JP2605080Y2 - Toothed belt - Google Patents
Toothed beltInfo
- Publication number
- JP2605080Y2 JP2605080Y2 JP1993003152U JP315293U JP2605080Y2 JP 2605080 Y2 JP2605080 Y2 JP 2605080Y2 JP 1993003152 U JP1993003152 U JP 1993003152U JP 315293 U JP315293 U JP 315293U JP 2605080 Y2 JP2605080 Y2 JP 2605080Y2
- Authority
- JP
- Japan
- Prior art keywords
- woven fabric
- resin film
- adhesive layer
- toothed belt
- belt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は動力伝達用の歯付きベル
トに関するものであって、特にその歯付きベルトを形成
する弾性材料としてポリウレタンエラストマーを使用し
た歯付きウレタンベルトに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a toothed belt for transmitting power, and more particularly to a toothed urethane belt using a polyurethane elastomer as an elastic material forming the toothed belt.
【０００２】[0002]
【従来の技術】従来から動力伝達の手段として、歯付き
ベルトが広く使用されている。この歯付きベルトは、ゴ
ムなどの弾性材料よりなる環状ベルトの肉厚内に長さ方
向に延びる抗張体を埋入し、内周面に一定間隔で噛合歯
を突設し、その歯形表面に沿って布帛を貼着してなるも
のである。2. Description of the Related Art Toothed belts have been widely used as a means for transmitting power. In this toothed belt, a tensile member extending in the length direction is embedded in the thickness of an annular belt made of an elastic material such as rubber, and meshing teeth are protruded at regular intervals on an inner peripheral surface. Is affixed along with the cloth.
【０００３】そして近年、これらの歯付きベルトの弾性
材料として、強度が大きく耐摩耗性に優れ、且つ耐久性
に優れたポリウレタンエラストマーを使用することが行
われている。[0003] In recent years, polyurethane elastomers having high strength, excellent wear resistance and excellent durability have been used as elastic materials for these toothed belts.
【０００４】しかしながらポリウレタンエラストマー
は、他の弾性材料に比べて摩耗係数が極めて大きく、プ
ーリーと噛合した際に騒音を発し、また発熱して耐久性
を低下させていた。[0004] However, polyurethane elastomers have an extremely high coefficient of wear as compared with other elastic materials, generate noise when engaged with a pulley, and generate heat to reduce durability.
【０００５】この問題点を解決するものとして、特公平
１−３５２２２号公報に記載されたものが知られてい
る。[0005] To solve this problem, there is known one described in Japanese Patent Publication No. 1-35222.
【０００６】このものは、歯形の表面に貼着される布帛
として、織布の片面にポリウレタンエラストマーよりも
摩擦係数が小さく且つ摩滅抵抗の小さい不浸透性樹脂を
重ね合わせ、これを織布に熱融着したものが使用されて
おり、その布帛の織布の面を歯形表面に貼着したもので
ある。In this method, an impervious resin having a lower coefficient of friction and a lower abrasion resistance than a polyurethane elastomer is superimposed on one side of a woven fabric as a fabric to be adhered to the surface of the tooth profile, and this is heat-bonded to the woven fabric. A fused product is used, and the woven fabric surface of the fabric is adhered to the tooth profile surface.
【０００７】そしてベルトの走行時には、不浸透性樹脂
はプーリーとの噛合により摩滅し、その後はポリウレタ
ンエラストマーが食込んだ織布がプーリーに接触するた
め、プーリーとの噛合による摩擦係数が減少し、騒音や
発熱が防止されるというものである。During the running of the belt, the impervious resin is worn away by the engagement with the pulley, and thereafter, the woven fabric in which the polyurethane elastomer bites comes into contact with the pulley, so that the coefficient of friction due to the engagement with the pulley decreases, Noise and heat generation are prevented.
【０００８】[0008]
【考案が解決しようとする課題】しかしながらこのもの
では、歯付きベルトの製造時に液状のポリウレタンエラ
ストマーが織布を透過するのを、不浸透性樹脂の層によ
り阻止するので、不浸透性樹脂の織布に対する貼着状態
によって歯形表面の状態が変動し、プーリーに対する摩
擦係数にむらが生じる。However, in this method, the liquid polyurethane elastomer is prevented from passing through the woven fabric during the production of the toothed belt by the layer of the impervious resin. The state of the tooth profile surface fluctuates depending on the state of application to the cloth, and the coefficient of friction with the pulley becomes uneven.
