JP3091899B2 - Hot water distribution - Google Patents
Hot water distributionInfo
- Publication number
- JP3091899B2 JP3091899B2 JP05240018A JP24001893A JP3091899B2 JP 3091899 B2 JP3091899 B2 JP 3091899B2 JP 05240018 A JP05240018 A JP 05240018A JP 24001893 A JP24001893 A JP 24001893A JP 3091899 B2 JP3091899 B2 JP 3091899B2
- Authority
- JP
- Japan
- Prior art keywords
- hot water
- water distribution
- spray coating
- coating layer
- castable refractory
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、溶解炉等から取鍋やラ
ドルへの軽合金溶湯の取り出し、及び、取鍋やラドルか
ら保持炉や金型への軽合金溶湯の補給・注湯等の際に使
用する配湯ジョウゴに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to the removal of molten light alloy from a melting furnace or the like to a ladle or a ladle, and the replenishment and pouring of the molten light alloy from a ladle or ladle to a holding furnace or a mold. About hot water distribution fungus used at the time.
【０００２】ここで、軽合金とは、アルミニウム、マグ
ネシウム、亜鉛等を言う。Here, the light alloy refers to aluminum, magnesium, zinc and the like.
【０００３】[0003]
【従来の技術とその課題】鉄製（鋳鉄又は鋼鉄製）の配
湯ジョウゴをそのまま使用すると、厚みが１０〜１５mm
と厚くても、熱歪みにより変形し、さらに、溶湯軽金属
（アルミニウム）と鉄が反応して溶損が発生する。2. Description of the Related Art When a hot water distribution funnel made of iron (cast iron or steel) is used as it is, the thickness becomes 10 to 15 mm.
Even if it is thick, it deforms due to thermal strain, and furthermore, the molten metal (aluminum) reacts with iron to cause erosion.
【０００４】このため、通常は、ジョウゴ本体の内周面
にキャスタブル耐火物層を形成して対応していた。ここ
で、キャスタブル耐火物とは、アルミナ、シリカ、ジル
コニア等の酸化物セラミックス及び／又は炭化ケイ素、
窒化ケイ素等の非酸化物セラミックスの粉末を無機バイ
ンダー及び水でスラリー状にし、施工するものを言う。For this reason, usually, a castable refractory layer has been formed on the inner peripheral surface of the funnel body. Here, the castable refractories are oxide ceramics such as alumina, silica, and zirconia and / or silicon carbide,
This refers to a method in which a powder of a non-oxide ceramic such as silicon nitride is slurried with an inorganic binder and water and then applied.
【０００５】しかし、キャスタブル耐火物は、１０〜２
０％の気孔率を有するため、鉄製本体がアルミニウム溶
湯等の軽金属溶湯の浸食をうけ、数十〜数百サイクルで
損傷し、耐久性に問題があった。[0005] However, castable refractories are 10-2.
Since it has a porosity of 0%, the iron body is eroded by a light metal melt such as an aluminum melt, and is damaged in tens to hundreds of cycles, resulting in a problem in durability.
【０００６】本発明の目的は、上記にかんがみて、鉄製
のジョウゴ本体の内周面にキャスタブル耐火物層が形成
されている配湯ジョウゴにおいて、キャスタブル耐火物
層の耐久性に問題が発生し難い配湯ジョウゴを提供する
ことにある。In view of the above, it is an object of the present invention to provide a castable refractory layer in which a castable refractory layer is formed on an inner peripheral surface of an iron-made refractory body. It is to provide hot water distribution funnel.
【０００７】[0007]
【課題を解決するための手段】本発明の配湯ジョウゴ
は、上記課題を下記構成により解決するものである。The hot water distribution funnel of the present invention solves the above problems by the following constitution.
