JP3112124B2 - Glass plate with molding or holder and method for producing the same - Google Patents
Glass plate with molding or holder and method for producing the sameInfo
- Publication number
- JP3112124B2 JP3112124B2 JP26140292A JP26140292A JP3112124B2 JP 3112124 B2 JP3112124 B2 JP 3112124B2 JP 26140292 A JP26140292 A JP 26140292A JP 26140292 A JP26140292 A JP 26140292A JP 3112124 B2 JP3112124 B2 JP 3112124B2
- Authority
- JP
- Japan
- Prior art keywords
- glass plate
- resin
- molding
- holder
- polyamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、無機質ならびに有機質
のガラス板状体、例えば平板状または曲げ板状を有する
生あるいは強化された単板、合せ、複層ガラスの窓部材
および扉部材等として、建築用ならびに車輌用等に採用
し得る、ことに昇降が必要な車輌用ならびに自動車用可
動窓ガラス等に有用な、ガラス板状体周縁部にモールま
たはホルダーを一体化形成する前の該ガラス表面に、特
定した接着性組成物のフイルムまたはフイルム状層を予
め被覆形成し、該被覆面にモールまたはホルダー用合成
樹脂、ことに特定した多相熱可塑性樹脂組成物で成るモ
ールまたはホルダーを一体成型するモールまたはホルダ
ー付ガラス板状体およびその製法を提供するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an inorganic or organic glass plate, for example, a raw or reinforced single plate having a flat or bent plate shape, a laminated or double-glazed window member and a door member, and the like. The glass before forming a molding or a holder integrally with the periphery of the glass plate-like body, which can be used for construction, for vehicles, etc., and is particularly useful for vehicles requiring moving up and down and for movable window glass for automobiles, etc. A film or a film-like layer of the specified adhesive composition is coated on the surface in advance, and the coated surface is integrated with a molding or a synthetic resin for a holder, particularly a molding or a holder made of the specified multi-phase thermoplastic resin composition. An object of the present invention is to provide a molding or a glass plate with a holder and a method for producing the same.
【０００２】[0002]
【従来の技術】従来、ガラスなどの基材への接着性を付
与する方法として、例えば特公昭37ー18392 号公報また
は特公昭52ー32654 号公報等には、ポリエチレンやポリ
プロピレンに代表されるポリオレフィンに、例えばアク
リル酸や無水マレイン酸などの不飽和カルボン酸または
その無水物でグラフト変性することによって極性基を導
入するもの、また例えば特公昭46ー27527 号公報または
特開昭48ー11388 号公報には、エチレンに代表されるα
ーオレフィンと（メタ）アクリル酸グリシジルエステル
などの極性モノマーとの共重合によるもの、さらに例え
ば特開昭47ー15486 号公報にはエチレンと無水マレイン
酸の共重合体とポリアミドとの積層体があり、またエチ
レンと無水マレイン酸の共重合体にポリイソブチレン等
のエラストマーを添加することによりポリアミド樹脂と
の接着性が改良されること等が知られている。2. Description of the Related Art Conventionally, as a method of imparting adhesiveness to a substrate such as glass, for example, Japanese Patent Publication No. 37-18392 or Japanese Patent Publication No. 52-32654 discloses a polyolefin represented by polyethylene or polypropylene. Into which a polar group is introduced by graft modification with, for example, an unsaturated carboxylic acid such as acrylic acid or maleic anhydride or an anhydride thereof, and, for example, JP-B-46-27527 or JP-A-48-11388. Has an α represented by ethylene
A copolymer obtained by copolymerization of an olefin and a polar monomer such as glycidyl (meth) acrylate; for example, JP-A-47-15486 discloses a laminate of a copolymer of ethylene and maleic anhydride and a polyamide; It is also known that the addition of an elastomer such as polyisobutylene to a copolymer of ethylene and maleic anhydride improves the adhesion to a polyamide resin.
【０００３】一方、ガラス板周縁部の所定箇所に接着剤
層を形成した後、モールあるいはホルダーを一体化成型
する方法として、例えば特開昭59ー199228号公報には、
ガラス板の外周縁を両面から囲むように、弾力性を有す
るゴム又は軟質合成樹脂からなり、断面略コ字状に成形
したシール材を兼ねる緩衝部材をガラス板の全外周縁に
装着した後、前記緩衝部材を介してコア型とキャビティ
型とからなるインジェクション成形型で挟持し、両型で
形成される空間内に、硬質合成樹脂の溶融樹脂を射出し
て枠部を成形し、枠部の内周縁に沿ってシール兼緩衝部
材に切れ目を入れ、緩衝部材を除去することにより、バ
リの発生を防止しようとすることが開示されている。On the other hand, as a method of integrally forming a molding or a holder after forming an adhesive layer at a predetermined portion of a peripheral portion of a glass plate, for example, JP-A-59-199228 discloses a method.
After surrounding the outer edge of the glass plate from both sides, after attaching a cushioning member made of elastic rubber or soft synthetic resin and also serving as a sealing material molded in a substantially U-shaped cross section to the entire outer edge of the glass plate, It is sandwiched by an injection mold composed of a core mold and a cavity mold via the cushioning member, and into a space formed by both molds, a molten synthetic resin is injected to form a frame portion, and a frame portion is formed. It is disclosed that an attempt is made to prevent the occurrence of burrs by making a cut in the seal / buffer member along the inner peripheral edge and removing the buffer member.
【０００４】また例えば、特開昭62ー25024 号公報に
は、板状の窓ガラスの周縁部に熱活性型の接着層を形成
し、接着剤層を形成した窓ガラスの周縁部を射出成形型
に挿入して合成樹脂の射出成形を行い、窓ガラスの周縁
部に枠材を形成するとともに、射出された樹脂の熱によ
り接着剤を活性化して窓ガラスと枠材を一体的に固着す
るという車両用ウインドウの製造方法が開示されてい
る。For example, Japanese Patent Application Laid-Open No. 62-25024 discloses that a thermally activated adhesive layer is formed on the periphery of a plate-shaped window glass, and the periphery of the window glass on which the adhesive layer is formed is injection-molded. Insert into a mold and perform injection molding of synthetic resin to form a frame material on the periphery of the window glass, and activate the adhesive by the heat of the injected resin to integrally fix the window glass and the frame material. A method for manufacturing a vehicle window is disclosed.
【０００５】さらに例えば、本出願人が既に出願した特
開平１ー209116号公報には、板状体周縁部の所要箇所に
モールまたはホルダーを一体成形して固着するに際し、
板状体周縁部の所要箇所に予め、60〜150 ℃の温度で融
着性を有しかつ厚みが５〜250 μの樹脂フイルムを少な
くとも一枚囲繞するよう表裏両面の周縁部から対応する
端面にかけて被着して板状体を型内に配置し、樹脂フイ
ルムの表面と型内面とからなるキャビティ空間に樹脂を
注入し、樹脂が固化した後、板状体を型から取出すモー
ルまたはホルダー付板状体の製造方法を提案している。Further, for example, Japanese Patent Application Laid-Open No. 1-209116 filed by the present applicant discloses that a molding or a holder is integrally formed and fixed at a required portion of a peripheral portion of a plate-like body.
The corresponding end faces from the peripheral edges of both front and back surfaces are arranged so as to surround at least one resin film having a fusing property at a temperature of 60 to 150 ° C. and a thickness of 5 to 250 μ in advance at a required portion of the peripheral portion of the plate-like body. With a molding or holder that removes the plate from the mold after placing the plate in the mold, injecting the resin into the cavity space consisting of the resin film surface and the mold inner surface, and solidifying the resin. A method for manufacturing a plate is proposed.
【０００６】さらにまた例えば、***特許第911,781 号
には、窓ガラスの周縁にゴム製のシール部材を取付ける
方法に関して記載され、ガラス板の縁部表面を例えばア
ルミニウムでメタライズ処理して0.05〜0.15mm程度の薄
い金属被膜を形成し、場合によってはその表面に接着
剤、例えば溶液状のゴム系接着剤を塗り、その後ガラス
板を型にセットしてゴムを成形して加熱加硫するという
ことが開示されている等が知られている。Further, for example, West German Patent No. 911,781 describes a method of attaching a rubber sealing member to the periphery of a window glass. The edge surface of a glass plate is metallized with aluminum, for example, to 0.05 to 0.15 mm. To form a thin metal coating, apply an adhesive, such as a solution-based rubber adhesive, to the surface in some cases, then set the glass plate in a mold, mold the rubber, and heat and vulcanize it. The disclosure is known.