【０００９】すなわち不浸透性樹脂の織布に対する食込
みが深いと、ポリウレタンエラストマーの露出が減少
し、プーリーに対する摩擦係数が過度に小さくなり、騒
音や発熱は減少するものの、プーリーとの噛合いで容易
に織布が摩耗し、ベルトの歯形状が変化して噛み合い不
良を起し勝ちである。That is, when the penetration of the impervious resin into the woven fabric is deep, the exposure of the polyurethane elastomer is reduced, the coefficient of friction on the pulley becomes excessively small, and noise and heat generation are reduced. The woven fabric is worn, and the tooth shape of the belt changes, which tends to cause poor meshing.
【００１０】また逆に不浸透性樹脂の織布に対する食込
みが浅いと、ポリウレタンエラストマーが部分的に露出
し、摩擦係数が大きくなり、騒音を生じ、また発熱によ
り耐久性が低下する。On the other hand, if the penetration of the impervious resin into the woven fabric is shallow, the polyurethane elastomer is partially exposed, the coefficient of friction increases, noise is generated, and durability decreases due to heat generation.
【００１１】従って一本の歯付きベルト１でも部分的に
摩擦係数が変動し、騒音や発熱を生じながら噛み合い不
良を起すことがあり、また製品の間にも品質にばらつき
が生じ易かった。Therefore, even with a single toothed belt 1, the friction coefficient partially fluctuates, noise and heat generation may occur, causing poor meshing, and the quality may easily vary among products.
【００１２】本考案はかかる事情に鑑みなされたもので
あって、不浸透性樹脂の織布に対する食込み深さを一定
ならしめ、ポリウレタンエラストマーの露出の程度を一
定にし、歯付きベルトのプーリーに対する摩擦係数をコ
ントロールして、走行時に噛み合い不良を起すことな
く、騒音や発熱を有効に防止すると共に、部分的な摩擦
係数の変動を低減し、また常に一定の品質の製品を得る
ことができる歯付きベルトを提供することを目的とする
ものである。The present invention has been made in view of such circumstances, and has a constant depth of penetration of an impermeable resin into a woven fabric, a constant degree of exposure of a polyurethane elastomer, and friction of a toothed belt against a pulley. Controlled coefficient to effectively prevent noise and heat generation without causing poor meshing during driving, reduce fluctuations in partial friction coefficient, and have a toothed surface that can always obtain products of constant quality It is intended to provide a belt.
【００１３】[0013]
【課題を解決する手段】而して本考案は、摩擦係数の大
きい弾性材料よりなる環状ベルトの肉厚内に長さ方向に
延びる抗張体を埋入し、内周面に一定間隔で噛合歯を突
設し、その歯形表面に沿って布帛を貼着してなる歯付き
ベルトにおいて、前記布帛が、合成繊維のウーリー加工
糸よりなるたて糸と通常の合成繊維よりなるよこ糸とを
織成してなる織布と、合成樹脂フィルムの片面に低融点
合成樹脂よりなる接着層を形成してなる不浸透性樹脂フ
ィルムとよりなり、当該不浸透性樹脂フィルムの前記接
着層が前記織布に接するように重ね合わされて融着され
ており、その布帛における前記織布の繊維間に前記環状
ベルトの弾性材料が浸透していることを特徴とするもの
である。According to the present invention, a tensile member extending in the length direction is embedded in the thickness of an annular belt made of an elastic material having a large coefficient of friction, and meshes with the inner peripheral surface at regular intervals. In a toothed belt in which teeth are protruded and a cloth is adhered along the tooth profile surface, the cloth is formed by weaving a warp yarn made of synthetic fiber woolly yarn and a weft yarn made of ordinary synthetic fiber. A woven fabric, comprising an impermeable resin film formed by forming an adhesive layer made of a low melting point synthetic resin on one side of a synthetic resin film, such that the adhesive layer of the impermeable resin film is in contact with the woven fabric. The elastic material of the annular belt permeates between the fibers of the woven fabric in the fabric.
