JP2023116058A - Manufacturing method of aluminum alloy and aluminum alloy material - Google Patents
Manufacturing method of aluminum alloy and aluminum alloy material Download PDFInfo
- Publication number
- JP2023116058A JP2023116058A JP2022018609A JP2022018609A JP2023116058A JP 2023116058 A JP2023116058 A JP 2023116058A JP 2022018609 A JP2022018609 A JP 2022018609A JP 2022018609 A JP2022018609 A JP 2022018609A JP 2023116058 A JP2023116058 A JP 2023116058A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- aluminum alloy
- content
- less
- brazing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、アルミニウム合金からなる自動車用熱交換器のスクラップ及び／又は自動車用熱交換器の製造に用いられるアルミニウム合金クラッド材のスクラップを用いるアルミニウム合金材の製造方法に関する。 TECHNICAL FIELD The present invention relates to a method for producing an aluminum alloy material using scrap aluminum alloy heat exchangers for automobiles and/or scrap aluminum alloy clad materials used in the production of automobile heat exchangers.
アルミニウム合金は軽量かつ高熱伝導性を備えており、適切な処理により高耐食性が実現できるため、自動車用熱交換器、例えば、ラジエータ、コンデンサ、エバポレータ、ヒータ、インタークーラなどに用いられている。これら自動車用熱交換器のチューブ材としては、３００３合金などのＡｌ－Ｍｎ系合金を心材として、一方の面に、Ａｌ－Ｓｉ系合金のろう材又はＡｌ－Ｚｎ系合金の犠牲陽極材をクラッドした２層クラッド材や、更に他方の面にＡｌ－Ｓｉ系合金のろう材をクラッドした３層クラッド材などが使用されている。 Aluminum alloys are lightweight, have high thermal conductivity, and can achieve high corrosion resistance with proper treatment, so they are used in automotive heat exchangers such as radiators, condensers, evaporators, heaters, and intercoolers. As the tube material for these automotive heat exchangers, an Al—Mn alloy such as 3003 alloy is used as a core material, and one surface is clad with an Al—Si alloy brazing material or an Al—Zn alloy sacrificial anode material. and a three-layer clad material in which the other surface is further clad with an Al--Si alloy brazing material.
熱交換器は、通常、このようなクラッド材を成形したチューブとコルゲート成形したフィンを組み合わせ、６００℃程度の温度でろう付することによって接合される。熱交換器として自動車に搭載された後、チューブが破壊することで貫通すれば、内部を循環している冷却水や冷媒の漏洩が生じる。そのため、製品寿命を向上させるために、ろう付後における強度や耐食性に優れたアルミニウム合金が必要不可欠とされている。 A heat exchanger is usually joined by combining a tube molded with such a clad material and corrugated fins and brazing them at a temperature of about 600.degree. After the tube is installed in an automobile as a heat exchanger, if the tube breaks and penetrates, the cooling water or refrigerant circulating inside will leak. Therefore, in order to improve product life, an aluminum alloy with excellent strength and corrosion resistance after brazing is considered essential.
従来、このようなアルミニウム合金を作製する場合、ろう付後における良好な強度や耐食性を確保するため、アルミニウム新地金を鋳造原料とし、ＳｉやＭｎなどの元素を添加することにより化学成分を所望の範囲に調整していた。しかし、アルミニウム新地金は製造時に多量の電力を消費するため、鋳造原料としてアルミニウム新地金を使用すると電力由来のＣＯ２排出量が多くなり、環境負荷が高くなるという問題がある。特に近年ではカーボンニュートラルの達成が世界中で社会的課題となっているため、新地金の使用量を減らすことの重要性が増している。 Conventionally, when producing such an aluminum alloy, in order to ensure good strength and corrosion resistance after brazing, new aluminum metal is used as a casting raw material, and elements such as Si and Mn are added to obtain the desired chemical composition. I adjusted the range. However, since virgin aluminum consumes a large amount of electric power during its production, the use of virgin aluminum as a raw material for casting results in a large amount of CO2 emissions derived from electric power, which poses a problem of increased environmental load. Especially in recent years, since the achievement of carbon neutrality has become a social issue all over the world, the importance of reducing the amount of new ingots used is increasing.
新地金の使用量を削減するための手段としてリサイクルが考えられるが、その際には廃材を、該廃材と同じ製品を作るための原料へと戻す水平リサイクルが合理的であり、その代表例がアルミニウム缶である。例えば、アルミニウム缶廃材を他の製品へリサイクルすると、社会全体ではリサイクル率が低下してしまうという不合理が生じる。 Recycling can be considered as a means to reduce the amount of new ingots used, but in that case, horizontal recycling that returns waste materials to raw materials for making the same products as the waste materials is rational, and a representative example is It's an aluminum can. For example, if aluminum can scraps are recycled into other products, the recycling rate of society as a whole will decline, which is irrational.
一方、熱交換器においては、上述したクラッド材が用いられ、更に異なる材質同士がろう付されるため、クラッド材の製造工程中に生じた屑や廃棄されたアルミニウム製熱交換器を再び熱交換器用材料の原料としてリサイクルすると、ろう付性や耐食性など所望の特性を損ねてしまうといった問題点がある。 On the other hand, in the heat exchanger, the above-mentioned clad material is used, and different materials are brazed together, so the scraps generated during the clad material manufacturing process and the discarded aluminum heat exchanger are reheated. When recycled as a raw material for dexterity materials, there is a problem that desired properties such as brazeability and corrosion resistance are impaired.
特許文献１では、６０００系合金やその他のＡｌ合金スクラップ材、低純度Ａｌ地金などを溶解原料として使用した場合に含まれる不純物元素を許容する規定がされている。 Patent Literature 1 specifies that impurity elements contained in 6000 series alloys, other Al alloy scrap materials, low-purity Al ingots, and the like are allowed when they are used as melting raw materials.
しかしながら、特許文献１では、クラッド材の製造工程中に生じた屑や廃棄されたアルミニウム製熱交換器を鋳造原料とした場合の課題やその解決方法については考慮されていない。 However, Patent Literature 1 does not take into account the problems and solutions of using scraps generated during the manufacturing process of the clad material and discarded aluminum heat exchangers as raw materials for casting.
そこで、本発明は、かかる背景に鑑みてなされたものであり、クラッド材の製造工程中に生じた屑や廃棄されたアルミニウム製熱交換器を、熱交換器用材料の原料として用い、且つ、ろう付性及びろう付後の耐食性に優れたアルミニウム合金材を製造する方法を提供することにある。 Therefore, the present invention has been made in view of this background, and uses scraps generated during the manufacturing process of clad materials and discarded aluminum heat exchangers as raw materials for heat exchanger materials, and To provide a method for producing an aluminum alloy material having excellent bondability and corrosion resistance after brazing.
上記課題は、以下の本発明により解決される。
すなわち、本発明（１）は、０．５０～１．２０質量％のＳｉ、０．０５～１．００質量％のＦｅ、０．１２～１．００質量％のＣｕ、０．６０～１．８０質量％のＭｎ、及び０．１１～０．６０質量％のＺｎを含有し、Ｍｇ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金部Ａを有するアルミニウム合金材の製造方法であり、
０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなる自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、０．５０～１．２０質量％のＳｉ、０．０５～１．００質量％のＦｅ、０．１２～１．００質量％のＣｕ、０．６０～１．８０質量％のＭｎ、及び０．１１～０．６０質量％のＺｎを含有し、Ｍｇ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなるアルミニウム合金鋳塊Ａを鋳造する鋳造工程を有すること、
を特徴とするアルミニウム合金材の製造方法を提供するものである。
The above problems are solved by the present invention described below.
That is, the present invention (1) comprises 0.50 to 1.20 mass% Si, 0.05 to 1.00 mass% Fe, 0.12 to 1.00 mass% Cu, 0.60 to 1 .80% by mass of Mn and 0.11 to 0.60% by mass of Zn, with a Mg content of 0.50% by mass or less, a Cr content of 0.30% by mass or less, and a Ti content of 0 .30% by mass or less, Zr content of 0.30% by mass or less, V content of 0.30% by mass or less, and aluminum alloy part A comprising the balance aluminum and unavoidable impurities. and
0.50% by weight or more Si, 0.10% by weight or more Fe, 0.10% by weight or more Cu, 0.50% by weight or more Mn, 0.05% by weight or more Mg, and 0.10% by weight scrap of automotive heat exchangers made of aluminum alloys containing one or more elements selected from the group consisting of Zn in an amount of Zn and/or scraps of aluminum alloy clad materials used in automotive heat exchangers Using a casting raw material containing 10.0% by mass or more, 0.50 to 1.20% by mass Si, 0.05 to 1.00% by mass Fe, 0.12 to 1.00% by mass Cu, 0.60 to 1.80% by mass of Mn and 0.11 to 0.60% by mass of Zn, the Mg content is 0.50% by mass or less, the Cr content is 0.30% by mass or less, Aluminum alloy casting made of an aluminum alloy having a Ti content of 0.30% by mass or less, a Zr content of 0.30% by mass or less, and a V content of 0.30% by mass or less, and the balance being aluminum and unavoidable impurities Having a casting process for casting ingot A;
To provide a method for producing an aluminum alloy material characterized by
また、本発明（２）は、前記鋳造工程を行い得られる前記アルミニウム合金鋳塊Ａを心材用のアルミニウム合金鋳塊として用い、１又は２の皮材用のアルミニウム合金鋳塊と組み合わせて、アルミニウム合金クラッド材を得ることを特徴とする（１）のアルミニウム合金材の製造方法を提供するものである。 Further, the present invention (2) uses the aluminum alloy ingot A obtained by performing the casting step as an aluminum alloy ingot for the core material, and combines it with the aluminum alloy ingot for the skin material of 1 or 2 to produce an aluminum alloy ingot. A method for producing an aluminum alloy material according to (1), characterized in that an alloy clad material is obtained.
また、本発明（３）は、前記皮材用のアルミニウム合金鋳塊が、２．５０～１３．００質量％のＳｉ及び０．０５～１．００質量％のＦｅを含有し、Ｚｎ含有量が５．５０質量％以下、Ｍｎ含有量が１．００質量％以下、Ｃｕ含有量が１．００質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％、Ｖ含有量が０．３０質量％以下、Ｓｒ含有量が０．１０質量％以下、Ｎａ含有量が０．１０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなるろう材用アルミニウム合金鋳塊Ｂ、又は０．５０～６．００質量％のＺｎ、０．０５～１．５０質量％のＳｉ、及び０．０５～２．００質量％のＦｅを含有し、Ｍｇ含有量が３．００質量％以下、Ｍｎ含有量が１．８０質量％以下、Ｃｕ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなる犠牲陽極材用アルミニウム合金鋳塊Ｃであることを特徴とする（２）のアルミニウム合金材の製造方法を提供するものである。 Further, in the present invention (3), the aluminum alloy ingot for the skin material contains 2.50 to 13.00% by mass of Si and 0.05 to 1.00% by mass of Fe, and the Zn content is is 5.50% by mass or less, Mn content is 1.00% by mass or less, Cu content is 1.00% by mass or less, Cr content is 0.30% by mass or less, and Ti content is 0.30% by mass. Below, the Zr content is 0.30% by mass, the V content is 0.30% by mass or less, the Sr content is 0.10% by mass or less, the Na content is 0.10% by mass or less, and the balance is aluminum and Aluminum alloy ingot for brazing material B made of an aluminum alloy containing unavoidable impurities, or 0.50 to 6.00% by mass of Zn, 0.05 to 1.50% by mass of Si, and 0.05 to 2.0% by mass of Zn. 00% by mass of Fe, Mg content of 3.00% by mass or less, Mn content of 1.80% by mass or less, Cu content of 0.50% by mass or less, and Cr content of 0.30% by mass % or less, the Ti content is 0.30 mass% or less, the Zr content is 0.30 mass% or less, the V content is 0.30 mass% or less, and the balance is aluminum and unavoidable impurities. The present invention provides a method for producing an aluminum alloy material according to (2), which is an aluminum alloy ingot C for a sacrificial anode material.
また、本発明（４）は、前記アルミニウム合金クラッド材が、ろう材／中間層材／心材／ろう材又は犠牲陽極材の順に積層されている４層材のアルミニウム合金クラッド材であり、
心材用のアルミニウム合金鋳塊として、前記心材用アルミニウム合金鋳塊Ａを用い、ろう材用のアルミニウム合金鋳塊として、前記ろう材用アルミニウム合金鋳塊Ｂを用い、犠牲陽極材用のアルミニウム合金鋳塊として、前記犠牲陽極材用アルミニウム合金鋳塊Ｃを用い、中間層材用のアルミニウム合金鋳塊と組み合わせて、前記アルミニウム合金クラッド材を得ること、
を特徴とする（３）のアルミニウム合金材の製造方法を提供するものである。
Further, the present invention (4) is a four-layer aluminum alloy clad material in which the aluminum alloy clad material is laminated in the order of brazing material/intermediate layer material/core material/brazing material or sacrificial anode material,
The aluminum alloy ingot A for the core material is used as the aluminum alloy ingot for the core material, the aluminum alloy ingot B for the brazing material is used as the aluminum alloy ingot for the brazing material, and the aluminum alloy ingot for the sacrificial anode material is used. Using the aluminum alloy ingot C for the sacrificial anode material as a lump and combining it with the aluminum alloy ingot for the intermediate layer material to obtain the aluminum alloy clad material;
A method for producing an aluminum alloy material according to (3) is provided.
また、本発明（５）は、前記アルミニウム合金クラッド材が、ろう材／中間層材／心材／中間層材／ろう材の順に積層されている５層材のアルミニウム合金クラッド材であり、
心材用のアルミニウム合金鋳塊として、前記心材用アルミニウム合金鋳塊Ａを用い、ろう材用のアルミニウム合金鋳塊として、前記ろう材用アルミニウム合金鋳塊Ｂを用い、中間層材用のアルミニウム合金鋳塊と組み合わせて、前記アルミニウム合金クラッド材を得ること、
を特徴とする（３）のアルミニウム合金材の製造方法を提供するものである。
In addition, the present invention (5) is an aluminum alloy clad material of a five-layer material in which the aluminum alloy clad material is laminated in the order of brazing material/intermediate layer material/core material/intermediate layer material/brazing material,
The aluminum alloy ingot A for the core material is used as the aluminum alloy ingot for the core material, the aluminum alloy ingot B for the brazing material is used as the aluminum alloy ingot for the brazing material, and the aluminum alloy ingot for the intermediate layer material is used. combining with a lump to obtain the aluminum alloy clad material;
A method for producing an aluminum alloy material according to (3) is provided.
