Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【産業上の利用分野】本発明は、脱酸素剤包装体に係わ
り、さらに詳しくは、微細孔を有するプラスチック積層
フィルムと不織布、微多孔膜及び自己ヒートシール性を
有する耐水耐油性の混抄紙よりなる群から選ばれた一種
の微細孔フィルムをラミネートしてなるフィルムを脱酸
素剤の包装材料として用いた脱酸素剤包装体に関する。
該脱酸素剤包装体は、安定した脱酸素性能を発揮するた
め、加工食品の保存剤として広い範囲で使用される。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an oxygen-absorbing agent package, and more particularly to a laminated plastic film having fine pores and a nonwoven fabric, a microporous film, and a water- and oil-resistant mixed paper having self-heat-sealing properties. The present invention relates to an oxygen-absorbing agent package using a film obtained by laminating a kind of microporous film selected from the group as a packaging material for an oxygen-absorbing agent.
The oxygen scavenger package is used in a wide range as a preservative for processed foods in order to exhibit stable oxygen scavenging performance.

【０００２】[0002]

【従来の技術】脱酸素剤は、酸素を吸収する性質を有す
る組成物であり、通常、通気性の小袋に封入して用いら
れる。一般に、脱酸素剤を封入する通気性小袋を構成す
る包装材料（以下「包材」と記す）には、例えば、紙と
有孔ポリエチレンフィルムをラミネートした包材、穿孔
プラスチックフィルムと紙と有孔ポリエチレンフィルム
を積層接着した包材、不織布や微多孔膜などを使用した
包材が用いられている。2. Description of the Related Art An oxygen scavenger is a composition having a property of absorbing oxygen, and is usually used by being enclosed in a gas-permeable small bag. In general, a packaging material (hereinafter referred to as a “wrapping material”) constituting a breathable pouch for enclosing an oxygen scavenger is, for example, a packaging material in which paper and a perforated polyethylene film are laminated, a perforated plastic film, a paper and a perforated material. A packaging material in which a polyethylene film is laminated and bonded, and a packaging material using a nonwoven fabric or a microporous film are used.

【０００３】[0003]

【発明が解決しようとする課題】脱酸素剤を用いた食品
保存技術上の問題点として、脱酸素剤は、乾燥食品、高
水分食品、酸性食品、油加工食品、アルコール含有食品
等の種々の食品に使用するため、脱酸素剤組成物中に含
まれる水分が乾燥食品に移行してし脱酸素性能が損われ
たり、高水分食品の水分が脱酸素剤組成物に移行するた
め、包材の表面に染みが発生して外観を損なったり、食
品の油が包材にしみ込み、包材の透気性が損なわれて脱
酸素性能が損われる。このような欠点を有するため、脱
酸素剤を使用する場合、状況に応じて包材の材質、構成
などを変えて対応しているのが現状である。As a problem in food preservation technology using an oxygen scavenger, oxygen scavengers are used in various types of foods such as dry foods, high moisture foods, acidic foods, oil processed foods, and alcohol-containing foods. For use in food, moisture contained in the oxygen scavenger composition migrates to the dried food and the oxygen scavenging performance is impaired, or the moisture of the high moisture food migrates to the oxygen scavenger composition, so the packaging material Stain occurs on the surface of the packaging material to impair the appearance, and oil of food permeates the packaging material, impairing the air permeability of the packaging material and deoxidizing performance. Due to these disadvantages, the use of oxygen scavengers is currently being addressed by changing the material and configuration of the packaging material depending on the situation.

【０００４】近年は、脱酸素剤の適用分野が多岐にわた
り、使用条件が過酷となる傾向にあるため、微多孔膜な
どを用いた耐久性の優れた包装材料が多用されている。
例えば、従来の不織布、微多孔膜若しくは耐水耐油性加
工紙を用いた包材として、不織布、微多孔膜若しくは耐
水耐油性加工紙に、ポリエチレン、ポリエチレン酢ビ共
重合体、アイオノマー樹脂等からなる低融点のシーラン
トフィルムを熱ラミネートしたものや、微多孔膜より低
い軟化点と高い軟化点を有するフィルムの有孔プラスチ
ック積層フィルムの低い軟化点を有するフィルム層を熱
ラミネート層とした包材が多く使用されているが、熱ラ
ミネート加工の際に低融点フィルムが熔融し、有孔プラ
スチックフィルムの開孔された径の小さい孔が塞がり、
透気性が低下することにより安定した透気度を確保する
ことができないなど、脱酸素剤用包材として改善すべき
点が多々認められた。[0004] In recent years, the application fields of oxygen scavengers have been diversified, and the use conditions have tended to be severe. Therefore, highly durable packaging materials using a microporous membrane or the like have been frequently used.
For example, as a packaging material using a conventional nonwoven fabric, microporous membrane or water- and oil-resistant processed paper, a nonwoven fabric, microporous membrane or water- and oil-resistant processed paper, and a low-density resin made of polyethylene, polyethylene acetic acid vinyl copolymer, ionomer resin, etc. Most often used are heat-laminated sealant films with a melting point, and packaging materials that have a film layer with a lower softening point as a heat-laminated layer of a perforated plastic laminated film of a film with a lower softening point and a higher softening point than a microporous film. However, during the heat laminating process, the low-melting point film melts, and the small-diameter holes that are opened in the perforated plastic film are closed,
There were many points that should be improved as a packaging material for oxygen scavengers, such as the inability to secure stable air permeability due to reduced air permeability.

【０００５】本発明は、上記の実情からみてなされたも
ので、製造及び製袋が容易で、かつ、安定した透気性、
シール強度、ラミネート強度を有するだけでなく、耐水
性、耐油性などの耐久性に優れ、安定した脱酸素性能を
発揮することのできる脱酸素剤用包材を用いてなる脱酸
素剤包装体を提供することを目的とする。[0005] The present invention has been made in view of the above circumstances, is easy to manufacture and bag making, and has a stable air permeability,
Oxygen absorber packaging using a packaging material for oxygen absorber that not only has sealing strength and lamination strength, but also has excellent durability such as water resistance and oil resistance, and can exhibit stable oxygen absorption performance. The purpose is to provide.