【０００８】軽合金溶湯の取り出し・補給等に使用さ
れ、鉄製のジョウゴ本体の内周面にキャスタブル耐火物
層が形成されてなる配湯ジョウゴにおいて、キャスタブ
ル耐火物層の上に、ホウ化物系セラミックス板又はサー
メット板が貼着されてなり、該ホウ化物系セラミックス
板又はサーメット板上に、耐熱・耐酸化合金からなる第
一溶射被覆層、及び、軽合金溶湯に対して非濡れ性のセ
ラミックスからなる第二溶射被覆層が順次積層されてな
なることを特徴とするものである。[0008] In a hot water distribution funnel used for taking out and replenishing a molten light alloy and having a castable refractory layer formed on the inner peripheral surface of an iron funnel body, a boride-based ceramic is provided on the castable refractory layer. A plate or a cermet plate is adhered, on the boride-based ceramic plate or the cermet plate, a first thermal spray coating layer made of a heat-resistant and oxidation-resistant alloy, and a ceramic that is non-wettable to a light alloy melt. The second spray coating layer is sequentially laminated.
【０００９】[0009]
【手段の詳細な説明】以下、本発明の各構成について詳
細に説明する（図１〜２参照）。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, each component of the present invention will be described in detail (see FIGS. 1 and 2).
【００１０】(1) 配湯ジョウゴ本体１は、鋳鉄製、又は
鋼鉄等からなるの鉄製板金から、通常、プレス加工によ
り形成する。その厚みは、従来同様、１０〜１５mmとす
る。(1) Hot water distribution funnel main body 1 is usually formed by pressing from an iron sheet metal made of cast iron or steel. Its thickness is set to 10 to 15 mm as in the related art.
【００１１】(2) キャスタブル耐火物層３は、前述の材
料を使用して、施工する。例えば、炭化ケイ素を８５％
含有する粉末耐火物を使用して１０〜２５mmの厚さに施
工する。(2) The castable refractory layer 3 is constructed using the aforementioned materials. For example, 85% silicon carbide
It is applied to a thickness of 10 to 25 mm using the contained powder refractory.
【００１２】(3) ホウ化物系セラミックス板４として
は、チタン、ジルコニウム、モリブデン等のホウ化物か
らなるものを好適に使用可能である。そして、その厚み
は、１０〜１５mmとする。またキャスタブル耐火物層３
上ヘの貼着は、アルカリ金属リン酸塩・ケイ酸塩等の水
溶性接着剤を使用して行う。(3) As the boride-based ceramic plate 4, a plate made of a boride such as titanium, zirconium, or molybdenum can be suitably used. And the thickness is set to 10 to 15 mm. Castable refractory layer 3
The attachment to the upper part is performed using a water-soluble adhesive such as an alkali metal phosphate and silicate.
【００１３】このホウ化物系セラミックス板４は、相対
的に金属的性質を有するため、セラミックス質であるキ
ャスタブル耐火物層３と金属質である第一溶射被覆層５
との双方に良好な接着性を示すとともに、それ自体、耐
熱性を有するとともに相対的に他のセラミックスに比し
て軽量であり、配湯ジョウゴの耐久性を全体として向上
させる作用を奏する。Since the boride-based ceramic plate 4 has relatively metallic properties, the castable refractory layer 3 made of ceramic and the first sprayed coating layer 5 made of metal are used.
In addition to exhibiting good adhesiveness to both, it has heat resistance itself, is relatively lighter than other ceramics, and has the effect of improving the durability of the hot water distribution funnel as a whole.
【００１４】なお、このホウ化物系セラミックス板４の
表面は、第一溶射被覆層５形成のための溶射に先立ち、
アルミナでショットブラスト処理して、粗面化しておく
ことが、第一溶射被覆層３のホウ化物系セラミックス板
４に対する密着性をより高めるため望ましい。The surface of the boride-based ceramic plate 4 is sprayed prior to thermal spraying for forming the first thermal spray coating 5.
It is desirable to roughen the surface by shot blasting with alumina in order to further enhance the adhesion of the first sprayed coating layer 3 to the boride-based ceramic plate 4.
