JP2941680B2 - Scroll compressor and movable scroll member - Google Patents
Scroll compressor and movable scroll memberInfo
- Publication number
- JP2941680B2 JP2941680B2 JP7048847A JP4884795A JP2941680B2 JP 2941680 B2 JP2941680 B2 JP 2941680B2 JP 7048847 A JP7048847 A JP 7048847A JP 4884795 A JP4884795 A JP 4884795A JP 2941680 B2 JP2941680 B2 JP 2941680B2
- Authority
- JP
- Japan
- Prior art keywords
- scroll member
- movable scroll
- compressor
- movable
- spiral
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】[0001]
【産業上の利用分野】この発明は、例えば車両の空調装
置に使用されるスクロール型圧縮機、及びその圧縮機に
用いられる可動スクロール部材に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a scroll type compressor used for, for example, a vehicle air conditioner, and a movable scroll member used for the compressor.
【0002】[0002]
【従来の技術】一般に、スクロール型圧縮機において
は、ハウジング内に、基板上に渦巻部を有する固定スク
ロール部材と、基板上に渦巻部を有する可動スクロール
部材とが、それらの渦巻部にて互いに噛み合わされた状
態で配設されている。そして、両スクロール部材間には
圧縮室が形成され、可動スクロール部材が固定スクロー
ル部材の軸心の周りで公転されることにより、この圧縮
室が渦巻部の外周側から中心側に移動されて、ガスが次
第に圧縮される。2. Description of the Related Art Generally, in a scroll compressor, a fixed scroll member having a spiral portion on a substrate and a movable scroll member having a spiral portion on a substrate are provided in a housing. They are arranged in an engaged state. A compression chamber is formed between the two scroll members, and the movable scroll member is revolved around the axis of the fixed scroll member, whereby the compression chamber is moved from the outer peripheral side of the spiral part to the center side, The gas is gradually compressed.
【0003】従来のこの種のスクロール型圧縮機として
は、可動スクロール部材とフロントハウジングとの間に
鉄系材料よりなる固定プレートが介装され、可動スクロ
ール部材の基板が、この固定プレートに接触した状態で
公転されるように構成したものが提案されている。この
圧縮機においては、可動スクロール部材に対しその中心
軸線に沿って作用する圧縮反力が、固定プレートを介し
てフロントハウジングの荷重受け面にて受け止められ
る。In this type of conventional scroll compressor, a fixed plate made of an iron-based material is interposed between a movable scroll member and a front housing, and a substrate of the movable scroll member contacts the fixed plate. A configuration that revolves in a state has been proposed. In this compressor, a compression reaction force acting on the movable scroll member along its central axis is received by the load receiving surface of the front housing via the fixed plate.
【0004】また、この従来のスクロール型圧縮機にお
いては、可動スクロール部材が軽量で且つ切削加工性に
優れたアルミニウム合金により形成されている。この圧
縮機では、可動スクロール部材が軽量なので、その公転
運動に伴う遠心力を抑制することができるとともに、圧
縮機全体の軽量化を図ることができる。加えて、切削加
工を容易に行うことができるので、可動スクロール部材
として寸法精度に優れたものを得ることができる。In this conventional scroll compressor, the movable scroll member is made of an aluminum alloy that is lightweight and has excellent cutting workability. In this compressor, since the movable scroll member is lightweight, it is possible to suppress the centrifugal force caused by the revolving motion, and to reduce the weight of the compressor as a whole. In addition, since cutting can be easily performed, a movable scroll member having excellent dimensional accuracy can be obtained.
【0005】[0005]
【発明が解決しようとする課題】ところで、この種のス
クロール型圧縮機においては、ガスに含まれる潤滑油に
より接触部等の各部の潤滑が行われるようになっている
が、圧縮機の運転停止時にガスが液化して、その液状態
で潤滑油とともに圧縮機内から配管を通して流れ出る場
合がある。そして、このような場合には、圧縮機内から
潤滑油が持ち出されることになるので、圧縮機がオイル
レス状態に陥る。このため、圧縮機がオイルレス状態で
起動されたときには、アルミニウム合金製の可動スクロ
ール部材と鉄系材料の固定プレートとの接触部におい
て、可動スクロール部材の圧縮反力の受け面が固定プレ
ートに瞬時に凝着して、圧縮機がロック状態になるとい
う問題があった。In this type of scroll type compressor, the lubricating oil contained in the gas lubricates each part such as the contact part. However, the operation of the compressor is stopped. Occasionally, the gas liquefies, and in that liquid state, flows out of the compressor through a pipe together with the lubricating oil. Then, in such a case, since the lubricating oil is taken out of the compressor, the compressor falls into an oilless state. For this reason, when the compressor is started in an oil-less state, the receiving surface of the movable scroll member receiving the compression reaction force instantaneously contacts the fixed plate at the contact portion between the movable scroll member made of aluminum alloy and the fixed plate made of an iron-based material. And the compressor is locked.
【0006】この発明は、このような従来の技術に存在
する問題点に着目してなされたものである。その目的
は、圧縮機がオイルレス状態になって起動された場合で
も、可動スクロール部材の圧縮反力の受け面が対面する
部材に凝着するおそれを防止することができるスクロー
ル型圧縮機及び可動スクロール部材を提供することにあ
る。The present invention has been made by paying attention to such problems existing in the conventional technology. It is an object of the present invention to provide a scroll type compressor and a movable scroll type compressor which can prevent the receiving surface of a movable scroll member from receiving a compression reaction force from sticking to a facing member even when the compressor is started in an oilless state. It is to provide a scroll member.
