JP2590028Y2 - Peripheral rubber mating type oil seal - Google Patents
Peripheral rubber mating type oil sealInfo
- Publication number
- JP2590028Y2 JP2590028Y2 JP1993052603U JP5260393U JP2590028Y2 JP 2590028 Y2 JP2590028 Y2 JP 2590028Y2 JP 1993052603 U JP1993052603 U JP 1993052603U JP 5260393 U JP5260393 U JP 5260393U JP 2590028 Y2 JP2590028 Y2 JP 2590028Y2
- Authority
- JP
- Japan
- Prior art keywords
- oil seal
- powder
- rubber
- housing
- outer peripheral
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】[0001]
【産業上の利用分野】本考案は、外周面をハウジングに
嵌合する外周ゴム嵌合型オイルシールに関する。更に詳
述すると、本考案は、抜け止め防止のための表面処理が
施された外周ゴム嵌合型オイルシールに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an oil seal having an outer peripheral surface fitted into a housing. More specifically, the present invention relates to an outer peripheral rubber-fitted oil seal that has been subjected to a surface treatment for preventing it from coming off.
【0002】[0002]
【従来の技術】一般に外周ゴム嵌合型と呼ばれるオイル
シールは、金属環の外周部をゴム材料で覆い、このゴム
材料の外周部分をハウジングに嵌合させて使用されるオ
イルシールであり、例えば図2に示すようなばね入りち
りよけ付き外周ゴムオイルシールやばね入り外周ゴムオ
イルシール等が例に挙げられる。図示の外周ゴムオイル
シールの場合、金属環1を覆うゴム材料2によってちり
よけリップ3とシール用リップ4とが構成され、ガータ
ースプリング5が装着されている。そして、シールを保
持するためのハウジング6の内側の空間(ハウジング
穴)7内に所要の嵌合代を以て圧入させることによって
嵌合力(抜け出しに要する力)を発現させ、ハウジング
6から抜け出さないようにすると共にハウジング6との
嵌合面・外周ゴム表面8の密封性を確保している。した
がって、ハウジング6に対するある程度の嵌合力を得る
ことが必要となる。2. Description of the Related Art An oil seal generally called an outer peripheral rubber fitting type is an oil seal which is used by covering an outer peripheral portion of a metal ring with a rubber material and fitting an outer peripheral portion of the rubber material to a housing. An outer peripheral rubber oil seal with a spring and a spring and an outer peripheral rubber oil seal with a spring as shown in FIG. 2 are examples. In the case of the illustrated outer peripheral rubber oil seal, a dust lip 3 and a sealing lip 4 are formed by a rubber material 2 covering the metal ring 1, and a garter spring 5 is mounted. Then, a fitting force (force required for disengagement) is developed by press-fitting a space (housing hole) 7 inside the housing 6 for holding the seal with a required fitting margin so that the housing 6 does not come off. In addition, the sealing performance of the fitting surface and the outer peripheral rubber surface 8 with the housing 6 is ensured. Therefore, it is necessary to obtain a certain fitting force with respect to the housing 6.
【0003】従来、このような外周ゴム嵌合型オイルシ
ールにおいて嵌合力を高める方策としては、例えばオイ
ルシールの外径寸法を変えてハウジングとの締め代を高
める方法やゴム材質としてヤング率の高い材料を使用す
ること等が、一般に行われている。Conventionally, as a method of increasing the fitting force in such an outer peripheral rubber fitting type oil seal, for example, a method of changing the outer diameter of the oil seal to increase the interference with the housing or a rubber material having a high Young's modulus is used. It is common to use materials and the like.
【0004】[0004]
【発明が解決しようとする課題】しかしながら、従来の
外周ゴム嵌合型オイルシールの場合、ハウジングに嵌合
した後に80℃〜150℃に加温されると、摩擦係数が
小さくなって嵌合力が著しく低下し、ついにはオイルシ
ールがハウジングから脱落するという問題を時として起
こす。また常温の状態であっても、ハウジング嵌合面に
オイルやグリス等が付着すると、オイルシールがハウジ
ングから抜け外れるという問題が生じる危険がある。However, in the case of a conventional oil seal of the outer peripheral rubber fitting type, when the oil seal is heated to 80 ° C. to 150 ° C. after being fitted to the housing, the friction coefficient becomes small and the fitting force is reduced. This can sometimes cause a significant drop, eventually causing the oil seal to fall out of the housing. Further, even when the housing is at room temperature, if oil, grease, or the like adheres to the housing fitting surface, there is a danger that a problem that the oil seal comes off the housing may occur.
