JP2023050959A - surgical sheet - Google Patents
surgical sheet Download PDFInfo
- Publication number
- JP2023050959A JP2023050959A JP2021161348A JP2021161348A JP2023050959A JP 2023050959 A JP2023050959 A JP 2023050959A JP 2021161348 A JP2021161348 A JP 2021161348A JP 2021161348 A JP2021161348 A JP 2021161348A JP 2023050959 A JP2023050959 A JP 2023050959A
- Authority
- JP
- Japan
- Prior art keywords
- fiber layer
- surgical sheet
- layer
- surgical
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本願発明は、手術用シートに関する。特には、手術時に人体（患者）の覆布として好適に使用できる他、患者が横たわる手術台のカバーとして、また、手術時の医療機器の汚染を防ぐための覆布や下敷きとしても好適に使用できる、手術用シートに関する。 The present invention relates to surgical sheets. In particular, it can be suitably used as a cover cloth for the human body (patient) during surgery, as a cover for the operating table on which the patient lies, and as a cover cloth or underlay to prevent contamination of medical equipment during surgery. It relates to surgical sheets.
従来から手術時には、手術を受ける患者の血液や体液等によって施術者等が感染又は汚染される危険を低減するために、また、患者の血液や体液等および手術に使用する薬液等の液体が床面へ滴り落ちるのを回避するために、手術を受ける患者を布で覆った状態で手術が行なわれている。 Conventionally, at the time of surgery, in order to reduce the risk of the operator being infected or contaminated by the patient's blood or body fluids, etc., the patient's blood, body fluids, etc. To avoid dripping onto the surface, surgery is performed with a cloth covering the patient undergoing surgery.
このような覆布として、例えば、特開２０１２－２２３３７９号公報（特許文献１）には、スパンボンド不織布とポリオレフィン系フィルムとを貼り合せた手術用資材が提案されている。しかしながら、このような手術用資材を用いたとしても、上述した液体が床面へ滴り落ちるのを充分に回避することができず、施術者等の感染又は汚染の危険に加えて手術時に施術者等が踏み滑る危険があった。 As such a cover cloth, for example, Japanese Patent Application Laid-Open No. 2012-223379 (Patent Document 1) proposes a surgical material obtained by bonding a spunbond nonwoven fabric and a polyolefin film. However, even if such surgical materials are used, it is not possible to sufficiently prevent the above-mentioned liquid from dripping onto the floor surface, and in addition to the risk of infection or contamination of the operator, etc., the operator during surgery There was a danger of slipping.
こういった問題を解決可能な手術用シートとして、例えば、特開２０２０－６９２９８号公報（特許文献２）には、繊維が一方向に配向した一方向配向層を有する不織布由来の繊維層とフィルム層とが接着一体化してなる手術用シートが提案されている。当該構成の不織布を備えた手術用シートを用いると共に、当該手術用シートにおける一方向配向層の繊維が配向する一方向と、人体（患者）の上下方向が略一致するようにして当該手術用シートで人体を覆い使用することで、人体の血液や体液等を、手術用シートにおける人体の上下方向へ誘導し拡散して床面へ滴り落ち難くできることが開示されている。 As a surgical sheet that can solve such problems, for example, Japanese Patent Application Laid-Open No. 2020-69298 (Patent Document 2) discloses a fiber layer and a film derived from a nonwoven fabric having a unidirectionally oriented layer in which fibers are oriented in one direction. A surgical sheet has been proposed in which layers are adhered and integrated. A surgical sheet comprising a nonwoven fabric having such a configuration is used, and the surgical sheet is arranged so that one direction in which the fibers of the unidirectionally oriented layer of the surgical sheet are oriented substantially coincides with the vertical direction of the human body (patient). It is disclosed that by covering the human body with the sheet, the blood, body fluids, etc. of the human body can be guided and diffused in the vertical direction of the human body on the surgical sheet, making it difficult for them to drip onto the floor surface.
しかし、特許文献２に開示されている発明において、当該繊維の配向方向へ血液や体液等を誘導して血液や体液等が床面へ滴り落ちるのを回避するために、手術用シートは必ず一方向配向層を有する不織布（特定の一方向に繊維配向を有する不織布）を備えていなければならない。 However, in the invention disclosed in Patent Document 2, in order to guide blood, body fluids, etc. in the orientation direction of the fibers and avoid dripping of the blood, body fluids, etc. onto the floor surface, the surgical sheet must always be one piece. It must have a nonwoven fabric with a directional orientation layer (nonwoven fabric with fiber orientation in one specific direction).
一方、不織布はその種類によっては、特定の一方向に繊維配向を有していないものがある。具体的には、繊維をニードルを用いて絡合してなる乾式不織布、繊維を水流を用いて絡合してなる水流絡合不織布、繊維を湿式抄造してなる湿式不織布、静電紡糸法やメルトブロー法、スパンボンド法などを用いて調製した不織布などは、特定の一方向に繊維配向を有していないことがある。そのため従来技術を用いる限りでは、特定の一方向に繊維配向を有する不織布を用いることなく、血液や体液等が床面へ滴り落ちるのを回避可能な手術用シートを実現できなかった。 On the other hand, some types of nonwoven fabrics do not have fibers oriented in a specific direction. Specifically, dry nonwoven fabrics obtained by entangling fibers using needles, hydroentangled nonwoven fabrics obtained by entangling fibers using water flow, wet nonwoven fabrics obtained by wet papermaking of fibers, electrostatic spinning methods, Non-woven fabrics prepared by using the meltblown method, spunbond method, etc. may not have fiber orientation in one specific direction. Therefore, as long as the conventional technology is used, it has not been possible to realize a surgical sheet capable of avoiding dripping of blood, bodily fluids, etc. onto the floor surface without using a nonwoven fabric having fibers oriented in a specific direction.
本願発明では、繊維層における繊維配向などの態様を問わず、床と平行をなし手術台などに寝た状態にある人体（患者）（以降、「人体」と略すことがある）の血液や体液等および手術に使用する薬液等の液体を誘導し拡散して、当該液体が床面へ滴り落ちるのを回避可能な、繊維層とフィルム層を有する積層体を備えた手術用シートを提供することを目的とする。 In the present invention, the blood and body fluids of a human body (patient) (hereinafter sometimes abbreviated as "human body") lying parallel to the floor and lying on an operating table, etc., regardless of the mode of fiber orientation in the fiber layer To provide a surgical sheet comprising a laminate having a fiber layer and a film layer, which guides and diffuses a liquid such as a medical solution used in surgery to prevent the liquid from dripping onto a floor surface. With the goal.
本願発明は、
「（請求項１）繊維層とフィルム層を有する積層体を備えた、手術用シートであって、
前記繊維層と前記フィルム層は部分的に接着一体化しており、
前記部分的に接着一体化している箇所は、前記繊維層の主面と平行を成す一方向に配向を有して存在している、
手術用シート。
（請求項２）前記フィルム層側を人体側へ向けると共に、前記部分的に接着一体化している箇所が配向する方向と、人体の上下方向とが略一致するように人体を覆って使用する、請求項１に記載の手術用シート。」
である。
The claimed invention is
"(Claim 1) A surgical sheet comprising a laminate having a fiber layer and a film layer,
The fiber layer and the film layer are partially bonded and integrated,
The partially bonded and integrated portions are oriented in one direction parallel to the main surface of the fiber layer,
surgical sheet.
(Claim 2) The film layer side is directed toward the human body, and the human body is covered so that the direction in which the partially bonded and integrated parts are oriented substantially coincides with the vertical direction of the human body. The surgical sheet according to claim 1. ”
is.
本願出願人は、繊維層とフィルム層を有する積層体を備えた手術用シートについて、その繊維層とフィルム層が接着一体化している態様に着目した。そして、繊維層とフィルム層が部分的に接着一体化していると共に、その接着一体化している箇所が、繊維層の主面と平行を成す一方向に配向を有する形状で存在している手術用シートは、人体の血液や体液等および手術に使用する薬液等の液体を、当該一方向へ効果的に誘導し拡散できることを見出した。 The applicant of the present application focused on a surgical sheet having a laminate having a fiber layer and a film layer, in which the fiber layer and the film layer are bonded and integrated. Then, the fiber layer and the film layer are partially bonded and integrated, and the bonded and integrated portion exists in a shape having orientation in one direction parallel to the main surface of the fiber layer. It was found that the sheet can effectively guide and diffuse the blood, body fluids, etc. of the human body and liquids such as medical solutions used in surgery in the one direction.
