JP2023506833A - 硫化物応力腐食割れ抵抗性に優れた鋼材及びその製造方法 - Google Patents
硫化物応力腐食割れ抵抗性に優れた鋼材及びその製造方法 Download PDFInfo
- Publication number
- JP2023506833A JP2023506833A JP2022536636A JP2022536636A JP2023506833A JP 2023506833 A JP2023506833 A JP 2023506833A JP 2022536636 A JP2022536636 A JP 2022536636A JP 2022536636 A JP2022536636 A JP 2022536636A JP 2023506833 A JP2023506833 A JP 2023506833A
- Authority
- JP
- Japan
- Prior art keywords
- less
- steel material
- cooling
- steel
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
[関係式1]
0.5≦Ca/S≦5.0(ここで、各元素は重量含量を意味する)
炭素(C)は、鋼の物性に最も大きな影響を与える元素である。Cの含量が0.02%未満である場合、製鋼工程中に成分制御コストが過度に発生し、溶接熱影響部が必要以上に軟化するという問題がある。一方、その含量が0.06%を超えると、鋼板の水素誘起割れ抵抗性を減少させ、溶接性を阻害するおそれがある。したがって、本発明では、Cを0.02~0.06%含むことができ、より好ましくは0.03~0.05%含むことができる。
シリコン(Si)は、製鋼工程の脱酸剤として使用されるだけでなく、鋼の強度を高める役割を果たす元素である。このようなSiの含量が0.5%を超えると、素材の低温靭性が劣化し、溶接性を阻害し、圧延時にスケール剥離性を低下させる。一方、Siの含量を0.1%未満に下げるためには、製造コストが増加することから、本発明では、Siの含量を0.1~0.5%に制限することができ、より好ましくは0.2~0.4%に制限することができる。
マンガン(Mn)は、低温靭性を阻害することなく、鋼の焼入れ性を向上させる元素であって、0.8%以上含むことができる。但し、その含量が1.8%を超えると、中心偏析(segregation)が発生し、低温靭性の劣化はもちろん、鋼の硬化能を高めて溶接性を阻害するという問題がある。また、Mn中心偏析は水素誘起割れを誘発する要因となる。したがって、本発明では、Mnを0.8~1.8%含むことができる。あるいは、中心偏析の観点から、好ましくは、Mnを0.8~1.6%含むことができ、より好ましくは1~1.4%含むことができる。
クロム(Cr)はスラブ再加熱時に、オーステナイトに固溶して鋼材の焼入れ性を増加させ、鋼板の強度を確保するのに寄与する。しかし、本発明者らは、Crが0.05%以上添加されると、硫化物応力腐食割れの伝播を促進させる可能性があることを見出した。すなわち、鋼材において、Crの含量を0.05%未満に制御することにより、硫化物応力腐食割れの伝播に対する抵抗性が確保される効果が発揮される。一方、本発明の一側面による鋼材は、Crを0%超過0.05%未満含有することもでき、より好ましくは0.04%以下含むことができ、最も好ましくは0.02%以下含むこともできる。但し、Cr含量の下限として、強度の確保が可能な場合にはCrを添加しないこともあるため、0%とすることができ、より好ましくは、Cr含量の下限は0.0005%とすることができる。
リン(P)は、鋼中に不可避に添加される元素であって、その含量が0.03%を超えると、溶接性が著しく低下するだけでなく、低温靭性が減少するという問題がある。したがって、Pの含量を0.03%以下に制限する必要があり、低温靭性の確保の観点から、より好ましくは、Pを0.01%以下含むことができる。但し、P含量の下限として、製鋼工程時の負荷を考慮して0%は除くことができ、より好ましくは、P含量の下限は0.0001%とすることができる。
