JP2021095093A - タイヤ - Google Patents
タイヤ Download PDFInfo
- Publication number
- JP2021095093A JP2021095093A JP2019229440A JP2019229440A JP2021095093A JP 2021095093 A JP2021095093 A JP 2021095093A JP 2019229440 A JP2019229440 A JP 2019229440A JP 2019229440 A JP2019229440 A JP 2019229440A JP 2021095093 A JP2021095093 A JP 2021095093A
- Authority
- JP
- Japan
- Prior art keywords
- metal
- belt
- tire
- cord
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記ベルト内で隣接する2層の前記ベルト層にそれぞれ埋設された前記金属フィラメントの表面間の距離である層間ゲージGと、前記金属コード同士の間の間隔w2との比率G/w2が、1.6以下であり、
前記金属コードを構成する該金属フィラメント同士の間隔w1と前記金属コードの幅Wとの比率w1/Wが0.07以上であり、かつ、
前記金属フィラメントの線径dと、前記金属コードを構成する該金属フィラメント同士の間隔w1との比率d/w1が、1.2以上2未満であることを特徴とするものである。
エラストマー被覆率=(ゴム被覆長/試料長)×100(%)
なお、エラストマーとして、ゴム以外のエラストマーを用いた場合、および、金属コードとして、スチールコード以外の金属コードを用いた場合も、同様に算出することができる。
下記の表1中に示す条件に従うスチールコードを、上下両側から、ゴム組成物よりなる厚さ0.5mm程度のシートにより被覆して、各ゴム−スチールコード複合体を作製した。コーティング用のゴム組成物は、常法に従い配合・混練することで調製した。得られた各ゴム−スチールコード複合体を160℃、20分にて加硫して、以下の評価を行った。
得られた各ゴム−スチールコード複合体を用いてベルト層サンプルを作製し、その重量を計測して、比較例1のベルト重量を100とする指数にて示した。数値が小さいほど軽量であって好ましい。
図1に示すようなタイヤサイズ195/65R15の乗用車用タイヤを、各ゴム−スチールコード複合体を2層のベルトに適用して作製した。ベルト角度は、タイヤ周方向に対して±28°とした。
各供試タイヤにつき、SAE J 1269に準拠して、転がり抵抗を、転動抵抗試験機を用いて測定した。結果は、比較例1を100とする指数で示した。数値が小さいほど結果は良好である。
各供試タイヤにつき、2層のベルト層間における歪の大きさを、有限要素法(FEM)により算出して求めた。結果は、比較例1を100とする指数で示した。数値が小さいほど結果は良好である。但し、90〜110の範囲内であれば、同等レベルと評価する。
各供試タイヤに内圧を充填してテスト用乗用車に装着し、BESドラム上を、サイドフォース(SF)一定で横力をかけて走行させた後、タイヤを解剖してベルト層端部に発生している亀裂の長さを測定した。ベルト端耐久性が不十分である場合を×、やや不十分である場合を△、優れている場合を○、非常に優れている場合を◎として評価した。
操縦安定性は、以下に従い求めた面内剛性の値に基づいて評価した。結果は、比較例1の面内剛性の値を100として指数化し、この指数値に基づき、90未満である場合を×、90以上100未満である場合を△、100以上110未満である場合を○、110以上である場合を◎として評価した。
*2)比較例1,2のコードは断面楕円形のコードであり、金属フィラメント間間隔(コード間間隔)はコードの打込みの向きにより変動する。
2 金属コード
3 エラストマー
10 エラストマー−金属コード複合体
100 タイヤ
101 トレッド部
102 サイドウォール部
103 ビード部
104 カーカス
105 ベルト
105a,105b ベルト層
106 ビードコア
Claims (6)
- 複数本の金属フィラメントが撚り合わされずに一列に引き揃えられた束からなる金属コードをエラストマーにより被覆してなるベルト層が、少なくとも2層で積層されてなるベルトを備えるタイヤであって、
前記ベルト内で隣接する2層の前記ベルト層にそれぞれ埋設された前記金属フィラメントの表面間の距離である層間ゲージGと、前記金属コード同士の間の間隔w2との比率G/w2が、1.6以下であり、
前記金属コードを構成する該金属フィラメント同士の間隔w1と前記金属コードの幅Wとの比率w1/Wが0.07以上であり、かつ、
前記金属フィラメントの線径dと、前記金属コードを構成する該金属フィラメント同士の間隔w1との比率d/w1が、1.2以上2未満であることを特徴とするタイヤ。 - 前記層間ゲージGが、0.10mm以上1.20mm以下である請求項1記載のタイヤ。
- 前記金属コードを構成する前記金属フィラメント同士の間隔w1が、0.01mm以上0.24mm以下である請求項1または2記載のタイヤ。
- 前記金属コード同士の間の間隔w2が、0.25mm以上2.0mm以下である請求項1〜3のうちいずれか一項記載のタイヤ。
- 前記金属コードが、2本以上20本以下の金属フィラメントの束からなる請求項1〜4のうちいずれか一項記載のタイヤ。
- 前記金属フィラメントの線径dが、0.15mm以上0.40mm以下である請求項1〜5のうちいずれか一項記載のタイヤ。