【０００７】[0007]
【発明が解決しようとする問題点】前述したように、例
えば特公昭37ー18392 号公報、特公昭52ー32654 号公
報、特公昭46ー27527 号公報、特開昭48ー11388 号公報
および特開昭47ー15486 号公報等に記載されている接着
性の付与方法等では、例えば建築用部品あるいは自動車
用部品等で使用される積層体、ことに該部品としてのガ
ラス板状体の場合には耐熱接着性が要求され、さらには
低温接着での接着力も必要であり、前記したこれら従来
の方法での改良では充分でなく、使用し難いものであ
り、むしろ使用できないと言うべきものである。As described above, for example, JP-B-37-18392, JP-B-52-32654, JP-B-46-27527, JP-A-48-11388 and In the method of imparting adhesiveness described in Japanese Patent Laid-Open No. 47-15486, etc., for example, in the case of a laminate used for building parts or automobile parts, especially in the case of a glass plate as such parts, Is required to have heat-resistant adhesiveness, and also needs adhesive strength at low-temperature bonding, and the improvement by the above-mentioned conventional methods is not sufficient, and it is difficult to use, and rather it cannot be used. .
【０００８】一方、特開昭62ー25024 号公報に記載の製
造方法では、ガラス板の外周縁を両面から囲むように、
弾力性を有するゴム又は軟質合成樹脂からなる断面略コ
字状に成形したシール材を兼ねる緩衝部材を単に装着し
てモールを一体成形したとしても、必ずしも接着力を強
力に向上させるものではないものである。また***特許
第911,781 号に記載の方法では、溶液状の接着剤を塗布
して接着剤層を設けることのみ記載し、接着剤層の厚さ
や溶融温度を記載していないし、例えば合せガラスの場
合には中間膜への悪影響を避けるためにはシール部材と
して成形するゴムの加硫温度が100 〜110 ℃程度が好ま
しいとあって、到底この温度ではゴムが溶融状態にはな
り難いと言えるものであり、必ずしも充分な接着力、こ
とに耐熱接着性でかつ低温接着での接着力を発現するも
のではないものであると言っても過言でないものであ
る。さらに特開平１ー209116号公報に記載の方法では、
前記種々の方法等より、かなり改善が認められるもの
の、例えば自動車用窓ガラスの昇降用窓ガラスにおい
て、温度上の種々の過酷な環境下で使用の際、耐熱接着
性が向上しているものの、充分長期的に確実に安定して
いるものとは必ずしも言い難いものである。On the other hand, in the manufacturing method described in Japanese Patent Application Laid-Open No. 62-25024, the outer peripheral edge of the glass plate is surrounded from both sides.
Even if a molding is integrally formed by simply mounting a cushioning member which also serves as a sealing material formed in a substantially U-shaped cross section made of elastic rubber or soft synthetic resin, it does not necessarily enhance the adhesive force strongly. It is. Further, the method described in West German Patent No. 911,781 only describes that a solution adhesive is applied to form an adhesive layer, and does not describe the thickness and melting temperature of the adhesive layer. In order to avoid the adverse effect on the interlayer, the vulcanization temperature of the rubber molded as the sealing member is preferably about 100 to 110 ° C., and it can be said that the rubber is hardly melted at this temperature. It is not an exaggeration to say that it does not necessarily exhibit sufficient adhesive strength, especially heat resistant adhesiveness, and does not exhibit adhesive strength at low temperature bonding. Further, in the method described in JP-A-1-209116,
Although a considerable improvement is recognized from the above various methods and the like, for example, in an ascending and descending window glass for an automobile window glass, when used in various severe environments on temperature, although the heat-resistant adhesiveness is improved, It is not always possible to say that it is stable for a sufficiently long period.
【０００９】[0009]
【問題点を解決するための手段】本発明は、従来のかか
る問題点に鑑みてなしたものであって、ガラス板状体周
縁部にモールまたはホルダーを一体成型して固着するに
際し、予めガラス板状体周縁部の所定箇所に、ポリアミ
ド樹脂を含む特定の接着性組成物のフイルムまたはフイ
ルム状層でもって、ガラス板状体周縁部を囲繞するよう
に被着した状態に介在させて行うこと、さらにはモール
またはホルダーがマトリックス相がポリアミド樹脂であ
る多相熱可塑性樹脂組成物とすることにより、ガラス板
状体、樹脂フイルムまたは樹脂フイルム状層ならびにモ
ールまたはホルダーの各構成間の接着性を改良して、高
強度の接着、取付け一の精度向上等はもちろん、ことに
耐熱性が格段に良好な、とくに低温接着による接着力な
らびに高温下での剥離に対する接着力を顕著に向上させ
る一体成型品であるモールまたはホルダー付ガラス板状
体およびその製法を提供するものである。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned conventional problems, and has been made in consideration of the fact that a molding or a holder is integrally molded and fixed to a peripheral portion of a glass plate-like body. At a predetermined position on the periphery of the plate-like body, a film or a film-like layer of a specific adhesive composition containing a polyamide resin is interposed in a state of being attached so as to surround the periphery of the glass plate-like body. Further, by making the molding or the holder a multiphase thermoplastic resin composition in which the matrix phase is a polyamide resin, the glass plate, the resin film or the resin film-like layer and the adhesion between the respective components of the molding or the holder are improved. Improved, high-strength bonding, improved accuracy in mounting, etc., of course, especially heat resistance is remarkably good, especially adhesive strength by low temperature bonding and high temperature Is integrally molded article to significantly improve adhesion molding or glass plate-like member with a holder for the release and is intended to provide the method.
【００１０】すなわち、本発明は、ガラス板状体周縁部
の所要箇所に、予め樹脂フイルムまたは樹脂フイルム状
層を少なくとも一枚または一層でガラス板状体周縁部を
囲繞するよう表裏両面の周縁部から対応する端面にかけ
て被着し、射出成形法により樹脂製のモールまたはホル
ダーを、該樹脂フィルムまたは樹脂フィルム状層を設け
たガラス板状体の周縁部にて、ガラス板状体と一体成形
した、モールまたはホルダー付ガラス板状体において、
前記樹脂フイルムまたは樹脂フイルム状層がエチレンー
α、βー不飽和カルボン酸エステルー無水マレイン酸三
元共重合体60〜95重量％と、ポリアミド樹脂40〜５重量
％とから成ることを特徴とするモールまたはホルダー付
ガラス板状体。That is, according to the present invention, at least one or more resin films or resin film-like layers are provided at predetermined positions on the periphery of the glass plate so as to surround the periphery of the glass plate in advance. It is applied from the peripheral edge of both sides to the corresponding end face , and a resin molding or holder is provided by the injection molding method , and the resin film or the resin film-like layer is provided.
In the peripheral portion of the glass plate-shaped body, the glass plate-shaped body integrally molded with the glass plate-shaped body with a molding or a holder,
The molding wherein the resin film or the resin film-like layer is composed of 60 to 95% by weight of an ethylene-α, β-unsaturated carboxylic acid ester-maleic anhydride terpolymer and 40 to 5% by weight of a polyamide resin. Or glass plate with holder.
【００１１】ならびに、前記エチレンーα、βー不飽和
カルボン酸エステルー無水マレイン酸三元共重合体が、
エチレン単位40〜90重量％、α、βー不飽和カルボン酸
アルキルエステル単位55〜５重量％、無水マレイン酸単
位0.1 〜10重量％から成る共重合体であることを特徴と
する上述したモールまたはホルダー付ガラス板状体。In addition, the ethylene-α, β-unsaturated carboxylic acid ester-maleic anhydride terpolymer is
A molding comprising 40 to 90% by weight of ethylene units, 55 to 5% by weight of α, β-unsaturated carboxylic acid alkyl ester units and 0.1 to 10% by weight of maleic anhydride units; Glass plate with holder.
