JP2023057249A - High-pressure pump - Google Patents
High-pressure pump Download PDFInfo
- Publication number
- JP2023057249A JP2023057249A JP2021166654A JP2021166654A JP2023057249A JP 2023057249 A JP2023057249 A JP 2023057249A JP 2021166654 A JP2021166654 A JP 2021166654A JP 2021166654 A JP2021166654 A JP 2021166654A JP 2023057249 A JP2023057249 A JP 2023057249A
- Authority
- JP
- Japan
- Prior art keywords
- resin layer
- pressure pump
- damping resin
- lifter
- damping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、燃料を加圧し吐出する高圧ポンプに関する。 The present invention relates to a high-pressure pump that pressurizes and discharges fuel.
従来、燃料を加圧し、加圧した燃料を内燃機関に供給する高圧ポンプが知られている。高圧ポンプは、シリンダと、プランジャとを備え、プランジャをシリンダの筒孔で往復移動させることにより、シリンダ及びプランジャで区画される加圧室を圧縮するときに燃料を加圧する。 Conventionally, a high-pressure pump is known that pressurizes fuel and supplies the pressurized fuel to an internal combustion engine. The high-pressure pump includes a cylinder and a plunger, and pressurizes fuel when compressing a pressurization chamber defined by the cylinder and the plunger by reciprocating the plunger in a bore of the cylinder.
高圧ポンプとして、例えば、特許文献１には、加圧室に吸入される燃料の量を調整するための吸入弁、及び吸入弁の開閉を制御するための電磁駆動部を備える高圧ポンプが記載されている。特許文献１に記載された高圧ポンプは、燃料室及び燃料室に連通する加圧室を有するハウジングと、往復移動可能に設けられ、加圧室内の燃料を加圧可能なプランジャと、開弁したとき燃料室と加圧室との間の燃料の流れを許容し、閉弁したとき燃料室と加圧室との間の燃料の流れを遮断可能な吸入弁と、一端がハウジングの内側に位置し、他端がハウジングの外側に位置し、一端が吸入弁に当接可能なよう又は接続するよう設けられたニードルと、ニードルの他端側に設けられニードルを駆動して吸入弁を開閉する電磁駆動部と、磁性材料により筒状に形成され、外径が電磁駆動部のヨークの外径より小さく、軸がニードルの軸に沿うようニードルの径方向外側に設けられ、ハウジングと電磁駆動部とを接続している筒部材と、を備えている。
As a high-pressure pump, for example,
このような高圧ポンプの構造では、電磁駆動部が、加圧室を有するハウジングから突出する筒部材の端部に設けられている。そして、電磁駆動部が、吸入弁を開閉するとき、電磁力を生じ、吸入弁に当接するニードルを軸方向に往復移動させる。また、プランジャが軸方向に往復移動し加圧室内の燃料を加圧する。よって、高圧ポンプの作動時、電磁駆動部が、筒部材の端部においてマスとなり、ハウジングに対し相対的に振動するおそれがある。そして、このような振動に起因して高圧ポンプから騒音が発生するおそれがある。このような問題に対処すべく、特許文献１に記載された高圧ポンプは、ハウジングと電磁駆動部との間において筒部材の径方向外側に設けられ、ハウジングに対する電磁駆動部の振動を抑制可能な制振部材をさらに備えている。
In such a high-pressure pump structure, the electromagnetic drive is provided at the end of a cylindrical member protruding from a housing having a pressure chamber. When the electromagnetic drive section opens and closes the intake valve, an electromagnetic force is generated to reciprocate the needle in contact with the intake valve in the axial direction. Also, the plunger reciprocates in the axial direction to pressurize the fuel in the pressurization chamber. Therefore, when the high-pressure pump is operated, the electromagnetic drive section becomes a mass at the end of the cylindrical member, and may vibrate relative to the housing. Such vibrations may cause noise to be generated from the high-pressure pump. In order to deal with such a problem, the high-pressure pump described in
しかしながら、特許文献１に記載された高圧ポンプでは、弾性体等から構成される制振部材を設けるためのスペースが必要であるため、制振部材を設ける部位が限定され、振動発生源や振動伝達経路における振動を抑制可能な箇所に制振部材を設けることが難しいことがある。また、場合によっては、制振部材を設けるためのスペースを確保するために高圧ポンプの既存の構造の設計を変更する必要が生じることがある。
However, the high-pressure pump described in
本発明は、このような点を鑑みてなされたものであり、その目的とするところは、振動の発生又は伝達を容易に抑制できる高圧ポンプを提供することにある。 SUMMARY OF THE INVENTION It is an object of the present invention to provide a high-pressure pump capable of easily suppressing the generation or transmission of vibration.
上記課題を解決すべく、本発明の高圧ポンプは、筒孔が設けられたシリンダと、上記シリンダの上記筒孔に往復摺動可能に嵌入されたプランジャと、駆動カムの回転に伴い往復移動し、上記プランジャを連動で往復移動させるリフタと、上記リフタを収容孔に収容し、上記リフタの往復移動をガイドするリフタガイドと、を備える高圧ポンプであって、上記高圧ポンプにおける振動発生源及び振動伝達経路の少なくとも一方に設けられた制振樹脂層をさらに備え、上記制振樹脂層は、耐熱性樹脂と、振動エネルギーを熱エネルギーに変換する制振フィラーとを含むことを特徴とする。 In order to solve the above problems, the high-pressure pump of the present invention provides a cylinder provided with a cylindrical hole, a plunger reciprocally slidably fitted in the cylindrical hole of the cylinder, and a plunger reciprocatingly moved in accordance with rotation of a drive cam. A high-pressure pump comprising: a lifter for interlocking and reciprocating the plunger; and a lifter guide for accommodating the lifter in an accommodation hole and for guiding the reciprocating movement of the lifter, wherein the source of vibration and the vibration in the high-pressure pump A damping resin layer is provided on at least one of the transmission paths, and the damping resin layer contains a heat-resistant resin and a damping filler that converts vibration energy into heat energy.
本発明の高圧ポンプによれば、振動の発生又は伝達を容易に抑制できる。 According to the high-pressure pump of the present invention, generation or transmission of vibration can be easily suppressed.
上記高圧ポンプにおいては、上記制振樹脂層として、上記リフタガイドの内周面及び上記リフタの外周面の少なくとも一方に設けられた制振樹脂層を備えてもよい。 In the high-pressure pump, the damping resin layer may include a damping resin layer provided on at least one of the inner peripheral surface of the lifter guide and the outer peripheral surface of the lifter.
上記高圧ポンプにおいては、上記制振樹脂層として、上記リフタガイドの内周面に設けられた制振樹脂層を備えてもよい。 In the high-pressure pump, a damping resin layer provided on the inner peripheral surface of the lifter guide may be provided as the damping resin layer.
上記高圧ポンプにおいては、上記シリンダの径外方向に位置するシリンダ保持部と、上記シリンダ保持部から上記径外方向へ突出するフランジ部とを有し、上記シリンダを支持する下ハウジングをさらに備え、上記制振樹脂層として、上記フランジ部における被取付け部材と対向する締結面及び上記締結面と反対側の座面の少なくとも一方に設けられた制振樹脂層を備えてもよい。 The high-pressure pump further includes a lower housing that has a cylinder holding portion positioned radially outwardly of the cylinder and a flange portion projecting radially outwardly from the cylinder holding portion and supports the cylinder, As the damping resin layer, a damping resin layer may be provided on at least one of a fastening surface of the flange portion facing the member to be attached and a seat surface opposite to the fastening surface.
上記高圧ポンプにおいては、上記制振樹脂層の厚さが、１０μｍ以上でもよい。 In the high-pressure pump, the damping resin layer may have a thickness of 10 μm or more.
本発明によれば、振動の発生又は伝達を容易に抑制できる。 According to the present invention, generation or transmission of vibration can be easily suppressed.
以下、本発明の高圧ポンプに係る実施形態について説明する。最初に、実施形態に係る高圧ポンプの概略について、第１及び第２実施形態に係る高圧ポンプを例示して説明する。 Embodiments of the high-pressure pump of the present invention will be described below. First, an overview of the high-pressure pump according to the embodiment will be described by exemplifying the high-pressure pumps according to the first and second embodiments.
（第１実施形態）
図１は、第１実施形態に係る高圧ポンプを概略的に示す断面図である。図２は、図１のＩＩ－ＩＩ線断面図であって一部の構成を省略して示す図である。図３は、図１のＩＩＩ－ＩＩＩ線断面図である。図４は、第１実施形態に係る高圧ポンプにおける下ハウジング材のフランジ部のエンジンヘッドへの取付け構造を概略的に示す断面図である。図５は、第１実施形態に係る高圧ポンプの燃料吐出リリーフ部の拡大断面図であって、図１の矢印ＩＶで示す箇所の拡大図である。図６は、第１実施形態に係る高圧ポンプの燃料吐出リリーフ部の拡大断面図であって、図３の矢印Ｖで示す箇所の拡大図である。以下の説明では、図１の上側を「上」、図１の下側を「下」として説明する。
(First embodiment)
FIG. 1 is a cross-sectional view schematically showing a high-pressure pump according to the first embodiment. FIG. 2 is a cross-sectional view taken along the line II-II of FIG. 1 with a part of the configuration omitted. FIG. 3 is a cross-sectional view taken along line III-III of FIG. FIG. 4 is a cross-sectional view schematically showing a mounting structure of the flange portion of the lower housing member to the engine head in the high-pressure pump according to the first embodiment. FIG. 5 is an enlarged cross-sectional view of the fuel discharge relief portion of the high-pressure pump according to the first embodiment, and is an enlarged view of the portion indicated by arrow IV in FIG. 6 is an enlarged cross-sectional view of the fuel discharge relief portion of the high pressure pump according to the first embodiment, and is an enlarged view of a portion indicated by an arrow V in FIG. 3. FIG. In the following description, the upper side of FIG. 1 is referred to as "upper", and the lower side of FIG. 1 is referred to as "lower".
