JP2022059166A - Method for producing kneaded material containing silicone rubber and calcium hydroxide powder, or method for making kneaded product, and method for forming the kneaded material or kneaded product - Google Patents
Method for producing kneaded material containing silicone rubber and calcium hydroxide powder, or method for making kneaded product, and method for forming the kneaded material or kneaded product Download PDFInfo
- Publication number
- JP2022059166A JP2022059166A JP2020166733A JP2020166733A JP2022059166A JP 2022059166 A JP2022059166 A JP 2022059166A JP 2020166733 A JP2020166733 A JP 2020166733A JP 2020166733 A JP2020166733 A JP 2020166733A JP 2022059166 A JP2022059166 A JP 2022059166A
- Authority
- JP
- Japan
- Prior art keywords
- kneaded
- shaped
- smelter
- calcium hydroxide
- silicone rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、シリコン・水酸化カルシウム粉体からなる混練材及びシリコン・水酸化カルシウム粉体からなる製錬体、及び当該混練材あるいは製錬体の形成方法に関する。 The present invention relates to a kneaded material made of silicon / calcium hydroxide powder, a smelter made of silicon / calcium hydroxide powder, and a method for forming the kneaded material or smelted material.
現在、非常に多くの分野に抗菌性グッズが汎用されている。抗ウイルス作用を持つ抗微生物物質の有用性、必要性が広く認識されている。 Currently, antibacterial goods are widely used in a great many fields. The usefulness and necessity of antimicrobial substances with antiviral activity are widely recognized.
このような状況下、ドロマイドが抗ウイルス作用を持つ新素材として注目される。 Under these circumstances, dolomide is attracting attention as a new material with antiviral activity.
ドロマイドの性状として次のようなことが知られる。 The following are known properties of dolomide.
１）ドロマイドは、自然界に無限に存在するカルシウム・マグネシウムの炭酸塩からなる鉱物。菱面体結晶。無色ないし白色半透明。極めて高い安全性を備える。 1) Dolomide is a mineral consisting of carbonates of calcium and magnesium that exists infinitely in nature. Rhombohedral crystals. Colorless or white translucent. It has extremely high safety.
２）粉状をなし、抗菌力は極めて強い。強力な殺ウイルス効果を持ち、短時間作用させただけで、ウイルスの感染力を効率的に消失させる。新興-再興感染病対策に有効と考えられる。 2) It is powdery and has extremely strong antibacterial activity. It has a strong virus-killing effect and effectively eliminates the infectivity of the virus even if it is allowed to act for a short time. Emerging-Re-emerging Infectious diseases are considered to be effective against infectious diseases.
３）純品は高いｐHを持ち、殺菌のメカニズムを生ずると考えられている。ドロマイトの濃度と菌数変化との間には濃度依存性が見られることが一般文献に報告される。 3) Pure products have a high pH and are thought to produce a sterilizing mechanism. It is reported in the general literature that there is a concentration dependence between the concentration of dolomite and the change in bacterial count.
このような性状を持つドロマイトは、プラスチックへの添加剤として使用されることが
知られ、従来、マスク、フイルタへの応用が提案された。
Dolomite having such properties is known to be used as an additive for plastics, and its application to masks and filters has been proposed.
特許文献１には、ドロマイトを焼成し、その一部を水和して粉末として抗ウイルス剤を生成し、得られた粉末を繊維（織布又は不織布）に保持してマスクを製造することが記載される。
特許文献２には、ドロマイトを含有することを特徴とする抗ウイルス性塗料組成物が記
載される。
特許文献３には、ドロマイトを焼成して水和した後、粉砕して微粒子とすること、シート状物に付着させた微粒子状の抗ウイルス剤の抗ウイルス活性が長時間持続して、シート表面に付着したウイルスがシート内部に取り込まれやすい抗ウイルス剤担持シートが提供されることが記載される。 Patent Document 3 states that dolomite is calcined and hydrated and then crushed into fine particles, and the antiviral activity of the finely divided antiviral agent attached to the sheet-like material is maintained for a long time on the sheet surface. It is described that an antiviral agent-carrying sheet is provided in which the virus attached to the sheet is easily taken into the inside of the sheet.
特許文献４には、ドロマイトのか焼物、又はドロマイトのか焼・消化物を含有する抗菌性があり、床材、幅木、腰壁、壁装材などの建材として利用可能な熱可塑性樹脂製建材が記載される。
特許文献５には、ドロマイト族粉末と角閑石粉末が所定の割合で混合された抗菌性のある複合セラミックスが記載される。
特許文献６には、レーヨン繊維中に酸化アルミニウム、酸化珪素及び酸化マグネシウムを主成分とする無機質抗菌材が1０～１５重量％混練されている抗菌靴下が記載される。 Patent Document 6 describes antibacterial socks in which 10 to 15% by weight of an inorganic antibacterial material containing aluminum oxide, silicon oxide and magnesium oxide as main components is kneaded into rayon fiber.
引用文献７には、オルガノポリシロキサン生ゴム、湿式シリカ、無機系抗菌剤及び硬化剤からなる抗菌性シリコーンゴムが記載される。 Reference 7 describes an antibacterial silicone rubber composed of an organopolysiloxane raw rubber, a wet silica, an inorganic antibacterial agent and a curing agent.
特許文献８は、シリコーンゴム組成物１００重量部、水酸化カルシウム０．１～２．０重量部からなる医療用シリコーンゴム組成物が記載される。シリコーンゴム組成物は、有機過酸化物によるラジカル反応架橋によりゴム状弾性体が形成される。 Patent Document 8 describes a medical grade silicone rubber composition comprising 100 parts by weight of a silicone rubber composition and 0.1 to 2.0 parts by weight of calcium hydroxide. In the silicone rubber composition, a rubber-like elastic body is formed by radical reaction cross-linking with an organic peroxide.
特許文献１～５に記載されるように、鉱物原料としてのドロマイト由来の抗ウイルス剤がマスク、フイルタ、塗料組成物、繊維あるいは担持シート、建材、複合セラミックスに適用応用されることが知られているが、混練材としてシリコン材及びドロマイトを用い、これらを混練してシリコン・ドロマイト混練材を生成し、シリコン・ドロマイト混練材から製錬体を形成し、抗ウイルス成形品とすることが知られていない。
As described in
特許文献６には、レーヨン繊維中に酸化アルミニウム、酸化珪素及び酸化マグネシウムを主成分とする無機質抗菌材が1０～１５重量％混練されていることが記載される。レーヨン繊維中に酸化アルミニウム、酸化珪素及び酸化マグネシウムを主成分とする無機質抗菌材が担持される。この文献は、混練材としてシリコン材及びドロマイトを用い、これらを混練してシリコン・ドロマイト混練材を生成し、シリコン・ドロマイト混練材から混合混練状態の製錬体を形成することを記載しない。 Patent Document 6 describes that an inorganic antibacterial material containing aluminum oxide, silicon oxide and magnesium oxide as main components is kneaded in rayon fiber in an amount of 10 to 15% by weight. An inorganic antibacterial material containing aluminum oxide, silicon oxide and magnesium oxide as main components is supported in the rayon fiber. This document does not describe that a silicon material and a dolomite are used as a kneading material, and these are kneaded to form a silicon dolomite kneaded material, and a smelted body in a mixed kneaded state is formed from the silicon dolomite kneaded material.
特許文献７には、無機系抗菌剤を含有する抗菌性シリコーンゴムが記載され、無機系抗菌剤が、抗ウイルス性の焼成ドロマイト水和物であること、そしてシリコーンゴム組成物が抗ウイルス性の混練材であることが記載されない。 Patent Document 7 describes an antibacterial silicone rubber containing an inorganic antibacterial agent, the inorganic antibacterial agent is an antiviral fired dolomite hydrate, and the silicone rubber composition is antiviral. It is not stated that it is a kneaded material.
特許文献８に記載されるシリコーンゴムは医療用シリコーンゴムであって、抗ウイル性混練材あるいは抗ウイルス性製錬体を記載しない。 The silicone rubber described in Patent Document 8 is a medical grade silicone rubber, and does not describe an anti-will kneaded material or an anti-virus smelter.
感染防止の有効な一つの手段として、当該分野の専門家から手を水洗することで各種のウイルスを除去励行することが勧められる。人は、水洗することは水のある家庭あるいは職場その他の施設にいることが必然である。水洗に加えて、家庭あるいは職場内の施設あるいはその他の施設で、人が日常手で接触する部材をウイルス不活性化処理することがウイルス感染に有効手段となる。 As an effective means of preventing infection, it is recommended that experts in the field wash their hands with water to remove various viruses. It is inevitable that a person is in a home with water, a workplace or other facility to wash with water. In addition to washing with water, it is an effective means for virus infection to inactivate the components that humans come into contact with by hand at home, at work, or at other facilities.
この場合、ウイルス不活性化状態を形成するという効果を得るために、ウイルス不活性化部材を人が日常に手で、もしくは他の箇所でしばしば接触する部材に取り付けするなどして配設しておくことが一つの有効手段となる。
配設に際し材料の粉体からウイルス不活性化部材として混練材を形成するために混練操作易さを確保すること、製錬体を形成するために製錬操作易さを確保するという問題を解決することが求められる。
In this case, in order to obtain the effect of forming the virus inactivating state, the virus inactivating member is arranged by attaching it to a member that is frequently contacted by a person on a daily basis or in other places. Keeping is one effective means.
Solved the problem of ensuring ease of kneading operation to form a kneaded material as a virus-inactivating member from the powder of the material at the time of arrangement, and ensuring ease of smelting operation to form a smelter. Is required to do.
本発明は、かかる点に鑑み、家庭あるいは職場内の施設あるいはその他の施設で、人が日常に手で、もしくは他の箇所でしばしば接触する部材に取り付けするなどしてウイルス不活性化部材を配設するに際して、材料の粉体からウイルス不活性化部材として混練材を形成するために混練操作易さを確保すること、製錬体を形成するために製錬操作易さを確保するという問題を解決することを課題とする。 In view of this point, the present invention disposes of a virus-inactivating member in a facility at home or in the workplace or other facility by attaching it to a member that a person often contacts by hand or in other places on a daily basis. At the time of installation, there are problems of ensuring the ease of kneading operation to form the kneaded material as a virus-inactivating member from the powder of the material and ensuring the smelting operation to form the smelter. The challenge is to solve it.
本発明において、不活性化部材形成に使用される材料の粉体は、シリコン材と抗ウイルス剤である。シリコン材と抗ウイルス剤を含有する材料の粉体から水を加えた混練で混練材が形成される。この場合に、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・混練材がシリコーンゴム及び水酸化カルシウム粉末を含有してなる混練材を提供する。
In the present invention, the powder of the material used for forming the inactivating member is a silicon material and an antiviral agent. A kneaded material is formed by kneading water from a powder of a material containing a silicon material and an antiviral agent. In this case,
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
-Providing a kneaded material in which the kneaded material contains silicone rubber and calcium hydroxide powder.
水酸化カルシウムは、消石灰とも呼ばれ、水溶液は石灰水、懸濁液は石灰乳とよばれ、共に強いアルカリ性を示す。 Calcium hydroxide is also called slaked lime, the aqueous solution is called lime water, and the suspension is called lime milk, both of which show strong alkalinity.
また、シリコン材と抗ウイルス剤を含有する製錬体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・混練材がシリコーンゴム及び水酸化カルシウム粉末を含有してなる製錬体を提供する。
In addition, it is a smelter containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
-Providing a smelted product in which the kneaded material contains silicone rubber and calcium hydroxide powder.
ここで、水酸化カルシウム粉末にはドロマイト粉末が含まれない。すなわち、水酸化カルシウムにはドロマイトが含まれない。本発明は、ドロマイト粉末を用いず、水酸化カルシウムを成分として用いるが、水酸化カルシウムに第３成分としてドロマイトを含有することを除外しない。混練材あるいは製錬体を、水酸化カルシウム粉末を主体として適切な量（重量）をシリコーンゴムに混練することで抗ウイルス性能を向上させた混練材あるいは製錬体を形成することができる。 Here, the calcium hydroxide powder does not contain the dolomite powder. That is, calcium hydroxide does not contain dolomite. The present invention does not use dolomite powder and uses calcium hydroxide as a component, but does not exclude calcium hydroxide containing dolomite as a third component. By kneading the kneaded material or smelter with an appropriate amount (weight) of calcium hydroxide powder as the main component, the kneaded material or smelter with improved antiviral performance can be formed.
本発明において、混練材中にあるいは製錬体中に、シリコーンゴム１ｋｇに対して含有させる水酸化カルシウム粉末の量を特定することを試みた。
図１は、本発明の抗ウイルス性混練材及び抗ウイルス性製錬体を表示するＸ―Ｙ座標図
である。
In the present invention, it has been attempted to specify the amount of calcium hydroxide powder contained in 1 kg of silicone rubber in the kneaded material or the smelted body.
FIG. 1 is an XY coordinate diagram showing the antiviral kneaded material and the antiviral smelter of the present invention.
図１は、シリコーンゴム及び水酸化カルシウム粉末からなるウイルス感染に有効な混練材を形成し、ウイルス不活性化部材の形成し易さ、すなわち製錬易い混練材を確保することができることを示す実験結果を示すＸ―Ｙ座標で示す図である。Ｘ軸は、シリコーンゴム１ｋｇに対して投入されたシリコーンゴム量を重量で示し、Ｙ軸は、混練材あるいは製錬体の表面ｐＨ値を示す。表面ｐＨ値は、抗ウイルス性の強さを示す。表面ｐＨ値が高いほど抗ウイルス性の強さは強い。 FIG. 1 is an experiment showing that a kneaded material made of silicone rubber and calcium hydroxide powder, which is effective against virus infection, can be formed, and the kneaded material which is easy to form a virus inactivating member, that is, easy to smelt can be secured. It is a figure which shows the result by the XY coordinates. The X-axis indicates the amount of silicone rubber charged with respect to 1 kg of silicone rubber by weight, and the Y-axis indicates the surface pH value of the kneaded material or the smelted product. The surface pH value indicates the strength of antiviral property. The higher the surface pH value, the stronger the antiviral strength.
当該実験は、本件特許出願人によって当該特許出願人の施設、設備を使用してなされ、シリコン原料及びドロマイト粉末は市販の低硬度のものが用いられた。実験室に用いられた温度は、室温（２２．５℃）であった。計量器は、一般的なものが使用された。 The experiment was carried out by the Patent Applicant using the facilities and equipment of the Patent Applicant, and commercially available low hardness silicon raw materials and dolomite powder were used. The temperature used in the laboratory was room temperature (22.5 ° C.). A general measuring instrument was used.
＜実験内容＞
シリコン原料混練時にドロマイト粉体を混合混練したときに、保持力を確保することができた例を示す実験
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末１００ｇを混錬して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末２００ｇを混錬して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末３００ｇを混錬して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末４００ｇを混錬して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末５００ｇを混錬して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末６００ｇを混錬して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末７００ｇを混錬して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末８００ｇを混錬して混練材を形成しようとしたが、混練ができなかった。
<Experimental content>
An experimental example showing an example in which the holding power could be secured when the dolomite powder was mixed and kneaded at the time of kneading the silicon
200 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
300 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
400 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
500 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
600 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
700 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
An attempt was made to knead 800 g of calcium hydroxide powder with 1 kg of silicone rubber to form a kneaded material, but kneading was not possible.
実験結果によれば、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末７２０ｇ程度までは混合し製錬して混練材を形成することができたが、混練材は、６００ｇを超えると脆く、各分離独立した製錬体とすることは困難であった。 According to the experimental results, it was possible to mix up to about 720 g of calcium hydroxide powder with 1 kg of silicone rubber and smelt to form a kneaded material, but the kneaded material is brittle when it exceeds 600 g, and each is separated and independent. It was difficult to make a smelted body.
したがって、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末７２０ｇまでは混練して混練材を形成することができた。 Therefore, it was possible to knead up to 720 g of calcium hydroxide powder with respect to 1 kg of silicone rubber to form a kneaded material.
分離独立した製錬体とする場合、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末６００ｇまでは製錬して製錬体を形成することができた。 In the case of making a separate and independent smelter, it was possible to smelt up to 600 g of calcium hydroxide powder with respect to 1 kg of silicone rubber to form a smelter.
この実験結果に、水酸化カルシウム粉末量に依存するウイルス不活性化有効下方ラインとウイルス不活性化有効上方ラインで形成されるウイルス不活性化領域を加えると、図１に示される図が構成される。 The figure shown in FIG. 1 is constructed by adding the virus inactivating region formed by the virus inactivating effective lower line and the virus inactivating effective upper line depending on the amount of calcium hydroxide powder to the experimental results. The virus.
図１は、Ｘ―Ｙ軸座標軸になる図である。Ｘ―Ｙ軸座標軸図内に、ウイルス不活性化領域が示される。 FIG. 1 is a diagram that serves as an XY axis coordinate axis. A virus-inactivated region is shown in the XY-axis axes diagram.
ここで、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末を所定の重量を、混練可能環境下、混練して混錬材として形成されたものを抗ウイルス性の混錬材（以下、混練材という。）といい、混練材から成形品原型に各分離独立させ、混錬材の内、成形品成形に最良な範囲である最良な実施可能な範囲にある混錬材を抗ウイルス性の製錬体（以下、製錬体という。）という。混練材あるいは製錬体を成形品成形するに際しては、混練可能環境の加熱状態下、加硫処理による硬化処理がなされる。 Here, a material formed as a kneaded material by kneading a predetermined weight of calcium hydroxide powder with respect to 1 kg of silicone rubber in a kneadable environment is referred to as an antiviral kneaded material (hereinafter referred to as a kneaded material). ), Which separates and separates the kneaded material into the molded product prototype, and among the kneaded materials, the kneaded material in the best feasible range, which is the best range for molding the molded product, is an anti-virus smelter. (Hereafter, it is called a smelting body.) When the kneaded material or the smelted product is molded into a molded product, it is cured by a vulcanization treatment under the heating state of a kneadable environment.
混練可能領域が、混練可能領域が混練可能長さＬ１で、製錬可能領域が製錬可能長さＬ２で、抗ウイルス性能を考慮したときに、実施可能な混練材形成長さｌ１で、実施可能な製錬体形成長さｌ２で示される。混練困難領域が、Ｌ１を延長した領域に、製錬困難領域がＬ２を延長した領域に示される。混練材及び製錬体のいずれもがビジネス上、製品として取り扱われ得る。 The kneadable area has a kneadable area of L 1 and the smeltable area has a smeltable length of L 2 , and the kneaded material forming length l 1 can be implemented when antiviral performance is taken into consideration. Indicated by the feasible smelter formation length l 2 . The difficult kneading region is shown in the region where L 1 is extended, and the difficult smelting region is shown in the region where L 2 is extended. Both kneaded materials and smelters can be treated as products for business purposes.
図１で、
Ｘ軸：シリコーンゴム１ｋｇに対して水酸化カルシウム粉末量を重量で示す軸。
In Figure 1,
X-axis: A shaft showing the amount of calcium hydroxide powder by weight with respect to 1 kg of silicone rubber.
Ｙ軸：製錬体あるいは混練材の表面ｐＨ値を示す軸。
Ｈ：座標上で、実験結果で得られたプロットを結んで得られた曲線状の線図
Ａ域：線図Ｈ内混練長で、混練材形成域
Ｂ域：線図Ｈ内製錬長で、製錬体形成域
Ｃ域：線図Ｈ内混練長外方で混練材形成困難域
Ｄ域：ウイルス不活性有効下方ラインＭのｐＨ値１１及びウイルス不活性有効上方ラインＮのｐＨ値１２で区画されるウイルス不活性域（抗ウイルス領域）
Ｅ域：Ａ域及びＤ域で区画されるウイルス不活性混練材域
Ｆ域：Ｂ域及びＤ域で区画されるウイルス不活性製錬体域
Ｇ域：Ｃ域及びＤ域で区画されるウイルス不活性域・混練材形成困難域
Ｌ１：混練可能長
Ｌ２：製錬可能長
ｌ１：実施可能な混練材形成可能長
ｌ２：実施可能な製錬長形成可能長
この実験結果から、・混練材における水酸化カルシウム粉末の含有量がシリコーンゴムの重量で、混練可能な値で、抗ウイルスとして有効なｐＨが11～１２に範囲にある、シリコーンゴム１ｋｇの重量に対し、５００ｇ～７２０ｇ重量である混練材が提供される。
Y-axis: An axis indicating the surface pH value of the smelter or kneaded material.
H: Curved diagram obtained by connecting the plots obtained from the experimental results on the coordinates Area A: In the kneading length in the diagram H, area B in the kneaded material forming region: In the diagram H in-smelting length Area C of smelting body formation: Area D where kneading material is difficult to form outside the kneading length in diagram H: At
Area E: Virus-inert kneaded material area partitioned by A and D areas F area: Virus-inactive smelter area partitioned by B and D areas G area: Virus partitioned by C and D areas Inactive area / difficult kneading material formation area L 1 : Kneading possible length L 2 : Smeltable length l 1 : Practical kneading material forming possible length l 2 : Implementable kneading length forming possible length From this experimental result, -The content of the calcium hydroxide powder in the kneading material is the weight of the silicone rubber, which is a value that can be kneaded, and the pH effective as an antivirus is in the range of 11 to 12, 500 g to 720 g with respect to the weight of 1 kg of the silicone rubber. The weight of the kneaded material is provided.
また、・製錬体における水酸化カルシウム粉末の含有量がシリコーンゴムの重量で、製錬可能な値で、抗ウイルスとして有効なｐＨが11～１２に範囲にある、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量である製錬体が提供される。 In addition, the content of calcium hydroxide powder in the smelter is the weight of silicone rubber, which is a value that can be smelted, and the pH effective as an antivirus is in the range of 11 to 12, with respect to the weight of 1 kg of silicone rubber. , A smelter weighing between 500 g and 600 g is provided.
よって、シリコン材と抗ウイルス剤を含有する製錬体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であり、製錬体がシリコーンゴム及び水酸化カルシウム粉末を含有してなり、
・当該水酸化カルシウム粉末の当該製錬体における含有量がシリコーンゴムの重量に対した値であって、当該対比重量値が、当該シリコーンゴム及び当該水酸化カルシウム粉末を製錬可能で、当該製錬体のｐＨが予め定めたウイルス不活性有効下方値と予め定めたウイルス不活性有効上方値の範囲のｐＨが11～１２に範囲にある重量値で、５００ｇ～６００ｇ重量であることを特徴とする製錬体が提供される。
Therefore, it is a smelter containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, the antiviral agent is calcium hydroxide powder, and the smelter contains silicone rubber and calcium hydroxide powder.
-The content of the calcium hydroxide powder in the smelted body is a value relative to the weight of the silicone rubber, and the relative weight value is such that the silicone rubber and the calcium hydroxide powder can be smelted. The pH of the smelt is a weight value in the range of 11 to 12 and a weight of 500 g to 600 g, which is in the range of the predetermined virus-inert effective lower value and the predetermined virus-inert effective upper value. A smelter is provided.
水酸化カルシウム粉末の含有量７２０ｇを超えて混練するとき、混練が困難であった。水酸化カルシウム粉末の含有量６００ｇを超えて混練するとき、作業にかなりの時間を要し、成型時に保持力が弱くなり、切断しやすい現象がみられたが混練可能であった。 When the content of the calcium hydroxide powder exceeded 720 g, the kneading was difficult. When the content of the calcium hydroxide powder exceeded 600 g and kneaded, a considerable amount of time was required for the work, the holding power was weakened at the time of molding, and a phenomenon of easy cutting was observed, but kneading was possible.
成形品を形成には、製錬体が用いられる。 A smelter is used to form the molded product.
抗ウイルス性混練材あるいは抗ウイルス性製錬体の形成に当たっては、抗ウイルス性混練材あるいは抗ウイルス性製錬体に、必要に応じて、ドロマイト、炭酸カルシウム、炭酸カルシウム、炭酸マグネシウム、酸化マグネシウムの化学成分を第３成分として含有させることができる。 In forming the anti-viral kneaded material or the anti-viral smelter, the anti-viral kneaded material or the anti-viral smelter may be prepared with dolomite, calcium carbonate, calcium carbonate, magnesium carbonate and magnesium oxide as needed. A chemical component can be contained as a third component.
本発明によれば、シリコーンゴム及び水酸化カルシウムを主体として形成され、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末が５００ｇ～７２０ｇ、特に５００ｇ～６００ｇ混練あるいは製錬されて、混錬性あるいは製錬性に優れた抗ウイルス性を呈する混練材あるいは製錬体を提供することができる。 According to the present invention, it is formed mainly of silicone rubber and calcium hydroxide, and 500 g to 720 g of calcium hydroxide powder, particularly 500 g to 600 g, is kneaded or smelted with respect to 1 kg of silicone rubber to be smeltable or smelted. It is possible to provide a kneaded material or a smelted product having excellent antiviral properties.
抗ウイルス性を呈する混練材あるいは製錬体は、衛生マスクのインナーシートに用いて、あるいは押圧体に用いて、例えば手のひらに付着した各種のウイルスを除去する目的のために使用を可能とする。例えば柔軟性のある抗ウイルス性のドアノブ被覆体を形成することができる。また、ボール状体、棒状体あるいは板状体を形成し、外部環境における活動中にあっても手持ちができ、手のひらに付着した各種のウイルスを有効に除去してウイルス感染防止を有効に行い得るようにすることができる。 The kneaded material or smelter exhibiting antiviral properties can be used as an inner sheet of a sanitary mask or as a pressing body, for example, for the purpose of removing various viruses adhering to the palm. For example, a flexible antiviral doorknob covering can be formed. In addition, it can form a ball-shaped body, a rod-shaped body, or a plate-shaped body, and can be held by hand even during activities in the external environment, and can effectively remove various viruses attached to the palm to effectively prevent virus infection. Can be done.
これによって、外部における活動中にあっても各種のウイルスによる感染防止を有効に行い得る。 This makes it possible to effectively prevent infection by various viruses even during external activities.
