JP2715303B2 - Magenta toner for full color image formation - Google Patents
Magenta toner for full color image formationInfo
- Publication number
- JP2715303B2 JP2715303B2 JP63049497A JP4949788A JP2715303B2 JP 2715303 B2 JP2715303 B2 JP 2715303B2 JP 63049497 A JP63049497 A JP 63049497A JP 4949788 A JP4949788 A JP 4949788A JP 2715303 B2 JP2715303 B2 JP 2715303B2
- Authority
- JP
- Japan
- Prior art keywords
- magenta toner
- color
- dye
- color image
- full
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 [産業上の利用分野] 本発明は、フルカラー電子写真法に用いられるカラー
トナーに関し、特にシリコンゴムローラー、テフロンコ
ントローラーを有する加熱ローラー定着器を用いるフル
カラー複写機を使用するフルカラー画像形成用に適した
マゼンタトナーに関する。The present invention relates to a color toner used for full-color electrophotography, and particularly to a full-color copying machine using a heat roller fixing device having a silicone rubber roller and a Teflon controller. The present invention relates to a magenta toner suitable for full-color image formation.
[従来の技術] カラー電子写真用マゼンタトナーの着色材に求められ
る要求品質として、1)分光反射特性(色特性)が優れ
る、つまり鮮明なマゼンタ色を有すること、2)樹脂に
対する分散性が良好で高着色力を有すること、3)光に
対する安定性に優れること、つまりコピーの耐光性が良
好であること、4)フルカラー複写機の要求する機能に
対してマッチングし、著しい副作用を与えないこと、例
えば定着ローラー表面への付着、染色性などがある。[Prior Art] The required quality required of a coloring material of a magenta toner for color electrophotography is 1) excellent spectral reflection characteristics (color characteristics), that is, having a clear magenta color, and 2) good dispersibility in a resin. 3) Excellent stability to light, that is, good light fastness of the copy, 4) Matching the functions required of the full-color copier, and not giving significant side effects. For example, there are adhesion to the surface of the fixing roller and dyeing properties.
従来のカラー電子写真用マゼンタ着色剤として、キナ
クリドン系顔料、チオインジゴ系顔料、キサンテン系染
顔料、アントラキノン系染料、アゾ系染顔料などがあ
る。Conventional magenta colorants for color electrophotography include quinacridone pigments, thioindigo pigments, xanthene dyes, anthraquinone dyes, and azo dyes.
例えば、特公昭49−46951号公報には、2,9−ジメチル
キナクリドン顔料の記載が、特開昭55−26574号公報に
はチオインジゴ系顔料に関して、特開昭59−57256号公
報ではキサンテン系染料に関する記載がある。また特公
昭55−42383号公報にはアントラキノン系染料について
記述されている。さらには、特公昭53−47147号公報で
は、本出願人は、キナクリドン系またはローダミン系の
着色剤を用い、適当な結着樹脂との組合せにおけるマゼ
ンタトナーの提案を行なってきた。しかし、いずれの着
色剤も1)〜4)の特性を全て満足する着色剤ではな
く、いずれも一長一短の品質を有している。そのため、
マゼンタ用着色剤として、単独の染顔料に頼るのは、非
常に難しく、各着色剤の短所を補うべく、2種以上の着
色剤を併用するのが現実的である。For example, JP-B-49-46951 describes 2,9-dimethylquinacridone pigments, JP-A-55-26574 relates to thioindigo pigments, and JP-A-59-57256 discloses xanthene dyes. There is a description about. JP-B-55-42383 describes an anthraquinone dye. Furthermore, in Japanese Patent Publication No. 53-47147, the present applicant has proposed a magenta toner in combination with an appropriate binder resin using a quinacridone-based or rhodamine-based colorant. However, none of the colorants satisfies all of the characteristics 1) to 4), and each has a strength and a disadvantage. for that reason,
It is very difficult to rely on a single dye or pigment as a magenta colorant, and it is practical to use two or more colorants in combination to compensate for the disadvantages of each colorant.