【００１２】また、前記樹脂製のモールまたはホルダー
が、ポリアミド樹脂または、マトリックス相がポリアミ
ド樹脂である多相熱可塑性樹脂から成ることを特徴とす
る上述したモールまたはホルダー付ガラス板状体。また
さらに、前記マトリックス相がポリアミド樹脂である多
相熱可塑性樹脂が、ポリアミド樹脂と、ポリフェニレン
エーテルまたはポリプロピレンあるいはＡＢＳから得ら
れる樹脂組成物であることを特徴とする上述したモール
またはホルダー付ガラス板状体。またさらに、前記マト
リックス相がポリアミド樹脂である多相熱可塑性樹脂
が、ポリアミド樹脂と、ポリフェニレンエーテルまたは
ポリプロピレンあるいはＡＢＳ、およびガラス繊維から
得られる樹脂組成物であることを特徴とする上述したモ
ールまたはホルダー付ガラス板状体。またさらに、前記
ポリアミド樹脂が、ポリアミドー６またはポリアミドー
６６であることを特徴とする上述したモールまたはホル
ダー付ガラス板状体。またさらに、前記マトリックス相
がポリアミド樹脂である多相熱可塑性樹脂が、ポリアミ
ド樹脂と、ポリフェニレンエーテルおよび相溶性改良剤
からなる樹脂組成物であることを特徴とする上述したモ
ールまたはホルダー付ガラス板状体。The resin molding or holder
Is polyamide resin or matrix phase is polyamide
Of multi-phase thermoplastic resin
Or a glass plate-like body with a holder as described above. Also
In addition,When the matrix phase is polyamide resin
Phase thermoplastic resinBut polyamide resin and polyphenylene
Obtained from ether or polypropylene or ABS
Characterized in that it is a resin composition which is
Or glass plate with holder. Still further,Mato
Multi-phase thermoplastic resin in which the rix phase is a polyamide resin
Is a polyamide resin, polyphenylene ether or
From polypropylene or ABS and glass fiber
The above-mentioned resin characterized by being a resin composition obtained.
Plate or glass plate with holder. Still further,
When the polyamide resin is polyamide-6 or polyamide-
66 or the mall or hall described above.
Glass plate with dar. Still further,Matrix phase
Is a polyamide resinBut polyamid
Resin, polyphenylene ether and compatibility improver
Characterized in that it is a resin composition comprising
Plate or glass plate with holder.
【００１３】さらに、ガラス板状体周縁部の所要箇所に
樹脂製のモールまたはホルダーを一体成形して固着する
に際し、前記所要箇所に、エチレンーα、βー不飽和カ
ルボン酸エステルー無水マレイン酸三元共重合体60〜95
重量％と、ポリアミド樹脂40〜５重量％とから成る樹脂
フイルムまたは樹脂フイルム状層を含む少なくとも一枚
または一層を、予め囲繞するよう表裏両面の周縁部から
対応する端面にかけて被着し、該ガラス板状体を型内に
配置して型締めし、前記樹脂フイルムの表面と該型内面
とからなるキャビティ空間に、ポリアミド樹脂または、
マトリックス相がポリアミド樹脂である多相熱可塑性樹
脂から成る樹脂組成物を注入し、該樹脂組成物が固化し
た後、前記ガラス板状体を前記型から取り出すことを特
徴とするモールまたはホルダー付ガラス板状体の製法。Further, when a resin molding or a holder is integrally molded and fixed to a required portion of the peripheral portion of the glass plate-like body, ethylene-α, β-unsaturated carboxylic acid ester-maleic anhydride ternary component is added to the required portion. Copolymer 60-95
At least one or a single layer including a resin film or a resin film-like layer composed of 40% to 5% by weight of a polyamide resin is applied from the peripheral edge of both front and back surfaces to the corresponding end surface so as to surround the glass in advance. Placing the plate-shaped body in a mold and clamping the mold, polyamide resin or in a cavity space formed by the surface of the resin film and the inner surface of the mold,
Multi-phase thermoplastic resin whose matrix phase is polyamide resin
A method for producing a molding or a glass plate with a holder, comprising: injecting a resin composition comprising a fat and solidifying the resin composition, and removing the glass plate from the mold.
【００１４】さらにまた、前記マトリックス相がポリア
ミド樹脂である多相熱可塑性樹脂が、ガラス繊維を含む
ことを特徴とする上述したモールまたはホルダー付ガラ
ス板状体の製法をそれぞれ提供するものである。Further, the matrix phase is a polymer
It is another object of the present invention to provide a method for producing a molding or a glass plate with a holder as described above , wherein the multi-phase thermoplastic resin as a mid resin contains glass fibers.
【００１５】ここで、前記したエチレンーα、βー不飽
和カルボン酸エステルー無水マレイン酸三元共重合体
は、高圧ラジカル共重合によって製造される共重合体で
ある。α、βー不飽和カルボン酸エステルとしては、炭
素数が３〜８個の不飽和カルボン酸、例えばアクリル
酸、メタクリル酸等のアルキルエステルであって、具体
例としては、アクリル酸メチル、アクリル酸エチル、ア
クリル酸ｎープロピル、アクリル酸イソプロピル、アク
リル酸ｎーブチル、アクリル酸ｔーブチル、アクリル酸
イソブチル、メタクリル酸メチル、メタクリル酸エチ
ル、メタクリル酸ｎープロピル、メタクリル酸イソプロ
ピル、メタクリル酸ｎーブチル、メタクリル酸ｔーブチ
ル、メタクリル酸イソブチル等であり、これらのうち、
とくにアクリル酸メチル、アクリル酸エチル、アクリル
酸ｎーブチル、メタクリル酸メチルが好ましく、またこ
れらのコモノマーは１種のみならず２種以上用いること
もできる。Here, the ethylene-α, β-unsaturated carboxylic acid ester-maleic anhydride terpolymer is a copolymer produced by high-pressure radical copolymerization. The α, β-unsaturated carboxylic acid ester is an unsaturated carboxylic acid having 3 to 8 carbon atoms, for example, an alkyl ester such as acrylic acid and methacrylic acid. Specific examples thereof include methyl acrylate and acrylic acid. Ethyl, n-propyl acrylate, isopropyl acrylate, n-butyl acrylate, t-butyl acrylate, isobutyl acrylate, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, t-methacrylate -Butyl, isobutyl methacrylate, and the like.
Particularly, methyl acrylate, ethyl acrylate, n-butyl acrylate and methyl methacrylate are preferred, and these comonomers can be used alone or in combination of two or more.
【００１６】また、前記α、βー不飽和カルボン酸エス
テルの含有量としては、５〜55重量％程度であり、５重
量％未満では接着性の改良効果が小さく好ましくなく、
55重量％を超えると接着力は充分であるものの製造コス
トが増大することおよび臭気が悪化すること等から好ま
しくないためである。Further, the content of the α, β-unsaturated carboxylic acid ester is about 5 to 55% by weight.
If the content exceeds 55% by weight, the adhesive strength is sufficient, but the production cost is increased and the odor is deteriorated.
【００１７】さらに、前記無水マレイン酸の含有量とし
ては、0.1 〜10重量％程度であり、0.1 重量％未満では
接着性の改良効果が小さく好ましくなく、10重量％を超
えると接着力は充分であるものの、製造コストが増大す
るので好ましくないためである。Further, the content of the maleic anhydride is about 0.1 to 10% by weight. When the content is less than 0.1% by weight, the effect of improving the adhesiveness is small, which is not preferable. When it exceeds 10% by weight, the adhesive strength is not sufficient. However, this is not preferable because the manufacturing cost increases.