【0005】このことについて本考案者等が種々研究し
た結果、これはハウジングと嵌合している外周ゴム表面
にゴム組成物中のワックス等が析出(ブルーミング)
し、それが80℃〜150℃に雰囲気温度が加温された
ときに溶融し液体に変化して摩擦係数を低下させること
を知見するに至った。また、オイルシールはハウジング
に圧入される際に符号9で示されるように部分的にゴム
2がハウジング6の外や穴の縁にはみ出て絶えずゴム2
が抜ける方向に力がかかっている。このため、使用雰囲
気温度が上がって摩擦係数が低下することによって嵌合
力(抜出力)が低下したとき、あるいはハウジング嵌合
面にグリス等が付着したとき、弾性変形していたゴムの
復元力の抜出方向の力に負けてオイルシールが脱落す
る。The inventors of the present invention have conducted various studies on this fact. As a result, it has been found that wax and the like in the rubber composition precipitate on the outer peripheral rubber surface fitted with the housing (blooming).
However, it has been found that when the ambient temperature is heated to 80 ° C. to 150 ° C., it melts and changes into a liquid to lower the friction coefficient. Further, when the oil seal is press-fitted into the housing, the rubber 2 partially protrudes outside the housing 6 or on the edge of the hole as indicated by reference numeral 9 and continuously.
The force is applied in the direction that comes out. For this reason, when the fitting temperature (extraction force) is reduced due to a decrease in the friction coefficient due to a rise in the use atmosphere temperature, or when grease or the like adheres to the housing fitting surface, the restoring force of the elastically deformed rubber is reduced. The oil seal comes off due to the force in the pull-out direction.
【0006】本考案は、使用環境温度が上がっても、ま
たハウジング嵌合面にグリス等が付着しても抜け外れる
ことのない外周ゴム嵌合型オイルシールを提供すること
を目的とする。SUMMARY OF THE INVENTION It is an object of the present invention to provide an outer rubber-fitted oil seal which does not come off even if the temperature of the operating environment rises or grease adheres to the housing fitting surface.
【0007】[0007]
【課題を解決するための手段】かかる目的を達成するた
め、本考案の外周ゴム嵌合型オイルシールは、融点が1
60℃以上の粉体を液状基材に分散させてオイルシール
の外周面に塗布するようにしている。ここで、粉体は、
ゴムとハウジングとの間に挟まれた力では容易には破壊
されない強度を有すること、また外周ゴム表面に付着し
たオイルやグリスによって容易には変質・弱体化しない
化学的安定性が要求される。そのため、粉体としては無
機質粉体が望ましく、例えばタルク、マグネシア、シリ
カ、クレーなどの使用が可能であり、これらの1種また
は2種以上の組み合わせ配合で用いても構わない。SUMMARY OF THE INVENTION In order to achieve the above object, the outer peripheral rubber fitting type oil seal of the present invention has a melting point of 1 point.
A powder having a temperature of 60 ° C. or higher is dispersed in a liquid base material and applied to the outer peripheral surface of the oil seal. Where the powder is
It is required to have a strength that is not easily broken by a force sandwiched between the rubber and the housing, and a chemical stability that is not easily deteriorated or deteriorated by oil or grease attached to the outer peripheral rubber surface. Therefore, inorganic powders are desirable as the powder, and for example, talc, magnesia, silica, clay and the like can be used, and one or a combination of two or more of them may be used.
【0008】また、粉体は、その融点が160℃以上で
あることを要する。このように160℃以上とする理由
は、オイルシールの一般的な使用環境で考えられる加温
上限の150℃までは固体から液体にならないようにす
るためである。[0008] The powder must have a melting point of 160 ° C or higher. The reason why the temperature is set to 160 ° C. or higher is to prevent the liquid from changing from a solid to a liquid up to a heating upper limit of 150 ° C. which is considered in a general use environment of an oil seal.