【０００６】[0006]

【課題を解決するための手段】本発明者等は、前記目的
を達成すべく鋭意研究した結果、特定の有孔プラスチッ
ク積層フィルム（Ａ）と微細孔フィルム（Ｂ）とを貼り
合わせて得られるガ−レ−式透気度が 1〜 10,000 秒／
100 ml である脱酸素剤用包装材料（Ｃ）を用い、該包
装材料（Ｃ）を構成する積層フィルム（Ａ）層を外側に
して脱酸素剤を包装し、シ−ルしてえられる脱酸素剤包
装体が、前記目的を達成することができること見出し、
本発明を完成した。Means for Solving the Problems The inventors of the present invention have conducted intensive studies to achieve the above object, and as a result, they have been obtained by laminating a specific perforated plastic laminated film (A) and a microporous film (B). Galley-type air permeability is 1 to 10,000 seconds /
Using a 100 ml oxygen-absorbing agent packaging material (C), the oxygen-absorbing agent is packaged with the laminated film (A) layer constituting the packaging material (C) facing outside, and the oxygen-absorbing agent is obtained by sealing. Finding that the oxygen agent package can achieve the above object,
The present invention has been completed.

【０００７】本発明は、下記の有孔プラスチック積層フ
ィルム（Ａ）と微細孔フィルム（Ｂ）とを貼り合わせて
得られるガ−レ−式透気度が 1〜 10,000 秒／ 100 ml
である脱酸素剤用包装材料（Ｃ）を用い、該包装材料
（Ｃ）を構成する積層フィルム（Ａ）層を外側にして脱
酸素剤を包装し、シ−ルしてなることを特徴とする脱酸
素剤包装体である。有孔プラスチック積層フィルム
（Ａ）：微細孔フィルム（Ｂ）と貼り合わせるフィルム
層（ａ）と他のフィルム層（ｂ）とから構成され、フィ
ルム層（ａ）の軟化点が、微細孔フィルム（Ｂ）の軟化
点以上であり、かつフィルム層（ｂ）より低い軟化点を
有する有孔プラスチック積層フィルム 微細孔フィルム（Ｂ）：常圧で水を通さない不織布、微
多孔膜であるプラスチックフィルム及び耐水耐油性の混
抄紙よりなる群から選ばれた一種の自己ヒートシール性
を有する微細孔フィルムAccording to the present invention, a Gurley-type air permeability obtained by laminating the following perforated plastic laminated film (A) and microporous film (B) is 1 to 10,000 seconds / 100 ml.
The packaging material for oxygen scavenger (C) is used, and the oxygen scavenger is packaged and sealed with the laminated film (A) layer constituting the packaging material (C) outside. It is a oxygen absorber package. Perforated plastic laminated film (A): Consists of a film layer (a) to be bonded to a microporous film (B) and another film layer (b), and the softening point of the film layer (a) is determined by the microporous film ( Perforated plastic laminated film having a softening point equal to or higher than B) and having a lower softening point than the film layer (b) Microporous film (B): a nonwoven fabric which is impermeable to water at normal pressure, a plastic film which is a microporous film, and A kind of self-heat sealing microporous film selected from the group consisting of water and oil resistant mixed paper

【０００８】以下、本発明を詳細に説明する。本発明に
おいて、有孔プラスチック積層フィルム（Ａ）とは、前
記の微細孔フィルム（Ｂ）と貼り合わせるフィルム層
（ａ）と他のフィルム層（ｂ）とから構成され、フィル
ム層（ａ）の軟化点が、微細孔フィルム（Ｂ）の軟化点
以上であり、かつフィルム層（ｂ）より低い軟化点を有
する有孔プラスチック積層フィルムである。該積層フィ
ルムは、フィルム層（ａ）の一層とフィルム層（ｂ）の
少なくとも一層とからなる二層以上の積層フィルムであ
って、孔径：１０〜５００μｍ、好ましくは５０〜２５
０μｍで開孔率 0.005〜15％、好ましくは 0.01 〜５％
の微細孔を有し、厚さが１０〜２００μｍ、好ましくは
１２〜５０μｍの透気性のプラスチックフィルムであ
る。Hereinafter, the present invention will be described in detail. In the present invention, the perforated plastic laminated film (A) is composed of a film layer (a) bonded to the microporous film (B) and another film layer (b). A perforated plastic laminated film having a softening point equal to or higher than the softening point of the microporous film (B) and having a lower softening point than the film layer (b). The laminated film is a laminated film of two or more layers composed of one layer of the film layer (a) and at least one layer of the film layer (b), and has a pore diameter of 10 to 500 μm, preferably 50 to 25 μm.
0.005 to 15%, preferably 0.01 to 5% porosity at 0 μm
And an air-permeable plastic film having a thickness of 10 to 200 μm, preferably 12 to 50 μm.

【０００９】例えば、前記フィルム層（ｂ）のフィルム
は、フィルム層（ａ）より、通常１０℃以上高い軟化点
を有するものが用いられる。また、フィルム層（ｂ）と
しては、ポリエチレンテレフタレート、ナイロン、ポリ
プロピレン等が用いられ、フィルム層（ａ）としては、
ＬＬＤＰＥ、ポリプロピレン等である。また、フィルム
層（ａ）として、ＬＤＰＥ、ＥＶＡコポリマー、アイオ
ノマーフィルム等の低温ヒートシール性の良好なシーラ
ントフィルムも使用可能であり、主に微細孔を有するフ
ィルム（Ｂ）と同一の材質が好んで用いられる。For example, a film having a softening point higher than that of the film layer (a) by 10 ° C. or more is used for the film (b). As the film layer (b), polyethylene terephthalate, nylon, polypropylene or the like is used. As the film layer (a),
LLDPE, polypropylene and the like. Further, as the film layer (a), a sealant film having good low-temperature heat sealability such as LDPE, EVA copolymer, and ionomer film can be used, and the same material as the film (B) having mainly micropores is preferably used. Used.

【００１０】また、フィルム層（ａ）は、微細孔を有す
るフィルム（Ｂ）の軟化点と同じか若しくは高いものが
用いられ、従来の様にフィルム層（ａ）に該（Ｂ）より
も低い軟化点を有する材質を使用した場合に比較して、
該（Ｂ）の包材特性を低下させずに微細孔を有するフィ
ルム（Ｂ）とのラミネートが可能となる。なお、フィル
ムの積層は、融着、接着、圧着、ドライラミネート法又
は押出しラミネート等によって製造することが可能であ
るが、主に同一の材質の場合は、熱融着法がより好まし
い。The film layer (a) has a softening point equal to or higher than the softening point of the film (B) having fine pores, and the film layer (a) has a lower softening point than that of the film (B). Compared to using a material with a softening point,
Laminating with the film (B) having micropores is possible without lowering the packaging material properties of (B). The lamination of the films can be manufactured by fusion, adhesion, pressure bonding, dry lamination, extrusion lamination, or the like. In the case of mainly using the same material, the thermal fusion is more preferable.

