JP3229694B2 - Recording medium with magnetic pattern - Google Patents
Recording medium with magnetic patternInfo
- Publication number
- JP3229694B2 JP3229694B2 JP03264093A JP3264093A JP3229694B2 JP 3229694 B2 JP3229694 B2 JP 3229694B2 JP 03264093 A JP03264093 A JP 03264093A JP 3264093 A JP3264093 A JP 3264093A JP 3229694 B2 JP3229694 B2 JP 3229694B2
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- recording medium
- pattern
- magnetic pattern
- bar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、記録媒体に関し、特に
偽造、改ざんを容易に検出し、また、防止することがで
きる磁気パターンを持った記録媒体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a recording medium, and more particularly to a recording medium having a magnetic pattern capable of easily detecting and preventing forgery and tampering.
【０００２】[0002]
【従来の技術】従来、磁気カード等の記録媒体におい
て、磁性材料によって不正使用を防止する（真偽判定
用）ためのバーコード状の磁気パターンを形成し、これ
を磁気センサ等で検出し、検出した情報によって該媒体
の真偽の判定を行い不正使用を防止するようにしてい
る。2. Description of the Related Art Conventionally, in a recording medium such as a magnetic card, a bar code-like magnetic pattern for preventing unauthorized use (for authenticity determination) is formed by a magnetic material, and this is detected by a magnetic sensor or the like. The authenticity of the medium is determined based on the detected information to prevent unauthorized use.
【０００３】このようなバーコード状の磁気パターンに
おいて、磁気パターンを構成する磁性材料の保磁力が高
い場合（例えば、磁性材料として、保磁力が約３００エ
ルステッドのγ−Ｆｅ2 Ｏ3 を用いることができる。）
に、一度外部磁界を印加すると磁気パターンの両端に残
留磁化が生じ、市販されているマグネティックテープビ
ュアーや「ＭＡＧＮＡ−ＳＥＥ」（登録商標、a produc
t of CBS RECORDS）等の磁気現像手段を用いることによ
って、容易に磁気パターンの両端の残留磁化を目視可能
な状態とすることができるために、磁気パターンの（磁
気パターンのエッジ部に生じる出力の大きさ及びピッチ
によって表される真偽判定用の）情報の検出後に毎回消
磁を行っていたが、システムの複雑化を招くという問題
があった。In such a bar-code-shaped magnetic pattern, when the magnetic material constituting the magnetic pattern has a high coercive force (for example, γ-Fe 2 O 3 having a coercive force of about 300 Oersted is used as the magnetic material). Can be.)
The, once across the resulting residual magnetization of the magnetic pattern when the external magnetic field to mark pressure, magnetic tapes viewer and "MAGNA-SEE" is commercially available (R, a produc
By using magnetic developing means such as t of CBS RECORDS, the residual magnetization at both ends of the magnetic pattern can be easily made visible, so that the output of the magnetic pattern Degaussing has been performed every time information (for authenticity determination represented by size and pitch) is detected, but there is a problem that the system becomes complicated.
【０００４】上述のような磁気パターンに生じる残留磁
化を消磁することのないバーコード状の磁気パターンを
得ることは、例えば、本出願人の出願に係る特開平１−
１０９５２４号に開示されているように、磁気パターン
を構成する磁性材料を３０エルステッド以下とすること
で、消磁することのない磁気パターンを得ることができ
るが、この保磁力を３０エルステッド以下とした磁気パ
ターンは磁気ヘッドに直流バイアスをかけながら読み取
ることができるため、より高度の偽造、改ざんを防止す
ることが可能で、セキュリティ性の高いバーコード状の
磁気パターンの開発が望まれている。[0004] Obtaining a bar-code-like magnetic pattern without demagnetizing the residual magnetization generated in the magnetic pattern as described above is disclosed, for example, in Japanese Patent Application Laid-Open No. HEI 1 (1998) -111, filed by the present applicant.
As disclosed in Japanese Patent No. 109524, a magnetic pattern without demagnetization can be obtained by setting the magnetic material constituting the magnetic pattern to 30 Oe or less, but the coercive force is set to 30 Oe or less. Since the pattern can be read while applying a DC bias to the magnetic head, it is possible to prevent a higher degree of forgery or falsification, and it is desired to develop a barcode-like magnetic pattern having high security.
