JP2577667Y2 - Radiation shielding mat - Google Patents
Radiation shielding matInfo
- Publication number
- JP2577667Y2 JP2577667Y2 JP1992001168U JP116892U JP2577667Y2 JP 2577667 Y2 JP2577667 Y2 JP 2577667Y2 JP 1992001168 U JP1992001168 U JP 1992001168U JP 116892 U JP116892 U JP 116892U JP 2577667 Y2 JP2577667 Y2 JP 2577667Y2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- radiation shielding
- shielding mat
- coated base
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本考案は、鉛繊維不織布を主材料
として用いた放射線遮蔽用マットに関するものであり、
さらに詳しくは表面平坦性および防汚性が良好で、とく
に除染性がすぐれ、清掃作業をきわめて容易に行うこと
ができ、しかも装着性および取扱性がすぐれた放射線遮
蔽用マットに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a radiation shielding mat using a lead fiber nonwoven fabric as a main material.
More specifically, the present invention relates to a radiation shielding mat which has excellent surface flatness and antifouling property, has particularly excellent decontamination properties, can perform cleaning work extremely easily, and has excellent wearability and handleability.
【０００２】[0002]
【従来の技術】原子力発電所などの放射線を取扱う現場
においては、γ線やＸ線などの放射線から作業者を保護
するために、各種の放射線遮蔽用材料が使用されてい
る。2. Description of the Related Art At a site where radiation is handled, such as a nuclear power plant, various radiation shielding materials are used to protect workers from radiation such as γ-rays and X-rays.
【０００３】従来、このような放射線遮蔽用材料として
は、鉛繊維不織布や鉛板などを樹脂コートした基布で被
覆したものが主流を占めており、例えば鉛繊維不織布に
対して樹脂コート基布を被せて、この樹脂コート基布の
端部をキルティング状に縫合したもの（実開昭６３−１
０５９００号公報）および前記樹脂コート基布の端部を
高周波ウェルダーで熱接着したもの（実開昭６３−７２
５９８号公報）などの具体例が知られている。Conventionally, as such a radiation shielding material, a lead fiber non-woven fabric or a lead plate coated with a resin-coated base fabric has predominantly been used. And sewn the end portion of the resin-coated base fabric in a quilted shape (Japanese Utility Model Application Laid-Open No. 63-1).
No. 05900 ) and those obtained by thermally bonding the ends of the resin-coated base cloth with a high-frequency welder (Japanese Utility Model Application Laid-Open No. 63-72).
598) is known.
【０００４】しかるに、前者においては表面に縫合部を
有することから、前記縫合部を樹脂により目止めする必
要があるため、目止め作業に手間がかかりコストアップ
になるばかりか、目止め部が凹凸状になり、その表面に
付着した残留放射線物質などの清掃作業に長時間を要す
るという問題があった。[0004] However, in the former, since the surface has a seam, it is necessary to seal the seam with a resin. And it takes a long time to clean residual radioactive substances and the like adhering to the surface.
【０００５】また、後者においては、樹脂コート基布の
端部の接着力強化を目的として、接合部に凹凸状溝部を
形成する必要があるが、この溝部の存在によって生ずる
清掃作業の困難性を解決するために、樹脂を注入して平
坦化する作業が必要となり、コストアップを招く。さら
に、この放射線遮蔽用マットの四方の端部に存在する前
記樹脂コート基布の熱接着端面には鉛材料が存在せず、
放射線遮蔽用マットの主体部分に比較して厚みが薄い上
に、通常約２０mm程度の幅を有している。したがって、
図１０および図１１に示したように、このような放射線
遮蔽用マット１を配管に巻き付けたり、機器回りに複数
並列に吊り下げたりして実用に供する場合には、前記放
射線遮蔽効果の小さい接合端部２を、主体部３である鉛
材料を有する面に重ねて配置する必要があり、装着面が
凹凸状になって、その外観に劣るばかりか、装着性およ
び取扱性にも劣るという問題があった。In the latter case, it is necessary to form a concave-convex groove at the joint for the purpose of strengthening the adhesive force at the end of the resin-coated base cloth. In order to solve the problem, an operation of injecting a resin and flattening is required, which leads to an increase in cost. Furthermore, there is no lead material on the heat-bonded end face of the resin-coated base cloth present at the four ends of the radiation shielding mat,
It is thinner than the main part of the radiation shielding mat and usually has a width of about 20 mm. Therefore,
As shown in FIGS. 10 and 11, when such a radiation shielding mat 1 is wound around a pipe or suspended in parallel around a plurality of devices to be put to practical use, the joint having a small radiation shielding effect is used. It is necessary to arrange the end portion 2 so as to overlap the surface having the lead material as the main body portion 3, and the mounting surface becomes uneven, so that not only the appearance is inferior, but also the mounting and handling are inferior. was there.
