JP2602691B2 - Water-floating solid pesticide formulation - Google Patents
Water-floating solid pesticide formulationInfo
- Publication number
- JP2602691B2 JP2602691B2 JP8784488A JP8784488A JP2602691B2 JP 2602691 B2 JP2602691 B2 JP 2602691B2 JP 8784488 A JP8784488 A JP 8784488A JP 8784488 A JP8784488 A JP 8784488A JP 2602691 B2 JP2602691 B2 JP 2602691B2
- Authority
- JP
- Japan
- Prior art keywords
- parts
- silicone
- water
- preparation according
- polyoxyalkylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 産業上の利用分野 本発明は、水浮遊性固状農薬製剤に関する。Description: TECHNICAL FIELD The present invention relates to a water-suspendable solid pesticide formulation.
従来の技術 最近、水浮遊性の担体に、殺虫成分等を、吸着・ある
いはコーテイングさせるか又は、担体と殺虫成分等を混
和し、造粒したものに、撥水剤をコーテイングする等し
て水浮遊性を付与した粒剤についての研究が試みられて
いる。2. Description of the Related Art In recent years, a water-floating carrier has been adsorbed or coated with a pesticidal component or the like, or a carrier and a pesticidal component have been mixed and granulated, and a water-repellent agent has been coated on the granulated water. Research on granules with floating properties has been attempted.
例えば、特公昭48−15613には、固型沈降物質と、浮
遊性物質を固結剤を用いて、付着・被覆して得られる基
材に、殺虫成分、界面活性物質または撥水剤を吸着させ
る浮遊性粒剤が、また特公昭47−1240には、焼成加工パ
ーライトにポリブテンを用いて殺虫成分を固着させた浮
遊性粒剤が、開示されている。特公昭49−11421は、ガ
ス効果を有する、つまり揮散して、殺虫作用を奏する殺
虫化合物の水面施用用粒剤を開示している。該粒剤は、
揮散性化合物を担体またはこれを加えずして撥水性物質
と混合して撥水性とした微粉状物を、粒基材の表面に付
着せしめて得ている。For example, Japanese Patent Publication No. 48-15613 discloses that a pesticidal component, a surfactant, or a water repellent is adsorbed on a substrate obtained by attaching and coating a solid sedimentation substance and a floating substance using a consolidation agent. Japanese Patent Publication No. 47-1240 discloses a floating granule in which an insecticidal component is fixed by using polybutene in calcined pearlite. JP-B-49-11421 discloses granules for water application of insecticidal compounds which have a gaseous effect, i.e. volatilize and exhibit insecticidal action. The granules are
The volatile compound is mixed with a water-repellent substance by adding a carrier or a carrier, and a water-repellent fine powder is obtained by adhering to the surface of the granular substrate.
更に、担体として吸水能35〜50％の粒状軽石または蛭
石を用い、これらの担体に主剤を吸着させ高級脂肪酸で
被覆してなる浮遊性粒状殺虫組成物が、特公昭44−8600
に開示されている。Further, a floating particulate insecticidal composition comprising a pumice or vermiculite having a water absorption capacity of 35 to 50% as a carrier, a main agent adsorbed on the carrier and coated with a higher fatty acid, is disclosed in JP-B-44-8600.
Is disclosed.
発明が解決しようとする課題 しかしながら前記した従来技術は、いずれも、水浮遊
性の担体を用いることが要件となるか（特公昭48−1561
3,47−1240）または、特定吸水能を有するか軽石や蛭石
に限って担体とし得る（特公昭44−8600）か、あるい
は、揮散性殺虫化合物を用いた粒剤に限られた（特公昭
49−11421）。あるいは、製剤が複雑な構成となってい
て、実用的でないといった欠点があった。更に、これら
は、いずれも粒剤として、製剤化され、水面施用した場
合に、浮遊するので土壌に吸着されたり水底の水に溶解
して、無駄になる分がかなり低減される効果を有してい
るが水面全体に、活性成分が広がるため、また植物体へ
の付着性が悪いため、やはり、植物体に接触しないまま
無駄になる部分が、かなりあるという欠点が依然として
残っていた。Problems to be Solved by the Invention However, all of the above-mentioned prior arts require the use of a water-floating carrier (Japanese Patent Publication No. 48-1561).
3,47-1240) or can be used only as pumice or vermiculite as a carrier (Japanese Patent Publication No. 44-8600), or limited to granules using volatile insecticide compounds Kimiaki
49-11421). Alternatively, there is a disadvantage that the preparation has a complicated structure and is not practical. Furthermore, these are all formulated as granules, and when applied to the surface of the water, they float, so that they are adsorbed on the soil or dissolved in the water at the bottom of the water, and have the effect of considerably reducing waste. However, since the active ingredient spreads over the entire surface of the water and adherence to the plant body is poor, there still remains a disadvantage that a considerable portion is wasted without contacting the plant body.