【００１４】また本考案においては、前記不浸透性樹脂
フィルムにおける接着層の厚みを、織布のたて糸を構成
する単繊維の直径の１／２〜１倍程度とするのが、最も
好ましい。In the present invention, the thickness of the adhesive layer in the impermeable resin film is most preferably about 1/2 to 1 times the diameter of the single fiber constituting the warp yarn of the woven fabric.
【００１５】図１は本考案の歯付きベルト１を示すもの
である。２はポリウレタンなどの摩擦係数の大きい弾性
材料よりなる環状ベルトであって、その肉厚内には長さ
方向に延びる抗張体３が配置されており、また環状ベル
ト２の内周面には一定間隔で噛合歯４が突設されてい
る。FIG. 1 shows a toothed belt 1 according to the present invention. Reference numeral 2 denotes an annular belt made of an elastic material having a large coefficient of friction such as polyurethane. A tensile member 3 extending in the length direction is disposed within the thickness of the annular belt. The meshing teeth 4 are provided at regular intervals.
【００１６】そしてこの歯付きベルト１の内周面には、
噛合歯４の歯形表面に沿って布帛５が貼着されている。
この布帛５は、織布６と不浸透性樹脂フィルム７とを重
ね合わせて融着したものであって、織布６側が歯付きベ
ルト１の歯形表面に貼着されている。On the inner peripheral surface of the toothed belt 1,
The cloth 5 is stuck along the tooth profile surface of the meshing tooth 4.
The fabric 5 is obtained by laminating a woven fabric 6 and an impermeable resin film 7 on top of each other and fusing the woven fabric 6, and the woven fabric 6 is adhered to the toothed surface of the toothed belt 1.
【００１７】而して織布６は、合成繊維のウーリー加工
糸よりなるたて糸８と、通常の合成繊維よりなるよこ糸
９とを織成したものであって、たて糸８が歯付きベルト
１の長さ方向に延びている。The woven fabric 6 is obtained by weaving a warp yarn 8 made of synthetic fiber wooly-processed yarn and a weft yarn 9 made of ordinary synthetic fiber. Extending in the direction.
【００１８】たて糸８は、ナイロン繊維、ポリエステル
繊維などの合成繊維に、ウーリー加工を施した糸条であ
って、その単繊維の直径が３０μ（ナイロン繊維の場合
で約７d ）以下が好ましい。The warp yarn 8 is a yarn obtained by subjecting a synthetic fiber such as a nylon fiber or a polyester fiber to a wooly process, and the diameter of the single fiber is preferably 30 μm (about 7 d in the case of a nylon fiber).
【００１９】またよこ糸９としては、ウーリー加工を施
さない通常のナイロン、ポリエステルなどの合成繊維が
使用される。As the weft yarn 9, ordinary synthetic fibers such as nylon and polyester not subjected to wooly processing are used.
【００２０】また不浸透性樹脂フィルム７は、合成樹脂
フィルム１０の片面に、低融点合成樹脂よりなる接着層
１１を形成してなるものであって、前記合成樹脂フィル
ム１０は環状ベルト２に使用される弾性材料よりも摩擦
係数が小さく、且つ摩耗され易い材料が使用される。The impermeable resin film 7 is formed by forming an adhesive layer 11 made of a low melting point synthetic resin on one surface of a synthetic resin film 10, and the synthetic resin film 10 is used for the annular belt 2. A material having a smaller coefficient of friction than the elastic material to be used and which is easily worn is used.
【００２１】合成樹脂フィルム１０としては、低密度ポ
リエチレン樹脂、高密度ポリエチレン樹脂、ポリプロピ
レン樹脂、エチレンメタアクリレート共重合体、エチレ
ンメチルメタアクリレート共重合体、エチレン酢酸ビニ
ル共重合体、ポリエステル樹脂、ナイロン樹脂、ポリビ
ニルアルコール樹脂、フッ素樹脂などのフィルムが使用
される。Examples of the synthetic resin film 10 include low density polyethylene resin, high density polyethylene resin, polypropylene resin, ethylene methacrylate copolymer, ethylene methyl methacrylate copolymer, ethylene vinyl acetate copolymer, polyester resin, and nylon resin. And films of polyvinyl alcohol resin, fluororesin and the like.
