（下半身の方向）に向けて伸びている。この例ではメッシュ生地２は、後身頃の下端にまで達しているが、ウェスト部分（胴回りの一番細い部分）にまで達しておれば、それより下方は身頃生地３など他の生地が来ても構わない。
(Underwear top)
The cooling sensation wearing product shown in FIG. 1 is implemented as underwear. Underwear is an upper garment that is worn directly on the upper body, and can take various forms such as a sleeveless tank top type, a T-shirt, and a front-end shirt type. In this embodiment, the front body and the back body with the left and right sleeves are provided, but the collar is not provided. A
（スポーツウェアの上衣）
次に図２に示す冷感装着品は、スポーツウエアとして実施されている。スポーツウエアは、上半身に直に着用されることもあるポロシャツなどの上衣であって、様々な形態をとることができる。この実施の形態では襟と左右の袖を備えた前身頃と後身頃と備えている。前身頃は、首回りから左右の肩並びに胸にかけて冷感生地１が配置されており、その他の部分には一般的な身頃生地３が用いられている。後身頃には、首回りから左右の肩にかけて冷感生地１が配置されているものであり、他の部分には一般的な身頃生地３が用いられている。
(Sportswear top)
Next, the cooling sensation wearing product shown in FIG. 2 is implemented as sportswear. Sportswear is a top such as a polo shirt that may be worn directly on the upper body and can take various forms. In this embodiment, the front body and the back body are provided with a collar and left and right sleeves. On the front body, a
（ファンウエア）
他方、今日特許文献３に示すような空調ファンを備えたファンウエアが実用化されている。前記ファンウエアは、図３に示すように、後身頃側の左右の体側下部（ウエストの付近）に外部の空気を内部に送る空調ファン４を備えているものが多い。
上記の実施の形態にかかるスポーツウエア及びアンダーウエアは、単独で用いることもできるが、ファンウエアと併用することが効果的である。特にアンダーウエアを肌の上に着用し、その上にファンウエアを着用すると、図３に示すように、左右両側の空調ファン４の間に後身頃のメッシュ生地２が位置するものとなる。その結果空調ファン４によって送られた空気の少なくとも一部は、メッシュ生地２から冷感生地１を通って首回りから外部に抜けるように導かれる。
(Fan wear)
On the other hand, fan wear provided with an air conditioning fan as shown in
The sportswear and underwear according to the above embodiment can be used alone, but it is effective to use them in combination with fan wear. In particular, when the underwear is worn on the skin and the fan wear is worn on the skin, the mesh fabric 2 of the back body is located between the air conditioning fans 4 on both the left and right sides, as shown in FIG. As a result, at least a part of the air sent by the air conditioning fan 4 is guided from the mesh fabric 2 through the cooling
（熱と汗のマッピング）
平均気温が２９度の夏季に体重６５kgの人が室内で活動すると、一日の汗の量は３リットル程度、これを超える高温環境の工場や屋外などで８時間働くと、最大で１２リットルにも達すると言われている。
図３に示すような着用形態を採ると、着用者がかく汗とファンウエアで使われる空調ファン４を使って、気化潜熱を発生させることによって、体温を効果的に下げることができる。
図４は、熱と汗のマッピングの概要を示す人体の前と後ろの図であって、前ではみぞおちから両肩、後ろでは左右の両肩付近の濃色で示す部位が最も熱がこもるヒートゾーンと言われる部分である。また、淡色で示す部分が最も発汗量が多いスウェットゾーンと言われる部分である。発汗量は平均約４００ｇ／m２であると言われており、体重６５kgの平均的な成人男性の場合、上半身の体表面の面積は約１．７m２であるため、
４００ｇ×１．７m２＝６８０ｇ
となり、毎時６８０gを発汗している。
従って平均労働時間の８時間で換算すると、
６８０ｇ×８時間＝５４４０ｇ
となり、１日約５．４４リットルもの発汗量に達する。
(Mapping of heat and sweat)
When a person weighing 65 kg works indoors in the summer when the average temperature is 29 degrees Celsius, the amount of sweat per day is about 3 liters, and when working for 8 hours in a factory or outdoors in a high temperature environment exceeding this, the maximum is 12 liters. Is said to reach.
When the wearing form as shown in FIG. 3 is adopted, the body temperature can be effectively lowered by generating the latent heat of vaporization by the wearer using the sweat and the air-conditioning fan 4 used in the fan wear.