【０００６】そこで本考案者らは、表面平坦性が良好で
清掃作業を容易に行うことができ、しかも装着性および
取扱性がすぐれた放射線遮蔽用マットの提供を目的とし
て検討した結果、鉛繊維不織布を主材料とする内部構成
部材の全表面を、樹脂コート基布にて被覆してなる放射
線遮蔽用マットにおいて、前記樹脂コート基布の略中央
部を折り曲げて前記内部構成部材を包み、前記樹脂コー
ト基布の対向する３辺の端部同志を熱接着することによ
り平坦状の接合部を構成した放射線遮蔽用マットが、端
部に縫合部を有さず、表面平滑性にすぐれると共に、清
掃作業を容易に行うことができるばかりか、容易な装着
性および取扱性のもとに、美観にすぐれた装着面を得る
ことができるものであることを見出し、先に実願平３−
６５７８５号として提案した。[0006] The inventors of the present invention have studied for the purpose of providing a radiation shielding mat which has a good surface flatness and can be easily cleaned, and which is excellent in mounting and handling properties. In a radiation shielding mat in which the entire surface of an internal component mainly composed of a nonwoven fabric is coated with a resin-coated base cloth, a substantially central portion of the resin-coated base cloth is bent to wrap the internal component, The radiation-shielding mat, which forms a flat joint by thermally bonding the three opposite ends of the resin-coated base fabric, has no seam at the end, and has excellent surface smoothness. It is found that not only can the cleaning work be performed easily, but also that a mounting surface excellent in aesthetic appearance can be obtained based on easy mounting and handling properties.
No. 65785 .
【０００７】しかるに、その後の検討によれば、上記放
射線遮蔽用マットにおいては、樹脂コート基布に塗布す
る樹脂として、ポリエステル基布の両面に対し、ポリ塩
化ビニル樹脂およびエチレン／酢酸ビニル共重合体など
をコーティングしたものを用いていたことから、これら
コーティングに使用する重合体は、除染性、すなわち表
面に付着した残留放射性物質をウェスなどで除去する際
の除去性において、さらに改良の余地があることが判明
した。However, according to a subsequent study, in the radiation shielding mat, as a resin to be applied to the resin-coated base fabric, a polyvinyl chloride resin and an ethylene / vinyl acetate copolymer are applied to both sides of the polyester base fabric. The polymer used for these coatings has room for further improvement in the decontamination properties, that is, the removability when removing residual radioactive substances attached to the surface with a waste cloth. It turned out to be.
【０００８】すなわち、上記重合体を塗布した樹脂コー
ト基布は、かなりすぐれた除染性を有してはいるが、最
近ではさらに短時間できわめて効率的に除染作業を行う
ことが要求されるようになってきたことから、この要求
性能を満たすにはいまだに除染性を十分満足していると
はいえないのである。That is, although the resin-coated base fabric coated with the polymer has a considerably excellent decontamination property, it has recently been required to perform the decontamination work more efficiently in a shorter time. Therefore, it cannot be said that the decontamination property is still sufficiently satisfied to satisfy the required performance.
【０００９】また、最近では、とくに放射線遮蔽用マッ
トを長期に亘り吊り下げ使用する場合に、高いレベルの
強度安全性が要求されている実状にある。In recent years, a high level of strength safety has been demanded, especially when a radiation shielding mat is used for hanging for a long period of time.
