JP3167586B2 - Flameproof curtain - Google Patents
Flameproof curtainInfo
- Publication number
- JP3167586B2 JP3167586B2 JP13505195A JP13505195A JP3167586B2 JP 3167586 B2 JP3167586 B2 JP 3167586B2 JP 13505195 A JP13505195 A JP 13505195A JP 13505195 A JP13505195 A JP 13505195A JP 3167586 B2 JP3167586 B2 JP 3167586B2
- Authority
- JP
- Japan
- Prior art keywords
- black
- carbon black
- polyester
- fiber
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、黒原着ポリエステル繊
維（以下、黒原着糸と称することがある）を構成繊維と
して含む暗幕に関する。さらに詳しくは、遮光性、黒度
及び防炎性能が共に良好な、黒原着糸を構成繊維として
含む防炎性暗幕に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a blackout curtain containing, as a constituent fiber, black-dyed polyester fiber (hereinafter sometimes referred to as black-dyed yarn). More specifically, the present invention relates to a flameproof blackout curtain having black-dyed yarn as a constituent fiber, having good light-shielding properties, blackness and flameproofing performance.
【０００２】[0002]
【従来の技術】従来暗幕は、例えば経糸又は緯糸の一方
に黒色糸を使用した朱子織、または互いに重なった２枚
の織物の一方が黒色糸からなる二重織で構成されてい
る。そしてその構成繊維としては、その機能性の面から
ポリエステル糸が広く用いられているが、ポリエステル
黒色糸としては糸染め糸（先染糸）に限定されているの
が実情である。2. Description of the Related Art Conventionally, a blackout curtain is constituted by, for example, satin weaving using black threads for one of a warp and a weft, or double weaving in which one of two overlapping fabrics is made of black threads. As the constituent fibers, polyester yarns are widely used from the viewpoint of their functionality, but the fact is that the polyester black yarns are limited to yarn-dyed yarns (yarn-dyed yarns).
【０００３】しかし、このような糸染めの黒色糸は、通
常パッケージ状態で染色されるため、糸条の収縮斑やパ
ーンの内外層における染色斑が発生し易い欠点がある。
このため、パッケージ形成時の巻取オーバーフィード率
を細心の注意を払って調整する必要があり、高コストの
ものとなることは避けられなかった。[0003] However, since such a black dyed yarn is usually dyed in a packaged state, there is a drawback that uneven spots in the yarn and uneven spots in the inner and outer layers of the pan are easily generated.
For this reason, it is necessary to adjust the take-up overfeed rate at the time of forming the package with great care, and it is unavoidable that the cost becomes high.
【０００４】一方コスト的、工程的に有利な黒色糸とし
て、カーボンブラックが配合された黒原着ポリエステル
繊維（黒原着糸）がある。しかしながら、カーボンブラ
ックが配合されたポリエステルは、カーボンブラックが
配合されていないポリエステルに比較して溶融粘度が高
くなるため、繊維に着火した際のドリップ効果、すなわ
ち着火周辺部のポリマーが熱によって低粘度化し着火部
分と共に落下して延焼を防止する効果が不足する欠点が
あり、かかる黒原着糸より得られる暗幕の防炎性能は不
充分となる（日本防炎協会発行 繊維と防炎 ２０５ペ
ージ）。On the other hand, as a black yarn which is advantageous in terms of cost and process, there is a black-dyed polyester fiber (black-dyed yarn) blended with carbon black. However, the polyester blended with carbon black has a higher melt viscosity than the polyester blended without carbon black, so the drip effect when the fiber is ignited, that is, the polymer around the ignition has a low viscosity due to heat There is a drawback that the effect of preventing the spread of fire by falling together with the ignited portion is insufficient, and the flameproofing performance of the blackout curtain obtained from such a black-colored yarn becomes insufficient (Fiber and Flameproofing, published by Japan Flame Protection Association, page 205).