【００１１】有孔プラスチック積層フィルム（Ａ）フィ
ルムの孔径が１０μｍ以下だと透気度が不足し、５００
μｍ以上だと外部から、水、油、酸、アルコールなどの
液体が浸入しやすく、耐久性に劣り望しくない。一方、
フィルムの厚さが１０μｍ以下では、薄すぎて加工が困
難であるのみならず耐久性に劣り、５００μｍ以上では
フィルムのフレキシビリティに欠けて望しくない。If the hole diameter of the perforated plastic laminated film (A) film is 10 μm or less, the air permeability is insufficient, and
If it is more than μm, liquids such as water, oil, acid, alcohol and the like easily penetrate from the outside, resulting in poor durability and undesirable. on the other hand,
When the thickness of the film is 10 μm or less, the film is too thin to be processed, and also has poor durability. When the thickness is 500 μm or more, the film lacks flexibility and is not desirable.

【００１２】本発明において、微細孔フィルム（Ｂ）と
は、常圧で水を通さない不織布、微多孔膜であるプラス
チックフィルム及び自己ヒートシール性を有する耐水耐
油性の混抄紙よりなる群から選ばれた一種の微細孔フィ
ルムである。In the present invention, the microporous film (B) is selected from the group consisting of a nonwoven fabric which is impermeable to water at normal pressure, a plastic film which is a microporous film, and a water- and oil-resistant mixed paper having self-heat sealing properties. It is a kind of microporous film.

【００１３】常圧で水を通さない不織布としては、ポリ
オレフィン、ポリエステル等からなる不織布であり、ガ
ーレー式透気度が、通常、約 0.01 〜 1,000秒／100 ml
であって、常圧で水を通さないものである。例えばばタ
イベック（デュポン社製）、ルクサー（旭化成工業
（株）製）などが知られている。The non-woven fabric that is impermeable to water at normal pressure is a non-woven fabric made of polyolefin, polyester, or the like, and has a Gurley-type air permeability of usually about 0.01 to 1,000 seconds / 100 ml.
And it is impervious to water at normal pressure. For example, Tyvek (manufactured by DuPont), Luxer (manufactured by Asahi Kasei Corporation) and the like are known.

【００１４】微多孔膜であるプラスチックフィルムとし
ては、孔径が 0.01〜50μｍの微細孔を有し、ガーレー
式透気度が通常、約0.01〜1,000 秒/100mlであって常圧
で水を通さないものである。微多孔膜はポリエチレン、
ポリプロピレンなどの合成樹脂フィルムを延伸して製造
されるが、その際、シリカ、タルク、炭酸カルシウム等
の微粉末を添加してフィルムを延伸し、微粉末を含有す
るフィルムから微粉末を抽出するなどの方法により製造
したものである。例えば、ＮＦシート（徳山曹達（株）
製）、ポーラム（徳山曹達（株）製）、セルポア（積水
化学工業（株）製）、ＦＰ−２（旭化成工業（株）
製）、ＮＯＰ（日本石油化学（株）製）、ニトフロンＮ
ＴＦ（日東電気工業（株）製）、ポリフロンペーパー
（ダイキン工業（株）製）、ジュラガード（セラニーズ
社製）、ゴーアテックス（ゴア社製） 、ＴＳＦ（興人
（株）製）等が知られている。The plastic film which is a microporous film has fine pores having a pore size of 0.01 to 50 μm, and has a Gurley-type air permeability of usually about 0.01 to 1,000 sec / 100 ml, and is impermeable to water at normal pressure. Things. The microporous membrane is polyethylene,
It is manufactured by stretching a synthetic resin film such as polypropylene.At that time, the film is stretched by adding fine powder such as silica, talc, calcium carbonate, etc., and the fine powder is extracted from the film containing the fine powder. Manufactured by the method described above. For example, NF sheet (Tokuyama Soda Co., Ltd.)
Porum (manufactured by Tokuyama Soda Co., Ltd.), Cellpore (manufactured by Sekisui Chemical Co., Ltd.), FP-2 (Asahi Kasei Kogyo Co., Ltd.)
NOP (Nippon Petrochemical Co., Ltd.), Nitoflon N
TF (manufactured by Nitto Denki Kogyo), Polyflon Paper (manufactured by Daikin Industries, Ltd.), Juraguard (manufactured by Celanese), Gore-Tex (manufactured by Gore), TSF (manufactured by Kojin) Are known.

【００１５】自己ヒートシール性を有する耐水耐油性の
混抄紙としては、ガーレー式透気度が 1〜1,000 秒／10
0 mlであり、かつ常圧で水を通さない熱可塑性のプラス
チックと熱不溶性のプラスチックもしくは紙からなる二
種以上の材料を選択し、抄紙してなるガス透過性フィル
ムである。このような包装材料としては、パルプにポリ
エチレン、ポリプロピレン等を抄紙してなる紙／熱可塑
性プラスチック系の混抄紙などであるが、ポリプロピレ
ン等を単独に抄紙したいわゆる合樹紙、ポリエチレンテ
レフタレート等の熱不溶性、又は高融点の熱可塑性プラ
スチックを芯として、ポリエチレン等の低融点の熱可塑
性プラスチックで被覆した繊維からなる不織布等の使用
も可能である。また、このような混抄紙は、撥水、撥油
処理等を施してあり、坪量が10〜 150g/m²、好ましく
は、12〜 100g/m²で、熱可塑性プラスチックの混抄率が
20 〜 80 % 、好ましくは、 30 〜 70 % である撥水撥
油性のガス透過性フィルムである。As a water- and oil-resistant mixed paper having self-heat sealing properties, Gurley-type air permeability is 1 to 1,000 sec / 10
It is a gas-permeable film made of two or more kinds of thermoplastic plastics and heat-insoluble plastics or papers which are 0 ml and which are impermeable to water at normal pressure. Examples of such packaging materials include paper / thermoplastic plastic mixed paper made of pulp made of polyethylene, polypropylene, etc., and so-called synthetic wood paper made of polypropylene alone or polyethylene terephthalate. It is also possible to use a non-woven fabric or the like made of fibers coated with a low-melting thermoplastic such as polyethylene with an insoluble or high-melting thermoplastic as a core. Further, such mixed paper has been subjected to water repellency, oil repellent treatment, etc., and has a basis weight of 10 to 150 g / m ² , preferably 12 to 100 g / m ² , and a mixing ratio of the thermoplastic plastic.
A water-repellent and oil-repellent gas-permeable film having a content of 20 to 80%, preferably 30 to 70%.