また、本発明（６）は、前記中間層材用のアルミニウム合金鋳塊が、０．０５～１．５０質量％のＳｉ、及び０．０５～２．００質量％のＦｅを含有し、Ｚｎ含有量が６．００質量％以下、Ｍｎ含有量が１．８０質量％以下、Ｃｕ含有量が１．００質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなる中間層材用アルミニウム合金鋳塊Ｄであることを特徴とする（４）又は（５）のアルミニウム合金材の製造方法を提供するものである。 Further, in the present invention (6), the aluminum alloy ingot for the intermediate layer material contains 0.05 to 1.50% by mass of Si and 0.05 to 2.00% by mass of Fe, and Zn The content is 6.00% by mass or less, the Mn content is 1.80% by mass or less, the Cu content is 1.00% by mass or less, the Cr content is 0.30% by mass or less, and the Ti content is 0.30%. % by mass or less, Zr content of 0.30 mass % or less, V content of 0.30 mass % or less, and an aluminum alloy ingot D for an intermediate layer material, the balance being aluminum and unavoidable impurities. A method for producing an aluminum alloy material according to (4) or (5) is provided.
また、本発明（７）は、０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなる自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、前記皮材用のアルミニウム合金鋳塊、前記ろう材用アルミニウム合金鋳塊Ｂ、前記犠牲陽極材用アルミニウム合金鋳塊Ｃ、前記中間層材用のアルミニウム合金鋳塊、又は前記中間層材用アルミニウム合金鋳塊Ｄを鋳造する工程を有することを特徴とする（２）～（６）いずれかのアルミニウム合金材の製造方法を提供するものである。 In addition, the present invention (7) includes 0.50% by mass or more of Si, 0.10% by mass or more of Fe, 0.10% by mass or more of Cu, 0.50% by mass or more of Mn, and 0.05% by mass. or more Mg and 0.10% by mass or more of Zn. Using a casting raw material containing 10.0% by mass or more of scrap of the aluminum alloy clad material used, the aluminum alloy ingot for the skin material, the aluminum alloy ingot B for the brazing material, and the aluminum alloy for the sacrificial anode material The aluminum alloy material according to any one of (2) to (6), characterized by having a step of casting the ingot C, the aluminum alloy ingot for the intermediate layer material, or the aluminum alloy ingot D for the intermediate layer material. It is intended to provide a manufacturing method of.
また、本発明（８）は、０．５０～１．２０質量％のＳｉ、０．０５～１．００質量％のＦｅ、０．１２～１．００質量％のＣｕ、０．６０～１．８０質量％のＭｎ、及び０．１１～０．６０質量％のＺｎを含有し、Ｍｇ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金部Ａを有することを特徴とするアルミニウム合金材を提供するものである。 In addition, the present invention (8) contains 0.50 to 1.20 mass% Si, 0.05 to 1.00 mass% Fe, 0.12 to 1.00 mass% Cu, 0.60 to 1 .80% by mass of Mn and 0.11 to 0.60% by mass of Zn, with a Mg content of 0.50% by mass or less, a Cr content of 0.30% by mass or less, and a Ti content of 0 .30% by mass or less, a Zr content of 0.30% by mass or less, a V content of 0.30% by mass or less, and an aluminum alloy part A comprising the balance aluminum and unavoidable impurities. An alloy material is provided.
また、本発明（９）は、心材として前記アルミニウム合金部Ａを有し、該心材の一方の面側又は両面側に皮材がクラッドされているアルミニウム合金クラッド材であることを特徴とする（８）のアルミニウム合金材を提供するものである。 In addition, the present invention (9) is an aluminum alloy clad material having the aluminum alloy portion A as a core material and having a skin material clad on one side or both sides of the core material ( 8) provides the aluminum alloy material.
また、本発明（１０）は、前記皮材が、２．５０～１３．００質量％のＳｉ及び０．０５～１．００質量％のＦｅを含有し、Ｚｎ含有量が５．５０質量％以下、Ｍｎ含有量が１．００質量％以下、Ｃｕ含有量が１．００質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％、Ｖ含有量が０．３０質量％以下、Ｓｒ含有量が０．１０質量％以下、Ｎａ含有量が０．１０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなるろう材Ｂ、又は０．５０～６．００質量％のＺｎ、０．０５～１．５０質量％のＳｉ、及び０．０５～２．００質量％のＦｅを含有し、Ｍｇ含有量が３．００質量％以下、Ｍｎ含有量が１．８０質量％以下、Ｃｕ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなる犠牲陽極材Ｃであることを特徴とする（９）のアルミニウム合金材を提供するものである。 Further, in the present invention (10), the skin material contains 2.50 to 13.00% by mass of Si and 0.05 to 1.00% by mass of Fe, and has a Zn content of 5.50% by mass. Below, the Mn content is 1.00% by mass or less, the Cu content is 1.00% by mass or less, the Cr content is 0.30% by mass or less, the Ti content is 0.30% by mass or less, and the Zr content is 0.30% by mass, V content of 0.30% by mass or less, Sr content of 0.10% by mass or less, Na content of 0.10% by mass or less, and the balance being aluminum and unavoidable impurities Brazing material B made of an alloy, or containing 0.50 to 6.00% by mass of Zn, 0.05 to 1.50% by mass of Si, and 0.05 to 2.00% by mass of Fe, and containing Mg Mn content is 1.80 mass% or less, Cu content is 0.50 mass% or less, Cr content is 0.30 mass% or less, Ti content is 0.30 mass% % or less, a Zr content of 0.30% by mass or less, a V content of 0.30% by mass or less, and the balance being aluminum and unavoidable impurities. It provides the aluminum alloy material of (9).
また、本発明（１１）は、前記アルミニウム合金クラッド材が、ろう材／中間層材／心材／ろう材又は犠牲陽極材の順に積層されている４層材のアルミニウム合金クラッド材であり、
該心材が前記アルミニウム合金部Ａであり、該ろう材が前記ろう材Ｂであり、該犠牲陽極材が前記犠牲陽極材Ｃであること、
を特徴とする（１０）のアルミニウム合金材を提供するものである。
The present invention (11) is a four-layer aluminum alloy clad material in which the aluminum alloy clad material is laminated in the order of brazing material/intermediate layer material/core material/brazing material or sacrificial anode material,
The core material is the aluminum alloy portion A, the brazing material is the brazing material B, and the sacrificial anode material is the sacrificial anode material C;
It provides the aluminum alloy material of (10) characterized by
また、本発明（１２）は、前記アルミニウム合金クラッド材が、ろう材／中間層材／心材／中間層材／ろう材の順に積層されている５層材のアルミニウム合金クラッド材であり、
該心材が前記アルミニウム合金部Ａであり、該ろう材が前記ろう材Ｂであること、
を特徴とする（１０）のアルミニウム合金材を提供するものである。
Further, the present invention (12) is an aluminum alloy clad material of a five-layer material in which the aluminum alloy clad material is laminated in the order of brazing material/intermediate layer material/core material/intermediate layer material/brazing material,
The core material is the aluminum alloy portion A, and the brazing material is the brazing material B;
It provides the aluminum alloy material of (10) characterized by
また、本発明（１３）は、前記中間層材が、０．０５～１．５０質量％のＳｉ、及び０．０５～２．００質量％のＦｅを含有し、Ｚｎ含有量が６．００質量％以下、Ｍｎ含有量が１．８０質量％以下、Ｃｕ含有量が１．００質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなる中間層材Ｄであることを特徴とする（１１）又は（１２）のアルミニウム合金材の製造方法を提供するものである。 Further, according to the present invention (13), the intermediate layer material contains 0.05 to 1.50% by mass of Si and 0.05 to 2.00% by mass of Fe, and has a Zn content of 6.00. % by mass or less, Mn content of 1.80 mass % or less, Cu content of 1.00 mass % or less, Cr content of 0.30 mass % or less, Ti content of 0.30 mass % or less, Zr content (11) or ( 12) provides a method for producing an aluminum alloy material.
本発明によれば、クラッド材の製造工程中に生じた屑や廃棄されたアルミニウム製熱交換器を再び熱交換器用材料の原料として用いることにより、アルミニウム新地金の使用に由来するＣＯ２排出量を削減し、且つ、ろう付性及びろう付後の耐食性に優れたアルミニウム合金材を製造する方法を提供することができる。 According to the present invention, scraps generated during the manufacturing process of clad materials and discarded aluminum heat exchangers are reused as raw materials for heat exchanger materials, thereby reducing CO2 emissions resulting from the use of new aluminum ingots. It is possible to provide a method of manufacturing an aluminum alloy material that reduces the amount of , and has excellent brazeability and corrosion resistance after brazing.
本発明のアルミニウム合金材の製造方法は、０．５０～１．２０質量％のＳｉ、０．０５～１．００質量％のＦｅ、０．１２～１．００質量％のＣｕ、０．６０～１．８０質量％のＭｎ、及び０．１１～０．６０質量％のＺｎを含有し、Ｍｇ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金部Ａを有するアルミニウム合金材の製造方法であり、
０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなる自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、０．５０～１．２０質量％のＳｉ、０．０５～１．００質量％のＦｅ、０．１２～１．００質量％のＣｕ、０．６０～１．８０質量％のＭｎ、及び０．１１～０．６０質量％のＺｎを含有し、Ｍｇ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなるアルミニウム合金鋳塊Ａを鋳造する鋳造工程を有することを特徴とするアルミニウム合金材の製造方法である。
以下、０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなる自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを、アルミニウム合金廃材とも記載する。
The method for producing an aluminum alloy material of the present invention comprises 0.50 to 1.20 mass% Si, 0.05 to 1.00 mass% Fe, 0.12 to 1.00 mass% Cu, 0.60 mass% ~1.80% by mass of Mn and 0.11 to 0.60% by mass of Zn, Mg content of 0.50% by mass or less, Cr content of 0.30% by mass or less, Ti content is 0.30% by mass or less, the Zr content is 0.30% by mass or less, the V content is 0.30% by mass or less, and the balance is aluminum and inevitable impurities. A manufacturing method,
0.50% by weight or more Si, 0.10% by weight or more Fe, 0.10% by weight or more Cu, 0.50% by weight or more Mn, 0.05% by weight or more Mg, and 0.10% by weight scrap of automotive heat exchangers made of aluminum alloys containing one or more elements selected from the group consisting of Zn in an amount of Zn and/or scraps of aluminum alloy clad materials used in automotive heat exchangers Using a casting raw material containing 10.0% by mass or more, 0.50 to 1.20% by mass Si, 0.05 to 1.00% by mass Fe, 0.12 to 1.00% by mass Cu, 0.60 to 1.80% by mass of Mn and 0.11 to 0.60% by mass of Zn, the Mg content is 0.50% by mass or less, the Cr content is 0.30% by mass or less, Aluminum alloy casting made of an aluminum alloy having a Ti content of 0.30% by mass or less, a Zr content of 0.30% by mass or less, and a V content of 0.30% by mass or less, and the balance being aluminum and unavoidable impurities A method for producing an aluminum alloy material, characterized by having a casting step of casting an ingot A.
0.50 mass % or more of Si, 0.10 mass % or more of Fe, 0.10 mass % or more of Cu, 0.50 mass % or more of Mn, 0.05 mass % or more of Mg, and 0.50 mass % or more of Si. Automotive heat exchanger scrap and/or aluminum alloy clad material used for automotive heat exchangers made of an aluminum alloy containing one or more elements selected from the group consisting of Zn in an amount of 10% by mass or more Scrap is also described as aluminum alloy scrap.
本発明のアルミニウム合金材の製造方法は、アルミニウム合金部Ａを有するアルミニウム合金材を製造する方法である。本発明のアルミニウム合金材の製造方法において、アルミニウム合金部Ａを有するアルミニウム合金材としては、アルミニウム合金部Ａ単体からなるアルミニウム合金材や、アルミニウム合金部Ａを心材として有し且つ適宜選択される材料がクラッドされているアルミニウム合金クラッド材が挙げられる。 The method for producing an aluminum alloy material of the present invention is a method for producing an aluminum alloy material having an aluminum alloy portion A. In the method for producing an aluminum alloy material of the present invention, the aluminum alloy material having the aluminum alloy portion A may be an aluminum alloy material consisting of the aluminum alloy portion A alone, or a material having the aluminum alloy portion A as a core material and appropriately selected. is an aluminum alloy clad material clad with
本発明のアルミニウム合金材の製造方法では、アルミニウム合金鋳塊Ａを鋳造する鋳造工程を有する。そして、本発明のアルミニウム合金材の製造方法では、鋳造工程を行った後、鋳造工程を行い得られたアルミニウム合金鋳塊Ａを用いて、種々の工程及び処理を経て、アルミニウム合金部Ａを有するアルミニウム合金材を得る。つまり、本発明のアルミニウム合金材は、アルミニウム合金部Ａを有するアルミニウム合金材である。 The method for producing an aluminum alloy material of the present invention has a casting step of casting an aluminum alloy ingot A. Then, in the method for producing an aluminum alloy material of the present invention, after performing the casting step, the aluminum alloy ingot A obtained by performing the casting step is used to undergo various steps and treatments to form the aluminum alloy part A. Obtain an aluminum alloy material. That is, the aluminum alloy material of the present invention is an aluminum alloy material having the aluminum alloy portion A.
アルミニウム合金部Ａ及びアルミニウム合金鋳塊Ａについて、説明する。 The aluminum alloy part A and the aluminum alloy ingot A will be explained.
Ｓｉは、アルミニウム合金廃材の成分に含まれるため、アルミニウム合金部Ａ及びアルミニウム合金鋳塊Ａが、Ｓｉを含有する必要がある。アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＳｉの含有量は、０．５０～１．２０質量％、好ましくは０．５０～１．００質量％、より好ましくは０．６５～１．００質量％である。Ｓｉ含有量が、０．５０質量％未満では、アルミニウム合金廃材の配合による新地金削減の効果が小さく、また、１．２０質量％を超えると、心材の融点が低下して心材へのろうの侵食が発生する。 Since Si is included in the components of the aluminum alloy waste material, the aluminum alloy part A and the aluminum alloy ingot A must contain Si. The Si content of the aluminum alloy part A and the aluminum alloy ingot A is 0.50 to 1.20% by mass, preferably 0.50 to 1.00% by mass, more preferably 0.65 to 1.00% by mass. %. If the Si content is less than 0.50% by mass, the effect of reducing new ingots by adding aluminum alloy scraps is small. Erosion occurs.