図１に示すように、第１実施形態に係る高圧ポンプ１は、車両用燃料タンク（図示せず）から低圧ポンプにより供給される燃料を加圧し、加圧した燃料をインジェクタが接続する燃料レールに吐出する燃料ポンプである。第１実施形態に係る高圧ポンプ１は、車両のエンジン９のエンジンヘッド１８に形成された収容孔１８０に取付けられている。高圧ポンプ１は、本体部１０、燃料供給部３０、プランジャ部５０、燃料吸入部７０及び燃料吐出リリーフ部９０を備えている。さらに、高圧ポンプ１は、リフタ２０と、リフタガイド２２とをさらに備えている。なお、第１実施形態に係るリフタガイド２２は、エンジンヘッド（シリンダヘッド）１８に形成された収容孔１８０の内壁１８１である。
As shown in FIG. 1, a high-
ここで、本体部１０について説明する。
本体部１０は、下ハウジング１１、シリンダ１３、及び上ハウジング１５を備えている。
下ハウジング１１は、シリンダ１３の径外方向に位置する円筒状のシリンダ保持部１１１と、シリンダ保持部１１１の下部から当該径外方向へ突出する環状のフランジ部１１２と、フランジ部１１２からシリンダ保持部１１１とは反対側に突出する、シリンダ保持部１１１よりも大径の円筒状のエンジン嵌合部１１３と、を有している。フランジ部１１２は、シリンダ保持部１１１の径外方向かつエンジン嵌合部１１３の径内方向で厚み方向に貫通する単数または複数の燃料流通孔１１４を有している。
Here, the
The
The
図１～図４に示すように、下ハウジング１１のエンジン嵌合部１１３は、エンジンヘッド１８の収容孔１８０の内側に収容され、下ハウジング１１のフランジ部１１２は、エンジンヘッド１８の締結面１８ｓ上に載置されている。フランジ部１１２におけるエンジンヘッド１８と対向する締結面１１２ｒ及び締結面１１２ｒと反対側の座面１１２ｓには、第１制振樹脂層２４ａ及び第２制振樹脂層２４ｂがそれぞれ設けられている。第１制振樹脂層２４ａ及び第２制振樹脂層２４ｂは、耐熱性樹脂と、振動エネルギーを熱エネルギーに変換する制振フィラーとを含んでいる。下ハウジング１１は、フランジ部１１２のボルト挿通孔１１７及びエンジンヘッド１８のボルト挿通孔１８７に挿通されたボルト１０１によりエンジンヘッド１８に締結されている。エンジンヘッド１８の締結面１８ｓ及びフランジ部１１２の締結面１１２ｒの間（振動伝達経路）には第１制振樹脂層２４ａが配置されている。フランジ部１１２の座面１１２ｓ及びボルト１０１の頭部１０１ｈの間（振動伝達経路）には第２制振樹脂層２４ｂが配置されている。
As shown in FIGS. 1 to 4, the
下ハウジング１１は、例えば、鍛造やプレス等により予めシリンダ保持部１１１及びエンジン嵌合部１１３が円筒状に成形された素材に、シリンダ保持部１１１の内壁面並びにエンジン嵌合部１１３の内壁面及び外壁面を仕上げるための切削加工が施されて作られる。下ハウジング１１は、耐錆性の高い例えばステンレス等の材料からなる。
The
シリンダ１３は、下側が開口する筒孔１３０が設けられた有底筒状の形状を有し、シリンダ保持部１１１の内壁に圧入されている。シリンダ１３は、シリンダ保持部１１１の下側で径外方向へ突出し、軸方向でシリンダ保持部１１１に当接する環状突起１３５を形成する。シリンダ１３は、環状突起１３５がシリンダ保持部１１１に当接することで上方向への移動が規制される。
シリンダ１３は、プランジャ５１を摺動可能に支持する有底筒状の内壁１３１を有している。当該内壁１３１は、プランジャ５１の上端面と共に加圧室１４を区画形成する。加圧室１４が液密に封止されるとき、加圧室１４内の燃料は、シリンダ１３内を上昇するプランジャ５１により加圧される。
The
The
シリンダ１３は、加圧室１４から外壁面まで貫通する第１連通孔１４１、及び加圧室１４から外壁面まで第１連通孔１４１とは反対方向へ貫通する第２連通孔１４２を有している。第１連通孔１４１及び第２連通孔１４２は、プランジャ５１の軸に対し対称に配置されている。
シリンダ１３は、プランジャ５１の摺動による焼付や摩耗を抑えるため、例えば焼き入れ等の熱処理によって硬度が高められている。当該熱処理は、プランジャ５１が摺動するシリンダ１３の内壁部に部分的に施されてもよいし、シリンダ１３全体に施されてもよい。
The
The hardness of the
上ハウジング１５は、下ハウジング１１とは別体であって、図１及び図３に示すようにシリンダ１３の軸方向に直交する方向に長手状をなす直方体状に形成されている。上ハウジング１５の長手方向の中央には、シリンダ１３の軸方向に貫通する圧入孔１５１が形成されている。シリンダ１３は、上ハウジング１５の圧入孔１５１に例えば圧入されている。これにより、シリンダ１３及び上ハウジング１５は、加圧室１４で加圧された燃料がシリンダ１３の外壁と圧入孔１５１の内壁との間から漏れないように接合している。第１実施形態では、上ハウジング１５と下ハウジング１１とがシリンダ１３の軸方向で互いに当接しているが、必ずしも当接する必要はない。
The
上ハウジング１５は、第１連通孔１４１に対し加圧室１４とは反対側に上ハウジング１５の長手方向に貫通する段付状の第１吸入孔１６１と、第１吸入孔１６１の内壁から外壁まで貫通する複数の第２吸入孔１６２とを有している。これらの第１吸入孔１６１及び複数の第２吸入孔１６２は、第１連通孔１４１を経由して加圧室１４に連通する吸入通路を構成し、加圧室１４に吸入される燃料が流通可能である。
The
上ハウジング１５は、第２連通孔１４２に対し加圧室１４とは反対側に上ハウジング１５の長手方向に貫通する段付状の第１吐出孔１６３を有している。当該第１吐出孔１６３は、第２連通孔１４２を経由して加圧室１４に連通する吐出通路を構成し、加圧室１４で加圧された燃料を吐出可能である。
上ハウジング１５は、例えば、横断面が矩形の棒状の素材に、圧入孔１５１、第１吸入孔１６１、第２吸入孔１６２、及び第１吐出孔１６３を形成するための切削加工が施されてなる。上ハウジング１５は、吸入通路及び吐出通路を形成する役割を果たす限りにおいて肉厚が薄く構成されている。
The
The
次に、燃料供給部３０について説明する。
図１～図３に示すように、燃料供給部３０は、カバー３１、パルセーションダンパ３３、及び燃料インレット３５を備えている。
カバー３１は、シリンダ１３の底部及び上ハウジング１５を収容する。当該カバー３１は、下ハウジング１１のフランジ部１１２側に開口端を有する有底円筒状をなし、カバー底部３１１とカバー筒部３１２とから構成されている。カバー底部３１１は、カバー筒部３１２の上端部を塞いでいる。カバー筒部３１２は、カバー底部３１１側から軸方向に順に第１円筒部３２１、多辺筒部３２２、及び第２円筒部３２３を有している。
Next, the
As shown in FIGS. 1 to 3, the
The
第１円筒部３２１及び第２円筒部３２３は、図示しないが、軸方向に直交する断面が円形となるように形成されている。第１円筒部３２１の内径は、第２円筒部３２３の内径と比べて小さく形成されている。
多辺筒部３２２は、図示しないが、軸方向に直交する断面が八辺形状となるように形成されている。ここで「八辺形状」とは、八つの線分で囲まれた図形である。以下、当該「八辺形状」を含む多辺形状は、複数の線分で囲まれた図形のことを意味し、例えば角部が丸みを帯びている、又は角部が面取りされている等の形状も含むものとする。
Although not shown, the first
Although not shown, the multi-sided
多辺筒部３２２の外壁面は、図示しないが、互いに平行に且つ軸に対し対称に配置されている４対の平面からなる。多辺筒部３２２と第１円筒部３２１とを接続する曲部、及び多辺筒部３２２と第２円筒部３２３とを接続する曲部は、カバー３１の剛性を高めている。
The outer wall surface of the multi-sided
多辺筒部３２２は、上記４対の平面のうち上ハウジング１５の長手方向において相対向する一対の平面それぞれに開口する第１貫通孔３２５及び第２貫通孔３２６を有している。第１吸入孔１６１に対し加圧室１４とは反対側に内外に貫通する第１貫通孔３２５には、吸入弁ボディ７２がカバー３１の外側から挿入されている。第１吐出孔１６３に対し加圧室１４とは反対側に内外に貫通する第２貫通孔３２６には、燃料吐出リリーフハウジング９１がカバー３１の外側から挿入されている。
The multi-sided
多辺筒部３２２は、図３に示すように、第２貫通孔３２６が開口する平面に対し周方向の隣に位置する平面に開口する第３貫通孔３２７を有している。第３貫通孔３２７には、カバー３１内に燃料を供給する燃料インレット３５の基端部が嵌合している。
カバー３１は、耐錆性の高い例えばステンレス等の板材がプレス加工により有底筒状に成形された後、第１貫通孔３２５、第２貫通孔３２６及び第３貫通孔３２７が例えば切削加工により形成されてなる。カバー３１は、内部に燃料ギャラリ３２を形成する役割を果たす限りにおいて肉厚が薄く形成されている。
As shown in FIG. 3, the multi-sided
The
カバー３１は、そのカバー３１の開口端とフランジ部１１２との隙間、第１貫通孔３２５と吸入弁ボディ７２との隙間、第２貫通孔３２６と燃料吐出リリーフハウジング９１との隙間、及び第３貫通孔３２７と燃料インレット３５との隙間が液密に封止されるように、例えば溶接により各部材に接合されている。カバー３１内には、カバー３１の内壁、フランジ部１１２のカバー３１側の外壁、並びに上ハウジング１５及びシリンダ１３の外壁により区画される空間からなる燃料ギャラリ３２が形成されている。燃料ギャラリ３２は、第２吸入孔１６２と連通している。燃料インレット３５から燃料ギャラリ３２に流入する燃料は、第２吸入孔１６２等を経由して加圧室１４に供給される。
The
燃料ギャラリ３２には、パルセーションダンパ３３が収容されている。パルセーションダンパ３３は、２枚の円形皿状のダイアフラム３３１及び３３２の外縁部が接合されることにより形成されている。パルセーションダンパ３３は、外縁部が上支持体３４１と下支持体３４２とに挟まれるようにしてカバー３１の第１円筒部３２１の内壁に固定されている。第１円筒部３２１の内壁とそれに嵌合する上支持体３４１との間には、図示しないが、複数の燃料流通路が形成されている。パルセーションダンパ３３の上方の空間には、図示しないが、燃料流通路を経由して燃料が供給される。
パルセーションダンパ３３の内部には所定圧の気体が密封されている。パルセーションダンパ３３は、燃料ギャラリ３２内の燃料の圧力変化に応じて弾性変形することにより燃料ギャラリ３２内の燃料の圧力脈動を低減する。カバー３１は、パルセーションダンパ３３の収容部材として機能している。
A
A predetermined pressure of gas is sealed inside the
次にプランジャ部５０について説明する。
図１及び図２に示すように、プランジャ部５０は、プランジャ５１、オイルシールホルダ５２、スプリングシート５３、及びプランジャスプリング５４などを備えている。
プランジャ５１は、シリンダ１３の筒孔１３０に軸方向に往復摺動可能に嵌入され、シリンダ１３の内壁１３１により軸方向に摺動可能に支持されている。プランジャ５１は、大径部５１２と小径部５１３とを形成する。加圧室１４側に位置する大径部５１２は、シリンダ１３の内壁１３１を摺動する。大径部５１２に対し加圧室１４とは反対側に位置する小径部５１３は、オイルシールホルダ５２に挿入されている。
Next, the
As shown in FIGS. 1 and 2, the
The
オイルシールホルダ５２は、シリンダ１３の開口側の端部に設けられており、プランジャ５１の小径部５１３の径外側に位置する基部５２１と、エンジン嵌合部１１３の内壁に圧入される圧入部５２２とを有している。
基部５２１は、内部にリング状のシール５２３を有している。シール５２３は、径内側のテフロン（登録商標）リングと、径外側のＯリングとからなる。シール５２３によってプランジャ５１の小径部５１３の周囲の燃料油膜の厚さが調整され、エンジンへの燃料のリークが抑制される。また基部５２１は、先端部分にオイルシール５２５を有している。オイルシール５２５によってプランジャ５１の小径部５１３の周囲のオイル油膜の厚さが規制され、オイルのリークが抑制される。
The
The
圧入部５２２は、基部５２１の周囲に円筒状に張り出す部分であり、円筒部分は縦断面が「Ｕの字」状となっている。下ハウジング１１には、圧入部５２２に対応する凹部５２６が形成されている。オイルシールホルダ５２は、圧入部５２２が凹部５２６の内壁に圧接するように圧入される。
The press-
スプリングシート５３は、プランジャ５１の下端部に設けられている。プランジャスプリング５４は、スプリングシート５３に一端を係止され、他端をオイルシールホルダ５２の圧入部５２２の深部に係止されている。これにより、プランジャスプリング５４は、プランジャ５１の戻しばねとして機能し、プランジャ５１をリフタ（タペット）２０に当接させるよう付勢する。
A
高圧ポンプ１は、エンジン９のエンジンヘッド１８の収容孔１８０の内側に、下ハウジング１１のエンジン嵌合部１１３、並びにシリンダ１３、プランジャ部５０のプランジャ５１、オイルシールホルダ５２、スプリングシート５３、及びプランジャスプリング５４などが収容されるようにして、エンジン９に取り付けられている。ここで、エンジン嵌合部１１３と収容孔１８０の内壁１８１との間には、ゴム製環状のシール部材１１５が設けられている。これにより、エンジン嵌合部１１３と収容孔１８０の内壁１８１との間は液密又は気密に保たれている。
The high-
リフタ２０は、有底筒状の形状を有し、エンジンヘッド１８の収容孔１８０に収容されている。リフタ２０は収容孔１８０の内側で軸方向に往復移動可能であり、収容孔１８０の内壁（リフタガイド）１８１（２２）はリフタ２０の往復移動をガイドする。収容孔１８０の内壁面（リフタガイドの内周面、振動発生源）１８１ｓには、第３制振樹脂層２４ｃが設けられている。第３制振樹脂層２４ｃは、耐熱性樹脂と、振動エネルギーを熱エネルギーに変換する制振フィラーとを含んでいる。
The
プランジャ５１の下端、すなわちプランジャ５１の小径部５１３の大径部５１２とは反対側の端がリフタ２０の底部に当接している。リフタ２０のプランジャ５１とは反対側にはローラ３及びカム軸５の駆動カム７が位置している。ローラ３は回転自在にリフタ２０を支持している。駆動カム７は、エンジン９の駆動軸に連動して回転するカム軸５と一緒に回転する。駆動カム７の回転に伴い、ローラ３が転動しながらリフタ２０の軸方向に往復移動することで、リフタ２０が軸方向に往復移動する。これにより、プランジャ５１をプランジャスプリング５４で付勢しながらリフタ２０により押圧することによって、プランジャ５１が連動してシリンダ１３の筒孔１３０で往復移動する。このとき、プランジャ５１の大径部５１２の移動によって加圧室１４の容積が周期的に変化する。なお、駆動カム７は、４つのカム山を有している。そのため、駆動カム７が１回転すると、プランジャ５１は、シリンダ１３の筒孔１３０において４回往復移動する。
The lower end of the
次に、燃料吸入部７０について説明する。
図１及び図３に示すように、燃料吸入部７０は、吸入通路を開閉可能であり、吸入弁部７１及び電磁駆動部８１を備えている。
吸入弁部７１は、吸入弁ボディ７２、シートボディ７３、吸入弁部材７４、及び第１スプリングホルダ７５などから構成されている。
円筒状の吸入弁ボディ７２は、第１吸入孔１６１に形成されたねじ穴に螺合することで上ハウジング１５に接合している。吸入弁ボディ７２の内部には、吸入室７１１が形成されている。吸入室７１１は、第２吸入孔１６２を経由して燃料ギャラリ３２と連通している。吸入室７１１には、略円筒状のシートボディ７３が設けられている。シートボディ７３の加圧室１４側には、吸入弁部材７４が当接可能な弁座７３１が形成されている。
Next, the
As shown in FIGS. 1 and 3 , the
The
The cylindrical
吸入弁部材７４は、シートボディ７３の内側で弁座７３１に当接及び離間可能に設けられている。吸入弁部材７４は、弁座７３１から離座することで吸入室７１１と加圧室１４とを連通させ、弁座７３１に着座することで吸入室７１１と加圧室１４とを遮断する。
第１スプリングホルダ７５は、吸入弁部材７４に対し加圧室１４側に設けられ、内側に、吸入弁部材７４を閉弁方向（図１の左方向）へ付勢する第１スプリング７６を収容している。
The
The
電磁駆動部８１は、固定コア８３、可動コア８４及びニードル８６などから構成されている。
円筒状の可動コア８４は、吸入弁ボディ７２内で軸方向に移動可能に設けられ、吸入弁部材７４と同軸上に配置されるニードル８６の一端部に固定されている。ニードル８６は、第２スプリングホルダ８５２により軸方向に移動可能に支持され、吸入弁部材７４に当接可能に設けられている。
