JP2736723B2 - Clad end treatment method and clad end treatment structure for partially unbonded PC steel strand - Google Patents
Clad end treatment method and clad end treatment structure for partially unbonded PC steel strandInfo
- Publication number
- JP2736723B2 JP2736723B2 JP29661392A JP29661392A JP2736723B2 JP 2736723 B2 JP2736723 B2 JP 2736723B2 JP 29661392 A JP29661392 A JP 29661392A JP 29661392 A JP29661392 A JP 29661392A JP 2736723 B2 JP2736723 B2 JP 2736723B2
- Authority
- JP
- Japan
- Prior art keywords
- wire
- stranded wire
- cladding tube
- partially
- unbonded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】この発明は、被覆管による部分的
な被覆によって、コンクリートに定着、固定されないア
ンボンド部分を構成した部分アンボンドPC鋼より線の被
覆管端末処理方法および被覆管端末処理構造に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method and a structure for treating the end of a partially unbonded PC steel stranded wire which constitutes an unbonded portion which is not fixed and fixed to concrete by partial covering with a cladding tube. .
【０００２】[0002]
【従来の技術】山崩れ等を防止する、いわゆるアースア
ンカー工法等に用いられる高強度鋼線として、たとえ
ば、数本の側ワイヤを芯ワイヤの回りで撚って形成した
PC鋼より線（ストランドまたはケーブルともいう）がよ
く知られている。このようなPC鋼より線は、通常、裸線
として形成され、一般に、打設されたコンクリートに定
着、固定可能となっている。2. Description of the Related Art As a high-strength steel wire used for a so-called earth anchoring method or the like for preventing a landslide or the like, for example, several side wires are formed by twisting around a core wire.
PC strands (also known as strands or cables) are well known. Such a PC steel stranded wire is usually formed as a bare wire, and can generally be fixed and fixed to the cast concrete.
【０００３】また、このような一般のPC鋼より線（定着
型PC鋼より線）に対して、コンクリートに定着、固定さ
れず、伸縮の抑制されないアンボンドPC鋼より線と称さ
れる非定着型のPC鋼より線も知られている。このアンボ
ンドPC鋼より線では、ポリエチレン樹脂等のプラスチッ
クからなる被覆管がPC鋼より線を覆うことによって、コ
ンクリートからPC鋼より線を隔離するとともに、グリー
ス等の防錆油を被覆管の内部に充填することによって、
PC鋼より線の錆を防止するとともに、被覆管、PC鋼より
線の間の摩擦抵抗を低減して、PC鋼より線の伸縮を可能
としている。[0003] Further, with respect to such general PC steel stranded wires (fixed type PC steel stranded wires), non-fixed type stranded wires called unbonded PC steel stranded wires which are not fixed and fixed to concrete and are not restricted in expansion and contraction. PC strands are also known. In this unbonded PC steel stranded wire, a cladding tube made of plastic such as polyethylene resin covers the PC steel stranded wire, thereby isolating the PC steel stranded wire from concrete and applying grease or other rust-preventive oil to the inside of the cladding tube. By filling
Prevents rusting of PC strands, reduces frictional resistance between cladding tube and PC strands, and enables expansion and contraction of PC strands.
【０００４】そして、更に、裸線のまま残した裸線部分
（ボンド部分）とグリース等を充填した被覆管で覆った
被覆部分（アンボンド部分）とを併存させた部分アンボ
ンドPC鋼より線も、アースアンカー工法に用いられるPC
鋼より線としてよく知られている。[0004] Furthermore, a part of unbonded PC steel wire in which a bare wire part (bond part) left as a bare wire and a coating part (unbonded part) covered with a cladding tube filled with grease or the like coexists. PC used for earth anchor method
Also known as steel strand.
【０００５】部分アンボンドPC鋼より線の成形方法とし
ては、押出成形による方法および差し込みによる方法が
一般的とされている。[0005] As a method of forming a partially unbonded PC steel strand, a method by extrusion and a method by insertion are generally considered.
【０００６】たとえば、前者の押出成形による成形方法
においては、まず、溶融プラスチック、たとえば、ポリ
エチレン樹脂をPC鋼より線の表面に押し出しながら、半
流動体状のグリースをPC鋼より線、溶融プラスチック間
に部分的に充填し、PC鋼より線が、ポリエチレン樹脂か
らなる被覆管により、全長にわたって被覆される。For example, in the former molding method by extrusion molding, first, while extruding a molten plastic, for example, a polyethylene resin onto the surface of a PC steel stranded wire, grease in a semi-fluid state is applied between the PC steel stranded wire and the molten plastic. And a PC steel strand is covered over the entire length with a cladding tube made of polyethylene resin.
【０００７】そして、グリースの充填されない部分にお
いては、被覆管を介した目視によるPC鋼より線の確認が
容易に行えるため、その部分の両端で被覆管を切断し、
グリースの充填されていない部分の被覆管を剥離するこ
とによって、アンボンド部分の残された部分アンボンド
PC鋼より線が成形されている。[0007] Then, in the portion where the grease is not filled, the PC steel stranded wire can be easily confirmed visually through the cladding tube. Therefore, the cladding tube is cut at both ends of the portion,
By peeling off the cladding tube where the grease is not filled, the remaining unbonded part is unbonded.
PC steel strand is formed.
【０００８】また、後者の差し込みによる方法において
は、アンボンド部分の長さに対応して予め成形された被
覆管を、PC鋼より線の対応する部分に、グリースを塗布
しながら挿着して、PC鋼より線の所定箇所を部分的に被
覆した部分アンボンドPC鋼より線が成形されている。In the latter method of insertion, a cladding tube formed in advance corresponding to the length of the unbonded portion is inserted into the corresponding portion of the PC steel stranded wire while applying grease, A partially unbonded PC steel wire is formed by partially covering a predetermined portion of the PC steel wire.