【００１５】(4) 上記ホウ化物系セラミックス板の代わ
りに使用するサーメット板としては、特に限定されない
が、チタン、ジルコニウム、モリブデン等のホウ化物
に、ニッケル、コバルト、クロム等の金属の混合物を焼
成してなるものを好適に使用可能である。そして、その
厚みは、１０〜１５mmとする。またキャスタブル耐火物
層３上ヘの貼着は、アルカリ金属リン酸塩・ケイ酸塩等
の水溶性接着剤を使用して行う。(4) The cermet plate used in place of the boride-based ceramic plate is not particularly limited. It is possible to suitably use those formed. And the thickness is set to 10 to 15 mm. The sticking on the castable refractory layer 3 is performed using a water-soluble adhesive such as alkali metal phosphate and silicate.
【００１６】このサーメット板４は、セラミック質であ
るキャスタブル耐火物層３と金属質である第一溶射被覆
層５との双方に良好な接着性を示すとともに、それ自
体、耐熱衝撃性を有し、配湯ジョウゴの耐久性を全体と
して向上させる作用を奏する。The cermet plate 4 has good adhesiveness to both the castable refractory layer 3 made of ceramic and the first sprayed coating layer 5 made of metal, and has thermal shock resistance itself. It has the effect of improving the durability of the hot water distribution funnel as a whole.
【００１７】なお、このサーメット板４の表面は、第一
溶射被覆層５形成のための溶射に先立ち、アルミナでシ
ョットブラスト処理して、粗面化しておくことが、第一
溶射被覆層５のサーメット板４に対する密着性をより高
めるため望ましい。The surface of the cermet plate 4 may be roughened by shot blasting with alumina prior to thermal spraying for forming the first thermal spray coating layer 5. It is desirable to further enhance the adhesion to the cermet plate 4.
【００１８】(5) 第一溶射被覆層５は、耐熱・耐酸化合
金からなる。該耐熱・耐酸化合金としては、コクラリー
（ＣｏＣｒＡｌＹ）、ニクラリー（ＮｉＣｒＡｌＹ）等
を挙げることができる。(5) The first spray coating layer 5 is made of a heat-resistant and oxidation-resistant alloy. Examples of the heat-resistant and oxidation-resistant alloy include Coclary (CoCrAlY) and Niclary (NiCrAlY).
【００１９】このコクラリー等は、表面にＣｒ2 Ｏ3 、
Ａｌ2 Ｏ3 等の酸化被膜が形成されて優れた耐酸化作用
を示すともに、Ｙ2 Ｏ3 が、それぞれ実質的にセラミッ
クス質であるホウ化物系セラミックス板４及びセラミッ
クス質である第二溶射被覆層７に対して楔効果を有し、
ホウ化物系セラミックス板４及び第二溶射被覆層７に対
して良好な密着性を有する。This coclary or the like has Cr 2 O 3 ,
An oxide film of Al 2 O 3 or the like is formed to exhibit excellent oxidation resistance, and Y 2 O 3 is a boride-based ceramic plate 4 which is substantially ceramic and a second thermal spray coating which is ceramic. Has a wedge effect on layer 7,
It has good adhesion to the boride-based ceramic plate 4 and the second spray coating layer 7.
【００２０】第一溶射被覆層５の厚さは、１０〜２００
μｍ、望ましくは４０μｍ〜１００μｍである。厚さが
上記範囲より薄いと、キャスタブル耐火物層３の保護、
及びキャスタブル耐火物層３・第一溶射被覆層５間の接
着層的作用を奏し難い。また、厚さが上記範囲を超えて
もそれ以上の効果の増大をほとんど期待できず、却って
経済性が低下する。The thickness of the first spray coating layer 5 is 10 to 200
μm, preferably 40 μm to 100 μm. If the thickness is smaller than the above range, protection of the castable refractory layer 3
In addition, it is difficult for the castable refractory layer 3 and the first spray coating layer 5 to function as an adhesive layer. Further, even if the thickness exceeds the above range, further increase in the effect cannot be expected, and the economical efficiency is rather lowered.