【0007】この発明のその他の目的は、可動スクロー
ル部材の渦巻部についても耐焼付性を向上させることが
できるとともに、その性能を長期に亘って維持すること
ができるスクロール型圧縮機及び可動スクロール部材を
提供することにある。Another object of the present invention is to provide a scroll-type compressor and a movable scroll member capable of improving the seizure resistance of the spiral portion of the movable scroll member and maintaining the performance for a long period of time. Is to provide.
【0008】[0008]
【課題を解決するための手段】上記の目的を達成するた
めに、請求項1に記載のスクロール型圧縮機の発明で
は、可動スクロール部材は、その中心軸線に沿って作用
する圧縮反力を受ける部分に錫メッキを施したものであ
る。In order to achieve the above object, in the scroll compressor according to the first aspect of the present invention, the movable scroll member receives a compression reaction force acting along its central axis. The parts are tin-plated.
【0009】請求項2に記載の発明では、請求項1に記
載のスクロール型圧縮機において、前記可動スクロール
部材の渦巻部にニッケル−リンメッキを施したものであ
る。請求項3に記載の発明では、請求項1または2に記
載のスクロール型圧縮機において、前記錫メッキ中には
銅が1〜4重量%含有されているものである。According to a second aspect of the present invention, in the scroll type compressor according to the first aspect, a spiral portion of the movable scroll member is subjected to nickel-phosphorus plating. According to a third aspect of the present invention, in the scroll compressor according to the first or second aspect, the tin plating contains 1 to 4% by weight of copper.
【0010】請求項4に記載の発明では、請求項1〜3
の何れかに記載のスクロール型圧縮機において、前記ハ
ウジング及び両スクロール部材をアルミニウム系材料に
より形成し、可動スクロール部材とハウジングとの間に
は、可動スクロール部材に対して作用する圧縮反力を受
け止めるための鉄系材料よりなる固定プレートを配設し
たものである。[0010] According to the invention described in claim 4, claims 1 to 3 are provided.
Wherein the housing and both scroll members are formed of an aluminum-based material, and a compression reaction force acting on the movable scroll member is received between the movable scroll member and the housing. A fixing plate made of an iron-based material is provided.
【0011】請求項5に記載の可動スクロール部材の発
明では、基板の渦巻部が設けられている側とは反対側の
部分に錫メッキを施したものである。請求項6に記載の
発明では、請求項5に記載の可動スクロール部材におい
て、前記渦巻部にニッケル−リンメッキを施したもので
ある。In the invention of the movable scroll member according to the fifth aspect, the portion of the substrate opposite to the side where the spiral portion is provided is tin-plated. According to a sixth aspect of the present invention, in the movable scroll member according to the fifth aspect, the spiral portion is plated with nickel-phosphorus.
【0012】[0012]
【作 用】請求項1及び5に記載の発明によれば、可動
スクロール部材の圧縮反力を受ける部分、言い換えれば
基板の渦巻部が設けられている側とは反対側の部分に、
固体潤滑作用を有する錫メッキが施されている。このた
め、圧縮機がオイルレス状態になって起動された場合で
も、可動スクロール部材の圧縮反力の受け面と対面する
部材との間の潤滑性が良好に保たれ、両者が凝着するお
それはない。According to the first and fifth aspects of the present invention, the portion of the movable scroll member that receives the compression reaction force, in other words, the portion of the substrate opposite to the side on which the spiral portion is provided,
Tin plating having a solid lubricating action is applied. For this reason, even when the compressor is started in an oil-less state, the lubricating property between the compression reaction force receiving surface of the movable scroll member and the member facing the movable scroll member is kept good, and the two may adhere to each other. It is not.
【0013】請求項2及び6に記載の発明によれば、可
動スクロール部材の渦巻部にニッケル−リンメッキを施
すことにより、固定スクロール部材の渦巻部に対する耐
焼付性が向上される。また、一般に、ニッケル−リンメ
ッキは錫メッキと比較してその被膜を厚く且つ強固に形
成できる。このため、可動スクロール部材において、圧
縮反力の受け面より大きな面圧が加わる渦巻部にニッケ
ル−リンメッキを施せば、その渦巻部に錫メッキを施し
た場合と比較して、メッキの被膜が磨耗によって消失す
るのを抑制することができる。According to the second and sixth aspects of the present invention, by applying nickel-phosphorus plating to the spiral portion of the movable scroll member, seizure resistance to the spiral portion of the fixed scroll member is improved. In general, nickel-phosphorus plating can form a thicker and stronger film than tin plating. For this reason, in the movable scroll member, if nickel-phosphorus plating is applied to the spiral portion where a greater surface pressure is applied than the receiving surface of the compression reaction force, the plated coating is worn as compared with the case where tin is applied to the spiral portion. Can be prevented from disappearing.
【0014】請求項3に記載の発明によれば、錫メッキ
中に銅を1〜4重量%含有させることにより、錫メッキ
の被膜が緻密化及び強化され、可動スクロール部材に対
する錫メッキの密着性が向上されるとともに、耐磨耗性
が向上される。尚、銅の含有率を1重量%より小さくす
ると、錫メッキ被膜が十分に緻密化及び強化されず、4
重量%より大きくすると、錫メッキの固体潤滑作用が十
分に発揮されなくなって耐焼付性が低下する。つまり、
銅の含有率を1〜4重量%の範囲とすることにより、凝
着が生じないのは勿論、錫メッキが剥離したり磨耗した
りすることを抑制することができ、長期に亘って錫メッ
キの優れた潤滑性能を維持できる。According to the third aspect of the present invention, by including 1 to 4% by weight of copper in the tin plating, the tin plating film is densified and strengthened, and the adhesion of the tin plating to the movable scroll member is improved. And abrasion resistance is improved. If the copper content is less than 1% by weight, the tin plating film is not sufficiently densified and strengthened.