本発明の目的は水面施用した場合に、農薬活性物質が
より効率的に、植物体に接し、桿表面を毛管現象により
上昇するか、又は、直接茎葉部に付着し、株元防除効果
が高められた農薬製剤を提供することにある。An object of the present invention is that when applied to the surface of water, the pesticidally active substance more efficiently contacts the plant and raises the rod surface by capillary action, or directly adheres to the foliage, enhancing the root control effect. To provide a pesticide formulation.
課題を解決するための手段 本発明者らは、本来、病害虫に対しすぐれた防除効果
を有する農薬も、従来の製剤では、水面施用した場合、
水面近くに棲息するウンカあるいは紋枯病等に対する防
除効果が十分でないという欠点を克服すべく、農薬活性
物質と固状担体に、種々の粘結剤や撥水剤等の添加物の
配合を検討した結果ポリオキシアルキレンシリコーンを
配合した製剤は、水面施用した場合、イネ等の株元へ凝
集し、かつ茎葉部への付着がすぐれていることを見出
し、さらに種々検討を加え、本発明を完成するに至っ
た。Means for Solving the Problems The present inventors originally, pesticides having an excellent control effect on pests, conventional formulations, when applied to the water,
In order to overcome the drawback of insufficient control effect on planthoppers and sheath blights living near the water surface, consider adding various binders, water repellents, and other additives to the pesticide active substance and solid carrier. As a result, it was found that the formulation containing the polyoxyalkylene silicone, when applied on the surface of the water, aggregated to the roots of rice and the like and had excellent adhesion to the foliage. I came to.
すなわち、本発明は、農薬主剤と固状担体とに、ポリ
オキシアルキレンシリコーンを配合してなる水浮遊性固
状製剤に関わる。That is, the present invention relates to a water-floating solid preparation obtained by blending a polyoxyalkylene silicone with a pesticide base and a solid carrier.
本発明製剤によれば、例えば、メイチュウ等に対しす
ぐれた防除効果を有するS,S′−（２−ジメチルアミノ
トリメチレン）ビス（チオカルバメート）塩酸塩（一般
名：カルタップ塩酸塩，以下カルタップ塩酸塩と称す
る。）が、ウンカの防除にもすぐれた効果を奏し、ウン
カ防除剤として利用できる。According to the preparation of the present invention, for example, S, S '-(2-dimethylaminotrimethylene) bis (thiocarbamate) hydrochloride (general name: cartap hydrochloride, hereinafter referred to as cartap hydrochloride) having an excellent controlling effect on meichu and the like. Which is also referred to as a salt) has an excellent effect on controlling planthoppers and can be used as a planthopper controlling agent.
かくして本発明を適用し得る農薬活性物質としては、
とりわけ、株元防除用殺虫剤及び殺菌剤が好ましい。カ
ルタップ塩酸塩の他に、例えばBPMC,MIPC,MPMC,MEP,NA
C,ダイアジノン，イソキサチオン，マラソン，ピレスロ
イド系殺虫剤等の殺虫剤及びバリダマイシン等の殺菌剤
が用いることができる。これらを単独で用いてもよく、
また所望により二種以上混合して用いることもできる。Thus, the pesticidal active substance to which the present invention can be applied,
In particular, insecticides and fungicides for controlling plant roots are preferred. In addition to cartap hydrochloride, for example, BPMC, MIPC, MPMC, MEP, NA
Insecticides such as C, diazinon, isoxathion, marathon, pyrethroid insecticides and fungicides such as validamycin can be used. These may be used alone,
If desired, two or more kinds may be used in combination.