そのため、本願発明にかかる手術用シートにおける、前記部分的に接着一体化している箇所が配向を有する方向（前記繊維層の主面と平行を成す前記一方向）と、人体の上下方向が略一致するようにして、本願発明にかかる手術用シートで人体を覆い使用することで、人体の血液や体液等および手術に使用する薬液等の液体を、手術用シートにおける人体の上下方向へ誘導し拡散して、床面へ滴り落ちるのを回避できることを見出した。 Therefore, in the surgical sheet according to the present invention, the direction in which the partially bonded and integrated portions are oriented (the one direction parallel to the main surface of the fiber layer) substantially coincides with the vertical direction of the human body. By covering the human body with the surgical sheet according to the present invention, blood, body fluids, etc. of the human body and liquids such as medical fluids used in surgery are guided and diffused in the vertical direction of the human body on the surgical sheet. It was found that dripping onto the floor can be avoided by doing so.
本願発明では、例えば以下の構成など、各種構成を適宜選択できる。なお、本願発明で説明する各種測定は特に記載や規定のない限り、常圧のもと２５℃温度条件下で測定を行った。そして、本願発明で説明する各種測定結果は特に記載や規定のない限り、求める値よりも一桁小さな値まで測定で求め、当該値を四捨五入することで求める値を算出した。具体例として、小数第一位までが求める値である場合、測定によって小数第二位まで値を求め、得られた小数第二位の値を四捨五入することで小数第一位までの値を算出し、この値を求める値とした。また、本願発明で例示する各上限値および各下限値は、任意に組み合わせることができる。 In the present invention, various configurations such as the following configurations can be appropriately selected. Various measurements described in the present invention were performed under normal pressure and at a temperature of 25° C., unless otherwise specified. Unless otherwise specified or specified, the various measurement results described in the present invention were obtained by measurement to a value one digit smaller than the desired value, and the value was calculated by rounding off the value. As a specific example, if the value to be obtained is to the first decimal place, the value to the second decimal place is obtained by measurement, and the value to the first decimal place is calculated by rounding off the obtained value to the second decimal place. and this value was used as the desired value. Moreover, each upper limit value and each lower limit value illustrated by this invention can be combined arbitrarily.
本願発明にかかる手術用シートが備える繊維層は、主に、人体の血液や体液等および手術に使用する薬液等の液体（以降、液体と略すことがある）を吸収する役割を担う。 The fiber layer included in the surgical sheet according to the present invention mainly serves to absorb liquids such as human blood, body fluids, and medical fluids used in surgery (hereinafter sometimes abbreviated as liquids).
繊維層は、その構成繊維同士が絡み合い形成されたシート状の層であって、繊維ウェブや不織布由来の構成繊維がランダムあるいは繊維配向を有するように絡み合ってなる繊維の層であっても、織物や編物由来の構成繊維が規則的に絡み合ってなる繊維の層であってもよい。しかし、より多量の液体を吸収できるよう、繊維層は繊維ウェブや不織布由来の構成繊維がランダムあるいは繊維配向を有するように絡み合ってなる繊維の層であるのが好ましい。 The fiber layer is a sheet-like layer formed by entangling its constituent fibers, and even if it is a fiber layer in which constituent fibers derived from a fiber web or nonwoven fabric are entangled so that they have a random or fiber orientation, it can be used as a woven fabric. It may be a layer of fibers in which constituent fibers derived from a knitted fabric are regularly entangled. However, in order to absorb a larger amount of liquid, the fiber layer is preferably a fiber layer in which constituent fibers derived from a fiber web or nonwoven fabric are entangled so as to have random or fiber orientation.
繊維層が構成繊維として含む繊維の種類は適宜選択できる。しかし、より多量の液体を吸収できるよう、繊維層は構成繊維として、例えば、レーヨン、キュプラなどの再生繊維；アセテートなどの半合成繊維；ナイロン、ビニロン、ビニリデン、ポリ塩化ビニル、ポリエステル、アクリル、ポリオレフィン（ポリプロピレン、ポリエチレンなど）、ポリウレタンなどの単一樹脂からなる、又はこれら樹脂を２種類以上含む合成繊維；綿、麻などの植物繊維；羊毛、絹などの動物繊維；などを単独で、又は２種類以上を含むのが好ましい。これらの中でも、レーヨン、キュプラ、アセテート、ナイロン、ビニロン、綿、麻、羊毛、絹などの公定水分率が４％以上の親水性繊維を含んでいるのが好ましい。なお、公定水分率が４％未満の非親水性繊維（例えば、ポリエステル繊維）に親水性を付与した親水性繊維も好適に使用できる。例えば、スルホン化処理、フッ素ガス処理、ビニルモノマーのグラフト重合処理、放電処理、界面活性剤付与処理、或いは親水性樹脂付与処理等により、非親水性繊維を親水性繊維とすることができる。理由は定かではないが、界面活性剤付与処理において、イオン性の異なる２種類以上の界面活性剤が付与された親水性繊維は、体液等に含まれる様々なイオン成分とイオン的に馴染みやすいためか、血液や体液等を保持し易く好適である。界面活性剤はイオン性が異なるアニオン系、カチオン系、ノニオン系、両性イオン系の中から選ばれる界面活性剤を１種類、又は２種類以上組み合わせて非親水性繊維へ付与し、親水性繊維とすることができる。 The type of fibers contained as constituent fibers in the fiber layer can be appropriately selected. However, in order to absorb a larger amount of liquid, the fiber layer is composed of fibers such as recycled fibers such as rayon and cupra; semi-synthetic fibers such as acetate; nylon, vinylon, vinylidene, polyvinyl chloride, polyester, acrylic, and polyolefin. (polypropylene, polyethylene, etc.), synthetic fibers made of a single resin such as polyurethane, or containing two or more of these resins; vegetable fibers such as cotton and hemp; animal fibers such as wool and silk; It is preferable to include more than one type. Among these, it is preferable that hydrophilic fibers such as rayon, cupra, acetate, nylon, vinylon, cotton, hemp, wool, and silk having an official moisture content of 4% or more are included. Hydrophilic fibers obtained by imparting hydrophilicity to non-hydrophilic fibers (for example, polyester fibers) having an official moisture content of less than 4% can also be suitably used. For example, non-hydrophilic fibers can be made hydrophilic fibers by sulfonation treatment, fluorine gas treatment, vinyl monomer graft polymerization treatment, discharge treatment, surfactant imparting treatment, or hydrophilic resin imparting treatment. Although the reason is not clear, hydrophilic fibers to which two or more types of surfactants with different ionic properties are applied in the surfactant application treatment are ionically compatible with various ionic components contained in body fluids. Moreover, it is suitable for easily holding blood, body fluids, and the like. Surfactants are selected from anionic, cationic, nonionic, and zwitterionic surfactants with different ionic properties. can do.
また、非親水性繊維に界面活性剤を付与した親水性繊維の中でも、非親水性繊維がポリエステル繊維であると、耐熱性、耐候性、耐薬品性などに優れているため、手術用シートの使用環境や保管環境の影響を受けることなく、液体の吸収性等の品質を維持しやすい。また、ポリエステル繊維はレーヨン繊維などの原始的に親水性を有する繊維のように繊維中に血液や体液等を取り込まず、長時間の手術において手術用シートが吸収と乾燥を繰り返しても、シワなどが発生しにくく、形態を維持でき、良好な使用感が得られるため好適である。 In addition, among hydrophilic fibers in which a surfactant is added to non-hydrophilic fibers, if the non-hydrophilic fibers are polyester fibers, they are excellent in heat resistance, weather resistance, chemical resistance, etc., so they are suitable for surgical sheets. It is easy to maintain quality such as liquid absorbency without being affected by usage and storage environments. In addition, polyester fibers do not absorb blood and body fluids like rayon fibers and other naturally hydrophilic fibers. It is suitable because it is difficult to generate , the shape can be maintained, and a good feeling of use can be obtained.
上述した効果に優れるように、繊維層の構成繊維の質量中に占める、親水性繊維（非親水性繊維に親水性を付与した親水性繊維を含む、以下同様）の質量の百分率は、３０ｍａｓｓ％以上であるのが好ましく、６０ｍａｓｓ％以上であるのがより好ましく、９０ｍａｓｓ％以上であるのがより好ましく、１００ｍａｓｓ％であるのが最も好ましい。 In order to achieve the above effects, the percentage of the mass of hydrophilic fibers (including hydrophilic fibers imparting hydrophilicity to non-hydrophilic fibers, the same shall apply hereinafter) in the mass of constituent fibers of the fiber layer is 30 mass%. It is preferably 60 mass % or more, more preferably 90 mass % or more, and most preferably 100 mass %.
