JP2908475B2 - Magnetic recording media - Google Patents
Magnetic recording mediaInfo
- Publication number
- JP2908475B2 JP2908475B2 JP1188098A JP18809889A JP2908475B2 JP 2908475 B2 JP2908475 B2 JP 2908475B2 JP 1188098 A JP1188098 A JP 1188098A JP 18809889 A JP18809889 A JP 18809889A JP 2908475 B2 JP2908475 B2 JP 2908475B2
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- back coat
- parts
- powder
- coat layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〔産業上の利用分野〕 この発明は、非磁性支持体の一面に磁性粉末と結合剤
とを含む塗膜タイプの磁性層を、他面にバツクコート層
を、それぞれ有する磁気テープなどの磁気記録媒体に関
する。DETAILED DESCRIPTION OF THE INVENTION [Industrial Application Field] This invention has a coating type magnetic layer containing a magnetic powder and a binder on one surface of a non-magnetic support, and a back coat layer on the other surface. The present invention relates to a magnetic recording medium such as a magnetic tape.
〔従来の技術〕 磁気テープなどの磁気記録媒体においては、走行性の
向上のため、磁性粉末と結合剤とを含む塗膜タイプの磁
性層を設けた非磁性支持体の背面側に、カーボンブラツ
クなどの粉体や潤滑剤などを含ませたバツクコート層を
形成することが、よく行われている。[Prior art] In a magnetic recording medium such as a magnetic tape, a carbon black is provided on the back side of a non-magnetic support provided with a coating type magnetic layer containing a magnetic powder and a binder in order to improve running properties. It is common practice to form a back coat layer containing a powder of such as a lubricant or the like.
しかるに、上記の如き従来公知のバツクコート層は、
ビデオテープレコーダの金属製ガイドに対する摩擦係数
の低下には効果があるが、プラスチツクガイドに対する
摩擦係数の低下にはまだ不充分であつて、走行性の面で
問題があつた。However, the conventionally known back coat layer as described above,
Although it is effective in reducing the coefficient of friction of the video tape recorder against the metal guide, it is still insufficient to reduce the coefficient of friction with the plastic guide, and there is a problem in running performance.
この発明は、上述の事情に照らし、プラスチツクガイ
ドに対する摩擦係数の低下にも寄与するバツクコート層
の形成によつて、磁気テープなどの磁気記録媒体の走行
性の改善を図ることを目的としている。SUMMARY OF THE INVENTION In view of the above circumstances, it is an object of the present invention to improve the runnability of a magnetic recording medium such as a magnetic tape by forming a back coat layer that also contributes to a reduction in the coefficient of friction with a plastic guide.
この発明者らは、上記の目的を達成するために鋭意検
討を加えた結果、磁性粉末と結合剤とを含む塗膜タイプ
の磁性層に対して、バツクコート層中に特定の添加剤を
含ませることにより、プラスチツクガイドに対する摩擦
係数を低下でき、これにより走行性を大幅に向上できる
ものであることを見い出し、この発明を完成するに至つ
た。The present inventors have made intensive studies to achieve the above object, and as a result, included a specific additive in the back coat layer for the coating type magnetic layer containing the magnetic powder and the binder. As a result, it has been found that the friction coefficient with respect to the plastic guide can be reduced, whereby the running performance can be greatly improved, and the present invention has been completed.
すなわち、この発明は、非磁性支持体の一面に磁性粉
末と結合剤とを含む塗膜タイプの磁性層を、他面にカー
ボンブラツクと充填剤と結合剤とを含むバツクコート層
を、それぞれ設けてなる磁気記録媒体において、上記の
バツクコート層中に、RCONH2（式中、Ｒは炭素数11〜21
の飽和または不飽和の一価の炭化水素基である）で表わ
される脂肪酸アミドが含有されていることを特徴とする
磁気記録媒体に係るものである。That is, the present invention provides a non-magnetic support having a coating type magnetic layer containing a magnetic powder and a binder on one surface and a back coat layer containing a carbon black, a filler and a binder on the other surface. In the magnetic recording medium, RCONH 2 (where R represents a carbon number of 11 to 21)
Which is a saturated or unsaturated monovalent hydrocarbon group).