第２スプリングホルダ８５２の内側には、ニードル８６を吸入弁部材７４側に付勢する第２スプリング８５１が設けられている。第２スプリング８５１は、第１スプリング７６が吸入弁部材７４を閉弁方向に付勢する力よりも強い力でニードル８６を開弁方向へ付勢する。
The
A cylindrical
A
固定コア８３は、可動コア８４に対し吸入弁部材７４とは反対側に設けられている。コイル８７は、固定コア８３の周りに設けられている。コイル８７に通電すると固定コア８３に磁力が発生する。磁力を帯びた固定コア８３は、第２スプリング８５１の付勢力に抗して可動コア８４を吸引する。ニードル８６は、固定コア８３に吸引される可動コア８４と共に吸入弁部材７４とは反対側に移動する。これにより、吸入弁部材７４が着座し、吸入弁部７１が閉弁する。
固定コア８３の磁力は、コイル８７への通電を止めると失われる。ニードル８６は、固定コア８３の磁気的吸引力が無くなると、第２スプリング８８の付勢力により固定コア８３とは反対側に移動する。これにより、吸入弁部材７４が離座し、吸入弁部７１が開弁する。
The fixed
The magnetic force of the fixed
次に、燃料吐出リリーフ部９０について説明する。
図１、図３、図５、及び図６に示すように、燃料吐出リリーフ部９０は、燃料吐出リリーフハウジング９１、吐出弁ボディ９２、吐出弁部材９４、及びリリーフ弁部材９６などを備えている。
燃料吐出リリーフハウジング９１は、円筒状に形成され、上ハウジング１５の第１吐出孔１６３に形成されたねじ穴に螺合することで上ハウジング１５に接合している。燃料吐出リリーフハウジング９１の内部には、吐出弁ボディ９２、吐出弁部材９４及びリリーフ弁部材９６などが収容されている。
Next, the fuel
As shown in FIGS. 1, 3, 5, and 6, the fuel
The fuel
吐出弁ボディ９２は、有底筒状の形状を有し、燃料吐出リリーフハウジング９１内に設けられ、加圧室１４側に開口している。吐出弁ボディ９２の底壁には、吐出通路９５と、その吐出通路９５に非連通のリリーフ通路９７とが形成されている。吐出通路９５は、吐出弁ボディ９２の底壁の加圧室１４側の壁面のうち径外側に開口し、また吐出弁ボディ９２の底壁の加圧室１４とは反対側の壁面のうち中央に開口している。リリーフ通路９７は、吐出弁ボディ９２の底壁の加圧室１４側の壁面のうち中央に開口するとともに、吐出弁ボディ９２の底壁の加圧室１４とは反対側の壁面のうち径外側に開口している。
The
吐出弁部材９４は、燃料吐出リリーフハウジング９１内において吐出弁ボディ９２の底壁の加圧室１４とは反対側に隣接して設けられている。吐出弁部材９４に対し加圧室１４とは反対側には吐出弁スプリングホルダ９４５が設けられている。吐出弁部材９４は、吐出弁スプリングホルダ９４５との間に介在されている吐出弁スプリング９４３により吐出弁ボディ９２の底壁の弁座９３に向けて付勢されており、吐出通路９５を開閉可能である。
The
リリーフ弁部材９６は、燃料吐出リリーフハウジング９１内において吐出弁ボディ９２の底部の加圧室１４側に隣接して設けられている。リリーフ弁部材９６は、加圧室１４側のリリーフ弁スプリングホルダ９６５との間に設けられているリリーフ弁スプリング９６３により吐出弁ボディ９２の底部に向けて付勢されており、リリーフ通路９７を開閉可能である。
The
次に、高圧ポンプ１の作動について説明する。
（Ｉ）吸入行程
カム軸５の回転によりプランジャ５１が上死点から下死点に向かって下降するとき、加圧室１４の容積が増加するとともに加圧室１４内の燃料の圧力が減少する。このとき、吐出通路９５は吐出弁部材９４により遮断される。また、コイル８７への通電が止められることにより、ニードル８６は第２スプリング８５の付勢力を受けて吸入弁部材７４側に移動する。これにより、ニードル８６が吸入弁部材７４を押圧し、吸入弁部７１は開弁する。その結果、吸入室７１１から第１連通孔１４１を経由して加圧室１４に燃料が吸入される。
Next, operation of the high-
(I) Intake stroke When the
（ＩＩ）調量行程
カム軸５の回転によりプランジャ５１が下死点から上死点に向かって上昇するとき、加圧室１４の容積が減少する。その際、所定の時期まではコイル８７への通電を止め、吸入弁部７１を開弁させる。このため、吸入行程で加圧室１４に吸入された低圧燃料の一部が燃料供給側に戻される。
そして、プランジャ５１が上昇する途中の所定の時期にコイル８７に通電することで、固定コア８３と可動コア８４との間に磁気的吸引力が発生する。当該磁気的吸引力が第２スプリング８５１の付勢力から第１スプリング７６の付勢力を引いた合力より大きくなると、可動コア８４及びニードル８６が固定コア８３側に移動する。これにより、ニードル８６の吸入弁部材７４への押圧力が解除される。その結果、吸入弁部材７４がシートボディ７３の弁座７３１に着座し、吸入弁部７１は閉弁する。
(II) Metering stroke When the
By energizing the
（ＩＩＩ）加圧行程
吸入弁部７１の閉弁後、プランジャ５１の上昇と共に加圧室１４の容積が減少し、加圧室１４内の燃料の圧力が増加する。加圧室１４の燃圧により吐出弁部材９４に作用する力が、吐出弁スプリング９４３の付勢力と燃料吐出口９９側の燃圧により吐出弁部材９４に作用する力との合計よりも大きくなると、吐出弁部材９４は開弁する。これにより、加圧室１４で加圧された加圧燃料が、第２連通孔１４２、第１吐出孔１６３等を経由して燃料吐出口９９から吐出する。
高圧ポンプ１は、吸入行程、調量行程及び加圧行程を繰り返し、吸入した燃料を調量し加圧して燃料吐出口９９から吐出する。
(III) Pressurization stroke After the
The high-
第１実施形態に係る高圧ポンプ１では、エンジンヘッド１８の収容孔１８０の内壁面（リフタガイドの内周面、振動発生源）１８１ｓに第３制振樹脂層２４ｃが設けられている。このため、リフタ２０が収容孔１８０の内側で軸方向に往復移動し、収容孔１８０の内壁（リフタガイド）１８１（２２）がリフタ２０の往復移動をガイドする時において、リフタ２０の外周面２０ｓが収容孔１８０の内壁面１８１ｓに直に接触して摺動するのではなく、リフタ２０の外周面２０ｓが収容孔１８０の内壁面１８１ｓに設けられた第３制振樹脂層２４ｃに接触して摺動する。これにより、リフタ２０の外周面２０ｓが収容孔１８０の内壁面１８１ｓに直に接触して摺動することで振動が発生することを回避できる。また、例えば、カム軸５の回転に応じたプランジャ５１の往復移動等により発生する振動の伝達を第３制振樹脂層２４ｃにより抑制できる。これにより、例えば、これらの振動或いは振動による騒音がエンジンヘッド１８等を介して車両の外部や居室等の系外に放射されることを抑制できる。
In the high-
また、第１実施形態に係る高圧ポンプ１では、エンジンヘッド１８の締結面１８ｓ及びフランジ部１１２の締結面１１２ｒの間（振動伝達経路）に第１制振樹脂層２４ａが配置されている。このため、例えば、カム軸５の回転に応じたプランジャ５１の往復移動等により発生する振動が、フランジ部１１２及びエンジンヘッド１８の間を伝達することを抑制できる。これにより、例えば、これらの振動或いは振動による騒音がエンジンヘッド１８等を介して車両の外部や居室等の系外に騒音として放射されることを抑制できる。また、フランジ部１１２の座面１１２ｓ及びボルト１０１の頭部１０１ｈの間（振動伝達経路）に第２制振樹脂層２４ｂが配置されている。このため、例えば、これらの振動が、フランジ部１１２及びボルト１０１の間を伝達することを抑制できる。これにより、例えば、これらの振動或いは振動による騒音がエンジンヘッド１８等を介して車両の外部や居室等の系外に騒音として放射されることを抑制できる。
Further, in the high-
（第２実施形態）
第２実施形態に係る高圧ポンプについて、第１実施形態とは異なる点を説明する。
図７は、第２実施形態に係る高圧ポンプを概略的に示す断面図である。以下の説明では、図７の上側を「上」、図７の下側を「下」として説明する。
(Second embodiment)
Regarding the high-pressure pump according to the second embodiment, the points that are different from the first embodiment will be described.
FIG. 7 is a cross-sectional view schematically showing a high-pressure pump according to the second embodiment. In the following description, the upper side of FIG. 7 is referred to as "upper", and the lower side of FIG. 7 is referred to as "lower".
図７に示すように、第２実施形態に係る高圧ポンプ１では、リフタ２０の外周面（振動発生源）２０ｓに第４制振樹脂層２４ｄが設けられている。第４制振樹脂層２４ｄは、耐熱性樹脂と、振動エネルギーを熱エネルギーに変換する制振フィラーとを含んでいる。一方、第１実施形態とは異なり、エンジンヘッド１８の収容孔１８０の内壁面（リフタガイドの内周面）１８１ｓには制振樹脂層が設けられていない。第２実施形態に係る高圧ポンプ１のその他の構成は、第１実施形態と同様である。
As shown in FIG. 7, in the high-
第２実施形態に係る高圧ポンプ１では、第１実施形態とは異なり、リフタ２０がエンジンヘッド１８の収容孔１８０の内側で軸方向に往復移動し、収容孔１８０の内壁（リフタガイド）１８１（２２）がリフタ２０の往復移動をガイドする時において、リフタ２０の外周面２０ｓに設けられた第４制振樹脂層２４ｄが収容孔１８０の内壁面（リフタガイドの内周面）１８１ｓに接触して摺動する。これにより、リフタ２０の外周面２０ｓが収容孔１８０の内壁面１８１ｓに直に接触して摺動することで振動が発生することを回避できる。また、例えば、カム軸５の回転に応じたプランジャ５１の往復移動等により発生する振動の伝達を第４制振樹脂層２４ｄにより抑制できる。これにより、例えば、これらの振動或いは振動による騒音がエンジンヘッド１８等を介して車両の外部や居室等の系外に放射されることを抑制できる。
In the high-
（作用効果）
従って、実施形態に係る高圧ポンプによれば、第１及び第２実施形態のように、例えば、リフタガイドの内周面やリフタの外周面等のような振動発生源、及び振動伝達経路の少なくとも一方に制振樹脂層が設けられていることにより、振動の発生又は伝達を抑制できる。また、例えば、制振部材として、数十μｍ程度の厚みに形成できる薄く軽量な制振樹脂層を用いるため、制振部材を設ける部位が限定されず、制振部材を設けるスペースを確保するために高圧ポンプの既存の構造の設計を変更する必要が生じることが少ない。よって、振動の発生又は伝達を容易に抑制できる。このため、振動或いは振動による騒音がエンジンヘッド等の被取付け部材を介して車両の外部や居室等の系外に放射されることを容易に抑制できる。また、例えば、リフタガイドの内周面やリフタの外周面等のような振動発生源となり得る狭いスペースとなる部位にも制振部材を設けることができる。このため、振動発生源への対策が容易になる。
(Effect)
Therefore, according to the high-pressure pump according to the embodiment, as in the first and second embodiments, for example, at least the vibration generation source such as the inner peripheral surface of the lifter guide and the outer peripheral surface of the lifter, and the vibration transmission path By providing the damping resin layer on one side, the generation or transmission of vibration can be suppressed. In addition, for example, since a thin and lightweight vibration damping resin layer that can be formed with a thickness of about several tens of μm is used as the vibration damping member, there is no limitation on the portion where the vibration damping member is provided, and a space for mounting the vibration damping member can be secured. Therefore, it is less necessary to change the design of the existing structure of the high pressure pump. Therefore, generation or transmission of vibration can be easily suppressed. Therefore, it is possible to easily suppress the vibration or the noise caused by the vibration from being radiated to the outside of the vehicle, such as a room, through the attached member such as the engine head. Also, for example, damping members can be provided in narrow spaces that can be sources of vibration, such as the inner peripheral surface of the lifter guide and the outer peripheral surface of the lifter. Therefore, it becomes easy to take measures against the vibration source.
さらに、弾性体等から構成される従来の制振部材は、熱により劣化するおそれがあり、長期の使用に伴うクリープ等による性能低下のおそれもあるのに対して、実施形態に係る高圧ポンプによれば、制振部材として制振樹脂層を用いることによりこれらの問題を回避できる。また、実施形態に係る高圧ポンプによれば、制振樹脂層が、弾性体等から構成される従来の制振部材と比べ薄く軽量であることにより、例えば、燃費性能等のその他の性能の低下を抑制できる。 Furthermore, the conventional vibration damping member made of an elastic material or the like may deteriorate due to heat, and there is also a risk of deterioration in performance due to creep due to long-term use. According to the above, these problems can be avoided by using a damping resin layer as the damping member. Further, according to the high-pressure pump according to the embodiment, since the damping resin layer is thinner and lighter than the conventional damping member made of an elastic body, other performances such as fuel efficiency are lowered. can be suppressed.
続いて、実施形態に係る高圧ポンプの詳細について説明する。 Next, details of the high-pressure pump according to the embodiment will be described.
