JP2021085202A - Weed germination prevention structure, installation method for the same, and weed germination prevention sheet - Google Patents

Weed germination prevention structure, installation method for the same, and weed germination prevention sheet Download PDF

Info

Publication number
JP2021085202A
JP2021085202A JP2019214093A JP2019214093A JP2021085202A JP 2021085202 A JP2021085202 A JP 2021085202A JP 2019214093 A JP2019214093 A JP 2019214093A JP 2019214093 A JP2019214093 A JP 2019214093A JP 2021085202 A JP2021085202 A JP 2021085202A
Authority
JP
Japan
Prior art keywords
prevention structure
weed germination
germination prevention
treatment material
sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2019214093A
Other languages
Japanese (ja)
Other versions
JP7341039B2 (en
Inventor
竜一 張ヶ谷
Ryuichi Harigaya
竜一 張ヶ谷
哲 井澤
Satoru Izawa
哲 井澤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shin Etsu Polymer Co Ltd
Shin Etsu Chemical Co Ltd
Original Assignee
Shin Etsu Polymer Co Ltd
Shin Etsu Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shin Etsu Polymer Co Ltd, Shin Etsu Chemical Co Ltd filed Critical Shin Etsu Polymer Co Ltd
Priority to JP2019214093A priority Critical patent/JP7341039B2/en
Publication of JP2021085202A publication Critical patent/JP2021085202A/en
Application granted granted Critical
Publication of JP7341039B2 publication Critical patent/JP7341039B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

To provide a weed germination prevention structure being easy to be fixed to a boundary between a road pavement surface and other structures and having excellent weather resistance, an installation method for the same, and a weed germination prevention sheet.SOLUTION: A weed germination prevention structure (10A) is installed in a retention part (A) at a boundary between a paved surface (1) of a road and a curb (2) being an example of other structures, in which the retention part comprising grooves, depressions, steps, gaps, or joints through which dust can be collected. The weed germination prevention structure (10A) includes: a primer layer (4) formed on the surface of an asphalt surface, concrete surface, or mortar surface constituting the retention part and its surroundings; a substrate treatment material (5) made of curable silicone that is in contact with the primer layer and fills at least a part of the retention part; and a sheet (6) comprising a curable silicone covering at least a part of the substrate treatment material and the primer layer.SELECTED DRAWING: Figure 1

Description

本発明は、雑草発芽防止構造及びその設置方法、並びに雑草発芽防止シートに関する。 The present invention relates to a weed germination prevention structure, a method for installing the same, and a weed germination prevention sheet.

車道や歩道の舗装面と、縁石や中央分離帯のコンクリートブロックとの境界（目地）に生えている雑草の除草作業が道路の維持業務として行われている。除草作業を怠ると運転者の視界を遮る恐れがあり、また、雨天時には道路脇の排水溝への速やかな排水を阻害することもある。これらは交通事故の原因になり得るので、除草作業は欠かさずに行われているが、コストがかかる問題がある。 Weeds growing on the boundary (joint) between the paved surface of the roadway or sidewalk and the concrete block of the curb or median strip are being weeded as road maintenance work. If weeding is neglected, the driver's view may be obstructed, and in rainy weather, prompt drainage to the drainage ditch on the side of the road may be hindered. Since these can cause traffic accidents, weeding work is carried out without fail, but there is a problem that it is costly.

上記問題に対して、特許文献１には、樹脂フィルムに接着剤層が積層された雑草抑止テープが提案されている。舗装面とそれ以外の構造物との間隙に土、砂、埃等が溜まり、雑草が発生し得る箇所に対して、この箇所を覆うように雑草抑止テープを貼付すると、雑草の発生を抑止できるとしている。 In response to the above problem, Patent Document 1 proposes a weed control tape in which an adhesive layer is laminated on a resin film. If soil, sand, dust, etc. collect in the gap between the pavement surface and other structures and weeds may grow, weed control tape can be applied to cover these places to prevent weeds from growing. It is said.

特開２００５−２１０９０６号公報Japanese Unexamined Patent Publication No. 2005-210906

しかしながら、特許文献１の雑草抑止テープは以下の問題を有する。貼付する面が平滑面であるとは限らず、例えば、２〜５ｍｍ程度の凸凹がある粗面の場合がある。このような粗面の複雑な表面形状に対して雑草抑止テープは追随できないため、その貼付が困難である。また、辛うじて貼付できたとしても、実質的な接着面積が小さいため、充分な接着力が得られない。さらに、アクリル系感圧接着剤層による接着を提案しているが、四季を通して風雨や直射日光に曝される屋外環境における耐候性は、必ずしも満足できるものではない。 However, the weed control tape of Patent Document 1 has the following problems. The surface to be attached is not always a smooth surface, and may be, for example, a rough surface having irregularities of about 2 to 5 mm. Since the weed control tape cannot follow such a complicated surface shape of a rough surface, it is difficult to attach it. Further, even if it can be barely attached, a sufficient adhesive force cannot be obtained because the substantially adhesive area is small. Furthermore, although we have proposed bonding with an acrylic pressure-sensitive adhesive layer, the weather resistance in an outdoor environment exposed to wind, rain and direct sunlight throughout the four seasons is not always satisfactory.

本発明は、道路の舗装面とその他の構造物との境界に固着させることが容易であり、耐候性に優れた雑草発芽防止構造及びその設置方法、並びに雑草発芽防止シートを提供する。 The present invention provides a weed germination prevention structure and an installation method thereof, which can be easily fixed to a boundary between a road pavement surface and other structures and has excellent weather resistance, and a weed germination prevention sheet.