【００２２】また接着層１１としては、合成樹脂フィル
ム１０との接着性が良好で、且つ合成樹脂フィルム１０
を構成する合成樹脂よりも融点が低いものが使用され
る。具体例としては、合成樹脂フィルム１０として高密
度ポリエチレン樹脂（融点約１３０℃）を、接着層１１
としてエチレンメチルメタアクリレート共重合体（融点
約１１０℃）を使用することができる。The adhesive layer 11 has good adhesion to the synthetic resin film 10 and
A resin having a lower melting point than the synthetic resin constituting the above is used. As a specific example, a high-density polyethylene resin (melting point of about 130 ° C.)
Can be used as an ethylene methyl methacrylate copolymer (melting point: about 110 ° C.).
【００２３】不浸透性樹脂フィルム７は、合成樹脂フィ
ルム１０と接着層１１とを二層押出しすることにより製
造できる。また合成樹脂フィルム１０の表面に接着層１
１をラミネート又は塗布することもできる。The impermeable resin film 7 can be manufactured by extruding the synthetic resin film 10 and the adhesive layer 11 in two layers. The adhesive layer 1 is formed on the surface of the synthetic resin film 10.
1 can also be laminated or applied.
【００２４】そしてこの不浸透性樹脂フィルム７を接着
層１１が織布６に接するように織布６に重ね合わせ、加
熱して接着層１１を溶融させ、不浸透性樹脂フィルム７
と織布６とを融着して布帛５を形成している。The impervious resin film 7 is superimposed on the woven fabric 6 so that the adhesive layer 11 is in contact with the woven fabric 6, and the adhesive layer 11 is melted by heating.
And the woven fabric 6 are fused to form the fabric 5.
【００２５】而してこの布帛５は、織布６の側が歯付き
ベルト１に接するように歯形表面に貼着され、環状ベル
ト２を構成する弾性材料は織布６を構成する繊維の間に
浸透している。The cloth 5 is attached to the toothed surface such that the side of the woven cloth 6 is in contact with the toothed belt 1, and the elastic material forming the annular belt 2 is formed between the fibers forming the woven cloth 6. Has penetrated.
【００２６】[0026]
【作用】本考案においては、不浸透性樹脂フィルム７が
合成樹脂フィルム１０の片面に接着層１１を形成したも
のであり、それを織布６に融着しているので、その融着
時には接着層１１が溶融しており、熔融した接着層１１
の樹脂が織布６を構成するたて糸８の繊維の間に浸透し
た状態となる。In the present invention, the impermeable resin film 7 has the adhesive layer 11 formed on one side of the synthetic resin film 10 and is fused to the woven cloth 6, so that the adhesive is The layer 11 is molten and the molten adhesive layer 11
Is infiltrated between the fibers of the warp yarns 8 constituting the woven fabric 6.
【００２７】そしてその融着に際しては、接着層１１は
溶融しているために、その厚み全体に亙って繊維間に浸
透し、また合成樹脂フィルム１０は溶融していないため
繊維間に浸透することはなく、図２に示されるように不
浸透性樹脂フィルム７はほゞ接着層１１の厚みまで繊維
間に浸透することとなり、その浸透深さは常に一定とな
る。At the time of fusion, the adhesive layer 11 is melted, so that it penetrates between the fibers over its entire thickness, and the synthetic resin film 10 is not melted, so that it penetrates between the fibers. As shown in FIG. 2, the impervious resin film 7 penetrates between the fibers to almost the thickness of the adhesive layer 11, and the penetration depth is always constant.
【００２８】合成樹脂フィルム１０は直接織布６の繊維
の間に浸透することはないが、接着層１１に対して接着
しており、不浸透性樹脂フィルム７は接着層１１の織布
６に対する楔効果により強固に接着する。Although the synthetic resin film 10 does not directly penetrate between the fibers of the woven fabric 6, it is adhered to the adhesive layer 11, and the impermeable resin film 7 is attached to the woven fabric 6 of the adhesive layer 11. Strong adhesion due to wedge effect.