繊維層を構成する繊維の繊度や繊維長は、適宜調整できる。繊度は、繊維間空隙に富み多量の液体を吸収できる繊維層を備えた手術用シートを実現できるよう、０．５ｄｔｅｘ以上であるのが好ましく、０．８ｄｔｅｘ以上であるのがより好ましい。他方で、繊度が大き過ぎると、液体を保液し難い傾向があることから、１０ｄｔｅｘ以下であるのが好ましく、７ｄｔｅｘ以下であるのがより好ましい。また、ＳＭＳ不織布のように、複数の異なる繊度の繊維を、複合した繊維層とすることもできる。 The fineness and fiber length of the fibers constituting the fiber layer can be adjusted as appropriate. The fineness is preferably 0.5 dtex or more, more preferably 0.8 dtex or more so as to realize a surgical sheet having a fiber layer rich in inter-fiber voids and capable of absorbing a large amount of liquid. On the other hand, if the fineness is too large, it tends to be difficult to retain the liquid, so it is preferably 10 dtex or less, more preferably 7 dtex or less. Also, like SMS nonwoven fabric, a plurality of fibers with different finenesses can be combined into a fiber layer.
繊維長は、繊維層としての形態を保持し、より多量の液体を吸収できるよう２５ｍｍ以上であるのが好ましく、３５ｍｍ以上であるのがより好ましい。短繊維を用いる場合には、繊維長が長過ぎると地合いが悪くなり液体の吸収にムラがでる傾向があることから、１１０ｍｍ以下であるのが好ましく、８０ｍｍ以下であるのがより好ましい。なお、メルトブロー法やスパンボンド法などの長繊維も用いる事ができる。 The fiber length is preferably 25 mm or more, more preferably 35 mm or more, so that the fiber layer can retain its shape and absorb a larger amount of liquid. When short fibers are used, the fiber length is preferably 110 mm or less, and more preferably 80 mm or less, because if the fiber length is too long, the texture tends to deteriorate and liquid absorption tends to be uneven. It is also possible to use long fibers obtained by the meltblown method, the spunbond method, or the like.
本願発明にかかる繊維層の構成繊維は、例えば、水流などの流体流やニードルによる絡合、構成繊維の融着やバインダによる接着により結合していることができる。これらの中でも、絡合により構成繊維同士が結合していると、繊維層表面に微細な凹凸が形成されていることから光を乱反射しやすく、手術時における施術者等の目の疲れを低減させることができる手術用シートを実現できるため好適である。特に、水流などの流体流により絡合してなる繊維ウェブあるいは不織布由来の繊維層は、繊維に付着した汚染物質が洗い流されているため衛生的に優れており、手術用シートの繊維層として好適である。 The constituent fibers of the fiber layer according to the present invention can be bound by, for example, entanglement by fluid flow such as water flow, needles, fusion bonding of constituent fibers, or adhesion by a binder. Among these, if the constituent fibers are bonded to each other by entanglement, fine unevenness is formed on the surface of the fiber layer, so that light is easily reflected diffusely, reducing eye fatigue of the operator during surgery. It is suitable because it can realize a surgical sheet that can In particular, a fiber web or a fiber layer derived from a non-woven fabric, which is entangled by a fluid flow such as water flow, is sanitary because contaminants adhering to the fibers are washed away, and is suitable as a fiber layer for surgical sheets. is.
繊維層の繊維配向は適宜選択できる。例えば、一方向（例えば、搬送方向と平行を成す方向）へ繊維が配向している繊維層（例えば一方向ウェブ由来の繊維層）、繊維が配向している層が複数積層してなる繊維層（例えばクロスレイウェブ由来の繊維層やクリスクロスウェブ由来の繊維層）、特定の繊維配向を有していない繊維層（例えばランダムウェブ由来の繊維層）であることができる。特に、繊維の配向が揃っていないことで、繊維が立体的に構成され、より多量の液体を吸収できると共に、手術用シートにおける人体の上下方向へ誘導し拡散して、床面へ滴り落ちるのを回避できるよう、繊維が配向している層が複数積層してなる繊維層、あるいは、特定の繊維配向を有していない繊維層を備えた手術用シートであるのが好ましい。 The fiber orientation of the fiber layer can be appropriately selected. For example, a fiber layer in which fibers are oriented in one direction (for example, a direction parallel to the conveying direction) (for example, a fiber layer derived from a unidirectional web), a fiber layer in which multiple layers in which fibers are oriented are laminated (for example, a fibrous layer derived from a crosslay web or a fibrous layer derived from a criss-cross web), or a fibrous layer having no specific fiber orientation (eg, a fibrous layer derived from a random web). In particular, since the orientation of the fibers is not uniform, the fibers are structured three-dimensionally and can absorb a larger amount of liquid. In order to avoid this, it is preferable that the surgical sheet is provided with a fiber layer formed by laminating a plurality of layers with oriented fibers or a fiber layer with no specific fiber orientation.
繊維層の目付や厚さは特に限定するものではないが、目付や厚さが大き過ぎるとドレープ性を損なって使用感が低下する傾向にある。一方で、目付や厚さが小さ過ぎると多量の液体を吸収し保持し難くなる恐れがある。そのため、目付は１５～２００ｇ／ｍ２であるのが好ましく、３０～１００ｇ／ｍ２であるのがより好ましい。本願発明における、「目付」は１ｍ２あたりの質量であり、ＪＩＳ Ｌ１０８５：１９９８、６．２「単位面積当たりの質量」に規定する方法により得られる。また、厚さは０．１～３．０ｍｍであるのが好ましく、０．２～１．５ｍｍであるのがより好ましい。「厚さ」は、基材の主面に対して、面積５ｃｍ２あたり厚さ方向へ０．９８Ｎ（＝１００ｇｆ）を荷重して行う荷重領域における厚さの測定を、無作為に選択した５カ所で実施し、それら厚さを算術平均した値を意味する。このような厚さの測定は、例えば、高精度デジタル測長機（株式会社ミツトヨ社製、ライトマチック（登録商標））により実施できる。 The basis weight and thickness of the fiber layer are not particularly limited, but if the basis weight and thickness are too large, the drape property is impaired and the feeling of use tends to deteriorate. On the other hand, if the basis weight and thickness are too small, it may become difficult to absorb and retain a large amount of liquid. Therefore, the basis weight is preferably 15-200 g/m 2 , more preferably 30-100 g/m 2 . In the present invention, the "basis weight" is the mass per square meter , which is obtained by the method defined in JIS L1085:1998, 6.2 "mass per unit area". Also, the thickness is preferably 0.1 to 3.0 mm, more preferably 0.2 to 1.5 mm. "Thickness" is a randomly selected measurement of the thickness in the load area by applying a load of 0.98 N (= 100 gf) in the thickness direction per 5 cm 2 area to the main surface of the base material. Arithmetic mean value of the thicknesses of the thicknesses measured at each location. Such thickness measurement can be performed, for example, by a high-precision digital length measuring machine (Lightmatic (registered trademark) manufactured by Mitutoyo Corporation).
本願発明にかかる手術用シートが備えるフィルム層は、主に、液体が手術用シートにおけるフィルム層側に漏出し人体と接触することがないようにする役割を担う。フィルム層はフィルム由来の層であっても、繊維層を構成可能な布帛（繊維ウェブや不織布、織物や編物）の主面に溶融した樹脂や樹脂溶液が付与されることで形成されてなる、繊維層上に形成された薄膜状の樹脂由来の層であってもよい。 The film layer included in the surgical sheet according to the present invention mainly plays a role of preventing liquid from leaking to the film layer side of the surgical sheet and coming into contact with the human body. Even if the film layer is a film-derived layer, it is formed by applying a molten resin or resin solution to the main surface of a fabric (fiber web, nonwoven fabric, woven fabric, or knitted fabric) that can constitute the fiber layer. It may be a thin resin-derived layer formed on the fiber layer.