【００１８】次いで、前記したポリアミド樹脂として
は、例えば３員環以上のラクタム、重合可能なωーアミ
ノ酸、２塩基酸とジアミン等との重縮合によって得られ
る各種のポリアミドを用いることができる。具体的に
は、例えばεーカプロラクタム、アミノカプロン酸、エ
ナントラクタム、７ーアミノヘプタン酸、11ーアミノウ
ンデカン酸等の重合体、あるいはブタンジアミン、ヘキ
サメチレンジアミン、ノナメチレンジアミン、ウンデカ
メチレンジアミン、ドデカメチレンジアミン、メタキシ
レンジアミン等のジアミン類と、テレフタル酸、イソフ
タル酸、アジピン酸、セバチン酸、ドデカン２塩基酸、
グルタール酸等のジカルボン酸とを重縮合せしめて得ら
れる重合体またはこれらの共重合体が挙げられる。具体
例としては、例えばポリアミド６、ポリアミド66、ポリ
アミド６・10、ポリアミド11、ポリアミド12、ポリアミ
ド６・12のような脂肪族ポリアミド、ポリヘキサメチレ
ンジアミンテレフタルアミド、ポリヘキサメチレンジア
ミンイソフタルアミド、キシレン基含有ポリアミドのよ
うな芳香族ポリアミド等が挙げられ、これらは２種以上
の混合物または共重合体として用いることもできる。Next, as the above-mentioned polyamide resin, for example, various polyamides obtained by polycondensation of a lactam having three or more ring members, a polymerizable ω-amino acid, a dibasic acid and a diamine can be used. Specifically, for example, polymers such as ε-caprolactam, aminocaproic acid, enantholactam, 7-aminoheptanoic acid, 11-aminoundecanoic acid, or butanediamine, hexamethylenediamine, nonamethylenediamine, undecamethylenediamine, dodecamethylenediamine , Diamines such as meta-xylene diamine, and terephthalic acid, isophthalic acid, adipic acid, sebacic acid, dodecane dibasic acid,
A polymer obtained by polycondensing a dicarboxylic acid such as glutaric acid or the like, or a copolymer thereof is exemplified. Specific examples thereof include aliphatic polyamides such as polyamide 6, polyamide 66, polyamide 6,10, polyamide 11, polyamide 12, and polyamide 6.12, polyhexamethylene diamine terephthalamide, polyhexamethylene diamine isophthalamide, and xylene group. Aromatic polyamides such as contained polyamides and the like can be mentioned, and these can be used as a mixture or a copolymer of two or more kinds.
【００１９】さらにまた、前記エチレンーα、βー不飽
和カルボン酸エステルー無水マレイン酸三元共重合体の
含有量が60〜95重量％としたのは、60重量％未満では低
温接着での接着力が低下し、95重量％を超えると耐熱接
着性が充分ではないためである。さらにまた、ポリアミ
ド樹脂が40〜５重量％の範囲をはずれると、接着性が低
下するためである。Furthermore, the reason why the content of the ethylene-α, β-unsaturated carboxylic acid ester-maleic anhydride terpolymer is set to 60 to 95% by weight is that when the content is less than 60% by weight, the adhesive strength at low temperature bonding is obtained. Is lower than 95% by weight, the heat resistance is not sufficient. Further, when the polyamide resin is out of the range of 40 to 5% by weight, the adhesiveness is reduced.
【００２０】さらに、前記マトリックス相がポリアミド
樹脂である多相熱可塑性樹脂については、ポリアミド樹
脂、例えばポリフェニレンエーテルやポリプロピレン、
ＡＢＳ樹脂等の樹脂からなる組成物であり、ポリアミド
樹脂としては例えばポリアミドー６、ポリアミドー66等
である。Further, as for the multi-phase thermoplastic resin in which the matrix phase is a polyamide resin, a polyamide resin such as polyphenylene ether or polypropylene,
It is a composition comprising a resin such as an ABS resin, and examples of the polyamide resin include polyamide-6, polyamide-66, and the like.
【００２１】さらにまた、前記ポリアミド樹脂とポリフ
ェニレンエーテルとからなる樹脂組成物は、親和性がよ
くないため極めて低い機械的物性しか示さないので、相
溶性改良剤を配合する。該相溶性改良剤としては、例え
ばマレイン酸、無水マレイン酸、フマール酸、不飽和ア
ミン、グリシジルメタクリレート等、また例えばクエン
酸、リンゴ酸、アガリシン酸等の飽和脂肪族ポリカルボ
ン酸のエステル化合物、アミド化合物、無水物、水化物
および塩等、また例えばクロロホルミルこはく酸無水
物、クロロエタノイルこはく酸無水物、トリメリット酸
無水物酸クロライド、トリメリット酸無水物酢酸無水
物、テレフタル酸クロライド等、および例えばビニルト
リメトキシシラン、ビニルトリエトキシシラン、ビニル
トリス（βーメトキシエトキシ）シラン、γーアミノプ
ロピルトリメトキシシラン、γーアミノプロピルトリエ
トキシシラン、Ｎー（βアミノエチル）ーアミノプロピ
ルトリメトキシシラン、Ｎー（βアミノエチル）ーアミ
ノプロピルトリエトキシシラン、γーメルカプトプロピ
ルトリメトキシシラン、γーメルカプトメチルエトキシ
シラン等の群から選ばれる少なくとも１種の化合物であ
る。なお、該相溶性改良剤を配合する際、ラジカル開始
剤を併用してもよい。Furthermore, since the resin composition comprising the polyamide resin and polyphenylene ether has poor affinity and exhibits only extremely low mechanical properties, a compatibility improver is added. Examples of the compatibility improver include maleic acid, maleic anhydride, fumaric acid, unsaturated amine, glycidyl methacrylate and the like, and ester compounds of saturated aliphatic polycarboxylic acids such as citric acid, malic acid and agaric acid, amides Compounds, anhydrides, hydrates and salts and the like, for example, chloroformyl succinic anhydride, chloroethanoyl succinic anhydride, trimellitic anhydride chloride, trimellitic anhydride acetic anhydride, terephthalic acid chloride, etc. And, for example, vinyltrimethoxysilane, vinyltriethoxysilane, vinyltris (β-methoxyethoxy) silane, γ-aminopropyltrimethoxysilane, γ-aminopropyltriethoxysilane, N- (βaminoethyl) -aminopropyltrimethoxysilane , N- (βaminoethyl)- It is at least one compound selected from the group of aminopropyltriethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-mercaptomethylethoxysilane and the like. When the compatibility improver is blended, a radical initiator may be used in combination.
【００２２】さらにまた、前記これらの樹脂組成物は、
例えばポリフェニレンエーテルの難加工性や低耐溶剤
性、ポリアミド樹脂の低耐熱性や高吸水性を改良し有用
であり、加工性を確保するためポリアミド樹脂をマトリ
ックスにしている。Furthermore, these resin compositions are
For example, polyphenylene ether is useful because it is difficult to process and has low solvent resistance, and the polyamide resin has low heat resistance and high water absorption, and is useful.
【００２３】さらにまた、前記ポリアミド樹脂とポリプ
ロピレンとからなる樹脂組成物は、例えばポリプロピレ
ンの耐熱性や塗装性、ポリアミド樹脂の耐水性、耐薬品
性、耐衝撃性を改良し、耐熱性を確保するためポリアミ
ド樹脂をマトリックスにしている。Further, the resin composition comprising the polyamide resin and the polypropylene improves, for example, heat resistance and coating properties of the polypropylene, water resistance, chemical resistance and impact resistance of the polyamide resin, and secures heat resistance. Therefore, a polyamide resin is used as a matrix.
【００２４】さらにまた、前記ポリアミド樹脂とＡＢＳ
とからなる樹脂組成物は、ポリアミド樹脂が有する耐熱
性、耐油性を活かし、欠点である耐衝撃性、吸湿性をＡ
ＢＳにより改良し、さらに成形収縮も小さくするもので
ある。Further, the polyamide resin and ABS
The resin composition comprising a polyamide resin has heat resistance and oil resistance possessed by the polyamide resin, and has the disadvantages of impact resistance and moisture absorption of A.
It is improved by BS and further reduces the molding shrinkage.
【００２５】また、前記合成樹脂組成物の補強材として
は、ガラス繊維等の無機繊維ならびにアラミド繊維等の
有機繊維など一般的な補強材が用いられるものである。
一方、前記樹脂フイルム化する方法としては、例えばベ
ント装置付30mmφ二軸押出機と20mmφＴダイフイルム成
形機等を用いて行い、約50〜200 ℃程度の温度で融着性
を示すものがよく、モールまたはホルダー成型時の樹脂
温度、例えば60〜250 ℃程度より少なくとも低い温度、
好ましくは10〜150 ℃程度低い温度が強固な融着力を発
揮するものとなるものであり、その温度は成形樹脂と樹
脂フイルムとの組合せ、フイルムの厚さ、型温（通常50
〜100 ℃）等によるものであり、また該樹脂フイルムの
厚さは約５〜250 μ程度であり、250 μを超えると一体
成形したホルダーあるいはモールのガラス板状体への付
着力の向上が得られにくくなり、例えば約100 〜 200μ
程度で１枚で用いることができ、５μ未満では付着力の
向上への効果が少なくなりやすいことと成形時における
フイルムの安定化が得にくいためであり、例えば15〜75
μの厚みのものを１〜３枚程度用いること等、好ましく
は総厚みが250 μ以下とすることである。As the reinforcing material for the synthetic resin composition, general reinforcing materials such as inorganic fibers such as glass fibers and organic fibers such as aramid fibers are used.