例えば、本出願人等は特開昭57−130044号公報、及び
特開昭57−130046号公報に開示する如く、2種の油溶性
染料を用いたマゼンタトナーを提案した。このマゼンタ
トナーは、色調は、鮮やかであり、彩度は優れている
が、反面加熱ローラー定着装置に用いるシリコンゴムを
汚染する成分が一方の染料に含まれているため、連続複
写により、徐々に定着シリコンローラーを染着し最終的
には、トナーが加熱ローラーに融着する、所謂オフセッ
ト現象を惹起することになる。またこれらの油溶性染料
の組合せは、トナーの帯電を高めるよりは、低下せしめ
る方向に効果がある。そのため、低温低湿下のチャージ
upを十分に防止する事は可能であり、好ましい画像濃度
を保証しうる。けれども、逆に高温高湿下における帯電
不足によるトナー飛散、これによる機内汚染、また低帯
電トナーによりカブリを生じ画像汚れを生じやすい。For example, the present applicants have proposed a magenta toner using two oil-soluble dyes as disclosed in JP-A-57-130044 and JP-A-57-130046. This magenta toner has a vivid color tone and excellent saturation, but on the other hand, one of the dyes contains a component that contaminates the silicone rubber used in the heating roller fixing device, so that it is gradually produced by continuous copying. The fixing silicon roller is dyed, and finally, a so-called offset phenomenon in which the toner is fused to the heating roller is caused. Also, the combination of these oil-soluble dyes is effective in reducing the toner charge rather than increasing it. Therefore, charge under low temperature and low humidity
Up can be sufficiently prevented, and a preferable image density can be guaranteed. However, conversely, the toner scatters due to insufficient charging under high temperature and high humidity, thereby contaminating the inside of the apparatus, and fogging due to the low-charged toner to easily cause image contamination.
[発明が解決しようとする問題点] しかるに、本発明の目的は上述の如き欠点を解決した
フルカラー画像形成用マゼンタトナーを提供するもので
ある。[Problems to be Solved by the Invention] However, an object of the present invention is to provide a magenta toner for forming a full-color image which has solved the above-mentioned disadvantages.
すなち本発明の目的は、鮮明色が得られ、着色力が大
きく、かつ耐光性に優れたフルカラー画像形成用マゼン
タトナーを提供するものである。That is, an object of the present invention is to provide a magenta toner for forming a full-color image, which can provide a clear color, has a large coloring power, and is excellent in light resistance.
さらに別の目的は、定着時、シリコンゴムローラー等
を染色劣化させないフルカラー画像形成用マゼンタトナ
ーを提供するものである。Still another object is to provide a magenta toner for full-color image formation that does not deteriorate the dyeing of a silicone rubber roller or the like during fixing.
また別の目的は、環境安定性に優れた帯電特性を有す
るフルカラー画像形成用マゼンタトナーを提供するもの
である。Another object of the present invention is to provide a magenta toner for forming a full-color image having a charging characteristic having excellent environmental stability.
また別の目的は、繰り返し複写によってもキャリアへ
のスペント化しにくいフルカラー画像形成用マゼンタト
ナーを提供するものである。Another object of the present invention is to provide a magenta toner for forming a full-color image which is less likely to be spent on a carrier even by repeated copying.
[問題点を解決するための手段および作用] 具体的には、本発明は、少なくとも、結着樹脂と、キ
ナクリドン系有機顔料及びキサンテン系染料と、負荷電
性制御剤としてアントラキノン系マゼンタ染料又はアル
キルサリチル酸の金属キレートとを含有するフルカラー
画像形成用マゼンタトナーであり、キナクリドン系有機
顔料及びキサンテン系染料を合わせた添加量が結着樹脂
100重量部に対して2〜20重量部であり、キナクリドン
系有機顔料とキサンテン系染料との添加比率が100:3〜1
00:20であることを特徴とするフルカラー画像形成用負
荷電性マゼンタトナーに関する。[Means and Actions for Solving the Problems] Specifically, the present invention provides at least a binder resin, a quinacridone-based organic pigment and a xanthene-based dye, and an anthraquinone-based magenta dye or alkyl as a negative charge control agent. A magenta toner for forming a full-color image containing a metal chelate of salicylic acid, wherein a combined amount of a quinacridone-based organic pigment and a xanthene-based dye is a binder resin.
