JP2022107469A - Decorative film, method for producing decorative film, decorative molding, and method for producing decorative molding - Google Patents

Decorative film, method for producing decorative film, decorative molding, and method for producing decorative molding Download PDF

Info

Publication number
JP2022107469A
JP2022107469A JP2021002439A JP2021002439A JP2022107469A JP 2022107469 A JP2022107469 A JP 2022107469A JP 2021002439 A JP2021002439 A JP 2021002439A JP 2021002439 A JP2021002439 A JP 2021002439A JP 2022107469 A JP2022107469 A JP 2022107469A
Authority
JP
Japan
Prior art keywords
decorative
layer
adhesive layer
peeled
decorative film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2021002439A
Other languages
Japanese (ja)
Inventor
翼 室伏
Tsubasa Murofushi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kyowa Leather Cloth Co Ltd
Original Assignee
Kyowa Leather Cloth Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kyowa Leather Cloth Co Ltd filed Critical Kyowa Leather Cloth Co Ltd
Priority to JP2021002439A priority Critical patent/JP2022107469A/en
Publication of JP2022107469A publication Critical patent/JP2022107469A/en
Pending legal-status Critical Current

Abstract

To provide a decorative film that allows any design pattern to be easily formed on an adherend without using a transfer sheet, a method for producing the decorative film, a decorative molding having the decorative film and a method for producing the decorative molding.SOLUTION: The present invention pertains to a decorative film used for decorating a molding, the decorative film having a decorative layer having a peelable part and a non-peelable part, an adhesive layer, and an adhesive layer protective sheet, in the stated order. The peelable part and the non-peelable part are separated along a tear-off line with its depth being less than 100% of the thickness of the decorative layer from the surface side of the decorative layer. There are also provided applications for the same.SELECTED DRAWING: Figure 1

Description

本開示は、加飾フィルム、加飾フィルムの製造方法、加飾成形体、及び加飾成形体の製造方法に関する。 The present disclosure relates to a decorative film, a method for producing a decorative film, a decorative molded product, and a method for producing a decorative molded product.

自動車、鉄道車輌、航空機などの外装材として、さまざまな意匠の合成樹脂加飾フィルム（以下、加飾フィルムと称することがある）が用いられている。加飾フィルムを、被着体、例えば、自動車等の外面に貼り付ける加飾方法を行うことで、自動車等の外装として、任意の意匠を簡易に付与することができる。また、加飾フィルムは、自動車等の本来の外装材を傷付けることなく剥離することができ、張り替えも行うことができる。
加飾フィルムとしては、例えば、自動車の屋根、スポイラーなどの一部領域の全面を被覆するために用いられる加飾シートが挙げられる。
加飾シートとしては、作業性の向上を図るために、形状保持層を備えた接着層を有する加飾シートが提案されている（特許文献１参照）。特許文献１に記載の加飾シートが形状保持層を有することで、加飾シートを貼り付ける成形体に適合する形状に予備成形を行うことで、貼り付け性が向上されるとされている。 Synthetic resin decorative films of various designs (hereinafter, may be referred to as decorative films) are used as exterior materials for automobiles, railroad vehicles, aircraft, and the like. By performing a decoration method in which the decorative film is attached to an adherend, for example, the outer surface of an automobile or the like, an arbitrary design can be easily applied as the exterior of the automobile or the like. In addition, the decorative film can be peeled off without damaging the original exterior material of an automobile or the like, and can be replaced.
Examples of the decorative film include a decorative sheet used to cover the entire surface of a part of an automobile roof, a spoiler, or the like.
As the decorative sheet, in order to improve workability, a decorative sheet having an adhesive layer provided with a shape-retaining layer has been proposed (see Patent Document 1). It is said that the decorative sheet described in Patent Document 1 has a shape-retaining layer, and pre-molding into a shape suitable for the molded body to which the decorative sheet is attached improves the stickability.

また、文字、図柄などのデザインパターンを貼り付けるためのアプリケーションシート（以下、「転写シート」と称する）が知られている。転写シートが有する文字、図柄などのデザインパターンのみを、被着体に貼り付けることで、任意のデザインパターンを任意の領域に形成することができる。
加飾用の転写シートは、装飾シート、装飾用粘着シート等（以下、「装飾シート等」と称する）が有する文字又は図柄などのデザインパターンを、転写シート形成用の基材シートに転写して加飾用の転写シートを得ることで形成される。形成された加飾用の転写シートを被着体へ貼り付け、転写シートの基材シートのみを剥がすことにより、デザインパターンによる被着体の加飾を施すことができる。
装飾シートとしては、立体的な成形体に貼付しても装飾面の伸び、歪みなどを生じないため、装飾フィルムとアプリケーションテープとを備え、且つ、装飾フィルム及びアプリケーションテープのそれぞれが特定の引っ張り弾性率を満たす加飾シートが提案されている（特許文献２参照）。
また、転写シートとしては、剥離体上に粘着剤層を介して貼着された装飾用粘着シートを用い、該装飾用粘着シートを所望の形状にカッティングして、カッティング形成されたデザイン部分を、感圧粘着剤層が設けられた特定の物性を有するアプリケーションテープに貼着させて転写シートを作製する方法が提案されている（特許文献３参照）。この転写シートから剥離体を引き剥がし、被着体にデザイン部分を貼り付け、アプリケーションテープを剥離することでデザインを被着体に転写する方法である。 Further, an application sheet (hereinafter referred to as "transfer sheet") for pasting a design pattern such as characters and patterns is known. By attaching only the design patterns such as characters and patterns of the transfer sheet to the adherend, an arbitrary design pattern can be formed in an arbitrary area.
The decorative transfer sheet transfers a design pattern such as characters or patterns of a decorative sheet, a decorative adhesive sheet, etc. (hereinafter referred to as "decorative sheet, etc.") to a base sheet for forming a transfer sheet. It is formed by obtaining a transfer sheet for decoration. By attaching the formed transfer sheet for decoration to the adherend and peeling off only the base sheet of the transfer sheet, it is possible to decorate the adherend according to the design pattern.
The decorative sheet is provided with a decorative film and an application tape because the decorative surface does not stretch or distort even when attached to a three-dimensional molded body, and each of the decorative film and the application tape has a specific tensile elastic modulus. A decorative sheet satisfying the rate has been proposed (see Patent Document 2).
Further, as the transfer sheet, a decorative adhesive sheet attached on the peeled body via an adhesive layer is used, and the decorative adhesive sheet is cut into a desired shape to form a cut-formed design portion. A method of producing a transfer sheet by attaching it to an application tape having a specific physical property provided with a pressure-sensitive pressure-sensitive adhesive layer has been proposed (see Patent Document 3). This is a method in which the release body is peeled off from the transfer sheet, the design portion is attached to the adherend, and the application tape is peeled off to transfer the design to the adherend.

特開２０１６―１９８９００号公報Japanese Unexamined Patent Publication No. 2016-198900 特開２００６－２４８１２０号公報Japanese Unexamined Patent Publication No. 2006-248120 特開平０６－０５１７０２号公報Japanese Unexamined Patent Publication No. 06-051702

しかし、特許文献１に記載の加飾シートでは、加飾シートを貼り付ける成形体に適合する形状に予備成形を行い、それをそのまま成形体に貼り付けるため、領域全面ではなく、特定の形状の文字又は図形等のデザイン部分のみを成形体に付与することは困難である。
また、特許文献２及び特許文献３に記載の装飾シート等では、装飾層とは別に、さらにアプリケーションテープなどの転写シートを必要とし、転写シートの弾性率、熱特性などを所定の範囲に制御する必要があった。また、転写までデザイン部分を転写シートに安定に保持するために、デザイン部分は転写シートとある程度の密着性が必要であった。 However, in the decorative sheet described in Patent Document 1, premolding is performed into a shape suitable for the molded body to which the decorative sheet is attached, and the decorative sheet is directly attached to the molded body. It is difficult to give only a design part such as a character or a figure to a molded product.
Further, the decorative sheets and the like described in Patent Documents 2 and 3 require a transfer sheet such as an application tape in addition to the decorative layer, and control the elastic modulus, thermal characteristics, etc. of the transfer sheet within a predetermined range. I needed it. Further, in order to stably hold the design portion on the transfer sheet until transfer, the design portion needs to have a certain degree of adhesion to the transfer sheet.

本発明の一実施形態の課題は、転写シートを用いることなく、任意のデザインパターンを被着体に容易に形成することができる加飾フィルム及び加飾フィルムの製造方法を提供することである。
また、本発明の別の実施形態の課題は、転写シートを用いることなく、任意のデザインパターンを被着体に容易に形成することができる加飾フィルムを用いた、意匠性が良好な加飾成形体及び加飾成形体の製造方法を提供することである。 An object of an embodiment of the present invention is to provide a decorative film and a method for producing a decorative film, which can easily form an arbitrary design pattern on an adherend without using a transfer sheet.
Further, a subject of another embodiment of the present invention is decoration with good design by using a decorative film capable of easily forming an arbitrary design pattern on an adherend without using a transfer sheet. The present invention provides a method for producing a molded product and a decorative molded product.

課題を解決するための手段は以下の態様を含む。
＜１＞ 剥離部と非剥離部とを有する加飾層と接着層とを有する加飾積層体、及び、接着層保護シート、をこの順で有し、前記剥離部と非剥離部とは、深さが、加飾層の厚みに対し、加飾層の表面側から１００％未満である切り取り線にて区画される、成形体の加飾に用いられる加飾フィルム。
＜２＞ 前記加飾層における切り取り線の深さは、加飾層の厚みに対し、加飾層の表面側から２５％以上１００％未満である、＜１＞に記載の加飾フィルム。
＜３＞ 前記剥離部は、剥離補助部を備える＜１＞又は＜２＞に記載の加飾フィルム。
＜４＞ 前記加飾層の、前記接着層側とは反対の面に、さらに、前記加飾層とは異なる色相の着色シートを有する＜１＞～＜３＞のいずれか１つに記載の加飾フィルム。 Means for solving the problem include the following aspects.
<1> A decorative laminate having a decorative layer having a peeled portion and a non-peeled portion and an adhesive layer, and an adhesive layer protective sheet are provided in this order, and the peeled portion and the non-peeled portion are referred to as each other. A decorative film used for decorating a molded body, which is partitioned by a cutting line whose depth is less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer.
<2> The decorative film according to <1>, wherein the depth of the cut line in the decorative layer is 25% or more and less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer.
<3> The decorative film according to <1> or <2>, wherein the peeling portion includes a peeling assisting portion.
<4> The method according to any one of <1> to <3>, wherein the decorative layer has a colored sheet having a hue different from that of the decorative layer on the surface opposite to the adhesive layer side. Decorative film.

＜５＞ 加飾層の一方の面に、接着層を形成して加飾積層体を形成する工程と、接着層保護シートを準備し、準備した接着層保護シートにより、前記接着層を被覆して、前記加飾層と前記接着層と前記接着層保護シートとを有する加飾フィルム前駆体を形成する工程と、前記加飾層に、剥離部と非剥離部とを区画する、深さが、加飾層の厚みに対し、加飾層の表面側から１００％未満である第一切り取り線を形成する工程と、前記加飾フィルム前駆体を貫通する第二切り取り線を、前記第一切り取り線との交部が生じる位置に形成する工程と、を有する、成形体の加飾に用いられる加飾フィルムの製造方法。 <5> A step of forming an adhesive layer on one surface of the decorative layer to form a decorative laminate, and preparing an adhesive layer protective sheet, and covering the adhesive layer with the prepared adhesive layer protective sheet. The step of forming the decorative film precursor having the decorative layer, the adhesive layer, and the adhesive layer protective sheet, and the depth of partitioning the peeled portion and the non-peeled portion in the decorative layer The step of forming the first cut line which is less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer and the second cut line penetrating the decorative film precursor are the first cut. A method for producing a decorative film used for decorating a molded product, which comprises a step of forming at a position where an intersection with a line occurs.

＜６＞ 成形体と、＜１＞～＜４＞のいずれか１つに記載の加飾フィルムから前記接着層保護シート及び加飾積層体の剥離部が剥離された加飾積層体の非剥離部と、を有する加飾成形体。
＜７＞ ＜１＞～＜４＞のいずれか１つに記載の加飾フィルムから接着層保護シートを剥離して加飾積層体を得る工程、接着層保護シートを剥離した加飾積層体を、接着層を介して成形体の表面に貼り付ける工程、及び、前記成形体の表面に貼り付けた加飾積層体の剥離部を剥離する工程、を有する加飾成形体の製造方法。 <6> Non-peeling of the decorative laminate in which the peeled portion of the adhesive layer protective sheet and the decorative laminate is peeled from the molded body and the decorative film according to any one of <1> to <4>. A decorative molded body having a part and.
<7> A step of peeling the adhesive layer protective sheet from the decorative film according to any one of <1> to <4> to obtain a decorative laminate, and a decorative laminate from which the adhesive layer protective sheet has been peeled off. A method for producing a decorative molded body, comprising: a step of attaching to the surface of the molded body via an adhesive layer, and a step of peeling off a peeled portion of the decorative laminated body attached to the surface of the molded body.

本発明の一実施形態によれば、転写シートを用いることなく、任意のデザインパターンを被着体に容易に形成することができる加飾フィルム及び加飾フィルムの製造方法を提供することができる。
本発明の別の実施形態によれば、転写シートを用いることなく、任意のデザインパターンを被着体に容易に形成することができる加飾フィルムを用いた、意匠性が良好な加飾成形体及び加飾成形体の製造方法を提供することができる。 According to one embodiment of the present invention, it is possible to provide a decorative film and a method for producing a decorative film, which can easily form an arbitrary design pattern on an adherend without using a transfer sheet.
According to another embodiment of the present invention, a decorative molded article having a good design using a decorative film capable of easily forming an arbitrary design pattern on an adherend without using a transfer sheet. And a method for producing a decorative molded product can be provided.

