JP2589829Y2 - Fire resistant wire - Google Patents
Fire resistant wireInfo
- Publication number
- JP2589829Y2 JP2589829Y2 JP1991105952U JP10595291U JP2589829Y2 JP 2589829 Y2 JP2589829 Y2 JP 2589829Y2 JP 1991105952 U JP1991105952 U JP 1991105952U JP 10595291 U JP10595291 U JP 10595291U JP 2589829 Y2 JP2589829 Y2 JP 2589829Y2
- Authority
- JP
- Japan
- Prior art keywords
- fire
- insulating layer
- foamed
- sheath
- heat insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本考案は、耐火電線に係り、特
に、その耐火特性の向上を図った電線に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fire-resistant electric wire, and more particularly to an electric wire whose fire resistance is improved.
【０００２】[0002]
【従来の技術】従来の耐火電線の場合、導体上にマイカ
付きガラステープ、シリコーンワニスやシリコーンゴム
引きガラステープなどの耐火層を施し、その上にポリエ
チレン、ポリオレフィンなどの絶縁層を施した線心を撚
り合わせ、さらに、その上にＰＶＣ、ハロゲンフリー難
燃ポリオレフィンなどのシースを施したものが主流であ
った。2. Description of the Related Art In the case of a conventional fire-resistant electric wire, a core having a conductor provided with a fire-resistant layer such as a glass tape with mica, a silicone varnish or a silicone rubberized glass tape, and an insulating layer such as polyethylene or polyolefin applied thereon. , And further, a sheath made of PVC, halogen-free flame-retardant polyolefin or the like is further provided thereon.
【０００３】これらの耐火電線は、火災時などの高熱下
に曝され、シースおよび絶縁層が分解焼失しても、耐火
層によって電線としての機能を保持するようにしたもの
で、ＪＩＳの火災温度曲線における８４０℃、３０分間
の耐火性能試験には、十分耐え得るものである。[0003] These fire-resistant electric wires are exposed to high heat such as in a fire, and even if the sheath and the insulating layer are decomposed and burned, the fire-resistant layer retains the function as an electric wire. It can withstand a fire performance test at 840 ° C. for 30 minutes in the curve.
【０００４】[0004]
【考案が解決しようとする課題】しかしながら、このよ
うな耐火電線において、石油火災などを考慮すると、さ
らに、高温で、かつより長時間の耐火性能を有する電線
の提供が望まれる。However, in consideration of oil fires and the like in such a fire-resistant wire, it is desired to provide a wire having a higher temperature and a longer-time fire resistance performance.
【０００５】[0005]
【課題を解決するための手段】本考案は、このような従
来の問題点に鑑みてなされたもので、その特徴とする点
は、導体上に耐火層を施し、その上に絶縁層を施した線
心とシースとの間に、シリコーン樹脂又はシリコーンゴ
ムに無機充填剤、有機化合物系の発泡剤を配合させて発
泡させた発泡シリコーン重合体組成物からなる断熱層を
設け、高熱下で前記断熱層がセラミック化発泡断熱層と
なる耐火電線にある。SUMMARY OF THE INVENTION The present invention has been made in view of such conventional problems, and is characterized in that a fireproof layer is provided on a conductor and an insulating layer is provided thereon. Between the core and the sheath
Blended with inorganic fillers and organic compound foaming agents
Providing a heat insulating layer made of a foamed silicone polymer composition , wherein the heat insulating layer under high heat and a ceramicized foam heat insulating layer
Become a refractory electric wire.
【０００６】[0006]
【作用】本考案では、上記発泡シリコーン重合体組成物
が、火災時などの高温時（８４０℃以上）において、セ
ラミック化してそのままの形状（発泡された形状）を保
って発泡セラミック断熱層を形成するため、電線内部の
温度上昇が効果的に防止され、より良好な耐火特性が得
られる。According to the present invention, the foamed silicone polymer composition is formed into a ceramic material at the time of high temperature (840 ° C. or higher) such as in a fire, thereby forming a foamed ceramic heat insulating layer while maintaining the shape (foamed shape). Therefore, a rise in the temperature inside the electric wire is effectively prevented, and better fire resistance is obtained.