本発明の最大の特徴は、従来結合剤あるいは粘結剤と
して通常用いられている、グリセリン，ポリエチレング
リコール，アラビアゴム等とは全く異なるポリオキシア
ルキレンシリコーンを用いることである。通常の結合剤
あるいは、水施用製剤によく配合される界面活性剤およ
び撥水剤の中には、水浮遊性を与えるものも、与えない
ものもあるが、いずれも、水面上または水中を、むしろ
株元から遠ざかろうとする傾向があるのに対し、本発明
のポリオキシアルキレンシリコーンは、特異的株元へ凝
集する性質を示す。このような株元へ凝集する性質は、
通常シリコーンオイルと称されるジメチルシリコーンオ
イル，メチルフェニルシリコーンオイルにも見られない
性質である。本発明に用いられるポリオキシアルキレン
シリコーンは、高分子化合物であるが、このように株元
へ凝集する性質を、示すものであればいずれのタイプで
もよい。このようなポリオキシアルキレンシリコーンと
しては、例えば式 の少なくとも１つのメチル基が式−(CH2)m−ＯAOn
Ｈで表わされるポリオキシアルキレン基で置換された化
合物（式中、l,mは０または１以上の整数を、ｎは１以
上の整数を、Ａは炭素数１〜８の分枝していてもよいア
ルキレン基を表す）があげられ好ましくは、Ａとして
は、炭素数１〜５のアルキレン、より好ましくは、エチ
レンまたはプロピレンである。また上記ポリオキシアル
キレンシリコーンは、平均分子量約500〜100000のも
の、さらに好ましくは平均分子量約1000〜20000のもの
が特に好適である。The greatest feature of the present invention is to use a polyoxyalkylene silicone which is completely different from glycerin, polyethylene glycol, gum arabic and the like, which are conventionally used as a binder or a binder. Among ordinary binders or surfactants and water repellents often blended in water-applied preparations, those that impart water buoyancy, and those that do not, all of which can be used on the water surface or in water, Rather, the polyoxyalkylene silicones of the present invention exhibit the property of aggregating to a specific strain, whereas they tend to move away from the strain. The property of agglutinating to such strains is
This property is not found in dimethyl silicone oil and methylphenyl silicone oil, which are usually called silicone oil. The polyoxyalkylene silicone used in the present invention is a high molecular compound, and any type may be used as long as it exhibits the property of aggregating at the stock. As such a polyoxyalkylene silicone, for example, At least one methyl group has the formula of - (CH 2) m -OAO n
A compound substituted with a polyoxyalkylene group represented by H (wherein l and m are integers of 0 or 1 or more, n is an integer of 1 or more, and A is A represents an alkylene group having 1 to 5 carbon atoms, and more preferably represents ethylene or propylene. The polyoxyalkylene silicone has an average molecular weight of about 500 to 100,000, more preferably about 1,000 to 20,000.
このようなポリオキシアルキレンシリコーンとして
は、例えば、塗料の添加剤（伸びを助長し、塗布を容易
にする）、色むら防止剤、アイロン用糊の滑り性改良剤
等として、市販されているものが、そのまま利用でき
る。Such polyoxyalkylene silicones are commercially available as, for example, paint additives (promoting elongation and facilitating application), color unevenness preventing agents, ironing paste slipperiness improvers, and the like. But it can be used as it is.
このような市販品として、例えば、TSF4452,TSF4460
｛東芝シリコーン（株）製｝等が挙げられる。As such commercially available products, for example, TSF4452, TSF4460
{Manufactured by Toshiba Silicone Co., Ltd.} and the like.
上記したようなポリオキシアルキレンシリコーンをそ
れぞれ単独で用いても、又二種以上を適宜組み合わせて
用いることもできる。The polyoxyalkylene silicones described above can be used alone or in combination of two or more.
本発明で用いられる固状担体としては、それ自体水浮
遊性を有するパーライト、バーミキュライト、軽石、ク
ルミの殻を粉砕して得られるクルミ粒、木粉等のみなら
ず、それ自体では沈む、砕砂（例えば、特開昭61−2863
02に記載のもの），硅砂｛例えば、川砂（林化成）｝，
流紋岩｛例えば、ヒノヤライト（日の家商会），カガラ
イト（丹後建設）｝，粒状珪藻土｛例えば、セラトム
（垣内商事）｝その他粒状鉱物質担体も用いられる。こ
のような担体のうち、パーライトとは、黒曜石、真珠
岩、その他、加熱により膨張するガラス質火山岩をい
い、各種の品質のものが用いられる。市販製品も、その
まま利用でき、このような市販製品としては例えば ｛以上、東興パーライト工業（株）｝、パーライト銘柄
１型｛宇部興産（株）｝等が挙げられる。また、バーミ
キュライトは、Mg（Si,Al）Ｏ（OH）Mg・H2Oのような構
成をもつが、焼成したものも、未焼成のものも含め、色
々の品質のものが使用できる。クルミ粒としては、例え
ば市販のウオルナットフラワー ｛日本ウオルナット
（株）｝等が挙げられる。 The solid carrier used in the present invention is a water carrier itself.