【０００５】もちろん、カーボンブラックの配合量を単
に少なくするのみで充分なドリップ効果を得ることはで
きるが、反面このような黒原着糸は黒度、遮光性が不足
して暗幕用としては不適当になる。[0005] Of course, a sufficient drip effect can be obtained simply by reducing the blending amount of carbon black. However, such a black dyed yarn lacks blackness and light-shielding properties and is unsuitable for blackout screens. become.
【０００６】かかる黒原着糸の問題点を解消せんと、特
公平４―４４０２９号公報には、カーボンブラック配合
量の減少に基づく遮光性の低下を、酸化チタン配合で補
った暗幕用黒原着糸が提案されている。しかしながら、
この黒原着糸を用いて得られる暗幕は遮光性に優れてい
るものの、黒度が低下して鮮明感が不足する問題を有し
ていた。To solve the problem of the black dyed yarn, Japanese Patent Publication No. 4-44029 discloses a black dyed yarn for blackout curtain in which titanium oxide is used to compensate for a decrease in light-shielding properties due to a decrease in the amount of carbon black. Has been proposed. However,
Although the black curtain obtained by using this black dyed yarn has excellent light-shielding properties, it has a problem that the blackness is reduced and the sharpness is insufficient.
【０００７】一方、特公平５−７９１０３号公報には、
カーボンブラックの平均粒子径と吸油量、及びその揮発
分量を規定したポリエステル組成物が提案され、かかる
組成物はカーボンブラックの凝集による粗大粒子が少な
くなっているのでフィルムや繊維への成形性が向上する
とされている。しかし、本発明者等の検討によれば、こ
のような要件のみでは暗幕用黒原着糸としては不十分
で、黒度、遮光性を満足する程度までカーボンブラック
を含有させると防炎性が不十分になることが判明した。On the other hand, Japanese Patent Publication No. 5-79103 discloses that
A polyester composition has been proposed in which the average particle size, oil absorption, and volatile content of carbon black are specified, and such a composition has improved formability into a film or fiber because the number of coarse particles due to the aggregation of carbon black is reduced. It has been done. However, according to the studies by the present inventors, such requirements alone are not sufficient as a black dyed yarn for blackout curtains, and if carbon black is contained to such an extent that blackness and light-shielding properties are satisfied, flame retardancy is not sufficient. It turned out to be enough.
【０００８】[0008]
【発明が解決しようとする課題】本発明は、上記従来技
術を背景になされたもので、その目的は、ポリエステル
黒原着糸に起因する上記従来技術の欠点を解決した防炎
性暗幕を提供することにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned prior art, and an object of the present invention is to provide a flameproof blackout which solves the above-mentioned drawbacks of the prior art caused by a polyester black yarn. It is in.
【０００９】[0009]
【課題を解決するための手段】本発明者等は、上記目的
を達成するため鋭意検討した結果、カーボンブラックの
粒子径及び吸油量を規定するだけでは不十分で、さらに
粒子径と吸油量の間に特定の関係式を満足させたとき初
めて遮光性及び黒度を低下させることなくドリップ効果
を改善し得ることを見出し、さらに検討を重ねた結果、
本発明に到達した。Means for Solving the Problems The inventors of the present invention have conducted intensive studies to achieve the above object, and as a result, it is not sufficient to only specify the particle size and oil absorption of carbon black. It was found that the drip effect could be improved without lowering the light-shielding property and blackness only when a specific relational expression was satisfied, and as a result of further study,
The present invention has been reached.
【００１０】すなわち、本発明によれば、「黒原着ポリ
エステル繊維を構成繊維として含む暗幕において、前記
黒原着ポリエステル繊維は、下記〜式を同時に満足
するカーボンブラックを、繊維重量を基準として０．５
〜２．０重量％含有していることを特徴とする防炎性暗
幕」が提供される。 粒子径ｄ（ｎｍ）：１０≦ｄ≦４０ 吸油量Ｈ（ｍｌ／１００ｇ）：４０≦Ｈ≦９０ Ｈ≦８６−１．１５×１０-2ｄ2 本発明の特徴的な点は、次の要件を満足するカーボンブ
ラックをポリエステル中に含有させることにある。すな
わち、第１にカーボンブラックの粒子径は１０〜４０ｎ
ｍ、好ましくは１５〜３５ｎｍである必要がある。この
粒子径が１０ｎｍ未満の場合には、ポリエステルの溶融
粘度が増加しすぎて充分なドリップ効果を得ることがで
きなくなり、得られる暗幕の防炎性が不十分となる。逆
に４０ｎｍを越える場合には、ドリップ効果の点では満
足し得るものが得られるものの、暗幕の黒度又は遮光性
の点で不十分となる。That is, according to the present invention, in a blackout curtain containing black-dyed polyester fiber as a constituent fiber, the black-dyed polyester fiber is made of carbon black satisfying the following formulas at the same time: 0.5% based on the fiber weight.