【００１０】[0010]
【考案が解決しようとする課題】本考案は、上述した本
考案者らの提案による放射線遮蔽用マットにおける除染
性を高め、さらには強度安全性をも改良することを目的
として検討を継続した結果、達成されたものである。[Problems to be Solved by the Invention] The present invention has been studied for the purpose of improving the decontamination property of the radiation shielding mat proposed by the inventors of the present invention and also improving the strength safety. The result has been achieved.
【００１１】[0011]
【課題を解決するための手段】上記目的を達成するため
に、本考案の放射線遮蔽用マットは、鉛繊維不織布を主
材料とする内部構成部材の全表面を、樹脂コート基布に
て被覆してなり、かつ前記樹脂コート基布の略中央部を
折り曲げて前記内部構成部材を包み、前記樹脂コート基
布の対向する３辺の端部同志を熱接着することにより平
坦状の接合部を構成した放射線遮蔽用マットにおいて、
前記樹脂コート基布としてポリフッ化ビニリデン樹脂を
被覆した基布を用いたことを特徴とする。Means for Solving the Problems To achieve the above object, the radiation shielding mat of the present invention comprises a resin-coated base cloth covering the entire surface of an internal structural member mainly composed of a lead fiber nonwoven fabric. A flat joint is formed by bending the substantially central portion of the resin-coated base cloth to wrap the internal constituent members and thermally bonding the three opposite ends of the resin-coated base cloth. Radiation shielding mat
The present invention is characterized in that a base cloth coated with polyvinylidene fluoride resin is used as the resin-coated base cloth.
【００１２】さらに、本考案の放射線遮蔽用マットは、
鉛繊維不織布を主材料とする内部構成部材に、金網また
はステンレス薄板を配置したことを特徴とする。Further, the radiation shielding mat according to the present invention includes:
It is characterized in that a wire mesh or a stainless steel thin plate is arranged on an internal constituent member mainly composed of a lead fiber nonwoven fabric.
【００１３】[0013]
【作用】本考案の放射線遮蔽用マットは、樹脂コート基
布の略中央部を折り曲げて前記内部構成部材を包み、前
記樹脂コート基布の対向する３辺の端部同志を熱接着す
ることにより平坦状の接合部を構成したため、端部に縫
合部を有さず、表面平滑性にすぐれると共に、清掃作業
を容易に行うことができる。The radiation shielding mat of the present invention is obtained by bending the substantially central portion of the resin-coated base cloth to wrap the internal structural members, and thermally bonding the three opposite ends of the resin-coated base cloth. Since the flat joint portion is formed, there is no sewn portion at the end portion, the surface is excellent in smoothness, and the cleaning operation can be easily performed.
【００１４】また、本考案の放射線遮蔽用マットを配管
に巻き付けたり、あるいは複数枚並列して使用する際に
は、上記樹脂コート基布の折り曲げ部分と、残る３辺の
接合部のいずれかとを重ね合わすことによって、容易な
装着性および取扱性のもとに、美観にすぐれた装着面を
得ることができ、安全性の面でも有利である。When the radiation shielding mat of the present invention is wound around a pipe or a plurality of the radiation shielding mats are used in parallel, the bent portion of the resin-coated base fabric and one of the remaining three sides are joined. By superimposing, it is possible to obtain an aesthetically pleasing mounting surface with easy mounting and handling properties, which is advantageous in terms of safety.
【００１５】さらにまた、本考案の放射線遮蔽用マット
は、樹脂コート基布としてポリフッ化ビニリデン樹脂を
被覆した基布を用いたため、従来よりも除染性が高めら
れ、防汚性が良好で、清掃作業を一層容易に行うことが
できる。Further, the radiation shielding mat of the present invention uses a base cloth coated with a polyvinylidene fluoride resin as a resin-coated base cloth, so that the decontamination property is improved and the antifouling property is better than before. The cleaning operation can be performed more easily.
【００１６】さらに加えて、本考案の放射線遮蔽用マッ
トは、鉛繊維不織布を主材料とする内部構成部材に、金
網またはステンレス薄板を配置することによって、柔軟
性を大きく損なうことなく、強度が一層高められ、長期
間吊り下げ使用する際の安全性を向上することができ
る。[0016] In addition, the radiation shielding mat of the present invention can further increase the strength without greatly impairing the flexibility by arranging a wire mesh or a stainless steel thin plate on the internal component mainly composed of a lead fiber non-woven fabric. It is possible to improve the safety when used for hanging for a long time.
