JP2511489Y2 - Particle-dispersed display device - Google Patents
Particle-dispersed display deviceInfo
- Publication number
- JP2511489Y2 JP2511489Y2 JP1989151069U JP15106989U JP2511489Y2 JP 2511489 Y2 JP2511489 Y2 JP 2511489Y2 JP 1989151069 U JP1989151069 U JP 1989151069U JP 15106989 U JP15106989 U JP 15106989U JP 2511489 Y2 JP2511489 Y2 JP 2511489Y2
- Authority
- JP
- Japan
- Prior art keywords
- transparent
- dispersed
- transparent substrate
- display device
- particle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【考案の詳細な説明】 [産業上の利用分野] 本考案は、粒子分散型表示素子に関する。DETAILED DESCRIPTION OF THE INVENTION [Industrial application] The present invention relates to a particle dispersion type display device.
[従来の技術] 従来の表示素子を例えば自動車のフロントガラスやリ
ヤガラスにサンシェードとして組み込み遮光と採光とを
可変とすることが考えられる。この表示素子は、間隔を
隔てて互いに対向する一対の透明基板と、一対の該透明
基板の互いに対向する表面にそれぞれ形成された一対の
透明電極と、前記一対の透明基板により形成されたセル
空間に封入された分散媒およびこの分散媒中にランダム
状に分散された偏光性物質よりなる。[Prior Art] It is conceivable to incorporate a conventional display element into, for example, a windshield or a rear glass of an automobile as a sunshade to make light blocking and lighting variable. The display device includes a pair of transparent substrates facing each other with a space therebetween, a pair of transparent electrodes formed on surfaces of the pair of transparent substrates facing each other, and a cell space formed by the pair of transparent substrates. And a polarizing substance randomly dispersed in the dispersion medium.
ところで前記セル中に封入された偏光性物質は、前記
一対の透明電極に電圧が印加されないとき、ブラウン運
動しランダムな状態に保持され分散媒に懸濁しているた
め、入射光(可視光線の一部)を吸収し、遮断すること
ができるので表示素子が暗く色づいて見える。By the way, since the polarizing substance sealed in the cell is in a random state by causing Brownian motion and suspended in a dispersion medium when a voltage is not applied to the pair of transparent electrodes, incident light (visible light Part) can be absorbed and blocked, so that the display element appears dark and colored.
また、偏光性物質は、前記一対の透明電極に電圧が印
加されたとき、透明基板に対して垂直方向(印加方向)
に配向して並び、入射光(可視光線の一部)が配向粒子
を透過することができるので表示素子が明るく透明に見
える。In addition, the polarizing substance is perpendicular to the transparent substrate (applying direction) when a voltage is applied to the pair of transparent electrodes.
Since the incident light (a part of visible light) can pass through the oriented particles, the display element looks bright and transparent.
このような機能をもつ表示素子として例えば特開昭53
-144764号公報には、前記偏光性物質のランダムな分散
状態と、配向状態とに変化させることができ、偏光性物
質が凝集したままになるのを防ぐことができる分散媒が
提案されている。As a display element having such a function, for example, Japanese Patent Laid-Open No.
-144764 discloses a dispersion medium that can be changed into a random dispersion state of the polarizing substance and an alignment state, and can prevent the polarizing substance from remaining aggregated. .
[考案が解決しようとする課題] また自動車のフロントガラスあるいはリヤガラスを形
成する場合においては、安全ガラスとしての基準を満た
すためガラスが破損した時にその飛散を防止する目的で
中間樹脂層としてポリビニルブチラールを2枚のガラス
板に挟み込んだいわゆる合わせガラスとして形成してい
る。このポリビニルブチラールは弾力性、ガラスの接着
性、透明性において他の樹脂よりも優れている。[Problems to be solved by the invention] Further, in the case of forming a windshield or a rear glass of an automobile, polyvinyl butyral is used as an intermediate resin layer for the purpose of preventing scattering when the glass is broken in order to satisfy the standard as a safety glass. It is formed as a so-called laminated glass sandwiched between two glass plates. This polyvinyl butyral is superior to other resins in elasticity, adhesiveness of glass, and transparency.
しかしポリビニルブチラールの溶融温度は130℃の高
温であるため前記安全ガラスの製造工程における予備圧
着から本圧着にかけて溶融して硬化するために130℃の
雰囲気下にさらす必要がある。However, since the melting temperature of polyvinyl butyral is a high temperature of 130 ° C., it is necessary to expose it to an atmosphere of 130 ° C. in order to melt and harden it from the preliminary pressure bonding to the main pressure bonding in the safety glass manufacturing process.
