JP2505031B2 - An easily openable seal material composed of a polyolefin composition or a laminate thereof - Google Patents
An easily openable seal material composed of a polyolefin composition or a laminate thereofInfo
- Publication number
- JP2505031B2 JP2505031B2 JP63245378A JP24537888A JP2505031B2 JP 2505031 B2 JP2505031 B2 JP 2505031B2 JP 63245378 A JP63245378 A JP 63245378A JP 24537888 A JP24537888 A JP 24537888A JP 2505031 B2 JP2505031 B2 JP 2505031B2
- Authority
- JP
- Japan
- Prior art keywords
- ethylene
- weight
- parts
- sealing
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 発明の技術分野 本発明は、ポリオレフィン組成物からなる易開封性シ
ール材料並びに該組成物を基材樹脂層に積層した積層体
からなる易開封性シール材料に関する。TECHNICAL FIELD OF THE INVENTION The present invention relates to an easily openable seal material comprising a polyolefin composition and an easily openable seal material comprising a laminate in which the composition is laminated on a base resin layer.
発明の技術的背景ならびにその問題点 食品包装用のフィルム素材はその種類も多く、単層フ
ィルムあるいは多層フィルムに関して種々の提案があ
る。一般には、密封の段階でヒートシールが行われてい
るため、単層フィルムにあってはヒートシール可能な素
材が常用されており、また多層フィルムにあっては最内
層にヒートシール可能な素材層が形成されたものが常用
されている。TECHNICAL BACKGROUND OF THE INVENTION AND PROBLEMS THEREOF There are many types of film materials for food packaging, and various proposals have been made regarding monolayer films or multilayer films. In general, heat sealing is performed at the sealing stage, so heat-sealable materials are commonly used for single-layer films and heat-sealable material layers for the innermost layer of multilayer films. The one in which is formed is commonly used.
このようなヒートシール素材として、ポリオレフィン
系重合体、例えばポリエチレン、ポリプロピレン、ある
いはこれら汎用ポリオレフィンにエチレン−酢酸ビニル
共重合体、ポリブテン−１などを混合した樹脂組成物な
どが知られている。As such a heat-sealing material, a polyolefin polymer such as polyethylene, polypropylene, or a resin composition obtained by mixing an ethylene-vinyl acetate copolymer, polybutene-1 and the like with these general-purpose polyolefins is known.
ところで、ヒートシールの形態として、ヒートシール
面が別の素材で形成される場合と、ポテトチップ、即席
ラーメン、スナック菓子などのような包装袋のように、
同一素材でヒートシールされる場合がある。前者の例と
しては、豆腐、ゼリー、羊かん、菓子などの食品を包装
するために、通常、ポリプロピレンなどの容器に、蓋体
としての合成樹脂フィルムが接着されて用いられてい
る。このようなフィルムとして前記のような樹脂あるい
は樹脂組成物を用いると、容器と蓋体とのシール強度が
必要以上に強いため、手による開封ができないという問
題点があった。By the way, as a form of heat sealing, when the heat sealing surface is formed of another material, like a packaging bag such as potato chips, instant ramen, snacks, etc.,
It may be heat-sealed with the same material. As an example of the former, in order to package foods such as tofu, jelly, sheepskin and confectionery, a synthetic resin film as a lid is usually used by being adhered to a container such as polypropylene. When the resin or the resin composition as described above is used as such a film, the sealing strength between the container and the lid is unnecessarily strong, so that there is a problem that it cannot be opened by hand.
このため種々の易開封性シール材料が提案されている
が、一般に易開封性シール材料は、密封性に劣っていた
り、ヒートシール面に挾雑物が入り込んだ場合に接着力
が大きく低下したり、あるいは熱湯中で加熱されたりす
ると、やはり接着力が大きく低下したりするという問題
点があった。さらにヒートシール面を加熱してシールす
る際に、過度なシール強度を示す温度範囲が狭いという
問題点もあった。For this reason, various easy-open seal materials have been proposed, but in general, the easy-open seal material is inferior in hermeticity, or the adhesive strength is greatly reduced when foreign matter enters the heat-sealing surface. Or, when it is heated in hot water, there is a problem that the adhesive strength is greatly reduced. Further, there is a problem that the temperature range showing excessive sealing strength is narrow when heating and sealing the heat-sealed surface.
例えば粘着付与樹脂を含む含有するヒートシール性の
樹脂組成物の提案があるが、一般に耐熱性、耐油性に劣
っているため、その用途は限定されていた。また粘着付
与樹脂を含有しない系として、たとえば特開昭60−2392
38号公報には、メルトインデックスが0.5〜100g/10分で
あるアイオノマー樹脂100重量部に対して、エチレン含
量が１〜50重量％であるエチレン・プロピレン共重合体
５〜65重量部を混合してなるヒートシール層を有してな
る、オレフィン系樹脂をシール相手とする易開封性シー
ル材料が開示されている。For example, there has been proposed a heat-sealable resin composition containing a tackifying resin, but its use is limited because it is generally inferior in heat resistance and oil resistance. Further, as a system containing no tackifying resin, for example, JP-A-60-2392
No. 38 discloses a mixture of 5 to 65 parts by weight of an ethylene / propylene copolymer having an ethylene content of 1 to 50% by weight with respect to 100 parts by weight of an ionomer resin having a melt index of 0.5 to 100 g / 10 minutes. An easily openable sealing material having an olefin resin as a sealing partner is disclosed, which has a heat-sealing layer as described above.