本開示の加飾フィルムの一例を示す概略断面図である。It is the schematic sectional drawing which shows an example of the decorative film of this disclosure. 本開示の加飾フィルムにおける凹部形状の剥離補助部の一例を示す概略平面図である。It is a schematic plan view which shows an example of the peeling auxiliary part of the concave shape in the decorative film of this disclosure. 本開示の加飾フィルムにおける凸部形状の剥離補助部であるタブの一例を示す概略平面図である。It is a schematic plan view which shows an example of the tab which is the peeling auxiliary part of the convex part shape in the decorative film of this disclosure. 本開示の加飾フィルムの製造方法の工程ＩＩＩにおける矩形の加飾フィルム前駆体に第一切り取り線を形成した状態の一態様を示す概略平面図である。FIG. 5 is a schematic plan view showing an aspect of a state in which a first cut line is formed on a rectangular decorative film precursor in step III of the method for producing a decorative film of the present disclosure. 本開示の加飾フィルムの製造方法の工程ＩＶにおける第一切り取り線を形成した矩形の加飾フィルム前駆体に、第二切り取り線を形成した状態の一態様を示す概略平面図である。It is a schematic plan view which shows one aspect of the state which formed the 2nd cut line in the rectangular decorative film precursor which formed the 1st cut line in step IV of the manufacturing method of the decorative film of this disclosure. 本開示の加飾フィルムの剥離部と非剥離部との区画の一例を示す概略平面図である。It is a schematic plan view which shows an example of the section of the peeling part and the non-peeling part of the decorative film of this disclosure. 本開示の加飾成形体の一例を示す部分概略断面図である。It is a partial schematic sectional view which shows an example of the decorative molded article of this disclosure. 本開示の着色シートを有する加飾積層体を成形体に貼り付け、剥離部の着色シートを剥離した状態の一例を示す概略断面図である。It is schematic cross-sectional view which shows an example of the state in which the decorative laminate having the colored sheet of the present disclosure is attached to a molded body, and the colored sheet of a peeling portion is peeled off. 実施例４の加飾フィルムに形成された剥離補助部である凹部の部分拡大図である。It is a partially enlarged view of the recess which is the peeling auxiliary part formed in the decorative film of Example 4. FIG.

以下、本開示の加飾フィルム、その製造方法、加飾成形体及びその製造方法について詳細に説明する。
以下に記載する構成要件の説明は、本開示の代表的な実施態様に基づいてなされることがあるが、本開示はそのような実施態様に限定されない。
なお、本開示において、数値範囲を示す「～」とはその前後に記載される数値を下限値及び上限値として含む意味で使用される。
本開示に段階的に記載されている数値範囲において、一つの数値範囲で記載された上限値又は下限値は、他の段階的な記載の数値範囲の上限値又は下限値に置き換えてもよい。また、本開示に記載されている数値範囲において、その数値範囲の上限値又は下限値は、実施例に示されている値に置き換えてもよい。
本開示において、２以上の好ましい態様の組み合わせは、より好ましい態様である。
本開示において「工程」との語は、独立した工程だけではなく、他の工程と明確に区別できない場合であってもその工程の所期の目的が達成されれば、本用語に含まれる。 Hereinafter, the decorative film of the present disclosure, a method for producing the same, a decorative molded product, and the method for producing the same will be described in detail.
The description of the constituents described below may be based on the representative embodiments of the present disclosure, but the present disclosure is not limited to such embodiments.
In the present disclosure, "-" indicating a numerical range is used to mean that the numerical values described before and after the numerical range are included as the lower limit value and the upper limit value.
In the numerical range described stepwise in the present disclosure, the upper limit value or the lower limit value described in one numerical range may be replaced with the upper limit value or the lower limit value of another numerical range described stepwise. Further, in the numerical range described in the present disclosure, the upper limit value or the lower limit value of the numerical range may be replaced with the value shown in the examples.
In the present disclosure, a combination of two or more preferred embodiments is a more preferred embodiment.
In the present disclosure, the term "process" is included in this term not only as an independent process but also as long as the intended purpose of the process is achieved even if it cannot be clearly distinguished from other processes.

本開示において「常温」とは、特に断らない限り、２３℃を指す。
本開示における「加飾フィルム」は、少なくとも、加飾層と接着層とを有する加飾積層体及び接着層保護シートとをこの順に有する。
本開示では、加飾層と接着層との積層体を「加飾積層体」と称する。即ち、被着体である成形体には、加飾積層体が、接着層を介して貼着され、その後、加飾積層体の剥離部を剥離することで、加飾積層体の非剥離部が成形体におけるデザインパターンを形成する。
ここで、本開示における「主成分である樹脂」とは、当該成分が含まれる樹脂組成物の全量に対し、６０質量％以上含有される樹脂を指す。本開示では、層を構成する主成分である樹脂を「主剤樹脂」とも称する。
本開示において「成形体」とは、加飾前の成形体（成形体の基体）を指す。
本開示においては、加飾フィルムの最外層、即ち、加飾層の接着層側とは反対の面であって、成形体に貼り付けられた場合に、視認される側を、加飾フィルムの表面と称する。 In the present disclosure, "normal temperature" refers to 23 ° C. unless otherwise specified.
The "decorative film" in the present disclosure includes at least a decorative laminate having a decorative layer and an adhesive layer and an adhesive layer protective sheet in this order.
In the present disclosure, a laminate of a decorative layer and an adhesive layer is referred to as a "decorative laminate". That is, the decorative laminate is attached to the molded body which is the adherend via the adhesive layer, and then the peeled portion of the decorative laminate is peeled off to form a non-peeled portion of the decorative laminate. Form a design pattern in the molded body.
Here, the "resin as the main component" in the present disclosure refers to a resin contained in an amount of 60% by mass or more with respect to the total amount of the resin composition containing the component. In the present disclosure, the resin which is the main component constituting the layer is also referred to as "main agent resin".
In the present disclosure, the "molded body" refers to a molded body (base of the molded body) before decoration.
In the present disclosure, the outermost layer of the decorative film, that is, the side opposite to the adhesive layer side of the decorative layer, which is visible when attached to the molded body, is the side of the decorative film. Called the surface.

［加飾フィルム］
本開示の加飾フィルムは、剥離部と非剥離部とを有する加飾層と、接着層と、接着層保護シートと、をこの順で有し、前記剥離部と非剥離部とは、深さが、加飾層の厚みに対し、加飾層の表面側から１００％未満である切り取り線にて区画される、成形体の加飾に用いられる加飾フィルムである。
本開示の加飾フィルムは、剥離部と非剥離部とは、深さが、加飾層の厚みに対し、加飾層の表面側から１００％未満である切り取り線にて区画されているため、加飾フィルムから接着層保護シートを剥離し、成形体に接着層を介して加飾層を貼着した後、切り取り線の存在により、剥離部のみを容易に剥離することができる。このため、加飾フィルムにおける非剥離部からなるデザインパターンを、複雑な形状であっても成形体の表面に容易に形成することができる。 [Decorative film]
The decorative film of the present disclosure has a decorative layer having a peeling portion and a non-peeling portion, an adhesive layer, and an adhesive layer protective sheet in this order, and the peeling portion and the non-peeling portion are deep. This is a decorative film used for decorating a molded body, which is partitioned by a cutting line that is less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer.
In the decorative film of the present disclosure, the peeled portion and the non-peeled portion are separated by a cut line whose depth is less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer. After peeling the adhesive layer protective sheet from the decorative film and attaching the decorative layer to the molded body via the adhesive layer, only the peeled portion can be easily peeled off due to the presence of the cut line. Therefore, a design pattern composed of non-peeling portions in the decorative film can be easily formed on the surface of the molded body even if it has a complicated shape.

図１は、本開示の加飾フィルムの一例を示す概略断面図である。図１に示す加飾フィルム１０は、加飾層１２と、接着層１４と、接着層保護シート１６とを有し、加飾層１２の剥離部と非剥離部とを区画する切り取り線２０を備える。図１に示す加飾フィルム１０は、さらに、任意の層としての表皮層１８を有する。
図１に示す加飾フィルム１０の切り取り線２０の深さは、加飾層１２の厚みに対し、加飾層１２の表面側から１００％未満の深さで形成される。従って、切り取り線は、接着層１４と加飾層１２とが接する界面には到達しない深さである。 FIG. 1 is a schematic cross-sectional view showing an example of the decorative film of the present disclosure. The decorative film 10 shown in FIG. 1 has a decorative layer 12, an adhesive layer 14, and an adhesive layer protective sheet 16, and has a cut line 20 that separates a peeled portion and a non-peeled portion of the decorative layer 12. Be prepared. The decorative film 10 shown in FIG. 1 further has an epidermis layer 18 as an arbitrary layer.
The depth of the cut line 20 of the decorative film 10 shown in FIG. 1 is formed at a depth of less than 100% from the surface side of the decorative layer 12 with respect to the thickness of the decorative layer 12. Therefore, the cut line has a depth that does not reach the interface where the adhesive layer 14 and the decorative layer 12 are in contact with each other.

加飾フィルム１０は、成形体を加飾する際には、接着層保護シート１６を剥離して、成形体に貼り付けられ、成形体には、図１に示す表皮層１８と加飾層１２と接着層１４との積層体が貼付される。
本開示では、既述のように、少なくとも加飾層１２と接着層１４とを有する積層体を「加飾積層体」と称する。加飾積層体は、加飾層１２及び接着層１４に加え、例えば、表皮層１８、プライマー層などの任意の層をさらに含んでいてもよい。
図１において、Ａで示す領域が加飾フィルムの剥離部であり、Ｂで示す領域が非剥離部である。 When decorating the molded body, the decorative film 10 is attached to the molded body by peeling off the adhesive layer protective sheet 16, and the molded body has the skin layer 18 and the decorative layer 12 shown in FIG. A laminate of the adhesive layer 14 and the adhesive layer 14 is attached.
In the present disclosure, as described above, a laminate having at least a decorative layer 12 and an adhesive layer 14 is referred to as a “decorative laminate”. In addition to the decorative layer 12 and the adhesive layer 14, the decorative laminate may further include any layer such as a skin layer 18 and a primer layer.
In FIG. 1, the region indicated by A is the peeling portion of the decorative film, and the region indicated by B is the non-peeling portion.

（加飾層）
本開示の加飾フィルムにおける加飾層の非剥離部は、接着層を介して成形体に貼付され、成形体に意匠性を付与する層である。
加飾層は、合成樹脂を含んで形成される。 (Decorative layer)
The non-peeling portion of the decorative layer in the decorative film of the present disclosure is a layer that is attached to the molded body via an adhesive layer to impart designability to the molded body.
The decorative layer is formed containing a synthetic resin.

－合成樹脂－
合成樹脂は、シート状に成形し得る樹脂であれば、特に制限なく用いることができる。合成樹脂としては、例えば、アクリル樹脂、ポリ塩化ビニル（以下、ＰＶＣとも称する）樹脂、アクリロニトリル／ブタジエン／スチレン共重合体（以下、ＡＢＳ樹脂とも称する）ウレタン樹脂、オレフィン樹脂などが挙げられる。
なかでも、加飾フィルムの耐久性がより良好であるという観点から、アクリル樹脂、ＰＶＣ樹脂及びＡＢＳ樹脂から選ばれる少なくとも１種の樹脂を含有することが好ましい。 -Synthetic resin-
The synthetic resin can be used without particular limitation as long as it is a resin that can be molded into a sheet shape. Examples of the synthetic resin include acrylic resin, polyvinyl chloride (hereinafter, also referred to as PVC) resin, acrylonitrile / butadiene / styrene copolymer (hereinafter, also referred to as ABS resin) urethane resin, and olefin resin.
Among them, from the viewpoint of better durability of the decorative film, it is preferable to contain at least one resin selected from acrylic resin, PVC resin and ABS resin.

加飾層に用いうるアクリル樹脂としては、例えば、ポリメチルメタクリレート（ＰＭＭＡ）に代表されるメタクリル酸又はメタクリル酸エステルの重合体或いは共重合体、メタクリル酸アルキルとアクリル酸アルキルとスチレンの共重合体等が挙げられ、成形性の観点からは、メタクリル酸アルキルとアクリル酸アルキルとスチレンの共重合体及びメタクリル酸メチルとアクリル酸メチルの共重合体の混合物等が挙げられる。 Examples of the acrylic resin that can be used for the decorative layer include a polymer or copolymer of methacrylic acid or methacrylic acid ester represented by polymethylmethacrylate (PMMA), and a copolymer of alkyl methacrylate, alkyl acrylate, and styrene. From the viewpoint of moldability, a copolymer of alkyl methacrylate, alkyl acrylate and styrene, a mixture of methyl methacrylate and methyl acrylate, and the like can be mentioned.

加飾層に用いうる塩化ビニル樹脂（ＰＶＣ）としては、従来、塩化ビニルレザーに使用されているものであれば特に制限なく使用できる。具体的には、平均重合度８００～２０００、好ましくは８００～１５００程度のポリ塩化ビニルの他、塩化ビニルを主体とする、エチレン、酢酸ビニル、メタクリル酸エステル等との共重合樹脂や、これらの樹脂とポリエステル樹脂、エポキシ樹脂、アクリル樹脂、酢酸ビニル樹脂、ウレタン樹脂、アクリロニトリル、スチレン－ブタジエン共重合樹脂、部分ケン化ビニルアルコール等との混合樹脂等が挙げられる。 The vinyl chloride resin (PVC) that can be used for the decorative layer is not particularly limited as long as it is conventionally used for vinyl chloride leather. Specifically, in addition to polyvinyl chloride having an average degree of polymerization of 800 to 2000, preferably about 800 to 1500, a copolymer resin mainly composed of vinyl chloride with ethylene, vinyl acetate, methacrylic acid ester and the like, and these. Examples thereof include a resin and a polyester resin, an epoxy resin, an acrylic resin, a vinyl acetate resin, a urethane resin, an acrylonitrile, a styrene-butadiene copolymer resin, a mixed resin of a partially saponified vinyl alcohol, and the like.

加飾層に用いるＡＢＳ樹脂は、公知のＡＢＳ樹脂を適宜選択して用いることができる。ＡＢＳ樹脂は１種のみを用いてもよく、互いに共重合比率の異なる２種以上を併用してもよい。
また、ＡＢＳ樹脂と、前記ＰＶＣ樹脂とを併用してもよい。 As the ABS resin used for the decorative layer, a known ABS resin can be appropriately selected and used. Only one type of ABS resin may be used, or two or more types having different copolymerization ratios may be used in combination.
Further, the ABS resin and the PVC resin may be used in combination.

加飾層には合成樹脂を１種のみ含んでもよく、目的に応じて２種以上含んでいてもよい。
２種以上の合成樹脂を含む場合には、互いに相溶性の高い樹脂同士を組み合わせることが好ましい。 The decorative layer may contain only one type of synthetic resin, or may contain two or more types depending on the purpose.
When two or more kinds of synthetic resins are contained, it is preferable to combine resins having high compatibility with each other.