【0009】また、粉体は、その平均粒子径が0.01
μmを越え10μm未満であることが好ましい。粉体の
粒径が0.01μm以下であると、ゴム表面に介在する
液膜の厚みと同等以下となり、粉体による嵌合力を発揮
できないからである。また、10μm以上であると、粉
体がオイルシールのリップに噛み込んだときにリップが
破損する危険があるからである。The powder has an average particle size of 0.01.
It is preferable that the thickness be more than μm and less than 10 μm. When the particle size of the powder is 0.01 μm or less, the thickness becomes equal to or less than the thickness of the liquid film interposed on the rubber surface, and the fitting force by the powder cannot be exhibited. If the thickness is 10 μm or more, there is a risk that the lip may be broken when the powder bites into the lip of the oil seal.
【0010】一方、液状基材は、粉体を含有した塗布剤
として無機質粉体を均一に分散できるものであることが
望ましい。また、液状基材は、オイルシールに塗布した
後、乾燥されるものであることが作業性を良くするため
望ましい。この乾燥は、好ましくは常温で、比較的短時
間、例えば最大でも3日間程度で乾燥し被膜を完成され
るものが望ましい。このような液状基材としては、例え
ば揮発性を有ししばしば防錆剤として用いられる乾性油
などの使用が可能である。On the other hand, the liquid base material is desirably a material capable of uniformly dispersing the inorganic powder as a coating agent containing the powder. In addition, it is desirable that the liquid base material be dried after being applied to the oil seal in order to improve workability. This drying is preferably performed at room temperature for a relatively short time, for example, at most about 3 days to complete the coating. As such a liquid base material, for example, a drying oil which has volatility and is often used as a rust inhibitor can be used.
【0011】また、粉体の液状基材への配合量は、液状
基材に対し40重量%以上80重量%以下であることが
好ましい。粉体の液状基材への配合量を40重量%未満
とすると、粉体量が少ないため、粉体による十分な嵌合
力を得ることができないからであり、80重量%を越え
ると液状基材の流動特性が得られず、塗布作業が極めて
悪くなるからである。The amount of the powder mixed with the liquid substrate is preferably from 40% by weight to 80% by weight based on the liquid substrate. If the amount of the powder mixed with the liquid base material is less than 40% by weight, the amount of the powder is small, so that a sufficient fitting force by the powder cannot be obtained. Is not obtained, and the coating operation becomes extremely poor.
【0012】[0012]
【作用】したがって、図1に示すように、ゴム2の外周
表面において液状基材10に含まれる粉体11が緻密に
分散されており、オイルシールをハウジング6に装着す
ると、粉体11がゴム2とハウジング6との間に介在さ
れる。オイルシールの使用雰囲気が80℃〜150℃に
加温されることによって、ゴム2表面に析出したワック
ス等が溶融しゴム2表面に液膜12を形成しても、粉体
11だけがその液膜12から突出してハウジング6と接
しており、外周ゴム表面・嵌合面の摩擦力を上げる。ま
た、常温においても、ハウジング嵌合面にグリス等が付
着しても、粉体11とハウジング6とが接して、摩擦力
を上げる。Therefore, as shown in FIG. 1, the powder 11 contained in the liquid base material 10 is finely dispersed on the outer peripheral surface of the rubber 2, and when the oil seal is mounted on the housing 6, the powder 11 is 2 and the housing 6. When the working atmosphere of the oil seal is heated to 80 ° C. to 150 ° C., even if wax or the like deposited on the surface of the rubber 2 is melted and a liquid film 12 is formed on the surface of the rubber 2, only the powder 11 It protrudes from the membrane 12 and is in contact with the housing 6 to increase the frictional force between the outer peripheral rubber surface and the fitting surface. Further, even at normal temperature, even if grease or the like adheres to the housing fitting surface, the powder 11 and the housing 6 come into contact with each other and increase the frictional force.
【0013】[0013]
【実施例】以下、本考案の構成を実施例に基づいて詳細
に説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The configuration of the present invention will be described below in detail based on embodiments.