【０００７】[0007]
【実施例】図１〜図３は、本考案に係る各耐火電線の実
施例を示したものである。図において、１は導体であっ
て、図１では単一線心の場合、図２では平行線心の場
合、図３では撚り合わせ線心の場合をそれぞれ示す。２
は上記導体１上に施されたマイカ付きガラステープ、シ
リコーンワニスやシリコーンゴム引きガラステープなど
からなる耐火層、３はこの耐火層２上に被覆されたポリ
エチレン、ポリオレフィンなどからなる絶縁層、４はこ
のように絶縁層３が施された線心の直上、または線心の
直上および線心間の間隙、さらには線心撚り合わせ上に
施された、高熱下でセラミック化発泡断熱層となる発泡
シリコーン重合体組成物からなる断熱層、５はこの断熱
層４上に施されたＰＶＣ、ハロゲンフリー難燃ポリオレ
フィンなどからなるシースである。1 to 3 show an embodiment of each refractory wire according to the present invention. In FIG. 1, reference numeral 1 denotes a conductor, FIG. 1 shows a single core, FIG. 2 shows a parallel core, and FIG. 3 shows a twisted core. 2
Is a fireproof layer made of a glass tape with mica, a silicone varnish or a silicone rubberized glass tape applied on the conductor 1, 3 is an insulating layer made of polyethylene, polyolefin or the like coated on the fireproof layer 2, 4 is Foaming to be a ceramized foam heat insulating layer under high heat, just above the wire core on which the insulating layer 3 is provided, or just above the wire core and the gap between the wire cores, and further on the wire core twisting A heat insulating layer 5 made of a silicone polymer composition is a sheath made of PVC, a halogen-free flame-retardant polyolefin, or the like provided on the heat insulating layer 4.
【０００８】上記高熱下でセラミック化する発泡シリコ
ーン重合体組成物としては、例えばジメチルシリーコ
ン、メチルビニルシリコーン、メチルフェニルシリコー
ンなどのシリコーン樹脂、シリコーンゴムに無機充填
剤、発泡剤などを配合したものが挙げられる。Examples of the foamed silicone polymer composition which can be ceramicized under high heat include, for example, silicone resins such as dimethylsilicon, methylvinylsilicone, methylphenylsilicone and the like, and silicone rubber mixed with an inorganic filler and a foaming agent. Is mentioned.
【０００９】この組成物には、他の添加剤として、例え
ば耐熱向上用の添加剤、加硫剤などを必要に応じて配合
することが可能である。また、上記無機充填剤として
は、ＳｉＯ２、Ａｌ２Ｏ３、タルク、クレー、アルカリ
金属酸化物、雲母属鉱物例えばイライト、セリサイト、
セラドナイトなどが挙げられる。上記アルカリ金属酸化
物を適当量配合すると、シリコーン重合体の加熱によっ
て生成するＳｉＯ２を主成分とするセラミックスの生成
温度を大幅に低下させることが可能である。また、上記
発泡剤としては、有機化合物系の発泡剤であるアゾ系発
泡剤、ニトロソ系発泡剤、スルホヒドラジド系発泡剤な
どが挙げられる。[0009] Other additives, such as an additive for improving heat resistance, a vulcanizing agent, and the like, can be added to the composition as required. Further, as the inorganic filler, SiO 2 , Al 2 O 3 , talc, clay, alkali metal oxide, mica minerals such as illite, sericite,
Celadonite and the like. When an appropriate amount of the above-mentioned alkali metal oxide is blended, it is possible to drastically lower the formation temperature of ceramics mainly composed of SiO 2 generated by heating the silicone polymer. Examples of the foaming agent include azo foaming agents, nitroso foaming agents, and sulfohydrazide foaming agents, which are organic compound foaming agents.
【００１０】このような構成からなる本考案では、上述
したように、火災時などの高温時において、発泡した形
で施された発泡シリコーン重合体組成物がセラミック化
してそのままの形状を保って発泡セラミック断熱層を形
成するため、電線内部の温度上昇が効果的に防止され、
より良好な耐火特性が得られる。[0010] In the present invention having such a configuration, as described above, at the time of high temperature such as a fire, the foamed shape
In order to form a foamed ceramic heat insulating layer while maintaining the shape of the foamed silicone polymer composition which has been ceramicized by being ceramicized, the temperature rise inside the electric wire is effectively prevented,
Better fire resistance is obtained.