【０００９】[0009]
【発明が解決しようとする課題】ところで、上記のよう
な公知の方法においては、ボンド部分、アンボンド部分
の境界部、つまり、被覆管の各端末に止水材等を塗布
し、ビニールテープ等で被覆して、削孔水、地下水の流
入や被覆管のずれ等が阻止されている。By the way, in the above-mentioned known method, a waterproof material or the like is applied to a boundary portion between a bonded portion and an unbonded portion, that is, to each end of a cladding tube, and is coated with a vinyl tape or the like. The coating prevents the inflow of drilling water and groundwater and the displacement of the cladding pipe.
【００１０】ここで、コンクリートの凝固熱やPC鋼より
線自体の高温化等によって、PC鋼より線のアンボンド部
分が加熱されると、被覆管、PC鋼より線間に充填された
グリースが液状化する虞れがある。PC鋼より線の表面に
おいては、止水材、ビニールテープ等によって、アンボ
ンド部分からのグリースの流出が阻止される。Here, when the unbonded portion of the PC steel stranded wire is heated due to the heat of solidification of the concrete or the high temperature of the PC steel stranded wire, the grease filled between the cladding tube and the PC steel stranded wire becomes liquid. There is a risk of becoming. On the surface of the PC stranded wire, the waterproof material, vinyl tape, etc. prevent the grease from flowing out from the unbonded portion.
【００１１】しかしながら、PC鋼より線においては、通
常、芯ワイヤ、側ワイヤ間に隙間が生じるため、液状化
されたグリースが隙間を伝わってアンボンド部分の外
部、つまりボンド部分に流出し、コンクリート、PC鋼よ
り線間の定着力を低下させる虞れがある。However, in the case of PC steel stranded wire, a gap is usually formed between the core wire and the side wire, so that the liquefied grease flows through the gap and flows out of the unbonded portion, that is, the bonded portion, and concrete, There is a possibility that the anchoring force between the strands of the PC steel may be reduced.
【００１２】また、特に差し込みによる方法において
は、PC鋼より線にグリースを塗布しながら被覆管を挿着
しているにすぎないため、グリースが十分に充填され
ず、被覆管、PC鋼より線間に隙間が生じやすい。そのた
め、境界部の止水加工が十分に施されていないと、定着
部への加圧注入の際にコンクリート材等が被覆管内に侵
入したり、削孔水、地下水等が侵入したりする虞れがあ
る。[0012] In particular, in the insertion method, the grease is not sufficiently filled because the cladding tube is simply inserted while applying grease to the PC steel stranded wire. A gap is easily generated between them. Therefore, if the boundary portion is not sufficiently waterproofed, there is a possibility that concrete material or the like may enter the cladding tube, or drilling water, groundwater, or the like may enter when the pressure is injected into the fixing portion. There is.
【００１３】被覆管内へのコンクリート材、削孔水等の
異物の侵入は、アンボンド部分でのPC鋼より線の伸縮動
作を妨げるため、好ましくない。Intrusion of foreign matters such as concrete material and drilling water into the cladding tube is not preferable because it hinders the expansion and contraction of the PC stranded wire at the unbonded portion.
【００１４】この発明は、被覆管内外を確実に隔離可能
な部分アンボンドPC鋼より線の被覆管端末処理方法およ
び被覆管端末処理構造の提供を目的としている。SUMMARY OF THE INVENTION An object of the present invention is to provide a method and a structure for terminally treating a clad tube of a partially unbonded PC steel strand which can reliably isolate the inside and the outside of the clad tube.
【００１５】[0015]
【課題を解決するための手段】この目的を達成するため
に、この発明の部分アンボンドPC鋼より線の被覆管端末
処理方法によれば、被覆管端末の隣接する側ワイヤ間を
外力のもとで強制的に拡開し、側ワイヤの隙間から、少
なくとも芯ワイヤの回りに止水材を注入、充填するとと
もに、PC鋼より線の止水材の充填された当該箇所の外周
面と被覆管とを被覆手段で連続的に被覆している。According to the present invention, there is provided a method for treating a cladding end of a partially unbonded PC stranded wire according to the present invention. Forcibly spread the water through the gap between the side wires, inject and fill the water-stop material at least around the core wire, and also fill the outer peripheral surface of the place where the water-stop material of the PC stranded wire is filled and the cladding tube. Are continuously coated by the coating means.
【００１６】[0016]
【実施例】以下、図面を参照しながらこの発明の実施例
について詳細に説明する。Embodiments of the present invention will be described below in detail with reference to the drawings.
【００１７】図１に示すように、この発明に係る部分ア
ンボンドPC鋼より線の被覆管端末処理構造10によれば、
部分アンボンドPC鋼より線12のアンボンド部分を形成す
る被覆管14の端末部分に、止水加工が施されている。As shown in FIG. 1, according to the cladding end treatment structure 10 for partially unbonded PC stranded wire according to the present invention,
The end portion of the cladding tube 14 that forms the unbonded portion of the partially unbonded PC stranded wire 12 is subjected to a water stopping process.
【００１８】図１に加えて図２を見るとわかるように、
数本、たとえば、６本の側ワイヤ16a を１本の芯ワイヤ
16b の回りで撚って、PC鋼より線16が形成され、アンボ
ンドチューブ等と称されるポリエチレン樹脂製の被覆管
14でPC鋼より線の所定部分を被覆して、部分アンボンド
PC鋼より線12が成形されている。As can be seen from FIG. 2 in addition to FIG.
Several, for example, six side wires 16a are replaced with one core wire
Twisted around 16b to form a PC steel stranded wire 16, a polyethylene resin cladding tube called unbonded tube etc.
Cover the specified part of the PC stranded wire with 14 and partially unbond
PC steel strand 12 is formed.