ところがこの易開封性シール材料は、密封性、易開封
性などの点で必ずしも充分に満足できるものではなかっ
た。However, this easy-open seal material is not always sufficiently satisfactory in terms of sealing property, easy opening property, and the like.
さらに従来提案されている多くの易開封性シール材料
は、通常異種材料にヒートシールする場合に適用される
べきものであり、同一素材でヒートシールされる場合に
は易開封性を示さないものがほとんどであった。Furthermore, many of the easily openable sealing materials that have been conventionally proposed should normally be applied when heat-sealing different kinds of materials, and those that do not show easy-opening property when heat-sealed with the same material. It was almost.
発明の目的 本発明は、上記のような従来技術に伴なう問題点を解
決しようとするものであって、シール相手面がオレフィ
ン系樹脂であっても、あるいは同一の材料から形成され
ていても、密封性、易開封性、耐熱性、耐油性に優れた
ポリオレフィン組成物からなる易開封性シール材料を提
供することを目的としている。OBJECT OF THE INVENTION The present invention is intended to solve the problems associated with the above-mentioned conventional techniques, and the sealing mating surface is made of the same material even if it is an olefin resin. Another object of the present invention is to provide an easily openable seal material composed of a polyolefin composition having excellent sealing property, easy opening property, heat resistance and oil resistance.
本発明はまた、それ自体、包装袋、蓋材のような易ヒ
ートシール性の積層体からなる易開封性シール材料を提
供することを目的としている。Another object of the present invention is to provide an easily-openable seal material, which itself is composed of an easily heat-sealable laminate such as a packaging bag and a lid material.
発明の概要 本発明に係るポリオレフィン組成物からなる易開封性
シール材料は、プロピレン系重合体20〜70重量部、ポリ
エチレン又はエチレンを主体とするエチレン・α−オレ
フィン共重合体20〜60重量部及びα，β−飽和カルボン
ン酸単位が１〜６モル％のエチレン・α，β−不飽和カ
ルボン酸共合体又はその金属塩５〜40重量部（全体で10
0重量部）の割合で配合してなることを特徴としてい
る。また本発明に係る積層体からなる易開封性シール材
料は、基材層に、必要に応じて接着材を介して、前記ポ
リオレフィン組成物層を積層してなることを特徴として
いる。Summary of the invention The easily-openable sealing material comprising the polyolefin composition according to the present invention is a propylene-based polymer 20 to 70 parts by weight, an ethylene / α-olefin copolymer mainly composed of polyethylene or ethylene 20 to 60 parts by weight, and 5 to 40 parts by weight of an ethylene / α, β-unsaturated carboxylic acid copolymer or a metal salt thereof having an α, β-saturated carboxylic acid unit of 1 to 6 mol% (total 10
(0 parts by weight). Further, the easily openable seal material comprising the laminate according to the present invention is characterized in that the polyolefin composition layer is laminated on the base material layer, if necessary with an adhesive.
発明の具体的説明 以下本発明に係るポリオレフィン組成物からなる易開
封性シール材料およびこのポリオレフィン組成物を積層
してなる積層体からなる易開封性シール材料を積層して
なる積層体について具体的に説明する。DETAILED DESCRIPTION OF THE INVENTION An easily openable seal material comprising the polyolefin composition according to the present invention and a laminate obtained by laminating the easily openable seal material comprising a laminate obtained by laminating the polyolefin composition are specifically described below. explain.
本発明で用いられるプロピレン系重合体は、プロピレ
ン単独重合体またはプロピレンを主体とする共重合体か
ら選ばれる高結晶性の重合体であり、とくに共重合体が
好適である。The propylene-based polymer used in the present invention is a highly crystalline polymer selected from a propylene homopolymer and a propylene-based copolymer, and a copolymer is particularly preferable.
プロピレン共重合体としては、プロピレンと、エチレ
ンおよびまたは炭素数が４〜８程度のα‐オレフィンと
の共重合体が用いられ、エチレンまたはα‐オレフィン
の含量は、0.5〜20モル％、好ましくは１〜10モル％で
ある。As the propylene copolymer, a copolymer of propylene and ethylene and / or an α-olefin having 4 to 8 carbon atoms is used, and the content of ethylene or α-olefin is 0.5 to 20 mol%, preferably It is 1 to 10 mol%.
このようなプロピレン共重合体は、メルトフローレー
ト（230℃、2160g荷重）が0.1〜500g/10分、とくに0.5
〜100g/10分程度であることが好ましい。Such a propylene copolymer has a melt flow rate (230 ° C, 2160 g load) of 0.1 to 500 g / 10 minutes, especially 0.5
It is preferably about 100 g / 10 minutes.