ここで前記表示素子を自動車のフロントガラスあるい
はリヤガラスにサンシェードとして組み込み形成する場
合に不具合を生じる。すなわち従来の表示素子用サスペ
ンションにおいては、例えば特開昭53-144764号公報、
特開昭53-144893号公報に示されるようにヘラパタイ
ト、ジヒドロシンコニジン硫酸塩過ヨウ化物の酢酸エス
テル系分散媒による分散液が用いられていた。この組成
物は、前記ポリビニルブチラールを溶融、硬化させるに
必要な130℃の高熱が付与されると、ほぼ瞬間的に青色
サスペンションが黄かっ色に変色してしまうとともに、
気泡が発生し、使用に耐えないものとなる。Here, a problem occurs when the display element is incorporated into a windshield or a rear glass of an automobile as a sunshade. That is, in the conventional display element suspension, for example, JP-A-53-144764,
As disclosed in JP-A-53-144893, a dispersion of herapatite and dihydrocinconidine sulfate periodate in an acetate dispersion medium has been used. The composition melts the polyvinyl butyral, and when a high heat of 130 ° C. necessary for curing is applied, the blue suspension discolors to yellowish yellow almost instantaneously,
Bubbles are generated, making it unusable.
さらに、またセル中に液状のサスペンションが充填さ
れている従来の表示素子では、セルの一部が破損しただ
けで、サスペンションが流出して表示素子としての機能
が損われるという問題点を有する。またセルのギャップ
の調整がしにくいとか、セルの面積が大きくなると透明
基材の変形やソリなどの製造上の問題も有している。Furthermore, in the conventional display element in which the liquid suspension is filled in the cell, there is a problem that the suspension flows out and the function as the display element is impaired even if a part of the cell is damaged. Further, it is difficult to adjust the cell gap, and when the cell area becomes large, there are problems in manufacturing such as deformation and warpage of the transparent substrate.
本考案は、前記の事情に鑑みてなされたもので自動車
の合せガラスに用いられる粒子分散型表示素子を提供す
ることを目的とする。The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a particle-dispersed display device used for a laminated glass of an automobile.
[課題を解決するための手段] 本考案の粒子分散型表示素子は、間隔を隔てて互いに
対向する透明基板と、 該透明基板の互いに対向する表面にそれぞれ形成され
た一対の透明電極と、 上記の対向する透明電極の間に設けた調光素子胞を含
むポリビニルブチラールからなる透明樹脂層と、よりな
り、 前記調光素子胞は液状フタル酸エステルと、該フタル
酸エステル中に分散された偏光性物質とを含むことを特
徴とする。[Means for Solving the Problems] A particle-dispersed display device of the present invention comprises: a transparent substrate facing each other with a space therebetween; and a pair of transparent electrodes formed on surfaces of the transparent substrate facing each other, respectively. And a transparent resin layer made of polyvinyl butyral containing a dimming element cell provided between the opposing transparent electrodes, wherein the dimming element cell is a liquid phthalate ester and polarized light dispersed in the phthalate ester. It is characterized by containing a sexual substance.
透明基板は、例えば自動車のフロントガラスやリヤガ
ラスの形状を備えた無機ガラス板や樹脂ガラス板で形成
される。また透明基板とは少々着色してあっても、透光
性を有するものであれば使用することができる。The transparent substrate is formed of, for example, an inorganic glass plate or a resin glass plate having the shape of an automobile windshield or rear glass. Further, even if the transparent substrate is slightly colored, any transparent substrate can be used.
対向する透明電極は、それぞれの透明基板の互いに対
向する表面に直接形成したITO(インジウム−チン−オ
キサイド)、二酸化錫等の透明導電性材料を用いること
ができる。また対向する透明電極は、それぞれの透明基
板の表面に他の材料を介して間接的に形成したもの、す
なわち、前記表面に近接した位置に配設されたシート状
のポリビニルブチラール(PVB)、ポリブチルアセテー
ト(PVA)、ポリエチレンテレフタレート(PET)に一体
的に形成したものを用いることができる。For the transparent electrodes facing each other, a transparent conductive material such as ITO (Indium-Tin-Oxide) or tin dioxide directly formed on the surfaces of the respective transparent substrates facing each other can be used. The opposing transparent electrodes are those indirectly formed on the surface of each transparent substrate via another material, that is, sheet-shaped polyvinyl butyral (PVB), poly-vinyl butyral (PVB), or poly-vinyl butyral (PVB), which is disposed in the vicinity of the surface. Butyl acetate (PVA) or polyethylene terephthalate (PET) integrally formed can be used.