FIG. 4 is a front and back view of the human body showing an outline of heat and sweat mapping. In the front, the heat is most accumulated from the epigastrium to both shoulders, and in the back, the part shown in dark color near the left and right shoulders is the most hot. This is the part called the zone. In addition, the part shown in light color is the part called the sweat zone where the amount of sweating is the largest. It is said that the average amount of sweating is about 400 g / m 2 , and in the case of an average adult male weighing 65 kg, the area of the upper body surface is about 1.7 m 2 .
400g x 1.7m 2 = 680g
And sweating 680g per hour.
Therefore, when converted to 8 hours of average working hours,
680g x 8 hours = 5440g
The amount of sweating reaches about 5.44 liters a day.
図１の実施の形態では、上記のヒートゾーンに冷感生地１を配置するとともに、蒸気のスエットゾーンにメッシュ生地２を配置している。
冷感生地１が配置される部位のサイズは幅７ｃｍ×１２ｃｍとなる。
この部位の発汗量は、
１０ｃｍ×７２ｃｍ＝０．０７２m２
であり、
０．０７２m２×１，１９７ｇ（スウェットゾーンの経表皮水分蒸散量）
＝８６．２ｇ／毎時となる。
次に水の気化潜熱は５８０ｃａｌ／ｇであり、人間の比熱は約０．８３である。
例えば、体重６０kgの場合、
６００００ｇ（６０kg）×０．８３＝４９８００ｃａｌとなるため、これだけのエネルギーが奪われたときに体温が１℃低下することになる。
従って、
４９８００ｃａｌ÷５８０ｃａｌ/ｇ=８５．８６ｇとなり、冷感生地１が配置された部分の発汗量とほぼ同じになる。そして、この部位にファンウエアの空調ファン４の風を送り続けることで、気化潜熱の効果により、体温を１℃下げる効果が期待できる。
In the embodiment of FIG. 1, the
The size of the portion where the
The amount of sweating in this area is
10 cm x 72 cm = 0.072 m 2
And
0.072m 2 x 1,197g (Transepidermal water loss in sweat zone)
= 86.2 g / hour.
Next, the latent heat of vaporization of water is 580 cal / g, and the specific heat of humans is about 0.83.
For example, if you weigh 60 kg
Since 60,000 g (60 kg) x 0.83 = 49,800 cal, the body temperature drops by 1 ° C. when this amount of energy is deprived.
Therefore,
49800 cal ÷ 580 cal / g = 85.86 g, which is almost the same as the amount of sweating in the portion where the
図１に示す実施の形態では、左右の体側に配置された空調ファン４からの風が、スウェットゾーン上に配置されたメッシュ生地２を通って、冷感生地１が配置されたから首へと抜けるものである。その際、メッシュ生地２は身頃生地３や冷感生地１よりも通気性が高く、空気の流れを阻害することを抑えることができると共に、スウェットゾーンからの湿気を含んだ風をメッシュ生地２に送ることによって気化潜熱の有効利用を図ることができる。
従って、図１の実施の形態に示すアンダーウェアとファンウエアと併用することによって、上記の試算を有効に実現することができる。
なお、図２の実施の形態に示すスポーツウェアとファンウエアと併用することもできる。このスポーツウェアの例では、襟にも冷感生地１を用いたことによって、首に対しても有効な冷却効果を発揮することができる。なお、アンダーウェアと同様の部位にファンウエアを配置して実施することができる。
In the embodiment shown in FIG. 1, the wind from the air-conditioning fans 4 arranged on the left and right body sides passes through the mesh fabric 2 arranged on the sweat zone, and the
Therefore, the above trial calculation can be effectively realized by using the underwear and fan wear shown in the embodiment of FIG. 1 in combination.