加飾層には、合成樹脂に加え、目的に応じてその他の成分を含んでもよい。その他の成分としては、着色剤、可塑剤、充填剤、滑剤、加工助剤、難燃剤、耐光安定剤、熱安定剤等が挙げられる。 In addition to the synthetic resin, the decorative layer may contain other components depending on the purpose. Examples of other components include colorants, plasticizers, fillers, lubricants, processing aids, flame retardants, light-resistant stabilizers, heat stabilizers and the like.

－着色剤－
加飾層が着色剤を含むことで、加飾フィルムに任意の色相を付与することができる。
加飾層に含まれ得る着色剤には特に制限はなく、例えば、染料、顔料、パール粒子、アルミ粉等の金属粉等が挙げられ、これらの着色剤から選択される１種以上を目的に応じて用いることができる。
加飾フィルムを、耐久性、耐候性を必要とする用途、例えば、車両用外装材、建造物の内外装材等に用いる場合には、顔料が好適に使用される。 -Colorant-
When the decorative layer contains a colorant, an arbitrary hue can be imparted to the decorative film.
The colorant that can be contained in the decorative layer is not particularly limited, and examples thereof include dyes, pigments, pearl particles, metal powders such as aluminum powder, and the like, for the purpose of one or more selected from these colorants. It can be used accordingly.
When the decorative film is used for applications requiring durability and weather resistance, for example, vehicle exterior materials, building interior / exterior materials, and the like, pigments are preferably used.

－加飾層の厚み－
加飾層の厚みには特に制限はない。成形体への貼り付け容易性の観点からは、加飾層の厚みは５０μｍ～４００μｍの範囲であることが好ましく、１００μｍ～３５０μｍの範囲であることがより好ましい。 -Thickness of decorative layer-
The thickness of the decorative layer is not particularly limited. From the viewpoint of ease of attachment to the molded product, the thickness of the decorative layer is preferably in the range of 50 μm to 400 μm, and more preferably in the range of 100 μm to 350 μm.

－加飾層の形成方法－
加飾層の形成方法には特に制限はなく、公知のシート成形法を適用すればよい。成形法としては、カレンダー法、キャスティング法、溶融押出し法、溶液法等が挙げられ、これらのいずれを用いてもよい。なかでも、製造の簡易性、装置のメンテナンスが容易であるという観点からは、カレンダー法が好ましい。
例えば、加飾層をカレンダー法により形成することで、種々の着色剤を含有する加飾層を簡易に製造することができ、また、着色剤の種類や添加量を変更する際に必要な装置内の清掃が容易に行われるため、所望の色相と、所望の絞模様と、を有する様々な変型例を簡易に製造しうる。
このため、色相と絞模様のバリエーションが豊富で、耐久性に優れる加飾フィルムの小ロット生産に適する。 -How to form a decorative layer-
The method for forming the decorative layer is not particularly limited, and a known sheet molding method may be applied. Examples of the molding method include a calendar method, a casting method, a melt extrusion method, a solution method and the like, and any of these may be used. Of these, the calendar method is preferable from the viewpoint of ease of manufacturing and easy maintenance of the device.
For example, by forming the decorative layer by the calendar method, a decorative layer containing various colorants can be easily manufactured, and an apparatus necessary for changing the type and amount of the colorant added. Since the inside is easily cleaned, various modified examples having a desired hue and a desired squeezed pattern can be easily manufactured.
Therefore, it is suitable for small-lot production of decorative films with abundant variations in hue and squeezing pattern and excellent durability.

（接着層）
本開示の加飾フィルムは、成形体に加飾積層体を接着する目的で、加飾層の一方の面に接着層を備える。
接着層の形成に使用される接着剤、粘着剤には特に制限はなく、加飾積層体を貼着する成形体の種類により適宜選択される。 (Adhesive layer)
The decorative film of the present disclosure includes an adhesive layer on one surface of the decorative layer for the purpose of adhering the decorative laminate to the molded body.
The adhesive and the adhesive used for forming the adhesive layer are not particularly limited, and are appropriately selected depending on the type of the molded body to which the decorative laminate is attached.

なかでも、接着層は、加飾積層体を成形体に貼り付ける際の作業性、及び、剥離部を剥離しやすいという観点からは、初期低タックである接着層であることが好ましく、さらに、加飾層の安定性の観点からは、後述するように貼り付け経時後の接着安定性が良好な接着層であることが好ましい。 Among them, the adhesive layer is preferably an adhesive layer having an initial low tack from the viewpoint of workability when the decorative laminate is attached to the molded body and easy peeling of the peeled portion. From the viewpoint of the stability of the decorative layer, it is preferable that the adhesive layer has good adhesive stability after a lapse of time as described later.

－接着層の初期低タック－
接着層の初期低タックの目安としては、下記剥離試験方法（Ｉ）にて測定した初期剥離強度が０．１Ｎ／ｃｍ～５Ｎ／ｃｍの範囲であることが好ましく、１Ｎ／ｃｍ～５Ｎ／ｃｍの範囲であることがより好ましい。
（剥離試験方法（Ｉ））
加飾フィルムから接着層保護シートを剥離し、加飾積層体の接着層側をステンレス鋼板に貼り付け、ＪＩＳ Ｚ ０２３７（２００９年）に規定する粘着テープの１８０°剥離試験に準じて剥離強度を測定する。 -Initial low tack of the adhesive layer-
As a guideline for the initial low tack of the adhesive layer, the initial peel strength measured by the following peeling test method (I) is preferably in the range of 0.1 N / cm to 5 N / cm, and is preferably 1 N / cm to 5 N / cm. It is more preferable that the range is.
(Peeling test method (I))
The adhesive layer protective sheet is peeled off from the decorative film, and the adhesive layer side of the decorative laminate is attached to a stainless steel plate, and the peeling strength is determined according to the 180 ° peeling test of the adhesive tape specified in JIS Z 0237 (2009). Measure.

－接着層の貼り付け経時後の接着安定性－
接着層の貼り付け経時後の接着安定性の観点からは、下記試験方法（ＩＩ）で測定した経時後の剥離強度が、６．５Ｎ／ｃｍ以上が好ましく、７Ｎ／ｃｍ以上がより好ましく、８Ｎ／ｃｍ以上が更に好ましい。 -Adhesive stability after aging of the adhesive layer-
From the viewpoint of adhesive stability after aging of the adhesive layer, the peel strength after aging measured by the following test method (II) is preferably 6.5 N / cm or more, more preferably 7 N / cm or more, and 8 N. / Cm or more is more preferable.

（剥離試験方法（ＩＩ））
加飾フィルムから接着層保護シートを剥離し、加飾積層体の接着層側をステンレス鋼板に貼り付け、２０℃にて２４時間保持した後、ＪＩＳ Ｚ ０２３７（２００９年）に規定する粘着テープの１８０°剥離試験に準じて剥離強度を測定する。 (Peeling test method (II))
The adhesive layer protective sheet is peeled off from the decorative film, the adhesive layer side of the decorative laminate is attached to a stainless steel plate, held at 20 ° C. for 24 hours, and then the adhesive tape specified in JIS Z 0237 (2009) is used. The peel strength is measured according to the 180 ° peel test.

接着層を有する試験片を被着体である硬質基材の表面に密着させ、２４時間養生することで、硬質基材と接着層との密着面積がより大きくなり、両者の分子間力がより多点で発生し、さらに、接着層の熟成が進み、硬質基材上に接着層がより安定に固定化される。 By adhering the test piece having the adhesive layer to the surface of the hard base material which is the adherend and curing it for 24 hours, the adhesion area between the hard base material and the adhesive layer becomes larger, and the intramolecular force between the two becomes stronger. It occurs at multiple points, and the aging of the adhesive layer progresses, and the adhesive layer is more stably fixed on the hard base material.

－接着層の形成－
接着層としては、エチレン酢酸ビニル、アクリル樹脂、ウレタン樹脂、オレフィン樹脂、ポリエステル、ポリアミド、及び合成ゴムから選ばれる少なくとも１種の樹脂を含む粘着剤又はホットメルト接着剤を含有する接着層であることが好ましい。
上記粘着剤又はホットメルト接着剤により形成される接着層の厚さは、接着安定性の観点から、乾燥膜厚で２０μｍ～８０μｍの範囲であることが好ましく、３０μｍ～６０μｍの範囲であることがより好ましい。
加飾層上に接着剤を形成する方法としては、転写法、塗布法等の層形成に係る公知の方法をいずれも使用できる。
均一な厚みの接着層を簡易に形成しうるという観点からは、転写法を用いることが好ましい。
また、後述のように接着層保護シートに凹凸設けて、接着層に凹凸を転写する場合には、接着剤の形成に塗布法を用いてもよい。 -Formation of adhesive layer-
The adhesive layer is an adhesive layer containing at least one resin selected from ethylene vinyl acetate, acrylic resin, urethane resin, olefin resin, polyester, polyamide, and synthetic rubber, or a hot melt adhesive. Is preferable.
From the viewpoint of adhesive stability, the thickness of the adhesive layer formed by the pressure-sensitive adhesive or the hot-melt adhesive is preferably in the range of 20 μm to 80 μm in terms of dry film thickness, and preferably in the range of 30 μm to 60 μm. More preferred.
As a method for forming the adhesive on the decorative layer, any known method related to layer formation such as a transfer method and a coating method can be used.
From the viewpoint that an adhesive layer having a uniform thickness can be easily formed, it is preferable to use the transfer method.
Further, when the adhesive layer protective sheet is provided with irregularities as described later and the irregularities are transferred to the adhesive layer, a coating method may be used to form the adhesive.

（接着層保護シート）
本開示の加飾フィルムは、接着層の加飾層とは反対側の面に接着層保護シートを有する。
接着層保護シートとしては、合成樹脂フィルム（合成樹脂基材）、及び離型処理された合成樹脂フィルムなどを用いることができる。
接着層保護シートに用いられる合成樹脂基材には、接着層保護シートとして、表面に接着層を形成し、保持し得る強度を有する限り、特に制限はない。 (Adhesive layer protective sheet)
The decorative film of the present disclosure has an adhesive layer protective sheet on the surface of the adhesive layer opposite to the decorative layer.
As the adhesive layer protective sheet, a synthetic resin film (synthetic resin base material), a release-treated synthetic resin film, or the like can be used.
The synthetic resin base material used for the adhesive layer protective sheet is not particularly limited as long as it has a strength capable of forming an adhesive layer on the surface and holding the adhesive layer protective sheet.

接着層保護シートにおける合成樹脂基材に用いうる合成樹脂としては、ポリエチレン（ＰＥ）、ポリプロピレン（ＰＰ）等のオレフィン樹脂、ポリエチレンテレフタレート（ＰＥＴ）、ポリエチレンナフタレート（ＰＥＮ）等が挙げられ、なかでも、寸法安定性の観点から、ＰＰ及びＰＥＴが好ましい。合成樹脂基材は、無延伸基材であっても、一軸又は二軸延伸基材であってもよい。 Examples of the synthetic resin that can be used as the synthetic resin base material in the adhesive layer protective sheet include olefin resins such as polyethylene (PE) and polypropylene (PP), polyethylene terephthalate (PET), polyethylene naphthalate (PEN), and the like. , PP and PET are preferable from the viewpoint of dimensional stability. The synthetic resin base material may be a non-stretched base material or a uniaxially or biaxially stretched base material.

接着層保護シートの厚みは、強度、作業性、及び取扱い性がより良好であるという観点からは、５μｍ～１００μｍであることが好ましく、４０μｍ～８０μｍであることがより好ましい。
接着層保護シートの厚みが上記範囲であることで、接着層保護シートをラミネートする際、剥離する際の作業性がより良好となり、接着層保護シートをロール状に巻き取ることができ、保存、搬送等をより容易に行えるため取り扱い性が良好となる。 The thickness of the adhesive layer protective sheet is preferably 5 μm to 100 μm, more preferably 40 μm to 80 μm, from the viewpoint of better strength, workability, and handleability.
When the thickness of the adhesive layer protective sheet is within the above range, the workability at the time of laminating and peeling the adhesive layer protective sheet becomes better, and the adhesive layer protective sheet can be wound into a roll shape and stored. Since it can be transported more easily, it is easy to handle.

接着層保護シートの接着剤と接する側の面は平滑であってもよく、凹凸を有していてもよい。
なかでも、接着層保護シートが凹凸を有する場合、接着層保護シートの凸部に対応して形成される接着層の凹部が、加飾積層体を成形体に貼り付ける際に、空気や水分などの流体の流通経路となり、所望されない流体がより速やかに排出され、貼り付け性が向上するという観点から好ましい。
接着層保護シート表面の凹凸は、接着層保護シートを構成する合成樹脂基材をエンボス加工することにより設けることができる。
接着層保護シート表面の凹凸に接して、接着層を設けることで、接着層の接着層保護シート表面と接する側の表面に、接着層保護シート表面の凹凸により形成された凹凸が形成される。
成形体に加飾積層体を密着させる際の流体の除去性がより向上するという観点からは、接着層の接着層保護シート表面と接する側の表面に、接着層保護シート表面の凹凸により形成された凹凸を有し、前記接着層表面の凹凸を、前記接着層表面の全面に亘り有することが好ましく、なかでも、凹凸の凹部が、接着層保護シートの端部に至るまでは連続的に形成されていることがより好ましい。 The surface of the adhesive layer protective sheet on the side in contact with the adhesive may be smooth or may have irregularities.
In particular, when the adhesive layer protective sheet has irregularities, the concave portions of the adhesive layer formed corresponding to the convex portions of the adhesive layer protective sheet are such as air and moisture when the decorative laminate is attached to the molded body. It is preferable from the viewpoint that it becomes a flow path for the fluid of the above, the undesired fluid is discharged more quickly, and the stickability is improved.
The unevenness on the surface of the adhesive layer protective sheet can be provided by embossing the synthetic resin base material constituting the adhesive layer protective sheet.
By providing the adhesive layer in contact with the unevenness of the surface of the adhesive layer protective sheet, the unevenness formed by the unevenness of the surface of the adhesive layer protective sheet is formed on the surface of the adhesive layer on the side in contact with the surface of the adhesive layer protective sheet.
From the viewpoint of further improving the fluid removability when the decorative laminate is brought into close contact with the molded body, it is formed on the surface of the adhesive layer on the side in contact with the surface of the adhesive layer protective sheet due to the unevenness of the surface of the adhesive layer protective sheet. It is preferable that the surface of the adhesive layer has irregularities over the entire surface of the adhesive layer, and in particular, concave portions of the irregularities are continuously formed up to the end of the adhesive layer protective sheet. It is more preferable that it is.

