JP2640638B2 - Ring gear manufacturing method by precision die forging - Google Patents
Ring gear manufacturing method by precision die forgingInfo
- Publication number
- JP2640638B2 JP2640638B2 JP8275495A JP8275495A JP2640638B2 JP 2640638 B2 JP2640638 B2 JP 2640638B2 JP 8275495 A JP8275495 A JP 8275495A JP 8275495 A JP8275495 A JP 8275495A JP 2640638 B2 JP2640638 B2 JP 2640638B2
- Authority
- JP
- Japan
- Prior art keywords
- ring gear
- ring
- outer diameter
- die
- tooth profile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明はプレスによる精密型抜き
鍛造によるリングギア製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing a ring gear by precision die forging with a press.
【０００２】[0002]
【従来の技術】一般に肉厚の薄い製品、例えば金属製の
リングやギア等を得る場合、型抜き用のプレスにダイス
及びポンチからなる雌雄の抜型（金型）を装着し、この
雌雄の抜型間に鋼板等の材料を供給して打ち抜いてリン
グやギア等を形成するようにしている。ところが、こう
したプレスの打ち抜きによるリングやギア等の製造方法
をそのまま厚さの厚いリングやギア等の製造に用いた場
合、剪断が始まる側の肩部分が丸くなるだれ、所謂“肩
だれ”を生じたり、崩れてしまう上、剪断切り口部分に
かえりや破断面等による勾配を生じてしまい、精密なリ
ングやギア等の製造には用いることが出来ないと言う問
題があった。特に、ダイスとポンチとのクリアランスが
大きくなればなるほど上記問題は顕著に表れる。そこ
で、ダイスとポンチとのクリアランスを極めて少なくし
て剪断切り口部分を綺麗にするファインブランキングプ
レスも用いられているが、ファインブランキングプレス
ではイニシャルコストが嵩んでしまう上、打ち抜き時の
歪みやクラックが発生し易いことから、打ち抜き間隔を
大きくしなくてはならず、歩留まりが悪も悪いと言う問
題がある。さらにファインブランキングプレスでは金型
の角部分の型崩れが早いことから、耐久性にも問題があ
り、厚さの厚いリングやギア等を製造するには切削によ
るのが一般的であった。2. Description of the Related Art Generally, when a thin product such as a metal ring or gear is to be obtained, a male and female die (die) comprising a die and a punch is attached to a die-pressing press. A material such as a steel plate is supplied and punched to form a ring, a gear, and the like. However, when such a method of manufacturing rings and gears by punching a press is used as it is for manufacturing thick rings and gears, the shoulder portion on the side where shearing starts becomes round, so-called “shoulder droop” occurs. In addition, there is a problem that the sheared cut portion has a gradient due to burrs, broken surfaces, and the like, and cannot be used for manufacturing precise rings and gears. In particular, the larger the clearance between the die and the punch is, the more the above-mentioned problem appears. Therefore, a fine blanking press that cleans the shear cut portion by minimizing the clearance between the die and the punch is also used, but the fine blanking press increases the initial cost, and also causes distortion and cracking during punching. Since pitting occurs easily, there is a problem that the punching interval has to be increased and the yield is bad or bad. Further, in the fine blanking press, since the corners of the mold are quickly collapsed, there is a problem in durability, and cutting is generally used to manufacture a thick ring or gear.
【０００３】[0003]
【発明が解決しようとする課題】上記切削によるリング
ギア等を製造する場合、その生産性が低く量産が出来な
いと言う問題があり、製造コストも高く成ってしまうと
言う問題があった。In the case of manufacturing a ring gear or the like by the above-mentioned cutting, there is a problem that the productivity is low and mass production cannot be performed, and a problem that the manufacturing cost increases.
【０００４】更に、ダイスとポンチとのクリアランスを
極めて少なくして剪断切り口部分を綺麗にするフアイン
ブランキングプレスでの加工では、そのプレスが加圧能
力の大きな大型で高価な専用のプレス機で行われること
からイニシャルコストが高くなるという問題があった。Further, in the processing by a fine blanking press for making the clearance between the die and the punch extremely small to clean the shearing cut portion, the press is performed by a large and expensive dedicated press machine having a large pressurizing ability. However, there is a problem that the initial cost is increased because of the above.
