JP2612534B2 - Method for producing pile warp knitted fabric and pile warp knitted fabric - Google Patents

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【産業上の利用分野】この発明はパイル環経編物に係
り、特にトリコット，ラッセル等経編物の両面に合成繊
維紡績糸のパイル環を形成し、編組後、熱収縮させて、
柔らかでかつ大きなパイル環を形崩れしないように固定
形成した、浴用垢すりタオル等に好適なパイル環経編物
に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pile ring warp knitted fabric, in particular, a pile ring of a synthetic fiber spun yarn is formed on both sides of a warp knitted fabric such as tricot, Russell, etc.
The present invention relates to a pile ring warp knitted fabric suitable for bath gripper towels and the like, in which a soft and large pile ring is fixed so as not to lose its shape.

【０００２】[0002]

【従来の技術】従来の浴用タオルはパイル織物が一般的
であり、また、いわゆる垢すりタオルは合成繊維フィラ
メント糸を用いたものが知られている。2. Description of the Related Art A conventional bath towel is generally a pile fabric, and a so-called ground towel using a synthetic fiber filament yarn is known.

【０００３】[0003]

【発明が解決しようとする課題】パイル織物はパイル糸
が経に入っており、パイル環を形成するためには緯糸の
代わりに針金や太い捨糸を仮り織して、織成後に針金や
捨糸を抜き取るために、手間がかかるという難があり、
感触が柔らかいので、垢すり用には不適である。また垢
すり用のタオルは、太い合成繊維で形成されていて、目
が粗く、パイル環が硬いために柔らかな肌に傷がつきや
すい難点があり、かつ目が粗いために水の含みが悪く、
石鹸の保持力に欠ける難があった。この発明はそれらの
実情に鑑みて、肌ざわりがよく、垢すりには好適な硬度
があり、保水力、石鹸付きにすぐれ、かつ安価に作成す
ることができる浴用タオルに好適なパイル環経編物を提
供することを目的として開発されたものである。The pile woven fabric contains pile yarns, and in order to form a pile ring, wire or thick waste yarn is temporarily woven in place of the weft yarn, and after weaving, the wire or the waste yarn is thrown away. There is a difficulty that it takes time to pull out the thread,
Because of its soft feel, it is not suitable for scouring. In addition, the towel for mortaring is made of thick synthetic fiber, has a coarse eye, and has a difficulty that the pile ring is hard, so the soft skin is easily scratched, and the coarse eyes have poor water content. ,
There was a difficulty in lack of soap holding power. In view of the above circumstances, the present invention provides a pile ring- knitted fabric suitable for bath towels that has a good texture, has suitable hardness for slime, has excellent water retention and soap, and can be produced at low cost. It was developed for the purpose of doing so.

【０００４】[0004]

【課題を解決するための手段】この発明は上記課題を解
決し、目的を達成するために次のような技術的な手段を
講じた。Means for Solving the Problems The present invention has taken the following technical means in order to solve the above problems and achieve the object.

【０００５】すなわち、熱収縮性合成繊維を経編組した
地組織と、合成繊維紡績糸を経編組したパイル部とで構
成されたパイル環経編物において、パイル部のパイル糸
が地糸より低融点であり、パイル環が地経糸数本置きに
表裏へ交互に突出しており、編組後に編生地幅を１０％
前後の熱収縮をさせ、組織面に対してパイル環を直立さ
せてパイル環を形崩れしないようにセットしたパイル環
経編物、とその製造方法から成る。That is, in a pile loop warp-knitted fabric composed of a ground structure formed by warp braiding of heat-shrinkable synthetic fibers and a pile portion formed by warp braiding of synthetic fiber spun yarn, the pile yarn in the pile portion has a lower melting point than the ground yarn. , and the pile ring protrudes alternately to the front and back every few ground warp, a knitted fabric width after braiding 10%
A pile ring knitted fabric set by heat shrinking back and forth to erect the pile ring with respect to the tissue surface so as not to deform the pile ring , and a method for producing the same.