本発明で用いられるポリエチレン又はエチレンを主体
とするエチレン・α‐オレフィン共重合体は、高圧法又
は中低圧法によって、エチレンの単独重合又はエチレン
とα‐オレフィンの共重合によって得られるものであ
る。その密度は、通常は0.88〜0.98g/cm3、好ましくは
0.90〜0.96g/cm3であることが望ましい。またこのポリ
エチレンまたはエチレン・α‐オレフィン共重合体は、
190℃、2160g荷重におけるメルトローレートが0.1〜500
g/10分、とくに0.5〜100g/10分程度であることが好まし
い、これらエチレン重合体としては、また中低圧法で製
造されるエチレン・α‐オレフィン共重合体を用いるこ
とがより好ましい。The ethylene / ethylene-α-olefin copolymer mainly composed of polyethylene used in the present invention is obtained by homopolymerization of ethylene or copolymerization of ethylene and α-olefin by a high pressure method or a medium / low pressure method. Its density is usually 0.88 to 0.98 g / cm 3 , preferably
It is preferably 0.90 to 0.96 g / cm 3 . Also, this polyethylene or ethylene / α-olefin copolymer is
Melt low rate at 190 ℃, 2160g load is 0.1 ~ 500
It is preferably g / 10 minutes, particularly about 0.5 to 100 g / 10 minutes. As these ethylene polymers, it is more preferable to use an ethylene / α-olefin copolymer produced by a medium-low pressure method.
エチレン・α‐オレフィン共重合体におけるα‐オレ
フィン成分としては、プロピレン、1-ブテン、1-ヘキセ
ン、1-オクテン、1-デセン、4-メチル‐1-ペンテンなど
を例示することができる。Examples of the α-olefin component in the ethylene / α-olefin copolymer include propylene, 1-butene, 1-hexene, 1-octene, 1-decene, 4-methyl-1-pentene and the like.
本発明で用いられるエチレン・α，β‐不飽和カルボ
ン酸共重合体又はその金属塩は、他にα，β‐不飽和カ
ルボン酸エステルやカルボン酸ビニルエステルを共重合
成分として含んでいてもよい。The ethylene / α, β-unsaturated carboxylic acid copolymer or its metal salt used in the present invention may further contain α, β-unsaturated carboxylic acid ester or carboxylic acid vinyl ester as a copolymerization component. .
上記のようなα，β‐不飽和カルボン酸としては、ア
クリル酸、メタクリル酸、マレイン酸、マレイン酸モノ
メチルなどを例示することができる。またα，β‐不飽
和カルボン酸エステルとしては、アクリル酸又は、メタ
クリル酸の炭素数１〜８のアルキルエステル、例えばメ
チル、エチル、プロピル、n-ブチル、イソブチル、2-エ
チルヘキシルなどのエステルを例示することができる。
またカルボン酸ビニルエステルとしては酢酸ビニルエス
テルを代表例として示すことができる。Examples of the above α, β-unsaturated carboxylic acid include acrylic acid, methacrylic acid, maleic acid, monomethyl maleate and the like. Further, as the α, β-unsaturated carboxylic acid ester, an alkyl ester of acrylic acid or methacrylic acid having 1 to 8 carbon atoms, for example, an ester such as methyl, ethyl, propyl, n-butyl, isobutyl and 2-ethylhexyl is exemplified. can do.
As the carboxylic acid vinyl ester, vinyl acetate can be shown as a typical example.
金属塩としては、リチウム、ナトリウム、カリウム、
セシウムなどの１価金属イオン、亜鉛、銅、マグネシウ
ム、カルシウム、ストロンチウム、バリウムなどの２価
金属イオン、アンモニウム、鉄、などの３価金属イオン
などの塩を使用することができる。このような共重合体
としては、エチレン単位が85〜99.5モル％、とくに94〜
99モル％、α，β‐不飽和カルボン酸単位が１〜６モル
％、その他のモノマーが０〜10モル％とくに０〜６モル
％の共重合体を用いるか、あるいは中和度が10％以下、
とくに80％以下となるように金属塩化したものが好適で
ある。Metal salts include lithium, sodium, potassium,
It is possible to use salts of monovalent metal ions such as cesium, divalent metal ions such as zinc, copper, magnesium, calcium, strontium and barium, and trivalent metal ions such as ammonium and iron. As such a copolymer, ethylene unit is 85 to 99.5 mol%, especially 94 to
Use a copolymer of 99 mol%, 1 to 6 mol% of α, β-unsaturated carboxylic acid unit and 0 to 10 mol% of other monomers, especially 0 to 6 mol%, or a neutralization degree of 10%. Less than,
Particularly preferred is a metal chloride so that the content thereof is 80% or less.
