JP2530711Y2 - Lid material - Google Patents
Lid materialInfo
- Publication number
- JP2530711Y2 JP2530711Y2 JP1990008733U JP873390U JP2530711Y2 JP 2530711 Y2 JP2530711 Y2 JP 2530711Y2 JP 1990008733 U JP1990008733 U JP 1990008733U JP 873390 U JP873390 U JP 873390U JP 2530711 Y2 JP2530711 Y2 JP 2530711Y2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- aluminum foil
- lid material
- adhesive layer
- rosin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】 ＜産業上の利用分野＞ 本考案は、アルミニウム箔の下面に耐油性を有する樹
脂層を設け、かつ開封性が良好な蓋材に関する。DETAILED DESCRIPTION OF THE INVENTION <Industrial application field> The present invention relates to a lid material provided with an oil-resistant resin layer on the lower surface of an aluminum foil and having good openability.
＜従来の技術＞ 従来から、主に即席食品の販売容器として、容器本体
が発泡ポリエチレン、ハイインパクトスチロール樹脂等
よりなり、その容器本体の口部に紙とアルミニウム箔の
複合材料からなる基材の下面にエチレン−エチルアクリ
レート共重合体、またはエチレン−酢酸ビニル共重合体
系ホットメルト接着剤層を設けた蓋材をヒートシールし
て使用している。<Conventional technology> Conventionally, as a container for selling instant foods, the container body is mainly made of foamed polyethylene, high-impact styrene resin, etc., and the mouth of the container body is made of a composite material of paper and aluminum foil. A lid material provided with an ethylene-ethyl acrylate copolymer or ethylene-vinyl acetate copolymer hot melt adhesive layer on the lower surface is heat-sealed and used.
しかしながら、かかる容器の蓋材は、アルミニウム箔
面が、空気、水分などによりきわめて酸化されやすく、
アルミニウム箔面の酸化に伴ってエチレン−酢酸ビニル
共重合体系ホットメルト接着剤層のアルミニウム箔面へ
の接着強度が低下し、開封前に剥離してしまう問題が発
生しやすい欠点を有していた。However, the lid material of such a container, the aluminum foil surface is very easily oxidized by air, moisture, etc.,
With the oxidation of the aluminum foil surface, the adhesive strength of the ethylene-vinyl acetate copolymer hot-melt adhesive layer to the aluminum foil surface was reduced, and there was a problem that the problem of peeling before opening was likely to occur. .
一方、前記のような接着強度の低下をみこして、例え
ばアルミニウム箔に予めポリエチレン樹脂をコートし、
ホットメルト接着剤の接着強度を最初から強いものにし
ておいたものがある。On the other hand, in view of the decrease in the adhesive strength as described above, for example, a polyethylene resin is previously coated on an aluminum foil,
In some cases, the adhesive strength of a hot melt adhesive is increased from the beginning.
しかし、このように形成した蓋材は、開封困難であ
り、開封時にホットメルト接着剤と共に容器本体の口部
を破壊してしまう欠点を有していた。However, the lid material thus formed has a drawback that it is difficult to open and the opening of the container body is destroyed together with the hot melt adhesive at the time of opening.
また、アルミニウム箔面に直接ホットメルト接着剤を
積層できないので、ポリエチレン層を介して積層しなけ
ればならないため、工程が増え、コストが高いものとな
っていた。Further, since the hot melt adhesive cannot be directly laminated on the aluminum foil surface, it must be laminated via a polyethylene layer, so that the number of steps is increased and the cost is high.
＜考案が解決しようとする課題＞ 本考案は、このような欠点を改善するもので、紙とア
ルミニウム箔の複合材料からなる基材のアルミニウム箔
にポリエチレン層を設けないで、接着剤層を設けてなる
耐油性、易開封性の蓋材を提供することを目的とする。<Problem to be Solved by the Invention> The present invention is intended to improve such a drawback. An aluminum foil of a base material made of a composite material of paper and an aluminum foil is provided with an adhesive layer without providing a polyethylene layer. It is an object of the present invention to provide an oil-resistant, easy-to-open lid material.