【００１９】このような部分アンボンドPC鋼より線12に
おいては、たとえば、PC鋼より線16の裸線部分がコンク
リート等に定着、固定可能なボンド部分、および、被覆
管14によって被覆された部分がアンボンド部分とそれぞ
れ称され、アンボンド部分のPC鋼より線が、被覆管に対
して伸縮可能となっている。In such a partially unbonded PC steel stranded wire 12, for example, a bare wire portion of the PC steel stranded wire 16 can be fixed and fixed to concrete or the like, and a portion covered by the cladding tube 14 can be fixed. The unbonded parts are called PC steel strands, and the PC stranded wire of the unbonded part is stretchable with respect to the cladding tube.
【００２０】このような構成においては、通常、被覆管
14、PC鋼より線16間にグリース等の防錆油18が充填さ
れ、被覆管、PC鋼より線間の摩擦抵抗の低減により、被
覆管内部における、PC鋼より線の円滑な伸縮が確保でき
る。In such a configuration, usually a cladding tube
14. The rust-preventive oil 18 such as grease is filled between the PC steel strands 16 to reduce the frictional resistance between the cladding and the PC steel strands, ensuring smooth expansion and contraction of the PC steel strands inside the cladding pipe. it can.
【００２１】なお、部分アンボンドPC鋼より線の成形方
法として、たとえば、被覆管の押出成形によりPC鋼より
線の全長を被覆し、不要部分の被覆管を後に剥離する押
出成形による方法、および、予め所定長に切断した被覆
管にPC鋼より線を差し込み、PC鋼より線の所定箇所を部
分的に被覆する差し込みによる方法等が、一般的に知ら
れている。As a method of forming a partially unbonded PC steel stranded wire, for example, a method of extruding a clad tube to cover the entire length of the PC steel stranded wire and exfoliating the unnecessary portion of the coated tube later, and A generally known method is to insert a PC steel stranded wire into a cladding tube cut in advance to a predetermined length and partially cover a predetermined portion of the PC steel stranded wire.
【００２２】しかし、部分アンボンドPC鋼より線12の構
成および成形方法等は公知であり、その構成、成形方法
自体はこの発明の趣旨でないため、詳細に説明しない。However, the configuration and the forming method of the partially unbonded PC steel strand 12 are known, and the configuration and the forming method itself are not the purpose of the present invention, and will not be described in detail.
【００２３】ここで、この発明の部分アンボンドPC鋼よ
り線の被覆管端末処理構造10においては、止水材20、被
覆手段22によって、被覆管端末の側方に止水加工が施さ
れている。Here, in the cladding end treatment structure 10 of the partially unbonded PC steel strand according to the present invention, the water-stopping material 20 and the coating means 22 apply a water-stopping process to the side of the cladding end. .
【００２４】図３に示すように、このような構成におい
ては、たとえば、芯ワイヤ16b の回り、および、隣接す
る側ワイヤ16a の間に、止水材20が隙間なく注入、充填
されている。止水材20として、たとえば、ゴム系止水材
が利用でき、止水材は、たとえば、170 〜190 ℃で溶融
されて注入、充填される。As shown in FIG. 3, in such a configuration, for example, the water blocking material 20 is injected and filled without gaps around the core wire 16b and between the adjacent side wires 16a. As the water-stopping material 20, for example, a rubber-based water-stopping material can be used, and the water-stopping material is melted at, for example, 170 to 190 ° C., and injected and filled.
【００２５】芯ワイヤ16b の回りへの止水材20の注入、
充填は、強制的に拡開した隣接する側ワイヤ16a の隙間
を介して行われる。Injection of the water-stopping material 20 around the core wire 16b,
The filling is performed through the gap between the adjacent side wires 16a that have been forcibly expanded.
【００２６】この発明の部分アンボンドPC鋼より線の被
覆管端末処理方法においては、図４に示すように、たと
えば、側ワイヤ16a 間への鋭利なくさび状の工具の差し
込みによって、側ワイヤ間を強制的に拡開している。く
さび状の工具として、たとえば、たがね23が利用でき
る。In the method for treating the cladding end of a partially unbonded PC stranded wire according to the present invention, as shown in FIG. 4, for example, a sharp wedge-shaped tool is inserted between the side wires 16a to cut the gap between the side wires. It is forcibly expanding. For example, a chisel 23 can be used as a wedge-shaped tool.
【００２７】ここで、このような、たがね23を利用する
側ワイヤ16a 間の拡開作業時においては、図４に示すよ
うに、通常、PC鋼より線16が所定の治具24によって支持
され、PC鋼より線の安定状態のもとで、側ワイヤ16a 間
の拡開作業が行われる。Here, during such an expanding operation between the side wires 16a utilizing the chisel 23, as shown in FIG. The spread operation between the side wires 16a is performed under the stable state of the supported PC steel strand.
【００２８】治具24は、たとえば、PC鋼より線16の外径
に応じた断面略半円形の溝26を有して形成され、溝への
嵌入によって、PC鋼より線が支持可能となっている。そ
して、治具24は、溝26に連続した段部28を中央部に有し
て形成され、段部に対応した位置における、任意の側ワ
イヤ16a 間へのたがね23の差し込みによって、芯ワイヤ
16b の露出状態まで、側ワイヤ間を拡開させる。The jig 24 is formed, for example, to have a groove 26 having a substantially semicircular cross section corresponding to the outer diameter of the PC steel stranded wire 16, and the PC steel stranded wire can be supported by fitting into the groove. ing. The jig 24 is formed so as to have a step portion 28 continuous with the groove 26 at the center, and the jig 24 is inserted into the space between the arbitrary side wires 16a at a position corresponding to the step portion, thereby forming a core. Wire
Spread between the side wires until the exposed state of 16b.
【００２９】なお、側ワイヤ16a 間の拡開作業時におい
て、たがね23は、通常、ハンマー（図示しない）等によ
って、PC鋼より線16の外径を貫通するまで打ち込まれ、
図５に示すように、たがねの１度の差し込み作業によっ
て、２本の側ワイヤ16a が分離されて、任意の側ワイヤ
間が拡開される。At the time of the expanding operation between the side wires 16a, the chisel 23 is usually driven by a hammer (not shown) until it penetrates the outer diameter of the PC steel strand 16,
As shown in FIG. 5, two insertions of the side wire 16a are separated by a single insertion operation of the chisel, and the space between arbitrary side wires is expanded.