【０００６】[0006]

【作用】上記のように構成されたこの発明によれば、パ
イル糸が紡績糸であるため、ヒートセットすると、パイ
ル環を構成する微細繊維が融点近い温度で収縮して、紡
績糸のため、長さの収縮というより太さの収縮として表
われ、パイル環は編組したままの状態、すなわち平面に
おいて経糸に対してやや傾斜し、かつ組織面に対して直
立した状態でヒートセットされる。しかして編物全体が
幅方向で１０％前後の収縮をするので、パイル糸は斜め
に蛇行していることから長さのゆとりが生じるために、
パイル環が縮むことはなく、むしろ生地より大きな環に
なる。従って、パイル環が大きく嵩高に突出し、しかも
パイル部が縞状に嵩高となっているためザラザラとした
感蝕を与える。しかしパイル部には紡績糸のパイル環が
浮き出ているために、肌に直接触れるのはパイル環であ
り、縞条状に硬く締まったパイル部の表面に紡績糸の柔
らかな感触のパイル環がある、という構成から、浴用垢
すりタオルに使用するとき、洗い心地がよく、垢すり効
果があるが、肌をいためない。また紡績糸が使用されて
いるために含水性にすぐれて石鹸保持力が抜群である。According to the present invention constructed as described above, since the pile yarn is a spun yarn, when heat-set, the fine fibers constituting the pile ring shrink at a temperature close to the melting point, so that the spun yarn is This manifests itself as shrinkage in thickness rather than shrinkage in length, and the pile ring is heat set in a braided state, ie, slightly inclined with respect to the warp in a plane and upright with respect to the texture plane. However, since the entire knitted fabric shrinks by about 10% in the width direction, since the pile yarn is meandering obliquely, the length of the knitted fabric is increased.
The pile ring does not shrink, but rather becomes larger than the dough. Therefore, the pile ring protrudes large and bulky, and the pile portion is striped and bulky, giving a rough sensation. However, since the pile ring of the spun yarn is protruding in the pile portion, it is the pile ring that directly touches the skin, and the pile ring of the soft feel of the spun yarn is on the surface of the pile portion that is tightly tightened in stripes. Because of its structure, when used for bath rubbing towels, it is comfortable to wash and has a rubbing effect, but it does not hurt the skin. In addition, since spun yarn is used, it is excellent in water content and has excellent soap holding power.

【０００７】[0007]