より具体的には、エチレン‐アクリル酸共重合体、エ
チレン‐メタクリル酸共重合体、エチレン‐アクリル酸
エチル‐アクリル酸共重合体、エチレン‐アクリル酸イ
ソブチル‐メタクリル酸共重合体あるいはこれらの塩な
どを一例としてあげることができる。More specifically, ethylene-acrylic acid copolymer, ethylene-methacrylic acid copolymer, ethylene-ethyl acrylate-acrylic acid copolymer, ethylene-isobutyl acrylate-methacrylic acid copolymer or salts thereof, etc. Can be given as an example.
これら共重合体またはその金属塩は、190℃における
メルトフローレートが0.1〜500g/10分、とくに0.5〜100
g〜10分程度であることが好ましい。These copolymers or metal salts thereof have a melt flow rate at 190 ° C. of 0.1 to 500 g / 10 minutes, particularly 0.5 to 100 g.
It is preferably about g to 10 minutes.
本発明に係るポリオレフィン組成物においては、プロ
ピレン系重合体は20〜70重量部、好ましくは30〜60重量
部、ポリエチレン又はエチレン・α‐オレフィン共重合
体は20〜60重量部、好ましくは25〜50重量部、エチレン
・α，β‐不飽和カルボン酸共重合体又はその金属塩は
５〜40重量部、好ましくは10〜30重量部（これらは合計
して100重量部）となる割合で配合される。このプロピ
レン系重合体の量が20重量部未満であると、広範囲な温
度域において適度なシール強度を示さず、またポリプロ
ピレンとの共押出フィルム化に際し、ポリプロピレン層
とシール層の間で層間剥離を起こし易くなるため好まし
くなく、一方70重量部を越えると、優れた易開封性を示
さず、また広範囲な温度域において適度なシール強度を
示さないので好ましくない。In the polyolefin composition according to the present invention, the propylene-based polymer is 20 to 70 parts by weight, preferably 30 to 60 parts by weight, the polyethylene or ethylene-α-olefin copolymer is 20 to 60 parts by weight, preferably 25 to 50 parts by weight, 5 parts by weight of ethylene / α, β-unsaturated carboxylic acid copolymer or its metal salt, preferably 10 to 30 parts by weight (these are 100 parts by weight in total). To be done. When the amount of this propylene-based polymer is less than 20 parts by weight, it does not exhibit an appropriate seal strength in a wide temperature range, and when forming a coextrusion film with polypropylene, delamination between the polypropylene layer and the seal layer occurs. On the other hand, if it exceeds 70 parts by weight, excellent easy-opening property is not exhibited and appropriate seal strength is not exhibited in a wide temperature range, which is not preferable.
一方、ポリエチレン又はエチレン・α‐オレフィン共
重合体の量が20重量部未満であると、シール強度が弱
く、一方60重量部を越えると、優れた易開封性を示さ
ず、また広範囲なシール温度域において適度なシール強
度を示さないため好ましくない。On the other hand, when the amount of polyethylene or ethylene / α-olefin copolymer is less than 20 parts by weight, the sealing strength is weak, while when it exceeds 60 parts by weight, excellent easy-opening property is not exhibited and a wide sealing temperature range is achieved. It is not preferable because it does not show an appropriate seal strength in the range.
さらにエチレン・α，β‐不飽和カルボン酸共重合体
又はその金属塩の量が前記範囲より少ない、優れた易開
封性を示さず、また広範囲な温度域において適度なシー
ル強度を示さないので好ましくなく、一方40重量部を越
えると、シール強度が弱すぎるため好ましくない。Further, the amount of the ethylene / α, β-unsaturated carboxylic acid copolymer or the metal salt thereof is less than the above range, does not exhibit excellent easy-opening property, and does not exhibit appropriate seal strength in a wide temperature range, which is preferable. On the other hand, if it exceeds 40 parts by weight, the sealing strength is too weak, which is not preferable.
本発明に係る組成物は、前記各成分を同時的にまたは
逐次的にドライブレンドまたはメルトブレンドすること
によって調製することができる。ドライブレンドの場合
には成形機中でブレンド物が溶融可塑化され、均一に溶
融混合され押し出される。メルトブレンドの場合には、
単軸押出機、２軸押出機、バンバリーミキサーなどの各
種ミキサー、ロール、各種ニーダーなどを用いて溶融混
合すればよく、その混合順序には特に制限がない。The composition according to the present invention can be prepared by dry-blending or melt-blending the above components simultaneously or sequentially. In the case of dry blending, the blended product is melt-plasticized in a molding machine, uniformly melt-mixed and extruded. In the case of melt blending,
A single-screw extruder, a twin-screw extruder, various mixers such as a Banbury mixer, rolls, various kneaders and the like may be used for melt mixing, and the mixing order is not particularly limited.
また本発明に係るポリオレフィン組成物中には、組成
物の性能を損わない範囲内において、酸化防止剤、耐候
安定剤、滑剤、防曇剤などを添加することも可能であ
る。It is also possible to add an antioxidant, a weather resistance stabilizer, a lubricant, an antifogging agent, etc. to the polyolefin composition according to the present invention within a range that does not impair the performance of the composition.