【００３０】そして、たがね23の差し込みによって拡開
された側ワイヤ16a の隙間を介して、芯ワイヤ16b の回
りで5 〜10cm程度の範囲に止水材20が注入、充填され
る。The water-stopping material 20 is injected and filled in a range of about 5 to 10 cm around the core wire 16b through the gap between the side wires 16a expanded by inserting the chisel 23.
【００３１】止水材20の注入後、たがね23を側ワイヤ16
a 間から抜き取れば、側ワイヤの復帰力のもとで、PC鋼
より線16が初期状態に戻り、止水材が芯ワイヤ16b の回
りに封入される。After the water-stopping material 20 is injected, the chisel 23 is connected to the side wire 16.
When the wire is removed from the space a, the PC steel stranded wire 16 returns to the initial state under the restoring force of the side wire, and the waterproof material is sealed around the core wire 16b.
【００３２】このとき、たがね23での側ワイヤ16a の一
度の拡開作業においては、前述したように、２本程度の
側ワイヤの分離が限度となるため、通常、差し込み角度
を変えた複数箇所でたがねを差し込み、芯ワイヤ16b の
全周に、止水材20を確実に充填、封入する。At this time, in the one-time opening operation of the side wire 16a with the chisel 23, as described above, since the separation of about two side wires is a limit, the insertion angle is usually changed. At the plurality of places, a chisel is inserted, and the entire periphery of the core wire 16b is securely filled and sealed with the water-stopping material 20.
【００３３】そして、たがね23を抜き取り、PC鋼より線
16を初期状態に復帰させた後、止水材20を封入した当該
箇所のPC鋼より線の表面上の側ワイヤ16a 間にも、止水
材を十分に塗布して、側ワイヤ間の隙間を埋め、図３に
示すように、止水材を被覆するように、たとえば、被装
用テープ30によってテーピングが施される。[0033] Then, pull out the chisel 23, and stranded PC steel
After the 16 is returned to the initial state, a sufficient amount of the water-stopping material is applied between the side wires 16a on the surface of the PC steel stranded wire where the water-stopping material 20 is sealed, and the gap between the side wires is removed. Then, as shown in FIG. 3, taping is performed by, for example, a covering tape 30 so as to cover the waterproof material.
【００３４】被装用テープ30として、たとえば、布テー
プが利用でき、布テープは、被覆管14と同等の外径とな
るまで、止水材20を充填した幅（5 〜10cm）と同等の範
囲で、PC鋼より線16に巻き付けられる。As the covering tape 30, for example, a cloth tape can be used. The cloth tape has a width equivalent to the width (5 to 10 cm) filled with the waterproof material 20 until the outer diameter of the cloth tape is equivalent to that of the cladding tube 14. And wound around PC steel strand 16.
【００３５】そして、図１ないし図３に示すように、被
覆手段22によって、被覆管14、被装用テープ30が連続的
に被覆されて、被覆管端末が、止水加工のもとで処理さ
れる。Then, as shown in FIGS. 1 to 3, the covering tube 14 and the covering tape 30 are continuously covered by the covering means 22, and the end of the covering tube is treated under a water stopping process. You.
【００３６】被覆手段22として、たとえば、被装用テー
プ30と同様に、布テープが利用でき、布テープは、全長
10〜15cmの範囲で巻き付けられる。As the covering means 22, for example, a cloth tape can be used in the same manner as the covering tape 30.
It is wound in the range of 10-15cm.
【００３７】このような構成では、被覆管端末側方のPC
鋼より線の内部、外部のいずれにも、止水材20が充填さ
れ、テーピングによる当該箇所と被覆管端末との連続的
な被覆によって、被覆管端末の露出が防止されている。In such a configuration, the PC on the side of the cladding tube terminal
Both the inside and the outside of the steel strand are filled with the water-stopping material 20, and the covering of the cladding tube end is prevented from being exposed by continuous coating of the portion and the cladding tube end by taping.
【００３８】上記のように、この発明によれば、芯ワイ
ヤ16b の回りに止水材20が充填されるとともに、被覆管
14の端末、当該箇所間が連続的なテーピングによって被
覆されて、被覆管の内外間が、止水加工のもとで隔離さ
れている。つまり、コンクリートの凝固熱等による加熱
のもとで、被覆管14の内部に充填されたグリース18が溶
融されて側ワイヤ16a 、芯ワイヤ16b に沿って外方に流
出しようとしても、その流出は止水材20によって確実に
阻止される。As described above, according to the present invention, the waterproof material 20 is filled around the core wire 16b,
The 14 terminals and the corresponding portions are covered by continuous taping, and the inside and outside of the cladding tube are isolated under a water stop process. In other words, even if the grease 18 filled in the cladding tube 14 is melted under the heating by the heat of solidification of the concrete and tries to flow outward along the side wire 16a and the core wire 16b, the outflow does not occur. It is surely prevented by the waterproof material 20.
【００３９】そのため、グリース18が被覆管14の外方に
流出されることもなく、部分アンボンドPC鋼より線12の
ボンド部分における、グリースの流出に起因するコンク
リート、PC鋼より線16間の定着不良が確実に防止でき
る。As a result, the grease 18 does not flow out of the cladding tube 14 and the concrete and PC steel strands 16 are fixed at the bond portion of the partially unbonded PC steel strand 12 due to the outflow of grease. Defects can be reliably prevented.
【００４０】また、止水材20、テーピング等により、被
覆管14の内部への削孔水、地下水等の異物の侵入等が確
実に阻止できるため、被覆管内、つまり、アンボンド部
分における、PC鋼より線16の円滑な伸縮が十分に確保で
きる。Further, since the penetration of foreign matters such as drilling water and groundwater into the inside of the cladding tube 14 can be reliably prevented by the water-stopping material 20, taping, etc., the PC steel inside the cladding tube, that is, in the unbonded portion, can be prevented. Smooth expansion and contraction of the stranded wire 16 can be sufficiently ensured.
