JP2991987B2 - Basic aluminum chloride and method for producing the same - Google Patents
Basic aluminum chloride and method for producing the sameInfo
- Publication number
- JP2991987B2 JP2991987B2 JP9067227A JP6722797A JP2991987B2 JP 2991987 B2 JP2991987 B2 JP 2991987B2 JP 9067227 A JP9067227 A JP 9067227A JP 6722797 A JP6722797 A JP 6722797A JP 2991987 B2 JP2991987 B2 JP 2991987B2
- Authority
- JP
- Japan
- Prior art keywords
- aluminum chloride
- basic aluminum
- basicity
- solution
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【発明の属する技術分野】本発明は水処理用凝集剤等に
使用する塩基性塩化アルミニウムにおいて、広いｐＨ範
囲において高い凝集性能を示し、上水中の残留アルミニ
ウムを低減させることを可能とする塩基性塩化アルミニ
ウム及びその製造方法に関する。TECHNICAL FIELD The present invention relates to a basic aluminum chloride used as a coagulant for water treatment and the like, which exhibits a high coagulation performance in a wide pH range and makes it possible to reduce residual aluminum in tap water. The present invention relates to aluminum chloride and a method for producing the same.
【０００２】[0002]
【従来の技術】塩基性塩化アルミニウムは高い凝集性を
有するためこの性質を利用して上下水、工場排水、土木
排水等の各種用排水の水処理凝集剤をはじめ、サイズ
剤、制汗剤、化粧品原料、医薬品等広範囲の用途に使用
されている。2. Description of the Related Art Basic aluminum chloride has a high cohesive property, and by utilizing this property, a water treatment coagulant for various wastewaters such as water and sewage, industrial wastewater, civil engineering wastewater, a sizing agent, an antiperspirant, It is used for a wide range of applications such as cosmetic raw materials and pharmaceuticals.
【０００３】このような塩基性塩化アルミニウム溶液の
製造方法は古くから研究され、多くの方法が開発されて
いる。例えば １）金属アルミニウムを当量以下の塩酸で溶解する方
法。 ２）金属アルミニウム、水酸化アルミニウム等のアルミ
ニウム化合物をオートクレーブ中で溶解する方法。 ３）金属アルミニウム、水酸化アルミニウム等のアルミ
ニウム化合物を常圧で溶解する方法。 ４）塩化アルミニウム溶液中にアルカリまたはアルミン
酸塩を加えて中和する方法。 ５）塩化アルミニウム溶液中の塩素イオンをイオン交換
樹脂で除去する方法。 ６）水酸化アルミニウムを塩酸と硫酸の混酸で溶解し、
これに炭酸カルシウム、水酸化カルシウム等のカルシウ
ム化合物を加えて硫酸カルシウムを除去する方法。７）
イオン交換膜を用いて塩化アルミニウム溶液から塩素イ
オンを除去する方法等である。[0003] Methods for producing such a basic aluminum chloride solution have been studied for a long time, and many methods have been developed. For example, 1) a method in which metallic aluminum is dissolved with an equivalent amount or less of hydrochloric acid. 2) A method in which an aluminum compound such as metallic aluminum or aluminum hydroxide is dissolved in an autoclave. 3) A method of dissolving aluminum compounds such as metallic aluminum and aluminum hydroxide at normal pressure. 4) A method of adding an alkali or aluminate to an aluminum chloride solution for neutralization. 5) A method of removing chloride ions in an aluminum chloride solution with an ion exchange resin. 6) Dissolve aluminum hydroxide with a mixed acid of hydrochloric acid and sulfuric acid,
A method in which a calcium compound such as calcium carbonate and calcium hydroxide is added thereto to remove calcium sulfate. 7)
It is a method of removing chloride ions from an aluminum chloride solution using an ion exchange membrane.
【０００４】ところで、近年、アルミニウムがアルツハ
イマー病の原因に強く関与している可能性があるとして
大きな話題となっており、上水快適水質項目に於いて処
理水中の残留アルミニウムの目標値は０．２ｐｐｍ以下
とされている。[0004] In recent years, it has been a big topic since aluminum may be strongly involved in the cause of Alzheimer's disease, and the target value of aluminum remaining in treated water in the item of clean water comfort water quality is 0. It is set to 2 ppm or less.
【０００５】残留アルミニウムを少なくする塩基性塩化
アルミニウムの製造方法として特公平7-10727号公報
は、常圧法に於いてアルミニウムイオンと塩素イオンと
硫酸イオンとを含む水溶液を調整する（ａ）段階と、こ
の水溶液をアルカリ土類金属化合物と接触させる（ｂ）
段階と、アルカリ土類硫酸塩を除去する（ｃ）段階とに
よって構成される塩基性クロロスルホン酸アルミニウム
の製造方法を開示している。しかしながら実際にこのよ
うな方法により製造された塩基性塩化アルミニウムは凝
集性が悪い。Japanese Patent Publication No. 7-10727 discloses a method for producing basic aluminum chloride for reducing residual aluminum, which comprises preparing an aqueous solution containing aluminum ions, chloride ions and sulfate ions in a normal pressure method (a). Contacting the aqueous solution with an alkaline earth metal compound (b)
A method for producing basic aluminum chlorosulfonate comprising a step and a step (c) of removing alkaline earth sulfate is disclosed. However, the basic aluminum chloride actually produced by such a method has poor cohesiveness.
【０００６】また残留アルミニウムの少ない塩基性塩化
アルミニウムとして特開平6-16416号公報には、その請
求項に下記の式：Ａｌ（ＯＨ）aＣｌb（ＳＯ4）cＭdＮe
（ここで、Ｍはアルカリ土類金属を表し、Ｎはアルカリ
金属を表し、ａ、ｂ、ｃ、ｄおよびｅは１．９５＜ａ＜
２．４、０＜ｃ＜０．１５、０＜ｄ＜０．１６、０＜ｅ
＜１．７、ａ＋ｂ＋２ｃ＝３＋２ｄ＋ｅを満たす数字で
ある）で表され且つアルミニウム濃度が０．０１Ｍの場
合にＡｌ13の形のアルミニウムを１モル％以上含む塩基
性度の高い水溶性のポリアルミニウムクロロ硫酸塩が開
示されている。しかしながら当該公報に開示されている
ポリアルミニウムクロロ硫酸塩の製造方法では本発明の
目的とする残留アルミニウムの少ない塩基性塩化アルミ
ニウムを製造することはできない。[0006] The Japanese Patent 6-16416 discloses a small basic aluminum chloride residual aluminum, the following formula in its claim: Al (OH) a Cl b (SO 4) c M d N e
(Where M represents an alkaline earth metal, N represents an alkali metal, and a, b, c, d and e are 1.95 <a <
2.4, 0 <c <0.15, 0 <d <0.16, 0 <e
<1.7, which is a number satisfying a + b + 2c = 3 + 2d + e) and having a basicity of 1 mol% or more of aluminum in the form of Al 13 when the aluminum concentration is 0.01 M. Sulfates are disclosed. However, the method for producing polyaluminum chlorosulfate disclosed in this publication cannot produce the basic aluminum chloride having low residual aluminum as the object of the present invention.
【０００７】ところで、現在最も優れた凝集性能を示す
とされている日本水道協会規格の塩基性塩化アルミニウ
ムに於ける塩基度は４５〜６５％であり、市販品は塩基
度４９〜６０％である。このような現在市販されている
塩基性塩化アルミニウムの処理水ｐＨ７以上における残
留アルミニウム値は極めて高いものである。By the way, the basicity of basic aluminum chloride according to the Japan Water Works Association standard, which is considered to present the most excellent coagulation performance, is 45 to 65%, and that of a commercially available product is 49 to 60%. . The residual aluminum value of such a currently commercially available basic aluminum chloride treated water at pH 7 or higher is extremely high.