この発明において使用する脂肪酸アミドは、上述のよ
うに、一般式RCONH2（式中、Ｒは炭素数11〜21の飽和ま
たは不飽和の一価の炭化水素基である）で表わされるも
のであつて、具体的には、ラウリン酸アミド、パルミチ
ン酸アミド、ステアリン酸アミドなどの飽和脂肪酸アミ
ド、オレイン酸アミド、リシノール酸アミドなどの不飽
和脂肪酸アミドなどが挙げられる。これらの中でも、溶
剤への溶解性の面から、取り扱いが容易な不飽和脂肪酸
アミドが特に好ましい。As described above, the fatty acid amide used in the present invention is represented by the general formula RCONH 2 (where R is a saturated or unsaturated monovalent hydrocarbon group having 11 to 21 carbon atoms). Specific examples thereof include saturated fatty acid amides such as lauric acid amide, palmitic acid amide and stearic acid amide, and unsaturated fatty acid amides such as oleic acid amide and ricinoleic acid amide. Among these, unsaturated fatty acid amides which are easy to handle are particularly preferable from the viewpoint of solubility in a solvent.
このような脂肪酸アミドの使用量としては、バツクコ
ート層中の粉体に対し、通常0.1〜10重量％、好ましく
は１〜５重量％であるのがよい。この量が過少では摩擦
係数の低下に効果がなく、過多となるとブルーミングが
発生し、走行系の汚濁などを引き起こすため、好ましく
ない。The amount of the fatty acid amide used is usually 0.1 to 10% by weight, preferably 1 to 5% by weight, based on the powder in the back coat layer. If the amount is too small, there is no effect in lowering the coefficient of friction. If the amount is too large, blooming occurs and polluting of the traveling system is caused, which is not preferable.
この発明において、上記の脂肪酸アミドを含有するバ
ツクコート層は、たとえば、カーボンブラツクや、炭酸
カルシウム粉末、硫酸バリウム粉末、酸化亜鉛粉末、α
−F2O3粉末、酸化クロム粉末、酸化チタン粉末の如き充
填剤などよりなる各種の粉体と、結合剤と、必要により
脂肪酸、脂肪酸エステルなどの公知の潤滑剤などととも
に、上記の脂肪酸アミドを均一に混合したバツクコート
用塗料を調製し、この塗料を一面側に磁性層を有するポ
リエステルフイルムなどの非磁性支持体の他面側に、乾
燥後の厚さが通常0.5〜1.5μｍとなるように塗着するこ
とにより、形成される。In the present invention, the back coat layer containing the fatty acid amide may be, for example, carbon black, calcium carbonate powder, barium sulfate powder, zinc oxide powder, α
-F 2 O 3 powder, chromium oxide powder, and various of the powder consisting of such fillers such as titanium oxide powder, a binder, a fatty acid, with such known lubricants such as fatty acid esters if necessary, the above-mentioned fatty acid amide To prepare a back coat paint, which is uniformly mixed, and apply the paint on the other side of a non-magnetic support such as a polyester film having a magnetic layer on one side so that the thickness after drying is usually 0.5 to 1.5 μm. It is formed by coating on the surface.
上記の結合剤としては、塩化ビニル−酢酸ビニル系共
重合体、ポリビニルブチラール系樹脂、繊維素系樹脂、
ポリウレタン系樹脂、ポリエステル系樹脂、架橋剤とし
てのポリイソシアネート化合物、放射線硬化型樹脂な
ど、従来よりバツクコート層のバインダとして知られる
ものをいずれも単独でまたは二種以上を混合して使用で
きる。As the above binder, vinyl chloride-vinyl acetate copolymer, polyvinyl butyral resin, cellulose resin,
Conventionally known binders for the back coat layer, such as polyurethane-based resins, polyester-based resins, polyisocyanate compounds as a crosslinking agent, and radiation-curable resins, can be used alone or in combination of two or more.
この発明の磁気記録媒体において、非磁性支持体の一
面側に設けられる磁性層は、磁性粉末、結合剤および必
要に応じて配合される各種の添加剤を含む磁性塗料を塗
着した塗膜タイプのものである。In the magnetic recording medium of the present invention, the magnetic layer provided on one surface side of the non-magnetic support is a coating type coated with a magnetic paint containing a magnetic powder, a binder, and various additives optionally added. belongs to.