Perlite, vermiculite, pumice stone,
If only walnut grains, wood flour, etc. obtained by crushing the shell of Lumi
Crushed sand that sinks by itself (for example, see JP-A-61-2863)
02), silica sand {for example, river sand (forest chemical formation)},
Rhyolite, for example, Hinoyarite (Hinoya Shokai), Kagara
Ito (Tango Construction)｝, granular diatomaceous earth ｛For example, Seratom
(Kakiuchi Shoji) Other particulate mineral carriers are also used. This
Among such carriers, pearlite is obsidian, pearl
Rocks and other vitreous volcanic rocks that expand when heated
Of various qualities. Commercial products are also
It can be used as is, such as commercial products｛Tokyo Perlite Industry Co., Ltd. パ ー, Perlite brand
Type 1 {Ube Industries, Ltd.} and the like. Also, Bami
Curite is Mg (Si, Al) O (OH) Mg ・ HTwoStructure like O
Color, including fired and unfired
Various qualities can be used. As a walnut grain,
Bamboo walnut flower ｛Japan Walnut
Co., Ltd.
上記担体のうち比重１を超えるものであって本発明の
ポリオキシアルキレンシリコーンを配合することにより
水に浮くものもある。このような担体の例としては、砕
砂 更に好ましくは粒径60〜600μｍの砕砂（特開昭61
−286302に記載の方法に従って、さらに微細に粉砕して
得られる。），軽石が都合よく用いられる。また比重１
以下のものとしては、焼成加工パーライトがとりわけ好
ましく用いられる。尚、上記砕砂は、例えば玄武岩，安
山岩，砂岩，石英班岩またはこれに準ずる石質を有する
ものが用いられる。原石は表土、その他の不純物を例え
ば、スカルピングスクリーン，リプルフロー型スクリー
ン等で除去した後粉砕される。原石の粉砕は、砕骨材製
造と同様の方法で行なわれる。例えば、採取された原石
は泥抜き等により不純物を除去したのち、公知の粉砕機
例えばジョークラッシャー（大塊破砕用クラッシャ
ー），コーンクラッシャー（中割用クラッシャー），イ
ンペラーブレーカ（細割用クラッシャー）等を用いて順
次細かく砕いた後、エアセパレーターで分級することに
より得られる。Among the above-mentioned carriers, some have a specific gravity of more than 1 and float on water by blending the polyoxyalkylene silicone of the present invention. Examples of such carriers include crushed sand, more preferably crushed sand having a particle size of 60 to 600 μm (JP-A-61
It is obtained by further finely pulverizing according to the method described in -286302. ), Pumice is conveniently used. Specific gravity 1
As the following, calcined perlite is particularly preferably used. As the crushed sand, for example, basalt, andesite, sandstone, quartz porphyry, or a stone having a similar lithology is used. The rough is pulverized after removing the topsoil and other impurities by, for example, a scalping screen, a ripple flow screen, or the like. The ore is crushed in the same manner as in the manufacture of crushed aggregate. For example, the collected ore is used to remove impurities by mud removal or the like, and then a known pulverizer such as a jaw crusher (crusher for crushing large blocks), a cone crusher (crusher for middle splitting), an impeller breaker (crusher for fine splitting), or the like is used. And then finely crushed using an air separator, and then classified by an air separator.
但し、上記した担体に加え、所望により、その他の植
物性粉末、クレイ類、タルク類、シリカ類（珪藻土
等）、ゼオライト、川砂，炭酸カルシウム等の固体担体
の一種以上を本発明の効果をそこなわない範囲で適宜混
合使用してよい。However, in addition to the above-mentioned carriers, if desired, one or more solid carriers such as other vegetable powders, clays, talcs, silicas (diatomaceous earth, etc.), zeolites, river sand, calcium carbonate, etc. may exert the effects of the present invention. They may be mixed and used as appropriate within a range not to be described.
本発明製剤を製造するにあたっては、担体と農薬主剤
さらには、シリコーンを、常法に従って混合することに
より、担体に、農薬主剤を、シリコーンによって付着あ
るいは被覆するのが好ましい。混合するに際しては、通
常、担体を、ドラム型等通常用いられる混合機に入れ、
主剤を混合し、シリコーンを加える方法が用いられる
が、担体と、シリコーンを混合し、その後主剤を加え
て、担体に付着してもよく、混合の順序は必ずしも限定
されない。In producing the preparation of the present invention, it is preferable that the carrier, the pesticide base and further the silicone are mixed in accordance with a conventional method so that the carrier is adhered or coated with the pesticide base to the carrier. In mixing, the carrier is usually put into a commonly used mixer such as a drum type,
Although a method of mixing the main agent and adding silicone is used, the carrier and the silicone may be mixed, and then the main agent may be added and adhered to the carrier, and the order of mixing is not necessarily limited.
混合、付着する際、さらに、適宜カルボキシメチルセ
ルロース ナトリウム（CMC−Na），ポリビニルアルコ
ール，デンプン等通常用いられる結合剤を加えてもよ
い。At the time of mixing and adhering, a commonly used binder such as sodium carboxymethylcellulose (CMC-Na), polyvinyl alcohol, and starch may be appropriately added.