ポリビニルブチラールからなる透明樹脂層は、例えば
厚さ0.2〜1.0mmのシート状のものや板状のものが使用で
きる。また、ポリビニルブチラールからなる透明樹脂層
は、その層中に後で述べる調光素子胞を0.5〜10wt%程
度に一体的に保持するとともに、対向する透明電極間
に、例えば一対の透明基板に挟持される。As the transparent resin layer made of polyvinyl butyral, for example, a sheet-shaped one having a thickness of 0.2 to 1.0 mm or a plate-shaped one can be used. In addition, the transparent resin layer made of polyvinyl butyral holds the dimming element cell described later in the layer integrally at about 0.5 to 10 wt%, and is sandwiched between opposing transparent electrodes, for example, between a pair of transparent substrates. To be done.
調光素子胞は、分散媒となる液状フタル酸エステルと
偏光性物質とをマイクロカプセルに封じ込めたものを前
記樹脂層中に分散させたものや、前記樹脂層中に直接液
胞状態に封じ込めたものを使用することができる。調光
素子胞は直径が10〜100μmで、前記透明樹脂層に保持
されて対向する透明基板に覆われる際、この透明基板と
の接触による損傷を防ぐため前記ポリビニルブチラール
からなる透明樹脂層の厚みよりも小さいことが好まし
い。The dimming element cell was obtained by encapsulating a liquid phthalate ester serving as a dispersion medium and a polarizing substance in a microcapsule dispersed in the resin layer, or directly encapsulating in a vacuole state in the resin layer. Things can be used. The dimming element cell has a diameter of 10 to 100 μm, and when it is held by the transparent resin layer and covered with an opposing transparent substrate, the thickness of the transparent resin layer made of polyvinyl butyral is prevented to prevent damage due to contact with the transparent substrate. It is preferably smaller than.
液状フタル酸エステルは、分散媒として単独で用いる
ことができる。また、液状フタル酸エステルは、界面活
性剤と酸化防止剤とのうち、いずれか一方あるいは両方
を組合せて用いることが好ましい。The liquid phthalate ester can be used alone as a dispersion medium. Further, the liquid phthalate ester is preferably used in combination with one or both of a surfactant and an antioxidant.
フタル酸エステルは、蒸気圧が低く、かつ偏光性物質
に対して不活性なもので、ガラス合せ工程時に受ける高
温に対して変質しないものである。フタル酸エステルと
して具体的にはフタル酸ジオクチル、フタル酸ジデシ
ル、フタル酸ジドデシル、フタル酸ジトリデシルが好ま
しい。より好ましくは、混合溶媒としてデカン、ウンデ
カン、ドデカン、トリデカン、テトラデカンを加えると
よい。その割合は任意であるが、フタル酸エステルの方
を過剰にした方がよい。The phthalic acid ester has a low vapor pressure, is inactive with respect to the polarizing substance, and does not deteriorate due to the high temperature received during the glass laminating process. As the phthalate ester, specifically, dioctyl phthalate, didecyl phthalate, didodecyl phthalate, and ditridecyl phthalate are preferable. More preferably, decane, undecane, dodecane, tridecane, and tetradecane may be added as a mixed solvent. The ratio is arbitrary, but it is better to make the phthalate ester excess.
この理由としては偏光性物質が高温で溶解して、分解
するのを防ぐ役割をするからである。The reason for this is that the polarizing substance plays a role of preventing it from melting and decomposing at high temperatures.
界面活性剤としては、エステル系溶媒に可溶でかつ偏
光性物質に対して不活性なものが用いられる。界面活性
剤として具体的にはソルビタン脂肪酸エステル、グリセ
リン脂肪酸エステル、ポリエチレングリコール脂肪酸エ
ステル、ポリオキシエチレンアルキルエーテルを用いる
ことが好ましい。As the surfactant, those which are soluble in the ester solvent and inactive to the polarizing substance are used. Specifically, it is preferable to use sorbitan fatty acid ester, glycerin fatty acid ester, polyethylene glycol fatty acid ester, and polyoxyethylene alkyl ether as the surfactant.
この理由として偏光性物質が高温で凝集するのを防ぐ
役割をするからである。The reason for this is that it serves to prevent the polarizing substance from aggregating at high temperatures.
酸化防止剤とてしては、エステル系溶媒に可溶でかつ
偏光性物質に不活性であるものが用いられる。酸化防止
剤として具体的にはゴム用の酸化防止剤であるジフェニ
ルアミン誘導体やフェノール誘導体を用いることが好ま
しい。これらは高温で酸化劣化を引き起す開始点を捕捉
し、劣化の進行をおさえる役目をする。ただし使用条件
によっては界面活性剤と酸化防止剤とのいずれも、ある
いは一方のみを添加しないこともある。As the antioxidant, those which are soluble in the ester solvent and inactive to the polarizing substance are used. As the antioxidant, specifically, it is preferable to use a diphenylamine derivative or a phenol derivative which is an antioxidant for rubber. These capture the starting points that cause oxidative deterioration at high temperatures and play a role in suppressing the progress of deterioration. However, depending on the conditions of use, neither the surfactant nor the antioxidant, or only one of them may be added.