【００１７】[0017]
【実施例】以下、図面にしたがって、本考案の放射線遮
蔽用マットの実施例について詳細に説明する。BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a perspective view of a radiation shielding mat according to the present invention;
【００１８】図１は本考案の放射線遮蔽用マットの第１
実施例を示す断面図、図２は同じく平面図、図３は同じ
く放射線遮蔽用マットを製造する当初の過程を示す平面
図、図４は本考案の放射線遮蔽用マットの第２実施例を
示す断面図、図５は同じく第３実施例を示す断面図、図
６は放射線遮蔽用マットの第４実施例を示す一部切欠き
平面図、図７は図６を１３ａ側から見た断面図、図８は
同じく１３ｃ側から見た断面図、図９は本考案の放射線
遮蔽用マットを複数枚並列に配置した状況を示す側面図
である。FIG. 1 shows a first embodiment of the radiation shielding mat of the present invention.
FIG. 2 is a plan view showing the embodiment, FIG. 2 is a plan view showing the same, FIG. 3 is a plan view showing an initial process of manufacturing the radiation shielding mat, and FIG. 4 shows a second embodiment of the radiation shielding mat of the present invention. 5 is a sectional view showing a third embodiment of the present invention. FIG. 6 is a partially cutaway plan view showing a fourth embodiment of the radiation shielding mat. FIG. 7 is a sectional view of FIG. FIG. 8 is a cross-sectional view of the same as viewed from the side 13c, and FIG. 9 is a side view showing a state in which a plurality of radiation shielding mats of the present invention are arranged in parallel.
【００１９】図１および図２に示した第１実施例におい
て、本考案の放射線遮蔽用マット１０は、鉛繊維不織布
１１ａを主材料とする内部構成部材１１と、この内部構
成部材１１の全表面を被覆した樹脂コート基布１２と、
この樹脂コート基布１２の対向する３辺の端部同志を熱
接着することにより形成された平坦状の接合部１３ａ、
１３ｂ、１３ｃおよび前記樹脂コート基布１２の折曲げ
部１４から構成されている。In the first embodiment shown in FIGS. 1 and 2, the radiation shielding mat 10 of the present invention comprises an internal component 11 mainly composed of a lead fiber non-woven fabric 11a and the entire surface of the internal component 11. A resin-coated base cloth 12 coated with
Flat joining portions 13a formed by thermally bonding the three opposite ends of the resin-coated base fabric 12;
13b and 13c and the bent portion 14 of the resin-coated base fabric 12.
【００２０】本考案で内部構成部材１１の主材料として
用いる鉛繊維不織布１１ａとは、通常繊維径が０．１〜
０．２mm程度の鉛繊維を分散、積層、不織布状にした
後、軽くプレスしたものであり、すぐれた柔軟性を有す
るものである。The lead fiber nonwoven fabric 11a used as the main material of the internal component member 11 in the present invention usually has a fiber diameter of 0.1 to
After dispersing, laminating, and forming a non-woven fabric, about 0.2 mm of lead fiber is pressed lightly, and has excellent flexibility.
【００２１】上記内部構成部材１１は鉛繊維不織布１１
ａ単独で用いることもできるが、図示したように寸法安
定性を改良するために、その内部に無機または有機繊維
織物、あるいはこれらを厚みが０．５mm以下の鉛板に貼
り合せた芯材１１ｂを配置したものであることが好まし
い。The internal constituent member 11 is a lead fiber nonwoven fabric 11
a can be used alone, but as shown in the figure, in order to improve dimensional stability, an inorganic or organic fiber woven fabric or a core material 11b in which these are bonded to a lead plate having a thickness of 0.5 mm or less. Are preferably arranged.
【００２２】また、内部構成部材１１は、図示したよう
に、好ましくはガラス・ポリエステル・ポリエチレン基
布などの内包材１１ｃで包まれ、さらには縫合部１１ｄ
で固定されている。Further, as shown in the figure, the internal component member 11 is preferably wrapped with an inner wrapping material 11c such as a glass, polyester, or polyethylene base cloth, and further, a suturing portion 11d.