On the other hand, as a method for forming the resin film, for example, a method using a 30 mmφ twin-screw extruder with a vent device and a 20 mmφT die film forming machine and the like, which shows a fusion property at a temperature of about 50 to 200 ° C., Resin temperature during molding of the molding or holder, for example, a temperature at least lower than about 60 to 250 ° C.,
Preferably, a temperature as low as about 10 to 150 ° C. exerts a strong fusion force. The temperature is determined by the combination of the molding resin and the resin film, the thickness of the film, and the mold temperature (usually 50 ° C.).
-100 ° C), and the thickness of the resin film is about 5 to 250 µm. If the thickness exceeds 250 µm, the adhesion of the integrally molded holder or molding to the glass plate is improved. It is difficult to obtain, for example, about 100 to 200 μ
When the thickness is less than 5 μm, the effect of improving the adhesion is likely to be reduced, and it is difficult to stabilize the film at the time of molding.
It is preferable that the total thickness be 250 μm or less, such as using about 1 to 3 sheets having a thickness of μ.
【００２６】さらに、シール材兼緩衝部材としては、例
えばフッ素樹脂、シリコン樹脂、シリコンゴム等が採用
できるものであり、前記シール材をスプリング等を用い
て固定してもよいことは言うまでもない。Further, as the sealing material and the cushioning member, for example, fluorine resin, silicone resin, silicone rubber, etc. can be adopted, and it goes without saying that the sealing material may be fixed using a spring or the like.
【００２７】さらにまた、前記射出成形法としては、例
えばRIM(反応射出成形）法、R-RIM(強化反応射出成形）
法、LIM(液状射出成形）法あるいはR-LIM(強化液状射出
成形）法等が一体成形に採用することができ、ホルダー
としては R-RIM法または R-LIM法がまた、モールとして
は RIM法または LIM法が好ましいものである。さらにガ
ラス板状体等へ塗布する際は、ハケ塗りや含浸布による
塗布でよいものであり、場合によっては通常のディッピ
ング法、スプレー法等の塗布手段が適宜採用し得るもの
である。Further, as the injection molding method, for example, RIM (reaction injection molding) method, R-RIM (reinforced reaction injection molding)
Method, LIM (Liquid Injection Molding) method or R-LIM (Reinforced Liquid Injection Molding) method can be adopted for integral molding. R-RIM method or R-LIM method is used for the holder, and RIM is used for the molding. The method or the LIM method is preferred. Further, when the composition is applied to a glass plate or the like, application by brushing or impregnated cloth may be used, and depending on the case, an ordinary application method such as a dipping method or a spray method may be appropriately employed.
【００２８】さらにまた、前記ガラス板状体としては、
無機質あるいは有機質の透明ガラス板であってもよく、
無色または着色、ならびにその種類あるいは色調、形状
等に特に限定されるものではなく、さらに曲げ板ガラス
としてはもちろん、各種強化ガラスや強度アップガラ
ス、熱線反射ガラス等の各種機能性ガラス、平板や単
板、複層ガラスあるいは合せガラス、必要に応じハード
コート処理されたアクリル板、ポリカーボネート板等で
あり、建築、家具、車輌、自動車等に用いられるもので
ある。Further, as the glass plate-like body,
It may be an inorganic or organic transparent glass plate,
It is not particularly limited to colorless or colored, and its type, color tone, shape, etc. Further, as well as bent sheet glass, various functional glass such as various strengthened glass, strengthened glass, heat ray reflective glass, flat plate and single plate And multi-layer glass or laminated glass, and an acrylic plate, a polycarbonate plate and the like which have been subjected to a hard coat treatment as required, and are used for construction, furniture, vehicles, automobiles and the like.
【００２９】さらにまた、ホルダーを一体成型するガラ
ス板状体周縁部の所要箇所とは、ガラス板状体の下縁側
が好ましいが、ガラス板状体の昇降方法ならびに開閉方
法等によっては、ガラス板状体の片方または両方の側縁
側あるいは上縁側でもよいものであり、ホルダーの一体
成型個数も広い部分に１個だけ設けてもよい視２個以上
に分割して設けてもよいものであって、その選択に当っ
ては前記昇降ならびに開閉方法とガラス板状体の大きさ
によるバランス、重量および形状等によって左右される
ものであり、またモール（ガスケットを含む）を一体成
型するガラス板状体周縁部の所要箇所とは、ガラス板状
体の少なくとも一辺から全周辺をいうものである。Further, the required portion of the peripheral portion of the glass plate in which the holder is integrally molded is preferably the lower edge side of the glass plate. One or both side edges or the upper edge side of the shape body may be provided, and the number of integrally molded holders may be provided in a wide portion. The selection depends on the lifting, opening and closing method and the balance, weight, shape, and the like of the size of the glass plate, and a glass plate formed integrally with a molding (including a gasket). The required portion of the peripheral portion means the entire periphery from at least one side of the glass plate.
【００３０】[0030]
【作用】前述したとおり、本発明のモールまたはホルダ
ー付ガラス板状体およびその製法によって、特異なホッ
トメルト性を有する、ことにポリイミド樹脂を含む特定
した接着性樹脂フイルムあるいは接着性樹脂フイルム状
層を、少なくともガラス板状体周縁部の所定箇所に被着
するように予めセットした状態で、ポリアミド層または
マトリックス相がポリアミド樹脂である多相熱可塑性樹
脂組成物でなるモールまたはホルダーを一体成型するこ
ととにしたので、樹脂フイルムまたは樹脂フイルム状層
自身を一種の溶融状態またはそれに近い状態にすること
となり、ガラス板状体とモールまたはホルダーとの融着
部をより強固で確実に理想的な一体化をなすことができ
るとともに、耐水性、耐候性、耐熱性、耐薬品性等耐久
性が増大、ことに耐熱性におけるせん断剥離強度が向上
することとなり、また従来のガラス板状体とモールまた
はホルダーとの接着では得られない、例えば接着性樹脂
フイルムまたはフイルム状層での一成分として、ポリア
ミドを配合することにより、該ポリアミド樹脂の融点よ
りはるかに低温での熱圧着による接着強度が向上するこ
ととなり、接着と成型とを同時かつ瞬時にできて高作業
効率ならびに工数が低減できて省力化ができ、さらには
作業環境の向上化がてきることなり、またガラス板状体
の曲率とのくるいを発現するようなこともなくて寸法精
度の向上をもたらし、かつガラス板状体の強度低下を来
しやすいものをさけることができて高品位となり、しか
もより軽量化、小型化ならびに薄肉厚化等が可能となる
などの数々の顕著な作用効果を奏するモールまたはホル
ダー付ガラス板状体とその製法を提供することができる
こととなって、車輌用ことに自動車用窓ガラス、とくに
昇降用窓ガラス、建築用窓ガラス、とくにドアガラス、
各種家具調度品等種々の用途に幅広く採用可能となるも
のである。According to the present invention, as described above, the adhesive resin film or the adhesive resin film layer having a specific hot-melt property, particularly containing a polyimide resin, is obtained by the method of the present invention. Is molded in advance in such a manner that the polyamide layer or the matrix phase is formed of a multi-phase thermoplastic resin composition in which the polyamide layer or the matrix phase is a polyamide resin in a state of being set in advance so as to be applied to at least a predetermined portion of the peripheral portion of the glass plate. As a result, the resin film or the resin film-like layer itself is brought into a kind of molten state or a state close to it, and the fused portion between the glass plate and the molding or holder is more firmly and ideally made. In addition to being able to be integrated, durability such as water resistance, weather resistance, heat resistance, and chemical resistance is increased. Incorporation of polyamide as one component in adhesive resin film or film-like layer, which results in improved shear peel strength in thermal properties and cannot be obtained by bonding conventional glass plate with molding or holder. Thereby, the adhesive strength by thermocompression bonding at a temperature much lower than the melting point of the polyamide resin will be improved, and bonding and molding can be performed simultaneously and instantly, and high working efficiency and man-hours can be reduced, and labor can be saved. Can improve the working environment, improve the dimensional accuracy without causing the curvature and curvature of the glass plate, and reduce the strength of the glass plate. High quality can be avoided by avoiding easy-to-use ones, and it has many remarkable effects such as lighter weight, smaller size and thinner wall. It becomes to be able to provide mall or a glass plate-like body with a holder and its manufacturing method, automotive window glass to be for a vehicle, in particular the lifting window glass, architectural window glass, in particular door glass,
It can be widely used for various applications such as various furniture furniture.