本製剤は、通常常法により粒剤とするのが望ましいが
より微細な、微粒剤，細粒剤，粉粒剤等の剤型にするこ
ともできる。This preparation is usually desirably prepared into granules by a usual method, but may be formed into finer forms such as fine granules, fine granules, and powder granules.
又製剤の撥水性及び／又は水浮遊性を向上させるべく
高級脂肪酸を添加してもよい。このような高級脂肪酸と
しては、炭素数８〜20のものが好ましい。とりわけステ
アリン酸、パルミチン酸、ラウリン酸等が好適である。
これら高級脂肪酸は単独でも用いてもよく、又二種以上
組み合わせて添加してもよい。A higher fatty acid may be added to improve the water repellency and / or water floating property of the preparation. Such higher fatty acids preferably have 8 to 20 carbon atoms. Particularly, stearic acid, palmitic acid, lauric acid and the like are suitable.
These higher fatty acids may be used alone or in combination of two or more.
本発明製剤には、その他所要の場合には、界面活性剤
（ポリオキシスチレン化フエノールなど），酸化防止剤
（イソプロピルアシッドホスフェートなど）、流動助
剤、湿潤剤・安定剤（リン酸，酒石酸など）などを本発
明の効果をそこなわない範囲で添加してもよい。In the preparation of the present invention, if necessary, a surfactant (eg, polyoxystyrenated phenol), an antioxidant (eg, isopropyl acid phosphate), a flow aid, a wetting agent / stabilizer (eg, phosphoric acid, tartaric acid, etc.) ) May be added in a range that does not impair the effects of the present invention.
各成分の配合比は、製剤全体を100重量部とした時、
農薬主剤は（二種以上混合する場合は、その合計量が）
約0.2〜40重量部，好ましくは約0.5〜35重量部である。
カルタップ塩酸塩製剤の場合は、特に約１〜30重量部の
カルタップ原体を用いるのが好ましい。The mixing ratio of each component, when the whole formulation is 100 parts by weight,
Pesticide base (when two or more are mixed, the total amount)
It is about 0.2 to 40 parts by weight, preferably about 0.5 to 35 parts by weight.
In the case of cartap hydrochloride preparations, it is particularly preferable to use about 1 to 30 parts by weight of cartap raw material.
ポリオキシアルキレンシリコーンは、製剤全体100重量
部とした時、約0.1〜15重量部、好ましくは約0.3〜13重
量部、更に好ましくは約0.5〜10重量部である。The polyoxyalkylene silicone is used in an amount of about 0.1 to 15 parts by weight, preferably about 0.3 to 13 parts by weight, more preferably about 0.5 to 10 parts by weight, based on 100 parts by weight of the whole preparation.
次に、実施例、試験例で、本発明をさらに具体的に説
明するが、本発明は、これらの実施例に限定されるもの
ではない。Next, the present invention will be described more specifically with reference to examples and test examples, but the present invention is not limited to these examples.
以下の実施例において、“部”とあるのは“重量部”
を意味する。In the following examples, "parts" means "parts by weight".
Means
実施例１ 粒径100〜600μｍの砕砂94.9部をドラムミキサーに入
れ、カルタップ塩酸塩原体４部を添加混合した後TSF446
0（東芝シリコーン（株）製）0.5部及びリン酸0.6部を
加えて更に十分混合して、コーテイングして粒剤を得
た。Example 1 94.9 parts of crushed sand having a particle size of 100 to 600 μm was put in a drum mixer, and 4 parts of cartap hydrochloride bulk material was added and mixed, and then TSF446 was added.
0 (manufactured by Toshiba Silicone Co., Ltd.) and 0.5 part of phosphoric acid were added, mixed well, and coated to obtain granules.
実施例２ 焼成加工パーライト56.5部をドラムミキサーに入れた
上、カルタップ塩酸塩原体30部を加え、混合した後TSF4
452（東芝シリコーン（株）製）7.5部およびイソプロピ
ルアシッドホスフェート６部を加えて更に十分混合して
焼成加工パーライトの表面にコーテイングして、粒剤を
得た。Example 2 56.5 parts of calcined perlite were put in a drum mixer, 30 parts of cartap hydrochloride bulk material was added, and after mixing, TSF4
452 (manufactured by Toshiba Silicone Co., Ltd.) and 7.5 parts of isopropyl acid phosphate were added, mixed well, and coated on the surface of calcined pearlite to obtain granules.