2 to 20 parts by weight with respect to 100 parts by weight, the addition ratio of the quinacridone-based organic pigment and the xanthene-based dye is 100: 3 to 1
00:20, which relates to a negatively charged magenta toner for full-color image formation.
キナクリドン系有機顔料はやや赤味を有する耐光性及
び帯電安定性に優れた高級顔料であるが、単独添加で
は、マゼンタ色としては十分な性能を有していない。す
なわち、色相に関して理想のマゼンタ色よりも青味部分
の反射が少なく、赤味によっている。鮮明性に関しても
彩度が劣り、鮮やかさが不十分であるなどの短所を有す
るため、単独使用では色再現性に関して、品質が不十分
である。しかし他方トナーとして用いた場合、繰り返し
複写によるキャリア汚染の少なさについては好ましい特
性を有している。The quinacridone-based organic pigment is a high-grade pigment having a slightly reddish color and excellent in light resistance and charge stability, but does not have sufficient performance as a magenta color when added alone. That is, with respect to the hue, the reflection in the bluish portion is less than the ideal magenta color, and the hue is reddish. It also has disadvantages such as poor chroma and inadequate vividness with respect to sharpness. Therefore, when used alone, the quality of color reproducibility is insufficient. However, when it is used as a toner, it has preferable characteristics in that carrier contamination due to repeated copying is small.
一方キサンテン系染料とは所謂ローダミン系染料のこ
とであり、蛍光を発し、鮮明な青味系ピンク色を呈する
着色剤である。この染料も単独使用では色味的にはマゼ
ンタ色として使用付加であるが、鮮明色が得られる、着
色力が大きい等の特徴を有している。しかし耐光性が劣
り、短時間で退色する欠点を有するため、添加量を多く
することができない。最近のフルカラーコピーは種々の
用途に用いられ、耐光性は極めて重要な項目であるた
め、ローダミン系染料のこの特徴は十分考慮しなければ
ならない。On the other hand, the xanthene-based dye is a so-called rhodamine-based dye, and is a colorant that emits fluorescence and exhibits a clear blueish pink color. This dye is also used as a magenta color when used alone, but has features such as obtaining a clear color and having a large coloring power. However, it has poor light resistance and has a disadvantage of fading in a short time, so that the amount of addition cannot be increased. This feature of rhodamine-based dyes must be fully considered since recent full-color copies are used for various applications and light fastness is a very important item.
すなわち、本発明者等はキナクリドン系顔料の欠点で
ある色相、鮮明さを補うべく、色相鮮明性に優れたキサ
ンテン系染料を併用し、色相、彩度、耐光性及び帯電性
や繰り返し複写によっても劣化しない優れたマゼンタト
ナーを提供するものである。本発明の着色剤添加量は総
着色剤量で樹脂100重量部に対して、2〜20重量部であ
り、好ましくは3〜15重量部である。またキナクリドン
系顔料とローダミン系染料の添加比率は、キナクリドン
顔料/ローダミン系染料=100/3〜100/20、好ましくは1
00/3〜90/5.1である。That is, the present inventors used a xanthene dye having excellent hue clarity in combination with a hue, which is a defect of the quinacridone pigment, and a sharpness, to compensate for the hue, chroma, light fastness and chargeability and repeated copying. An object of the present invention is to provide an excellent magenta toner that does not deteriorate. The amount of the colorant added in the present invention is 2 to 20 parts by weight, preferably 3 to 15 parts by weight, based on 100 parts by weight of the total colorant. The addition ratio of the quinacridone pigment and the rhodamine dye is such that the quinacridone pigment / rhodamine dye = 100/3 to 100/20, preferably 1
00/3 to 90 / 5.1.