Ｚｎは、アルミニウム合金廃材の成分に含まれるため、アルミニウム合金部Ａ及びアルミニウム合金鋳塊Ａが、Ｚｎを含有する必要がある。通常、一般的なアルミニウム合金クラッド材の製造工場において生じるアルミニウム合金廃材及び自動車用熱交換器のスクラップの平均Ｚｎ含有量は１．１０質量％程度以上である。そのため、アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＺｎの含有量は、０．１１～０．６０質量％である。Ｚｎ含有量が、０．１１質量％未満では、アルミニウム合金廃材の配合による新地金削減の効果が小さく、また、０．６０質量％を超えると、心材の孔食電位が卑化して、腐食速度を増大させる恐れがある。そして、アルミニウム合金廃材の使用量を多くし易くなる点や、Ｚｎ含有量が高いアルミニウム合金廃材の使用が可能となり、アルミニウム合金廃材の使用の自由度が高くなる点で、アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＺｎの含有量は、好ましくは０．２０～０．６０質量％である。 Since Zn is included in the components of the aluminum alloy waste material, the aluminum alloy part A and the aluminum alloy ingot A must contain Zn. Generally, the average Zn content of aluminum alloy waste materials and automobile heat exchanger scraps produced in general aluminum alloy clad material manufacturing plants is about 1.10% by mass or more. Therefore, the Zn content of the aluminum alloy part A and the aluminum alloy ingot A is 0.11 to 0.60% by mass. If the Zn content is less than 0.11% by mass, the effect of reducing new ingots by adding aluminum alloy scraps is small, and if it exceeds 0.60% by mass, the pitting potential of the core material becomes base, and the corrosion rate may increase In addition, the aluminum alloy part A and the aluminum alloy part A and the aluminum The Zn content of the alloy ingot A is preferably 0.20 to 0.60% by mass.
Ｃｕは、上記Ｚｎによる孔食電位卑化の影響を抑制する働きを持つ。アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＣｕの含有量は、０．１２～１．００質量％、好ましくは０．２０～０．９０質量％である。Ｃｕ含有量が、０．１２質量％未満ではアルミニウム合金廃材の配合による新地金削減の効果が小さく、また、１．００質量％を超えると鋳造時に割れが生じ易く、製造の難易度が上がる。 Cu has a function of suppressing the influence of the pitting potential lowering caused by Zn. The Cu content of the aluminum alloy part A and the aluminum alloy ingot A is 0.12 to 1.00% by mass, preferably 0.20 to 0.90% by mass. If the Cu content is less than 0.12% by mass, the effect of reducing new ingots by adding aluminum alloy scraps is small, and if it exceeds 1.00% by mass, cracks are likely to occur during casting, increasing the difficulty of production.
ＣｕとＺｎは、同時に添加するとアノード反応とカソード反応の両方を加速し、耐食性を悪化させてしまう。一般的にアノード反応は指数関数的に、カソード反応は線形に腐食速度に影響するため、それぞれ％の数値でＣｕ含有量をＡ質量％、Ｚｎ含有量をＢ質量％、自然対数の底ｅ＝２．７１８２８１８２８４５９０４と置いたとき、Ｖ＝Ａ×ｅＢによってよく整理できる。このＶ値は、１．５０以下が好ましく、より好ましくは１．１５以下である。 When Cu and Zn are added at the same time, they accelerate both the anodic reaction and the cathodic reaction and deteriorate the corrosion resistance. In general, the anodic reaction affects the corrosion rate exponentially, and the cathodic reaction linearly affects the corrosion rate. 2.71828182845904 can be well arranged by V=A× eB . This V value is preferably 1.50 or less, more preferably 1.15 or less.
以上で述べたアルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＳｉ、Ｚｎ及びＣｕの含有量が、アルミニウム合金廃材を配合する上で重要である。 The contents of Si, Zn and Cu in the aluminum alloy part A and the aluminum alloy ingot A described above are important in mixing the aluminum alloy waste material.
Ｆｅは、再結晶核となり得るサイズの金属間化合物を形成し易い。アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＦｅの含有量は、０．０５～１．００質量％、好ましくは０．１０～０．８０質量％である。Ｆｅ含有量が上記範囲にあることにより、ろう付後の結晶粒径を粗大にしてろう拡散を抑制することができる。一方、Ｆｅ含有量が、０．０５質量％未満では高純度アルミニウム地金を使用しなければならずコスト高となり、また、１．００質量％を超えるとろう付後の結晶粒径が微細となり、ろう拡散が生じる。 Fe tends to form an intermetallic compound having a size that can become a recrystallization nucleus. The Fe content of the aluminum alloy part A and the aluminum alloy ingot A is 0.05 to 1.00% by mass, preferably 0.10 to 0.80% by mass. When the Fe content is within the above range, the crystal grain size after brazing can be made coarser to suppress brazing diffusion. On the other hand, if the Fe content is less than 0.05% by mass, high-purity aluminum ingots must be used, resulting in high costs. , wax diffusion occurs.
Ｍｎは、ＳｉとともにＡｌ－Ｍｎ－Ｓｉ系の金属間化合物を形成し、分散強化により強度を向上させ、また、アルミニウム母相中に固溶して固溶強化により強度を向上させる。アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＭｎの含有量は、０．６０～１．８０質量％、好ましくは０．７０～１．７０質量％である。Ｍｎ含有量が、０．６０質量％未満ではその効果が小さく、また、１．８０質量％を超えると鋳造時に巨大金属間化合物が形成され易くなり、塑性加工性を低下させる。 Mn forms an Al--Mn--Si intermetallic compound together with Si, improves strength by dispersion strengthening, and dissolves in the aluminum matrix to improve strength by solid solution strengthening. The Mn content of the aluminum alloy part A and the aluminum alloy ingot A is 0.60 to 1.80% by mass, preferably 0.70 to 1.70% by mass. If the Mn content is less than 0.60% by mass, the effect is small, and if it exceeds 1.80% by mass, a large intermetallic compound is likely to be formed during casting, resulting in deterioration of plastic workability.
アルミニウム合金部Ａ及びアルミニウム合金鋳塊Ａは、Ｍｇを含有してもよい。Ｍｇは、Ｍｇ２Ｓｉの析出により強度を向上させる。アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＭｇ含有量は、０．５０質量％以下（０．００質量％を含む）、好ましくは０．１０～０．４０質量％である。Ｍｇ含有量が、０．５０質量％を超えるとろう付が困難となる場合がある。 The aluminum alloy part A and the aluminum alloy ingot A may contain Mg. Mg improves strength by precipitation of Mg 2 Si. The Mg content of the aluminum alloy part A and the aluminum alloy ingot A is 0.50% by mass or less (including 0.00% by mass), preferably 0.10 to 0.40% by mass. If the Mg content exceeds 0.50% by mass, brazing may become difficult.
アルミニウム合金部Ａ及びアルミニウム合金鋳塊Ａは、Ｔｉを含有してもよい。Ｔｉは、固溶強化により強度を向上させる。アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＴｉ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．１０～０．２０質量％である。Ｔｉ含有量が、０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy part A and the aluminum alloy ingot A may contain Ti. Ti improves strength by solid solution strengthening. The Ti content of the aluminum alloy part A and the aluminum alloy ingot A is 0.30% by mass or less (including 0.00% by mass), preferably 0.10 to 0.20% by mass. If the Ti content exceeds 0.30% by mass, a large intermetallic compound is likely to be formed, which may reduce plastic workability.
アルミニウム合金部Ａ及びアルミニウム合金鋳塊Ａは、Ｚｒを含有してもよい。Ｚｒは、固溶強化により強度を向上させ、また、Ａｌ－Ｚｒ系の金属間化合物が析出してろう付後の結晶粒粗大化に作用する。アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＺｒ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．１０～０．２０質量％である。Ｚｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy portion A and the aluminum alloy ingot A may contain Zr. Zr improves the strength by solid-solution strengthening, and precipitates an Al--Zr intermetallic compound to act on grain coarsening after brazing. The Zr content of the aluminum alloy part A and the aluminum alloy ingot A is 0.30% by mass or less (including 0.00% by mass), preferably 0.10 to 0.20% by mass. When the Zr content exceeds 0.30% by mass, a large intermetallic compound is likely to be formed, which may reduce plastic workability.
アルミニウム合金部Ａ及びアルミニウム合金鋳塊Ａは、Ｃｒを含有してもよい。Ｃｒは、固溶強化により強度を向上させ、また、Ａｌ－Ｃｒ系の金属間化合物が析出してろう付後の結晶粒粗大化に作用する。アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＣｒ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｃｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy part A and the aluminum alloy ingot A may contain Cr. Cr improves the strength by solid-solution strengthening, and precipitates an Al—Cr-based intermetallic compound to act to coarsen grains after brazing. The Cr content of the aluminum alloy part A and the aluminum alloy ingot A is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. When the Cr content exceeds 0.30% by mass, it tends to form a large intermetallic compound, which may reduce the plastic workability.
アルミニウム合金部Ａ及びアルミニウム合金鋳塊Ａは、Ｖを含有してもよい。Ｖは、固溶強化により強度を向上させる。アルミニウム合金部Ａ及びアルミニウム合金鋳塊ＡのＶ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｃｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy part A and the aluminum alloy ingot A may contain V. V improves strength by solid solution strengthening. The V content of the aluminum alloy part A and the aluminum alloy ingot A is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. When the Cr content exceeds 0.30% by mass, it tends to form a large intermetallic compound, which may reduce the plastic workability.
本発明のアルミニウム合金材の製造方法に係る鋳造工程では、アルミニウム合金廃材を１０．０質量％以上含有する鋳造原料を用い、該鋳造原料を、溶解及び鋳造することにより、アルミニウム合金鋳塊Ａを得る。 In the casting process according to the method for producing an aluminum alloy material of the present invention, a casting raw material containing 10.0% by mass or more of aluminum alloy waste is used, and the casting raw material is melted and cast to obtain an aluminum alloy ingot A. obtain.
鋳造工程において、鋳造原料の一部として用いられるアルミニウム合金廃材は、０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなる自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップである。アルミニウム合金廃材に含有される成分は、自動車用熱交換器の材料において、Ａｌ－Ｍｎ－Ｓｉ－Ｃｕ系合金の心材、Ａｌ－Ｚｎ系またはＡｌ－Ｚｎ－Ｍｇ系合金の犠牲陽極材、Ａｌ－Ｓｉ系のろう材等が用いられることに起因する。なお、本発明において、アルミニウム合金クラッド材のスクラップとは、アルミニウム合金クラッド材の製造工程中で生じるアルミニウム合金クラッド材の屑であり、例えば、アルミニウム合金クラッド材の圧延工程やスリット工程などで発生する端材や、熱交換器の部品の成型で発生する端材などを指す。 In the casting process, the aluminum alloy waste used as part of the casting raw material contains 0.50% by mass or more of Si, 0.10% by mass or more of Fe, 0.10% by mass or more of Cu, and 0.50% by mass or more. Automotive heat exchanger scrap made of an aluminum alloy containing one or more elements selected from the group consisting of Mn of 0.05% by mass or more, Mg of 0.05% by mass or more, and Zn of 0.10% by mass or more, and / Or scrap of aluminum alloy clad material used for heat exchangers for automobiles. The components contained in the aluminum alloy waste material are Al--Mn--Si--Cu based alloy core material, Al--Zn based or Al--Zn--Mg based alloy sacrificial anode material, Al-- This is due to the use of a Si-based brazing material or the like. In the present invention, the scrap of the aluminum alloy clad material is the scrap of the aluminum alloy clad material generated during the manufacturing process of the aluminum alloy clad material, for example, the aluminum alloy clad material generated in the rolling process or the slitting process. It refers to offcuts and offcuts generated in the molding of heat exchanger parts.
鋳造工程において、鋳造原料の一部がアルミニウム合金廃材である。そして、鋳造工程において用いられる鋳造原料のうち、アルミニウム合金廃材の配合量は、１０．０質量％以上、好ましくは１５．０質量％以上である。鋳造原料に占めるアルミニウム合金廃材の配合量が、上記範囲にあることにより、新地金の使用に由来するＣＯ２排出量を削減することができる。また、鋳造工程において用いる鋳造原料のうち、アルミニウム合金廃材の配合量が、５０．０質量％を超えると、ＳｉやＺｎの含有量が適切な範囲を超えてしまう可能性があるため、鋳造原料のうちのアルミニウム合金廃材の配合量は、５０．０質量％以下が好ましく、４５．０質量％以下がより好ましい。 In the casting process, part of the raw material for casting is aluminum alloy waste. The content of the aluminum alloy waste material in the casting raw material used in the casting process is 10.0% by mass or more, preferably 15.0% by mass or more. When the content of the aluminum alloy waste material in the casting raw material is within the above range, it is possible to reduce CO 2 emissions resulting from the use of new ingots. In addition, if the amount of aluminum alloy waste in the casting raw material used in the casting process exceeds 50.0% by mass, the content of Si and Zn may exceed the appropriate range. The content of the aluminum alloy waste material is preferably 50.0% by mass or less, more preferably 45.0% by mass or less.
そのため、アルミニウム合金部Ａのうち、１０．０質量％以上、好ましくは１５．０～５０．０質量％が、アルミニウム合金廃材に由来する。アルミニウム合金部Ａは、鋳造原料として、１０．０質量％以上、好ましくは１５．０～５０．０質量％のアルミニウム合金廃材が配合された鋳造原料を用いて得られたものである。 Therefore, 10.0% by mass or more, preferably 15.0 to 50.0% by mass, of the aluminum alloy portion A is derived from the aluminum alloy waste material. The aluminum alloy part A is obtained by using a casting raw material containing 10.0% by mass or more, preferably 15.0 to 50.0% by mass of aluminum alloy waste as a casting raw material.
本発明のアルミニウム合金材の製造方法では、鋳造工程より後の工程及び処理並びのそれらの条件は、製造目的とするアルミニウム合金材により、適宜選択される。 In the method for producing an aluminum alloy material of the present invention, the processes and treatments after the casting process and their conditions are appropriately selected depending on the aluminum alloy material to be produced.
例えば、アルミニウム合金部Ａ単体からなるアルミニウム合金材を製造する場合、アルミニウム合金鋳塊Ａの鋳造工程、均質化処理工程、加熱工程を経て、熱間圧延にて所望の板厚にし、熱間圧延の後は、冷間圧延、中間焼鈍、最終焼鈍を組み合わせて、調質Ｈ１ｎ、Ｈ２ｎ、Ｈ３ｎ、Ｏの板材として、アルミニウム合金部Ａ単体からなるアルミニウム合金材を製造する。均質化処理及び／又は中間焼鈍及び／又は最終焼鈍は、目的の調質によっては省略される場合がある。最終的な板厚は、用途によって適宜選択されるが、０．０３ｍｍ～５ｍｍ程度が通常である。 For example, when manufacturing an aluminum alloy material consisting of an aluminum alloy part A alone, the aluminum alloy ingot A is subjected to a casting process, a homogenization process, and a heating process, and then hot-rolled to a desired thickness, and then hot-rolled. After that, cold rolling, intermediate annealing, and final annealing are combined to manufacture aluminum alloy materials consisting of the aluminum alloy part A alone as heat refining H1n, H2n, H3n, and O sheet materials. Homogenization treatment and/or intermediate annealing and/or final annealing may be omitted depending on the desired refining. The final plate thickness is appropriately selected depending on the application, but is usually about 0.03 mm to 5 mm.