【００４１】そして、止水材20を充填、塗布した当該箇
所が、被装用テープ30でのテーピングによって保護され
るため、止水材の硬化を待つことなく、次の作業工程に
移行できる。そのため、作業の中断が避けられ、作業性
の向上がはかられる。Since the portion where the water-stopping material 20 is filled and applied is protected by taping with the tape 30 to be covered, the process can be shifted to the next operation step without waiting for the water-stopping material to harden. Therefore, interruption of the work can be avoided, and workability can be improved.
【００４２】なお、ここでは、鋭利な工具としてたがね
23を例示しているが、これに限定されず、マイナスドラ
イバー等を利用してもよい。In this case, it is a sharp tool.
Although 23 is illustrated, the invention is not limited to this, and a minus driver or the like may be used.
【００４３】ここで、実施例の方法においては、たがね
23の差し込みによって、隣接する側ワイヤ16a 間を拡開
しているが、止水材20を注入可能な隙間を側ワイヤ間に
形成すれば足りるため、これに限定されない。Here, in the method of the embodiment,
Although the space between the adjacent side wires 16a is expanded by the insertion of the wire 23, the gap is not limited to this, because it is sufficient to form a gap between the side wires where the water stopping material 20 can be injected.
【００４４】たとえば、図６に示すような、治具32に設
けられた固定の把持具（固定具）34と、固定具から所定
間隔離反して配設された可動の把持具（可動支持具）36
とを利用し、固定具に対する可動支持具の回動により、
隣接するPC鋼より線の側ワイヤ16a 間を拡開する方法と
してもよい。For example, as shown in FIG. 6, a fixed gripping tool (fixing tool) 34 provided on a jig 32 and a movable gripping tool (movable supporting tool) disposed at a predetermined distance from the fixing tool. ) 36
By using the movable support with respect to the fixture,
A method of expanding between adjacent PC steel stranded wires 16a may be used.
【００４５】治具の固定具（把持具）34は、たとえば、
操作ハンドル38の回転操作に伴う、ナット（図示しな
い）に対するリードスクリュー40の螺進、螺退によって
把持片42を昇降させる万力状に構成され、把持片と台座
44との間で、PC鋼より線16が把持、固定可能となってい
る。The jig fixture (gripping tool) 34 is, for example,
The rotation of the operation handle 38 causes the lead screw 40 to advance and retreat with respect to a nut (not shown), so that the grip piece 42 is raised and lowered by a vice.
Between PC and 44, the PC steel strand 16 can be gripped and fixed.
【００４６】また、治具32は、部分アンボンドPC鋼より
線12を支持可能な一対の支持片46、47 を有して形成さ
れ、安定した状態での部分アンボンドPC鋼より線の載置
が可能となっている。The jig 32 is formed with a pair of support pieces 46 and 47 capable of supporting the partially unbonded PC stranded wire 12, so that the partially unbonded PC stranded wire can be stably placed. It is possible.
【００４７】そして、図６を見るとわかるように、可動
支持具（把持具）36として、たとえば、ハンドタイプの
パイプレンチが利用でき、固定具34から30cm程度離反し
た位置において、PC鋼より線16がパイプレンチによって
把持される。As can be seen from FIG. 6, for example, a hand-type pipe wrench can be used as the movable support (grip) 36, and at a position separated from the fixture 34 by about 30 cm, a PC steel stranded wire is used. 16 is gripped by a pipe wrench.
【００４８】このような方法において、パイプレンチ
（把持具）36を側ワイヤ16a の撚り方向とは逆の方向
に、固定具34に対して回すと、図７に示すように、側ワ
イヤ16aの撚りが部分的に緩められて、隣接する側ワイ
ヤ間が拡開される。そして、側ワイヤ16a 間に形成され
た隙間を介して、止水材20を芯ワイヤ16b の回りに注
入、充填し、止水材の充填後、パイプレンチ36での回動
操作力を解除すれば、側ワイヤの復帰力のもとで、PC鋼
より線16が初期状態に復帰して、止水材が芯ワイヤの回
りに封入される。In this method, when the pipe wrench (gripping tool) 36 is turned with respect to the fixing tool 34 in a direction opposite to the twisting direction of the side wire 16a, as shown in FIG. The twist is partially loosened and the space between adjacent side wires is widened. Then, the water-stopping material 20 is injected and filled around the core wire 16b through a gap formed between the side wires 16a, and after the water-stopping material is filled, the turning operation force of the pipe wrench 36 is released. For example, under the return force of the side wire, the PC steel stranded wire 16 returns to the initial state, and the waterproof material is sealed around the core wire.
【００４９】この後、前記実施例と同様に、被装用テー
プ30で当該箇所のテーピング、および、当該箇所、被覆
管14の端末間の連続的なテーピングを行えば、止水加工
の施された、図１に示すこの発明のアンボンドPC鋼より
線の被覆管端末処理構造10が、十分に得られる。After that, as in the above-described embodiment, taping of the relevant portion with the covering tape 30 and continuous taping between the relevant portion and the end of the cladding tube 14 are performed, so that the waterproofing process is performed. 1, an unbonded PC steel strand cladding end treatment structure 10 according to the present invention shown in FIG. 1 is sufficiently obtained.
【００５０】そして、この方法においては、PC鋼より線
の側ワイヤ16a の撚りを緩めるため、全周の側ワイヤ間
に隙間が形成される。そのため、一度の拡開作業のもと
で、芯ワイヤ16b の全周への止水材20の充填が行え、作
業性が向上される。In this method, a gap is formed between the side wires of the entire circumference in order to loosen the twist of the side wire 16a of the PC stranded wire. Therefore, the entire circumference of the core wire 16b can be filled with the water-stopping material 20 under a single expanding operation, thereby improving workability.