偏光性物質は、調光素子胞の単位毎に前記液状フタル
酸エステル中に分散され使用される針状、板状等の結晶
粒子で、例えばジヒドロシンコニジン硫酸塩過ヨウ化物
が使用できる。この偏光性物質は、透明基板に形成され
ている透明電極への電圧の印加および解除により配向し
たりランダム状になるのを可能にしている。すなわち透
明電極に電圧が印加されると偏光性物質が基板に対して
垂直方向に配向して入射光(可視光線の一部)を透過さ
せる。そしてこの粒子分散型表示素子が透明になり明る
くなる。透明電極への電圧の印加を止めると、偏光性物
質はランダム状に分散し入射光(可視光線の一部)が吸
収され調光素子は暗くなる。The polarizing substance is needle-shaped or plate-shaped crystal particles used by being dispersed in the liquid phthalate ester for each unit of the light control device cell, and for example, dihydrocinchonidine sulfate periodate can be used. This polarizing substance can be oriented or become random by applying and releasing a voltage to the transparent electrode formed on the transparent substrate. That is, when a voltage is applied to the transparent electrode, the polarizing substance is oriented in the direction perpendicular to the substrate and transmits incident light (a part of visible light). And this particle dispersion type display element becomes transparent and bright. When the voltage application to the transparent electrode is stopped, the polarizing substance is dispersed in a random manner, incident light (a part of visible light) is absorbed, and the light control element becomes dark.
[作用] 本考案の粒子分散型表示素子によれば、液状フタル酸
エステルと、液状フタル酸エステル中に分散された偏光
性物質からなる調光素子胞を含むポリビニルブチラール
からなる透明樹脂層が対向する透明電極間に設けられ、
対向する透明基板間に挟持されている。そしてこの粒子
分散型表示素子は電極に電界を印加することにより着色
と透明状態を可逆的にくり返す。また衝撃で破損した時
も液がとび散らない。[Operation] According to the particle dispersion type display device of the present invention, the liquid phthalate ester and the transparent resin layer made of polyvinyl butyral containing the light control device cell made of the polarizing substance dispersed in the liquid phthalate ester face each other. Is provided between the transparent electrodes,
It is sandwiched between opposing transparent substrates. The particle-dispersed display device reversibly repeats the coloring and the transparent state by applying an electric field to the electrodes. Also, the liquid does not scatter when it is damaged by impact.
[実施例] (実施例1) 本実施例1の粒子分散型表示素子A(以下、表示素子
と称す)は、斜視として示す第4図のように自動車のフ
ロントガラスBのサンシェードとして用いられる。この
表示素子Aは、断面として示す第1図のように、互いに
所定間隔を隔てて配設された第1透明基板1及び第2透
明基板2と、第1透明電極3及び第2透明電極4と、前
記一対の第1透明電極3及び第2透明電極4と接すると
ともに前記第1透明基板1及び第2透明基板2の間に挟
持されたポリビニルブチラール製透明樹脂層5よりな
る。[Examples] (Example 1) The particle-dispersed display element A (hereinafter referred to as a display element) of Example 1 is used as a sunshade for a windshield B of an automobile, as shown in Fig. 4 as a perspective view. The display element A includes a first transparent substrate 1 and a second transparent substrate 2, a first transparent electrode 3 and a second transparent electrode 4 which are arranged at a predetermined distance from each other, as shown in FIG. And a polyvinyl butyral transparent resin layer 5 which is in contact with the pair of the first transparent electrode 3 and the second transparent electrode 4 and is sandwiched between the first transparent substrate 1 and the second transparent substrate 2.
第1透明基板1及び第2透明基板2は、自動車のフロ
ントガラスを形成する透明なガラス板からなる。また、
前記第1透明基板1及び第2透明基板2において、フロ
ントガラスBのサンシェードが形成される位置、すなわ
ち後で述べるマイクロカプセル6が分散される部分の内
側表面10及び20には、それぞれ透明な第1透明電極3及
び第2透明電極4が形成されている。これら両透明電極
3及び4は、第1透明基板1及び第2透明基板2の内側
表面10及び20に真空蒸着により形成された厚さ300ÅのI
TOよりなり、前記第1透明基板1の内側表面10側より第
2透明基板2の内側表面20側への光の透過方向に対して
ほぼ垂直な面状となっている、いわゆる面状電極と称さ
れる。なお、第1、第2透明電極3及び4には、互いに
対向する面の上端部に印加電圧を伝達するための導電性
テープ7.7が接着されている。またこの導電性テープ7.7
は第1、第2透明基板1、2の端部間に充填された絶縁
性シール部材8により固定保持されている。The 1st transparent substrate 1 and the 2nd transparent substrate 2 consist of a transparent glass plate which forms the windshield of a car. Also,
In the first transparent substrate 1 and the second transparent substrate 2, the positions where the sunshade of the windshield B is formed, that is, the inner surfaces 10 and 20 of the portions where the microcapsules 6 to be described later are dispersed, respectively, are transparent. The first transparent electrode 3 and the second transparent electrode 4 are formed. These both transparent electrodes 3 and 4 are formed on the inner surfaces 10 and 20 of the first transparent substrate 1 and the second transparent substrate 2 by vacuum deposition and have a thickness of 300Å.