【０００５】加えて、ファインブランキングプレスでは
ダイスとポンチとのクリアランスが極めて少ない特殊な
装置であり、金型の耐久性が低くメンテナンスにも多大
の手間と費用とを要してしまい、成形時にリングギアの
隅部にクラックが生じ易いうえ、面だれも残り、精度を
要するリングギア等を製造するのは更に難しいと言う問
題があった。本発明は上記問題点に鑑み提案されたもの
で、肉厚の厚いリングギア等の製造を従来のプレスを利
用して簡単で且つ安価に高精度に製造できるようにする
ことを目的とするものである。[0005] In addition, the fine blanking press is a special device in which the clearance between the die and the punch is extremely small, the durability of the mold is low, and maintenance requires a great deal of labor and cost. Cracks are easily generated at the corners of the ring gear, and there is a problem that it is even more difficult to manufacture a ring gear or the like that requires precision. SUMMARY OF THE INVENTION The present invention has been proposed in view of the above problems, and has as its object to enable the manufacture of a thick ring gear or the like to be easily, inexpensively, and accurately manufactured using a conventional press. It is.
【０００６】[0006]
【課題を解決するための手段】上記目的を達成するため
に本発明に係る精密型抜き鍛造によるリングギア製造方
法は、リングギアの仕上げ外径より大径に形成されたリ
ング素材をその表裏面の何れか一方からプレスし、その
プレスされた一方の面に歯形を形成して歯形素材を形成
する第１工程と、第１工程で形成された歯形素材の歯形
の間の余肉を第１工程と同じ方向からプレスして切断し
歯形を形成するとともに、その外径をリング素材の外径
より小径で且つ仕上げ外径より僅かに大径となるように
縮小させて粗型を形成する第２工程と、第２工程で得ら
れた粗型を第１工程及び第２工程とは逆の方向からプレ
スすることにより第１工程乃至第２工程で生じた肩だれ
及び剪断面の勾配を修正加工し、これと同時にその外径
を所望するリングギアの仕上げ外径となるように縮小さ
せる第３工程とからなることを特徴とするものである。In order to achieve the above object, a method of manufacturing a ring gear by precision die forging according to the present invention comprises the steps of: forming a ring material having a diameter larger than a finished outer diameter of the ring gear on its front and back surfaces; A first step of forming a tooth profile material by forming a tooth profile on one of the pressed surfaces, and a first step of forming excess tooth space between the tooth profiles of the tooth profile material formed in the first step. Pressing from the same direction as the process and cutting to form a tooth profile, and reducing the outer diameter of the ring material to be smaller than the outer diameter of the ring material and slightly larger than the finished outer diameter to form a rough mold Pressing the rough mold obtained in the second step and the second step from the opposite direction to the first step and the second step corrects the shoulder drop and the gradient of the shear surface generated in the first step and the second step. Ring that is processed and at the same time its outer diameter is desired It is characterized in comprising a third step of reduction so as to finish the outer diameter of the A.
【０００７】また、所定の厚さを有する金属製管材をそ
の軸芯に直交する方向に所望の幅で切断して第１工程で
加工されるリング素材を形成したり、所定の厚さを有す
る金属製板材を環状に打ち抜いて第１工程で加工される
リング素材を形成したことも特徴とするものである。In addition, a metal tube having a predetermined thickness is cut at a desired width in a direction perpendicular to the axis of the metal tube to form a ring material to be processed in the first step, or to have a predetermined thickness. It is also characterized in that a ring material to be processed in the first step is formed by punching out a metal plate material in a ring shape.