To 2.0% by weight ". Particle size d (nm): 10 ≦ d ≦ 40 Oil absorption H (ml / 100 g): 40 ≦ H ≦ 90 H ≦ 86-1.15 × 10 −2 d 2 The characteristic points of the present invention are as follows. It is to contain carbon black satisfying the requirements in the polyester. That is, first, the particle diameter of carbon black is 10 to 40 n.
m, preferably 15 to 35 nm. When the particle size is less than 10 nm, the melt viscosity of the polyester is too high to obtain a sufficient drip effect, and the flame resistance of the obtained blackout curtain is insufficient. On the other hand, when the thickness exceeds 40 nm, a satisfactory drip effect can be obtained, but the blackness of the blackout or the light-shielding property becomes insufficient.
【００１１】第２にカーボンブラックの吸油量は４０〜
９０ｍｌ／１００ｇ、好ましくは５０〜８０ｍｌ／１０
０ｇである必要がある。この吸油量はカーボンブラック
乾燥試料１．００ｇを表面が平滑な石版石上にとり、ジ
ブチルフタレートを少量づつ滴下し、ステンレス製スパ
チュラーでよく練り合わせ、試料とジブチルフタレート
が１ヶの球状に形成される最低のジブチルフタレート量
を測定し、カーボンブラック１００ｇあたりのジブチル
フタレート量（ｍｌ）に換算することにより求められ
る。この吸油量が９０ｍｌ／１００ｇを越える場合に
は、このようなカーボンブラックはその粒子が特別な立
体構造を形成しているため、ポリエステル中に配合した
場合その溶融粘度を大きく増大させる結果、前記ドリッ
プ効果の点で不十分となって暗幕の防炎性が低下する。
一方、吸油量が４０ｍｌ／１００ｇ未満のカーボンブラ
ックは、凝集による粗大粒子の含有量が多くなるため黒
度及び遮光性が不十分になる等の欠点が発生する。Second, the oil absorption of carbon black is 40 to
90 ml / 100 g, preferably 50-80 ml / 10
It must be 0 g. This oil absorption was measured by taking 1.00 g of a dry sample of carbon black on a lithograph having a smooth surface, dripping dibutyl phthalate little by little, and kneading well with a stainless steel spatula. It is determined by measuring the amount of dibutyl phthalate and converting it to the amount of dibutyl phthalate (ml) per 100 g of carbon black. When the oil absorption exceeds 90 ml / 100 g, such carbon black particles have a special three-dimensional structure. Therefore, when incorporated in polyester, the melt viscosity of the carbon black greatly increases. The effect is insufficient and the flame resistance of the blackout curtain is reduced.
On the other hand, carbon black having an oil absorption of less than 40 ml / 100 g has disadvantages such as insufficient blackness and light-shielding properties due to an increased content of coarse particles due to aggregation.
【００１２】第３にカーボンブラックの粒子径と吸油量
との間には、式で表される関係を満足していること
が、暗幕の防炎性能と黒度、遮光性とを両立させるため
に必要である。吸油量が式を満たさずに大きい場合に
は、ポリエステルの溶融粘度が大きく増大するため防炎
性能が不十分となる。Thirdly, the relationship between the particle diameter of the carbon black and the oil absorption satisfies the relationship represented by the equation, which is necessary to achieve both the flameproofing performance of the blackout curtain, the blackness, and the light-shielding property. Is necessary for If the oil absorption is large without satisfying the formula, the melt viscosity of the polyester will be greatly increased, and the flameproofing performance will be insufficient.