ローダミン系染料の比率を100/20以上に増すと、耐光
性、ローラー染色性が悪化し、100/3以下に減らすと、
色相、鮮明さが悪くなる。When the ratio of the rhodamine-based dye is increased to 100/20 or more, light resistance and roller dyeability deteriorate, and when the ratio is reduced to 100/3 or less,
Hue and sharpness deteriorate.
キナクリドン系有機顔料の代表例としては、 などがある。中でも5.C.I.Pigment Red 122は特にマゼ
ンタ用着色剤として適している。Representative examples of quinacridone organic pigments include: and so on. Among them, 5. CI Pigment Red 122 is particularly suitable as a colorant for magenta.
また、キサンテン系染料の代表例としては、 が挙げられる。Also, as typical examples of xanthene dyes, Is mentioned.
6〜8はいずれも鮮明な青味系ピンク色を有してい
る。Each of Nos. 6 to 8 has a clear bluish pink color.
6,7は塩基性染料であるため、若干の吸湿性があり、
また樹脂との相溶性を考慮すると、本発明においては、
油溶性であり、樹脂との相溶性に優れ、着色力が大きい
C.I.Solvent Red 49.が特に適している。Because 6,7 is a basic dye, it has some hygroscopicity,
In consideration of the compatibility with the resin, in the present invention,
Oil-soluble, excellent compatibility with resin, high coloring power
CISolvent Red 49. is particularly suitable.
本発明トナーに適用する結着樹脂としては、公知のも
のがすべて使用可能であるが、例えばポリスチレン、ポ
リp−クロルスチレン、ポリビニルトルエンなどのスチ
レン及びその置換体の単重合体、スチレン−p−クロル
スチレン共重合体、スチレン−プロピレン共重合体、ス
チレン−ビニルトルエン共重合体、スチレン−ビニルナ
フタリン共重合体、スチレン−アクリル酸メチル共重合
体、スチレン−アクリル酸エチル共重合体、スチレン−
アクリル酸ブチル共重合体、スチレン−アクリル酸オク
チル共重合体、スチレン−メタクリル酸メチル共重合
体、スチレン−メタクリル酸エチル共重合体、スチレン
−メタクリル酸ブチル共重合体、スチレン−α−クロル
メタクリル酸メチル共重合体、スチレン−アクリロニト
リル共重合体、スチレン−ビニルメチルエーテル共重合
体、スチレン−ビニルエチルエーテル共重合体、スチレ
ン−ビニルメチルケトン共重合体、スチレン−ブタジエ
ン共重合体、スイレン−イソプレン共重合体、スチレン
−アクリロニトリル−インデン共重合体、スチレン−マ
レイン酸共重合体、スチレン−マレイン酸エステル共重
合体などのスチレン系共重合体、ポリメチルメタクリレ
ート、ポリブチルメタクリレート、ポリ塩化ビニル、ポ
リ酢酸ビニル、ポリエチレン、ポリプロピレン、ポリエ
ステル、ポリウレタン、ポリアミド、エポキシ樹脂、ポ
リビニルブチラール、ポリアマイド、ポリアクリル酸樹
脂、ロジン、変性ロジン、テルペン樹脂、フェノール樹
脂、脂肪族または脂環族炭化水素樹脂、芳香族系石油樹
脂、塩素化パラフィン、パラフィンワックスなどが単独
或いは混合して使用できる。好ましくは、後述の実施例
で示されている如く、結着樹脂は不飽和ポリエステル樹
脂が好ましい。As the binder resin applied to the toner of the present invention, all known resins can be used. For example, polystyrene, poly-p-chlorostyrene, a homopolymer of styrene such as polyvinyltoluene and a substituted product thereof, styrene-p- Chlorostyrene copolymer, styrene-propylene copolymer, styrene-vinyltoluene copolymer, styrene-vinylnaphthalene copolymer, styrene-methyl acrylate copolymer, styrene-ethyl acrylate copolymer, styrene-
Butyl acrylate copolymer, styrene-octyl acrylate copolymer, styrene-methyl methacrylate copolymer, styrene-ethyl methacrylate copolymer, styrene-butyl methacrylate copolymer, styrene-α-chloromethacrylic acid Methyl copolymer, Styrene-acrylonitrile copolymer, Styrene-vinyl methyl ether copolymer, Styrene-vinyl ethyl ether copolymer, Styrene-vinyl methyl ketone copolymer, Styrene-butadiene copolymer, Styrene-isoprene