硫黄(S)は、鋼中に不可避に添加される元素であって、その含量が0.003%を超えると、鋼の延性、低温靭性、及び溶接性を減少させるという問題がある。したがって、Sの含量を0.003%以下に制限する必要がある。一方、Sは、鋼中のMnと結合してMnS介在物を形成し、この場合、鋼の水素誘起割れ抵抗性が低下するため、より好ましくは0.002%以下含むことができる。但し、S含量の下限として、製鋼工程時の負荷を考慮して0%は除くことができ、より好ましくは、S含量の下限は0.0001%とすることができる。
アルミニウム(Al)は、通常、溶鋼中に存在する酸素(O)と反応して酸素を除去する脱酸剤としての役割を果たす。したがって、Alは、鋼中で十分な脱酸力を有することができる程度に添加することができる。但し、その含量が0.06%を超えると、酸化物系介在物が多量に形成され、素材の低温靭性、水素誘起割れ抵抗性及び硫化物応力腐食割れ抵抗性を阻害するため、好ましくない。したがって、Alを0.06%以下含むことができ、より好ましくは0.04%以下含むことができる。但し、Al含量の下限として、脱酸剤として必須に添加される点を考慮して0%は除くことができ、より好ましくは、Al含量の下限は0.005%とすることができる。
窒素(N)は、鋼中から工業的に完全に除去することが難しいため、製造工程において許容できる範囲である0.01%を上限とする。一方、Nは、鋼中のAl、Ti、Nb、V等と反応して窒化物を形成することにより、オーステナイト結晶粒の成長を抑制し、これにより素材の靭性及び強度の向上に有利な影響を与えるが、その含量が0.01%を超えて過度に添加されると、固溶状態のNが存在し、これは低温靭性に悪影響を与える。したがって、Nを0.01%以下に制限することができ、より好ましくは0.009%以下に制御することができる。但し、N含量の下限として、製鋼工程時の負荷を考慮して0%は除くことができ、より好ましくは、N含量の下限は0.0005%とすることができる。
ニオブ(Nb)は、スラブ加熱時に固溶されて、後続の熱間圧延中にオーステナイト結晶粒の成長を抑制し、その後、析出されて鋼の強度を向上させるのに有効な元素である。また、鋼中のCと結合して炭化物として析出することにより、降伏比の増加を最小化しながら、鋼の強度を向上させる役割を果たす。このようなNbの含量が0.005%未満であると、上述の効果を十分に得ることができない。これに対し、その含量が0.08%を超えると、オーステナイト結晶粒が必要以上に微細化するだけでなく、粗大な析出物の形成により低温靭性及び水素誘起割れ抵抗性が劣化するという問題がある。したがって、本発明では、Nbを0.005~0.08%含むことができる。一方、Nb含量の下限は、より好ましくは0.02%とすることができ、Nb含量の上限は0.05%とすることができる。
チタン(Ti)は、スラブ加熱時にNと結合してTiNの形態で析出することにより、オーステナイト結晶粒の成長を抑制するのに効果的である。このようなTiが0.005%未満で添加された場合、オーステナイト結晶粒が粗大となり低温靭性を減少させる。これに対し、その含量が0.05%を超える場合にも、粗大なTi系析出物が形成されて低温靭性及び水素誘起割れ抵抗性を減少させる。したがって、本発明では、Tiを0.005~0.05%含むことができる。一方、Ti含量の下限は、より好ましくは0.006%とすることができ、Ti含量の上限は、低温靭性の確保の観点から、より好ましくは0.03%とすることができる。
カルシウム(Ca)は、製鋼工程中にSと結合してCaSを形成することにより、水素誘起割れを誘発させるMnSの偏析を抑制する役割を果たす。上述したMnSの偏析を抑制する効果を十分に得るためには、Caを0.0005%以上添加する必要があるが、その含量が0.005%を超えると、CaSの形成だけでなく、CaO介在物を形成して介在物による水素誘起割れを引き起こすという問題がある。したがって、本発明では、Caを0.0005~0.005%含むことができ、水素誘起割れ抵抗性の確保の観点から、より好ましくは0.001~0.003%含むことができる。