【０００８】[0008]
【作用】本発明に係る精密型抜き鍛造によるリングギア
製造方法では、先ず、所定の厚さを有する金属製管材を
その軸芯に直交する方向に所望の幅で切断したり、所定
の厚さを有する金属製板材を環状に打ち抜いたリング素
材が第１工程でその周面部分に歯形を形成した歯形素材
が形成される。この時、歯形素材の歯形間には歯形形成
のために圧潰された部分が余肉として寄せられている。
次に、第２工程で歯形素材の歯形間の余肉が切断される
と同時にリング素材の外形が縮められるので形成された
歯形の径も縮められ、リングギアの仕上げ外径より大径
の粗型が形成されるのである。In the method of manufacturing a ring gear by precision die forging according to the present invention, first, a metal pipe having a predetermined thickness is cut into a desired width in a direction perpendicular to the axis of the metal pipe, or a predetermined thickness is cut. In a first step, a tooth material having a tooth profile formed on a peripheral surface portion of a ring material obtained by punching out a metal plate material having an annular shape is formed. At this time, the portion crushed for forming the tooth profile is left as excess between the tooth profiles of the tooth profile material.
Next, in the second step, the excess thickness between the tooth profiles of the tooth profile material is cut, and at the same time, the outer shape of the ring material is reduced, so that the diameter of the formed tooth profile is also reduced. A mold is formed.
【０００９】此処で、第１工程乃至第２工程で形成され
た粗型は表裏の何れか一方からプレス成形されているこ
とから、このプレス成形された側の周縁の角部は肩だれ
及び剪断面の勾配が発生している。次に、この粗型を第
３工程で第１工程と第２工程とは逆の方向からプレス
し、リングギアの仕上げ外径となるようにサイジング加
工で縮小させると、サイジングの等により上記第１工程
乃至第２工程で生じた肩だれ及び剪断面の勾配が殆ど無
い状態に修正されるのである。Here, since the rough mold formed in the first and second steps is press-formed from one of the front and back sides, the corner of the peripheral edge on the press-formed side is shouldered and sheared. A surface gradient has occurred. Next, in a third step, the rough mold is pressed from the opposite direction of the first step and the second step, and is reduced by sizing processing so as to have a finished outer diameter of the ring gear. This is corrected so that the shoulder droop and the shear surface gradient generated in the first and second steps are almost completely eliminated.
【００１０】[0010]
【実施例】以下、本発明にかかる精密型抜き鍛造による
リングギア製造方法の一実施例をトルクコンバーター用
パーキングギアの生産を例に図面に基づいて説明する。
一般に、自動車用トルクコンバーターに使用されている
パーキングギアは、自動車の駐車時に、シフトレバーを
パーキング位置に投入すると自動車をロック状態にする
もので、８mm前後の厚みで外周面に凹凸からなる歯形を
形成したリング状に形成されている。図１はパーキング
ギアを製造する第１工程で使用されるプレス装置におけ
るダイセット部分の縦断正面図であって図上左半部はプ
レスが作動した状態、右半部はプレスの作動前または後
の図、図２はダイセット部分の下型部分の平面図を示
し、図中符号１はこのダイセット部分を全体的に示す。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of a method for manufacturing a ring gear by precision die forging according to the present invention will be described below with reference to the drawings, taking production of a parking gear for a torque converter as an example.
Generally, a parking gear used in a torque converter for a vehicle is such that when the vehicle is parked, a shift lever is put into a parking position to lock the vehicle. It is formed in a formed ring shape. FIG. 1 is a vertical sectional front view of a die set portion in a press device used in a first step of manufacturing a parking gear, wherein the left half in the figure is in a state where the press is operated, and the right half is before or after the press is operated. 2 and FIG. 2 show a plan view of a lower die portion of the die set portion, and reference numeral 1 in the drawing indicates the entire die set portion.
【００１１】このプレス装置におけるダイセット部分１
は、雌ダイス２が装着される下型３と、パンチ４が装着
される上型５とからなる。下型３はプレス装置（全体は
図示せず）に下型ダイセットプレート６を固定し、その
上面部分に雌ダイス２を固定するとともに、雌ダイス２
の内部中央には下型ダイセットプレート６に固定された
ガイド部材８が立設され、ガイド部材８の周縁と雌ダイ
ス２との間の成形隙間９には第１工程で成形されたリン
グ素材１０を押し出すノックアウト手段１１が設けられ
ている。Die set part 1 in this press machine
Consists of a lower die 3 on which the female die 2 is mounted and an upper die 5 on which the punch 4 is mounted. The lower die 3 fixes the lower die set plate 6 to a press device (the whole is not shown), and fixes the female die 2 to the upper surface portion thereof.