１．高圧ポンプ
高圧ポンプは、筒孔が設けられたシリンダと、上記シリンダの上記筒孔に往復摺動可能に嵌入されたプランジャと、駆動カムの回転に伴い往復移動し、上記プランジャを連動で往復移動させるリフタと、上記リフタを収容孔に収容し、上記リフタの往復移動をガイドするリフタガイドと、を備えるものである。
1. High-Pressure Pump A high-pressure pump reciprocates with a cylinder provided with a cylindrical hole, a plunger fitted in the cylindrical hole of the cylinder so as to be reciprocally slidable, and a driving cam, and reciprocates the plunger in conjunction with the rotation of the drive cam. and a lifter guide that accommodates the lifter in the accommodation hole and guides the reciprocating movement of the lifter.
高圧ポンプは、上記のようなものであれば特に限定されないが、第１及び第２実施形態に係る高圧ポンプのように、上記シリンダの径外方向に位置するシリンダ保持部と、上記シリンダ保持部から上記径外方向へ突出するフランジ部とを有し、上記シリンダを支持する下ハウジングをさらに備えるものでもよい。 The high-pressure pump is not particularly limited as long as it is as described above. However, like the high-pressure pumps according to the first and second embodiments, the cylinder holding portion located radially outward of the cylinder and the cylinder holding portion A lower housing may be further provided which has a flange portion protruding radially outward from the lower housing and supports the cylinder.
リフタガイドとしては、リフタの往復移動をガイドするものであれば特に限定されないが、例えば、第１及び第２実施形態に係るリフタガイドのようにエンジンヘッドに形成された収容孔の内壁でもよいが、例えば、エンジンヘッドとは別の部材であって、リフタの往復移動をガイドする筒状の内壁を有するものであって、エンジンヘッドの収容孔に収容されるものでもよい。 The lifter guide is not particularly limited as long as it guides the reciprocating movement of the lifter. For example, it may be the inner wall of the housing hole formed in the engine head like the lifter guides according to the first and second embodiments. For example, it may be a member separate from the engine head, having a cylindrical inner wall for guiding the reciprocating movement of the lifter, and accommodated in the accommodation hole of the engine head.
２．制振樹脂層
高圧ポンプは、上記高圧ポンプにおける振動発生源及び振動伝達経路の少なくとも一方に設けられた制振樹脂層をさらに備える。上記制振樹脂層は、耐熱性樹脂と、振動エネルギーを熱エネルギーに変換する制振フィラーとを含む。
2. Damping Resin Layer The high-pressure pump further includes a damping resin layer provided on at least one of the vibration source and the vibration transmission path in the high-pressure pump. The damping resin layer includes a heat-resistant resin and a damping filler that converts vibration energy into heat energy.
高圧ポンプは、上記のような制振樹脂層を備えるものあれば特に限定されないが、上記制振樹脂層として、第１実施形態に係る第３及び第４制振樹脂層のように上記リフタガイドの内周面及び上記リフタの外周面の少なくとも一方に設けられた制振樹脂層を備えるものが好ましい。リフタガイドの内周面及びリフタの外周面は、リフタの往復移動時において互いに直に接触して摺動することで振動を発生させる振動発生源であるため、これらの面の少なくとも一方に設けられた制振樹脂層を備えることにより、振動の発生自体を抑制できるからである。高圧ポンプとしては、中でも上記リフタガイドの内周面に設けられた制振樹脂層を備えるものが好ましい。リフタの往復移動時において、リフタの外周面は常に全体で摺動するのに対して、リフタガイドの内周面の摺動部位はリフタの移動に応じて変化するため、リフタの外周面に設けられた制振樹脂層を備えるものと比べて、制振樹脂層の摩耗が抑制される結果、制振樹脂層の性能が維持され易いからである。 The high-pressure pump is not particularly limited as long as it has a damping resin layer as described above. and a damping resin layer provided on at least one of the inner peripheral surface of the lifter and the outer peripheral surface of the lifter. Since the inner peripheral surface of the lifter guide and the outer peripheral surface of the lifter are vibration generating sources that generate vibration by sliding in direct contact with each other during the reciprocating movement of the lifter, the inner peripheral surface of the lifter guide and the outer peripheral surface of the lifter are provided on at least one of these surfaces. This is because the occurrence of vibration itself can be suppressed by providing the damping resin layer. Among the high-pressure pumps, those having a damping resin layer provided on the inner peripheral surface of the lifter guide are preferable. During reciprocation of the lifter, the entire outer peripheral surface of the lifter always slides, whereas the sliding portion of the inner peripheral surface of the lifter guide changes according to the movement of the lifter. This is because, as a result of suppressing wear of the damping resin layer, the performance of the damping resin layer is likely to be maintained, as compared with the case where the damping resin layer is provided with a thickened damping resin layer.
高圧ポンプは、上記制振樹脂層として、第１実施形態に係る第１及び第２制振樹脂層のように上記フランジ部における被取付け部材と対向する締結面及び上記締結面と反対側の座面の少なくとも一方に設けられた制振樹脂層を備えるものでもよい。ここで、「被取付け部材」とは、高圧ポンプを取り付ける部材のことを指し、例えば、車両などのエンジンのエンジンヘッド等である。 In the high-pressure pump, as the damping resin layer, a fastening surface facing the attached member in the flange portion and a seat on the side opposite to the fastening surface, like the first and second damping resin layers according to the first embodiment. A damping resin layer may be provided on at least one of the surfaces. Here, the term "member to be attached" refers to a member to which the high-pressure pump is attached, such as an engine head of an engine of a vehicle or the like.
制振樹脂層の厚さは、振動を抑制できれば特に限定されないが、例えば、１０μｍ以上が好ましく、中でも２０μｍ以上が好ましく、特に５０μｍ以上が好ましい。振動の伝達の遮断作用が十分に得られるようになるからである。制振樹脂層の厚さは、例えば、４００μｍ以下が好ましく、中でも２００μｍ以下が好ましく、特に１００μｍ以下が好ましい、中でも特に５０μｍ以下が好ましい。振動の遮断作用の向上が飽和するからであり、コーティングによる層の形成が容易になるからである。 The thickness of the vibration-damping resin layer is not particularly limited as long as it can suppress vibration, but is preferably 10 μm or more, more preferably 20 μm or more, and particularly preferably 50 μm or more. This is because a sufficient effect of blocking the transmission of vibration can be obtained. The thickness of the damping resin layer is, for example, preferably 400 μm or less, more preferably 200 μm or less, particularly preferably 100 μm or less, and particularly preferably 50 μm or less. This is because the improvement in the vibration isolation action is saturated, and the formation of a layer by coating is facilitated.
制振樹脂層に含まれる耐熱性樹脂は、特に限定されずに、１００℃以上の熱変形温度を有するものであれば特に限定されないが、１５０℃以上の熱変形温度を有するものが好ましい。耐熱性樹脂の例としては、特に限定されずに、ポリアミドイミド樹脂、ポリイミド樹脂、フェノール樹脂、エポキシ樹脂、ポリエーテルサルフォン樹脂、ポリフェニルサルファイド樹脂等を挙げることができる。被膜を形成する際の作業性と摩擦による発熱に対する耐熱性の観点からポリアミドイミド樹脂がさらに好ましい。これらの耐熱性樹脂は、１種のみを単独で使用してもよく、２種以上を併用してもよい。 The heat-resistant resin contained in the vibration-damping resin layer is not particularly limited as long as it has a heat distortion temperature of 100° C. or higher, but preferably has a heat distortion temperature of 150° C. or higher. Examples of heat-resistant resins include, but are not limited to, polyamideimide resins, polyimide resins, phenol resins, epoxy resins, polyethersulfone resins, polyphenylsulfide resins, and the like. A polyamideimide resin is more preferable from the viewpoint of workability in forming a film and heat resistance against heat generation due to friction. These heat-resistant resins may be used alone or in combination of two or more.
制振樹脂層に含まれる制振フィラーは、振動エネルギーを熱エネルギーに変換するものである。制振フィラーとしては、特に限定されないが、低弾性率で変形し易い材料と、内部でエネルギー散逸が起こり易い材料とに大別できる。低弾性率で変形し易い材料とは、より具体的には、固体であるが、顕著に弾性的な特性と粘性的な特性の両方を合わせ持った材料のことである。弾性的な特性と粘性的な特性は全ての材料が合わせ持つ特性であるが、低弾性率で変形し易い材料は、顕著にこれらの特性の両方を合わせ持っている。このため、低弾性率で変形し易い材料を制振樹脂層に含有させることにより、常温域での制振樹脂層自体のゴム弾性を増加できる。これにより、制振樹脂層により効果的に外部から入力される振動を吸収し熱エネルギーに変換することで、振動の伝達を効果的に遮断できると考えられる。一方、内部でエネルギー散逸が起こり易い材料は、振動を材料内に存在する空気層で乱反射させて熱エネルギーへ変換させることにより、振動を減衰させる効果を有している。このため、内部でエネルギー散逸が起こり易い材料を制振樹脂層に含有させると、制振樹脂層により振動の伝達を効果的に遮断できると考えられる。 The damping filler contained in the damping resin layer converts vibration energy into heat energy. Although the damping filler is not particularly limited, it can be broadly classified into a material that has a low elastic modulus and is easily deformed, and a material that is likely to dissipate energy inside. Low elastic modulus and easily deformable materials are more specifically materials that are solid but have both significant elastic and viscous properties. Elastic and viscous properties are common properties of all materials, but low modulus and easily deformable materials significantly combine both properties. Therefore, the rubber elasticity of the vibration-damping resin layer itself in the normal temperature range can be increased by including a material that has a low elastic modulus and is easily deformed in the vibration-damping resin layer. As a result, the damping resin layer effectively absorbs externally input vibrations and converts them into heat energy, so that transmission of vibrations can be effectively cut off. On the other hand, materials that tend to dissipate energy inside have the effect of attenuating vibrations by diffusely reflecting vibrations in the air layer present in the material and converting them into thermal energy. For this reason, it is considered that if the vibration-damping resin layer contains a material that easily dissipates energy inside, the vibration transmission can be effectively blocked by the vibration-damping resin layer.
低弾性率で変形し易い材料の例としては、熱可塑性エラストマー、ウレタン系化合物、ポリエチレン系化合物、エステル共重合体、ゴム系材料などが挙げられる。熱可塑性エラストマーは、一般的に、常温では、ゴムの特性を有し、高温では、熱可塑性プラスチックと同等の性能を有している。熱可塑性エラストマーの例としては、スチレン系熱可塑性エラストマー、オレフィン系熱可塑性エラストマー、塩化ビニル系熱可塑性エラストマー、ウレタン系熱可塑性エラストマー、エステル系熱可塑性エラストマー、アミド系熱可塑性エラストマー等が挙げられる。これらの例は、例えば、特開２０１６－１１３６１４号公報、特開２０１７－１９７７３３号公報等に挙げられている。ウレタン系化合物の例としては、ウレタン樹脂等が挙げられる。これらの例は、例えば、特開平８－１８３９４５号公報等に挙げられている。ポリエチレン系化合物の例としては、エチレンの単独重合体、エチレンとα－オレフィレン単量体との共重合体等が挙げられる。これらの例は、例えば、特表２００９－５３２５７０号公報等に挙げられている。エステル共重合体の例としては、アクリル酸エステル共重合体等が挙げられる。これらの例は、例えば、特許第３２０９４９９号公報等に挙げられている。ゴム系材料の例としては、ブチルゴム、フッ素ゴム等が挙げられる。これらの例は、例えば、特開２００９－２３６１７２号公報等に挙げられている。 Examples of easily deformable materials with a low elastic modulus include thermoplastic elastomers, urethane compounds, polyethylene compounds, ester copolymers, and rubber materials. Thermoplastic elastomers generally have the properties of rubber at room temperature and have performance equivalent to thermoplastics at elevated temperatures. Examples of thermoplastic elastomers include styrene-based thermoplastic elastomers, olefin-based thermoplastic elastomers, vinyl chloride-based thermoplastic elastomers, urethane-based thermoplastic elastomers, ester-based thermoplastic elastomers, amide-based thermoplastic elastomers, and the like. Examples of these are given in, for example, JP-A-2016-113614, JP-A-2017-197733, and the like. Examples of urethane-based compounds include urethane resins. Examples of these are given, for example, in Japanese Patent Application Laid-Open No. 8-183945. Examples of polyethylene compounds include homopolymers of ethylene and copolymers of ethylene and α-olefin monomers. Examples of these are listed, for example, in Japanese Patent Publication No. 2009-532570. Examples of ester copolymers include acrylic acid ester copolymers. Examples of these are given in Japanese Patent No. 3209499, for example. Examples of rubber-based materials include butyl rubber and fluororubber. Examples of these are given, for example, in Japanese Patent Application Laid-Open No. 2009-236172.
内部でエネルギー散逸が起こり易い材料の例としては、マイクロカプセル系材料、低密度材料などが挙げられる。マイクロカプセル系材料の例としては、熱可塑性高分子からなるシェルの内部に所定の温度域になると膨張する気化物質を内包する熱膨張性マイクロカプセル等が挙げられる。これらの例は、特開２０１３－１８８５５号公報等に挙げられている。低密度材料の例としては、例えば、材料内部に空気層を含有する材料全般であり、具体的には、例えば、発泡材料、多孔質体、不織布、層状化合物等が挙げられる。これらの例は、例えば、特開平３－２２１１７３号公報、特許第４２０３５８９号公報等に挙げられている。以上に挙げた制振フィラーは、１種のみを単独で使用しても良く、２種以上を併用してもよい。 Examples of materials that tend to dissipate energy inside include microcapsule-based materials, low-density materials, and the like. Examples of microcapsule-based materials include thermally expandable microcapsules in which a vaporized substance that expands in a predetermined temperature range is enclosed in a shell made of a thermoplastic polymer. Examples of these are given in Japanese Unexamined Patent Application Publication No. 2013-18855. Examples of low-density materials include, for example, all materials containing an air layer inside the material, and specific examples thereof include foamed materials, porous bodies, non-woven fabrics, layered compounds, and the like. Examples of these are given in, for example, Japanese Patent Application Laid-Open No. 3-221173 and Japanese Patent No. 4203589. The damping fillers listed above may be used alone or in combination of two or more.