The sportswear and fanwear shown in the embodiment of FIG. 2 can also be used in combination. In this example of sportswear, by using the
（冷感生地１について）
上記の実施の形態に示された冷感生地１は、図５〜図８に示すように、複数本の編糸１１によって編成された編地２０によって構成されている。
編地２０は、図５に示すように、少なくとも表面側に凸部２２を備え、凸部２２は平面視において、図６にて点の集合で表記したように略多角形などの環状部２３が並べられたハニカム構造やそれに類似する並列形態を示すものである。この凸部２２は、図６に示すように、３本以上の編糸１１が密接する密集部２４を備えるものであり、裏面側の平編ないしは浮編による基層（凹部２１）から表面側に突出している。図７にその組織図を示す。
(About cold fabric 1)
As shown in FIGS. 5 to 8, the
As shown in FIG. 5, the knitted
編糸１１は、図８に示すように、繊維断面が凹凸を備えたポリエステル繊維製の異形糸である。この異形糸は、４つの繊維凸部１３が略放射状に繊維凹部１２から突出しているのであり、毛細管現象が生じやすい構造を示す。繊維凸部１３の数は４つ以上であることが好ましいが、あまり多くすると断面円形の通常のポリエステル繊維に近くなってしまうため４〜８つの繊維凸部１３を備えたものであることが適当である。
編糸１１は、鉱物からなる冷感結晶体のナノ粒子を含有することによって熱伝導率を高めて瞬間的な熱の移動量を示す接触冷感値（ＱＭＡ×値）が０．２８W/cm２以上のポリエステル繊維糸であることが特に好ましい。
なお、芯にポリエステル、鞘にポリエチレン樹脂とポリビニルアルコール樹脂との複合樹脂などを用いた芯鞘複合繊維を用いて実施しても構わない。
As shown in FIG. 8, the
The
It should be noted that the core-sheath composite fiber using polyester as the core and a composite resin of polyethylene resin and polyvinyl alcohol resin as the sheath may be used.
この実施の形態に係る冷感生地１は、ＪＩＳ Ｌ １９０７＿２０１０に準拠する繊維製品の吸水性試験方法（滴下法）による吸水性試験結果が１秒である。本考案の滴下法は、弛みなく張られた試験片に対して水を１滴滴下し、水が生地に到達した時点から完全に吸水されるまでの時間（秒）を測定するもので、下記の方法で実施される。
・試験片を円形の保持枠に弛みなく張った状態にて取り付ける。
・試験片上１０mmの高さから水を１滴（約０．０４ml）滴下する。
・水滴が試験片に到達してから水の鏡面反射（キラキラした反射）が完全になくなるまでの時間をストップウォッチで測定する。
The
-Attach the test piece to the circular holding frame with no slack.
-Drop 1 drop (about 0.04 ml) of water from a height of 10 mm above the test piece.
-Measure the time from when the water droplet reaches the test piece until the specular reflection (glittering reflection) of water completely disappears with a stopwatch.
より詳しくは、次の器具等で実施される。
1)試験片保持枠は、金属製のリング又はこれと同等に試験片が弛みなく張った状態に保持できるもの。
2)活栓付きビュレット。
3)0.5秒を計測できるストップウォッチ。
4)水の鏡面反射が目で確認できる500l×〜１０00l×の明るさ光源。
5)温度は２０℃±２℃の水。
More specifically, it is carried out with the following equipment and the like.
1) The test piece holding frame is a metal ring or equivalent that can hold the test piece in a stretched state without slack.
2) Burette with a stopcock.
3) A stopwatch that can measure 0.5 seconds.
4) A 500l x 1000l x brightness light source that allows you to visually confirm the specular reflection of water.
5) Water with a temperature of 20 ° C ± 2 ° C.
操作
試料から大きさ約２０0mm×２０0mmの試験片を5枚採取する。次に、試験片を試験片保持枠に取り付け、光源と観察者との間に置く。試験片の表面からビュレットの先端までの距離が１０mmの高さになるように配置する。観察者は水による光の反射が明らかに見える角度から観察する。
ビュレットから水を１滴滴下させる。水滴が試験片の表面に達したときからその試験片が水滴を吸収するにつれて鏡面反射が消え、湿潤だけが残った状態までの時間をストップウォッチで１秒単位まで測定する。
Collect 5 test pieces with a size of about 200 mm × 200 mm from the operation sample. Next, the test piece is attached to the test piece holding frame and placed between the light source and the observer. Arrange so that the distance from the surface of the test piece to the tip of the burette is 10 mm high. The observer observes from an angle where the reflection of light by water is clearly visible.
Drop a drop of water from the burette. The time from when the water droplet reaches the surface of the test piece until the specular reflection disappears as the test piece absorbs the water droplet and only the wetness remains is measured with a stopwatch in units of 1 second.