A so-called planar electrode which is made of TO and has a planar shape substantially perpendicular to the light transmission direction from the inner surface 10 side of the first transparent substrate 1 to the inner surface 20 side of the second transparent substrate 2. Is called. A conductive tape 7.7 for transmitting an applied voltage is adhered to the upper ends of the surfaces facing each other on the first and second transparent electrodes 3 and 4. Also this conductive tape 7.7
Is fixedly held by an insulating seal member 8 filled between the ends of the first and second transparent substrates 1 and 2.
ポリビニルブチラール製透明樹脂層5は、接着用中間
層として前記第1透明基板1及び第2透明基板2の間に
挟持され保持されている。そしてこのポリビニルブチラ
ール製透明樹脂層5のうち上記のように挟持された部分
は、調光素子胞としてのマイクロカプセル6を多数含ん
でいる。そしてマイクロカプセル6内にはジドデシルフ
タレートを主とする分散媒60と、この分散媒60中に分散
され主としてジヒドロシンコニジン硫酸塩過ヨウ化物針
状結晶よりなる偏光性物質61とが封入されている。The polyvinyl butyral transparent resin layer 5 is sandwiched and held between the first transparent substrate 1 and the second transparent substrate 2 as an intermediate layer for adhesion. The portion of the polyvinyl butyral transparent resin layer 5 sandwiched as described above includes a large number of microcapsules 6 as light control element cells. In the microcapsule 6, a dispersion medium 60 mainly composed of didodecyl phthalate and a polarizing substance 61 dispersed in the dispersion medium 60 and mainly composed of dihydrocinchonidine sulfate periodate needle crystals are enclosed. There is.
以下に前記マイクロカプセル6の作製方法を詳細に説
明する。The method for producing the microcapsules 6 will be described in detail below.
まず500ccのエルレンマイヤーフラスコに水168.0g、9
7%硫酸15.0g、シンコニジン40.0g、及び塩化パラジウ
ムの2%水溶液150ccを磁力攪拌機で攪拌しながら挿入
した。First, 168.0 g of water in a 500 cc Erlenmeyer flask, 9
15.0 g of 7% sulfuric acid, 40.0 g of cinchonidine, and 150 cc of a 2% aqueous solution of palladium chloride were inserted while stirring with a magnetic stirrer.
フラスコ中の空気は、水柱80〜100cmの加圧下に挿入
する水素で置換した。水素化反応はパラジウムが完全に
還元されるまで緩慢に進行し、この間充分に攪拌した。The air in the flask was replaced with hydrogen which was inserted under a pressure of 80-100 cm of water. The hydrogenation reaction proceeded slowly until palladium was completely reduced, and the mixture was sufficiently stirred during this period.
反応生成物をパラジウムから濾別し、攪拌しながら水
600ccに希釈した。反応生成物に充分な攪拌下に約25gの
50%苛性ソーダを急激に加えてPH9〜10にした。その後1
0分間攪拌を続けた。ジヒドロシンコニジンの無定形結
晶を真空濾過し、水で充分に洗浄した。次いで生成物を
できるだけ水分がなくなるまでつき固めてから、広げて
空気中で乾燥した。生成物は50%エタノール水から0〜
2℃で8〜10時間結晶させた。生成物は濾別して最少量
の50%冷エタノール水で洗浄し82℃で4時間乾燥してジ
ヒドロシンコニジンを得た。The reaction product is filtered off from palladium and stirred with water.
Diluted to 600cc. Approximately 25 g of reaction product with sufficient stirring
50% caustic soda was added rapidly to bring the pH to 9-10. Then 1
Stirring was continued for 0 minutes. Amorphous crystals of dihydrocinchonidine were vacuum filtered and washed thoroughly with water. The product was then compacted as dry as possible, then spread and dried in air. The product is 0% from 50% ethanol water
Crystallized at 2 ° C for 8-10 hours. The product was separated by filtration, washed with the minimum amount of cold 50% ethanol water, and dried at 82 ° C. for 4 hours to obtain dihydrocinchonidine.