制振樹脂層は、耐熱性樹脂及び制振フィラーに加えて、固体潤滑剤や硬質粒子等の任意の成分を含んでもよい。制振樹脂層に、耐摩耗性、耐焼付き性、低摩擦特性等の特性を付与できるからである。固体潤滑剤としては、特に限定されずに、例えば、ポリテトラフルオロチエチレン（ＰＴＦＥ）、二硫化モリブデン（ＭｏＳ２）、グラファイト（黒鉛）等が挙げられる。これらの固体潤滑剤は、１種のみを単独で使用しても良く、２種以上を併用してもよい。硬質粒子としては、特に限定されずに、アルミナ（Ａｌ２Ｏ３）、シリカ等が挙げられる。これらの硬質粒子は、１種のみを単独で使用しても良く、２種以上を併用してもよい。 The damping resin layer may contain optional components such as a solid lubricant and hard particles in addition to the heat-resistant resin and damping filler. This is because properties such as wear resistance, seizure resistance, and low friction properties can be imparted to the damping resin layer. Examples of solid lubricants include, but are not limited to, polytetrafluorothethylene (PTFE), molybdenum disulfide (MoS 2 ), and graphite. These solid lubricants may be used alone or in combination of two or more. Examples of hard particles include alumina (Al 2 O 3 ), silica, and the like, without being particularly limited. These hard particles may be used individually by 1 type, and may use 2 or more types together.
制振樹脂層における耐熱性樹脂及び制振フィラーの合計体積に対する制振フィラーの体積比は、特に限定されないが、例えば、２０体積％以上８０体積％以下が好ましく、中でも４０体積％以上６０体積％以下の範囲内が好ましい。これらの範囲の下限以上であることにより、より効率的に、フィラーによって、振動エネルギーを熱エネルギーに変換できるからである。また、これらの範囲の上限以下であることにより、樹脂コーティングとしての耐久性（例えば耐摩耗性や密着力など）を担保できるからである。なお、制振樹脂層における耐熱性樹脂及び制振フィラー以外の任意の成分の体積比は、特に限定されず、種類に応じて選択することができる。 The volume ratio of the damping filler to the total volume of the heat-resistant resin and the damping filler in the damping resin layer is not particularly limited, but is preferably 20% by volume or more and 80% by volume or less, especially 40% by volume or more and 60% by volume. The following ranges are preferred. This is because vibration energy can be more efficiently converted into heat energy by the filler when it is at least the lower limits of these ranges. In addition, the durability (for example, abrasion resistance, adhesion strength, etc.) as a resin coating can be ensured by keeping the upper limit of these ranges or less. The volume ratio of any components other than the heat-resistant resin and the damping filler in the damping resin layer is not particularly limited, and can be selected according to the type.
制振樹脂層は、特に限定されず、所望の周波数の振動の伝達を抑制するものであればよいが、例えば、周波数２ｋＨｚの振動の伝達を抑制するものが好ましい。騒音を特に効果的に抑制できるからである。なお、制振樹脂層を所望の周波数の振動の伝達を抑制するものに調整するためには、例えば、制振樹脂層における制振フィラーや耐熱性樹脂等の各成分の種類や含有量、制振樹脂層の厚さなどを調整すればよい。 The damping resin layer is not particularly limited as long as it suppresses the transmission of vibrations of a desired frequency. For example, it is preferable to suppress the transmission of vibrations of a frequency of 2 kHz. This is because noise can be suppressed particularly effectively. In addition, in order to adjust the damping resin layer to suppress the transmission of the vibration of the desired frequency, for example, the type and content of each component such as the damping filler and the heat-resistant resin in the damping resin layer, the damping The thickness of the vibration resin layer may be adjusted.
制振樹脂層の形成方法は、特に限定されないが、例えば、下記の方法等が挙げられる。
まず、所定量の耐熱性樹脂を有機溶剤に溶解させることで溶解液を調製する。次に、所定量の制振フィラーを溶解液に加え、必要に応じてさらに任意の成分を加え、混錬することで塗工材を調製する。次に、塗工材を、高圧ポンプが備える部材における振動発生源又は振動伝達経路を構成する部位（例えば、リフタガイドの内周面、リフタの外周面、フランジ部の締結面や座面等）に塗工する。次に、部材に塗工された塗工材を加熱し、乾燥、硬化させる。これにより、制振樹脂層を形成する。
A method for forming the damping resin layer is not particularly limited, and examples thereof include the following methods.
First, a solution is prepared by dissolving a predetermined amount of heat-resistant resin in an organic solvent. Next, a predetermined amount of damping filler is added to the solution, and if necessary, optional components are added and kneaded to prepare a coating material. Next, the coating material is applied to a portion constituting a vibration source or a vibration transmission path in a member provided in the high-pressure pump (for example, the inner peripheral surface of the lifter guide, the outer peripheral surface of the lifter, the fastening surface and the seating surface of the flange portion, etc.). to be coated. Next, the coating material applied to the member is heated, dried and cured. Thereby, a damping resin layer is formed.
上記の方法に用いる有機溶剤は、特に限定されずに耐熱性樹脂の種類に応じて選択される。有機溶剤としては、例えば、耐熱性樹脂としてポリアミドイミド樹脂を用いる場合には、Ｎ－メチル－２－ピロリドン（ＮＭＰ）、Ｎ－エチル－２－ピロリドン（ＮＥＰ）、１，３－ジメチル－２－イミダゾリジノン（ＤＭＩ）、γ－ブチロラクトン（ＧＢＬ）等が挙げられる。また、エポキシ樹脂を用いる場合には、メチルエチルケトン（ＭＥＫ）、トルエン等が挙げられる。 The organic solvent used in the above method is not particularly limited and is selected according to the type of heat-resistant resin. Examples of organic solvents include N-methyl-2-pyrrolidone (NMP), N-ethyl-2-pyrrolidone (NEP), 1,3-dimethyl-2- imidazolidinone (DMI), γ-butyrolactone (GBL) and the like. Moreover, when using an epoxy resin, methyl ethyl ketone (MEK), toluene, etc. are mentioned.
塗工材を調製するための混錬の方法は、例えば、ニーダーを使用し、１時間混錬を行う方法等が挙げられる。高圧ポンプが備える部材への塗工材の塗工方法は、特に限定されず、一般的な塗工方法を用いることができるが、スプレーコーティング、スクリーン印刷、ディッピング等が挙げられる。塗工材を乾燥、硬化させるための加熱条件は、特に限定されずに、例えば、１００℃以上３７０℃以下の温度で３０分以上３時間以下の時間加熱する条件等が挙げられる。 The kneading method for preparing the coating material includes, for example, a method of kneading for one hour using a kneader. The method of applying the coating material to the members provided in the high-pressure pump is not particularly limited, and general coating methods can be used, including spray coating, screen printing, dipping, and the like. The heating conditions for drying and curing the coating material are not particularly limited, and include, for example, heating at a temperature of 100° C. or more and 370° C. or less for 30 minutes or more and 3 hours or less.
以下、実施例、参考例、及び比較例を挙げて、実施形態に係る高圧ポンプをさらに具体的に説明する。 EXAMPLES Hereinafter, the high-pressure pump according to the embodiment will be described more specifically with reference to examples, reference examples, and comparative examples.
１．テストピースの作製及びテストピースでの制振樹脂層のＮＶ性能の評価
参考例１～１１で基材に制振樹脂層が形成されたテストピースを作製し、比較例１で基材のみからなるテストピースを準備した上で、これらのテストピースにおいて、制振樹脂層のＮＶ性能を評価した。
1. Preparation of test piece and evaluation of NV performance of damping resin layer in test piece In Reference Examples 1 to 11, test pieces in which a damping resin layer was formed on the base material were prepared, and in Comparative Example 1, it consisted only of the base material. After preparing the test pieces, the NV performance of the damping resin layer was evaluated in these test pieces.
［参考例１］
最初に、高圧ポンプの制振樹脂層に形成に用いる塗工材を調製した。具体的には、まず、ポリアミドイミド樹脂を耐熱性樹脂として準備し、Ｎ－エチル－２－ピロリドン（ＮＥＰ）（有機溶剤）に所定量溶解させることで溶解液を調製した。次に、熱可塑性エラストマーを制振フィラーとして準備し、溶解液に所定量加え、ニーダーを使用し、１時間混錬した。これにより、制振樹脂層における耐熱性樹脂及び制振フィラーの合計体積に対する制振フィラーの体積比が５０体積％となるように、塗工材を調製した。
[Reference example 1]
First, a coating material was prepared for forming a damping resin layer of a high-pressure pump. Specifically, first, a polyamideimide resin was prepared as a heat-resistant resin, and dissolved in a predetermined amount of N-ethyl-2-pyrrolidone (NEP) (organic solvent) to prepare a solution. Next, a thermoplastic elastomer was prepared as a damping filler, added in a predetermined amount to the solution, and kneaded for 1 hour using a kneader. Thus, the coating material was prepared so that the volume ratio of the damping filler to the total volume of the heat-resistant resin and the damping filler in the damping resin layer was 50% by volume.
続いて、ブロック形状の基材の表面に制振樹脂層が形成されたテストピースを作製した。具体的には、まず、ＳＵＳ４４０Ｃからなるブロック形状の基材を準備し、基材の表面に塗工材をスプレーコーティングにより所定量塗工した。次に、基材に塗工された塗工材を１８０℃で９０分間加熱することにより、有機溶剤を揮発させ、塗工材を乾燥、硬化させた。これにより、基材の表面に厚さが１μｍの制振樹脂層を形成することでテストピースを作製した。 Subsequently, a test piece was produced in which a damping resin layer was formed on the surface of a block-shaped base material. Specifically, first, a block-shaped base material made of SUS440C was prepared, and a predetermined amount of coating material was applied to the surface of the base material by spray coating. Next, the coating material applied to the substrate was heated at 180° C. for 90 minutes to volatilize the organic solvent, and the coating material was dried and cured. Thus, a test piece was produced by forming a damping resin layer having a thickness of 1 μm on the surface of the substrate.
［参考例２］
厚さが５μｍとなるように制振樹脂層を形成した点を除いて、参考例１と同様にテストピースを作製した。
[Reference example 2]
A test piece was produced in the same manner as in Reference Example 1, except that the damping resin layer was formed to have a thickness of 5 μm.
［参考例３］
厚さが１０μｍとなるように制振樹脂層を形成した点を除いて、参考例１と同様にテストピースを作製した。
[Reference example 3]
A test piece was produced in the same manner as in Reference Example 1, except that the damping resin layer was formed to have a thickness of 10 μm.
［参考例４］
厚さが２０μｍとなるように制振樹脂層を形成した点を除いて、参考例１と同様にテストピースを作製した。
[Reference Example 4]
A test piece was produced in the same manner as in Reference Example 1, except that the damping resin layer was formed to have a thickness of 20 μm.
［参考例５］
厚さが５０μｍとなるように制振樹脂層を形成した点を除いて、参考例１と同様にテストピースを作製した。
[Reference Example 5]
A test piece was produced in the same manner as in Reference Example 1, except that the damping resin layer was formed to have a thickness of 50 μm.
［参考例６］
厚さが１００μｍとなるように制振樹脂層を形成した点を除いて、参考例１と同様にテストピースを作製した。
[Reference Example 6]
A test piece was produced in the same manner as in Reference Example 1, except that the damping resin layer was formed to have a thickness of 100 μm.
［参考例７］
厚さが２００μｍとなるように制振樹脂層を形成した点を除いて、参考例１と同様にテストピースを作製した。
[Reference Example 7]
A test piece was produced in the same manner as in Reference Example 1, except that the damping resin layer was formed to have a thickness of 200 μm.
［参考例８］
最初に、ウレタン樹脂を制振フィラーとして準備し、溶解液に所定量加えた点を除いて、参考例１と同様に塗工材を調製した。
[Reference Example 8]
First, a coating material was prepared in the same manner as in Reference Example 1, except that a urethane resin was prepared as a damping filler and added to the solution in a predetermined amount.
続いて、本参考例で調製した塗工材を用い、厚さが１００μｍとなるように制振樹脂層を形成した点を除いて、参考例１と同様にテストピースを作製した。 Subsequently, a test piece was produced in the same manner as in Reference Example 1, except that the coating material prepared in this Reference Example was used to form a damping resin layer having a thickness of 100 μm.
［参考例９］
最初に、厚さが２００μｍとなるように制振樹脂層を形成した点を除いて、参考例８と同様にテストピースを作製した。
[Reference Example 9]
First, a test piece was produced in the same manner as in Reference Example 8, except that a damping resin layer was formed so as to have a thickness of 200 μm.
［参考例１０］
最初に、マイクロカプセルを制振フィラーとして準備し、溶解液に所定量加えた点を除いて、参考例１と同様に塗工材を調製した。
[Reference Example 10]
First, a coating material was prepared in the same manner as in Reference Example 1, except that microcapsules were prepared as a damping filler and added to the solution in a predetermined amount.
続いて、本参考例で調製した塗工材を用い、厚さが１００μｍとなるように制振樹脂層を形成した点を除いて、参考例１と同様にテストピースを作製した。 Subsequently, a test piece was produced in the same manner as in Reference Example 1, except that the coating material prepared in this Reference Example was used to form a damping resin layer having a thickness of 100 μm.