【０００８】前述目標値を達成するために現在の水処理
方法に於いては凝集剤として硫酸アルミニウムあるいは
上記塩基性塩化アルミニウムを使用する場合、沈殿物と
して生成する水酸化アルミニウムの溶解度が最も小さい
ｐＨ６〜７に於いて被処理水を処理し、上水の場合にお
いてはおいしい水とされているｐＨ７．５近傍にするた
めアルカリ剤を用いてｐＨを調整している。In order to achieve the above-mentioned target value, in the present water treatment method, when aluminum sulfate or the above-mentioned basic aluminum chloride is used as a coagulant, the solubility of aluminum hydroxide formed as a precipitate is minimized at pH6. The water to be treated is treated in Steps (1) to (7), and in the case of clean water, the pH is adjusted using an alkaline agent to make the pH close to 7.5 which is regarded as delicious water.
【０００９】本発明者らは、前記の各種方法で製造され
る塩基性塩化アルミニウムについて塩基度、製造時の温
度、アルミニウム原料、原料の添加速度、添加順序、塩
基度を上げるために使用されるアルカリ剤種等について
鋭意検討を重ねた結果、残留アルミニウムに関係する大
きな要因は塩基性塩化アルミニウム製造時の温度及び塩
基度であることをつきとめた。The present inventors use the basic aluminum chloride produced by the above-described various methods to increase the basicity, the temperature during production, the aluminum raw material, the rate of addition of the raw material, the order of addition, and the basicity. As a result of intensive studies on the types of alkaline agents, it was found that the major factors related to the residual aluminum are the temperature and basicity during the production of basic aluminum chloride.
【００１０】即ち、製造時の温度がある一定温度以上で
あり且つ、後述する第一工程に於ける製造時の塩基度が
ある一定塩基度以上であることである。That is, the temperature at the time of production is equal to or higher than a certain temperature, and the basicity at the time of manufacturing in the first step described later is equal to or higher than a certain basicity.
【００１１】製造時の温度が高く、また同時に塩基度も
比較的高い製造方法として最も良く知られている方法
は、加圧加熱法、即ちオートクレーブ法である。オート
クレーブを用いて塩基性塩化アルミニウムを製造する方
法については、特開昭47-20096号公報、特開昭48-10139
8公報、特開昭48-101399号公報、特公昭50-839号公報、
特開昭50-137897号公報、特開昭53-37596号公報、特公
昭53-43739号公報、特開昭59-116125号公報、特開平2-4
533号公報等に技術開示が行われ枚挙にいとまがない。The method most well known as a production method in which the production temperature is high and the basicity is relatively high at the same time is the pressure heating method, that is, the autoclave method. Regarding the method for producing basic aluminum chloride using an autoclave, JP-A-47-20096, JP-A-48-10139
8 gazette, JP-A-48-101399, JP-B-50-839,
JP-A-50-137897, JP-A-53-37596, JP-B-53-43739, JP-A-59-116125, JP-A-2-4
There is no shortage of technical disclosures in Japanese Patent Publication No. 533 and the like.
【００１２】これら公報には塩基度７０％の塩基性塩化
アルミニウムを製造できる旨が記載されている公報もあ
るが、実際に製造された例はなく高々５７％である。た
だ特開昭50-137897号公報に塩基度６５．０％（実施例
２）のものを製造した例が記載されているが、このよう
な製造法では凝集性の良い水処理剤を製造することはで
きない。一方、常圧法に於いても沸点近くの高温で反応
を行い高塩基度の塩基性塩化アルミニウムを製造する方
法が開示（特開昭52-111496号公報）されている。この
方法によれば、塩基度８３％の塩基性塩化アルミニウム
を製造できる旨が記載されているが実際に製造されてい
る例は高々、塩基度５４．９％である。前記特公平7-10
727号公報にも常圧法に於いて７０〜１１５℃の高温で
反応させる方法が技術開示されている。Although these publications disclose that a basic aluminum chloride having a basicity of 70% can be produced, there is no example of actual production and the maximum is 57%. However, Japanese Patent Application Laid-Open No. 50-137897 discloses an example in which a product having a basicity of 65.0% (Example 2) is produced, but such a production method produces a water treatment agent having good cohesiveness. It is not possible. On the other hand, a method for producing a basic aluminum chloride having a high basicity by carrying out a reaction at a high temperature near the boiling point also in the normal pressure method is disclosed (JP-A-52-111496). According to this method, it is described that a basic aluminum chloride having a basicity of 83% can be produced. However, an example of an actual production is at most 54.9% basicity. 7-10
No. 727 also discloses a technique of reacting at a high temperature of 70 to 115 ° C. in the normal pressure method.
【００１３】また本件出願人も特公平2-58209号公報に
於いて塩化アルミニウムあるいは塩基性塩化アルミニウ
ム溶液に硫酸アルミニウムとカルシウム化合物を高温で
加えて高塩基度の塩基性塩化アルミニウム溶液を製造す
る方法を開示している。また、特開昭52−11384号公報
にも塩化アルミニウムまたは塩基性塩化アルミニウムに
６０℃以上の温度でアルカリ化合物あるいはアルカリ土
類化合物を加えて塩基度を６５〜７０％に高め凝集性の
良い塩基性塩化アルミニウムを製造する方法が記載され
ている。The present applicant also discloses in Japanese Patent Publication No. 2-58209 a method for producing a basic aluminum chloride solution having a high basicity by adding aluminum sulfate and a calcium compound to an aluminum chloride or basic aluminum chloride solution at a high temperature. Is disclosed. JP-A-52-11384 also discloses a base having good cohesiveness by adding an alkali compound or an alkaline earth compound to aluminum chloride or basic aluminum chloride at a temperature of 60 ° C. or higher to increase the basicity to 65 to 70%. A method for producing crystalline aluminum chloride is described.
【００１４】また凝集性、貯蔵安定性の良い塩基性塩化
アルミニウムの製造法として特開昭53-1699号公報には
硫酸イオンを含む塩基度４２〜４５％の塩基性塩化アル
ミニウム溶液に炭酸カルシウムを加え塩基度５５〜５８
％に調整した後６０℃以下の温度でアルカリ金属化合物
あるいは、アルカリ土類金属化合物を加えて塩基度６０
〜７０％の塩基性塩化アルミニウムを製造する方法が開
示されている。JP-A-53-1699 discloses a method for producing basic aluminum chloride having good cohesiveness and storage stability, by adding calcium carbonate to a basic aluminum chloride solution having a basicity of 42 to 45% containing sulfate ions. Basicity 55-58
% And then add an alkali metal compound or an alkaline earth metal compound at a temperature of 60 ° C. or lower to add a basicity of 60%.
A method for producing ~ 70% basic aluminum chloride is disclosed.
【００１５】[0015]
【発明が解決しようとする課題】上述の如く塩基性塩化
アルミニウムの製造時の温度がある一定温度以上であり
且つ後に詳記する第一工程に於ける製造時の塩基度が一
定塩基度以上である塩基性塩化アルミニウムはこれを凝
集剤として使用した場合、残留アルミニウムが極めて小
さくなることを発見したが、このようにして製造した塩
基性塩化アルミニウムは凝集性が悪いことが判明した。As described above, when the temperature during the production of basic aluminum chloride is above a certain temperature, and when the basicity at the time of production in the first step described later is more than a certain basicity. Certain basic aluminum chlorides have been found to have very low residual aluminum when used as a flocculant, but the basic aluminum chloride thus produced has been found to have poor cohesiveness.
【００１６】そこで、更に研究を進めた結果、これに低
温でアルカリ剤を加え更に塩基度を上げれば凝集性が著
しく向上し、しかも残留アルミニウムが少なくなること
を発見した。Therefore, as a result of further study, it was found that when an alkali agent was added thereto at a low temperature and the basicity was further increased, the cohesiveness was remarkably improved and the residual aluminum was reduced.