If it is larger than the weight percentage, the solid lubricating action of the tin plating cannot be sufficiently exhibited, and the seizure resistance decreases. That is,
When the content of copper is in the range of 1 to 4% by weight, not only adhesion does not occur but also tin plating can be suppressed from peeling or abrasion. Excellent lubrication performance can be maintained.
【0015】請求項4に記載の発明によれば、アルミニ
ウム系材料の可動スクロール部材に対して作用する圧縮
反力が、鉄系材料の固定プレートを介してアルミニウム
系材料のハウジングにて確実に受け止められる。このと
き、可動スクロール部材の圧縮反力の受け面に錫メッキ
が施されているので、その受け面が固定プレートに対し
て凝着するおそれはない。また、可動スクロール部材の
渦巻部にニッケル−リンメッキを施した場合には、アル
ミニウム系材料の固定スクロール部材に対する耐焼付性
が向上される。しかも、ニッケル−リンメッキはアルミ
ニウム系材料に対する密着性が良好で剥離し難いので、
メッキ被膜を厚く且つ強固に形成できることとも相まっ
て、その性能を長期に亘って維持できる。なお、ニッケ
ル−リンメッキは鉄系材料との馴染みが良く、鉄系材料
に対して焼付きを生じ易いが、鉄系材料である固定プレ
ートとの摺動部分には錫メッキが施されているので、問
題を生じない。According to the fourth aspect of the invention, the compression reaction force acting on the movable scroll member made of the aluminum-based material is reliably received by the housing made of the aluminum-based material via the fixing plate made of the iron-based material. Can be At this time, since the receiving surface of the movable scroll member for receiving the compression reaction force is tin-plated, there is no possibility that the receiving surface adheres to the fixed plate. Further, when nickel-phosphorus plating is applied to the spiral portion of the movable scroll member, seizure resistance to the fixed scroll member made of an aluminum-based material is improved. Moreover, nickel-phosphorus plating has good adhesion to aluminum-based materials and is difficult to peel off,
The performance can be maintained for a long period of time in combination with the fact that the plating film can be formed thickly and firmly. Nickel-phosphorous plating is familiar with iron-based materials and easily seizes on iron-based materials. However, since the sliding portion with a fixing plate made of iron-based material is tin-plated, , No problem.
【0016】[0016]
【実施例】以下、この発明の一実施例を、図面に基づい
て詳細に説明する。まず、スクロール型圧縮機の構成に
ついて述べると、図2及び図3に示すように、固定スク
ロール部材11はセンタハウジングを兼用し、その両端
面にはフロントハウジング12及びリヤハウジング13
が固定されている。回転軸14はベアリング15により
フロントハウジング12内に回転可能に支持され、その
内端には偏心軸16が突設されている。ブッシュ17は
偏心軸16に回転可能に支持されている。なお、固定ス
クロール部材11、フロントハウジング12及びリヤハ
ウジング13は、圧縮機全体の軽量化を図るため、アル
ミニウムまたはアルミニウム合金により形成されてい
る。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the present invention will be described below in detail with reference to the drawings. First, the structure of the scroll compressor will be described. As shown in FIGS. 2 and 3, the fixed scroll member 11 also serves as a center housing, and a front housing 12 and a rear housing 13 are provided on both end surfaces thereof.
Has been fixed. The rotating shaft 14 is rotatably supported in the front housing 12 by a bearing 15, and an eccentric shaft 16 protrudes from the inner end thereof. The bush 17 is rotatably supported by the eccentric shaft 16. The fixed scroll member 11, the front housing 12, and the rear housing 13 are made of aluminum or an aluminum alloy in order to reduce the weight of the entire compressor.
【0017】可動スクロール部材18はその外面の軸受
ボス部18cにおいて、前記ブッシュ17にベアリング
19を介して相対回転可能に嵌合支持されている。そし
て、この可動スクロール部材18は、回転軸14が回転
されたとき、偏心軸16によりブッシュ17及びベアリ
ング19を介して、回転軸14の軸線の周りで公転され
る。なお、可動スクロール部材18は、公転運動に伴う
遠心力を抑制するとともに、圧縮機全体の軽量化等を図
るため、アルミニウム合金により形成されている。The movable scroll member 18 is rotatably fitted to and supported by the bush 17 via a bearing 19 at a bearing boss 18c on the outer surface thereof. When the rotary shaft 14 is rotated, the movable scroll member 18 is revolved around the axis of the rotary shaft 14 by the eccentric shaft 16 via the bush 17 and the bearing 19. The movable scroll member 18 is formed of an aluminum alloy in order to suppress the centrifugal force caused by the revolving motion and to reduce the weight of the compressor as a whole.
【0018】前記固定スクロール部材11は、基板11
aとその内面に一体に形成された渦巻部11bとを備え
ている。同様に、可動スクロール部材18も、基板18
aとその内面に一体形成された渦巻部18bとを備えて
いる。そして、両スクロール部材11,18は渦巻部1
1b,18bにおいて互いに噛み合わされ、各渦巻部1
1b,18bの軸線方向の端縁が、対向するスクロール
部材11,18の基板11a,18aに当接されてい
る。この状態で、両スクロール部材11,18の基板1
1a,18a及び渦巻部11b,18bにて圧縮室20
が形成される。The fixed scroll member 11 includes a substrate 11
a and a spiral part 11b integrally formed on the inner surface thereof. Similarly, the movable scroll member 18 also
a and a spiral portion 18b integrally formed on the inner surface thereof. The scroll members 11 and 18 are provided in the spiral part 1.