【００１３】本発明におけるカーボンブラックは、上述
の三要件を同時に満足していれば、特にその製造法は限
定されない。カーボンブラックの製造方法としては、例
えば、ファーネス式不完全燃焼法、コンタクト式不完全
燃焼法、熱分解法等の方法が知られている。このうち、
本発明におけるカーボンブラックの製造方法としては、
カーボンブラック表面の官能基の生成を抑制して、カー
ボンブラック粒子が立体構造を形成するのを押さえる意
味から、ファーネス式不完全燃焼法が好ましい。The production method of the carbon black in the present invention is not particularly limited as long as the above three requirements are simultaneously satisfied. Known methods for producing carbon black include, for example, a furnace-type incomplete combustion method, a contact-type incomplete combustion method, and a pyrolysis method. this house,
As a method for producing carbon black in the present invention,
The furnace type incomplete combustion method is preferred from the viewpoint of suppressing the formation of functional groups on the carbon black surface and suppressing the formation of the three-dimensional structure of the carbon black particles.
【００１４】本発明における粒子径、吸油量を満足する
カーボンブラックを得るためには、上記ファーネス式不
完全燃焼法においては、例えば芳香族成分の少ない原料
油を使用する、油噴霧ノズルの噴霧角を小さくする、反
応温度を高めに設定するなどに留意すればよいが、もち
ろんこれらの方法に限定されるものではない。In order to obtain carbon black satisfying the particle diameter and oil absorption in the present invention, in the above furnace type incomplete combustion method, for example, a spray angle of an oil spray nozzle using a raw oil having a small aromatic component is used. , And the reaction temperature should be set higher. Of course, the present invention is not limited to these methods.
【００１５】上記カーボンブラックの黒原着糸における
含有量は、繊維重量を基準として０．５〜２重量％、好
ましくは０．８〜１．５重量％とする必要がある。含有
量が０．５重量％未満の場合には、充分な黒度が得られ
ず暗幕の遮光性能は不十分なものとなる。一方２重量％
を越える場合には、黒度の増加が頭打ちとなるばかりで
なく、上記〜式を同時に満足するカーボンブラック
を用いても溶融粘度の増加のために、暗幕の防炎性能が
不充分となるので避けるべきである。The content of the carbon black in the black dyed yarn must be 0.5 to 2% by weight, preferably 0.8 to 1.5% by weight, based on the weight of the fiber. When the content is less than 0.5% by weight, sufficient blackness cannot be obtained, and the light shielding performance of the blackout curtain becomes insufficient. 2% by weight
When the carbon black exceeds the above, not only does the increase in blackness level off, but even if carbon black that simultaneously satisfies the above formulas is used, the flameproofing performance of the blackout curtain becomes insufficient due to the increase in melt viscosity. Should be avoided.
【００１６】本発明において、上記カーボンブラックを
配合するポリエステルは、エチレンテレフタレートを主
たる繰返し単位とするポリエステルを対象とするが、第
３成分を少量（例えばテレフタル酸成分に対して２０モ
ル％以下、好ましくは１０モル％以下）共重合したもの
であってもよい。なかでも、エステル形成性官能基を２
個有するリン化合物を共重合したものは、防炎性能が一
段と改善されるのでより好ましい。ポリエステルの固有
粘度は、あまりに高すぎるとドリップ効果が低下して防
炎性能が不充分となる場合があるので、０．６〜０．８
の範囲が好ましい。In the present invention, the polyester blended with the carbon black is intended to be a polyester having ethylene terephthalate as a main repeating unit, but a small amount of a third component (for example, 20 mol% or less, preferably not more than 20 mol% based on a terephthalic acid component). May be 10 mol% or less). Among them, the ester-forming functional group is 2
Those obtained by copolymerizing phosphorus compounds having two or more phosphorus compounds are more preferable because the flameproofing performance is further improved. If the intrinsic viscosity of the polyester is too high, the drip effect may be reduced and the flameproofing performance may be insufficient.