また、例えば、アルミニウム合金部Ａを心材として有するアルミニウム合金クラッド材を製造する場合、皮材用のアルミニウム合金鋳塊の鋳造工程、均質化工程、加熱工程、熱間圧延工程を経て所望の板厚の皮材用のアルミニウム合金鋳塊の熱間圧延物を得る。また、必要に応じて、中間層材用のアルミニウム合金鋳塊の鋳造工程、均質化工程、加熱工程、熱間圧延工程を経て所望の板厚の中間層材用のアルミニウム合金鋳塊の熱間圧延物を得る。また、心材用のアルミニウム合金鋳塊Ａの鋳造工程、均質化工程を行い、次いで、心材用のアルミニウム合金鋳塊Ａと皮材用のアルミニウム合金鋳塊の熱間圧延物を、必要に応じて更に、中間層材用のアルミニウム合金鋳塊の熱間圧延物を、所望の積層構成となるように、組み合わせる工程、加熱工程、熱間圧延工程を経て、所望の板厚のクラッド物を得る。熱間圧延の後は、冷間圧延、中間焼鈍、最終焼鈍を組み合わせて、調質Ｈ１ｎ、Ｈ２ｎ、Ｈ３ｎ、Ｏの板材として、アルミニウム合金部Ａを心材として有するアルミニウム合金クラッド材を製造する。均質化処理及び／又は中間焼鈍及び／又は最終焼鈍は、目的の調質によっては省略される場合がある。最終的な板厚は、用途によって適宜選択されるが、０．０３ｍｍ～５ｍｍ程度が通常である。 Further, for example, when producing an aluminum alloy clad material having the aluminum alloy part A as a core material, the desired plate thickness is obtained through the casting process of the aluminum alloy ingot for the skin material, the homogenization process, the heating process, and the hot rolling process. obtain a hot-rolled product of an aluminum alloy ingot for the skin material. In addition, if necessary, the aluminum alloy ingot for the intermediate layer material is hot-rolled to a desired thickness through the casting process, homogenization process, heating process, and hot rolling process of the aluminum alloy ingot for the intermediate layer material. Get a rolling product. In addition, a casting process and a homogenization process are performed for the aluminum alloy ingot A for the core material, and then hot-rolled products of the aluminum alloy ingot A for the core material and the aluminum alloy ingot for the skin material are produced as necessary. Furthermore, the hot-rolled aluminum alloy ingots for the intermediate layer material are combined, heated, and hot-rolled so as to have a desired lamination structure to obtain a clad material having a desired plate thickness. After hot rolling, cold rolling, intermediate annealing, and final annealing are combined to produce tempered H1n, H2n, H3n, and O sheet materials as aluminum alloy clad materials having the aluminum alloy part A as a core material. Homogenization treatment and/or intermediate annealing and/or final annealing may be omitted depending on the desired refining. The final plate thickness is appropriately selected depending on the application, but is usually about 0.03 mm to 5 mm.
本発明のアルミニウム合金材の製造方法の形態について、説明する。本発明の第一の形態のアルミニウム合金材の製造方法は、アルミニウム合金部Ａ単体からなるアルミニウム合金材の製造方法であり、アルミニウム合金鋳塊Ａを鋳造する鋳造工程を有する。また、本発明の第二の形態のアルミニウム合金材の製造方法は、アルミニウム合金部Ａを心材として有するアルミニウム合金クラッド材の製造方法であり、アルミニウム合金鋳塊Ａを鋳造する鋳造工程を有する。 A mode of the method for producing an aluminum alloy material according to the present invention will be described. A method for producing an aluminum alloy material according to the first embodiment of the present invention is a method for producing an aluminum alloy material consisting of an aluminum alloy portion A alone, and has a casting step of casting an aluminum alloy ingot A. A method for producing an aluminum alloy material according to the second embodiment of the present invention is a method for producing an aluminum alloy clad material having an aluminum alloy portion A as a core material, and includes a casting step of casting an aluminum alloy ingot A.
本発明の第二の形態のアルミニウム合金材の製造方法としては、アルミニウム合金鋳塊Ａを得る鋳造工程を有し、鋳造工程を行い得られるアルミニウム合金鋳塊Ａを心材用のアルミニウム合金鋳塊として用い、１つ又は２つの皮材用のアルミニウム合金鋳塊と組み合わせて、すなわち、心材用のアルミニウム合金鋳塊Ａの一方の面側又は両面側に、皮材用のアルミニウム合金鋳塊を組み合わせて、アルミニウム合金クラッド材を得るアルミニウム合金材の製造方法が挙げられる。２つの皮材用の鋳塊を組み合わせる場合、それらは、同一の組成のものであっても、異なる組成のものであってもよい。また、皮材用のアルミニウム合金鋳塊から形成される皮材の機能としては、特に制限されず、ろう材、犠牲陽極材、拡散防止材（ろう付を阻害する元素がろう付中に材料表面に拡散するのを防止する材料）等の機能を有する皮材が挙げられる。また、本発明の第二の形態のアルミニウム合金材の製造方法では、心材用のアルミニウム合金鋳塊Ａに、１つ又は２つの皮材用のアルミニウム合金鋳塊に加えて、更に中間層材用のアルミニウム合金鋳塊を組み合わせてもよい。アルミニウム合金クラッド材の層構成としては、例えば、ろう材／心材の順に積層された２層材、ろう材／心材／ろう材の順に積層された３層材、ろう材／心材／犠牲陽極材の順に積層された３層材、ろう材／中間層材／心材の順に積層された３層材、ろう材／中間層材／心材／ろう材の順に積層された４層材、ろう材／中間層材／心材／犠牲陽極材の順に積層された４層材、ろう材／中間層材／心材／中間層材／ろう材の順に積層された５層材等が挙げられる。ろう材用のアルミニウム合金鋳塊の成分、犠牲陽極材用のアルミニウム合金鋳塊の成分及び中間層材用のアルミニウム合金鋳塊の成分は、本発明の効果であるアルミニウム合金廃材の配合とは無関係であるため、従来知見に基づき適切な範囲を添加すればよい。そして、本発明の第二の形態のアルミニウム合金材の製造方法により、心材としてアルミニウム合金部Ａを有し、心材の一方の面側又は両面側に皮材がクラッドされているアルミニウム合金クラッド材を得る。つまり、本発明の第二の形態のアルミニウム合金材としては、心材としてアルミニウム合金部Ａを有し、心材の一方の面側又は両面側に皮材がクラッドされているアルミニウム合金クラッド材が挙げられる。なお、心材の一方の面側に皮材がクラッドされているとは、心材の一方の面又は両面に直接皮材がクラッドされている場合と、心材の一方の面又は両面に直接クラッドされている中間材層等を介して、皮材がクラッドされている場合の両方を指す。 The method for producing an aluminum alloy material according to the second embodiment of the present invention includes a casting process for obtaining an aluminum alloy ingot A, and the aluminum alloy ingot A obtained by the casting process is used as an aluminum alloy ingot for the core material. used, in combination with one or two aluminum alloy ingots for the skin material, that is, on one side or both sides of the aluminum alloy ingot A for the core material, in combination with the aluminum alloy ingot for the skin material and a method for producing an aluminum alloy material to obtain an aluminum alloy clad material. When two skin ingots are combined, they may be of the same composition or of different compositions. In addition, the functions of the skin material formed from the aluminum alloy ingot for the skin material are not particularly limited, and include a brazing material, a sacrificial anode material, and a diffusion preventing material (an element that inhibits brazing is added to the surface of the material during brazing). materials that prevent diffusion into the body). In addition, in the method for producing an aluminum alloy material according to the second embodiment of the present invention, in addition to the aluminum alloy ingot A for the core material, one or two aluminum alloy ingots for the skin material are further added to the aluminum alloy ingot for the intermediate layer material. of aluminum alloy ingots may be combined. Examples of the layer structure of the aluminum alloy clad material include a two-layer material in which brazing material/core material is laminated in this order, a three-layer material in which brazing material/core material/brazing material are laminated in this order, and a brazing material/core material/sacrificial anode material. 3-layer material laminated in order, 3-layer material laminated in order of brazing material/intermediate layer material/core material, 4-layer material laminated in order of brazing material/intermediate layer material/core material/brazing material, brazing material/intermediate layer Examples include a four-layer material laminated in the order of material/core material/sacrificial anode material, and a five-layer material laminated in the order of brazing material/intermediate layer material/core material/intermediate layer material/brazing material. The composition of the aluminum alloy ingot for the brazing filler metal, the composition of the aluminum alloy ingot for the sacrificial anode material, and the composition of the aluminum alloy ingot for the intermediate layer material are irrelevant to the composition of the aluminum alloy scrap, which is the effect of the present invention. Therefore, an appropriate range may be added based on conventional knowledge. Then, by the method for producing an aluminum alloy material according to the second embodiment of the present invention, an aluminum alloy clad material having an aluminum alloy portion A as a core material and having a skin material clad on one side or both sides of the core material is produced. obtain. That is, the aluminum alloy material of the second embodiment of the present invention includes an aluminum alloy clad material having an aluminum alloy portion A as a core material and having a skin material clad on one side or both sides of the core material. . The phrase “one surface of the core material is clad with skin material” means that one surface or both surfaces of the core material are directly clad with skin material, or that one surface or both surfaces of the core material is directly clad with skin material. It refers to both cases where the skin material is clad via an intermediate material layer or the like.
本発明の第二の形態のアルミニウム合金材の製造方法において、心材用のアルミニウム合金鋳塊Ａに皮材用のアルミニウム合金鋳塊を組み合わせる場合、心材用のアルミニウム合金鋳塊Ａに組み合わせる皮材用のアルミニウム合金鋳塊としては、ろう材用アルミニウム合金鋳塊Ｂ又は犠牲陽極材用アルミニウム合金鋳塊Ｃが挙げられる。本発明の第二の形態のアルミニウム合金材の製造方法としては、アルミニウム合金鋳塊Ａを得る鋳造工程を有し、鋳造工程を行い得られるアルミニウム合金鋳塊Ａを心材用のアルミニウム合金鋳塊として用い、１つ又は２つのろう材用アルミニウム合金鋳塊Ｂ又は犠牲陽極材用アルミニウム合金鋳塊Ｃと組み合わせて、すなわち、心材用のアルミニウム合金鋳塊Ａの一方の面側又は両面側に、ろう材用アルミニウム合金鋳塊Ｂ又は犠牲陽極材用アルミニウム合金鋳塊Ｃを組み合わせて、アルミニウム合金クラッド材を得るアルミニウム合金材の製造方法が挙げられる。つまり、本発明の第二の形態のアルミニウム合金材としては、心材としてアルミニウム合金部Ａを有し、心材の一方の面側又は両面側に、ろう材Ｂ又は犠牲陽極材Ｃがクラッドされているアルミニウム合金クラッド材、すなわち、ろう材Ｂ／アルミニウム合金部Ａからなる心材の順に積層された２層材、ろう材Ｂ／アルミニウム合金部Ａからなる心材／ろう材Ｂの順に積層された３層材、ろう材Ｂ／アルミニウム合金部Ａからなる心材／犠牲陽極材Ｃの順に積層された３層材が挙げられる。 In the method for producing an aluminum alloy material according to the second embodiment of the present invention, when combining the aluminum alloy ingot A for the core material with the aluminum alloy ingot for the skin material, Examples of the aluminum alloy ingots include aluminum alloy ingot B for brazing material and aluminum alloy ingot C for sacrificial anode material. The method for producing an aluminum alloy material according to the second embodiment of the present invention includes a casting process for obtaining an aluminum alloy ingot A, and the aluminum alloy ingot A obtained by the casting process is used as an aluminum alloy ingot for the core material. In combination with one or two brazing aluminum alloy ingots B or sacrificial anode aluminum alloy ingots C, that is, on one side or both sides of the core aluminum alloy ingot A, the brazing A method for producing an aluminum alloy material, in which an aluminum alloy clad material is obtained by combining the aluminum alloy ingot B for the material or the aluminum alloy ingot C for the sacrificial anode material. That is, the aluminum alloy material of the second embodiment of the present invention has an aluminum alloy portion A as a core material, and is clad with a brazing material B or a sacrificial anode material C on one side or both sides of the core material. Aluminum alloy clad material, that is, a two-layer material in which a core material consisting of brazing material B/aluminum alloy part A is laminated in this order, and a three-layer material in which a core material consisting of brazing material B/aluminum alloy part A/brazing material B is laminated in this order , brazing material B/aluminum alloy part A, and a core material/sacrificial anode material C laminated in this order.
本発明の第二の形態のアルミニウム合金材の製造方法において、心材用のアルミニウム合金鋳塊Ａに、皮材用のアルミニウム合金鋳塊に加え、更に中間層材用のアルミニウム合金鋳塊を組み合わせる場合として、ろう材／中間層材／心材／ろう材又は犠牲陽極材の順に積層されている４層材のアルミニウム合金クラッド材の製造方法であり、アルミニウム合金鋳塊Ａを得る鋳造工程を有し、心材用のアルミニウム合金鋳塊として、鋳造工程を行い得られるアルミニウム合金鋳塊Ａを用い、ろう材用のアルミニウム合金鋳塊として、ろう材用アルミニウム合金鋳塊Ｂを用い、犠牲陽極材用のアルミニウム合金鋳塊として、犠牲陽極材用アルミニウム合金鋳塊Ｃを用い、中間層材用のアルミニウム合金鋳塊と組み合わせて、アルミニウム合金クラッド材を得るアルミニウム合金材の製造方法が挙げられる。つまり、本発明の第二の形態のアルミニウム合金材としては、ろう材／中間層材／心材／ろう材又は犠牲陽極材の順に積層されている４層材のアルミニウム合金クラッド材であり、心材がアルミニウム合金部Ａであり、ろう材がろう材Ｂであり、犠牲陽極材が犠牲陽極材Ｃであるアルミニウム合金クラッド材、すなわち、ろう材Ｂ／中間層材／アルミニウム合金Ａからなる心材／ろう材Ｂの順に積層された４層材、ろう材Ｂ／中間層材／アルミニウム合金Ａからなる心材／犠牲陽極材Ｃの順に積層された４層材が挙げられる。 In the method for producing an aluminum alloy material according to the second embodiment of the present invention, when combining the aluminum alloy ingot A for the core material with the aluminum alloy ingot for the skin material and further with the aluminum alloy ingot for the intermediate layer material. is a method for producing a four-layer aluminum alloy clad material in which brazing material/intermediate layer material/core material/brazing material or sacrificial anode material are laminated in this order, comprising a casting step of obtaining an aluminum alloy ingot A, An aluminum alloy ingot A obtained by a casting process is used as the aluminum alloy ingot for the core material, an aluminum alloy ingot B for the brazing material is used as the aluminum alloy ingot for the brazing material, and aluminum is used as the sacrificial anode material. There is a method of manufacturing an aluminum alloy material in which an aluminum alloy ingot C for a sacrificial anode material is used as an alloy ingot and combined with an aluminum alloy ingot for an intermediate layer material to obtain an aluminum alloy clad material. That is, the aluminum alloy material of the second embodiment of the present invention is a four-layer aluminum alloy clad material in which brazing material/intermediate layer material/core material/brazing material or sacrificial anode material is laminated in this order, and the core material is An aluminum alloy clad material having an aluminum alloy portion A, a brazing material B as a brazing material, and a sacrificial anode material C as a sacrificial anode material, that is, a core material/brazing material consisting of brazing material B/intermediate layer material/aluminum alloy A and a four-layer material in which brazing material B/intermediate layer material/aluminum alloy A core material/sacrificial anode material C are laminated in this order.