このフィルム層を構成する素材は特に限定するものではないが、例えば、ポリプロピレン、ポリエチレンなどのポリオレフィン系樹脂；ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリカーボネートなどのポリエステル系樹脂；ポリ塩化ビニル、ポリエーテルエーテルケトン、塩素化ポリ塩化ビニル等の樹脂等のフィルムに形成可能な有機高分子から構成することができる。また、シリコーン樹脂のような、無機成分を含有する樹脂から構成することもできる。 The material constituting the film layer is not particularly limited, but examples include polyolefin resins such as polypropylene and polyethylene; polyester resins such as polyethylene terephthalate, polybutylene terephthalate and polycarbonate; polyvinyl chloride, polyether ether ketone, It can be composed of an organic polymer that can be formed into a film, such as a resin such as chlorinated polyvinyl chloride. It can also be made of a resin containing an inorganic component, such as a silicone resin.
フィルム層の目付や厚さは特に限定するものではないが、目付や厚さが大き過ぎるとドレープ性を損なって使用感が低下する傾向にある。一方で、目付や厚さが小さ過ぎると、液体が手術用シートにおけるフィルム層側に漏出する恐れがある。そのため、目付は５～６０ｇ／ｍ２であることができ、１０～４０ｇ／ｍ２であることができる。また、厚さは０．００５～１ｍｍであることができ、０．０１～０．５ｍｍであることができ、０．０１５～０．１ｍｍであることができる。 The basis weight and thickness of the film layer are not particularly limited. On the other hand, if the basis weight and thickness are too small, the liquid may leak to the film layer side of the surgical sheet. As such, the basis weight can be from 5 to 60 g/m 2 and can be from 10 to 40 g/m 2 . Also, the thickness can be 0.005-1 mm, can be 0.01-0.5 mm, and can be 0.015-0.1 mm.
本願発明にかかる手術用シートが備える積層体において、繊維層とフィルム層は部分的に接着一体化している。繊維層とフィルム層とが接着一体化してなる積層体を調製する方法は適宜選択可能だが、例えば、ドライラミネート法、押出しラミネート法、ホットメルトラミネート法、ウェットラミネート法、ワックスラミネート法、或いはサーマルラミネート法を採用できる。例えば、繊維層を構成可能な布帛の主面上に、フィルム層を構成可能な樹脂を溶融させた状態や当該樹脂の溶液の状態で、繊維層と当該薄膜状の樹脂が部分的に接触しているようにして、薄膜状に付与することで本願発明にかかる積層体を調製できる。あるいは、繊維層を構成可能な布帛と、フィルム層を構成可能なフィルムとを、樹脂溶液や樹脂分散液あるいは溶融した樹脂を用いて部分的に接着一体化してなる積層体や、ヒートシールや超音波溶着などの接着処理などを用いて部分的に接着一体化してなる積層体あってもよい。 In the laminate of the surgical sheet according to the present invention, the fiber layer and the film layer are partially bonded and integrated. A method for preparing a laminate formed by bonding and integrating a fiber layer and a film layer can be appropriately selected. Law can be adopted. For example, on the main surface of the fabric capable of forming the fiber layer, the fiber layer and the thin-film resin are partially in contact with each other in a state in which the resin capable of forming the film layer is melted or in the state of a solution of the resin. The layered product according to the present invention can be prepared by applying it in the form of a thin film as described above. Alternatively, a laminate obtained by partially bonding and integrating a fabric capable of forming a fiber layer and a film capable of forming a film layer using a resin solution, a resin dispersion, or a melted resin, a heat seal or a super There may be a laminated body that is partially bonded and integrated by using an adhesive treatment such as sonic welding.
樹脂付着量も適宜選択可能であるが、付着量が多過ぎると、繊維層側の繊維空隙や、全体的な風合いに影響する為、３０ｇ／ｍ2以下が好ましく、２０ｇ／ｍ2以下が好ましく、１０ｇ／ｍ2以下が好ましい。また、付着量が少な過ぎると、十分な接着力が得られない為、０．１ｇ／ｍ2以上が好ましく、０．５ｇ／ｍ2以上が好ましく、１ｇ／ｍ2以上が好ましい。 The resin adhesion amount can also be selected appropriately, but if the adhesion amount is too large, it affects the fiber voids on the fiber layer side and the overall texture, so it is preferably 30 g/m 2 or less, preferably 20 g/m 2 or less. , 10 g/m 2 or less. On the other hand, if the adhesion amount is too small, sufficient adhesive strength cannot be obtained, so it is preferably 0.1 g/m 2 or more, preferably 0.5 g/m 2 or more, and preferably 1 g/m 2 or more.
ホットメルトラミネート法は、接着一体化の箇所の形状（例えば、直線状、波線状、破線状、など）を変える事が、比較的容易であり、また、サーマルラミネートなどと比較して、繊維層側の形態（例えば、厚み、繊維配向など）に影響を与えずに、接着一体化ができるため、好ましい。ホットメルトラミネート法で使用するホットメルト樹脂量（樹脂付着量）は適宜選択可能である。 In the hot melt lamination method, it is relatively easy to change the shape (for example, straight line, wavy line, dashed line, etc.) of the part of adhesion integration, and compared with thermal lamination, the fiber layer It is preferable because it can be bonded and integrated without affecting the shape of the side (for example, thickness, fiber orientation, etc.). The hot-melt resin amount (resin adhesion amount) used in the hot-melt lamination method can be appropriately selected.
本願発明にかかる積層体は、繊維層とフィルム層が対面している層間において、繊維層とフィルム層が接着一体化している箇所を有している。そして、積層体における繊維層とフィルム層が対面している層間の全てにおいて、繊維層とフィルム層とが接着一体化しているものではなく、当該層間には繊維層とフィルム層とが接着一体化している箇所と、接着一体化していない箇所が存在している。そして、当該繊維層とフィルム層の接着一体化している箇所が、前記繊維層の主面と平行を成す一方向に配向を有する形状で存在していることを特徴としている。 The laminate according to the present invention has a portion where the fiber layer and the film layer are bonded and integrated between the layers where the fiber layer and the film layer face each other. The fiber layer and the film layer are not bonded and integrated in all the layers in the laminate where the fiber layer and the film layer face each other, but the fiber layer and the film layer are bonded and integrated between the layers. There are places where the adhesive is not integrated and places where the adhesive is not integrated. Further, it is characterized in that the portion where the fiber layer and the film layer are bonded and integrated exists in a shape oriented in one direction parallel to the main surface of the fiber layer.
ここでいう、繊維層とフィルム層とが接着一体化している箇所が、繊維層の主面と平行を成す一方向（例えば、手術用シートの使用時における人体の上下方向と平行をなす方向）に配向を有する形状であるか否かは、以下の方法で判断できる。 The part where the fiber layer and the film layer are bonded together is in one direction parallel to the main surface of the fiber layer (for example, the direction parallel to the vertical direction of the human body when using the surgical sheet). The following method can be used to determine whether or not the shape has an orientation in the direction.
（１）繊維層とフィルム層を有する積層体を備えた手術用シートであって、前記繊維層と前記フィルム層が部分的に接着一体化している箇所を有する手術用シートを用意する。あるいは、手術用シートを構成する繊維層とフィルム層を有する積層体であって、前記繊維層と前記フィルム層が部分的に接着一体化している箇所を有する積層体を用意する。
（２）用意した手術用シートあるいは積層体から、一辺２０ｃｍの正方形形状の試料を採取する。
（３）試料における繊維層が露出している主面、あるいは、当該試料から繊維層を剥がした後の主面の写真を撮影する。このとき、試料における一方の主面全てが写るように写真を撮影する。
（４）撮影した写真上に、当該主面を横断する複数の直線を引く。
（５）当該引いた複数の直線のうち、撮影した写真上から確認できる、繊維層とフィルム層が部分的に接着一体化している箇所と交わる部分の長さが、最も長い直線Ａを選出する。
（６）このとき、測定に使用した手術用シート、あるいは、測定に使用した積層体を備えた手術用シートが有する、繊維層とフィルム層が部分的に接着一体化している箇所は、当該直線Ａと平行を成す方向に対して配向を有している（繊維層の主面と平行を成す一方向に配向を有する形状で存在している）と判断できる。
(1) Prepare a surgical sheet having a laminated body having a fiber layer and a film layer, the surgical sheet having a part where the fiber layer and the film layer are partially bonded and integrated. Alternatively, a laminate having a fiber layer and a film layer constituting a surgical sheet and having a portion where the fiber layer and the film layer are partially bonded and integrated is prepared.
(2) A square sample of 20 cm on each side is taken from the prepared surgical sheet or laminate.