［参考例１１］
最初に、厚さが２００μｍとなるように制振樹脂層を形成した点を除いて、参考例１０と同様にテストピースを作製した。
[Reference Example 11]
First, a test piece was produced in the same manner as in Reference Example 10, except that a damping resin layer was formed so as to have a thickness of 200 μm.
［比較例１］
参考例１と同様のブロック形状の基材を準備し、制振樹脂層を形成せずにそのままテストピースとした。
[Comparative Example 1]
A block-shaped base material similar to that of Reference Example 1 was prepared and used as a test piece as it was without forming a damping resin layer.
［落球試験による制振樹脂層のＮＶ性能の評価］
参考例１～１１及び比較例１で得られたテストピースにおいて、落球試験を行い、ＮＶ性能への制振樹脂層の厚さの影響を評価した。図８は、落球試験機を模式的に示す断面図である。
[Evaluation of NV performance of damping resin layer by falling ball test]
The test pieces obtained in Reference Examples 1 to 11 and Comparative Example 1 were subjected to a falling ball test to evaluate the influence of the thickness of the damping resin layer on the NV performance. FIG. 8 is a cross-sectional view schematically showing a falling ball tester.
落球試験では、図８に示すように、テストピースを落球試験機の土台の上部に設置された加速度ピックアップ上の鋼板上に設置した。設置の際には、参考例１～１１のテストピースについては、制振樹脂層が鋼板に当接するようにした。これは、落球試験の目的が、部品と部品の隙間に配置した制振樹脂層に衝撃が付与された際、騒音がどの程度抑制されるかを測定することにあるからである。落球試験機では、テストピースの直上にφ６．３ｍｍのＳＵＪ２製鋼球が電磁石で保持される。落球試験では、鋼球の落球前の高さ（テストピース上面からの距離）を５００ｍｍとした上で、落球試験機の磁力をオフにすることで鋼球を落下させることにより、テストピースに衝突させた。そして、衝突時に生じた音を、テストピース直上に設置したマイクロホンで集音し、周波数２０Ｈｚ～１０ｋＨｚ帯域でのオーバーオール値の音圧レベルを計測した。計測結果を下記の表１に示す。図９は、参考例１～１１及び比較例１のテストピースにおける制振樹脂層の厚さに対する鋼球衝突時に生じた音の音圧レベルを示すグラフである。 In the falling ball test, as shown in FIG. 8, the test piece was placed on a steel plate on an acceleration pickup placed on the top of the base of the falling ball tester. At the time of installation, the damping resin layers of the test pieces of Reference Examples 1 to 11 were brought into contact with the steel plate. This is because the purpose of the falling ball test is to measure how much noise is suppressed when an impact is applied to the damping resin layer arranged in the gap between the parts. In the falling ball tester, a φ6.3 mm SUJ2 steel ball is held by an electromagnet directly above the test piece. In the falling ball test, the height of the steel ball before falling (distance from the top surface of the test piece) was set to 500 mm, and the magnetic force of the falling ball tester was turned off to let the steel ball fall and collide with the test piece. let me Then, the sound generated at the time of collision was collected by a microphone placed directly above the test piece, and the sound pressure level of the overall value in the frequency band of 20 Hz to 10 kHz was measured. The measurement results are shown in Table 1 below. 9 is a graph showing the sound pressure level of the sound generated when the steel ball collides with the thickness of the damping resin layer in the test pieces of Reference Examples 1 to 11 and Comparative Example 1. FIG.
下記の表１及び図９に示すように、制振樹脂層の厚さの増加に伴い、音圧レベルが低減していることから、ＮＶ性能は制振樹脂層の厚さの増加に伴い向上すると考えられる。比較例１の基材のみからなるテストピース、及び制振樹脂層の組成が同一の参考例１～７のテストピースを比較すると、制振樹脂層の厚さが１０μｍより薄いテストピースでは、基材のみからなるテストピースに対する音圧レベルの低減効果は認められるものの、大幅な低減効果は認められない。一方、制振樹脂層の厚さが１０μｍ以上のテストピースでは、基材のみからなるテストピースに対し、５ｄＢ以上の音圧レベルの低減効果が認められる。従って、制振樹脂層の厚さとしては、１０μｍ以上が好ましく、中でも２０μｍ以上、特に５０μｍ以上が好ましいと考えられる。さらに、下記の表１及び図９に示すように、制振樹脂層の制振フィラーの種類を変更したとしても、同様の傾向が認められる。 As shown in Table 1 and Figure 9 below, as the thickness of the damping resin layer increases, the sound pressure level decreases, so the NV performance improves as the thickness of the damping resin layer increases. It is thought that Comparing the test piece consisting only of the base material of Comparative Example 1 and the test pieces of Reference Examples 1 to 7, in which the composition of the damping resin layer is the same, it is found that the test pieces having a damping resin layer thickness of less than 10 μm have a thickness of less than 10 μm. Although the effect of reducing the sound pressure level for the test piece made of only material is recognized, a significant reduction effect is not recognized. On the other hand, the test piece with the damping resin layer having a thickness of 10 μm or more showed an effect of reducing the sound pressure level by 5 dB or more as compared with the test piece consisting only of the base material. Therefore, the thickness of the damping resin layer is considered to be preferably 10 μm or more, more preferably 20 μm or more, particularly preferably 50 μm or more. Furthermore, as shown in Table 1 and FIG. 9 below, even if the type of damping filler in the damping resin layer is changed, the same tendency is observed.
２．高圧ポンプの作製及び高圧ポンプのＮＶ性能の評価
実施例１－１～３－７において、エンジンのエンジンヘッド（シリンダヘッド）に取付けられた高圧ポンプを作製し、これらの高圧ポンプのＮＶ性能を評価した。
2. Production of high-pressure pump and evaluation of NV performance of high-pressure pump In Examples 1-1 to 3-7, high-pressure pumps attached to the engine head (cylinder head) of the engine were produced, and the NV performance of these high-pressure pumps was evaluated. bottom.
［実施例１－１］
高圧ポンプとして、厚さが１００μｍの制振樹脂層がリフタの外周面（１）に設けられたものを作製した。
[Example 1-1]
A high-pressure pump having a damping resin layer with a thickness of 100 μm provided on the outer peripheral surface (1) of the lifter was manufactured.
具体的には、まず、有底筒状の形状を有するリフタ（材質：ＪＩＳ Ｇ３６０１：２０１２でステンレスクラッド鋼の一種として区分されている拡散クラッド鋼Ｄ２）を準備した。次に、リフタの外周面に参考例１で調製した塗工材をスプレーコーティングにより所定量塗工した。次に、リフタに塗工された塗工材を１８０℃で９０分間加熱することにより、有機溶剤を揮発させ、塗工材を乾燥、硬化させた。これにより、リフタの外周面に厚さが１００μｍとなるように制振樹脂層を形成した。 Specifically, first, a bottomed cylindrical lifter (material: diffusion clad steel D2 classified as a type of stainless clad steel in accordance with JIS G3601:2012) was prepared. Next, a predetermined amount of the coating material prepared in Reference Example 1 was applied to the outer peripheral surface of the lifter by spray coating. Next, the coating material applied to the lifter was heated at 180° C. for 90 minutes to volatilize the organic solvent, and the coating material was dried and cured. Thus, a damping resin layer was formed on the outer peripheral surface of the lifter so as to have a thickness of 100 μm.
次に、制振樹脂層が形成されたリフタと、下ハウジングのシリンダ保持部、フランジ部（材質：ＪＩＳ Ｇ４３０５で区分されているＳＵＳ４３６）、及びエンジン嵌合部、並びにシリンダ、プランジャ等を含む他の部品とから高圧ポンプの取付け前の半製品を組み立てた。次に、当該半製品を制振樹脂層が形成されていないエンジンヘッドに取り付けた。この際には、エンジンヘッドの収容孔の内側に、リフタ、下ハウジングのエンジン嵌合部、並びにシリンダ、プランジャ等を収容し、下ハウジングのフランジ部をエンジンヘッドの締結面上に載置した。ボルトを下ハウジングのフランジ部のボルト挿通孔及びエンジンヘッドのボルト挿通孔に挿通することにより、下ハウジングをエンジンヘッドに締結した。これにより、高圧ポンプを作製した。当該高圧ポンプでは、リフタの往復移動時に、リフタの外周面に設けられた制振樹脂層が収容孔の内壁面に接触して摺動する。 Next, a lifter on which a damping resin layer is formed, a cylinder holding portion of the lower housing, a flange portion (material: SUS436 classified by JIS G4305), an engine fitting portion, a cylinder, a plunger, etc. A semi-finished product before installation of the high-pressure pump was assembled from the parts of Next, the semi-finished product was attached to an engine head on which no damping resin layer was formed. At this time, the lifter, the engine fitting portion of the lower housing, the cylinder, the plunger, etc. were accommodated inside the accommodation hole of the engine head, and the flange portion of the lower housing was placed on the fastening surface of the engine head. The lower housing was fastened to the engine head by inserting bolts through the bolt insertion holes of the flange portion of the lower housing and the bolt insertion holes of the engine head. Thus, a high-pressure pump was produced. In the high-pressure pump, when the lifter reciprocates, the damping resin layer provided on the outer peripheral surface of the lifter contacts and slides on the inner wall surface of the accommodation hole.
［実施例１－２］
高圧ポンプとして、厚さが１００μｍの制振樹脂層がエンジンヘッドの収容孔の内壁面（リフタガイドの内周面）（２）に設けられたものを作製した。
[Example 1-2]
A high-pressure pump was prepared in which a damping resin layer having a thickness of 100 μm was provided on the inner wall surface (inner peripheral surface of the lifter guide) (2) of the housing hole of the engine head.
具体的には、まず、エンジンヘッドの収容孔の内壁面に参考例１で調製した塗工材をスプレーコーティングにより所定量塗工した。次に、内壁面に塗工された塗工材を１８０℃で９０分間加熱することにより、有機溶剤を揮発させ、塗工材を乾燥、硬化させた。これにより、エンジンヘッドの収容孔の内壁面に厚さが１００μｍとなるように制振樹脂層を形成した。 Specifically, first, a predetermined amount of the coating material prepared in Reference Example 1 was applied to the inner wall surface of the accommodation hole of the engine head by spray coating. Next, the coating material applied to the inner wall surface was heated at 180° C. for 90 minutes to volatilize the organic solvent, and the coating material was dried and cured. As a result, a damping resin layer having a thickness of 100 μm was formed on the inner wall surface of the accommodation hole of the engine head.
次に、制振樹脂層形成前のリフタを用いた点を除いて実施例１－１と同様に高圧ポンプの取付け前の半製品を組み立てた。次に、当該半製品を制振樹脂層が形成された当該エンジンヘッドに取り付けた点を除いて実施例１－１と同様に半製品をエンジンヘッドに取り付けた。これにより、高圧ポンプを作製した。当該高圧ポンプでは、リフタの往復移動時に、リフタの外周面が収容孔の内壁面に設けられた制振樹脂層に接触して摺動する。 Next, a semi-finished product before mounting the high-pressure pump was assembled in the same manner as in Example 1-1, except that the lifter before forming the damping resin layer was used. Next, the semi-finished product was attached to the engine head in the same manner as in Example 1-1, except that the semi-finished product was attached to the engine head on which the damping resin layer was formed. Thus, a high-pressure pump was produced. In the high-pressure pump, when the lifter reciprocates, the outer peripheral surface of the lifter contacts and slides on the damping resin layer provided on the inner wall surface of the housing hole.
［実施例１－３］
高圧ポンプとして、厚さが５０μｍの制振樹脂層がリフタの外周面（１）及びエンジンヘッドの収容孔の内壁面（リフタガイドの内周面）（２）の両方に設けられたものを作製した。
[Example 1-3]
As a high-pressure pump, a damping resin layer having a thickness of 50 μm is provided on both the outer peripheral surface (1) of the lifter and the inner wall surface (inner peripheral surface of the lifter guide) (2) of the housing hole of the engine head. bottom.
具体的には、まず、厚さが５０μｍとなるように制振樹脂層を形成した点を除いて実施例１－１と同様にリフタの外周面に制振樹脂層を形成した。次に、厚さが５０μｍとなるように制振樹脂層を形成した点を除いて実施例１－２と同様にエンジンヘッドの収容孔の内壁面に制振樹脂層を形成した。 Specifically, first, a damping resin layer was formed on the outer peripheral surface of the lifter in the same manner as in Example 1-1, except that the damping resin layer was formed to have a thickness of 50 μm. Next, a damping resin layer was formed on the inner wall surface of the housing hole of the engine head in the same manner as in Example 1-2, except that the damping resin layer was formed so as to have a thickness of 50 μm.
次に、制振樹脂層が形成された当該リフタを用いた点を除いて実施例１－１と同様に高圧ポンプの取付け前の半製品を組み立てた。次に、当該半製品を制振樹脂層が形成された当該エンジンヘッドに取り付けた点を除いて実施例１－１と同様に半製品をエンジンヘッドに取り付けた。これにより、高圧ポンプを作製した。当該高圧ポンプでは、リフタの往復移動時に、リフタの外周面に設けられた制振樹脂層が収容孔の内壁面に設けられた制振樹脂層に接触して摺動する。 Next, a semi-finished product before attachment of the high-pressure pump was assembled in the same manner as in Example 1-1, except that the lifter on which the damping resin layer was formed was used. Next, the semi-finished product was attached to the engine head in the same manner as in Example 1-1, except that the semi-finished product was attached to the engine head on which the damping resin layer was formed. Thus, a high-pressure pump was produced. In the high-pressure pump, when the lifter reciprocates, the damping resin layer provided on the outer peripheral surface of the lifter contacts and slides on the damping resin layer provided on the inner wall surface of the accommodation hole.