本発明の第二の形態のアルミニウム合金材の製造方法において、心材用のアルミニウム合金鋳塊Ａに、皮材用のアルミニウム合金鋳塊に加え、更に中間層材用のアルミニウム合金鋳塊を組み合わせる場合として、ろう材／中間層材／心材／中間層材／ろう材の順に積層されている５層材のアルミニウム合金クラッド材の製造方法であり、アルミニウム合金鋳塊Ａを得る鋳造工程を有し、心材用のアルミニウム合金鋳塊として、鋳造工程を行い得られるアルミニウム合金鋳塊Ａを用い、ろう材用のアルミニウム合金鋳塊として、ろう材用アルミニウム合金鋳塊Ｂを用い、中間層材用のアルミニウム合金鋳塊と組み合わせて、アルミニウム合金クラッド材を得るアルミニウム合金材の製造方法が挙げられる。つまり、本発明の第二の形態のアルミニウム合金材としては、ろう材／中間層材／心材／中間層材／ろう材の順に積層されている５層材のアルミニウム合金クラッド材であり、心材がアルミニウム合金部Ａであり、ろう材がろう材Ｂであるアルミニウム合金クラッド材、すなわち、ろう材Ｂ／中間層材／アルミニウム合金部Ａからなる心材／中間層材／ろう材Ｂの順に積層された５層材が挙げられる。２つのろう材用アルミニウム合金鋳塊は、同一の組成のものであっても、異なる組成のものであってもよい。また、２つの中間層材は、同一の組成であっても、異なる組成であってもよい。 In the method for producing an aluminum alloy material according to the second embodiment of the present invention, when combining the aluminum alloy ingot A for the core material with the aluminum alloy ingot for the skin material and further with the aluminum alloy ingot for the intermediate layer material. is a method for manufacturing an aluminum alloy clad material of a five-layer material in which brazing material/intermediate layer material/core material/intermediate layer material/brazing material are laminated in this order, comprising a casting step of obtaining an aluminum alloy ingot A, Aluminum alloy ingot A obtained by a casting process is used as the aluminum alloy ingot for the core material, aluminum alloy ingot B for the brazing material is used as the aluminum alloy ingot for the brazing material, and aluminum for the intermediate layer material. A method for producing an aluminum alloy material, in which an aluminum alloy clad material is obtained in combination with an alloy ingot. That is, the aluminum alloy material of the second embodiment of the present invention is a five-layer aluminum alloy clad material in which brazing material/intermediate layer material/core material/intermediate layer material/brazing material are laminated in this order, and the core material is An aluminum alloy clad material having an aluminum alloy portion A and a brazing material B, that is, a core material composed of brazing material B/intermediate layer material/aluminum alloy portion A/intermediate layer material/brazing material B laminated in this order. A five-layer material is mentioned. The two brazing aluminum alloy ingots may have the same composition or different compositions. Also, the two intermediate layer materials may have the same composition or different compositions.
本発明の第二の形態のアルミニウム合金材の製造方法において、中間層材用のアルミニウム合金鋳塊としては、中間層材用アルミニウム合金鋳塊Ｄが挙げられる。また、本発明の第二の形態のアルミニウム合金材において、中間層材としては、中間層材Ｄが挙げられる。 In the method for producing an aluminum alloy material according to the second aspect of the present invention, an aluminum alloy ingot D for an intermediate layer material can be used as the aluminum alloy ingot for the intermediate layer material. In addition, in the aluminum alloy material of the second embodiment of the present invention, the intermediate layer material D may be mentioned as the intermediate layer material.
上記本発明の第二の形態のアルミニウム合金材の製造方法に用いられるろう材用アルミニウム合金鋳塊Ｂ、犠牲陽極材用アルミニウム合金鋳塊Ｃ、中間層材用アルミニウム合金鋳塊Ｄ、及び上記本発明の第二の形態のアルミニウム合金材に係るろう材Ｂ、犠牲陽極材Ｃ、中間層材Ｄについて、説明する。 Aluminum alloy ingot B for brazing material, aluminum alloy ingot C for sacrificial anode material, aluminum alloy ingot D for intermediate layer material, and the present invention, which are used in the method for producing an aluminum alloy material according to the second embodiment of the present invention. The brazing material B, the sacrificial anode material C, and the intermediate layer material D relating to the aluminum alloy material of the second embodiment of the invention will be explained.
ろう材用アルミニウム合金鋳塊Ｂ及びろう材Ｂは、２．５０～１３．００質量％のＳｉ及び０．０５～１．００質量％のＦｅを含有し、Ｚｎ含有量が５．５０質量％以下、Ｍｎ含有量が１．００質量％以下、Ｃｕ含有量が１．００質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％、Ｖ含有量が０．３０質量％以下、Ｓｒ含有量が０．１０質量％以下、Ｎａ含有量が０．１０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなる。 The aluminum alloy ingot B for brazing material and the brazing material B contain 2.50 to 13.00% by mass of Si and 0.05 to 1.00% by mass of Fe, and the Zn content is 5.50% by mass. Below, the Mn content is 1.00% by mass or less, the Cu content is 1.00% by mass or less, the Cr content is 0.30% by mass or less, the Ti content is 0.30% by mass or less, and the Zr content is 0.30% by mass, V content of 0.30% by mass or less, Sr content of 0.10% by mass or less, Na content of 0.10% by mass or less, and the balance being aluminum and unavoidable impurities Made of alloy.
Ｓｉは、融点を低下させて液相を生じ、ろう付けを可能にする。ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＳｉ含有量は、２．５０～１３．００質量％、好ましくは３．５０～１２．５０質量％、更に好ましくは４．００～１２．５０質量％である。Ｓｉの含有量が、２．５０質量％未満では、生じる液相が僅かであり、ろう付けが機能し難くなり、また、１３．００質量％を超えると、例えばフィンなどの相手材へ拡散するＳｉ量が過剰となり、相手材の溶融が発生する。 Si lowers the melting point to produce a liquid phase and enables brazing. The Si content of the brazing aluminum alloy ingot B and the brazing material B is 2.50 to 13.00% by mass, preferably 3.50 to 12.50% by mass, more preferably 4.00 to 12.50. % by mass. If the Si content is less than 2.50% by mass, the amount of liquid phase generated is small, making brazing difficult to function. The amount of Si becomes excessive and the mating material melts.
Ｆｅは、Ａｌ－Ｆｅ系やＡｌ－Ｆｅ－Ｓｉ系の化合物を形成し易い。Ａｌ－Ｆｅ－Ｓｉ系化合物の形成によりろう材の有効Ｓｉ量を低下させ、また、Ａｌ－Ｆｅ系やＡｌ－Ｆｅ－Ｓｉ系の化合物の形成によりろう付時におけるろうの流動性を低下させ、ろう付性を阻害する。そのため、ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＦｅの含有量は、０．０５～１．００質量％、好ましくは０．１０～０．８０質量％である。Ｆｅ含有量が１．００質量％を超えると、上述のようにろう付性を阻害してろう付が不十分となり、また、Ｆｅ含有量が０．０５質量％未満では、高純度アルミニウム地金を使用しなければならなくなってコスト高を招く。 Fe tends to form Al--Fe-based and Al--Fe--Si-based compounds. The formation of an Al-Fe-Si-based compound reduces the effective amount of Si in the brazing filler metal, and the formation of an Al-Fe-based or Al-Fe-Si-based compound reduces the fluidity of the brazing filler metal during brazing, Impairs brazability. Therefore, the Fe content of the brazing aluminum alloy ingot B and the brazing material B is 0.05 to 1.00% by mass, preferably 0.10 to 0.80% by mass. If the Fe content exceeds 1.00% by mass, the brazeability is impaired as described above, resulting in insufficient brazing. must be used, resulting in high costs.
ろう材用アルミニウム合金鋳塊Ｂ及びろう材Ｂは、Ｚｎを含有してもよい。Ｚｎは、電位を卑にすることができ、心材との電位差を形成することで犠牲陽極効果により耐食性を向上でき、また、Ｚｎの含有は、Ｚｎを含有するアルミニウム合金廃材の配合許容量を増大させる。ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＺｎの含有量は、５．５０質量％以下（０．００質量％を含む）、好ましくは０．１０～３．００質量％である。Ｚｎ含有量が５．５０質量％を超えると、例えばフィンなどの相手材との接合部にＺｎが濃縮し、これが優先腐食して相手材が剥離する場合がある。 The aluminum alloy ingot B for brazing material and the brazing material B may contain Zn. Zn can make the potential base, and by forming a potential difference with the core material, the corrosion resistance can be improved by the sacrificial anode effect.In addition, the inclusion of Zn increases the allowable blending amount of aluminum alloy scrap containing Zn. Let The Zn content of the aluminum alloy ingot B for brazing material and the brazing material B is 5.50% by mass or less (including 0.00% by mass), preferably 0.10 to 3.00% by mass. When the Zn content exceeds 5.50% by mass, Zn concentrates in the joints with the mating material such as fins, which may lead to preferential corrosion and exfoliation of the mating material.
ろう材用アルミニウム合金鋳塊Ｂ及びろう材Ｂは、Ｍｎを含有してもよい。Ｍｎの含有は、Ｍｎを含有するアルミニウム合金廃材の配合許容量を増大させる。ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＭｎの含有量は、１．００質量％以下（０．００質量％を含む）、好ましくは０．１０～０．９０質量％である。Ｍｎ含有量が１．００質量％を超えると粗大な化合物が生成して冷間加工で割れが発生する可能性があり、製造の難易度が上がる。 The aluminum alloy ingot B for brazing material and the brazing material B may contain Mn. The inclusion of Mn increases the permissible blending amount of aluminum alloy scraps containing Mn. The content of Mn in the brazing aluminum alloy ingot B and the brazing material B is 1.00% by mass or less (including 0.00% by mass), preferably 0.10 to 0.90% by mass. If the Mn content exceeds 1.00% by mass, coarse compounds may form and cracks may occur during cold working, increasing the difficulty of production.
ろう材用アルミニウム合金鋳塊Ｂ及びろう材Ｂは、Ｃｕを含有してもよい。Ｃｕの含有は、Ｃｕを含有するアルミニウム合金廃材の配合許容量を増大させる。ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＣｕの含有量は、１．００質量％以下（０．００質量％を含む）、好ましくは０．２０～０．９０質量％である。Ｃｕ含有量が１．００質量％を超えると鋳造時に割れが生じやすく、製造の難易度が上がる。 The aluminum alloy ingot B for brazing material and the brazing material B may contain Cu. The inclusion of Cu increases the permissible blending amount of Cu-containing aluminum alloy scraps. The content of Cu in the brazing aluminum alloy ingot B and the brazing material B is 1.00% by mass or less (including 0.00% by mass), preferably 0.20 to 0.90% by mass. If the Cu content exceeds 1.00% by mass, cracks are likely to occur during casting, increasing the difficulty of production.
ろう材用アルミニウム合金鋳塊Ｂ及びろう材Ｂは、Ｔｉを含有してもよい。Ｔｉは、固溶強化により強度を向上させる。ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＴｉ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｔｉ含有量が、０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy ingot B for brazing material and the brazing material B may contain Ti. Ti improves strength by solid solution strengthening. The Ti content of the aluminum alloy ingot B for brazing material and the brazing material B is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. If the Ti content exceeds 0.30% by mass, a large intermetallic compound is likely to be formed, which may reduce plastic workability.
ろう材用アルミニウム合金鋳塊Ｂ及びろう材Ｂは、Ｚｒを含有してもよい。Ｚｒは、固溶強化により強度を向上させ、また、Ａｌ－Ｚｒ系の金属間化合物が析出してろう付後の結晶粒粗大化に作用する。ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＺｒ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｚｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy ingot B for brazing material and the brazing material B may contain Zr. Zr improves the strength by solid-solution strengthening, and precipitates an Al--Zr intermetallic compound to act on grain coarsening after brazing. The Zr content of the aluminum alloy ingot B for brazing material and the brazing material B is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. When the Zr content exceeds 0.30% by mass, a large intermetallic compound is likely to be formed, which may reduce plastic workability.
ろう材用アルミニウム合金鋳塊Ｂ及びろう材Ｂは、Ｃｒを含有してもよい。Ｃｒは、固溶強化により強度を向上させ、また、Ａｌ－Ｃｒ系の金属間化合物が析出してろう付後の結晶粒粗大化に作用する。ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＣｒ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｃｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy ingot B for brazing material and the brazing material B may contain Cr. Cr improves the strength by solid-solution strengthening, and precipitates an Al—Cr-based intermetallic compound to act to coarsen grains after brazing. The Cr content of the brazing aluminum alloy ingot B and the brazing material B is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. When the Cr content exceeds 0.30% by mass, it tends to form a large intermetallic compound, which may reduce the plastic workability.
ろう材用アルミニウム合金鋳塊Ｂ及びろう材Ｂは、Ｖを含有してもよい。Ｖは、固溶強化により強度を向上させる。ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＶ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｃｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy ingot B for brazing material and the brazing material B may contain V. V improves strength by solid solution strengthening. The aluminum alloy ingot B for brazing material and the brazing material B have a V content of 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. When the Cr content exceeds 0.30% by mass, it tends to form a large intermetallic compound, which may reduce the plastic workability.
ろう材用アルミニウム合金鋳塊Ｂ及びろう材Ｂは、Ｓｒを含有してもよい。Ｓｒは、Ｓｉ粒子を微細化してろう付性を向上させる。ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＳｒ含有量は、０．１０質量％以下（０．００質量％を含む）である。Ｓｒは鋳造中に酸化しやすいため、Ｓｒ含有量が０．１０質量％を超えて製造するのは困難である。 The aluminum alloy ingot B for brazing material and the brazing material B may contain Sr. Sr refines Si particles to improve brazeability. The Sr content of the brazing aluminum alloy ingot B and the brazing material B is 0.10% by mass or less (including 0.00% by mass). Since Sr is easily oxidized during casting, it is difficult to manufacture the Sr content exceeding 0.10% by mass.