copolymer Styrene-based copolymers such as polymers, styrene-acrylonitrile-indene copolymers, styrene-maleic acid copolymers, styrene-maleic acid ester copolymers, polymethyl methacrylate, polybutyl methacrylate, polyvinyl chloride, and polyacetic acid Vinyl, poly Tylene, polypropylene, polyester, polyurethane, polyamide, epoxy resin, polyvinyl butyral, polyamide, polyacrylic acid resin, rosin, modified rosin, terpene resin, phenol resin, aliphatic or alicyclic hydrocarbon resin, aromatic petroleum resin, Chlorinated paraffin, paraffin wax or the like can be used alone or as a mixture. Preferably, the binder resin is an unsaturated polyester resin, as shown in the examples below.
さらに、本発明のマゼンタトナーは、負荷電性制御剤
としてアントラキノン系マゼンタ染料又はアルキルサリ
チル酸の金属キレートを含有している。Furthermore, the magenta toner of the present invention contains an anthraquinone-based magenta dye or a metal chelate of alkyl salicylic acid as a negative charge control agent.
また現像剤にキャリヤを使用する場合は従来から公知
のものが使える。例えば鉄、コバルト、ニッケルなどの
磁性物質、及びそれらの合金や混合物、あるいはこれら
の表面にコーティングを施したものである。When a carrier is used for the developer, a conventionally known carrier can be used. For example, magnetic materials such as iron, cobalt, and nickel, and alloys and mixtures thereof, or coatings on the surfaces thereof.
さらに本発明トナーが使用される現像剤に対しては、
コロイダルシリカなどの帯電制御剤、流動性改質剤をト
ナーに対して0.01〜5重量%(好ましくは0.1〜2重量
%)程度添加することは好ましい。Further, for the developer in which the toner of the present invention is used,
It is preferable to add a charge control agent such as colloidal silica or a fluidity modifier to the toner in an amount of about 0.01 to 5% by weight (preferably 0.1 to 2% by weight).
本発明染料を含有するマゼンタトナーの一般的製造法
としては次のようである。A general method for producing a magenta toner containing the dye of the present invention is as follows.
樹脂、着色剤(場合により帯電制御剤)をヘンシェ
ルミキサー等で均一に分散する。The resin and the colorant (charge control agent in some cases) are uniformly dispersed with a Henschel mixer or the like.
分散物をニーダー、エクスルーダー、ロールミル等
で溶融混練する。The dispersion is melt-kneaded with a kneader, extruder, roll mill or the like.
混練物をカッターミル、ハンマーミル等で粗粉砕し
た後、ジェットミル、I式ミル等で微粉砕する。The kneaded material is roughly pulverized by a cutter mill, a hammer mill, or the like, and then finely pulverized by a jet mill, an I-type mill, or the like.
微粉砕物をDS、ジグザグ分級機で分級する。 The finely pulverized material is classified by DS and a zigzag classifier.
場合により、分級物中にシリカ等をヘンシェルミキ
サー等で分散する。In some cases, silica or the like is dispersed in the classified material using a Henschel mixer or the like.
また、本発明の着色剤は懸濁重合法による重合トナー
でも使用可能である。Further, the colorant of the present invention can also be used in a toner polymerized by a suspension polymerization method.