実施例３ 焼成加工パーライト65部をドラムミキサーに入れ、カ
ルタップ塩酸塩原体24部を加えて混合した後TSF4460
（東芝シリコーン（株）製）6.0部,TSF4452（東芝シリ
コーン（株）製）3.5部及びイソプロピルアシッドホス
フェート1.5部を加えて更に十分混合して焼成加工パー
ライトの表面にコーテイングして粒剤を得た。Example 3 65 parts of calcined perlite were put in a drum mixer, and 24 parts of cartap hydrochloride bulk material was added and mixed, and then TSF4460 was added.
6.0 parts (manufactured by Toshiba Silicone Co., Ltd.), 3.5 parts of TSF4452 (manufactured by Toshiba Silicone Co., Ltd.) and 1.5 parts of isopropyl acid phosphate were added, mixed well, and coated on the surface of calcined pearlite to obtain granules. .
実施例４ 600〜100μｍの軽石92.9部をドラムミキサーに入れ、
カルタップ塩酸塩原体４部を加えて、混合した後TSF445
2（東芝シリコーン（株）製）2.3部，酒石酸0.8部を加
えて、十分混合して軽石の表面にコーテイングして粒剤
を得た。Example 4 92.9 parts of 600 to 100 μm pumice was placed in a drum mixer,
After adding 4 parts of cartap hydrochloride bulk and mixing, TSF445
2. 2.3 parts of Toshiba Silicone Co., Ltd. and 0.8 parts of tartaric acid were added, mixed well, and coated on the surface of pumice to obtain granules.
実施例５ 粒径100〜600μｍの砕砂94.9部をドラムミキサーに入
れ、MIPC原体４部を添加混合した後TSF4460（東芝シリ
コーン（株）製）0.5部及びリン酸0.6部を加えて更に十
分混合して、コーティングして粒剤を得た。Example 5 94.9 parts of crushed sand having a particle size of 100 to 600 μm were put in a drum mixer, 4 parts of an MIPC material was added and mixed, and then 0.5 part of TSF4460 (manufactured by Toshiba Silicone Co., Ltd.) and 0.6 part of phosphoric acid were added and further mixed sufficiently. Then, coating was performed to obtain granules.
実施例６ 焼成加工パーライト56.5部をドラムミキサーに入れた
上、BPMC原体30部を加え、混合した後TSF4452（東芝シ
リコーン（株）製）7.5部およびイソプロピルアシッド
ホスフェート６部を加えて更に十分混合して焼成加工パ
ーライトにコーティングして、粒剤を得た。Example 6 56.5 parts of calcined perlite were put in a drum mixer, 30 parts of BPMC material were added and mixed, and then 7.5 parts of TSF4452 (manufactured by Toshiba Silicone Co., Ltd.) and 6 parts of isopropyl acid phosphate were added and further mixed well. Then, it was coated on calcined pearlite to obtain granules.
実施例７ 焼成加工パーライト65部をドラムミキサーに入れ、ME
P原体24部を加えて混合した後TSF4460（東芝シリコーン
（株）製）6.0部,TSF4452（東芝シリコーン（株）製）
3.5部及びイソプロピルアシッドホスフェート1.5部を加
えて更に十分混合して焼成加工パーライトにコーティン
グして粒剤を得た。Example 7 65 parts of baked perlite were put into a drum mixer and ME
After adding and mixing 24 parts of the P substance, 6.0 parts of TSF4460 (manufactured by Toshiba Silicone Co., Ltd.) and TSF4452 (manufactured by Toshiba Silicone Co., Ltd.)
3.5 parts and 1.5 parts of isopropyl acid phosphate were added, mixed well, and coated on calcined pearlite to obtain granules.
実施例８ 600〜100μｍの軽石96.1部をドラムミキサーに入れ、
バリダマイシン原体1.5部を加えて、混合した後TSF4452
（東芝シリコーン（株）製）2.3部，ソルビン酸カリウ
ム0.1部を加えて、十分混合して軽石の表面にコーティ
ングして粒剤を得た。Example 8 96.1 parts of 600-100 μm pumice was placed in a drum mixer,
After adding 1.5 parts of validamycin drug substance and mixing, TSF4452
2.3 parts of Toshiba Silicone Co., Ltd. and 0.1 part of potassium sorbate were added, mixed well, and coated on the surface of pumice to obtain granules.
実施例９ カルタップ塩酸塩６部，ステアリン酸2.4部,TSF4460
（東芝シリコーン（株）製）0.2部，イソプロピルアシ
ッドホスフェート0.5部，粒径250〜50μｍの砕砂88.9部
を用いて実施例１と同様にして粒剤を得た。Example 9 Cartap hydrochloride 6 parts, stearic acid 2.4 parts, TSF4460
Granules were obtained in the same manner as in Example 1 using 0.2 parts (manufactured by Toshiba Silicone Co., Ltd.), 0.5 parts of isopropyl acid phosphate, and 88.9 parts of crushed sand having a particle size of 250 to 50 μm.