1b and 18b, each spiral part 1
The axial edges of 1b and 18b are in contact with the substrates 11a and 18a of the scroll members 11 and 18 facing each other. In this state, the substrate 1 of both scroll members 11 and 18
1a, 18a and the spiral parts 11b, 18b
Is formed.
【0019】吸入室21は前記固定スクロール部材11
の周壁と可動スクロール部材18の渦巻部18bの外周
部との間に形成されている。吸入ポート22はフロント
ハウジング12の斜め上部に形成され、この吸入ポート
22から吸入室21内に冷媒ガスが吸入される。吐出孔
23は固定スクロール部材11の基板11aの中心に形
成され、この吐出孔23を介して圧縮室20がリヤハウ
ジング13内の吐出室24に連通される。吐出弁25は
吐出孔23の外端部に配設され、リテーナ26によりそ
の開放位置が規制される。The suction chamber 21 is provided with the fixed scroll member 11.
And the outer peripheral portion of the spiral portion 18b of the movable scroll member 18. The suction port 22 is formed diagonally above the front housing 12, and refrigerant gas is sucked into the suction chamber 21 from the suction port 22. The discharge hole 23 is formed at the center of the substrate 11 a of the fixed scroll member 11, and the compression chamber 20 communicates with the discharge chamber 24 in the rear housing 13 via the discharge hole 23. The discharge valve 25 is disposed at the outer end of the discharge hole 23, and its open position is regulated by a retainer 26.
【0020】図2〜図4に示すように、バネ鋼や炭素工
具鋼等の鉄系材料よりなるリング状の固定プレート27
は、前記フロントハウジング12の内壁面に配設され、
可動スクロール部材18の基板18aの外面に接触され
ている。2本の回り止めピン28はフロントハウジング
12の内壁面に突設され、これらのピン28が固定プレ
ート27上の孔29に嵌合されることにより、固定プレ
ート27がフロントハウジング12に対して回り止めさ
れている。As shown in FIGS. 2 to 4, a ring-shaped fixing plate 27 made of an iron-based material such as spring steel or carbon tool steel is used.
Is disposed on the inner wall surface of the front housing 12,
The movable scroll member 18 is in contact with the outer surface of the substrate 18a. The two detent pins 28 project from the inner wall surface of the front housing 12, and these pins 28 are fitted into holes 29 on the fixing plate 27, whereby the fixing plate 27 rotates with respect to the front housing 12. It has been stopped.
【0021】そして、前記圧縮室20内でのガス圧縮に
伴って作用する圧縮反力のうちで、可動スクロール部材
18に対しその軸線方向に沿って作用する圧縮反力が、
この固定プレート27によって受け止められる。なお、
固定プレート27の可動スクロール部材18と接触する
面に、ニッケル−リンメッキ等の硬化処理を施すように
してもよい。Among the compression reaction forces acting upon the gas compression in the compression chamber 20, the compression reaction force acting on the movable scroll member 18 along its axial direction is:
It is received by the fixing plate 27. In addition,
The surface of the fixed plate 27 that contacts the movable scroll member 18 may be subjected to a hardening process such as nickel-phosphorus plating.
【0022】図2、図3、図5及び図6に示すように、
複数対の自転防止ピン30,31は前記可動スクロール
部材18の基板18a及びフロントハウジング12の内
壁に突設され、各一対のピン30,31の先端部が互い
に所定間隔をおいて近接配置されている。自転防止リン
グ32は各一対のピン30,31にそれぞれ嵌挿され、
この自転防止リング32と自転防止ピン30,31との
協働により、可動スクロール部材18の自転が規制され
て、公転運動のみが許容されるようになっている。As shown in FIGS. 2, 3, 5 and 6,
A plurality of pairs of anti-rotation pins 30, 31 protrude from the base plate 18a of the movable scroll member 18 and the inner wall of the front housing 12, and the tips of the pair of pins 30, 31 are arranged close to each other at a predetermined interval. I have. The anti-rotation ring 32 is inserted into each of the pair of pins 30 and 31, respectively.
By the cooperation of the rotation preventing ring 32 and the rotation preventing pins 30, 31, the rotation of the movable scroll member 18 is restricted, and only the revolving motion is allowed.
【0023】次に、前記可動スクロール部材18につい
てさらに詳細に説明する。図1及び図2に示すように、
この実施例の可動スクロール部材18はその表面におい
て、圧縮反力を受ける基板18aの外面側の部分、言い
換えれば基板18aの渦巻部18bが設けられている側
とは反対側の部分に、錫メッキによる第1被膜層33が
形成されている。そして、基板18aの渦巻部18bが
設けられている側の部分及び渦巻部18bの部分に、ニ
ッケル−リンメッキによる第2被膜層34が形成されて
いる。Next, the movable scroll member 18 will be described in more detail. As shown in FIGS. 1 and 2,
In the movable scroll member 18 of this embodiment, tin plating is applied to a portion of the outer surface of the substrate 18a that receives the compression reaction force, in other words, a portion of the substrate 18a opposite to the side where the spiral portion 18b is provided. A first coating layer 33 is formed. The second coating layer 34 formed by nickel-phosphorus plating is formed on the portion of the substrate 18a on the side where the spiral portion 18b is provided and on the portion of the spiral portion 18b.