A guide member 8 fixed to the lower die set plate 6 is provided upright in the center of the inner surface of the mold. A ring material formed in the first step is formed in a forming gap 9 between a peripheral edge of the guide member 8 and the female die 2. Knock-out means 11 for pushing out 10 are provided.
【００１２】雌ダイス２の内周面には図２及び図３に示
すように、パーキングギア用の歯形１２が形成してあ
り、この雌ダイス２の上端寄り部の歯形１２の上端部分
は上開きテーパー状に形成された所謂“コニカルダイ
ス”になっている。上記ノックアウト手段１１は、成形
隙間９から上端が上方に進退摺動するノックアウトプレ
ート１３と、ノックアウトプレート１３を突き上げるノ
ックアウトピン１４及び図外の油圧シリンダ等によりノ
ックアウトピン１４を押し上げる昇降板１５とからな
る。As shown in FIGS. 2 and 3, a tooth profile 12 for a parking gear is formed on the inner peripheral surface of the female die 2, and the upper end portion of the tooth profile 12 near the upper end of the female die 2 has an upper end. It is a so-called "conical dice" formed in an open tapered shape. The knockout means 11 includes a knockout plate 13 whose upper end slides upward and backward from the molding gap 9, a knockout pin 14 that pushes up the knockout plate 13, and an elevating plate 15 that pushes up the knockout pin 14 by a hydraulic cylinder (not shown) or the like. .
【００１３】一方、パンチ４が装着される上型５は、周
知の押圧手段により昇降する上型ダイセットプレート１
６にパンチプレート１７及びパンチホルダー１８を固定
するとともに、パンチプレート１７とパンチホルダー１
８との間にパンチ４を保持させて構成したもので、パン
チ４の外形は雌ダイス２の歯形１２よりも大きい形状と
なっており、パンチ４の下降量はリング素材１０の厚さ
の約７０％のストロークにしてある。On the other hand, the upper die 5 on which the punch 4 is mounted is moved up and down by a well-known pressing means.
6, the punch plate 17 and the punch holder 18 are fixed.
The outer shape of the punch 4 is larger than the tooth profile 12 of the female die 2, and the lowering amount of the punch 4 is about the thickness of the ring material 10. The stroke is 70%.
【００１４】次に図４及び図５は第２工程に使用するプ
レス装置におけるダイセット部分に係るもので、図４中
左半部はプレスが作動した状態、右半部はプレスの作動
後の図であって、このプレス装置に於けるダイセット部
分１は、雌ダイス２が装着される下型３と、パンチ４が
装着される上型５とからなる点は第１工程で使用するプ
レス装置におけるダイセット部分１と略同様であるが、
下型３では第１工程のプレス装置１におけるガイド部材
８を省略した点やパンチ４の下降量がリング素材１０の
厚さより大きい点及びパンチ４及び雌ダイス２の外径が
第１工程に使用されるパンチ４及び雌ダイス２の径より
僅かに小径にして有る点が異なる。尚、パンチ４はダイ
ス２にり小径のギア形状になっている。上型５では周知
の押圧手段により昇降する上型ダイセットプレート１６
にパンチプレート１７及びパンチホルダー１８を固定
し、パンチホルダー１８に固定されたパンチ４の中央部
分にはパンチダイス１９が配設されるとともに、パンチ
４の外周に嵌合してパンチ４に対して相対移動可能なス
トリッパー２０がゴム製の弾性部材２１を介してパンチ
プレート１７に固定して構成してある。Next, FIGS. 4 and 5 relate to a die set portion in the press device used in the second step. In FIG. 4, the left half portion is in a state where the press is operated, and the right half portion is after the press operation. In the drawing, the die set portion 1 of the press device is composed of a lower die 3 on which a female die 2 is mounted and an upper die 5 on which a punch 4 is mounted. It is almost the same as the die set part 1 in the apparatus, but
In the lower die 3, the point where the guide member 8 is omitted in the press device 1 in the first step, the point that the descending amount of the punch 4 is larger than the thickness of the ring material 10, and the outer diameters of the punch 4 and the female die 2 are used in the first step. The difference is that the diameter is slightly smaller than the diameter of the punch 4 and the female die 2 to be formed. The punch 4 is formed in a small-diameter gear shape around the die 2. In the upper die 5, an upper die set plate 16 which moves up and down by a known pressing means.