Is preferable.
【００１７】ポリエステル繊維中に上記カーボンブラッ
クを配合するには特別な方法を採用する必要はなく、例
えばポリエステルの重合工程で加える方法、マスターペ
レット化したのちベースポリエステルと混練する方法、
カーボンブラックと液状ポリエステルとをあらかじめ混
合した液状の着色剤を紡糸直前の溶融ポリエステル流中
にギアポンプ等で計量しながら注入添加した後静的ある
いは動的に混練分散を行う方法等があげられる。なかで
も紡糸装置の汚染や取り扱い性、コスト等を考慮すると
マスターペレットによる方法が最も一般的であると言え
る。いずれの方法であっても配合後は公知の溶融紡糸方
法によって繊維化することができる。その際の繊維断面
形状は任意であり、丸断面繊維、異形断面繊維、中空繊
維等いずれであってもよい。It is not necessary to employ a special method for blending the above carbon black into the polyester fiber. For example, a method of adding the carbon black in a polyester polymerization step, a method of forming a master pellet and kneading it with a base polyester,
A method in which a liquid colorant obtained by previously mixing carbon black and a liquid polyester is injected into a molten polyester stream just before spinning while being measured by a gear pump or the like, and then statically or dynamically kneaded and dispersed. Among them, the method using master pellets can be said to be the most common in consideration of the contamination of the spinning device, the handling property, the cost, and the like. In any case, after blending, fiberization can be performed by a known melt spinning method. The fiber cross-sectional shape at that time is arbitrary, and may be any of a round cross-section fiber, a modified cross-section fiber, and a hollow fiber.
【００１８】また、本発明においては黒原着ポリエステ
ル繊維中に、上記カーボンブラックの他に艶消剤、制電
剤、蛍光増白剤、吸湿剤、紫外線吸収剤、光安定剤、抗
菌剤等の改質剤や機能性付与剤が、本発明の効果を損な
わない範囲で含有されていてもよい。Further, in the present invention, in addition to the above carbon black, a black matting polyester, an antistatic agent, a fluorescent whitening agent, a hygroscopic agent, an ultraviolet absorber, a light stabilizer, an antibacterial agent, etc. A modifier and a function-imparting agent may be contained within a range that does not impair the effects of the present invention.
【００１９】このようにして得られる黒原着ポリエステ
ル繊維は、フィラメント、短繊維または仮撚加工糸と
し、これを単独または他の繊維と併用して従来公知の方
法で製織したり製編して暗幕用原反とすることができ
る。例えば、黒原着糸を緯糸に用い、一方通常の白色ポ
リエステル延伸糸を経糸に用いた朱子織、または一方の
面に黒原着糸が配される二重織にして、暗幕用の原反と
なせばよい。ここで織密度は、用いる黒原着糸条の総デ
ニール数によっても変わってくるが、下記式で表わされ
るカバーファクターを２０〜３５の範囲内とすることが
好ましい。 カバーファクター＝（経糸の密度）／（経糸の綿番手）
0.5 ＋（緯糸の密度）／（緯糸の綿番手）0.5 ただし、密度は、織物１インチ巾あたりの黒原着糸条の
本数である。次いで得られた原反は、必要に応じてさら
に染色処理、防炎加工処理を施した後暗幕となし、例え
ばカーテン等に縫製する。The black dyed polyester fiber thus obtained is used as a filament, a staple fiber or a false twisted yarn, and woven or knitted by itself or in combination with other fibers by a conventionally known method to form a black screen. It can be used as material. For example, use a black spun yarn for the weft, and a satin weave using a normal white polyester drawn yarn for the warp, or a double weave with the black spun yarn on one side, and use it as a material for blackout curtains. I just need. Here, the weaving density varies depending on the total denier of the black dyed yarn to be used, but it is preferable that the cover factor represented by the following equation be within the range of 20 to 35. Cover factor = (density of warp) / (cotton count of warp)
0.5 + (density of the weft) / (cotton count of weft) 0.5 where density is the number of black dope Chakuitojo per fabric 1 inch wide. Next, the obtained raw material is further subjected to a dyeing treatment and a flameproofing treatment, if necessary, to form a blackout curtain, for example, sewn on a curtain or the like.