【0024】前記第1被膜層33を形成する錫は固体潤
滑作用を有し、非常に潤滑性に優れた材料である。この
第1被膜層33は、予め所定寸法に切削加工された可動
スクロール部材18を錫置換メッキ浴中に浸漬する無電
界メッキ法により形成される。即ち、電界メッキ法によ
りメッキを行うと、そのための設備が大がかりとなっ
て、製作コストが上昇するとともに、膜厚の調整が難し
くなるという問題がある。加えて、可動スクロール部材
18が電位を持ち、それにより可動スクロール部材18
が焼けて黒くなったりして、製品管理上の問題が生じ
る。しかしながら、無電界メッキ法によれば、そのよう
な問題は生じない。The tin forming the first coating layer 33 has a solid lubricating action and is a material having extremely excellent lubricity. The first coating layer 33 is formed by an electroless plating method in which the movable scroll member 18 previously cut to a predetermined size is immersed in a tin displacement plating bath. That is, when plating is performed by the electroplating method, there is a problem that the equipment for the plating becomes large-scale, the production cost increases, and it is difficult to adjust the film thickness. In addition, the movable scroll member 18 has an electric potential, thereby
Burns and turns black, causing problems in product management. However, according to the electroless plating method, such a problem does not occur.
【0025】そして、上記のようにして形成された第1
被膜層33は1〜3μm程度の厚さとなる。この場合、
メッキ前における可動スクロール部材18の面粗度は
1.5〜3μm程度が好ましい。即ち、可動スクロール
部材18の表面をある程度粗くしておくことにより、そ
の表面の凹凸に第1被膜層33が入り込んだ状態とな
る。その結果、可動スクロール部材18に対する第1被
膜層33の密着性が向上されて、同被膜層33が剥がれ
難くなる。加えて、第1被膜層33が前記固定プレート
27との摺動により磨耗しても、その被膜層33が完全
に消失するのを抑制することができ、第1被膜層33の
潤滑性能を長期に亘って維持することが可能となる。Then, the first formed as described above
The coating layer 33 has a thickness of about 1 to 3 μm. in this case,
The surface roughness of the movable scroll member 18 before plating is preferably about 1.5 to 3 μm. That is, by making the surface of the movable scroll member 18 rough to some extent, the first coating layer 33 enters the unevenness on the surface. As a result, the adhesion of the first coating layer 33 to the orbiting scroll member 18 is improved, and the coating layer 33 is less likely to be peeled off. In addition, even if the first coating layer 33 is worn by sliding with the fixing plate 27, it is possible to prevent the coating layer 33 from completely disappearing, and the lubricating performance of the first coating layer 33 can be improved for a long time. Can be maintained over the entire range.
【0026】また、本実施例では、前記錫置換メッキ浴
中に銅イオンが所定量添加され、形成される第1被膜層
33中に銅が1〜4重量%含有されるようになってい
る。即ち、錫メッキ中に銅を1〜4重量%含有させるこ
とにより、錫メッキの被膜層33が緻密化及び強化さ
れ、可動スクロール部材18に対する第1被膜層33の
密着性が向上されるとともに、耐磨耗性が向上される。In this embodiment, a predetermined amount of copper ions is added to the tin-substituted plating bath, and the first coating layer 33 formed contains 1 to 4% by weight of copper. . That is, by containing 1 to 4% by weight of copper in the tin plating, the tin plating coating layer 33 is densified and strengthened, and the adhesion of the first coating layer 33 to the movable scroll member 18 is improved, The wear resistance is improved.
【0027】尚、銅の含有率を1重量%より小さくする
と、第1被膜層33が十分に緻密化及び強化されない。
また、銅の含有率を4重量%より大きくすると、潤滑性
に優れる第1被膜層33中の錫成分が、可動スクロール
部材18の圧縮反力の受け面に対して円滑に供給されな
くなる。つまり、錫の固体潤滑作用が十分に発揮されな
くなって、耐焼付性が低下する。従って、銅の含有率を
1〜4重量%の範囲とすることにより、第1被膜層33
の耐焼付性が低下するのを抑制しつつ、その被膜層33
が剥離したり磨耗したりすることも抑制することがで
き、長期に亘って第1被膜層33の優れた潤滑性能を維
持できる。If the copper content is less than 1% by weight, the first coating layer 33 is not sufficiently densified and strengthened.
If the copper content is more than 4% by weight, the tin component in the first coating layer 33 having excellent lubricity will not be smoothly supplied to the compression reaction force receiving surface of the movable scroll member 18. That is, the solid lubricating action of tin cannot be sufficiently exhibited, and the seizure resistance is reduced. Therefore, by setting the copper content in the range of 1 to 4% by weight, the first coating layer 33 is formed.
Of the coating layer 33 while preventing the seizure resistance of the
Can be suppressed from being peeled or worn, and the excellent lubricating performance of the first coating layer 33 can be maintained for a long period of time.
【0028】前記第2被膜層34も、前述の第1被膜層
33の場合とほぼ同様にして、可動スクロール部材18
をメッキ浴中に浸漬することにより形成される。そし
て、このように形成された第2被膜層34は20μm程
度の厚さとなり、前記第1被膜層33と比較して厚く且
つ強固な被膜となる。また、この第2被膜層34を形成
するニッケル−リンメッキは、アルミニウム系材料に対
する密着性が良好であり、可動スクロール部材18に対
して強固に付着される。なお、このニッケル−リンメッ
キは鉄系材料との馴染みが良く、鉄系材料に対して焼付
きを生じ易いので、鉄系材料である固定プレート27と
の摺動面に使用することはできないが、アルミニウム系
材料に対しては良好な耐焼付性を示す。The second coating layer 34 is formed on the movable scroll member 18 in substantially the same manner as the first coating layer 33 described above.
Is immersed in a plating bath. The second coating layer 34 thus formed has a thickness of about 20 μm, and is a thicker and stronger coating than the first coating layer 33. Further, the nickel-phosphorous plating forming the second coating layer 34 has good adhesion to an aluminum-based material and is firmly attached to the movable scroll member 18. Note that this nickel-phosphorous plating is familiar with iron-based materials and easily seizes on iron-based materials, and thus cannot be used on the sliding surface with the fixing plate 27, which is an iron-based material. It shows good seizure resistance to aluminum-based materials.