A punch plate 17 and a punch holder 18 are fixed to the punch 4, and a punch die 19 is provided at a central portion of the punch 4 fixed to the punch holder 18. A relatively movable stripper 20 is fixed to the punch plate 17 via an elastic member 21 made of rubber.
【００１５】また、図６及び図７は第３工程に使用する
プレス装置におけるダイセット部分１に係るもので、図
６中左半部はプレスが作動した状態、右半部はプレスの
作動後の図であって、このプレス装置のダイセット部分
１は、パンチ４及びパンチダイス１９の外径と雌ダイス
２の内径が第２工程に使用するプレス装置におけるダイ
セット部分１に比べて小径で略仕上がり寸法になってい
る点が異なり、その他は上記第２工程に使用するプレス
装置におけるダイセット部分１と略同様の構成となって
いる。FIGS. 6 and 7 relate to the die set portion 1 in the press apparatus used in the third step. In FIG. 6, the left half is in a state where the press is operated, and the right half is after the press is operated. The outer diameter of the punch 4 and the punch die 19 and the inner diameter of the female die 2 are smaller in diameter than the die set part 1 in the press machine used in the second step. The difference is that the dimensions are substantially finished, and the other configuration is substantially the same as that of the die set portion 1 in the press device used in the second step.
【００１６】上記のプレス装置におけるダイセット部分
１を使用してリングギアを成形する場合を次に説明す
る。先ず、図８に示すように特殊鋼（ＳＣＭ４２０・Ｓ
ＣＲ４２０・Ｓ４５Ｃ等）からなる所定の厚さを有する
金属製管材２１を図中点線Ａで示すようにその軸芯に直
交する方向に所望の幅で切断してリング素材１０を形成
し、このリング素材１０を図１及び図２に示す第１工程
のダイセット部分１の雌ダイス２に載置してパンチ４を
下降させる。パンチ４の下降量がリング素材１０の７０
％であることから、このパンチ４の下降によりリング素
材１０の周縁部分が雌ダイス２内に形成されている歯形
１２で押圧されてリング素材１０の下面部分から約７０
％の高さに歯形２２を形成した歯形素材２３が形成され
る。A case where a ring gear is formed by using the die set portion 1 in the above-described press apparatus will be described below. First, as shown in FIG. 8, special steel (SCM420 · S
CR420 / S45C) having a predetermined thickness is cut at a desired width in a direction orthogonal to the axis thereof as shown by a dotted line A in the figure to form a ring material 10. The material 10 is placed on the female die 2 of the die set portion 1 in the first step shown in FIGS. 1 and 2, and the punch 4 is lowered. The lowering amount of the punch 4 is 70 of the ring material 10.
%, The periphery of the ring material 10 is pressed by the tooth shape 12 formed in the female die 2 by the downward movement of the punch 4, and about 70% from the lower surface of the ring material 10.
% Of the tooth profile material 23 is formed.
【００１７】この時、歯形素材２３の歯形間には歯形形
成のために雌ダイス２内の歯形１２で圧縮して塑性変形
された部分の余肉の大部分が寄せられる。このように、
塑性変形された部分の余肉の移動があることから、これ
を見越してパンチ４の外径をリング素材１０の外径より
大きくしてある。At this time, a large part of the excess portion of the portion that is plastically deformed by being compressed by the tooth shape 12 in the female die 2 for forming the tooth shape is brought between the tooth shapes of the tooth shape material 23. in this way,
The excess diameter of the punch 4 is made larger than the outer diameter of the ring blank 10 in anticipation of the movement of the excess thickness of the plastically deformed portion.