（その他の層）
本開示の加飾フィルムは、加飾層、接着層及び接着層保護シートに加え、目的に応じて任意の層（その他の層と称する）をさら設けてもよい。
その他の層としては、耐久性をより向上させる目的で、加飾層の、接着層を有する面とは反対側の面、即ち、加飾フィルムの表面に設けられる表皮層、加飾層と接着層との密着性をより向上させる目的で設けられるプライマー層、加飾積層体の剥離部と非剥離部との視認性を向上させる目的で設けられる加飾層とは異なる色相の着色シートなどが挙げられる。 (Other layers)
In the decorative film of the present disclosure, in addition to the decorative layer, the adhesive layer and the adhesive layer protective sheet, an arbitrary layer (referred to as another layer) may be further provided depending on the purpose.
As the other layer, for the purpose of further improving the durability, the surface of the decorative layer opposite to the surface having the adhesive layer, that is, the skin layer provided on the surface of the decorative film and the decorative layer are adhered to each other. A primer layer provided for the purpose of further improving the adhesion to the layer, a colored sheet having a hue different from that of the decorative layer provided for the purpose of improving the visibility between the peeled portion and the non-peeled portion of the decorative laminate, etc. Can be mentioned.

（表皮層）
本開示の加飾フィルムは、表皮層を有していてもよい。
表皮層は、加飾フィルムの最表面に設けられ、表皮層により、加飾フィルムに耐久性を付与することができる。
表皮層は、合成樹脂を用いて形成されることが好ましい。
加飾フィルムの耐久性の観点から、表皮層は、フッ素樹脂、アクリル樹脂、ポリ塩化ビニル（ＰＶＣ）樹脂から選ばれる少なくとも１種の合成樹脂を含有することが好ましい。 (Epidermis layer)
The decorative film of the present disclosure may have a skin layer.
The skin layer is provided on the outermost surface of the decorative film, and the skin layer can impart durability to the decorative film.
The epidermis layer is preferably formed using a synthetic resin.
From the viewpoint of the durability of the decorative film, the skin layer preferably contains at least one synthetic resin selected from a fluororesin, an acrylic resin, and a polyvinyl chloride (PVC) resin.

表皮層に用い得るフッ素樹脂としては、分子内に１以上のフッ素原子を含有する樹脂が挙げられ、例えば、フッ素原子を含むオレフィンを重合して得られる樹脂等が挙げられる。
フッ素樹脂としては、より具体的には、四フッ化エチレン樹脂、三フッ化塩化エチレン樹脂、六フッ化エチレンプロピレン樹脂、エチレン－四フッ化エチレン共重合体、フッ化ビニリデン樹脂等が挙げられる。 Examples of the fluororesin that can be used for the skin layer include resins containing one or more fluorine atoms in the molecule, and examples thereof include resins obtained by polymerizing an olefin containing a fluorine atom.
More specific examples of the fluororesin include an ethylene tetrafluoride resin, an ethylene trifluoride resin, an ethylene hexafluoride propylene resin, an ethylene-ethylene tetrafluoride copolymer, and a vinylidene fluoride resin.

表皮層に用い得るアクリル樹脂、及びポリ塩化ビニル（ＰＶＣ）樹脂としては、加飾層に用いる合成樹脂と同様の樹脂を挙げることができる。 Examples of the acrylic resin and polyvinyl chloride (PVC) resin that can be used for the skin layer include resins similar to the synthetic resin used for the decorative layer.

表皮層は、Ｔダイなどで押出し成形する押出し法、カレンダー法、キャスティング法等を適用して形成してもよく、市販のフィルムを適用して形成してもよい。
表皮層の厚みは、耐久性及び凹凸模様を形成した際の凹凸模様保持性の観点から、５μｍ～１００μｍが好ましく、１０μｍ～６０μｍがより好ましい。 The skin layer may be formed by applying an extrusion method, a calendar method, a casting method or the like which is extruded by T-die or the like, or may be formed by applying a commercially available film.
The thickness of the epidermis layer is preferably 5 μm to 100 μm, more preferably 10 μm to 60 μm, from the viewpoint of durability and retention of the uneven pattern when the uneven pattern is formed.

（プライマー層）
本開示の加飾フィルムは、加飾層と接着層との密着性をより向上させることを目的として、加飾層と接着層との間にプライマー層を設けてもよい。
プライマー層は、例えば、プライマー層形成用の樹脂を適切な溶媒で溶解し、加飾層の裏面に塗布し、乾燥して形成することができる。
プライマー層の形成に用いる樹脂は、加飾層に含まれる合成樹脂、及び、接着層に含まれる接着剤又は粘着剤としての樹脂との親和性の観点から、ポリエステル樹脂等を含んで形成されることが好ましい。
プライマー層の塗布量には特に制限はなく、目的に応じて適宜選択される。一般的には、接着性向上効果の観点から、１ｇ／ｍ２～５ｇ／ｍ２の範囲であることが好ましく、２ｇ／ｍ２～３ｇ／ｍ２の範囲であることがさらに好ましい。 (Primer layer)
In the decorative film of the present disclosure, a primer layer may be provided between the decorative layer and the adhesive layer for the purpose of further improving the adhesion between the decorative layer and the adhesive layer.
The primer layer can be formed, for example, by dissolving a resin for forming a primer layer with an appropriate solvent, applying it to the back surface of the decorative layer, and drying it.
The resin used for forming the primer layer is formed by including a synthetic resin contained in the decorative layer and a polyester resin or the like from the viewpoint of compatibility with the adhesive contained in the adhesive layer or the resin as an adhesive. Is preferable.
The amount of the primer layer applied is not particularly limited, and is appropriately selected depending on the intended purpose. Generally, from the viewpoint of the effect of improving the adhesiveness, the range is preferably 1 g / m 2 to 5 g / m 2 , and more preferably 2 g / m 2 to 3 g / m 2 .

（加飾層とは異なる色相の着色シート）
本開示の加飾フィルムは、加飾層の、接着層側とは反対の面に、さらに、加飾層とは異なる色相の着色シートを有していてもよい。
加飾層とは異なる色相の着色シート（以下、単に「着色シート」と称することがある）は、加飾積層体の剥離部と非剥離部との区画の視認性を向上させる目的で加飾フィルムの表面に設けられる。
着色シートにおける「色相」は、無彩色も含む意味で用いられる。加飾層が無彩色、例えば、加飾層が白色の場合、着色シートとして黒色のシートを有する例等が挙げられる。加飾層が有色の場合、例えば、加飾層の色相に対し、色相環の反対の位置にある補色又はそれに近い色の着色シートを有する例が挙げられ、加飾層の色相とは対照的な色相の着色シートを選択することが好ましい。
着色シートは、合成樹脂製、紙製等の任意のものでよく、市販品であってもよい。着色シートの、加飾フィルムの表皮層又は加飾層と接触する側の面は、粘着層を有し、着色シートを剥離するまでの間、安定して固定化されることが好ましい。なお、着色シートが有する粘着層の粘着性は、接着層において述べたと同程度の低粘着性であることが、着色シートの安定な固定化と、剥離しやすさとの両立という観点から好ましい。
着色シートの使用方法については、加飾成形体の製造方法において詳述する。 (Colored sheet with a different hue from the decorative layer)
The decorative film of the present disclosure may further have a colored sheet having a hue different from that of the decorative layer on the surface of the decorative layer opposite to the adhesive layer side.
A colored sheet having a hue different from that of the decorative layer (hereinafter, may be simply referred to as a “colored sheet”) is decorated for the purpose of improving the visibility of the section between the peeled portion and the non-peeled portion of the decorative laminate. It is provided on the surface of the film.
"Hue" in a colored sheet is used to mean including achromatic color. When the decorative layer is achromatic, for example, when the decorative layer is white, an example of having a black sheet as a colored sheet can be mentioned. When the decorative layer is colored, for example, there is an example in which a colored sheet having a complementary color or a color close to the complementary color at the position opposite to the hue of the decorative layer is provided, which is in contrast to the hue of the decorative layer. It is preferable to select a colored sheet having a different hue.
The colored sheet may be any one made of synthetic resin, paper, or the like, and may be a commercially available product. It is preferable that the surface of the colored sheet on the skin layer of the decorative film or the surface on the side in contact with the decorative layer has an adhesive layer and is stably fixed until the colored sheet is peeled off. The adhesiveness of the adhesive layer of the colored sheet is preferably as low as that described in the adhesive layer from the viewpoint of both stable immobilization of the colored sheet and ease of peeling.
The method of using the colored sheet will be described in detail in the method of manufacturing a decorative molded product.

（切り取り線）
本開示の加飾フィルムの層構成は、上記の通りである。
上記層構成を有する加飾フィルムには、加飾積層体の剥離部と非剥離部とを区画するための切り取り線を有する。切り取り線の深さは、加飾層の厚みに対し、加飾層の表面側から１００％未満である。
本開示においては、前記剥離部と非剥離部とを区画する切れ込みであって、加飾層に形成された切れ込みが加飾フィルムの平面視にて線状に連続して形成された状態を「切り取り線」と称する。切り取り線における切れ込みの深さは、加飾層の厚みに対し、加飾層の表面側から１００％未満であり、加飾フィルムの切り取り線で区画された剥離部を剥離することにより、加飾フィルムの被着体に、加飾フィルムによるデザインパターンが形成される。 (Cut line)
The layer structure of the decorative film of the present disclosure is as described above.
The decorative film having the above-mentioned layer structure has a cut line for partitioning the peeled portion and the non-peeled portion of the decorative laminated body. The depth of the cut line is less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer.
In the present disclosure, a notch that separates the peeled portion and the non-peeled portion, and a state in which the notch formed in the decorative layer is continuously formed linearly in a plan view of the decorative film is defined as ". It is called "cut line". The depth of cut in the cut line is less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer, and the peeling portion partitioned by the cut line of the decorative film is peeled off for decoration. A design pattern made of a decorative film is formed on the adherend of the film.

加飾フィルムにおいて、加飾積層体の剥離部と非剥離部とを区画する切り取り線の深さは、剥離部と非剥離部との連繋性、及び、剥離部の剥離容易性を両立しうるという観点から、加飾層の厚みを１００％としたとき、加飾層の表面側から２５％以上の深さであることが好ましく、６０％以上の深さであることがより好ましい。切り取り線の深さは、加飾層の厚みに対し、加飾層の表面側から１００％未満であり、加飾層の表面側から９８％以下の深さであることが好ましい。
即ち、加飾層における切り取り線の深さは、加飾層の厚みに対し、加飾層の表面側から２５％以上１００％未満であることが好ましい。
切り取り線の深さが、上記範囲にあることで、加飾フィルムの剥離部を、切り取り線の形状に沿って、特に力を加えることなく、容易に剥離することが可能となり、切り取り線の形状に対応するデザイン性に優れるデザインパターンを有する意匠表現がより容易に実現できる。 In the decorative film, the depth of the cut line that separates the peeled portion and the non-peeled portion of the decorative laminated body can achieve both the connection between the peeled portion and the non-peeled portion and the ease of peeling of the peeled portion. From this point of view, when the thickness of the decorative layer is 100%, the depth is preferably 25% or more, more preferably 60% or more from the surface side of the decorative layer. The depth of the cut line is preferably less than 100% from the surface side of the decorative layer and 98% or less from the surface side of the decorative layer with respect to the thickness of the decorative layer.
That is, the depth of the cut line in the decorative layer is preferably 25% or more and less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer.
When the depth of the cut line is within the above range, the peeled portion of the decorative film can be easily peeled along the shape of the cut line without applying any particular force, and the shape of the cut line can be easily peeled. It is possible to more easily realize a design expression having a design pattern having an excellent design property corresponding to the above.

図１により、切り取り線の深さについて説明する。加飾層１２における切り取り線２０において、図１において、加飾層１２の厚みをαとし、切り取り線２０の深さをβとした場合、αとβとは、下記式に表される関係にある。
α＞β 式
好ましくは、α＞β≧（α×０．２５）であり、
より好ましくは、（α×０．９８）≧β≧（α×０．６０）である。 The depth of the cut line will be described with reference to FIG. In the cut line 20 of the decorative layer 12, when the thickness of the decorative layer 12 is α and the depth of the cut line 20 is β in FIG. 1, α and β have a relationship represented by the following formula. be.
α> β equation Preferably, α> β ≧ (α × 0.25).
More preferably, (α × 0.98) ≧ β ≧ (α × 0.60).

切り取り線の深さが２５％未満である場合には、剥離部の剥離により高い応力を要するため、剥離部の剥離が容易に行えない懸念がある。
また、切り取り線の深さが、加飾層の厚みに対し、１００％以上となった場合、具体的には、切り取り線の深さが加飾層の厚みに対して１００％以上となり、切り込み線の先端が接着層に到達する場合（１００％深さ）、又は、接着層の内部まで到達する場合（１００％を超える深さ）等でも、剥離部と非剥離部との区画は行うことができるが、剥離部と非剥離部との連繋性が低くなり、加飾フィルムから接着層保護シートを剥離する際に、慎重に剥離しないと、加飾積層体の剥離部と非剥離部とが分離する懸念があるため、好ましくない。 If the depth of the cut line is less than 25%, a high stress is required to peel off the peeled portion, and there is a concern that the peeled portion cannot be easily peeled off.
Further, when the depth of the cut line is 100% or more with respect to the thickness of the decorative layer, specifically, the depth of the cut line is 100% or more with respect to the thickness of the decorative layer, and the cut is made. Even when the tip of the wire reaches the adhesive layer (100% depth) or reaches the inside of the adhesive layer (depth exceeding 100%), the peeled portion and the non-peeled portion should be separated. However, the connection between the peeled part and the non-peeled part becomes low, and when peeling the adhesive layer protective sheet from the decorative film, if it is not peeled carefully, the peeled part and the non-peeled part of the decorative laminate Is not preferable because there is a concern that it will separate.