［１］ 道路の舗装面と、その他の構造物との境界に設置された、雑草発芽防止構造であって、前記雑草発芽防止構造は、プライマー層、硬化型シリコーンからなる下地処理材、及び、硬化型シリコーンからなるシートから選択される少なくとも一つであることを特徴とする雑草発芽防止構造。
［２］ 前記境界には滞留部が形成されており、前記滞留部は、土埃が溜まり得る溝、窪み、段差、隙間又は目地からなり、前記滞留部及びその周囲を構成する面は、アスファルト面、コンクリート面又はモルタル面からなる、［１］記載の雑草発芽防止構造。
［３］ 前記下地処理材及び前記シートのうち少なくとも一方が遮光材を含有する、［１］に記載の雑草発芽防止構造。
［４］ 前記下地処理材及び前記シートのうち少なくとも一方の全光線透過率が３０％以下である、［１］〜［３］の何れか一項に記載の雑草発芽防止構造。
［５］ 前記下地処理材及び前記シートのうち少なくとも一方が、黒色もしくは灰色である、［１］〜［４］の何れか一項に記載の雑草発芽防止構造。
［６］ 前記その他の構造物が、縁石または柱である、［１］〜［５］の何れか一項に記載の雑草発芽防止構造。
［７］ 前記下地処理材および前記シートの少なくとも一方に発芽防止剤または防草剤を含有する［１］〜［６］何れか一項に記載の雑草発芽防止構造。
［８］ 道路の舗装面と、その他の構造物との境界にある滞留部に、雑草発芽防止構造を設置する方法であって、前記滞留部は、土埃が溜まり得る溝、窪み、段差、隙間又は目地からなり、前記滞留部及びその周囲を構成するアスファルト面、コンクリート面又はモルタル面の表面を清浄にする工程と、前記表面にプライマー剤を塗布し、乾燥することによりプライマー層を形成する工程と、前記プライマー層が形成された前記滞留部に未硬化シリコーンからなるペーストを塗布し、前記滞留部の少なくとも一部を充填することにより下地処理材を形成する工程と、前記下地処理材及び前記プライマー層の少なくとも一部を覆う、未硬化シリコーンからなるシートを貼付する工程と、を有することを特徴とする雑草発芽防止構造の設置方法。
［９］ 前記プライマー剤の塗布量が、１００ｇ／ｍ２〜５００ｇ／ｍ２である、［８］に記載の雑草発芽防止構造の設置方法。
［１０］ 前記舗装面を上方から見て、前記プライマー剤を塗布する領域が湾曲または屈曲している、［８］または［９］に記載の雑草発芽防止構造の設置方法。
［１１］ 未硬化の硬化型シリコーンからなるシートであり、［８］〜［１０］の何れか一項に記載の雑草発芽防止構造の設置方法にて、前記下地処理材及び前記プライマー層の少なくとも一部を覆う用途で使用される、雑草発芽防止シート。
［Ｘ］ 道路の舗装面と、その他の構造物との境界にある滞留部に設置された、雑草発芽防止構造であって、前記滞留部は、土埃が溜まり得る溝、窪み、段差、隙間又は目地からなり、前記滞留部及びその周囲を構成するアスファルト面、コンクリート面又はモルタル面の表面に形成されたプライマー層と、前記プライマー層に接し、前記滞留部の少なくとも一部を充填する硬化型シリコーンからなる下地処理材と、前記下地処理材及び前記プライマー層の少なくとも一部を覆う硬化型シリコーンからなるシートと、を備えることを特徴とする雑草発芽防止構造。 [1] A weed germination prevention structure installed at the boundary between the pavement surface of a road and other structures, wherein the weed germination prevention structure includes a primer layer, a base treatment material made of curable silicone, and a base treatment material. A weed germination prevention structure characterized in that it is at least one selected from a sheet made of curable silicone.
[2] A retention portion is formed at the boundary, and the retention portion is composed of grooves, dents, steps, gaps or joints where dust can collect, and the retention portion and the surface constituting the surrounding portion are asphalt surfaces. The weed germination prevention structure according to [1], which comprises a concrete surface or a mortar surface.
[3] The weed germination prevention structure according to [1], wherein at least one of the base treatment material and the sheet contains a light-shielding material.
[4] The weed germination prevention structure according to any one of [1] to [3], wherein the total light transmittance of at least one of the base treatment material and the sheet is 30% or less.
[5] The weed germination prevention structure according to any one of [1] to [4], wherein at least one of the base treatment material and the sheet is black or gray.
[6] The weed germination prevention structure according to any one of [1] to [5], wherein the other structure is a curb or a pillar.
[7] The weed germination prevention structure according to any one of [1] to [6], wherein at least one of the base treatment material and the sheet contains a germination inhibitor or a herbicide.
[8] A method of installing a weed sprouting prevention structure in a retention portion at the boundary between the pavement surface of a road and other structures, and the retention portion is a groove, a depression, a step, or a gap where dust can collect. Alternatively, a step of cleaning the surface of the asphalt surface, concrete surface or mortar surface which is composed of joints and constitutes the retention portion and its surroundings, and a step of applying a primer agent to the surface and drying it to form a primer layer. A step of applying a paste made of uncured silicone to the retaining portion on which the primer layer is formed and filling at least a part of the retaining portion to form a base treatment material, and the base treatment material and the above. A method for installing a weed sprouting prevention structure, which comprises a step of attaching a sheet made of uncured silicone that covers at least a part of a primer layer.
[9] The coating amount of the primer agent is 100g / m 2 ~500g / m 2 , the installation method of weed germination prevention structure according to [8].
[10] The method for installing a weed germination prevention structure according to [8] or [9], wherein the area to which the primer is applied is curved or bent when the pavement surface is viewed from above.
[11] A sheet made of uncured curable silicone, at least of the base treatment material and the primer layer by the method for installing the weed germination prevention structure according to any one of [8] to [10]. A weed germination prevention sheet used to cover a part.
[X] A weed germination prevention structure installed in a retention portion at the boundary between the pavement surface of a road and other structures, and the retention portion is a groove, a depression, a step, a gap, or a gap where dust can collect. A primer layer composed of joints and formed on the surface of the asphalt surface, concrete surface or mortar surface constituting the retention portion and its surroundings, and a curable silicone that is in contact with the primer layer and fills at least a part of the retention portion. A weed germination prevention structure comprising: a base treatment material made of, and a sheet made of a curable silicone covering at least a part of the base treatment material and the primer layer.