【００２１】溶射方法は、特に限定されず、ガス式、爆
裂式等の火炎溶射、又は、プラズマ溶射により、大気中
又は減圧雰囲気で行う。これらの内で、プラズマ溶射
が、溶射材料の変質が少なく、且つ、非溶射体に対する
密着性も良好で望ましい。The thermal spraying method is not particularly limited, and the thermal spraying is performed in the air or in a reduced-pressure atmosphere by flame spraying such as gas type or explosive type, or plasma spraying. Of these, plasma spraying is desirable because the quality of the sprayed material is small and the adhesion to a non-sprayed body is good.
【００２２】(6) 第二溶射被覆層７は、軽金属溶湯に対
して非濡れ性を有するセラミックスからなる。例えば、
アルミナ−ジルコニア、ジルコニア等を使用する。ここ
で、ジルコニアとしては、熱相転移が発生しないように
マグネシア、酸化カルシウム、希土類酸化物（例えば、
Ｙ2 Ｏ3 ）等のを数％添加させた安定化ジルコニアを使
用することが望ましい。(6) The second spray coating layer 7 is made of ceramics having non-wetting properties with respect to the molten light metal. For example,
Alumina-zirconia, zirconia or the like is used. Here, as zirconia, magnesia, calcium oxide, rare earth oxide (for example,
It is desirable to use stabilized zirconia to which several percent of Y 2 O 3 ) is added.
【００２３】この第二溶射覆層７は、配湯ジョウゴの最
表面層に配設させることにより、配湯ジョウゴに、軽合
金溶湯に対する付着防止性（非濡れ性）を向上させる作
用を与える。The second thermal spray coating layer 7 is provided on the outermost surface layer of the hot water distribution funnel, thereby giving the hot water distribution funnel an effect of improving the adhesion preventing property (non-wetting property) to the light alloy melt.
【００２４】第二溶射被覆層７の厚さは、３０〜５００
μｍ、望ましくは５０μｍ〜２００μｍである。厚さが
上記範囲より薄いと、第二溶射被覆層７の形成効果（軽
金属溶湯の付着防止）を奏し難く、厚さが上記範囲を超
えてもそれ以上の効果の増大をほとんど期待できず、却
って経済性が低下する。The thickness of the second spray coating layer 7 is 30 to 500
μm, preferably 50 μm to 200 μm. If the thickness is smaller than the above range, the effect of forming the second thermal spray coating layer 7 (prevention of the adhesion of the molten metal) is difficult to be exhibited, and even if the thickness exceeds the above range, further increase in the effect cannot be expected. On the contrary, economic efficiency decreases.
【００２５】この第二溶射被覆層の溶射は、上記第一溶
射被覆層の場合と同様にして行う。The thermal spraying of the second thermal spray coating is performed in the same manner as in the case of the first thermal spray coating.
【００２６】(7) なお、第二溶射被覆層７は、必然的で
はないが、耐熱性塗料を塗布及び／又は含浸させて封孔
処理９をしておくことが望ましい。軽合金溶湯の下層へ
の侵入を確実に阻止する作用を奏するためである。(7) The second thermal spray coating layer 7 is preferably, but not necessarily, subjected to a sealing treatment 9 by applying and / or impregnating a heat-resistant paint. This is because the effect of reliably preventing entry of the light alloy melt into the lower layer is achieved.
【００２７】第二溶射被覆層７には、通常、多数の微小
孔が存在しており、微小孔のなかには下層面に到達して
いるものが存在する可能性があるためである。This is because the second sprayed coating layer 7 usually has a large number of micropores, and there is a possibility that some of the micropores may reach the lower layer surface.