本開示の加飾フィルムは、剥離部の剥離を効率よく行う目的で、剥離部は、剥離補助部を有していてもよい。
剥離補助部は、剥離部をめくり易くするために設けられる部分構造であり、剥離部に凹部を設けて、凹部の端部をつまんで剥離する態様、剥離部に突出部（タブ）を設けて、タブをつまんで剥離する態様が挙げられる。 The decorative film of the present disclosure may have a peeling auxiliary portion for the purpose of efficiently peeling the peeling portion.
The peeling auxiliary portion has a partial structure provided to facilitate turning of the peeling portion. A recess is provided in the peeling portion, and an end portion of the recess is pinched for peeling, and a protrusion (tab) is provided in the peeling portion. , The mode of pinching the tab and peeling it off can be mentioned.

図２は、剥離部に凹部を設けた状態の一例を示す概略部分平面図である。図２では、剥離補助部である凹部２１Ａは、破線で囲まれた部分に形成されている。図２の平面図に示す破線２０は、加飾層に設けられた切り取り線２０を表し、Ａが剥離部を示し、Ｂが非剥離部を示す。図２に示すように、加飾フィルムの端部に、先端が鋭角となる三角形状の凹部（剥離補助部）２１Ａを有する場合、凹部の先端とは反対側の加飾フィルムの端部において剥離部をつまむことで剥離部をより剥離しやすくなる。
図２では、剥離補助部である凹部２１Ａは、三角形状の凹部であるが、凹部の形状には制限はなく、任意の形状を選択することができる。
図２に示す如く、剥離補助部としての凹部が三角形状の凹部である場合、凹部の頂部、即ち、２本の線の交差する三角形の頂部の角度は鋭角であることが、剥離がより容易に行えるという観点から好ましい。 FIG. 2 is a schematic partial plan view showing an example of a state in which a recess is provided in the peeled portion. In FIG. 2, the recess 21A, which is a peeling auxiliary portion, is formed in a portion surrounded by a broken line. The broken line 20 shown in the plan view of FIG. 2 represents a cut line 20 provided on the decorative layer, where A indicates a peeled portion and B indicates a non-peeled portion. As shown in FIG. 2, when the decorative film has a triangular recess (peeling auxiliary portion) 21A having an acute-angled tip, the decorative film is peeled at the edge opposite to the tip of the recess. By pinching the part, it becomes easier to peel off the peeled part.
In FIG. 2, the recess 21A, which is the peeling auxiliary portion, is a triangular recess, but the shape of the recess is not limited, and any shape can be selected.
As shown in FIG. 2, when the concave portion as the peeling auxiliary portion is a triangular concave portion, it is easier to peel off if the angle of the top of the concave portion, that is, the top of the triangle where the two lines intersect is an acute angle. It is preferable from the viewpoint that it can be done easily.

図３は、剥離部に剥離補助部であるタブ２１Ｂを設けた態様を示す概略平面図である。図３では、矢印に示される箇所がタブ２１Ｂであり、剥離部は加飾フィルムの端部に突出したタブ、即ち、凸状の剥離補助部２１Ｂをつまむことで容易に剥離できる。図３の平面図に示す破線２０は、加飾層に設けられた切り取り線２０を表し、切り取り線２０で囲まれた領域Ａが剥離部を示し、領域Ｂが非剥離部を示す。
図３では、タブである凸部の形状は、平行四辺形の形状が示されるが、タブの形状には特に制限はなく、任意の形状を選択することができる。
タブは、加飾フィルムの製造時に、例えば、後述する加飾フィルムの製造方法において、工程ＩＶで第二切り取り線を加飾フィルム前駆体に形成する際に、第二切り取り線の形成と同時に、図３に仮想線としての一点破線で示す如き第二切り取り線を形成することで、凸部としてのタブ２１Ｂを容易に形成することができる。 FIG. 3 is a schematic plan view showing a mode in which the tab 21B, which is a peeling auxiliary portion, is provided on the peeling portion. In FIG. 3, the portion indicated by the arrow is the tab 21B, and the peeling portion can be easily peeled off by pinching the tab protruding from the end portion of the decorative film, that is, the convex peeling auxiliary portion 21B. The broken line 20 shown in the plan view of FIG. 3 represents a cut line 20 provided on the decorative layer, a region A surrounded by the cut line 20 shows a peeled portion, and a region B shows a non-peeled portion.
In FIG. 3, the shape of the convex portion as the tab is shown as a parallelogram shape, but the shape of the tab is not particularly limited, and any shape can be selected.
The tab is used at the same time as the formation of the second cut line when the second cut line is formed on the decorative film precursor in the step IV, for example, in the method of manufacturing the decorative film described later, when the decorative film is manufactured. By forming the second cut line as shown by the alternate long and short dash line in FIG. 3, the tab 21B as the convex portion can be easily formed.

本開示の加飾フィルムは、前記構成としたため、転写シートを用いることなく、任意のデザインパターンを被着体に容易に形成することができる。本開示の加飾フィルムによれば、複雑なデザインパターンを任意の成形体に設けることができ、その応用範囲は広い。応用範囲としては、車両の外装材、建造物の内外装材、窓等のディスプレイ、船舶の内外装などが挙げられるが、これに限定されない。 Since the decorative film of the present disclosure has the above-mentioned structure, an arbitrary design pattern can be easily formed on the adherend without using a transfer sheet. According to the decorative film of the present disclosure, a complicated design pattern can be provided on an arbitrary molded body, and its application range is wide. The range of application includes, but is not limited to, vehicle exterior materials, building interior / exterior materials, windows and other displays, and ship interior / exterior materials.

本開示の加飾フィルムの製造方法には特に制限はないが、以下に述べる本開示の加飾フィルムの製造方法により製造することで効率よく、複雑なデザインパターンを有する加飾成フィルムが製造できる。 The method for producing the decorative film of the present disclosure is not particularly limited, but the decorative film having a complicated design pattern can be efficiently produced by producing the decorative film according to the present disclosure described below. ..

［加飾フィルムの製造方法］
本開示の加飾フィルムの製造方法（以下、本開示の製造方法Ａと称することがある）は、加飾層の一方の面に、接着層を形成して加飾積層体を形成する工程（工程Ｉ）と、前記接着層を接着層保護シートにより被覆して、加飾層と接着層と接着層保護シートとを有する加飾フィルム前駆体を形成する工程（工程ＩＩ）と、前記加飾層に、前記剥離部と非剥離部とを区画する、深さが、加飾層の厚みに対し、加飾層の表面側から１００％未満である第一切り取り線を形成する工程（工程ＩＩＩ）と、前記加飾フィルム前駆体を貫通する第二切り取り線を、前記第一切り取り線との交部が生じる位置に形成する工程（工程ＩＶ）と、を有する成形体の加飾に用いられる加飾フィルムの製造方法である。 [Manufacturing method of decorative film]
The method for producing a decorative film of the present disclosure (hereinafter, may be referred to as the production method A of the present disclosure) is a step of forming an adhesive layer on one surface of the decorative layer to form a decorative laminated body (hereinafter, may be referred to as a decorative laminate). Step I), a step of covering the adhesive layer with an adhesive layer protective sheet to form a decorative film precursor having a decorative layer, an adhesive layer, and an adhesive layer protective sheet (step II), and the decoration. A step of forming a first cutting line (step III) in which the depth of the layer is less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer, which divides the peeled portion and the non-peeled portion. ), And a step (step IV) of forming a second cut line penetrating the decorative film precursor at a position where an intersection with the first cut line occurs, is used for decorating a molded product. This is a method for manufacturing a decorative film.

（工程Ｉ）
工程Ｉでは、加飾層の一方の面に、接着層を形成して加飾積層体を形成する。
まず、加飾層形成用の合成樹脂を含む加飾層形成用組成物を用いて、加飾層を形成し、得られた加飾層の一方の面に、接着層を形成して、加飾積層体を得る。
加飾層及び接着層の形成方法は既述の通りである。
即ち、加飾層は、合成樹脂として、好ましくは、ＰＶＣ樹脂、アクリル樹脂及びＡＢＳ樹脂から選ばれる少なくとも１種を含み、所望により着色剤を含む加飾層形成用組成物をカレンダー法等によりシート状に成形して形成することが好ましい。
接着層は常法により形成することができ、好ましくは、接着層の形成に用いられる粘着剤又はホットメルト接着剤を用いて、塗布法又は転写法により形成すればよい。
加飾層及び接着層の好ましい厚みは、加飾フィルムの説明において述べたとおりである。
得られた加飾積層体が、成形体に付与されて成形体の加飾に適用される。 (Step I)
In step I, an adhesive layer is formed on one surface of the decorative layer to form a decorative laminate.
First, a decorative layer is formed using a decorative layer forming composition containing a synthetic resin for forming a decorative layer, and an adhesive layer is formed on one surface of the obtained decorative layer to add the decorative layer. Obtain a decorative laminate.
The method for forming the decorative layer and the adhesive layer is as described above.
That is, the decorative layer contains at least one selected from PVC resin, acrylic resin and ABS resin as the synthetic resin, and if desired, a decorative layer forming composition containing a colorant is sheeted by a calendar method or the like. It is preferably formed by molding into a shape.
The adhesive layer can be formed by a conventional method, and preferably, it may be formed by a coating method or a transfer method using an adhesive or a hot melt adhesive used for forming the adhesive layer.
The preferable thicknesses of the decorative layer and the adhesive layer are as described in the description of the decorative film.
The obtained decorative laminate is applied to the molded body and applied to the decoration of the molded body.

工程Ｉでは、加飾層の形成後に、プライマー層を形成し、その後、接着層を形成する工程（工程Ｖ）を有していてもよい。プライマー層を設けることにより、加飾層と接着層との密着性をより向上させることができる。
プライマー層の形成に用いられる樹脂の種類、プライマー層の厚みなどは既述のとおりである。プライマー層の形成工程である工程Ｖは、任意の工程である。 In step I, there may be a step (step V) of forming a primer layer after forming a decorative layer and then forming an adhesive layer. By providing the primer layer, the adhesion between the decorative layer and the adhesive layer can be further improved.
The type of resin used to form the primer layer, the thickness of the primer layer, and the like are as described above. Step V, which is a step of forming the primer layer, is an arbitrary step.

（工程ＩＩ）
工程ＩＩでは、接着層保護シートを準備し、準備した接着層保護シートにより、接着層を被覆して、加飾層と接着層と接着層保護シートとを有する加飾フィルム前駆体を形成する。本開示において「加飾フィルム前駆体」とは、加飾層、接着層及び接着層保護シートを有する積層体であって、剥離部と非剥離部との区画をするための切り取り線が形成されていない積層体を指す。
接着層保護シートは、加飾フィルムの項で説明したように、接着層と接する側の面は平滑であるか、又は凹凸を有するフィルムであって、合成樹脂フィルム、離型処理された合成樹脂フィルム等を用いることができる。
接着層保護シートの好ましい厚みは、加飾フィルムの項で述べたとおりである。接着層保護シートの一方の面が離型処理されている場合には、離型処理された面を、加飾積層体の接着層と接するように接着層を被覆すればよい。
接着層保護シートは、市販品を用いてもよい。 (Step II)
In step II, an adhesive layer protective sheet is prepared, and the adhesive layer is coated with the prepared adhesive layer protective sheet to form a decorative film precursor having a decorative layer, an adhesive layer, and an adhesive layer protective sheet. In the present disclosure, the "decorative film precursor" is a laminate having a decorative layer, an adhesive layer, and an adhesive layer protective sheet, and a cut line for partitioning a peeled portion and a non-peeled portion is formed. Refers to a laminate that is not.
As described in the section of the decorative film, the adhesive layer protective sheet is a film whose surface in contact with the adhesive layer is smooth or has irregularities, and is a synthetic resin film or a release-treated synthetic resin. A film or the like can be used.
The preferable thickness of the adhesive layer protective sheet is as described in the section of the decorative film. When one surface of the adhesive layer protective sheet is mold-released, the adhesive layer may be coated so that the mold-released surface is in contact with the adhesive layer of the decorative laminate.
A commercially available product may be used as the adhesive layer protective sheet.

（工程ＩＩＩ）
工程ＩＩＩは、工程ＩＩにおいて得られた加飾フィルム前駆体の前記加飾層に、前記剥離部と非剥離部とを区画する、深さが、加飾層の厚みに対し、加飾層の表面側から１００％未満である第一切り取り線を形成する工程である。第一切り取り線の形成は、カッティング装置により行うことができる。任意の深さの切り取り線を形成できるカッティング装置であれば、特に制限なく用いることができる。
工程ＩＩＩでは、カッティング装置を使用し、加飾層の表面側から刃を入れ、加飾層に第一切り取り線を形成する。カッティング装置に使用する刃種は任意のものでよい。
カッティング装置のカッターヘッドに把持したカッター（刃）を、加飾層に押接させながら、カッターヘッドをＸ－Ｙ方向に移動させることにより、所望の形状の第一切り取り線２６を加飾層に形成すればよい。 (Step III)
In step III, the peeled portion and the non-peeled portion are partitioned into the decorative layer of the decorative film precursor obtained in step II, and the depth of the decorative layer is relative to the thickness of the decorative layer. This is a step of forming a first cut line that is less than 100% from the surface side. The formation of the first cutting line can be performed by a cutting device. Any cutting device capable of forming a cutting line of an arbitrary depth can be used without particular limitation.
In step III, a cutting device is used to insert a blade from the surface side of the decorative layer to form a first cutting line in the decorative layer. The blade type used for the cutting device may be arbitrary.
By moving the cutter head in the XY directions while pressing the cutter (blade) gripped by the cutter head of the cutting device against the decorative layer, the first cutting line 26 having a desired shape is formed into the decorative layer. It may be formed.

図４は、矩形の加飾フィルム前駆体２４に第一切り取り線２６を形成した状態の一態様を示す概略平面図である。第一切り取り線２６は、所定の深さで連続して形成され、実線で表示すべきところ、図４では、第一切り取り線２６は、他の線との区別を明確にするため、便宜上、破線で示している。図４に示す態様では、非剥離部は、複雑なデザインパターンをなす連続した領域である。工程ＩＩＩでは、第一切り取り線により、任意のデザインパターンを加飾フィルム前駆体に形成する。第一切り取り線の深さは、加飾層の厚みを１００％とした場合、加飾層の表面側から２５％以上１００％未満の深さであることが、剥離部と非剥離部との連繋性、及び、剥離部の剥離容易性を両立しうるという観点から好ましい。 FIG. 4 is a schematic plan view showing an aspect of a state in which the first cutting line 26 is formed on the rectangular decorative film precursor 24. The first cut line 26 is formed continuously at a predetermined depth and should be indicated by a solid line. However, in FIG. 4, the first cut line 26 is used for convenience in order to clearly distinguish it from other lines. It is shown by a broken line. In the aspect shown in FIG. 4, the non-peeling portion is a continuous region forming a complicated design pattern. In step III, an arbitrary design pattern is formed on the decorative film precursor by the first cutting line. When the thickness of the decorative layer is 100%, the depth of the first cut line is 25% or more and less than 100% from the surface side of the decorative layer. It is preferable from the viewpoint that both the connectivity and the ease of peeling of the peeled portion can be achieved.