【００３１】[0031]
【実施例】以下、本発明の実施例を図面に従って説明す
る。ただし本発明は係る実施例に限定されるものではな
い。Embodiments of the present invention will be described below with reference to the drawings. However, the present invention is not limited to such an embodiment.
【００３２】図１に正面概略図で示すような、大きさ約
1000mmｘ800mm程度、板厚約４mm程度の所要形状を有す
るクリア・フロートガラス板状体２の自動車用サイドウ
インドウである昇降用ドアガラスの所要箇所の周縁部３
に、図４に拡大した部分側断面図で示すように、型６に
おけるホルダー４用液状合成樹脂を射出注入する直前で
樹脂フイルム５のセット状態でもって射出一体成形する
本発明のモールまたはホルダー付ガラス板状体の製法に
よって、図１においてＩーＩ視した図２および図３にホ
ルダー成型部を拡大した部分側断面図で示すような、側
断面を有する所期のホルダー４が一体に取付けられ、図
１に示す本発明のモールまたはホルダー付ガラス板状体
の一実施例であるホルダー付ガラス板状体１を得た。As shown in the schematic front view of FIG.
Peripheral edge 3 of a required portion of a door glass for elevation, which is a side window for an automobile, of a clear float glass plate 2 having a required shape of about 1000 mm x 800 mm and a thickness of about 4 mm.
As shown in an enlarged partial side sectional view of FIG. 4, a molding or a holder according to the present invention, which is integrally molded with the resin film 5 in a set state immediately before injection of the liquid synthetic resin for the holder 4 in the mold 6 . Due to the manufacturing method of the glass plate, an intended holder 4 having a side cross section is integrally attached as shown in a partial side sectional view in which the holder molding portion is enlarged in FIGS. was to obtain a mall or holder with a glass plate-like body 1 which is an embodiment of a glass plate body with the holder of the present invention shown in FIG.
【００３３】先ず、ベント装置付30mmφ二軸押出機を用
いて、設定温度約 260℃でもって、エチレンーα、βー
不飽和カルボン酸エステルー無水マレイン酸三元共重合
体としてポンダインTX8030〔エチレン／エチルアクリレ
ート／無水マレイン酸＝85/11.5/3.5 重量％、MRF=3.0g
/10 分(190℃、2160ｇ) 〕、およびポリアミド樹脂とし
てA1022S〔ポリアミドー６、相対粘度＝2.17dl/g、ユニ
チカ製〕を、重量部割合で７対３に溶融混練した接着組
成物とし、乾燥後、20mmφT ダイフイルム成形機を用い
て、設定温度約 260℃でフイルム化し、厚み約50μ、約
150 μ前後等の樹脂フイルム５を得て予め用意した。First, using a 30 mmφ twin screw extruder equipped with a vent device, at a set temperature of about 260 ° C., a terpolymer of ethylene-α, β-unsaturated carboxylic acid ester-maleic anhydride was prepared as Pondyne TX8030 [ethylene / ethyl Acrylate / maleic anhydride = 85 / 11.5 / 3.5% by weight, MRF = 3.0g
/ 10 min (190 ° C, 2160 g)], and A1022S (polyamide 6, relative viscosity = 2.17 dl / g, manufactured by Unitika) as a polyamide resin was melt-kneaded at a ratio of 7 to 3 by weight, and dried. After that, using a 20mmφT die film molding machine, the film is formed at a set temperature of about 260 ° C, and the thickness is about 50μ.
A resin film 5 of about 150 μm or the like was obtained and prepared in advance.
【００３４】次いで、図４に示すように、型６は下側部
分のコア型部材７と上側部分のキャビ型部材８とからな
り、両型部材７、８は開閉できる合せ型になっていて、
先ず両部分を開放してコア型部材７の挟持部９の緩衝材
でもあるシール材10上に、ガラス板状体２の周縁部３の
うち所要箇所周縁部表裏両面と端面11にかけて、３ーア
ミノプロピルトリエトキシシラン等のシランカップリン
グ剤でプライマー処理層12を施し、該処理部に予め上述
した約150 μ前後の樹脂フイルム５を囲繞するように被
着したガラス板状体２の周縁部３が所定部分に当接する
ように載置し、次に前記キャビ型部材８を緩衝材でもあ
るシール材10を介して約70℃前後の前記ガラス板状体２
の上部に当接し、約120 〜150kg ／cm2 程度の圧力で型
締めによって両型部材７、８の挟持部９でガラス板状体
２をクランプしてシールすることによってキャビティ空
間13を形成させセットを完了するものである。Next, as shown in FIG. 4, the mold 6 is composed of a core mold member 7 on the lower side and a mold mold member 8 on the upper side. ,
First, the both parts are opened, and a required portion of the peripheral part 3 of the glass plate body 2 is put on the sealing material 10 which is also a cushioning material of the holding part 9 of the core type member 7. The peripheral portion of the glass plate 2 which has been coated with the primer treatment layer 12 with a silane coupling agent such as aminopropyltriethoxysilane or the like so as to surround the above-mentioned resin film 5 of about 150 μm in advance in the treated portion. 3 is placed in contact with a predetermined portion, and then the mold member 8 is placed on the glass plate 2 at about 70 ° C. via a sealing material 10 which is also a cushioning material.
A glass space 2 is formed by clamping and sealing the glass plate 2 at the clamping portions 9 of the mold members 7 and 8 by clamping with a pressure of about 120 to 150 kg / cm 2. Complete the set.
【００３５】これに図示していない射出成形装置本体か
ら送られる、ポリアミド樹脂、例えばポリアミドー６あ
るいはポリアミドー66（PA-6,PA-66）と、ポリフェニレ
ンエーテル（PPE)および無水マレイン酸（MAH)、さらに
ガラスファイバー(GF)を溶融混練して得る組成物（PPE/
PA-6またはPA-66/MAH/GF=35/35/0.5/30 重量部）で、ポ
リアミド樹脂マトリックス中にポリフェニレンエーテル
が微分散している多相構造体であるホルダー４用液状合
成樹脂組成物を約240 〜280 ℃程度で、型温約70〜80℃
程度の条件にあるキャビティ空間13内にアフターミキサ
ー等を通って注入口から約110 〜130kg ／cm2 程度で約
60秒前後射出注入し一体成型し、該合成樹脂組成物が固
化した後、前記ガラス板状体２を前記型６から取り出す
ことによって図１乃至図３に示すように ガラス板状体
２の周縁部３の所要箇所にホルダー４を成型するもので
ある。A polyamide resin, for example, polyamide-6 or polyamide-66 (PA-6, PA-66), polyphenylene ether (PPE) and maleic anhydride (MAH) sent from an injection molding apparatus main body (not shown) Furthermore, a composition obtained by melt-kneading glass fiber (GF) (PPE /
PA-6 or PA-66 / MAH / GF = 35/35 / 0.5 / 30 parts by weight), a liquid synthetic resin composition for holder 4 which is a multiphase structure in which polyphenylene ether is finely dispersed in a polyamide resin matrix. About 240-280 ° C, mold temperature about 70-80 ° C
About 110 to 130 kg / cm 2 from the inlet through an after-mixer etc. in the cavity space 13 under the condition of about
After the injection and injection for about 60 seconds, the molding is performed and the synthetic resin composition is solidified. Then, the glass plate 2 is taken out from the mold 6 to remove the peripheral edge of the glass plate 2 as shown in FIGS. The holder 4 is molded at a required portion of the part 3.