ジヒドロシンコニジン3.06g、97%硫酸0.60g、2−エ
トキシエタノール20.0g、水10.0gの溶液と、ニトロセル
ロース14.17g、2−エトキシエタノール28.35g、トリク
レジルフォスフェート10.0gの溶液を混合し、よく攪拌
した。この溶液にヨウ化カルシウム0.40g、ヨウ素3.04
g、n−プロパノール12.0g、トリクレジルフォスフェー
ト35.0gの溶液を一気に加え、激しく攪拌した。30分の
攪拌後、液をガラス板上に広げて揮発性成分を除去し
た。Dihydrocinchonidine 3.06 g, 97% sulfuric acid 0.60 g, 2-ethoxyethanol 20.0 g, water 10.0 g solution and nitrocellulose 14.17 g, 2-ethoxyethanol 28.35 g, tricresyl phosphate 10.0 g solution mixed. , Stirred well. 0.40 g of calcium iodide and 3.04 of iodine were added to this solution.
A solution of g, n-propanol 12.0 g and tricresyl phosphate 35.0 g was added all at once, and the mixture was vigorously stirred. After stirring for 30 minutes, the liquid was spread on a glass plate to remove volatile components.
このペースト状物質100gをトリルアセテート150g中に
入れ、超音波でよく分散させて懸濁液を作製した。100 g of this paste-like substance was put in 150 g of tolyl acetate and well dispersed by ultrasonic waves to prepare a suspension.
そして、この懸濁液を株式会社日立製作所製高速冷却
遠心器タイプSCR20B、RPR-20-2ロータを用い、18000回
転/分(遠心加速度、39917g)で30分遠心分離をし、上
澄み液を捨てた。Then, this suspension was centrifuged at 18,000 rpm for 30 minutes using a high speed cooling centrifuge type SCR20B, RPR-20-2 rotor manufactured by Hitachi, Ltd., and the supernatant was discarded. It was
さらに沈澱物を2000回転/分(遠心加速度、492g)で
5分間遠心分離し、沈澱物を捨てた。Further, the precipitate was centrifuged at 2000 rpm (centrifugal acceleration, 492 g) for 5 minutes, and the precipitate was discarded.
この上澄み液を18000回転/分で30分間遠心分離を
し、沈澱物を回収した。この沈澱物にジトリデシルフタ
レート60gを加え、超音波で分散させた。その後、ドデ
カン40gを加えよく混合させサスペンションを得た。そ
こへ1.0gのポリオキシエチレンステアリルエーテル(日
光ケミカルズ株式会社製 NIKKOL BS-2)と2.0gのジオ
クチルジフェニルアミン(精工化学株式会社製ノンレッ
クスOD-R)を添加し、超音波でよく分散させた。The supernatant was centrifuged at 18,000 rpm for 30 minutes to collect the precipitate. 60 g of ditridecyl phthalate was added to this precipitate and dispersed by ultrasonic waves. Then, 40 g of dodecane was added and mixed well to obtain a suspension. 1.0 g of polyoxyethylene stearyl ether (NIKKOL BS-2 manufactured by Nikko Chemicals Co., Ltd.) and 2.0 g of dioctyldiphenylamine (Nonlex OD-R manufactured by Seiko Chemical Co., Ltd.) were added thereto and dispersed well by ultrasonic waves. .
これをホモミキサーを用いて高濃度のスチレンのジク
ロルメタン溶液へ分散させ60℃の温水中へ添加すること
によりマイクロカプセル6を得た。濾過してマイクロカ
プセル6を乾燥し、これを公知手法によりポリビニルブ
チラール膜に埋込んだ。そして、2枚のITO付きガラス
板の中へ上記のポリビニルブチラールを封入し、100℃
で200mmHgの減圧下20分処理をした。その後13気圧のオ
ートクレーブ中で130℃、30分処理をして第1図に示さ
れるように、安全ガラスに組み込まれた粒子分散型表示
素子Aを作製した。This was dispersed in a high-concentration solution of styrene in dichloromethane using a homomixer and added to warm water at 60 ° C. to obtain microcapsules 6. The microcapsules 6 were dried by filtration and embedded in a polyvinyl butyral film by a known method. Then, the above polyvinyl butyral is enclosed in two glass plates with ITO and the temperature is 100 ° C.
The sample was treated under reduced pressure of 200 mmHg for 20 minutes. Then, it was treated at 130 ° C. for 30 minutes in an autoclave at 13 atm to prepare a particle dispersion type display element A incorporated in safety glass as shown in FIG.