以下、本発明の実施例を図面に基づいて説明する。 Hereinafter, embodiments of the present invention will be described with reference to the drawings.
図１で、混練材が練り状態のシリコーンゴム及び水酸化カルシウム粉末を含有してなる混練材又は製錬体形成の基本構成について説明した。 In FIG. 1, the basic configuration of forming a kneaded material or a smelted body in which the kneaded material contains a kneaded silicone rubber and calcium hydroxide powder has been described.
練り状態のシリコーンゴムは、シリコーンパウダーから生成される。シリコーンパウダーは、潤滑性や衝撃吸収性、光拡散性、耐熱性など、シリコーンの優れた特性を併せ持った高性能な粉体であって、プラスチックや各種ゴム、塗料、インキ、コーテイング剤といったさまざまな製品に添加することにより、これらの材質にシリコーンならではの優れた特性を付与する。 The kneaded silicone rubber is produced from silicone powder. Silicone powder is a high-performance powder that has excellent properties of silicone such as lubricity, shock absorption, light diffusivity, and heat resistance, and is a variety of plastics, various rubbers, paints, inks, and coating agents. By adding it to the product, these materials are given excellent properties unique to silicone.
図２は、本発明の実施例になる、抗ウイルス剤を含有した抗ウイルス性混練材を形成するミキサーの構成を示す図である。 FIG. 2 is a diagram showing the configuration of a mixer for forming an antiviral kneading material containing an antiviral agent, which is an embodiment of the present invention.
柔軟性のあるシリコン材（例えば、上述した低硬度―中硬度のシリコーンゴム）、抗ウイルス剤として水酸化カルシウム粉末及び必要に応じて第３成分が準備される。 A flexible silicone material (for example, the above-mentioned low-hardness-medium-hardness silicone rubber), calcium hydroxide powder as an antiviral agent, and, if necessary, a third component are prepared.
図２において、ミキサー１は、横置きされた円筒状の混練筒２、この混練筒２の入口側である上流側に設けられた基体原料としてのシリコン材（シリコーンゴム）投入口部３、この混練筒２の出口側に設けられた混練材取り出し口部４、この混練筒２の内部に横方向に設置された回転軸５、この回転軸の周囲に設けた攪拌スクリュー６、この攪拌スクリュー６の上流側に設けた送り羽根７、この攪拌スクリュー６の下流側に設けた送り羽根８、回転軸５に回転力を付与する駆動源としてのモータ９、抗ウイルス剤としての水酸化カルシウム粉体を投入するための水酸化カルシウム投入口部１０及び水酸化カルシウム投入管１１が形成される。必要に応じて第３成分が水酸化カルシウム投入口部１０の下流の混合部１３で混合され、混練される。
In FIG. 2, the
準備された練り状態のシリコーンゴムがシリコン材投入口部３から混練筒２に投入される。
The prepared silicone rubber in a kneaded state is charged into the
水酸化カルシウム粉末が水酸化カルシウム投入口部１０及び抗ウイルス剤投入管１１を経て混練筒２に投入される。加硫剤が加硫剤投入口１４から混練筒２に投入される。
The calcium hydroxide powder is charged into the
混練筒２の内部には、シリコン材投入口部３に面し、送り羽根７が設けられ、投入シリコン材を混練する領域Aに搬送部２１が、水酸化カルシウム投入管１１、加硫剤投入口１４に面した領域Bに練り状態のシリコーンゴムと水酸化カルシウム粉末と加硫剤を混合混練する混練部２２が、そして下流の混練材取り出し口部４に面し、送り羽根８が設けられた領域Cに送給部２３が形成される。
Inside the
投入された練り状態のシリコーンゴム、水酸化カルシウム粉体は、加硫剤の添加状態下、混練部２２で、例えば１４０―１７０°の加熱下で混錬に要する時間混練され、混練状態の混練材２４が生成される。
The charged silicone rubber and calcium hydroxide powder are kneaded in the kneading section 22 under the addition of the vulcanizing agent for the time required for kneading, for example, under heating at 140-170 °, and kneaded in the kneaded state.
加硫剤は、加熱状態下、混練材を硬化させる作用を呈する。したがって、混練材は、硬化され得る状態にあって、シリコーンゴム及び水酸化カルシウム粉体が混練されて混合状態にある成形材である。シリコーンゴム及び水酸化カルシウム粉体の一部が化学反応しても、成形された混練材あるいは製錬体の抗ウイルス性を阻害することはない。 The vulcanizing agent has the effect of curing the kneaded material under heating conditions. Therefore, the kneaded material is a molded material in which silicone rubber and calcium hydroxide powder are kneaded and mixed in a state where it can be cured. Even if a part of the silicone rubber and the calcium hydroxide powder chemically reacts, the antiviral property of the molded kneaded material or the smelted material is not impaired.
シリコン材の典型的な例としては、シリコーンゴム（共和工業株式会社製）が知られる。 Silicone rubber (manufactured by Kyowa Kogyo Co., Ltd.) is known as a typical example of a silicon material.
シリコーンゴムとしては、低硬度シリコーンゴム、中硬度シリコーンゴム、高硬度シリコーンゴムが知られる。本発明には、低硬度シリコーンゴムが好んで用いられる。低硬度シリコーンゴムで柔らかい伸びと密着特性の成形品を製造できる。 As the silicone rubber, low hardness silicone rubber, medium hardness silicone rubber, and high hardness silicone rubber are known. Low hardness silicone rubber is preferably used in the present invention. It is possible to manufacture molded products with low hardness silicone rubber and soft elongation and adhesion characteristics.
シリコーンゴムは、オルガノポリシキロサンにシリカ系充填剤を配合したものが一般的とされ、充填剤としてはフュームドシリカ、沈降性シリカ、石英粉末、けいそう土などが代表的なものとして挙げられる。 Silicone rubber is generally composed of organopolycyclisan mixed with a silica-based filler, and typical examples of the filler include fumed silica, precipitated silica, quartz powder, and diatomaceous earth. ..
シリコーンゴム（共和工業株式会社製）は、
１°～２０°：低硬度
５°の場合 ：耳たぶのような柔らかさを持つ。半透明、黒色。着色され得る。
Silicone rubber (manufactured by Kyowa Kogyo Co., Ltd.)
1 ° to 20 °:
１０°の場合 ：肌と似た硬さを持つ。半透明、黒色。着色され得る。ブレンド可。 At 10 °: Has a hardness similar to that of skin. Translucent, black. Can be colored. Can be blended.
２０°の場合 ：半透明、黒色。機能製品に用いられる。 At 20 °: translucent, black. Used for functional products.
３０°～７０°：一般硬度（中硬度）
８０°～９０°：高硬度
と分類される。
30 ° -70 °: General hardness (medium hardness)
80 ° -90 °: Classified as high hardness.
本実施例にあっては、硬度５°～２５°あるいは５°～４０°内の低硬度シリコーンゴムあるいは低硬度―中硬度シリコーンゴムが採用される。 In this embodiment, low hardness silicone rubber or low hardness-medium hardness silicone rubber having a hardness within 5 ° to 25 ° or 5 ° to 40 ° is adopted.
低硬度シリコーンゴムの特徴：
・柔軟性に富んでいる。元の形状に戻る。
Features of low hardness silicone rubber:
・ It is very flexible. It returns to the original shape.
・表面のタック感が強く、自己密着性が強い。 -Strong surface tackiness and strong self-adhesion.
・伸び率が非常に高い。 ・ The growth rate is very high.
等の特徴を持つ。 It has features such as.
混練部２２では、固体と固体との混練がなされ、混練状態の混練材を生成する特徴がある。 The kneading unit 22 is characterized in that the solid and the solid are kneaded to produce a kneaded material in a kneaded state.
生成された混練材２４は、混練材取り出し口部４からミキサー外部に連続して排出される。
The generated kneaded
混練材取り出し口部４の近辺に型３１が設けられる。
A
型３１は、混練材２４からボール状製錬体、棒状製錬体あるいは板状製錬体を形成するための型であり、ボール体状、棒体状あるいは板体状の窪み３２を備える。
The
混練材２４が型３１のボール体、棒体あるいは板体状の窪み３２に流し込まれ、所定時間保持され、冷却される。
The kneading
上述したように、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末を所定の重量を混練したときに、混練して混錬材として形成されたものを混錬材といい、混練材から成形品原型に各分離独立させ、混錬材の内、成形品成形に最良な範囲である最良な実施可能な範囲にある混錬材を製錬体という。 As described above, when a predetermined weight of calcium hydroxide powder is kneaded with 1 kg of silicone rubber, the material formed as a kneaded material by kneading is called a kneaded material, and the kneaded material is used as a prototype of a molded product. Of the kneaded materials that are separated and made independent, the kneaded material that is in the best feasible range, which is the best range for molding molded products, is called a smelter.
シリコン材と抗ウイルス剤を含有する混練材であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・混練材がシリコーンゴム及び水酸化カルシウム粉末を含有してなり、
・当該当該混練材における水酸化カルシウム粉末の含有量がシリコーンゴムの重量に対して適切な値（重量）を有して、シリコーンゴム１ｋｇの重量に対し、５００ｇ～７２０ｇ重量である混練材が生成される。
A kneading material containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
・ The kneaded material contains silicone rubber and calcium hydroxide powder.
-A kneaded material having a calcium hydroxide powder content in the kneaded material having an appropriate value (weight) with respect to the weight of the silicone rubber and having a weight of 500 g to 720 g with respect to the weight of 1 kg of the silicone rubber is produced. Will be done.
また、 シリコン材と抗ウイルス剤を含有する製錬体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・製錬体がシリコーンゴム及び水酸化カルシウム粉末含有してなり、
・当該製錬体における水酸化カルシウム粉末の含有量がシリコーンゴムの重量に対して適切な値（重量）を有して、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量であること
を特徴とする製錬体が生成される。
In addition, it is a smelter containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
・ The smelter contains silicone rubber and calcium hydroxide powder.
The content of the calcium hydroxide powder in the smelted product has an appropriate value (weight) with respect to the weight of the silicone rubber, and is characterized in that the weight is 500 g to 600 g with respect to the weight of 1 kg of the silicone rubber. A smelter is generated.
混練材中で、水酸化カルシウム粉末重量が所定の量に特定された混練材が幅広い成形品の原料に適した製錬体となる。 Among the kneaded materials, the kneaded material in which the weight of the calcium hydroxide powder is specified to a predetermined amount is a smelter suitable for a wide range of raw materials for molded products.
混練材は、例えば混練材を粒状物質にして不織布あるいは織布上に、もしくは不織布中にあるいは織布中に担持させてシートにして抗ウイルス性のインナーシートを形成し、衛生マスクの内部に挟持させる用途、あるいは多孔性の薄いフイルタシート状にした抗ウイルス性のフイルタとしての用途がある。 The kneaded material is, for example, made into a granular material and supported on a non-woven fabric or a woven fabric, or carried in a non-woven fabric or in a woven fabric to form a sheet to form an antiviral inner sheet, which is sandwiched inside a sanitary mask. There is an application to make it, or an antiviral filter in the form of a thin porous filter sheet.
製錬体は、シリコーンゴム及び水酸化カルシウムを含有するボール状製錬体、棒状製錬体あるいは板状製錬体であって、全体がボール、棒あるいは板に似た形態をなす柔軟性のある抗ウイルス性のハンド用のボール状抗ウイルス製錬体、棒状抗ウイルス製錬体あるいは板状抗ウイルス製錬体、ドアノブ被覆抗ウイルス製錬体あるいは携帯電話機被覆抗ウイルス製錬体を形成することができる。 The smelter is a ball-shaped smelter, a rod-shaped smelter, or a plate-shaped smelter containing silicone rubber and calcium hydroxide, and has a flexibility that resembles a ball, a rod, or a plate as a whole. Form a ball-shaped anti-virus smelter, a rod-shaped anti-virus smelter or a plate-shaped anti-virus smelter, a doorknob-coated anti-virus smelter or a mobile phone-coated anti-virus smelter for a certain anti-virus hand. be able to.
図２に、ミキサー１が、横置きされた例が示されたが、竪型配置とすることができる。
Although FIG. 2 shows an example in which the
図３は、混練材から抗ウイルス性製錬体が形成されることを示す図である。 FIG. 3 is a diagram showing that an antiviral smelter is formed from the kneaded material.
型３１は、製錬体２５から成形品、例えばボール状抗ウイルス製錬体、棒状抗ウイルス製錬体あるいは板状抗ウイルス製錬体、ドアノブ被覆抗ウイルス製錬体あるいは携帯電話機被覆抗ウイルス製錬体を形成するための型であり、X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。混練材が抗ウイルス製錬体とされて窪み３２に流し込まれ、所定時間保持され、冷却され、成形品が製作される。
The
混練材２４は、混練材取り出し口部４から型３１に投入される。混練材取り出し口部４に混練材切り分け手段２６が設けられ、連続して生成された混練材取り出し口部４は切断され、製錬体２５とされる。すなわち製錬体２５は、混練材２４から成型されたものである。
The kneading
型３１は、矢印で示されるようにX軸及びY軸方向に移動可能とされる。移動は、ミキサー１との関係で相対的である。
The
一つ一つの独立した製錬体２５が型３１に形成された窪み３２に一つ一つに投入される。
Each independent smelter 25 is put into the
窪み３２に流し込まれた製錬体２５は、所定時間保持され、室温まで冷却され、一つ一つの成形品としての製品とされる。
The smelter 25 poured into the
図４は、製錬体を形成するための各種の型の構造を示す図である。 FIG. 4 is a diagram showing the structures of various molds for forming a smelter.
図３示す型３１についての各種の型３１の構造が示される。型は、合わせ面を中央として相似の上方型と下方型との組み合わせになり、図４には下方型が示される。上方型と下方型との組み合わせによって双方の間には用途に応じた空間部が形成され、この空間部を充填するようにして製錬体が流し込み路（図示せず）から流し込まれる。各種の型３１を利用して、混練材２４から切り取られた製錬体２５から各種の製品が製作される。
The structures of
図４（ａ）は、製錬体２５から、柔軟性のある抗ウイルス性の手のひらで接触用のボール体を形成する型３１を示す。
FIG. 4A shows a
X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、半球体形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部に製錬体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用のボール体が製作される。
It is provided with a plurality of
図４（ｂ）は、製錬体２５から、柔軟性のある抗ウイルス性の手のひらで接触用の棒体を形成する型３１を示す。
FIG. 4B shows a
X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、棒が長手方向に半分にされた半円形断面を持つ形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部に製錬体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手ひらで接触用の棒状製錬体が製作される。
It is provided with a plurality of
図４（ｃ）は、製錬体２５から、柔軟性のある抗ウイルス性の手のひらで接触用の製錬体を形成する他の型３１を示す。
FIG. 4 (c) shows another
型３１は、X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、板状形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部に製錬体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用の板状製錬体が製作される。
The
図４（ｄ）は、製錬体２５から、柔軟性のある抗ウイルス性の手のひらで接触用のハンドノブ被覆製錬体を形成する型３１を示す。
FIG. 4D shows a
型３１は、上面に１個もしくは整列した複数の窪み３２を備える。ここでは１個の窪みが設けられた例が示される。窪み３２は、ドアノブ状形状をなす。型３１には、ドアノブ状形状の窪みの中央部に配置される中子３３が備えられる。中子３３は外方向きに複数の突起３４を備え、一部が窪み内面に接する。上方型と下方型とが組み合わされ、中子３３を持つ窪みの組み合わせで形成された空間部に製錬体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用のドアノブ被覆状製錬体が製作される。
The
図４（e）は、製錬体２５から、柔軟性のある抗ウイルス性の手のひらで接触用の携帯電話機被覆状製錬体を形成する型３１を示す。
FIG. 4 (e) shows a
型３１は、上面に１個もしくは整列した複数の窪み３２を備える。ここでは１個の窪みが設けられた例が示される。窪み３２は、携帯電話機状形状をなす。型３１には、携帯電話機状形状の窪みの中央部に配置されえ携帯電話機状形状の中子３６が備えられる。中子の一部が窪みの内面に接する。上方型と下方型とが組み合わされ、中子３３を持つ窪みの組み合わせで形成された空間部に製錬体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用の携帯電話機被覆状製錬体が製作される
。
The
図５から図９は、柔軟性のある抗ウイルス性の手のひらに接触して効果のある成形品である製品の例を具体的に示す図である。 5 to 9 are views specifically showing an example of a product which is a molded product which is effective in contact with a flexible antiviral palm.
図５、抗ウイルス性のボール状製錬体を示す図である。 FIG. 5 is a diagram showing an antiviral ball-shaped smelter.
この例の場合、ボールは球状をなす。球状としては、硬式野球ボールあるいはゴルフボール形状、ミカン形状、丸形おもちゃ形状等の身近ななじみの形態に模することができる。 In this example, the ball is spherical. As the spherical shape, it can be imitated in a familiar shape such as a hardball baseball ball or a golf ball shape, a mandarin orange shape, or a round toy shape.
図５（ａ）は、抗ウイルス性の手のひらに接触するボール状製錬体を示し、図４（ｂ）は、形成されたボール状製錬体１００（１００A）が人間の手のひらで握られている状態を示す。 FIG. 5 (a) shows a ball-shaped smelter in contact with an antiviral palm, and FIG. 4 (b) shows a formed ball-shaped smelter 100 (100A) held by a human palm. Indicates the state of being.
図４（ａ）に示される型３１が用いられて柔軟性のある抗ウイルス性のボール状製錬体１００（１００A）が形成される。
The
柔軟性のある抗ウイルス性のボール状製錬体１００（１００A）は、全体がボールに似た形態をなして、シリコン材及びドロマイトの混練材からなり、当該混練材が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手のひら４０に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。
The flexible anti-virus ball-shaped smelter 100 (100A) has a ball-like shape as a whole and is composed of a kneaded material of silicon material and dolomite, and the kneaded material has a flexible interior and dolomite. It consists of the surface part (surface) of the outward exposure, and the surface part of the dolomite external exposure exhibits antiviral properties, and when it is held by the
ボール状製錬体１００（１００A）は、柔軟性を備えているので手のひらで握られ、押圧されると、手のひらに接触用のボール状製錬体１００（１００A）の表面の手のひらへの接触面積が押圧前の接触面積に比べて増大する。抗ウイルス作用面積が増大する。この状態にあっても、ボール状製錬体１００（１００A）は、全体の形態を変えながら柔軟性を保持し、手のひらにフイットする。 Since the ball-shaped smelter 100 (100A) has flexibility, it is gripped by the palm, and when pressed, the contact area of the surface of the ball-shaped smelter 100 (100A) for contact with the palm. Increases compared to the contact area before pressing. Increases antiviral area. Even in this state, the ball-shaped smelter 100 (100A) retains its flexibility while changing its overall shape, and fits in the palm of the hand.
ボール状製錬体１００（１００A）は、抗菌作用面積が増大した抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 The ball-shaped smelter 100 (100A) kills virus bacteria attached to the palm by contact with the palm due to its antiviral performance with an increased antibacterial area. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、手のひらに接触用のボール状製錬体１００（１００A）の表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらから除去することが効果的になされる。 When an external force is applied, the contact area of the surface of the ball-shaped smelter 100 (100A) for contact with the palm increases, so it is effective to remove the virus adhering to the palm from the palm. It is done.
ボール状製錬体１００（１００A）は、柔軟性を備えているので、外力を加えることで、元のボール形状に戻すことができ、繰り返して用いられ得る。 Since the ball-shaped smelter 100 (100A) has flexibility, it can be returned to the original ball shape by applying an external force, and can be used repeatedly.
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちに除菌操作を行うことができる。 It can be used even in an environment that is not convenient for the use of wash water, and for example, when riding on a train and being caught by a strap, or when getting on or off the train, the sterilization operation can be performed immediately.
図５（ｃ）に示されるように、球状に替えて楕円形球状、すなわちラグビー状あるいは卵状の形状をなすボール状製錬体１００（１００A）が用いられ得る。 As shown in FIG. 5 (c), an elliptical spherical shape, that is, a ball-shaped smelter 100 (100A) having a rugby-like or egg-like shape can be used instead of the spherical shape.
手のひらでボールを握る関係で、ボール状製錬体１００（１００A）の大きさは、野球ボールの大きさ以下で、ピンポン玉の大きさ以上であることが推奨される。手のひらにボール状製錬体製錬体１００（１００A）が接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。 It is recommended that the size of the ball-shaped smelter 100 (100A) be smaller than the size of a baseball ball and larger than the size of a ping-pong ball because the ball is held by the palm of the hand. The contact of the ball-shaped smelter smelter 100 (100A) with the palm means that the smelter is within the size that can be grasped by the palm.
図５（ｃ）に示さるボール状製錬体１００（１００A）の大きさは、１例として長手方向に、５０ｍｍ、横方向に３０ｍｍ、他の例として７８ｍｍ、横方向に４４ｍｍが採用された。 The size of the ball-shaped smelter 100 (100A) shown in FIG. 5 (c) was 50 mm in the longitudinal direction and 30 mm in the lateral direction as an example, 78 mm in the other example, and 44 mm in the lateral direction. ..
ボール状製錬体１００（１００A）の中央部に固形材を内蔵させることができる。 A solid material can be incorporated in the central portion of the ball-shaped smelter 100 (100A).
図６は、抗ウイルス性の棒状製錬体を示す図である。 FIG. 6 is a diagram showing an antiviral rod-shaped smelter.
図６（ａ）は、抗ウイルス性のハンド接触用の棒状製錬体を示し、図６（ｂ）は、形成された棒状製錬体１００（１００B）が人間の手のひらで握られている状態を示す。球状としては、硬式野球バット、あるいはゴルフクラブ形状、ボールペン形状、棒形おもちゃ形状等の身近になじみの形態に模することができる。 FIG. 6 (a) shows a rod-shaped smelter for anti-virus hand contact, and FIG. 6 (b) shows a state in which the formed rod-shaped smelter 100 (100B) is held by a human palm. Is shown. As the spherical shape, it can be imitated in a familiar shape such as a hardball baseball bat, a golf club shape, a ballpoint pen shape, or a stick-shaped toy shape.
図４（ｂ）に示される型３１が用いられて柔軟性のある抗ウイルス性の棒状製錬体１００（１００B）が形成される。
The
柔軟性のある抗ウイルス性の棒状製錬体１００（１００B）は、全体が棒に似た形態をなして、シリコーンゴム及び水酸化カルシウムを主体とした製錬体からなり、当該製錬体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。そして容易に元の形状に戻され得る。 The flexible and anti-virus rod-shaped smelter 100 (100B) has a shape similar to that of a rod as a whole, and is composed of a smelter mainly composed of silicone rubber and calcium hydroxide. It consists of the inside of flexibility and the surface part (surface) of the outside exposure of calcium hydroxide, and the surface part of the outside exposure of calcium hydroxide exhibits antiviral properties, and is held by a human hand to exert an external force. With the action of, it retains its flexibility while changing its overall form. And it can be easily restored to its original shape.
棒状製錬体１００（１００B）は、柔軟性を備えているので手のひらで握られ、押圧されると、棒状製錬体１００（１００B）の表面の手のひらへの接触面積が増大する。この状態にあっても、棒状製錬体１００（１００B）は、全体の形態を変えながら柔軟性を保持する。 Since the rod-shaped smelter 100 (100B) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the rod-shaped smelter 100 (100B) with the palm increases. Even in this state, the rod-shaped smelter 100 (100B) retains its flexibility while changing its overall shape.
棒状製錬体１００（１００B）は、その抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 Due to its antibacterial performance, the rod-shaped smelter 100 (100B) kills virus bacteria attached to the palm by contact with the palm. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、棒状製錬体１００（１００B）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからのウイルスの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the rod-shaped smelter 100 (100B) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
棒状製錬体１００（１００B）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the rod-shaped smelter 100 (100B) has flexibility, it can be restored to the original rod shape by applying an external force, and can be used repeatedly.
洗浄水の便宜のあるところでない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちにウイルスを除去する操作を行うことができる。 It can be used even in an environment where there is no convenience of washing water, and it is possible to perform an operation of immediately removing a virus while riding or getting off, for example, when riding on a train and being caught by a strap.
棒状製錬体１００（１００B）には、円筒形にした棒状製錬体が含まれる。また、棒状製錬体１００（１００B）には、中心部に固体状の心棒を挿入した棒状製錬体が含まれる。 The rod-shaped smelter 100 (100B) includes a cylindrical smelter. Further, the rod-shaped smelter 100 (100B) includes a rod-shaped smelter in which a solid mandrel is inserted in the center.
図７は、抗ウイルス性の板状製錬体を示す図である。 FIG. 7 is a diagram showing an anti-virus plate-shaped smelter.
図７（ａ）は、抗ウイルス性の板状製錬体を示し、図７（ｂ）は、形成された板状製錬体１００（１００C）が人間の手のひらで握られている状態を示す。 FIG. 7 (a) shows an anti-virus plate-shaped smelter, and FIG. 7 (b) shows a state in which the formed plate-shaped smelter 100 (100C) is held by a human palm. ..
図４（ｃ）に示される型３１が用いられて柔軟性のある抗ウイルス性の板状製錬体１００（１００C）が形成される。
The
柔軟性のある抗ウイルス性の板状製錬体１００（１００C）は、全体が板に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製錬体からなり、当該製錬体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。 The flexible anti-virus plate-shaped smelter 100 (100C) has a shape similar to a plate as a whole and is composed of a smelter of silicone rubber and calcium hydroxide, and the smelter is flexible. The surface of the calcium hydroxide externally exposed is composed of the inside of the calcium hydroxide and the surface of the externally exposed calcium hydroxide. With, it retains flexibility while changing the overall form.
板状製錬体１００（１００C）は、柔軟性を備えているので手のひらで握られ、押圧されると、板状製錬体１００（１００C）の表面の手のひらへの接触面積が増大する。この状態にあっても、板状製錬体１００（１００C）は、全体の形態を変えながら柔軟性を保持する。 Since the plate-shaped smelter 100 (100C) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the plate-shaped smelter 100 (100C) with the palm increases. Even in this state, the plate-shaped smelter 100 (100C) retains its flexibility while changing its overall shape.