【００２８】この耐熱性塗料としては、ポリメタロカル
ボシラン、ポリボロシロキサン、ポリシロキサン（シリ
コーン樹脂）等の半無機系樹脂、あるいはＳｉ、Ｔｉ、
Ｚｒのアルコキシドおよびこれらの加水分解生成物、Ｓ
ｉ、Ａｌの酸化物微粒子を含むゾル等が例示できる。こ
れらは、単独、あるいは二種以上を混合して使用しても
良い。さらに、溶射被覆層の封孔効果を一層向上させる
ために、上記耐熱性塗料に無機充填剤を含有させても良
い。Examples of the heat-resistant paint include semi-inorganic resins such as polymetallocarbosilane, polyborosiloxane, and polysiloxane (silicone resin);
Alkoxides of Zr and their hydrolysis products, S
Examples of the sol include i and Al oxide fine particles. These may be used alone or in combination of two or more. Further, in order to further improve the sealing effect of the thermal spray coating layer, an inorganic filler may be contained in the heat resistant paint.
【００２９】具体的には、ポリメタロカルボシラン系バ
インダー１００部に対して、窒化ホウ素粉末（六方晶
系、粒径１〜５μｍ）４０部、キシレン系溶剤１４０部
を添加した塗料組成物（商品名「チラノコート ＢＮタ
イプ」、宇部興産株式会社製造販売）を使用できる。窒
化ホウ素が含まれているため、この耐熱性塗料は、軽金
属溶湯に対して、非濡れ性が優れているため望ましい。Specifically, a coating composition (commercially available) is obtained by adding 40 parts of boron nitride powder (hexagonal, particle size 1 to 5 μm) and 140 parts of a xylene solvent to 100 parts of a polymetallocarbosilane-based binder. (Tiranocoat BN type, manufactured and sold by Ube Industries, Ltd.). Since boron nitride is contained, this heat-resistant paint is desirable because it has excellent non-wetting properties with respect to molten light metal.
【００３０】[0030]
＜実施例１＞図１示すような形態の配湯ジョウゴを、下
記仕様で製造した。<Example 1> A hot water distribution funnel having a form as shown in Fig. 1 was manufactured according to the following specifications.
【００３１】ジョウゴ本体…鋼鉄製、１０mmｔ、 キャスタブル耐火物層…「ドライシック８５」旭ガラ
ス社製、１５mmｔ、 ホウ化物系セラミックス板（ホウ化チタン）…セント
ラルガラス社製、約１０mmｔ（表面をアルミナでブラス
ト処理） 第一溶射被服層…ＣｏＣｒＡｌＹのプラズマ（Ａｒ／
Ｈ2 ）溶射、層厚：１５０μｍ 第二溶射被覆層…Ａｌ2 Ｏ3 ／ＺｒＯ2 のプラズマ
（Ａｒ／Ｈ2 ）溶射、層厚：１００μｍ 封孔処理…「チラノコートＢＮタイプ」を乾燥膜厚３
０〜４０μｍとなるように塗布後、焼成 ＜実施例２＞実施例１において、ホウ化物系セラミック
ス板の代わりに、サーメット板（ホウ化モリブデン系）
…「ＵＤ２」旭ガラス社製、５mmｔを使用する以外は、
すべて同一仕様で、配湯ジョウゴを製造した。Fungo body: steel, 10 mmt, castable refractory layer: "Dry Chic 85" manufactured by Asahi Glass Co., 15 mmt, boride-based ceramic plate (titanium boride): manufactured by Central Glass Co., approximately 10 mmt (surface is alumina Blast treatment) First spray coating layer: CoCrAlY plasma (Ar /
H 2 ) Thermal spraying, layer thickness: 150 μm Second thermal spray coating layer: plasma (Ar / H 2 ) spraying of Al 2 O 3 / ZrO 2 , layer thickness: 100 μm Sealing treatment: Drying of “Tyranno coat BN type” 3
After coating so as to have a thickness of 0 to 40 μm, baking is performed. <Example 2> In Example 1, a cermet plate (molybdenum boride-based) is used instead of the boride-based ceramic plate.
… "UD2" manufactured by Asahi Glass Co., Ltd.
Hot water distribution funnels were manufactured with the same specifications.