塗膜タイプの磁性層における磁性粉末には、たとえば
γ−Fe2O3、Fe3O4、これらの中間的酸化物、Co含有γ−
Fe2O3、Co含有Fe3O4の如き針状酸化鉄粉末、バリウムフ
エライトの如き六方晶系板状フエライトなどの酸化物系
磁性粉末のほか、Fe、Co、Ni、これらの合金などの金属
磁性粉末など、従来公知のものを広く使用できる。The magnetic powder in the coating type magnetic layer includes, for example, γ-Fe 2 O 3 , Fe 3 O 4 , an intermediate oxide thereof, and Co-containing γ-
Fe 2 O 3 , Co-containing iron oxide powder such as Fe 3 O 4 , oxide-based magnetic powder such as hexagonal plate-like ferrite such as barium ferrite, Fe, Co, Ni, and alloys thereof Conventionally known materials such as metal magnetic powder can be widely used.
また、結合剤としては、前記したバツクコート層の結
合剤として列挙したものなどを同様に使用でき、さら
に、必要に応じて配合される添加剤としては、分散剤、
潤滑剤、研摩剤、帯電防止剤、充填剤などが挙げられ
る。Further, as the binder, those listed above as the binder of the back coat layer and the like can be used in the same manner.
Lubricants, abrasives, antistatic agents, fillers and the like can be mentioned.
以上のように、この発明においては、磁性粉末と結合
剤とを含む塗膜タイプの磁性層に対して、バツクコート
層中に特定の脂肪酸アミドを含ませたことにより、プラ
スチツクガイドに対する摩擦係数が低下して、走行性の
大幅に改善された磁気記録媒体を得ることができる。As described above, in the present invention, a specific fatty acid amide is included in the back coat layer of the coating type magnetic layer containing the magnetic powder and the binder, so that the friction coefficient with respect to the plastic guide is reduced. As a result, it is possible to obtain a magnetic recording medium having greatly improved runnability.
つぎに、この発明を実施例に基づいて具体的に説明す
る。なお、以下部とあるのは重量部を意味する。Next, the present invention will be specifically described based on examples. The following parts mean parts by weight.
実施例１ 厚さ14μｍのポリエステルフイルムの一面側に、Co含
有γ−Fe2O3粉末（平均長軸径0.15μｍ、平均軸比10）1
00部、カーボンブラツク（キャボツト社製のモーガル
Ｌ）６部、α−Fe2O3粉末（戸田工業社製のTF−100）３
部、塩化ビニル−酢酸ビニル−ビニルアルコール共重合
体11部、ポリウレタン樹脂７部、ポリイソシアネート化
合物５部、ミリスチン酸３部、シクロヘキサノン110
部、トルエン110部からなる磁性塗料を、乾燥後の厚さ
が3.0μｍとなるように塗布し、乾燥後、鏡面化処理を
施して、磁性層を形成した。Example 1 Co-containing γ-Fe 2 O 3 powder (average major axis diameter 0.15 μm, average axis ratio 10) was placed on one side of a 14 μm-thick polyester film.
00 parts, carbon black (Mogal L, manufactured by Cabot Corporation) 6 parts, α-Fe 2 O 3 powder (TF-100, manufactured by Toda Kogyo) 3
Parts, vinyl chloride-vinyl acetate-vinyl alcohol copolymer 11 parts, polyurethane resin 7 parts, polyisocyanate compound 5 parts, myristic acid 3 parts, cyclohexanone 110
Parts, and 110 parts of toluene, a magnetic paint was applied so that the thickness after drying was 3.0 μm, and after drying, a mirror surface treatment was performed to form a magnetic layer.
つぎに、このポリエステルフイルムの他面側に、カー
ボンブラツク（キャボツト社製のモーガルＬ、平均粒子
径0.024μｍ）120部、炭酸カルシウム（白石工業社製の
ホモカルＤ、平均粒子径0.07μｍ）60部、α−Fe2O3粉
末（戸田工業社製のTF−100、平均粒子径0.1μｍ）20
部、ニトロセルロース82.5部、ポリウレタン樹脂82.5
部、オレイン酸アミド（日本化成社製のダイヤミツド
Ｏ）６部、シクロヘキサノン750部、トルエン750部から
なるバツクコート用塗料を、塗布乾燥して、0.8〜1.0μ
ｍのバツクコート層を形成し、その後1.27cm幅に裁断し
て、磁気テープを作製した。Next, on the other side of the polyester film, 120 parts of carbon black (Mogal L, manufactured by Cabot Corporation, average particle size 0.024 μm), and 60 parts of calcium carbonate (Homocal D, manufactured by Shiraishi Industry Co., average particle size 0.07 μm) , Α-Fe 2 O 3 powder (TF-100 manufactured by Toda Kogyo Co., Ltd., average particle size 0.1 μm) 20
Parts, nitrocellulose 82.5 parts, polyurethane resin 82.5
Parts, oleic acid amide (Diamond O manufactured by Nippon Kasei Co., Ltd.) 6 parts, cyclohexanone 750 parts, toluene 750 parts, a back coat paint was applied and dried to obtain 0.8 to 1.0 μm.