実施例10 カルタップ塩酸塩原体５部，パルミチン酸2.5部,TSF4
452（東芝シリコーン（株）製）0.15部，リン酸0.7部，
クレー1.8部，粒径300〜100μｍの砕砂89.85部を用い
て、実施例１と同様にして粒剤を得た。Example 10 Cartap hydrochloride bulk 5 parts, palmitic acid 2.5 parts, TSF4
452 (manufactured by Toshiba Silicone Co., Ltd.) 0.15 parts, phosphoric acid 0.7 parts,
Granules were obtained in the same manner as in Example 1 using 1.8 parts of clay and 89.85 parts of crushed sand having a particle size of 300 to 100 μm.
実施例11 カルタップ塩酸塩原体４部，ラウリン酸3.5部,TSF446
0（東芝シリコーン（株）製）0.1部,TSF4452（東芝シリ
コーン（株）製）0.25部，リン酸0.6部，粒径300〜100
μｍの砕砂91.55部を用いて実施例１と同様にして粒剤
を得た。Example 11 Cartap hydrochloride bulk 4 parts, lauric acid 3.5 parts, TSF446
0 (Toshiba Silicone Co., Ltd.) 0.1 part, TSF4452 (Toshiba Silicone Co., Ltd.) 0.25 part, phosphoric acid 0.6 part, particle size 300-100
Granules were obtained in the same manner as in Example 1 using 91.55 parts of crushed sand of μm.
本発明に属さない対照製剤を以下に示す。 Control formulations not belonging to the invention are shown below.
対照製剤１ カルタップ塩酸塩原体４部，ポリオキシエチレンスチ
レン化フエノール1.5部，リン酸0.5部，粒径1000〜800
μｍの川砂94部を用いて、実施例１と同様にして粒剤を
得た。Control preparation 1 Cartap hydrochloride bulk 4 parts, polyoxyethylene styrenated phenol 1.5 parts, phosphoric acid 0.5 parts, particle size 1000-800
Granules were obtained in the same manner as in Example 1 using 94 parts of river sand of μm.
対照製剤２ カルタップ塩酸塩原体４部，ステアリン酸1.2部，リ
ン酸0.3部，粒径1000〜800μｍの川砂94.5部を用いて、
実施例１と同様にして粒剤を得た。Control formulation 2 Using 4 parts of cartap hydrochloride bulk material, 1.2 parts of stearic acid, 0.3 parts of phosphoric acid, and 94.5 parts of river sand having a particle size of 1000 to 800 μm,
A granule was obtained in the same manner as in Example 1.
対照製剤３ カルタップ塩酸塩原体４部，リン酸0.5部,44μｍ以下
の微粉クレー90.5部及び結合剤としてポリビニルアルコ
ール５部を加え、均一に混合し練合水17.5部を加え、よ
く練合し、粒径1000μｍに造粒し乾燥して粒剤を得た。Control formulation 3 4 parts of cartap hydrochloride bulk material, 0.5 part of phosphoric acid, 90.5 parts of fine powder clay of 44 μm or less and 5 parts of polyvinyl alcohol as a binder were added, mixed uniformly, and kneaded with 17.5 parts of kneading water. It was granulated to a particle size of 1000 μm and dried to obtain granules.
対照製剤４ カルタップ塩酸塩原体４部，リン酸0.5部，ステアリ
ン酸3.5部,44μｍ以下の微粉クレー87部及び結合剤とし
てポリビニルアルコール５部を加え、均一に混合し、練
合水17.5部を加えよく練合し粒径1000μｍに造粒し乾燥
して粒剤を得た。Control preparation 4 4 parts of cartap hydrochloride bulk material, 0.5 part of phosphoric acid, 3.5 parts of stearic acid, 87 parts of fine powder clay of 44 μm or less and 5 parts of polyvinyl alcohol as a binder, uniformly mixed, and 17.5 parts of kneading water were added. The mixture was kneaded well, granulated to a particle size of 1000 μm, and dried to obtain granules.
対照製剤５ カルタップ塩酸塩原体４部，メチルシリコンオイル0.
5部，リン酸0.6部，粒径800〜600μｍの川砂94.9部を用
いて、実施例１と同様にして粒剤を得た。Control preparation 5 Cartap hydrochloride bulk 4 parts, methyl silicone oil 0.
Granules were obtained in the same manner as in Example 1 using 5 parts, phosphoric acid 0.6 parts, and 94.9 parts of river sand having a particle size of 800 to 600 μm.