【0029】さて、上記のように構成されたスクロール
型圧縮機において、回転軸14が回転されると、偏心軸
16の偏心回転に伴い、可動スクロール部材18が自転
を阻止された状態で回転軸14の軸線の周りで公転され
る。この動作により、冷媒ガスが吸入室21から両スク
ロール部材11,18間の圧縮室20内に取り込まれる
とともに、圧縮室20が渦巻部11b,18bの外周側
から中心側に移動されて、容積を徐々に減少する。従っ
て、冷媒ガスは圧縮室20内において次第に圧縮され、
吐出孔23から吐出弁25を押し開いて吐出室24内に
吐出される。In the scroll compressor having the above structure, when the rotary shaft 14 is rotated, the eccentric rotation of the eccentric shaft 16 prevents the movable scroll member 18 from rotating. It revolves around 14 axes. By this operation, the refrigerant gas is taken from the suction chamber 21 into the compression chamber 20 between the scroll members 11 and 18, and the compression chamber 20 is moved from the outer peripheral side of the spiral portions 11b and 18b to the center side to reduce the volume. Decrease gradually. Therefore, the refrigerant gas is gradually compressed in the compression chamber 20,
The discharge valve 25 is pushed open from the discharge hole 23 to be discharged into the discharge chamber 24.
【0030】このとき、可動スクロール部材18にはそ
の軸線方向に沿う圧縮反力が作用するが、その圧縮反力
は鉄系材料の固定プレート27により確実に受け止めら
れる。At this time, a compression reaction force is applied to the movable scroll member 18 along its axial direction. The compression reaction force is reliably received by the fixed plate 27 made of an iron-based material.
【0031】また、この実施例の可動スクロール部材1
8においては、圧縮反力を受ける基板18aの外面側の
部分に、潤滑性に優れた錫メッキによる第1被膜層33
が形成されている。このため、圧縮機の運転停止時にお
いて、液化した冷媒ガスの流出に伴い圧縮機内から潤滑
油が持ち出されて、オイルレス状態に陥った場合でも、
そのオイルレス状態の起動時に、可動スクロール部材1
8の圧縮反力の受け面が鉄系材料の固定プレート27に
凝着するおそれはない。従って、可動スクロール部材1
8の凝着により、圧縮機がロック状態になるのを防止す
ることができる。The movable scroll member 1 of this embodiment
8, the first coating layer 33 made of tin plating having excellent lubricity is provided on the outer surface of the substrate 18 a which receives the compression reaction force.
Are formed. For this reason, when the operation of the compressor is stopped, even if lubricating oil is taken out of the compressor with the outflow of the liquefied refrigerant gas and the oil-less state occurs,
When the oilless state starts, the movable scroll member 1
There is no fear that the receiving surface of the compression reaction force of 8 adheres to the fixing plate 27 made of an iron-based material. Therefore, the movable scroll member 1
The adhesion of 8 can prevent the compressor from being locked.
【0032】また、この実施例の可動スクロール部材1
8においては、渦巻部18bにニッケル−リンメッキに
よる第2被膜層34が形成されている。このため、前述
したオイルレス状態の起動時においても、可動スクロー
ル部材18の渦巻部18bと固定スクロール部材11の
渦巻部11bとの間で焼付きが生じるおそれはない。The movable scroll member 1 of this embodiment
In 8, the second coating layer 34 is formed on the spiral part 18b by nickel-phosphorus plating. For this reason, even when the oilless state is started, there is no possibility that seizure may occur between the spiral portion 18b of the movable scroll member 18 and the spiral portion 11b of the fixed scroll member 11.
【0033】なお、可動スクロール部材18の渦巻部1
8bには圧縮反力の受け面より大きな面圧が加わって、
固定スクロール部材11の渦巻部11bとの間での摺動
抵抗が非常に大きくなる。しかし、第2被膜層34を形
成するニッケル−リンメッキは、前記錫メッキと比較し
て厚く且つ強固な被膜になるとともに、可動スクロール
部材18に対して強固に付着される。従って、可動スク
ロール部材18の渦巻部18bにニッケル−リンメッキ
を施せば、その渦巻部18bに錫メッキを施した場合と
比較して、メッキの被膜が磨耗によって消失するのを抑
制することができる。そのため、このニッケル−リンメ
ッキの優れた耐焼付性を長期に亘って維持できる。The scroll portion 1 of the movable scroll member 18
8b receives a greater contact pressure than the receiving surface of the compression reaction force.
The sliding resistance between the fixed scroll member 11 and the spiral portion 11b becomes extremely large. However, the nickel-phosphorous plating forming the second coating layer 34 is thicker and stronger than the tin plating, and is firmly attached to the movable scroll member 18. Therefore, if the spiral portion 18b of the movable scroll member 18 is plated with nickel-phosphorus, it is possible to suppress the plating film from disappearing due to abrasion, as compared with the case where the spiral portion 18b is plated with tin. Therefore, the excellent seizure resistance of the nickel-phosphorous plating can be maintained for a long time.
【0034】以上のように、本実施例では、可動スクロ
ール部材18において、鉄系材料である固定プレート2
7との摺動面に錫メッキを施すことにより、その固定プ
レート27に対する凝着のおそれを防止することができ
る。しかも、その錫メッキ中に銅を1〜4重量%含有さ
せることにより、第1被膜層33の優れた潤滑性能を長
期に亘って維持できる。As described above, in the present embodiment, in the movable scroll member 18, the fixed plate 2 made of an iron-based material is used.