ろう材用アルミニウム合金鋳塊Ｂ及びろう材Ｂは、Ｎａを含有してもよい。Ｎａは、Ｓｉ粒子を微細化してろう付性を向上させる。ろう材用アルミニウム合金鋳塊Ｂ及びろう材ＢのＮａ含有量は、０．１０質量％以下（０．００質量％を含む）である。Ｎａは鋳造中に酸化しやすいため、Ｎａ含有量が０．１０質量％を超えて製造するのは困難である。 The aluminum alloy ingot B for brazing material and the brazing material B may contain Na. Na refines Si particles to improve brazeability. The aluminum alloy ingot B for brazing material and the Na content of the brazing material B are 0.10% by mass or less (including 0.00% by mass). Since Na is easily oxidized during casting, it is difficult to produce the Na content exceeding 0.10% by mass.
犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材Ｃは、０．５０～６．００質量％のＺｎ、０．０５～１．５０質量％のＳｉ、及び０．０５～２．００質量％のＦｅを含有し、Ｍｇ含有量が３．００質量％以下、Ｍｎ含有量が１．８０質量％以下、Ｃｕ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなる。 The sacrificial anode material aluminum alloy ingot C and the sacrificial anode material C contain 0.50 to 6.00 mass% Zn, 0.05 to 1.50 mass% Si, and 0.05 to 2.00 mass% contains Fe, Mg content is 3.00% by mass or less, Mn content is 1.80% by mass or less, Cu content is 0.50% by mass or less, Cr content is 0.30% by mass or less, The aluminum alloy has a Ti content of 0.30% by mass or less, a Zr content of 0.30% by mass or less, a V content of 0.30% by mass or less, and the balance being aluminum and unavoidable impurities.
Ｚｎは、電位を卑にすることができ、心材との電位差を形成することで犠牲陽極効果により耐食性を向上できる。犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材ＣのＺｎの含有量は、０．５０～６．００質量％、好ましくは１．００～５．００質量％である。Ｚｎ含有量が０．５０質量％未満ではその効果が十分ではなく、６．００質量％を超えると腐食速度が速くなり早期に犠牲陽極材が消失し、耐食性が低下する。 Zn can make the potential base, and by forming a potential difference with the core material, the corrosion resistance can be improved by the sacrificial anode effect. The content of Zn in the aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C is 0.50 to 6.00% by mass, preferably 1.00 to 5.00% by mass. If the Zn content is less than 0.50% by mass, the effect is not sufficient, and if the Zn content exceeds 6.00% by mass, the corrosion rate increases, the sacrificial anode material disappears early, and the corrosion resistance decreases.
Ｓｉは、Ｓｉを含有するアルミニウム合金廃材の配合許容量を増大させる。犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材ＣのＳｉ含有量は、０．０５～１．５０質量％、好ましくは０．０５～１．２０質量％である。Ｓｉ含有量が、０．０５質量％未満では、高純度アルミニウム地金を使用しなければならずコスト高となり、また、１．５０質量％を超えると犠牲陽極材の融点が低下して溶融してしまい、また、犠牲陽極材の電位を貴にするため、犠牲陽極効果を阻害して耐食性を低下させる場合がある。 Si increases the mixing tolerance of aluminum alloy waste containing Si. The Si content of the aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C is 0.05 to 1.50% by mass, preferably 0.05 to 1.20% by mass. If the Si content is less than 0.05% by mass, high-purity aluminum ingots must be used, resulting in high costs. In addition, since the potential of the sacrificial anode material is made noble, the sacrificial anode effect may be inhibited and the corrosion resistance may be lowered.
Ｆｅは、Ｓｉ、ＭｎとともにＡｌ－Ｆｅ－Ｍｎ－Ｓｉ系の化合物を形成し、分散強化により強度を向上させる。犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材ＣのＦｅ含有量は、０．０５～２．００質量％、好ましくは０．０５～１．５０質量％以下である。Ｆｅ含有量が、０．０５％未満では、高純度アルミニウム地金を使用しなければならずコスト高となり、また、２．００質量％を超えると鋳造時に巨大金属間化合物が形成され易くなり、塑性加工性を低下させる。 Fe forms an Al--Fe--Mn--Si compound together with Si and Mn, and improves strength by dispersion strengthening. The Fe content of the aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C is 0.05 to 2.00% by mass, preferably 0.05 to 1.50% by mass or less. If the Fe content is less than 0.05%, high-purity aluminum ingots must be used, resulting in high costs. Reduces plastic workability.
犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材Ｃは、Ｍｎ含有することができる。Ｍｎの含有は、Ｍｎを含有するアルミニウム合金廃材の配合許容量を増大させる。犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材ＣのＭｎ含有量は、１．８０質量％以下（０．００質量％を含む）、好ましくは０．１０～１．５０質量％である。Ｍｎ含有量が１．８０質量％を超えると粗大な化合物が生成して冷間加工で割れが発生する可能性があり、製造の難易度が上がる。 The aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C can contain Mn. The inclusion of Mn increases the permissible blending amount of aluminum alloy scraps containing Mn. The Mn content of the aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C is 1.80% by mass or less (including 0.00% by mass), preferably 0.10 to 1.50% by mass. If the Mn content exceeds 1.80% by mass, coarse compounds may form and cracks may occur during cold working, increasing the difficulty of production.
犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材Ｃは、Ｍｇを含有することができる。Ｍｇは、Ｍｇ２Ｓｉの析出により強度を向上させ、また、犠牲陽極材自身の強度を向上させるだけでなく、ろう付加熱することにより心材へＭｇが拡散して心材の強度も向上させる。犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材ＣのＭｇ含有量は、３．００質量％以下（０．００質量％を含む）、好ましくは０．５０～２．００質量％である。Ｍｇ含有量が３．００質量％を超えると熱間クラッド圧延時の圧着が困難となる場合がある。なお、Ｍｇはノコロックろう付におけるろう付性を阻害するため、犠牲陽極材が０．５０質量％以上のＭｇを含有する場合は、犠牲陽極材にノコロックろう付をすることができない。この場合には、例えばチューブ同士の接合には溶接などの手段を用いる必要がある。 The aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C can contain Mg. Mg not only improves the strength of the sacrificial anode material itself by precipitation of Mg 2 Si, but also improves the strength of the core material by diffusing Mg into the core material by brazing additional heating. The Mg content of the aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C is 3.00% by mass or less (including 0.00% by mass), preferably 0.50 to 2.00% by mass. When the Mg content exceeds 3.00% by mass, pressure bonding during hot clad rolling may become difficult. Since Mg impairs brazeability in Nocolok brazing, when the sacrificial anode material contains 0.50% by mass or more of Mg, the sacrificial anode material cannot be Nocolok brazed. In this case, for example, it is necessary to use means such as welding to join the tubes together.
犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材Ｃは、Ｃｕを含有してもよい。Ｃｕの含有は、Ｃｕを含有するアルミニウム合金廃材の配合許容量を増大させる。犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材ＣのＣｕの含有量は、０．５０質量％以下（０．００質量％を含む）、好ましくは０．１０～０．４０質量％である。Ｃｕ含有量が０．５０質量％を超えると犠牲陽極材の孔食電位が貴化してしまい、犠牲防食の効果を低下させる場合がある。 The aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C may contain Cu. The inclusion of Cu increases the permissible blending amount of Cu-containing aluminum alloy scraps. The content of Cu in the aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C is 0.50% by mass or less (including 0.00% by mass), preferably 0.10 to 0.40% by mass. . If the Cu content exceeds 0.50% by mass, the pitting potential of the sacrificial anode material becomes noble, which may reduce the effect of sacrificial corrosion protection.
犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材Ｃは、Ｔｉを含有してもよい。Ｔｉは、固溶強化により強度を向上させる。犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材ＣのＴｉ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｔｉ含有量が、０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C may contain Ti. Ti improves strength by solid solution strengthening. The Ti content of the aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. If the Ti content exceeds 0.30% by mass, a large intermetallic compound is likely to be formed, which may reduce plastic workability.
犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材Ｃは、Ｚｒを含有してもよい。Ｚｒは、固溶強化により強度を向上させ、また、Ａｌ－Ｚｒ系の金属間化合物が析出してろう付後の結晶粒粗大化に作用する。犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材ＣのＺｒ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｚｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C may contain Zr. Zr improves the strength by solid-solution strengthening, and precipitates an Al--Zr intermetallic compound to act on grain coarsening after brazing. The Zr content of the aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. When the Zr content exceeds 0.30% by mass, a large intermetallic compound is likely to be formed, which may reduce plastic workability.
犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材Ｃは、Ｃｒを含有してもよい。Ｃｒは、固溶強化により強度を向上させ、また、Ａｌ－Ｃｒ系の金属間化合物が析出してろう付後の結晶粒粗大化に作用する。犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材ＣのＣｒ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｃｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C may contain Cr. Cr improves the strength by solid-solution strengthening, and precipitates an Al—Cr-based intermetallic compound to act to coarsen grains after brazing. The Cr content of the aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. When the Cr content exceeds 0.30% by mass, it tends to form a large intermetallic compound, which may reduce the plastic workability.
犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材Ｃは、Ｖを含有してもよい。Ｖは、固溶強化により強度を向上させる。犠牲陽極材用アルミニウム合金鋳塊Ｃ及び犠牲陽極材ＣのＶ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｃｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C may contain V. V improves strength by solid solution strengthening. The aluminum alloy ingot C for sacrificial anode material and the sacrificial anode material C have a V content of 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. When the Cr content exceeds 0.30% by mass, it tends to form a large intermetallic compound, which may reduce the plastic workability.
中間層材用アルミニウム合金鋳塊Ｄ及び中間層材Ｄは、０．０５～１．５０質量％のＳｉ、及び０．０５～２．００質量％のＦｅを含有し、Ｚｎ含有量が６．００質量％以下、Ｍｎ含有量が１．８０質量％以下、Ｃｕ含有量が１．００質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなる。 The intermediate layer material aluminum alloy ingot D and the intermediate layer material D contain 0.05 to 1.50% by mass of Si and 0.05 to 2.00% by mass of Fe, and the Zn content is 6.00% by mass. 00% by mass or less, Mn content of 1.80% by mass or less, Cu content of 1.00% by mass or less, Cr content of 0.30% by mass or less, Ti content of 0.30% by mass or less, Zr The aluminum alloy has a content of 0.30% by mass or less, a V content of 0.30% by mass or less, and the balance being aluminum and unavoidable impurities.
Ｓｉは、Ｓｉを含有するアルミニウム合金廃材の配合許容量を増大させる。中間層材用アルミニウム合金鋳塊Ｄ及び中間層材ＤのＳｉの含有量は、０．０５～１．５０質量％、好ましくは０．０５～１．２０質量％である。Ｓｉ含有量が、０．０５質量％未満では、高純度アルミニウム地金を使用しなければならずコスト高となり、また、１．５０質量％を超えると中間層材の融点が低下して溶融してしまい、また、中間層材の電位を貴にするため、犠牲陽極効果を阻害して耐食性を低下させる場合がある。 Si increases the mixing tolerance of aluminum alloy waste containing Si. The content of Si in the intermediate layer material aluminum alloy ingot D and the intermediate layer material D is 0.05 to 1.50% by mass, preferably 0.05 to 1.20% by mass. If the Si content is less than 0.05% by mass, high-purity aluminum ingots must be used, resulting in high costs. In addition, since the potential of the intermediate layer material is made noble, the sacrificial anode effect may be inhibited and the corrosion resistance may be lowered.
Ｆｅは、Ｓｉ、ＭｎとともにＡｌ－Ｆｅ－Ｍｎ－Ｓｉ系の化合物を形成し、分散強化により強度を向上させる。中間層材用アルミニウム合金鋳塊Ｄ及び中間層材ＤのＦｅの含有量は、０．０５～２．００質量％、好ましくは０．０５～１．５０質量％である。Ｆｅ含有量が、０．０５質量％未満では、高純度アルミニウム地金を使用しなければならずコスト高となり、また、２．００質量％を超えると鋳造時に巨大金属間化合物が形成され易くなり、塑性加工性を低下させる。 Fe forms an Al--Fe--Mn--Si compound together with Si and Mn, and improves strength by dispersion strengthening. The content of Fe in the intermediate layer material aluminum alloy ingot D and the intermediate layer material D is 0.05 to 2.00% by mass, preferably 0.05 to 1.50% by mass. If the Fe content is less than 0.05% by mass, high-purity aluminum ingots must be used, resulting in high costs. On the other hand, if it exceeds 2.00% by mass, a large intermetallic compound is likely to be formed during casting. , lowers the plastic workability.
中間層材用アルミニウム合金鋳塊Ｄ及び中間層材Ｄは、Ｚｎを含有してもよい。Ｚｎは、電位を卑にすることができ、また、Ｚｎの含有は、Ｚｎを含有するアルミニウム合金廃材の配合許容量を増大させる。中間層材用アルミニウム合金鋳塊Ｄ及び中間層材ＤのＺｎの含有量は、６．００質量％以下（０．００質量％を含む）、好ましくは０．１０～５．００質量％である。Ｚｎ含有量が６．００質量％を超えると腐食速度が速くなり早期に中間層材が消失し、耐食性が低下する場合がある。 The intermediate layer material aluminum alloy ingot D and the intermediate layer material D may contain Zn. Zn can make the potential base, and the inclusion of Zn increases the permissible blending amount of Zn-containing aluminum alloy scraps. The content of Zn in the intermediate layer material aluminum alloy ingot D and the intermediate layer material D is 6.00% by mass or less (including 0.00% by mass), preferably 0.10 to 5.00% by mass. . If the Zn content exceeds 6.00% by mass, the corrosion rate increases and the intermediate layer material disappears early, which may reduce the corrosion resistance.
中間層材用アルミニウム合金鋳塊Ｄ及び中間層材Ｄは、Ｍｎを含有してもよい。Ｍｎの含有は、Ｍｎを含有するアルミニウム合金廃材の配合許容量を増大させる。中間層材用アルミニウム合金鋳塊Ｄ及び中間層材ＤのＭｎの含有量は、１．８０質量％以下（０．００質量％を含む）、好ましくは０．１０～１．５０質量％である。Ｍｎ含有量が１．８０質量％を超えると粗大な化合物が生成して冷間加工で割れが発生する可能性があり、製造の難易度が上がる。 The intermediate layer material aluminum alloy ingot D and the intermediate layer material D may contain Mn. The inclusion of Mn increases the permissible blending amount of aluminum alloy scraps containing Mn. The content of Mn in the intermediate layer material aluminum alloy ingot D and the intermediate layer material D is 1.80% by mass or less (including 0.00% by mass), preferably 0.10 to 1.50% by mass. . If the Mn content exceeds 1.80% by mass, coarse compounds may form and cracks may occur during cold working, increasing the difficulty of production.