試験結果は，５枚の試験片の平均値を、四捨五入によって整数に丸めて表す。
ＱＴＥＣ ＴＭ１１Ｂ法準用による保水性試験結果が保水率１８０％〜２１０％となっている。保水率が低すぎると、冷却に必要な水を十分に保持することができない。他方、綿のタオル地のように保水率が４００％に達するなど、保水率が高すぎると、濡らして振る際に、うまく振れず効果的に温度が下がらない。冷感生地１としての用途を考えた場合、保水率１８０％〜２１０％とすることが好ましく、約１時間冷感を保つことができると共に濡らして振る際に、うまく振ることができて効果的に温度を下げることができる。
The test results are expressed by rounding the average value of the five test pieces to an integer.
The water retention test result by applying the QTEC TM11B method mutatis mutandis shows that the water retention rate is 180% to 210%. If the water retention rate is too low, the water required for cooling cannot be sufficiently retained. On the other hand, if the water retention rate is too high, such as when the water retention rate reaches 400% like a cotton towel cloth, the temperature does not drop effectively because it does not shake well when wet and shaken. Considering the use as a
本考案におけるＱＴＥＣ ＴＭ１１Ｂ法準用による保水性試とは、
試料の質量を測定し、常温の水に30分間浸漬し、水中より取り出して垂直に吊り下げ10分間放置後直ちに試料の質量を測定し、保水率を次式によって求める。
保水率（％）＝給水量（ｍｌ）／原試験料質量（ｇ）×１００
給水量（ｍｌ）＝浸漬後の質量（ｇ）−原試験料質量（ｇ）
The water retention test by applying the QTEC TM11B method in the present invention is
Measure the mass of the sample, immerse it in water at room temperature for 30 minutes, take it out of the water, hang it vertically, leave it for 10 minutes, measure the mass of the sample immediately, and calculate the water retention rate by the following formula.
Water retention rate (%) = Water supply amount (ml) / Original test fee mass (g) x 100
Water supply amount (ml) = mass after immersion (g) -original test charge mass (g)
この冷感生地１は、気温２５．７℃、湿度６６％の室内における６０分以内の温度変化が１℃以内であるように構成されている。
そして、熱伝導性と吸水性と保水性のバランスをとることによって、着用した際に優れた冷感効果を発揮するとともに、着用開始後６０分経過した後でも振ることによって冷感が回復する冷感回復性を備えるものである。
The
By balancing thermal conductivity, water absorption, and water retention, it exerts an excellent cooling sensation effect when worn, and the cooling sensation is restored by shaking even 60 minutes after the start of wearing. It has a feeling of recovery.
（冷感回復性）
この実施の形態に係る冷感生地１にあっては、上記のような冷感回復性を備えているものである。従って、着用時に図１や図２に示す上衣を、濡らして必要に応じて軽く絞った状態で着用することによって、上記の気化潜熱の活用による冷却効果を発揮させることができることはもちろん、その効果を継続的に発揮させることができると共に体を動かすことなどによって生じる発汗による水分を、気化潜熱による冷却効果に活用することができる。
(Recovery of cold feeling)
The
（フェイスガード・アームカバー）
上記の冷感生地１は、図９（Ａ）に示すようなフェイスガードにも適用することができる。このフェイスガードはその全体が冷感生地１の編地によって筒状に構成されており、首回りから顎にかけての部位を良好に冷却することができる。
また、上記の冷感生地１は、図９（Ｂ）に示すようなアームカバーにも適用することができる。このアームカバーはその全体が冷感生地１の筒状の編地によって構成されており、肘から前腕部にかけての部位を良好に冷却することができるし、さらに手の甲などの手を覆うようにしても構わない。また、図示は省略するが手袋やマスクや靴下などに適用することもできる。
(Face guard / arm cover)
The above-mentioned
Further, the above-mentioned
（動物用の冷感装着品）
本考案に係る冷感装着品は、動物用の装着品としても実施することができる。
上記の冷感生地１は、図１０（Ａ）に示すような犬などの愛玩動物用の衣服にも適用することができる。この愛玩動物用の衣服は愛玩動物の肩から胴にかけて着用させるもので、その全体又は一部が冷感生地１の編地によって構成されており、冷感生地１が配置された愛玩動物の部位を良好に冷却することができる。なお、今日においては、愛玩動物の衣服は前に示されたものの他に様々な形態のものが提案もしくは実用化されているが、本考案は様々な形態の愛玩動物用の衣服に適用することもできるし、愛玩動物用のハーネスに適用して実施することもできる。
また、上記の冷感生地１は、図１０（Ｂ）に示すような馬用のネックカバーにも適用することができる。このネックカバーはその全体が冷感生地１の筒状の編地によって構成されており、馬の首を良好に冷却することができる。さらに顔面や胴などを覆うようにしても構わないし、その一部分のみに冷感生地１を配置しても構わない。また、愛玩動物や馬以外の動物についても、本考案を適用することができる。
(Cold feeling equipment for animals)
The cooling sensation wearing product according to the present invention can also be implemented as a wearing product for animals.