［実施例１－４］
高圧ポンプとして、厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部におけるエンジンヘッドと対向する締結面（３）に設けられたものを作製した。
[Example 1-4]
A high-pressure pump was produced in which a damping resin layer having a thickness of 200 μm was provided on the fastening surface (3) of the flange portion of the lower housing facing the engine head.
具体的には、まず、フランジ部の締結面に参考例１で調製した塗工材をスプレーコーティングにより所定量塗工した。次に、フランジ部に塗工された塗工材を１８０℃で９０分間加熱することにより、有機溶剤を揮発させ、塗工材を乾燥、硬化させた。これにより、フランジ部の締結面に厚さが２００μｍとなるように制振樹脂層を形成した。 Specifically, first, a predetermined amount of the coating material prepared in Reference Example 1 was applied to the fastening surface of the flange portion by spray coating. Next, by heating the coating material applied to the flange portion at 180° C. for 90 minutes, the organic solvent was volatilized, and the coating material was dried and cured. As a result, a damping resin layer was formed on the fastening surface of the flange portion so as to have a thickness of 200 μm.
次に、制振樹脂層形成前のリフタを用いた点及び制振樹脂層が形成された当該フランジ部を有する下ハウジングを用いた点を除いて実施例１－１と同様に高圧ポンプの取付け前の半製品を組み立てた。次に、当該半製品をエンジンヘッドに取り付けた点を除いて実施例１－１と同様に半製品をエンジンヘッドに取り付けた。これにより、高圧ポンプを作製した。当該高圧ポンプでは、エンジンヘッドの締結面及びフランジ部の締結面の間に制振樹脂層が配置されている。 Next, the high-pressure pump is mounted in the same manner as in Example 1-1 except that a lifter before the formation of the damping resin layer is used and a lower housing having the flange portion on which the damping resin layer is formed is used. Assembled the previous semi-finished product. Next, the semi-finished product was attached to the engine head in the same manner as in Example 1-1, except that the semi-finished product was attached to the engine head. Thus, a high-pressure pump was produced. In this high-pressure pump, a damping resin layer is arranged between the fastening surface of the engine head and the fastening surface of the flange portion.
［実施例１－５］
高圧ポンプとして、厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部における締結面と反対側の座面（４）に設けられたものを作製した。
[Example 1-5]
A high-pressure pump was fabricated in which a damping resin layer having a thickness of 200 μm was provided on the bearing surface (4) on the side opposite to the fastening surface of the flange portion of the lower housing.
具体的には、まず、フランジ部の座面に参考例１で調製した塗工材をスプレーコーティングにより所定量塗工した。次に、フランジ部に塗工された塗工材を１８０℃で９０分間加熱することにより、有機溶剤を揮発させ、塗工材を乾燥、硬化させた。これにより、フランジ部の座面に厚さが２００μｍとなるように制振樹脂層を形成した。 Specifically, first, a predetermined amount of the coating material prepared in Reference Example 1 was applied to the bearing surface of the flange portion by spray coating. Next, by heating the coating material applied to the flange portion at 180° C. for 90 minutes, the organic solvent was volatilized, and the coating material was dried and cured. As a result, a damping resin layer was formed on the bearing surface of the flange portion so as to have a thickness of 200 μm.
次に、制振樹脂層形成前のリフタを用いた点及び制振樹脂層が形成された当該フランジ部を有する下ハウジングを用いた点を除いて実施例１－１と同様に高圧ポンプの取付け前の半製品を組み立てた。次に、当該半製品をエンジンヘッドに取り付けた点を除いて実施例１－１と同様に半製品をエンジンヘッドに取り付けた。これにより、高圧ポンプを作製した。当該高圧ポンプでは、フランジ部の座面及びボルトの頭部の間に制振樹脂層が配置されている。 Next, the high-pressure pump is mounted in the same manner as in Example 1-1 except that a lifter before the formation of the damping resin layer is used and a lower housing having the flange portion on which the damping resin layer is formed is used. Assembled the previous semi-finished product. Next, the semi-finished product was attached to the engine head in the same manner as in Example 1-1, except that the semi-finished product was attached to the engine head. Thus, a high-pressure pump was produced. In this high-pressure pump, a damping resin layer is arranged between the bearing surface of the flange and the head of the bolt.
［実施例１－６］
高圧ポンプとして、厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部におけるエンジンヘッドと対向する締結面（３）及び締結面と反対側の座面（４）の両方に設けられたものを作製した。
[Example 1-6]
As a high-pressure pump, a damping resin layer having a thickness of 200 μm is provided on both the fastening surface (3) facing the engine head in the flange portion of the lower housing and the seat surface (4) opposite to the fastening surface. made.
具体的には、まず、厚さが２００μｍとなるように制振樹脂層を形成した点を除いて実施例１－４と同様にフランジ部の締結面に制振樹脂層を形成した。次に、厚さが２００μｍとなるように制振樹脂層を形成した点を除いて実施例１－５と同様にフランジ部の座面に制振樹脂層を形成した。 Specifically, first, a damping resin layer was formed on the fastening surface of the flange portion in the same manner as in Example 1-4, except that the damping resin layer was formed so as to have a thickness of 200 μm. Next, a damping resin layer was formed on the bearing surface of the flange portion in the same manner as in Example 1-5, except that the damping resin layer was formed so as to have a thickness of 200 μm.
次に、制振樹脂層形成前のリフタを用いた点及び制振樹脂層が形成された当該フランジ部を有する下ハウジングを用いた点を除いて実施例１－１と同様に高圧ポンプの取付け前の半製品を組み立てた。次に、当該半製品をエンジンヘッドに取り付けた点を除いて実施例１－１と同様に半製品をエンジンヘッドに取り付けた。これにより、高圧ポンプを作製した。 Next, the high-pressure pump is mounted in the same manner as in Example 1-1 except that a lifter before the formation of the damping resin layer is used and a lower housing having the flange portion on which the damping resin layer is formed is used. Assembled the previous semi-finished product. Next, the semi-finished product was attached to the engine head in the same manner as in Example 1-1, except that the semi-finished product was attached to the engine head. Thus, a high-pressure pump was produced.
［実施例１－７］
高圧ポンプとして、厚さが１００μｍの制振樹脂層がリフタの外周面（１）に設けられ、かつ厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部におけるエンジンヘッドと対向する締結面（３）及び締結面と反対側の座面（４）の両方に設けられたものを作製した。
[Example 1-7]
As a high-pressure pump, a damping resin layer with a thickness of 100 μm is provided on the outer peripheral surface (1) of the lifter, and a damping resin layer with a thickness of 200 μm is provided on the flange portion of the lower housing on the fastening surface facing the engine head ( 3) and on both the fastening surface and the seat surface (4) on the opposite side.
具体的には、まず、実施例１－１と同様にリフタの外周面に制振樹脂層を形成した。次に、厚さが２００μｍとなるように制振樹脂層を形成した点を除いて実施例１－４と同様にフランジ部の締結面に制振樹脂層を形成した。次に、厚さが２００μｍとなるように制振樹脂層を形成した点を除いて実施例１－５と同様にフランジ部の座面に制振樹脂層を形成した。 Specifically, first, a damping resin layer was formed on the outer peripheral surface of the lifter in the same manner as in Example 1-1. Next, a damping resin layer was formed on the fastening surface of the flange portion in the same manner as in Example 1-4, except that the damping resin layer was formed so as to have a thickness of 200 μm. Next, a damping resin layer was formed on the bearing surface of the flange portion in the same manner as in Example 1-5, except that the damping resin layer was formed so as to have a thickness of 200 μm.
次に、これらの制振樹脂層が形成された当該フランジ部を有する下ハウジングを用いた点を除いて実施例１－１と同様に高圧ポンプの取付け前の半製品を組み立てた。次に、当該半製品をエンジンヘッドに取り付けた点を除いて実施例１－１と同様に半製品をエンジンヘッドに取り付けた。これにより、高圧ポンプを作製した。 Next, a semi-finished product before attachment of the high-pressure pump was assembled in the same manner as in Example 1-1, except that the lower housing having the flange portion on which these damping resin layers were formed was used. Next, the semi-finished product was attached to the engine head in the same manner as in Example 1-1, except that the semi-finished product was attached to the engine head. Thus, a high-pressure pump was produced.
［実施例２－１］
参考例１で調製した塗工材の代わりに参考例８で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－１と同様に厚さが１００μｍの制振樹脂層がリフタの外周面に設けられた高圧ポンプを作製した。
[Example 2-1]
A damping resin layer having a thickness of 100 μm was formed in the same manner as in Example 1-1, except that the coating material prepared in Reference Example 8 was used instead of the coating material prepared in Reference Example 1 to form a damping resin layer. A high-pressure pump was produced in which a vibrating resin layer was provided on the outer peripheral surface of the lifter.
［実施例２－２］
参考例１で調製した塗工材の代わりに参考例８で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－２と同様に厚さが１００μｍの制振樹脂層がエンジンヘッドの収容孔の内壁面（リフタガイドの内周面）に設けられた高圧ポンプを作製した。
[Example 2-2]
A damping resin layer having a thickness of 100 μm was formed in the same manner as in Example 1-2, except that the coating material prepared in Reference Example 8 was used instead of the coating material prepared in Reference Example 1 to form a damping resin layer. A high-pressure pump was produced in which a vibrating resin layer was provided on the inner wall surface of the housing hole of the engine head (the inner peripheral surface of the lifter guide).
［実施例２－３］
参考例１で調製した塗工材の代わりに参考例８で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－３と同様に厚さが５０μｍの制振樹脂層がリフタの外周面及びエンジンヘッドの収容孔の内壁面（リフタガイドの内周面）の両方に設けられた高圧ポンプを作製した。
[Example 2-3]
A damping resin layer having a thickness of 50 μm was formed in the same manner as in Example 1-3, except that the coating material prepared in Reference Example 8 was used instead of the coating material prepared in Reference Example 1 to form the damping resin layer. A high-pressure pump was produced in which a vibrating resin layer was provided on both the outer peripheral surface of the lifter and the inner wall surface of the housing hole of the engine head (the inner peripheral surface of the lifter guide).
［実施例２－４］
参考例１で調製した塗工材の代わりに参考例８で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－４と同様に厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部におけるエンジンヘッドと対向する締結面に設けられた高圧ポンプを作製した。
[Example 2-4]
A damping resin layer having a thickness of 200 μm was formed in the same manner as in Example 1-4, except that the coating material prepared in Reference Example 8 was used instead of the coating material prepared in Reference Example 1 to form the damping resin layer. A high-pressure pump was manufactured in which a vibrating resin layer was provided on the fastening surface of the flange portion of the lower housing facing the engine head.
［実施例２－５］
参考例１で調製した塗工材の代わりに参考例８で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－５と同様に厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部における締結面と反対側の座面に設けられた高圧ポンプを作製した。
[Example 2-5]
A damping resin layer having a thickness of 200 μm was formed in the same manner as in Example 1-5, except that the coating material prepared in Reference Example 8 was used instead of the coating material prepared in Reference Example 1 to form the damping resin layer. A high-pressure pump was manufactured in which a vibrating resin layer was provided on the bearing surface opposite to the fastening surface of the flange portion of the lower housing.
［実施例２－６］
参考例１で調製した塗工材の代わりに参考例８で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－６と同様に厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部におけるエンジンヘッドと対向する締結面及び締結面と反対側の座面の両方に設けられた高圧ポンプを作製した。
[Example 2-6]
A damping resin layer having a thickness of 200 μm was formed in the same manner as in Example 1-6, except that the coating material prepared in Reference Example 8 was used instead of the coating material prepared in Reference Example 1 to form a damping resin layer. A high-pressure pump was produced in which a vibrating resin layer was provided on both the fastening surface facing the engine head in the flange portion of the lower housing and the seat surface opposite to the fastening surface.
［実施例２－７］
参考例１で調製した塗工材の代わりに参考例８で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－７と同様に厚さが１００μｍの制振樹脂層がリフタの外周面に設けられ、かつ厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部におけるエンジンヘッドと対向する締結面及び締結面と反対側の座面の両方に設けられた高圧ポンプを作製した。
[Example 2-7]
A damping resin layer having a thickness of 100 μm was formed in the same manner as in Example 1-7, except that the coating material prepared in Reference Example 8 was used instead of the coating material prepared in Reference Example 1 to form the damping resin layer. A vibration resin layer is provided on the outer peripheral surface of the lifter, and a vibration damping resin layer having a thickness of 200 μm is provided on both the fastening surface facing the engine head in the flange portion of the lower housing and the seat surface opposite to the fastening surface. A high-pressure pump was fabricated.
［実施例３－１］
参考例１で調製した塗工材の代わりに参考例１０で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－１と同様に厚さが１００μｍの制振樹脂層がリフタの外周面に設けられた高圧ポンプを作製した。
[Example 3-1]
A damping resin layer having a thickness of 100 μm was formed in the same manner as in Example 1-1, except that the coating material prepared in Reference Example 10 was used instead of the coating material prepared in Reference Example 1 to form the damping resin layer. A high-pressure pump was produced in which a vibrating resin layer was provided on the outer peripheral surface of the lifter.
［実施例３－２］
参考例１で調製した塗工材の代わりに参考例１０で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－２と同様に厚さが１００μｍの制振樹脂層がエンジンヘッドの収容孔の内壁面（リフタガイドの内周面）に設けられた高圧ポンプを作製した。
[Example 3-2]
A damping resin layer having a thickness of 100 μm was formed in the same manner as in Example 1-2, except that the coating material prepared in Reference Example 10 was used instead of the coating material prepared in Reference Example 1 to form the damping resin layer. A high-pressure pump was produced in which a vibrating resin layer was provided on the inner wall surface of the housing hole of the engine head (the inner peripheral surface of the lifter guide).