板状製錬体１００（１００C）は、その抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルスを死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 The plate-shaped smelter 100 (100C) kills the virus attached to the palm by contact with the palm due to its antiviral performance. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、板状製錬体１００（１００C）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらからの除去することが効果的になされる。 When an external force is applied, the contact area of the surface of the plate-shaped smelter 100 (100C) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
板状製錬体１００（１００C）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the plate-shaped smelter 100 (100C) has flexibility, it can be restored to its original rod shape by applying an external force, and can be used repeatedly.
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちにウイルスを除去する操作を行うことができる。 It can be used in an environment that is not convenient for the use of wash water, and can be operated to remove the virus immediately, for example, when riding on a train and being caught by a strap, while riding or getting off.
以上のように、全体がボール、棒あるいは板に似た形態をなして、混練材が主成分のシリコン材及び副成分の水酸化カルシウムを含有し、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムの混練で生成された製錬体になり、全体の形態を変えながらボール体、棒体あるいは板体の形態を保持し及び柔軟性を保持して、手のひら接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の手のひらで接触用のボール状製錬体、棒状製錬体あるいは板状製錬体が形成される。 As described above, the whole has a shape similar to a ball, a rod or a plate, and the kneaded material contains a silicon material as a main component and calcium hydroxide as a sub component, exhibits antiviral properties, and exhibits the above-mentioned silicone rubber and water. It becomes a smelting body produced by kneading calcium oxide, and keeps the morphology of the ball, rod or plate while changing the overall morphology, and retains the flexibility, is touched by the palm, and the surface is pressed. Then, the contact area of the surface with the palm is increased as compared with that before the pressing action, and the ball-shaped smelter, the rod-shaped smelter or the plate-shaped smelter for contact with the flexible antiviral palm is characterized. A smelting body is formed.
図８は、柔軟性のある抗ウイルス性の手のひらに接触して効果のある成形品であるドアノブ被覆製錬体を示す図である。
この例の場合、ドアノブ被覆製錬体は、長手方向に細い筒状の形状をなす。筒状部とすることで、内側におけるドアノブ表面のウイルス除去及び外側において手のひら付着のウイルスを除去する抗ウイルス性能が期待できる。
FIG. 8 is a diagram showing a doorknob-coated smelter, which is a molded product that is effective in contact with a flexible antiviral palm.
In the case of this example, the doorknob-coated smelter has a thin cylindrical shape in the longitudinal direction. By forming the tubular portion, antiviral performance can be expected to remove the virus on the surface of the doorknob on the inside and the virus attached to the palm on the outside.
図８（ａ）は、成形された抗ウイルス性のドアノブ被覆製錬体を示す写真であり、図８（ｂ）は、形成されたドアノブ被覆製錬体１００（１００D）が装着されるドアノブの例を示す。図８（ｂ）には、先端解放のドアノブが示される。 FIG. 8 (a) is a photograph showing a molded anti-virus doorknob-coated smelter, and FIG. 8 (b) shows a doorknob to which the formed doorknob-coated smelter 100 (100D) is mounted. An example is shown. FIG. 8B shows a doorknob with an open tip.
図４（ｄ）に示される型３１が用いられて柔軟性のある抗ウイルス性のドアノブ被覆製錬体１００（１００D）が形成される。
The
ドアノブ被覆製錬体１００（１００D）は、手のひら接触に用いられる表面確保のための体積を有し、ドアノブ４１を収納可能とする筒状部４２を有する。
The doorknob-covered smelter 100 (100D) has a volume for securing a surface used for palm contact, and has a
図８（ａ）に示さるドアノブ被覆製錬体１００（１００D）の大きさは、１例として長手方向に、１４２ｍｍ、横方向に最太部で，取っ手部径２１ｍｍが採用された。 As an example, the size of the doorknob-coated smelter 100 (100D) shown in FIG. 8A is 142 mm in the longitudinal direction, the thickest portion in the lateral direction, and a handle diameter of 21 mm.
柔軟性のある抗ウイルス性のドアノブ被覆製錬体１００（１００Ｄ）は、全体がドアノブに似た形態をなして、シリコーンゴム及び水酸化カルシウムの混練材からなり、当該製錬体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変え、接触面積を増大させながら柔軟性を保持する。 The flexible and anti-virus door knob coated smelter 100 (100D) has a shape similar to that of a door knob and is made of a kneaded material of silicone rubber and calcium hydroxide, and the smelter is flexible. It consists of the inside and the surface part (surface) of the outside exposure of calcium hydroxide, and the surface part of the outside exposure of calcium hydroxide exhibits antiviral properties, and is held by a human hand and the action of external force is applied. If present, it changes the overall shape and retains flexibility while increasing the contact area.
ドアノブ被覆製錬体１００（１００D）は、柔軟性を備えているので手のひらで握られ、押圧されると、ドアノブ被覆製錬体１００（１００D）の表面の手のひらへの接触面積が増大する。この状態にあっても、ドアノブ被覆製錬体１００（１００D）は、全体の形態を変えながら柔軟性を保持する。 Since the doorknob-coated smelter 100 (100D) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the doorknob-coated smelter 100 (100D) with the palm increases. Even in this state, the doorknob-covered smelter 100 (100D) retains its flexibility while changing its overall shape.
ドアノブ被覆製錬体１００（１００D）は、その抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルスを死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 The doorknob-coated smelter 100 (100D) kills the virus attached to the palm by contact with the palm due to its antiviral performance. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、ドアノブ被覆製錬体１００（１００D）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the doorknob-coated smelter 100 (100D) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
ドアノブ被覆製錬体１００（１００D）は、柔軟性を備えているので、外力を加えることで、元の形状に戻すことができ、繰り返して用いられ得る。 Since the doorknob-coated smelter 100 (100D) has flexibility, it can be restored to its original shape by applying an external force and can be used repeatedly.
洗浄水の便宜のあるところでない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちにウイルスを除去する操作を行うことができる。 It can be used even in an environment where there is no convenience of washing water, and it is possible to perform an operation of immediately removing a virus while riding or getting off, for example, when riding on a train and being caught by a strap.
図８（ｃ）は、成形された突起型のドアノブに適用されるドアノブ被覆製錬体を示す。 FIG. 8 (c) shows a doorknob-coated smelter applied to a molded protruding doorknob.
図８（ｃ）に示されるように、この例の場合、ドアノブ被覆製錬体は、長手方向と直径方向の長さがほぼ等しい筒状の形状をなす筒体４２で形成される。筒体４２は、図で、長手方向の左右方に孔４３，４４を持つ。筒体４２の内部は、空間部４５となる。
As shown in FIG. 8 (c), in the case of this example, the doorknob-covered smelter is formed of a
図８（ｄ）は、で表面を回転することで開放する突起型のドアノブ４１を示す。
FIG. 8D shows a protruding
突起型のドアノブ４１にドアノブ被覆製錬体１００（１００Ｄ）の筒体４２が被覆されることで、筒内に突起型のドアノブ４１が配設される。これで、ドアノブ被覆製錬体１００（１００D）が突起型のドアノブ４１に被覆して配設される。
By covering the protruding
手のひらでドアノブを握る関係で、ドアノブ被覆製錬体１００（１００D）の大きさは、ドアノブの大きさに対して１０～２０％程度大きさであることが推奨される。ドアノブ被覆製錬体１００（１００Ｄ）に接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。 It is recommended that the size of the doorknob-covered smelter 100 (100D) be about 10 to 20% of the size of the doorknob because the doorknob is gripped by the palm of the hand. Contacting the doorknob-coated smelter 100 (100D) means that it is within a size that can be grasped by the palm of the hand.
図８（ｃ）に示さるドアノブ被覆製錬体１００（１００D）の大きさは、１例として長手方向の筒体長さ４３ｍｍ、孔４３の径３４ｍｍ、孔４４の径３８ｍｍが採用された。
As an example, the size of the doorknob-coated smelter 100 (100D) shown in FIG. 8C is a tubular body length of 43 mm in the longitudinal direction, a
以上のように、全体がドアノブに似た形態をなして、混練材が主成分のシリコーンゴム及び副成分の水酸化カルシウムからなり、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムの混合混練で生成された製錬体になり、当該製錬体がドアノブを収納しドアノブに嵌め込まれるドアノブ収納空間部を有し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の手のひらで接触用のドアノブ被覆製錬体が形成される。 As described above, the whole has a shape similar to a doorknob, and the kneading material is composed of silicone rubber as a main component and calcium hydroxide as a sub component, exhibits antiviral properties, and is a mixed kneading of the silicone rubber and calcium hydroxide. The smelter is a smelter produced in the above, and the smelter has a doorknob storage space that stores the doorknob and is fitted into the doorknob. Flexible anti-viral palm contact characterized by the fact that when the surface is pressed against the palm, the contact area of the surface with the palm increases as compared to before the pressing action. A doorknob-covered smelter is formed.
図９は、抗ウイルス性の携帯電話機被覆製錬体を示す図である。
この例の場合、携帯電話機被覆製錬体は、携帯電話機を包む包袋状の形状をなす。
FIG. 9 is a diagram showing an anti-virus mobile phone coated smelter.
In the case of this example, the mobile phone covering smelter has a bag-like shape that wraps the mobile phone.
図９（ａ）は、抗ウイルス性の携帯電話機被覆製錬体を示し、図８（ｂ）は、形成された携帯電話機被覆製錬体１００（１００E）が装着される携帯電話機の例を示す。 FIG. 9A shows an antiviral mobile phone coated smelter, and FIG. 8B shows an example of a mobile phone to which the formed mobile phone coated smelter 100 (100E) is attached. ..
図４（e）に示される型３１が用いられて柔軟性のある抗ウイルス性の携帯電話機被覆製錬体１００（１００E）が形成される。
The
携帯電話機被覆製錬体１００（１００E）は、手のひら接触に用いられる体積を有し、携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部５２を有する。袋状部とすることで、内側における携帯電話機表面のウイルス除菌及び外側において手のひら付着のウイルスを除去する抗ウイルス性能が期待できる。
The mobile phone covering smelter 100 (100E) has a volume used for palm contact and has a bag-shaped
図４（e）に示される型３１が用いられて柔軟性のある抗ウイルス性の携帯電話機被覆製錬体１００（１００E）が形成される。
The
携帯電話機被覆製錬体１００（１００E）は、手のひら接触に用いられる体積を有し、携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部５２を有する。袋状部とすることで、内側における携帯電話機表面のウイルス除菌及び外側において手のひら付着のウイルス除菌になる抗菌性能が期待できる。
The mobile phone covering smelter 100 (100E) has a volume used for palm contact and has a bag-shaped
図９（ｂ）に示さる携帯電話機被覆製錬体１００（１００E）の大きさは、１例として長手方向に、１５０ｍｍ、横方向に９０ｍｍが採用された。 As an example, the size of the mobile phone coated smelter 100 (100E) shown in FIG. 9B is 150 mm in the longitudinal direction and 90 mm in the lateral direction.
柔軟性のある抗ウイルス性の携帯電話機被覆製錬体１００（１００E）は、全体が携帯電話機に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製錬体からなり、当該製錬体が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変え、接触面積を増大させながら柔軟性を保持する。 The flexible and anti-virus mobile phone coated smelter 100 (100E) has a form similar to that of a mobile phone as a whole, and is composed of a smelter of silicone rubber and calcium hydroxide. It consists of the inside of flexibility and the surface part (surface) of the outside exposure of dolomite, and the surface part of the outside exposure of dolomite exhibits antiviral properties, and is held by a human hand and has the action of external force. It changes the overall shape and maintains flexibility while increasing the contact area.
携帯電話機被覆製錬体１００（１００E）は、柔軟性を備えているので手のひらで握られ、押圧されると、携帯電話機被覆製錬体１００（１００Ｅ）の表面の手のひらへの接触面積が増大する。この状態にあっても、携帯電話機被覆製錬体１００（１００E）は、全体の形態を変えながら柔軟性を保持する。 Since the mobile phone coated smelter 100 (100E) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the mobile phone coated smelter 100 (100E) with the palm increases. .. Even in this state, the mobile phone coated smelter 100 (100E) maintains flexibility while changing the overall form.
携帯電話機被覆製錬体１００（１００E）は、その抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 Due to its antibacterial performance, the mobile phone-coated smelter 100 (100E) kills virus bacteria attached to the palm by contact with the palm. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、携帯電話機被覆製錬体１００（１００E）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらから除去することが効果的になされる。 When an external force is applied, the contact area of the surface of the mobile phone coated smelter 100 (100E) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
携帯電話機被覆製錬体１００（１００E）は、柔軟性を備えているので、外力を加えることで、元の形状に戻すことができ、繰り返して用いられ得る。 Since the mobile phone covering smelter 100 (100E) has flexibility, it can be returned to its original shape by applying an external force and can be used repeatedly.
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちにウイルスを除去する操作を行うことができる。 It can be used in an environment that is not convenient for the use of wash water, and can be operated to remove the virus immediately, for example, when riding on a train and being caught by a strap, while riding or getting off.
手のひらで携帯電話機を握る関係で、携帯電話機被覆製錬体１００（１００E）の大きさは携帯電話機の大きさに対して１０～２０％程度大きさであることが推奨される。携帯電話機被覆製錬体１００（１００E）に接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。 Since the mobile phone is held by the palm of the hand, it is recommended that the size of the mobile phone coated smelter 100 (100E) is about 10 to 20% of the size of the mobile phone. Contacting the mobile phone covering smelter 100 (100E) means that it is within a size that can be grasped by the palm of the hand.
以上のように、全体が携帯電話機に似た形態をなして、混練材が主成分のシリコーンゴム及び副成分の水酸化カルシウムからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混練で生成された製錬体になり、当該製錬体が携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部を有し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の携帯電話機被覆製錬体が形成される。 As described above, the whole is in a form similar to that of a mobile phone, and the kneaded material is composed of silicone rubber as a main component and calcium hydroxide as a sub component, exhibits antiviral properties, and is kneaded with the silicon material and the dolomite. It becomes the generated smelter, and the smelter has a bag-shaped part that can store the mobile phone together with the mobile phone cover, and keeps the shape similar to the mobile phone as a whole while changing the outer shape. And a flexible anti-virus mobile phone that retains flexibility and is characterized by an increase in the contact area of the surface with the palm when it is in contact with the palm and the surface is pressed compared to before the action. A coated smelter is formed.
図１０は、抗ウイルス性の室内フロアマット状製錬体及び自動車車内フロアマット状製錬体を示す図である。 FIG. 10 is a diagram showing an anti-virus indoor floor mat-shaped smelter and an automobile vehicle interior floor mat-shaped smelter.
図１０（ａ）は、抗ウイルス性の室内フロア状製錬体を示し、図１０（ｂ）は、形成された室内フロア状製錬体１００（１００Ｆ）に人間の足が載置されている状態を示し、柔軟性のある抗ウイルス性で、人間の足に接触して効果のある成形品である室内フロア状製錬体を示す。 FIG. 10 (a) shows an anti-virus indoor floor-shaped smelter, and FIG. 10 (b) shows a human foot placed on the formed indoor floor-shaped smelter 100 (100F). Shows the state, flexible, anti-virus, indoor floor-shaped smelter, which is a molded product that is effective in contact with human feet.
図１０（ｃ）は、抗ウイルス性の自動車車内フロア状製錬体を示し、図１０（ｄ）は、形成された自動車車内フロア状製錬体１００（１００Ｇ）に靴が載置されている状態を示し、柔軟性のある抗ウイルス性で、靴に接触して効果のある成形品である自動車車内フロア状製錬体を示す。 FIG. 10 (c) shows an anti-virus vehicle interior floor-shaped smelter, and FIG. 10 (d) shows shoes placed on the formed vehicle interior floor-shaped smelter 100 (100G). It shows the state, is a flexible anti-virus property, and shows a floor-shaped smelter in an automobile, which is a molded product that is effective in contact with shoes.
図４に示される型３１が用いられて柔軟性のある抗ウイルス性の室内フロア状製錬体１００（１００Ｆ）あるいは自動車車内フロア状製錬体１００（１００Ｇ）が形成される。
The
図１０（ａ）において、柔軟性のある抗ウイルス性の室内フロア状製錬体１００（１００Ｆ）は、全体が室内フロア板に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製錬体からなり、当該製錬体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、図１０（ｂ）に示されるように人間の足５２が載せられて押圧されると、その形態を変え、接触面積を増大させながら柔軟性を保持する。
In FIG. 10A, the flexible antiviral indoor floor-shaped smelter 100 (100F) has a shape similar to that of an indoor floor board as a whole, and is a smelted body of silicone rubber and calcium hydroxide. The smelter is composed of a flexible interior and a surface portion (surface) of calcium hydroxide externally exposed, and the surface portion of the calcium hydroxide externally exposed exhibits antiviral properties, and is shown in FIG. 10 (b). ), When the
室内フロア状製錬体１００（１００Ｆ）は、柔軟性を備えているので足で押圧されると、室内フロア状製錬体１００（１００Ｆ）の表面の足底表面への接触面積が増大する。この状態にあっても室内フロア状製錬体１００（１００Ｆ）は、形態を変えながら柔軟性を保持する。 Since the indoor floor-shaped smelter 100 (100F) has flexibility, when pressed by a foot, the contact area of the surface of the indoor floor-shaped smelter 100 (100F) with the sole surface increases. Even in this state, the indoor floor-shaped smelter 100 (100F) maintains flexibility while changing its form.
室内フロア状製錬体１００（１００Ｆ）は、その抗菌性性能によって足底への接触で、足底に付着したウイルス菌を死滅させる。これによって、足底に付着したウイルスが足から除去されたことになる。 The indoor floor-shaped smelter 100 (100F) kills virus bacteria attached to the sole by contact with the sole due to its antibacterial performance. This means that the virus attached to the sole of the foot has been removed from the foot.
外方からの力を作用させると室内フロア状製錬体１００（１００Ｆ）表面の足底への接触面積が増大するので、足に付着したウイルスの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the indoor floor-shaped smelter 100 (100F) with the sole of the foot increases, so that the virus attached to the foot is effectively removed.
室内フロア状製錬体１００（１００Ｆ）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the indoor floor-shaped smelter 100 (100F) has flexibility, it can be restored to its original rod shape by applying an external force, and can be used repeatedly.
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば室内でテレビ観戦しているようなとき、ウイルスを除去する操作を行うことができる。 It can be used in an environment that is not convenient for the use of wash water, and can be operated to remove a virus, for example, when watching TV indoors.
図１０（ｃ）において、柔軟性のある抗ウイルス性の自動車車内フロア状製錬体１００（１００Ｇ）は、周辺に飾りスカート５３を備えたプレート上に載置される。自動車車内フロア状製錬体１００（１００Ｇ）は、全体が自動車車内フロア板に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製錬体からなり、当該製錬体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、図１０（ｄ）に示されるように靴５４が載置されて押圧されると、その形態を変え、接触面積を増大させながら柔軟性を保持する。
In FIG. 10 (c), the flexible anti-virus vehicle interior floor-shaped smelter 100 (100G) is placed on a plate provided with a
自動車車内フロア状製錬体１００（１００Ｇ）は、柔軟性を備えているので足で押圧されると、自動車車内フロア状製錬体１００（１００Ｇ）の表面の足底表面への接触面積が増大する。この状態にあっても自動車車内フロア状製錬体１００（１００Ｇ）は、形態を変えながら柔軟性を保持する。 Since the floor-shaped smelter 100 (100G) in an automobile vehicle has flexibility, when pressed by a foot, the contact area of the surface of the floor-shaped smelter 100 (100G) in the automobile vehicle with the sole surface increases. do. Even in this state, the floor-shaped smelter 100 (100G) in the automobile vehicle maintains flexibility while changing its form.
自動車車内フロア状製錬体１００（１００Ｇ）は、その抗菌性性能によって足底への接触で、足底に付着したウイルス菌を死滅させる。これによって、足底に付着したウイルスが足から除去されたことになる。 Due to its antibacterial performance, the floor-shaped smelter 100 (100G) in an automobile kills virus bacteria attached to the sole by contact with the sole. This means that the virus attached to the sole of the foot has been removed from the foot.
外方からの力を作用させると自動車車内フロア状製錬体１００（１００Ｇ）表面の足底への接触面積が増大するので、足に付着したウイルスの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the floor-shaped smelter 100 (100G) in the automobile vehicle with the sole of the foot increases, so that the virus attached to the foot is effectively removed.
自動車車内フロア状製錬体１００（１００Ｇ）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the floor-shaped smelter 100 (100G) in an automobile has flexibility, it can be restored to its original rod shape by applying an external force, and can be used repeatedly.
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば自動車車内で運転手の脇に乗っているようなとき、ウイルスを除去する操作を行うことができる。 It can be used in an environment that is not convenient for the use of wash water, and it is possible to perform an operation for removing a virus, for example, when riding on the side of a driver in a car.
以上のように、シリコン材と抗ウイルス剤を含有する混練材の形成方法であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、混練材がシリコーンゴム及び水酸化カルシウム粉末からなり、
・当該水酸化カルシウム粉末の当該混練材における含有量がシリコーンゴムの重量に比較した値で、シリコーンゴム１ｋｇの重量に対し、５００ｇ～７２０ｇ重量で混練する混練材の形成方法が形成される。
As described above, it is a method for forming a kneaded material containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, the antiviral agent is calcium hydroxide powder, and the kneading material is silicone rubber and calcium hydroxide powder.
The content of the calcium hydroxide powder in the kneaded material is a value compared to the weight of the silicone rubber, and a method for forming the kneaded material to be kneaded with a weight of 500 g to 720 g with respect to the weight of 1 kg of the silicone rubber is formed.
さらに、シリコン材と抗ウイルス剤を含有する製錬体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・製錬体がシリコーンゴム及び水酸化カルシウム粉末含有してなり、
・当該製錬体における水酸化カルシウム粉末の含有量がシリコーンゴムの重量に対した値を有して、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量であること
を特徴とする製錬体が形成される。
Furthermore, it is a smelter containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
・ The smelter contains silicone rubber and calcium hydroxide powder.
A smelter characterized in that the content of calcium hydroxide powder in the smelter has a value relative to the weight of the silicone rubber and is 500 g to 600 g with respect to the weight of 1 kg of the silicone rubber. It is formed.
以上のように、シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状製錬体であって、
全体が室内フロアマットあるいは自動車車内フロアマットに似た形態をなして、混練材が主成分のシリコーンゴム及び副成分の水酸化カルシウムからなり、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムの混練で生成された製錬体になり、人間の足あるいは靴に接触して表面が押圧されると、柔軟性を保持し、当該人間の足あるいは靴への接触面積が押圧作用前に比べて増大することを特徴とする室内フロアマットあるいは自動車車内フロアマット状製錬体が形成される。
As described above, it is an indoor floor mat or a car interior floor mat-like smelter containing a silicon material and an antiviral agent.
The whole is shaped like an interior floor mat or a car interior floor mat, and is composed of silicone rubber as the main component and calcium hydroxide as a sub-component, and exhibits antiviral properties. It becomes a smelting body produced by kneading, and when the surface is pressed by contact with human feet or shoes, it retains flexibility and the contact area with the human feet or shoes is larger than before the pressing action. An interior floor mat or a car interior floor mat-like smelting body characterized by an increase is formed.
シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状の製錬体であって、
混練材として主成分のシリコン材及び副成分のドロマイトを準備し、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムを混練し、押圧体、例えば手のひらに接触されて、表面が押圧されると、柔軟性を保持し、当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製錬体を形成することを特徴とする抗ウイルス性の押圧体状の製錬体の形成方法が形成される。
An indoor floor mat or a car interior floor mat-like smelter containing a silicon material and an antiviral agent.
When a silicon material as a main component and a dolomite as a sub component are prepared as a kneading material to exhibit antiviral properties, the silicone rubber and calcium hydroxide are kneaded, and the surface is pressed by contact with a pressing body, for example, the palm. A method for forming an antiviral pressed body-shaped smelter, which is characterized in that the smelter retains flexibility and the contact area of the surface with the palm is increased as compared with that before the pressing action. It is formed.
また、製錬体を型に入れ、全体がボール、棒あるいは板に似た形に形成し、全体の形態を変えながらボール体、棒体あるいは板体の形態を保持し及び柔軟性を保持して、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製錬体を形成することを特徴とする柔軟性のある抗ウイルス性の手のひらに接触用のボール状、棒状あるいは板状製錬体の形成方法が形成される。 In addition, the smelting body is placed in a mold to form the whole into a shape similar to a ball, a rod or a plate, and the shape of the ball, the rod or the plate is maintained and the flexibility is maintained while changing the overall shape. The flexible antiviral property is characterized in that when the surface is pressed against the palm, the contact area of the surface with the palm is increased as compared with that before the pressing action. A method for forming a ball-shaped, rod-shaped or plate-shaped smelting body for contact is formed on the palm.
また、シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状の製錬体であって、
製錬体を型に入れ、全体がドアノブに似た形に形成し、外形の形態を変えながら柔軟性を保持して、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製錬体を形成することを特徴とする抗ウイルス性のドアノブ被覆製錬体の形成方法が形成される。
Further, it is a smelter in the form of an indoor floor mat or a car interior floor mat containing a silicon material and an antiviral agent.
The smelter is placed in a mold, formed into a shape similar to a doorknob, and retains flexibility while changing the shape of the outer shape. A method for forming an antiviral doorknob-coated smelter is formed, which comprises forming a smelter in which the contact area is increased as compared with that before the pressing action.
また、シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状の製錬体であって、
製錬体を型に入れ、全体が携帯電話機に似た形に形成し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひら接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製錬体を形成することを特徴とする柔軟性のある抗ウイルス性の携帯電話機被覆製錬体の形成方法が形成される。
Further, it is a smelter in the form of an indoor floor mat or a car interior floor mat containing a silicon material and an antiviral agent.