【実施例】この発明の実施例を図面に基づいて説明す
る。パイル環経編物１はトリコット地を示しており熱収
縮性合成繊維糸（ポリエステルフィラメント）から成る
地組織２．２…と、合成繊維紡績糸（ポリエステル紡績
糸）をパイル糸３Ｂとして編組した縦縞状のパイル部
３．３…から構成されている。前記地組織２の合成繊維
糸は軟化点１８０°Ｃ前後のフィラメントが選択され、
パイル糸３Ｂは軟化点９０°Ｃ前後の合成繊維紡績糸が
選択されている。経編組織は特に限定されるものではな
いが、図２においては、緯糸に対して直角方向に経糸編
組条２Ａ，２Ａ…が等間隔に配列され、該経糸編組条２
Ａ．２Ａ…の一条おきにパイル環３Ａが表出するように
編組されてパイル部３…が形成されている。またパイル
糸３Ｂは前記経糸編組条２Ａ…を一条おきに隣へ斜めに
渡ってその折り返し角部でパイル環３Ａを形成して地組
織に結合されて斜めに戻ってくる蛇行を繰り返してい
る。また表出するパイル環３Ａの属するパイル部３Ｂの
隣の経糸編組条２Ａ（図２の糸番２，５）においては、
裏面にパイル環３Ｃ…が表出するように組織されてい
る。この編組の駒組は、Ｂ＝５−５，０−０。Ｍ＝１−
０，４−３，４−５，１−２。Ｆ＝１−０，０−１。に
構成されている。組織としては図示するように０番から
５番まで６本ある経糸群の中で、０，２，４，５番を地
経糸とし、１番のパイル糸、３番のパイル糸とし、１番
パイル糸は０番から４番間を斜めに蛇行編組し、０番と
４番において折り返してパイル環を形成すると共に、３
番パイル糸は２番と５番間において斜めに蛇行編組し、
２番と５番で折り返してパイル環を形成している。上記
構成から成るこの実施例において、完成されたパイル環
経編物１を９０°Ｃ〜１３０°の雰囲気でヒートセット
すると、パイル糸３Ｂは熱収縮をするので、該収縮率を
１０％前後収縮させると、パイル環３Ａが組織面に対し
て直立して固定（ヒートセット）されて嵩高となるため
パイル部３．３…が地組織２…部分に縞条となり、かつ
パイル環３Ａが経糸列に対して傾斜して組織面に対して
直立状にセットされる。そのため柔らかなパイル糸であ
るが細繊維が熱収縮によって硬化し、ザラッとした感触
となり、紡績糸は細かい繊維の集合体であるから、太い
フィラメント糸と比較すると全体としての硬度は柔らか
く、すなわち、肌に当接してこすっても、洗い心地はよ
いが、硬いフィラメント糸のように肌を傷つける恐れが
ない。またパイル環３Ａは生地編立ての状態でその形を
ヒートセット（固定）されるので、組織面に対して直立
して環形の形崩れが生じず、かつ力が加わっても揺動し
て弾力性が生じていて肌触りがよい。熱収縮したことに
よって編目が詰まった分だけ地厚になり、パイル糸が紡
績糸であるために水を含み、石鹸保持力にすぐれてい
る。An embodiment of the present invention will be described with reference to the drawings. The pile ring warp knitted fabric 1 shows a tricot fabric, and has a ground structure 2.2... Made of heat-shrinkable synthetic fiber yarn (polyester filament) and a vertical striped braided synthetic fiber spun yarn (polyester spun yarn) as a pile yarn 3B. Of the pile sections 3.3... As the synthetic fiber yarn of the ground structure 2, a filament having a softening point of about 180 ° C is selected,
As the pile yarn 3B, a synthetic fiber spun yarn having a softening point of about 90 ° C. is selected. Although the warp knitting structure is not particularly limited, in FIG. 2, the warp braids 2A are arranged at equal intervals in a direction perpendicular to the weft.
A. The pile portions 3 are formed by braiding such that the pile ring 3A is exposed every other line of 2A. The pile yarn 3B repeats the meandering of the warp braids 2A... Alternately crossing every other diagonally, forming a pile ring 3A at the turning corners thereof, being connected to the ground structure, and returning diagonally. In the warp braid 2A (yarn numbers 2 and 5 in FIG. 2) next to the pile portion 3B to which the pile ring 3A to be exposed belongs,
The pile rings 3C are arranged on the back surface. The piece set of this braid has B = 5-5, 0-0. M = 1−
0,4-3,4-5,1-2. F = 1-0,0-1. Is configured. As shown in the figure, among the six warp groups from No. 0 to No. 5, No. 0, 2, 4, and 5 are ground warp yarns, No. 1 pile yarn, No. 3 pile yarn and No. 1 The pile yarn is braided obliquely from No. 0 to No. 4 and folded at No. 0 and No. 4 to form a pile ring.
No. pile yarn is braided meandering obliquely between No. 2 and No. 5,
It is folded at Nos. 2 and 5 to form a pile ring. In this embodiment having the above-described structure, when the completed pile loop knitted fabric 1 is heat-set in an atmosphere of 90 ° C. to 130 °, the pile yarn 3B undergoes heat shrinkage. %, The pile ring 3A is fixed upright (heat set) to the tissue surface and fixed (heat-set) to be bulky, so that the pile portions 3.3 become stripes in the ground structure 2, and the pile ring 3A. Are set upright with respect to the texture plane while being inclined with respect to the warp row. Therefore, although it is a soft pile yarn, the fine fibers are hardened by heat shrinkage and have a rough feel, and since the spun yarn is an aggregate of fine fibers, the overall hardness is soft compared to the thick filament yarn, that is, Even if it rubs against the skin, it is comfortable to wash, but there is no danger of damaging the skin like hard filament yarn. Further, the pile ring 3A is heat set (fixed) in a knitted state, so that the pile ring 3A stands upright against the tissue surface so that the ring does not lose its shape. It has good texture and feels good. Due to the heat shrinkage, the ground thickness becomes as much as the stitch is clogged, the pile yarn is spun yarn, contains water, and has excellent soap holding power.