(3) Take a photograph of the main surface of the sample where the fiber layer is exposed, or the main surface of the sample after the fiber layer has been peeled off. At this time, a photograph is taken so that one main surface of the sample can be captured.
(4) Draw a plurality of straight lines across the main surface on the photographed photograph.
(5) Among the plurality of drawn straight lines, select straight line A that has the longest length of the part that intersects with the part where the fiber layer and the film layer are partially bonded and integrated, which can be confirmed from the photographed photograph. .
(6) At this time, the part where the fiber layer and the film layer of the surgical sheet used for measurement or the surgical sheet with the laminate used for measurement are partially bonded and integrated is the straight line It can be determined that the fibers are oriented in a direction parallel to A (existing in a shape oriented in one direction parallel to the main surface of the fiber layer).
このような、繊維層とフィルム層が部分的に接着一体化している箇所の形状として、直線形状、波線形状、直線や波線の破線状、それ以外にも、四角形（長方形や正方形など）や円形（円や楕円形）あるいは不定形などの図柄が一方向へ並んでいる図形などを挙げることができる。 The shape of the part where the fiber layer and the film layer are partially bonded and integrated may be a linear shape, a wavy line shape, a dashed line shape of straight or wavy lines, or a quadrangle (rectangle, square, etc.) or a circle. (circle or ellipse) or indeterminate figures arranged in one direction.
また、上述した方法で求めた直線Ａと平行をなす方向、あるいは、当該直線Ａと０°より大きく３０°以下の鋭角を成す方向へ向かい伸び存在する態様で、他にも繊維層とフィルム層が部分的に接着一体化している他の箇所を有していてもよい。このような態様で存在する繊維層とフィルム層が部分的に接着一体化している他の箇所もまた、当該直線Ａと平行を成す方向に対して配向を有している（繊維層の主面と平行を成す一方向に配向を有する形状で存在している）と判断できる。 In addition, in a mode in which it extends in a direction parallel to the straight line A obtained by the above method, or in a direction forming an acute angle of 0 ° or more and 30 ° or less with the straight line A, there are other fiber layers and film layers. may have other locations where it is partially adhered and integrated. Other portions where the fiber layer and the film layer that exist in such a manner are partially bonded and integrated also have an orientation in a direction parallel to the straight line A (main surface of the fiber layer It can be judged that it exists in a shape having an orientation in one direction parallel to ).
このような、繊維層とフィルム層が部分的に接着一体化している他の箇所の形状として、直線形状、波線形状、直線や波線の破線状、それ以外にも、四角形（長方形や正方形など）や円形（円や楕円形）あるいは不定形などの図柄が一方向へ並んでいる図形などを挙げることができる。 Other shapes where the fiber layer and the film layer are partially bonded and integrated include a linear shape, a wavy line shape, a broken line shape of straight lines and wavy lines, and other shapes such as a quadrangle (rectangle, square, etc.). , circles (circles and ovals), irregular shapes, and other patterns are arranged in one direction.
なお、上述のようにして撮影した写真上から確認した際に、主面全てで繊維層とフィルム層が接着一体化している場合や、繊維層とフィルム層が接着一体化している箇所が主面上で均等に分布して存在している場合（ピンドット状に分布して存在している場合など）、これらの手術用シートあるいは積層体は、本願発明の構成（部分的に接着一体化している箇所は、繊維層の主面と平行を成す一方向に配向を有して存在している）を満足するものではない。 In addition, when checking from the photograph taken as described above, if the fiber layer and the film layer are bonded and integrated on the entire main surface, or if the fiber layer and the film layer are bonded and integrated, the main surface When evenly distributed on the surface (such as when distributed in a pin-dot shape), these surgical sheets or laminates have the configuration of the present invention (partially bonded and integrated are oriented in one direction parallel to the main surface of the fiber layer) is not satisfied.
繊維層とフィルム層が接着一体化している箇所の総数に占める、繊維層の主面と平行を成す一方向に配向を有する形状で存在している箇所の数の百分率は、適宜調整できる。しかし、液体を当該一方向へ効果的に誘導し拡散できるよう、いずれの箇所も繊維層の主面と平行を成す一方向に配向を有する形状で存在しているのが好ましい。 The percentage of the number of locations oriented in one direction parallel to the main surface of the fiber layer to the total number of locations where the fiber layer and the film layer are bonded together can be adjusted as appropriate. However, in order to effectively guide and diffuse the liquid in the one direction, it is preferable that all the portions are oriented in one direction parallel to the main surface of the fiber layer.
また、本発明にかかる積層体では、繊維層の主面全面が接着一体化することなくフィルム層と接着一体化しているため、フィルム層との接着一体化により生じる、繊維層が有する液体の吸収性能の低下が発生し難い。その結果、本発明にかかる手術用シートは、液体の吸収量に富む。 In addition, in the laminate according to the present invention, since the entire main surface of the fiber layer is bonded and integrated with the film layer without being bonded and integrated, the absorption of liquid contained in the fiber layer caused by bonding and integration with the film layer Performance deterioration is unlikely to occur. As a result, the surgical sheet according to the present invention has a high liquid absorption capacity.
積層体における繊維層とフィルム層が対面している部分に存在する、繊維層とフィルム層とが接着一体化していない箇所の分布態様は適宜調整できる。液体を手術用シートにおける人体の上下方向へ誘導し拡散して、床面へ滴り落ちるのを回避できる手術用シートを提供できるよう適宜調整するが、繊維層の主面と平行を成す一方向に配向を有して存在する、繊維層とフィルム層とが部分的に接着一体化している箇所同士の間隔が、平行を成しているなど等間隔を成し存在しているのが好ましい。 The distribution mode of the portions where the fiber layer and the film layer are not bonded and integrated, which are present in the portion where the fiber layer and the film layer face each other in the laminate, can be appropriately adjusted. The liquid is guided and diffused in the vertical direction of the human body on the surgical sheet, and adjusted appropriately so as to provide a surgical sheet that can avoid dripping onto the floor surface. It is preferable that the oriented portions of the fiber layer and the film layer are partially bonded and integrated with an equal interval such as being parallel to each other.
本願発明にかかる手術用シートは、繊維層とフィルム層を有する積層体のみで構成されているものであっても良いが、 別途用意したカバー材や支持体あるいは機能性材などを積層して手術用シートを調製してもよい。カバー材や支持体あるいは機能性材として、布帛、フィルム（多孔あるいは無孔）、発泡体（多孔あるいは無孔）あるいは機能剤粒子などを用いることができる。 The surgical sheet according to the present invention may be composed only of a laminate having a fiber layer and a film layer. You may prepare a sheet for A cloth, a film (porous or non-porous), a foam (porous or non-porous), functional agent particles, or the like can be used as the cover material, support or functional material.
例えば、不織布とフィルムおよび支持体からなる手術用シートの場合、不織布層／フィルム層／支持体由来の層、の順に積層配置してなる積層体を備える手術用シートであることができる。このような積層状態にあると、新たに設けた支持体由来の層によってフィルム層が人体と接触しないため患者の不快感を抑制することができる。この場合、新たに設けた支持体由来の層の組成は適宜調整でき、本願発明にかかる不織布層と同じであっても異なっていても良い。なお、カバー材や支持体などとの積層態様は適宜調整でき、ただ重ね合わせた態様であっても、バインダやホットメルトウェブあるいは繊維接着によって、または、ヒートシールや超音波溶着などの接着処理へ供することによって層間接着してなる態様であっても良い。 For example, in the case of a surgical sheet comprising a nonwoven fabric, a film and a support, the surgical sheet may be a surgical sheet comprising a laminate in which a nonwoven fabric layer/film layer/layer derived from the support are laminated in this order. In such a laminated state, the film layer does not come into contact with the human body due to the newly provided layer derived from the support, so discomfort to the patient can be suppressed. In this case, the composition of the newly provided layer derived from the support can be adjusted as appropriate, and may be the same as or different from the nonwoven fabric layer according to the present invention. The mode of lamination with the cover material, the support, etc. can be adjusted as appropriate. A mode in which the interlayer is adhered by providing is also possible.
更に、別の態様として、不織布層とフィルム層の間に高吸水性パウダーなどの機能剤粒子などが存在していてもよい。これらの存在によって、機能性に富んだ手術用シートを提供できる。 Furthermore, as another aspect, functional agent particles such as superabsorbent powder may be present between the nonwoven fabric layer and the film layer. Due to the existence of these, it is possible to provide a highly functional surgical sheet.