The above-mentioned
Further, the above-mentioned
以下、本考案の理解を高めるために実施例を示すが、本考案はこの実施例に限定して理解されるべきではない。
（実施例１）
図８に示す繊維断面が凹凸を備えたポリエステル繊維製の異形糸（７５Ｄ １４４Ｆ）７５デニール １４４フィラメントを用いて、図６、図７に示す組織を備えた編地によって図５に示す冷感生地１を作成した。
比較例として、市販の３種類のタオル生地（比較例１〜３）について、吸水性、保水性、紫外線遮蔽率及び接触冷温感に関する試験を日本繊維製品品質技術センターの中四国試験センターにて行い、その試験結果を表１に示した。
Hereinafter, examples will be shown to enhance the understanding of the present invention, but the present invention should not be understood only in this embodiment.
(Example 1)
A cooling sensation fabric shown in FIG. 5 using a deformed yarn (75D 144F) 75 denier 144 filament made of polyester fiber having an uneven fiber cross section shown in FIG. 8 and knitted fabric having the structure shown in FIGS. 6 and 7. 1 was created.
As a comparative example, three types of commercially available towel fabrics (Comparative Examples 1 to 3) were tested for water absorption, water retention, ultraviolet shielding rate, and cool contact feeling at the Chugoku-Shikoku Testing Center of the Japan Textile Product Quality Technology Center. The test results are shown in Table 1.
（乾燥性と温度の試験）
次に実施例１と比較例２とについて、乾燥性と温度の試験を行い、その結果を図１１に示した。
(Drying and temperature test)
Next, the drying property and temperature of Example 1 and Comparative Example 2 were tested, and the results are shown in FIG.
この試験は、室温２５．７℃、湿度６６％の室内にて、それぞれの長方形の生地について水道水で濡らした後、２５ｃｍ程度の長さに折りたたみ常法によって絞り動作（両端を持った左右の手を約１８０度回して絞る動作）を２回行なった後に、振る動作（広げたそれぞれの生地の左上端と右上端を左右の手で持って体の前方に広げ、両手を顔の高さまで上げた後に素早く手首を返しながら腕を振り下ろす動作）を６回行なった後、ハンガーに幅方向に沿って二つ折りにしてぶら下げて、試験開始時点（図１１（Ａ））から６３分経過（図１１（E））までのサーモグラフィーによる温度変化と触感による水分状態の変化を観察したものである。これらの図において、実施例１は右側aに配置され、比較例２は左側bに配置されている。 In this test, after wetting each rectangular cloth with tap water in a room with a room temperature of 25.7 ° C and a humidity of 66%, it is folded to a length of about 25 cm and squeezed by a conventional method (left and right with both ends). After performing the movement of squeezing by turning the hand about 180 degrees twice, the movement of shaking (holding the upper left and upper right edges of each spread fabric with the left and right hands and spreading them in front of the body, both hands to the height of the face After raising the wrist and swinging the arm down while quickly returning the wrist), fold it in half along the width direction and hang it on the hanger, and 63 minutes have passed since the start of the test (Fig. 11 (A)) (Fig. 11 (A)). It is the observation of the temperature change by thermography and the change of moisture state by tactile sensation up to FIG. 11 (E). In these figures, Example 1 is located on the right side a and Comparative Example 2 is located on the left side b.
試験開始時点（図１１（Ａ））：実施例１及び比較例２ともほぼ全体が濡れており、表面温度は約２１℃であった。
試験開始後４７分経過（図１１（Ｂ））：実施例１は全体が濡れており、表面温度は約２１℃であった。比較例２は上部の一部に乾燥が見られた。
試験開始後５３分経過（図１１（Ｃ））：実施例１は全体が濡れており、表面温度は約２１℃であった。比較例２は上半分に乾燥が見られ、当該部分の温度が約２４℃に上昇した。
試験開始後６０分経過（図１１（Ｄ））：実施例１は全体が濡れており、表面温度は約２１℃であった。比較例２は上部２／３に乾燥が見られ、当該部分の温度は約２４℃であった。
試験開始後６３分経過（図１１（Ｅ））：実施例１は全体が濡れており、表面温度は約２１℃であった。比較例２は略全体に乾燥が見られ、当該部分の温度が約２４℃であった。
実施例１と比較例２の温度変化のグラフを図１１（Ｅ）に示した。グラフ中、ａは実施例１の温度変化を示し、ｂは比較例２の温度変化を示す。
At the start of the test (FIG. 11 (A)): Almost all of Example 1 and Comparative Example 2 were wet, and the surface temperature was about 21 ° C.