【0014】[実施例1] 粉体としてタルク(日本タルク(株)製;商品名 ミク
ロエースL−2)、また液状基材として防錆油(日本グ
リース(株)製;商品名 ラスファイター)を用いて、
この防錆油へ20重量%のタルクを配合した。このタル
クを含有した防錆油をアクリルゴム製の外周ゴム嵌合型
オイルシールの外周面に塗布し、常温にて乾燥させた。[Example 1] Talc (manufactured by Nippon Talc Co., Ltd., trade name: Micro Ace L-2) as a powder, and rust preventive oil (manufactured by Nippon Grease Co., Ltd., trade name: Las Fighter) as a liquid base material. Using,
20% by weight of talc was added to the rust preventive oil. The rust-preventive oil containing this talc was applied to the outer peripheral surface of an acrylic rubber outer peripheral rubber fitting type oil seal, and dried at room temperature.
【0015】[実施例2] 粉体および液状基材として実施例1と同じタルクおよび
防錆油を用いているが、本実施例では防錆油に40重量
%のタルクを配合した。他は実施例1と同じである。Example 2 The same talc and rust-preventive oil as in Example 1 were used as the powder and the liquid base material, but in this example, 40% by weight of talc was mixed with the rust-preventive oil. Others are the same as the first embodiment.
【0016】[実施例3] 防錆油に60重量%のタルクを配合した。他は実施例1
と同じである。Example 3 Rust-preventing oil was mixed with 60% by weight of talc. Others are Example 1.
Is the same as
【0017】[実施例4] 防錆油に80重量%のタルクを配合した。他は実施例1
と同じである。Example 4 80% by weight of talc was mixed with rust preventive oil. Others are Example 1.
Is the same as
【0018】[比較例 従来品] 本考案のような無機質粉体を含有した液状基材を塗布し
ていないアクリルゴム製の外周ゴム嵌合型オイルシール
である。[Comparative Example Conventional Product] An outer rubber-fitting oil seal made of acrylic rubber which is not coated with a liquid base material containing inorganic powder as in the present invention.
【0019】以上のようにして得られた実施例1〜4お
よび比較例の外周ゴム嵌合型オイルシールとを常温下で
ハウジングに圧入し、120℃雰囲気下でオイルシール
がハウジングから抜け出るのに必要な荷重(嵌合力)を
測定した。その実験結果を表1に示す。The outer peripheral rubber-fitting oil seals of Examples 1 to 4 and Comparative Example obtained as described above were pressed into the housing at room temperature, and the oil seals came out of the housing at 120 ° C. in an atmosphere. The required load (fitting force) was measured. Table 1 shows the experimental results.
【0020】[0020]
【表1】 実施例1 実施例2 実施例3 実施例4 比較例 無機粉体量(wt/%) 20 40 60 80 0 抜出荷重(kgf) 5 15 20 20 0 判定 やや劣る 良好 良好 良好 不良Table 1 Example 1 Example 2 Example 3 Example 4 Comparative Example Inorganic powder amount (wt /%) 20 40 60 80 0 Extraction load (kgf) 5 15 20 20 0 Judgment Somewhat poor Good Good Good Bad
【0021】この実験の結果、無機質粉体を含有する液
状基材を塗布してしないオイルシール(比較例)は、ゴ
ム表面に析出したワックスが120℃雰囲気温度下で溶
融して液体化して直接ハウジングに接触するので、摩擦
係数が低下し、容易に抜け出した。一方、無機粉体を含
有した液状基材をオイルシール表面に塗布した実施例
3,4は、20kgfの引出荷重を必要とし、十分な嵌
合力を有していると評価できた。実施例2は、15kg
fの引出荷重でハウジングから抜け出たが、これも十分
な嵌合力を有していると評価できた。実施例1は5kg
fの引出荷重でハウジングから抜け出たが、これによっ
てタルクの防錆油への配合量が20重量%と比較的少な
いと、摩擦力を上げる効果が少なく、十分な嵌合力を得
ることができないことが解った。As a result of this experiment, an oil seal (comparative example) in which a liquid base material containing an inorganic powder was not applied was directly melted and liquefied at 120 ° C. under an ambient temperature of 120 ° C. Because it came into contact with the housing, the coefficient of friction was reduced and it slipped out easily. On the other hand, Examples 3 and 4, in which the liquid base material containing the inorganic powder was applied to the surface of the oil seal, required a pull-out load of 20 kgf and could be evaluated as having a sufficient fitting force. Example 2 is 15 kg
Although it came out of the housing with a pulling load of f, it could be evaluated that this also had a sufficient fitting force. Example 1 is 5 kg
When the talc was added to the rust preventive oil at a relatively small amount of 20% by weight, the frictional force was not effectively increased, and a sufficient mating force could not be obtained. I understand.