本発明の雑草発芽防止構造によれば、滞留部の少なくとも一部を下地処理材が充填し、さらに硬化型シリコーンからなるシート（雑草発芽防止シート）が覆えば、滞留部に土埃が溜まり難くなり、雑草の発芽に適さない環境となり、雑草の発芽を防止することができる。下地処理材は、設置する箇所が粗面であったとしてもほぼ完全に追従することができる。また、下地処理材が粗面を埋めて比較的平滑な表面を形成することができる。さらに、下地処理材を覆うように設置された雑草発芽防止シートは、同じく硬化型シリコーンからなる下地処理材に対する接着性が優れる。この結果、本発明の雑草発芽防止構造は、滞留部に対して充分に固着している。
また、本発明の雑草発芽防止構造にあっては、耐候性に優れる硬化型シリコーンからなる下地処理材及びシートを備えれば、それらは充分な厚みを有しており、設置面に対する接着性も温度変化や湿度変化に対して安定して高いので、優れた耐候性を発揮し得る。
本発明の雑草発芽防止構造の設置方法によれば、上述の優れた効果を奏する雑草発芽防止構造を容易に形成することができる。 According to the weed germination prevention structure of the present invention, if at least a part of the retention portion is filled with a base treatment material and further covered with a sheet made of curable silicone (weed germination prevention sheet), dust is less likely to accumulate in the retention portion. , The environment is not suitable for weed germination, and weed germination can be prevented. The base treatment material can almost completely follow even if the place where it is installed is a rough surface. In addition, the surface treatment material can fill the rough surface to form a relatively smooth surface. Further, the weed germination prevention sheet installed so as to cover the base treatment material has excellent adhesiveness to the base treatment material also made of curable silicone. As a result, the weed germination prevention structure of the present invention is sufficiently adhered to the retention portion.
Further, in the weed germination prevention structure of the present invention, if a base treatment material and a sheet made of curable silicone having excellent weather resistance are provided, they have a sufficient thickness and have adhesiveness to the installation surface. Since it is stable and high against changes in temperature and humidity, it can exhibit excellent weather resistance.
According to the method for installing the weed germination prevention structure of the present invention, the weed germination prevention structure having the above-mentioned excellent effect can be easily formed.

雑草発芽防止構造を二カ所に設置した様子の一例を示す斜視図である。It is a perspective view which shows an example of a weed germination prevention structure installed in two places. 図１のＸ−Ｘ線で切断した断面図である。FIG. 5 is a cross-sectional view taken along the line XX of FIG. 図１の雑草発芽防止構造１０Ａを部分拡大した断面図の一例である。This is an example of a partially enlarged cross-sectional view of the weed germination prevention structure 10A of FIG. 図１の雑草発芽防止構造１０Ｂを部分拡大した断面図の一例である。This is an example of a partially enlarged cross-sectional view of the weed germination prevention structure 10B of FIG. 雑草発芽防止構造を設置する前の縁石と舗装面の一例を示す斜視図である。It is a perspective view which shows an example of a curb and a pavement surface before installing a weed germination prevention structure. 雑草発芽防止構造を設置せず、縁石と舗装面の境界の滞留部から雑草が発芽し、生育した様子の一例を示す斜視図である。It is a perspective view which shows an example of how weeds germinated and grew from the retention part of the boundary between a curb and a pavement surface without installing a weed germination prevention structure.

《雑草発芽防止構造》
本発明の第一態様は、道路の舗装面と、その他の構造物との境界にある滞留部に設置された、雑草発芽防止構造である。
本態様の雑草発芽防止構造は、プライマー層、硬化型シリコーンからなる下地処理材、及び、硬化型シリコーンからなるシートから選択される少なくとも一つである。 《Weed germination prevention structure》
The first aspect of the present invention is a weed germination prevention structure installed at a retention portion at the boundary between a paved surface of a road and other structures.
The weed germination prevention structure of this embodiment is at least one selected from a primer layer, a base treatment material made of curable silicone, and a sheet made of curable silicone.

以下、図面を参照して本発明にかかる好適な実施形態を例示する。
図１〜４には、車道の舗装面１と、縁石２と、歩道の舗装面３が描かれている。
車道や歩道等の道路の舗装面は、アスファルト面、コンクリート面又はモルタル面からなる。ここで、アスファルト面はアスファルトを含む表面を意味し、コンクリート面はコンクリートを含む表面を意味し、モルタル面はモルタルを含む表面を意味する。コンクリート面はモルタル面でもあるが、粗骨材を含む点でモルタル面とは相違する。
縁石２の側面２ａ及び上面２ｂはともにコンクリート面からなる。 Hereinafter, preferred embodiments according to the present invention will be illustrated with reference to the drawings.
In FIGS. 1 to 4, the pavement surface 1 of the roadway, the curb 2 and the pavement surface 3 of the sidewalk are drawn.
The paved surface of a road such as a roadway or a sidewalk consists of an asphalt surface, a concrete surface or a mortar surface. Here, the asphalt surface means a surface containing asphalt, the concrete surface means a surface containing concrete, and the mortar surface means a surface containing mortar. The concrete surface is also a mortar surface, but differs from the mortar surface in that it contains coarse aggregate.
Both the side surface 2a and the upper surface 2b of the curb 2 are made of a concrete surface.

車道の舗装面１と縁石２の境界において、舗装面１から縁石２の側面２ａが立ち上がっている。舗装面１と側面２ａの境界に沿って土埃が溜まり得る窪みからなる滞留部Ａがある。また、歩道の舗装面３と縁石２の上面２ｂとの境界に沿って土埃が溜まり得る溝からなる滞留部Ｂがある。 At the boundary between the pavement surface 1 and the curb 2 of the roadway, the side surface 2a of the curb 2 rises from the pavement surface 1. Along the boundary between the pavement surface 1 and the side surface 2a, there is a retention portion A composed of a depression in which dust can collect. Further, there is a retention portion B formed of a groove in which dust can collect along the boundary between the pavement surface 3 of the sidewalk and the upper surface 2b of the curb 2.

図１〜２は、滞留部Ａを覆う雑草発芽防止構造１０Ａと、滞留部Ｂを覆う雑草発芽防止構造１０Ｂが設置された様子を示す。
図３〜４は、雑草発芽防止構造１０Ａ，１０Ｂを部分拡大した断面図の一例を示す。 FIGS. 1 and 2 show a state in which the weed germination prevention structure 10A covering the retention portion A and the weed germination prevention structure 10B covering the retention portion B are installed.
3 to 4 show an example of a partially enlarged cross-sectional view of the weed germination prevention structures 10A and 10B.

［プライマー層４］
滞留部Ａ、Ｂとその周囲を構成するアスファルト面及びコンクリート面の表面は、予め土埃等が除去された清浄な表面とされており、この表面をプライマー層４がコーティングしている。 [Primer layer 4]
The surfaces of the asphalt surface and the concrete surface constituting the retention portions A and B and their surroundings are considered to be clean surfaces from which dust and the like have been removed in advance, and the surface is coated with the primer layer 4.