47 minutes after the start of the test (FIG. 11 (B)): Example 1 was entirely wet and had a surface temperature of about 21 ° C. In Comparative Example 2, dryness was observed in a part of the upper part.
53 minutes after the start of the test (FIG. 11 (C)): Example 1 was entirely wet and had a surface temperature of about 21 ° C. In Comparative Example 2, drying was observed in the upper half, and the temperature of the portion rose to about 24 ° C.
60 minutes after the start of the test (FIG. 11 (D)): Example 1 was entirely wet and had a surface temperature of about 21 ° C. In Comparative Example 2, drying was observed in the upper two-thirds, and the temperature of the portion was about 24 ° C.
63 minutes after the start of the test (FIG. 11 (E)): Example 1 was entirely wet and had a surface temperature of about 21 ° C. In Comparative Example 2, drying was observed almost entirely, and the temperature of the portion was about 24 ° C.
Graphs of temperature changes of Example 1 and Comparative Example 2 are shown in FIG. 11 (E). In the graph, a shows the temperature change of Example 1, and b shows the temperature change of Comparative Example 2.
（冷感回復性の試験）
次に実施例１について、冷感回復性の試験を行った。
この試験は、前述の乾燥性と温度の試験と同様な室内で、実施例１の冷感生地をぬるま湯で濡らした後、乾燥性と温度の試験と同じく絞る動作（２回）と振る動作（６回）を行い、テスターの首にかけて両端をクロスさせた状態とし、テスターの体温で暖かくなった後に、振る動作（６回）を行ったもので、その温度変化の状態をサーモグラフィーで観察し、その結果を図１２に示した。
(Cold sensation recovery test)
Next, for Example 1, a cooling sensation recovery test was conducted.
In this test, the cold dough of Example 1 is wetted with lukewarm water in the same room as the above-mentioned dryness and temperature test, and then squeezed (twice) and shaken (twice) as in the dryness and temperature test. 6 times) was performed, and both ends were crossed around the neck of the tester, and after warming up with the body temperature of the tester, the shaking motion (6 times) was performed, and the state of the temperature change was observed by thermography. The result is shown in FIG.
図１２（Ａ）：実施例１の冷感生地をぬるま湯で濡らして広げた状態を示すもので、生地の略全面が高温（薄白色）となっていることが示されている。
図１２（Ｂ）：絞る動作（２回）と振る動作（６回）を行なって生地を広げた状態を示すもので、生地の略全面が低温（濃厚色）となっていることが示されている。
図１２（Ｃ）：生地をテスターの首にかけて両端をクロスさせた当初の状態を示すもので、生地の略全体が低温（濃厚色）であることが示されている。
図１２（Ｄ）：生地がテスターの体温で暖かくなった状態を示すもので、テスターの手より上では、生地の略全体が高温（薄白色）であることが示されている。
図１２（Ｅ）：生地をテスターの首からはずして広げた状態を示すもので、生地の上部約２／３では高温（薄白色）であることが示され、下部約１／３では低温（濃厚色）であることが示されている。
図１２（Ｆ）（Ｇ）：再度振る動作（６回）を行なっている状態と、これを広げた状態を示すもので、生地の略全面が低温（濃厚色）に戻っていることが示されている。
以上のように本考案の冷感生地は、着用開始後に体温で温かくなってしまっても、振ることによって冷感効果が回復することが確認されたものである。
FIG. 12A: shows a state in which the cooling sensation fabric of Example 1 is wetted with lukewarm water and spread out, and it is shown that substantially the entire surface of the fabric is hot (light white).
FIG. 12B: A state in which the dough is spread by performing a squeezing operation (2 times) and a shaking operation (6 times), and it is shown that substantially the entire surface of the dough is at a low temperature (dark color). ing.
FIG. 12 (C): Shows the initial state in which the dough is hung on the neck of the tester and both ends are crossed, and it is shown that substantially the entire dough is at a low temperature (dark color).