【００１６】また、このような自己ヒートシール性を有
する微多孔膜、不織布若しくは耐水耐油性の混抄紙は、
有孔プラスチック積層フィルム（Ａ）と貼り合わせて脱
酸素剤用の包装材料としており、微多孔膜、不織布若し
くは耐水耐油性の混抄紙は、自己ヒートシール性を有す
る微細孔を有するフィルムとして、包装材料の透気性を
付与するだけでなく、該脱酸素剤用包装材料（Ｃ）のシ
ール層として働く。したがって、該脱酸素剤用包装材料
の製袋性、ヒートシール性等の向上を目的として、該脱
酸素剤用包装材料の内側に改めてシール層、補強用にワ
リフ等の補強材を設ける必要がない。しかし、該脱酸素
剤用包装材料の内側にシール層として、有孔のプラスチ
ックフィルムのラミネート加工、又は樹脂の押出ラミネ
ート加工、印刷法、塗布法等によって多数の筋状若しく
は微細な網目状に形成してもなんら差し支えない。ただ
し、シール層の樹脂の軟化点は、微細孔を有するフィル
ム（Ｂ）と同等以下でなければならない。Further, such a microporous membrane, nonwoven fabric or water- and oil-resistant mixed paper having self-heat-sealing properties is
It is bonded to the perforated plastic laminated film (A) and used as a packaging material for an oxygen scavenger. A microporous membrane, nonwoven fabric or water- and oil-resistant mixed paper is packaged as a film with self-heat-sealing micropores. Not only does the material provide air permeability, but also acts as a seal layer for the oxygen-absorbing agent packaging material (C). Therefore, for the purpose of improving the bag making property, heat sealing property, etc. of the oxygen scavenger packaging material, it is necessary to newly provide a sealing layer inside the oxygen scavenger packaging material, and a reinforcing material such as a warif for reinforcement. Absent. However, as a sealing layer inside the oxygen-absorbing agent packaging material, a large number of streaks or fine meshes are formed by laminating a perforated plastic film, or extruding laminating a resin, printing, coating or the like. It doesn't hurt anything. However, the softening point of the resin of the sealing layer must be equal to or less than that of the film (B) having micropores.

【００１７】本発明において使用される脱酸素剤用包材
（Ｃ）のガーレー式透気度は、 1〜10,000 秒／100ml
の範囲である。透気度は、有孔プラスチック積層フィル
ム（Ａ）の孔径の大小、孔数、使用される微細孔を有す
るフィルム（Ｂ）の種類及び有孔プラスチック積層フィ
ルム（Ａ）との貼り合わせ条件で決まる。該脱酸素剤用
包材の透気度に加えて、接着強度、製袋の容易さ、包装
密封された脱酸素剤がこぼれない、耐錆性等の耐久性な
どの諸因子を考慮して包材構成が決められる。The Gurley-type air permeability of the packaging material for oxygen scavenger (C) used in the present invention is 1 to 10,000 seconds / 100 ml.
Range. The air permeability is determined by the size and the number of pores of the perforated plastic laminated film (A), the number of holes, the type of the film (B) having micropores to be used, and the bonding conditions with the perforated plastic laminated film (A). . In addition to the air permeability of the packaging material for oxygen scavenger, taking into account various factors such as adhesive strength, ease of bag making, the oxygen scavenger sealed and spilled, and durability such as rust resistance. The packaging material configuration is determined.

【００１８】本発明は、前記脱酸素剤用包材（Ｃ）を、
包装材料の（Ａ）を外側にして脱酸素剤の包装材料の両
面又は片面として用い、片面の場合は別の片面にプラス
チック積層フィルム若しくは微細孔を有するフィルムを
用いて脱酸素剤を包装し、シ−ルした脱酸素剤包装体で
あるため、微細孔を有するフィルム（Ｂ）の特徴を生か
せるので、使用用途、使用形態、作業方法などを考慮し
て適宜包材の選択が可能である。なお、脱酸素剤用包材
を片面の場合、別の片面には主として非通気性のプラス
チック積層フィルムが用いられるが、必要に応じて、耐
久性等の実用上の問題のない範囲で微細孔を有するフィ
ルムを使用してもよい。In the present invention, the packaging material for oxygen scavenger (C)
Using the packaging material (A) as the outside and using it as both sides or one side of the oxygen absorber packaging material, in the case of one side, packaging the oxygen absorber using a plastic laminated film or a film having micropores on another side, Since it is a sealed oxygen absorber package, the characteristics of the film (B) having micropores can be utilized, so that the packaging material can be appropriately selected in consideration of the intended use, use form, work method, and the like. When the oxygen-absorbing packaging material is on one side, a non-breathable plastic laminated film is mainly used on the other side. If necessary, fine pores may be used as long as there is no practical problem such as durability. May be used.

【００１９】前記脱酸素剤用包材（Ｃ）に包装する脱酸
素剤としては、亜硫酸塩、亜硫酸水素塩、亜ニチオン酸
塩、ヒドロキノン、カテコール、レゾルシン、ピロガロ
ール、没食子酸、鉄粉等の金属粉、アスコルビン酸等を
含有するものが使用され、特に限定されない。Examples of the oxygen scavenger to be packaged in the oxygen scavenger packaging material (C) include metals such as sulfites, bisulfites, nitrites, hydroquinone, catechol, resorcinol, pyrogallol, gallic acid and iron powder. A powder containing powder, ascorbic acid and the like is used and is not particularly limited.

【００２０】[0020]

【作用】本発明は、有孔プラスチック積層フィルム
（Ａ）と不織布、微多孔膜及び自己ヒートシール性を有
する耐水耐油性の混抄紙よりなる群から選ばれた一種の
微細孔を有するフィルム（Ｂ）をラミネートした脱酸素
剤用包材（Ｃ）フィルムを脱酸素剤包装体の包装材料と
して、両面又は片面に用い、（Ａ）を外側にして脱酸素
剤を包装し、該脱酸素剤用包材は、該包材の内側の微細
孔を有するフィルム（Ｂ）自体に自己ヒートシール性の
ない素材を採用せず、自己ヒートシール性を有する包材
に限定し、外側の有孔プラスチック積層フィルム（Ａ）
も（Ａ）を構成するフィルムの低い軟化点を有するフィ
ルム層（ａ）が、該（Ｂ）と同じか若しくは高い軟化点
を有し、かつヒートシール可能な樹脂層を有する積層フ
ィルムに限定した包材構成で加工されている。According to the present invention, there is provided a film having a kind of fine pores (B) selected from the group consisting of a perforated plastic laminated film (A), a nonwoven fabric, a microporous film and a water- and oil-resistant mixed paper having self-heat-sealing properties. ) Is laminated on both sides or one side as a packaging material for an oxygen-absorbing agent package, and the oxygen-absorbing agent is packaged with (A) on the outside. The packaging material is not limited to the self-heat-sealing material, but is not limited to the self-heat-sealing material. Film (A)
Also, the film layer (a) having a low softening point of the film constituting (A) is limited to a laminated film having the same or higher softening point as (B) and having a heat-sealable resin layer. It is processed in a packaging material configuration.