【００５１】なお、ここでは、可動支持具36としてパイ
プレンチを例示しているが、固定具34に対して回動可能
な工具であれば足りるため、これに限定されない。Here, a pipe wrench is exemplified as the movable support member 36, but a tool that can rotate with respect to the fixture 34 is sufficient, and the present invention is not limited to this.
【００５２】ここで、実施例においては、ゴム系止水材
を止水材20として例示しているが、溶融されたグリース
の流出、削孔水の流入等を阻止可能であれば足りるた
め、これに限定されず、たとえば、樹脂系の接着剤等を
利用してもよい。Here, in the embodiment, the rubber-based water-blocking material is exemplified as the water-blocking material 20, but it is sufficient if it can prevent the outflow of the molten grease and the inflow of the drilling water. The invention is not limited to this, and for example, a resin-based adhesive or the like may be used.
【００５３】また、被装用テープ30、被覆手段22とし
て、布テープが利用されているが、これに限定されず、
たとえば、ビニールテープ等を利用してもよい。しかし
ながら、布テープは、ビニールテープに比較してゴム系
止水材の安定性に優れているため、被装用テープ30、被
覆手段22に布テープを利用することによって、作業性お
よび作業後における止水効果の確実性が向上される。Although a cloth tape is used as the covering tape 30 and the covering means 22, the present invention is not limited to this.
For example, a vinyl tape or the like may be used. However, the cloth tape is more excellent in stability of the rubber waterproofing material than the vinyl tape. Therefore, by using the cloth tape for the covering tape 30 and the covering means 22, the workability and the post-work stoppage can be improved. The certainty of the water effect is improved.
【００５４】更に、被覆手段22は、止水材20の充填箇所
と被覆管14の端末とを連続的に被覆可能であれば足りる
ため、テーピングに限定されず、たとえば、熱収縮チュ
ーブ50を被覆手段として利用してもよい。Further, the covering means 22 is not limited to taping, because it is sufficient if the filling portion of the water-stopping material 20 and the end of the covering tube 14 can be covered continuously. It may be used as a means.
【００５５】熱収縮チューブ50は、止水材20の充填箇
所、つまりは被装テープ30の巻装箇所と被覆管14の端末
とを連続的に被覆可能な長さ、たとえば、20cm程度に形
成され、図８に示すように、被覆管に予め遊挿されてい
る。そして、被装用テープ30での当該箇所のテーピング
後、熱収縮チューブ50をずらして被装用テープ30、被覆
管14の端末に架設させ、加熱のもとで熱収縮チューブを
収縮させて、図９のように、被装用テープ、被覆管端末
間が連続的に被覆される。The heat-shrinkable tube 50 is formed to have a length, for example, about 20 cm, capable of continuously covering the portion filled with the water-stopping material 20, that is, the portion where the covering tape 30 is wound and the end of the covering tube 14. Then, as shown in FIG. 8, it is loosely inserted in the cladding tube in advance. Then, after taping of the portion with the covering tape 30, the heat-shrinkable tube 50 is shifted so as to bridge the end of the covering tape 30 and the covering tube 14, and the heat-shrinkable tube is shrunk under heating, and FIG. As described above, the space between the covering tape and the end of the cladding tube is continuously covered.
【００５６】このような熱収縮チューブ50を利用した構
成においても、図９に示すように、被覆管14の端末、被
装用テープ30間が、連続して被覆されるため、テーピン
グによって被覆する前記実施例と同様の効果が確実に得
られる。In such a configuration using the heat-shrinkable tube 50, as shown in FIG. 9, the end of the coating tube 14 and the space between the covering tapes 30 are continuously coated. The same effect as that of the embodiment can be reliably obtained.
【００５７】そして、熱収縮チューブ50を加熱すれば足
りるため、被覆作業時における作業性が、一層向上され
る。Since it is sufficient to heat the heat-shrinkable tube 50, the workability during the coating operation is further improved.
【００５８】上述した実施例は、この発明を説明するた
めのものであり、この発明を何等限定するものでなく、
この発明の技術範囲内で変形、改造等の施されたものも
全てこの発明に包含されることはいうまでもない。The embodiments described above are for explaining the present invention, and do not limit the present invention in any way.
It goes without saying that all modifications and alterations within the technical scope of the present invention are included in the present invention.
【００５９】[0059]
【発明の効果】上記のように、この発明に係る部分アン
ボンドPC鋼より線の被覆管端末処理方法によれば、止水
材、被覆手段による止水加工によって、被覆管内部と外
部とが確実に隔離されている。そのため、グリースが被
覆管の外方に流出することもなく、部分アンボンドPC鋼
より線のボンド部分におけるコンクリート、PC鋼より線
間の定着不良が確実に防止できる。As described above, according to the method for treating the end of a partially unbonded PC stranded steel cladding tube according to the present invention, the inside and outside of the cladding tube can be reliably formed by the water stopping material and the coating means. Isolated. Therefore, the grease does not flow out of the cladding tube, and the fixing failure between the concrete and PC steel strands at the bond portion of the partially unbonded PC steel strand can be reliably prevented.
【００６０】また、止水材、被覆手段により、被覆管内
部へのコンクリート材、削孔水等の異物の侵入が確実に
阻止できるため、被覆管内、つまり、アンボンド部分に
おける、PC鋼より線の円滑な伸縮が十分に確保できる。Further, since the intrusion of foreign matter such as concrete material and drilling water into the inside of the cladding tube can be reliably prevented by the water-stopping material and the covering means, the PC steel stranded wire in the cladding tube, that is, in the unbonded portion, can be prevented. Smooth expansion and contraction can be sufficiently secured.
【００６１】たがねなどの工具を利用する方法、一対の
把持具で側ワイヤの撚りを緩める方法のいずれにおいて
も、側ワイヤの拡開が十分に得られるため、側ワイヤ間
の隙間を介した止水材の注入、充填が確実、容易に行え
る。In both the method using a tool such as a chisel and the method of loosening the twist of the side wire with a pair of gripping tools, the side wire can be sufficiently widened. Injection and filling of the waterproof material can be performed reliably and easily.