（工程ＩＶ）
工程ＩＶでは、前記加飾フィルム前駆体を貫通する第二切り取り線を、前記第一切り取り線との交部が生じる位置に形成する。
工程ＩＶでは、加飾層の表面側から刃を入れ、加飾層、接着層及び接着層保護シートを有する加飾フィルム前駆体を貫通する第二切り取り線を形成する。
第二切り取り線の形成に使用する刃種は任意のものでよい。工程ＩＶでは、第二切り取り線の形成に用いられるカッティング装置のカッターヘッドに把持したカッター（刃）を、加飾層に押接させながら、カッターヘッドをＸ－Ｙ方向に移動させることにより、加飾フィルム前駆体を貫通する第二切り取り線を形成する。
第二切り取り線の形成に際して、第二切り取りを第一切り取り線との交部が生じる位置に形成する。その結果、第二切り取り線と第一切り取り線との交部を有する剥離部が形成される。 (Step IV)
In step IV, a second cut line penetrating the decorative film precursor is formed at a position where an intersection with the first cut line occurs.
In step IV, a blade is inserted from the surface side of the decorative layer to form a second cut line penetrating the decorative film precursor having the decorative layer, the adhesive layer and the adhesive layer protective sheet.
The blade type used to form the second cutting line may be arbitrary. In step IV, the cutter (blade) gripped by the cutter head of the cutting device used for forming the second cutting line is pressed against the decorative layer, and the cutter head is moved in the XY directions. A second cut line is formed through the decorative film precursor.
When forming the second cut line, the second cut is formed at a position where an intersection with the first cut line occurs. As a result, a peeling portion having an intersecting portion between the second cutting line and the first cutting line is formed.

図５は、第一切り取り線２６を形成した矩形の加飾フィルム前駆体２４に、第二切り取り線２８を形成した状態の一態様を示す概略平面図である。図５では、第二切り取り線２８は一点破線で示される。
矢印で明示した箇所が、第一切り取り線２６と第二切り取り線２８との交部である。
第二切り取り線の形成により、加飾フィルム１０を得る。
既述のように、第二切り取り線の形成時に、加飾フィルム前駆体において、剥離部に相当する領域の端部に凸部を設ける形状で第二切り取り線を形成することで、工程ＩＶにおいて、剥離補助部としての凸部（タブ）を形成することができる。 FIG. 5 is a schematic plan view showing an aspect of a state in which the second cut line 28 is formed on the rectangular decorative film precursor 24 on which the first cut line 26 is formed. In FIG. 5, the second cut line 28 is indicated by a dashed line.
The part indicated by the arrow is the intersection of the first cutting line 26 and the second cutting line 28.
The decorative film 10 is obtained by forming the second cut line.
As described above, in step IV, when the second cut line is formed, the second cut line is formed in the decorative film precursor in a shape in which a convex portion is provided at the end of the region corresponding to the peeled portion. , A convex portion (tab) as a peeling auxiliary portion can be formed.

図６は、第二切り取り線の形成により、完成した加飾フィルムにおいて、第一切り取り線２６で区画された剥離部と非剥離部との一例を示す概略平面図である。図６では、非剥離部の領域がＢで示され、剥離部の領域がＡ－１～Ａ－７で示される。図６で斜線の領域Ｂが、非剥離部としてのデザインパターンとして成形体に固定される。図６に示すように、剥離部は、複数の領域に分割されることにより、非剥離部が鋭角的な先端を有する場合でも、容易に剥離することができ、剥離部を剥離する際に、非剥離部からなるデザインパターンの変形を抑制することができる。 FIG. 6 is a schematic plan view showing an example of a peeled portion and a non-peeled portion partitioned by the first cut line 26 in the decorative film completed by forming the second cut line. In FIG. 6, the region of the non-peeling portion is indicated by B, and the region of the peeling portion is indicated by A-1 to A-7. In FIG. 6, the shaded area B is fixed to the molded body as a design pattern as a non-peeling portion. As shown in FIG. 6, the peeled portion is divided into a plurality of regions so that the peeled portion can be easily peeled even when the non-peeled portion has an acute-angled tip, and when the peeled portion is peeled, the peeled portion can be easily peeled. Deformation of the design pattern composed of the non-peeling portion can be suppressed.

（任意の工程）
本開示の加飾フィルムの製造方法では、既述の工程Ｉ、工程ＩＩ、工程ＩＩＩ及び工程ＩＶに加え、任意の工程をさらに含むことができる。
任意の工程としては、既述のプライマー層を形成する工程（工程Ｖ）、表皮層を形成する工程（工程ＶＩ）、着色シートを付与する工程（工程ＶＩＩ）等が挙げられる。 (Arbitrary process)
The method for producing a decorative film of the present disclosure may further include any step in addition to the above-mentioned steps I, II, III and IV.
Examples of the optional step include a step of forming the above-mentioned primer layer (step V), a step of forming the epidermis layer (step VI), a step of applying a colored sheet (step VII), and the like.

（工程ＶＩ）
本開示の加飾フィルムの製造方法では、加飾層の接着層側とは反対の面に表皮層を形成する工程（工程ＶＩ）を有してもよい。
表皮層は、合成樹脂としてフッ素樹脂、アクリル樹脂、ポリ塩化ビニル樹脂から選ばれる少なくとも１種の樹脂を含有することが好ましい。表皮層の形成は、公知の方法により行うことができる。また、市販の表皮層を用いてもよい。
表皮層の形成は、加飾層の表面（接着層を有する側とは反対の面）に、成形した表皮層を積層することで行うことができる。
工程Ｉで得た加飾層に表皮層を積層させ、一対のロールを用いてラミネート加工を行い、両者を加熱圧着する方法が好ましく挙げられる。加熱圧着の際のラミネート温度は１００℃～１９０℃が好ましい。
表皮層を形成することで、加飾フィルムの耐久性をより向上させることができる。 (Process VI)
In the method for producing a decorative film of the present disclosure, a step (step VI) of forming a skin layer on a surface opposite to the adhesive layer side of the decorative layer may be provided.
The skin layer preferably contains at least one resin selected from fluororesin, acrylic resin, and polyvinyl chloride resin as the synthetic resin. The formation of the epidermis layer can be performed by a known method. Moreover, you may use a commercially available epidermis layer.
The skin layer can be formed by laminating the molded skin layer on the surface of the decorative layer (the surface opposite to the side having the adhesive layer).
A method in which a skin layer is laminated on the decorative layer obtained in step I, laminating is performed using a pair of rolls, and both are heat-bonded is preferable. The laminating temperature at the time of heat crimping is preferably 100 ° C. to 190 ° C.
By forming the skin layer, the durability of the decorative film can be further improved.

（工程ＶＩＩ）
本開示の加飾フィルムの製造方法では、剥離層と非剥離部との区画をより明確にするため、加飾層又は任意の層である表皮層の表面に着色シートを付与することができる。
着色シートを付与することで、剥離部と非剥離部とを色分けし、剥離部の視認性をより高めることができる。例えば、加飾層が白色であり、着色シートとして黒色のシートを用いることにより、まず、第一切り取り線に沿って、剥離部の着色シートを剥離することで、剥離部（黒色）と非剥離部（白色）との境界が鮮明となり、非剥離部のデザインパターンが、デザイン性に優れる複雑な形状であるとしても、剥離部のみを確実に剥離することがより容易となる。 (Process VII)
In the method for producing a decorative film of the present disclosure, a colored sheet can be applied to the surface of the decorative layer or an arbitrary layer, the epidermis layer, in order to make the division between the peeling layer and the non-peeling portion clearer.
By adding a colored sheet, the peeled portion and the non-peeled portion can be color-coded, and the visibility of the peeled portion can be further improved. For example, by using a white sheet for the decorative layer and a black sheet as the colored sheet, first, the colored sheet of the peeled portion is peeled along the first cutting line, so that the peeled portion (black) and the non-peeled portion are not peeled. The boundary with the portion (white) becomes clear, and even if the design pattern of the non-peeling portion has a complicated shape with excellent design, it becomes easier to reliably peel off only the peeled portion.

工程ＶＩＩは、既述の工程ＩＩＩ、即ち、第一切り取り線の形成前に行われる。
まず、加飾フィルムにおける加飾層の色相とは対照的な色相を有する着色シートを準備する。
着色シートは、合成樹脂製、紙製等の任意のものでよく、市販品を用いてもよい。着色シートは、加飾フィルムの加飾層又は表皮層と接触する側の面は、粘着層を有する物を用いる。既述のように、粘着層の粘着性は、一時的に着色シートを加飾フィルム前駆体に固定すればよいため、既述した接着層における低粘着性と同じ程度の粘着性であることが好ましい。
着色シートを、粘着層を介して、加飾フィルム前駆体の加飾層又は表皮層に積層する。得られた着色シートを有する加飾フィルム前駆体に対して、既述の第一切り取り線の形成工程（工程ＩＩＩ）及び第二切り取り線の形成工程（工程ＩＶ）を行って切り取り線を形成して、着色シートを有する加飾フィルムを得ることができる。 Step VII is performed before step III, i.e., the formation of the first cut line, as described above.
First, a colored sheet having a hue contrasting with the hue of the decorative layer in the decorative film is prepared.
The colored sheet may be any one made of synthetic resin, paper, or the like, and a commercially available product may be used. As the colored sheet, a material having an adhesive layer is used for the surface of the decorative film on the side in contact with the decorative layer or the skin layer. As described above, the adhesiveness of the adhesive layer may be the same as the low adhesiveness of the adhesive layer described above because the colored sheet may be temporarily fixed to the decorative film precursor. preferable.
The colored sheet is laminated on the decorative layer or the epidermis layer of the decorative film precursor via the adhesive layer. The decorative film precursor having the obtained colored sheet is subjected to the above-mentioned first cut line forming step (step III) and second cut line forming step (step IV) to form a cut line. A decorative film having a colored sheet can be obtained.

［加飾成形体］
本開示の加飾成形体は、成形体と、既述の本開示の加飾フィルムから前記接着層保護シート及び加飾積層体の剥離部が剥離された 加飾積層体の非剥離部と、を有する加飾成形体である。
図７は、本開示の加飾成形体の一例を示す概略断面図である。図７に示す加飾成形体３０は、成形体（成形体基材）３２と、成形体３２の面上に、接着層１４と、加飾層１２と、任意の層である表皮層１８とを有する加飾積層体の非剥離部を有する。
加飾成形体３０は、図１に示す加飾フィルム１０から接着層保護シート１６を剥離した加飾積層体を成形体３２に貼付し、その後、加飾積層体の剥離部を剥離することで形成される。 [Decorative molding]
The decorative molded body of the present disclosure includes a molded body, a non-peeled portion of the decorative laminated body in which the peeled portion of the adhesive layer protective sheet and the decorative laminated body is peeled off from the decorative film of the present disclosure described above. It is a decorative molded body having.
FIG. 7 is a schematic cross-sectional view showing an example of the decorative molded article of the present disclosure. The decorative molded body 30 shown in FIG. 7 includes a molded body (molded body base material) 32, an adhesive layer 14, a decorative layer 12, and an arbitrary layer, a skin layer 18, on the surface of the molded body 32. It has a non-peelable portion of the decorative laminate having.
The decorative molded body 30 is formed by attaching a decorative laminated body obtained by peeling the adhesive layer protective sheet 16 from the decorative film 10 shown in FIG. 1 to the molded body 32, and then peeling off the peeled portion of the decorative laminated body. It is formed.

本開示の加飾フィルムが適用される成形体には、特に制限はなく、樹脂成形体、自動車などの車両、窓ガラス、建造物の外装など、いずれにも適用することができる。
従って、本開示の加飾フィルムによれば、任意の成形体を被加飾体として、意匠性の高いデザインパターンを有する加飾成形体とすることができる。
本開示の加飾成形体は、本開示の加飾フィルムを用いて形成されるために、複雑なデザインパターンを有する意匠性に優れた加飾成形体となり、その応用範囲は広い。 The molded body to which the decorative film of the present disclosure is applied is not particularly limited, and can be applied to any of a resin molded body, a vehicle such as an automobile, a window glass, an exterior of a building, and the like.
Therefore, according to the decorative film of the present disclosure, an arbitrary molded body can be used as a decorative molded body to have a highly designed design pattern.
Since the decorative molded body of the present disclosure is formed by using the decorative film of the present disclosure, it is a decorative molded body having a complicated design pattern and excellent in design, and its application range is wide.

［加飾成形体の製造方法］
本開示の加飾成形体は、本開示の加飾成形体の製造方法により製造されることが好ましい。
本開示の加飾成形体の製造方法は、既述の本開示の加飾フィルムから接着層保護シートを剥離する工程（工程ｉ）、接着層保護シートを剥離した加飾積層体を、接着層を介して成形体の表面に貼り付ける工程（工程ｉｉ）、及び、前記成形体の表面に貼り付けた加飾積層体の剥離部を剥離する工程（工程ｉｉｉ）を有する。 [Manufacturing method of decorative molded product]
The decorative molded article of the present disclosure is preferably produced by the method for producing a decorative molded article of the present disclosure.
The method for producing a decorative molded article of the present disclosure is a step of peeling the adhesive layer protective sheet from the decorative film of the present disclosure described above (step i), and the decorative laminate from which the adhesive layer protective sheet has been peeled off is used as an adhesive layer. It has a step of sticking to the surface of the molded body (step ii) and a step of peeling off the peeled portion of the decorative laminate stuck to the surface of the molded body (step iii).

（工程ｉ）
工程ｉでは、本開示の加飾フィルムから接着層保護シートを剥離する。加飾フィルムから接着層保護シートを剥離して加飾積層体を形成することで、加飾積層体の接着層が露出する。 (Step i)
In step i, the adhesive layer protective sheet is peeled off from the decorative film of the present disclosure. By peeling the adhesive layer protective sheet from the decorative film to form the decorative laminate, the adhesive layer of the decorative laminate is exposed.