【００１７】本発明はこれらの知見に基づきなされたも
のであって、例えば水処理剤として使用した場合、残留
アルミニウムが少なく且つ凝集性に優れた新規なる塩基
性塩化アルミニウムを製造することを目的とする。The present invention has been made based on these findings, and it is an object of the present invention to produce a novel basic aluminum chloride having a small amount of residual aluminum and excellent cohesiveness when used as a water treatment agent. I do.
【００１８】[0018]
【課題を解決するための手段】即ち、本発明は組成、Ｍ
／Ａｌ（モル比）（但し、Ｍはアルカリ金属またはアル
カリ土類金属を示す）０．０４〜１．８０、Ｃｌ／Ａｌ
（モル比）０．５０〜１．９５、塩基度６５〜８３％の
塩基性塩化アルミニウムに於いて、当該塩基性塩化アル
ミニウムを蒸留水約５００ｍｌ（２０±２℃）にＡｌ2
Ｏ3として１０ｐｐｍ添加し、５重量％炭酸水素ナトリ
ウム（ＮａＨＣＯ3）溶液でｐＨ７．８〜８．２に調整
し、３０分間５０ｒｐｍで攪拌し、３０分間静置後、Ｎ
ｏ．５Ｃ濾紙（ＪＩＳ Ｐ ３８０１［濾紙（化学分析
用）］に規定される５種Ｃに相当）で濾過した後に於け
る濾過水の残留アルミニウム（Ａｌ）量がＹ≦０．６２
５Ｘ−４．６２５（但し、ＹはＡｌ量（ｐｐｍ）、Ｘは
ｐＨを示し、７．８≦Ｘ≦８．２である。）を満足する
ことを特徴とする新規なる塩基性塩化アルミニウム及び
その製造方法に関する。That is, the present invention provides a composition, M
/ Al (molar ratio) (where M represents an alkali metal or an alkaline earth metal) 0.04 to 1.80, Cl / Al
(Molar ratio) from 0.50 to 1.95, in the basicity from 65 to 83% of basic aluminum chloride, Al 2 the basic aluminum chloride in distilled water about 500 ml (20 ± 2 ° C.)
10 ppm was added as O 3 , the pH was adjusted to 7.8 to 8.2 with a 5% by weight sodium bicarbonate (NaHCO 3 ) solution, the mixture was stirred at 50 rpm for 30 minutes, and allowed to stand for 30 minutes.
o. The amount of residual aluminum (Al) in the filtered water after filtration through 5C filter paper (corresponding to 5 types C specified in JIS P 3801 [filter paper (for chemical analysis)]) is Y ≦ 0.62.
A new basic aluminum chloride characterized by satisfying 5X-4.625 (where Y represents the amount of Al (ppm), X represents pH and 7.8 ≦ X ≦ 8.2); It relates to the manufacturing method.
【００１９】[0019]
【発明の実施の形態】本発明の塩基性塩化アルミニウム
は一般式 Ｍa LＡｌM（ＯＨ）NＣｌPＹQ b（但し、Ｍは
アルカリ金属またはアルカリ土類金属を示しＹは多価ア
ニオンを、またａ、ｂはそれぞれＭ、Ｙの価数を示し、
ａＬ＋３Ｍ＝Ｎ＋Ｐ＋ｂＱである。）で示され、本発明
に於ける塩基度はＮ／３Ｍ ×１００で示される。Basic aluminum chloride DETAILED DESCRIPTION OF THE INVENTION The present invention has the general formula M a L Al M (OH) N Cl P Y Q b ( where, M represents an alkali metal or alkaline earth metal Y is a polyvalent anion And a and b represent the valences of M and Y, respectively.
aL + 3M = N + P + bQ. ), And the basicity in the present invention is represented by N / 3M × 100.
【００２０】まず、本発明の塩基性塩化アルミニウムの
物理的性質について述べると、本発明のＭ／Ａｌ（モル
比）は0.04〜1.80の範囲にあり、この範囲以下では凝集
能力が顕著に低下する。また、この範囲以上では塩基性
塩化アルミニウム溶液が極めて不安定となる。First, the physical properties of the basic aluminum chloride of the present invention will be described. The M / Al (molar ratio) of the present invention is in the range of 0.04 to 1.80. Below this range, the coagulation ability is significantly reduced. . Above this range, the basic aluminum chloride solution becomes extremely unstable.
【００２１】塩基度については、塩基度６５〜８３％の
範囲にあり、この範囲を下回ると凝集能力が低下し、残
留アルミニウムも多くなる。一方上記範囲を上回ると製
造が困難であるばかりでなく、そのような塩基性塩化ア
ルミニウム溶液は極めて不安定となる。The basicity is in the range of 65-83% basicity, and if it is less than this range, the cohesive ability is reduced and the residual aluminum is increased. On the other hand, if it exceeds the above range, not only is production difficult, but such a basic aluminum chloride solution becomes extremely unstable.
【００２２】ところで、本発明の新規なる塩基性塩化ア
ルミニウムの特徴は、上記物理的性質に加えて、これを
蒸留水５００ｍｌ（２０±２℃）にＡｌ2Ｏ3として１０
ｐｐｍ加え、５重量％炭酸水素ナトリウム（ＮａＨＣＯ
3）溶液でｐＨを7.8〜8.2に調整し３０分間５０ｒｐｍ
で攪拌し、３０分間静置後、Ｎｏ．５Ｃ濾紙で濾過した
後に於ける濾過水の残留アルミニウム（Ａｌ）量がＹ≦
０．６２５Ｘ-４．６２５（但し、ＹはＡｌ量（ｐｐ
ｍ）、ＸはｐＨを示し７．８≦Ｘ≦８．２である。）を
満足する量である。By the way, the feature of the novel basic aluminum chloride of the present invention is that, in addition to the above-mentioned physical properties, it is added to 500 ml of distilled water (20 ± 2 ° C.) as Al 2 O 3.
ppm, and 5% by weight of sodium hydrogen carbonate (NaHCO
3 ) Adjust the pH to 7.8-8.2 with the solution, and rotate at 50 rpm for 30 minutes.
, And allowed to stand for 30 minutes. The amount of residual aluminum (Al) in the filtered water after filtration through 5C filter paper is Y ≦
0.625X-4.625 (where Y is the amount of Al (pp
m), X indicates pH, and 7.8 ≦ X ≦ 8.2. ).
【００２３】このような物理的性質を有する本発明の新
規なる塩基性塩化アルミニウムの製造方法について述べ
ると、本発明の製造方法は大きく二つの工程に分けるこ
とができる。The production method of the novel basic aluminum chloride of the present invention having such physical properties will be described. The production method of the present invention can be roughly divided into two steps.
【００２４】先ず、第一工程は塩基度の低い塩基性塩化
アルミニウムを製造する工程であり、第二工程はアルカ
リ金属またはアルカリ土類金属を用いて塩基度を更に上
げる工程である。First, the first step is a step for producing basic aluminum chloride having a low basicity, and the second step is a step for further increasing the basicity using an alkali metal or an alkaline earth metal.
【００２５】第一工程の塩基性塩化アルミニウムの製造
方法は、公知のいかなる方法を利用しても良いが、最も
望ましい方法はオートクレーブ法、即ち水酸化アルミニ
ウムに塩酸あるいは塩化アルミニウムを加えて１４０℃
〜１８０℃で４〜８時間溶解する方法である。As the method for producing the basic aluminum chloride in the first step, any known method may be used, but the most preferable method is an autoclave method, that is, a method in which hydrochloric acid or aluminum chloride is added to aluminum hydroxide at 140 ° C.
This is a method of dissolving at ~ 180 ° C for 4 to 8 hours.