【００１８】次に、歯形素材２３が形成されるとこの歯
形素材２３は、図４及び図５に示す第２工程のダイセッ
ト部分１の雌ダイス２に載置してパンチ４を歯形素材２
３の厚みｔより大きく下降させる。すると、第２工程の
歯形素材２３に形成された歯形間の余肉が切断されて歯
形が形成されるとともに、歯形素材２３の外径が雌ダイ
ス２で少し縮められてリングギア２６の仕上げ外径より
大径の粗型２４が形成されるのである（図１０参照）。
こうした第１工程及び第２工程を経て形成された粗型２
４には雌ダイス２側面の周縁の角部に肩だれ２５が生
じ、剪断面には勾配２７が発生した状態となっている。Next, when the tooth profile material 23 is formed, the tooth profile material 23 is placed on the female die 2 of the die set portion 1 in the second step shown in FIGS.
3 is lowered more than the thickness t. Then, the excess between the tooth profiles formed on the tooth profile material 23 in the second step is cut to form a tooth profile, and the outer diameter of the tooth profile material 23 is slightly reduced by the female die 2 to finish the ring gear 26. The coarse mold 24 having a diameter larger than the diameter is formed (see FIG. 10).
The rough mold 2 formed through the first step and the second step
In FIG. 4, shoulder droop 25 is formed at the corner of the peripheral edge of the female die 2 side surface, and a gradient 27 is generated in the shear surface.
【００１９】そして、この粗型２４を図６及び図７の第
３工程のダイセット部分１の雌ダイス２に反転させて載
置し、パンチ４を下降させる。すると、雌ダイス２の内
径がリングギア２６の仕上げ外径となるように小径に形
成されていることから、この雌ダイス２で粗型２４が絞
られて縮小される時、絞られた余肉等が上記第１工程及
び第２工程で生じた肩だれ２５部分や剪断面部分の勾配
２７部分に回り、肩だれ２５、面だれや勾配２７が殆ど
無い状態に修正された所定の大きさの精密なリングギア
２６が形成されるのである。Then, the rough mold 24 is inverted and placed on the female die 2 of the die set portion 1 in the third step of FIGS. 6 and 7, and the punch 4 is lowered. Then, since the inner diameter of the female die 2 is formed to be a small diameter so as to be the finished outer diameter of the ring gear 26, when the rough mold 24 is narrowed down by the female die 2 and reduced, the excess surplus thickness is reduced. And so on around the shoulder droop 25 portion and the shear surface portion gradient 27 portion generated in the first step and the second step, and the shoulder droop 25, the surface droop and the gradient 27 are corrected to have almost no predetermined size. A precise ring gear 26 is formed.
【００２０】尚、上記実施例では特殊鋼（ＳＣＭ４２０
・ＳＣＲ４２０・Ｓ４５Ｃ等）からなる金属製管材をそ
の軸芯に直交する方向に所望の幅で切断してリング素材
１０を形成するようにしてあるが、こうしたものに限ら
れず、図示は省略したが、所定の厚さを有する上記特殊
鋼からなる金属製板材を環状に打ち抜いてリング素材１
０を形成するようにしてもよいことは勿論である。In the above embodiment, the special steel (SCM420
A ring material 10 is formed by cutting a metal tube made of SCR420, S45C, or the like at a desired width in a direction orthogonal to the axis of the metal tube, but the material is not limited to this and is not shown. A metal plate made of the above-mentioned special steel having a predetermined thickness is punched into a ring to obtain a ring material 1;
Of course, 0 may be formed.
【００２１】[0021]
【発明の効果】本発明にかかる精密型抜き鍛造によるリ
ングギア製造方法は、以上に説明したようにリング素材
が第１工程でその周面部分に歯形を形成した歯形素材に
形成され、第２工程で歯形素材の歯形間の余肉が切断さ
れるとともに、リング素材の外形が縮められ、第３工程
で第１工程とは逆の方向からプレスしてリングギアの仕
上げ外径となるように絞って縮小させると同時に、この
絞られた余肉等により上記第１工程乃至第２工程で生じ
た肩だれ及び剪断面の勾配が殆ど無い状態に修正されて
精密なリングギアを形成するようにしてあるので、リン
グ素材からリングギアまでをプレスで短時間のうちに成
形することができる。これにより品質の向上を図れると
ともに、高品質のリングギアを安定して生産することが
できると言う利点がある。According to the method for manufacturing a ring gear by precision die forging according to the present invention, as described above, the ring material is formed in the first step into the tooth profile material having a tooth profile formed on the peripheral surface thereof. In the process, the excess material between the tooth profiles of the tooth profile material is cut, and the outer shape of the ring material is reduced. In the third process, pressing is performed from the opposite direction to the first process so that the finished outer diameter of the ring gear is obtained. At the same time as squeezing and reducing, the shoulder excess caused by the squeezed excess material and the like and the gradient of the shear surface generated in the first and second steps are corrected to be almost non-existent, thereby forming a precise ring gear. Therefore, the process from the ring material to the ring gear can be formed in a short time by a press. This has the advantage that quality can be improved and a high quality ring gear can be stably produced.