【００２９】而してこの布帛５を歯付きベルト１の歯形
表面に貼着する際には、弾性材料は織布６を構成する繊
維の間に浸透するが、織布６の表面の既に接着層１１が
浸透している部分にまで浸透することはない。従って弾
性材料は接着層１１の樹脂が浸透した部分を除いて織布
６の繊維間にくまなく充填され、その織布６に対する浸
透状態も常に一定となる。When the cloth 5 is applied to the toothed surface of the toothed belt 1, the elastic material penetrates between the fibers constituting the woven cloth 6, but is not adhered to the surface of the woven cloth 6. It does not penetrate to the part where the layer 11 has penetrated. Therefore, the elastic material is filled all over the fibers of the woven fabric 6 except for the portion of the adhesive layer 11 where the resin has penetrated, and the state of penetration into the woven fabric 6 is always constant.
【００３０】従って本考案の歯付きベルト１を走行させ
た場合、先の従来例のものと同様に不浸透性樹脂フィル
ム７は速かに摩滅し、織布６が露出する。このとき織布
６に弾性材料が浸透しており、その弾性材料も繊維の間
から歯形表面に露出することとなるが、繊維によりスプ
ロケットとの接触面積が減殺され、適度の摩擦係数に調
整される。Therefore, when the toothed belt 1 of the present invention is run, the impervious resin film 7 is quickly worn away and the woven fabric 6 is exposed, as in the prior art. At this time, the elastic material has penetrated into the woven fabric 6, and the elastic material is also exposed on the tooth surface from between the fibers. However, the contact area with the sprocket is reduced by the fibers, and the friction coefficient is adjusted to an appropriate value. You.
【００３１】また本考案によれば、弾性材料の織布６に
対する浸透状態が常に一定であるため、歯形表面への弾
性材料の露出状態にばらつきがなく、全体に亙って均等
な摩擦係数を有する。Further, according to the present invention, since the state of penetration of the elastic material into the woven fabric 6 is always constant, the state of exposure of the elastic material to the tooth profile surface does not vary, and a uniform friction coefficient is obtained throughout. Have.
【００３２】[0032]
【考案の効果】従って本考案によれば、不浸透性樹脂フ
ィルム７により織布６の表面まで弾性材料が露出するの
を阻止し、織布６によって歯付きベルト１の摩擦係数を
低下せしめ、走行時の騒音を防止すると共に、発熱を防
止して耐久性を向上させることができる。According to the present invention, the elastic material is prevented from being exposed to the surface of the woven fabric 6 by the impermeable resin film 7, and the woven fabric 6 lowers the coefficient of friction of the toothed belt 1. Noise during running can be prevented, and heat generation can be prevented to improve durability.
【００３３】さらに本考案によれば、不浸透性樹脂フィ
ルム７の接着層１１を一定の深さまで織布６に浸透せし
めることにより、弾性材料の織布６への浸透深さを調整
しているので、弾性材料の織布６への浸透状態及び、織
布６の露出の状態が常に一定であり、部分的に摩擦係数
が変動し、騒音や発熱を生じながら噛み合い不良を起こ
すことがないと共に、一定の品質を有する製品を安定し
て製造することができる。Further, according to the present invention, the penetration depth of the elastic material into the woven fabric 6 is adjusted by allowing the adhesive layer 11 of the impermeable resin film 7 to penetrate the woven fabric 6 to a certain depth. Therefore, the state of infiltration of the elastic material into the woven fabric 6 and the state of exposure of the woven fabric 6 are always constant, the friction coefficient partially changes, and noise and heat generation do not cause poor meshing. In addition, a product having a certain quality can be stably manufactured.
【００３４】本考案においては不浸透性樹脂フィルム７
の接着層１１の厚みを、織布６のたて糸８を構成する繊
維の直径の１／２〜１倍とすることにより、弾性材料の
歯形表面への露出状態が最適となり、最も良好な走行が
得られるが、歯付きベルト１の用途により、また弾性材
料の柔軟性や摩擦係数などの物性により、接着層１１の
厚みをコントロールすることによって歯付きベルト１の
摩擦係数を調節することができる。In the present invention, the impermeable resin film 7 is used.