【００２６】この方法が推奨される最大の理由は反応温
度が高温、即ち８０℃以上であることである。反応温度
が８０℃以下の場合、残留アルミニウムの少ない塩基性
塩化アルミニウムを製造することはできない。尚、オー
トクレーブ法を用いる場合、可能な限り活性の大きい、
即ち易溶性の水酸化アルミニウムを使用することが望ま
しい。The main reason for recommending this method is that the reaction temperature is high, ie above 80 ° C. When the reaction temperature is 80 ° C. or lower, it is not possible to produce basic aluminum chloride with little residual aluminum. When the autoclave method is used, the activity is as large as possible.
That is, it is desirable to use easily soluble aluminum hydroxide.
【００２７】従って、常圧法で製造する場合、例えば金
属アルミニウムあるいは水酸化アルミニウムを塩酸と硫
酸の混酸で溶解し、これに炭酸カルシウムあるいは水酸
化カルシウム等のカルシウム化合物を加えて硫酸カルシ
ウムを除去する方法により製造する場合に於いても金属
アルミニウムあるいは水酸化アルミニウムの溶解中、即
ち反応中は反応温度は８０℃以上に維持されなければな
らない。Therefore, in the case of producing by a normal pressure method, for example, a method of dissolving metallic aluminum or aluminum hydroxide with a mixed acid of hydrochloric acid and sulfuric acid and adding a calcium compound such as calcium carbonate or calcium hydroxide to remove calcium sulfate. The reaction temperature must be maintained at 80 ° C. or higher during the dissolution of metallic aluminum or aluminum hydroxide, that is, during the reaction.
【００２８】また、特開昭52-111496号公報に記載の如
く濃厚塩酸と水酸化アルミニウムを沸点近くで反応させ
ることによっても第一工程の塩基性塩化アルミニウムを
製造することができる。The basic aluminum chloride in the first step can also be produced by reacting concentrated hydrochloric acid with aluminum hydroxide near the boiling point as described in JP-A-52-111496.
【００２９】いずれにしても、本発明に於いて極めて肝
要なることは、金属アルミニウムあるいは水酸化アルミ
ニウム等のアルミニウム化合物の溶解中あるいは混酸法
における脱硫工程中は反応温度が８０℃以上に維持され
ているということである。In any case, it is extremely important in the present invention that the reaction temperature is maintained at 80 ° C. or higher during the dissolution of aluminum compounds such as metallic aluminum or aluminum hydroxide or during the desulfurization step in the mixed acid method. That is.
【００３０】第一工程に於いて留意すべき第二の点は、
製造された塩基性塩化アルミニウムの組成Ｃｌ／Ａｌ
（モル比）が０．５〜１．２の範囲にあることである。
即ち前記一般式で表される塩基度が６０〜８０％の範囲
にあることである。一般に反応温度が高い程、また塩基
度が高い程残留アルミニウムは少なくなる。The second point to be noted in the first step is that
Composition of manufactured basic aluminum chloride Cl / Al
(Molar ratio) is in the range of 0.5 to 1.2.
That is, the basicity represented by the general formula is in the range of 60 to 80%. Generally, the higher the reaction temperature and the higher the basicity, the lower the residual aluminum.
【００３１】さて、次に第二工程について述べると、第
二工程は塩基度を上げる工程であるが、塩基度はアルカ
リ金属またはアルカリ土類金属の水酸化物、炭酸塩、炭
酸水素塩を加えることによって上げられる。具体的に
は、水酸化ナトリウム、水酸化カリウム、炭酸ナトリウ
ム、炭酸カリウム、炭酸水素ナトリウム、炭酸水素カリ
ウム、水酸化カルシウム、水酸化マグネシウム、炭酸カ
ルシウム、炭酸マグネシウム、炭酸水素カルシウム、炭
酸水素マグネシウムであり、最も好ましいアルカリ剤は
炭酸ナトリウム、炭酸カリウムである。Next, the second step will be described. The second step is a step of increasing the basicity. The basicity is determined by adding a hydroxide, carbonate or hydrogen carbonate of an alkali metal or alkaline earth metal. Raised by things. Specific examples include sodium hydroxide, potassium hydroxide, sodium carbonate, potassium carbonate, sodium hydrogen carbonate, potassium hydrogen carbonate, calcium hydroxide, magnesium hydroxide, calcium carbonate, magnesium carbonate, calcium hydrogen carbonate, and magnesium hydrogen carbonate. The most preferred alkaline agents are sodium carbonate and potassium carbonate.
【００３２】この第二工程に於いて肝要なることは溶液
温度が４０℃以下の温度に於いてアルカリ金属またはア
ルカリ土類金属が添加されることであり、且つその添加
量はＭ／Ａｌ（モル比）０．０４〜１．８０の範囲にあ
ることである。この範囲を逸脱すると前述の通り本発明
の新規なる塩基性塩化アルミニウムを製造することがで
きない。What is essential in the second step is that the alkali metal or alkaline earth metal is added at a solution temperature of 40 ° C. or lower, and the amount of addition is M / Al (molar). Ratio) in the range of 0.04 to 1.80. If the ratio deviates from this range, as described above, the novel basic aluminum chloride of the present invention cannot be produced.
【００３３】即ち溶液温度が４０℃以上の温度に於いて
アルカリ金属またはアルカリ土類金属を添加すると凝集
性に優れた新規なる塩基性塩化アルミニウムを製造する
ことができない。一般的には１０〜４０℃の範囲が好ま
しい。このようにして、製造された塩基性塩化アルミニ
ウムの塩基度は６５〜８３％の範囲である。That is, if an alkali metal or alkaline earth metal is added at a solution temperature of 40 ° C. or more, a new basic aluminum chloride having excellent cohesiveness cannot be produced. Generally, the range of 10 to 40 ° C. is preferable. The basicity of the basic aluminum chloride thus produced ranges from 65 to 83%.
【００３４】尚、アルカリ剤を用いて塩基度を上げる方
法は特公昭53-43739号公報あるいは特開昭52-111496号
公報に記載の如く良く知られた方法であり、上記の事項
が厳守される限りに於いて常法を踏襲すれば良い。The method of increasing the basicity by using an alkali agent is a well-known method as described in JP-B-53-43739 or JP-A-52-111496, and the above items are strictly observed. You may follow the law as far as possible.
【００３５】次に本発明の新規なる塩基性塩化アルミニ
ウムの更なる凝集能力、貯蔵安定性を高める方法につい
て述べると、硫酸イオンあるいはリン酸イオン等の多価
アニオンを存在せしめることである。Next, the method for further improving the aggregation ability and storage stability of the novel basic aluminum chloride of the present invention is described in that a polyvalent anion such as a sulfate ion or a phosphate ion is allowed to exist.
【００３６】多価アニオンを存在せしめる方法として
は、先に述べた混酸法を利用する場合にはアルミニウム
溶解後の溶液に硫酸に対して化学当量以下のカルシウム
化合物を加えれば良い。その他の方法を利用する場合、
第一工程の塩基性塩化アルミニウム製造工程中に多価酸
あるいはその水溶性塩を加えても良いし製造後に加えて
も良い。更に別法としては、第二工程中にあるいは第二
工程終了後に加えても良い。As a method for causing a polyvalent anion to be present, when the above-mentioned mixed acid method is used, a calcium compound having a chemical equivalent or less to sulfuric acid may be added to the solution after dissolving aluminum. If you use any other method,
A polyacid or a water-soluble salt thereof may be added during the first step of producing the basic aluminum chloride, or may be added after the production. As a further alternative, it may be added during the second step or after the second step.
【００３７】最も好ましい多価アニオンは硫酸イオンで
あり、具体的には硫酸、硫酸ナトリウム、硫酸カリウ
ム、硫酸アルミニウムを添加する。塩基性塩化アルミニ
ウム中に存在させる多価アニオンの量としてはＹ／Ａｌ
（モル比）0.05〜0.20の範囲である。下限を下廻ると凝
集性、貯蔵安定性が上がらず、上限を上廻ると溶液は極
めて不安定となり貯蔵中に沈殿物を生成する。The most preferred polyvalent anion is a sulfate ion. Specifically, sulfuric acid, sodium sulfate, potassium sulfate, and aluminum sulfate are added. The amount of the polyvalent anion to be present in the basic aluminum chloride is Y / Al
(Molar ratio) It is in the range of 0.05 to 0.20. Below the lower limit, the cohesiveness and storage stability do not increase, while above the upper limit, the solution becomes extremely unstable and precipitates during storage.