このようにして得られるポリオレフィン組成物を、た
とえばポリプロピレン、ポリエチレンテレフタレート、
ポリ塩化ビニリデン、エチレン‐酢酸ビニル共重合体ケ
ン化物、ポリアミド、アルミニウム箔、金属蒸着フィル
ムなどの基材上に、必要に応じて高圧法ポリエチレン、
エチレン‐α，β‐不飽和カルボン酸共重合体等の樹脂
あるいはアンカーコート剤などの接着剤を介して積層さ
れる。The polyolefin composition thus obtained, for example, polypropylene, polyethylene terephthalate,
Polyvinylidene chloride, saponified ethylene-vinyl acetate copolymer, polyamide, aluminum foil, metallized film, etc.
It is laminated via a resin such as an ethylene-α, β-unsaturated carboxylic acid copolymer or an adhesive such as an anchor coating agent.
積層体の製造方法は、とくに限定されないが、本発明
に係る組成物をシール層に用いる場合、たとえば次のよ
うな方法によって行うことができる。The method for producing the laminate is not particularly limited, but when the composition according to the present invention is used for the seal layer, it can be performed, for example, by the following method.
（１）熱融着法 予め成形した基材とシール層フィルムとを、接着剤を
用いて積層体とする場合には、基材、接着剤、シール層
フィルムを熱圧着する方法、あるいは基材、シール層の
少くとも一方の面に共押出法、押出被覆法等により予め
接着剤を積層した後熱圧着する方法が採用される。(1) Heat fusion method When a preformed base material and a seal layer film are formed into a laminate using an adhesive, a method of thermocompression bonding the base material, the adhesive and the seal layer film, or the base material A method is used in which an adhesive is preliminarily laminated on at least one surface of the seal layer by a coextrusion method, an extrusion coating method, or the like, and then thermocompression bonding is performed.
（２）サンドイッチラミネーション法 Ｔ−ダイ法などによる接着剤の溶融膜を介して基材と
シール層を貼り合せる方法である。(2) Sandwich lamination method This is a method in which the base material and the seal layer are bonded together via a molten film of an adhesive by the T-die method or the like.
（３）共押出法 基材とシール層とを、あるいは基材、接着剤層、シー
ル層を共押出成形法で積層する方法である。(3) Coextrusion method This is a method of laminating the base material and the seal layer, or laminating the base material, the adhesive layer, and the seal layer by the coextrusion molding method.
（４）接着剤法 基材またはシール層の少くとも一方の面に接着剤を塗
布し圧着、接着させる方法である。(4) Adhesive Method This is a method in which an adhesive is applied to at least one surface of the base material or the seal layer, and pressure-bonded.
もちろん、これらの方法は、例えば（４）接着剤法で
接着剤を塗布した基材を、（２）サイドイッチラミネー
ション法により別の接着剤の溶融膜を介してシール層と
貼り合わせる方法のように組合せて使用することも可能
である。Of course, these methods are, for example, (4) a method in which a base material coated with an adhesive by an adhesive method is bonded to a seal layer via a melt film of another adhesive by (2) a side-itch lamination method. It is also possible to use in combination with.
とくにポリプロピレンなどの基材を用いた場合には、
共押出ラミネート法により積層することができる。Especially when using a base material such as polypropylene,
It can be laminated by a coextrusion laminating method.
なお基材、シール層は接着力を向上させるために、そ
の表面を公知の方法例えばコロナ処理等の操作を事前に
行っておくことも可能である。In order to improve the adhesive strength of the base material and the seal layer, the surface thereof may be subjected to a known method such as corona treatment in advance.
シール面の厚みは、特に限定されないが、一般に５〜
200μｍ、好ましくは10〜50μｍ程度である。基材面の
厚みも任意であるが、一般に２〜500μｍ、好ましくは
５〜100μｍ程度である。The thickness of the sealing surface is not particularly limited, but generally 5 to
The thickness is 200 μm, preferably about 10 to 50 μm. Although the thickness of the surface of the base material is arbitrary, it is generally 2 to 500 μm, preferably 5 to 100 μm.
このようにして得られた積層体からなる易開封性シー
ル材料は、同一のシール材と接着させることができ、こ
の場合にも接着面は易開封性を示す。すなわち、基材上
に前記組成物をヒートシール面として形成した積層同士
を、互いにヒートシール面を接するようにヒートシール
することができ、このようにしてヒートシールされた接
合面は優れた密封性を有するとともに易開封性を示す。The easily openable sealing material composed of the laminate thus obtained can be adhered to the same sealing material, and in this case as well, the adhesive surface exhibits easy opening. That is, it is possible to heat-seal a laminate in which the composition is formed as a heat-sealing surface on a substrate so that the heat-sealing surfaces are in contact with each other, and thus the heat-sealed joint surface has excellent sealing property. And has an easy opening property.