（工程ｉｉ）
工程ｉｉでは、加飾積層体の接着層を介して、加飾積層体を成形体の表面に貼り付ける。接着層保護シートの剥離と、加飾積層体の成形体への貼り付けは、作業者の手作業により、段階的に実施してもよい。即ち、工程ｉにおいて、接着層保護シートを徐々に剥離し、加飾積層体の接着層を部分的に露出させ、工程ｉで露出させた加飾積層体の接着層を、立体形状を有する成形体の表面に対向させ、加飾積層体を押圧することで、接着層を介して成形体の表面に貼り付ける。
上記の接着層保護シートの部分的な剥離と、引き続き行われる加飾積層体の貼り付けを交互に段階的に実施し、最終的に加飾積層体全体を成形体に貼り付けてもよい。
また、面積の小さい加飾フィルムの場合には、一段階で貼り付けてもよい。 (Step ii)
In step ii, the decorative laminate is attached to the surface of the molded product via the adhesive layer of the decorative laminate. The peeling of the adhesive layer protective sheet and the attachment of the decorative laminate to the molded body may be carried out step by step by the manual operation of the operator. That is, in step i, the adhesive layer protective sheet is gradually peeled off to partially expose the adhesive layer of the decorative laminate, and the adhesive layer of the decorative laminate exposed in step i is molded having a three-dimensional shape. By facing the surface of the body and pressing the decorative laminate, it is attached to the surface of the molded body via the adhesive layer.
The partial peeling of the adhesive layer protective sheet and the subsequent attachment of the decorative laminate may be carried out in a stepwise manner, and finally the entire decorative laminate may be attached to the molded body.
Further, in the case of a decorative film having a small area, it may be attached in one step.

（工程ｉｉｉ）
工程ｉｉｉでは、成形体の表面に貼り付けた加飾積層体の剥離部を剥離する。この工程ｉｉｉにより、成形体の面上には、加飾積層体の非剥離部のみが貼付され、加飾積層体の非剥離部からなるデザインパターンが成形体上に形成されて、加飾成形体を得る。 (Step iii)
In step iii, the peeled portion of the decorative laminate attached to the surface of the molded body is peeled off. By this step iii, only the non-peeling portion of the decorative laminate is attached on the surface of the molded body, and a design pattern composed of the non-peeling portion of the decorative laminate is formed on the molded body to perform decorative molding. Get the body.

既述の加飾フィルムの製造方法において任意の工程である工程ＶＩＩで得られた着色シートを有する加飾フィルムを用いて成形体を加飾する場合について説明する。
着色シートを有する加飾フィルムを成形体に貼付し、その後、着色シートの加飾フィルムの剥離部に対応する部位の着色シートのみを剥離する。加飾フィルムを成形体に貼り付ける前に、着色シートの加飾フィルムの剥離部に対応する部位の着色シートのみを剥離してもよい。
その結果、図８に概略断面図の一例として示すように、成形体３２の面上に、着色シート２２が貼付された、表皮層１８と加飾層１２と接着層１４とを有する加飾積層体が、接着層１４を介して貼り付けられる。加飾積層体の剥離部（領域Ａ）は着色シート２２を有さない領域となり、非剥離部（領域Ｂ）は、剥離部とは色相の異なる着色シート２２が貼付された領域となるため、加飾積層体の剥離部と非剥離部とのコントラストが際立ち、剥離部のみを確実に剥離することがより容易となる。
成形体に貼付した後、工程ｉｉｉで剥離部を剥離し、その後、非剥離部の上に残置している着色シート２２を剥離することで、図７に一例として示す如き層構成を有する本開示の加飾成形体３０が得られる。 A case where the molded product is decorated with the decorative film having the colored sheet obtained in the step VII, which is an arbitrary step in the method for producing the decorative film described above, will be described.
A decorative film having a colored sheet is attached to a molded body, and then only the colored sheet at a portion corresponding to the peeled portion of the decorative film of the colored sheet is peeled off. Before attaching the decorative film to the molded body, only the colored sheet at the portion corresponding to the peeled portion of the decorative film of the colored sheet may be peeled off.
As a result, as shown as an example of a schematic cross-sectional view in FIG. 8, a decorative laminate having a skin layer 18, a decorative layer 12, and an adhesive layer 14 having a colored sheet 22 attached on the surface of the molded body 32. The body is attached via the adhesive layer 14. The peeled portion (region A) of the decorative laminate is a region that does not have the colored sheet 22, and the non-peeled portion (region B) is a region to which the colored sheet 22 having a hue different from that of the peeled portion is attached. The contrast between the peeled portion and the non-peeled portion of the decorative laminate stands out, and it becomes easier to reliably peel only the peeled portion.
After being attached to a molded body, the peeled portion is peeled off in step iii, and then the colored sheet 22 left on the non-peeled portion is peeled off to have a layer structure as shown as an example in FIG. The decorative molded body 30 of the above is obtained.

本開示の加飾成形体は、任意の成形体に複雑なデザインパターンを有する成形体であり、本開示の加飾成形体の製造方法によれば、任意の成形体としては、自動車、鉄道等の車両、窓ガラス、家具、建装、壁装などが挙げられ、本開示の加飾成形体の製造方法によれば、これら種々の成形体に、複雑なデザインパターンの意匠を容易に付与できることから、その応用範囲は広い。 The decorative molded body of the present disclosure is a molded body having a complicated design pattern in an arbitrary molded body, and according to the manufacturing method of the decorative molded body of the present disclosure, the arbitrary molded body may be an automobile, a railway, or the like. Vehicles, window glass, furniture, construction, wall coverings, etc., and according to the method for manufacturing decorative molded bodies of the present disclosure, it is possible to easily impart a design of a complicated design pattern to these various molded bodies. Therefore, its application range is wide.

以下、実施例を挙げて本開示の加飾フィルム、その製造方法、加飾成形体及びその製造方法について具体的に説明するが、本開示は以下の具体例に制限されるものではない。
以下の実施例において、濃度及び各成分の含有量を示す「％」は、特に断らない限り、質量基準である。 Hereinafter, the decorative film of the present disclosure, a method for producing the same, a decorative molded product and the method for producing the same will be specifically described with reference to examples, but the present disclosure is not limited to the following specific examples.
In the following examples, "%" indicating the concentration and the content of each component is based on mass unless otherwise specified.

〔実施例１〕
（工程ＶＩ：表皮層の準備）
ＫＦＣフィルム ＦＴ－５０Ｙ（商品名）、クレハエクステック（株）（厚み：５０μｍ）を表皮層として準備した。表皮層は無色透明であった。 [Example 1]
(Process VI: Preparation of epidermis layer)
KFC film FT-50Y (trade name) and Kureha Extec Co., Ltd. (thickness: 50 μm) were prepared as the epidermis layer. The epidermis layer was colorless and transparent.

（工程Ｉ：加飾層及び接着層を有する加飾積層体の成形）
ＰＶＣ樹脂〔ＴＨ８００（商品名）、大洋塩ビ（株）〕１００ｋｇに、顔料〔ＰＶ ＭＡＦ ７２５（商品名）、大日精化工業（株）〕２ｋｇを投入し、カレンダー法により、乾燥後の厚みが１５０μｍになるようにシート状に成形して加飾層を得た。加飾層は、目視で黒色であった。
加飾層と、表皮層とを積層し、積層体を一対のロールを用いてラミネート加工を行った。ラミネート温度は１５０℃であった。
加飾層の表皮層を有しない側にアクリル系粘着剤〔Ｔｇ：－２０℃、分子量：２０万〕を、乾燥後の膜厚が３５μｍとなる量で塗布し、これを乾燥させて接着層形成し、加飾積層体を得た。
得られた接着層を、試験方法（Ｉ）により剥離強度を測定したところ、初期剥離強度は４．７Ｎ／ｃｍであり、試験方法（ＩＩ）にて測定した経時後剥離強度は７．１Ｎ／ｃｍであった。 (Step I: Molding of a decorative laminate having a decorative layer and an adhesive layer)
2 kg of pigment [PV MAF 725 (trade name), Dainichi Seika Kogyo Co., Ltd.] was added to 100 kg of PVC resin [TH800 (trade name), Taiyo PVC Co., Ltd.], and the thickness after drying was increased by the calendar method. A decorative layer was obtained by molding into a sheet so as to have a thickness of 150 μm. The decorative layer was visually black.
The decorative layer and the skin layer were laminated, and the laminated body was laminated using a pair of rolls. The laminating temperature was 150 ° C.
An acrylic pressure-sensitive adhesive [Tg: -20 ° C, molecular weight: 200,000] is applied to the side of the decorative layer that does not have the epidermis layer in an amount that makes the film thickness after drying 35 μm, and this is dried to form an adhesive layer. It was formed to obtain a decorative laminate.
When the peel strength of the obtained adhesive layer was measured by the test method (I), the initial peel strength was 4.7 N / cm, and the peel strength after aging measured by the test method (II) was 7.1 N / cm. It was cm.

（工程ＩＩ：接着層保護シートの貼付）
表面平滑な平らなＰＰ樹脂シート（フジコー（株）、ＢＫ０Ａ（商品名）、厚さ：６０μｍ）を準備し、樹脂シートの表面温度を１５０℃とする条件で凹凸を形成した。凹凸を形成したＰＰ樹脂シートの断面を電子顕微鏡で測定したところ、凸部のサイズは、幅１２０μｍ、高さ２５μｍであった。
得られた凹凸を有する接着層保護シートにより、工程Ｉで得た加飾積層体の接着層を被覆して、加飾フィルム前駆体を得た。 (Step II: Adhesive layer protective sheet affixed)
A flat PP resin sheet with a smooth surface (Fujiko Co., Ltd., BK0A (trade name), thickness: 60 μm) was prepared, and irregularities were formed under the condition that the surface temperature of the resin sheet was 150 ° C. When the cross section of the PP resin sheet having the unevenness formed was measured with an electron microscope, the size of the convex portion was 120 μm in width and 25 μm in height.
The adhesive layer of the decorative laminate obtained in step I was coated with the obtained adhesive layer protective sheet having irregularities to obtain a decorative film precursor.

（工程ＩＩＩ：第一切り取り線の形成）
カッティング装置（コングスバーグ社製）を用いて、工程ＩＩで得た加飾フィルム前駆体の表皮層側と、カッターヘッドに把持されているカッターの刃先とが対向するように、加飾フィルム前駆体をカッティング装置の所定位置に載置し、図４にて破線で示す形状の第一切り取り線を加飾層の表皮層側から形成した。第一切り取り線の深さは３８．８μｍであり、加飾層の厚みの２５．８％の深さであった。 (Step III: Formation of first cut line)
Using a cutting device (manufactured by Kongsburg), the decorative film precursor so that the epidermis layer side of the decorative film precursor obtained in step II and the cutting edge of the cutter gripped by the cutter head face each other. The body was placed in a predetermined position of the cutting device, and a first cutting line having a shape shown by a broken line in FIG. 4 was formed from the epidermis layer side of the decorative layer. The depth of the first cutting line was 38.8 μm, which was 25.8% of the thickness of the decorative layer.

（工程ＩＶ：第二切り取り線の形成）
加飾フィルム前駆体の接着層保護シートまでを貫通する第二切り取り線を、第一切り取り線との交部が生じるように形成して剥離部を形成した。第二切り取り線は、図５の一点破線で示す形状で、第二切り取り線を第一切り取り線との交部が生じるように形成して剥離部を形成した。 (Step IV: Formation of second cut line)
A second cut line penetrating to the adhesive layer protective sheet of the decorative film precursor was formed so as to form an intersection with the first cut line to form a peeled portion. The second cut line has a shape shown by a broken line at one point in FIG. 5, and the second cut line is formed so as to form an intersection with the first cut line to form a peeled portion.

上記工程を経て、図６の概略平面図に示す剥離部Ａ－１～Ａ－７と、非剥離部Ｂとを有する実施例１の加飾フィルムを得た。 Through the above steps, the decorative film of Example 1 having the peeling portions A-1 to A-7 and the non-peeling portion B shown in the schematic plan view of FIG. 6 was obtained.

〔実施例２〕
実施例１の工程ＩＩＩにおいて、第一切り取り線の深さを、加飾層の厚みの６１．２％である深さ９１．９μｍに変更した以外は、実施例１と同様にして実施例２の加飾フィルムを得た。 [Example 2]
In Step III of Example 1, the depth of the first cut line was changed to 91.9 μm, which is 61.2% of the thickness of the decorative layer, except that the depth was changed to 91.9 μm in the same manner as in Example 1. I got a decorative film.

〔実施例３〕
実施例１の工程ＩＩＩにおいて、第一切り取り線の深さを、加飾層の厚みの９８．０％である深さ１４７．０μｍに変更した以外は、実施例１と同様にして実施例３の加飾フィルムを得た。 [Example 3]
In Step III of Example 1, the depth of the first cut line was changed to 147.0 μm, which is 98.0% of the thickness of the decorative layer, in the same manner as in Example 1. I got a decorative film.

〔実施例４〕
実施例１の工程ＩＩＩ及び工程ＩＶの後に、以下の剥離補助部の形成工程を実施して、図９（Ａ）に部分拡大図で示した如き凹部としての剥離補助部（めくり部）を形成した以外は、実施例１と同様にして実施例４の加飾フィルムを得た。
図９（Ａ）は、実施例４の加飾フィルムの部分拡大平面図であり、剥離補助部としての凹部が形成された領域を二点破線で囲むことで明示している。 [Example 4]
After the steps III and IV of the first embodiment, the following peeling assisting portion forming step is carried out to form the peeling assisting portion (turning portion) as a recess as shown in the partially enlarged view in FIG. 9 (A). A decorative film of Example 4 was obtained in the same manner as in Example 1.
FIG. 9A is a partially enlarged plan view of the decorative film of Example 4, which is clearly shown by surrounding the region where the recess as the peeling auxiliary portion is formed with a two-dot broken line.

（剥離補助部の形成工程）
工程ＩＶにおいて成された第一切り取り線と第二切り取り線との交部を起点として凹部形状の剥離補助部（めくり部）を形成した。
めくり部は、図９（Ｂ）に概略的に示す如き頂部の角度αが３０℃であって、底辺が３ｍｍの三角形の先端部の形状の凹部として形成した。
図９（Ａ）において、Ａ－３及びＡ－４で示される領域が剥離部であり、剥離部は、剥離補助部である凹部を有することで、剥離容易性がより良好となることが期待できる。 (Formation process of peeling auxiliary part)
A concave-shaped peeling auxiliary portion (turning portion) was formed starting from the intersection of the first cutting line and the second cutting line formed in step IV.
The flipped portion was formed as a concave portion in the shape of a triangular tip portion having a top angle α of 30 ° C. and a base of 3 mm as schematically shown in FIG. 9 (B).
In FIG. 9A, the regions shown by A-3 and A-4 are the peeling portions, and the peeling portion is expected to have a recess which is a peeling auxiliary portion, so that the peelability is further improved. can.