プライマー層４は、滞留部に対する下地処理材や雑草発芽防止シートの接着性を向上させるための表面改質層であり、市販のプライマー剤を表面に塗布して乾燥してなる硬化層である。
プライマー層４の厚さは、０．０５ｍｍ〜１ｍｍが好ましく、０．１ｍｍ〜０．５ｍｍがより好ましく、０．１５ｍｍ〜０．３ｍｍがさらに好ましい。
上記範囲であると、下地処理材や雑草発芽防止シートの接着性をより向上させることができる。ここで例示したプライマー層の好適な厚さは、一般的な接着用途で使用されるプライマー層の厚さよりも厚い。プライマー層４を形成する道路の舗装面は一般的な接着面（例えば、タイルや瓦の表面）よりも粗いので、プライマー層が厚い方が強力な接着性を得られ易い。 The primer layer 4 is a surface modification layer for improving the adhesiveness of the base treatment material and the weed germination prevention sheet to the retention portion, and is a cured layer obtained by applying a commercially available primer agent to the surface and drying.
The thickness of the primer layer 4 is preferably 0.05 mm to 1 mm, more preferably 0.1 mm to 0.5 mm, and even more preferably 0.15 mm to 0.3 mm.
Within the above range, the adhesiveness of the base treatment material and the weed germination prevention sheet can be further improved. The suitable thickness of the primer layer exemplified here is thicker than the thickness of the primer layer used in general adhesive applications. Since the pavement surface of the road forming the primer layer 4 is rougher than a general adhesive surface (for example, the surface of a tile or a roof tile), a thicker primer layer makes it easier to obtain strong adhesiveness.

好適なプライマー層４を形成するプライマー剤の具体例として、例えば、信越化学工業社製のプライマーＭＴ等が挙げられる。 Specific examples of the primer agent for forming a suitable primer layer 4 include Primer MT manufactured by Shin-Etsu Chemical Co., Ltd.

［下地処理材５］
滞留部Ａ，Ｂには、それぞれ硬化型シリコーンからなる下地処理材５が設置されている。
下地処理材５は、未硬化の段階ではペースト状のシリコーンであり、滞留部Ａ，Ｂの窪みや溝の少なくとも一部を充填するように塗布され、その後硬化されてなる弾性部材であり、予め形成されたプライマー層４を介して滞留部Ａ，Ｂに強固に接着している。下地処理材５が滞留部Ａ，Ｂの窪みや溝を埋めているので、下地処理材５の表面は比較的平滑な面となり得る。
下地処理材５の厚さは、滞留部Ａ，Ｂを埋められる厚さであることが好ましく、例えば、１ｍｍ〜２０ｍｍが好ましく、５ｍｍ〜１０ｍｍがより好ましい。ここで、下地処理材５の厚さは、無作為に選択される５箇所について、舗装面１から上方に見た方向の厚さを測定した値の平均値とする。
下地処理材５の長手方向の長さは、滞留部Ａ，Ｂの長さに応じて適宜設定され、例えば、１０ｃｍ〜１０００ｃｍとすることができる。下地処理材５は一続きに設置されていてもよいし、途中で分断されて複数に分けて設置されたものであってもよい。なお、滞留部の凸凹が５ｍｍ以下の場合は、下地処理材を有しない構造であってもよい。 [Base treatment material 5]
Base treatment materials 5 made of curable silicone are installed in the retention portions A and B, respectively.
The primer 5 is a paste-like silicone in the uncured stage, and is an elastic member that is applied so as to fill at least a part of the dents and grooves of the retention portions A and B and then cured. It is firmly adhered to the retention portions A and B via the formed primer layer 4. Since the base treatment material 5 fills the dents and grooves of the retention portions A and B, the surface of the base treatment material 5 can be a relatively smooth surface.
The thickness of the base treatment material 5 is preferably a thickness that can fill the retention portions A and B, for example, preferably 1 mm to 20 mm, and more preferably 5 mm to 10 mm. Here, the thickness of the base treatment material 5 is an average value of the measured thicknesses in the upward direction from the pavement surface 1 at five randomly selected locations.
The length of the base treatment material 5 in the longitudinal direction is appropriately set according to the lengths of the retention portions A and B, and can be, for example, 10 cm to 1000 cm. The base treatment material 5 may be installed in succession, or may be divided in the middle and installed in a plurality of parts. When the unevenness of the retention portion is 5 mm or less, the structure may not have a base treatment material.

下地処理材５を形成する硬化型シリコーンは、縮合硬化型でもよいし、付加硬化型でもよい。付加硬化型は、未使用時には低温で保存し、使用時には常温以上に加熱することによって硬化させる。縮合硬化型は、未使用時には乾燥環境（防湿環境）で保存し、使用時には空気中の水分を吸湿させることによって硬化させる。施工の容易さの観点から、縮合硬化型のシリコーンが好ましい。 The curable silicone that forms the base treatment material 5 may be a condensation curing type or an addition curing type. The addition-curing type is stored at a low temperature when not in use, and is cured by heating to a temperature higher than room temperature when in use. The condensation-curing type is stored in a dry environment (moisture-proof environment) when not in use, and is cured by absorbing moisture in the air when in use. From the viewpoint of ease of construction, condensation-curable silicone is preferable.