［実施例３－３］
参考例１で調製した塗工材の代わりに参考例１０で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－３と同様に厚さが５０μｍの制振樹脂層がリフタの外周面及びエンジンヘッドの収容孔の内壁面（リフタガイドの内周面）の両方に設けられた高圧ポンプを作製した。
[Example 3-3]
A damping resin layer having a thickness of 50 μm was formed in the same manner as in Example 1-3, except that the coating material prepared in Reference Example 10 was used instead of the coating material prepared in Reference Example 1 to form the damping resin layer. A high-pressure pump was produced in which a vibrating resin layer was provided on both the outer peripheral surface of the lifter and the inner wall surface of the housing hole of the engine head (the inner peripheral surface of the lifter guide).
［実施例３－４］
参考例１で調製した塗工材の代わりに参考例１０で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－４と同様に厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部におけるエンジンヘッドと対向する締結面に設けられた高圧ポンプを作製した。
[Example 3-4]
A damping resin layer having a thickness of 200 μm was formed in the same manner as in Example 1-4, except that the coating material prepared in Reference Example 10 was used instead of the coating material prepared in Reference Example 1 to form the damping resin layer. A high-pressure pump was manufactured in which a vibrating resin layer was provided on the fastening surface of the flange portion of the lower housing facing the engine head.
［実施例３－５］
参考例１で調製した塗工材の代わりに参考例１０で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－５と同様に厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部における締結面と反対側の座面に設けられた高圧ポンプを作製した。
[Example 3-5]
Except that the coating material prepared in Reference Example 10 was used in place of the coating material prepared in Reference Example 1 to form the damping resin layer, a damping resin layer having a thickness of 200 μm was formed in the same manner as in Example 1-5. A high-pressure pump was manufactured in which a vibrating resin layer was provided on the bearing surface opposite to the fastening surface of the flange portion of the lower housing.
［実施例３－６］
参考例１で調製した塗工材の代わりに参考例１０で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－６と同様に厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部におけるエンジンヘッドと対向する締結面及び締結面と反対側の座面の両方に設けられた高圧ポンプを作製した。
[Example 3-6]
Except that the coating material prepared in Reference Example 10 was used in place of the coating material prepared in Reference Example 1 to form the damping resin layer, a damping resin layer having a thickness of 200 μm was formed in the same manner as in Example 1-6. A high-pressure pump was produced in which a vibrating resin layer was provided on both the fastening surface facing the engine head in the flange portion of the lower housing and the seat surface opposite to the fastening surface.
［実施例３－７］
参考例１で調製した塗工材の代わりに参考例１０で調製した塗工材を用いて制振樹脂層を形成した点を除いて、実施例１－７と同様に厚さが１００μｍの制振樹脂層がリフタの外周面に設けられ、かつ厚さが２００μｍの制振樹脂層が下ハウジングのフランジ部におけるエンジンヘッドと対向する締結面及び締結面と反対側の座面の両方に設けられた高圧ポンプを作製した。
[Example 3-7]
A damping resin layer having a thickness of 100 μm was formed in the same manner as in Example 1-7, except that the coating material prepared in Reference Example 10 was used instead of the coating material prepared in Reference Example 1 to form the damping resin layer. A vibration resin layer is provided on the outer peripheral surface of the lifter, and a vibration damping resin layer having a thickness of 200 μm is provided on both the fastening surface facing the engine head in the flange portion of the lower housing and the seat surface opposite to the fastening surface. A high-pressure pump was fabricated.
［比較例２］
高圧ポンプとして、制振樹脂層が設けられていないものを作製した。具体的には、制振樹脂層形成前のリフタを用いた点を除いて実施例１－１と同様に高圧ポンプの取付け前の半製品を組み立てた。次に、当該半製品をエンジンヘッドに取り付けた点を除いて実施例１－１と同様に半製品をエンジンヘッドに取り付けた。これにより、高圧ポンプを作製した。
[Comparative Example 2]
A high-pressure pump without a damping resin layer was produced. Specifically, a semi-finished product was assembled before mounting the high-pressure pump in the same manner as in Example 1-1, except that the lifter was used before forming the damping resin layer. Next, the semi-finished product was attached to the engine head in the same manner as in Example 1-1, except that the semi-finished product was attached to the engine head. Thus, a high-pressure pump was produced.
〔高圧ポンプのＮＶ性能の評価〕
実施例１－１～３－７及び比較例２で作製された高圧ポンプのＮＶ性能を評価した。
[Evaluation of NV performance of high-pressure pump]
The NV performance of the high-pressure pumps produced in Examples 1-1 to 3-7 and Comparative Example 2 was evaluated.
具体的には、実施例１－１～３－７及び比較例２の高圧ポンプがエンジンヘッドに取付けられたエンジンにおいて、高圧ポンプの上面及びエンジンヘッドの高圧ポンプ近傍に加速度ピックアップを取り付けた。その上で、エンジンを駆動して２０００ｒｐｍの一定の回転数で回転させることで高圧ポンプを作動させた。そして、加速度ピックアップにより、高圧ポンプの上面及びエンジンヘッドの高圧ポンプ近傍に伝達される周波数２０Ｈｚ～２０ｋＨｚ帯域の振動のオーバーオール値の加速度レベルを計測した。高圧ポンプの上面に伝達される振動の加速度レベルの計測結果を下記の表２に示す。図１０は、実施例１－１～～３－７の高圧ポンプのうち制振樹脂層の形成箇所が（１）～（４）、（３）＋（４）、及び（１）＋（３）＋（４）である高圧ポンプがエンジンヘッドに取付けられたエンジンでの高圧ポンプの上面に伝達される振動の加速度レベルを示すグラフである。なお、下記の表２及び図１０のグラフでは、比較例２の加速度レベルを基準値とし、実施例の加速度レベルを基準値に対する相対値で示した。 Specifically, in the engines in which the high-pressure pumps of Examples 1-1 to 3-7 and Comparative Example 2 were attached to the engine head, acceleration pickups were attached on the upper surface of the high-pressure pumps and near the high-pressure pumps on the engine head. Then, the high-pressure pump was operated by driving the engine to rotate at a constant rotation speed of 2000 rpm. Then, an acceleration pickup was used to measure the overall acceleration level of the vibration in the frequency range of 20 Hz to 20 kHz transmitted to the upper surface of the high pressure pump and the vicinity of the high pressure pump of the engine head. Table 2 below shows the measurement results of the vibration acceleration level transmitted to the upper surface of the high-pressure pump. FIG. 10 shows that in the high-pressure pumps of Examples 1-1 to 3-7, the locations where the damping resin layers are formed are (1) to (4), (3)+(4), and (1)+(3). ) + (4) is a graph showing the acceleration level of the vibration transmitted to the top surface of the high pressure pump in an engine with the high pressure pump mounted on the engine head. In Table 2 below and the graph of FIG. 10, the acceleration level of Comparative Example 2 is used as a reference value, and the acceleration levels of Examples are shown as relative values to the reference value.
下記の表２及び図１０に示すように、実施例１－１～３－７の高圧ポンプにおいて、制振樹脂層を設ける部位にかかわらず、制振樹脂層が設けられることで、加速度レベルが、制振樹脂層が設けられない比較例２の基準値に対して大きく低減している。これは、制振樹脂層の制振効果によるものであると考えられる。下記の表２及び図１０に示す結果から、制振樹脂層がフランジ部の締結面（３）又は座面（４）に設けられる場合でも、制振樹脂層の制振効果は認められるが、制振樹脂層がリフタの外周面（１）又はエンジンヘッドの収容孔の内壁面（リフタガイドの内周面）（２）に設けられる場合には、制振樹脂層の制振効果がより大きくなることが認められる。これは、振動発生源で振動の発生自体を抑制できるためであると考えられる。また、制振樹脂層がフランジ部の締結面（３）及び座面（４）の両方に設けられる場合には、一方に設けられる場合と比べて制振効果がいっそう大きくなることが認められる。制振樹脂層がフランジ部の締結面（３）及び座面（４）に加えてリフタの外周面（１）に設けられる場合には、制振効果がよりいっそう大きくなることが認められる。 As shown in Table 2 and FIG. 10 below, in the high-pressure pumps of Examples 1-1 to 3-7, regardless of the location where the damping resin layer is provided, the acceleration level is reduced by providing the damping resin layer. , is greatly reduced from the reference value of Comparative Example 2 in which no damping resin layer is provided. This is considered to be due to the damping effect of the damping resin layer. From the results shown in Table 2 and FIG. 10 below, even when the damping resin layer is provided on the fastening surface (3) or the seating surface (4) of the flange portion, the damping effect of the damping resin layer is recognized. When the damping resin layer is provided on the outer peripheral surface (1) of the lifter or the inner wall surface (inner peripheral surface of the lifter guide) (2) of the housing hole of the engine head, the damping effect of the damping resin layer is greater. It is allowed to become It is considered that this is because the generation of vibration itself can be suppressed at the vibration source. Moreover, when the damping resin layer is provided on both the fastening surface (3) and the seating surface (4) of the flange portion, it is recognized that the damping effect is further enhanced compared to the case where it is provided on one side. When the damping resin layer is provided on the outer peripheral surface (1) of the lifter in addition to the fastening surface (3) and bearing surface (4) of the flange portion, it is recognized that the damping effect is further enhanced.
以上のことから、振動発生源への対策が可能という観点では、高圧ポンプとしては、制振樹脂層として、リフタガイドの内周面及びリフタの外周面の少なくとも一方に設けられた制振樹脂層を備えるものが好ましいと考えられる。さらに、リフタの往復移動時において、リフタの外周面は常に全体で摺動するのに対して、リフタガイドの内周面の摺動部位はリフタの移動に応じて変化するため、リフタガイドの内周面に設けられた制振樹脂層を備える高圧ポンプは、リフタの外周面に設けられた制振樹脂層を備える高圧ポンプと比べて、制振樹脂層の摩耗が抑制される結果、制振樹脂層の性能が維持され易い。よって、高圧ポンプとしては、中でもリフタガイドの内周面に設けられた制振樹脂層を備えるものが好ましいと考えられる。 From the above, from the viewpoint of being able to take measures against vibration sources, as a high-pressure pump, a vibration-damping resin layer is provided on at least one of the inner peripheral surface of the lifter guide and the outer peripheral surface of the lifter. is considered preferable. Furthermore, when the lifter reciprocates, the entire outer peripheral surface of the lifter always slides, whereas the sliding portion of the inner peripheral surface of the lifter guide changes according to the movement of the lifter. A high-pressure pump provided with a damping resin layer provided on the peripheral surface suppresses wear of the damping resin layer compared to a high-pressure pump provided with a damping resin layer provided on the outer peripheral surface of the lifter. The performance of the resin layer is easily maintained. Therefore, it is considered preferable that the high-pressure pump includes a damping resin layer provided on the inner peripheral surface of the lifter guide.
以上、本発明の高圧ポンプに係る実施形態について詳述したが、本発明は、上記の実施形態に限定されるものではなく、特許請求の範囲に記載された本発明の精神を逸脱しない範囲で、種々の設計変更を行うことができるものである。 Although the embodiments of the high-pressure pump of the present invention have been described in detail above, the present invention is not limited to the above-described embodiments, and is within the spirit of the present invention described in the claims. , various design changes can be made.
１ 高圧ポンプ
９ エンジン
１８ エンジンヘッド
１８０ 収容孔
１８１ 内壁（リフタガイド）
１８１ｓ 内壁面
１０ 本体部
１１ 下ハウジング
１１１ シリンダ保持部
１１２ フランジ部
１１３ エンジン嵌合部
１３ シリンダ
１５ 上ハウジング
２０ リフタ
２０ｓ 外周面
２２ リフタガイド
２４ａ 第１制振樹脂層
２４ｂ 第２制振樹脂層
２４ｃ 第３制振樹脂層
２４ｄ 第４制振樹脂層
３０ 燃料供給部
５０ プランジャ部
５１ プランジャ
７０ 燃料吸入部
９０ 燃料吐出リリーフ部
1 high-
181s
Claims (5)
前記シリンダの前記筒孔に往復摺動可能に嵌入されたプランジャと、
駆動カムの回転に伴い往復移動し、前記プランジャを連動で往復移動させるリフタと、
前記リフタを収容孔に収容し、前記リフタの往復移動をガイドするリフタガイドと、を備える高圧ポンプであって、
前記高圧ポンプにおける振動発生源及び振動伝達経路の少なくとも一方に設けられた制振樹脂層をさらに備え、
前記制振樹脂層は、耐熱性樹脂と、振動エネルギーを熱エネルギーに変換する制振フィラーとを含むことを特徴とする高圧ポンプ。 a cylinder provided with a bore;
a plunger reciprocally slidably fitted into the cylindrical hole of the cylinder;
a lifter that reciprocates with the rotation of the drive cam and interlocks with the plunger to reciprocate;
A high-pressure pump comprising: a lifter guide that accommodates the lifter in an accommodation hole and guides the reciprocating movement of the lifter,
further comprising a damping resin layer provided on at least one of a vibration source and a vibration transmission path in the high-pressure pump;
A high-pressure pump, wherein the damping resin layer contains a heat-resistant resin and a damping filler that converts vibration energy into heat energy.
前記制振樹脂層として、前記フランジ部における被取付け部材と対向する締結面及び前記締結面と反対側の座面の少なくとも一方に設けられた制振樹脂層を備える請求項１から３のいずれか一項に記載の高圧ポンプ。 a lower housing having a cylinder holding portion positioned radially outward of the cylinder and a flange portion projecting radially outward from the cylinder holding portion and supporting the cylinder;
4. The damping resin layer according to any one of claims 1 to 3, wherein the damping resin layer is provided on at least one of a fastening surface of the flange portion facing the member to be attached and a seating surface opposite to the fastening surface. 1. The high-pressure pump according to item 1.