＜課題を解決するための手段＞ 本考案は、スチレン系樹脂からなる容器の開口部をヒ
ートシールにより封止するための蓋材であって、紙とア
ルミニウム箔の複合材料からなる基材の前記アルミニウ
ム箔面に、塩化ビニルー酢酸ビニル共重合体に下記から
選ばれる粘着付与剤；ロジン、変成ロジン、ポリテルペ
ン系樹脂、テルペン変性体、シクロペンタジエン樹脂、
芳香族系石油樹脂；を添加したアンカー剤層を介してエ
チレン−エチルアクリレート共重合体からなる接着剤層
を設けてなる蓋材である。また、本考案は、スチレン系
樹脂からなる容器の開口部をヒートシールにより封止す
るための蓋材であって、紙とアルミニウム箔の複合材料
からなる基材の前記アルミニウム箔面に、エチレン−メ
タクリレート共重合体に下記から選ばれる粘着付与剤；
ロジン、変成ロジン、ポリテルペン系樹脂、テルペン変
性体、シクロペンタジエン樹脂、芳香族系石油樹脂；を
添加した樹脂からなる接着剤層を設けてなる蓋材であ
る。<Means for Solving the Problems> The present invention is a lid material for sealing an opening of a container made of a styrene-based resin by heat sealing, wherein the lid material is a base material made of a composite material of paper and aluminum foil. On the aluminum foil surface, a tackifier selected from the following for a vinyl chloride-vinyl acetate copolymer: rosin, modified rosin, polyterpene resin, modified terpene, cyclopentadiene resin,
A lid member provided with an adhesive layer made of an ethylene-ethyl acrylate copolymer via an anchor agent layer to which an aromatic petroleum resin is added. Further, the present invention is a lid material for sealing an opening of a container made of a styrene-based resin by heat sealing, wherein the aluminum foil surface of a base material made of a composite material of paper and aluminum foil has ethylene- A tackifier selected from the following for the methacrylate copolymer;
A lid member provided with an adhesive layer made of a resin to which rosin, modified rosin, polyterpene resin, modified terpene, cyclopentadiene resin, and aromatic petroleum resin are added.
＜作用＞ 接着剤層がエチレン−エチルアクリレート共重合体、
またはエチレン−メタクリレート共重合体からなるの
で、耐油性が優れ、また、スチレン系樹脂からなる容器
に適用した際の剥離性が優れている。<Action> The adhesive layer is an ethylene-ethyl acrylate copolymer,
Alternatively, since it is made of an ethylene-methacrylate copolymer, it has excellent oil resistance and also has excellent releasability when applied to a container made of a styrene resin.
また、接着剤層、または接着剤層を設けるためのアン
カー剤層のいずれかに粘着付与剤を添加した構成とした
ので、アルミニウム箔と接着剤層の接着強度の低下を抑
制することができる。In addition, since a tackifier is added to either the adhesive layer or the anchor layer for providing the adhesive layer, a decrease in the adhesive strength between the aluminum foil and the adhesive layer can be suppressed.
ここで、接着剤層、またはアンカー剤層に添加する粘
着付与剤は、ロジン、変成ロジン、ポリテルペン系樹
脂、テルペン変成体、シクロペンタジエン樹脂、芳香族
系石油樹脂等が挙げられる。Here, examples of the tackifier added to the adhesive layer or the anchor agent layer include rosin, modified rosin, polyterpene-based resin, modified terpene, cyclopentadiene resin, and aromatic petroleum resin.
＜実施例１＞ 以下、本考案の実施例について説明する。<Example 1> Hereinafter, an example of the present invention will be described.