It is fixed at.
【００２３】そして、この内部構成部材１１はその全表
面が樹脂コート基布１２にて被覆されており、放射線遮
蔽用マット１０の４辺の端部の内１辺はこの樹脂コート
基布１２の折曲げ部１４から、また他の３辺は前記樹脂
コート基布１２の端部同志を熱接着してなる平坦状の接
合部１３ａ、１３ｂ、１３ｃからそれぞれなっている。The entire surface of the internal constituent member 11 is covered with a resin-coated base cloth 12, and one of four ends of the radiation shielding mat 10 is covered with the resin-coated base cloth 12. The bent portion 14 and the other three sides are formed of flat joints 13a, 13b, 13c formed by thermally bonding the ends of the resin-coated base fabric 12, respectively.
【００２４】上記樹脂コート基布１２は、ガラス基布、
ポリエステル基布などにポリフッ化ビニリデン樹脂を被
覆したもの、およびポリエステル基布にポリ塩化ビニル
樹脂などを被覆しさらにその上にポリフッ化ビニリデン
樹脂を被覆したものなどが挙げられる。ようするに基布
１２の表面には必ずポリフッ化ビニリデン樹脂が被覆さ
れていることが重要であり、このポリフッ化ビニリデン
樹脂被覆のすぐれた防汚性によって、除染性および清掃
作業性を著しく改良することができる。さらに、基布１
２は防炎対策上難燃性のものが好ましく使用される。The resin-coated base cloth 12 is a glass base cloth,
Examples thereof include a polyester base cloth or the like coated with a polyvinylidene fluoride resin, and a polyester base cloth coated with a polyvinyl chloride resin or the like and further coated with a polyvinylidene fluoride resin. As described above, it is important that the surface of the base cloth 12 is always coated with polyvinylidene fluoride resin, and the excellent antifouling property of the polyvinylidene fluoride resin coating significantly improves the decontamination property and the cleaning workability. Can be. Furthermore, the base cloth 1
2 is preferably flame-retardant in view of flame prevention.
【００２５】なお、図２においては、この放射線遮蔽用
マット１０を例えば吊り下げて装着使用するのに便利な
ように、接合部１３ｂおよび１３ｃの辺にハトメ部１５
を形成しているが、放射線遮蔽用マット１０を吊り下げ
使用しない場合にはこのハトメ部１５を省略することが
できる。In FIG. 2, the eyelets 15 are provided on the sides of the joints 13b and 13c so that the radiation shielding mat 10 can be conveniently used, for example, by hanging it.
The eyelet 15 can be omitted when the radiation shielding mat 10 is not used for hanging.
【００２６】かかる構造からなる放射線遮蔽用マット
は、次のようにして製造することができる。The radiation shielding mat having such a structure can be manufactured as follows.
【００２７】すなわち、図３に示したように、まず樹脂
コート基布１２の略中央部１２ａに沿わせて内部構成部
材１１を載置し、次いで樹脂コート基布１２をその略中
央部１２ａに沿って折り曲げることにより、前記内部構
成部材１１を両面から包み込む。That is, as shown in FIG. 3, first, the internal component member 11 is placed along the substantially central portion 12a of the resin-coated base fabric 12, and then the resin-coated base fabric 12 is placed on the substantially central portion 12a. The internal component 11 is wrapped from both sides by being bent along.
【００２８】そして、前記樹脂コート基布１２の対向す
る３辺の端部同志を熱接着することにより、平坦状の接
合部を１３ａ、１３ｂ、１３ｃを形成する。Then, flat ends 13a, 13b and 13c are formed by thermally bonding the three ends of the resin-coated base fabric 12 facing each other.