【００３６】なお、上記した樹脂フイルムはガラス板状
体の所要箇所周縁部に被着するに際し、例えば前記樹脂
フイルムの周縁部を前記シール材で押え込むようにして
挟持して固定してもよく、場合によってはバリ発生の防
止策にすることもでき、また前記液状合成樹脂組成物の
射出注入口については形状によって上下２箇所あるいは
単に型周に数箇所設けてもよく、さらに各型部分は温度
制御ができるようにし適温に保持するものであり、こと
に熱ショックまたは前記合成樹脂組成物の発泡あるいは
スキン層の形成等を考慮して制御するものであり、いず
れにせよ随時、温度、注入場所、注入量等を調節しなが
ら射出注入できるようにすることは当然である。When the above-mentioned resin film is adhered to a peripheral portion of a required portion of the glass plate, for example, the peripheral portion of the resin film may be sandwiched and fixed by being pressed by the sealing material. Depending on the shape, the injection port of the liquid synthetic resin composition may be provided at two upper and lower locations or simply at several locations around the mold depending on the shape. It is intended to maintain a suitable temperature so that it can be controlled in consideration of heat shock or foaming of the synthetic resin composition or formation of a skin layer, and in any case, at any time, temperature, injection location, It is natural that injection injection can be performed while adjusting the injection amount and the like.
【００３７】得られたホルダー付ガラス板状体１は、図
１に示すように、略台形に切断加工したガラス板状体
２、とくにガラス板状体２の下辺の周縁部３に平面皿状
の凸状部14（必ずしもこのような形状でなくてもよい
し、場合によってはなくてもよい）を設け、該平面皿状
の凸状部14を囲繞する表裏両面の周縁部３から対応する
端面11にかけ、前記樹脂組成物による一体成形をして、
平面Ｔ形状であるホルダー４を固着して成り、該ホルダ
ー４は昇降装置（図示せず）に結合するためのガイドチ
ャンネル等を固定するねじ部15を有する舌片16を備えて
いるものであり、図２および図２のさらに部分拡大図で
ある図３に示すように、前記ガラス板状体２とカップリ
ング処理層12、該カップリング処理層12と樹脂フイルム
５、ならびに該樹脂フイルム５と合成樹脂組成物で成る
ホルダー４でなる構成とすることによって、該各間での
接着力はもちろん、全体としての接着力が顕著に向上す
るものである。As shown in FIG. 1, the obtained glass plate-like body 1 with a holder is formed into a substantially plate-shaped glass plate-like body 2, in particular, a flat plate-like shape on the lower peripheral edge 3 of the glass plate-like body 2. (It is not always necessary to have such a shape or may be omitted in some cases.), And the projections 14 correspond to the peripheral portions 3 on the front and back surfaces surrounding the flat dish-shaped projection 14. Over the end face 11, and integrally molded with the resin composition,
Made by fixing the holder 4 is a plan T shape, the holder 4 are those provided with a tongue 16 having a threaded portion 15 for fixing the guide channel or the like for coupling to the lifting device (not shown) 2 and FIG. 3, which is a partially enlarged view of FIG. 2, the glass plate 2 and the coupling treatment layer 12, the coupling treatment layer 12 and the resin film 5, and the resin film 5 By using the holder 4 made of the synthetic resin composition, not only the adhesive strength between the respective members but also the overall adhesive strength is remarkably improved.
【００３８】すなわち、該得られた本発明のホルダー付
ガラス板状体と、従来の前記樹脂フイルムなしである単
なる接着したものとで、せん断剥離強度を比較したとこ
ろ、例えば従来の樹脂フイルムなしでは約1.2 〜1.5kg
／cm2 程度あるいはそれ以下であったのが、本発明のホ
ルダー付ガラス板状体では約13kg／cm2 以上でも異常が
ないものであり、しかも耐熱性、ことに例えば約50〜70
℃程度で約３〜４時間程度の雰囲気に晒された後でも、
前記強度の向上がみられるものであった。That is, when the obtained glass plate-like body with a holder of the present invention and a mere bonded one without the conventional resin film were compared in terms of shear peel strength, for example, without the conventional resin film, About 1.2-1.5kg
/ Cm 2 or less, but the glass plate with a holder of the present invention has no abnormality even at about 13 kg / cm 2 or more, and has heat resistance, for example, about 50 to 70
Even after being exposed to the atmosphere for about 3 to 4 hours at about
The improvement in the strength was observed.
【００３９】上記本発明のホルダー付ガラス板状体の強
度は一体成形でない例えばシリコン等による従来の接着
法より格段に差がある極めて高いものである。また樹脂
フイルムとして例えば約300 〜350 μ程度の厚さのポリ
ビニルブチラール樹脂またはポリアセタール共重合体樹
脂、あるいは約150 μ程度の厚さのエチレン共重合体樹
脂を用い、前記と同様の成形樹脂を用いた同様の試作品
は前記強度の向上はほとんどみられないようなもの、あ
るいは所期のめざすものとはならないものであった。さ
らに上記本発明のホルダー付ガラス板状体の強度は本出
願人が既に出願提案した特開平１ー209116号公報に示す
ものの強度より、ことに耐熱性の点での強度がより向上
するものであった。なお、上記本発明のホルダー付ガラ
ス板状体は耐湿性（例えば約40〜50℃程度、約95〜98％
RH程度、約160 〜170H程度）および耐候性（約20℃前後
水浸漬、約160 〜170H程度）においても充分と言えるも
のであった。The strength of the above-mentioned glass plate with holder of the present invention is extremely high, which is markedly different from that of a conventional bonding method using, for example, silicon, which is not integrally formed. As the resin film, for example, a polyvinyl butyral resin or a polyacetal copolymer resin having a thickness of about 300 to 350 μm, or an ethylene copolymer resin having a thickness of about 150 μm is used. Similar prototypes had little or no improvement in the strength, or were not what was expected. Further, the strength of the glass plate with holder of the present invention is higher than the strength of the glass plate with holder of the present invention already proposed in Japanese Patent Application Laid-Open No. 1-209116, particularly in terms of heat resistance. there were. In addition, the glass plate-shaped body with a holder of the present invention has moisture resistance (for example, about 40 to 50 ° C., about 95 to 98%
RH, about 160-170H) and weather resistance (about 20 ° C immersion in water, about 160-170H) were satisfactory.
【００４０】[0040]
【発明の効果】以上前述したように、本発明によれば、
ガラス板状体に融着しかつモールまたはホルダー用合成
樹脂組成物とも一体化した融着をして傾斜組成的働きを
し、より効果的な一体成型化を達成することができ、各
物質間の接着強度を大きくし、従来にない全体としての
強度を付与し、ことに耐熱性における強度を向上させる
ことができ、とくにポリアミド樹脂の融点よりはるかに
低温での熱圧着による接着強度が向上し、さらに耐水性
が向上する等種々の作用効果をもたらすとともに、高級
観、高機能あるいは多機能指向にも対応し得ることとな
り、しかも作業の省力化および効率化ならびに高環境化
ができ、寸法精度等が向上し高品位で高生産性となるな
ど幅広い卓効を奏するものである有用なモールまたはホ
ルダー付ガラス板状体およびその製法を提供するもので
ある。As described above, according to the present invention,
It is fused to the glass plate and fused with the synthetic resin composition for moldings or holders to function as a gradient composition, achieving more effective integral molding. To increase the adhesive strength of the resin and to provide an unprecedented overall strength, and in particular to improve the strength in heat resistance, and especially to improve the adhesive strength by thermocompression bonding at a temperature much lower than the melting point of the polyamide resin. In addition to providing various functions and effects such as improved water resistance, it can also respond to high-grade, high-performance or multi-functional orientation, and can save labor and efficiency of work and environmental protection, and achieve dimensional accuracy. It is an object of the present invention to provide a useful molding or a glass plate with a holder, which has a wide range of effects such as improved high quality and high productivity, and a method for producing the same.
【図１】本発明の一実施例であるホルダー付ガラス板状
体の正面概略図である。FIG. 1 is a schematic front view of a glass plate with a holder according to an embodiment of the present invention.
【図２】図１においてＩーＩ視した、ホルダー一体成型
部を拡大した部分側断面図である。FIG. 2 is an enlarged partial side sectional view of the holder integrated molding portion, as viewed from II in FIG.