まず、第１図に示した実施例は、表面に印刷層１を設
けた紙（58g/m2）２に、ポリエチレン層（15μｍ）３を
介してアルミニウム箔（７μｍ）４を一体化した基材Ａ
のアルミニウム箔４面に、塩化ビニル−酢酸ビニル共重
合体に粘着付与剤（ポリテルペン系樹脂）を添加したア
ンカー剤層５を設け、このアンカー剤層５の上にエチレ
ン−メタクリレート共重合体（EL5050C 大日本インキ化
学社製）からなる接着剤層（30μｍ）６を押出コート法
により設けた蓋材である。First, the embodiment shown in FIG. 1 is based on a paper (58 g / m 2 ) 2 provided with a printing layer 1 on its surface and an aluminum foil (7 μm) 4 integrated with a polyethylene layer (15 μm) 3 via a polyethylene layer 3. Material A
The aluminum foil 4 is provided with an anchor agent layer 5 obtained by adding a tackifier (polyterpene resin) to a vinyl chloride-vinyl acetate copolymer, and an ethylene-methacrylate copolymer (EL5050C) is formed on the anchor agent layer 5. This is a lid member provided with an adhesive layer (30 μm) 6 made of Dainippon Ink and Chemicals, Inc. by an extrusion coating method.
この蓋材を発泡ポリスチレンからなる容器本体の開口
部に重ね、150℃、2kg/cm2、１秒の条件でヒートシール
後、蓋材を剥離したところ、容器本体の開口部を破壊す
ることなく、きれいに開封することができた。This lid material was placed on the opening of the container body made of expanded polystyrene, and after heat sealing at 150 ° C. and 2 kg / cm 2 for 1 second, the lid material was peeled off without breaking the opening portion of the container body. , Could be opened neatly.
＜実施例２＞ 第２図に示した実施例は、実施例１で用いた基材Ａの
アルミニウム箔４面に、エチレン−メタクリレート共重
合体に粘着付与剤（ポリテルペン系樹脂）を添加した樹
脂（TL9104−１三井デュポン社製）を押出塗布し、接着
剤層（30μｍ）６を設けた蓋材である。<Example 2> The example shown in FIG. 2 is a resin obtained by adding a tackifier (polyterpene-based resin) to an ethylene-methacrylate copolymer on the surface of the aluminum foil 4 of the substrate A used in Example 1. (TL9104-1 manufactured by Du Pont-Mitsui Co., Ltd.) is a cover material provided with an adhesive layer (30 μm) 6 by extrusion coating.
この蓋材を用い、実施例１と同様の容器本体に同様の
条件でヒートーシールしたところ、同様に容器本体の開
口部を破壊することなくきれいに開封することができ
た。Using this lid, the container was heat-sealed in the same condition as in Example 1 under the same conditions. Similarly, the opening could be cleanly opened without breaking the opening of the container.
＜比較例１＞ 第３図に示すように実施例１の蓋材Ａ、アルミニウム
箔４面に、塩化ビニル−酢酸ビニル共重合体からなるア
ンカー剤層10、押出しポリエチレン層11（20μｍ）を介
して、エチレン−エチルアクリレート共重合体（EL5050
大日本インキ化学社製）を押出塗布し、接着剤層（25μ
ｍ）12を設け、比較例の蓋材を得た。<Comparative Example 1> As shown in Fig. 3, an anchor agent layer 10 made of a vinyl chloride-vinyl acetate copolymer and an extruded polyethylene layer 11 (20 µm) were interposed on the lid material A of Example 1 and four surfaces of the aluminum foil. And ethylene-ethyl acrylate copolymer (EL5050
Extrusion coating of Dainippon Ink and Chemicals, Inc., and adhesive layer
m) 12 was provided to obtain a lid material of a comparative example.
この蓋材を用い実施例１と同様のテストを行ったとこ
ろ、容器本体の開口部の一部が破壊された状態で開封さ
れた。When a test similar to that of Example 1 was performed using this lid material, the container was opened with a part of the opening of the container body broken.