【００３８】本発明の新規なる塩基性塩化アルミニウム
は、上述の如く溶液として製造されるが、熱風乾燥機等
の乾燥機を利用し常法に従って乾燥し粉末として利用す
ることもできる。The novel basic aluminum chloride of the present invention is produced as a solution as described above, but it can also be dried as a powder using a dryer such as a hot-air dryer in accordance with a conventional method.
【００３９】以下に実施例を挙げて本発明を更に詳記す
る。尚、％は特に断らない限り全て重量％を示す。Hereinafter, the present invention will be described in more detail with reference to examples. All percentages are by weight unless otherwise specified.
【００４０】[0040]
（実施例１）水酸化アルミニウム（Ａｌ2Ｏ3６５．４
％）をオートクレーブを用いて、加圧下に塩酸溶解する
ことによって得られた塩基性塩化アルミニウム（Ａｌ2
Ｏ3１３．９６％、Ｃｌ １５．７９％、塩基度４５．７
％）４００ｇを攪拌装置、冷却管、温度計を備えた１Ｌ
容四つ口フラスコに入れ、９０℃に加熱する。攪拌下
に、炭酸カルシウム粉末７８ｇと硫酸アルミニウム溶液
（Ａｌ2Ｏ3８．２０％、ＳＯ4２３．０％）３１２ｇを
３０分間かけて同時に添加した。引き続き３０分間この
温度で熟成させた後、生成石膏を濾過分離し、Ａｌ2Ｏ3
１３．３９％、Ｃｌ１０．５９％、ＳＯ4１．４０％、
Ｃａ １．０９％なる組成で塩基度６５．３％の塩基性
塩化アルミニウム溶液４９７ｇを得た。この塩基性塩化
アルミニウム溶液８０ｇを室温下に保持しながら炭酸ナ
トリウム５．９６ｇを蒸留水１８．７ｇに溶解させた液
を徐々に添加攪拌して溶解し、さらに硫酸アルミニウム
溶液４．８ｇを混合し、１０７ｇの本発明の塩基性塩化
アルミニウム溶液を得た。この分析値は、下記の通りで
ある。Ａｌ2Ｏ3 １０．４０％、Ｃｌ ７．８２％、Ｃ
ａ ０．８１％、Ｎａ ２．６７％、ＳＯ4 ２．０５
％、塩基度８２．６％(Example 1) Aluminum hydroxide (Al 2 O 3 65.4)
%) Was dissolved in hydrochloric acid under pressure using an autoclave to obtain basic aluminum chloride (Al 2
O 3 13.96%, Cl 15.79%, basicity 45.7
%) 400 g of 1 L equipped with a stirrer, cooling tube and thermometer
Place in a four-necked flask and heat to 90 ° C. Under stirring, 78 g of calcium carbonate powder and 312 g of an aluminum sulfate solution (8.20% of Al 2 O 3 , 23.0% of SO 4 ) were simultaneously added over 30 minutes. After subsequent aging at this temperature for 30 minutes, the formed gypsum is separated by filtration and Al 2 O 3
13.39%, Cl 10.59%, SO 4 1.40%,
497 g of a basic aluminum chloride solution having a composition of 1.09% Ca and a basicity of 65.3% was obtained. While maintaining 80 g of this basic aluminum chloride solution at room temperature, a solution obtained by dissolving 5.96 g of sodium carbonate in 18.7 g of distilled water was gradually added and dissolved by stirring, and 4.8 g of an aluminum sulfate solution was further mixed. , 107 g of the basic aluminum chloride solution of the invention were obtained. The analysis values are as follows. Al 2 O 3 10.40%, Cl 7.82%, C
a 0.81%, Na 2.67%, SO 4 2.05
%, Basicity 82.6%
【００４１】（実施例２）実施例１の炭酸ナトリウム
５．９６ｇに代えて、炭酸マグネシウム５．３ｇを蒸留
水２４．５ｇに溶解させた溶液を徐々に添加攪拌して溶
解し、さらに硫酸アルミニウム溶液４．８ｇを混合し、
１０９ｇの本発明の塩基性塩化アルミニウム溶液を得
た。この分析値は下記の通りである。Ａｌ2Ｏ3 １０．
２０％、Ｃｌ ７．７７％、Ｃａ ０．８０％、Ｍｇ
１．４０％、ＳＯ4 ２．０４％ 塩基度８２．２％Example 2 Instead of 5.96 g of sodium carbonate of Example 1, a solution in which 5.3 g of magnesium carbonate was dissolved in 24.5 g of distilled water was gradually added and dissolved by stirring. Mix 4.8 g of the solution,
109 g of a basic aluminum chloride solution according to the invention were obtained. The analytical values are as follows. Al 2 O 3 10.
20%, Cl 7.77%, Ca 0.80%, Mg
1.40%, SO 4 2.04% basicity 82.2%
【００４２】（実施例３）水酸化アルミニウムを塩酸と
硫酸の混酸で溶解し、これに炭酸カルシウムを加えて硫
酸カルシウムを除去する方法によって得られた塩基性塩
化アルミニウム（Ａｌ2Ｏ3１２．４２％、Ｃｌ ９．６
６％、ＳＯ4 ３．１７％、Ｃａ ０．５３％、塩基度５
７．３％）７００ｇを実施例１と同じ反応器に入れ８５
℃に加熱した。攪拌下に炭酸カルシウム２７．４ｇと硫
酸アルミニウム溶液（Ａｌ2Ｏ3８．２０％、ＳＯ4２
３．０％）１２．７ｇを１７分間かけて同時に添加し
た。引き続き１５分間この温度で熟成させた後、生成石
膏を濾過分離し、Ａｌ2Ｏ3１３．２０％、Ｃｌ １０．
０７％、ＳＯ4１．６２％、Ｃａ１．３２％なる組成で
塩基度６７．６％の塩基性塩化アルミニウム溶液６４７
ｇを得た。この塩基性塩化アルミニウム溶液６４７ｇを
４０℃以下に保持しながら硫酸アルミニウム溶液２０ｇ
を混合し、さらに３０％炭酸ナトリウム溶液１２４ｇを
徐々に添加、攪拌して溶解した後に、蒸留水８０ｇを加
えて８５６ｇの本発明の塩基性塩化アルミニウム溶液を
得た。この分析値は、下記の通りである。Ａｌ2Ｏ3 １
０．１６％、 Ｃｌ ７．７４％、Ｃａ １．０１％、Ｎ
ａ２．０１％、ＳＯ4 １．７９％、塩基度８０．３％Example 3 Aluminum hydroxide was dissolved in a mixed acid of hydrochloric acid and sulfuric acid, and calcium carbonate was added to the solution to remove calcium sulfate. Basic aluminum chloride (Al 2 O 3 12.42) was obtained. %, Cl 9.6
6%, SO 4 3.17%, Ca 0.53%, basicity 5
7.3%) into a reactor as in Example 1
Heated to ° C. Under stirring, 27.4 g of calcium carbonate and an aluminum sulfate solution (8.20% of Al 2 O 3 , SO 4 2
(3.0%) was added simultaneously over 17 minutes. After subsequently aged at this temperature for 15 minutes, the product gypsum is filtered off, Al 2 O 3 13.20%, Cl 10.