実施例1の粒子分散型表示素子Aは、第1図に示され
る第1透明電極3及び第2透明電極4とに電圧が印加さ
れないとき、マイクロカプセル6内の分散媒60中の偏光
性物質61は第3図に示されるようにランダムに分散して
おり、入射光R(可視光線の一部)は偏光性物質61に吸
収される。このため粒子分散型表示素子Aは透明な青色
に表示され、かつ、入射光Rの透過光量を減少させサン
シェードとして役立つ。そしてこの粒子分散型表示素子
Aは、サンシェードとしての機能を解除すべく第1透明
電極層3及び第2透明電極層4に50VRMS 400Hzの電圧を
印加したところ、青色透明から無色透明へすばやく変色
し、可逆的な応答を示し、かつ第2図に示されるように
印加の方向へ配向し、入射光R(可視光線の一部)を透
過させた。またガラスをハンマーで破損させた場合もガ
ラスおよび液が飛散せず安全ガラスの機能も具備してい
た。The particle-dispersed display device A of Example 1 has a polarizing substance in the dispersion medium 60 in the microcapsules 6 when no voltage is applied to the first transparent electrode 3 and the second transparent electrode 4 shown in FIG. 61 are randomly dispersed as shown in FIG. 3, and incident light R (a part of visible light) is absorbed by the polarizing substance 61. Therefore, the particle-dispersed display device A is displayed in a transparent blue color and reduces the amount of transmitted incident light R to serve as a sun shade. Then, in this particle dispersion type display element A, when a voltage of 50 VRMS 400 Hz was applied to the first transparent electrode layer 3 and the second transparent electrode layer 4 in order to cancel the function as the sunshade, the color rapidly changed from blue transparent to colorless transparent. , Showed a reversible response, and was oriented in the direction of application as shown in FIG. 2, and transmitted incident light R (a part of visible light). Further, even when the glass was broken with a hammer, the glass and the liquid did not scatter, and the glass also had the function of a safety glass.
(変形例1) 本変形例1の場合には、分散媒としてジブチルフタレ
ートを用いた以外は、実施例1と同じである。(Modification 1) The modification 1 is the same as the embodiment 1 except that dibutyl phthalate is used as the dispersion medium.
(変形例2) 本変形例2の場合には、第1透明電極3a及び第2透明
電極4aを2枚のポリエチレンテレフタレート(PET)フ
ィルム30a及び40aに形成した以外は、実施例と同様であ
る(第5図参照)。(Modification 2) This modification 2 is the same as the embodiment except that the first transparent electrode 3a and the second transparent electrode 4a are formed on two polyethylene terephthalate (PET) films 30a and 40a. (See FIG. 5).
(変形例3) 本変形例3の場合には、マイクロカプセル6を分散さ
せたポリビニルブチラール製透明樹脂層5aを用いるとと
もに、ポリブチルアセテートを中間膜50aとして用いた
以外は、実施例1と同様である(第5図参照)。(Modification 3) This modification 3 is the same as Example 1 except that the polyvinyl butyral transparent resin layer 5a in which the microcapsules 6 are dispersed is used and polybutyl acetate is used as the intermediate film 50a. (See FIG. 5).
[効果] 本考案の粒子分散型表示素子によれば、配向状態で光
を透過させ、ランダム状態で光を吸収(遮断)させる偏
光性物質を分散している液状フタル酸エステルは、沸点
が高く、耐熱性に優れているため、調光素子胞を含むポ
リビニルブチラールからなる透明樹脂層を一対の透明基
板間に介在させる工程で高熱が作用しても、蒸発しない
ので気泡を発生させず、変質しない利点をもつ。[Effects] According to the particle dispersion type display device of the present invention, the liquid phthalate ester in which a polarizing substance that transmits light in an aligned state and absorbs (blocks) light in a random state is dispersed has a high boiling point. Since it has excellent heat resistance, it does not evaporate even when high heat is applied in the process of interposing a transparent resin layer made of polyvinyl butyral containing a light control element cell between a pair of transparent substrates, so that it does not generate bubbles Not have the advantage.
さらに本考案では、偏光性物質が従来の表示素子のよ
うに、一対の透明基板の間に形成された広いセル空間内
に分散するものと異なり、小胞状の小空間内に分散され
るため、偏光性物質の凝集するような不具合を防止しや
すくなり表示機能の低下を少なくすることができる。Further, in the present invention, unlike the conventional display element in which the polarizing substance is dispersed in the wide cell space formed between the pair of transparent substrates, it is dispersed in the vesicle-shaped small space. It is easy to prevent problems such as aggregation of the polarizing substance, and it is possible to reduce deterioration of the display function.