The smelter is placed in a mold to form the whole into a shape similar to a mobile phone, and the whole retains a shape similar to a mobile phone and retains flexibility while changing the shape of the outer shape, and is touched by the palm of the surface. A method for forming a flexible anti-virus mobile phone coated smelting body, which comprises forming a smelting body in which the contact area of the surface with the palm is increased as compared with that before the pressing action. Is formed.
抗ウイルス性の効果を十分に発揮させるためには、水酸化カルシウムが成形体である製品の表面により多く露出した表面積増大状態にすることが好ましいが、長期間に亘って手のひらへの接触する機能を発現するために製錬体を形成し、保持力を確保することが不可欠である。 In order to fully exert the antiviral effect, it is preferable to make the surface area of the product in which calcium hydroxide is exposed more exposed, but the function of contacting the palm for a long period of time is preferable. It is indispensable to form a smelter and secure the holding power in order to express.
本実施例によれば、
抗ウイルス性を呈する、柔軟性のある抗ウイルス性のハンド接触用の、例えば手のひらに接触させて効果のある混練材あるいは製錬体を提供することができる。
According to this embodiment
It is possible to provide a kneaded material or a smelter that exhibits antiviral properties and is effective for flexible antiviral hand contact, for example, in contact with the palm.
抗ウイルス性能向上のために接触面積の増大が可能な柔軟性のある材料が用いられること、例えば手のひらに付着した各種のウイルスを除去する目的のために使用可能とすること、例えば柔軟性のある抗ウイルス性ボール状体、棒状体あるいは板状体を形成し、外部環境における活動中にあっても手持ちができ、手のひらに付着した各種のウイルスを有効に除去してウイルス感染防止を有効に行い得るようにすることができる。 A flexible material that can increase the contact area is used to improve antiviral performance, for example, it can be used for the purpose of removing various viruses adhering to the palm, for example, flexible. It forms an antiviral ball-shaped body, rod-shaped body or plate-shaped body, can be held by hand even during activities in the external environment, and effectively removes various viruses attached to the palm to effectively prevent virus infection. You can get it.
これによって、外部における活動中にあっても各種のウイルスによる感染防止を有効に行い得る。例えば、水酸化カルシウムになる抗ウイルス性の柔軟性のある抗ウイルス性のハンド用のボール形状、棒形状あるいは板形状の製錬体の形成に適用応用できる。 This makes it possible to effectively prevent infection by various viruses even during external activities. For example, it can be applied and applied to the formation of a ball-shaped, rod-shaped or plate-shaped smelter for an antiviral and flexible antiviral hand that becomes calcium hydroxide.
１…ミキサー、２…横置きされた円筒状の混練筒、３…混練筒２の入口側である上流側に設けられたシリコン材投入口部、４…混練筒２の出口側に設けられた混練材取り出し口部、５…混練筒２の内部に横方向に設置された回転軸、６…回転軸の周囲に設けた攪拌スクリュー、７…攪拌スクリュー６の上流側に設けた送り羽根、８…攪拌スクリュー６の下流側に設けた送り羽根、９…回転軸５に回転力を付与する駆動源としてのモータ、１０…水酸化カルシウム粉末投入口部、１１…水酸化カルシウム投入管、１４…加硫剤投入口、２１…搬送部、２２…混練部、２３…供給部、２４…混練材、２５…製錬体、３１…型、３２…窪み、４０…手のひら、４２…筒状部、５２…袋状部、１００（１００A、１００B、１００C、１００D、１００E、１００Ｆ，１００Ｇ）…柔軟性のある抗ウイルス性のハンド接触用のボール体、棒体、板体ドアノブ被覆製錬体あるいは携帯電話機被覆製錬体。
1 ... Mixer, 2 ... Horizontally placed cylindrical kneading cylinder, 3 ... Silicon material input port provided on the upstream side, which is the inlet side of the
型３１は、上面に１個もしくは整列した複数の窪み３２を備える。ここでは１個の窪みが設けられた例が示される。窪み３２は、携帯電話機状形状をなす。型３１には、携帯電話機状形状の窪みの中央部に配置され、携帯電話機状形状の中子３６が備えられる。中子の一部が窪みの内面に接する。上方型と下方型とが組み合わされ、中子３３を持つ窪みの組み合わせで形成された空間部に製錬体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用の携帯電話機被覆状製錬体が製作される。
The
板状製錬体１００（１００C）は、その抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルスを死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。
The plate-shaped smelter 100 (100C) kills the virus attached to the palm by contact with the palm due to its antiviral performance. As a result, the virus attached to the palm has been removed from the palm.
本発明は、シリコン・水酸化カルシウム粉体からなる混練材及びシリコン・水酸化カルシウム粉体からなる製練体、及び当該混練材あるいは製練体の形成方法に関する。 The present invention relates to a kneaded material made of silicon / calcium hydroxide powder, a kneaded material made of silicon / calcium hydroxide powder, and a method for forming the kneaded material or kneaded material.
特許文献１～５に記載されるように、鉱物原料としてのドロマイト由来の抗ウイルス剤がマスク、フイルタ、塗料組成物、繊維あるいは担持シート、建材、複合セラミックスに適用応用されることが知られているが、混練材としてシリコン材及びドロマイトを用い、これらを混練してシリコン・ドロマイト混練材を生成し、シリコン・ドロマイト混練材から製練体を形成し、抗ウイルス成形品とすることが知られていない。
As described in
特許文献６には、レーヨン繊維中に酸化アルミニウム、酸化珪素及び酸化マグネシウムを主成分とする無機質抗菌材が1０～１５重量％混練されていることが記載される。レーヨン繊維中に酸化アルミニウム、酸化珪素及び酸化マグネシウムを主成分とする無機質抗菌材が担持される。この文献は、混練材としてシリコン材及びドロマイトを用い、これらを混練してシリコン・ドロマイト混練材を生成し、シリコン・ドロマイト混練材から混合混練状態の製練体を形成することを記載しない。 Patent Document 6 describes that 10 to 15% by weight of an inorganic antibacterial material containing aluminum oxide, silicon oxide and magnesium oxide as main components is kneaded in rayon fiber. An inorganic antibacterial material containing aluminum oxide, silicon oxide and magnesium oxide as main components is supported in the rayon fiber. This document does not describe that a silicon material and a dolomite are used as a kneading material, and these are kneaded to form a silicon dolomite kneaded material, and a kneaded body in a mixed kneaded state is formed from the silicon dolomite kneaded material.
特許文献８に記載されるシリコーンゴムは医療用シリコーンゴムであって、抗ウイル性混練材あるいは抗ウイルス性製練体を記載しない。 The silicone rubber described in Patent Document 8 is a medical grade silicone rubber, and does not describe an anti-will kneading material or an anti-virus kneaded product.
この場合、ウイルス不活性化状態を形成するという効果を得るために、ウイルス不活性化部材を人が日常に手で、もしくは他の箇所でしばしば接触する部材に取り付けするなどして配設しておくことが一つの有効手段となる。
配設に際し材料の粉体からウイルス不活性化部材として混練材を形成するために混練操作易さを確保すること、製練体を形成するために製練操作易さを確保するという問題を解決することが求められる。
In this case, in order to obtain the effect of forming the virus inactivating state, the virus inactivating member is arranged by attaching it to a member that is frequently contacted by a person on a daily basis or in other places. Keeping is one effective means.
Solved the problem of ensuring the ease of kneading operation to form the kneaded material as a virus-inactivating member from the powder of the material at the time of arrangement, and ensuring the ease of kneading operation to form the kneaded body. Is required to do.
本発明は、かかる点に鑑み、家庭あるいは職場内の施設あるいはその他の施設で、人が日常に手で、もしくは他の箇所でしばしば接触する部材に取り付けするなどしてウイルス不活性化部材を配設するに際して、材料の粉体からウイルス不活性化部材として混練材を形成するために混練操作易さを確保すること、製練体を形成するために製練操作易さを確保するという問題を解決することを課題とする。 In view of this point, the present invention disposes of a virus-inactivating member in a facility at home or in the workplace or other facility by attaching it to a member that a person often contacts by hand or in other places on a daily basis. At the time of installation, there are the problems of ensuring the ease of kneading operation to form the kneaded material as a virus inactivating member from the powder of the material and ensuring the ease of kneading operation to form the kneaded body. The challenge is to solve it.
また、シリコン材と抗ウイルス剤を含有する製練体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・混練材がシリコーンゴム及び水酸化カルシウム粉末を含有してなる製練体を提供する。
In addition, it is a kneaded body containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
-Providing a kneaded body in which the kneaded material contains silicone rubber and calcium hydroxide powder.
ここで、水酸化カルシウム粉末にはドロマイト粉末が含まれない。すなわち、水酸化カルシウムにはドロマイトが含まれない。本発明は、ドロマイト粉末を用いず、水酸化カルシウムを成分として用いるが、水酸化カルシウムに第３成分としてドロマイトを含有することを除外しない。混練材あるいは製練体を、水酸化カルシウム粉末を主体として適切な量（重量）をシリコーンゴムに混練することで抗ウイルス性能を向上させた混練材あるいは製練体を形成することができる。 Here, the calcium hydroxide powder does not contain the dolomite powder. That is, calcium hydroxide does not contain dolomite. The present invention does not use dolomite powder and uses calcium hydroxide as a component, but does not exclude calcium hydroxide containing dolomite as a third component. By kneading the kneaded material or kneaded body with silicone rubber in an appropriate amount (weight) mainly of calcium hydroxide powder, a kneaded material or kneaded body having improved antiviral performance can be formed.
本発明において、混練材中にあるいは製練体中に、シリコーンゴム１ｋｇに対して含有させる水酸化カルシウム粉末の量を特定することを試みた。
図１は、本発明の抗ウイルス性混練材及び抗ウイルス性製練体を表示するＸ―Ｙ座標図
である。
In the present invention, it has been attempted to specify the amount of calcium hydroxide powder contained in 1 kg of silicone rubber in the kneaded material or the kneaded body.
FIG. 1 is an XY coordinate diagram showing the antiviral kneading material and the antiviral kneaded product of the present invention.
図１は、シリコーンゴム及び水酸化カルシウム粉末からなるウイルス感染に有効な混練材を形成し、ウイルス不活性化部材の形成し易さ、すなわち製練し易い混練材を確保することができることを示す実験結果を示すＸ―Ｙ座標で示す図である。Ｘ軸は、シリコーンゴム１ｋｇに対して投入されたシリコーンゴム量を重量で示し、Ｙ軸は、混練材あるいは製練体の表面ｐＨ値を示す。表面ｐＨ値は、抗ウイルス性の強さを示す。表面ｐＨ値が高いほど抗ウイルス性の強さは強い。 FIG. 1 shows that a kneading material made of silicone rubber and calcium hydroxide powder, which is effective against virus infection, can be formed, and the kneading material which is easy to form a virus inactivating member, that is , easy to knead can be secured. It is a figure which shows the experimental result by the XY coordinates. The X-axis indicates the amount of silicone rubber charged with respect to 1 kg of silicone rubber by weight, and the Y-axis indicates the surface pH value of the kneaded material or kneaded product . The surface pH value indicates the strength of antiviral property. The higher the surface pH value, the stronger the antiviral strength.
＜実験内容＞
シリコン原料混練時にドロマイト粉体を混合混練したときに、保持力を確保することができた例を示す実験
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末１００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末２００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末３００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末４００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末５００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末６００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末７００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末８００ｇを混練して混練材を形成しようとしたが、混練ができなかった。
<Experimental content>
An experimental example showing an example in which the holding power could be secured when the dolomite powder was mixed and kneaded at the time of kneading the silicon
200 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
300 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
400 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
500 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
600 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
700 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
An attempt was made to knead 800 g of calcium hydroxide powder with 1 kg of silicone rubber to form a kneaded material, but the kneading was not possible.
実験結果によれば、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末７２０ｇ程度までは混合し製練して混練材を形成することができたが、混練材は、６００ｇを超えると脆く、各分離独立した製練体とすることは困難であった。 According to the experimental results, it was possible to mix and knead up to about 720 g of calcium hydroxide powder with 1 kg of silicone rubber to form a kneaded material, but the kneaded material is brittle when it exceeds 600 g, and each is separated and independent. It was difficult to make a kneaded body.
分離独立した製練体とする場合、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末６００ｇまでは製練して製練体を形成することができた。 In the case of making a separate and independent kneaded body, it was possible to knead up to 600 g of calcium hydroxide powder with respect to 1 kg of silicone rubber to form a kneaded body.
ここで、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末を所定の重量を、混練可能環境下、混練して混錬材として形成されたものを抗ウイルス性の混錬材（以下、混練材という。）といい、混練材から成形品原型に各分離独立させ、混錬材の内、成形品成形に最良な範囲である最良な実施可能な範囲にある混錬材を抗ウイルス性の製練体（以下、製練体という。）という。混練材あるいは製練体を成形品成形するに際しては、混練可能環境の加熱状態下、加硫処理による硬化処理がなされる。 Here, a material formed as a kneaded material by kneading a predetermined weight of calcium hydroxide powder with respect to 1 kg of silicone rubber in a kneadable environment is referred to as an antiviral kneaded material (hereinafter referred to as a kneaded material). ), Which separates and separates the kneaded material into the molded product prototype, and among the kneaded materials, the kneaded material in the best feasible range, which is the best range for molding the molded product, is an anti-virus kneaded product. (Hereafter, it is called a kneaded body .) When the kneaded material or the kneaded product is molded into a molded product, it is cured by a vulcanization treatment under the heating state of a kneadable environment.
混練可能領域が、混練可能領域が混練可能長さＬ１で、製練可能領域が製練可能長さＬ２で、抗ウイルス性能を考慮したときに、実施可能な混練材形成長さｌ１で、実施可能な製練体形成長さｌ２で示される。混練困難領域が、Ｌ１を延長した領域に、製練困難領域がＬ２を延長した領域に示される。混練材及び製練体のいずれもがビジネス上、製品として取り扱われ得る。 The kneadable area has a kneadable area of L 1 and the kneadable area has a kneadable length of L 2 , and the kneaded material forming length l 1 can be implemented when antiviral performance is taken into consideration. Indicated by the feasible kneaded body formation length l 2 . The difficult kneading region is shown in the region where L 1 is extended, and the difficult kneading region is shown in the region where L 2 is extended. Both the kneaded material and the kneaded body can be treated as a product in business.
Ｙ軸：製練体あるいは混練材の表面ｐＨ値を示す軸。
Ｈ：座標上で、実験結果で得られたプロットを結んで得られた曲線状の線図
Ａ域：線図Ｈ内混練長で、混練材形成域
Ｂ域：線図Ｈ内製練長で、製練体形成域
Ｃ域：線図Ｈ内混練長外方で混練材形成困難域
Ｄ域：ウイルス不活性有効下方ラインＭのｐＨ値１１及びウイルス不活性有効上方ラインＮのｐＨ値１２で区画されるウイルス不活性域（抗ウイルス領域）
Ｅ域：Ａ域及びＤ域で区画されるウイルス不活性混練材域
Ｆ域：Ｂ域及びＤ域で区画されるウイルス不活性製練体域
Ｇ域：Ｃ域及びＤ域で区画されるウイルス不活性域・混練材形成困難域
Ｌ１：混練可能長
Ｌ２：製練可能長
ｌ１：実施可能な混練材形成可能長
ｌ２：実施可能な製練長形成可能長
この実験結果から、・混練材における水酸化カルシウム粉末の含有量がシリコーンゴムの重量で、混練可能な値で、抗ウイルスとして有効なｐＨが11～１２に範囲にある、シリコーンゴム１ｋｇの重量に対し、５００ｇ～７２０ｇ重量である混練材が提供される。
Y-axis: An axis indicating the surface pH value of the kneaded body or kneaded material.
H: Curved diagram obtained by connecting the plots obtained from the experimental results on the coordinates Area A: In the kneading length in the diagram H, area B in the kneaded material forming region: In the kneading length in the diagram H Area C of kneaded body formation: Area D where kneading material is difficult to form outside the kneading length in diagram H: At
Area E: Virus-inert kneaded material area partitioned by A and D areas F area: Virus-inactive kneading body area partitioned by B and D areas G area: Virus partitioned by C and D areas Inactive area / difficult kneading material formation area L 1 : Kneading possible length L 2 : Kneading possible length l 1 : Implementable kneading material forming possible length l 2 : Implementable kneading length forming possible length From this experimental result, -The content of the calcium hydroxide powder in the kneading material is the weight of the silicone rubber, which is a value that can be kneaded, and the pH effective as an antivirus is in the range of 11 to 12, 500 g to 720 g with respect to the weight of 1 kg of the silicone rubber. The weight of the kneaded material is provided.
また、・製練体における水酸化カルシウム粉末の含有量がシリコーンゴムの重量で、製練可能な値で、抗ウイルスとして有効なｐＨが11～１２に範囲にある、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量である製練体が提供される。 In addition, the content of calcium hydroxide powder in the kneaded product is the weight of the silicone rubber, which is a value that can be kneaded , and the pH effective as an antivirus is in the range of 11 to 12, with respect to the weight of 1 kg of the silicone rubber. , 500 g-600 g weight is provided.
よって、シリコン材と抗ウイルス剤を含有する製練体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であり、製練体がシリコーンゴム及び水酸化カルシウム粉末を含有してなり、
・当該水酸化カルシウム粉末の当該製練体における含有量がシリコーンゴムの重量に対した値であって、当該対比重量値が、当該シリコーンゴム及び当該水酸化カルシウム粉末を製練可能で、当該製練体のｐＨが予め定めたウイルス不活性有効下方値と予め定めたウイルス不活性有効上方値の範囲のｐＨが11～１２に範囲にある重量値で、５００ｇ～６００ｇ重量であることを特徴とする製練体が提供される。
Therefore, it is a kneaded body containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, the antiviral agent is calcium hydroxide powder, and the kneaded product contains silicone rubber and calcium hydroxide powder.
-The content of the calcium hydroxide powder in the kneaded product is a value relative to the weight of the silicone rubber, and the relative weight value is such that the silicone rubber and the calcium hydroxide powder can be kneaded . The pH of the dough is a weight value in the range of 11 to 12 and a weight of 500 g to 600 g, which is in the range of the predetermined virus-inert effective lower value and the predetermined virus-inert effective upper value. The kneaded body is provided.
成形品を形成には、製練体が用いられる。 A kneaded body is used to form a molded product.
抗ウイルス性混練材あるいは抗ウイルス性製練体の形成に当たっては、抗ウイルス性混練材あるいは抗ウイルス性製練体に、必要に応じて、ドロマイト、炭酸カルシウム、炭酸カルシウム、炭酸マグネシウム、酸化マグネシウムの化学成分を第３成分として含有させることができる。 In forming the anti-viral kneaded material or the anti-viral kneaded material, the anti-viral kneaded material or the anti-viral kneaded material may be prepared with dolomite, calcium carbonate, calcium carbonate, magnesium carbonate or magnesium oxide as required. A chemical component can be contained as a third component.
本発明によれば、シリコーンゴム及び水酸化カルシウムを主体として形成され、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末が５００ｇ～７２０ｇ、特に５００ｇ～６００ｇ混練あるいは製練されて、混練性あるいは製練性に優れた抗ウイルス性を呈する混練材あるいは製練体を提供することができる。 According to the present invention, it is formed mainly of silicone rubber and calcium hydroxide, and 500 g to 720 g of calcium hydroxide powder, particularly 500 g to 600 g, is kneaded or kneaded with respect to 1 kg of silicone rubber to be kneaded or kneaded . It is possible to provide a kneaded material or a kneaded product having excellent antiviral properties.
抗ウイルス性を呈する混練材あるいは製練体は、衛生マスクのインナーシートに用いて、あるいは押圧体に用いて、例えば手のひらに付着した各種のウイルスを除去する目的のために使用を可能とする。例えば柔軟性のある抗ウイルス性のドアノブ被覆体を形成することができる。また、ボール状体、棒状体あるいは板状体を形成し、外部環境における活動中にあっても手持ちができ、手のひらに付着した各種のウイルスを有効に除去してウイルス感染防止を有効に行い得るようにすることができる。 The kneaded material or kneaded material exhibiting antiviral properties can be used as an inner sheet of a sanitary mask or as a pressing body, for example, for the purpose of removing various viruses adhering to the palm. For example, a flexible antiviral doorknob covering can be formed. In addition, it can form a ball-shaped body, a rod-shaped body, or a plate-shaped body, and can be held by hand even during activities in the external environment, and can effectively remove various viruses attached to the palm to effectively prevent virus infection. Can be done.
図１で、混練材が練り状態のシリコーンゴム及び水酸化カルシウム粉末を含有してなる混練材又は製練体形成の基本構成について説明した。 In FIG. 1, the basic configuration of forming a kneaded material or a kneaded body in which the kneaded material contains a kneaded silicone rubber and calcium hydroxide powder has been described.
投入された練り状態のシリコーンゴム、水酸化カルシウム粉体は、加硫剤の添加状態下、混練部２２で、例えば１４０―１７０°の加熱下で混錬に要する時間混練され、混練状態の混練材２４が生成される。
The charged silicone rubber and calcium hydroxide powder are kneaded in the kneading section 22 under the addition of the vulcanizing agent for the time required for kneading, for example, under heating at 140-170 °, and kneaded in the kneaded state.
加硫剤は、加熱状態下、混練材を硬化させる作用を呈する。したがって、混練材は、硬化され得る状態にあって、シリコーンゴム及び水酸化カルシウム粉体が混練されて混合状態にある成形材である。シリコーンゴム及び水酸化カルシウム粉体の一部が化学反応しても、成形された混練材あるいは製練体の抗ウイルス性を阻害することはない。 The vulcanizing agent has the effect of curing the kneaded material under heating conditions. Therefore, the kneaded material is a molded material in which silicone rubber and calcium hydroxide powder are kneaded and mixed in a state where it can be cured. Even if a part of the silicone rubber and the calcium hydroxide powder undergoes a chemical reaction, the antiviral property of the molded kneaded material or kneaded material is not impaired .
型３１は、混練材２４からボール状製練体、棒状製練体あるいは板状製練体を形成するための型であり、ボール体状、棒体状あるいは板体状の窪み３２を備える。
The
上述したように、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末を所定の重量を混練したときに、混練して混練材として形成されたものを混練材といい、混練材から成形品原型に各分離独立させ、混練材の内、成形品成形に最良な範囲である最良な実施可能な範囲にある混練材を製練体という。 As described above, when a predetermined weight of calcium hydroxide powder is kneaded with 1 kg of silicone rubber, the kneaded material formed as a kneaded material is called a kneaded material, and the kneaded material is used as a molded product prototype. Of the kneaded materials that are separated and made independent, the kneaded material that is in the best feasible range, which is the best range for molding a molded product, is called a kneaded body .
また、 シリコン材と抗ウイルス剤を含有する製練体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・製練体がシリコーンゴム及び水酸化カルシウム粉末含有してなり、
・当該製練体における水酸化カルシウム粉末の含有量がシリコーンゴムの重量に対して適切な値（重量）を有して、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量であること
を特徴とする製練体が生成される。
In addition, it is a kneaded body containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
・ The kneaded product contains silicone rubber and calcium hydroxide powder.
The content of the calcium hydroxide powder in the kneaded product has an appropriate value (weight) with respect to the weight of the silicone rubber, and is characterized in that the weight is 500 g to 600 g with respect to the weight of 1 kg of the silicone rubber. A kneaded body is produced.
混練材中で、水酸化カルシウム粉末重量が所定の量に特定された混練材が幅広い成形品の原料に適した製練体となる。 Among the kneaded materials, the kneaded material in which the weight of the calcium hydroxide powder is specified to a predetermined amount is suitable as a raw material for a wide range of molded products.
製練体は、シリコーンゴム及び水酸化カルシウムを含有するボール状製練体、棒状製練体あるいは板状製練体であって、全体がボール、棒あるいは板に似た形態をなす柔軟性のある抗ウイルス性のハンド用のボール状抗ウイルス製練体、棒状抗ウイルス製練体あるいは板状抗ウイルス製練体、ドアノブ被覆抗ウイルス製練体あるいは携帯電話機被覆抗ウイルス製練体を形成することができる。 The kneaded body is a ball-shaped kneaded body, a rod-shaped kneaded body or a plate-shaped kneaded body containing silicone rubber and calcium hydroxide, and has a flexibility that resembles a ball, a rod or a plate as a whole. Form a ball-shaped anti-virus kneaded body, rod-shaped anti-virus kneaded body or plate-shaped anti-virus kneaded body, door knob-coated anti-virus kneaded body or mobile phone-coated anti-virus kneaded body for a certain anti-virus hand. be able to.
図３は、混練材から抗ウイルス性製練体が形成されることを示す図である。 FIG. 3 is a diagram showing that an antiviral kneaded product is formed from the kneaded material.
型３１は、製練体２５から成形品、例えばボール状抗ウイルス製練体、棒状抗ウイルス製練体あるいは板状抗ウイルス製練体、ドアノブ被覆抗ウイルス製練体あるいは携帯電話機被覆抗ウイルス製練体を形成するための型であり、X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。混練材が抗ウイルス製練体とされて窪み３２に流し込まれ、所定時間保持され、冷却され、成形品が製作される。
The
混練材２４は、混練材取り出し口部４から型３１に投入される。混練材取り出し口部４に混練材切り分け手段２６が設けられ、連続して生成された混練材取り出し口部４は切断され、製練体２５とされる。すなわち製練体２５は、混練材２４から成型されたものである。
The kneading
一つ一つの独立した製練体２５が型３１に形成された窪み３２に一つ一つに投入される。
Each independent kneading body 25 is put into the
窪み３２に流し込まれた製練体２５は、所定時間保持され、室温まで冷却され、一つ一つの成形品としての製品とされる。
The kneaded body 25 poured into the
図４は、製練体を形成するための各種の型の構造を示す図である。 FIG. 4 is a diagram showing the structures of various molds for forming a kneaded body.