硬化型シリコーンは未硬化時には所望の形状に成形可能であり、硬化後にはその形状を保持する。下地処理材５の設置に用いる硬化型シリコーンの未硬化時のウイリアム可塑度（２５℃）は、５〜４５が好ましく、５〜３０がより好ましい。ウイリアム可塑度が前記範囲内にあると、未硬化の状態で流動性を有し、所望の形状に成形することが容易である。
ここで、ウイリアム可塑度は、ＪＩＳ Ｋ ６２４９：１９９７の「未硬化及び硬化シリコーンゴムの試験方法」に準じて測定して算出された値である。すなわち、２５℃において硬化型シリコーンゴム２ｇの略球状の試験片を準備し、この試験片をセロハン紙に挟んでダイヤルゲージの付いた平行板可塑度計（上島製作所製「ウイリアムプラスとメータ」）中にセットし、５ｋｇの荷重を加えて３分間放置した後、ダイヤルゲージの目盛をミリメートルで読み取り、試験片の厚さを記録して、この数値を１００倍した値である。 The curable silicone can be molded into a desired shape when uncured, and retains that shape after curing. The uncured William plasticity (25 ° C.) of the curable silicone used for installing the base treatment material 5 is preferably 5 to 45, more preferably 5 to 30. When the William plasticity is within the above range, it has fluidity in an uncured state, and it is easy to form it into a desired shape.
Here, the William plasticity is a value calculated by measuring according to JIS K 6249: 1997 "Test method for uncured and cured silicone rubber". That is, a substantially spherical test piece of 2 g of curable silicone rubber was prepared at 25 ° C., and the test piece was sandwiched between cellophane paper and a parallel plate plasticity meter with a dial gauge (“William Plus and Meter” manufactured by Ueshima Seisakusho). After setting the inside and leaving it for 3 minutes with a load of 5 kg, the scale of the dial gauge is read in millimeters, the thickness of the test piece is recorded, and this value is multiplied by 100.

雑草発芽防止構造の耐候性を高める観点から、下地処理材５を構成する硬化型シリコーンゴムの硬化後の硬度を、ＪＩＳ Ｋ ６２５３：２０１２の「第３部：デュロメータ硬さ（タイプＡ）」に基づいて評価した場合、Ａ ４０以上であることが好ましい。上限値は特に限定されないが、経年劣化（例えば交通による路面沈下、地震等）により滞留部Ａ，Ｂの形状が変化したときに、下地処理材５がその変化に追随することを考慮して、例えば、Ａ９０程度が上限として挙げられる。 From the viewpoint of improving the weather resistance of the weed germination prevention structure, the hardness of the curable silicone rubber constituting the base treatment material 5 after curing has been changed to "Part 3: Durometer Hardness (Type A)" of JIS K 6253: 2012. When evaluated based on the above, it is preferably A 40 or more. The upper limit is not particularly limited, but in consideration of the fact that when the shapes of the retention portions A and B change due to aged deterioration (for example, road surface subsidence due to traffic, earthquake, etc.), the base treatment material 5 follows the change. For example, about A90 is mentioned as an upper limit.

下地処理材５としての好適なウイリアム可塑度や硬度を呈する好適な硬化型シリコーンとなる、未硬化シリコーンのペーストは、公知方法により製造され得る。 An uncured silicone paste, which is a suitable curable silicone that exhibits suitable William plasticity and hardness as the base treatment material 5, can be produced by a known method.

［シート６］
各滞留部に設けられた下地処理材５及びプライマー層４の少なくとも一部は、硬化型シリコーンからなるシート（雑草発芽防止シート）６によって覆われている。各滞留部を覆うシート６の表面は平滑であるので、シート６の表面に土埃や雨水が滞留することを防止することができる。 [Sheet 6]
At least a part of the base treatment material 5 and the primer layer 4 provided in each retention portion is covered with a sheet (weed germination prevention sheet) 6 made of curable silicone. Since the surface of the sheet 6 covering each retention portion is smooth, it is possible to prevent dust and rainwater from accumulating on the surface of the sheet 6.

シート６は、未硬化の段階でシート状に成形されており、下地処理材５及びプライマー層４を覆うように貼付され、その後硬化されてなる弾性部材である。シート６は下地処理材５の全体を覆い、さらに、下地処理材５に覆われずに露出した領域のプライマー層４に接していることが好ましい。この構造であると、シート６の接着面積が広くなるので、シート６は強力に固着する。また、この構造であると、雑草発芽防止構造の外面全体をシート６の平滑な表面で覆うので、土埃や雨水が滞留し難くなり、雑草の発芽を確実に防止することができる。
上記の好適な構造とするためには、図１に示すように雑草発芽防止構造１０Ａ，１０Ｂをそれぞれ上方から見て、プライマー層４の面積＞シート６の面積＞下地処理材５の面積の関係であることが好ましい。 The sheet 6 is an elastic member that is formed into a sheet shape at an uncured stage, is attached so as to cover the base treatment material 5 and the primer layer 4, and is then cured. It is preferable that the sheet 6 covers the entire surface treatment material 5 and is in contact with the primer layer 4 in the exposed region without being covered by the surface treatment material 5. With this structure, the adhesive area of the sheet 6 becomes large, so that the sheet 6 is strongly fixed. Further, in this structure, since the entire outer surface of the weed germination prevention structure is covered with the smooth surface of the sheet 6, dust and rainwater are less likely to accumulate, and weed germination can be reliably prevented.
In order to obtain the above-mentioned suitable structure, as shown in FIG. 1, the weed germination prevention structures 10A and 10B are viewed from above, and the relationship between the area of the primer layer 4> the area of the sheet 6> the area of the base treatment material 5. Is preferable.

シート６の厚さは、風雨に曝されたり、車からの飛び石が当たったりすることに耐え得る厚さであることが好ましく、例えば、０．５ｍｍ〜８ｍｍが好ましく、１ｍｍ〜６ｍｍがより好ましく、２ｍｍ〜４ｍｍがさらに好ましい。ここで、シート６の厚さは、無作為に選択される５箇所について、その断面の厚さを測定した値の平均値とする。
シート６のたて×よこの長さは、滞留部Ａ，Ｂの面積に応じて適宜設定され、例えば、たて１ｃｍ〜１０ｃｍ×よこ１０ｃｍ〜１０００ｃｍとすることができる。シート６は一続きの一枚が設置されていてもよいし、途中で分断されて複数枚に分かれて設置されていてもよい。 The thickness of the seat 6 is preferably a thickness that can withstand exposure to wind and rain or a stepping stone from a car, for example, 0.5 mm to 8 mm, more preferably 1 mm to 6 mm. 2 mm to 4 mm is more preferable. Here, the thickness of the sheet 6 is the average value of the measured values of the cross-sectional thicknesses of the five randomly selected locations.
The length of the vertical and horizontal sides of the sheet 6 is appropriately set according to the areas of the retention portions A and B, and can be, for example, 1 cm to 10 cm in length and 10 cm to 1000 cm in width. The sheet 6 may be installed as a series of sheets, or may be divided in the middle and installed in a plurality of sheets.