The thickness of the adhesive layer 11 is set to 1/2 to 1 times the diameter of the fiber constituting the warp yarn 8 of the woven fabric 6, so that the state of exposure of the elastic material to the tooth profile surface is optimized, and the best running is achieved. Although it is obtained, the friction coefficient of the toothed belt 1 can be adjusted by controlling the thickness of the adhesive layer 11 depending on the use of the toothed belt 1 and physical properties such as the flexibility and friction coefficient of the elastic material.
【００３５】[0035]
【実施例】前記構成の歯付きベルト１において、織布６
のたて糸８として、単繊維繊度が２．０６d （直径１６
μ）の４２０d ナイロン糸のウーリー加工糸を７２本／
inch使用し、よこ糸９として２１０d ナイロン糸を８２
本／inch使用して、２／２綾織組織で織布６を織成し
た。DESCRIPTION OF THE PREFERRED EMBODIMENTS In the toothed belt 1 having the above-described structure, the woven fabric 6
The warp yarn 8 has a single fiber fineness of 2.06 d (diameter 16
μ) 420d nylon thread wooly processed yarn 72 /
inch, and 210d nylon thread as the weft thread 82
Using the book / inch, the woven fabric 6 was woven with a 2/2 twill weave structure.
【００３６】また不浸透性樹脂フィルム７は、合成樹脂
フィルム１０として高密度ポリエチレン樹脂（融点１３
０℃）を使用し、接着層１１としてエチレンメチルメタ
アクリレート共重合体（融点１１０℃）を使用した。こ
の両者を、接着層１１の厚みが約１５μとなるように両
者を二層押出し成型することにより、二層の不浸透性樹
脂フィルム７を得た。The impermeable resin film 7 is a high-density polyethylene resin (having a melting point of 13) as the synthetic resin film 10.
0 ° C.) and an ethylene methyl methacrylate copolymer (melting point 110 ° C.) as the adhesive layer 11. The two layers were extruded into two layers so that the thickness of the adhesive layer 11 became about 15 μ, thereby obtaining a two-layer impervious resin film 7.
【００３７】そして前記織布６に不浸透性樹脂フィルム
７を、接着層１１が織布６に接するように重ね合わせ、
１２０℃に加熱して線圧２０kg／cmの力で押圧し、熱融
着して布帛５を得た。Then, an impervious resin film 7 is overlaid on the woven fabric 6 so that the adhesive layer 11 is in contact with the woven fabric 6.
The fabric 5 was heated to 120 ° C., pressed with a linear pressure of 20 kg / cm, and thermally fused to obtain a fabric 5.
【００３８】この布帛５を金型の歯形に沿って配置し、
その外周に抗張体３を巻回し、金型を閉じて当該金型内
に液状ポリウレタンエラストマーを注入し、硬化させて
歯付きベルト１を得た。This cloth 5 is arranged along the tooth shape of a mold,
The tensile member 3 was wound around the outer periphery, the mold was closed, and a liquid polyurethane elastomer was injected into the mold and cured to obtain the toothed belt 1.
【００３９】この歯付きベルト１を、２８５mmの間隔を
隔てて配置された歯数２０の原動プーリーと歯数４０の
被動プーリーとに掛回し、回転数６０００rpm の条件で
駆動した。そのときの騒音の発生は少く、ベルト温度の
異常な上昇もなく、極めて安定した回転が得られた。The toothed belt 1 was wound around a driving pulley having 20 teeth and a driven pulley having 40 teeth, which were arranged at an interval of 285 mm, and was driven at a rotation speed of 6000 rpm. At that time, noise generation was small, and there was no abnormal rise in belt temperature, and extremely stable rotation was obtained.
【図１】 本考案の歯付きベルト１の一部の斜視図FIG. 1 is a perspective view of a part of a toothed belt 1 of the present invention.