しかも本発明に係る組成物を基材上にヒートシール面
として有するシール材同士をヒートシールする際には、
広範囲な温度域たとえば130〜160℃において適度なシー
ル強度を示す。Moreover, when heat-sealing the sealing material having the composition according to the present invention as the heat-sealing surface on the substrate,
It exhibits appropriate seal strength in a wide temperature range, for example, 130 to 160 ° C.
前記のようにして得られた積層体からなる易開封性シ
ール材料は、本発明の組成物側をヒートシール面として
ポリオレフィン系樹脂に対して接着した場合にも、接合
面は優れた密封性を有するとともに易開封性を示す。The easy-open seal material composed of the laminate obtained as described above has excellent sealing property even when the composition side of the present invention is adhered to a polyolefin resin as a heat-sealing surface. It has an easy opening property.
相手面としてのポリオレフィン系樹脂としては、ポリ
プロピレン、低密度ポリエチレン、エチレン‐酢酸ビニ
ル共重合体などが用いられ、これらのポリオレフィン系
樹脂は通常容器本体の形状とされている。Polypropylene, low density polyethylene, ethylene-vinyl acetate copolymer and the like are used as the polyolefin resin as the mating surface, and these polyolefin resins are usually in the shape of the container body.
そして本発明に係る積層体からなる易開封性シール材
料は、通常、上記のような容器本体に対する蓋体として
用いられる。The easy-open seal material comprising the laminate according to the present invention is usually used as a lid for the container body as described above.
このような使用態様でヒートシールする際には、広範
囲な温度域たとえば140〜200℃において適度なシール強
度を示す。その上、得られた接合体は、熱湯中あるいは
電子レンジ中で加熱されても接着力が大きく低下するこ
とがないという優れた特性を有する。When heat-sealing in such a usage mode, it exhibits appropriate sealing strength in a wide temperature range, for example, 140 to 200 ° C. In addition, the obtained joined body has an excellent property that the adhesive strength does not significantly decrease even when heated in hot water or in a microwave oven.
発明の効果 本発明に係るポリオレフィン組成物からなる易開封性
シール材料をヒートシール層に用いた場合、かかるヒー
トシール層同士でヒートシールした場合にもあるいはオ
レフィン系樹脂に対してヒートシールする場合にも、と
もに優れた密封性、優れた易開封性を有し、かつ広範囲
な温度域において適当のシール強度を示す。そしてこの
ようなヒートシール面は、耐熱性、耐油性に優れている
ので、油性食品用包装材あるいは加熱使用される包装材
などに好適である。EFFECT OF THE INVENTION When an easily openable sealing material comprising the polyolefin composition according to the present invention is used for the heat-sealing layer, even when heat-sealing between the heat-sealing layers, or when heat-sealing the olefin resin. Both have excellent sealing property and excellent easy-opening property, and exhibit appropriate sealing strength in a wide temperature range. Since such a heat-sealed surface has excellent heat resistance and oil resistance, it is suitable as a packaging material for oily foods, a packaging material to be used under heating, or the like.
実施例 以下に実施例により本発明を説明するが、本発明はこ
れら実施例に限定されるものではない。Examples The present invention is described below with reference to examples, but the present invention is not limited to these examples.
なお、実施例で使用した重合体およびシール強度の測
定法を以下に示す。The polymers used in the examples and the methods for measuring the seal strength are shown below.
（１）使用した重合体 （ａ）酸コポリマー：エチレン‐メタクリル酸共重合体
（酸含量９重量％）であり、MFRは3g/10分である。(1) Polymer used (a) Acid copolymer: ethylene-methacrylic acid copolymer (acid content 9% by weight), and MFR is 3 g / 10 minutes.
（ｂ）中密度ポリエチレン・三井石油化学工業（株）製
中密度ポリエチレン（ネオゼックス:NZ3510F）であり、
密度は0.935g/cm3であり、MFRは1.6g/10分である。(B) Medium-density polyethylene, which is Mitsui Petrochemical Industrial Co., Ltd. medium-density polyethylene (Neozex: NZ3510F),
The density is 0.935 g / cm 3 and the MFR is 1.6 g / 10 minutes.
（ｃ）低圧法低密度ポリエチレン（LLDPE）：三井石油
化学工業（株）製のLLDPE（ウルトゼックス:VZ1520L）
であり、密度は0.915g/cm3であり、MFRは2.0g/10分であ
る。(C) Low pressure low density polyethylene (LLDPE): LLDPE manufactured by Mitsui Petrochemical Industry Co., Ltd. (Ultzex: VZ1520L)
And the density is 0.915 g / cm 3 and the MFR is 2.0 g / 10 min.
（ｄ）エチレン‐1-ブテン共重合体：密度は0.88g/cm3
であり、MFRは3.69g/10分である。(D) Ethylene-1-butene copolymer: Density 0.88 g / cm 3
And the MFR is 3.69 g / 10 minutes.