【００２２】更にファインブランキングプレスに比べて
金型の磨耗が少なく、プレス装置の耐久性を大幅に向上
させることができると言う利点もある。Furthermore, there is an advantage that the abrasion of the mold is less than that of the fine blanking press, and the durability of the press device can be greatly improved.
【００２３】従来のようにリングギアを切削により製造
するものに比べてその生産性を大幅に向上させすること
ができ、大量生産による製造コストの低下を図ることが
できると言う利点がある。There is an advantage that productivity can be greatly improved as compared with a conventional ring gear manufactured by cutting, and the manufacturing cost can be reduced by mass production.
【００２４】また、本発明にかかる精密型抜き鍛造によ
るリングギア製造方法ではリング素材からリングギアま
でをプレスで成形するようになっていることから、歯形
の周縁部はプレスの圧力により組織が密になっており、
切削で形成する時のように組織流れを切断することも少
なく、リングギアの強度を向上させることができるとい
う利点もある。Further, in the ring gear manufacturing method by precision die forging according to the present invention, from the ring material to the ring gear is formed by pressing, the peripheral portion of the tooth profile has a dense structure due to the pressure of the press. It has become
There is also an advantage that the tissue flow is hardly cut as in the case of forming by cutting, and the strength of the ring gear can be improved.
【００２５】更に、本発明にかかる精密型抜き鍛造によ
るリングギア製造方法ではリング素材からリングギアま
でを一般的なプレスで径を縮小しながら成形するので、
例えばリングギアの角部にクラックが発生しない程度の
アールを形成し、これを縮小することにより精密な角部
を有するリングギアを成形することができ、高価なフア
インブランキングプレスでの加工に比べてイニシャルコ
ストを大幅に低減することができると言う利点もある。Further, in the method of manufacturing a ring gear by precision die forging according to the present invention, a range from the ring material to the ring gear is formed while reducing the diameter by a general press.
For example, by forming a radius that does not cause cracks at the corners of the ring gear and reducing it, a ring gear with precise corners can be formed, compared to processing with an expensive fine blanking press. This has the advantage that the initial cost can be greatly reduced.
【００２６】加えて、所定の厚さを有する金属製板材を
環状に打ち抜いて、リング素材を形成するようにしたも
のでは、フアインブランキングプレスに比べて打ち抜き
間隔を縮めることができ、材料の歩留まりも向上させる
ことができると言う利点もある。In addition, in the case where a metal plate material having a predetermined thickness is punched in a ring shape to form a ring material, the punching interval can be reduced as compared with a fine blanking press, and the material yield can be reduced. There is also an advantage that it can be improved.
【００２７】しかも、汎用プレスで金属製板材からリン
グギアまでを連続して製造することができ、生産性を向
上させることができ、イニシャルコストの低減も図るこ
とができる利点もある。In addition, there is the advantage that the metal plate material to the ring gear can be continuously manufactured by a general-purpose press, so that the productivity can be improved and the initial cost can be reduced.
【００２８】また、所定の厚さを有する金属製管材をそ
の軸芯に直交する方向に所望の幅で切断したものでは、
素材の無駄をなくすことができ、かかる点でも製造コス
トの低減を図ることができるという利点がある。Further, in a case where a metal pipe material having a predetermined thickness is cut at a desired width in a direction orthogonal to the axis of the metal tube,
There is an advantage that the waste of the material can be eliminated and the manufacturing cost can be reduced in this respect as well.
【図１】第１工程に使用するダイセット部分の縦断正面
図である。FIG. 1 is a vertical sectional front view of a die set portion used in a first step.