また、手術用シートの外形は適宜調整でき、特に限定するものではないが、切り抜かれた部分や切れ込みのある部分を有する外形、当該切り抜かれた部分が透明なフィルムに置き換えられた形状などであることができる。例えば、手術用シートの所望箇所を部分的に透明なフィルムで構成することによって、透明なフィルム箇所を通して手術用機器を操作することができる。そのため、患者に加えて手術用機器を一緒に覆うことによって、床面に加えて手術用機器を汚染することなく、手術を実施することができる。 In addition, the outer shape of the surgical sheet can be adjusted as appropriate, and is not particularly limited, but may be an outer shape having a cutout portion or a notched portion, a shape in which the cutout portion is replaced with a transparent film, or the like. be able to. For example, by configuring a desired portion of the surgical sheet with a partially transparent film, surgical instruments can be manipulated through the transparent film portion. Thus, by covering the surgical equipment together in addition to the patient, surgery can be performed without contaminating the surgical equipment in addition to the floor surface.
本願発明にかかる手術用シートで人体を覆い使用する際に、繊維層とフィルム層が部分的に接着一体化してなる箇所の配向している一方向（繊維層の主面と平行を成す一方向）と、人体の上下方向が略一致するようにすることで、人体の血液や体液等および手術に使用する薬液等の液体を、手術用シートにおける人体の上下方向へ誘導し拡散して、床面へ滴り落ちるのを回避できる。ここでいう、「略一致」とは、前記一方向と人体の上下方向（頭と足先を結ぶ方向）のなす角度（鋭角）が３０°以内であることを意味する。 When the surgical sheet according to the present invention is used to cover the human body, one direction in which the fiber layer and the film layer are partially bonded and integrated (one direction parallel to the main surface of the fiber layer ) and the vertical direction of the human body are substantially aligned with each other, the blood, body fluids, etc. of the human body and liquids such as medical fluids used in surgery are guided and diffused in the vertical direction of the human body on the surgical sheet, and are spread on the floor. Avoid dripping onto surfaces. Here, "substantially coincident" means that the angle (acute angle) between the one direction and the vertical direction of the human body (the direction connecting the head and the toes) is within 30°.
また、人体を覆って使用する場合には、手術の操作を実施しやすいように、所望箇所に開口を設けることができ、開口の形状や数は手術内容により適宜調整できる。本願発明の手術用シートはフィルム層を備えているため開口を形成しても、その開口から繊維層の構成繊維が解れにくく、発塵性が低い特徴を有する。 In addition, when used to cover the human body, openings can be provided at desired locations so that surgical operations can be easily performed, and the shape and number of openings can be appropriately adjusted according to the type of surgery. Since the surgical sheet of the present invention has a film layer, even if an opening is formed, the constituent fibers of the fiber layer are less likely to fray from the opening, resulting in low dust generation.
以下に、本願発明の実施例を記載するが、本願発明は以下の実施例に限定されるものではない。 Examples of the present invention are described below, but the present invention is not limited to the following examples.
（水流絡合不織布の準備）
アニオン系界面活性剤及びノニオン系界面活性剤を合計で０．３ｍａｓｓ％付与したポリエステル短繊維（繊度：１．６ｄｔｅｘ、繊維長：５１ｍｍ）１００ｍａｓｓ％を、ローラーカード機によって開繊して、搬送方向に繊維が配向した一方向性繊維ウェブ（目付：１８ｇ／ｍ２）を形成した。
また、アニオン系界面活性剤及びノニオン系界面活性剤を合計で０．３ｍａｓｓ％付与したポリエステル短繊維（繊度：１．６ｄｔｅｘ、繊維長：５１ｍｍ）１００ｍａｓｓ％を、ローラーカード機によって開繊して、一方向性繊維ウェブを形成した後、クロスラッパーにより繊維ウェブの搬送方向に対して交差させるように繊維ウェブを積層して、多方向性繊維ウェブ（目付：１６ｇ／ｍ２）を２枚形成した。
次いで、一方向性繊維ウェブ／多方向性繊維ウェブ／多方向性繊維ウェブの順で、一方向性繊維ウェブの搬送方向と多方向性繊維ウェブが搬送されてきた方向とが一致するように積層した後、多方向性繊維ウェブ側から圧力１３ＭＰａの水流を噴出して繊維同士を絡合し、親水性を有する水流絡合不織布（目付：５０ｇ／ｍ２、厚さ：０．４ｍｍ）を製造した。
このようにして製造した水流絡合不織布は、一方向性繊維ウェブの繊維配向と平行と成す方向（特定の一方向）に繊維配向を有する、一方向配向層（一方向性繊維ウェブ由来の繊維層）を有するものであった。
(Preparation of hydroentangled nonwoven fabric)
Polyester short fibers (fineness: 1.6 dtex, fiber length: 51 mm) 100 mass% to which a total of 0.3 mass% of anionic surfactant and nonionic surfactant are added are opened by a roller card machine, and are spread in the conveying direction. A unidirectional fiber web (basis weight: 18 g/m 2 ) in which fibers were oriented was formed.
In addition, 100 mass% of polyester short fibers (fineness: 1.6 dtex, fiber length: 51 mm) to which a total of 0.3 mass% of anionic surfactant and nonionic surfactant is applied are opened by a roller card machine, After forming the unidirectional fibrous web, the fibrous web was laminated so as to cross the conveying direction of the fibrous web with a crosslapper to form two multidirectional fibrous webs (basis weight: 16 g/m 2 ). .
Next, the unidirectional fibrous web/multidirectional fibrous web/multidirectional fibrous web are laminated in this order such that the conveying direction of the unidirectional fibrous web matches the direction in which the multidirectional fibrous web has been conveyed. After that, a water stream with a pressure of 13 MPa is jetted from the side of the multidirectional fiber web to entangle the fibers, producing a hydrophilic hydroentangled nonwoven fabric (basis weight: 50 g/m 2 , thickness: 0.4 mm). bottom.
The hydroentangled nonwoven fabric thus produced has a unidirectionally oriented layer (fibers derived from the unidirectional fibrous web layer).
（ＳＭＳ不織布の準備）
親水化剤を練り込んでなる親水性を有するポリプロピレン樹脂のメルトブローウェブの両主面に、親水化剤を練り込んでなる親水性を有するポリプロピレン樹脂のスパンボンドウェブを積層一体化してなる、親水性を有するＳＭＳ不織布（目付：５０ｇ／ｍ２、厚さ：０．３ｍｍ）を用意した。
このようにして製造したＳＭＳ不織布は、特定の一方向に繊維配向を有する一方向配向層を有していないものであった。
(Preparation of SMS nonwoven fabric)
A hydrophilic polypropylene resin melt-blown web in which a hydrophilizing agent is kneaded and a spunbond web of a hydrophilic polypropylene resin in which a hydrophilizing agent is kneaded is laminated and integrated on both main surfaces of the meltblown web. An SMS nonwoven fabric (basis weight: 50 g/m 2 , thickness: 0.3 mm) was prepared.
The SMS nonwoven fabric thus produced did not have a unidirectionally oriented layer having fiber orientation in one specific direction.
（フィルムの準備）
ポリエチレンフィルム（目付：１８ｇ／ｍ２、厚さ：０．０２０ｍｍ）を用意した。
(film preparation)
A polyethylene film (basis weight: 18 g/m 2 , thickness: 0.020 mm) was prepared.
（比較例１）
水流絡合不織布における一方向性繊維ウェブ側の主面に対し、ポリオレフィン系ホットメルト樹脂を用いたホットメルトラミネート法により、全面に溶融したポリオレフィン系ホットメルト樹脂を塗布（塗布量：３ｇ／ｍ２）した。そして、溶融したポリオレフィン系ホットメルト樹脂を間に介し、水流絡合不織布の一方の主面上にポリエチレンフィルムを貼り合わせた。
その後、水流絡合不織布における一方向配向層の配向方向と手術用シートの長手方向とが一致するようにして、水流絡合不織布の搬送方向（長手方向）に３２０ｃｍ、水流絡合不織布の搬送方向と直交する方向（短手方向）に２１０ｃｍの長方形に切断した。
このようにして、繊維層とフィルム層とがポリオレフィン系ホットメルト樹脂により、層間の全てにおいて接着一体化した積層体からなる、長方形状の手術用シート（目付：７１ｇ／ｍ２、厚さ：０．４ｍｍ）を製造した。
(Comparative example 1)
A molten polyolefin hot melt resin is applied to the entire surface of the hydroentangled nonwoven fabric on the unidirectional fiber web side by a hot melt lamination method using a polyolefin hot melt resin (coating amount: 3 g/m 2 ) . )bottom. Then, a polyethylene film was attached to one main surface of the water-entangled nonwoven fabric with a melted polyolefin hot-melt resin interposed therebetween.