【０００８】図３は第２実施例を示すパイル環経編物の
平面図である。この実施例は広幅で形成して所望のサイ
ズに細断しやすくしたパイル環経編物である。パイル環
経編物１の組織は前例と同じものであるが、図中符号
４．４は耳であり、符号５．５は中耳である。該耳４、
並びに中耳５は編密度を密にしてあるもので、中耳５…
の中央にヒートカッタ（例えば高周波ミシン、ハンダゴ
テ）を当てることによって切断することができ、かつ切
断面は熱収縮並びに熱溶着するためほつれることがな
い。図中符号６．６は界切である。該界切６…の中央も
前述のようなヒートカッタで切断させることができ、こ
れによって例えばタオル７．７が得られる。このパイル
環経編物１は、浴用垢すりタオルに限らず広範囲な用途
に使用することができる。例えば夏期用の枕カバー，同
じく夏期用の敷布とするとき、汗ばむ季節にさわやかな
感触が得られる。また、ステテコ，パジャマ等に用いて
夏期に清涼感が得られる。なおこの発明は前記実施例に
限定されるものではない。例えばパイル部３は模様状に
形成することができるし、組織もラッシェルにすること
ができる。FIG. 3 is a plan view of a pile loop warp knitted fabric showing a second embodiment. This example is a pile loop warp knitted material formed in a wide width and easily cut into a desired size. The structure of the pile ring knitted fabric 1 is the same as that of the previous example, but reference numeral 4.4 in the figure denotes an ear, and reference numeral 5.5 denotes a middle ear. The ears 4,
The middle ear 5 has a high knitting density.
Can be cut by applying a heat cutter (for example, a high-frequency sewing machine, a soldering iron) to the center thereof, and the cut surface does not fray due to heat shrinkage and heat welding. In the figure, reference numeral 6.6 is a boundary. The center of the boundaries 6 can also be cut with a heat cutter as described above, thereby obtaining, for example, a towel 7.7. This pile
The circular knitted fabric 1 can be used for a wide range of applications, not limited to bath rubbed towels. For example, when a pillow cover for summer and a mattress for summer are used, a refreshing feel can be obtained in a sweaty season. Also, it can be used for steteco, pajamas, etc. to provide a refreshing feeling in summer. The present invention is not limited to the above embodiment. For example, the pile part 3 can be formed in a pattern shape, and the structure can also be Raschel.

【０００９】[0009]

【発明の効果】以上説明したようにこの発明は、パイル
糸を地組織用糸よりも熱軟化点の低い合成繊維紡績糸を
使用し、編組後にパイル糸を熱収縮させたために、生地
全体が１０％前後の収縮をし、かつパイル部が地組織表
面より嵩高となり、パイル環が紡績糸の状態より硬くな
って形崩れしないようにヤットされているため、浴用垢
すりタオルとして使用するときは肌への感触、特に垢す
りに好適で、かつ肌を傷つけない効果がある。As described above, the present invention uses a synthetic fiber spun yarn having a lower thermal softening point than that of the ground structure yarn, and heat shrinks the pile yarn after braiding, so that the whole fabric is made. When shrinking by about 10%, the pile part becomes bulkier than the surface of the ground structure, and the pile ring is made harder than the spun yarn so as not to lose its shape. It has an effect that it is suitable for touching the skin, especially for scouring, and does not damage the skin.