【図２】第１工程に使用するダイセット部分における下
型の平面図である。FIG. 2 is a plan view of a lower die in a die set portion used in a first step.
【図３】リング素材が下降されている状態のダイセット
部分の要部拡大縦断正面図である。FIG. 3 is an enlarged vertical sectional front view of a main part of a die set portion in a state where a ring material is lowered.
【図４】第２工程に使用するダイセット部分の縦断正面
図である。FIG. 4 is a vertical sectional front view of a die set used in a second step.
【図５】第２工程に使用するダイセット部分における下
型の平面図である。FIG. 5 is a plan view of a lower die in a die set portion used in a second step.
【図６】第３工程に使用するダイセット部分の縦断正面
図である。FIG. 6 is a vertical sectional front view of a die set used in a third step.
【図７】第３工程に使用するダイセット部分における下
型の平面図である。FIG. 7 is a plan view of a lower die in a die set portion used in a third step.
【図８】リング素材を形成する母材の斜視図である。FIG. 8 is a perspective view of a base material forming a ring material.
【図９】第１工程で加工されて形成された歯形素材の縦
断正面図である。FIG. 9 is a longitudinal sectional front view of a tooth profile material formed by processing in the first step.
【図１０】第２工程で加工されて形成された粗型の縦断
正面図である。FIG. 10 is a longitudinal sectional front view of a rough mold formed by processing in a second step.
【図１１】第３工程で加工されて形成されたリングギア
の縦断正面図である。FIG. 11 is a longitudinal sectional front view of a ring gear formed by processing in a third step.
１０・・・リング素材 ２１・・・金属製管材 ２２・・・歯形 ２３・・・歯形素材 ２４・・・粗型 DESCRIPTION OF SYMBOLS 10 ... Ring material 21 ... Metal tube material 22 ... Tooth shape 23 ... Tooth shape material 24 ... Coarse type
Claims (3)
れたリング素材をその表裏面の何れか一方からプレス
し、そのプレスされた一方の面に歯形を形成して歯形素
材を形成する第１工程と、第１工程で形成された歯形素
材の歯形の間の余肉を第１工程と同じ方向からプレスし
て切断し歯形を形成するとともに、その外径をリング素
材の外径より小径で且つ仕上げ外径より僅かに大径とな
るように縮小させて粗型を形成する第２工程と、第２工
程で得られた粗型を第１工程及び第２工程とは逆の方向
からプレスすることにより第１工程乃至第２工程で生じ
た肩だれ及び剪断面の勾配を修正加工し、これと同時に
その外径を所望するリングギアの仕上げ外径となるよう
に縮小させる第３工程とからなることを特徴とする精密
型抜き鍛造によるリングギア製造方法。1. A ring material formed to have a diameter larger than the finished outer diameter of a ring gear is pressed from one of its front and back surfaces, and a tooth profile is formed on one of the pressed surfaces to form a tooth profile material. In the first step, the excess thickness between the tooth profiles of the tooth profile material formed in the first step is pressed and cut from the same direction as in the first step to form a tooth profile, and the outer diameter is determined from the outer diameter of the ring material. A second step of forming a rough mold by reducing the diameter so as to have a small diameter and slightly larger than the finished outer diameter, and applying the rough mold obtained in the second step in a direction opposite to the first step and the second step. The third step is to correct the shoulder droop and the gradient of the shear surface generated in the first and second steps by pressing from the first step, and at the same time, to reduce the outer diameter to the desired outer diameter of the ring gear. Process by precision die forging Gugia manufacturing method.
に直交する方向に所望の幅で切断して第１工程で加工さ
れるリング素材を形成したことを特徴とする請求項１に
記載の精密型抜き鍛造によるリングギア製造方法。2. A ring material to be processed in the first step by cutting a metal tube having a predetermined thickness at a desired width in a direction orthogonal to the axis of the tube. 3. A method of manufacturing a ring gear by precision die forging according to item 1.
ち抜いて第１工程で加工されるリング素材を形成したこ
とを特徴とする請求項１に記載の精密型抜き鍛造による
リングギア製造方法。3. The ring gear manufacturing according to claim 1, wherein a ring material to be processed in the first step is formed by annularly punching a metal plate material having a predetermined thickness. Method.