【００２０】[0020]
【発明の作用・効果】本発明の暗幕に用いられている黒
原着糸は、従来の原着糸に比較して吸油量が小さいカー
ボンブラックを用いているので、粒子径が小さくとも、
黒度及び遮光性を満足できる量ポリエステル中に配合し
てもポリエステルの溶融粘度増加が少なく、暗幕に着火
してもその近傍の繊維は容易に溶融脱落するドリップ効
果によって防炎性能が向上するのである。The black dyed yarn used in the blackout curtain of the present invention uses carbon black having a smaller oil absorption than conventional dyed yarns.
Amount that satisfies blackness and light-shielding properties Even if blended in polyester, the increase in melt viscosity of polyester is small, and even if a blackout curtain is ignited, the fibers in the vicinity are easily melted and dropped. is there.
【００２１】したがって、本発明によれば、従来の糸染
めによる暗幕と比較して遜色のない黒度、防炎性を有す
る暗幕を、より安価に提供することが可能となる。Therefore, according to the present invention, it is possible to provide a black curtain having blackness and flameproofness which is comparable to that of the conventional black dyeing screens by yarn dyeing at a lower cost.
【００２２】[0022]
【実施例】以下、実施例によって本発明をさらに具体的
に説明するが、本発明の範囲はこれに限定されるもので
はない。なお、実施例における各特性値は下記方法によ
り測定した。The present invention will be described in more detail with reference to the following examples, but the scope of the present invention is not limited thereto. In addition, each characteristic value in an Example was measured by the following method.
【００２３】（黒度）黒原着糸を靴下編み地に編み立
て、マクベス社製カラー測定装置「Ｍａｃｂｅｔｈ Ｃ
ＯＬＯＲ―ＥＹＥ」を用い、２度視野としＤ６５光源を
使用して波長３６０〜７４０ｎｍで測定し、Ｌ* 値を求
めた。なお、Ｌ* が２０以下のものが合格である。(Blackness) Knitted black yarn is knitted on a sock knitted fabric, and a Macbeth color measuring device "Macbeth C" is used.
"OLOR-EYE", a field of view of 2 degrees was used, and measurement was performed at a wavelength of 360 to 740 nm using a D65 light source to obtain an L * value. In addition, the thing whose L * is 20 or less is pass.
【００２４】（遮光性）染色後の暗幕サンプルを、ＪＩ
Ｓ Ｌ１０５５に準拠して測定し、遮光率で表わした。
なお、遮光率が９９．９９％以上のものが合格である。 遮光率（％）＝（１−ｉ／ｉ0 ）×１００ 但し、ｉ ：サンプルを装着した時の照度（ルクス） ｉ0 ：サンプルを装着しない時の照度（ルクス） （防炎性）染色後の暗幕サンプルを、ＪＩＳに定められ
ている４５°コイル法に準拠して測定し、接炎回数（１
０回テストの平均値）で表した。なお、３回以上のもの
が合格である。(Light-shielding properties)
It was measured in accordance with SL1055 and expressed as a light blocking ratio.
In addition, those with a light-shielding rate of 99.99% or more pass. Shading ratio (%) = (1−i / i 0 ) × 100 where i: illuminance (lux) when sample is attached i 0 : illuminance (lux) when sample is not attached (flameproof) after staining Was measured in accordance with the 45 ° coil method defined by JIS, and the number of flame contact times (1
(Average value of 0 tests). In addition, three or more times pass.