【００１０】パイル部が地組織より嵩高に突出している
ことと、パイル糸が熱収縮によって硬度が高くなってい
るため、肌触りがサラサラとしており、肌にベタと接触
しないので、夏用敷布，枕カバー，ステテコ，パジャマ
用生地等多目的に使用できる効果がある。Since the pile portion protrudes more than the ground structure and the pile yarn has a high hardness due to heat shrinkage, the skin feels smooth and does not come into solid contact with the skin. It has the effect that it can be used for multipurpose such as cover, steteco, pajamas cloth.

【図面の簡単な説明】[Brief description of the drawings]

【図１】パイル環経編物の平面図である。FIG. 1 is a plan view of a pile loop warp knitted fabric.

【図２】パイル環経編物の組織図である。FIG. 2 is a structural diagram of a pile ring warp knitted fabric.

【図３】第２実施例を示すパイル環経編物の平面図であ
る。FIG. 3 is a plan view of a pile loop warp knitted fabric showing a second embodiment.

【符号の説明】[Explanation of symbols]

１ パイル環経編物 ２ 地組織 ２Ａ 経糸編組条 ３ パイル部 ３Ａ パイル環 ４ 耳 ５ 中耳 ６ 界切 ７ 垢すりタオルDESCRIPTION OF SYMBOLS 1 Pile ring warp knitting 2 Ground structure 2A Warp braided braid 3 Pile part 3A Pile ring 4 Ears 5 Middle ear 6 Barrier 7 Dust towel

Claims (2)

(57)【特許請求の範囲】(57) [Claims] 【請求項１】 合成繊維を編組した地組織と合成繊維紡
績糸をパイル糸として経編組するパイル環経編物におい
て、前記パイル糸を地経糸より熱軟化点が低い紡績糸を
用いて経糸１群間を斜蛇行の折返しを繰返して、該折返
角部に組織面と直交するパイル環を形成すると共に、編
組後に該パイル糸の熱軟化点より高い温度で加熱して編
組生地幅を１０％前後熱収縮させて、組織面に対して直
立状にパイル環の形をヒートセットすることを特徴とす
るパイル環経編物の製造方法。1. A pile ring through knit braiding over the ground structure was braided synthetic fiber synthetic fiber yarn as a pile yarn, warp 1 group using a thermal softening point is lower yarn from ground warp the pile yarn between repeated the return of the swash meandering, returned該折
A pile ring perpendicular to the tissue surface is formed at the corner , and after braiding, the pile yarn is heated at a temperature higher than the thermal softening point to thermally shrink the braided fabric width by about 10%, thereby forming an upright state on the tissue surface. Heat-setting the shape of a pile ring to a pile ring warp knitted fabric. 【請求項２】 合成繊維を経編組した地組織と、合成繊
維紡績糸をパイル糸として経編組したパイル部とで構成
されたパイル環経編物において、前記パイル糸は地糸よ
り熱融点が低い紡績糸から成り、経編組後に加熱して編
組生地幅を１０％前後熱収縮させ、経編組織面に対して
直立状にパイル環形をセットしたことを特徴とするパイ
ル環経編物。And earth tissue wherein the braid through the synthetic fiber, a synthetic fiber yarn in a pile ring through knitted fabric is composed of a braided pile section through a pile yarn, said pile yarn has a lower thermal melting point than the ground yarn A pile ring warp knitted fabric comprising a spun yarn, heat-treated after warp braiding to shrink the braided fabric width by about 10%, and setting a pile ring shape upright with respect to the warp knitting structure surface.