Basic aluminum chloride solution 647 having a composition of 7%, 1.62% SO 4 , 1.32% Ca and a basicity of 67.6%.
g was obtained. While maintaining 647 g of this basic aluminum chloride solution at 40 ° C. or less, 20 g of aluminum sulfate solution
Was further added, and 124 g of a 30% sodium carbonate solution was gradually added thereto, and the mixture was dissolved by stirring. Then, 80 g of distilled water was added to obtain 856 g of a basic aluminum chloride solution of the present invention. The analysis values are as follows. Al 2 O 3 1
0.16%, Cl 7.74%, Ca 1.01%, N
a2.01%, SO 4 1.79%, basicity 80.3%
【００４３】（実施例４）水酸化アルミニウム（Ａｌ2
Ｏ3 ６５．４％）２８０ｇに３５％塩酸３７５ｇ、７
０％硫酸４６７ｇ及び蒸留水１９０ｇを攪拌装置、冷却
管、温度計を備えた３Ｌ容四つ口フラスコに入れ、１０
０℃以上に加熱し水酸化アルミニウムを溶解させた。こ
れを９０℃に冷却した後、攪拌下に炭酸カルシウムの５
０％スラリー７０５ｇを３５分間で徐々に添加した。添
加中及び添加後も温度は９０℃を保持し続け、引き続き
６０分間この温度で熟成させた後、生成石膏を濾過分離
し、Ａｌ2Ｏ3 １４．３９％、Ｃｌ １０．２８％、ＳＯ
4 １．５８％、Ｃａ １．０５％なる組成で塩基度６
８．３％の塩基性塩化アルミニウム溶液１０６０ｇを得
た。この塩基性塩化アルミニウム溶液６７．４ｇに室温
下で硫酸アルミニウム溶液６．１ｇを混合し、さらに２
１％炭酸ナトリウム溶液１５．５ｇを徐々に添加、攪拌
して溶解した後に蒸留水１１ｇを加えて、９８ｇの本発
明の塩基性塩化アルミニウム溶液を得た。この分析値
は、下記の通りである。Ａｌ2Ｏ3１０．４１％、Ｃｌ
６．９４％、Ｃａ０．６６％、Ｎａ１．５６％、 ＳＯ
4２．４８％、塩基度７６．１％Example 4 Aluminum hydroxide (Al 2
(35.4% O 3 ), 375 g of 35% hydrochloric acid in 280 g, 7
467 g of 0% sulfuric acid and 190 g of distilled water were put into a 3 L four-necked flask equipped with a stirrer, a condenser, and a thermometer, and 10 g
The mixture was heated to 0 ° C. or higher to dissolve the aluminum hydroxide. After cooling to 90 ° C., the calcium carbonate 5
705 g of a 0% slurry was gradually added in 35 minutes. During and after the addition, the temperature was maintained at 90 ° C., and after aging at this temperature for 60 minutes, the formed gypsum was separated by filtration, and 14.39% of Al 2 O 3 , 10.28% of Cl, and SO.
4 1.58% Ca, 1.05% Ca and basicity 6
1060 g of a 8.3% basic aluminum chloride solution were obtained. 6.1 g of an aluminum sulfate solution was mixed with 67.4 g of this basic aluminum chloride solution at room temperature,
After slowly adding 15.5 g of a 1% sodium carbonate solution and stirring to dissolve, 11 g of distilled water was added to obtain 98 g of a basic aluminum chloride solution of the present invention. The analysis values are as follows. Al 2 O 3 10.41%, Cl
6.94%, Ca 0.66%, Na 1.56%, SO
4 2.48%, basicity 76.1%
【００４４】（実施例５）金属アルミニウム４５ｇを３
５％塩酸１０９ｇと蒸留水２７３ｇ中で９９℃に加熱し
ながら攪拌下、徐々に添加、溶解することによって、Ａ
ｌ2Ｏ3２０．０％Ｃｌ ８．３４％なる組成で、塩基度
８０％の塩基性塩化アルミニウム溶液４２５ｇを得た。
この塩基性塩化アルミニウム１００ｇを室温下に保持し
ながら、硫酸アルミニウム溶液１８．８ｇを混合し、さ
らに２１％炭酸ナトリウム溶液２７．８ｇを添加し、攪
拌して溶解した後に、蒸留水６７ｇを加えて２１１ｇの
本発明の塩基性塩化アルミニウム溶液を得た。この分析
値は、下記の通りである。Ａｌ2Ｏ3 １０．２１％、Ｃ
ｌ ３．９５％、Ｎａ １．２０％、ＳＯ4 ２．０５％、
塩基度８３％Example 5 45 g of metallic aluminum was added to 3
A. By slowly adding and dissolving while stirring at 99 ° C. in 109 g of 5% hydrochloric acid and 273 g of distilled water, A
425 g of a basic aluminum chloride solution having a composition of 1 2 O 3 20.0% Cl 8.34% and a basicity of 80% was obtained.
While keeping 100 g of the basic aluminum chloride at room temperature, 18.8 g of the aluminum sulfate solution was mixed, 27.8 g of a 21% sodium carbonate solution was added, and the mixture was stirred to dissolve, and then 67 g of distilled water was added. 211 g of a basic aluminum chloride solution according to the invention were obtained. The analysis values are as follows. Al 2 O 3 10.21%, C
l 3.95%, Na 1.20%, SO 4 2.05%,
83% basicity
【００４５】（実施例６）実施例５に於いて第二工程に
おける硫酸アルミニウム溶液の添加を行わず、２１％炭
酸ナトリウム溶液５．９４ｇを添加し、蒸留水８９ｇを
加えて１９２ｇの本発明の塩基性塩化アルミニウム溶液
を得た。この分析値は下記の通りである。Ａｌ2Ｏ3 １
０．４０％、Ｃｌ ４．３３％、Ｎａ ０．２８％、塩基
度８１．７％(Example 6) In Example 5, without adding the aluminum sulfate solution in the second step, 5.94 g of a 21% sodium carbonate solution was added, and 89 g of distilled water was added to obtain 192 g of the present invention. A basic aluminum chloride solution was obtained. The analytical values are as follows. Al 2 O 3 1
0.40%, Cl 4.33%, Na 0.28%, basicity 81.7%
【００４６】（実施例７）金属アルミニウム４５ｇを３
５％塩酸２０３ｇと蒸留水３６０ｇ中で９９℃に加熱し
ながら攪拌下、徐々に添加、溶解することによって、Ａ
ｌ2Ｏ3 １４．３５％、Ｃｌ １１．６７％なる組成で、
塩基度６１％の塩基性塩化アルミニウム溶液５９２ｇを
得た。この塩基性塩化アルミニウム１００ｇを室温下に
保持しながら、硫酸アルミニウム溶液１７ｇを混合し、
さらに２１％炭酸ナトリウム溶液２６．７ｇを添加し、
攪拌して溶解した後に、蒸留水１１．６ｇを加えて１５
３ｇの本発明の塩基性塩化アルミニウム溶液を得た。こ
の分析値は、下記の通りである。Ａｌ2Ｏ3 １０．２９
％、Ｃｌ ７．６３％、Ｎａ １．５９％、ＳＯ4 ２．５
６％、塩基度 ６７．１％(Example 7) 45 g of aluminum metal was added to 3
A by slowly adding and dissolving while stirring at 99 ° C. in 203 g of 5% hydrochloric acid and 360 g of distilled water, A
l 2 O 3 14.35%, a composition comprising 11.67% Cl,
592 g of a basic aluminum chloride solution having a basicity of 61% were obtained. While maintaining 100 g of the basic aluminum chloride at room temperature, 17 g of an aluminum sulfate solution was mixed,
Further add 26.7 g of a 21% sodium carbonate solution,
After stirring and dissolving, 11.6 g of distilled water was added to add 15 g.