シート６を形成する硬化型シリコーンは、縮合硬化型でもよいし、付加硬化型でもよい。施工の容易さの観点から、縮合硬化型のシリコーンが好ましい。
シート６を構成する硬化型シリコーンの未硬化時のウイリアム可塑度（２５℃）は、５０〜４５０が好ましく、５０〜３００がより好ましい。ウイリアム可塑度が前記範囲内にあると、未硬化の状態で下地処理材５の形状に沿って貼付することが容易である。ここで、ウイリアム可塑度は、上述の方法により求められた値である。
ウイリアム可塑度が前記下限値以上であれば、シート形状が充分に維持され、前記上限値以下であれば、設置箇所に容易になじませることができる。 The curable silicone forming the sheet 6 may be a condensation-curable type or an addition-curable type. From the viewpoint of ease of construction, condensation-curable silicone is preferable.
The uncured William plasticity (25 ° C.) of the curable silicone constituting the sheet 6 is preferably 50 to 450, more preferably 50 to 300. When the William plasticizer is within the above range, it is easy to attach the material along the shape of the base treatment material 5 in an uncured state. Here, the William plasticity is a value obtained by the above-mentioned method.
When the William plasticity is not less than the lower limit value, the sheet shape is sufficiently maintained, and when it is not more than the upper limit value, it can be easily adapted to the installation location.

雑草発芽防止構造の耐候性を高める観点から、シート６を構成する硬化型シリコーンゴムの硬化後の硬度を、ＪＩＳ Ｋ ６２５３：２０１２の「第３部：デュロメータ硬さ（タイプＡ）」に基づいて評価した場合、Ａ ４０以上であることが好ましい。上限値は特に限定されないが、経年劣化（例えば交通による地盤沈下、地震等）により滞留部Ａ，Ｂの形状が変化したときに、下地処理材５がその変化に追随することを考慮して、例えば、Ａ９０程度が上限として挙げられる。 From the viewpoint of improving the weather resistance of the weed germination prevention structure, the hardness of the curable silicone rubber constituting the sheet 6 after curing is determined based on "Part 3: Durometer Hardness (Type A)" of JIS K 6253: 2012. When evaluated, it is preferably A 40 or more. The upper limit is not particularly limited, but in consideration of the fact that when the shapes of the retention portions A and B change due to aged deterioration (for example, ground subsidence due to traffic, an earthquake, etc.), the base treatment material 5 follows the change. For example, about A90 is mentioned as an upper limit.

シート６としての好適なウイリアム可塑度や硬度を呈する好適な硬化型シリコーンとなる、未硬化シリコーンのシートとしては、例えば、信越ポリマー社製の「ポリマエース」として販売されている、ＨＲ−２３８８Ｓ（付加硬化型、常温硬化）、ＨＲ−１２０Ｓ（付加硬化型、加熱硬化）、ＨＲ−１２０ＮＰ（付加硬化型、加熱硬化）、ＨＪ−１４Ｓ（縮合硬化型）、ＨＪ−１５８８Ｌ（縮合硬化型）、ポリマエースＰＡ等が挙げられる。 As a sheet of uncured silicone, which is a suitable curable silicone having suitable William plasticity and hardness as a sheet 6, for example, HR-2388S (additional) sold as "Polyma Ace" manufactured by Shinetsu Polymer Co., Ltd. Curing type, room temperature curing), HR-120S (additional curing type, heat curing), HR-120NP (additional curing type, heat curing), HJ-14S (condensation curing type), HJ-1588L (condensation curing type), Polyma Ace PA and the like can be mentioned.

［遮光材］
雑草発芽防止構造１０Ａ，１０Ｂを構成する下地処理材５及びシート６の少なくとも一方が遮光材を含有していてもよい。遮光材が含まれていれば、日光が雑草発芽防止構造を透過することを抑制し、滞留部Ａ，Ｂに雑草の種子や地下茎が残留していた場合にも、それらから雑草が発芽することをより確実に防止することができる。なお、遮光材を含有していなくても、雑草発芽防止構造は滞留部を覆っているので、滞留部における雑草の発芽や生育を物理的に防止することができる。
前記遮光材は、日光を散乱、反射または吸収する物質である。具体例として、金属、炭素材料、色素、顔料等の微粒子が挙げられる。遮光材は下地処理材５及びシート６に均一に分散されていることが好ましい。 [Shading material]
At least one of the base treatment material 5 and the sheet 6 constituting the weed germination prevention structures 10A and 10B may contain a light-shielding material. If a light-shielding material is included, it suppresses the penetration of sunlight through the weed germination prevention structure, and even if weed seeds and rhizomes remain in the retention portions A and B, weeds will germinate from them. Can be prevented more reliably. Even if the light-shielding material is not contained, the weed germination prevention structure covers the retention portion, so that the germination and growth of weeds in the retention portion can be physically prevented.
The light-shielding material is a substance that scatters, reflects or absorbs sunlight. Specific examples include fine particles such as metals, carbon materials, pigments, and pigments. It is preferable that the light-shielding material is uniformly dispersed in the base treatment material 5 and the sheet 6.

［全光線透過率］
上述の目的で日光を遮る観点から、下地処理材５及びシート６のうち少なくとも一方の全光線透過率は３０％以下が好ましく、２０％以下がより好ましく、１０％以下がさらに好ましい。当然ながら、０％であってもよい。
ここで、上記部材の全光線透過率は、照度計の光センサーを各部材で覆ったときに光センサーが受光する白色光の照度ＬＸ１と、その光センサーを各部材で覆っていないときに光センサーが受光する白色光の照度ＬＸ２との比率（ＬＸ１／ＬＸ２×１００％）により算出されたものである。 [Total light transmittance]
From the viewpoint of blocking sunlight for the above-mentioned purpose, the total light transmittance of at least one of the base treatment material 5 and the sheet 6 is preferably 30% or less, more preferably 20% or less, still more preferably 10% or less. Of course, it may be 0%.
Here, the total light transmittance of the above members is the illuminance LX1 of the white light received by the photosensor when the photosensor of the photometer is covered with each member, and the light when the photosensor is not covered with each member. It is calculated by the ratio (LX1 / LX2 × 100%) of the white light received by the sensor to the illuminance LX2.