By applying tin plating to the sliding surface with the fixing plate 7, the possibility of adhesion to the fixing plate 27 can be prevented. Moreover, by including 1 to 4% by weight of copper in the tin plating, the excellent lubricating performance of the first coating layer 33 can be maintained for a long time.
【0035】また、本実施例では、可動スクロール部材
18において、その渦巻部18bにニッケル−リンメッ
キを施すことにより、アルミニウム合金製の固定スクロ
ール部材11に対する焼付きのおそれを防止することが
できるとともに、その優れた耐焼付性を長期に亘って維
持できる。In the present embodiment, the scroll portion 18b of the movable scroll member 18 is plated with nickel-phosphorus, thereby preventing the fixed scroll member 11 made of aluminum alloy from being seized. Its excellent seizure resistance can be maintained for a long time.
【0036】つまり、本実施例では、可動スクロール部
材18の部位に応じて、施すメッキの種類を変えること
により、対面する部材に対してそれぞれ優れた耐焼付性
を発揮できるとともに、その性能を長期に亘って維持で
きるのである。That is, in the present embodiment, by changing the type of plating to be applied in accordance with the position of the movable scroll member 18, excellent seizure resistance can be exhibited for the members facing each other, and the performance can be improved over a long period of time. Can be maintained.
【0037】なお、この発明は、次のように変更して具
体化することも可能である。 (1) 第1被膜層33を形成する錫メッキ中における
銅の含有率を、1〜4重量%の範囲内で適宜に変更する
こと。例えば、銅の含有率を2.5〜3.0重量%の範
囲とすると、第1被膜層33の耐焼付性を全く低下させ
ることなく、その被膜層33の密着性及び耐磨耗性を十
分なものとすることができ、よりバランスのとれた好ま
しいものとすることができる。The present invention can be embodied with the following modifications. (1) The content of copper in the tin plating forming the first coating layer 33 is appropriately changed within a range of 1 to 4% by weight. For example, when the content of copper is in the range of 2.5 to 3.0% by weight, the adhesion and abrasion resistance of the first coating layer 33 can be reduced without deteriorating the seizure resistance of the first coating layer 33 at all. Sufficient, more balanced and preferred.
【0038】上記実施例から把握できる技術的思想につ
いて以下に記載する。 (1) 前記錫メッキ中には銅が1〜4重量%含有され
ている請求項5又は6に記載の可動スクロール部材。The technical ideas that can be grasped from the above embodiment will be described below. (1) The movable scroll member according to claim 5 or 6, wherein copper is contained in the tin plating at 1 to 4% by weight.
【0039】このようにすれば、錫メッキの優れた潤滑
性能を長期に亘って維持できる。 (2) 銅の含有率を2.5〜3.0重量%の範囲とし
た請求項3に記載のスクロール型圧縮機。In this way, the excellent lubricating performance of tin plating can be maintained for a long time. (2) The scroll compressor according to claim 3, wherein the copper content is in the range of 2.5 to 3.0% by weight.
【0040】このようにすれば、錫メッキの耐焼付性を
全く低下させることなく、その錫メッキ被膜の密着性及
び耐磨耗性を十分なものとすることができる。In this way, the tin plating film can have sufficient adhesion and abrasion resistance without any reduction in the seizure resistance of the tin plating.
【0041】[0041]
【発明の効果】この発明は、以上のように構成されてい
るため、次のような効果を奏する。請求項1及び5に記
載の発明によれば、圧縮機がオイルレス状態になって起
動された場合でも、可動スクロール部材の圧縮反力の受
け面が対面する部材に凝着するおそれを防ぐことができ
る。従って、可動スクロール部材の凝着により圧縮機が
ロック状態になるのを防止することができる。The present invention is configured as described above, and has the following effects. According to the first and fifth aspects of the present invention, even when the compressor is started in an oil-less state, it is possible to prevent the possibility that the receiving surface of the movable scroll member receiving the compression reaction force adheres to the facing member. Can be. Therefore, it is possible to prevent the compressor from being locked due to adhesion of the movable scroll member.
【0042】請求項2及び6に記載の発明によれば、圧
縮機がオイルレス状態になって起動された場合でも、可
動スクロール部材の渦巻部が固定スクロール部材に対し
て焼付くおそれを防止することができるとともに、その
優れた耐焼付性を長期に亘って維持できる。According to the second and sixth aspects of the present invention, even when the compressor is started up in an oilless state, it is possible to prevent the spiral portion of the movable scroll member from seizing on the fixed scroll member. And excellent seizure resistance can be maintained for a long period of time.
【0043】請求項3に記載の発明によれば、可動スク
ロール部材の凝着が生じないのは勿論、錫メッキが剥離
したり磨耗したりすることを抑制することができ、長期
に亘って錫メッキの優れた潤滑性能を維持できる。According to the third aspect of the invention, it is possible to prevent the tin plating from peeling off or abrasion as well as to prevent the movable scroll member from sticking to each other. Excellent plating lubrication performance can be maintained.
【0044】請求項4に記載の発明によれば、鉄系材料
の固定プレートにより圧縮反力を確実に受け止めること
ができる。又、その固定プレートに対して可動スクロー
ル部材の圧縮反力の受け面が凝着するおそれがない。According to the fourth aspect of the invention, the compression reaction force can be reliably received by the fixing plate made of the iron-based material. Further, there is no possibility that the receiving surface of the movable scroll member receiving the compression reaction force adheres to the fixed plate.
【図1】 この発明の可動スクロール部材の一実施例を
示す縦断面図。FIG. 1 is a longitudinal sectional view showing one embodiment of a movable scroll member of the present invention.