【００２１】有孔プラスチック積層フィルム（Ａ）は、
フィルム積層後の開孔工程にて開孔し、更に微細孔を有
するフィルム（Ｂ）をラミネートする工程となっている
ので、該脱酸素剤用包材の加工工程において、開孔工程
後に一回のラミネート工程しかへていないのでラミネー
ト時の加熱による包材のダメージが抑えられるだけでな
く、有孔プラスチック積層フィルム（Ａ）の前述フィル
ム層（ａ）、（ｂ）の各軟化点が、フィルム層（ａ）は
（ｂ）より低く、フィルム層（ａ）は微細孔を有するフ
ィルム（Ｂ）の軟化点よりも同じか若しくは高いので、
微細孔を有するフィルム（Ｂ）の軟化点が最も低い場合
と異なり有孔プラスチック積層フィル（Ａ）閉孔も防止
できる。つまり、微細孔を有するフィルム（Ｂ）自体が
有している透気度の極端な低下もなく安定した包材性能
が確保できる。The perforated plastic laminated film (A) is
Since the film is opened in the opening step after lamination of the film and the film (B) having fine pores is further laminated, in the processing step of the oxygen-absorbing material packaging, once after the opening step, In this case, damage to the packaging material due to heating during lamination is suppressed, and the softening points of the film layers (a) and (b) of the perforated plastic laminated film (A) are Since layer (a) is lower than (b) and film layer (a) is the same or higher than the softening point of film (B) having micropores,
Unlike the case where the film (B) having micropores has the lowest softening point, it is possible to prevent the perforated plastic laminate fill (A) from closing. In other words, stable performance of the packaging material can be secured without an extreme decrease in the air permeability of the film (B) having the micropores.

【００２２】従来の様に孔径の小さい有孔プラスチック
積層フィルムと微細孔を有するフィルムを有孔プラスチ
ック積層フィルムの低い軟化点を有するフィルム層を接
着層として積層して後、更に、微細孔を有するフィルム
の別の片面に有孔の低融点のシーラントフィルムをラミ
ネート加工する方法等の包材構成では、開孔後に複数の
熱履歴を経るので、ラミネート加工時の熱で低い軟化点
を有するフィルム層の樹脂が熔溶し、孔径の小さな孔が
塞がって安定した透気度が得られない。また、加工順序
を変えても、同様の理由で有孔の低融点のシーラントフ
ィルム又は、有孔プラスチック積層フィルムのいずれか
の孔が塞がり透気度の確保、調整が難しく、かつ加工が
困難である等の欠点を解決した。A laminated plastic film having a small pore size and a film having fine pores as in the prior art are laminated with a film layer having a low softening point of the laminated plastic film having pores as an adhesive layer. In a packaging material structure such as a method of laminating a perforated low-melting sealant film on another side of the film, a film layer having a low softening point due to heat during lamination because a plurality of heat histories are passed after opening. Resin is melted, and pores having a small diameter are closed, and stable air permeability cannot be obtained. In addition, even if the processing order is changed, for the same reason, one of the holes of the perforated low-melting-point sealant film or the perforated plastic laminated film is closed and the air permeability is difficult to secure, adjustment is difficult, and processing is difficult. Some disadvantages were solved.

【００２３】微細孔を有するフィルム（Ｂ）は、単に、
片面のみ有孔プラスチック積層フィルム（Ａ）とラミネ
ート加工しただけであり、別の片面は、何ら加工されて
おらず、そのまま保持されるので、不織布、微多孔膜若
しくは自己ヒートシール性を有する耐水耐油性の混抄紙
の特徴をそのまま生かされ、本来、有している透気度を
大巾に低下させることなく安定した透気度が保持される
ため、脱酸素剤包装体は安定した脱酸素性能を発揮する
ことができる。The film (B) having micropores is simply
Only one side is laminated with the perforated plastic laminated film (A), and the other side is not processed at all and is kept as it is. The characteristics of mixed papermaking are utilized as they are, and the stable air permeability is maintained without significantly reducing the inherent air permeability. Can be demonstrated.

【００２４】また、有孔プラスチック積層フィルム
（Ａ）は、微細孔を有するフィルム（Ｂ）とラミネート
されて、微細孔を有するフィルム（Ｂ）の補強材として
の働きも併せ持つので、その包材強度と製袋性に起因す
る使い易さに優れている。使用用途、使用形態、作業方
法などを考慮して適宜包材を選択することが可能とな
り、広範囲な分野へ適用できる。The perforated plastic laminated film (A) is laminated with the film (B) having micropores, and also has a function as a reinforcing material for the film (B) having micropores. It is excellent in ease of use due to bag making. A packaging material can be appropriately selected in consideration of a use application, a use form, a working method, and the like, and can be applied to a wide range of fields.

【００２５】有孔プラスチック積層フィルム（Ａ）で微
細孔を有するフィルム（Ｂ）を被覆するようにラミネー
トした包材構成の該脱酸素剤用包材は、外側のプラスチ
ック積層フィルム（Ａ）で微細孔を有するフィルム
（Ｂ）を保護し、外部からの汚染、脱酸素剤包装体内部
からの錆の浮き出しを防ぐだけでなく、裏印刷が可能な
ど脱酸素剤の耐久性、衛生面に与える効果が期待され
る。The packaging material for an oxygen scavenger having a packaging material laminated so as to cover the film (B) having micropores with the perforated plastic laminated film (A) is finely divided by the outer plastic laminated film (A). In addition to protecting the film (B) with holes, preventing contamination from the outside and the appearance of rust from the inside of the oxygen scavenger package, the effect on the durability and hygiene of the oxygen scavenger such as back printing is possible. There is expected.

【００２６】したがって、本発明において、該脱酸素剤
用包材は、包材自体が本来有している透気度、耐久性、
製袋性等の性能をそのまま保持しつつ、再現されるので
安定した脱酸素性能を有し、かつ耐水性、耐油性に極め
て優れた脱酸素剤包装体が得られる。Therefore, in the present invention, the oxygen-absorbing material packaging material has the air permeability, durability, and the like originally possessed by the packaging material itself.
The oxygen-absorbing agent package having stable deoxygenation performance and extremely excellent water resistance and oil resistance can be obtained while reproducing performance while maintaining performance such as bag-making properties.