中間層材用アルミニウム合金鋳塊Ｄ及び中間層材Ｄは、Ｃｕを含有してもよい。Ｃｕの含有は、Ｃｕを含有するアルミニウム合金廃材の配合許容量を増大させる。中間層材用アルミニウム合金鋳塊Ｄ及び中間層材ＤのＣｕの含有量は、１．００質量％以下（０．００質量％を含む）、好ましくは０．１０～０．９０質量％である。Ｃｕ含有量が１．００質量％を超えると鋳造時に割れが生じ易く、製造の難易度が上がり、また、中間層材の孔食電位が貴化してしまい、犠牲防食の効果を低下させる場合がある。 The intermediate layer material aluminum alloy ingot D and the intermediate layer material D may contain Cu. The inclusion of Cu increases the permissible blending amount of Cu-containing aluminum alloy scraps. The content of Cu in the intermediate layer material aluminum alloy ingot D and the intermediate layer material D is 1.00% by mass or less (including 0.00% by mass), preferably 0.10 to 0.90% by mass. . If the Cu content exceeds 1.00% by mass, cracks are likely to occur during casting, increasing the difficulty of manufacturing, and the pitting potential of the intermediate layer material becomes noble, which may reduce the effect of sacrificial corrosion protection. be.
中間層材用アルミニウム合金鋳塊Ｄ及び中間層材Ｄは、Ｔｉを含有してもよい。Ｔｉは、固溶強化により強度を向上させる。中間層材用アルミニウム合金鋳塊Ｄ及び中間層材ＤのＴｉ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｔｉ含有量が、０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The intermediate layer material aluminum alloy ingot D and the intermediate layer material D may contain Ti. Ti improves strength by solid solution strengthening. The Ti content of the intermediate layer material aluminum alloy ingot D and the intermediate layer material D is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. If the Ti content exceeds 0.30% by mass, a large intermetallic compound is likely to be formed, which may reduce plastic workability.
中間層材用アルミニウム合金鋳塊Ｄ及び中間層材Ｄは、Ｚｒを含有してもよい。Ｚｒは、固溶強化により強度を向上させ、また、Ａｌ－Ｚｒ系の金属間化合物が析出してろう付後の結晶粒粗大化に作用する。中間層材用アルミニウム合金鋳塊Ｄ及び中間層材ＤのＺｒ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｚｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The intermediate layer material aluminum alloy ingot D and the intermediate layer material D may contain Zr. Zr improves the strength by solid-solution strengthening, and precipitates an Al--Zr intermetallic compound to act on grain coarsening after brazing. The Zr content of the intermediate layer material aluminum alloy ingot D and the intermediate layer material D is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. When the Zr content exceeds 0.30% by mass, a large intermetallic compound is likely to be formed, which may reduce plastic workability.
中間層材用アルミニウム合金鋳塊Ｄ及び中間層材Ｄは、Ｃｒを含有してもよい。Ｃｒは、固溶強化により強度を向上させ、また、Ａｌ－Ｃｒ系の金属間化合物が析出してろう付後の結晶粒粗大化に作用する。中間層材用アルミニウム合金鋳塊Ｄ及び中間層材ＤのＣｒ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｃｒ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The intermediate layer material aluminum alloy ingot D and the intermediate layer material D may contain Cr. Cr improves the strength by solid-solution strengthening, and precipitates an Al—Cr-based intermetallic compound to act to coarsen grains after brazing. The Cr content of the intermediate layer material aluminum alloy ingot D and the intermediate layer material D is 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. When the Cr content exceeds 0.30% by mass, it tends to form a large intermetallic compound, which may reduce the plastic workability.
中間層材用アルミニウム合金鋳塊Ｄ及び中間層材Ｄは、Ｖを含有してもよい。Ｖは、固溶強化により強度を向上させる。中間層材用アルミニウム合金鋳塊Ｄ及び中間層材ＤのＶ含有量は、０．３０質量％以下（０．００質量％を含む）、好ましくは０．０５～０．２０質量％である。Ｖ含有量が０．３０質量％を超えると巨大金属間化合物を形成し易くなり、塑性加工性を低下させる場合がある。 The intermediate layer material aluminum alloy ingot D and the intermediate layer material D may contain V. V improves strength by solid solution strengthening. The aluminum alloy ingot D for the intermediate layer material and the intermediate layer material D have a V content of 0.30% by mass or less (including 0.00% by mass), preferably 0.05 to 0.20% by mass. If the V content exceeds 0.30% by mass, it tends to form a large intermetallic compound, which may reduce the plastic workability.
本発明の第二の形態のアルミニウム合金材の製造方法では、ろう材用アルミニウム合金鋳塊Ｂ等のろう材用のアルミニウム合金鋳塊、犠牲陽極材用アルミニウム合金鋳塊Ｃ等の犠牲陽極材用のアルミニウム合金鋳塊、又は中間層材用アルミニウム合金鋳塊Ｄ等の中間層材用のアルミニウム合金鋳塊の調製において、上記アルミニウム合金鋳塊Ａの組成に、更に化学成分を加えることにより、成分調節が可能となるのであれば、各アルミニウム合金鋳塊の鋳造原料として、アルミニウム合金廃材を、１０．０質量％以上、好ましくは１５．０～４５．０質量％含有する鋳造原料を用いて、各アルミニウム合金鋳塊を製造してもよい。 In the method for producing an aluminum alloy material according to the second embodiment of the present invention, an aluminum alloy ingot for brazing material such as aluminum alloy ingot B for brazing material, and an aluminum alloy ingot for sacrificial anode material such as aluminum alloy ingot C for sacrificial anode material are used. or an aluminum alloy ingot for an intermediate layer material such as an aluminum alloy ingot D for an intermediate layer material, by adding a chemical component to the composition of the aluminum alloy ingot A, If it is possible to adjust, as a casting raw material for each aluminum alloy ingot, using a casting raw material containing 10.0% by mass or more, preferably 15.0 to 45.0% by mass, of aluminum alloy waste material, Each aluminum alloy ingot may be produced.
本発明のアルミニウム合金材の製造方法を行い得られるアルミニウム合金材及び本発明のアルミニウム合金材の強度や耐食性に関する性能は、全てろう付後のものである。なお、ろう付は、通常、６００℃程度まで加熱しその後に空冷することにより行なわれるものであって、加熱の方法、加熱速度や冷却速度、加熱や冷却の保持時間などについては特に限定するものではない。 The aluminum alloy material obtained by the method for producing the aluminum alloy material of the present invention and the aluminum alloy material of the present invention have all performances related to strength and corrosion resistance after brazing. Brazing is usually performed by heating to about 600° C. and then air cooling, and the heating method, heating rate, cooling rate, heating and cooling holding time, etc. are particularly limited. isn't it.
本発明のアルミニウム合金材の製造方法では、本発明のアルミニウム合金材の製造方法を行い得られるアルミニウム合金材のＳｉ、Ｃｕ及びＺｎの含有量を調節することにより、アルミニウム合金廃材を、鋳造原料に１０．０質量％、好ましくは１０．０～５０．０質量％配合させても、ろう付性及びろう付後の耐食性に優れたアルミニウム合金材が得られるので、アルミニウム新地金の使用に由来するＣＯ２排出量を削減することができる。更に詳細に説明すると、本発明のアルミニウム合金材の製造方法では、本発明のアルミニウム合金材の製造方法を行い得られるアルミニウム合金材のＳｉ含有量を０．５０～１．２０質量％、好ましくは０．５０～１．００質量％、より好ましくは０．６５～１．００質量％と多くし、且つ、Ｚｎ含有量を０．１１～０．６０質量％、好ましくは０．２０～０．６０質量％と多くした上で、Ｃｕ含有量を０．１２～１．００質量％、好ましくは０．２０～０．９０質量％と規定することにより、ろう付後のアルミニウム合金材の耐食性を制御し、得られるアルミニウム合金材の優れたろう付性及びろう付後の耐食性を維持しつつ、鋳造原料への１０．０質量％、好ましくは１０．０～５０．０質量％のアルミニウム合金廃材の配合を可能としている。 In the method for producing an aluminum alloy material of the present invention, by adjusting the contents of Si, Cu and Zn in the aluminum alloy material obtained by the method for producing an aluminum alloy material of the present invention, the aluminum alloy waste material is used as a casting raw material. 10.0% by mass, preferably 10.0 to 50.0% by mass, an aluminum alloy material with excellent brazeability and corrosion resistance after brazing can be obtained. CO2 emissions can be reduced. More specifically, in the method for producing an aluminum alloy material of the present invention, the Si content of the aluminum alloy material obtained by performing the method for producing an aluminum alloy material of the present invention is 0.50 to 1.20% by mass, preferably 0.50 to 1.00% by mass, more preferably 0.65 to 1.00% by mass, and a Zn content of 0.11 to 0.60% by mass, preferably 0.20 to 0.20% by mass. By increasing the Cu content to 60% by mass and defining the Cu content to be 0.12 to 1.00% by mass, preferably 0.20 to 0.90% by mass, the corrosion resistance of the aluminum alloy material after brazing is improved. 10.0% by mass, preferably 10.0 to 50.0% by mass of aluminum alloy waste to the casting raw material while maintaining excellent brazeability and corrosion resistance after brazing of the aluminum alloy material obtained by controlling Allows compounding.
以下に、実施例を示して、本発明を具体的に説明するが、本発明は、以下に示す実施例に限定されるものではない。 EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to the examples shown below.
（実施例及び比較例）
表１に示す合金組成を有する心材合金、表２に示す合金組成を有するろう材合金、表３に示す合金組成を有する犠牲陽極材合金をそれぞれＤＣ鋳造により鋳造し、均質化処理を施し、各々両面を面削して仕上げた。ろう材合金及び犠牲陽極材合金を加熱、熱間圧延により所望の板厚とし、心材合金と組み合わせ、再度加熱、熱間圧延によりクラッド板材と成した。その後、Ｈ１４調質の場合は冷間圧延、中間焼鈍、冷間圧延を経て、Ｏ調質の場合は冷間圧延、最終焼鈍を経て、所定の最終板厚の材料を得た。各層の合金、クラッド率、調質、板厚の組み合わせを表４に示す。
(Examples and Comparative Examples)
A core alloy having an alloy composition shown in Table 1, a brazing alloy having an alloy composition shown in Table 2, and a sacrificial anode alloy having an alloy composition shown in Table 3 were each cast by DC casting, subjected to homogenization treatment, and each Finished by chamfering on both sides. The brazing alloy and the sacrificial anode material alloy were heated and hot-rolled to a desired plate thickness, combined with the core alloy, heated again, and hot-rolled to form a clad plate. After that, in the case of H14 temper, cold rolling, intermediate annealing, and cold rolling were performed, and in the case of O temper, cold rolling and final annealing were performed to obtain a material having a predetermined final thickness. Table 4 shows the combination of alloy, cladding ratio, thermal refining, and plate thickness for each layer.
得られた材料を、６００℃３分間のろう付相当の加熱処理に供して試験材とした。引張試験においては、引張速度１０ｍｍ／分、ゲージ長５０ｍｍの条件で、ＪＩＳ Ｚ２２４１に従って引張試験に供した。得られた応力－ひずみ曲線から引張強さ（ＴＳ）を読み取った。電位測定においては、心材の中央部を面削により露出した面および犠牲材表面を試験面とし、５％ＮａＣｌに酢酸を添加してｐＨ３に調整した液に浸漬し、参照電極をＡｇ／ＡｇＣｌとして自然電極電位を測定した。なお、実施例６及び比較例１１については、犠牲材表面電位としてろう材表面の電位を測定した。これらの評価結果及び心材電位から犠牲材表面電位を引いた電位差について表４に示す。心材電位が－６７０ｍＶ以上且つ電位差９０ｍＶ以上の場合を耐食性十分として○とし、心材電位が－６７０ｍＶ未満又は電位差９０ｍＶ未満の場合を耐食性不十分として×とし、その結果を表４に示す。 The obtained material was subjected to a heat treatment equivalent to brazing at 600° C. for 3 minutes to obtain a test material. The tensile test was performed according to JIS Z2241 under the conditions of a tensile speed of 10 mm/min and a gauge length of 50 mm. Tensile strength (TS) was read from the obtained stress-strain curve. In the potential measurement, the surface exposed by chamfering the central part of the core material and the surface of the sacrificial material were used as test surfaces, immersed in a solution adjusted to pH 3 by adding acetic acid to 5% NaCl, and Ag/AgCl was used as a reference electrode. Natural electrode potentials were measured. For Example 6 and Comparative Example 11, the surface potential of the brazing material was measured as the surface potential of the sacrificial material. Table 4 shows these evaluation results and the potential difference obtained by subtracting the surface potential of the sacrificial material from the potential of the core material. When the core potential was −670 mV or more and the potential difference was 90 mV or more, the corrosion resistance was evaluated as ◯.
また、通常、一般的なアルミニウム合金クラッド材の製造工場において生じるアルミニウム合金廃材及び自動車用熱交換器のスクラップの平均Ｚｎ含有量は１．１０質量％程度以上なので、その含有量に基づいて、鋳造原料として配合するアルミニウム合金廃材の配合可能割合が、１０．０質量％以上となる場合を〇、１０．０質量％未満の場合を×とし、その結果を表４に示す。 In addition, since the average Zn content of aluminum alloy waste materials and automobile heat exchanger scraps generated in general aluminum alloy clad material manufacturing plants is about 1.10% by mass or more, casting Table 4 shows the results.
実施例１～７は、本発明で規定する条件を満たしており、ろう付後の電位および廃材配合率ともに合格であった。
比較例８及び９は、心材のＣｕ成分が低すぎたため、心材の電位が卑になりすぎ、また犠牲材表面と心材との電位差が不十分であったため、心材の自己耐食性および犠牲材による犠牲防食作用が不十分であった。
比較例１０～１２は、心材のＺｎ成分が低過ぎたため、廃材配合率が不十分であった。
Examples 1 to 7 satisfied the conditions stipulated in the present invention, and both the potential after brazing and the content of waste material were acceptable.
In Comparative Examples 8 and 9, since the Cu content of the core material was too low, the potential of the core material became too base, and the potential difference between the surface of the sacrificial material and the core material was insufficient. The anticorrosive action was insufficient.
In Comparative Examples 10 to 12, the content of Zn in the core material was too low, resulting in an insufficient content of waste materials.
上記課題は、以下の本発明により解決される。
すなわち、本発明（１）は、０．５０～１．２０質量％のＳｉ、０．０５～１．００質量％のＦｅ、０．１２～１．００質量％のＣｕ、０．６０～１．８０質量％のＭｎ、及び０．１１～０．６０質量％のＺｎを含有し、Ｍｇ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金部Ａを有するアルミニウム合金材の製造方法であり、
０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなり、クラッド材が用いられている自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、０．５０～１．２０質量％のＳｉ、０．０５～１．００質量％のＦｅ、０．１２～１．００質量％のＣｕ、０．６０～１．８０質量％のＭｎ、及び０．１１～０．６０質量％のＺｎを含有し、Ｍｇ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなるアルミニウム合金鋳塊Ａを鋳造する鋳造工程を有し、
該アルミニウム合金部Ａの電位が－６７０（ｍＶ ｖｓ Ａｇ／ＡｇＣｌ）以上であること、
を特徴とするアルミニウム合金材の製造方法を提供するものである。
The above problems are solved by the present invention described below.