【０００５】[0005]
【発明が解決しようとする課題】上記のようにバーコー
ド状の磁気パターンを形成する磁性材料の保磁力が、或
る程度高い場合には、磁気パターンの両端の残留磁化を
前述の磁気現像手段によって目視可能とすることがで
き、磁性材料の保磁力が低い場合には、磁気パターンを
直流バイアスを印加した磁気ヘッドで走査することで読
み取ることができ、いずれの場合でも、そのバーコード
状の磁気パターンのエッジ部のみに生じる出力レベルお
よび、その間隔によって表される情報を真偽判定用の情
報として用いているので、その情報を読み取ることによ
って比較的容易に偽造、改ざんされる恐れがあった。As described above, when the coercive force of the magnetic material forming the bar code-like magnetic pattern is somewhat high, the residual magnetization at both ends of the magnetic pattern is reduced by the magnetic developing means. be a visible way, if the coercive magnetic force of the magnetic material is low, can be read by scanning a magnetic head in which a magnetic pattern to mark pressurizing a DC bias, in any case, the bar code Since the output level generated only at the edge of the magnetic pattern and the information represented by the interval are used as the information for judging the authenticity, the information may be read and forged or falsified relatively easily. was there.
【０００６】本発明は、上述の従来の問題点を解消しよ
うとするものであり、その目的は、簡単な構成でセキュ
リティ性の高い磁気パターンを持った記録媒体を提供す
ることにある。An object of the present invention is to solve the above-mentioned conventional problems, and an object of the present invention is to provide a recording medium having a simple configuration and a magnetic pattern having high security.
【０００７】[0007]
【課題を解決するための手段】本発明によれば、磁気パ
ターンを持った記録媒体において、磁気パターンを構成
する磁気バーの少なくとも１つは、断面形状が磁性材料
によって凹凸を有するように形成され、磁気パターンを
構成する磁気バーは、その形状変化点を検出されるもの
である。また、その不正使用防止手段としては、磁気パ
ターンを持った記録媒体において、磁気パターンを構成
する磁気バーの少なくとも１つは、断面形状が磁性材料
によって凹凸を有するように形成され、磁気パターンを
構成する磁気バーの形状変化点に生じる出力レベル及び
出力間隔の組み合わせが、少なくとも真偽判定用の情報
の一部を構成していることにより、不正使用を防止する
ものである。According to the present invention, in a recording medium having a magnetic pattern, at least one of the magnetic bars constituting the magnetic pattern is formed so that the cross-sectional shape thereof is made of a magnetic material so as to have irregularities. , The magnetic bar that constitutes the magnetic pattern , the shape change point of which is detected
It is. As a means for preventing unauthorized use, in a recording medium having a magnetic pattern, at least one of the magnetic bars constituting the magnetic pattern is formed so that the cross-sectional shape is made of a magnetic material so as to have irregularities. Output level at the shape change point of the magnetic bar
The combination of output intervals is at least information for true / false judgment
, Prevents unauthorized use.
【０００８】[0008]
【作用】従って、バーコード状の磁気パターンを形成す
る磁性材料の保磁力が高い場合、もしくは低い場合で
も、そのバーコード状の磁気パターンを構成する磁気バ
ーのエッジ部のみに生じる出力レベル及び、その間隔に
よって表される情報に加えて、磁気バーの形状変化点に
生じる出力レベル及び、その間隔を組み合わせることに
よって真偽判定用の情報としているので、従来、知られ
ているように磁気バーのエッジ部にのみに生じる出力レ
ベル及び、その間隔によって表される情報だけでは、そ
の記録媒体を偽造、改ざんすることができない。Therefore, even when the coercive force of the magnetic material forming the bar code magnetic pattern is high or low, the output level generated only at the edge of the magnetic bar forming the bar code magnetic pattern, and In addition to the information represented by the interval, the output level generated at the shape change point of the magnetic bar and the interval are used as information for authenticity determination. The recording medium cannot be falsified or falsified only by the output level generated only at the edge portion and the information represented by the interval.
【０００９】[0009]
【実施例】次に本発明による記録媒体の実施例を図面を
用いて説明する。尚、この実施例で例示してある磁気バ
ーは、保磁力が３０エルステッド以下の磁性材料を用い
て磁気バーを形成した場合についての説明である。Next, an embodiment of a recording medium according to the present invention will be described with reference to the drawings. The magnetic bar illustrated in this embodiment is an example in which the magnetic bar is formed using a magnetic material having a coercive force of 30 Oe or less.
【００１０】図１（ａ）には、本発明による記録媒体に
形成される磁気バー１０の断面形状の一例が示されてい
る。同図に示されるように磁気バー１０は、２つの凸部
１２および１４を有するように形成されている。２つの
凸部１２および１４に挟まれた部分は、略一定の高さに
形成されている。本発明の記録媒体は、このような磁気
バー１０によって、図２に示すように磁気パターン２０
が形成されている。FIG. 1A shows an example of a cross-sectional shape of a magnetic bar 10 formed on a recording medium according to the present invention. As shown in the figure, the magnetic bar 10 is formed to have two convex portions 12 and 14. The portion sandwiched between the two convex portions 12 and 14 is formed at a substantially constant height. The recording medium of the present invention uses such a magnetic bar 10 to form a magnetic pattern 20 as shown in FIG.
Are formed.
【００１１】上記の磁気バー１０は、直流バイアスを印
加した磁気ヘッド（図示しない）で読み取ると、図１
（ｂ）に示すように、２つの凸部すなわち２つの山１２
および１４の両端（形状変化点）の位置に対応する出力
を得ることができる。従って、所定の値のしきい値Ｓを
設定することによって、４つの出力を直流バイアスを印
加した磁気ヘッドにより読み取る（検出）ことができ
る。[0011] The magnetic bar 10 described above, reads a sign a DC bias <br/> pressurized the magnetic head (not shown), Fig. 1
As shown in (b), two convex portions, that is, two peaks 12 are formed.
And 14 corresponding to the positions of both ends (shape change points). Therefore, by setting the threshold S of a predetermined value, it is possible to read the four magnetic heads marked <br/> pressurizing a DC bias output (detection).
【００１２】図３（ａ）に示すような、従来の形状の磁
気バーは、略一つの山の形状（磁気バーの形状変化点が
ない）に形成されているから、図３（ｂ）に示すように
直流バイアスを印加した磁気ヘッド（図示しない）で読
み取った場合の出力は、磁気バーのエッジ部のみの２つ
となる。この出力は、磁気バーのエッジ部の位置に対応
しているから、単に直流バイアスを印加した磁気ヘッド
で読み取ることによって、磁気パターンの情報を読み取
ることが行え、偽造、改ざんされる可能性をもってい
た。The magnetic bar having the conventional shape as shown in FIG. 3A is formed in a substantially single mountain shape (there is no change in the shape of the magnetic bar). output when read by a DC bias indicia pressurized with magnetic head (not shown) as shown are made two and only the edge portion of the magnetic bar. This output, because they correspond to the position of the edge portion of the magnetic bars, simply by reading a magnetic head having indicia pressure to the DC bias, can be read the information of the magnetic pattern, with forgery, the possibility of tampering Was.
【００１３】図１に示すように本実施例によれば、上述
のように４つの出力が検出され、これらの出力の中で磁
気バー内の形状変化点の出力をも真偽判定用の情報とし
て用いていることを知らなければ、記録媒体の磁気パタ
ーンの情報を正確に読み取ることが困難となり偽造、改
ざんを有効に防止することができる。As shown in FIG. 1, according to this embodiment, four outputs are detected as described above, and among these outputs, the output of the shape change point in the magnetic bar is also used as information for authenticity determination. If it is not known that the information is used, it is difficult to accurately read the information on the magnetic pattern of the recording medium, and forgery and falsification can be effectively prevented.
【００１４】図４（ａ）には、本発明による記録媒体に
形成される磁気バーの断面形状の他の例が示されてい
る。同図に示されるものは、磁気バー１０の中央部に凸
部１６が形成されている。この磁気バー１０を、直流バ
イアスを印加した磁気ヘッド（図示しない）で読み取る
と、図４（ｂ）に示すように、磁気バー１０のエッジ部
に加えて中央部の凸部１６（形状変化点）の位置に対応
する出力を得ることができる。従って、所定の値のしき
い値Ｓを設定することによって、４つの出力を直流バイ
アスを印加した磁気ヘッドにより読み取る（検出）こと
ができる。FIG. 4A shows another example of the cross-sectional shape of the magnetic bar formed on the recording medium according to the present invention. The projection shown in FIG. 1 is formed at the center of the magnetic bar 10. The magnetic bar 10, reads the DC bias indicia pressurized with magnetic head (not shown), as shown in FIG. 4 (b), the convex portion 16 (the shape change of the central portion in addition to the edge portion of the magnetic bars 10 The output corresponding to the position of (point) can be obtained. Therefore, by setting the threshold S of a predetermined value, it is possible four output read by magnetic head indicia pressurizing a DC bias (detection).
【００１５】尚、本発明の記録媒体に用いることのでき
る磁気バーの形状は、図４（ａ）に示すように凸部が１
つ形成されたもの、図１（ａ）に示すように凸部が２つ
形成されたものの他、磁気バーの形状（幅）が広くな
く、目視により一つの磁気バーとして認識できる程度の
形状（幅、大きさ）であれば、凸部が３つ以上形成され
たものでも、図５に示すように段差を設けたような形状
に形成されたものでもよく。パターンとしては、これら
の任意の組み合わせを用いることができる。また、磁気
バーの幅としては０．１〜数ｍｍ、望ましくは０．５〜
２ｍｍの範囲に形成することができる。Incidentally, the shape of the magnetic bar which can be used for the recording medium of the present invention is as shown in FIG.
1 (a), two convex portions are formed as shown in FIG. 1 (a), and the shape (width) of the magnetic bar is not wide, and the shape is such that it can be visually recognized as one magnetic bar ( (Width, size), it may be formed with three or more convex portions, or may be formed in a shape having a step as shown in FIG. Any combination of these can be used as the pattern. Further, the width of the magnetic bar is 0.1 to several mm, preferably 0.5 to
It can be formed in a range of 2 mm.
【００１６】本発明の記録媒体は、上述のような磁気バ
ー１０のみの組み合わせによって磁気パターン２０を形
成してもよいし、上述のような磁気バー１０と図３
（ａ）に示すような従来の磁気バー１０との組み合わせ
によって磁気パターン２０を形成してもよい。さらに、
磁気バーに似せた非磁性のダミーバーを組み合わせて磁
気パターン２０を形成することもできる。In the recording medium of the present invention, the magnetic pattern 20 may be formed by combining only the magnetic bar 10 as described above, or the magnetic bar 10 as described above and FIG.
The magnetic pattern 20 may be formed by a combination with a conventional magnetic bar 10 as shown in FIG. further,
The magnetic pattern 20 can also be formed by combining non-magnetic dummy bars that resemble magnetic bars.
【００１７】次に、本発明の記録媒体を磁気カードに適
用した場合について説明する。Next, a case where the recording medium of the present invention is applied to a magnetic card will be described.
【００１８】本発明の記録媒体の基材としては、紙、Ｐ
ＥＴ、ＰＶＣ、ＰＣの単体およびこれらを適宜組み合わ
せたフィルム状の合成紙等を用いることができ、この基
材上の表面または裏面に直接パターンを設けてもよい
し、基材上の表面または裏面に磁気記録層（保磁力が３
００〜３０００エルステッドの磁気インキをコーティン
グしたもの）が形成され、その磁気記録層上にパターン
を設けてもよい。As the base material of the recording medium of the present invention, paper, P
ET, PVC, PC alone or a film-like synthetic paper obtained by appropriately combining them may be used. A pattern may be directly provided on the front or back surface of the base material, or the front or back surface of the base material may be used. The magnetic recording layer (coercivity is 3
(A magnetic ink coated from 0.00 to 3000 Oe), and a pattern may be provided on the magnetic recording layer.
【００１９】磁気バーの形成を一度の印刷で行う場合に
は、粘度が１５０ポイズ以上の磁気インキをシルクスク
リーン印刷することにより得ることができる。磁気イン
キの組成としては、 バインダ用樹脂 （ＶＡＧＨ：ＵＣＣ社製） １５ 重量部 シルクシンナー （シクロヘキサノン：ブチルセロソルブ＝１：１） ３０ 重量部 磁性材料 （カルボニル鉄粉） ５０ 重量部 に増粘剤を添加し粘度が１５０ポイズ以上となるように
調整した。When the magnetic bar is formed by one printing, it can be obtained by silk-screen printing a magnetic ink having a viscosity of 150 poise or more. The composition of the magnetic ink is as follows. Binder resin (VAGH: manufactured by UCC) 15 parts by weight Silk thinner (cyclohexanone: butyl cellosolve = 1: 1) 30 parts by weight Adds a thickener to 50 parts by weight of magnetic material (carbonyl iron powder) The viscosity was adjusted to be 150 poise or more.
【００２０】この他に用いることのできるバインタ用樹
脂としては、アルキッド系樹脂、ビニル系樹脂およびポ
リウレタン系樹脂の単体もしくはこれらの混合系等を用
いることができる。また、磁性材料としては、保磁力が
３０エルステッド以下の材料として、Ｃｕ−Ｚｎフェラ
イト、Ｍｕ−ＺｎフェライトまたはＮｉ−Ｚｎフェライ
ト等の軟磁性金属微粉末、Ｍｏ−パーマロイまたはセン
ダスト等の軟磁性合金微粉末なども用いることができ
る。これらの組成比は、例示した重量部と略同じ組成比
によって用いることができる。As the other binder resins that can be used, alkyd resins, vinyl resins and polyurethane resins can be used alone or in combination. The magnetic material may be a material having a coercive force of 30 Oe or less, a soft magnetic metal powder such as Cu-Zn ferrite, Mu-Zn ferrite or Ni-Zn ferrite, or a soft magnetic alloy fine powder such as Mo-permalloy or Sendust. Powder and the like can also be used. These composition ratios can be used in substantially the same composition ratio as the exemplified parts by weight.
【００２１】保磁力が３００エルステッド以上の磁性材
料としては、Ｂａ−フェライト、Ｓｒ−フェライト、Ｃ
ｒＯ2 、Ｃｏ被着γ−Ｆｅ2 Ｏ3 およびγ−Ｆｅ2 Ｏ3
等の磁気記録材料を用いることができる。（この場合に
は、上述したように保磁力が低い場合と読み取り方法が
異なる。）さらに、上述の組成の磁気インキの印刷適性
等を向上させるために必要に応じて少量の分散剤（シリ
コーン系等の）を添加してもよい。As a magnetic material having a coercive force of 300 Oe or more, Ba-ferrite, Sr-ferrite, C
rO 2 , Co-coated γ-Fe 2 O 3 and γ-Fe 2 O 3
And other magnetic recording materials can be used. (In this case, the reading method is different from the case where the coercive force is low as described above.) Further, if necessary, a small amount of a dispersant (silicone-based Etc.) may be added.
【００２２】刷版は、図６にその断面を示すように、乳
剤３０の厚みが総厚（紗３２の厚み＋乳剤３０の厚み）
に対して約１／５以上であることを必要とする。このよ
うな刷版を用いてシルクスクリーン印刷を行うと、印刷
時には図７（ａ）に示すように紗３２がたわみ、形成さ
れる磁気バー１０は図７（ｂ）に示すように２つの山を
持ったような形状に印刷され、その磁気バー１０の形状
を保持するために印刷後１分以内に強制乾燥を行った。The printing plate has a total thickness (thickness of gauze 32 + thickness of emulsion 30) as shown in FIG.
About 1/5 or more. When silk screen printing is performed using such a printing plate, the gauze 32 bends during printing as shown in FIG. 7A, and the formed magnetic bar 10 has two peaks as shown in FIG. 7B. The magnetic bar 10 was subjected to forced drying within 1 minute after printing in order to maintain the shape of the magnetic bar 10.
【００２３】また、図８（ａ）に断面、（ｂ）に平面を
示すような２つの山を持った形状を得やすい刷版を用い
て、シルクスクリーン印刷を行うことによって図８
（ｃ）に示すように２つの山を持ったような形状に印刷
し、その磁気バー１０の形状を保持するために印刷後１
分以内に強制乾燥を行った。FIG. 8 (a) is a cross-sectional view, and FIG.
As shown in (c), printing is performed in a shape having two peaks, and after the printing, one
Forced drying was performed within minutes.
【００２４】上述の印刷によって得られた磁気バーを表
面荒さ試験機で、その表面形状を測定したところ、図９
に示すように２つの山を持ったような形状に印刷形成さ
れていることが測定され、その出力を特性試験機で測定
したところ図１０に示すような出力を得られることが確
かめられた。When the surface shape of the magnetic bar obtained by the above printing was measured by a surface roughness tester, the results were as shown in FIG.
It was measured that the print was formed in a shape having two peaks as shown in FIG. 10. When the output was measured by a characteristic tester, it was confirmed that an output as shown in FIG. 10 could be obtained.
【００２５】次に、上述で示した磁気インキの組成の磁
性材料を非磁性材料（カーボンブラック）に変え、その
他の材料および分量を同様の量として、ダミーパターン
を所定の位置にシルクスクリーン印刷により形成した。
このときのダミーインキの粘度は、そのパターン形状を
保持する必要がないので磁気インキのように１５０ポイ
ズ以上ではなく１００ポイズ程度（通常のシルクスクリ
ーン印刷用インキの粘度）でよい。Next, the magnetic material having the above-described composition of the magnetic ink is changed to a non-magnetic material (carbon black), and the other materials and the amounts are set to the same amounts. Formed.
At this time, the viscosity of the dummy ink is not required to be 150 poise or more as in magnetic ink, but may be about 100 poise (viscosity of ordinary silk screen printing ink) because it is not necessary to maintain the pattern shape.
【００２６】また、必要に応じてこれらのパターンを隠
蔽するための材料は従来知られている材料によって隠蔽
層および保護層（図示しない）を設けることもできる。As a material for concealing these patterns, if necessary, a concealing layer and a protective layer (not shown) can be provided by a conventionally known material.
【００２７】図１１（ａ）には、従来の凹凸のない磁気
バーと本発明の磁気バーおよびダミーバーを組み合わせ
た場合の読み取り方法の概略について説明するための磁
気カード５０の部分断面図である。FIG. 11A is a partial cross-sectional view of the magnetic card 50 for explaining the outline of the reading method when the conventional magnetic bar without unevenness is combined with the magnetic bar and the dummy bar of the present invention.
【００２８】まず、バイアス用コイル６１に２０〔ｍ
Ａ〕程度の直流バイアス電流を印加し、１０００エルテ
ッド程度の漏洩磁場を生じさせる。そして磁気カード５
０を図中の矢印方向に搬送して磁気パターンを走査し出
力を検出する。その際、出力のレベルの低下を防止する
ために、磁気ヘッド６のヘッドギャップと走査方向のパ
ターン（磁気バー１０およびダミーバー）の端片とが垂
直となるように位置させる。また、磁気カード５０の搬
送速度は、約４５ｃｍ／ｓｅｃとした。First, 20 [m] is applied to the bias coil 61.
And indicia pressure to the DC bias current of about A], causing leakage magnetic field of about 1000 Eruteddo. And magnetic card 5
0 is conveyed in the direction of the arrow in the figure to scan the magnetic pattern and detect the output. At this time, in order to prevent the output level from lowering, the head gap of the magnetic head 6 and the end piece of the pattern (magnetic bar 10 and dummy bar) in the scanning direction are positioned so as to be perpendicular. The transport speed of the magnetic card 50 was about 45 cm / sec.
【００２９】磁気カード５０が搬送され、磁気ヘッド６
が磁気バー１０上を通過すると、磁気的なカップリング
を起こし磁束が変化し、図１１（ｂ）に示すように磁気
バーの両端および形状変化点で検出コイル６２に出力電
圧が発生する。この出力電圧の出力成分を抽出したもの
を図１１（ｃ）に示す。The magnetic card 50 is conveyed, and the magnetic head 6
When magnetic flux passes over the magnetic bar 10, magnetic coupling occurs and the magnetic flux changes, and as shown in FIG. 11B, an output voltage is generated at the detection coil 62 at both ends of the magnetic bar and at the shape change point. FIG. 11C shows an extracted output component of the output voltage.
【００３０】上述のように得られた出力の間隔および出
力レベルの組み合わせによって、また図１１（ｃ）に示
すようにしきい値ＳおよびＳ’の設定およびその組み合
わせによっても任意の情報を真偽判定用の情報として用
いることができる。The arbitrary information is determined by the combination of the output intervals and the output levels obtained as described above, and also by the setting and combination of the thresholds S and S 'as shown in FIG. 11C. Can be used as information for
【００３１】[0031]
【発明の効果】本発明によれば、記録媒体に形成された
磁気パターンを構成する（ダミーパターンもしくはダミ
ーバーを含む）磁気バーの凹凸（形状変化点）によっ
て、磁気バーからの読み取り出力はその磁気バーの両端
に加えて磁気バー内の凹凸（形状変化点）でも出力が得
られ、これらを検出することによって偽造、改ざん等の
不正使用を防止することができる。According to the present invention, the read output from the magnetic bar is changed by the unevenness (shape change point) of the magnetic bar (including the dummy pattern or the dummy bar) constituting the magnetic pattern formed on the recording medium. An output can be obtained not only at both ends of the bar but also at irregularities (shape change points) in the magnetic bar, and by detecting these, illegal use such as forgery or falsification can be prevented.
【図１】本発明の磁気パターンを持った記録媒体に形成
される磁気バーとその読み取り出力の一例を示す図であ
る。FIG. 1 is a diagram showing an example of a magnetic bar formed on a recording medium having a magnetic pattern according to the present invention and its read output.
【図２】本発明の磁気パターンを持った記録媒体の外観
を示す図である。FIG. 2 is a diagram showing the appearance of a recording medium having a magnetic pattern according to the present invention.
【図３】従来の磁気パターンを持った記録媒体に形成さ
れる磁気バーとその読み取り出力の一例を示す図であ
る。FIG. 3 is a diagram showing an example of a magnetic bar formed on a recording medium having a conventional magnetic pattern and its read output.
【図４】本発明の磁気パターンを持った記録媒体に形成
される磁気バーとその読み取り出力の他の例を示す図で
ある。FIG. 4 is a diagram illustrating another example of a magnetic bar formed on a recording medium having a magnetic pattern according to the present invention and its read output.
【図５】本発明の磁気パターンを持った記録媒体に形成
される磁気バーの他の例を示す図である。FIG. 5 is a diagram showing another example of a magnetic bar formed on a recording medium having a magnetic pattern according to the present invention.
【図６】本発明の磁気パターンを持った記録媒体に形成
される磁気バーの形成に使用される刷版を示す図であ
る。FIG. 6 is a diagram showing a printing plate used for forming a magnetic bar formed on a recording medium having a magnetic pattern according to the present invention.
【図７】本発明の磁気パターンを持った記録媒体の磁気
バーの形成工程を示す図である。FIG. 7 is a diagram showing a process of forming a magnetic bar of a recording medium having a magnetic pattern according to the present invention.
【図８】本発明の磁気パターンを持った記録媒体の磁気
バーの他の形成工程を示す図である。FIG. 8 is a diagram showing another process of forming a magnetic bar of a recording medium having a magnetic pattern according to the present invention.
【図９】本発明の磁気パターンを持った記録媒体の磁気
バーの断面形状を示す図である。FIG. 9 is a diagram showing a cross-sectional shape of a magnetic bar of a recording medium having a magnetic pattern according to the present invention.
【図１０】本発明の磁気パターンを持った記録媒体の磁
気バーから得られる出力を示す図である。FIG. 10 is a diagram showing an output obtained from a magnetic bar of a recording medium having a magnetic pattern according to the present invention.
【図１１】本発明の磁気パターンを持った記録媒体に凹
凸のない磁気バーと有る磁気バーおよびダミーバーを組
み合わせた場合の読み取り方法の概略について説明する
ための図である。FIG. 11 is a diagram for explaining an outline of a reading method when a magnetic bar having no unevenness, a magnetic bar having a magnetic bar, and a dummy bar are combined with a recording medium having a magnetic pattern according to the present invention.
６ 磁気ヘッド １０ 磁気バー １２、１４、１６ 凸部 ２０ 磁気パターン ３０ 乳剤 ３２ 紗 ５０ 磁気カード ６１ バイアス用コイル ６２ 検出コイル Reference Signs List 6 magnetic head 10 magnetic bar 12, 14, 16 convex part 20 magnetic pattern 30 emulsion 32 gauze 50 magnetic card 61 bias coil 62 detection coil
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) G06K 19/06 G06K 19/10 G11B 5/09 301 G11B 5/80 G11B 11/20 B42D 15/10 ──────────────────────────────────────────────────続 き Continued on the front page (58) Field surveyed (Int. Cl. 7 , DB name) G06K 19/06 G06K 19/10 G11B 5/09 301 G11B 5/80 G11B 11/20 B42D 15/10
Claims (6)
て、前記磁気パターンを構成する磁気バーの少なくとも
１つは、断面形状が磁性材料によって凹凸を有するよう
に形成されていることを特徴とする磁気パターンを持っ
た記録媒体。1. A magnetic recording medium having a magnetic pattern, wherein at least one of the magnetic bars constituting the magnetic pattern is formed so that a cross-sectional shape thereof is uneven by a magnetic material. Recording medium with.
記録媒体において、前記磁気パターンを構成する磁気バ
ーの幅が同一もしくは異なることを特徴とする磁気パタ
ーンを持った記録媒体。2. The recording medium having a magnetic pattern according to claim 1, wherein the width of magnetic bars constituting the magnetic pattern is the same or different.
記録媒体において、前記磁気パターンを構成する磁気バ
ーの幅が異なるものが混在していることを特徴とする磁
気パターンを持った記録媒体。3. A recording medium having a magnetic pattern according to claim 1, wherein a plurality of recording media having different widths of magnetic bars constituting said magnetic pattern are mixed. .
記録媒体において、前記磁気パターンと、少なくとも非
磁性材料によって形成されたダミーパターンとの組み合
わせによってパターンが構成されていることを特徴とす
る磁気パターンを持った記録媒体。4. A recording medium having a magnetic pattern according to claim 1, wherein a pattern is constituted by a combination of the magnetic pattern and at least a dummy pattern formed of a non-magnetic material. A recording medium with a magnetic pattern.
て、前記磁気パターンを構成する磁気バーの少なくとも
１つは、断面形状が磁性材料によって凹凸を有するよう
に形成され、前記磁気パターンを構成する磁気バーは、その形状変化
点を検出されるものである ことを特徴とする磁気パター
ンを持った記録媒体。5. A recording medium having a magnetic pattern, wherein at least one of the magnetic bars constituting the magnetic pattern is formed so that a cross-sectional shape thereof has irregularities by a magnetic material, and the magnetic bar constituting the magnetic pattern is formed. Changes its shape
A recording medium having a magnetic pattern, wherein points are detected .
て、前記磁気パターンを構成する磁気バーの少なくとも
１つは、断面形状が磁性材料によって凹凸を有するよう
に形成され、前記磁気パターンを構成する磁気バーの形状変化点に生
じる出力レベル及び出力間隔の組み合わせが、少なくと
も真偽判定用の情報の一部を構成している ことを特徴と
する磁気パターンを持った記録媒体。6. In a recording medium having a magnetic pattern, at least one of the magnetic bars constituting the magnetic pattern is formed so that a cross-sectional shape thereof is uneven by a magnetic material, and the magnetic bar constituting the magnetic pattern is formed. At the shape change point of
The combination of output level and output interval
A recording medium having a magnetic pattern, wherein the recording medium also constitutes a part of information for authenticity determination .