【図2】 この発明のスクロール型圧縮機の全体を示す
縦断面図。FIG. 2 is a longitudinal sectional view showing the whole scroll compressor of the present invention.
【図3】 同じくスクロール型圧縮機の要部分解斜視
図。FIG. 3 is an exploded perspective view of a main part of the scroll compressor.
【図4】 固定プレートの回り止め機構を示す部分拡大
断面図。FIG. 4 is a partially enlarged cross-sectional view showing a rotation preventing mechanism of a fixing plate.
【図5】 自転防止機構を示す部分拡大断面図。FIG. 5 is a partially enlarged sectional view showing a rotation preventing mechanism.
【図6】 同じく自転防止機構を示す部分拡大断面図。FIG. 6 is a partially enlarged cross-sectional view showing the rotation preventing mechanism.
11…センタハウジングを兼用する固定スクロール部
材、11a…基板、11b…渦巻部、12…フロントハ
ウジング、13…リヤハウジング、18…可動スクロー
ル部材、18a…基板、18b…渦巻部、20…圧縮
室、27…固定プレート、33…錫メッキによる第1被
膜層、34…ニッケル−リンメッキによる第2被膜層。11: fixed scroll member also serving as center housing, 11a: substrate, 11b: spiral part, 12: front housing, 13: rear housing, 18: movable scroll member, 18a: substrate, 18b: spiral part, 20: compression chamber, 27: fixing plate, 33: first coating layer by tin plating, 34: second coating layer by nickel-phosphorus plating.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 磯村 賢児 愛知県刈谷市豊田町2丁目1番地 株式 会社 豊田自動織機製作所 内 (72)発明者 秋山 訓孝 愛知県刈谷市昭和町1丁目1番地 日本 電装 株式会社 内 (72)発明者 高津 浩 愛知県刈谷市昭和町1丁目1番地 日本 電装 株式会社 内 (72)発明者 大見 裕司 愛知県刈谷市昭和町1丁目1番地 日本 電装 株式会社 内 (72)発明者 佐藤 公彦 愛知県刈谷市昭和町1丁目1番地 日本 電装 株式会社 内 (56)参考文献 特開 平2−245487(JP,A) 特開 平2−125988(JP,A) 特開 昭62−159781(JP,A) (58)調査した分野(Int.Cl.6,DB名) F04C 18/02 311 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Kenji Isomura 2-1-1 Toyota-cho, Kariya-shi, Aichi Prefecture Inside the Toyota Industries Corporation (72) Inventor Noritaka Akiyama 1-1-1, Showa-cho, Kariya-shi, Aichi Japan Denso Co., Ltd. (72) Inventor Hiroshi Takatsu 1-1-1, Showa-cho, Kariya City, Aichi Prefecture, Japan Denso Co., Ltd. (72) Inventor Yuji Omi 1-1-1, Showa-cho, Kariya City, Aichi Prefecture, Japan Denso Corporation ( 72) Inventor Kimihiko Sato 1-1-1, Showa-cho, Kariya-shi, Aichi Japan Inside of Denso Co., Ltd. (56) References JP-A-2-245487 (JP, A) JP-A-2-125988 (JP, A) JP 62-159781 (JP, A) (58) Fields investigated (Int. Cl. 6 , DB name) F04C 18/02 311
Claims (6)
る固定スクロール部材と、基板上に渦巻部を有する可動
スクロール部材とを、それらの渦巻部にて互いに噛み合
わせた状態で配設して、両スクロール部材間に圧縮室を
形成し、可動スクロール部材を固定スクロール部材の軸
心の周りで公転させることにより、圧縮室を渦巻部の外
周側から中心側に移動させて、ガスの圧縮作用を行うよ
うにしたスクロール型圧縮機において、 前記可動スクロール部材は、その中心軸線に沿って作用
する圧縮反力を受ける部分に錫メッキを施したスクロー
ル型圧縮機。In a housing, a fixed scroll member having a spiral portion on a substrate and a movable scroll member having a spiral portion on a substrate are arranged in such a manner that they are meshed with each other by the spiral portions. By forming a compression chamber between the two scroll members and revolving the movable scroll member around the axis of the fixed scroll member, the compression chamber is moved from the outer peripheral side of the spiral part to the center side, thereby compressing the gas. In the scroll type compressor, the movable scroll member is tin-plated at a portion which receives a compression reaction force acting along a central axis of the movable scroll member.
ケル−リンメッキを施した請求項1に記載のスクロール
型圧縮機。2. The scroll type compressor according to claim 1, wherein a spiral portion of said movable scroll member is plated with nickel-phosphorus.
有されている請求項1または2に記載のスクロール型圧
縮機。3. The scroll compressor according to claim 1, wherein copper is contained in the tin plating in an amount of 1 to 4% by weight.
アルミニウム系材料により形成し、可動スクロール部材
とハウジングとの間には、可動スクロール部材に対して
作用する圧縮反力を受け止めるための鉄系材料よりなる
固定プレートを配設した請求項1〜3の何れかに記載の
スクロール型圧縮機。4. The housing and both scroll members are formed of an aluminum-based material, and between the movable scroll member and the housing are formed of an iron-based material for receiving a compression reaction force acting on the movable scroll member. The scroll compressor according to any one of claims 1 to 3, further comprising a fixed plate.
ロール部材において、 前記基板の渦巻部が設けられている側とは反対側の部分
に錫メッキを施した可動スクロール部材。5. A movable scroll member comprising a spiral part on a substrate, wherein the part of the substrate opposite to the side on which the spiral part is provided is tin-plated.
した請求項5に記載の可動スクロール部材。6. The movable scroll member according to claim 5, wherein said spiral portion is plated with nickel-phosphorus.