（ｅ）ポリプロピレン：三井石油化学工業（株）製ポリ
プロピレンF 65.8（プロピレン・エチレンランダムポリ
マー）であり、密度は0.91g/cm3であり、MFRは6.0g/10
分である。(E) Polypropylene: polypropylene F 65.8 (propylene / ethylene random polymer) manufactured by Mitsui Petrochemical Industries, Ltd., density 0.91 g / cm 3 , MFR 6.0 g / 10
Minutes.
（２）シール強度の測定 （ａ）面々ヒートシール強度の測定法 片面加熱方式のヒートシーラーを用いて、 シール温度:120 130 140 150 160 170 180℃ シール圧力（実圧）:2kg/cm2 シール時間:0.5秒 シールバー巾:10mm のシール条件で面々ヒートシールを行なった。(2) Seal strength measurement (a) Face-to-face heat seal strength measurement method Using a single-sided heat sealer, seal temperature: 120 130 140 150 160 170 180 ° C Seal pressure (actual pressure): 2 kg / cm 2 seal Time: 0.5 seconds Seal bar width: Heat sealing was performed on each side under the sealing condition of 10 mm.
またシール強度の測定は、15mm巾の試片を引張速度30
0mm/minの条件で行なった。In addition, the seal strength was measured using a 15 mm wide specimen at a pulling speed of 30
It was performed under the condition of 0 mm / min.
（ｂ）ポリプロピレン製トレーにタ対するシール強度の
測定法 片面加熱方式のトレー用ヒートシールを用いて実施し
た。(B) Method for measuring seal strength against polypropylene tray One-sided heating heat sealing for trays was performed.
使用トレー：ポリプロピレン製（縦80×横110×深さ40m
m） シール温度:160℃、180℃ シール圧力:4kg/cm2 シール時間:1秒 シールバー巾:3mm なおシール性能としては、単に蓋材フィルムをトレー
にシールした場合、トレー内に水を完全に充填しシール
した場合、および水充填トレーを120℃、30分オートク
レーブ中に放置した場合のそれぞれについて、ブラン
ク、水充填（水挾雑物）シール性、レトルト処理後のシ
ール後の３つのシール性能を評価した。Tray used: polypropylene (length 80 x width 110 x depth 40 m
m) Sealing temperature: 160 ℃, 180 ℃ Sealing pressure: 4kg / cm 2 Sealing time: 1 second Seal bar width: 3mm As for the sealing performance, if the lid material film is simply sealed on the tray, the water in the tray is completely removed. Blank, water-filled (water-contaminated) sealability, and three seals after sealing after retort treatment, when filled with water and sealed, and when the water-filled tray was left in an autoclave for 30 minutes at 120 ° C. The performance was evaluated.
なおシール強度の測定は15mm巾の試片を、引張速度30
0mm/minの条件で行なった。The seal strength was measured using a 15 mm wide specimen at a pulling speed of 30
It was performed under the condition of 0 mm / min.
実施例１ 酸コポリマー20重量部と、中密度ポリエチレン40重量
部と、ポリプロピレン40重量部とを樹脂温度180℃の条
件下で単軸押出機を用いて溶融混練した。この組成物を
樹脂温度230℃の条件下、Ｔダイキャストフィルム成形
機を用いて厚さ30μｍのフィルムに成形し、片面にコロ
ナ処理を施した。Example 1 20 parts by weight of an acid copolymer, 40 parts by weight of medium density polyethylene, and 40 parts by weight of polypropylene were melt-kneaded using a single screw extruder under the condition of a resin temperature of 180 ° C. This composition was molded into a film having a thickness of 30 μm using a T die cast film molding machine under the condition of a resin temperature of 230 ° C., and one side thereof was subjected to corona treatment.
次にドライラミネーターを用いて前記作成フィルム
に、アンカーコート剤を塗布した厚さ12μｍのポリエチ
レンテレフタレートフィルムを貼り合せた。Next, using a dry laminator, a 12 μm-thick polyethylene terephthalate film coated with an anchor coating agent was attached to the prepared film.
得られた積層物を酸コポリマー、中密度ポリエチレン
とポリプロピレンとからなる組成物のフィルム層をシー
ル層として、面々ヒートシールを行ない引張試験機を用
いてシール強度を測定した。Using the obtained laminate as a seal layer, a film layer of a composition comprising an acid copolymer and medium density polyethylene and polypropylene, heat sealing was performed on each side and the seal strength was measured using a tensile tester.
また同様にポリプロピレントレーに対してヒートシー
ルを行ない、引張試験機に用いて、シール強度を測定し
た。（フランク、水挾雑物シール、レトルト処理後のシ
ール） 結果を表１及び表２に示す。Similarly, a polypropylene tray was heat-sealed and used in a tensile tester to measure the seal strength. (Franks, water contaminant seals, seals after retort treatment) The results are shown in Tables 1 and 2.
表１及び表２から、実施例１の組成物は、ヒートシー
ル性能において優れた密封性を有するとともに優れた易
開封性を有し、かつ広範囲な温度域において適度のシー
ル強度を有することがわかる。From Table 1 and Table 2, it can be seen that the composition of Example 1 has excellent sealing property in heat sealing performance, excellent easy opening property, and appropriate seal strength in a wide temperature range. .