【図３】図２に示すホルダー一体成型部をさらに部分拡
大した側断面図である。FIG. 3 is a side cross-sectional view in which the holder integrally molded portion shown in FIG. 2 is further partially enlarged.
【図４】本発明による製法を実施する際の説明図で一体
成型前における型内セット状態を拡大して示す部分側断
面図である。FIG. 4 is a partial side cross-sectional view showing, in an enlarged scale, an in-mold set state before integral molding in an explanatory view when the manufacturing method according to the present invention is performed.
【符号の説明】１ ホルダー付ガラス板状体 ２ ガラス板状体 ３ 周縁部４ ホルダー ５ 樹脂フイルム６ 型 ７ コア型部材 ８ キャビ型部材 13 キャビティ空間[Description of Signs] 1 Glass plate with holder 2 Glass plate 3 Peripheral part 4 Holder 6 Resin film 6 type 7 Core type member 8 Cabi type member 13 Cavity space
フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ Ｃ０３Ｃ 27/12 Ｅ０６Ｂ 3/54 Ｚ Ｅ０６Ｂ 3/54 Ｂ６０Ｊ 1/17 Ｃ // Ｂ２９Ｋ 105:20 Ｂ２９Ｌ 31:30 (58)調査した分野(Int.Cl.7，ＤＢ名) B29C 45/14 B32B 27/28 B60J 1/00 B60J 1/17 C03C 27/06 C03C 27/12 E06B 3/54 Continued on the front page (51) Int.Cl. 7 Identification code FI C03C 27/12 E06B 3/54 Z E06B 3/54 B60J 1/17 C // B29K 105: 20 B29L 31:30 (58) Int.Cl. 7 , DB name) B29C 45/14 B32B 27/28 B60J 1/00 B60J 1/17 C03C 27/06 C03C 27/12 E06B 3/54
Claims (9)
樹脂フイルムまたは樹脂フイルム状層を少なくとも一枚
または一層でガラス板状体周縁部を囲繞するよう表裏両
面の周縁部から対応する端面にかけて被着し、射出成形
法により樹脂製のモールまたはホルダーを、該樹脂フィ
ルムまたは樹脂フィルム状層を設けたガラス板状体の周
縁部にて、ガラス板状体と一体成型した、モールまたは
ホルダー付ガラス板状体において、前記樹脂フイルムま
たは樹脂フイルム状層がエチレンーα、βー不飽和カル
ボン酸エステルー無水マレイン酸三元共重合体60〜95重
量％と、ポリアミド樹脂40〜５重量％とから成ることを
特徴とするモールまたはホルダー付ガラス板状体。1. An end face corresponding to a peripheral portion of a glass plate body from a peripheral portion on both front and back sides so as to surround a peripheral portion of the glass plate body with a resin film or at least one or more resin film-like layers at predetermined positions on the peripheral portion of the glass plate body. subjected deposited, a resin molding or the holder by injection molding, the resin film
Around a glass plate with a layer of
The resin film or the resin film-like layer is a ternary copolymer of ethylene-α, β-unsaturated carboxylic acid ester and maleic anhydride in a molding or a glass plate with holder , which is integrally molded with the glass plate at the edge. A glass plate having a molding or a holder, comprising 60 to 95% by weight of a combined resin and 40 to 5% by weight of a polyamide resin.
酸エステルー無水マレイン酸三元共重合体が、エチレン
単位40〜90重量％、α、βー不飽和カルボン酸アルキル
エステル単位55〜５重量％、無水マレイン酸単位0.1 〜
10重量％から成る共重合体であることを特徴とする請求
項１記載のモールまたはホルダー付ガラス板状体。2. The ethylene-α, β-unsaturated carboxylic acid ester-maleic anhydride terpolymer comprises 40 to 90% by weight of ethylene units and 55 to 5% by weight of α, β-unsaturated carboxylic acid alkyl ester units. , Maleic anhydride unit 0.1 ~
3. The glass plate with a molding or a holder according to claim 1, which is a copolymer comprising 10% by weight.
ポリアミド樹脂または、マトリックス相がポリアミド樹
脂である多相熱可塑性樹脂から成ることを特徴とする請
求項１記載のモールまたはホルダー付ガラス板状体。3. The resin molding or holder,
2. A molding or a glass plate with a holder according to claim 1, wherein said glass plate is made of a polyamide resin or a multi-phase thermoplastic resin whose matrix phase is a polyamide resin.
ある多相熱可塑性樹脂が、ポリアミド樹脂と、ポリフェ
ニレンエーテルまたはポリプロピレンあるいはＡＢＳか
ら得られる樹脂組成物であることを特徴とする請求項３
記載のモールまたはホルダー付ガラス板状体。4. The matrix phase is a polyamide resin.
4. The resin composition according to claim 3, wherein the certain thermoplastic resin is a polyamide resin and a resin composition obtained from polyphenylene ether, polypropylene or ABS.
The glass plate-like body with the molding or holder described in the above.
ある多相熱可塑性樹脂が、ポリアミド樹脂と、ポリフェ
ニレンエーテルまたはポリプロピレンあるいはＡＢＳ、
およびガラス繊維から得られる樹脂組成物であることを
特徴とする請求項３記載のモールまたはホルダー付ガラ
ス板状体。5. The matrix phase is a polyamide resin.
Certain multi-phase thermoplastics comprise a polyamide resin and polyphenylene ether or polypropylene or ABS,
The molding or the glass plate-like body with a holder according to claim 3, which is a resin composition obtained from a glass fiber.
またはポリアミドー６６であることを特徴とする請求項
４または５記載のモールまたはホルダー付ガラス板状
体。6. The method according to claim 1, wherein the polyamide resin is polyamide-6.
6. The glass plate with a molding or a holder according to claim 4, wherein the glass plate is a polyamide 66.
ある多相熱可塑性樹脂が、ポリアミド樹脂と、ポリフェ
ニレンエーテルおよび相溶性改良剤からなる樹脂組成物
であることを特徴とする請求項３記載のモールまたはホ
ルダー付ガラス板状体。7. The matrix phase is a polyamide resin.
4. A molding or a glass plate with a holder according to claim 3, wherein the certain multi-phase thermoplastic resin is a resin composition comprising a polyamide resin, polyphenylene ether and a compatibility improver.
のモールまたはホルダーを一体成形して固着するに際
し、前記所要箇所に、エチレンーα、βー不飽和カルボ
ン酸エステルー無水マレイン酸三元共重合体60〜95重量
％と、ポリアミド樹脂40〜５重量％とから成る樹脂フイ
ルムまたは樹脂フイルム状層を含む少なくとも一枚また
は一層を、予め囲繞するよう表裏両面の周縁部から対応
する端面にかけて被着し、該ガラス板状体を型内に配置
して型締めし、前記樹脂フイルムの表面と該型内面とか
らなるキャビティ空間に、ポリアミド樹脂または、マト
リックス相がポリアミド樹脂である多相熱可塑性樹脂か
ら成る樹脂組成物を射出注入し、該樹脂組成物が固化し
た後、前記ガラス板状体を前記型から取り出すことを特
徴とするモールまたはホルダー付ガラス板状体の製法。8. When a resin molding or a holder is integrally molded and fixed to a required portion of the peripheral portion of the glass plate-like body, ethylene-α, β-unsaturated carboxylic acid ester-maleic anhydride ternary component is added to the required portion. At least one or more layers including a resin film or a resin film-like layer composed of 60 to 95% by weight of a copolymer and 40 to 5% by weight of a polyamide resin are preliminarily surrounded from the peripheral portions of both front and back surfaces to the corresponding end surfaces. The glass plate is placed in a mold and clamped. The multi-phase heat in which a polyamide resin or a matrix phase is a polyamide resin is provided in a cavity space defined by the surface of the resin film and the inner surface of the mold. A resin composition comprising a plastic resin is injected and injected, and after the resin composition is solidified, the glass plate is removed from the mold. Manufacturing method of a glass plate-like body with Zehnder.
ある多相熱可塑性樹脂が、ガラス繊維を含むことを特徴
とする請求項８記載のモールまたはホルダー付ガラス板
状体の製法。9. The matrix phase is a polyamide resin.
9. The method for producing a molding or a glass plate with a holder according to claim 8, wherein a certain multi-phase thermoplastic resin contains glass fibers.