3 g of a basic aluminum chloride solution according to the invention were obtained. The analysis values are as follows. Al 2 O 3 10.29
%, Cl 7.63%, Na 1.59%, SO 4 2.5
6%, basicity 67.1%
【００４７】（比較例１）実施例１において９０℃に加
熱するまでは同じ操作で製造した塩基性塩化アルミニウ
ム溶液を９０℃に加熱、攪拌し、これに炭酸カルシウム
粉末２５．１ｇと硫酸アルミニウム溶液１００ｇを同時
に添加し、熟成後、生成石膏を濾過分離し、Ａｌ2Ｏ3１
３．２０％、Ｃｌ １３．００％、ＳＯ4１．３０％、Ｃ
ａ ０．９０％なる組成で、塩基度５５．０％の塩基性
塩化アルミニウム溶液４３７ｇを得た。この塩基性塩化
アルミニウム溶液８０ｇを室温下に保持しながら炭酸ナ
トリウム９．６ｇを蒸留水２２．４ｇに溶解させた溶液
を徐々に添加攪拌して溶解し、さらに硫酸アルミニウム
溶液４．８ｇを混合し、１１３ｇの塩基性塩化アルミニ
ウム溶液を得た。この分析値は、下記の通りである。Ａ
ｌ2Ｏ3 ９．６９％、Ｃｌ ９．２０％、Ｃａ ０．６
４％、Ｎａ ３．６９％、ＳＯ4 １．９０％、塩基度８
１．３％Comparative Example 1 A basic aluminum chloride solution prepared in the same manner as in Example 1 until heated to 90 ° C. was heated and stirred at 90 ° C., and 25.1 g of calcium carbonate powder and aluminum sulfate solution were added thereto. 100 g was added at the same time, and after aging, the formed gypsum was separated by filtration, and Al 2 O 3 1
3.20%, Cl 13.00%, SO 4 1.30%, C
a 437 g of a basic aluminum chloride solution having a composition of 0.90% and a basicity of 55.0% was obtained. While maintaining 80 g of the basic aluminum chloride solution at room temperature, a solution of 9.6 g of sodium carbonate dissolved in 22.4 g of distilled water was gradually added and dissolved by stirring, and 4.8 g of an aluminum sulfate solution was further mixed. 113 g of a basic aluminum chloride solution was obtained. The analysis values are as follows. A
l 2 O 3 9.69%, Cl 9.20%, Ca 0.6
4%, Na 3.69%, SO 4 1.90%, basicity 8
1.3%
【００４８】（比較例２）実施例３に於いて、第一工程
における炭酸カルシウムと硫酸アルミニウム溶液の同時
添加温度を７０℃にした以外は全く同一の方法により塩
基性塩化アルミニウム溶液を製造した。この分析値は下
記の通りである。Ａｌ2Ｏ3 １０．２１％、Ｃｌ ７．
８０％、Ｃａ ０．９０％、Ｎａ ２．００％、ＳＯ4
１．８０％、塩基度７９．１％(Comparative Example 2) A basic aluminum chloride solution was produced in exactly the same manner as in Example 3, except that the simultaneous addition temperature of the calcium carbonate and aluminum sulfate solutions in the first step was 70 ° C. The analytical values are as follows. Al 2 O 3 10.21%, Cl 7.
80%, Ca 0.90%, Na 2.00%, SO 4
1.80%, basicity 79.1%
【００４９】（比較例３）実施例４に於いて第二工程に
おける炭酸ナトリウム溶液の添加温度を９０℃にした以
外は全く同一の方法により塩基性塩化アルミニウム溶液
を製造した。この分析値は下記の通りである。Ａｌ2Ｏ3
１０．５２％、Ｃｌ ６．８４％、Ｃａ ０．７１％、
Ｎａ １．５８％、ＳＯ4 ２．５０％、塩基度７７％(Comparative Example 3) A basic aluminum chloride solution was produced in exactly the same manner as in Example 4, except that the addition temperature of the sodium carbonate solution in the second step was 90 ° C. The analytical values are as follows. Al 2 O 3
10.52%, Cl 6.84%, Ca 0.71%,
Na 1.58%, SO 4 2.50%, basicity 77%
【００５０】（比較例４）実施例４に於いて第二工程に
おける炭酸ナトリウム溶液の添加を行なわず、室温下で
硫酸アルミニウム溶液７．０ｇと蒸留水２３．６ｇを加
え９８ｇの塩基性塩化アルミニウム溶液を製造した。こ
の分析値は下記の通りである。Ａｌ2Ｏ3 １０．４８
％、Ｃｌ ７．０７％、Ｃａ ０．６６％、ＳＯ4 ２．
７３％、塩基度６５．２％Comparative Example 4 In Example 4, without adding the sodium carbonate solution in the second step, 7.0 g of an aluminum sulfate solution and 23.6 g of distilled water were added at room temperature, and 98 g of basic aluminum chloride was added. A solution was prepared. The analytical values are as follows. Al 2 O 3 10.48
%, Cl 7.07%, Ca 0.66%, SO 4 2.
73%, basicity 65.2%
【００５１】（比較例５）実施例５と同様の操作により
製造したＡｌ2Ｏ3 ２０．０％、Ｃｌ ８．３４％なる組
成で、塩基度８０％の塩基性塩化アルミニウム溶液１０
０ｇを室温に保持しながら硫酸アルミニウム溶液１８．
８ｇを混合し、さらに２１％炭酸ナトリウム溶液２．１
３ｇを添加し、攪拌して溶解した後に、蒸留水９０ｇを
加えて２１１ｇの塩基性塩化アルミニウム溶液を製造し
た。この分析結果は、下記の通りである。Ａｌ2Ｏ3 １
０．２０％、Ｃｌ ３．９５％、ＳＯ4 ２．０５％、Ｎ
ａ ０．０９％、塩基度 ７５．０％Comparative Example 5 A basic aluminum chloride solution having a composition of 20.0% of Al 2 O 3 and 8.34% of Cl and a basicity of 80% was prepared by the same operation as in Example 5.
While keeping 0 g at room temperature.
8 g, and then a 21% sodium carbonate solution 2.1
After adding 3 g and dissolving by stirring, 90 g of distilled water was added to prepare 211 g of a basic aluminum chloride solution. The results of this analysis are as follows. Al 2 O 3 1
0.20%, Cl 3.95%, SO 4 2.05%, N
a 0.09%, basicity 75.0%
【００５２】Ａ）残留アルミニウム測定試験 塩基性塩化アルミニウム溶液を、５００ｍｌの蒸留水中
（２１℃）にＡｌ2Ｏ3として１０ｐｐｍ添加し、５％炭
酸水素ナトリウム（ＮａＨＣＯ3）溶液でｐＨを表１の
ように調整し、３０分間５０ｒｐｍで攪拌した。次いで
３０分間静置後、Ｎｏ．５Ｃ濾紙で濾過した後における
濾過水のアルミニウム量を測定した。その結果は表１の
通りである。A) Residual aluminum measurement test A basic aluminum chloride solution was added as 10 ppm as Al 2 O 3 to 500 ml of distilled water (21 ° C.), and the pH was adjusted with a 5% sodium hydrogen carbonate (NaHCO 3 ) solution as shown in Table 1. And stirred at 50 rpm for 30 minutes. Then, after standing for 30 minutes, The amount of aluminum in the filtered water after filtration through 5C filter paper was measured. Table 1 shows the results.
【００５３】[0053]
【表１】 ※１ 多木化学(株)製塩基性塩化アルミニウム（商品名ＰＡＣ２５０Ａ 組成 Ａｌ2Ｏ3１０．２％、塩基度５０．３％、ＳＯ4 ２．８％） [Table 1] ※ 1 Taki Chemical Co. salt production group of aluminum chloride (trade name PAC250A composition Al 2 O 3 10.2%, basicity 50.3%, SO 4 2.8%)
【００５４】表１から本発明の新規なる塩基性塩化アル
ミニウムは公知の方法により製造した塩基性塩化アルミ
ニウムあるいは市販の塩基性塩化アルミニウムに比べて
極めて残留アルミニウムが少ないことが判る。From Table 1, it can be seen that the novel basic aluminum chloride of the present invention has much less residual aluminum than the basic aluminum chloride produced by a known method or a commercially available basic aluminum chloride.