また本考案の粒子分散型表示素子では、液状フタル酸
エステルと、この液状フタル酸エステル中に分散された
偏光性物質とからなる調光素子胞が第1、第2透明基板
間に挟持されているので破損しにくく、また一部が破損
した場合であっても、各調光素子胞毎にサスペンション
を備えているので、その一定量が保持でき、粒子分散型
表示素子としての機能が損われることがない。また製造
時におけるガラス間のギャップの調整が容易となるとと
もに、セルの面積が大きくなることによる透明基板の変
形やソリなどの構造上の問題を低減することができる。Further, in the particle-dispersed display device of the present invention, a light control device cell composed of a liquid phthalate ester and a polarizing substance dispersed in the liquid phthalate ester is sandwiched between the first and second transparent substrates. Since it has a suspension for each light control element cell even if it is partially damaged, it can hold a certain amount and impairs the function as a particle dispersion type display element. Never. In addition, it is possible to easily adjust the gap between the glasses at the time of manufacturing, and it is possible to reduce structural problems such as deformation and warpage of the transparent substrate due to an increase in cell area.
第1図は本考案の実施例1の粒子分散型表示素子を示す
縦断面図である。第2図は第1図におけるマイクロカプ
セルを拡大して示し、電圧が印加され偏光性物質の配向
した状態を示す拡大縦断面図である。第3図は、第2図
におけるマイクロカプセルに電圧を印加しない状態であ
り、偏光性物質が不配向状態(ランダムな状態)を示す
拡大縦断面図である。第4図は第1図における粒子分散
型表示素子を、自動車のフロントガラスにサンシェード
として用いた使用例を示す斜視図である。第5図は、実
施例1の粒子分散型表示素子の第2、第3の変形例を示
す縦断面図である。 1……第1透明基板、2……第2透明基板 3、3a……第1透明電極 4、4a……第2透明電極 5、5a……ポリビニルブチラール製透明樹脂層 6……調光素子胞としてのマイクロカプセル 60……分散媒 61……偏光性物質FIG. 1 is a vertical sectional view showing a particle dispersion type display device of Example 1 of the present invention. FIG. 2 is an enlarged vertical cross-sectional view showing the microcapsule in FIG. 1 in an enlarged manner and showing a state in which a polarizing substance is oriented by applying a voltage. FIG. 3 is an enlarged vertical cross-sectional view showing a state in which a voltage is not applied to the microcapsules in FIG. 2 and the polarizing substance is in a non-aligned state (random state). FIG. 4 is a perspective view showing a usage example in which the particle-dispersed display device in FIG. 1 is used as a sunshade on a windshield of an automobile. FIG. 5 is a vertical sectional view showing second and third modifications of the particle dispersion type display device of Example 1. 1 ... 1st transparent substrate, 2 ... 2nd transparent substrate 3, 3a ... 1st transparent electrode 4, 4a ... 2nd transparent electrode 5, 5a ... Polyvinyl butyral transparent resin layer 6 ... Light control element Microcapsules as cells 60 …… Dispersion medium 61 …… Polarizing substance
───────────────────────────────────────────────────── フロントページの続き (72)考案者 龍田 成人 愛知県愛知郡長久手町大字長湫字横道41 ―1 株式会社豊田中央研究所内 (72)考案者 広瀬 美治 愛知県愛知郡長久手町大字長湫字横道41 ―1 株式会社豊田中央研究所内 (72)考案者 臼杵 有光 愛知県愛知郡長久手町大字長湫字横道41 ―1 株式会社豊田中央研究所内 (56)参考文献 特開 昭63−137211(JP,A) 特開 昭53−144893(JP,A) ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor, Tatsuta Adult, Nagakute-cho, Aichi-gun, Aichi-gun, Nagaminate, Yokomichi 41-1 Toyota Central Research Institute, Ltd. Yokoichi 41-1 Toyota Central Research Institute Co., Ltd. (72) Creator Usuki Arimitsu Aichi Prefecture Aichi-gun Nagakute-machi Oogata Yoko Yoko 41-1 Toyota Central Research Institute Co., Ltd. (56) Reference JP-A-63-137211 (JP) , A) JP-A-53-144893 (JP, A)
Claims (1)
一対の透明電極と、 上記の対向する透明電極の間に設けた調光素子胞を含む
ポリビニルブチラールからなる透明樹脂層と、よりな
り、 前記調光素子胞は液状フタル酸エステルと、該フタル酸
エステル中に分散された偏光性物質とを含むことを特徴
とする粒子分散型表示素子。1. A transparent substrate facing each other at a distance, a pair of transparent electrodes respectively formed on mutually facing surfaces of the transparent substrate, and a light control device cell provided between the facing transparent electrodes. And a transparent resin layer made of polyvinyl butyral containing, wherein the light control device cell includes a liquid phthalate ester and a polarizing substance dispersed in the phthalate ester. element.