【００１１】この断熱層は、発泡による多孔質化によ
り、極めて良好な断熱性能を発揮する。そして、さら
に、この発泡多孔質化と上記セラミック化との相乗効果
により、断熱層自体の耐熱性もより高くなるため、火災
などの高温によっても焼失することはない。これに対し
て、例えば導体の耐火層外側に単に発泡性防火塗料を塗
布して炭化発泡被膜を形成した場合には、セラミックス
と異なり炭化物であるため耐火性が不十分で、火災など
際には、燃えて焼失してしまう。つまり、本考案では、
発泡による多孔質化とセラミック化が不可欠である。This heat insulating layer exhibits extremely good heat insulating performance by being made porous by foaming. Further, the heat resistance of the heat insulating layer itself is further increased due to the synergistic effect of the formation of the foamed porous material and the above-mentioned ceramic formation, so that the heat insulating layer does not burn out even at a high temperature such as a fire. On the other hand, for example, if a foamed fire-resistant coating is formed by simply applying a foaming fire-resistant paint to the outside of the fireproof layer of the conductor, the fire resistance is insufficient because it is a carbide unlike ceramics, and in the case of fire, etc. Burns and burns. In other words, in the present invention,
Porosity and ceramic formation by foaming are indispensable.
【００１２】[0012]
【考案の効果】このように本考案の耐火電線では、導体
上に従来ど同様耐火層を施すと同時に火災発生時などの
高熱下でセラミック化する発泡シリコーン重合体組成物
からなる断熱層を施してあるため、極めて良好な断熱機
能が果たされ、電線内部の温度上昇は効果的に防止さ
れ、従来の耐火電線に比較して、石油火災などのような
より高温で、かつ長時間の加熱状態が続く苛酷な条件に
も耐えることができる、優れた耐火性能が得られる。As described above, in the fireproof electric wire of the present invention, a fireproof layer is formed on the conductor in the same manner as before, and at the same time, a heat insulating layer made of a foamed silicone polymer composition which is ceramicized under high heat at the time of fire or the like is provided. As a result, an extremely good heat insulation function is achieved, the temperature inside the electric wire is effectively prevented from rising, and compared to conventional fire-resistant electric wires, heating is performed at higher temperatures such as oil fires and for a longer time. Excellent fire resistance that can withstand severe conditions where conditions continue.
【図１】本考案に係る耐火電線の一実施例を示した断面
図である。FIG. 1 is a cross-sectional view showing an embodiment of a fire-resistant wire according to the present invention.
【図２】本考案に係る耐火電線の他の実施例を示した断
面図である。FIG. 2 is a cross-sectional view illustrating another embodiment of the refractory wire according to the present invention.
【図３】本考案に係る耐火電線のさらに他の実施例を示
した断面図である。FIG. 3 is a cross-sectional view illustrating a fire-resistant wire according to another embodiment of the present invention.
１ 導体、 ２ 耐火層、 ３ 絶縁層、 ４ 発泡シリコーン重合体組成物からなる
断熱層、 ５ シース、1 conductor, 2 refractory layer, 3 insulating layer, 4 heat insulating layer made of foamed silicone polymer composition, 5 sheath,
───────────────────────────────────────────────────── フロントページの続き (72)考案者 丹羽 利夫 東京都江東区木場１丁目５番１号 藤倉 電線株式会社内 (56)参考文献 特開 昭63−53807（ＪＰ，Ａ) 特開 昭62−169834（ＪＰ，Ａ) (58)調査した分野(Int.Cl.6，ＤＢ名) H01B 7/34 H01B 3/46──────────────────────────────────────────────────続 き Continuation of the front page (72) Inventor Toshio Niwa 1-5-1 Kiba, Koto-ku, Tokyo Fujikura Electric Wire Co., Ltd. (56) References JP-A-63-53807 (JP, A) JP-A-62 −169834 (JP, A) (58) Field surveyed (Int. Cl. 6 , DB name) H01B 7/34 H01B 3/46
Claims (1)
を施した線心とシースとの間に、シリコーン樹脂又はシ
リコーンゴムに無機充填剤、有機化合物系の発泡剤を配
合させて発泡させた発泡シリコーン重合体組成物からな
る断熱層を設け、高熱下で前記断熱層がセラミック化発
泡断熱層となることを特徴とする耐火電線。1. A silicone resin or sheath is provided between a sheath and a sheath having a refractory layer provided on a conductor and an insulating layer provided thereon.
Inorganic filler and organic compound-based foaming agent
A heat insulating layer made of a foamed silicone polymer composition which is foamed by mixing is provided .
A fire-resistant electric wire characterized by being a foam insulation layer .