また同様に表１及び表２から、実施例１の組成物は、
ポリプロピレン製トレーに対しても、優れた密封性を有
するとともに、優れた易開封性を有し、かつ広範囲な温
度域において適度のシール強度を示し、しかも挾雑物が
シール面に入り込んでも優れた密封性を示し、レトルト
条件下にさらされてもシール強度が大きく低下すること
がないことがわかる。Similarly, from Table 1 and Table 2, the composition of Example 1 was
It also has excellent sealing performance for polypropylene trays, excellent easy-opening properties, and shows appropriate sealing strength in a wide temperature range, and is excellent even if foreign matter enters the sealing surface. It can be seen that it exhibits a sealing property and that the seal strength does not significantly decrease even when exposed to retort conditions.
実施例２ 実施例１において酸コポリマー、中密度ポリエチレ
ン、ポリプロピレンの使用割合を10:50:40に変更した以
外は、実施例１と同様の試験を行なった。Example 2 The same test as in Example 1 was carried out except that the ratio of the acid copolymer, medium density polyethylene and polypropylene used in Example 1 was changed to 10:50:40.
結果を表１及び表２に示す。 The results are shown in Tables 1 and 2.
実施例３ 実施例１において、中密度ポリエチレンのかわりに低
圧法低密度ポリエチレンを用いた以外は実施例と同様の
試験を行なった。Example 3 The same test as in Example 1 was carried out except that low-pressure low-density polyethylene was used in place of the medium-density polyethylene.
結果を表１及び表２に示す。 The results are shown in Tables 1 and 2.
実施例４ 実施例２において、使用樹脂を中密度ポリエチレン50
重量部のかわりに、中密度ポリエチレン40重量部、エチ
レン・1-ブテン共重合体10重量部に変更した以外は、実
施例２と同様の試験を行なった。Example 4 In Example 2, the resin used was medium density polyethylene 50.
The same test as in Example 2 was carried out except that 40 parts by weight of medium density polyethylene and 10 parts by weight of ethylene / 1-butene copolymer were used instead of the parts by weight.
結果を表１及び表２に示す。 The results are shown in Tables 1 and 2.
比較例1,2,3 実施例１において酸コポリマーと、中密度ポリエチレ
ンとポリプロピレンの使用割合を3:20:77（比較例
１）、または50:10:40（比較例２）、または30:60:10
（比較例３）に変更した以外は実施例１と同様の試験を
行なった。Comparative Examples 1, 2, and 3 In Example 1, the ratio of the acid copolymer to the medium density polyethylene and polypropylene used was 3:20:77 (Comparative Example 1), or 50:10:40 (Comparative Example 2), or 30: 60:10
The same test as in Example 1 was performed except that (Comparative Example 3) was changed.
結果を表１及び表２に示す。 The results are shown in Tables 1 and 2.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０８Ｌ 23/08 Ｃ０８Ｌ 23/08 23/26 ＬＤＰ 23/26 ＬＤＰ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI Technical display location C08L 23/08 C08L 23/08 23/26 LDP 23/26 LDP
Claims (2)
チレン又はエチレンを主体とするエチレン・α−オレフ
ィン共重合体20〜60重量部及びα，β−不飽和カルボン
酸単位が１〜６モル％のエチレン・α，β−不飽和カル
ボン酸共重合体又はその金属塩５〜40重量部（全体で10
0重量部）の割合で配合してなるポリオレフィン組成物
からなる易開封性シール材料。1. A propylene-based polymer of 20 to 70 parts by weight, a polyethylene or ethylene-based ethylene / α-olefin copolymer of 20 to 60 parts by weight, and an α, β-unsaturated carboxylic acid unit of 1 to 6 mol. % Ethylene / α, β-unsaturated carboxylic acid copolymer or its metal salt 5 to 40 parts by weight (total 10
An easily-openable sealing material comprising a polyolefin composition blended in a proportion of 0 part by weight).
プロピレン系重合体20〜70重量部、ポリエチレン又はエ
チレンを主体とするエチレン・α−オレフィン共重合体
20〜60重量部及びα，β−不飽和カルボン酸単位が１〜
６モル％のエチレン・α，β−不飽和カルボン酸共重合
体又はその金属塩５〜40重量部（全体で100重量部）の
割合で配合してなるポリオレフィン組成物層を積層して
なる積層体からなる易開封性シール材料。2. A base material layer, optionally with an adhesive,
20-70 parts by weight of propylene-based polymer, ethylene or ethylene / α-olefin copolymer mainly composed of ethylene
20-60 parts by weight and 1 unit of α, β-unsaturated carboxylic acid unit
Lamination formed by laminating polyolefin composition layers formed by blending 6 mol% of ethylene / α, β-unsaturated carboxylic acid copolymer or metal salt thereof in an amount of 5 to 40 parts by weight (total 100 parts by weight) An easy-open seal material consisting of the body.