[関係式1]
0.5≦[Ca]/[S]≦5.0
ニッケル(Ni)は、鋼の低温靭性の劣化なく強度を向上させるのに効果的な元素である。このような低温靭性の劣化のない強度増加の効果を得るためには、Niを0.05%以上添加することができるが、Niは、高価な元素であって、その含量が0.3%を超えると、製造コストが大幅に上昇するという問題がある。したがって、本発明では、Niの添加時に0.05~0.3%含むことができる。一方、Ni含量の下限は、好ましくは0.08%とすることができ、より好ましくは0.1%とすることができる。あるいは、Ni含量の上限は、好ましくは0.28%とすることができ、より好ましくは0.21%とすることができる。
モリブデン(Mo)は、Crと同様に、鋼材の焼入れ性を向上させ、強度を増加させる役割を果たす。上述の焼入れ性向上の効果を得るためには、Moを0.02%以上添加することができるが、その含量が0.2%を超えると、上部ベイナイト(upper bainite)のような低温靭性に脆弱な組織を形成させ、水素誘起割れ抵抗性及び硫化物応力腐食割れ抵抗性を阻害するという問題がある。したがって、本発明では、Moの添加時に0.02~0.2%含むことができる。一方、Mo含量の下限は、より好ましくは0.05%とすることができ、Mo含量の上限は0.15%とすることができる。
バナジウム(V)は、鋼材の焼入れ性を増加させて強度を向上させる元素であって、このような効果を得るためには、0.005%以上添加することができる。但し、その含量が0.1%を超えると、鋼の焼入れ性が過度に増加して低温靭性に脆弱な組織が形成され、水素誘起割れ抵抗性が減少する。したがって、本発明では、Vの添加時に0.005~0.1%含むことができる。一方、V含量の下限は、より好ましくは0.005%とすることができ、V含量の上限は、より好ましくは0.05%とすることができる。
本発明で提案する合金組成及び成分関係を満たす鋼スラブを準備した後、これを加熱することができる。このとき1100~1300℃で2時間以上行うことができる。加熱時の温度が1300℃を超えると、スケール(scale)欠陥が増加するだけでなく、オーステナイト結晶粒が粗大化して鋼の焼入れ性を増加させるおそれがある。また、中央部において上部ベイナイトのような低温靭性に脆弱な組織の分率を増加させることにより、水素誘起割れ抵抗性及び低温靭性抵抗性が劣化するという問題がある。
加熱された鋼スラブを熱間圧延して熱延板材として製造することができる。このとき、Ar3+80℃~Ar3+200℃の温度範囲で累積圧下率50%以上で熱間圧延を行うことができ、熱間圧延後30秒以上保持(空冷)することができる。
熱間圧延により製造された熱延板材を冷却することができ、特に本発明では、表面部の硬度を効果的に下げた鋼材を得ることができる最適の冷却工程を提案することに技術的意義があると言える。
本発明では、上述した熱間圧延-30秒以上の保持後に、1次冷却を行うことができる。具体的には、上述の過程を通じて得られた熱延板材の表面部の温度がAr3-20℃~Ar3+50℃であるときに1次冷却を開始することが好ましい。
上述の条件で1次冷却を完了した熱延板材を空冷することが好ましく、空冷工程を通じて相対的に高温である中心部により表面部が復熱される効果を得ることができる。空冷は、熱延板材の表面部の温度がAr3-50℃~Ar3-10℃の温度範囲になったときに、終了することが好ましい。
空冷が上述の温度範囲(表面部の温度基準)で完了した直後に、2次冷却を行うことが好ましく、空冷終了時の表面部の温度は2次冷却時の開始温度と同じである。一方、2次冷却は、表面部の温度が300~600℃となるように50~500℃/sの冷却速度で行うことが好ましい。