図３示す型３１についての各種の型３１の構造が示される。型は、合わせ面を中央として相似の上方型と下方型との組み合わせになり、図４には下方型が示される。上方型と下方型との組み合わせによって双方の間には用途に応じた空間部が形成され、この空間部を充填するようにして製練体が流し込み路（図示せず）から流し込まれる。各種の型３１を利用して、混練材２４から切り取られた製練体２５から各種の製品が製作される。
The structures of
図４（ａ）は、製練体２５から、柔軟性のある抗ウイルス性の手のひらで接触用のボール体を形成する型３１を示す。
FIG. 4A shows a
X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、半球体形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部に製練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用のボール体が製作される。
It is provided with a plurality of
図４（ｂ）は、製練体２５から、柔軟性のある抗ウイルス性の手のひらで接触用の棒体を形成する型３１を示す。
FIG. 4B shows a
X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、棒が長手方向に半分にされた半円形断面を持つ形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部に製練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手ひらで接触用の棒状製練体が製作される。
It is provided with a plurality of
図４（ｃ）は、製練体２５から、柔軟性のある抗ウイルス性の手のひらで接触用の製練体を形成する他の型３１を示す。
FIG. 4 (c) shows another
型３１は、X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、板状形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部に製練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用の板状製練体が製作される。
The
図４（ｄ）は、製練体２５から、柔軟性のある抗ウイルス性の手のひらで接触用のハンドノブ被覆製練体を形成する型３１を示す。
FIG. 4D shows a
型３１は、上面に１個もしくは整列した複数の窪み３２を備える。ここでは１個の窪みが設けられた例が示される。窪み３２は、ドアノブ状形状をなす。型３１には、ドアノブ状形状の窪みの中央部に配置される中子３３が備えられる。中子３３は外方向きに複数の突起３４を備え、一部が窪み内面に接する。上方型と下方型とが組み合わされ、中子３３を持つ窪みの組み合わせで形成された空間部に製練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用のドアノブ被覆状製練体が製作される。
The
図４（e）は、製練体２５から、柔軟性のある抗ウイルス性の手のひらで接触用の携帯電話機被覆状製練体を形成する型３１を示す。
FIG. 4 (e) shows a
型３１は、上面に１個もしくは整列した複数の窪み３２を備える。ここでは１個の窪みが設けられた例が示される。窪み３２は、携帯電話機状形状をなす。型３１には、携帯電話機状形状の窪みの中央部に配置され、携帯電話機状形状の中子３６が備えられる。中子の一部が窪みの内面に接する。上方型と下方型とが組み合わされ、中子３３を持つ窪みの組み合わせで形成された空間部に製練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用の携帯電話機被覆状製練体が製作される。
The
図５、抗ウイルス性のボール状製練体を示す図である。 FIG. 5 is a diagram showing an antiviral ball-shaped kneaded body.
図５（ａ）は、抗ウイルス性の手のひらに接触するボール状製練体を示し、図４（ｂ）は、形成されたボール状製練体１００（１００A）が人間の手のひらで握られている状態を示す。 FIG. 5 (a) shows a ball-shaped kneaded body in contact with an antiviral palm, and FIG. 4 (b) shows a formed ball-shaped kneaded body 100 (100A) held by a human palm. Indicates the state of being.
図４（ａ）に示される型３１が用いられて柔軟性のある抗ウイルス性のボール状製練体１００（１００A）が形成される。
The
柔軟性のある抗ウイルス性のボール状製練体１００（１００A）は、全体がボールに似た形態をなして、シリコン材及びドロマイトの混練材からなり、当該混練材が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手のひら４０に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。
The flexible anti-virus ball-shaped kneaded product 100 (100A) has a ball-like shape as a whole and is composed of a kneaded material of silicon material and dolomite, and the kneaded material has a flexible interior and dolomite. It consists of the surface part (surface) of the externally exposed, and the surface part of the externally exposed dolomite exhibits antiviral properties, and when it is held by the
ボール状製練体１００（１００A）は、柔軟性を備えているので手のひらで握られ、押圧されると、手のひらに接触用のボール状製練体１００（１００A）の表面の手のひらへの接触面積が押圧前の接触面積に比べて増大する。抗ウイルス作用面積が増大する。この状態にあっても、ボール状製練体１００（１００A）は、全体の形態を変えながら柔軟性を保持し、手のひらにフイットする。 Since the ball-shaped kneading body 100 (100A) has flexibility, it is gripped by the palm, and when pressed, the contact area of the surface of the ball-shaped kneading body 100 (100A) for contact with the palm is in contact with the palm. Increases compared to the contact area before pressing. Increases antiviral area. Even in this state, the ball-shaped kneaded body 100 (100A) retains its flexibility while changing its overall shape, and fits in the palm of the hand.
ボール状製練体１００（１００A）は、抗菌作用面積が増大した抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 The ball-shaped kneaded body 100 (100A) kills virus bacteria adhering to the palm by contact with the palm due to its antiviral performance with an increased antibacterial area. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、手のひらに接触用のボール状製練体１００（１００A）の表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらから除去することが効果的になされる。 When an external force is applied, the contact area of the surface of the ball-shaped kneading body 100 (100A) for contact with the palm increases, so it is effective to remove the virus adhering to the palm from the palm. It is done.
ボール状製練体１００（１００A）は、柔軟性を備えているので、外力を加えることで、元のボール形状に戻すことができ、繰り返して用いられ得る。 Since the ball-shaped kneaded body 100 (100A) has flexibility, it can be returned to the original ball shape by applying an external force, and can be used repeatedly.
図５（ｃ）に示されるように、球状に替えて楕円形球状、すなわちラグビー状あるいは卵状の形状をなすボール状製練体１００（１００A）が用いられ得る。 As shown in FIG. 5 (c), an elliptical spherical shape, that is, a ball-shaped kneaded body 100 (100A) having a rugby-shaped or egg-shaped shape can be used instead of the spherical shape.
手のひらでボールを握る関係で、ボール状製練体１００（１００A）の大きさは、野球ボールの大きさ以下で、ピンポン玉の大きさ以上であることが推奨される。手のひらにボール状製練体１００（１００A）が接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。 It is recommended that the size of the ball-shaped kneaded body 100 (100A) be smaller than the size of a baseball ball and larger than the size of a ping-pong ball because the ball is held by the palm of the hand. The contact of the ball-shaped kneaded body 100 (100A) with the palm means that the ball-shaped kneaded body 100 (100A) is within the size range that can be grasped by the palm.
図５（ｃ）に示さるボール状製練体１００（１００A）の大きさは、１例として長手方向に、５０ｍｍ、横方向に３０ｍｍ、他の例として７８ｍｍ、横方向に４４ｍｍが採用された。 The size of the ball-shaped kneaded body 100 (100A) shown in FIG. 5 (c) was 50 mm in the longitudinal direction and 30 mm in the lateral direction as an example, 78 mm in the other example, and 44 mm in the lateral direction. ..
ボール状製練体１００（１００A）の中央部に固形材を内蔵させることができる。 A solid material can be incorporated in the central portion of the ball-shaped kneaded body 100 (100A).
図６は、抗ウイルス性の棒状製練体を示す図である。 FIG. 6 is a diagram showing an antiviral rod-shaped kneaded body.
図６（ａ）は、抗ウイルス性のハンド接触用の棒状製練体を示し、図６（ｂ）は、形成された棒状製練体１００（１００B）が人間の手のひらで握られている状態を示す。球状としては、硬式野球バット、あるいはゴルフクラブ形状、ボールペン形状、棒形おもちゃ形状等の身近になじみの形態に模することができる。 FIG. 6 (a) shows a rod-shaped kneaded body for anti-virus hand contact, and FIG. 6 (b) shows a state in which the formed rod-shaped kneaded body 100 (100B) is held by a human palm. Is shown. As the spherical shape, it can be imitated in a familiar shape such as a hardball baseball bat, a golf club shape, a ballpoint pen shape, or a stick-shaped toy shape.
図４（ｂ）に示される型３１が用いられて柔軟性のある抗ウイルス性の棒状製練体１００（１００B）が形成される。
The
柔軟性のある抗ウイルス性の棒状製練体１００（１００B）は、全体が棒に似た形態をなして、シリコーンゴム及び水酸化カルシウムを主体とした製練体からなり、当該製練体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。そして容易に元の形状に戻され得る。 The flexible anti-virus rod-shaped kneaded body 100 (100B) has a shape similar to a rod as a whole, and is composed of a kneaded body mainly composed of silicone rubber and calcium hydroxide. It consists of the inside of flexibility and the surface part (surface) of the outside exposure of calcium hydroxide, and the surface part of the outside exposure of calcium hydroxide exhibits antiviral properties, and is held by a human hand to exert an external force. With the action of, it retains its flexibility while changing its overall form. And it can be easily restored to its original shape.
棒状製練体１００（１００B）は、柔軟性を備えているので手のひらで握られ、押圧されると、棒状製練体１００（１００B）の表面の手のひらへの接触面積が増大する。この状態にあっても、棒状製練体１００（１００B）は、全体の形態を変えながら柔軟性を保持する。 Since the rod-shaped kneaded body 100 (100B) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the rod-shaped kneaded body 100 (100B) with the palm increases. Even in this state, the rod-shaped kneaded body 100 (100B) maintains flexibility while changing the overall shape.
棒状製練体１００（１００B）は、その抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 Due to its antibacterial performance, the rod-shaped kneaded body 100 (100B) kills virus bacteria attached to the palm by contact with the palm. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、棒状製練体１００（１００B）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからのウイルスの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the rod-shaped kneaded body 100 (100B) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
棒状製練体１００（１００B）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the rod-shaped kneaded body 100 (100B) has flexibility, it can be restored to the original rod shape by applying an external force, and can be used repeatedly.
棒状製練体１００（１００B）には、円筒形にした棒状製練体が含まれる。また、棒状製練体１００（１００B）には、中心部に固体状の心棒を挿入した棒状製練体が含まれる。 The rod-shaped kneaded body 100 (100B) includes a cylindrical kneaded body. Further, the rod-shaped kneaded body 100 (100B) includes a rod-shaped kneaded body in which a solid mandrel is inserted in the center.
図７は、抗ウイルス性の板状製練体を示す図である。 FIG. 7 is a diagram showing an anti-virus plate-shaped kneaded body.
図７（ａ）は、抗ウイルス性の板状製練体を示し、図７（ｂ）は、形成された板状製練体１００（１００C）が人間の手のひらで握られている状態を示す。 FIG. 7 (a) shows an anti-virus plate-shaped kneaded body, and FIG. 7 (b) shows a state in which the formed plate-shaped kneaded body 100 (100C) is held by a human palm. ..
図４（ｃ）に示される型３１が用いられて柔軟性のある抗ウイルス性の板状製練体１００（１００C）が形成される。
The
柔軟性のある抗ウイルス性の板状製練体１００（１００C）は、全体が板に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製練体からなり、当該製練体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。 The flexible anti-virus plate-shaped kneaded product 100 (100C) has a shape similar to a plate as a whole and is composed of a kneaded material of silicone rubber and calcium hydroxide, and the kneaded body is flexible. The surface of the calcium hydroxide externally exposed is composed of the inside of the calcium hydroxide and the surface of the externally exposed calcium hydroxide. With, it retains flexibility while changing the overall form.
板状製練体１００（１００C）は、柔軟性を備えているので手のひらで握られ、押圧されると、板状製練体１００（１００C）の表面の手のひらへの接触面積が増大する。この状態にあっても、板状製練体１００（１００C）は、全体の形態を変えながら柔軟性を保持する。 Since the plate-shaped kneaded body 100 (100C) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the plate-shaped kneaded body 100 (100C) with the palm increases. Even in this state, the plate-shaped kneaded body 100 (100C) maintains flexibility while changing the overall shape.
板状製練体１００（１００C）は、その抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルスを死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 The plate-shaped kneaded body 100 (100C) kills the virus attached to the palm by contact with the palm due to its antiviral performance. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、板状製練体１００（１００C）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらからの除去することが効果的になされる。 When an external force is applied, the contact area of the surface of the plate-shaped kneaded body 100 (100C) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
板状製練体１００（１００C）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the plate-shaped kneaded body 100 (100C) has flexibility, it can be returned to the original rod shape by applying an external force, and can be used repeatedly.
以上のように、全体がボール、棒あるいは板に似た形態をなして、混練材が主成分のシリコン材及び副成分の水酸化カルシウムを含有し、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムの混練で生成された製練体になり、全体の形態を変えながらボール体、棒体あるいは板体の形態を保持し及び柔軟性を保持して、手のひら接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の手のひらで接触用のボール状製練体、棒状製練体あるいは板状製練体が形成される。 As described above, the whole has a shape similar to a ball, a rod or a plate, and the kneaded material contains a silicon material as a main component and calcium hydroxide as a sub component, exhibits antiviral properties, and exhibits the above-mentioned silicone rubber and water. It becomes a kneaded body produced by kneading calcium oxide, and keeps the morphology of the ball, rod or plate while changing the overall morphology, and retains the flexibility, is touched by the palm, and the surface is pressed. Then, the contact area of the surface with the palm is increased as compared with that before the pressing action, and the ball-shaped kneaded body, the rod-shaped kneaded body or the plate-shaped body for contact with the flexible antiviral palm is characterized. A kneaded body is formed.
図８は、柔軟性のある抗ウイルス性の手のひらに接触して効果のある成形品であるドアノブ被覆製練体を示す図である。
この例の場合、ドアノブ被覆製練体は、長手方向に細い筒状の形状をなす。筒状部とすることで、内側におけるドアノブ表面のウイルス除去及び外側において手のひら付着のウイルスを除去する抗ウイルス性能が期待できる。
FIG. 8 is a diagram showing a doorknob-coated kneaded body, which is a molded product that is effective in contact with a flexible antiviral palm.
In the case of this example, the doorknob-coated kneaded body has a thin cylindrical shape in the longitudinal direction. By forming the tubular portion, antiviral performance can be expected to remove the virus on the surface of the doorknob on the inside and the virus attached to the palm on the outside.
図８（ａ）は、成形された抗ウイルス性のドアノブ被覆製練体を示す写真であり、図８（ｂ）は、形成されたドアノブ被覆製練体１００（１００D）が装着されるドアノブの例を示す。図８（ｂ）には、先端解放のドアノブが示される。 FIG. 8 (a) is a photograph showing a molded anti-virus doorknob-coated kneaded body, and FIG. 8 (b) shows a doorknob to which the formed doorknob-coated kneaded body 100 (100D) is mounted. An example is shown. FIG. 8B shows a doorknob with an open tip.
図４（ｄ）に示される型３１が用いられて柔軟性のある抗ウイルス性のドアノブ被覆製練体１００（１００D）が形成される。
The
ドアノブ被覆製練体１００（１００D）は、手のひら接触に用いられる表面確保のための体積を有し、ドアノブ４１を収納可能とする筒状部４２を有する。
The doorknob-coated kneaded body 100 (100D) has a volume for securing a surface used for palm contact, and has a
図８（ａ）に示さるドアノブ被覆製練体１００（１００D）の大きさは、１例として長手方向に、１４２ｍｍ、横方向に最太部で，取っ手部径２１ｍｍが採用された。 As an example, the size of the doorknob-coated kneaded body 100 (100D) shown in FIG. 8A is 142 mm in the longitudinal direction, the thickest portion in the lateral direction, and a handle diameter of 21 mm.
柔軟性のある抗ウイルス性のドアノブ被覆製練体１００（１００Ｄ）は、全体がドアノブに似た形態をなして、シリコーンゴム及び水酸化カルシウムの混練材からなり、当該製練体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変え、接触面積を増大させながら柔軟性を保持する。 The flexible and anti-virus door knob coated kneaded product 100 (100D) has a shape similar to that of a door knob as a whole and is made of a kneaded material of silicone rubber and calcium hydroxide. It consists of the inside and the surface part (surface) of the outside exposure of calcium hydroxide, and the surface part of the outside exposure of calcium hydroxide exhibits antiviral properties, and is held by a human hand and the action of external force is applied. If present, it changes the overall shape and retains flexibility while increasing the contact area.
ドアノブ被覆製練体１００（１００D）は、柔軟性を備えているので手のひらで握られ、押圧されると、ドアノブ被覆製練体１００（１００D）の表面の手のひらへの接触面積が増大する。この状態にあっても、ドアノブ被覆製練体１００（１００D）は、全体の形態を変えながら柔軟性を保持する。 Since the doorknob-coated kneaded body 100 (100D) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the doorknob-coated kneaded body 100 (100D) with the palm increases. Even in this state, the doorknob-coated kneaded body 100 (100D) maintains flexibility while changing the overall shape.
ドアノブ被覆製練体１００（１００D）は、その抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルスを死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 The doorknob-coated kneaded body 100 (100D) kills the virus attached to the palm by contact with the palm due to its antiviral performance. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、ドアノブ被覆製練体１００（１００D）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the doorknob-coated kneaded body 100 (100D) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
ドアノブ被覆製練体１００（１００D）は、柔軟性を備えているので、外力を加えることで、元の形状に戻すことができ、繰り返して用いられ得る。 Since the doorknob-coated kneaded body 100 (100D) has flexibility, it can be returned to its original shape by applying an external force, and can be used repeatedly.
図８（ｃ）は、成形された突起型のドアノブに適用されるドアノブ被覆製練体を示す。 FIG. 8 (c) shows a doorknob-coated kneaded body applied to a molded protruding doorknob.
図８（ｃ）に示されるように、この例の場合、ドアノブ被覆製練体は、長手方向と直径方向の長さがほぼ等しい筒状の形状をなす筒体４２で形成される。筒体４２は、図で、長手方向の左右方に孔４３，４４を持つ。筒体４２の内部は、空間部４５となる。
As shown in FIG. 8 (c), in the case of this example, the doorknob-coated kneaded body is formed of a
突起型のドアノブ４１にドアノブ被覆製練体１００（１００Ｄ）の筒体４２が被覆されることで、筒内に突起型のドアノブ４１が配設される。これで、ドアノブ被覆製練体１００（１００D）が突起型のドアノブ４１に被覆して配設される。
By covering the protruding
手のひらでドアノブを握る関係で、ドアノブ被覆製練体１００（１００D）の大きさは、ドアノブの大きさに対して１０～２０％程度大きさであることが推奨される。ドアノブ被覆製練体１００（１００Ｄ）に接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。 It is recommended that the size of the doorknob-coated kneaded body 100 (100D) be about 10 to 20% of the size of the doorknob because the doorknob is gripped by the palm of the hand. Contacting the doorknob-coated kneaded body 100 (100D) means that it is within a size range that can be grasped by the palm of the hand.
図８（ｃ）に示さるドアノブ被覆製練体１００（１００D）の大きさは、１例として長手方向の筒体長さ４３ｍｍ、孔４３の径３４ｍｍ、孔４４の径３８ｍｍが採用された。
As an example, the size of the doorknob-coated kneaded body 100 (100D) shown in FIG. 8C has a tubular body length of 43 mm in the longitudinal direction, a
以上のように、全体がドアノブに似た形態をなして、混練材が主成分のシリコーンゴム及び副成分の水酸化カルシウムからなり、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムの混合混練で生成された製練体になり、当該製練体がドアノブを収納しドアノブに嵌め込まれるドアノブ収納空間部を有し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の手のひらで接触用のドアノブ被覆製練体が形成される。 As described above, the whole has a shape similar to a doorknob, and the kneading material is composed of silicone rubber as a main component and calcium hydroxide as a sub component, exhibits antiviral properties, and is a mixed kneading of the silicone rubber and calcium hydroxide. The kneaded body has a doorknob storage space that stores the doorknob and is fitted into the doorknob. Flexible anti-viral palm contact characterized by the fact that when the surface is pressed against the palm, the contact area of the surface with the palm increases as compared to before the pressing action. A doorknob-coated kneaded body for use is formed.
図９は、抗ウイルス性の携帯電話機被覆製練体を示す図である。
この例の場合、携帯電話機被覆製練体は、携帯電話機を包む包袋状の形状をなす。
FIG. 9 is a diagram showing an anti-virus mobile phone coated kneaded body.
In the case of this example, the mobile phone-coated kneaded body has a bag-like shape that wraps the mobile phone.
図９（ａ）は、抗ウイルス性の携帯電話機被覆製練体を示し、図８（ｂ）は、形成された携帯電話機被覆製練体１００（１００E）が装着される携帯電話機の例を示す。 9 (a) shows an anti-virus mobile phone coated kneaded body, and FIG. 8 (b) shows an example of a mobile phone to which the formed mobile phone coated kneaded body 100 (100E) is attached. ..
図４（e）に示される型３１が用いられて柔軟性のある抗ウイルス性の携帯電話機被覆製練体１００（１００E）が形成される。
The
携帯電話機被覆製練体１００（１００E）は、手のひら接触に用いられる体積を有し、携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部５２を有する。袋状部とすることで、内側における携帯電話機表面のウイルス除菌及び外側において手のひら付着のウイルスを除去する抗ウイルス性能が期待できる。
The mobile phone-coated kneaded body 100 (100E) has a volume used for palm contact, and has a bag-shaped
図４（e）に示される型３１が用いられて柔軟性のある抗ウイルス性の携帯電話機被覆製練体１００（１００E）が形成される。
The
携帯電話機被覆製練体１００（１００E）は、手のひら接触に用いられる体積を有し、携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部５２を有する。袋状部とすることで、内側における携帯電話機表面のウイルス除菌及び外側において手のひら付着のウイルス除菌になる抗菌性能が期待できる。
The mobile phone-coated kneaded body 100 (100E) has a volume used for palm contact, and has a bag-shaped
図９（ｂ）に示さる携帯電話機被覆製練体１００（１００E）の大きさは、１例として長手方向に、１５０ｍｍ、横方向に９０ｍｍが採用された。 As an example, the size of the mobile phone coated kneaded body 100 (100E) shown in FIG. 9B is 150 mm in the longitudinal direction and 90 mm in the lateral direction.
柔軟性のある抗ウイルス性の携帯電話機被覆製練体１００（１００E）は、全体が携帯電話機に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製練体からなり、当該製練体が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変え、接触面積を増大させながら柔軟性を保持する。 The flexible and anti-virus mobile phone coated kneaded body 100 (100E) has a shape similar to that of a mobile phone as a whole, and is composed of a kneaded body of silicone rubber and calcium hydroxide. It consists of the inside of flexibility and the surface part (surface) of the outside exposure of dolomite, and the surface part of the outside exposure of dolomite exhibits antiviral properties, and it is held by a human hand and has the action of external force. It changes the overall shape and maintains flexibility while increasing the contact area.
携帯電話機被覆製練体１００（１００E）は、柔軟性を備えているので手のひらで握られ、押圧されると、携帯電話機被覆製練体１００（１００Ｅ）の表面の手のひらへの接触面積が増大する。この状態にあっても、携帯電話機被覆製練体１００（１００E）は、全体の形態を変えながら柔軟性を保持する。 Since the mobile phone coated kneaded body 100 (100E) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the mobile phone coated kneaded body 100 (100E) with the palm increases. .. Even in this state, the mobile phone coated kneaded body 100 (100E) maintains flexibility while changing the overall form.
携帯電話機被覆製練体１００（１００E）は、その抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 Due to its antibacterial performance, the mobile phone-coated kneaded body 100 (100E) kills virus bacteria attached to the palm by contact with the palm. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、携帯電話機被覆製練体１００（１００E）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらから除去することが効果的になされる。 When an external force is applied, the contact area of the surface of the mobile phone coated kneaded body 100 (100E) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
携帯電話機被覆製練体１００（１００E）は、柔軟性を備えているので、外力を加えることで、元の形状に戻すことができ、繰り返して用いられ得る。 Since the mobile phone coated kneaded body 100 (100E) has flexibility, it can be returned to its original shape by applying an external force and can be used repeatedly.
手のひらで携帯電話機を握る関係で、携帯電話機被覆製練体１００（１００E）の大きさは携帯電話機の大きさに対して１０～２０％程度大きさであることが推奨される。携帯電話機被覆製練体１００（１００E）に接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。 Since the mobile phone is held by the palm of the hand, it is recommended that the size of the mobile phone coated kneaded body 100 (100E) is about 10 to 20% of the size of the mobile phone. Contacting the mobile phone-coated kneaded body 100 (100E) means that it is within a size range that can be grasped by the palm of the hand.
以上のように、全体が携帯電話機に似た形態をなして、混練材が主成分のシリコーンゴム及び副成分の水酸化カルシウムからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混練で生成された製練体になり、当該製練体が携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部を有し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の携帯電話機被覆製練体が形成される。 As described above, the whole is in a form similar to that of a mobile phone, and the kneaded material is composed of silicone rubber as a main component and calcium hydroxide as a sub component, exhibits antiviral properties, and is kneaded with the silicon material and the dolomite. It becomes the generated kneaded body, and the kneaded body has a bag-shaped part that allows the mobile phone to be stored together with the mobile phone cover, and keeps the shape similar to the mobile phone as a whole while changing the outer shape. And a flexible anti-virus mobile phone that retains flexibility and is characterized by an increase in the contact area of the surface with the palm when it is in contact with the palm and the surface is pressed compared to before the action. A coated kneaded body is formed.
図１０は、抗ウイルス性の室内フロアマット状製練体及び自動車車内フロアマット状製練体を示す図である。 FIG. 10 is a diagram showing an anti-virus indoor floor mat-shaped kneaded body and an automobile vehicle interior floor mat-shaped kneaded body.
図１０（ａ）は、抗ウイルス性の室内フロア状製練体を示し、図１０（ｂ）は、形成された室内フロア状製練体１００（１００Ｆ）に人間の足が載置されている状態を示し、柔軟性のある抗ウイルス性で、人間の足に接触して効果のある成形品である室内フロア状製練体を示す。 FIG. 10 (a) shows an anti-virus indoor floor-shaped kneaded body, and FIG. 10 (b) shows a human foot placed on the formed indoor floor-shaped kneaded body 100 (100F). It shows the state, is flexible and antiviral, and shows an indoor floor-like kneaded product which is a molded product that is effective in contact with human feet.