[実施例] 以下実施例をもって本発明を詳細に説明する。[Examples] Hereinafter, the present invention will be described in detail with reference to Examples.
実施例1 以上の処方をロールミルで溶融混練し、冷却後、ジェ
ットミルで微粉砕し、分級し、体積平均粒径12μの負荷
電性マゼンタトナーを得た。この負荷電性マゼンタトナ
ーに、0.5重量%の疎水性シリカ(商品名R−972、日本
アエロジル社製)をヘンシェルミキサーで外添し、マゼ
ンタトナーを得た。このトナー濃度キャリア(樹脂コー
トフェライト粉、平均粒径70μ)と混合し、トナーを6
%の現像剤とした。この現像剤を使用して、第1図に示
すOPC感光ドラムを有した、マゼンタ用現像器、シアン
用現像器、イエロー用現像器及びブラック用現像器を有
するフルカラー電子写真装置を具備したフルカラー複写
機[(CLC−1、商品名)キヤノン製]を用いて複写試
験を行った。Example 1 The above formulation was melt-kneaded in a roll mill, cooled, finely pulverized in a jet mill, and classified to obtain a negatively-charged magenta toner having a volume average particle size of 12 μm. To this negatively charged magenta toner, 0.5% by weight of hydrophobic silica (trade name: R-972, manufactured by Nippon Aerosil Co., Ltd.) was externally added using a Henschel mixer to obtain a magenta toner. This toner concentration carrier (resin-coated ferrite powder, average particle size 70μ) is mixed with
% Developer. Using this developer, a full-color copying machine equipped with a full-color electrophotographic apparatus having a magenta developing device, a cyan developing device, a yellow developing device, and a black developing device having the OPC photosensitive drum shown in FIG. A copy test was performed using a machine [(CLC-1, trade name) manufactured by Canon Inc.].
得られた複写物は、色味(色相、彩度)、耐光性、ロ
ーラー染色性とも十分満足すべきものであった。The obtained copy had satisfactory color tone (hue and saturation), light fastness, and roller dyeability.
この負荷電性マゼンタトナーの環境特性をみるため高
温高湿、低温低湿下における帯電量を測定した。その値
はそれぞれ−18.4μC/g、−15.2μC/gとほとんど変化せ
ず、それぞれの環境においても、光学反射濃度で約1.5
の、ほぼ同一の好ましい画像濃度が得られた。In order to examine the environmental characteristics of the negatively charged magenta toner, the charge amount was measured under high temperature, high humidity, and low temperature, low humidity. The values were almost unchanged at -18.4 μC / g and -15.2 μC / g, respectively.
Approximately the same desirable image density was obtained.
また、30,000枚の複写耐久試験によっても、画像の劣
化はほとんど見られなかった。Also, even in a 30,000-sheet copy durability test, almost no image deterioration was observed.
実施例2 キナクリドン系顔料100重量部に対し、0.9×100/5.1
=90/5.1(≒17.6)重量部のキサンテン系染料を使用し
ている以上の処方で、実施例1と同様にして体積平均粒
径10μの負荷電性マゼンタトナーを作製し、評価したと
ころ、色味、耐光性、ローラー染色性とも十分満足すべ
きものであった。Example 2 0.9 × 100 / 5.1 based on 100 parts by weight of quinacridone pigment
= 90 / 5.1 (≒ 17.6) A negatively chargeable magenta toner having a volume average particle size of 10 μm was prepared and evaluated in the same manner as in Example 1 by using the above-mentioned formulation using a xanthene dye in an amount of 1 part by weight. The color, light fastness, and roller dyeability were also satisfactory.
比較例1 以上の処方で実施例1と同様にしてトナーを作製し、
評価した。コピーの色味では色相が赤側へシフトし、彩
度が劣り、かなりくすんだ色調となり、鮮明なマゼンタ
色は得られなかった。Comparative Example 1 A toner was prepared with the above formulation in the same manner as in Example 1,
evaluated. In the color of the copy, the hue was shifted to the red side, the saturation was inferior, the color tone was considerably dull, and a clear magenta color could not be obtained.