【００２７】[0027]

【実施例】本発明を、実施例及び比較例により、更に具
体的に説明する。ただし、本発明の範囲は、これらの実
施例に何等制限を受けるものではない。 （１）試料及び比較試料The present invention will be described more specifically with reference to examples and comparative examples. However, the scope of the present invention is not limited by these examples. (1) Sample and comparative sample

【００２８】試料−１ 有孔プラスチック積層フィルム（Ａ）である有孔 PET/P
E フィルム〔厚み：37μｍ（PET;12μｍ、PE;25 μ
ｍ）、孔径： 100μｍ、 2×2 m/m の格子状に開孔〕と
微細孔を有するフィルム（Ｂ）であるＴＳＦ−ＥＵ〔厚
み：60μｍ、興人（株）製 PE 微多孔膜〕とを（Ａ）の
低い軟化点を有するフィルム層（ａ）を介して、 100〜
120 ℃でラミネートして、積層フィルム：試料−１を作
製した。Sample-1 Perforated PET / P which is a perforated plastic laminated film (A)
E film [Thickness: 37 µm (PET; 12 µm, PE; 25 µm
m), pore size: 100 μm, 2 × 2 m / m openings in a lattice pattern) and TSF-EU, which is a film (B) having micropores (thickness: 60 μm, PE microporous membrane manufactured by Kojin Co., Ltd.) Through the film layer (a) having a low softening point of (A),
Lamination was performed at 120 ° C. to prepare a laminated film: Sample-1.

【００２９】試料−２、３ 前記、試料−１の調整において、有孔プラスチック積層
フィルム（Ａ）として使用した有孔 PET/PE フィルム
（前出）を有孔 PET/PP フィルム〔厚み：37μｍ（PET;
12μｍ、PP;25 μｍ）、孔径： 100μｍ、 2×2 m/m の
格子状に開孔〕、微細孔を有するフィルム（Ｂ）として
使用したＴＳＦ−ＥＵ（前出）をＮＦシートＳ１４０
〔厚み： 140μｍ、徳山曹達（株）製 PP 微多孔膜〕、
セルポア〔厚み： 100μｍ、積水化学工業（株）製 PP
微多孔膜〕にかえて使用する以外は、試料−１と全く同
様の方法でラミネートして、積層フィルム：試料−２、
３を作製した。Samples-2 and 3 In the preparation of Sample-1, the perforated PET / PE film (described above) used as the perforated plastic laminated film (A) was used for the perforated PET / PP film [thickness: 37 μm ( PET;
12 μm, PP; 25 μm), pore size: 100 μm, holes formed in a 2 × 2 m / m lattice pattern], NF sheet S140 using TSF-EU (supra) used as film (B) having micropores
[Thickness: 140 µm, PP microporous membrane manufactured by Tokuyama Soda Co., Ltd.],
Cellpore [Thickness: 100 μm, PP manufactured by Sekisui Chemical Co., Ltd.]
Microporous membrane], and laminated in exactly the same manner as in Sample-1, except that the laminated film was used instead of Sample-1.
3 was produced.

【００３０】試料−４ 前記、試料−１の調整において、微細孔を有するフィル
ム（Ｂ）として使用したＴＳＦ−ＥＵ（前出）をタイベ
ック１０５９Ｂ（デュポン社製、ポリエチレン不織布）
にかえて使用する以外は、試料−１と全く同様の方法で
ラミネートして、積層フィルム：試料−４を作製した。Sample-4 In the preparation of Sample-1, TSF-EU (described above) used as the film (B) having micropores was Tyvek 1059B (a polyethylene nonwoven fabric manufactured by DuPont).
A laminated film: sample-4 was produced by laminating in exactly the same manner as in sample-1, except that the sample was used instead.

【００３１】試料−５ 前記、試料−１の調整において、微細孔を有するフィル
ム（Ｂ）として使用したＴＳＦ−ＥＵ（前出）をパルプ
／PE混抄紙〔坪量：60g/m²、パルプにPEを 60%の割合で
混抄したガス透通性、かつ撥水撥油性を付与した混抄
紙〕にかえて使用する以外は、試料−１と全く同様の方
法でラミネートして、積層フィルム：試料−５を作製し
た。Sample-5 In the preparation of Sample-1, TSF-EU (described above) used as the film (B) having micropores was mixed with pulp / PE mixed paper [basis weight: 60 g / m ² , pulp A mixed film obtained by mixing the PE at a rate of 60% and having gas permeability and water / oil repellency] is used in the same manner as in Sample-1 except that the laminated film is prepared as follows: -5 was produced.

【００３２】試料−６ 前記、試料−１の調整において、有孔プラスチック積層
フィルム（Ａ）として使用した有孔 PET/PE フィルム
（前出）の孔径、開孔パターンをかえて、孔径：300μ
ｍ、 2.5×2.5 m/m の格子状に開孔した厚み：37μｍの
有孔 PET/PE フィルムを使用する以外は、試料−１と全
く同様の方法でラミネートして、積層フィルム：試料−
６を作製した。Sample-6 In the preparation of Sample-1 described above, the hole diameter and hole pattern of the perforated PET / PE film (described above) used as the perforated plastic laminated film (A) were changed to 300 μm.
m, 2.5 x 2.5 m / m Opened in a grid pattern: Laminated in exactly the same way as Sample-1 except that a perforated PET / PE film with a thickness of 37 µm was used.
No. 6 was produced.

【００３３】試料−Ａ 押出ラミネート法によって PET（厚み：12μｍ）とPE
（厚み：25μｍ）からなる非通気性 PET/PE フィルムの
試料−Ａを作製した。Sample A: PET (thickness: 12 μm) and PE by extrusion lamination
A non-breathable PET / PE film sample-A (thickness: 25 μm) was prepared.

【００３４】試料−Ｂ ドライラミネート法によって、 PET（前出）とアルミ箔
（厚み：15μｍ）をラミネートした積層フィルムのアル
ミニウム面上に、PEを厚み 20 μｍに押出ラミネートし
た包装材料の試料−Ｂを作製した。以上作製した本発明
における各試料内容を表１に示した。Sample B Sample B of a packaging material obtained by extrusion laminating PE to a thickness of 20 μm on the aluminum surface of a laminated film obtained by laminating PET (described above) and aluminum foil (thickness: 15 μm) by the dry lamination method. Was prepared. Table 1 shows the content of each sample according to the present invention prepared as described above.