【００２５】［実施例１］固有粘度０．６５のポリエチ
レンテレフタレート１００重量部に対して表１記載の粒
子径、吸油量を有するカーボンブラックを４３重量部配
合して得たマスターチップを、上記ポリエチレンテレフ
タレートのチップと、繊維中カーボンブラック含有量が
表１記載の割合となるよう混合した後、２９０℃に加熱
溶融して３０の吐出孔を有する紡糸口金から吐出し、次
いで１１００ｍ／分の速度で引取った。得られた未延伸
糸を常法にしたがって３倍に延伸し、１５０デニール／
３０フィラメントの黒原着ポリエステル繊維を得た。Example 1 A master chip obtained by blending 43 parts by weight of carbon black having a particle diameter and an oil absorption amount shown in Table 1 with 100 parts by weight of polyethylene terephthalate having an intrinsic viscosity of 0.65 was used as the polyethylene chip. The terephthalate chip was mixed with the carbon black content in the fiber so as to have the ratio shown in Table 1, heated and melted at 290 ° C., discharged from a spinneret having 30 discharge holes, and then at a speed of 1100 m / min. I took it. The obtained unstretched yarn is stretched 3 times according to a conventional method, and 150 denier /
A 30-filament black dyed polyester fiber was obtained.
【００２６】また、上記ポリエチレンテレフタレートで
あって重縮合反応時に二酸化チタンを０．３重量％添加
したものに、上記カーボンブラックを添加することなく
紡糸延伸して白色ポリエステル繊維（１５０デニール／
４８フィラメント）を得た。The above-mentioned polyethylene terephthalate to which 0.3% by weight of titanium dioxide was added at the time of the polycondensation reaction was spun and drawn without adding the above-mentioned carbon black to obtain white polyester fibers (150 denier / 150
48 filaments).
【００２７】これらのポリエステル繊維を用い、経糸に
黒原着ポリエステル繊維１４２本／２５ｍｍ、緯糸に白
色ポリエステル繊維８７本／２５ｍｍ、織組織が朱子織
の織物を作成し、得られた織物の白色ポリエステル繊維
を赤色に染色し、これを暗幕用生地として使用した。そ
の結果、従来の黒原着糸と同程度の遮光性を呈し、防炎
性能も良好であった。Using these polyester fibers, a black-dyed polyester fiber 142/25 mm for the warp, a white polyester fiber 87/25 mm for the weft, and a weave fabric of satin weave, the white polyester fiber of the obtained fabric is obtained. Was dyed red, and this was used as a blackout cloth. As a result, the light-shielding property was substantially the same as that of the conventional black dyed yarn, and the flameproofing performance was also good.
【００２８】［実施例２〜６、比較例１〜６］実施例１
において、カーボンブラックの粒子径、吸油量及び含有
量を表１記載のとおり変更する以外は実施例１と同様に
して暗幕を得た。結果は表１にまとめて示す。[Examples 2 to 6, Comparative Examples 1 to 6] Example 1
In Example 1, a blackout curtain was obtained in the same manner as in Example 1 except that the particle size, oil absorption and content of carbon black were changed as shown in Table 1. The results are summarized in Table 1.
【００２９】[0029]
【表１】 [Table 1]
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) A47H 23/08 A62C 2/00 D01F 6/92 304 D03D 1/00 ──────────────────────────────────────────────────続 き Continued on the front page (58) Fields surveyed (Int. Cl. 7 , DB name) A47H 23/08 A62C 2/00 D01F 6/92 304 D03D 1/00
Claims (1)
て含む暗幕において、前記黒原着ポリエステル繊維は、
下記〜式を同時に満足するカーボンブラックを、繊
維重量を基準として０．５〜２．０重量％含有している
ことを特徴とする防炎性暗幕。 粒子径ｄ（ｎｍ）：１０≦ｄ≦４０ 吸油量Ｈ（ｍｌ／１００ｇ）：４０≦Ｈ≦９０ Ｈ≦８６−１．１５×１０-2ｄ2 1. A black curtain comprising a black-dyed polyester fiber as a constituent fiber, wherein the black-dyed polyester fiber is
A flameproof blackout curtain containing 0.5 to 2.0% by weight of carbon black, which satisfies the following formulas at the same time, based on the weight of the fiber. Particle size d (nm): 10 ≦ d ≦ 40 Oil absorption H (ml / 100 g): 40 ≦ H ≦ 90 H ≦ 86-1.15 × 10 −2 d 2