JP2021144839A - ノンハロゲン難燃性樹脂組成物を用いた送電ケーブルの製造方法 - Google Patents
ノンハロゲン難燃性樹脂組成物を用いた送電ケーブルの製造方法 Download PDFInfo
- Publication number
- JP2021144839A JP2021144839A JP2020042060A JP2020042060A JP2021144839A JP 2021144839 A JP2021144839 A JP 2021144839A JP 2020042060 A JP2020042060 A JP 2020042060A JP 2020042060 A JP2020042060 A JP 2020042060A JP 2021144839 A JP2021144839 A JP 2021144839A
- Authority
- JP
- Japan
- Prior art keywords
- resin composition
- layer
- power transmission
- transmission cable
- retardant resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
以下に、本実施の形態の送電ケーブルの製造方法について説明する。図1は、送電ケーブルの構成を示す断面図である。本実施の形態においては、図1に示す送電ケーブルの製造方法を例に説明する。
以下に、本実施の形態の送電ケーブルに用いるノンハロゲン難燃性樹脂組成物について実施例に基づいてさらに具体的に説明する。
(材料名)
1)EVA:ランクセス社製「レバプレン600HV」(VA量:質量60%)
2)酸変性ポリオレフィン:酸変性エチレン−α−オレフィンコポリマー、三井化学社製「タフマーMH5040」
3)水酸化マグネシウム:ヒューバー社製「マグニフィンH10A」(ビニルシラン0.8−1.1μm)
4)水酸化アルミニウム:日本軽金属製「BF013STV」(シラン1.0μm)
5)シリカ:エルケム社製「シディスターT120U」(球状、平均粒径0.15μm)
6)t−ブチルパーオキシ2−エチルヘキシルカーボネート:Nouryon製「トリゴノックス117」
7)トリアリルイソシアネート:日本化成製「TAIC」
8)酸化亜鉛:堺化学製「亜鉛華3号」
9)ブレンド系酸化防止剤:アデカ製「AO−18(AO20/412S=6/4)
10)カーボン:旭カーボン社製「FTカーボン」
11)ヒドロキステアリン酸リチウム:日東化成工業社製「LS−6」
12)ステアリン酸亜鉛:日東化成工業社製「EZ−101」
(実施例1〜5)
表1に示す成分配合でノンハロゲン難燃性樹脂組成物を調整し、ロールを用いて混練を行った後、厚さ1mmのシート形状に成形した。成形したシートに対して、架橋管を用いて蒸気架橋を行った。具体的には、シート(混練したノンハロゲン難燃性樹脂組成物)に、飽和水蒸気圧1MPaの蒸気(水蒸気)を直接接触させ、180℃×10分間の架橋を行い、蒸気架橋したシートを得た。
成分配合を表1に示すように変えて、実施例1〜5の場合と同様にして、蒸気架橋したシートを得た。
得られたシートを120℃のオーブンに168時間暴露した後、ダンベル6号形により打ち抜き、標線間距離が20mmの試験片を作製した。この試験片を、引張速度は200mm/minで引っ張り破断点での伸びを測定した。以下の式より熱老化後伸び(%)を求めた。
さらに、以下の式より熱老化後伸び残率(%)を求めた。
熱老化前伸び(%)および熱老化後伸び残率(%)を表1に示す。
上記実施の形態においては、図1に示す複数の積層体で送電ケーブルを構成したが、導体2とその周囲に設けられた絶縁層4とを有する絶縁電線をコア層としてその周囲にシース層9が設けられた送電ケーブルとしてもよい。また、複数の絶縁電線をコア層としてもよい。このような構成の送電ケーブルのシース層として、上記ノンハロゲン難燃性樹脂組成物を用い、上記実施の形態と同様にして、上記コア層の周囲にシース層を形成してもよい。
2 導体
3 内部半導電層
4 絶縁層
5 外部半導電層
6 半導電性テープ層
7 遮蔽層
8 押えテープ層
9 シース層
200 押出機
220 スクリュー
221 材料投入口(ホッパー)
230 押出ヘッド
240 蒸気管(架橋管)
C コア部
Claims (5)
- (a)導体と前記導体の外周に形成された絶縁層とを有するコア部に、シース層となるノンハロゲン難燃性樹脂組成物を被覆する工程、
(b)前記シース層を水蒸気と接触させることにより架橋させる工程、
を有し、
前記シース層は、ベースポリマと、難燃剤とを含有するノンハロゲン難燃性樹脂組成物からなり、
前記難燃剤は、
水酸化マグネシウム単独、
水酸化アルミニウム単独、
シリカ単独、
水酸化マグネシウムおよび水酸化アルミニウムの併用、
水酸化アルミニウムおよびシリカの併用、
のいずれかであり、
前記難燃剤の含有量は、前記ベースポリマ100質量部に対し、50質量部以上である、ノンハロゲン難燃性樹脂組成物を用いた送電ケーブルの製造方法。 - 請求項1記載のノンハロゲン難燃性樹脂組成物を用いた送電ケーブルの製造方法において、
前記ベースポリマは、エチレン酢酸ビニル共重合体を含む、ノンハロゲン難燃性樹脂組成物を用いた送電ケーブルの製造方法。 - 請求項1記載のノンハロゲン難燃性樹脂組成物を用いた送電ケーブルの製造方法において、
前記難燃剤の含有量は、前記ベースポリマ100質量部に対し、100質量部以上150質量部以下である、ノンハロゲン難燃性樹脂組成物を用いた送電ケーブルの製造方法。 - 請求項1記載のノンハロゲン難燃性樹脂組成物を用いた送電ケーブルの製造方法において、
前記シース層は、120℃で168時間の熱老化試験後の引張伸び残率が75%以上である、ノンハロゲン難燃性樹脂組成物を用いた送電ケーブルの製造方法。 - 導体の外周に、内側から順に内部半導電層、絶縁層および外部半導電層を形成する工程、
前記外部半導電層の外周にワイヤーを巻き付けることにより遮蔽層を形成する工程、
前記遮蔽層の外周に押えテープを巻き付けることにより押えテープ層を形成する工程、
前記押えテープ層の外周にシース層を形成する工程、を有し、
前記シース層を形成する工程は、
(a)前記押えテープ層の外周に、前記シース層となるノンハロゲン難燃性樹脂組成物を被覆する工程、
(b)前記シース層を水蒸気と接触させることにより架橋させる工程、
を含み、
前記シース層は、ベースポリマと、難燃剤とを含有するノンハロゲン難燃性樹脂組成物からなり、
前記難燃剤は、
水酸化マグネシウム単独、
水酸化アルミニウム単独、
シリカ単独、
水酸化マグネシウムおよび水酸化アルミニウムの併用、
水酸化アルミニウムおよびシリカの併用、
のいずれかであり、
前記難燃剤の含有量は、前記ベースポリマ100質量部に対し、50質量部以上である、ノンハロゲン難燃性樹脂組成物を用いた送電ケーブルの製造方法。