FIG. 12 (D): shows a state in which the dough is warmed by the body temperature of the tester, and it is shown that substantially the entire dough is hot (light white) above the hands of the tester.
FIG. 12 (E): The state in which the dough is removed from the neck of the tester and spread out is shown. The upper part of the dough is shown to be hot (light white), and the lower part is shown to be cold (light white). It is shown to be a dark color).
FIGS. 12 (F) (G): Shows a state in which the shaking operation (6 times) is performed again and a state in which the shaking operation is performed, and shows that substantially the entire surface of the fabric has returned to a low temperature (dark color). Has been done.
As described above, it has been confirmed that the cooling sensation fabric of the present invention recovers the cooling sensation effect by shaking even if it becomes warm at body temperature after the start of wearing.
（スポーツウェアのサーモグラフィー試験）
図２に示すスポーツウェアについて、サーモグラフィーによる簡易試験を行った。冷感生地１には実施例１に係る生地を用い、身頃生地３にはポリエステル繊維による吸汗速乾素材の生地を用いた。
試験は、気温約２７℃の室内にて、地肌に直接スポーツウェアを着用し、霧吹きにて水を全体に噴霧し、約２０分経過後にスポーツウェアの胸を掴んで、５回前後に振る動作を行ない、図１３に示すサーモグラフィーによって、表面温度を確認した。その結果、前身頃のみぞおち部分では、２５．８℃の低温となっていることが確認されると共に、胸から肩にかけての部分（上記の振る動作を行うことで生地が動いた部分）でも同程度の温度となっていることがサーモグラフィーの色彩によって確認された。
冷感生地１の部分は霧吹き後２０分経過しても適度に保水し、掴んで振ったあとは気化作用で温度が下がるが、身頃生地３の部分は吸汗速乾素材のため、急速に乾いていることが確認された。
従って、運動中であれば発汗により、冷感生地１の部分は吸水し続けるので、効果は継続的に続くと考えられる。
(Sportswear thermography test)
The sportswear shown in FIG. 2 was subjected to a simple thermographic test. The fabric according to Example 1 was used as the
In the test, the sportswear is worn directly on the skin in a room with a temperature of about 27 ° C, water is sprayed over the entire surface by spraying, and after about 20 minutes, the chest of the sportswear is grasped and shaken about 5 times. The surface temperature was confirmed by the thermography shown in FIG. As a result, it was confirmed that the temperature of the epigastrium of the front body was as low as 25.8 ° C, and the same was true for the part from the chest to the shoulders (the part where the fabric moved by performing the above shaking motion). It was confirmed by the color of the thermography that the temperature was about the same.
The part of the
Therefore, during exercise, the part of the
（スポーツウェアとファンウエアのサーモグラフィー試験）
図２に示すスポーツウェアをファンウェアとの組み合わせて、サーモグラフィーによる簡易試験を行った。冷感生地１には実施例１に係る生地を用い、身頃生地３にはポリエステル繊維による吸汗速乾素材の生地を用いた。その上に、市販のファンウエアを着用した。
まず図１４（Ａ）に示すように、外気温約36℃の日陰において、地肌に直接スポーツウェアを着用して、その温度を測定したところ、その表面温度は外気温とほぼ等しい約36℃であった。
次に図１４（Ｂ）に示すように、スポーツウェアの上からファンウェアを着て後身頃下部の左右の空調ファンを作動させ、約１０分経過後に、ファンウェアの後身頃の表面温度を確認したところ、３７．５ ℃であったが、サーモグラフィーの色彩から肩を中心に温度が下がっていることが視認された。
最後に図１４（Ｃ）に示すように、ファンウェアの着用後約１５分経過後に、ファンウェアを脱いで、スポーツウエアの温度を確認した。図１４（Ｃ）の左側に示す前身頃では３２．５℃であり、図１４（Ｃ）の右側に示す後身頃では３２．７℃であった。
スポーツウエアの冷感生地１の部分は長時間保水し続けるので、 効果は継続的に続くと考えられる。また、襟にも冷感生地１を使うことにより、ファンウェアの吹き出し口と相まって首廻りが冷やされ、効果的に冷感を維持することが出来る。
(Sportswear and fanwear thermography test)
A simple test by thermography was performed by combining the sportswear shown in FIG. 2 with fanwear. The fabric according to Example 1 was used as the
First, as shown in FIG. 14 (A), in the shade of an outside air temperature of about 36 ° C., when sportswear was worn directly on the skin and the temperature was measured, the surface temperature was about 36 ° C., which is almost equal to the outside air temperature. there were.