【００２９】なお、上記接合部１３ａ、１３ｂ、１３ｃ
を形成するための熱接着法としては、高周波ウェルダー
法および熱板プレス法などが採用できるが、いずれの方
法においても熱接着用加圧治具には凹凸のない平板状の
ものを用いることが重要であり、例えば通常の高周波ウ
ェルダー法で用いられている溝状凹凸表面を有する治具
を用いる場合には、得られる接合面の清掃作業性が劣る
ため好ましくない。The joints 13a, 13b, 13c
As the thermal bonding method for forming the substrate, a high-frequency welding method and a hot plate pressing method can be adopted, but in any method, a flat jig having no unevenness is used as the pressing jig for thermal bonding. This is important, for example, when a jig having a groove-shaped uneven surface used in a normal high-frequency welding method is used, it is not preferable because the workability of cleaning the joining surface obtained is poor.
【００３０】熱接着の条件は、樹脂コート基布１２素材
の種類によって相違するが、通常は１６０〜１８０℃の
温度で、５〜１０Kg／cm2 の圧力に加圧する条件が採用
される。The conditions of the heat bonding differ depending on the kind of the material of the resin-coated base cloth 12, but usually, the conditions of pressing at a temperature of 160 to 180 ° C. and a pressure of 5 to 10 kg / cm 2 are adopted.
【００３１】次に、図４に示した第２実施例は、内部構
成部材１１の一方の面に、各接合部１３ａ、１３ｂ、１
３ｃへかけて熱接着性フィルム１６を配置し、前記各接
合部１３ａ、１３ｂ、１３ｃにおける樹脂コート基布１
２の対向部に前記熱接着性フィルム１６を介在させるこ
とにより、前記各接合部１３ａ、１３ｂ、１３ｃの接合
強度を強化した点が上述した第１実施例と相違してい
る。Next, in the second embodiment shown in FIG. 4, each of the joining portions 13a, 13b, 1
3c, the heat-adhesive film 16 is disposed, and the resin-coated base cloth 1 at each of the joints 13a, 13b, 13c is formed.
The second embodiment differs from the above-described first embodiment in that the bonding strength of each of the bonding portions 13a, 13b, and 13c is enhanced by interposing the heat-adhesive film 16 between the two opposing portions.
【００３２】さらに、図５に示した第３実施例は、上述
した接合部１３ａ、１３ｂ、１３ｃに熱接着性フィルム
１６を介在せしめた第２実施例の態様において、接合部
１３ｂ、１３ｃの辺にハトメ部１５を形成した例を示
す。Furthermore, the third embodiment shown in FIG. 5, the joint 13a discussed above, 13b, in the aspect of the second embodiment was allowed interposed thermal adhesive film 16 to 13c, junction
It shows an example of forming the eyelet 15 to the side of the 1 3b, 13 c.
【００３３】次に、図６〜８に示した第４実施例は、鉛
繊維不織布１１ａを主材料とする内部構成部材１１の内
部に、金網またはステンレス薄板１７を配置し、これを
ハトメ部１５で固定することにより、長期間吊り下げ使
用する際のハトメ部１５の強度信頼性を一層高めた点が
上述した第１〜第３実施例と相違している。Next, in a fourth embodiment shown in FIGS. 6 to 8, a wire mesh or a stainless steel thin plate 17 is arranged inside an internal component member 11 mainly composed of a lead fiber nonwoven fabric 11a, The third embodiment differs from the first to third embodiments in that the strength reliability of the eyelet portion 15 when used for hanging for a long time is further improved by fixing the eyelet 15.
【００３４】すなわち、本第４実施例において、金網ま
たはステンレス薄板１７は芯材１１ｂに挟まれて、内部
構成部材１１のほぼ中央にサンドイッチ状に配置されて
いる。そして、図６に示したように、金網またはステン
レス薄板１７は長手方向中央部を切り欠いて縮径されて
おり、この縮径部に位置する内部構成部材１１と芯材１
１ｂに縫合部１１ｅを形成することで、その動きが規制
されている。That is, in the fourth embodiment, the wire mesh or the thin stainless steel plate 17 is sandwiched between the core members 11b, and is arranged in a sandwich shape at substantially the center of the internal component member 11 . Their to, as shown in FIG. 6, wire mesh or a stainless thin plate 17 is reduced in diameter by cutting out a longitudinal center part, inner component 11 and the core 1 is located in the reduced diameter portion
By forming the suturing portion 11e in 1b, its movement is regulated.