【図２】 本考案の歯付きベルト１の主要部を拡大して
示した横断面図FIG. 2 is an enlarged cross-sectional view showing a main part of the toothed belt 1 of the present invention.
１ 歯付きベルト ２ 環状ベルト ３ 抗張体 ４ 噛合歯 ５ 布帛 ６ 織布 ７ 不浸透性樹脂フィルム ８ たて糸 ９ よこ糸 １０ 合成樹脂フィルム １１ 接着層 DESCRIPTION OF SYMBOLS 1 Toothed belt 2 Annular belt 3 Tensile body 4 Intermeshing teeth 5 Fabric 6 Woven cloth 7 Impermeable resin film 8 Warp 9 Weft 10 Synthetic resin film 11 Adhesive layer
───────────────────────────────────────────────────── フロントページの続き (72)考案者 塩唐松 善行 大阪府摂津市鳥飼和道２丁目６番８− 304号 (72)考案者 松木 敦 大阪府寝屋川市大字打上414番地の２ ライツシティ東寝屋川２−509 (56)参考文献 特開 昭63−135631（ＪＰ，Ａ) 特開 昭63−19444（ＪＰ，Ａ) 特開 昭60−81536（ＪＰ，Ａ) 特公 平１−35222（ＪＰ，Ｂ２) (58)調査した分野(Int.Cl.7，ＤＢ名) F16G 1/00 - 5/20 B29D 29/00 - 29/10 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Yoshiyuki Shiomatsu 2-6-8-304, Torikai-Wado, Settsu-shi, Osaka (72) Inventor Atsushi Matsuki 414 No. 2, Oaza Launch, Neyagawa-shi, Osaka 2 Rights City East 2-509 Neyagawa (56) References JP-A-63-135631 (JP, A) JP-A-63-19444 (JP, A) JP-A-60-81536 (JP, A) JP-B-1-35222 (JP, A) , B2) (58) Field surveyed (Int. Cl. 7 , DB name) F16G 1/00-5/20 B29D 29/00-29/10
Claims (2)
ベルト（２）の肉厚内に長さ方向に延びる抗張体（３）
を埋入し、内周面に一定間隔で噛合歯（４）を突設し、
その歯形表面に沿って布帛（５）を貼着してなる歯付き
ベルト（１）において、前記布帛（５）が、合成繊維の
ウーリー加工糸よりなるたて糸（８）と通常の合成繊維
よりなるよこ糸（９）とを織成してなる織布（６）と、
合成樹脂フィルム（１０）の片面に低融点合成樹脂より
なる接着層（１１）を形成してなる不浸透性樹脂フィル
ム（７）とよりなり、当該不浸透性樹脂フィルム（７）
の前記接着層（１１）が前記織布（６）に接するように
重ね合わされて融着されており、その布帛（５）におけ
る前記織布（６）の繊維間に前記環状ベルト（２）の弾
性材料が浸透していることを特徴とする、歯付きベルトA tensile member (3) extending longitudinally within the thickness of an annular belt (2) made of an elastic material having a high coefficient of friction.
, And meshing teeth (4) are protruded at regular intervals on the inner peripheral surface,
In a toothed belt (1) obtained by adhering a cloth (5) along the tooth profile surface, the cloth (5) is made of a warp yarn (8) made of synthetic fiber wooly yarn and ordinary synthetic fiber. A woven fabric (6) formed by weaving a weft (9);
An impermeable resin film (7) formed by forming an adhesive layer (11) made of a low melting point synthetic resin on one side of a synthetic resin film (10), and the impermeable resin film (7)
The adhesive layer (11) is overlapped and fused so as to be in contact with the woven fabric (6), and between the fibers of the woven fabric (6) in the fabric (5), Toothed belt characterized by being impregnated with an elastic material
る接着層（１１）の厚みが、織布（６）のたて糸（８）
を構成する単繊維の直径の１／２〜１倍であることを特
徴とする、請求項１に記載の歯付きベルト2. The warp yarn (8) of the woven fabric (6) has a thickness of the adhesive layer (11) in the impermeable resin film (7).
The toothed belt according to claim 1, wherein the diameter of the belt is 1/2 to 1 times the diameter of a single fiber constituting the belt.