【００５５】Ｂ）凝集性試験 １）供試水 水道水に上水試験法により精製したカオリナイトを分散
懸濁させた。供試水の性状は表２に示した通りである。B) Coagulation test 1) Test water Kaolinite purified by a tap water test method was dispersed and suspended in tap water. The properties of the test water are as shown in Table 2.
【表２】 ２）試験方法 供試水１０００ｍｌに試験例の塩基性塩化アルミニウム
溶液を所定量加え、急速攪拌（１２０ｒｐｍ×３分）、
緩速攪拌（４０ｒｐｍ×１０分）を行い１０分間静置後
上澄水１００ｍｌを採取し濁度を測定した。その結果は
表３の通りである。[Table 2] 2) Test method A predetermined amount of the basic aluminum chloride solution of the test example was added to 1,000 ml of test water, and the mixture was rapidly stirred (120 rpm × 3 minutes).
After gentle stirring (40 rpm × 10 minutes), the mixture was allowed to stand for 10 minutes, and then 100 ml of supernatant water was collected to measure turbidity. Table 3 shows the results.
【００５６】[0056]
【表３】 [Table 3]
【００５７】表３から本発明の塩基性塩化アルミニウム
は優れた凝集性能を有することが判る。Table 3 shows that the basic aluminum chloride of the present invention has excellent coagulation performance.
【００５８】Ｃ）安定性試験 試験例の塩基性塩化アルミニウムを５０℃で７日間保存
した後、Ｂ）凝集性試験に従って凝集性試験を行った。
結果は表４の通りである。C) Stability test After the basic aluminum chloride of the test example was stored at 50 ° C. for 7 days, a cohesion test was performed according to B) cohesion test.
Table 4 shows the results.
【表４】 [Table 4]
【００５９】表４から硫酸根を含有させた場合、塩基性
塩化アルミニウム溶液は卓抜した貯蔵安定性を示すこと
が判る。Table 4 shows that when a sulfate group is contained, the basic aluminum chloride solution exhibits excellent storage stability.
【００６０】[0060]
【発明の効果】本発明の新規なる塩基性塩化アルミニウ
ムは、上水処理において近年問題となっている上水中の
残留アルミニウムによるアルツハイマー病への影響の問
題を回避し、処理上水中の残留アルミニウムが極めて少
ない優れた水処理用の凝集剤である。EFFECT OF THE INVENTION The novel basic aluminum chloride of the present invention avoids the problem of Alzheimer's disease caused by residual aluminum in water that has recently become a problem in water treatment. Very few excellent coagulants for water treatment.
【００６１】また、このような残留アルミニウムを軽減
する場合に、従来の凝集剤を使用すると限られた狭いｐ
Ｈ範囲のみでしか使用できず、そのｐＨ範囲（ｐＨ６〜
７）を逸脱すると除濁性能等の凝集性能が低下し、且つ
処理水中の残留アルミニウムが極端に多くなる問題があ
ったが、本発明の塩基性塩化アルミニウムの使用では、
広いｐＨ範囲においてこのような凝集性能を低下させる
ことなく、上水中の残留アルミニウムを低減させること
が可能となる。In order to reduce such residual aluminum, the use of a conventional flocculant is limited to a narrow p-type.
It can be used only in the H range and its pH range (pH 6 ~
When deviating from 7), there is a problem that the coagulation performance such as the turbidity performance is reduced and the residual aluminum in the treated water becomes extremely large. However, in the use of the basic aluminum chloride of the present invention,
It is possible to reduce the residual aluminum in the tap water without deteriorating such cohesive performance in a wide pH range.
【００６２】更に、本発明の塩基性塩化アルミニウムの
製造方法によれば、従来塩基性塩化アルミニウムの高塩
基度化によって問題となった製品の安定性の低下や、凝
集性能の低下の問題を回避し、長期間での製品安定性と
凝集性能の維持が可能である。Further, according to the method for producing basic aluminum chloride of the present invention, it is possible to avoid the problems of a decrease in product stability and a decrease in coagulation performance, which have conventionally been caused by the increase in basicity of basic aluminum chloride. However, it is possible to maintain product stability and coagulation performance for a long period of time.
【００６３】従って、本発明の新規なる塩基性塩化アル
ミニウムは、これを水処理用凝集剤殊に上水用の凝集剤
として使用するときに最も良くその効果を発揮するが、
このような利用のみでなく、本発明の塩基性塩化アルミ
ニウムは、その凝集性を利用して一般の塩基性塩化アル
ミニウムと同様に、制汗剤、化粧品原料、サイズ剤、医
薬品等の各種用途に使用できることは勿論である。Therefore, the novel basic aluminum chloride of the present invention exerts its effects best when it is used as a coagulant for water treatment, especially for water supply.
In addition to such utilization, the basic aluminum chloride of the present invention can be used in various applications such as antiperspirants, cosmetic raw materials, sizing agents, pharmaceuticals, etc., similarly to general basic aluminum chloride by utilizing its cohesiveness. Of course, it can be used.
Claims (3)
８０（但し、Ｍはアルカリ金属またはアルカリ土類金属
を示す。）、Ｃｌ／Ａｌ（モル比）０．５０〜１．９
５、塩基度６５〜８３％の塩基性塩化アルミニウムに於
いて、当該塩基性塩化アルミニウムを蒸留水約５００ｍ
ｌ（２０±２℃）にＡｌ2Ｏ3として１０ｐｐｍ添加し、
５重量％炭酸水素ナトリウム（ＮａＨＣＯ3）溶液でｐ
Ｈ７．８〜８．２に調整し３０分間５０ｒｐｍで攪拌
し、３０分間静置後、Ｎｏ．５Ｃ濾紙で濾過した後に於
ける濾過水の残留アルミニウム（Ａｌ）量がＹ≦０．６
２５Ｘ−４．６２５（但し、ＹはＡｌ量（ｐｐｍ）、Ｘ
はｐＨを示し、７．８≦Ｘ≦８．２である。）を満足す
る量であることを特徴とする新規なる塩基性塩化アルミ
ニウム。1. Composition M / Al (molar ratio) 0.04-1.
80 (where M represents an alkali metal or an alkaline earth metal), Cl / Al (molar ratio) 0.50 to 1.9
5. In basic aluminum chloride having a basicity of 65 to 83%, the basic aluminum chloride is distilled water about 500 m.
1 (20 ± 2 ° C.), 10 ppm as Al 2 O 3
5% by weight sodium bicarbonate (NaHCO 3 ) solution
H was adjusted to 7.8 to 8.2, stirred at 50 rpm for 30 minutes, and allowed to stand for 30 minutes. The amount of residual aluminum (Al) in the filtered water after filtration through 5C filter paper is Y ≦ 0.6.
25X-4.625 (where Y is the amount of Al (ppm), X
Represents pH, and 7.8 ≦ X ≦ 8.2. A novel basic aluminum chloride, characterized in that the amount satisfies (1).
ミニウムからなる水処理用凝集剤。2. A coagulant for water treatment comprising the novel basic aluminum chloride according to claim 1.
する塩基度６０％以上の塩基性塩化アルミニウム水溶液
に４０℃以下の温度でアルカリ金属及び／またはアルカ
リ土類金属の炭酸塩、炭酸水素ナトリウムまたは水酸化
物の１種以上を添加することを特徴とする請求項１記載
の新規なる塩基性塩化アルミニウムの製造方法。3. An alkali metal and / or alkaline earth metal carbonate or hydrogen carbonate at a temperature of 40 ° C. or less in a basic aluminum chloride aqueous solution of a basicity of 60% or more having a history of exposure to a temperature of 80 ° C. or more. The method for producing a novel basic aluminum chloride according to claim 1, wherein one or more of sodium and hydroxide are added.