比較例2 以上の処方で実施例1と同様にしてトナー作製し、評
価した。色相については若干のくすみのあるマゼンタ色
であった。耐光性については、フェードメーターでわず
か10hrでも退色が認められ、商品化レベルに達していな
かった。さらに複写機で連続コピーを行ったが、コピー
開始後5,000枚頃より定着ローラーがマゼンタ色に染色
し始め、7,000枚でホットオフセットが発生した。定着
ローラーを観察すると著しい染色がおこっていた。さら
に顕微鏡観察によると顔料のローラー内部へのかなりの
浸透が認められた。また高温高湿下ではその帯電量が−
5.4μC/gと非常に低く、画像の白地部へのカブリが著し
く認められた。Comparative Example 2 A toner was prepared with the above formulation in the same manner as in Example 1, and evaluated. The hue was a slightly dull magenta color. Regarding the light fastness, fading was observed even after only 10 hours with a fade meter, and the product did not reach the commercial level. Further, continuous copying was performed with a copying machine, but the fixing roller began to dye magenta around 5,000 sheets after the start of copying, and hot offset occurred on 7,000 sheets. Observation of the fixing roller revealed remarkable dyeing. Further, microscopic observation revealed that the pigment had considerably penetrated into the inside of the roller. Also, under high temperature and high humidity, the charge amount is-
The image was extremely low at 5.4 μC / g, and fogging of the image on a white background was remarkably observed.
[発明の効果] 以上説明したように、キナクリドン系顔料と、キサン
テン系染料を適当量併用することにより、鮮明なマゼン
タ色が得られ、耐光性が向上し、シリコンゴムローラー
への染色がなくなり、本発明が工業的に非常に有用であ
ることがわかる。[Effects of the Invention] As described above, by using an appropriate amount of a quinacridone-based pigment and a xanthene-based dye, a clear magenta color is obtained, light fastness is improved, and dyeing on a silicone rubber roller is eliminated. It turns out that this invention is very useful industrially.
第1図は本発明のカラートナーが適用されるカラー電子
写真複写機を概略的に示した断面図を示した図である。FIG. 1 is a sectional view schematically showing a color electrophotographic copying machine to which the color toner of the present invention is applied.
Claims (3)
有機顔料及びキサンテン系染料と、負荷電性制御剤とし
てアントラキノン系マゼンタ染料又はアルキルサリチル
酸の金属キレートとを含有するフルカラー画像形成用マ
ゼンタトナーであり、キナクリドン系有機顔料及びキサ
ンテン系染料を合わせた添加量が結着樹脂100重量部に
対して2〜20重量部であり、キナクリドン系有機顔料と
キサンテン系染料との添加比率が100:3〜100:20である
ことを特徴とするフルカラー画像形成用負荷電性マゼン
タトナー。1. A magenta toner for forming a full-color image comprising at least a binder resin, a quinacridone-based organic pigment and a xanthene-based dye, and a metal chelate of an anthraquinone-based magenta dye or an alkyl salicylic acid as a negative charge control agent. The addition amount of the quinacridone-based organic pigment and the xanthene-based dye is 2 to 20 parts by weight based on 100 parts by weight of the binder resin, and the addition ratio of the quinacridone-based organic pigment to the xanthene-based dye is 100: 3 to 100. : 20, a negatively chargeable magenta toner for full-color image formation.
請求項1に記載のフルカラー画像形成用負荷電性マゼン
タトナー。2. The negatively charged magenta toner for full-color image formation according to claim 1, wherein the binder resin is an unsaturated polyester resin.
料との添加比率が100:3〜100:90/5.1である請求項1又
は2に記載のフルカラー画像形成用負荷電性マゼンタト
ナー。3. The negatively charged magenta toner for full-color image formation according to claim 1, wherein the addition ratio of the quinacridone-based organic pigment to the xanthene-based dye is 100: 3 to 100: 90 / 5.1.