図１０（ｃ）は、抗ウイルス性の自動車車内フロア状製練体を示し、図１０（ｄ）は、形成された自動車車内フロア状製練体１００（１００Ｇ）に靴が載置されている状態を示し、柔軟性のある抗ウイルス性で、靴に接触して効果のある成形品である自動車車内フロア状製練体を示す。 FIG. 10 (c) shows an anti-virus in-vehicle floor-shaped kneaded body, and FIG. 10 (d) shows shoes placed on the formed in-vehicle floor-shaped kneaded body 100 (100G). It shows the state, is a flexible anti-virus property, and shows a floor-shaped kneaded body in an automobile, which is a molded product that is effective in contact with shoes.
図４に示される型３１が用いられて柔軟性のある抗ウイルス性の室内フロア状製練体１００（１００Ｆ）あるいは自動車車内フロア状製練体１００（１００Ｇ）が形成される。
The
図１０（ａ）において、柔軟性のある抗ウイルス性の室内フロア状製練体１００（１００Ｆ）は、全体が室内フロア板に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製練体からなり、当該製練体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、図１０（ｂ）に示されるように人間の足５２が載せられて押圧されると、その形態を変え、接触面積を増大させながら柔軟性を保持する。
In FIG. 10A, the flexible antiviral indoor floor-shaped kneaded body 100 (100F) has a shape similar to that of an indoor floor board as a whole, and is a kneaded body of silicone rubber and calcium hydroxide. The kneaded product is composed of a flexible interior and a surface portion (surface) of calcium hydroxide externally exposed, and the surface portion of the calcium hydroxide externally exposed exhibits antiviral properties, and is shown in FIG. 10 (b). ), When the
室内フロア状製練体１００（１００Ｆ）は、柔軟性を備えているので足で押圧されると、室内フロア状製練体１００（１００Ｆ）の表面の足底表面への接触面積が増大する。この状態にあっても室内フロア状製練体１００（１００Ｆ）は、形態を変えながら柔軟性を保持する。 Since the indoor floor-shaped kneaded body 100 (100F) has flexibility, when pressed by a foot, the contact area of the surface of the indoor floor-shaped kneaded body 100 (100F) with the sole surface increases. Even in this state, the indoor floor-shaped kneaded body 100 (100F) maintains flexibility while changing its form.
室内フロア状製練体１００（１００Ｆ）は、その抗菌性性能によって足底への接触で、足底に付着したウイルス菌を死滅させる。これによって、足底に付着したウイルスが足から除去されたことになる。 The indoor floor-shaped kneaded body 100 (100F) kills virus bacteria adhering to the sole by contact with the sole due to its antibacterial performance. This means that the virus attached to the sole of the foot has been removed from the foot.
外方からの力を作用させると室内フロア状製練体１００（１００Ｆ）表面の足底への接触面積が増大するので、足に付着したウイルスの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the indoor floor-shaped kneaded body 100 (100F) with the sole of the foot increases, so that the virus attached to the foot is effectively removed.
室内フロア状製練体１００（１００Ｆ）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the indoor floor-shaped kneaded body 100 (100F) has flexibility, it can be returned to the original rod shape by applying an external force, and can be used repeatedly.
図１０（ｃ）において、柔軟性のある抗ウイルス性の自動車車内フロア状製練体１００（１００Ｇ）は、周辺に飾りスカート５３を備えたプレート上に載置される。自動車車内フロア状製練体１００（１００Ｇ）は、全体が自動車車内フロア板に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製練体からなり、当該製練体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、図１０（ｄ）に示されるように靴５４が載置されて押圧されると、その形態を変え、接触面積を増大させながら柔軟性を保持する。
In FIG. 10 (c), a flexible anti-virus vehicle interior floor-shaped kneaded body 100 (100G) is placed on a plate provided with a
自動車車内フロア状製練体１００（１００Ｇ）は、柔軟性を備えているので足で押圧されると、自動車車内フロア状製練体１００（１００Ｇ）の表面の足底表面への接触面積が増大する。この状態にあっても自動車車内フロア状製練体１００（１００Ｇ）は、形態を変えながら柔軟性を保持する。 Since the floor-shaped kneading body 100 (100G) in an automobile vehicle has flexibility, when pressed by a foot, the contact area of the surface of the floor-shaped kneading body 100 (100G) in the automobile vehicle with the sole surface increases. do. Even in this state, the floor-shaped kneaded body 100 (100G) in the automobile car maintains flexibility while changing its form.
自動車車内フロア状製練体１００（１００Ｇ）は、その抗菌性性能によって足底への接触で、足底に付着したウイルス菌を死滅させる。これによって、足底に付着したウイルスが足から除去されたことになる。 The floor-shaped kneaded body 100 (100G) in an automobile car kills virus bacteria attached to the sole by contact with the sole due to its antibacterial performance. This means that the virus attached to the sole of the foot has been removed from the foot.
外方からの力を作用させると自動車車内フロア状製練体１００（１００Ｇ）表面の足底への接触面積が増大するので、足に付着したウイルスの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the floor-shaped kneaded body 100 (100G) in the automobile car with the sole of the foot increases, so that the virus attached to the foot is effectively removed.
自動車車内フロア状製練体１００（１００Ｇ）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the floor-shaped kneaded body 100 (100G) in an automobile car has flexibility, it can be returned to the original rod shape by applying an external force, and can be used repeatedly.
さらに、シリコン材と抗ウイルス剤を含有する製練体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・製練体がシリコーンゴム及び水酸化カルシウム粉末含有してなり、
・当該製練体における水酸化カルシウム粉末の含有量がシリコーンゴムの重量に対した値を有して、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量であること
を特徴とする製練体が形成される。
Furthermore, it is a kneaded body containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
・ The kneaded product contains silicone rubber and calcium hydroxide powder.
A kneaded product characterized in that the content of calcium hydroxide powder in the kneaded product has a value relative to the weight of the silicone rubber and is 500 g to 600 g with respect to the weight of 1 kg of the silicone rubber. It is formed.
以上のように、シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状製練体であって、
全体が室内フロアマットあるいは自動車車内フロアマットに似た形態をなして、混練材が主成分のシリコーンゴム及び副成分の水酸化カルシウムからなり、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムの混練で生成された製練体になり、人間の足あるいは靴に接触して表面が押圧されると、柔軟性を保持し、当該人間の足あるいは靴への接触面積が押圧作用前に比べて増大することを特徴とする室内フロアマットあるいは自動車車内フロアマット状製練体が形成される。
As described above, it is an indoor floor mat or a car interior floor mat-like kneaded body containing a silicon material and an antiviral agent.
The whole is shaped like an interior floor mat or a car interior floor mat, and is composed of silicone rubber as the main component and calcium hydroxide as a sub-component, and exhibits antiviral properties. It becomes a kneaded body produced by kneading, and when the surface is pressed by contact with human feet or shoes, it retains flexibility and the contact area with the human feet or shoes is larger than before the pressing action. An indoor floor mat or a floor mat-like kneaded body in an automobile is formed, which is characterized by an increase.
シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状の製練体であって、
混練材として主成分のシリコン材及び副成分のドロマイトを準備し、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムを混練し、押圧体、例えば手のひらに接触されて、表面が押圧されると、柔軟性を保持し、当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製練体を形成することを特徴とする抗ウイルス性の押圧体状の製練体の形成方法が形成される。
An indoor floor mat or a car interior floor mat-like kneaded body containing a silicon material and an antiviral agent.
When a silicon material as a main component and a dolomite as a sub component are prepared as a kneading material to exhibit antiviral properties, the silicone rubber and calcium hydroxide are kneaded, and the surface is pressed by contact with a pressing body, for example, the palm. A method for forming an antiviral pressed body-shaped kneaded body, which is characterized by forming a kneaded body that maintains flexibility and increases the contact area of the surface with the palm as compared with that before the pressing action. It is formed.
また、製練体を型に入れ、全体がボール、棒あるいは板に似た形に形成し、全体の形態を変えながらボール体、棒体あるいは板体の形態を保持し及び柔軟性を保持して、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製練体を形成することを特徴とする柔軟性のある抗ウイルス性の手のひらに接触用のボール状、棒状あるいは板状製練体の形成方法が形成される。 In addition, the kneaded body is placed in a mold to form the whole into a shape similar to a ball, a rod or a plate, and the shape of the ball, the rod or the plate is maintained and the flexibility is maintained while changing the overall shape. The flexible antiviral property is characterized in that when the surface is pressed against the palm, the contact area of the surface with the palm is increased as compared with that before the pressing action. A method for forming a ball-shaped, rod-shaped or plate-shaped kneaded body for contact is formed on the palm.
また、シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状の製練体であって、
製練体を型に入れ、全体がドアノブに似た形に形成し、外形の形態を変えながら柔軟性を保持して、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製練体を形成することを特徴とする抗ウイルス性のドアノブ被覆製練体の形成方法が形成される。
Further, it is a kneaded body in the form of an indoor floor mat or a car interior floor mat containing a silicon material and an antiviral agent.
The kneaded body is put into a mold, and the whole is formed into a shape similar to a doorknob, and it retains flexibility while changing the shape of the outer shape. A method for forming an antiviral doorknob-coated kneaded body is formed, which comprises forming a kneaded body in which the contact area is increased as compared with that before the pressing action.
また、シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状の製練体であって、
製練体を型に入れ、全体が携帯電話機に似た形に形成し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひら接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製練体を形成することを特徴とする柔軟性のある抗ウイルス性の携帯電話機被覆製練体の形成方法が形成される。
Further, it is a kneaded body in the form of an indoor floor mat or a car interior floor mat containing a silicon material and an antiviral agent.
The kneaded body is put into a mold and formed into a shape similar to a mobile phone as a whole, and the whole retains a shape similar to a mobile phone and retains flexibility while changing the outer shape, and is touched by the palm of the surface. A method for forming a flexible anti-virus mobile phone-coated kneaded body, which comprises forming a kneaded body in which the contact area of the surface with the palm is increased as compared with that before the pressing action. Is formed.
抗ウイルス性の効果を十分に発揮させるためには、水酸化カルシウムが成形体である製品の表面により多く露出した表面積増大状態にすることが好ましいが、長期間に亘って手のひらへの接触する機能を発現するために製練体を形成し、保持力を確保することが不可欠である。 In order to fully exert the antiviral effect, it is preferable to make the surface area of the product in which calcium hydroxide is exposed more exposed, but the function of contacting the palm for a long period of time is preferable. It is indispensable to form a kneaded body and secure the holding power in order to express.
本実施例によれば、
抗ウイルス性を呈する、柔軟性のある抗ウイルス性のハンド接触用の、例えば手のひらに接触させて効果のある混練材あるいは製練体を提供することができる。
According to this embodiment
It is possible to provide a kneaded material or a kneaded product which is effective for contact with a flexible antiviral hand, for example, in contact with the palm, which exhibits antiviral properties.
これによって、外部における活動中にあっても各種のウイルスによる感染防止を有効に行い得る。例えば、水酸化カルシウムになる抗ウイルス性の柔軟性のある抗ウイルス性のハンド用のボール形状、棒形状あるいは板形状の製練体の形成に適用応用できる。 This makes it possible to effectively prevent infection by various viruses even during external activities. For example, it can be applied and applied to the formation of ball-shaped, rod-shaped or plate-shaped kneaded bodies for antiviral and flexible antiviral hands that become calcium hydroxide.
１…ミキサー、２…横置きされた円筒状の混練筒、３…混練筒２の入口側である上流側に設けられたシリコン材投入口部、４…混練筒２の出口側に設けられた混練材取り出し口部、５…混練筒２の内部に横方向に設置された回転軸、６…回転軸の周囲に設けた攪拌スクリュー、７…攪拌スクリュー６の上流側に設けた送り羽根、８…攪拌スクリュー６の下流側に設けた送り羽根、９…回転軸５に回転力を付与する駆動源としてのモータ、１０…水酸化カルシウム粉末投入口部、１１…水酸化カルシウム投入管、１４…加硫剤投入口、２１…搬送部、２２…混練部、２３…供給部、２４…混練材、２５…製練体、３１…型、３２…窪み、４０…手のひら、４２…筒状部、５２…袋状部、１００（１００A、１００B、１００C、１００D、１００E、１００Ｆ，１００Ｇ）…柔軟性のある抗ウイルス性のハンド接触用のボール体、棒体、板体ドアノブ被覆製練体あるいは携帯電話機被覆製練体。
1 ... Mixer, 2 ... Horizontally placed cylindrical kneading cylinder, 3 ... Silicon material input port provided on the upstream side, which is the inlet side of the
本発明は、シリコン・水酸化カルシウム粉体からなる混練材及びシリコン・水酸化カルシウム粉体からなる製練体、及び当該混練材あるいは製練体の形成方法に関する。 The present invention relates to a kneaded material made of silicon / calcium hydroxide powder, a kneaded material made of silicon / calcium hydroxide powder, and a method for forming the kneaded material or kneaded material.
特許文献１～５に記載されるように、鉱物原料としてのドロマイト由来の抗ウイルス剤がマスク、フイルタ、塗料組成物、繊維あるいは担持シート、建材、複合セラミックスに適用応用されることが知られているが、混練材としてシリコン材及びドロマイトを用い、これらを混練してシリコン・ドロマイト混練材を生成し、シリコン・ドロマイト混練材から製練体を形成し、抗ウイルス成形品とすることが知られていない。
As described in
特許文献６には、レーヨン繊維中に酸化アルミニウム、酸化珪素及び酸化マグネシウムを主成分とする無機質抗菌材が1０～１５重量％混練されていることが記載される。レーヨン繊維中に酸化アルミニウム、酸化珪素及び酸化マグネシウムを主成分とする無機質抗菌材が担持される。この文献は、混練材としてシリコン材及びドロマイトを用い、これらを混練してシリコン・ドロマイト混練材を生成し、シリコン・ドロマイト混練材から混合混練状態の製練体を形成することを記載しない。 Patent Document 6 describes that an inorganic antibacterial material containing aluminum oxide, silicon oxide and magnesium oxide as main components is kneaded in rayon fiber in an amount of 10 to 15% by weight. An inorganic antibacterial material containing aluminum oxide, silicon oxide and magnesium oxide as main components is supported in the rayon fiber. This document does not describe that a silicon material and a dolomite are used as a kneading material, and these are kneaded to form a silicon dolomite kneaded material, and a kneaded body in a mixed kneaded state is formed from the silicon dolomite kneaded material.
特許文献８に記載されるシリコーンゴムは医療用シリコーンゴムであって、抗ウイル性混練材あるいは抗ウイルス性製練体を記載しない。 The silicone rubber described in Patent Document 8 is a medical grade silicone rubber, and does not describe an anti-will kneading material or an anti-virus kneaded product.
この場合、ウイルス不活性化状態を形成するという効果を得るために、ウイルス不活性化部材を人が日常に手で、もしくは他の箇所でしばしば接触する部材に取り付けするなどして配設しておくことが一つの有効手段となる。
配設に際し材料の粉体からウイルス不活性化部材として混練材を形成するために混練操作易さを確保すること、製練体を形成するために製練操作易さを確保するという問題を解決することが求められる。
In this case, in order to obtain the effect of forming the virus inactivating state, the virus inactivating member is arranged by attaching it to a member that is frequently contacted by a person on a daily basis or in other places. Keeping is one effective means.
Solved the problem of ensuring ease of kneading operation to form a kneaded material as a virus-inactivating member from the powder of the material at the time of arrangement, and ensuring ease of kneading operation to form a kneaded body. Is required to do.
本発明は、かかる点に鑑み、家庭あるいは職場内の施設あるいはその他の施設で、人が日常に手で、もしくは他の箇所でしばしば接触する部材に取り付けするなどしてウイルス不活性化部材を配設するに際して、材料の粉体からウイルス不活性化部材として混練材を形成するために混練操作易さを確保すること、製練体を形成するために製練操作易さを確保するという問題を解決することを課題とする。 In view of this point, the present invention disposes of a virus-inactivating member in a facility at home or in the workplace or other facility by attaching it to a member that a person often contacts by hand or in other places on a daily basis. At the time of installation, there are the problems of ensuring the ease of kneading operation to form the kneaded material as a virus inactivating member from the powder of the material and ensuring the ease of kneading operation to form the kneaded body. The challenge is to solve it.
また、シリコン材と抗ウイルス剤を含有する製練体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・混練材がシリコーンゴム及び水酸化カルシウム粉末を含有してなる製練体を提供する。
In addition, it is a kneaded body containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
-Providing a kneaded body in which the kneaded material contains silicone rubber and calcium hydroxide powder.
ここで、水酸化カルシウム粉末にはドロマイト粉末が含まれない。すなわち、水酸化カルシウムにはドロマイトが含まれない。本発明は、ドロマイト粉末を用いず、水酸化カルシウムを成分として用いるが、水酸化カルシウムに第３成分としてドロマイトを含有することを除外しない。混練材あるいは製練体を、水酸化カルシウム粉末を主体として適切な量（重量）をシリコーンゴムに混練することで抗ウイルス性能を向上させた混練材あるいは製練体を形成することができる。 Here, the calcium hydroxide powder does not contain the dolomite powder. That is, calcium hydroxide does not contain dolomite. The present invention does not use dolomite powder and uses calcium hydroxide as a component, but does not exclude calcium hydroxide containing dolomite as a third component. By kneading the kneaded material or kneaded body with silicone rubber in an appropriate amount (weight) mainly of calcium hydroxide powder, a kneaded material or kneaded body having improved antiviral performance can be formed.
本発明において、混練材中にあるいは製練体中に、シリコーンゴム１ｋｇに対して含有させる水酸化カルシウム粉末の量を特定することを試みた。
図１は、本発明の抗ウイルス性混練材及び抗ウイルス性製練体を表示するＸ―Ｙ座標図
である。
In the present invention, it has been attempted to specify the amount of calcium hydroxide powder contained in 1 kg of silicone rubber in the kneaded material or the kneaded body.
FIG. 1 is an XY coordinate diagram showing the antiviral kneading material and the antiviral kneaded product of the present invention.
図１は、シリコーンゴム及び水酸化カルシウム粉末からなるウイルス感染に有効な混練材を形成し、ウイルス不活性化部材の形成し易さ、すなわち製練し易い混練材を確保することができることを示す実験結果を示すＸ―Ｙ座標で示す図である。Ｘ軸は、シリコーンゴム１ｋｇに対して投入されたシリコーンゴム量を重量で示し、Ｙ軸は、混練材あるいは製練体の表面ｐＨ値を示す。表面ｐＨ値は、抗ウイルス性の強さを示す。表面ｐＨ値が高いほど抗ウイルス性の強さは強い。 FIG. 1 shows that a kneading material made of silicone rubber and calcium hydroxide powder, which is effective against virus infection, can be formed, and the kneading material which is easy to form a virus inactivating member, that is , easy to knead can be secured. It is a figure which shows the experimental result by the XY coordinates. The X-axis indicates the amount of silicone rubber charged with respect to 1 kg of silicone rubber by weight, and the Y-axis indicates the surface pH value of the kneaded material or kneaded product . The surface pH value indicates the strength of antiviral property. The higher the surface pH value, the stronger the antiviral strength.
＜実験内容＞
シリコン原料混練時にドロマイト粉体を混合混練したときに、保持力を確保することができた例を示す実験
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末１００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末２００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末３００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末４００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末５００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末６００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末７００ｇを混練して混練材を形成した。
シリコーンゴム１ｋｇに対して水酸化カルシウム粉末８００ｇを混練して混練材を形成しようとしたが、混練ができなかった。
<Experimental content>
An experimental example showing an example in which the holding power could be secured when the dolomite powder was mixed and kneaded at the time of kneading the silicon
200 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
300 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
400 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
500 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
600 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
700 g of calcium hydroxide powder was kneaded with 1 kg of silicone rubber to form a kneaded material.
An attempt was made to knead 800 g of calcium hydroxide powder with 1 kg of silicone rubber to form a kneaded material, but the kneading was not possible.
実験結果によれば、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末７２０ｇ程度までは混合し製練して混練材を形成することができたが、混練材は、６００ｇを超えると脆く、各分離独立した製練体とすることは困難であった。 According to the experimental results, it was possible to mix and knead up to about 720 g of calcium hydroxide powder with 1 kg of silicone rubber to form a kneaded material, but the kneaded material is brittle when it exceeds 600 g, and each is separated and independent. It was difficult to make a kneaded body.
分離独立した製練体とする場合、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末６００ｇまでは製練して製練体を形成することができた。 In the case of making a separate and independent kneaded body, it was possible to knead up to 600 g of calcium hydroxide powder with respect to 1 kg of silicone rubber to form a kneaded body.
ここで、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末を所定の重量を、混練可能環境下、混練して混練材として形成されたものを抗ウイルス性の混練材（以下、混練材という。）といい、混練材から成形品原型に各分離独立させ、混練材の内、成形品成形に最良な範囲である最良な実施可能な範囲にある混練材を抗ウイルス性の製練体（以下、製練体という。）という。混練材あるいは製練体を成形品成形するに際しては、混練可能環境の加熱状態下、加硫処理による硬化処理がなされる。 Here, a material formed as a kneading material by kneading a predetermined weight of calcium hydroxide powder with respect to 1 kg of silicone rubber in a kneadable environment is referred to as an antiviral kneading material (hereinafter referred to as a kneading material). ), Which separates and separates the kneaded material into the molded product prototype, and among the kneaded materials, the kneaded material in the best feasible range, which is the best range for molding the molded product, is an anti-virus kneaded product. (Hereafter, it is called a kneaded body .) When the kneaded material or the kneaded product is molded into a molded product, it is cured by a vulcanization treatment under the heating state of a kneadable environment.
混練可能領域が、混練可能領域が混練可能長さＬ１で、製練可能領域が製練可能長さＬ２で、抗ウイルス性能を考慮したときに、実施可能な混練材形成長さｌ１で、実施可能な製練体形成長さｌ２で示される。混練困難領域が、Ｌ１を延長した領域に、製練困難領域がＬ２を延長した領域に示される。混練材及び製練体のいずれもがビジネス上、製品として取り扱われ得る。 The kneadable area has a kneadable area of L 1 and the kneadable area has a kneadable length of L 2 , and the kneaded material forming length l 1 can be implemented when antiviral performance is taken into consideration. Indicated by the feasible kneaded body formation length l 2 . The difficult kneading region is shown in the region where L 1 is extended, and the difficult kneading region is shown in the region where L 2 is extended. Both the kneaded material and the kneaded body can be treated as a product in business.
Ｙ軸：製練体あるいは混練材の表面ｐＨ値を示す軸。
Ｈ：座標上で、実験結果で得られたプロットを結んで得られた曲線状の線図
Ａ域：線図Ｈ内混練長で、混練材形成域
Ｂ域：線図Ｈ内製練長で、製練体形成域
Ｃ域：線図Ｈ内混練長外方で混練材形成困難域
Ｄ域：ウイルス不活性有効下方ラインＭのｐＨ値１１及びウイルス不活性有効上方ラインＮのｐＨ値１２で区画されるウイルス不活性域（抗ウイルス領域）
Ｅ域：Ａ域及びＤ域で区画されるウイルス不活性混練材域
Ｆ域：Ｂ域及びＤ域で区画されるウイルス不活性製練体域
Ｇ域：Ｃ域及びＤ域で区画されるウイルス不活性域・混練材形成困難域
Ｌ１：混練可能長
Ｌ２：製練可能長
ｌ１：実施可能な混練材形成可能長
ｌ２：実施可能な製練長形成可能長
この実験結果から、・混練材における水酸化カルシウム粉末の含有量がシリコーンゴムの重量で、混練可能な値で、抗ウイルスとして有効なｐＨが11～１２に範囲にある、シリコーンゴム１ｋｇの重量に対し、５００ｇ～７２０ｇ重量である混練材が提供される。
Y-axis: An axis indicating the surface pH value of the kneaded body or kneaded material.
H: Curved diagram obtained by connecting the plots obtained from the experimental results on the coordinates Area A: In the kneading length in the diagram H, area B in the kneaded material forming region: In the kneading length in the diagram H Area C of kneaded body formation: Area D where kneading material is difficult to form outside the kneading length in diagram H: At
Area E: Virus-inert kneaded material area partitioned by A and D areas F area: Virus-inactive kneading body area partitioned by B and D areas G area: Virus partitioned by C and D areas Inactive area / difficult kneading material formation area L 1 : Kneading possible length L 2 : Kneading possible length l 1 : Implementable kneading material forming possible length l 2 : Implementable kneading length forming possible length From this experimental result, -The content of the calcium hydroxide powder in the kneading material is the weight of the silicone rubber, which is a value that can be kneaded, and the pH effective as an antivirus is in the range of 11 to 12, 500 g to 720 g with respect to the weight of 1 kg of the silicone rubber. The weight of the kneaded material is provided.
また、・製練体における水酸化カルシウム粉末の含有量がシリコーンゴムの重量で、製練可能な値で、抗ウイルスとして有効なｐＨが11～１２に範囲にある、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量である製練体が提供される。 In addition, the content of calcium hydroxide powder in the kneaded product is the weight of the silicone rubber, which is a value that can be kneaded , and the pH effective as an antivirus is in the range of 11 to 12, with respect to the weight of 1 kg of silicone rubber. , 500 g-600 g weight is provided.
よって、シリコン材と抗ウイルス剤を含有する製練体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であり、製練体がシリコーンゴム及び水酸化カルシウム粉末を含有してなり、
・当該水酸化カルシウム粉末の当該製練体における含有量がシリコーンゴムの重量に対した値であって、当該対比重量値が、当該シリコーンゴム及び当該水酸化カルシウム粉末を製練可能で、当該製練体のｐＨが予め定めたウイルス不活性有効下方値と予め定めたウイルス不活性有効上方値の範囲のｐＨが11～１２に範囲にある重量値で、５００ｇ～６００ｇ重量であることを特徴とする製練体が提供される。
Therefore, it is a kneaded body containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, the antiviral agent is calcium hydroxide powder, and the kneaded product contains silicone rubber and calcium hydroxide powder.
-The content of the calcium hydroxide powder in the kneaded product is a value relative to the weight of the silicone rubber, and the relative weight value is such that the silicone rubber and the calcium hydroxide powder can be kneaded . The pH of the dough is a weight value in the range of 11 to 12 and a weight of 500 g to 600 g, which is in the range of the predetermined virus-inert effective lower value and the predetermined virus-inert effective upper value. The kneaded body is provided.
成形品を形成には、製練体が用いられる。 A kneaded body is used to form a molded product.
抗ウイルス性混練材あるいは抗ウイルス性製練体の形成に当たっては、抗ウイルス性混練材あるいは抗ウイルス性製練体に、必要に応じて、ドロマイト、炭酸カルシウム、炭酸カルシウム、炭酸マグネシウム、酸化マグネシウムの化学成分を第３成分として含有させることができる。 In forming the anti-viral kneaded material or the anti-viral kneaded material, the anti-viral kneaded material or the anti-viral kneaded material may be prepared with dolomite, calcium carbonate, calcium carbonate, magnesium carbonate or magnesium oxide as required. A chemical component can be contained as a third component.
本発明によれば、シリコーンゴム及び水酸化カルシウムを主体として形成され、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末が５００ｇ～７２０ｇ、特に５００ｇ～６００ｇ混練あるいは製練されて、混練性あるいは製練性に優れた抗ウイルス性を呈する混練材あるいは製練体を提供することができる。 According to the present invention, it is formed mainly of silicone rubber and calcium hydroxide, and 500 g to 720 g of calcium hydroxide powder, particularly 500 g to 600 g, is kneaded or kneaded with respect to 1 kg of silicone rubber to be kneaded or kneaded . It is possible to provide a kneaded material or a kneaded product having excellent antiviral properties.
抗ウイルス性を呈する混練材あるいは製練体は、衛生マスクのインナーシートに用いて、あるいは押圧体に用いて、例えば手のひらに付着した各種のウイルスを除去する目的のために使用を可能とする。例えば柔軟性のある抗ウイルス性のドアノブ被覆体を形成することができる。また、ボール状体、棒状体あるいは板状体を形成し、外部環境における活動中にあっても手持ちができ、手のひらに付着した各種のウイルスを有効に除去してウイルス感染防止を有効に行い得るようにすることができる。 The kneaded material or kneaded material exhibiting antiviral properties can be used as an inner sheet of a sanitary mask or as a pressing body, for example, for the purpose of removing various viruses adhering to the palm. For example, a flexible antiviral doorknob covering can be formed. In addition, it can form a ball-shaped body, a rod-shaped body, or a plate-shaped body, and can be held by hand even during activities in the external environment, and can effectively remove various viruses attached to the palm to effectively prevent virus infection. Can be done.
図１で、混練材が練り状態のシリコーンゴム及び水酸化カルシウム粉末を含有してなる混練材又は製練体形成の基本構成について説明した。 In FIG. 1, the basic configuration of forming a kneaded material or a kneaded body in which the kneaded material contains a kneaded silicone rubber and calcium hydroxide powder has been described.
投入された練り状態のシリコーンゴム、水酸化カルシウム粉体は、加硫剤の添加状態下、混練部２２で、例えば１４０―１７０°の加熱下で混練に要する時間混練され、混練状態の混練材２４が生成される。
The charged silicone rubber and calcium hydroxide powder are kneaded in the kneading section 22 under the addition of the vulcanizing agent for the time required for kneading , for example, under heating at 140-170 °, and kneaded in the kneaded state.
加硫剤は、加熱状態下、混練材を硬化させる作用を呈する。したがって、混練材は、硬化され得る状態にあって、シリコーンゴム及び水酸化カルシウム粉体が混練されて混合状態にある成形材である。シリコーンゴム及び水酸化カルシウム粉体の一部が化学反応しても、成形された混練材あるいは製練体の抗ウイルス性を阻害することはない。 The vulcanizing agent has the effect of curing the kneaded material under heating conditions. Therefore, the kneaded material is a molded material in which silicone rubber and calcium hydroxide powder are kneaded and mixed in a state where it can be cured. Even if a part of the silicone rubber and the calcium hydroxide powder undergoes a chemical reaction, the antiviral property of the molded kneaded material or kneaded material is not impaired .
型３１は、混練材２４からボール状製練体、棒状製練体あるいは板状製練体を形成するための型であり、ボール体状、棒体状あるいは板体状の窪み３２を備える。
The
上述したように、シリコーンゴム１ｋｇに対して水酸化カルシウム粉末を所定の重量を混練したときに、混練して混練材として形成されたものを混練材といい、混練材から成形品原型に各分離独立させ、混練材の内、成形品成形に最良な範囲である最良な実施可能な範囲にある混練材を製練体という。 As described above, when a predetermined weight of calcium hydroxide powder is kneaded with 1 kg of silicone rubber, the kneaded material formed as a kneaded material is called a kneaded material, and the kneaded material is used as a molded product prototype. Of the kneaded materials that are separated and made independent, the kneaded material that is in the best feasible range, which is the best range for molding a molded product, is called a kneaded body .
また、 シリコン材と抗ウイルス剤を含有する製練体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・製練体がシリコーンゴム及び水酸化カルシウム粉末含有してなり、
・当該製練体における水酸化カルシウム粉末の含有量がシリコーンゴムの重量に対して適切な値（重量）を有して、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量であること
を特徴とする製練体が生成される。
In addition, it is a kneaded body containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
・ The kneaded product contains silicone rubber and calcium hydroxide powder.
The content of the calcium hydroxide powder in the kneaded product has an appropriate value (weight) with respect to the weight of the silicone rubber, and is characterized in that the weight is 500 g to 600 g with respect to the weight of 1 kg of the silicone rubber. A kneaded body is produced.
混練材中で、水酸化カルシウム粉末重量が所定の量に特定された混練材が幅広い成形品の原料に適した製練体となる。 Among the kneaded materials, the kneaded material in which the weight of the calcium hydroxide powder is specified to a predetermined amount is suitable as a raw material for a wide range of molded products.
製練体は、シリコーンゴム及び水酸化カルシウムを含有するボール状製練体、棒状製練体あるいは板状製練体であって、全体がボール、棒あるいは板に似た形態をなす柔軟性のある抗ウイルス性のハンド用のボール状抗ウイルス製練体、棒状抗ウイルス製練体あるいは板状抗ウイルス製練体、ドアノブ被覆抗ウイルス製練体あるいは携帯電話機被覆抗ウイルス製練体を形成することができる。 The kneaded body is a ball-shaped kneaded body, a rod-shaped kneaded body or a plate-shaped kneaded body containing silicone rubber and calcium hydroxide, and has a flexibility that resembles a ball, a rod or a plate as a whole. Form a ball-shaped anti-virus kneaded body, rod-shaped anti-virus kneaded body or plate-shaped anti-virus kneaded body, door knob-coated anti-virus kneaded body or mobile phone-coated anti-virus kneaded body for a certain anti-virus hand. be able to.
図３は、混練材から抗ウイルス性製練体が形成されることを示す図である。 FIG. 3 is a diagram showing that an antiviral kneaded product is formed from the kneaded material.
型３１は、製練体２５から成形品、例えばボール状抗ウイルス製練体、棒状抗ウイルス製練体あるいは板状抗ウイルス製練体、ドアノブ被覆抗ウイルス製練体あるいは携帯電話機被覆抗ウイルス製練体を形成するための型であり、X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。混練材が抗ウイルス製練体とされて窪み３２に流し込まれ、所定時間保持され、冷却され、成形品が製作される。
The
混練材２４は、混練材取り出し口部４から型３１に投入される。混練材取り出し口部４に混練材切り分け手段２６が設けられ、連続して生成された混練材取り出し口部４は切断され、製練体２５とされる。すなわち製練体２５は、混練材２４から成型されたものである。
The kneading
一つ一つの独立した製練体２５が型３１に形成された窪み３２に一つ一つに投入される。
Each independent kneading body 25 is put into the
窪み３２に流し込まれた製練体２５は、所定時間保持され、室温まで冷却され、一つ一つの成形品としての製品とされる。
The kneaded body 25 poured into the
図４は、製練体を形成するための各種の型の構造を示す図である。 FIG. 4 is a diagram showing the structures of various molds for forming a kneaded body.
図３示す型３１についての各種の型３１の構造が示される。型は、合わせ面を中央として相似の上方型と下方型との組み合わせになり、図４には下方型が示される。上方型と下方型との組み合わせによって双方の間には用途に応じた空間部が形成され、この空間部を充填するようにして製練体が流し込み路（図示せず）から流し込まれる。各種の型３１を利用して、混練材２４から切り取られた製練体２５から各種の製品が製作される。
The structures of
図４（ａ）は、製練体２５から、柔軟性のある抗ウイルス性の手のひらで接触用のボール体を形成する型３１を示す。
FIG. 4A shows a
X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、半球体形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部に製練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用のボール体が製作される。
It is provided with a plurality of
図４（ｂ）は、製練体２５から、柔軟性のある抗ウイルス性の手のひらで接触用の棒体を形成する型３１を示す。
FIG. 4B shows a
X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、棒が長手方向に半分にされた半円形断面を持つ形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部に製練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手ひらで接触用の棒状製練体が製作される。
It is provided with a plurality of
図４（ｃ）は、製練体２５から、柔軟性のある抗ウイルス性の手のひらで接触用の製練体を形成する他の型３１を示す。
FIG. 4 (c) shows another
型３１は、X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、板状形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部に製練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用の板状製練体が製作される。
The
図４（ｄ）は、製練体２５から、柔軟性のある抗ウイルス性の手のひらで接触用のハンドノブ被覆製練体を形成する型３１を示す。
FIG. 4D shows a
型３１は、上面に１個もしくは整列した複数の窪み３２を備える。ここでは１個の窪みが設けられた例が示される。窪み３２は、ドアノブ状形状をなす。型３１には、ドアノブ状形状の窪みの中央部に配置される中子３３が備えられる。中子３３は外方向きに複数の突起３４を備え、一部が窪み内面に接する。上方型と下方型とが組み合わされ、中子３３を持つ窪みの組み合わせで形成された空間部に製練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用のドアノブ被覆状製練体が製作される。
The
図４（e）は、製練体２５から、柔軟性のある抗ウイルス性の手のひらで接触用の携帯電話機被覆状製練体を形成する型３１を示す。
FIG. 4 (e) shows a
型３１は、上面に１個もしくは整列した複数の窪み３２を備える。ここでは１個の窪みが設けられた例が示される。窪み３２は、携帯電話機状形状をなす。型３１には、携帯電話機状形状の窪みの中央部に配置され、携帯電話機状形状の中子３６が備えられる。中子の一部が窪みの内面に接する。上方型と下方型とが組み合わされ、中子３３を持つ窪みの組み合わせで形成された空間部に製練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手のひらで接触用の携帯電話機被覆状製練体が製作される。
The
図５、抗ウイルス性のボール状製練体を示す図である。 FIG. 5 is a diagram showing an antiviral ball-shaped kneaded body.
図５（ａ）は、抗ウイルス性の手のひらに接触するボール状製練体を示し、図４（ｂ）は、形成されたボール状製練体１００（１００A）が人間の手のひらで握られている状態を示す。 FIG. 5 (a) shows a ball-shaped kneaded body in contact with an antiviral palm, and FIG. 4 (b) shows a formed ball-shaped kneaded body 100 (100A) held by a human palm. Indicates the state of being.
図４（ａ）に示される型３１が用いられて柔軟性のある抗ウイルス性のボール状製練体１００（１００A）が形成される。
The
柔軟性のある抗ウイルス性のボール状製練体１００（１００A）は、全体がボールに似た形態をなして、シリコン材及びドロマイトの混練材からなり、当該混練材が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手のひら４０に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。
The flexible anti-virus ball-shaped kneaded product 100 (100A) has a ball-like shape as a whole and is composed of a kneaded material of silicon material and dolomite, and the kneaded material has a flexible interior and dolomite. It consists of the surface part (surface) of the externally exposed, and the surface part of the externally exposed dolomite exhibits antiviral properties, and when it is held by the
ボール状製練体１００（１００A）は、柔軟性を備えているので手のひらで握られ、押圧されると、手のひらに接触用のボール状製練体１００（１００A）の表面の手のひらへの接触面積が押圧前の接触面積に比べて増大する。抗ウイルス作用面積が増大する。この状態にあっても、ボール状製練体１００（１００A）は、全体の形態を変えながら柔軟性を保持し、手のひらにフイットする。 Since the ball-shaped kneading body 100 (100A) has flexibility, it is gripped by the palm, and when pressed, the contact area of the surface of the ball-shaped kneading body 100 (100A) for contact with the palm is in contact with the palm. Increases compared to the contact area before pressing. Increases antiviral area. Even in this state, the ball-shaped kneaded body 100 (100A) retains its flexibility while changing its overall shape, and fits in the palm of the hand.
ボール状製練体１００（１００A）は、抗菌作用面積が増大した抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 The ball-shaped kneaded body 100 (100A) kills virus bacteria adhering to the palm by contact with the palm due to its antiviral performance with an increased antibacterial area. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、手のひらに接触用のボール状製練体１００（１００A）の表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらから除去することが効果的になされる。 When an external force is applied, the contact area of the surface of the ball-shaped kneading body 100 (100A) for contact with the palm increases, so it is effective to remove the virus adhering to the palm from the palm. It is done.
ボール状製練体１００（１００A）は、柔軟性を備えているので、外力を加えることで、元のボール形状に戻すことができ、繰り返して用いられ得る。 Since the ball-shaped kneaded body 100 (100A) has flexibility, it can be returned to the original ball shape by applying an external force, and can be used repeatedly.
図５（ｃ）に示されるように、球状に替えて楕円形球状、すなわちラグビー状あるいは卵状の形状をなすボール状製練体１００（１００A）が用いられ得る。 As shown in FIG. 5 (c), an elliptical spherical shape, that is, a ball-shaped kneaded body 100 (100A) having a rugby-shaped or egg-shaped shape can be used instead of the spherical shape.
手のひらでボールを握る関係で、ボール状製練体１００（１００A）の大きさは、野球ボールの大きさ以下で、ピンポン玉の大きさ以上であることが推奨される。手のひらにボール状製練体１００（１００A）が接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。 It is recommended that the size of the ball-shaped kneaded body 100 (100A) be smaller than the size of a baseball ball and larger than the size of a ping-pong ball because the ball is held by the palm of the hand. The contact of the ball-shaped kneaded body 100 (100A) with the palm means that the ball-shaped kneaded body 100 (100A) is within the size range that can be grasped by the palm.
図５（ｃ）に示さるボール状製練体１００（１００A）の大きさは、１例として長手方向に、５０ｍｍ、横方向に３０ｍｍ、他の例として７８ｍｍ、横方向に４４ｍｍが採用された。 The size of the ball-shaped kneaded body 100 (100A) shown in FIG. 5 (c) was 50 mm in the longitudinal direction and 30 mm in the lateral direction as an example, 78 mm in the other example, and 44 mm in the lateral direction. ..
ボール状製練体１００（１００A）の中央部に固形材を内蔵させることができる。 A solid material can be incorporated in the central portion of the ball-shaped kneaded body 100 (100A).
図６は、抗ウイルス性の棒状製練体を示す図である。 FIG. 6 is a diagram showing an antiviral rod-shaped kneaded body.
図６（ａ）は、抗ウイルス性のハンド接触用の棒状製練体を示し、図６（ｂ）は、形成された棒状製練体１００（１００B）が人間の手のひらで握られている状態を示す。球状としては、硬式野球バット、あるいはゴルフクラブ形状、ボールペン形状、棒形おもちゃ形状等の身近になじみの形態に模することができる。 FIG. 6 (a) shows a rod-shaped kneaded body for anti-virus hand contact, and FIG. 6 (b) shows a state in which the formed rod-shaped kneaded body 100 (100B) is held by a human palm. Is shown. As the spherical shape, it can be imitated in a familiar shape such as a hardball baseball bat, a golf club shape, a ballpoint pen shape, or a stick-shaped toy shape.
図４（ｂ）に示される型３１が用いられて柔軟性のある抗ウイルス性の棒状製練体１００（１００B）が形成される。
The
柔軟性のある抗ウイルス性の棒状製練体１００（１００B）は、全体が棒に似た形態をなして、シリコーンゴム及び水酸化カルシウムを主体とした製練体からなり、当該製練体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。そして容易に元の形状に戻され得る。 The flexible anti-virus rod-shaped kneaded body 100 (100B) has a shape similar to a rod as a whole, and is composed of a kneaded body mainly composed of silicone rubber and calcium hydroxide. It consists of the inside of flexibility and the surface part (surface) of the outside exposure of calcium hydroxide, and the surface part of the outside exposure of calcium hydroxide exhibits antiviral properties, and is held by a human hand to exert an external force. With the action of, it retains its flexibility while changing its overall form. And it can be easily restored to its original shape.
棒状製練体１００（１００B）は、柔軟性を備えているので手のひらで握られ、押圧されると、棒状製練体１００（１００B）の表面の手のひらへの接触面積が増大する。この状態にあっても、棒状製練体１００（１００B）は、全体の形態を変えながら柔軟性を保持する。 Since the rod-shaped kneaded body 100 (100B) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the rod-shaped kneaded body 100 (100B) with the palm increases. Even in this state, the rod-shaped kneaded body 100 (100B) maintains flexibility while changing the overall shape.
棒状製練体１００（１００B）は、その抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 Due to its antibacterial performance, the rod-shaped kneaded body 100 (100B) kills virus bacteria attached to the palm by contact with the palm. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、棒状製練体１００（１００B）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからのウイルスの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the rod-shaped kneaded body 100 (100B) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
棒状製練体１００（１００B）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the rod-shaped kneaded body 100 (100B) has flexibility, it can be restored to the original rod shape by applying an external force, and can be used repeatedly.
棒状製練体１００（１００B）には、円筒形にした棒状製練体が含まれる。また、棒状製練体１００（１００B）には、中心部に固体状の心棒を挿入した棒状製練体が含まれる。 The rod-shaped kneaded body 100 (100B) includes a cylindrical kneaded body. Further, the rod-shaped kneaded body 100 (100B) includes a rod-shaped kneaded body in which a solid mandrel is inserted in the center.
図７は、抗ウイルス性の板状製練体を示す図である。 FIG. 7 is a diagram showing an anti-virus plate-shaped kneaded body.
図７（ａ）は、抗ウイルス性の板状製練体を示し、図７（ｂ）は、形成された板状製練体１００（１００C）が人間の手のひらで握られている状態を示す。 FIG. 7 (a) shows an anti-virus plate-shaped kneaded body, and FIG. 7 (b) shows a state in which the formed plate-shaped kneaded body 100 (100C) is held by a human palm. ..
図４（ｃ）に示される型３１が用いられて柔軟性のある抗ウイルス性の板状製練体１００（１００C）が形成される。
The
柔軟性のある抗ウイルス性の板状製練体１００（１００C）は、全体が板に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製練体からなり、当該製練体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。 The flexible anti-virus plate-shaped kneaded product 100 (100C) has a shape similar to a plate as a whole and is composed of a kneaded material of silicone rubber and calcium hydroxide, and the kneaded body is flexible. The surface of the calcium hydroxide externally exposed is composed of the inside of the calcium hydroxide and the surface of the externally exposed calcium hydroxide. With, it retains flexibility while changing the overall form.
板状製練体１００（１００C）は、柔軟性を備えているので手のひらで握られ、押圧されると、板状製練体１００（１００C）の表面の手のひらへの接触面積が増大する。この状態にあっても、板状製練体１００（１００C）は、全体の形態を変えながら柔軟性を保持する。 Since the plate-shaped kneaded body 100 (100C) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the plate-shaped kneaded body 100 (100C) with the palm increases. Even in this state, the plate-shaped kneaded body 100 (100C) maintains flexibility while changing the overall shape.
板状製練体１００（１００C）は、その抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルスを死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 The plate-shaped kneaded body 100 (100C) kills the virus attached to the palm by contact with the palm due to its antiviral performance. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、板状製練体１００（１００C）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらからの除去することが効果的になされる。 When an external force is applied, the contact area of the surface of the plate-shaped kneaded body 100 (100C) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
板状製練体１００（１００C）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the plate-shaped kneaded body 100 (100C) has flexibility, it can be returned to the original rod shape by applying an external force, and can be used repeatedly.
以上のように、全体がボール、棒あるいは板に似た形態をなして、混練材が主成分のシリコン材及び副成分の水酸化カルシウムを含有し、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムの混練で生成された製練体になり、全体の形態を変えながらボール体、棒体あるいは板体の形態を保持し及び柔軟性を保持して、手のひら接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の手のひらで接触用のボール状製練体、棒状製練体あるいは板状製練体が形成される。 As described above, the whole has a shape similar to a ball, a rod or a plate, and the kneaded material contains a silicon material as a main component and calcium hydroxide as a sub component, exhibits antiviral properties, and exhibits the above-mentioned silicone rubber and water. It becomes a kneaded body produced by kneading calcium oxide, and keeps the morphology of the ball, rod or plate while changing the overall morphology, and retains the flexibility, is touched by the palm, and the surface is pressed. Then, the contact area of the surface with the palm is increased as compared with that before the pressing action, and the ball-shaped kneaded body, the rod-shaped kneaded body or the plate-shaped body for contact with the flexible antiviral palm is characterized. A kneaded body is formed.
図８は、柔軟性のある抗ウイルス性の手のひらに接触して効果のある成形品であるドアノブ被覆製練体を示す図である。
この例の場合、ドアノブ被覆製練体は、長手方向に細い筒状の形状をなす。筒状部とすることで、内側におけるドアノブ表面のウイルス除去及び外側において手のひら付着のウイルスを除去する抗ウイルス性能が期待できる。
FIG. 8 is a diagram showing a doorknob-coated kneaded body, which is a molded product that is effective in contact with a flexible antiviral palm.
In the case of this example, the doorknob-coated kneaded body has a thin cylindrical shape in the longitudinal direction. By forming the tubular portion, antiviral performance can be expected to remove the virus on the surface of the doorknob on the inside and the virus attached to the palm on the outside.
図８（ａ）は、成形された抗ウイルス性のドアノブ被覆製練体を示す写真であり、図８（ｂ）は、形成されたドアノブ被覆製練体１００（１００D）が装着されるドアノブの例を示す。図８（ｂ）には、先端解放のドアノブが示される。 FIG. 8 (a) is a photograph showing a molded anti-virus doorknob-coated kneaded body, and FIG. 8 (b) shows a doorknob to which the formed doorknob-coated kneaded body 100 (100D) is mounted. An example is shown. FIG. 8B shows a doorknob with an open tip.
図４（ｄ）に示される型３１が用いられて柔軟性のある抗ウイルス性のドアノブ被覆製練体１００（１００D）が形成される。
The
ドアノブ被覆製練体１００（１００D）は、手のひら接触に用いられる表面確保のための体積を有し、ドアノブ４１を収納可能とする筒状部４２を有する。
The doorknob-coated kneaded body 100 (100D) has a volume for securing a surface used for palm contact, and has a
図８（ａ）に示さるドアノブ被覆製練体１００（１００D）の大きさは、１例として長手方向に、１４２ｍｍ、横方向に最太部で，取っ手部径２１ｍｍが採用された。 As an example, the size of the doorknob-coated kneaded body 100 (100D) shown in FIG. 8A is 142 mm in the longitudinal direction, the thickest portion in the lateral direction, and a handle diameter of 21 mm.
柔軟性のある抗ウイルス性のドアノブ被覆製練体１００（１００Ｄ）は、全体がドアノブに似た形態をなして、シリコーンゴム及び水酸化カルシウムの混練材からなり、当該製練体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変え、接触面積を増大させながら柔軟性を保持する。 The flexible and anti-virus door knob coated kneaded product 100 (100D) has a shape similar to that of a door knob as a whole and is made of a kneaded material of silicone rubber and calcium hydroxide. It consists of the inside and the surface part (surface) of the outside exposure of calcium hydroxide, and the surface part of the outside exposure of calcium hydroxide exhibits antiviral properties, and is held by a human hand and the action of external force is applied. If present, it changes the overall shape and retains flexibility while increasing the contact area.
ドアノブ被覆製練体１００（１００D）は、柔軟性を備えているので手のひらで握られ、押圧されると、ドアノブ被覆製練体１００（１００D）の表面の手のひらへの接触面積が増大する。この状態にあっても、ドアノブ被覆製練体１００（１００D）は、全体の形態を変えながら柔軟性を保持する。 Since the doorknob-coated kneaded body 100 (100D) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the doorknob-coated kneaded body 100 (100D) with the palm increases. Even in this state, the doorknob-coated kneaded body 100 (100D) maintains flexibility while changing the overall shape.
ドアノブ被覆製練体１００（１００D）は、その抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルスを死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 The doorknob-coated kneaded body 100 (100D) kills the virus attached to the palm by contact with the palm due to its antiviral performance. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、ドアノブ被覆製練体１００（１００D）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the doorknob-coated kneaded body 100 (100D) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
ドアノブ被覆製練体１００（１００D）は、柔軟性を備えているので、外力を加えることで、元の形状に戻すことができ、繰り返して用いられ得る。 Since the doorknob-coated kneaded body 100 (100D) has flexibility, it can be returned to its original shape by applying an external force, and can be used repeatedly.
図８（ｃ）は、成形された突起型のドアノブに適用されるドアノブ被覆製練体を示す。 FIG. 8 (c) shows a doorknob-coated kneaded body applied to a molded protruding doorknob.
図８（ｃ）に示されるように、この例の場合、ドアノブ被覆製練体は、長手方向と直径方向の長さがほぼ等しい筒状の形状をなす筒体４２で形成される。筒体４２は、図で、長手方向の左右方に孔４３，４４を持つ。筒体４２の内部は、空間部４５となる。
As shown in FIG. 8 (c), in the case of this example, the doorknob-coated kneaded body is formed of a
突起型のドアノブ４１にドアノブ被覆製練体１００（１００Ｄ）の筒体４２が被覆されることで、筒内に突起型のドアノブ４１が配設される。これで、ドアノブ被覆製練体１００（１００D）が突起型のドアノブ４１に被覆して配設される。
By covering the protruding
手のひらでドアノブを握る関係で、ドアノブ被覆製練体１００（１００D）の大きさは、ドアノブの大きさに対して１０～２０％程度大きさであることが推奨される。ドアノブ被覆製練体１００（１００Ｄ）に接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。 It is recommended that the size of the doorknob-coated kneaded body 100 (100D) be about 10 to 20% of the size of the doorknob because the doorknob is gripped by the palm of the hand. Contacting the doorknob-coated kneaded body 100 (100D) means that it is within a size range that can be grasped by the palm of the hand.
図８（ｃ）に示さるドアノブ被覆製練体１００（１００D）の大きさは、１例として長手方向の筒体長さ４３ｍｍ、孔４３の径３４ｍｍ、孔４４の径３８ｍｍが採用された。
As an example, the size of the doorknob-coated kneaded body 100 (100D) shown in FIG. 8C has a tubular body length of 43 mm in the longitudinal direction, a
以上のように、全体がドアノブに似た形態をなして、混練材が主成分のシリコーンゴム及び副成分の水酸化カルシウムからなり、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムの混合混練で生成された製練体になり、当該製練体がドアノブを収納しドアノブに嵌め込まれるドアノブ収納空間部を有し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の手のひらで接触用のドアノブ被覆製練体が形成される。 As described above, the whole has a shape similar to a doorknob, and the kneading material is composed of silicone rubber as a main component and calcium hydroxide as a sub component, exhibits antiviral properties, and is a mixed kneading of the silicone rubber and calcium hydroxide. The kneaded body has a doorknob storage space that stores the doorknob and is fitted into the doorknob. Flexible anti-viral palm contact characterized by the fact that when the surface is pressed against the palm, the contact area of the surface with the palm increases as compared to before the pressing action. A doorknob-coated kneaded body for use is formed.
図９は、抗ウイルス性の携帯電話機被覆製練体を示す図である。
この例の場合、携帯電話機被覆製練体は、携帯電話機を包む包袋状の形状をなす。
FIG. 9 is a diagram showing an anti-virus mobile phone coated kneaded body.
In the case of this example, the mobile phone-coated kneaded body has a bag-like shape that wraps the mobile phone.
図９（ａ）は、抗ウイルス性の携帯電話機被覆製練体を示し、図８（ｂ）は、形成された携帯電話機被覆製練体１００（１００E）が装着される携帯電話機の例を示す。 9 (a) shows an anti-virus mobile phone coated kneaded body, and FIG. 8 (b) shows an example of a mobile phone to which the formed mobile phone coated kneaded body 100 (100E) is attached. ..
図４（e）に示される型３１が用いられて柔軟性のある抗ウイルス性の携帯電話機被覆製練体１００（１００E）が形成される。
The
携帯電話機被覆製練体１００（１００E）は、手のひら接触に用いられる体積を有し、携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部５２を有する。袋状部とすることで、内側における携帯電話機表面のウイルス除菌及び外側において手のひら付着のウイルスを除去する抗ウイルス性能が期待できる。
The mobile phone-coated kneaded body 100 (100E) has a volume used for palm contact, and has a bag-shaped
図４（e）に示される型３１が用いられて柔軟性のある抗ウイルス性の携帯電話機被覆製練体１００（１００E）が形成される。
The
携帯電話機被覆製練体１００（１００E）は、手のひら接触に用いられる体積を有し、携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部５２を有する。袋状部とすることで、内側における携帯電話機表面のウイルス除菌及び外側において手のひら付着のウイルス除菌になる抗菌性能が期待できる。
The mobile phone-coated kneaded body 100 (100E) has a volume used for palm contact, and has a bag-shaped
図９（ｂ）に示さる携帯電話機被覆製練体１００（１００E）の大きさは、１例として長手方向に、１５０ｍｍ、横方向に９０ｍｍが採用された。 As an example, the size of the mobile phone coated kneaded body 100 (100E) shown in FIG. 9B is 150 mm in the longitudinal direction and 90 mm in the lateral direction.
柔軟性のある抗ウイルス性の携帯電話機被覆製練体１００（１００E）は、全体が携帯電話機に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製練体からなり、当該製練体が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変え、接触面積を増大させながら柔軟性を保持する。 The flexible and anti-virus mobile phone coated kneaded body 100 (100E) has a shape similar to that of a mobile phone as a whole, and is composed of a kneaded body of silicone rubber and calcium hydroxide. It consists of the inside of flexibility and the surface part (surface) of the outside exposure of dolomite, and the surface part of the outside exposure of dolomite exhibits antiviral properties, and it is held by a human hand and has the action of external force. It changes the overall shape and maintains flexibility while increasing the contact area.
携帯電話機被覆製練体１００（１００E）は、柔軟性を備えているので手のひらで握られ、押圧されると、携帯電話機被覆製練体１００（１００Ｅ）の表面の手のひらへの接触面積が増大する。この状態にあっても、携帯電話機被覆製練体１００（１００E）は、全体の形態を変えながら柔軟性を保持する。 Since the mobile phone coated kneaded body 100 (100E) has flexibility, when it is gripped and pressed by the palm, the contact area of the surface of the mobile phone coated kneaded body 100 (100E) with the palm increases. .. Even in this state, the mobile phone coated kneaded body 100 (100E) maintains flexibility while changing the overall form.
携帯電話機被覆製練体１００（１００E）は、その抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 Due to its antibacterial performance, the mobile phone-coated kneaded body 100 (100E) kills virus bacteria attached to the palm by contact with the palm. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、携帯電話機被覆製練体１００（１００E）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらから除去することが効果的になされる。 When an external force is applied, the contact area of the surface of the mobile phone coated kneaded body 100 (100E) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
携帯電話機被覆製練体１００（１００E）は、柔軟性を備えているので、外力を加えることで、元の形状に戻すことができ、繰り返して用いられ得る。 Since the mobile phone coated kneaded body 100 (100E) has flexibility, it can be returned to its original shape by applying an external force and can be used repeatedly.
手のひらで携帯電話機を握る関係で、携帯電話機被覆製練体１００（１００E）の大きさは携帯電話機の大きさに対して１０～２０％程度大きさであることが推奨される。携帯電話機被覆製練体１００（１００E）に接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。 Since the mobile phone is held by the palm of the hand, it is recommended that the size of the mobile phone coated kneaded body 100 (100E) is about 10 to 20% of the size of the mobile phone. Contacting the mobile phone-coated kneaded body 100 (100E) means that it is within a size range that can be grasped by the palm of the hand.
以上のように、全体が携帯電話機に似た形態をなして、混練材が主成分のシリコーンゴム及び副成分の水酸化カルシウムからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混練で生成された製練体になり、当該製練体が携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部を有し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の携帯電話機被覆製練体が形成される。 As described above, the whole is in a form similar to that of a mobile phone, and the kneaded material is composed of silicone rubber as a main component and calcium hydroxide as a sub component, exhibits antiviral properties, and is kneaded with the silicon material and the dolomite. It becomes the generated kneaded body, and the kneaded body has a bag-shaped part that allows the mobile phone to be stored together with the mobile phone cover, and keeps the shape similar to the mobile phone as a whole while changing the outer shape. And a flexible anti-virus mobile phone that retains flexibility and is characterized by an increase in the contact area of the surface with the palm when it is in contact with the palm and the surface is pressed compared to before the action. A coated kneaded body is formed.
図１０は、抗ウイルス性の室内フロアマット状製練体及び自動車車内フロアマット状製練体を示す図である。 FIG. 10 is a diagram showing an anti-virus indoor floor mat-shaped kneaded body and an automobile vehicle interior floor mat-shaped kneaded body.
図１０（ａ）は、抗ウイルス性の室内フロア状製練体を示し、図１０（ｂ）は、形成された室内フロア状製練体１００（１００Ｆ）に人間の足が載置されている状態を示し、柔軟性のある抗ウイルス性で、人間の足に接触して効果のある成形品である室内フロア状製練体を示す。 FIG. 10 (a) shows an anti-virus indoor floor-shaped kneaded body, and FIG. 10 (b) shows a human foot placed on the formed indoor floor-shaped kneaded body 100 (100F). It shows the state, is flexible and antiviral, and shows an indoor floor-like kneaded product which is a molded product that is effective in contact with human feet.
図１０（ｃ）は、抗ウイルス性の自動車車内フロア状製練体を示し、図１０（ｄ）は、形成された自動車車内フロア状製練体１００（１００Ｇ）に靴が載置されている状態を示し、柔軟性のある抗ウイルス性で、靴に接触して効果のある成形品である自動車車内フロア状製練体を示す。 FIG. 10 (c) shows an anti-virus in-vehicle floor-shaped kneaded body, and FIG. 10 (d) shows shoes placed on the formed in-vehicle floor-shaped kneaded body 100 (100G). It shows the state, is a flexible anti-virus property, and shows a floor-shaped kneaded body in an automobile, which is a molded product that is effective in contact with shoes.
図４に示される型３１が用いられて柔軟性のある抗ウイルス性の室内フロア状製練体１００（１００Ｆ）あるいは自動車車内フロア状製練体１００（１００Ｇ）が形成される。
The
図１０（ａ）において、柔軟性のある抗ウイルス性の室内フロア状製練体１００（１００Ｆ）は、全体が室内フロア板に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製練体からなり、当該製練体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、図１０（ｂ）に示されるように人間の足５２が載せられて押圧されると、その形態を変え、接触面積を増大させながら柔軟性を保持する。
In FIG. 10A, the flexible antiviral indoor floor-shaped kneaded body 100 (100F) has a shape similar to that of an indoor floor board as a whole, and is a kneaded body of silicone rubber and calcium hydroxide. The kneaded product is composed of a flexible interior and a surface portion (surface) of calcium hydroxide externally exposed, and the surface portion of the calcium hydroxide externally exposed exhibits antiviral properties, and is shown in FIG. 10 (b). ), When the
室内フロア状製練体１００（１００Ｆ）は、柔軟性を備えているので足で押圧されると、室内フロア状製練体１００（１００Ｆ）の表面の足底表面への接触面積が増大する。この状態にあっても室内フロア状製練体１００（１００Ｆ）は、形態を変えながら柔軟性を保持する。 Since the indoor floor-shaped kneaded body 100 (100F) has flexibility, when pressed by a foot, the contact area of the surface of the indoor floor-shaped kneaded body 100 (100F) with the sole surface increases. Even in this state, the indoor floor-shaped kneaded body 100 (100F) maintains flexibility while changing its form.
室内フロア状製練体１００（１００Ｆ）は、その抗菌性性能によって足底への接触で、足底に付着したウイルス菌を死滅させる。これによって、足底に付着したウイルスが足から除去されたことになる。 The indoor floor-shaped kneaded body 100 (100F) kills virus bacteria adhering to the sole by contact with the sole due to its antibacterial performance. This means that the virus attached to the sole of the foot has been removed from the foot.
外方からの力を作用させると室内フロア状製練体１００（１００Ｆ）表面の足底への接触面積が増大するので、足に付着したウイルスの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the indoor floor-shaped kneaded body 100 (100F) with the sole of the foot increases, so that the virus attached to the foot is effectively removed.
室内フロア状製練体１００（１００Ｆ）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the indoor floor-shaped kneaded body 100 (100F) has flexibility, it can be returned to the original rod shape by applying an external force, and can be used repeatedly.
図１０（ｃ）において、柔軟性のある抗ウイルス性の自動車車内フロア状製練体１００（１００Ｇ）は、周辺に飾りスカート５３を備えたプレート上に載置される。自動車車内フロア状製練体１００（１００Ｇ）は、全体が自動車車内フロア板に似た形態をなして、シリコーンゴム及び水酸化カルシウムの製練体からなり、当該製練体が柔軟性の内部と水酸化カルシウム外方露出の表面部（表面）からなって、当該水酸化カルシウム外方露出の表面部が抗ウイルス性を呈し、図１０（ｄ）に示されるように靴５４が載置されて押圧されると、その形態を変え、接触面積を増大させながら柔軟性を保持する。
In FIG. 10 (c), a flexible anti-virus vehicle interior floor-shaped kneaded body 100 (100G) is placed on a plate provided with a
自動車車内フロア状製練体１００（１００Ｇ）は、柔軟性を備えているので足で押圧されると、自動車車内フロア状製練体１００（１００Ｇ）の表面の足底表面への接触面積が増大する。この状態にあっても自動車車内フロア状製練体１００（１００Ｇ）は、形態を変えながら柔軟性を保持する。 Since the floor-shaped kneading body 100 (100G) in an automobile vehicle has flexibility, when pressed by a foot, the contact area of the surface of the floor-shaped kneading body 100 (100G) in the automobile vehicle with the sole surface increases. do. Even in this state, the floor-shaped kneaded body 100 (100G) in the automobile car maintains flexibility while changing its form.
自動車車内フロア状製練体１００（１００Ｇ）は、その抗菌性性能によって足底への接触で、足底に付着したウイルス菌を死滅させる。これによって、足底に付着したウイルスが足から除去されたことになる。 The floor-shaped kneaded body 100 (100G) in an automobile car kills virus bacteria attached to the sole by contact with the sole due to its antibacterial performance. This means that the virus attached to the sole of the foot has been removed from the foot.
外方からの力を作用させると自動車車内フロア状製練体１００（１００Ｇ）表面の足底への接触面積が増大するので、足に付着したウイルスの除去が効果的になされる。 When an external force is applied, the contact area of the surface of the floor-shaped kneaded body 100 (100G) in the automobile car with the sole of the foot increases, so that the virus attached to the foot is effectively removed.
自動車車内フロア状製練体１００（１００Ｇ）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。 Since the floor-shaped kneaded body 100 (100G) in an automobile car has flexibility, it can be returned to the original rod shape by applying an external force, and can be used repeatedly.
さらに、シリコン材と抗ウイルス剤を含有する製練体であって、
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・製練体がシリコーンゴム及び水酸化カルシウム粉末含有してなり、
・当該製練体における水酸化カルシウム粉末の含有量がシリコーンゴムの重量に対した値を有して、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量であること
を特徴とする製練体が形成される。
Furthermore, it is a kneaded body containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
・ The kneaded product contains silicone rubber and calcium hydroxide powder.
A kneaded product characterized in that the content of calcium hydroxide powder in the kneaded product has a value relative to the weight of the silicone rubber and is 500 g to 600 g with respect to the weight of 1 kg of the silicone rubber. It is formed.
以上のように、シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状製練体であって、
全体が室内フロアマットあるいは自動車車内フロアマットに似た形態をなして、混練材が主成分のシリコーンゴム及び副成分の水酸化カルシウムからなり、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムの混練で生成された製練体になり、人間の足あるいは靴に接触して表面が押圧されると、柔軟性を保持し、当該人間の足あるいは靴への接触面積が押圧作用前に比べて増大することを特徴とする室内フロアマットあるいは自動車車内フロアマット状製練体が形成される。
As described above, it is an indoor floor mat or a car interior floor mat-like kneaded body containing a silicon material and an antiviral agent.
The whole has a form similar to an interior floor mat or an automobile interior floor mat, and is composed of silicone rubber as a main component and calcium hydroxide as a sub component, which exhibits antiviral properties, and is composed of the silicone rubber and calcium hydroxide. It becomes a kneaded body produced by kneading, and when the surface is pressed by contact with human feet or shoes, it retains flexibility and the contact area with the human feet or shoes is larger than before the pressing action. An indoor floor mat or a floor mat-like kneaded body in an automobile is formed, which is characterized by an increase.
シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状の製練体であって、
混練材として主成分のシリコン材及び副成分のドロマイトを準備し、抗ウイルス性を呈し、前記シリコーンゴム及び水酸化カルシウムを混練し、押圧体、例えば手のひらに接触されて、表面が押圧されると、柔軟性を保持し、当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製練体を形成することを特徴とする抗ウイルス性の押圧体状の製練体の形成方法が形成される。
An indoor floor mat or a car interior floor mat-like kneaded body containing a silicon material and an antiviral agent.
When a silicon material as a main component and a dolomite as a sub component are prepared as a kneading material to exhibit antiviral properties, the silicone rubber and calcium hydroxide are kneaded, and the surface is pressed by contact with a pressing body, for example, the palm. A method for forming an antiviral pressed body-shaped kneaded body, which is characterized by forming a kneaded body that maintains flexibility and increases the contact area of the surface with the palm as compared with that before the pressing action. It is formed.
また、製練体を型に入れ、全体がボール、棒あるいは板に似た形に形成し、全体の形態を変えながらボール体、棒体あるいは板体の形態を保持し及び柔軟性を保持して、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製練体を形成することを特徴とする柔軟性のある抗ウイルス性の手のひらに接触用のボール状、棒状あるいは板状製練体の形成方法が形成される。 In addition, the kneaded body is placed in a mold to form the whole into a shape similar to a ball, a rod or a plate, and the shape of the ball, the rod or the plate is maintained and the flexibility is maintained while changing the overall shape. The flexible antiviral property is characterized in that when the surface is pressed against the palm, the contact area of the surface with the palm is increased as compared with that before the pressing action. A method for forming a ball-shaped, rod-shaped or plate-shaped kneaded body for contact is formed on the palm.
また、シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状の製練体であって、
製練体を型に入れ、全体がドアノブに似た形に形成し、外形の形態を変えながら柔軟性を保持して、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製練体を形成することを特徴とする抗ウイルス性のドアノブ被覆製練体の形成方法が形成される。
Further, it is a kneaded body in the form of an indoor floor mat or a car interior floor mat containing a silicon material and an antiviral agent.
The kneaded body is put into a mold, and the whole is formed into a shape similar to a doorknob, and it retains flexibility while changing the shape of the outer shape. A method for forming an antiviral doorknob-coated kneaded body is formed, which comprises forming a kneaded body in which the contact area is increased as compared with that before the pressing action.
また、シリコン材と抗ウイルス剤を含有する室内フロアマットあるいは自動車車内フロアマット状の製練体であって、
製練体を型に入れ、全体が携帯電話機に似た形に形成し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひら接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する製練体を形成することを特徴とする柔軟性のある抗ウイルス性の携帯電話機被覆製練体の形成方法が形成される。
Further, it is a kneaded body in the form of an indoor floor mat or a car interior floor mat containing a silicon material and an antiviral agent.
The kneaded body is put into a mold, and the whole is formed into a shape similar to a mobile phone, and the whole retains a shape similar to a mobile phone and retains flexibility while changing the outer shape, and is touched by the palm and the surface. A method for forming a flexible anti-virus mobile phone-coated kneaded body, which comprises forming a kneaded body in which the contact area of the surface with the palm is increased as compared with that before the pressing action. Is formed.
抗ウイルス性の効果を十分に発揮させるためには、水酸化カルシウムが成形体である製品の表面により多く露出した表面積増大状態にすることが好ましいが、長期間に亘って手のひらへの接触する機能を発現するために製練体を形成し、保持力を確保することが不可欠である。 In order to fully exert the antiviral effect, it is preferable to make the surface area of the product in which calcium hydroxide is exposed more exposed, but the function of contacting the palm for a long period of time is preferable. It is indispensable to form a kneaded body and secure the holding power in order to express.
本実施例によれば、
抗ウイルス性を呈する、柔軟性のある抗ウイルス性のハンド接触用の、例えば手のひらに接触させて効果のある混練材あるいは製練体を提供することができる。
According to this embodiment
It is possible to provide a kneaded material or a kneaded product which is effective for contact with a flexible antiviral hand, for example, in contact with the palm, which exhibits antiviral properties.
これによって、外部における活動中にあっても各種のウイルスによる感染防止を有効に行い得る。例えば、水酸化カルシウムになる抗ウイルス性の柔軟性のある抗ウイルス性のハンド用のボール形状、棒形状あるいは板形状の製練体の形成に適用応用できる。 This makes it possible to effectively prevent infection by various viruses even during external activities. For example, it can be applied and applied to the formation of ball-shaped, rod-shaped or plate-shaped kneaded bodies for antiviral and flexible antiviral hands that become calcium hydroxide.
１…ミキサー、２…横置きされた円筒状の混練筒、３…混練筒２の入口側である上流側に設けられたシリコン材投入口部、４…混練筒２の出口側に設けられた混練材取り出し口部、５…混練筒２の内部に横方向に設置された回転軸、６…回転軸の周囲に設けた攪拌スクリュー、７…攪拌スクリュー６の上流側に設けた送り羽根、８…攪拌スクリュー６の下流側に設けた送り羽根、９…回転軸５に回転力を付与する駆動源としてのモータ、１０…水酸化カルシウム粉末投入口部、１１…水酸化カルシウム投入管、１４…加硫剤投入口、２１…搬送部、２２…混練部、２３…供給部、２４…混練材、２５…製練体、３１…型、３２…窪み、４０…手のひら、４２…筒状部、５２…袋状部、１００（１００A、１００B、１００C、１００D、１００E、１００Ｆ，１００Ｇ）…柔軟性のある抗ウイルス性のハンド接触用のボール体、棒体、板体ドアノブ被覆製練体あるいは携帯電話機被覆製練体。
1 ... Mixer, 2 ... Horizontally placed cylindrical kneading cylinder, 3 ... Silicon material input port provided on the upstream side, which is the inlet side of the
Claims (8)
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・混練材がシリコーンゴム及び水酸化カルシウム粉末を含有してなり、
・当該当該混練材における水酸化カルシウム粉末の含有量がシリコーンゴムの重量に対した値を有して、シリコーンゴム１ｋｇの重量に対し、５００ｇ～７２０ｇ重量であること
を特徴とする混練材。 A kneading material containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
・ The kneaded material contains silicone rubber and calcium hydroxide powder.
A kneading material characterized in that the content of calcium hydroxide powder in the kneading material has a value relative to the weight of the silicone rubber and is 500 g to 720 g in weight with respect to the weight of 1 kg of the silicone rubber.
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、
・製錬体がシリコーンゴム及び水酸化カルシウム粉末含有してなり、
・当該製錬体における水酸化カルシウム粉末の含有量がシリコーンゴムの重量に対した値を有して、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量であること
を特徴とする製錬体。 A smelter containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, and the antiviral agent is calcium hydroxide powder.
・ The smelter contains silicone rubber and calcium hydroxide powder.
A smelter characterized in that the content of calcium hydroxide powder in the smelter has a value relative to the weight of the silicone rubber and is 500 g to 600 g with respect to the weight of 1 kg of the silicone rubber.
・全体がボール、棒あるいは板に似た形態をなす製錬体であること
を特徴とするボール状、棒状あるいは板状の抗ウイルス性の製錬体。 The smelter according to claim 2.
-A ball-shaped, rod-shaped or plate-shaped antiviral smelter characterized by being a smelter having a shape similar to a ball, a rod or a plate as a whole.
・全体がドアノブに似た形態をなし、当該ドアノブに嵌め込まれるドアノブ収納空間部を有する製錬体であること
を特徴とするドアノブを被覆する抗ウイルス性の製錬体。 The smelter according to claim 2.
-An anti-virus smelter that covers a doorknob, which has a shape similar to a doorknob as a whole and has a doorknob storage space to be fitted into the doorknob.
・全体が携帯電話機に似た形態をなし、当該携帯電話機を収納可能とした袋状部を有する製錬体であること
を特徴とするドアノブを被覆する抗ウイルス性の製錬体。 The smelter according to claim 2.
-An anti-virus smelter that covers a doorknob, which has a shape similar to that of a mobile phone as a whole and has a bag-shaped portion that can store the mobile phone.
・全体が室内フロアマットあるいは自動車車内フロアマットに似た形態をなす製錬体であること
を特徴とする室内フロアマット状あるいは自動車車内フロアマット状の抗ウイルス性の製錬体。 The smelter according to claim 2.
-An anti-virus smelter in the shape of an interior floor mat or a floor mat in an automobile, which is characterized by being a smelter having a form similar to an interior floor mat or an in-car floor mat as a whole.
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、混練材がシリコーンゴム及び水酸化カルシウム粉末からなり、
・当該水酸化カルシウム粉末の当該混練材における含有量がシリコーンゴムの重量に比較した値で、シリコーンゴム１ｋｇの重量に対し、５００ｇ～７２０ｇ重量で混練可能環境下、混練すること
を特徴とする混練材の形成方法。 A method for forming a kneaded material containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, the antiviral agent is calcium hydroxide powder, and the kneading material is silicone rubber and calcium hydroxide powder.
The content of the calcium hydroxide powder in the kneading material is a value compared to the weight of the silicone rubber, and the kneading is characterized by kneading in an environment where the kneading is possible with a weight of 500 g to 720 g with respect to the weight of 1 kg of the silicone rubber. How to form the material.
・前記シリコン材がシリコーンゴムであり、前記抗ウイルス剤が水酸化カルシウム粉末であって、混練材がシリコーンゴム及び水酸化カルシウム粉末からなり、
・当該水酸化カルシウム粉末の当該混練材における含有量がシリコーンゴムの重量に比較した値で、シリコーンゴム１ｋｇの重量に対し、５００ｇ～６００ｇ重量で混練可能環境下、製錬すること
を特徴とする製錬体の形成方法。 A method for forming a smelter containing a silicon material and an antiviral agent.
-The silicon material is silicone rubber, the antiviral agent is calcium hydroxide powder, and the kneading material is silicone rubber and calcium hydroxide powder.
The content of the calcium hydroxide powder in the kneaded material is a value compared to the weight of the silicone rubber, and is characterized in that the smelting is performed in an environment where kneading is possible with a weight of 500 g to 600 g with respect to the weight of 1 kg of the silicone rubber. How to form a smelter.