［色］
上述の目的で日光を遮る観点から、下地処理材５及びシート６のうち少なくとも一方は黒色または灰色であることが好ましい。なお、下地処理材５及びシート６の色は、これらの部材に含有させる色素や顔料の色や配合量によって調整することができる。例えば、カーボンブラック等の炭素材料を配合することにより、黒色のシリコーン部材が得られる。 [color]
From the viewpoint of blocking sunlight for the above-mentioned purpose, it is preferable that at least one of the base treatment material 5 and the sheet 6 is black or gray. The colors of the base treatment material 5 and the sheet 6 can be adjusted by adjusting the colors and blending amounts of the pigments and pigments contained in these members. For example, by blending a carbon material such as carbon black, a black silicone member can be obtained.

［発芽防止剤、防草剤］
雑草発芽防止構造１０Ａ，１０Ｂを構成する下地処理材５及びシート６の少なくとも一方が発芽防止剤または防草剤を含有していてもよい。下地処理材５またはシート６から周囲へ発芽防止剤または防草剤が拡散することにより、滞留部Ａ，Ｂに雑草の種子や地下茎が残留していた場合にも、それらから雑草が発芽することをより確実に防止することができる。発芽防止剤または防草剤は、雑草に対して使用される市販品が用いられる。下地処理材５の総質量に対する発芽防止剤または防草剤の含有量は、例えば０．１〜５質量％程度とすることができる。シート６の総質量に対する発芽防止剤または防草剤の含有量も同様とすることができる。 [Germination inhibitor, herbicide]
At least one of the base treatment material 5 and the sheet 6 constituting the weed germination prevention structures 10A and 10B may contain a germination prevention agent or a weed control agent. Even if weed seeds or rhizomes remain in the retention portions A and B due to the diffusion of the germination inhibitor or weed control agent from the base treatment material 5 or the sheet 6, weeds germinate from them. Can be prevented more reliably. As the germination inhibitor or herbicide, a commercially available product used for weeds is used. The content of the germination inhibitor or herbicide with respect to the total mass of the base treatment material 5 can be, for example, about 0.1 to 5% by mass. The content of the germination inhibitor or herbicide with respect to the total mass of the sheet 6 can be the same.

［他の実施形態］
上述の説明では、「その他の構造物」が車道と歩道を隔てる縁石である場合を例示したが、本発明の「その他の構造物」はこの例に限定されず、中央分離帯を構成する境界ブロック、Ｕ字溝を構成するコンクリートブロック、電柱、壁等であってもよい。
また、上述の説明では、「滞留部」が溝や窪みである場合を例示したが、本発明の「滞留部」はこの例に限定されず、数ミリから数センチ程度の段差、隙間、目地等であってもよい。 [Other Embodiments]
In the above description, the case where the "other structure" is a curb separating the roadway and the sidewalk has been illustrated, but the "other structure" of the present invention is not limited to this example, and the boundary constituting the median strip is not limited to this example. It may be a block, a concrete block constituting a U-shaped groove, a utility pole, a wall, or the like.
Further, in the above description, the case where the "retention portion" is a groove or a depression is illustrated, but the "retention portion" of the present invention is not limited to this example, and a step, a gap, or a joint of about several millimeters to several centimeters is used. And so on.

《雑草発芽防止構造の設置方法》
本発明の第二態様は、道路の舗装面と、その他の構造物との境界にある滞留部に、第一態様の雑草発芽防止構造を設置する方法であり、少なくとも次の工程Ａ〜工程Ｄを有する。 << Installation method of weed germination prevention structure >>
The second aspect of the present invention is a method of installing the weed germination prevention structure of the first aspect at the retention portion at the boundary between the pavement surface of the road and other structures, and at least the following steps A to D Has.

［工程Ａ］
工程Ａは、前記滞留部及びその周囲を構成するアスファルト面、コンクリート面又はモルタル面の表面を清浄にする工程である。清掃前の滞留部Ａ，Ｂの様子を図４に示す。雑草発芽防止構造を設置していないので、縁石２と舗装面１，３の境界にある滞留部Ａ，Ｂから雑草Ｇが発芽し、生育している。これらの雑草を刈り取り、滞留部Ａに堆積していた土埃を箒やブラシで掻き出すことにより、滞留部Ａ，Ｂとその周囲を清浄な表面とした後の様子を図３に示す。 [Step A]
The step A is a step of cleaning the surface of the asphalt surface, the concrete surface or the mortar surface constituting the stagnant portion and its surroundings. FIG. 4 shows the states of the stagnant portions A and B before cleaning. Since the weed germination prevention structure is not installed, weeds G germinate and grow from the retention portions A and B at the boundary between the curb 2 and the pavement surfaces 1 and 3. FIG. 3 shows a state after cutting these weeds and scraping off the dust accumulated in the retention portion A with a broom or a brush to make the retention portions A and B and their surroundings a clean surface.

［工程Ｂ］
工程Ｂは、滞留部Ａ，Ｂおよびその周囲の清浄にした表面にプライマー剤を塗布し、乾燥することによりプライマー層４を形成する工程である。
好適なプライマー剤は前述の通りである。前述した好適な厚さのプライマー層４を形成するために、プライマー剤の塗布量は、５０ｇ／ｍ２〜１０００ｇ／ｍ２が好ましく、１００ｇ／ｍ２〜５００ｇ／ｍ２がより好ましく、１５０ｇ／ｍ２〜３００ｇ／ｍ２がさらに好ましい。
プライマー剤を塗布した後の乾燥方法は、自然に乾燥するのを待つのが好ましい。 [Step B]
Step B is a step of applying a primer agent to the retention portions A and B and the cleaned surface around them and drying them to form the primer layer 4.
Suitable primer agents are as described above. To form the primer layer 4 of a suitable thickness as described above, the coating amount of the primer agent is preferably 50g / m 2 ~1000g / m 2 , more preferably 100g / m 2 ~500g / m 2 , 150g / More preferably, m 2 to 300 g / m 2.
As for the drying method after applying the primer agent, it is preferable to wait for it to dry naturally.