下記表1、2の合金組成及び性質を有する鋼スラブを準備した。このとき、下記合金組成の含量は重量%であり、残りはFe及びその他の不可避不純物からなる。準備された鋼スラブを下記表3、4に示す条件で加熱、熱間圧延及び冷却の工程を経てそれぞれの鋼材を製造した。下記表1、2に記載の発明鋼及び比較鋼は、表3、4に記載の製造条件に従う以外は同じ工程により製造された。
Ar1=742-7.1×C-14.1×Mn+16.3×Si+11.5×Cr-49.7×Ni
Claims (9)
- 鋼材は、重量%で、炭素(C):0.02~0.06%、シリコン(Si):0.1~0.5%、マンガン(Mn):0.8~1.8%、クロム(Cr):0.05%未満、リン(P):0.03%以下、硫黄(S):0.003%以下、アルミニウム(Al):0.06%以下、窒素(N):0.01%以下、ニオブ(Nb):0.005~0.08%、チタン(Ti):0.005~0.05%、カルシウム(Ca):0.0005~0.005%と;ニッケル(Ni):0.05~0.3%、モリブデン(Mo):0.02~0.2%及びバナジウム(V):0.005~0.1%のうち1種以上、残部はFe及び不可避不純物からなり、
前記CaとSは、下記関係式1を満たし、
前記鋼材は、表面部の微細組織がフェライトで構成されるか、又はフェライトとパーライトの複合組織で構成され、中央部の微細組織がアシキュラーフェライトで構成されることを特徴とする鋼材。
[関係式1]
0.5≦Ca/S≦5.0(ここで、各元素は重量含量を意味する) - 前記表面部のビッカース硬度が200Hv以下であることを特徴とする請求項1に記載の鋼材。
- 前記鋼材は450MPa以上の降伏強度を有するものであることを特徴とする請求項1に記載の鋼材。
- 重量%で、炭素(C):0.02~0.06%、シリコン(Si):0.1~0.5%、マンガン(Mn):0.8~1.8%、クロム(Cr):0.05%未満、リン(P):0.03%以下、硫黄(S):0.003%以下、アルミニウム(Al):0.06%以下、窒素(N):0.01%以下、ニオブ(Nb):0.005~0.08%、チタン(Ti):0.005~0.05%、カルシウム(Ca):0.0005~0.005%と;ニッケル(Ni):0.05~0.3%、モリブデン(Mo):0.02~0.2%及びバナジウム(V):0.005~0.1%のうち1種以上、残部はFe及び不可避不純物からなり、前記CaとSは、下記関係式1を満たす鋼スラブを1100~1300℃の温度範囲で2時間以上加熱する段階と、前記加熱された鋼スラブを熱間圧延して熱延板材を製造する段階と、前記熱間圧延後に冷却する段階と、を含み、
前記冷却は、1次冷却する段階と、空冷する段階と、2次冷却する段階と、を含み、
前記1次冷却は、前記熱延板材の表面部の温度がAr1-50℃~Ar3-50℃となるように5~40℃/sの冷却速度で行い、前記2次冷却は、前記熱延板材の表面部の温度が300~600℃となるように50~500℃/sの冷却速度で行うことを特徴とする鋼材の製造方法。
[関係式1]
0.5≦Ca/S≦5.0(ここで、各元素は重量含量を意味する) - 前記熱間圧延は、Ar3+80℃~Ar3+200℃の温度範囲で累積圧下率50%以上で行うものであることを特徴とする請求項4に記載の鋼材の製造方法。
- 前記熱間圧延後の冷却前に、30秒以上保持する段階をさらに含むことを特徴とする請求項4に記載の鋼材の製造方法。
- 前記1次冷却は、前記熱延板材の表面部の温度がAr3-20℃~Ar3+50℃であるときに開始するものであることを特徴とする請求項4に記載の鋼材の製造方法。
- 前記1次冷却を完了した後、前記熱延板材の中心部の温度がAr3-30℃~Ar3+30℃であることを特徴とする請求項4に記載の鋼材の製造方法。
- 前記空冷を完了した後、前記熱延板材の表面部の温度がAr3-10℃~Ar3-50℃であることを特徴とする請求項4に記載の鋼材の製造方法。