【００３５】ここで、縫合部１１ｄ、１１ｅを形成する
縫糸としては、主として合成繊維製のものが用いられる
が、これら縫合部と共に、または縫合部の代わりに、金
属リベット状物を用いた固定となすこともできる。な
お、金属リベット状物で固定する場合には、金網または
ステンレス薄板１７の長手方向中央部の切欠きは不要と
なる。Here, as the sutures forming the sewn portions 11d and 11e, mainly those made of synthetic fibers are used, but it is necessary to use a metal rivet-like material together with or instead of these sewn portions. You can do it. In the case of fixing with a metal rivet, a notch at the center in the longitudinal direction of the wire mesh or the stainless steel thin plate 17 is not required.
【００３６】また、金網１７としては線径０．１〜１．
２mmのステンレス線を密度６〜５０メッシュの網状に織
成したものが、ステンレス薄板１７としては、厚み０．
０８〜０．２mm程度のものが好ましく用いられる。The wire mesh 17 has a wire diameter of 0.1-1.
A 2 mm stainless steel wire woven into a mesh having a density of 6 to 50 mesh has a thickness of 0.
Those having a thickness of about 08 to 0.2 mm are preferably used.
【００３７】かくしてなる本考案の放射線遮蔽用マット
は、一般に配管に巻き付けたり、または複数枚並列して
実用に供されるが、例えば複数枚並列する場合には、図
９に示したように、各端部の内で上記接合部１３ａ、１
３ｂ、１３ｃのいずれか（図面では１３ａ）に折曲げ部
１４を重ねればよく、このようにすることによって重ね
合わせ部分が従来（図１０および１１参照）のように突
出せず、平坦で清掃作業性の良好な取付け構造を、すぐ
れた装着性および取扱性のもとに得ることができる。The radiation shielding mat of the present invention thus constructed is generally wrapped around a pipe or used in parallel with a plurality of mats. For example, when a plurality of mats are arranged in parallel, as shown in FIG. In each end, the joints 13a, 1
The bent portion 14 may be overlapped on one of the bent portions 3b and 13c (in the drawing, 13a), so that the overlapped portion does not protrude as in the related art (see FIGS. 10 and 11), and is flat and clean. A mounting structure with good workability can be obtained with excellent mounting and handling properties.
【００３８】[0038]
【考案の効果】以上説明したように、本考案の放射線遮
蔽用マットは、端部に縫合部を有さず、表面平滑性にす
ぐれると共に、表面の除染性がとくにすぐれているた
め、清掃作業をきわめて容易に行うことができる。[Effects of the Invention] As described above, the radiation shielding mat of the present invention does not have a sewn portion at the end, has excellent surface smoothness, and has excellent surface decontamination properties. Cleaning work can be performed very easily.
【００３９】また、本考案の放射線遮蔽用マットを配管
に巻き付けたり、または複数枚並列して使用する際に
は、上記樹脂コート基布の折り曲げ部分と、残る３辺の
接合部のいずれかとを重ね合わすことによって、容易な
装着性および取扱性のもとに、美観にすぐれた装着面を
得ることができる。When the radiation shielding mat of the present invention is wound around a pipe or when a plurality of the radiation shielding mats are used in parallel, the bent portion of the resin-coated base fabric and any of the remaining three sides are joined together. By superimposing, it is possible to obtain an aesthetically pleasing mounting surface under easy mounting and handling properties.
【００４０】さらに、本考案の放射線遮蔽用マットは、
長期間吊り下げ使用する際の、強度安全性にもすぐれる
ものである。Furthermore, the radiation shielding mat of the present invention is:
It has excellent strength and safety when used for hanging for a long time.
【００４１】したがって、本考案の放射線遮蔽用マット
は、原子力発電所などの放射線を取扱う現場において、
γ線やＸ線などの放射線から作業者を保護するための放
射線遮蔽用材料としてきわめて有用である。Therefore, the radiation shielding mat of the present invention can be used in a site where radiation is handled, such as a nuclear power plant.
It is extremely useful as a radiation shielding material for protecting workers from radiation such as γ-rays and X-rays.
【図１】図１は本考案の放射線遮蔽用マットの第１実施
例を示す断面図である。FIG. 1 is a sectional view showing a first embodiment of the radiation shielding mat of the present invention.