【0022】[0022]
【考案の効果】以上の説明より明らかなように、本考案
の外周ゴム嵌合型オイルシールは、融点が160゜以上
の粉体を液状基材に分散させてオイルシールの外周面に
塗布しているので、粉体がゴムとハウジングとの間に介
在され、外周オイルシールの使用雰囲気によってゴム表
面に析出したワックス等が溶融し液膜を形成しても、ま
た、常温においてハウジング嵌合面にグリス等が付着し
ても粉体だけがその液膜から突出してハウジングと接し
て外周ゴム表面・嵌合面の摩擦力を維持する。したがっ
て、使用環境温度が上がってもオイルシールがハウジン
グから抜け外れることがない。特に、粉体の平均粒子径
が0.01μmを越えかつ10μm未満とする場合に
は、リップを破損することがないし、粉体による嵌合力
の維持を確保できる。また、粉体の液体の液状基材への
分散量を40重量%以上80重量%以下とする場合に
は、粉体をゴム表面にむらなく均一に塗布できるし塗布
作業も容易である。As is apparent from the above description, the outer peripheral rubber-fitting type oil seal of the present invention disperses powder having a melting point of 160 ° or more in a liquid base material and applies it to the outer peripheral surface of the oil seal. Therefore, even if the powder is interposed between the rubber and the housing, and wax or the like deposited on the rubber surface is melted by the use atmosphere of the outer peripheral oil seal to form a liquid film, the housing mating surface can be formed at room temperature. Even if grease or the like adheres, only the powder protrudes from the liquid film and comes into contact with the housing to maintain the frictional force between the outer peripheral rubber surface and the fitting surface. Therefore, the oil seal does not come off from the housing even when the operating environment temperature rises. In particular, when the average particle diameter of the powder is more than 0.01 μm and less than 10 μm, the lip is not broken, and the maintenance of the fitting force by the powder can be ensured. Further, when the amount of dispersion of the powder liquid in the liquid base material is 40% by weight or more and 80% by weight or less, the powder can be evenly and uniformly applied to the rubber surface and the coating operation is easy.
【図1】本考案の外周ゴム嵌合型オイルシールのハウジ
ングとの嵌合部分の拡大断面図である。FIG. 1 is an enlarged cross-sectional view of a fitting part of a peripheral rubber fitting type oil seal of the present invention with a housing.
【図2】外周ゴム嵌合型オイルシールの一例を示す断面
図である。FIG. 2 is a cross-sectional view showing an example of an outer rubber-fitted oil seal.
2 ゴム 6 ハウジング 10 液状基材 11 粉体 12 液膜 2 Rubber 6 Housing 10 Liquid base material 11 Powder 12 Liquid film
Claims (3)
分散させてオイルシールの外周面に塗布したことを特徴
とする外周ゴム嵌合型オイルシール。1. An outer rubber-fitted oil seal characterized in that powder having a melting point of 160 ° C. or higher is dispersed in a liquid base material and applied to the outer peripheral surface of the oil seal.
越えかつ10μm未満であることを特徴とする請求項1
記載の外周ゴム嵌合型オイルシール。2. The powder according to claim 1, wherein the powder has an average particle diameter of more than 0.01 μm and less than 10 μm.
The outer peripheral rubber fitting type oil seal described in the above.
上80重量%以下含有されていることを特徴とする請求
項1または2記載の外周ゴム嵌合型オイルシール。3. The oil seal according to claim 1, wherein the powder is contained in an amount of 40% by weight or more and 80% by weight or less with respect to the liquid base material.