【００６２】ここで、一対の把持具で側ワイヤの撚りを
緩める方法によれば、一度の拡開作業のもとで、全周の
側ワイヤが全体的に拡開されるため、止水材の充填作業
が複数回にわたることもなく、作業性が向上される。Here, according to the method of loosening the twist of the side wire with a pair of gripping tools, the side wire of the entire circumference is expanded as a whole under a single expanding operation. The workability is improved without the filling work of being performed a plurality of times.
【００６３】また、それぞれの方法に対応した治具で部
分アンボンドPC鋼より線を支持、固定すれば、安定した
状態での作業が確実に得られるため、作業性が確実に向
上される。Further, if the partially unbonded PC steel strand is supported and fixed by a jig corresponding to each method, work in a stable state can be reliably obtained, and workability is surely improved.
【００６４】そして、止水材を充填した箇所の表面上の
側ワイヤ間に止水材を更に塗布し、テーピングによって
保護すれば、側ワイヤの表面上の隙間が確実に埋められ
るため、この点からも、削孔水の流入等が十分に防止で
きる。If the waterproof material is further applied between the side wires on the surface of the portion filled with the waterproof material and protected by taping, the gap on the surface of the side wire is securely filled. Therefore, the inflow of drilling water can be sufficiently prevented.
【００６５】また、表面上の止水材をテーピングによっ
て保護するため、止水材の硬化を待つことなく、次の作
業工程に移行できるため、作業の中断が避けられ、作業
性の向上がはかられる。Further, since the water-stopping material on the surface is protected by taping, it is possible to shift to the next operation step without waiting for the water-stopping material to harden. Get off.
【００６６】更に、被覆手段を布テープとすれば、布テ
ープは止水材の安定性に優れているため、作業性および
作業後の止水効果の確実性が向上される。Furthermore, if the covering means is a cloth tape, the cloth tape is excellent in the stability of the water-stopping material, so that the workability and the reliability of the water-stopping effect after the work are improved.
【００６７】また、被覆手段を熱収縮チューブとすれ
ば、熱収縮チューブの加熱作業によって止水材充填の当
該箇所、被覆管端末間が連続的に被覆できるため、作業
性が一層向上される。If the covering means is a heat-shrinkable tube, the work of heating the heat-shrinkable tube can continuously cover the portion where the water-stopping material is filled, and between the ends of the covering tube, so that the workability is further improved.
【図１】この発明の一実施例に係る部分アンボンドPC鋼
より線の被覆管端末処理構造の概略正面図である。FIG. 1 is a schematic front view of a cladding end treatment structure of a partially unbonded PC steel strand according to an embodiment of the present invention.
【図２】図１の線Ａ−Ａに沿った断面図である。FIG. 2 is a sectional view taken along line AA of FIG. 1;
【図３】図１の線Ｂ−Ｂに沿った断面図である。FIG. 3 is a sectional view taken along line BB of FIG. 1;
【図４】この発明の部分アンボンドPC鋼より線の被覆管
端末処理方法の一例における、治具に載置された部分ア
ンボンドPC鋼より線の概略斜視図である。FIG. 4 is a schematic perspective view of a partially unbonded PC steel stranded wire placed on a jig in an example of the method for treating a cladding tube of a partially unbonded PC steel stranded wire according to the present invention.
【図５】この発明の部分アンボンドPC鋼より線の被覆管
端末処理方法の一例における、側ワイヤの拡開状態を示
す、PC鋼より線の縦断面図である。FIG. 5 is a longitudinal sectional view of a PC steel stranded wire showing an expanded state of a side wire in an example of the method for treating a partially unbonded PC steel stranded wire cladding tube of the present invention.
【図６】別の方法における、治具に固定された部分アン
ボンドPC鋼より線の概略斜視図である。FIG. 6 is a schematic perspective view of a partially unbonded PC steel strand fixed to a jig in another method.
【図７】別の方法における、側ワイヤの拡開状態を示
す、PC鋼より線の概略正面図である。FIG. 7 is a schematic front view of a PC steel strand showing an expanded state of a side wire in another method.
【図８】別の実施例に係る被覆手段での被覆前におけ
る、部分アンボンドPC鋼より線の概略斜視図である。FIG. 8 is a schematic perspective view of a partially unbonded PC steel strand before coating with a coating means according to another embodiment.
【図９】別の実施例に係る被覆手段での被覆後におけ
る、部分アンボンドPC鋼より線の被覆管端末処理構造の
概略正面図である。FIG. 9 is a schematic front view of a cladding tube end treatment structure of a partially unbonded PC steel strand after coating with a coating means according to another embodiment.
10 部分アンボンドPC鋼より線の被覆管端末処理構造 12 部分アンボンドPC鋼より線 14 被覆管 16 PC鋼より線 16a 側ワイヤ 16b 芯ワイヤ 18 グリース（防錆油） 20 止水材 22 被覆手段（布テープ） 23 たがね（工具） 24 治具 26 溝 28 段部 30 被装用テープ（布テープ） 32 治具 34 把持具（固定具） 36 把持具（可動支持具） 50 熱収縮チューブ（被覆手段） 10 Partially unbonded PC stranded wire cladding tube termination structure 12 Partially unbonded PC stranded wire 14 Clad tube 16 PC steel stranded wire 16a Side wire 16b Core wire 18 Grease (rust-proof oil) 20 Waterproof material 22 Coating means (cloth) Tape) 23 Jig (tool) 24 Jig 26 Groove 28 Step 30 Tape for covering (cloth tape) 32 Jig 34 Holder (fixer) 36 Holder (movable support) 50 Heat shrink tube (covering means) )
Claims (10)
部分を形成する被覆管端末の側方において、隣接する側
ワイヤ間を外力のもとで強制的に拡開して、側ワイヤの
隙間から、少なくとも芯ワイヤの回りに止水材を注入、
充填し、PC鋼より線の止水材の充填された当該箇所の外
周面と被覆管とを被覆手段で連続的に被覆して、被覆管
の端末処理を行う部分アンボンドPC鋼より線の被覆管端
末処理方法。1. On the side of a cladding end forming an unbonded part of a partially unbonded PC stranded wire, a force between the adjacent side wires is forcibly expanded under an external force, and a gap between the side wires is Inject a waterproof material at least around the core wire,
Filled, the outer peripheral surface of the place filled with the waterproof material of the PC steel stranded wire and the cladding tube are continuously coated with the coating means, and the terminal treatment of the cladding tube is performed. Tube terminal processing method.