〔実施例５〕
実施例１の工程ＩＩＩの前に、工程ＶＩＩの着色シート付与を行った以外は、実施例１と同様にして実施例５の加飾フィルムを得た。
着色シートとして、リンテックサインシステム（株）、品番：ＡＰ１１１、厚み：１１０μｍの白色の着色シートを準備した。
着色シートの粘着層の初期剥離強度は、実施例１の接着層と同程度であった。
着色シートの粘着層を介して、着色シートを、加飾フィルムの表皮層上に積層した。
その後、着色シートを有する加飾フィルム前駆体に対し、実施例１と同様に、工程ＩＩＩ及び工程ＩＶを行って第一切り取り線及び第二切り取り線を形成して、実施例５の加飾フィルムを得た。 [Example 5]
A decorative film of Example 5 was obtained in the same manner as in Example 1 except that the colored sheet of Step VII was applied before Step III of Example 1.
As a colored sheet, a white colored sheet of Lintec Sign System Co., Ltd., product number: AP111, and thickness: 110 μm was prepared.
The initial peel strength of the adhesive layer of the colored sheet was about the same as that of the adhesive layer of Example 1.
The colored sheet was laminated on the epidermis layer of the decorative film via the adhesive layer of the colored sheet.
Then, in the same manner as in Example 1, steps III and IV are performed on the decorative film precursor having the colored sheet to form the first cut line and the second cut line, and the decorative film of Example 5 is formed. Got

〔比較例１〕
実施例１において、工程ＩＩＩを行わず、第一切り取り線を形成しなかった以外は、実施例１と同様にして比較例１の加飾フィルムを得た。 [Comparative Example 1]
In Example 1, the decorative film of Comparative Example 1 was obtained in the same manner as in Example 1 except that step III was not performed and the first cut line was not formed.

〔比較例２〕
実施例１の工程ＩＩＩにおいて、第一切り取り線の深さを、加飾層の厚みの１００％である深さ１５０μｍに変更した以外は、実施例１と同様にして比較例２の加飾フィルムを得た。 [Comparative Example 2]
The decorative film of Comparative Example 2 in the same manner as in Example 1 except that the depth of the first cutting line was changed to 150 μm, which is 100% of the thickness of the decorative layer, in step III of Example 1. Got

〔加飾フィルムの評価〕
得られた加飾フィルムを用いて、以下に記載された手順にて加飾成形体を作製し、以下の項目を評価した。
結果を表１に示す。 [Evaluation of decorative film]
Using the obtained decorative film, a decorative molded product was prepared by the procedure described below, and the following items were evaluated.
The results are shown in Table 1.

（加飾成形体の製造）
まず、被着体である成形体を準備した。成形体は、表面が曲面である車両のサイドドア部を用いた。
実施例１～実施例５及び比較例１～比較例２で得た加飾フィルムから接着層保護シートを剥離し、加飾積層体を得た。（工程ｉ）
得られた加飾積層体の接着層を介して、加飾積層体を成形体に貼り付けた。このとき、接着層保護シートの剥離と、加飾積層体の成形体への貼り付けを、作業者の手作業により行い、接着層保護シートを徐々に剥離し、加飾積層体の接着層を部分的に露出させ、露出させた加飾積層体の接着層を、立体形状を有する成形体の表面に対向させ、加飾積層体を押圧することで、接着層を介して加飾積層体を成形体に貼り付けた。（工程ｉｉ） (Manufacturing of decorative molded products)
First, a molded body as an adherend was prepared. As the molded body, a side door portion of a vehicle having a curved surface was used.
The adhesive layer protective sheet was peeled off from the decorative films obtained in Examples 1 to 5 and Comparative Examples 1 to 2 to obtain a decorative laminate. (Step i)
The decorative laminate was attached to the molded product via the adhesive layer of the obtained decorative laminate. At this time, the adhesive layer protective sheet is peeled off and the decorative laminated body is attached to the molded body manually, and the adhesive layer protective sheet is gradually peeled off to release the adhesive layer of the decorative laminated body. The adhesive layer of the partially exposed decorative laminate is opposed to the surface of the molded body having a three-dimensional shape, and the decorative laminate is pressed to form the decorative laminate via the adhesive layer. It was attached to the molded body. (Step ii)

貼り付け後、成形体の表面に貼り付けた加飾積層体の剥離部を剥離した。（工程ｉｉｉ）このようにして、成形体の面上に加飾積層体の非剥離部のみを有し、加飾積層体の非剥離部からなるデザインパターンが成形体上に形成された加飾成形体を得た。
剥離部を剥離除去した後、２４時間熟成した。 After the attachment, the peeled portion of the decorative laminate attached to the surface of the molded body was peeled off. (Step iii) In this way, a decoration having only a non-peeling portion of the decorative laminate on the surface of the molded body and a design pattern composed of the non-peeling portion of the decorative laminate formed on the molded body. A molded product was obtained.
After peeling and removing the peeled portion, it was aged for 24 hours.

評価基準は、作業者１０名の実作業による評価とし、最も評価数の多いランクを採用した。 The evaluation criteria were the actual work of 10 workers, and the rank with the highest number of evaluations was adopted.

－１．剥離部と非剥離部との連繋性－
Ａ：接着層保護シートの剥離工程において、剥離部と非剥離部との連繋が維持され、問題なし
Ｂ：接着層保護シートの剥離工程において、剥離部と非剥離部との連繋が解消され、問題あり
Ｃ：剥離部と非剥離部とが形成されていないので、問題あり
上記では、ランクＡが実用上問題のない評価結果である。 -1. Connection between peeled part and non-peeled part-
A: In the peeling step of the adhesive layer protective sheet, the connection between the peeled part and the non-peeled part is maintained, and there is no problem. B: In the peeling step of the adhesive layer protective sheet, the connection between the peeled part and the non-peeled part is eliminated. Problem C: There is a problem because the peeled part and the non-peeled part are not formed. In the above, rank A is an evaluation result without a problem in practical use.

－２．剥離部の剥離容易性－
Ａ：加飾積層体の剥離部の剥離作業が極めて容易であり、問題なし
Ｂ：加飾積層体の剥離部の剥離作業が容易であり、問題なし
Ｃ：加飾積層体の剥離部の剥離作業が困難であり、問題あり
Ｄ：加飾積層体の剥離部の剥離作業が不可能であり、問題あり
上記では、Ａ及びＢが実用上問題のない評価結果である。 -2. Ease of peeling of the peeled part-
A: The peeling work of the peeling part of the decorative laminate is extremely easy and there is no problem. B: The peeling work of the peeling part of the decorative laminate is easy and there is no problem. C: The peeling part of the decorative laminate is peeled. The work is difficult and there is a problem. D: The peeling work of the peeling portion of the decorative laminate is impossible and there is a problem. In the above, A and B are the evaluation results without any problem in practical use.

－総合評価－
Ａ：１．の連繋性及び２．の剥離容易性が、いずれも良好であり、問題なし
Ｂ：１．の連繋性及び２．の剥離容易性の、双方又は一方が不良であり、問題あり
総合評価では、Ａが問題のない評価結果である。 -Comprehensive evaluation-
A: 1. Connection and 2. The ease of peeling is good, and there is no problem. B: 1. Connection and 2. Both or one of the easiness of peeling is defective and there is a problem. In the comprehensive evaluation, A is an evaluation result without a problem.

Figure 2022107469000002
Figure 2022107469000002

表１の結果より、実施例１～実施例５の加飾フィルムは、いずれも、加飾成形体の製造に適しており、複雑なデザインパターンを加飾成形体に製造することができた。
また、切り取り線の深さが加飾層の６０％以上である実施例２及び実施例３の加飾フィルム、剥離補助部を有する実施例４の加飾フィルム、着色シートを有する実施例５の加飾フィルムは、実施例１の加飾フィルムに対して剥離部の剥離容易性がより良好であった。 From the results shown in Table 1, all of the decorative films of Examples 1 to 5 were suitable for producing a decorative molded product, and a complicated design pattern could be produced on the decorative molded product.
Further, the decorative film of Examples 2 and 3 in which the depth of the cut line is 60% or more of the decorative layer, the decorative film of Example 4 having a peeling auxiliary portion, and the decorative film of Example 5 having a colored sheet. The decorative film had better peelability of the peeled portion than the decorative film of Example 1.

これに対し、第一切り取り線を有しない比較例１の加飾フィルムは剥離容易性に劣り、第一切り取り線の深さが深すぎる比較例２の加飾フィルムでは剥離部と非剥離部との連携性が低く、加飾積層体全体を成形体に貼り付けすることができなかった。 On the other hand, the decorative film of Comparative Example 1 having no first cut line is inferior in peelability, and the decorative film of Comparative Example 2 in which the depth of the first cut line is too deep has a peeled portion and a non-peeled portion. The cooperation between the two was low, and the entire decorative laminate could not be attached to the molded body.

１０ 加飾フィルム
１２ 加飾層
１４ 接着層
１６ 接着層保護シート
１８ 表皮層
２０ 切り取り線
２１Ａ 剥離補助部（凹部）
２１Ｂ 剥離補助部（凸部、タブ）
２２ 着色シート
２４ 加飾フィルム前駆体
２６ 第一切り取り線
２８ 第二切り取り線
３０ 加飾成形体
３２ 成形体
Ａ 剥離部
Ｂ 非剥離部
α 加飾層の厚み
β 切り取り線深さ
10 Decorative film 12 Decorative layer 14 Adhesive layer 16 Adhesive layer Protective sheet 18 Skin layer 20 Cut line 21A Peeling auxiliary part (recess)
21B Peeling auxiliary part (convex part, tab)
22 Colored sheet 24 Decorative film precursor 26 1st cut line 28 2nd cut line 30 Decorative molded body 32 Molded body A Peeled part B Non-peeled part α Thickness of decorative layer β Cut line depth

Claims (7)

剥離部と非剥離部とを有する加飾層と接着層とを有する加飾積層体、及び、
接着層保護シート、をこの順で有し、
前記剥離部と非剥離部とは、深さが、加飾層の厚みに対し、加飾層の表面側から１００％未満である切り取り線にて区画される、成形体の加飾に用いられる加飾フィルム。 A decorative laminate having a decorative layer having a peeled portion and a non-peeled portion and an adhesive layer, and a decorative laminate having an adhesive layer, and
Adhesive layer protective sheet, in this order,
The peeled portion and the non-peeled portion are used for decorating a molded body, which is partitioned by a cutting line whose depth is less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer. Decorative film. 前記加飾層における切り取り線の深さは、加飾層の厚みに対し、加飾層の表面側から２５％以上１００％未満である請求項１に記載の加飾フィルム。 The decorative film according to claim 1, wherein the depth of the cut line in the decorative layer is 25% or more and less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer. 前記剥離部は、剥離補助部を備える請求項１又は請求項２に記載の加飾フィルム。 The decorative film according to claim 1 or 2, wherein the peeling portion includes a peeling assisting portion. 前記加飾層の、前記接着層側とは反対の面に、さらに、前記加飾層とは異なる色相の着色シートを有する請求項１～請求項３のいずれか１項に記載の加飾フィルム。 The decorative film according to any one of claims 1 to 3, further comprising a colored sheet having a hue different from that of the decorative layer on the surface of the decorative layer opposite to the adhesive layer side. .. 加飾層の一方の面に、接着層を形成して加飾積層体を形成する工程と、
接着層保護シートを準備し、準備した接着層保護シートにより、前記接着層を被覆して、前記加飾層と接着層と接着層保護シートとを有する加飾フィルム前駆体を形成する工程と、
前記加飾層に、剥離部と非剥離部とを区画する、深さが、加飾層の厚みに対し、加飾層の表面側から１００％未満である第一切り取り線を形成する工程と、
前記加飾フィルム前駆体を貫通する第二切り取り線を、前記第一切り取り線との交部が生じる位置に形成する工程と、を有する、
成形体の加飾に用いられる加飾フィルムの製造方法。 A process of forming an adhesive layer on one surface of the decorative layer to form a decorative laminate, and
A step of preparing an adhesive layer protective sheet, covering the adhesive layer with the prepared adhesive layer protective sheet, and forming a decorative film precursor having the decorative layer, the adhesive layer, and the adhesive layer protective sheet.
A step of forming a first cutting line in which the peeled portion and the non-peeled portion are separated from each other in the decorative layer and the depth is less than 100% from the surface side of the decorative layer with respect to the thickness of the decorative layer. ,
It comprises a step of forming a second cut line penetrating the decorative film precursor at a position where an intersection with the first cut line occurs.
A method for manufacturing a decorative film used for decorating a molded product. 成形体と、
請求項１～請求項４のいずれか１項に記載の加飾フィルムから前記接着層保護シート及び加飾積層体の剥離部が剥離された加飾積層体の非剥離部と、を有する加飾成形体。 Mold and
A decoration having the adhesive layer protective sheet and the non-peeling portion of the decorative laminate from which the peeled portion of the decorative laminate is peeled from the decorative film according to any one of claims 1 to 4. Molded body. 請求項１～請求項４のいずれか１項に記載の加飾フィルムから接着層保護シートを剥離して加飾積層体を得る工程、
接着層保護シートを剥離した加飾積層体を、接着層を介して成形体の表面に貼り付ける工程、及び、
前記成形体の表面に貼り付けた加飾積層体の剥離部を剥離する工程、
を有する加飾成形体の製造方法。 A step of peeling an adhesive layer protective sheet from the decorative film according to any one of claims 1 to 4 to obtain a decorative laminate.
The process of attaching the decorative laminate from which the adhesive layer protective sheet has been peeled off to the surface of the molded product via the adhesive layer, and
The step of peeling off the peeled portion of the decorative laminate attached to the surface of the molded body,
A method for manufacturing a decorative molded product having.
JP2021002439A 2021-01-08 2021-01-08 Decorative film, method for producing decorative film, decorative molding, and method for producing decorative molding Pending JP2022107469A (en)