【００３２】＜評価試験＞そして、上記実施例１・２の
各配湯ジョウゴを、自動車エンジン部品をアルミニウム
合金（材質：ＡＡ規格のＡ３９０相当材、溶湯温度：７
８０℃）で鋳造するラインで使用し、使用限度回数（サ
イクル数）で製品評価を行った。即ち、配湯ジョウゴの
キャスタブル耐火物層に溶損が発生するまでのサイクル
数により評価した。同時に、キャスタブル耐火物層のみ
を形成した従来例の配湯ジョウゴについても、同様に評
価をした。<Evaluation Test> Each of the hot water distribution funnels in Examples 1 and 2 was replaced with an aluminum alloy (material: A390 equivalent material of AA standard, molten metal temperature: 7).
(80 ° C.), and the product was evaluated at the use limit number of times (cycle number). In other words, the evaluation was made based on the number of cycles until melt damage occurred in the castable refractory layer of the hot water distribution funnel. At the same time, the conventional hot water distribution funnel having only the castable refractory layer was similarly evaluated.
【００３３】評価結果は、実施例１・２のいずれも、５
０００サイクル後もキャスタブル耐火物層に溶損が発生
しなかったのに対し、従来例は、２５０サイクルでキャ
スタブル耐火物層に溶損が発生した。The evaluation results were 5 in each of Examples 1 and 2.
No erosion occurred in the castable refractory layer even after 000 cycles, whereas in the conventional example, erosion occurred in the castable refractory layer after 250 cycles.
【００３４】[0034]
【発明の作用・効果】本発明に係る配湯ジョウゴは、キ
ャスタブル耐火物層の上面に、ホウ化物系セラミックス
板またはサーメット板、耐熱・耐酸化合金からなる第一
溶射被覆層、及び、軽合金溶湯に対して非濡れ性のセラ
ミックスからなる第二溶射被覆層が順次積層されてな
り、第二溶射被覆層が耐熱性塗料で封孔処理されてなる
ことを特徴とする構成により下記のような作用・効果を
奏する。The hot water distribution funnel according to the present invention comprises a castable refractory layer, a first spray coating layer comprising a boride-based ceramic plate or a cermet plate, a heat-resistant and oxidation-resistant alloy, and a light alloy. A second thermal spray coating layer made of ceramics that is non-wettable with respect to the molten metal is sequentially laminated, and the second thermal spray coating layer is sealed by a heat-resistant paint as described below. It works and effects.
【００３５】ホウ化物系セラミックス板またはサーメッ
ト板は、セラミックス質であるキャスタブル耐火物層と
金属質である第一溶射被覆層との双方に良好な接着性を
示すとともに、それ自体、耐熱性を有するとともに相対
的に他のセラミックスに比して軽量であり、配湯ジョウ
ゴの耐久性を全体として向上させる作用を奏する。The boride-based ceramic plate or cermet plate has good adhesiveness to both the ceramic castable refractory layer and the metallic first spray coating layer, and has heat resistance itself. In addition, it is relatively lighter than other ceramics, and has the effect of improving the durability of the hot water distribution funnel as a whole.
【００３６】第一溶射被覆層は、キャスタブル耐火物層
と第二溶射被覆層との密着性を向上させるとともに、キ
ャスタブル耐火物層の低耐衝撃性を補完する効果を奏す
る。The first sprayed coating layer has the effect of improving the adhesion between the castable refractory layer and the second sprayed coating layer and complementing the low impact resistance of the castable refractory layer.
【００３７】第二溶射被覆層は、配湯ジョウゴの内周面
最上層側に形成させることにより、配湯ジョウゴに、軽
合金溶湯に対する付着防止性を向上させる機能を与え
る。The second thermal spray coating layer is formed on the uppermost layer on the inner peripheral surface of the hot water distribution funnel, thereby giving the hot water distribution funnel a function of improving the anti-adhesion property to the light alloy melt.