After that, the orientation direction of the unidirectionally oriented layer in the hydroentangled nonwoven fabric and the longitudinal direction of the surgical sheet are aligned, and the hydroentangled nonwoven fabric is conveyed 320 cm in the conveying direction (longitudinal direction). It was cut into a rectangle of 210 cm in the direction (transverse direction) perpendicular to .
Thus, a rectangular surgical sheet (basis weight: 71 g/m 2 , thickness: 0 .4 mm) were manufactured.
（実施例１）
水流絡合不織布における一方向性繊維ウェブ側の主面に対し、当該主面の一方向（水流絡合不織布を構成する一方向性繊維ウェブの繊維配向と平行と成す方向）と平行をなす複数の直線となる態様で、溶融したポリオレフィン系ホットメルト樹脂を塗布（塗布量：３ｇ／ｍ２）した。そして、溶融したポリオレフィン系ホットメルト樹脂を間に介し、水流絡合不織布の一方の主面上にポリエチレンフィルムを貼り合わせた。
それ以外は比較例１と同様にして、繊維層とフィルム層とがポリオレフィン系ホットメルト樹脂により部分的に接着一体化した積層体からなる、長方形状の手術用シート（目付：７１ｇ／ｍ２、厚さ：０．４ｍｍ）を製造した。
なお、当該積層体における繊維層とフィルム層が対面している部分（層間）において、ポリオレフィン系ホットメルト樹脂は、繊維層の主面と平行を成す一方向（手術用シートにおける長辺方向）に対し平行を成すと共に、等間隔で存在する複数の直線となる態様で存在しており、両層を接着一体化していた。
(Example 1)
A plurality parallel to one direction of the main surface of the hydroentangled nonwoven fabric on the side of the unidirectional fiber web (the direction parallel to the fiber orientation of the unidirectional fiber web constituting the hydroentangled nonwoven fabric) A molten polyolefin hot-melt resin was applied (coating amount: 3 g/m 2 ) in a linear manner. Then, a polyethylene film was attached to one main surface of the water-entangled nonwoven fabric with a melted polyolefin hot-melt resin interposed therebetween.
Otherwise, in the same manner as in Comparative Example 1, a rectangular surgical sheet (basis weight: 71 g/m 2 , thickness: 0.4 mm).
In the portion (interlayer) where the fiber layer and the film layer face each other in the laminate, the polyolefin hot-melt resin is applied in one direction parallel to the main surface of the fiber layer (the long side direction in the surgical sheet). It existed in a form of a plurality of straight lines which were parallel to each other and which existed at equal intervals, and both layers were bonded and integrated.
（比較例２）
ＳＭＳ不織布の一方の主面に対し、ポリオレフィン系ホットメルト樹脂を用いたホットメルトラミネート法により、全面に溶融したポリオレフィン系ホットメルト樹脂を塗布（塗布量：３ｇ／ｍ２）した。そして、溶融したポリオレフィン系ホットメルト樹脂を間に介し、ＳＭＳ不織布の一方の主面上にポリエチレンフィルムを貼り合わせた。
その後、ＳＭＳ不織布の搬送方向（長手方向）に３２０ｃｍ、ＳＭＳ不織布の搬送方向と直交する方向（短手方向）に２１０ｃｍの長方形に切断した。
このようにして、繊維層とフィルム層とがポリオレフィン系ホットメルト樹脂により、層間の全てにおいて接着一体化した積層体からなる、長方形状の手術用シート（目付：７１ｇ／ｍ２、厚さ：０．４ｍｍ）を製造した。
(Comparative example 2)
One main surface of the SMS nonwoven fabric was coated with a melted polyolefin hot-melt resin (coating amount: 3 g/m 2 ) on the entire surface by a hot-melt lamination method using a polyolefin hot-melt resin. Then, a polyethylene film was attached to one main surface of the SMS nonwoven fabric with a melted polyolefin hot-melt resin interposed therebetween.
Then, it was cut into rectangles of 320 cm in the conveying direction (longitudinal direction) of the SMS nonwoven fabric and 210 cm in the direction perpendicular to the conveying direction of the SMS nonwoven fabric (lateral direction).
Thus, a rectangular surgical sheet (basis weight: 71 g/m 2 , thickness: 0 .4 mm) were manufactured.
（実施例２）
ＳＭＳ不織布の一方の主面に対し、当該主面の一方向と平行をなす複数の直線となる態様で、溶融したポリオレフィン系ホットメルト樹脂を塗布（塗布量：３ｇ／ｍ２）した。そして、溶融したポリオレフィン系ホットメルト樹脂を間に介し、ＳＭＳ不織布の一方の主面上にポリエチレンフィルムを貼り合わせた。
それ以外は比較例２と同様にして、繊維層とフィルム層とがポリオレフィン系ホットメルト樹脂により部分的に接着一体化した積層体からなる、長方形状の手術用シート（目付：７１ｇ／ｍ２、厚さ：０．４ｍｍ）を製造した。
なお、当該積層体における繊維層とフィルム層が対面している部分（層間）において、ポリオレフィン系ホットメルト樹脂は、繊維層の主面と平行を成す一方向（手術用シートにおける長辺方向）に対し平行を成すと共に、等間隔で存在する複数の直線となる態様で存在しており、両層を接着一体化していた。
(Example 2)
A molten polyolefin-based hot-melt resin was applied (coating amount: 3 g/m 2 ) to one main surface of the SMS nonwoven fabric in a form of a plurality of straight lines parallel to one direction of the main surface. Then, a polyethylene film was attached to one main surface of the SMS nonwoven fabric with a melted polyolefin hot-melt resin interposed therebetween.
Otherwise, in the same manner as in Comparative Example 2, a rectangular surgical sheet (basis weight: 71 g/m 2 , thickness: 0.4 mm).
In the portion (interlayer) where the fiber layer and the film layer face each other in the laminate, the polyolefin hot-melt resin is applied in one direction parallel to the main surface of the fiber layer (the long side direction in the surgical sheet). It existed in a form of a plurality of straight lines which were parallel to each other and which existed at equal intervals, and both layers were bonded and integrated.
（吸水性の評価）
次の手順により、手術用シートの吸水性を評価した。
（１）長方形の手術用シートを、端部にＲ８０ｍｍのカーブを有する作業台の天面となる上部で固定し作業台から垂れ下げる。この時、手術用シートにおける作業台から垂れ下がっている部分では、手術用シートの長手方向は重力方向と垂直をなし、短手方向は重力方向と平行をなし、作業台の端部から３０ｃｍ垂れ下がっている。また、作業台の天面において、重力方向と反対側に繊維層が露出する態様とする。
（２）手術用シートにおける作業台の端部側から、繊維層上へシリンジを用いて蒸留水５ｍＬを２０秒かけて垂らす。
（３）蒸留水を垂らしてから１０秒経過した後における、手術用シートの繊維層に拡散した蒸留水の範囲を確認する。そして、当該範囲内に、手術用シートの短手方向と平行を成すと共に最も長い線分Ａを引く。そして、当該線分Ａの中点と交点を有し、当該線分Ａと垂直を成す線分Ｂを引く。
（４）線分Ａの長さ（単位：ｃｍ）と線分Ｂの長さ（単位：ｃｍ）を測る。
（５）上述の測定を５枚の手術用シートに対してそれぞれ行ない、線分Ａの長さの平均値（単位：ｃｍ）、および、線分Ｂの長さの平均値（単位：ｃｍ）を求める。次いで、線分Ｂの長さの平均値を線分Ａの長さの平均値で割り、当該範囲のＢ／Ａ割合（単位なし）を算出する。
(Evaluation of water absorption)
The following procedure evaluated the water absorption of the surgical sheet.
(1) A rectangular surgical sheet is fixed at the upper part, which is the top surface of a workbench having a curve of R80 mm at the end, and hangs down from the workbench. At this time, in the portion of the surgical sheet hanging from the workbench, the longitudinal direction of the surgical sheet is perpendicular to the direction of gravity, and the widthwise direction is parallel to the direction of gravity. there is In addition, the fiber layer is exposed on the top surface of the workbench on the side opposite to the direction of gravity.