Next, as shown in FIG. 14 (B), the fan wear is worn over the sportswear to operate the left and right air-conditioning fans at the bottom of the back body, and after about 10 minutes, the surface temperature of the back body of the fan wear is confirmed. As a result, the temperature was 37.5 ° C, but it was visually recognized from the color of the thermography that the temperature had dropped mainly on the shoulder.
Finally, as shown in FIG. 14 (C), about 15 minutes after wearing the fan wear, the fan wear was taken off and the temperature of the sports wear was confirmed. The temperature of the front body shown on the left side of FIG. 14 (C) was 32.5 ° C, and that of the rear body shown on the right side of FIG. 14 (C) was 32.7 ° C.
Since the
１ 冷感生地
２ メッシュ生地
３ 身頃生地
１１ 編糸
１２ 繊維凹部
１３ 繊維凸部
２０ 編地
２１ 凹部
２２ 凸部
２３ 環状部
２４ 密集部
1 Cold feeling fabric 2
Claims (6)
前記冷感生地は、滴下法による吸水性試験結果が２秒未満の吸水性であり、保水性試験結果が１８０％〜２１０％の保水率であり、
前記冷感生地を構成する構成糸の接触冷感値（ＱＭＡ×値）が０．２８W/cm２以上のポリエステル繊維糸であり、
前記冷感生地が着用者の皮膚を覆う領域に配置されたことを特徴とする冷感装着品。 Equipped with a cool fabric with high water absorption and water retention
The cooling sensation fabric has a water absorption test result of less than 2 seconds by the dropping method, and a water retention test result of 180% to 210%.
It is a polyester fiber yarn having a contact cooling sensation value (QMA × value) of 0.28 W / cm 2 or more of the constituent yarns constituting the cooling sensation fabric.
A cooling sensation wearing product, characterized in that the cooling sensation fabric is arranged in an area covering the wearer's skin.
前記構成糸として、繊維断面が凹凸を備えたポリエステル繊維製の異形糸を用い、
前記編地は少なくとも表面側に凸部を備え、
前記凸部は、３本以上の前記編糸が密接する部分を備えると共に、平面視において環状部が並べられた並列形態を備え、
ことを特徴とする請求項１又は２に記載の冷感装着品。 The cold-feeling fabric is a knitted fabric using the constituent yarns as knitting yarns.
As the constituent yarn, a deformed yarn made of polyester fiber having an uneven fiber cross section is used.
The knitted fabric has a convex portion at least on the surface side.
The convex portion includes a portion in which three or more of the knitting yarns are in close contact with each other, and also has a parallel form in which annular portions are arranged in a plan view.
The cold feeling wearing product according to claim 1 or 2.
前記上衣の前身頃は、首回りから胸にかけて前記冷感生地が配置され、
前記アンダーウェアの後身頃は、首回りから肩甲骨の間にかけて前記冷感生地が配置され、且つ、この後身頃の前記冷感生地の下から下方に向けて前記冷感生地よりも通気性の高いメッシュ生地が配置されていることを特徴とする請求項１〜４の何れかに記載の冷感装着品。 The cold feeling wearing item is an underwear or sportswear top.
On the front body of the upper garment, the cold feeling fabric is arranged from around the neck to the chest.
In the back body of the underwear, the cooling sensation fabric is arranged from around the neck to between the shoulder blades, and the cooling sensation fabric is more breathable than the cooling sensation fabric from the bottom to the bottom of the back body. The cold feeling wearing product according to any one of claims 1 to 4, wherein a high mesh fabric is arranged.
前記ファンウエアは、左右の体側に外部の空気を内部に送る空調ファンを備え、
前記空調ファンの間に前記メッシュ生地が位置するものであり、
前記空調ファンによって送られた空気の少なくとも一部が、前記メッシュ生地から前記冷感生地を通って前記首回りから外部に抜けるように導くことを特徴とする冷感装着品とファンウエアの組み合わせ。
The cold feeling wearing product according to claim 5 and the fan wear to be worn on the cold feeling wearing product are provided.
The fan wear is equipped with an air-conditioning fan that sends external air to the inside on the left and right body sides.
The mesh fabric is located between the air conditioning fans.
A combination of a cooling sensation wearing product and fan wear, characterized in that at least a part of the air sent by the air conditioning fan is guided from the mesh fabric through the cooling sensation fabric to the outside from the neck circumference.