【００３８】従って、本発明に係る配湯ジョウゴは、耐
衝撃性に優れ、かつ溶湯に対する耐性（耐熱衝撃性を含
む）を有し、アルミニウム等の軽金属の鋳造に際して、
キャスタブル耐火物層の耐久性の大幅な向上が期待でき
る。Therefore, the hot water distribution funnel according to the present invention has excellent impact resistance and resistance to molten metal (including thermal shock resistance), and is suitable for casting light metals such as aluminum.
A significant improvement in the durability of the castable refractory layer can be expected.
【図１】本発明を適用する配湯ジョウゴの斜視図。FIG. 1 is a perspective view of a hot water distribution funnel to which the present invention is applied.
【図２】本発明の配湯ジョウゴの断面模式図。FIG. 2 is a schematic sectional view of a hot water distribution funnel of the present invention.
１…配湯ジョウゴ本体 ３…キャスタブル耐火物層 ４…ホウ化物系セラミックス板またはサーメット板 ５…第一溶射被覆層 ７…第二溶射被覆層 ９…封孔処理 DESCRIPTION OF SYMBOLS 1 ... Hot water distribution fungus main body 3 ... Castable refractory layer 4 ... Boride type ceramic plate or cermet plate 5 ... 1st thermal spray coating layer 7 ... 2nd thermal spray coating layer 9 ... Sealing treatment
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平６−15439（ＪＰ，Ａ) 特開 平６−7918（ＪＰ，Ａ) 特開 昭52−129603（ＪＰ，Ａ) 実開 昭62−165056（ＪＰ，Ｕ) 実開 昭59−32291（ＪＰ，Ｕ) (58)調査した分野(Int.Cl.7，ＤＢ名) B22D 35/00 B32B 18/00 C04B 41/90 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-6-15439 (JP, A) JP-A-6-7918 (JP, A) JP-A-52-129603 (JP, A) 165056 (JP, U) Actually open sho 59-32291 (JP, U) (58) Fields investigated (Int. Cl. 7 , DB name) B22D 35/00 B32B 18/00 C04B 41/90
Claims (2)
れ、鉄製のジョウゴ本体の内周面にキャスタブル耐火物
層が形成されてなる配湯ジョウゴにおいて、 前記キャスタブル耐火物層の上面に、ホウ化物系セラミ
ックス板が貼着されてなり、該ホウ化物系セラミックス
板上に、耐熱・耐酸化合金からなる第一溶射被覆層、及
び、軽合金溶湯に対して非濡れ性のセラミックスからな
る第二溶射被覆層が順次積層されてなることを特徴とす
る配湯ジョウゴ。1. A hot water distribution funnel having a castable refractory layer formed on an inner peripheral surface of an iron funnel main body, which is used for taking out and replenishing a molten light alloy, wherein an upper surface of the castable refractory layer has A boride-based ceramic plate, a first thermal spray coating layer made of a heat-resistant and oxidation-resistant alloy, and a second A hot water distribution funnel comprising a thermal spray coating layer sequentially laminated.
れ、鉄製のジョウゴ本体の内周面にキャスタブル耐火物
層が形成されてなる配湯ジョウゴにおいて、 前記キャスタブル耐火物層の上面に、サーメット板が貼
着されてなり、該サーメット板上に、耐熱・耐酸化合金
からなる第一溶射被覆層、及び、軽合金溶湯に対して非
濡れ性のセラミックスからなる第二溶射被覆層が順次積
層されてなることを特徴とする配湯ジョウゴ。2. A hot water distribution funnel used for taking out and replenishing a light alloy melt and having a castable refractory layer formed on an inner peripheral surface of an iron funnel body, wherein a cermet is provided on an upper surface of the castable refractory layer. A first thermal spray coating layer made of a heat-resistant and oxidation-resistant alloy, and a second thermal spray coating layer made of a ceramic that is non-wettable on a light alloy melt are sequentially laminated on the cermet plate. A hot water distribution funnel characterized by being made.