That is, the present invention (1) comprises 0.50 to 1.20 mass% Si, 0.05 to 1.00 mass% Fe, 0.12 to 1.00 mass% Cu, 0.60 to 1 .80% by mass of Mn and 0.11 to 0.60% by mass of Zn, with a Mg content of 0.50% by mass or less, a Cr content of 0.30% by mass or less, and a Ti content of 0 .30% by mass or less, Zr content of 0.30% by mass or less, V content of 0.30% by mass or less, and aluminum alloy part A comprising the balance aluminum and unavoidable impurities. and
0.50% by weight or more Si, 0.10% by weight or more Fe, 0.10% by weight or more Cu, 0.50% by weight or more Mn, 0.05% by weight or more Mg, and 0.10% by weight % or more of aluminum alloy containing one or more elements selected from the group consisting of Zn , and for automotive heat exchanger scrap and/or automotive heat exchangers using clad materials Using a casting raw material containing 10.0% by mass or more of scrap of the aluminum alloy clad material used, 0.50 to 1.20% by mass of Si, 0.05 to 1.00% by mass of Fe, 0.12 ~1.00% by mass of Cu, 0.60 to 1.80% by mass of Mn, and 0.11 to 0.60% by mass of Zn, Mg content of 0.50% by mass or less, Cr content is 0.30% by mass or less, the Ti content is 0.30% by mass or less, the Zr content is 0.30% by mass or less, the V content is 0.30% by mass or less, and the balance is aluminum and unavoidable impurities Having a casting step of casting an aluminum alloy ingot A made of an aluminum alloy consisting of
The potential of the aluminum alloy portion A is −670 (mV vs Ag/AgCl) or more ,
To provide a method for producing an aluminum alloy material characterized by
また、本発明（７）は、０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなり、クラッド材が用いられている自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、前記皮材用のアルミニウム合金鋳塊を鋳造する工程を有することを特徴とする（２）～（６）いずれかのアルミニウム合金材の製造方法を提供するものである。
また、本発明（８）は、０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなり、クラッド材が用いられている自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、前記ろう材用アルミニウム合金鋳塊Ｂを鋳造する工程を有することを特徴とする（３）～（６）いずれかのアルミニウム合金材の製造方法を提供するものである。
また、本発明（９）は、０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなり、クラッド材が用いられている自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、前記犠牲陽極材用アルミニウム合金鋳塊Ｃを鋳造する工程を有することを特徴とする（３）～（６）いずれかのアルミニウム合金材の製造方法を提供するものである。
また、本発明（１０）は、０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなり、クラッド材が用いられている自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、前記中間層材用のアルミニウム合金鋳塊を鋳造する工程を有することを特徴とする（４）～（６）いずれかのアルミニウム合金材の製造方法を提供するものである。
また、本発明（１１）は、０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなり、クラッド材が用いられている自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、前記中間層材用アルミニウム合金鋳塊Ｄを鋳造する工程を有することを特徴とする（６）のアルミニウム合金材の製造方法を提供するものである。
In addition, the present invention (7) includes 0.50% by mass or more of Si, 0.10% by mass or more of Fe, 0.10% by mass or more of Cu, 0.50% by mass or more of Mn, and 0.05% by mass. above Mg and 0.10% by mass or more of Zn, made of an aluminum alloy containing one or more elements selected from the group consisting of 0.10% by mass or more , scrap of automotive heat exchangers using a clad material and/or casting an aluminum alloy ingot for the skin material using a casting raw material containing 10.0% by mass or more of aluminum alloy clad material scrap used in heat exchangers for automobiles. The present invention provides a method for producing an aluminum alloy material according to any one of (2) to (6).
In addition, the present invention (8) includes 0.50% by mass or more of Si, 0.10% by mass or more of Fe, 0.10% by mass or more of Cu, 0.50% by mass or more of Mn, and 0.05% by mass. above Mg and 0.10% by mass or more of Zn, which is made of an aluminum alloy containing one or more elements selected from the group consisting of 0.10% by mass or more, and a scrap of an automotive heat exchanger using a clad material; and/or casting the aluminum alloy ingot B for brazing material using a casting raw material containing 10.0% by mass or more of aluminum alloy clad material scrap used in heat exchangers for automobiles. The present invention provides a method for producing an aluminum alloy material according to any one of (3) to (6).
In addition, the present invention (9) contains 0.50% by mass or more of Si, 0.10% by mass or more of Fe, 0.10% by mass or more of Cu, 0.50% by mass or more of Mn, and 0.05% by mass. above Mg and 0.10% by mass or more of Zn, which is made of an aluminum alloy containing one or more elements selected from the group consisting of 0.10% by mass or more, and a scrap of an automotive heat exchanger using a clad material; / or casting the aluminum alloy ingot C for sacrificial anode material using a casting raw material containing 10.0% by mass or more of scrap of aluminum alloy clad material used for heat exchangers for automobiles. The present invention provides a method for producing an aluminum alloy material according to any one of (3) to (6).
In addition, the present invention (10) includes 0.50% by mass or more of Si, 0.10% by mass or more of Fe, 0.10% by mass or more of Cu, 0.50% by mass or more of Mn, and 0.05% by mass. above Mg and 0.10% by mass or more of Zn, which is made of an aluminum alloy containing one or more elements selected from the group consisting of 0.10% by mass or more, and a scrap of an automotive heat exchanger using a clad material; /or casting the aluminum alloy ingot for the intermediate layer material using a casting raw material containing 10.0% by mass or more of aluminum alloy clad material scrap used in heat exchangers for automobiles. The present invention provides a method for producing an aluminum alloy material according to any one of (4) to (6).
In addition, the present invention (11) includes 0.50% by mass or more of Si, 0.10% by mass or more of Fe, 0.10% by mass or more of Cu, 0.50% by mass or more of Mn, and 0.05% by mass. above Mg, and aluminum alloy containing one or more elements selected from the group consisting of 0.10% by mass or more of Zn, scrap of automotive heat exchangers using clad materials and / or casting the aluminum alloy ingot D for the intermediate layer material using a casting raw material containing 10.0% by mass or more of aluminum alloy clad material scrap used in heat exchangers for automobiles. The present invention provides a method of manufacturing an aluminum alloy material of (6).
上記課題は、以下の本発明により解決される。
すなわち、本発明（１）は、０．５０～１．２０質量％のＳｉ、０．０５～１．００質量％のＦｅ、０．１２～１．００質量％のＣｕ、０．６０～１．８０質量％のＭｎ、及び０．１１～０．６０質量％のＺｎを含有し、Ｍｇ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金部Ａを有するアルミニウム合金材の製造方法であり、
０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなり、クラッド材が用いられている自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、０．５０～１．２０質量％のＳｉ、０．０５～１．００質量％のＦｅ、０．１２～１．００質量％のＣｕ、０．６０～１．８０質量％のＭｎ、及び０．１１～０．６０質量％のＺｎを含有し、Ｍｇ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなるアルミニウム合金鋳塊Ａを鋳造する鋳造工程を有し、
５％ＮａＣｌに酢酸を添加してｐＨ３に調整した液に浸漬し、参照電極をＡｇ／ＡｇＣｌとして自然電極電位を測定したときの該アルミニウム合金部Ａの自然電極電位が－６７０（ｍＶ ｖｓ Ａｇ／ＡｇＣｌ）以上であること、
を特徴とするアルミニウム合金材の製造方法を提供するものである。
The above problems are solved by the present invention described below.
That is, the present invention (1) comprises 0.50 to 1.20 mass% Si, 0.05 to 1.00 mass% Fe, 0.12 to 1.00 mass% Cu, 0.60 to 1 .80% by mass of Mn and 0.11 to 0.60% by mass of Zn, with a Mg content of 0.50% by mass or less, a Cr content of 0.30% by mass or less, and a Ti content of 0 .30% by mass or less, Zr content of 0.30% by mass or less, V content of 0.30% by mass or less, and aluminum alloy part A comprising the balance aluminum and unavoidable impurities. and
0.50% by weight or more Si, 0.10% by weight or more Fe, 0.10% by weight or more Cu, 0.50% by weight or more Mn, 0.05% by weight or more Mg, and 0.10% by weight % or more of aluminum alloy containing one or more elements selected from the group consisting of Zn, and used for automotive heat exchanger scrap and / or automotive heat exchangers using clad materials Using a casting raw material containing 10.0% by mass or more of aluminum alloy clad material scrap, 0.50 to 1.20% by mass Si, 0.05 to 1.00% by mass Fe, 0.12 to 1.00% by mass of Cu, 0.60 to 1.80% by mass of Mn, and 0.11 to 0.60% by mass of Zn, Mg content of 0.50% by mass or less, Cr content is 0.30% by mass or less, Ti content is 0.30% by mass or less, Zr content is 0.30% by mass or less, V content is 0.30% by mass or less, and the balance is aluminum and inevitable impurities Having a casting step of casting an aluminum alloy ingot A made of an aluminum alloy consisting of
The natural electrode potential of the aluminum alloy portion A was -670 (mV vs. Ag/ AgCl) or more,
To provide a method for producing an aluminum alloy material characterized by
Claims (13)
０．５０質量％以上のＳｉ、０．１０質量％以上のＦｅ、０．１０質量％以上のＣｕ、０．５０質量％以上のＭｎ、０．０５質量％以上のＭｇ、及び０．１０質量％以上のＺｎからなる群より選択される１種又は２種以上の元素を含むアルミニウム合金からなる自動車用熱交換器のスクラップ及び／又は自動車用熱交換器に用いられるアルミニウム合金クラッド材のスクラップを１０．０質量％以上含有する鋳造原料を用いて、０．５０～１．２０質量％のＳｉ、０．０５～１．００質量％のＦｅ、０．１２～１．００質量％のＣｕ、０．６０～１．８０質量％のＭｎ、及び０．１１～０．６０質量％のＺｎを含有し、Ｍｇ含有量が０．５０質量％以下、Ｃｒ含有量が０．３０質量％以下、Ｔｉ含有量が０．３０質量％以下、Ｚｒ含有量が０．３０質量％以下、Ｖ含有量が０．３０質量％以下であり、残部アルミニウム及び不可避的不純物からなるアルミニウム合金からなるアルミニウム合金鋳塊Ａを鋳造する鋳造工程を有すること、
を特徴とするアルミニウム合金材の製造方法。 0.50-1.20 wt% Si, 0.05-1.00 wt% Fe, 0.12-1.00 wt% Cu, 0.60-1.80 wt% Mn, and 0 .11 to 0.60% by mass of Zn, Mg content of 0.50% by mass or less, Cr content of 0.30% by mass or less, Ti content of 0.30% by mass or less, Zr content is 0.30% by mass or less, the V content is 0.30% by mass or less, and the balance is aluminum and inevitable impurities.
0.50% by weight or more Si, 0.10% by weight or more Fe, 0.10% by weight or more Cu, 0.50% by weight or more Mn, 0.05% by weight or more Mg, and 0.10% by weight scrap of automotive heat exchangers made of aluminum alloys containing one or more elements selected from the group consisting of Zn in an amount of Zn and/or scraps of aluminum alloy clad materials used in automotive heat exchangers Using a casting raw material containing 10.0% by mass or more, 0.50 to 1.20% by mass Si, 0.05 to 1.00% by mass Fe, 0.12 to 1.00% by mass Cu, 0.60 to 1.80% by mass of Mn and 0.11 to 0.60% by mass of Zn, the Mg content is 0.50% by mass or less, the Cr content is 0.30% by mass or less, Aluminum alloy casting made of an aluminum alloy having a Ti content of 0.30% by mass or less, a Zr content of 0.30% by mass or less, and a V content of 0.30% by mass or less, and the balance being aluminum and unavoidable impurities Having a casting process for casting ingot A;
A method for producing an aluminum alloy material, characterized by:
心材用のアルミニウム合金鋳塊として、前記心材用アルミニウム合金鋳塊Ａを用い、ろう材用のアルミニウム合金鋳塊として、前記ろう材用アルミニウム合金鋳塊Ｂを用い、犠牲陽極材用のアルミニウム合金鋳塊として、前記犠牲陽極材用アルミニウム合金鋳塊Ｃを用い、中間層材用のアルミニウム合金鋳塊と組み合わせて、前記アルミニウム合金クラッド材を得ること、
を特徴とする請求項３記載のアルミニウム合金材の製造方法。 The aluminum alloy clad material is a four-layer aluminum alloy clad material in which brazing material/intermediate layer material/core material/brazing material or sacrificial anode material is laminated in this order,
The aluminum alloy ingot A for the core material is used as the aluminum alloy ingot for the core material, the aluminum alloy ingot B for the brazing material is used as the aluminum alloy ingot for the brazing material, and the aluminum alloy ingot for the sacrificial anode material is used. Using the aluminum alloy ingot C for the sacrificial anode material as a lump and combining it with the aluminum alloy ingot for the intermediate layer material to obtain the aluminum alloy clad material;
The method for producing an aluminum alloy material according to claim 3, characterized by:
心材用のアルミニウム合金鋳塊として、前記心材用アルミニウム合金鋳塊Ａを用い、ろう材用のアルミニウム合金鋳塊として、前記ろう材用アルミニウム合金鋳塊Ｂを用い、中間層材用のアルミニウム合金鋳塊と組み合わせて、前記アルミニウム合金クラッド材を得ること、
を特徴とする請求項３記載のアルミニウム合金材の製造方法。 The aluminum alloy clad material is a five-layer aluminum alloy clad material in which brazing material/intermediate layer material/core material/intermediate layer material/brazing material are laminated in this order,
The aluminum alloy ingot A for the core material is used as the aluminum alloy ingot for the core material, the aluminum alloy ingot B for the brazing material is used as the aluminum alloy ingot for the brazing material, and the aluminum alloy ingot for the intermediate layer material is used. combining with a lump to obtain the aluminum alloy clad material;
The method for producing an aluminum alloy material according to claim 3, characterized by:
該心材が前記アルミニウム合金部Ａであり、該ろう材が前記ろう材Ｂであり、該犠牲陽極材が前記犠牲陽極材Ｃであること、
を特徴とする請求項１０記載のアルミニウム合金材。 The aluminum alloy clad material is a four-layer aluminum alloy clad material in which brazing material/intermediate layer material/core material/brazing material or sacrificial anode material is laminated in this order,
The core material is the aluminum alloy portion A, the brazing material is the brazing material B, and the sacrificial anode material is the sacrificial anode material C;
The aluminum alloy material according to claim 10, characterized by:
該心材が前記アルミニウム合金部Ａであり、該ろう材が前記ろう材Ｂであること、
を特徴とする請求項１０記載のアルミニウム合金材。 The aluminum alloy clad material is a five-layer aluminum alloy clad material in which brazing material/intermediate layer material/core material/intermediate layer material/brazing material are laminated in this order,
The core material is the aluminum alloy portion A, and the brazing material is the brazing material B;
The aluminum alloy material according to claim 10, characterized by: