JP2021165328A - Antiviral kneaded body, formation method of antiviral kneaded material and formation method of antiviral kneaded body - Google Patents
Antiviral kneaded body, formation method of antiviral kneaded material and formation method of antiviral kneaded body Download PDFInfo
- Publication number
- JP2021165328A JP2021165328A JP2020068215A JP2020068215A JP2021165328A JP 2021165328 A JP2021165328 A JP 2021165328A JP 2020068215 A JP2020068215 A JP 2020068215A JP 2020068215 A JP2020068215 A JP 2020068215A JP 2021165328 A JP2021165328 A JP 2021165328A
- Authority
- JP
- Japan
- Prior art keywords
- dolomite
- silicon
- kneaded
- palm
- antiviral
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、柔軟性のある抗ウイルス性のシリコン・ドロマイト混練材または混練体、シリコン・ドロマイト混練体になるボール状、棒状あるいは板状シリコン・ドロマイト混練体、ドアノブ被覆シリコン・ドロマイト混練体、携帯電話機被覆シリコン・ドロマイト混練体及びシリコン・ドロマイト混練材または混練体の形成方法に関する。 The present invention relates to a flexible antiviral silicon dolomite kneading material or kneaded body, a ball-shaped, rod-shaped or plate-shaped silicon dolomite kneaded body that becomes a silicon dolomite kneaded body, a door knob-coated silicon dolomite kneaded body, and a portable body. The present invention relates to a telephone-coated silicon dolomite kneaded body and a method for forming a silicon dolomite kneaded material or a kneaded body.
現在、非常に多くの分野に抗菌性グッズが汎用されている。抗ウイルス作用を持つ抗微生物物質の有用性、必要性が広く認識されている。
このような状況下、ドロマイドが抗ウイルス作用を持つ新素材として注目される。
ドロマイドの性状として次のようなことが知られる。
Currently, antibacterial goods are widely used in a great many fields. The usefulness and necessity of antimicrobial substances with antiviral activity are widely recognized.
Under these circumstances, dolomide is attracting attention as a new material with antiviral activity.
The following are known properties of dolomide.
１）→ドロマイドは、自然界に無限に存在するカルシウム・マグネシウムの炭酸塩からなる鉱物。菱面体結晶。無色ないし白色半透明。極めて高い安全性を備える。
２）→粉状をなし、抗菌力は極めて強い。強力な殺ウイルス効果を持ち、短時間作用させただけで、ウイルスの感染力を効率的に消失させる。新興-再興感染病対策に有効と考えられる。
３）→純品は高いｐHを持ち、殺菌のメカニズムを生ずると考えられている。ドロマイトの濃度と菌数変化との間には濃度依存性が見られることが一般文献に報告される。
1) → Dolomide is a mineral consisting of carbonates of calcium and magnesium that exist infinitely in nature. Rhombohedral crystal. Colorless to white translucent. It has extremely high safety.
2) → It is powdery and has extremely strong antibacterial activity. It has a strong virus-killing effect and effectively eliminates the infectivity of the virus even if it is allowed to act for a short time. Emerging-Re-emerging Infectious disease control is considered effective.
3) → Pure products have a high pH and are thought to produce a sterilization mechanism. It is reported in the general literature that there is a concentration dependence between the concentration of dolomite and the change in the number of bacteria.
このような性状を持つドロマイトは、プラスチックへの添加剤として使用されることが
知られ、従来、マスク、フイルターへの応用が提案された。
Dolomite having such properties is known to be used as an additive to plastics, and applications to masks and filters have been proposed in the past.
特許文献１には、ドロマイトを焼成し、その一部を水和して粉末として抗ウイルス剤を生成し、得られた粉末を繊維（織布又は不織布）に保持してマスクを製造することが記載される。
特許文献２には、ドロマイトを含有することを特徴とする抗ウイルス性塗料組成物が記
載される。
特許文献３には、ドロマイトを焼成して水和した後、粉砕して微粒子とすること、シート状物に付着させた微粒子状の抗ウイルス剤の抗ウイルス活性が長時間持続して、シート表面に付着したウイルスがシート内部に取り込まれやすい抗ウイルス剤担持シートが提供されることが記載される。
特許文献４には、ドロマイトのか焼物、又はドロマイトのか焼・消化物を含有する抗菌性があり、床材、幅木、腰壁、壁装材などの建材として利用可能な熱可塑性樹脂製建材が記載される。
特許文献５には、ドロマイト族粉末と角閑石粉末が所定の割合で混合された抗菌性のある複合セラミックスが記載される。 Patent Document 5 describes antibacterial composite ceramics in which dolomite group powder and dolomite powder are mixed in a predetermined ratio.
特許文献６には、レーヨン繊維中に酸化アルミニウム、酸化珪素及び酸化マグネシウムを主成分とする無機質抗菌材が1０〜１５重量％混練されている抗菌靴下が記載される。 Patent Document 6 describes antibacterial socks in which 10 to 15% by weight of an inorganic antibacterial material containing aluminum oxide, silicon oxide and magnesium oxide as main components is kneaded in rayon fiber.
特許文献１〜５に記載されるように、鉱物原料としてのドロマイト由来の抗ウイルス剤がマスク、フイルター、塗料組成物、繊維あるいは担持シート、建材、複合セラミックスに適用応用されることが知られているが、混練材としてシリコン材及びドロマイトを用い、これらを混練してシリコン・ドロマイト混練材を生成し、シリコン・ドロマイト混練材からシリコン・ドロマイト混練体を形成し、抗ウイルス成形品とすることが知られていない。
As described in
特許文献６には、レーヨン繊維中に酸化アルミニウム、酸化珪素及び酸化マグネシウムを主成分とする無機質抗菌材が1０〜１５重量％混練されていることが記載される。レーヨン繊維中に酸化アルミニウム、酸化珪素及び酸化マグネシウムを主成分とする無機質抗菌材担持される。この文献は、混練材としてシリコン材及びドロマイトを用い、これらを混練してシリコン・ドロマイト混練材を生成し、シリコン・ドロマイト混練材から混合混練状態のシリコン・ドロマイト混練体を形成することを記載しない。 Patent Document 6 describes that an inorganic antibacterial material containing aluminum oxide, silicon oxide and magnesium oxide as main components is kneaded in rayon fiber in an amount of 10 to 15% by weight. An inorganic antibacterial material containing aluminum oxide, silicon oxide and magnesium oxide as main components is supported in rayon fibers. This document does not describe that a silicon material and a dolomite are used as a kneading material, and these are kneaded to produce a silicon dolomite kneaded material, and a silicon dolomite kneaded body in a mixed kneaded state is formed from the silicon dolomite kneaded material. ..
感染防止の有効な一つの手段として、当該分野の専門家から手を水洗することで各種のウイルスを除去励行することが勧められる。人は、水洗することは水のある家庭あるいは職場その他の施設にいることが必然である。家庭あるいは職場その他の施設以外のところにいる場合、例えば外部環境における活動中、例えば歩行中にあっても手のひらに付着したウイルスを除菌したいことがあり、任意のときに手のひらに付着したウイルスを除菌することができれば、ウイルス感染防止に有効で安心である。 As an effective means of infection control, it is recommended that experts in the field wash their hands with water to remove various viruses. It is inevitable that a person is in a home, workplace or other facility with water to wash with water. If you are not at home, at work or in any other facility, you may want to sterilize the virus that has adhered to your palm even while you are active in the external environment, for example, while walking. If the bacteria can be eradicated, it is effective and safe in preventing virus infection.
シリコン・ドロマイト混合混練体は、単体成形品として構成でき、抗ウイルス性を呈することで、簡便に常に持参可能な手のひら接触用の抗ウイルス性体として利用し得る。例えば、抗ウイルス性のボール体、棒体あるいは板体として利用し得る。手のひら接触用の抗ウイルス性体を形成するにあたっては、手のひらに付着した各種のウイルスを除去する目的のために、主成分として簡便に常に持参可能な柔軟性のある材料が用いることが求められる。さらにはドロマイトの含有量の比率を高めた、手のひら接触用の抗ウイルス性体とすることが求められる。 The silicon / dolomite mixed kneaded product can be configured as a single molded product, and by exhibiting antiviral properties, it can be easily and always used as an antiviral body for palm contact. For example, it can be used as an antiviral ball, rod or plate. In forming an antiviral body for palm contact, it is required to use a flexible material that can be easily and always carried as a main component for the purpose of removing various viruses adhering to the palm. Furthermore, it is required to be an antiviral substance for palm contact with an increased ratio of the content of dolomite.
本発明は、かかる点に鑑み、例えば手のひら接触用の抗ウイルス性体を形成するにあたって、主成分として簡便に常に手持ち可能な材料が用いられること、ドロマイト含有量、すなわち抗ウイルス剤の含有量の比率が高められること、ドロマイト含有量、すなわち抗ウイルス剤の含有量の比率を高めたときに当該材料に確実に保持されること、ドロマイトの抗菌性能向上のために接触面積の増大が可能であることを有効に行い得るようにすることを課題とする。例えば手のひらに付着した各種のウイルスを除去する目的のために使用可能とすること、例えば柔軟性のある抗ウイルス性ボール状体、棒状体あるいは板状体を形成し、外部環境における活動中にあっても手持ちができ、手のひらに付着した各種のウイルスを有効に除去してウイルス感染防止を有効に行い得るようにすることを課題とする。 In view of this point, for example, in forming an antiviral substance for palm contact, the present invention uses a material that can be easily and always held as a main component, and the dolomite content, that is, the content of the antiviral agent. It is possible to increase the ratio, ensure that the dolomite content is retained in the material when the ratio of the content of the antiviral agent is increased, and increase the contact area in order to improve the antibacterial performance of the dolomite. The challenge is to be able to do things effectively. For example, to make it usable for the purpose of removing various viruses attached to the palm, for example, to form a flexible antiviral ball-shaped body, rod-shaped body or plate-shaped body, and during activity in the external environment. However, it is an object to be able to hold it in hand and effectively remove various viruses attached to the palm so that virus infection can be effectively prevented.
本発明は、混練材が主成分のシリコン材及び副成分のドロマイトからなり、シリコン材を主成分としドロマイトを副成分として含有するシリコン・ドロマイト混練体になる。
本発明において、混練材を単に添加し混合する操作がなされるでは足りず、柔軟性で固体性のシリコン材に粉体で固体性のドロマイトを混合混練し、ドロマイトのシリコン材への保持力が高められたシリコン・ドロマイト混練材が形成される。
The present invention comprises a silicon material containing a kneading material as a main component and a dolomite as a sub component, and a silicon dolomite kneaded body containing the silicon material as a main component and dolomite as a sub component.
In the present invention, it is not enough to simply add and mix the kneading material, but the flexible and solid silicon material is mixed and kneaded with powdered solid dolomite, and the holding power of the dolomite to the silicon material is increased. An enhanced silicone dolomite kneading material is formed.
生成されたシリコン・ドロマイト混練材は、押圧体に接触して柔軟性があり、表面が押圧されると当該表面の押圧体への接触面積が押圧作用前に比べて増大する。
このシリコン・ドロマイト混練材からシリコン・ドロマイト混練体が生成される。シリコン・ドロマイト混練体は、シリコン・ドロマイト混練材を同一の性能を持ち、用途に対応した体積を持つ独立した成形品形態を呈する。
The produced silicon dolomite kneaded material is flexible in contact with the pressing body, and when the surface is pressed, the contact area of the surface with the pressing body increases as compared with that before the pressing action.
A silicon dolomite kneaded body is produced from this silicon dolomite kneaded material. The silicon dolomite kneaded product exhibits an independent molded product form in which the silicon dolomite kneaded material has the same performance and has a volume corresponding to the application.
抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトが混練され、押圧体に接触して柔軟性を保持し、用途に対応した体積を有する混練体が生成される。混練材が用途に対応して切り分けられて適切なシリコン・ドロマイト混練体が形成される。
シリコン・ドロマイト混練体の形成に当たって、主成分として簡便に常に手持ち可能な柔軟性のある材料としてシリコン材を用いること、ドロマイト含有量、すなわちドロマイトからなる抗ウイルス剤の含有量の比率が高められること、ドロマイト含有量、すなわち抗ウイルス剤の含有量の比率を高めたときにシリコン材に確実に保持されることを考慮する必要がある。
The silicon material and the dolomite are kneaded to exhibit antiviral properties, and the kneaded body having a volume suitable for the intended use is produced by contacting with the pressing body to maintain the flexibility. The kneaded material is cut according to the application to form an appropriate silicon dolomite kneaded body.
In forming the silicon-dromite kneaded body, use a silicon material as a flexible material that can be easily and always held as a main component, and increase the ratio of the dromite content, that is, the content of the antiviral agent composed of dromite. It is necessary to consider that when the ratio of the dolomite content, that is, the content of the antiviral agent is increased, the silicone material is reliably retained.
製造されたリコン・ドロマイト混練体は、押圧体に付着した各種のウイルスを除去する目的のために使用可能とされる。例えば柔軟性のある抗ウイルス性ボール体、棒体あるいは板体を形成し、外部環境における活動中にあっても手のひらに付着した各種のウイルスを有効に除去してウイルス感染防止を有効に行い得るようにすることが可能になる。 The produced recon-dromite kneaded product can be used for the purpose of removing various viruses adhering to the pressed body. For example, a flexible antiviral ball, rod or plate can be formed, and various viruses attached to the palm can be effectively removed even during activities in the external environment to effectively prevent virus infection. It becomes possible to do so.
鉱物原料としてのドロマイト由来の抗ウイルス剤を用い得る。このような抗ウイルス剤は市販される。ドロマイト由来の抗ウイルス剤としては、ドロマイト、焼成ドロマイトあるいは焼成ドロマイト水和物が用いられる。ドロマイトとしては、炭酸カルシウム及び炭酸マグネシウムばかりでなく、炭酸カルシウム、炭酸マグネシウム、酸化マグネシウム、水酸化カルシウム及び水酸化マグネシウムからなる主体的化学成分を含んで形成される。 An antiviral agent derived from dolomite as a mineral raw material can be used. Such antiviral agents are commercially available. As the antiviral agent derived from dolomite, dolomite, calcined dolomite or calcined dolomite hydrate is used. The dolomite is formed by containing not only calcium carbonate and magnesium carbonate but also a main chemical component composed of calcium carbonate, magnesium carbonate, magnesium oxide, calcium hydroxide and magnesium hydroxide.
本発明は、シリコン材を主成分としドロマイトを副成分として含有するシリコン・ドロマイト混練材であって、
混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトが混合混練された状態にあり、押圧体に接触して柔軟性を保持する混練体であることを特徴とする抗菌性のシリコン・ドロマイト混練材あるいはシリコン・ドロマイト混練体、及びシリコン・ドロマイト混練材あるいはシリコン・ドロマイト混練材の形成方法を提供する。シリコン・ドロマイト混練材は、シリコン・ドロマイト混練体と読み替えることができる。
The present invention is a silicon-dromite kneading material containing a silicon material as a main component and a dolomite as a sub-component.
A kneaded material in which the kneaded material is composed of a silicon material as a main component and a dolomite as a sub component, exhibits antiviral properties, and is in a state in which the silicon material and the dolomite are mixed and kneaded, and retains flexibility in contact with a pressing body. Provided is an antibacterial silicon dolomite kneaded material or a silicon dolomite kneaded body, and a method for forming a silicon dolomite kneaded material or a silicon dolomite kneaded material. The silicon dolomite kneaded material can be read as a silicon dolomite kneaded body.
本発明によれば、抗ウイルス性を呈する、柔軟性のある抗ウイルス性で、押圧体、例えば手のひらに接触して効果のあるシリコン・ドロマイト混練材あるいはシリコン・ドロマイト混練体を提供することができる。 According to the present invention, it is possible to provide a silicone dolomite kneading material or a silicon dolomite kneading material which is flexible and has antiviral properties and is effective in contact with a pressing body, for example, the palm of the hand. ..
ドロマイトの抗菌性能向上のために接触面積の増大が可能な柔軟性のある材料が用いられること、押圧体、例えば手のひらに付着した各種のウイルスを除去する目的のために使用を可能とする。例えば柔軟性のある抗ウイルス性ボール状体、棒状体あるいは板状体を形成し、外部環境における活動中にあっても手持ちができ、手のひらに付着した各種のウイルスを有効に除去してウイルス感染防止を有効に行い得るようにすることができる。 A flexible material capable of increasing the contact area is used to improve the antibacterial performance of the dolomite, and it can be used for the purpose of removing various viruses adhering to the pressing body, for example, the palm. For example, it forms a flexible antiviral ball-shaped body, rod-shaped body, or plate-shaped body, can be held by hand even during activities in the external environment, and effectively removes various viruses attached to the palm to cause virus infection. The prevention can be effectively performed.
これによって、外部における活動中にあっても各種のウイルスによる感染防止を有効に行い得る。例えば、鉱物原料としてのドロマイト由来の抗ウイルス剤を含有する柔軟性のある抗ウイルス性のハンド用のボール形状、棒形状あるいは板形状のシリコン・ドロマイト混練体の形成に適用応用できる。 As a result, it is possible to effectively prevent infection by various viruses even during external activities. For example, it can be applied to the formation of a ball-shaped, rod-shaped or plate-shaped silicon dolomite kneaded body for a flexible antiviral hand containing an antiviral agent derived from dolomite as a mineral raw material.
以下、本発明の実施例を図面に基づいて説明する。 Hereinafter, examples of the present invention will be described with reference to the drawings.
図１は、本発明の実施例になる、鉱物原料としてのドロマイト由来の抗ウイルス剤を含有するドロマイト含有シリコン材を生成するミキサーの構成を示す図である。
図１において、ミキサー１は、横置きされた円筒状の混練筒２、この混練筒２の入口側である上流側に設けられたシリコン原料としてのシリコン材（シリコン材質、シリコーン原料）投入口部３、この混練筒２の出口側に設けられたシリコン・ドロマイト混練材取り出し口部４、この混練筒２の内部に横方向に設置された回転軸５、この回転軸の周囲に設けた攪拌スクリュー６、この攪拌スクリュー６の上流側に設けた送り羽根７、この攪拌スクリュー６の下流側に設けた送り羽根８、回転軸５に回転力を付与する駆動源としてのモーター９、鉱物原料としてのドロマイト由来の抗ウイルス剤を投入するための抗ウイルス剤投入口部１０及び抗ウイルス剤投入管１１から形成される。
FIG. 1 is a diagram showing a configuration of a mixer for producing a dolomite-containing silicon material containing an antiviral agent derived from dolomite as a mineral raw material, which is an embodiment of the present invention.
In FIG. 1, the
柔軟性のあるシリコン材（例えば、上述した低硬度のシリコーンゴム）が準備される。このシリコン材がシリコン材投入口部３から混練筒２に投入される。鉱物原料としてのドロマイト由来の抗ウイルス剤が準備され、この抗ウイルス剤が抗ウイルス剤投入口部１０及び抗ウイルス剤投入管１１から混練筒２に投入される。この抗ウイルス剤は、例えば鉱物原料としてのドロマイトを焼成し、焼成後に水和し、粉体化することで生成され、市販される。市販される抗ウイルス剤を購入することで投入準備がなされる。
A flexible silicone material (for example, the low hardness silicone rubber described above) is prepared. This silicon material is charged into the
混練筒２の内部には、シリコン材投入口部３に面し、送り羽根７が設けられ、投入シリコン材を混練する領域Aに搬送部２１が、抗ウイルス剤投入管１１に面した領域Bにシリコン材混練材とドロマイト粉末を混合混練する混練部２２が、そして下流のドロマイト含有シリコン材取り出し口部４に面し、送り羽根８が設けられた領域Cに送給部２３が形成される。
Inside the
投入された柔軟性のあるシリコン材及び粉体状のドロマイトである抗ウイルス剤は、混練部２２で混練され、シリコン及びドロマイトになる混合混練状態のシリコン・ドロマイト混練材が生成され、シリコン・ドロマイト混練材（以下、単に混練材と称する場合がある。）２４となる。
シリコン材の典型的な例としては、シリコーンゴム（共和工業株式会社製）が知られる。
シリコーンゴムとしては、低硬度シリコーンゴム、中硬度シリコーンゴム、高硬度シリコーンゴムが知られる。本発明には、低硬度シリコーンゴムが好んで用いられる。低硬度シリコーンゴムで柔らかい伸びと密着特性の成形品を製造できる。
The charged flexible silicon material and the antiviral agent which is a powdery dolomite are kneaded in the kneading unit 22 to produce a mixed-kneaded silicon dolomite kneaded material which becomes silicon and dolomite, and silicon dolomite. The kneading material (hereinafter, may be simply referred to as a kneading material) 24.
Silicone rubber (manufactured by Kyowa Kogyo Co., Ltd.) is known as a typical example of a silicon material.
As the silicone rubber, low-hardness silicone rubber, medium-hardness silicone rubber, and high-hardness silicone rubber are known. Low hardness silicone rubber is preferably used in the present invention. It is possible to manufacture molded products with soft elongation and adhesion characteristics using low-hardness silicone rubber.
シリコーンゴム（共和工業株式会社製）は、
１°〜２０°：低硬度
５°の場合 ：耳たぶのような柔らかさを持つ。半透明、黒色。着色され得る。
１０°の場合 ：肌と似た硬さを持つ。半透明、黒色。着色され得る。ブレンド可。
２０°の場合 ：半透明、黒色。機能製品に用いられる。
３０°〜７０°：一般硬度
８０°〜９０°：高硬度
と分類される。
Silicone rubber (manufactured by Kyowa Kogyo Co., Ltd.)
1 ° to 20 °: Low hardness 5 °: Softness like an earlobe. Translucent, black. Can be colored.
At 10 °: Has hardness similar to that of skin. Translucent, black. Can be colored. Can be blended.
At 20 °: translucent, black. Used for functional products.
30 ° to 70 °: General hardness 80 ° to 90 °: Classified as high hardness.
低硬度シリコーンゴムの特徴：
・柔軟性に富んでいる。元の形状に戻る。
・表面のタック感が強く、自己密着性が強い。
・伸び率が非常に高い。
等の特徴を持つ。
Features of low hardness silicone rubber:
・ It is very flexible. Return to the original shape.
-Strong surface tackiness and strong self-adhesion.
・ The growth rate is very high.
It has features such as.
混練部２２では、固体と固体との混合混練がなされ、混合混練状態のシリコン・ドロマイト混練材を生成する特徴がある。
生成された混練材２４は、シリコン・ドロマイト混練材取り出し口部（以下、混練材取り出し口部という。）４からミキサー外部に連続して排出される。
混練材取り出し口部４の近辺に型３１が設けられる。
The kneading unit 22 is characterized in that solids are mixed and kneaded to produce a silicon-dromite kneaded material in a mixed and kneaded state.
The generated kneading
A
型３１は、混練材２４からボール状混練体、棒状混練体あるいは板状混練体を形成するための型であり、ボール体状、棒体状あるいは板体状の窪み３２を備える。
混練材２４が型３１のボール体、棒体あるいは板体状の窪み３２に流し込まれ、所定時間保持され、冷却される。
The
The kneading
シリコン材を主成分としてドロマイトを含有するボール状混練体、棒状混練体あるいは板状混練体であって、全体がボール、棒あるいは板に似た形態をなして、シリコン材及びドロマイトの混練材からなる柔軟性のある抗ウイルス性のハンド用のボール状シリコン・ドロマイト混練体、棒状シリコン・ドロマイト混練体あるいは板状シリコン・ドロマイト混練体が形成される。 A ball-shaped kneaded body, a rod-shaped kneaded body, or a plate-shaped kneaded body containing silicon material as a main component and containing dolomite, which is formed in a form similar to a ball, a rod, or a plate as a whole, and is made of a silicon material and a dolomite kneaded material. A flexible antiviral hand ball-shaped silicon dolomite kneaded body, a rod-shaped silicon dolomite kneaded body, or a plate-shaped silicon dolomite kneaded body is formed.
図１において、ミキサー１が、横置きされた例が示されたが、竪型配置とすることができる。
In FIG. 1, an example in which the
図２は、シリコン・ドロマイト混練材からシリコン・ドロマイト混練体が形成されることを示す図である。 FIG. 2 is a diagram showing that a silicon dolomite kneaded body is formed from a silicon dolomite kneaded material.
型３１は、シリコン・ドロマイト混練体２５から成形品、例えばボール状混練シリコン・ドロマイト体、棒状シリコン・ドロマイト混練体あるいは板状シリコン・ドロマイト混練体、ドアノブ被覆シリコン・ドロマイト混練体あるいは携帯電話機被覆シリコン・ドロマイト混練体を形成するための型であり、X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。シリコン・ドロマイト混練体２５が窪み３２に流し込まれ、所定時間保持され、冷却され、成形品が製作される。
The
シリコン・ドロマイト混練材２４は、混練材取り出し口部４から型３１に投入される。混練材取り出し口部４に混練材切り分け手段２６が設けられ、連続して生成された混練材取り出し口部４は切断され、シリコン・ドロマイト混練体２５とされる。すなわちシリコン・ドロマイト混練体２５は、シリコン・ドロマイト混練材２４から成型されたものである。
The silicon
型３１は、矢印で示されるようにX軸及びY軸方向に移動可能とされる。移動は、ミキサー１との関係で相対的である。
一つ一つの独立したシリコン・ドロマイト混練体２５が型３１に形成された窪み３２に一つ一つに投入される。
窪み３２に流し込まれたシリコン・ドロマイト混練体２５は、所定時間保持され、冷却され、一つ一つの成形品としての製品とされる。
The
Each independent silicon dolomite kneaded body 25 is put into the
The silicon dolomite kneaded body 25 poured into the
図３は、シリコン・ドロマイト混練体を形成するための各種の型の構造を示す図である。図２に示す型３１についての各種の型３１の構造が示される。型は、合わせ面を中央として相似の上方型と下方型との組み合わせになり、図３には下方型が示される。上方型と下方型との組み合わせによって双方の間には用途に応じた空間部が形成され、この空間部を充填するようにしてシリコン・ドロマイト混練体が流し込み路（図示せず）から流し込まれる。各種の型３１を利用して、シリコン・ドロマイト混練材２４から切り取られたシリコン・ドロマイト混練体２５から各種の製品が製作される。
FIG. 3 is a diagram showing the structures of various molds for forming a silicon dolomite kneaded body. The structures of
図３（ａ）は、シリコン・ドロマイト混練体２５から、柔軟性のある抗ウイルス性の手ひらで接触用のボール体を形成する型３１を示す。
X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、半球体形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部にシリコン・ドロマイト混練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手ひらで接触用のボール体が製作される。
FIG. 3A shows a
A plurality of
図３（ｂ）は、シリコン・ドロマイト混練体２５から、柔軟性のある抗ウイルス性の手ひらで接触用の棒体を形成する型３１を示す。
X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、棒が長手方向に半分にされた半円形断面を持つ形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部にシリコン・ドロマイト混練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手ひらで接触用の棒状シリコン・ドロマイト混練体が製作される。
FIG. 3B shows a
A plurality of
図３（ｃ）は、シリコン・ドロマイト混練体２５から、柔軟性のある抗ウイルス性の手ひらで接触用の板状シリコン・ドロマイト混練体を形成する他の型３１を示す。
型３１は、X軸Y軸で形成される座標上の面に規則正しく整列した複数の窪み３２を備える。窪み３２は、板状形状をなす。上方型と下方型とが組み合わされ、窪みの組み合わせで形成された空間部にシリコン・ドロマイト混練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手ひらで接触用の板状シリコン・ドロマイト混練体が製作される。
FIG. 3 (c) shows another
The
図３（ｄ）は、シリコン・ドロマイト混練体２５から、柔軟性のある抗ウイルス性の手ひらで接触用のハンドノブ被覆リコン・ドロマイト混練体を形成する型３１を示す。
型３１は、上面に１個もしくは整列した複数の窪み３２を備える。ここでは１個の窪みが設けられた例が示される。窪み３２は、ドアノブ状形状をなす。型３１には、ドアノブ状形状の窪みの中央部に配置される中子３３が備えられる。中子３３は外方向きに複数の突起３４を備え、一部が窪み内面に接する。上方型と下方型とが組み合わされ、中子３３を持つ窪みの組み合わせで形成された空間部にシリコン・ドロマイト混練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手ひらで接触用のドアノブ被覆状シリコン・ドロマイト混練体が製作される。
FIG. 3D shows a
The
図３（e）は、シリコン・ドロマイト混練体２５から、柔軟性のある抗ウイルス性の手ひらで接触用の携帯電話機被覆状シリコン・ドロマイト混練体を形成する型３１を示す。
型３１は、上面に１個もしくは整列した複数の窪み３２を備える。ここでは１個の窪みが設けられた例が示される。窪み３２は、携帯電話機状形状をなす。型３１には、携帯電話機状形状の窪みの中央部に配置されえ携帯電話機状形状の中子３６が備えられる。中子の一部が窪みの内面に接する。上方型と下方型とが組み合わされ、中子３３を持つ窪みの組み合わせで形成された空間部にシリコン・ドロマイト混練体２５が流し込まれ、所定時間保持され、冷却され、成形品である柔軟性のある抗ウイルス性の手ひらで接触用の携帯電話機被覆状シリコン・ドロマイト混練体が製作される。
FIG. 3 (e) shows a
The
図４から図８は、柔軟性のある抗ウイルス性の手ひらに接触して効果のある成形品である製品の例を具体的に示す図である。 4 to 8 are views specifically showing an example of a product which is a molded product which is effective in contact with a flexible antiviral palm.
図４は、柔軟性のある抗ウイルス性の手ひらに接触効果のあるボール状シリコン・ドロマイト混練体を示す図である。この例の場合、ボールは球状をなす。球状としては、硬式野球ボールあるいはゴルフボール形状、ミカン形状、丸形おもちゃ形状等の身近ななじみの形態に模することができる。 FIG. 4 is a diagram showing a ball-shaped silicon dolomite kneaded body having a flexible antiviral palm contact effect. In the case of this example, the ball is spherical. As the spherical shape, it can be imitated in a familiar shape such as a hardball baseball ball or a golf ball shape, a mandarin orange shape, or a round toy shape.
図４（ａ）は、抗ウイルス性の手のひらに接触するボール状混練体を示し、図４（ｂ）は、形成されたボール状混練体１００（１００A）が人間の手のひらで握られている状態を示す。 FIG. 4A shows a ball-shaped kneaded body in contact with an antiviral palm, and FIG. 4B shows a state in which the formed ball-shaped kneaded body 100 (100A) is held by a human palm. Is shown.
図３（ａ）に示される型３１が用いられて柔軟性のある抗ウイルス性のボール状シリコン・ドロマイト混練体１００（１００A）が形成される。
The
柔軟性のある抗ウイルス性のボール状シリコン・ドロマイト混練体１００（１００A）は、全体がボールに似た形態をなして、シリコン材及びドロマイトの混練材からなり、当該混練材が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手のひら４０に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。
The flexible antiviral ball-shaped silicon dolomite kneaded product 100 (100A) has a ball-like shape as a whole and is composed of a kneaded material of silicon material and dolomite, and the kneaded material is inside the flexibility. And the surface part (surface) of the externally exposed dolomite, and the surface part of the externally exposed dolomite exhibits antiviral properties, and when it is held by the
ボール状シリコン・ドロマイト混練体１００（１００A）は、柔軟性を備えているので手のひらで握られ、押圧されると、手ひらに接触用のボール状シリコン・ドロマイト混練体１００（１００A）の表面の手のひらへの接触面積が押圧前の接触面積に比べて増大する。抗菌作用面積が増大する。この状態にあっても、ボール状シリコン・ドロマイト混練体１００（１００A）は、全体の形態を変えながら柔軟性を保持し、手のひらにフイットする。 Since the ball-shaped silicon dolomite kneaded body 100 (100A) has flexibility, it is gripped by the palm, and when pressed, the surface of the ball-shaped silicon dolomite kneaded body 100 (100A) for contact with the palm. The contact area with the palm is increased as compared with the contact area before pressing. The antibacterial area increases. Even in this state, the ball-shaped silicon dolomite kneaded product 100 (100A) retains its flexibility while changing its overall shape and fits in the palm of the hand.
ボール状シリコン・ドロマイト混練体１００（１００A）は、抗菌作用面積が増大した抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。
外方からの力を作用させると、手ひらに接触用のボール状シリコン・ドロマイト混練体１００（１００A）の表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからの除去が効果的になされる。
The ball-shaped silicon dolomite kneaded product 100 (100A) kills virus bacteria attached to the palm by contact with the palm due to the antibacterial performance with an increased antibacterial area. As a result, the virus attached to the palm has been removed from the palm.
When an external force is applied, the contact area of the surface of the ball-shaped silicon dolomite kneaded body 100 (100A) for contact with the palm increases, so that the virus attached to the palm is removed from the palm. Is done effectively.
ボール状シリコン・ドロマイト混練体１００（１００A）は、柔軟性を備えているので、外力を加えることで、元のボール形状に戻すことができ、繰り返して用いられ得る。
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちに除菌操作を行うことができる。
Since the ball-shaped silicon dolomite kneaded body 100 (100A) has flexibility, it can be returned to the original ball shape by applying an external force, and can be used repeatedly.
It can be used in an environment that is not convenient due to the use of wash water. For example, when riding on a train and being caught by a strap, or when getting on or off, the sterilization operation can be performed immediately.
図４（ｃ）に示されるように、球状に替えて楕円形球状、すなわちラグビー状あるいは卵状の形状をなすボール状シリコン・ドロマイト混練体１００（１００A）が用いられ得る。
手のひらでボールを握る関係で、ボール状シリコン・ドロマイト混練体１００（１００A）の大きさは、野球ボールの大きさ以下で、ピンポン玉の大きさ以上であることが推奨される。手ひらにボール状シリコン・ドロマイト混練体１００（１００A）が接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。
As shown in FIG. 4C, an elliptical spherical shape, that is, a ball-shaped silicon dolomite kneaded body 100 (100A) having a rugby-like or oval-like shape can be used instead of the spherical shape.
It is recommended that the size of the ball-shaped silicon dolomite kneaded body 100 (100A) be less than or equal to the size of a baseball ball and greater than or equal to the size of a ping-pong ball because the ball is held by the palm of the hand. The contact of the ball-shaped silicon dolomite kneaded body 100 (100A) with the palm means that the size is within the size that can be grasped by the palm.
図４（ｃ）に示さるボール状シリコン・ドロマイト混練体１００（１００A）の大きさは、１例として長手方向に、５０ｍｍ、横方向に３０ｍｍ、他の例として７８ｍｍ、横方向に４４ｍｍが採用された。
ボール状シリコン・ドロマイト混練体１００（１００A）の中央部に固形材を内蔵させることができる。
The size of the ball-shaped silicon dolomite kneaded body 100 (100A) shown in FIG. 4C is 50 mm in the longitudinal direction and 30 mm in the lateral direction as an example, 78 mm in the other example, and 44 mm in the lateral direction. Was done.
A solid material can be incorporated in the central portion of the ball-shaped silicon dolomite kneaded body 100 (100A).
図５は、柔軟性のある抗ウイルス性の手ひらに接触して効果のある成形品である棒状シリコン・ドロマイト混練体を示す図である。
図５（ａ）は、抗ウイルス性のハンド接触用の棒状シリコン・ドロマイト混練体を示し、図５（ｂ）は、形成された棒状シリコン・ドロマイト混練体１００（１００B）が人間の手のひらで握られている状態を示す。球状としては、硬式野球バット、あるいはゴルフクラブ形状、ボールペン形状、棒形おもちゃ形状等の身近になじみの形態に模することができる。
FIG. 5 is a diagram showing a rod-shaped silicon dolomite kneaded product, which is a molded product that is effective in contact with a flexible antiviral palm.
FIG. 5 (a) shows a rod-shaped silicon dolomite kneaded body for antiviral hand contact, and FIG. 5 (b) shows a rod-shaped silicon dolomite kneaded body 100 (100B) formed by a human palm. Indicates the state of being virus. As the spherical shape, it can be imitated in a familiar shape such as a hardball baseball bat, a golf club shape, a ballpoint pen shape, or a stick-shaped toy shape.
図３（ｂ）に示される型３１が用いられて柔軟性のある抗ウイルス性の棒状シリコン・ドロマイト混練体１００（１００B）が形成される。
柔軟性のある抗ウイルス性の棒状シリコン・ドロマイト混練体１００（１００B）は、全体が棒に似た形態をなして、シリコン材及びドロマイトの混練材からなり、当該混練材が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。そして容易に元の形状に戻され得る。
The
The flexible antiviral rod-shaped silicon dolomite kneaded product 100 (100B) has a shape similar to that of a rod as a whole and is composed of a kneaded material of silicon material and dolomite. It consists of the surface part (surface) of the externally exposed dolomite, and when the surface part of the externally exposed dolomite exhibits antiviral properties and is held by a human hand and has an action of external force, the whole form is formed. Keep flexibility while changing. And it can be easily returned to its original shape.
棒状混練シリコン・ドロマイト体１００（１００B）は、柔軟性を備えているので手のひらで握られ、押圧されると、棒状シリコン・ドロマイト混練体１００（１００B）の表面の手のひらへの接触面積が増大する。この状態にあっても、棒状シリコン・ドロマイト混練体１００（１００B）は、全体の形態を変えながら柔軟性を保持する。 Since the rod-shaped silicon dolomite body 100 (100B) has flexibility, it is gripped by the palm, and when pressed, the contact area of the surface of the rod-shaped silicon dolomite kneaded body 100 (100B) with the palm increases. .. Even in this state, the rod-shaped silicon dolomite kneaded product 100 (100B) retains its flexibility while changing its overall shape.
棒状シリコン・ドロマイト混練体１００（１００B）は、その抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。
外方からの力を作用させると、棒状シリコン・ドロマイト混練体１００（１００B）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからの除去が効果的になされる。
Due to its antibacterial performance, the rod-shaped silicon dolomite kneaded product 100 (100B) kills virus bacteria attached to the palm when it comes into contact with the palm. As a result, the virus attached to the palm has been removed from the palm.
When an external force is applied, the contact area of the surface of the rod-shaped silicon dolomite kneaded body 100 (100B) with the palm is increased, so that the virus attached to the palm is effectively removed from the palm.
棒状シリコン・ドロマイト混練体１００（１００B）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。
洗浄水の便宜のあるところでない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちに除菌操作を行うことができる。
Since the rod-shaped silicon dolomite kneaded product 100 (100B) has flexibility, it can be restored to the original rod shape by applying an external force, and can be used repeatedly.
It can be used even in an environment where there is no convenience of washing water, and for example, when riding on a train and being caught by a strap, or when getting on or off, the sterilization operation can be performed immediately.
棒状シリコン・ドロマイト混練体１００（１００B）には、円筒形にした棒状混練体が含まれる。また、棒状シリコン・ドロマイト混練体１００（１００B）には、中心部に固体状の心棒を挿入した棒状シリコン・ドロマイト混練体が含まれる。 The rod-shaped silicon dolomite kneaded product 100 (100B) includes a cylindrical rod-shaped kneaded product. Further, the rod-shaped silicon dolomite kneaded body 100 (100B) includes a rod-shaped silicon dolomite kneaded body in which a solid mandrel is inserted in the central portion.
図６は、柔軟性のある抗ウイルス性の手ひらに接触して効果のある成形品である板状混練体を示す図である。 FIG. 6 is a diagram showing a plate-shaped kneaded product which is a molded product that is effective in contact with a flexible antiviral palm.
図６（ａ）は、抗ウイルス性の板状シリコン・ドロマイト混練体を示し、図６（ｂ）は、形成された板状シリコン・ドロマイト混練体１００（１００C）が人間の手のひらで握られている状態を示す。
図３（ｃ）に示される型３１が用いられて柔軟性のある抗ウイルス性の板状シリコン・ドロマイト混練体１００（１００C）が形成される。
柔軟性のある抗ウイルス性の板状シリコン・ドロマイト混練体１００（１００C）は、全体が板に似た形態をなして、シリコン材及びドロマイトの混練材からなり、当該混練材が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変えながら柔軟性を保持する。
FIG. 6 (a) shows an antiviral plate-shaped silicon dolomite kneaded product, and FIG. 6 (b) shows a formed plate-shaped silicon dolomite kneaded product 100 (100C) held by a human palm. Indicates the state of being.
The
The flexible antiviral plate-shaped silicon dolomite kneaded product 100 (100C) has a shape similar to a plate as a whole and is composed of a kneaded material of silicon material and dolomite, and the kneaded material is inside the flexibility. And the surface part (surface) of the externally exposed dolomite, and the surface part of the externally exposed dolomite exhibits antiviral properties, and when it is held by a human hand and has the action of external force, the whole Maintains flexibility while changing form.
板状シリコン・ドロマイト混練体１００（１００C）は、柔軟性を備えているので手のひらで握られ、押圧されると、板状シリコン・ドロマイト混練体１００（１００C）の表面の手のひらへの接触面積が増大する。この状態にあっても、板状シリコン・ドロマイト混練体１００（１００C）は、全体の形態を変えながら柔軟性を保持する。 Since the plate-shaped silicon dolomite kneaded body 100 (100C) has flexibility, it is grasped by the palm, and when pressed, the contact area of the surface of the plate-shaped silicon dolomite kneaded body 100 (100C) with the palm is increased. Increase. Even in this state, the plate-shaped silicon dolomite kneaded product 100 (100C) retains its flexibility while changing its overall shape.
板状シリコン・ドロマイト混練体１００（１００C）は、その抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 The plate-shaped silicon dolomite kneaded product 100 (100C) kills virus bacteria attached to the palm by contact with the palm due to its antibacterial performance. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、板状シリコン・ドロマイト混練体１００（１００C）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからの除去が効果的になされる。
板状シリコン・ドロマイト混練体１００（１００C）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。
When an external force is applied, the contact area of the surface of the plate-shaped silicon dolomite kneaded body 100 (100C) with the palm increases, so that the virus attached to the palm is effectively removed from the palm.
Since the plate-shaped silicon dolomite kneaded product 100 (100C) has flexibility, it can be restored to the original rod shape by applying an external force, and can be used repeatedly.
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちに除菌操作を行うことができる。 It can be used in an environment that is not convenient due to the use of wash water. For example, when riding on a train and being caught by a strap, or when getting on or off, the sterilization operation can be performed immediately.
以上のように、全体がボール、棒あるいは板に似た形態をなして、混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混合混練で生成された混練体になり、全体の形態を変えながらボール体、棒体あるいは板体の形態を保持し及び柔軟性を保持して、手のひら接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の手のひらで接触用のボール状混練体、棒状混練体あるいは板状混練体が形成される。 As described above, the whole is formed in a form similar to a ball, a rod or a plate, and the kneaded material is composed of a silicon material as a main component and a dolomite as a sub component, and exhibits antiviral properties, and is a mixture of the silicon material and the dolomite. The kneaded body is produced by kneading, and while changing the overall shape, it retains the shape of the ball, rod or plate, and retains its flexibility. A flexible antiviral palm is formed with a ball-shaped kneaded body, a rod-shaped kneaded body, or a plate-shaped kneaded body for contact, which is characterized in that the contact area with the palm of the hand is increased as compared with that before the pressing action. ..
図７は、柔軟性のある抗ウイルス性の手ひらに接触して効果のある成形品であるドアノブ被覆シリコン・ドロマイト混練体を示す図である。
この例の場合、ドアノブ被覆混練体は、長手方向に細い筒状の形状をなす。筒状部とすることで、内側におけるドアノブ表面のウイルス除菌及び外側において手のひら付着のウイルス除菌になる抗菌性能が期待できる。
FIG. 7 is a diagram showing a doorknob-coated silicone dolomite kneaded product, which is a molded product that is effective in contact with a flexible antiviral palm.
In the case of this example, the doorknob-covered kneaded body has a tubular shape that is thin in the longitudinal direction. By forming the tubular part, antibacterial performance can be expected to sterilize the virus on the surface of the doorknob on the inside and the virus on the palm on the outside.
図７（ａ）は、成形された抗ウイルス性のドアノブ被覆シリコン・ドロマイト混練体を示す写真であり、図７（ｂ）は、形成されたドアノブ被覆シリコン・ドロマイト混練体１００（１００D）が装着されるドアノブの例を示す。図７（ｂ）には、先端解放のドアノブが示される。
図３（ｄ）に示される型３１が用いられて柔軟性のある抗ウイルス性のドアノブ被覆シリコン・ドロマイト混練体１００（１００D）が形成される。
ドアノブ被覆混練体１００（１００D）は、手のひら接触に用いられる表面確保のための体積を有し、ドアノブ４１を収納可能とする筒状部４２を有する。
FIG. 7 (a) is a photograph showing a molded anti-virus doorknob-coated silicon-dromite kneaded body, and FIG. 7 (b) is a photograph showing the formed doorknob-coated silicon-dromite kneaded body 100 (100D). An example of a doorknob to be used is shown. FIG. 7B shows a doorknob with an open tip.
The
The doorknob covering kneaded body 100 (100D) has a volume for securing a surface used for palm contact, and has a
図７（ａ）に示さるドアノブ被覆シリコン・ドロマイト混練体１００（１００D）の大きさは、１例として長手方向に、１４２ｍｍ、横方向に最太部で，取っ手部径２１ｍｍが採用された。
柔軟性のある抗ウイルス性のドアノブ被覆シリコン・ドロマイト混練体１００（１００Ｄ）は、全体がドアノブに似た形態をなして、シリコン材及びドロマイトの混練材からなり、当該混練材が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変え、接触面積を増大させながら柔軟性を保持する。
As an example, the size of the doorknob-coated silicon dolomite kneaded body 100 (100D) shown in FIG. 7A is 142 mm in the longitudinal direction, the thickest portion in the lateral direction, and a handle diameter of 21 mm.
The flexible, antiviral doorknob-coated silicon dolomite kneaded body 100 (100D) has a shape similar to that of a doorknob and is composed of a kneaded material of silicon material and dolomite. And the surface part (surface) of the externally exposed dolomite, and the surface part of the externally exposed dolomite exhibits antiviral properties, and when it is held by a human hand and has the action of external force, the whole It changes shape and retains flexibility while increasing the contact area.
ドアノブ被覆シリコン・ドロマイト混練体１００（１００D）は、柔軟性を備えているので手のひらで握られ、押圧されると、ドアノブ被覆シリコン・ドロマイト混練体１００（１００D）の表面の手のひらへの接触面積が増大する。この状態にあっても、ドアノブ被覆シリコン・ドロマイト混練体１００（１００D）は、全体の形態を変えながら柔軟性を保持する。 Since the doorknob-coated silicone dolomite kneaded body 100 (100D) has flexibility, it is grasped by the palm, and when pressed, the contact area of the surface of the doorknob-coated silicone dolomite kneaded body 100 (100D) with the palm is increased. Increase. Even in this state, the doorknob-coated silicon dolomite kneaded product 100 (100D) retains its flexibility while changing its overall shape.
ドアノブ被覆シリコン・ドロマイト混練体１００（１００D）は、その抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。
外方からの力を作用させると、ドアノブ被覆シリコン・ドロマイト混練体１００（１００D）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからの除去が効果的になされる。
The doorknob-coated silicone dolomite kneaded product 100 (100D) kills virus bacteria attached to the palm by contact with the palm due to its antibacterial performance. As a result, the virus attached to the palm has been removed from the palm.
When an external force is applied, the contact area of the surface of the doorknob-coated silicon dolomite kneaded body 100 (100D) with the palm is increased, so that the virus attached to the palm is effectively removed from the palm.
ドアノブ被覆シリコン・ドロマイト混練体１００（１００D）は、柔軟性を備えているので、外力を加えることで、元の形状に戻すことができ、繰り返して用いられ得る。
洗浄水の便宜のあるところでない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちに除菌操作を行うことができる。
Since the doorknob-coated silicon dolomite kneaded product 100 (100D) has flexibility, it can be restored to its original shape by applying an external force, and can be used repeatedly.
It can be used even in an environment where there is no convenience of washing water, and for example, when riding on a train and being caught by a strap, or when getting on or off, the sterilization operation can be performed immediately.
図７（ｃ）は、成形された突起型のドアノブに適用されるドアノブ被覆混練体を示す。
図７（ｃ）に示されるように、この例の場合、ドアノブ被覆混練体は、長手方向と直径方向の長さがほぼ等しい筒状の形状をなす筒体４２で形成される。筒体４２は、図で、長手方向の左右方に孔４３，４４を持つ。筒体４２の内部は、空間部４５となる。
FIG. 7 (c) shows a doorknob-covered kneaded body applied to a molded protruding doorknob.
As shown in FIG. 7 (c), in the case of this example, the doorknob-covered kneaded body is formed of a
図７（ｄ）は、で表面を回転することで開放する突起型のドアノブ４１を示す。
突起型のドアノブ４１にドアノブ被覆シリコン・ドロマイト混練体１００（１００Ｄ）の筒体４２が被覆されることで、筒内に突起型のドアノブ４１が配設される。これで、ドアノブ被覆混練体１００（１００D）が突起型のドアノブ４１に被覆して配設される。
手のひらでドアノブを握る関係で、ドアノブ被覆シリコン・ドロマイト混練体１００（１００D）の大きさは、ドアノブの大きさに対して１０〜２０％程度大きさであることが推奨される。ドアノブ被覆シリコン・ドロマイト混練体１００（１００Ｄ）に接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。
FIG. 7D shows a protruding
By covering the protruding
Since the doorknob is gripped by the palm of the hand, it is recommended that the size of the doorknob-coated silicon dolomite kneaded body 100 (100D) is about 10 to 20% of the size of the doorknob. Contact with the doorknob-coated silicone dolomite kneaded body 100 (100D) means that it is within a size range that can be grasped by the palm of the hand.
図７（ｃ）に示さるドアノブ被覆シリコン・ドロマイト混練体１００（１００D）の大きさは、１例として長手方向の筒体長さ４３ｍｍ、孔４３の径３４ｍｍ、孔４４の径３８ｍｍが採用された。
As an example, the size of the doorknob-coated silicon dolomite kneaded body 100 (100D) shown in FIG. 7 (c) is a tubular body length of 43 mm in the longitudinal direction, a
以上のように、全体がドアノブに似た形態をなして、混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混合混練で生成された混練体になり、当該混練体がドアノブを収納しドアノブに嵌め込まれるドアノブ収納空間部を有し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の手のひらで接触用のドアノブ被覆混練体が形成される。 As described above, the whole has a shape similar to a doorknob, and the kneaded material is composed of a silicon material as a main component and a dolomite as a sub component, exhibits antiviral properties, and is produced by a mixed kneading of the silicon material and the dolomite. It becomes a kneaded body, and the kneaded body has a doorknob storage space for storing the doorknob and being fitted into the doorknob. A flexible anti-viral palm-covered doorknob kneading characterized in that when the surface is pressed against the palm, the contact area of the surface with the palm increases compared to before the pressing action. The body is formed.
図８は、柔軟性のある抗ウイルス性の手ひらに接触して効果のある成形品である携帯電話機被覆混練体を示す図である。柔軟性のある抗ウイルス性の手ひらで接触用の携帯電話機被覆混練体を示す図である。
この例の場合、携帯電話機被覆混練体は、携帯電話機を包む包袋状の形状をなす。
FIG. 8 is a diagram showing a mobile phone-coated kneaded product, which is a molded product that is effective in contact with a flexible antiviral palm. It is a figure which shows the mobile phone covering kneading body for contact with a flexible antiviral palm.
In the case of this example, the mobile phone covering kneaded body has a bag-like shape that wraps the mobile phone.
図８（ａ）は、抗ウイルス性の携帯電話機被覆混練体を示し、図８（ｂ）は、形成された携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）が装着される携帯電話機の例を示す。
図３（e）に示される型３１が用いられて柔軟性のある抗ウイルス性の携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）が形成される。
携帯電話機被覆混練体１００（１００E）は、手のひら接触に用いられる体積を有し、携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部５２を有する。袋状部とすることで、内側における携帯電話機表面のウイルス除菌及び外側において手のひら付着のウイルス除菌になる抗菌性能が期待できる。
FIG. 8 (a) shows an anti-virus mobile phone-coated kneaded product, and FIG. 8 (b) shows an example of a mobile phone to which the formed mobile phone-coated silicon dolomite kneaded product 100 (100E) is mounted. show.
The
The mobile phone-coated kneaded body 100 (100E) has a volume used for palm contact, and has a bag-shaped
図８（ｂ）に示さる携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）の大きさは、１例として長手方向に、１５０ｍｍ、横方向に９０ｍｍが採用された。
柔軟性のある抗ウイルス性の携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）は、全体が携帯電話機に似た形態をなして、シリコン材及びドロマイトの混練材からなり、当該混練材が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、人間の手に握られて外方からの力の作用があると、全体の形態を変え、接触面積を増大させながら柔軟性を保持する。
As an example, the size of the mobile phone coated silicon dolomite kneaded body 100 (100E) shown in FIG. 8B was 150 mm in the longitudinal direction and 90 mm in the lateral direction.
The flexible anti-virus mobile phone coated silicon dolomite kneaded product 100 (100E) has a form similar to that of a mobile phone as a whole, and is composed of a kneaded material of silicon material and dolomite, and the kneaded material is flexible. It consists of the inside of the phone and the surface of the outside exposure of the dolomite. It changes the overall shape and retains flexibility while increasing the contact area.
携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）は、柔軟性を備えているので手のひらで握られ、押圧されると、携帯電話機被覆シリコン・ドロマイト混練体１００（１００Ｅ）の表面の手のひらへの接触面積が増大する。この状態にあっても、携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）は、全体の形態を変えながら柔軟性を保持する。
携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）は、その抗菌性性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。
Since the mobile phone coated silicon dolomite kneaded body 100 (100E) has flexibility, it is grasped by the palm, and when pressed, the surface of the mobile phone coated silicon dolomite kneaded body 100 (100E) comes into contact with the palm. The area increases. Even in this state, the mobile phone-coated silicon dolomite kneaded product 100 (100E) retains its flexibility while changing its overall form.
The mobile phone coated silicon dolomite kneaded product 100 (100E) kills virus bacteria attached to the palm by contact with the palm due to its antibacterial performance. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからの除去が効果的になされる。
携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）は、柔軟性を備えているので、外力を加えることで、元の形状に戻すことができ、繰り返して用いられ得る。
When an external force is applied, the contact area of the surface of the mobile phone coated silicon dolomite kneaded body 100 (100E) with the palm increases, so that the virus attached to the palm is effectively removed from the palm. ..
Since the mobile phone coated silicon dolomite kneaded product 100 (100E) has flexibility, it can be returned to its original shape by applying an external force and can be used repeatedly.
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちに除菌操作を行うことができる。
手のひらで携帯電話機を握る関係で、携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）の大きさは携帯電話機の大きさに対して１０〜２０％程度大きさであることが推奨される。携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）に接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。
It can be used in an environment that is not convenient due to the use of wash water. For example, when riding on a train and being caught by a strap, or when getting on or off, the sterilization operation can be performed immediately.
Since the mobile phone is held in the palm of the hand, it is recommended that the size of the mobile phone-coated silicon dolomite kneaded product 100 (100E) is about 10 to 20% of the size of the mobile phone. Contact with the mobile phone coated silicone dolomite kneaded body 100 (100E) means that it is within a size range that can be grasped by the palm of the hand.
以上のように、全体が携帯電話機に似た形態をなして、混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混合混練で生成されたシリコン・ドロマイト混練体になり、当該混練体が携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部を有し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の携帯電話機被覆シリコン・ドロマイト混練体が形成される。 As described above, the whole is in a form similar to that of a mobile phone, and the kneaded material is composed of a silicon material as a main component and a dolomite as a sub component, exhibits antiviral properties, and is produced by a mixed kneading of the silicon material and the dolomite. It becomes a silicon dolomite kneaded body, and the kneaded body has a bag-shaped part that allows the mobile phone to be stored together with the mobile phone cover, and keeps the shape similar to the mobile phone as a whole while changing the outer shape. And a flexible anti-virus mobile phone that retains flexibility and that when the surface is pressed against the palm, the contact area of the surface with the palm increases compared to before the action. A coated silicon dolomite kneaded body is formed.
図９は、成形品である室内フロア状シリコン・ドロマイト混練体及び自動車車内フロア状シリコン・ドロマイト混練体を示す図である。 FIG. 9 is a diagram showing an indoor floor-shaped silicon / dolomite kneaded product and an automobile vehicle interior floor-shaped silicon / dolomite kneaded product, which are molded products.
図９（ａ）は、抗ウイルス性の室内フロア状混練体を示し、図９（ｂ）は、形成された室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）に人間の足が載置されている状態を示し、柔軟性のある抗ウイルス性で、人間の足に接触して効果のある成形品である室内フロア状シリコン・ドロマイト混練体を示す。 FIG. 9A shows an antiviral indoor floor-shaped kneaded body, and FIG. 9B shows a human foot placed on the formed indoor floor-shaped silicon dolomite kneaded body 100 (100F). It shows an indoor floor-like silicon dolomite kneaded product, which is a molded product that is flexible, antiviral, and effective in contact with human feet.
図９（ｃ）は、抗ウイルス性の自動車車内フロア状混練体を示し、図９（ｄ）は、形成された自動車車内フロア状シリコン・ドロマイト混練体１００（１００Ｇ）に靴が載置されている状態を示し、柔軟性のある抗ウイルス性で、靴に接触して効果のある成形品である自動車車内フロア状シリコン・ドロマイト混練体を示す。
図３に示される型３１が用いられて柔軟性のある抗ウイルス性の室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）あるいは自動車車内フロア状シリコン・ドロマイト混練体１００（１００Ｇ）が形成される。
FIG. 9 (c) shows an anti-virus in-vehicle floor-shaped kneaded product, and FIG. 9 (d) shows shoes placed on the formed in-vehicle floor-shaped silicon dolomite kneaded product 100 (100 G). It shows a state of being present, and shows a floor-shaped silicon dolomite kneaded body in an automobile, which is a molded product that is flexible, antiviral, and effective in contact with shoes.
The
図９（ａ）において、柔軟性のある抗ウイルス性の室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）は、全体が室内フロア板に似た形態をなして、シリコン材及びドロマイトの混練材からなり、当該混練材が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、図９（ｂ）に示されるように人間の足５２が載せられて押圧されると、その形態を変え、接触面積を増大させながら柔軟性を保持する。
In FIG. 9A, the flexible antiviral indoor floor-shaped silicon dolomite kneaded product 100 (100F) has a shape similar to that of an indoor floor board as a whole, and is made of a kneaded material of silicon material and dolomite. The kneaded material is composed of a flexible interior and a surface portion (surface) of the externally exposed dolomite, and the surface portion of the externally exposed dolomite exhibits antiviral properties, as shown in FIG. 9 (b). When the
室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）は、柔軟性を備えているので足で押圧されると、室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）の表面の足底表面への接触面積が増大する。この状態にあっても室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）は、形態を変えながら柔軟性を保持する。
室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）は、その抗菌性性能によって足底への接触で、足底に付着したウイルス菌を死滅させる。これによって、足底に付着したウイルスが足から除去されたことになる。
Since the indoor floor-shaped silicon dolomite kneaded body 100 (100F) has flexibility, when pressed by a foot, the contact area of the surface of the indoor floor-shaped silicon dolomite kneaded body 100 (100F) with the sole surface. Increases. Even in this state, the indoor floor-shaped silicon dolomite kneaded body 100 (100F) retains its flexibility while changing its form.
The indoor floor-shaped silicon dolomite kneaded body 100 (100F) kills virus bacteria adhering to the sole of the foot by contact with the sole due to its antibacterial performance. As a result, the virus attached to the sole of the foot has been removed from the foot.
外方からの力を作用させると室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）表面の足底への接触面積が増大するので、足に付着したウイルスの除去が効果的になされる。
室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば室内でテレビ観戦しているようなとき、除菌操作を行うことができる。
When an external force is applied, the contact area of the surface of the indoor floor-shaped silicon dolomite kneaded body 100 (100F) with the sole of the foot increases, so that the virus adhering to the foot is effectively removed.
Since the indoor floor-shaped silicon dolomite kneaded body 100 (100F) has flexibility, it can be restored to the original rod shape by applying an external force, and can be used repeatedly.
It can be used in an environment that is not convenient due to the use of wash water, and the sterilization operation can be performed, for example, when watching TV indoors.
図９（ｃ）において、柔軟性のある抗ウイルス性の自動車車内フロア状シリコン・ドロマイト混練体１００（１００Ｇ）は、周辺に飾りスカート５３を備えたプレート上に載置される。自動車車内フロア状シリコン・ドロマイト混練体１００（１００Ｇ）は、全体が自動車車内フロア板に似た形態をなして、シリコン材及びドロマイトの混練材からなり、当該混練材が柔軟性の内部とドロマイト外方露出の表面部（表面）からなって、当該ドロマイト外方露出の表面部が抗ウイルス性を呈し、図９（ｄ）に示されるように靴５４が載置されて押圧されると、その形態を変え、接触面積を増大させながら柔軟性を保持する。
自動車車内フロア状シリコン・ドロマイト混練体１００（１００Ｇ）は、柔軟性を備えているので足で押圧されると、自動車車内フロア状混練体１００（１００Ｇ）の表面の足底表面への接触面積が増大する。この状態にあっても自動車車内フロア状シリコン・ドロマイト混練体１００（１００Ｇ）は、形態を変えながら柔軟性を保持する。
In FIG. 9 (c), the flexible antiviral vehicle interior floor-shaped silicon dolomite kneaded body 100 (100G) is placed on a plate provided with a
Since the floor-shaped silicon dolomite kneaded body 100 (100G) in the car has flexibility, when pressed by a foot, the contact area of the surface of the floor-shaped kneaded body 100 (100G) in the car with the sole surface is increased. Increase. Even in this state, the floor-shaped silicon dolomite kneaded body 100 (100G) in the automobile vehicle retains its flexibility while changing its form.
自動車車内フロア状シリコン・ドロマイト混練体１００（１００Ｇ）は、その抗菌性性能によって足底への接触で、足底に付着したウイルス菌を死滅させる。これによって、足底に付着したウイルスが足から除去されたことになる。
外方からの力を作用させると自動車車内フロア状シリコン・ドロマイト混練体１００（１００Ｇ）表面の足底への接触面積が増大するので、足に付着したウイルスの除去が効果的になされる。
The floor-shaped silicon dolomite kneaded body 100 (100G) in an automobile car kills virus bacteria adhering to the sole of the foot by contact with the sole due to its antibacterial performance. As a result, the virus attached to the sole of the foot has been removed from the foot.
When an external force is applied, the contact area of the surface of the floor-shaped silicon dolomite kneaded body 100 (100G) in the automobile vehicle with the sole of the foot increases, so that the virus adhering to the foot is effectively removed.
自動車車内フロア状シリコン・ドロマイト混練体１００（１００Ｇ）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば自動車車内で運転手の脇に乗っているようなとき、除菌操作を行うことができる。
Since the floor-shaped silicon dolomite kneaded body 100 (100G) in an automobile has flexibility, it can be returned to the original rod shape by applying an external force, and can be used repeatedly.
It can be used in an environment that is not convenient due to the use of wash water, and the sterilization operation can be performed, for example, when riding on the side of a driver in a car.
以上のように、シリコン材を主成分としドロマイトを副成分として含有する室内フロアマットあるいは自動車車内フロアマット状シリコン・ドロマイト混練体であって、
全体が室内フロアマットあるいは自動車車内フロアマットに似た形態をなして、混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混合混練で生成された混練体になり、人間の足あるいは靴に接触して表面が押圧されると、柔軟性を保持し、当該人間の足あるいは靴への接触面積が押圧作用前に比べて増大することを特徴とする柔軟性のある抗ウイルス性の人間の足あるいは靴に接触用の室内フロアマットあるいは自動車車内フロアマット状混練体が形成される。
As described above, it is an indoor floor mat or a car interior floor mat-like silicon-dromite kneaded body containing a silicon material as a main component and a dolomite as a sub-component.
The whole is in a form similar to an interior floor mat or a floor mat in an automobile, and is composed of a silicon material as a main component and a dolomite as a sub component, which exhibits antiviral properties, and is mixed and kneaded with the silicon material and the dolomite. When the kneaded product is produced and the surface is pressed by contact with the human foot or shoe, the flexibility is maintained and the contact area with the human foot or shoe is increased as compared with that before the pressing action. An interior floor mat for contact or a floor mat-like kneaded body in an automobile is formed on a flexible antiviral human foot or shoe.
以上のように、シリコン材を主成分としドロマイトを副成分として含有するシリコン・ドロマイト混練体の形成方法であって、
混練材として主成分のシリコン材及び副成分のドロマイトを準備し、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトを混練し、押圧体、例えば手のひらに接触されて、表面が押圧されると、柔軟性を保持し、当該表面の手のひらへの接触面積が押圧作用前に比べて増大する混練体を形成することを特徴とする柔軟性のある抗ウイルス性の押圧体、例えば手のひらで接触用のシリコン・ドロマイト混練体の形成方法が形成される。
As described above, it is a method for forming a silicon-dromite kneaded body containing a silicon material as a main component and dromite as a sub-component.
When a silicon material as a main component and a dolomite as a sub-component are prepared as a kneading material to exhibit antiviral properties, the silicon material and the dolomite are kneaded, and the surface is pressed by contact with a pressing body, for example, the palm. A flexible antiviral press, eg, for contact with the palm, which retains flexibility and forms a kneaded body in which the contact area of the surface with the palm is increased as compared to before the pressing action. A method for forming a silicon dolomite kneaded body is formed.
また、シリコン・ドロマイト混練体を型に入れ、全体がボール、棒あるいは板に似た形に形成し、全体の形態を変えながらボール体、棒体あるいは板体の形態を保持し及び柔軟性を保持して、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する混練体を形成することを特徴とする柔軟性のある抗ウイルス性の手のひらに接触用のボール状、棒状あるいは板状シリコン・ドロマイト混練体の形成方法が形成される。 In addition, the silicon dolomite kneaded body is put into a mold to form the whole into a shape similar to a ball, a rod or a plate, and the shape of the ball, the rod or the plate is maintained and flexibility is maintained while changing the overall shape. Flexible antiviral properties characterized by forming a kneaded body that holds and is in contact with the palm and the contact area of the surface with the palm is increased as compared to before the pressing action when the surface is pressed. A method for forming a ball-shaped, rod-shaped or plate-shaped silicon dolomite kneaded body for contact is formed on the palm of the hand.
また、シリコン・ドロマイト混練体を型に入れ、全体がドアノブに似た形に形成し、外形の形態を変えながら柔軟性を保持して、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する混練体を形成することを特徴とする柔軟性のある抗ウイルス性のドアノブ被覆混練体の形成方法が形成される。 In addition, the silicon dolomite kneaded body is put into a mold, and the whole is formed into a shape similar to a doorknob, and the flexibility is maintained while changing the shape of the outer shape. A method for forming a flexible antiviral doorknob-coated kneaded body is formed, which comprises forming a kneaded body in which the contact area with the palm of the hand is increased as compared with that before the pressing action.
また、シリコン・ドロマイト混練体を型に入れ、全体が携帯電話機に似た形に形成し、外形の形態を変えながら全体が携帯電話機に似た形態を保持し及び柔軟性を保持し、手のひら接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する混練体を形成することを特徴とする柔軟性のある抗ウイルス性の携帯電話機被覆シリコン・ドロマイト混練体の形成方法が形成される。 In addition, the silicon dolomite kneaded body is put into a mold to form the whole into a shape similar to a mobile phone, and while changing the outer shape, the whole retains a shape similar to a mobile phone and retains flexibility, and palm contact. A flexible, antiviral mobile phone-coated silicon dolomite, characterized in that when the surface is pressed, the contact area of the surface with the palm increases as compared to before the pressing action. A method of forming the kneaded body is formed.
抗ウイルス性の効果を十分に発揮させるためには、ドロマイト成分が成形体である製品の表面により多く露出した表面積増大状態にすることが好ましいが、長期間に亘って手のひらへの接触する機能を発現するためにシリコン・ドロマイト混練体を形成し、保持力を確保することが不可欠である。 In order to fully exert the antiviral effect, it is preferable to increase the surface area of the product in which the dolomite component is exposed more than the surface of the molded product, but the function of contacting the palm for a long period of time is provided. In order to develop it, it is indispensable to form a silicon dolomite kneaded product and secure the holding power.
図１０は、シリコン・ドロマイト混練体を形成し、保持力を確保することができることを示す実験結果を示す図である。当該実験は、本件特許出願人によって当該特許出願人の施設、設備を使用してなされ、シリコン原料及びドロマイト粉末は市販の低硬度のものが用いられた。実験室に用いられた温度は、室温であった。計量器は、一般的なものが使用された。 FIG. 10 is a diagram showing experimental results showing that a silicon dolomite kneaded body can be formed and a holding force can be secured. The experiment was carried out by the Patent Applicant using the facilities and equipment of the Patent Applicant, and commercially available low hardness silicon raw materials and dolomite powder were used. The temperature used in the laboratory was room temperature. A general measuring instrument was used.
＜実験内容＞
シリコン原料混練時にドロマイト粉体を混合混練したときに、保持力を確保することができた例を示す実験
１）シリコン原料１０００ｇにドロマイト粉末２００ｇを混合混練（ドロマイト含有量１７％）
混練体を形成し、十分に保持力を確保することができた。
２）シリコン原料１０００ｇにドロマイト粉末４００ｇを混合混練（ドロマイト含有量２８．６％）。
混練体を形成し、十分に保持力を確保することができた。
３）シリコン原料１０００ｇにドロマイト粉末６００ｇを混合混練（ドロマイト含有量３７．５％）。
シリコン・ドロマイト混練体を形成し、十分に保持力を確保することができた。
<Experimental content>
Experiment showing an example in which the holding power could be secured when the dolomite powder was mixed and kneaded during the kneading of the silicon raw material 1) 200 g of the dolomite powder was mixed and kneaded with 1000 g of the silicon raw material (dolomite content 17%).
A kneaded body was formed, and sufficient holding power could be secured.
2) 400 g of dolomite powder is mixed and kneaded with 1000 g of silicon raw material (dromite content 28.6%).
A kneaded body was formed, and sufficient holding power could be secured.
3) 600 g of dolomite powder is mixed and kneaded with 1000 g of a silicon raw material (dromite content 37.5%).
A silicon dolomite kneaded body was formed, and sufficient holding power could be secured.
これらの実験結果から、シリコン原料単位重量に対してドロマイト量０．２−０．６の範囲で混在混合させれば、混練体を形成し、十分に保持力を確保した製品とすることができる。
ドロマイト量０．６を超えて混練するとき、混練することができたが、混練作業にかなりの作業を要し、成型時に保持力が弱くなり、切断しやすい現象がみられた。ドロマイト量０．６を超えて混合混練し、全体の形態を変えながらボール形状、棒形状あるいは板形状のシリコン・ドロマイト混練体の形成することは、柔軟性を持ったそれらの形態及びドロマイトの保持性で劣ることになった。ドロマイト量０．２０未満では抗ウイルス性の発現が困難である。
From these experimental results, it is possible to form a kneaded product and obtain a product having a sufficient holding power by mixing and mixing the dolomite amount in the range of 0.2 to 0.6 with respect to the unit weight of the silicon raw material. ..
When the kneading was performed when the amount of dolomite exceeded 0.6, the kneading was possible, but the kneading work required a considerable amount of work, the holding force was weakened at the time of molding, and a phenomenon of easy cutting was observed. Forming ball-shaped, rod-shaped or plate-shaped silicon dolomite kneaded bodies by mixing and kneading with a dolomite amount exceeding 0.6 and changing the overall form is to retain those forms and dolomites with flexibility. It became inferior in sex. If the amount of dolomite is less than 0.20, it is difficult to develop antiviral properties.
シリコン・ドロマイト混練材中における抗ウイルス性成分、すなわちドロマイトの含有量は、低硬度のシリコン原料を採用して、ドロマイト量０．３以上で０．５未満％であることが好ましい。
シリコン・ドロマイト混練材２４の形成に当たっては、必要に応じて炭酸カルシウム及び炭酸マグネシウムばかりでなく、炭酸カルシウム、炭酸マグネシウム、酸化マグネシウム、水酸化カルシウム及び水酸化マグネシウムからなる主体的化学成分を第３成分として含有させることができる。
The content of the antiviral component, that is, dolomite in the silicon dolomite kneading material is preferably 0.3 or more and less than 0.5% when a low hardness silicon raw material is used.
In forming the silicon /
これらのことから、シリコン材を主成分としドロマイトを副成分として含有するシリコン・ドロマイト混練材であって、
混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材重量で１に対して前記ドロマイトが０．２−０．６、望ましくは０．３−０．５の範囲で混合混練された状態にあり、柔軟性を保持し、手のひらに接触されて、表面が押圧されると当該表面の手のひらへの接触面積が押圧作用前に比べて増大する混練材であることを特徴とする抗菌性のシリコン・ドロマイト混練材が提供される。
From these facts, it is a silicon-dromite kneading material containing a silicon material as a main component and a dolomite as a sub-component.
The kneaded material is composed of a silicon material as a main component and a dolomite as a sub component, and exhibits antiviral properties. The dolomite is 0.2-0.6, preferably 0.3-0. A kneaded material that is in a state of being mixed and kneaded in the range of 5, retains flexibility, is in contact with the palm, and when the surface is pressed, the contact area of the surface with the palm increases compared to before the pressing action. Provided is an antibacterial silicone dolomite kneading material, which is characterized by being present.
本実施例によれば、
抗ウイルス性を呈する、柔軟性のある抗ウイルス性のハンド接触用の、例えば手のひらに接触させて効果のあるシリコン・ドロマイト混練材あるいはシリコン・ドロマイト混練体を提供することができる。
According to this embodiment
It is possible to provide a silicone dolomite kneading material or a silicone dolomite kneading material which is effective in contact with the palm, for example, for a flexible antiviral hand contact exhibiting antiviral properties.
ドロマイトの抗菌性能向上のために接触面積の増大が可能な柔軟性のある材料が用いられること、例えば手のひらに付着した各種のウイルスを除去する目的のために使用可能とすること、例えば柔軟性のある抗ウイルス性ボール状体、棒状体あるいは板状体を形成し、外部環境における活動中にあっても手持ちができ、手のひらに付着した各種のウイルスを有効に除去してウイルス感染防止を有効に行い得るようにすることができる。 A flexible material that can increase the contact area is used to improve the antibacterial performance of dolomite, for example, it can be used for the purpose of removing various viruses attached to the palm, for example, of flexibility. It forms a certain anti-virus ball-like body, rod-like body or plate-like body, can be held by hand even during activities in the external environment, effectively removes various viruses attached to the palm, and effectively prevents virus infection. It can be done.
これによって、外部における活動中にあっても各種のウイルスによる感染防止を有効に行い得る。例えば、鉱物原料としてのドロマイト由来の抗ウイルス剤を含有する柔軟性のある抗ウイルス性のハンド用のボール形状、棒形状あるいは板形状のシリコン・ドロマイト混練体の形成に適用応用できる。 As a result, it is possible to effectively prevent infection by various viruses even during external activities. For example, it can be applied to the formation of a ball-shaped, rod-shaped or plate-shaped silicon dolomite kneaded body for a flexible antiviral hand containing an antiviral agent derived from dolomite as a mineral raw material.
１…ミキサー、２…横置きされた円筒状の混練筒、３…混練筒２の入口側である上流側に設けられたシリコン材投入口部、４…混練筒２の出口側に設けられたシリコン・ドロマイト混練材取り出し口部（混練材取り出し口部という。）、５…混練筒２の内部に横方向に設置された回転軸、６…回転軸の周囲に設けた攪拌スクリュー、７…攪拌スクリュー６の上流側に設けた送り羽根、８…攪拌スクリュー６の下流側に設けた送り羽根、９…回転軸５に回転力を付与する駆動源としてのモーター、１０…鉱物原料としてのドロマイト由来の抗ウイルス剤を投入するための抗ウイルス剤投入口部、１１…抗ウイルス剤投入管、２１…搬送部、２２…混練部、２３…搬送部、２４…シリコン・ドロマイト混練材（混練材という。）、２５…シリコン・ドロマイト混練体（混練体という。）、３１…型、３２…窪み、４０…手のひら、４２…筒状部、５２…袋状部、１００（１００A、１００B、１００C、１００D、１００E、１００Ｆ，１００Ｇ）…柔軟性のある抗ウイルス性のハンド接触用のボール体、棒体、板体ドアノブ被覆シリコン・ドロマイト混練体あるいは携帯電話機被覆シリコン・ドロマイト混練体。
1 ... Mixer, 2 ... Horizontally placed cylindrical kneading cylinder, 3 ... Silicon material input port provided on the upstream side, which is the inlet side of the
本発明は、シリコン・焼成ドロマイト水和物からなる混練材または混練体、ボール状、棒状あるいは板状のシリコン・焼成ドロマイト水和物からなる混練体、ドアノブを被覆するシリコン・焼成ドロマイト水和物からなる混練体、携帯電話機を被覆するシリコン・焼成ドロマイト水和物からなる混練体及びシリコン・焼成ドロマイト水和物からなる混練材または混練体の形成方法に関する。 The present invention is kneaded material or kneading body made of a silicon-burnt dolomite hydrate, ball-like, kneading body made of rod-like or plate-like silicon burnt dolomite hydrate, silicon calcined dolomite hydrate covering the doorknob The present invention relates to a kneaded body made of, a kneaded body made of silicon / calcined dolomite hydrate for coating a mobile phone, and a kneaded material or kneaded body made of silicon / calcined dolomite hydrate.
本発明は、ドロマイト由来の抗ウイルス剤が焼成され水和された焼成ドロマイト水和物であり、混練材が主成分のシリコン材及び副成分の焼成ドロマイト水和物からなり、前記シリコン材及び前記焼成ドロマイト水和物が混合混練された状態にあって、抗ウイルス性を呈するシリコン・焼成ドロマイト水和物からなる混練材または混練体を提供する。
本発明において、混練材を単に添加し混合する操作がなされるでは足りず、柔軟性で固体性のシリコン材に粉体で固体性の前記焼成ドロマイト水和物を混合混練し、ドロマイトのシリコン材への保持力が高められたシリコン・焼成ドロマイト水和物からなる混練材が形成される。
The present invention is a calcined dolomite hydrate antiviral agent is hydrated calcined from dolomite, kneading material consists burnt dolomite hydrate silicon material and subcomponents of the main component, prior Symbol silicon material and Provided is a kneaded material or a kneaded product made of silicon / calcined dolomite hydrate exhibiting antiviral properties in a state in which the calcined dolomite hydrate is mixed and kneaded.
In the present invention, it is not sufficient to simply add and mix the kneading material, and the calcined dolomite hydrate, which is powdery and solid, is mixed and kneaded with the flexible and solid silicon material, and the dolomite silicon material is mixed and kneaded. A kneaded material made of silicon calcined dolomite hydrate with enhanced holding power is formed.
生成されたシリコン・焼成ドロマイト水和物からなる混練材は、抗ウイルス性を呈し、押圧体に接触して柔軟性があり、表面が押圧されると当該表面の押圧体への接触面積が押圧作用前に比べて増大する。
このシリコン・焼成ドロマイト水和物からなる混練材からシリコン・焼成ドロマイト水和物からなる混練体が生成される。シリコン・焼成ドロマイト水和物からなる混練体は、シリコン・焼成ドロマイト水和物からなる混練材と同一の性能を持ち、用途に対応した体積を持つ独立した成形品形態を呈する。
The kneaded material composed of the produced silicon and calcined dolomite hydrate exhibits antiviral properties and is flexible in contact with the pressing body, and when the surface is pressed, the contact area of the surface with the pressing body is pressed. Increases compared to before action.
Kneading body made of silicon burnt dolomite hydrate from the kneading material made of the silicon-burnt dolomite hydrate is produced. Kneading body made of silicon burnt dolomite hydrate has a kneading member and the same performance consisting of silicon burnt dolomite hydrate exhibits an independent molded product form has a volume corresponding to the application.
前記シリコン材及び前記焼成ドロマイト水和物が混練され、抗ウイルス性を呈し、押圧体に接触して柔軟性を保持し、用途に対応した体積を有する混練体が生成される。混練材が用途に対応して切り分けられて適切なシリコン・焼成ドロマイト水和物からなる混練体が形成される。
シリコン・焼成ドロマイト水和物からなる混練体の形成に当たって、主成分として簡便に常に手持ち可能な柔軟性のある材料としてシリコン材を用いること、焼成ドロマイト水和物の含有量、すなわち焼成ドロマイト水和物からなる抗ウイルス剤の含有量の比率が高められること、焼成ドロマイト水和物の含有量、すなわち抗ウイルス剤の含有量の比率を高めたときにシリコン材に確実に保持されることを考慮する必要がある。
The silicon material and the calcined dolomite hydrate are kneaded to produce a kneaded product having antiviral properties , contacting a pressing body to maintain flexibility, and having a volume suitable for the intended use. The kneaded material is cut into pieces according to the intended use to form a kneaded product made of appropriate silicon / calcined dolomite hydrate.
In forming a kneaded product composed of silicon and calcined dolomite hydrate , use a silicon material as a flexible material that can be easily and always held as a main component, and the content of calcined dolomite hydrate , that is, calcined dolomite hydration. Considering that the ratio of the content of the antiviral agent consisting of the substance is increased, and that the content of the calcined dolomite hydrate , that is, the content of the antiviral agent is increased, the silicon material is reliably retained. There is a need to.
製造されたシリコン・焼成ドロマイト水和物からなる混練体は、押圧体に付着した各種のウイルスを除去する目的のために使用可能とされる。例えば柔軟性のある抗ウイルス性ボール体、棒体あるいは板体を形成し、外部環境における活動中にあっても手のひらに付着した各種のウイルスを有効に除去してウイルス感染防止を有効に行い得るようにすることが可能になる。 The produced kneaded product made of silicon / calcined dolomite hydrate can be used for the purpose of removing various viruses adhering to the pressed body. For example, a flexible antiviral ball, rod or plate can be formed, and various viruses attached to the palm can be effectively removed even during activities in the external environment to effectively prevent virus infection. It becomes possible to do so.
本発明は、主成分のシリコン材と副成分のドロマイト由来の抗ウイルス剤からなる混練材に関し、
当該混練材が主成分のシリコン材及び副成分の焼成ドロマイト水和物からなり、前記シリコン材及び前記焼成ドロマイト水和物が混合混練された状態にあって、抗ウイルス性を呈し、押圧体に接触して柔軟性を保持する混練体であることを特徴とする抗菌性のシリコン・ドロマイト混練材を提供する。
本発明は、シリコン・焼成ドロマイト水和物からなる混練体を提供する。
本発明は、シリコン・焼成ドロマイト水和物からなる混練材の形成方法を提供する。シリコン・焼成ドロマイト水和物からなる混練材は、シリコン・ドロマイト混練体と読み替えることができる。
The present invention relates to a mixed kneaded material consisting of an antiviral agent from dolomite of the silicon material and the subcomponent of the main component,
The kneading material is made of burnt dolomite hydrate silicon material and subcomponents of the main component, the silicon material and the conditions near said burnt dolomite hydrate is mixed and kneaded, exhibit anti-viral, pressing body Provided is an antibacterial silicone dolomite kneading material, which is a kneaded product that retains flexibility in contact with a virus.
The present invention provides a kneaded product made of silicon and calcined dolomite hydrate.
The present invention provides a method for forming a kneading material composed of silicon and calcined dolomite hydrate. The kneaded material composed of silicon / calcined dolomite hydrate can be read as a silicon / dolomite kneaded product.
本発明によれば、抗ウイルス性を呈し、柔軟性で、押圧体、例えば手のひらに接触して効果のあるシリコン・焼成ドロマイト水和物からなる混練材あるいはシリコン・焼成ドロマイト水和物からなる混練体を提供することができる。
According to the present invention exhibit anti-viral, in flexibility, consisting pressing body, for example, kneading material or silicon-burnt dolomite hydrate in contact with the palm made of silicon and sintering dolomite hydrate is effective kneading Can provide the body.
ボール状シリコン・ドロマイト混練体１００（１００A）は、柔軟性を備えているので手のひらで握られ、押圧されると、手ひらに接触用のボール状シリコン・ドロマイト混練体１００（１００A）の表面の手のひらへの接触面積が押圧前の接触面積に比べて増大する。抗ウイルス作用面積が増大する。この状態にあっても、ボール状シリコン・ドロマイト混練体１００（１００A）は、全体の形態を変えながら柔軟性を保持し、手のひらにフイットする。 Since the ball-shaped silicon dolomite kneaded body 100 (100A) has flexibility, it is gripped by the palm, and when pressed, the surface of the ball-shaped silicon dolomite kneaded body 100 (100A) for contact with the palm. The contact area with the palm is increased as compared with the contact area before pressing. Anti-viral activity area is increased. Even in this state, the ball-shaped silicon dolomite kneaded product 100 (100A) retains its flexibility while changing its overall shape and fits in the palm of the hand.
ボール状シリコン・ドロマイト混練体１００（１００A）は、抗菌作用面積が増大した抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルス菌を死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。
外方からの力を作用させると、手ひらに接触用のボール状シリコン・ドロマイト混練体１００（１００A）の表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらから除去することが効果的になされる。
The ball-shaped silicon dolomite kneaded product 100 (100A) kills virus bacteria adhering to the palm by contact with the palm due to its antiviral performance with an increased antibacterial area. As a result, the virus attached to the palm has been removed from the palm.
When a force is applied from outside, the contact area of the surface of the palm of the ball-shaped silicon dolomite kneading member for contact with the hand flat 100 (100A) increases, to remove the virus attached to the palm from the palm it is effectively made.
棒状シリコン・ドロマイト混練体１００（１００B）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。
洗浄水の便宜のあるところでない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちにウイルスを除去する操作を行うことができる。
Since the rod-shaped silicon dolomite kneaded product 100 (100B) has flexibility, it can be restored to the original rod shape by applying an external force, and can be used repeatedly.
It can be used even in an environment where there is no convenience of washing water, and it is possible to perform an operation of immediately removing the virus , for example, when riding on a train and being caught by a strap, while riding or getting off.
板状シリコン・ドロマイト混練体１００（１００C）は、その抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルスを死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。 Plate-shaped silicon dolomite kneaded body 100 (100C) is in contact with the palm by its antiviral properties, it kills the virus attached to the palm. As a result, the virus attached to the palm has been removed from the palm.
外方からの力を作用させると、板状シリコン・ドロマイト混練体１００（１００C）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらからの除去することが効果的になされる。
板状シリコン・ドロマイト混練体１００（１００C）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。
When a force is applied from outside, the contact area of the plate-like silicon dolomite kneaded body 100 (100C) surface of the palm is increased, it is effectively made for removing from palm viruses adhering to the palm NS.
Since the plate-shaped silicon dolomite kneaded product 100 (100C) has flexibility, it can be restored to the original rod shape by applying an external force, and can be used repeatedly.
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちにウイルスを除去する操作を行うことができる。 It can be used even in an environment that is not convenient due to the use of wash water, and it is possible to perform an operation of immediately removing the virus , for example, when riding on a train and being caught by a strap, while riding or getting off.
図７は、柔軟性のある抗ウイルス性の手ひらに接触して効果のある成形品であるドアノブ被覆シリコン・ドロマイト混練体を示す図である。
この例の場合、ドアノブ被覆混練体は、長手方向に細い筒状の形状をなす。筒状部とすることで、内側におけるドアノブ表面のウイルス除去及び外側において手のひら付着のウイルスを除去する抗ウイルス性能が期待できる。
FIG. 7 is a diagram showing a doorknob-coated silicone dolomite kneaded product, which is a molded product that is effective in contact with a flexible antiviral palm.
In the case of this example, the doorknob-covered kneaded body has a tubular shape that is thin in the longitudinal direction. With the cylindrical portion, it can be expected antiviral ability to remove viruses palm attached in virus removal and outer door knob surface in the inner.
ドアノブ被覆シリコン・ドロマイト混練体１００（１００D）は、その抗ウイルス性能によって手のひらへの接触で、手のひらに付着したウイルスを死滅させる。これによって、手のひらに付着したウイルスが手のひらから除去されたことになる。
外方からの力を作用させると、ドアノブ被覆シリコン・ドロマイト混練体１００（１００D）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスが手のひらからの除去が効果的になされる。
Doorknob coated silicon dolomite kneaded body 100 (100D) is the contact to the palm by its antiviral properties, it kills the virus attached to the palm. As a result, the virus attached to the palm has been removed from the palm.
When an external force is applied, the contact area of the surface of the doorknob-coated silicon dolomite kneaded body 100 (100D) with the palm is increased, so that the virus attached to the palm is effectively removed from the palm.
ドアノブ被覆シリコン・ドロマイト混練体１００（１００D）は、柔軟性を備えているので、外力を加えることで、元の形状に戻すことができ、繰り返して用いられ得る。
洗浄水の便宜のあるところでない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちにウイルスを除去する操作を行うことができる。
Since the doorknob-coated silicon dolomite kneaded product 100 (100D) has flexibility, it can be restored to its original shape by applying an external force, and can be used repeatedly.
It can be used even in an environment where there is no convenience of washing water, and it is possible to perform an operation of immediately removing the virus , for example, when riding on a train and being caught by a strap, while riding or getting off.
図８（ａ）は、抗ウイルス性の携帯電話機被覆混練体を示し、図８（ｂ）は、形成された携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）が装着される携帯電話機の例を示す。
図３（e）に示される型３１が用いられて柔軟性のある抗ウイルス性の携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）が形成される。
携帯電話機被覆混練体１００（１００E）は、手のひら接触に用いられる体積を有し、携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部５２を有する。袋状部とすることで、内側における携帯電話機表面のウイルス除菌及び外側において手のひら付着のウイルスを除去する抗ウイルス性能が期待できる。
FIG. 8 (a) shows an anti-virus mobile phone-coated kneaded product, and FIG. 8 (b) shows an example of a mobile phone to which the formed mobile phone-coated silicon dolomite kneaded product 100 (100E) is mounted. show.
The
The mobile phone-coated kneaded body 100 (100E) has a volume used for palm contact, and has a bag-shaped
外方からの力を作用させると、携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）表面の手のひらへの接触面積が増大するので、手のひらに付着したウイルスを手のひらから除去することが効果的になされる。
携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）は、柔軟性を備えているので、外力を加えることで、元の形状に戻すことができ、繰り返して用いられ得る。
When a force is applied from outside, the contact area of the palm of the mobile phone coated silicon dolomite kneaded body 100 (100E) surface increases, it is made effective to remove viruses adhering to the palm from the palm NS.
Since the mobile phone coated silicon dolomite kneaded product 100 (100E) has flexibility, it can be returned to its original shape by applying an external force and can be used repeatedly.
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば電車に乗ってつり革に掴まったようなとき、乗車中にあるいは降車したとき直ちにウイルスを除去する操作を行うことができる。
手のひらで携帯電話機を握る関係で、携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）の大きさは携帯電話機の大きさに対して１０〜２０％程度大きさであることが推奨される。携帯電話機被覆シリコン・ドロマイト混練体１００（１００E）に接触するとは、手のひらで握り得る大きさの範囲にあることを意味する。
It can be used even in an environment that is not convenient due to the use of wash water, and it is possible to perform an operation of immediately removing the virus , for example, when riding on a train and being caught by a strap, while riding or getting off.
Since the mobile phone is held in the palm of the hand, it is recommended that the size of the mobile phone-coated silicon dolomite kneaded product 100 (100E) is about 10 to 20% of the size of the mobile phone. Contact with the mobile phone coated silicone dolomite kneaded body 100 (100E) means that it is within a size range that can be grasped by the palm of the hand.
外方からの力を作用させると室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）表面の足底への接触面積が増大するので、足に付着したウイルスの除去が効果的になされる。
室内フロア状シリコン・ドロマイト混練体１００（１００Ｆ）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば室内でテレビ観戦しているようなとき、ウイルスを除去する操作を行うことができる。
When an external force is applied, the contact area of the surface of the indoor floor-shaped silicon dolomite kneaded body 100 (100F) with the sole of the foot increases, so that the virus adhering to the foot is effectively removed.
Since the indoor floor-shaped silicon dolomite kneaded body 100 (100F) has flexibility, it can be restored to the original rod shape by applying an external force, and can be used repeatedly.
It can be used in an environment that is not convenient for the use of wash water, and can be operated to remove a virus, for example, when watching TV indoors.
自動車車内フロア状シリコン・ドロマイト混練体１００（１００Ｇ）は、柔軟性を備えているので、外力を加えることで、元の棒形状に戻すことができ、繰り返して用いられ得る。
洗浄水の使用の上で便宜でない環境下でも用いられ得、例えば自動車車内で運転手の脇に乗っているようなとき、ウイルスを除去する操作を行うことができる。
Since the floor-shaped silicon dolomite kneaded body 100 (100G) in an automobile has flexibility, it can be returned to the original rod shape by applying an external force, and can be used repeatedly.
It can be used in an environment that is not convenient for the use of wash water, and it is possible to perform an operation for removing a virus, for example, when riding on the side of a driver in a car.
本発明は、主成分のシリコン材と副成分のドロマイト由来の抗ウイルス剤からなる混練材から成形された抗ウイルス性の混練体であって、
前記ドロマイト由来の抗ウイルス剤が焼成され水和された焼成ドロマイト水和物であり、シリコン材がシリコーンゴムであって、主成分のシリコーンゴム及び副成分の焼成ドロマイト水和物を含有し、前記シリコーンゴム及び前記焼成ドロマイト水和物が混練されたものであって、抗ウイルス性を呈し、押圧体に接触して表面が押圧されると、柔軟性を保持し、当該表面の前記押圧体への接触面積が押圧作用前に比べて増大する混練体を提供する。また、本発明は、当該混練体の形成方法を提供する。
The present invention is an antiviral kneaded product formed from a kneaded material composed of a silicon material as a main component and an antiviral agent derived from dolomite as a sub component.
It is a calcined dolomite hydrate obtained by calcining and hydrating the antiviral agent derived from the dolomite, and the silicon material is silicone rubber, which contains silicone rubber as a main component and calcined dolomite hydrate as a sub component. Silicone rubber and the calcined dolomite hydrate are kneaded and exhibit antiviral properties. When the surface is pressed in contact with the pressing body, the flexibility is maintained and the pressed body on the surface is pressed. Provided is a kneaded body in which the contact area of is increased as compared with that before the pressing action. The present invention also provides a method for forming the kneaded product.
本発明によれば、抗ウイルス性を呈する、柔軟性のある抗ウイルス性で、押圧体、例えば手のひらに接触して、柔軟性を保持し、当該表面の前記押圧体への接触面積が押圧作用前に比べて増大する効果のあるシリコン・ドロマイト混練体を提供することができる。
According to the present invention, it is a flexible antiviral property exhibiting antiviral property, and it is in contact with a pressing body, for example, the palm, and retains flexibility, and the contact area of the surface with the pressing body acts as a pressing force. it is possible to provide a Oh Cie amplicon dolomite kneaded body effect which increases than before.
Claims (8)
混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトが混合混練された状態にあり、押圧体に接触して表面が押圧されると、柔軟性を保持し、当該表面の前記押圧体への接触面積が押圧作用前に比べて増大するシリコン・ドロマイト混練材であることを特徴とするシリコン・ドロマイト混練材。 A silicon-dromite kneading material containing silicon as the main component and dolomite as a sub-ingredient.
When the kneaded material is composed of a silicon material as a main component and a dolomite as a sub component, exhibits antiviral properties, and the silicon material and the dolomite are in a mixed and kneaded state, and the surface is pressed in contact with a pressing body, A silicon-dromite kneaded material, which is a silicon-dromite kneaded material that retains flexibility and increases the contact area of the surface with the pressing body as compared with that before the pressing action.
混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトが混合混練された状態にあり、押圧体に接触して表面が押圧されると、柔軟性を保持し、当該表面の前記押圧体への接触面積が押圧作用前に比べて増大するシリコン・ドロマイト混練体であることを特徴とするシリコン・ドロマイト混練体。 A silicon-dromite kneaded body containing a silicon material as a main component and a dolomite as a sub-ingredient.
When the kneaded material is composed of a silicon material as a main component and a dolomite as a sub component, exhibits antiviral properties, and the silicon material and the dolomite are in a mixed and kneaded state, and the surface is pressed in contact with a pressing body, A silicon-dromite kneaded body, which is a silicon-dromite kneaded body that retains flexibility and increases the contact area of the surface with the pressing body as compared with that before the pressing action.
全体がボール、棒あるいは板に似た形態をなして、混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混合混練で生成された混練体になり、人間の手に接触して表面が押圧されると、柔軟性を保持し、当該人間のてのひらへの接触面積が押圧作用前に比べて増大することを特徴とするボール状、棒状あるいは板状シリコン・ドロマイト混練体。 A ball-shaped, rod-shaped or plate-shaped silicon-dromite kneaded body containing a silicon material as a main component and a dolomite as a sub-component.
The whole was formed in a form similar to a ball, a rod or a plate, and the kneaded material was composed of a silicon material as a main component and a dolomite as a sub component, exhibited antiviral properties, and was produced by a mixed kneading of the silicon material and the dolomite. A ball-shaped body, which becomes a kneaded body and retains its flexibility when it comes into contact with a human hand and the surface is pressed, and the contact area with the human palm is increased as compared with that before the pressing action. Rod-shaped or plate-shaped silicon dolomite kneaded body.
全体がドアノブに似た形態をなして、混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混合混練で生成された混練体になり、当該混練体がドアノブに嵌め込まれるドアノブ収納空間部を有してドアノブを収納し、人間の手に接触して表面が押圧されると、柔軟性を保持し、当該人間のてのひらへの接触面積が押圧作用前に比べて増大することを特徴とするドアノブ被覆シリコン・ドロマイト混練体。 A doorknob-coated silicon-dromite kneaded body containing a silicon material as a main component and a dolomite as a sub-component.
The whole has a shape similar to a doorknob, and the kneaded material is composed of a silicon material as a main component and a dolomite as a sub component, exhibits antiviral properties, and becomes a kneaded body produced by a mixed kneading of the silicon material and the dolomite. The kneaded body has a doorknob storage space for being fitted into the doorknob, and when the doorknob is stored in contact with a human hand and the surface is pressed, the flexibility is maintained and the contact area with the human palm is maintained. A doorknob-coated silicon dolomite kneaded body characterized by an increase in the amount of pressure compared to before the pressing action.
全体が携帯電話機に似た形態をなして、混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混合混練で生成された混練体になり、当該混練体が携帯電話機を当該携帯電話機カバーと共に収納可能とする袋状部を有して当該携帯電話機を収納し、人間の手に接触して表面が押圧されると、柔軟性を保持し、当該人間のてのひらへの接触面積が押圧作用前に比べて増大することを特徴とする携帯電話機被覆シリコン・ドロマイト混練体。 A mobile phone-coated silicon-dromite kneaded body containing a silicon material as a main component and a dolomite as a sub-component.
The whole is in a form similar to that of a mobile phone, and the kneaded material is composed of a silicon material as a main component and a dolomite as a sub component, and exhibits antiviral properties. The kneaded body has a bag-shaped portion that allows the mobile phone to be stored together with the mobile phone cover to store the mobile phone, and when the surface is pressed by contact with a human hand, the flexibility is maintained. However, the mobile phone-coated silicon dolomite kneaded body is characterized in that the contact area with the human palm is increased as compared with that before the pressing action.
全体が室内フロアマットあるいは自動車車内フロアマットに似た形態をなして、混練材が主成分のシリコン材及び副成分のドロマイトからなり、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトの混合混練で生成された混練体になり、人間の足あるいは靴に接触して表面が押圧されると、柔軟性を保持し、当該人間の足あるいは靴への接触面積が押圧作用前に比べて増大することを特徴とする室内フロアマット状あるいは自動車車内フロアマット状シリコン・ドロマイト混練体。 An indoor floor mat-like or car interior floor mat-like silicon-dromite kneaded body containing a silicon material as a main component and a dolomite as a sub-ingredient.
The whole is in a form similar to an interior floor mat or a floor mat in an automobile, and is composed of a silicon material as a main component and a dolomite as a sub component, which exhibits antiviral properties, and is mixed and kneaded with the silicon material and the dolomite. When the kneaded product is produced and the surface is pressed by contact with the human foot or shoe, the flexibility is maintained and the contact area with the human foot or shoe is increased as compared with that before the pressing action. An indoor floor mat-like or car interior floor mat-like silicon dolomite kneaded body.
混練材として主成分のシリコン材及び副成分のドロマイトを準備し、抗ウイルス性を呈し、前記シリコン材及び前記ドロマイトを混合混練し、押圧体に接触して表面が押圧されると、柔軟性を保持し、当該表面の前記押圧体への接触面積が押圧作用前に比べて増大するシリコン・ドロマイト混練材を形成することを特徴とするシリコン・ドロマイト混練材の形成方法。 It is a method for forming a silicon-dromite kneading material containing a silicon material as a main component and a dolomite as a sub-component.
A silicon material as a main component and a dolomite as a sub-component are prepared as a kneading material to exhibit antiviral properties. A method for forming a silicon-dromite kneaded material, which comprises forming a silicon-dromite kneaded material that is held and the contact area of the surface with the pressing body is increased as compared with that before the pressing action.
請求項７に記載したシリコン・ドロマイト混練体の形成方法によってシリコン・ドロマイト混練材を生成し、当該シリコン・ドロマイト混練材からシリコン・ドロマイト混練体を形成することを特徴とするシリコン・ドロマイト混練体の形成方法。 It is a method for forming a silicon-dromite kneaded body containing a silicon material as a main component and a dolomite as a sub-component.
A silicon dolomite kneaded material according to claim 7, wherein a silicon dolomite kneaded material is produced, and a silicon dolomite kneaded body is formed from the silicon dolomite kneaded material. Forming method.