【図２】図２は同じく平面図である。FIG. 2 is a plan view of the same.
【図３】図３は同じく放射線遮蔽用マットを製造する当
初の過程を示す平面図である。FIG. 3 is a plan view showing an initial process of manufacturing the radiation shielding mat.
【図４】図４は本考案の放射線遮蔽用マットの第２実施
例を示す断面図である。FIG. 4 is a sectional view showing a second embodiment of the radiation shielding mat of the present invention.
【図５】図５は同じく第３実施例を示す断面図である。FIG. 5 is a sectional view showing a third embodiment in the same manner.
【図６】図６は本考案の放射線遮蔽用マットの第４実施
例を示す一部切欠平面図である。FIG. 6 is a partially cutaway plan view showing a fourth embodiment of the radiation shielding mat of the present invention.
【図７】図７は図６を１３ａ方向から見た断面図であ
る。FIG. 7 is a cross-sectional view of FIG. 6 viewed from a direction 13a.
【図８】図８は同じく図６を１３ｃ方向から見た断面図
である。FIG. 8 is a sectional view of FIG. 6 viewed from a direction 13c.
【図９】図９は本考案の放射線遮蔽用マットを複数枚並
列に配置した状況を示す側面図である。FIG. 9 is a side view showing a state where a plurality of radiation shielding mats of the present invention are arranged in parallel.
【図１０】図１０は従来の放射線遮蔽用マットを複数枚
並列に配置した状況を示す側面図である。FIG. 10 is a side view showing a state where a plurality of conventional radiation shielding mats are arranged in parallel.
【図１１】図１１は同じく従来の放射線遮蔽用マットを
複数枚並列に配置した状況を示す側面図である。FIG. 11 is a side view showing a state in which a plurality of conventional radiation shielding mats are arranged in parallel.
１０ 放射線遮蔽用マット １１ 内部構成部材 １１ａ 鉛繊維不織布 １１ｂ 芯材 １１ｃ 内包材 １１ｄ 縫合部 １１ｅ 〃 １２ 樹脂コート基布 １３ａ 接合部 １３ｂ 〃 １３ｃ 〃 １４ 折曲げ部 １５ ハトメ部 １６ 熱接着性フィルム １７ 金網またはステンレス薄板 DESCRIPTION OF SYMBOLS 10 Radiation shielding mat 11 Internal constituent member 11a Lead fiber nonwoven fabric 11b Core material 11c Inner wrapping material 11d Suturing part 11e １２ 12 Resin coat base cloth 13a Joining part 13b １３ 13c １４ 14 Bent part 15 Eyelet part 16 Thermal adhesive film 17 Wire mesh Or stainless steel sheet
フロントページの続き (58)調査した分野(Int.Cl.6，ＤＢ名) G21F 3/00Continuation of the front page (58) Field surveyed (Int.Cl. 6 , DB name) G21F 3/00
Claims (2)
材の全表面を、樹脂コート基布にて被覆してなり、かつ
前記樹脂コート基布の略中央部を折り曲げて前記内部構
成部材を包み、前記樹脂コート基布の対向する３辺の端
部同志を熱接着することにより平坦状の接合部を構成し
た放射線遮蔽用マットにおいて、前記樹脂コート基布と
してポリフッ化ビニリデン樹脂を被覆した基布を用いた
ことを特徴とする放射線遮蔽用マット。1. A resin-coated base cloth covering the entire surface of an internal constituent member mainly composed of a lead fiber nonwoven fabric, and a substantially central portion of the resin-coated base cloth is bent to form the internal constituent member. A radiation-shielding mat having a flat joint portion formed by wrapping and thermally bonding the three opposite ends of the resin-coated base fabric, wherein the resin-coated base fabric is coated with polyvinylidene fluoride resin. A radiation shielding mat using a cloth.
材に、金網またはステンレス薄板を配置したことを特徴
とする請求項１に記載の放射線遮蔽用マット。2. The radiation shielding mat according to claim 1, wherein a wire mesh or a stainless steel thin plate is disposed on an internal component member mainly composed of a lead fiber nonwoven fabric.