(2) Using a syringe, 5 mL of distilled water is dripped over 20 seconds onto the fiber layer from the end side of the workbench of the surgical sheet.
(3) Check the range of distilled water that has diffused into the fiber layer of the surgical sheet after 10 seconds have passed since the distilled water was dropped. Then, the longest line segment A parallel to the widthwise direction of the surgical sheet is drawn within the range. Then, draw a line segment B which has a midpoint and an intersection of the line segment A and is perpendicular to the line segment A.
(4) Measure the length of line segment A (unit: cm) and the length of line segment B (unit: cm).
(5) The above measurements are performed on each of the five surgical sheets, and the average length of line segment A (unit: cm) and the average length of line segment B (unit: cm) Ask for Next, the average value of the length of the line segment B is divided by the average value of the length of the line segment A to calculate the B/A ratio (unitless) in the range.
なお、算出されたＢ／Ａ割合の値が１．００に近いほど、水分を線分Ａが伸びる方向（手術用シートにおける短辺方向）のみならず、線分Ｂが伸びる方向（手術用シートにおける長辺方向）へも効果的に誘導し、拡散できる手術用シートであることを意味する。 It should be noted that the closer the calculated B/A ratio value is to 1.00, the more the moisture is absorbed not only in the direction in which the line segment A extends (the short side direction in the surgical sheet) but also in the direction in which the line segment B extends (the surgical sheet It means that it is a surgical sheet that can be effectively guided and diffused also in the long side direction of the
この結果は表１に示す通りであった。なお、線分Ａの長さの値に線分Ｂの長さの値をかけて算出値（単位なし）を求め、これを液体の吸収面積とした。そして、求めた液体の吸収面積から、手術用シートが有する液体の吸収性能を評価した。つまり、液体の吸収面積が小さい手術用シートであるほど、単位面積あたりに保持可能な液体の量が多いことを意味し液体の吸収性能に富む手術用シートであったことを意味する。 The results were as shown in Table 1. The value of the length of the line segment A was multiplied by the value of the length of the line segment B to obtain a calculated value (without units), which was used as the liquid absorption area. Then, the liquid absorption performance of the surgical sheet was evaluated from the obtained liquid absorption area. In other words, the smaller the liquid absorption area of the surgical sheet, the greater the amount of liquid that can be retained per unit area, which means that the surgical sheet has excellent liquid absorption performance.
比較例１と実施例１を比較した結果から、また、比較例２と実施例２を比較した結果から、本願発明にかかる構成を有する手術用シートは、水分を手術用シートの長手方向へも効果的に誘導し、拡散できるものであった。 From the results of comparison between Comparative Example 1 and Example 1, and from the results of comparison between Comparative Example 2 and Example 2, the surgical sheet having the structure according to the present invention also allows water to flow in the longitudinal direction of the surgical sheet. It could be effectively induced and diffused.
また、比較例１と実施例１を比較した結果から、また、比較例２と実施例２を比較した結果から、本願発明にかかる構成を有する手術用シートは、繊維層の主面全面が接着一体化することなくフィルム層と接着一体化していることで、液体の吸収面積が小さいものであり、単位面積あたりに保持可能な液体の量が多く液体の吸収性能に富む手術用シートであった。 Further, from the results of comparison between Comparative Example 1 and Example 1, and from the results of comparison between Comparative Example 2 and Example 2, the surgical sheet having the configuration according to the present invention is bonded on the entire main surface of the fiber layer. By bonding and integrating with the film layer without being integrated, the surgical sheet has a small liquid absorption area, a large amount of liquid that can be retained per unit area, and excellent liquid absorption performance. .
（実施例３）
ＳＭＳ不織布の一方の主面に対し、当該主面の一方向へ延びる複数の波線状となる態様で、溶融したポリオレフィン系ホットメルト樹脂を塗布（塗布量：３ｇ／ｍ２）した。そして、溶融したポリオレフィン系ホットメルト樹脂を間に介し、ＳＭＳ不織布の一方の主面上にポリエチレンフィルムを貼り合わせた。
それ以外は比較例２と同様にして、繊維層とフィルム層とがポリオレフィン系ホットメルト樹脂により部分的に接着一体化した積層体からなる、長方形状の手術用シート（目付：７１ｇ／ｍ２、厚さ：０．４ｍｍ）を製造した。
なお、当該積層体における繊維層とフィルム層が対面している部分（層間）において、ポリオレフィン系ホットメルト樹脂は、繊維層の主面と平行を成す一方向（手術用シートにおける長辺方向）へ延びると共に、等間隔で存在する複数の波線となる態様で存在しており、両層を接着一体化していた。
(Example 3)
A molten polyolefin-based hot-melt resin was applied (coating amount: 3 g/m 2 ) to one main surface of the SMS nonwoven fabric in a form of a plurality of wavy lines extending in one direction of the main surface. Then, a polyethylene film was attached to one main surface of the SMS nonwoven fabric with a melted polyolefin hot-melt resin interposed therebetween.
Otherwise, in the same manner as in Comparative Example 2, a rectangular surgical sheet (basis weight: 71 g/m 2 , thickness: 0.4 mm).
In the portion (interlayer) where the fiber layer and the film layer face each other in the laminate, the polyolefin hot-melt resin is applied in one direction parallel to the main surface of the fiber layer (the long side direction in the surgical sheet). While extending, it existed in a form of a plurality of wavy lines existing at equal intervals, and both layers were adhered and integrated.
このようにして作製した実施例３の手術用シートは、実施例２で作成した手術用シートと同等の性能を発揮するものであった。そのため、比較例２で作成した手術用シートよりも、水分を手術用シートの長手方向へも効果的に誘導し、拡散できるものであると共に、単位面積あたりに保持可能な液体の量が多く液体の吸収性能に富む手術用シートであった。 The surgical sheet of Example 3 produced in this manner exhibited performance equivalent to that of the surgical sheet produced in Example 2. Therefore, compared to the surgical sheet prepared in Comparative Example 2, the surgical sheet can effectively induce and diffuse moisture in the longitudinal direction, and the amount of liquid that can be retained per unit area is large. It was a surgical sheet with high absorption performance.
以上から、本願発明にかかる手術用シートは、人体の血液や体液等および手術に使用する薬液等の液体を、当該一方向へ効果的に誘導し拡散できる手術用シートである。 As described above, the surgical sheet according to the present invention is a surgical sheet capable of effectively guiding and diffusing human blood, bodily fluids, and liquids such as medical solutions used in surgery in the one direction.
そのため、本願発明にかかる手術用シートにおける、部分的に接着一体化している箇所が配向を有する方向（具体例として、手術用シートの長手方向）と、人体の上下方向が略一致するようにして、本願発明にかかる手術用シートで人体を覆い使用することで、人体の血液や体液等および手術に使用する薬液等の液体を、手術用シートにおける人体の上下方向へ誘導し拡散して、床面へ滴り落ちるのを回避できる。 Therefore, in the surgical sheet according to the present invention, the direction in which the partially bonded and integrated portions are oriented (specifically, the longitudinal direction of the surgical sheet) and the vertical direction of the human body are made to substantially match. By covering the human body with the surgical sheet according to the present invention, the blood, body fluids, etc. of the human body and liquids such as medical fluids used in surgery are guided and diffused in the vertical direction of the human body in the surgical sheet, and spread on the floor. Avoid dripping onto surfaces.
本願発明の手術用シートは、手術時に人体（患者）の覆布として好適に使用できる他、患者が横たわる手術台のカバーとして、また、手術時の医療機器の汚染を防ぐための覆布や下敷きとしても好適に使用できる。 The surgical sheet of the present invention can be suitably used as a cover cloth for the human body (patient) during surgery, as a cover for the operating table on which the patient lies, and as a cover cloth or underlay for preventing contamination of medical equipment during surgery. It can also be suitably used as
Claims (2)
前記繊維層と前記フィルム層は部分的に接着一体化しており、
前記部分的に接着一体化している箇所は、前記繊維層の主面と平行を成す一方向に配向を有して存在している、
手術用シート。
A surgical sheet comprising a laminate having a fiber layer and a film layer,
The fiber layer and the film layer are partially bonded and integrated,
The partially bonded and integrated portions are oriented in one direction parallel to the main surface of the fiber layer,
surgical sheet.