差し込んで側ワイヤ間を拡開し、側ワイヤ間の隙間か
ら、芯ワイヤの回りに止水材を注入、充填する請求項１
記載の部分アンボンドPC鋼より線の被覆管端末処理方
法。2. The method according to claim 1, wherein a tool is inserted between the adjacent twisted side wires to widen the gap between the side wires, and a waterproof material is injected and filled around the core wire from a gap between the side wires. 1
A method for treating a cladding tube of a partially unbonded PC steel strand according to the description.
の治具の溝に、PC鋼より線を嵌入、支持させ、溝に連続
した治具の段部に対応した位置における、側ワイヤを介
した工具の貫通によって、隣接した側ワイヤ間を拡開す
る請求項２記載の部分アンボンドPC鋼より線の被覆管端
末処理方法。3. A PC steel stranded wire is fitted into and supported by a groove of a jig having a substantially semicircular cross section corresponding to the outer diameter of the PC steel stranded wire, and is positioned at a position corresponding to a step portion of the jig continuous with the groove. 3. The method according to claim 2, wherein the gap between adjacent side wires is expanded by penetrating the tool through the side wires.
具間に、被覆管端末のPC鋼より線が架設、固定され、一
対の把持具の少なくとも一方をPC鋼より線の側ワイヤの
撚り方向の逆方向に回して、側ワイヤの撚りを部分的に
緩めて側ワイヤ間を拡開し、側ワイヤ間の隙間から、芯
ワイヤの回りに止水材を注入、充填する請求項１記載の
部分アンボンドPC鋼より線の被覆管端末処理方法。4. A PC steel stranded wire of the cladding tube terminal is erected and fixed between a pair of gripping tools disposed opposite to each other by a predetermined distance, and at least one of the pair of gripping tools is a side wire of the PC steel stranded wire. The twist in the direction opposite to the twisting direction of the side wire, partially twisting the side wires to partially loosen and widen the gap between the side wires, and injecting and filling the water-stopping material around the core wire from the gap between the side wires. 2. A method for treating a cladding end of a partially unbonded PC steel strand according to 1.
の把持具とするとともに、固定具に対する可動支持具を
他方の把持具とし、固定具に対する可動支持具の回動に
より、側ワイヤの撚りを部分的に緩める請求項４記載の
部分アンボンドPC鋼撚り線の被覆管端末処理方法。5. A vice-shaped fixing tool provided on the jig is used as one gripping tool, and a movable support for the fixing tool is used as the other gripping tool. 5. The method according to claim 4, wherein the twist of the side wire is partially relaxed.
ヤ間に、止水材を更に塗布し、表面上の止水材をテーピ
ングによって保護するとともに、当該箇所と被覆管端末
とを被覆手段によって連続的に被覆する請求項１ないし
５のいずれか記載の部分アンボンドPC鋼より線の被覆管
端末処理方法。6. A waterproof material is further applied between the side wires on the surface of the location filled with the waterproof material, the waterproof material on the surface is protected by taping, and the location and the end of the cladding tube are connected. 6. The method according to claim 1, wherein the coating is continuously performed by the coating means.
て形成したPC鋼より線を所定長の被覆管で部分的に被覆
した部分アンボンドPC鋼より線の被覆管端末処理構造に
おいて、被覆管端末の側方で、少なくともPC鋼より線の
芯ワイヤの回りに止水材を充填するとともに、止水材の
充填箇所に対応するPC鋼より線の外周面と被覆管とを被
覆手段で連続的に被覆して、止水加工を施したことを特
徴とする部分アンボンドPC鋼より線の被覆管端末処理構
造。7. A partially unbonded PC stranded wire cladding treatment structure in which a PC stranded wire formed by twisting several side wires around a core wire is partially covered with a cladding tube of a predetermined length. At the side of the cladding tube end, at least around the core wire of the PC steel stranded wire is filled with the waterproof material, and the outer peripheral surface of the PC steel stranded wire and the cladding tube corresponding to the filled portion of the waterproof material are covered A partially unbonded PC stranded wire cladding tube treatment structure characterized by being continuously coated by means and subjected to a water stopping process.
イヤ間に、止水材を更に塗布するとともに、止水材をテ
ーピングによって保護した請求項７記載の部分アンボン
ドPC鋼より線の被覆管端末処理構造。8. The partially unbonded PC steel stranded wire according to claim 7, wherein the waterproof material is further applied between the side wires on the surface of the portion filled with the waterproof material, and the waterproof material is protected by taping. Clad tube termination structure.
被覆管端末間が、連続したテーピングによって被覆され
た請求項７または８記載の部分アンボンドPC鋼より線の
被覆管端末処理構造。9. The covering means is a cloth tape;
9. The cladding end treatment structure of a partially unbonded PC steel strand according to claim 7, wherein a portion between the cladding ends is coated by continuous taping.
に架設された状態で配置、熱収縮された熱収縮チューブ
である請求項７または８記載の部分アンボンドPC鋼より
線の被覆管端末処理構造。10. The partially unbonded PC steel stranded cladding tube end according to claim 7 or 8, wherein the coating means is a heat-shrinkable tube arranged and heat-shrinked in such a state as to extend between the ends of the cladding tube. Processing structure.