JP2021120344A - 化学強化可能なガラス板 - Google Patents
化学強化可能なガラス板 Download PDFInfo
- Publication number
- JP2021120344A JP2021120344A JP2021071417A JP2021071417A JP2021120344A JP 2021120344 A JP2021120344 A JP 2021120344A JP 2021071417 A JP2021071417 A JP 2021071417A JP 2021071417 A JP2021071417 A JP 2021071417A JP 2021120344 A JP2021120344 A JP 2021120344A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- composition
- glass plate
- weight
- mgo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
− ガラス製造ライン、特にフロートラインは、かなりの出資となり、組成物によって、たとえば耐火物質が損傷しても修復できないため;および
− ある組成から別の組成に変更する移行時間は、この時間が長いと最終ガラスの製造コストに大きな悪影響が生じるので、ガラス製造時の非常に重要なパラメータの1つとなるためである。
65≦SiO2≦78%
5≦Na2O≦20%
0≦K2O<5%
3<Al2O3≦5%
0<CaO<4.5%
4≦MgO≦12%を含み;
0.88≦[MgO/(MgO+CaO)]<1を含むホウ素フリーおよびリチウムフリーガラス組成を有するガラス板に関する。
65≦SiO2≦78%
5≦Na2O≦20%
0≦K2O≦3%
3<Al2O3≦5%
0<CaO<3%
4≦MgO≦12%を含み;
0.88≦[MgO/(MgO+CaO)]<1を含む。
65≦SiO2≦78%
5≦Na2O≦20%
0≦K2O≦2%
4≦Al2O3≦5%
0<CaO<2%
6≦MgO≦10%を含み;
0.88≦[MgO/(MgO+CaO)]<1を含む。
前項で作製した試料について、同時に同時に同じ条件で化学強化した。異なる組成の試料を1つのカセット中に入れ、予備加熱し、次に420℃の溶融KNO3(>99%)浴中に220分間浸漬した。イオン交換後、試料を冷却し、洗浄した。続いて、表面圧縮応力(CS)および交換された層の深さ(DoL)を光弾性測定法によって測定した。以下の表は、本発明による組成物1〜3および比較例1〜2の組成物のそれぞれの10の無作為の試料のCSおよびDoLの平均値をまとめている。
Fluegelモデル(Glass Technol.:Europ.J.Glass Sci.Technol.A 48(1):13−30(2007);およびJournal of the American Ceramic Society 90(8):2622(2007))を使用して、本発明による実施例1〜4および比較例比較例1〜2の組成物に関して、ガラス組成に基づいた以下の性質の評価を行った:
− 1200℃および1400℃で評価されるガラス溶融密度;
− 「融点温度T2」での粘度;
− 「作用点温度T4」;
− 失透温度T0;
− 熱膨張係数(CET)。
融点温度T2は、好ましくは最高1550℃、より好ましくは最高1520℃、最も好ましくは最高1500℃である。
− これらの融点温度T2は1500℃未満であり、これらは従来のソーダ石灰ガラス(比較例1)と同等であり、アルミノケイ酸塩ガラス(比較例2)よりもはるかに低い;
− これらの作用点温度T4は1100℃未満であり、これらは従来のソーダ石灰ガラス(比較例1)と同等であり、アルミノケイ酸塩ガラス(比較例2)よりも低い;
− これらの失透温度T0は、作用点温度T4よりも低いため適切である;
− これらのガラス密度は、ソーダ石灰ガラスおよびアルミノケイ酸塩ガラス(比較例1および2)に非常に近く、そのため組成物の変更(移行)中の密度の欠陥が回避/限定される。
Claims (13)
- ガラスの全重量に対して表した重量パーセント値の単位で:
65≦SiO2≦78%
5≦Na2O≦20%
0≦K2O<5%
4≦Al2O3≦5%
0<CaO<4.5%
4≦MgO≦12%を含み;
0.88≦[MgO/(MgO+CaO)]≦0.98
を含む、ホウ素フリーおよびリチウムフリーのガラス組成を有するガラス板。 - 前記組成が0<CaO<2重量%を含むことを特徴とする請求項1に記載のガラス板。
- 前記組成が0.002〜1.7重量%の範囲の含有量の全鉄(Fe2O3の形態で表される)を含むことを特徴とする請求項2に記載のガラス板。
- 前記組成が0.002〜0.06重量%の範囲の含有量の全鉄(Fe2O3の形態で表される)を含むことを特徴とする請求項3に記載のガラス板。
- 前記組成が0.002〜0.02重量%の範囲の含有量の全鉄(Fe2O3の形態で表される)を含むことを特徴とする請求項4に記載のガラス板。
- 前記組成が4≦Al2O3≦4.5重量%を含むことを特徴とする請求項1に記載のガラス板。
- 前記組成が4.5≦Al2O3≦5重量%を含むことを特徴とする請求項5に記載のガラス板。
- 前記組成が0≦K2O≦4重量%を含むことを特徴とする請求項1〜7のいずれか一項に記載のガラス板。
- 前記組成が0.9≦[MgO/(MgO+CaO)]<1を含むことを特徴とする請求項1〜8のいずれか一項に記載のガラス板。
- 前記組成が0.9≦[MgO/(MgO+CaO)]≦0.98を含むことを特徴とする請求項1に記載のガラス板。
- 前記組成が0.92≦[MgO/(MgO+CaO)]≦0.98を含むことを特徴とする請求項10に記載のガラス板。
- 化学強化される、請求項1〜11のいずれか一項に記載のガラス板。
- 電子デバイス中での請求項1〜12のいずれか一項に記載のガラス板の使用。