＜考案の効果＞ 本考案の蓋材は、以上の構成からなるので、基材のア
ルミニウム箔面にポリエチレン層を設けなくても、十分
な接着強度を有する接着剤層を設けることができるの
で、ポリエチレン層、およびこのポリエチレン層を設け
る工程を省略することができ、コストを低下させること
ができた。<Effect of the Invention> Since the lid material of the present invention has the above configuration, it is possible to provide an adhesive layer having sufficient adhesive strength without providing a polyethylene layer on the aluminum foil surface of the base material. The polyethylene layer and the step of providing the polyethylene layer could be omitted, and the cost could be reduced.
また、アルミニウム箔にオポリエチレン層を設けない
構成としたので、容器本体にヒートシールした時、シー
ル強度が大きくなりすぎることなく、容器本体の開口部
を破壊することなく、きれいに剥離開封することができ
る。In addition, since the aluminum foil is not provided with an polyethylene layer, when heat-sealed to the container body, the sealing strength does not become too large, and the opening of the container body is not broken, and the container can be peeled and opened cleanly. it can.
さらに、接着剤層に用いる樹脂が、エチレン−エチル
アクリレート共重合体、またはエチレン−メチクリレー
ト共重合体からなるので、即席食品の容器として汎用さ
れているポリスチレン系樹脂に対して、適度の接着強度
を示すと共に、耐油性が優れるので、即席食品用蓋材と
して好適である。Furthermore, since the resin used for the adhesive layer is made of an ethylene-ethyl acrylate copolymer or an ethylene-methacrylate copolymer, it has a moderate adhesive strength with respect to a polystyrene resin widely used as an instant food container. In addition, it is suitable as an instant food lid because of its excellent oil resistance.
【図面の簡単な説明】 第１図および第２図は、本考案の実施例を示す断面図、
第３図は従来の蓋材の一例を示す断面図である。 Ａ……蓋材、１……印刷層 ２……紙、３……ポリエチレン層 ４……アルミニウム箔、５……アンカー剤層 ６……接着剤層BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 and FIG. 2 are sectional views showing an embodiment of the present invention.
FIG. 3 is a sectional view showing an example of a conventional lid member. A: lid material, 1: printing layer 2, paper, 3: polyethylene layer 4, aluminum foil, 5, anchor agent layer 6, adhesive layer
Claims (2)
ートシールにより封止するための蓋材であって、紙とア
ルミニウム箔の複合材料からなる基材の前記アルミニウ
ム箔面に、塩化ビニルー酢酸ビニル共重合体に下記から
選ばれる粘着付与剤； ロジン、変成ロジン、ポリテルペン系樹脂、テルペン変
性体、シクロペンタジエン樹脂、芳香族系石油樹脂； を添加したアンカー剤層を介してエチレン−エチルアク
リレート共重合体からなる接着剤層を設けてなる蓋材。1. A lid material for sealing an opening of a container made of styrene resin by heat sealing, wherein vinyl chloride-acetic acid is provided on the aluminum foil surface of a base material made of a composite material of paper and aluminum foil. A tackifier selected from the following: a rosin, a modified rosin, a polyterpene-based resin, a modified terpene, a cyclopentadiene resin, an aromatic petroleum resin; A cover material provided with an adhesive layer made of a polymer.
ートシールにより封止するための蓋材であって、紙とア
ルミニウム箔の複合材料からなる基材の前記アルミニウ
ム箔面に、エチレン−メタクリレート共重合体に下記か
ら選ばれる粘着付与剤； ロジン、変成ロジン、ポリテルペン系樹脂、テルペン変
性体、シクロペンタジエン樹脂、芳香族系石油樹脂； を添加した樹脂からなる接着剤層を設けてなる蓋材。2. A lid material for sealing an opening of a container made of styrene resin by heat sealing, wherein ethylene-methacrylate is provided on the aluminum foil surface of a base material made of a composite material of paper and aluminum foil. A lid material provided with an adhesive layer made of a resin obtained by adding a tackifier selected from the following to the copolymer: rosin, modified rosin, polyterpene-based resin, modified terpene, cyclopentadiene resin, aromatic petroleum resin .