【００３５】[0035]

【表１】 [Table 1]

【００３６】比較試料−１ 前記、試料−１の調整において、有孔プラスチック積層
フィルム（Ａ）として使用した有孔 PET/PE フィルム
（前出）の孔径、開孔パターンをかえて、孔径：50μ
ｍ、 2×2 m/m の格子状に開孔した厚み：37μｍの有孔
PET/PE フィルムを使用する以外は、試料−１と全く同
様の方法でラミネートして、積層フィルム比較試料−１
を作製した。Comparative Sample-1 In the preparation of Sample-1 described above, the hole diameter and the hole opening pattern of the perforated PET / PE film (described above) used as the perforated plastic laminated film (A) were changed to 50 μm.
m, 2 x 2 m / m, perforated in a grid form: 37 μm perforated
Except for using a PET / PE film, the same method as in Sample-1 was used for lamination, and a laminated film Comparative Sample-1 was used.
Was prepared.

【００３７】比較試料−２ 前記、試料−１の調整において、有孔プラスチック積層
フィルム（Ａ）として使用した有孔 PET/PE フィルム
（前出）の孔径、開孔パターンをかえて、孔径：500μ
ｍ、 2×2 m/m の格子状に開孔した厚み：37μｍの有孔
PET/PE フィルムを、微細孔を有するフィルム（Ｂ）と
して使用したＴＳＦ−ＥＵ（前出）を湿式不織布（坪
量：60g/m²、ポリエチレン製）にかえて使用する以外
は、試料−１と全く同様の方法でラミネートして、積層
フィルム：比較試料−２を作製した。Comparative Sample-2 In the preparation of Sample-1 described above, the hole diameter and the hole opening pattern of the perforated PET / PE film (described above) used as the perforated plastic laminated film (A) were changed to 500 μm.
m, 2 x 2 m / m, perforated in a grid form: 37 μm perforated
Sample-1 except that the PET / PE film was used as the film (B) having micropores, and the TSF-EU (described above) was used instead of a wet nonwoven fabric (basis weight: 60 g / m ² , made of polyethylene). And a laminated film: comparative sample-2 was produced.

【００３８】比較試料−３ 前記、試料−５の調整において、微細孔を有するフィル
ム（Ｂ）として使用したパルプ／PE混抄紙（前出）に有
孔低密度ポリエチレン（Ｂ穴）を、90〜100 ℃で熱ラミ
ネートして、積層フィルム：比較試料−３を作製した。Comparative Sample-3 In the preparation of Sample-5, the pulp / PE blended paper (described above) used as the film (B) having micropores was prepared by adding perforated low-density polyethylene (B holes) to 90 to 90%. Laminating at 100 ° C. was performed to prepare a laminated film: Comparative Sample-3.

【００３９】比較試料−４ 前記、試料−１の調整において、微細孔を有するフィル
ム（Ｂ）として使用したＴＳＦ−ＥＵ（前出）に有孔低
密度ポリエチレン（Ｂ穴）を、90〜100 ℃で熱ラミネー
トして、積層フィルム：比較試料−４を作製した。Comparative Sample-4 In the preparation of Sample-1, TSF-EU (described above) used as the film (B) having micropores was prepared by adding a porous low-density polyethylene (B holes) to 90-100 ° C. To produce a laminated film: Comparative Sample-4.

【００４０】比較試料−５ 前記、試料−４の調整において、微細孔を有するフィル
ム（Ｂ）として使用したタイベック１０５９Ｂ（前出）
に有孔低密度ポリエチレン（Ｂ穴）を、90〜100 ℃で熱
ラミネートして、積層フィルム：比較試料−５を作製し
た。以上作製した比較用試料１〜５における各試料内容
を表２に示した。Comparative Sample-5 Tyvek 1059B used as a film (B) having micropores in the preparation of Sample-4 (described above)
Then, a perforated low-density polyethylene (hole B) was thermally laminated at 90 to 100 ° C. to produce a laminated film: Comparative Sample-5. Table 2 shows the content of each of the comparative samples 1 to 5 produced as described above.

【００４１】[0041]

【表２】 [Table 2]

【００４２】（２）包装材料試験 前記第（１）項で調整した各試料及び比較試料につい
て、透気度、接着強度、ヒートシール強度、製袋性、加
工性及び耐久性の測定を行った。測定結果を表３（実施
例）、表４（比較例）に示した。(2) Packaging Material Test The air permeability, adhesive strength, heat seal strength, bag formability, workability, and durability of each sample and the comparative sample prepared in the above item (1) were measured. . The measurement results are shown in Table 3 (Example) and Table 4 (Comparative Example).

【００４３】（３）脱酸素剤包装体 前記第（１）項で調整した包装材料の試料１〜６及び比
較試料１〜５を脱酸素剤包装体の両面、片面の場合は試
料−Ａ又は試料−Ｂとを合わせて使用して、有孔プラス
チック積層フルム（Ａ）を外側にして、 50 × 50mm の
包材に製袋し、鉄粉を主剤とする酸素吸収能力が 100ml
の脱酸素剤を充填し、本発明の脱酸素剤包装体を作成し
た。これらの各脱酸素剤包装体及び 500mlの空気を酸素
バリヤー性包材（KON/PE、15×30cm）の袋に入れて密封
し、25℃に放置して酸素濃度が零になるまでの時間を測
定した。なお、サンプル数は各実施例、比較例とも１０
点で行い、測定結果を表３（実施例）及び表４（比較
例）に示した。(3) Oxygen absorber package Samples 1 to 6 and comparative samples 1 to 5 of the packaging material prepared in the above item (1) were prepared on both sides of the oxygen absorber package, and in the case of one side, sample A or Using in combination with Sample-B, make a perforated plastic laminated film (A) outside, make a bag of 50 x 50 mm, and have an oxygen absorption capacity of 100 ml with iron powder as the main agent.
Of the present invention to prepare an oxygen-absorbing agent package of the present invention. Put each of these oxygen absorber packages and 500 ml of air into a bag of oxygen barrier packaging material (KON / PE, 15 x 30 cm), seal and leave at 25 ° C until the oxygen concentration becomes zero. Was measured. The number of samples was 10 in each of the examples and comparative examples.
The measurement was performed in the following points, and the measurement results are shown in Table 3 (Example) and Table 4 (Comparative Example).