Then, a back coat layer having a length of m was formed and then cut into 1.27 cm width to prepare a magnetic tape.
実施例２ バツクコート用塗料におけるオレイン酸アミドに代え
て、ラウリン酸アミド（日本化成社製のダイヤミツド
Ｙ）６部を使用した以外は、実施例１と同様にして磁気
テープを作製した。Example 2 A magnetic tape was produced in the same manner as in Example 1 except that 6 parts of lauric amide (Diamond Y manufactured by Nippon Kasei Co., Ltd.) was used instead of oleic amide in the backcoat paint.
比較例１ バツクコート用塗料におけるオレイン酸アミド６部を
除いた以外は、実施例１と同様にして磁気テープを作製
した。Comparative Example 1 A magnetic tape was produced in the same manner as in Example 1 except that 6 parts of oleic amide in the backcoat paint was omitted.
以上の実施例および比較例の各磁気テープにつき、バ
ツクコート層の摩擦係数と、バツクコート層および磁性
層の耐久性とを、下記の要領で調べた結果は、第１表に
示されるとおりであつた。For each of the magnetic tapes of the above Examples and Comparative Examples, the friction coefficient of the back coat layer and the durability of the back coat layer and the magnetic layer were examined in the following manner. The results are as shown in Table 1. .
＜バツクコート層の摩擦係数＞ ポリアセタール樹脂ピンに90度で巻き付け、荷重31.4
g、摺接速度1,000mm/分で摺接して、摩擦係数を測定し
た。<Friction coefficient of back coat layer> Wrap around polyacetal resin pin at 90 degrees, load 31.4
g, sliding contact was performed at a sliding contact speed of 1,000 mm / min, and the friction coefficient was measured.
＜バツクコート層および磁性層の耐久性＞ VHS式のVTR（ビデオテープレコーダ）を用い、テープ
長さ100mを1,000回パスしたときのバツクコート層と磁
性層の損傷程度を目視観察し、それぞれ５段階（5:優←
→1:劣）で評価した。<Durability of back coat layer and magnetic layer> Using a VHS type VTR (video tape recorder), visually inspect the degree of damage to the back coat layer and the magnetic layer when the tape length 100m is passed 1,000 times. 5: Yu ←
→ 1: Poor).
上記の第１表から、この発明の磁気テープ（実施例1,
2）は、バツクコート層の摩擦係数が小さく、走行性に
非常にすぐれているため、バツクコート層のみならず磁
性層の耐久性にも好結果が得られていることがわかる。 From the above Table 1, it can be seen that the magnetic tape of the present invention (Example 1,
In the case of 2), since the friction coefficient of the back coat layer was small and the running property was excellent, it was found that good results were obtained not only in the back coat layer but also in the durability of the magnetic layer.
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.6，ＤＢ名) G11B 5/704 G11B 5/66 ──────────────────────────────────────────────────続 き Continued on the front page (58) Field surveyed (Int.Cl. 6 , DB name) G11B 5/704 G11B 5/66
Claims (1)
を含む塗膜タイプの磁性層を、他面にカーボンブラツク
と充填剤と結合剤とを含むバツクコート層を、それぞれ
有する磁気記録媒体において、上記のバツクコート層中
に、RCONH2（式中、Ｒは炭素数11〜21の飽和または不飽
和の一価の炭化水素基である）で表わされる脂肪酸アミ
ドが含まれていることを特徴とする磁気記録媒体。1. A magnetic recording system comprising a nonmagnetic support having a coating-type magnetic layer containing a magnetic powder and a binder on one surface and a backcoat layer containing a carbon black, a filler and a binder on the other surface. In the medium, a fatty acid amide represented by RCONH 2 (where R is a saturated or unsaturated monovalent hydrocarbon group having 11 to 21 carbon atoms) is contained in the back coat layer. Characteristic magnetic recording medium.