トビイロウンカに対する効力試験方法 アクリル製大型温室内のベッド（1m×1m）に移植され
たイネ（品種：日本晴，薬剤処理時の生育ステージ：最
高分げつ期，栽植密度:20株／m2）に薬剤処理22日前
（実験１）及び〜29日前（実験２）にトビイロウンカの
成熟雌成虫24頭〜30頭を５〜６日間放して産卵させその
次世代の幼虫主体の虫を対象として前記の各薬剤の所定
量をイネ体の上から均一に手蒔した。Bed efficacy testing method in acrylic large greenhouse for brown planthopper (1 m × 1 m) in transplanted rice (cultivar: Nipponbare, drug treatment during growth stage: maximum tillering stage, planting density: 20 strains / m 2) to Twenty-four to thirty days after 24 to 30 adult female adult female brown planthoppers were laid eggs for 22 days before (Experiment 1) and ~ 29 days before (Experiment 2) treatment with the chemicals, each of the above-mentioned larval-mainly insects A predetermined amount of the drug was uniformly sowed from above the rice body.
薬剤処理前、処理１日後および処理３日後に各ベッド
の中心部の４株について生存虫数を調べ、下式により補
正密度指数を求め、平均補正密度指数により薬効を評価
した。Before, 1 day after, and 3 days after treatment, the number of surviving insects was examined for the four strains at the center of each bed, the corrected density index was determined by the following formula, and the drug efficacy was evaluated by the average corrected density index.
補正密度指数＝100×（Xi/Xo）／（Ci/Co）：ただ
し、Xi,Xoは各々処理１日後及び処理前の各処理区の生
存虫数,Ci,Coは各々処理ｉ日後及び処理前の無処理区の
生存虫数を表す。補正密度指数100は、薬剤の効果が認
められないことを示す。Corrected density index = 100 × (Xi / Xo) / (Ci / Co), where Xi and Xo are the number of surviving insects in each treatment group one day after and before treatment, respectively, and Ci and Co are i days after treatment and treatment respectively. The number of surviving insects in the untreated plot is shown. A corrected density index of 100 indicates no effect of the drug.
発明の効果 本発明の水浮遊性固状農薬製剤は、水面施用した際に
水に浮くとともに、株元に凝集する性質を有するため、
より効率的に、株元付近の農薬活性物質の濃度が高ま
り、ウンカ，紋枯病等に対する株元防除の点ですぐれて
いる。 Effect of the Invention The water-floating solid pesticide formulation of the present invention floats on water when applied to the surface of the water, and has a property of aggregating at the root of the strain,
More efficiently, the concentration of the pesticide active substance in the vicinity of the plant base is increased, and the plant base is excellent in controlling plant bases against planthoppers, sheath blight and the like.
Claims (9)
キレンシリコーンを配合してなる水浮遊性固状製剤An aqueous floating solid preparation comprising a polyoxyalkylene silicone mixed with an agricultural chemical base and a solid carrier.
キシアルキレンシリコーンを、約0.1〜15重量部配合し
てなる請求項１記載の製剤2. The preparation according to claim 1, wherein the polyoxyalkylene silicone is blended in an amount of about 0.1 to 15 parts by weight based on 100 parts by weight of the whole preparation.
Ｈで表されるポリオキシアルキレン基で置換された化合
物（式中、l,mは０または１以上の整数を、ｎは１以上
の整数を、Ａは炭素数１〜８の分枝していてもよいアル
キレン基を表す）である請求項１記載の製剤4. The polyoxyalkylene silicone of the formula At least one methyl group has the formula of - (CH 2) m -OAO n
A compound substituted with a polyoxyalkylene group represented by H (wherein l and m are 0 or an integer of 1 or more, n is an integer of 1 or more, and A is a C1-8 branched Which represents an alkylene group which may be present).
キシエチレンシリコーンおよび／又はポリオキシプロピ
レンシリコーンである請求項１記載の製剤5. The preparation according to claim 1, wherein the polyoxyalkylene silicone is polyoxyethylene silicone and / or polyoxypropylene silicone.
砂，焼成パーライトおよび軽石から選ばれた一種以上で
ある請求項１記載の製剤6. The preparation according to claim 1, wherein the solid carrier is at least one selected from crushed sand, calcined perlite and pumice having a particle size of about 60 to 600 μm.
１記載の製剤7. The preparation according to claim 1, wherein the pesticidal agent is an insecticide for controlling plant roots.
１記載の製剤8. The preparation according to claim 1, wherein the pesticidal agent is a fungicide for controlling a plant strain.
トリメチレン）ビス（チオカルバメート）塩酸塩である
請求項１記載の製剤9. The preparation according to claim 1, wherein the pesticidal agent is S, S '-(2-dimethylaminotrimethylene) bis (thiocarbamate) hydrochloride.