【００４４】[0044]

【発明の効果】本発明は、脱酸素剤を高水分食品、乾燥
食品、酸性食品、油加工食品、アルコール含有食品等の
種々の条件の異なる過酷な用途に使用しても、錆、染
み、付着による汚染の抑制、脱酸素剤の劣化等がなく、
安定した脱酸素性能を有するので、従来、脱酸素剤の使
用が困難な用途への展開が可能な保存剤として広い範囲
で使用することができる。したがって、その食品分野を
始めとする産業上における意義は極めて大きい。According to the present invention, even when the oxygen scavenger is used for severe applications under various conditions such as high moisture food, dried food, acidic food, oil processed food, alcohol-containing food, etc. No pollution due to adhesion, no deterioration of oxygen scavenger, etc.
Since it has stable deoxidation performance, it can be used in a wide range as a preservative which can be developed for applications where it is conventionally difficult to use an oxygen absorber. Therefore, its significance in the food and other industries is extremely large.

【００４５】[0045]

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明に用いる脱酸素剤用包装材料の断面図を
示す。FIG. 1 is a cross-sectional view of a packaging material for an oxygen scavenger used in the present invention.

【符号の説明】[Explanation of symbols]

Ａ：有孔プラスチック積層フィルム（Ａ） Ｂ：微細孔フィルム（Ｂ） Ｃ：脱酸素剤用包装材料（Ｃ） Ｄ有孔プラスチック積層フィルム（Ａ）のラミネート層 Ｅ：有孔プラスチック積層フィルム（Ａ）と微細孔フィ
ルム（Ｂ）のラミネート層 ａ：積層フィルム（Ａ）を構成するフィルム層（ａ） ｂ：積層フィルム（Ａ）を構成するフィルム層（ｂ） Ｘ：有孔プラスチック積層フィルム（Ａ）の孔A: Perforated plastic laminated film (A) B: Microporous film (B) C: Packaging material for oxygen absorber (C) D Laminated layer of perforated plastic laminated film (A) E: Perforated plastic laminated film (A) ) And a microporous film (B) laminated film a: a film layer (a) constituting the laminated film (A) b: a film layer (b) constituting the laminated film (A) X: a perforated plastic laminated film (A) ) Hole

【図２】およびFIG. 2 and

【図３】本発明に用いる該脱酸素剤用包装材料を脱酸素
剤の包装材料の両面又は片面として使用して脱酸素剤を
充填して包装し、シールした本発明の脱酸素剤包装体の
各断面図を示す。（両面：図２ 、片面：図３）FIG. 3 shows a package of the oxygen absorber according to the present invention in which the oxygen absorber packaging material used in the present invention is used as both sides or one side of the oxygen absorber packaging material, filled with the oxygen absorber and packaged and sealed. The sectional views of FIG. (Both sides: Fig. 2, one side: Fig. 3)

【符号の説明】[Explanation of symbols]

Ａ：有孔プラスチック積層フィルム（Ａ） Ｂ：微細孔フィルム（Ｂ） Ｅ：有孔プラスチック積層フィルム（Ａ）と微細孔フィ
ルム（Ｂ）のラミネート層 Ｆ：脱酸素剤包装体のヒートシール層 Ｇ：脱酸素剤 Ｈ：脱酸素剤包装体の他の片面の包装材料 （以下余白）A: Perforated plastic laminated film (A) B: Microporous film (B) E: Laminated layer of perforated plastic laminated film (A) and microporous film (B) F: Heat seal layer of oxygen absorber package G : Oxygen scavenger H: Oxygen scavenger packaging material on the other side of the package (margin)

【表３】 [Table 3]

【表４】 [Table 4]

───────────────────────────────────────────────────── フロントページの続き (72)発明者 山川 洋一 東京都千代田区大手町２−２−１ 日本 曹達株式会社内 (56)参考文献 特開 平３−238045（ＪＰ，Ａ) (58)調査した分野(Int.Cl.⁷，ＤＢ名) B65D 81/26 ────────────────────────────────────────────────── ─── Continuation of front page (72) Inventor Yoichi Yamakawa 2-2-1 Otemachi, Chiyoda-ku, Tokyo Inside Soda Co., Ltd. (56) References JP-A-3-238045 (JP, A) (58) Survey Field (Int.Cl. ⁷ , DB name) B65D 81/26

Claims (2)

(57)【特許請求の範囲】(57) [Claims] 【請求項１】下記の有孔プラスチック積層フィルム
（Ａ）と微細孔フィルム（Ｂ）とを貼り合わせて得られ
るガ−レ−式透気度が 1〜 10,000 秒／ 100 ml である
脱酸素剤用包装材料（Ｃ）を用い、該包装材料（Ｃ）を
構成する積層フィルム（Ａ）層を外側にして脱酸素剤を
包装し、シ−ルしてなることを特徴とする脱酸素剤包装
体。有孔プラスチック積層フィルム（Ａ）：微細孔フィ
ルム（Ｂ）と貼り合わせるフィルム層（ａ）と他のフィ
ルム層（ｂ）とから構成され、フィルム層（ａ）の軟化
点が、微細孔フィルム（Ｂ）の軟化点以上であり、かつ
フィルム層（ｂ）より低い軟化点を有する有孔プラスチ
ック積層フィルム 微細孔フィルム（Ｂ）：常圧で水を通さない不織布、微
多孔膜であるプラスチックフィルム及び耐水耐油性の混
抄紙よりなる群から選ばれた一種の自己ヒートシール性
を有する微細孔フィルムAn oxygen scavenger having a Galley-type air permeability of 1 to 10,000 seconds / 100 ml obtained by laminating a perforated plastic laminated film (A) and a microporous film (B) as described below. Oxygen absorber packaging, characterized in that a packaging material (C) is used, and an oxygen absorber is packaged and sealed with the laminated film (A) layer constituting the packaging material (C) outside. body. Perforated plastic laminated film (A): Consists of a film layer (a) to be bonded to a microporous film (B) and another film layer (b), and the softening point of the film layer (a) is determined by the microporous film ( Perforated plastic laminated film having a softening point higher than or equal to the softening point of B) and having a softening point lower than that of the film layer (b) Microporous film (B): a nonwoven fabric impermeable to water at normal pressure, a plastic film which is a microporous film, and A kind of self-heat sealing microporous film selected from the group consisting of water and oil resistant mixed paper 【請求項２】有孔プラスチック積層フィルム（Ａ）の孔
径が、10〜 500μm 、開孔率0.005 〜15％である請求項
１記載の脱酸素剤包装体。2. The oxygen scavenger package according to claim 1, wherein the perforated plastic laminated film (A) has a pore size of 10 to 500 μm and a porosity of 0.005 to 15%.