本工程の後で設置する硬化型のシリコーン部材は、湾曲した箇所や屈曲した箇所に対してもその形状に対して完全に追随させて接着することができる。このため、本工程でプライマー剤を塗布する領域は湾曲または屈曲していても何ら問題はない。これに対して、特許文献１で提案されている雑草抑止テープを湾曲又は屈曲した領域に貼る場合、その湾曲のＲが大きかったり、屈曲の折れ曲がり具合が大きかったりすると、貼付する雑草抑止テープに皺が生じ易く、充分に密着させることが困難である。
なお、本工程でプライマー剤を塗布する領域が湾曲または屈曲しているとは、舗装面１又は舗装面３を上方から見下ろしたときに、前記領域が湾曲または屈曲していることをいう。従って、図１〜４の滞留部Ａ，Ｂは両方とも湾曲または屈曲した領域ではない。図示しないが、例えば、カーブした道路に沿って設置された縁石は、湾曲または屈曲した滞留部を有することがある。 The curable silicone member installed after this step can be adhered to a curved portion or a bent portion by completely following the shape. Therefore, there is no problem even if the region to which the primer is applied in this step is curved or bent. On the other hand, when the weed control tape proposed in Patent Document 1 is attached to a curved or bent region, if the curved R is large or the bending is large, the weed control tape to be attached is wrinkled. Is likely to occur, and it is difficult to bring them into close contact with each other.
The region to which the primer is applied in this step is curved or bent means that the region is curved or bent when the pavement surface 1 or the pavement surface 3 is looked down from above. Therefore, neither the retention portions A and B in FIGS. 1 to 4 are curved or bent regions. Although not shown, for example, curbs installed along curved roads may have curved or curved stagnant portions.

［工程Ｃ］
工程Ｃは、プライマー層４が形成された滞留部Ａ，Ｂに未硬化シリコーンからなるペーストを塗布し、滞留部Ａ，Ｂの少なくとも一部を充填することにより下地処理材５を形成する工程である。
好適な未硬化シリコーンのペーストは前述の通りである。縮合硬化型のシリコーンを使用する場合、カートリッジから押し出されたペーストを滞留部Ａ，Ｂに塗布し、ヘラ等で軽く塗り込めることにより、滞留部Ａ，Ｂおよびその周囲の粗面に対して、ペーストを充分に充填することができる。
その後、塗布したペーストからなる下地処理材５が硬化するまで待ってもよいし、硬化するのを待たずに次の工程Ｄに進んでもよい。 [Step C]
Step C is a step of applying a paste made of uncured silicone to the retention portions A and B on which the primer layer 4 is formed and filling at least a part of the retention portions A and B to form the base treatment material 5. is there.
Suitable uncured silicone pastes are as described above. When a condensation-curing type silicone is used, the paste extruded from the cartridge is applied to the retention portions A and B and lightly applied with a spatula or the like to cover the retention portions A and B and the rough surface around them. The paste can be fully filled.
After that, it may wait until the base treatment material 5 made of the applied paste is cured, or it may proceed to the next step D without waiting for the curing.

［工程Ｄ］
工程Ｄは、下地処理材５及びプライマー層４の少なくとも一部を覆う、未硬化シリコーンからなるシート（雑草発芽防止シート）６を貼付する工程である。
未硬化シリコーンを貼付し、その後に硬化させることにより、シート６を下地処理材５及びプライマー層４に対して充分に接着することができる。
貼付前のシート６を構成する好適な未硬化シリコーンは前述の通りである。
以上の工程で設置した下地処理材５及びシート６を構成する硬化型のシリコーンは、しばらく放置すると完全に硬化する。 [Step D]
Step D is a step of attaching a sheet (weed germination prevention sheet) 6 made of uncured silicone that covers at least a part of the base treatment material 5 and the primer layer 4.
By applying the uncured silicone and then curing it, the sheet 6 can be sufficiently adhered to the base treatment material 5 and the primer layer 4.
Suitable uncured silicones constituting the sheet 6 before sticking are as described above.
The curable silicone constituting the base treatment material 5 and the sheet 6 installed in the above steps is completely cured after being left for a while.

《雑草発芽防止シート》
本発明の第三態様は、未硬化の硬化型シリコーンからなるシートであり、第二態様の雑草発芽防止構造の設置方法において、前記下地処理材及び前記プライマー層の少なくとも一部を覆う用途で使用される、雑草発芽防止シートである。シート自体は、従来の未硬化シリコーンシートと同じであるが、その用途は従来とは異なる新規なものである。 《Weed germination prevention sheet》
The third aspect of the present invention is a sheet made of uncured curable silicone, which is used in the application of covering at least a part of the base treatment material and the primer layer in the method of installing the weed germination prevention structure of the second aspect. It is a weed germination prevention sheet. The sheet itself is the same as the conventional uncured silicone sheet, but its use is new and different from the conventional one.

［実施例１］
信越ポリマー株式会社の東京工場の敷地内において、アスファルト舗装された路面と、この路面に沿って設置されたコンクリート製の縁石との境界の窪みに、土埃が溜まり、雑草が生えている箇所（長さ約４０ｃｍ）を見つけた。
この雑草を引き抜き、箒で土や砂を除去し、前記境界の窪みとその周囲の表面を清浄化した。ここに、プライマー剤（信越化学工業社製、プライマーＭＴ）を約２００ｇ／ｍ２の厚さで塗り、自然に乾燥させ、プライマー層（厚さ約０．２ｍｍ）を形成した。
次に、前記窪みを中心として、未硬化の縮合硬化型シリコーンからなる市販のペーストを厚さ約５ｍｍ以上となるように塗布し、スポンジのヘラで表面を均した。これにより、前記窪みと、周囲のアスファルト面の凹凸を充填する下地処理材を形成した。
続いて、下地処理材とそれよりも広範囲に形成されたプライマー層の一部を覆うように、未硬化の縮合硬化型シリコーンからなるシート（信越ポリマー社製、ポリマエースＰＡ）を貼付し、設置面に対してなじませるように押し付けた。
以上の方法で、図１〜２の雑草発芽防止構造１０Ａと同様な雑草発芽防止構造を設置した。この雑草発芽防止構造を構成するシリコーン部材（下地処理材及びシート）は、設置後、表面からゴム状になり完全に硬化した。
以上で設置した雑草発芽防止構造を６ヶ月間に亘り観察したところ、風雨に曝され、直射日光を受けていたにも関わらず、何の変化も生じず、安定に維持された。 [Example 1]
On the premises of Shin-Etsu Polymer Co., Ltd.'s Tokyo factory, a place where dust accumulates and weeds grow in the depression at the boundary between the asphalt-paved road surface and the concrete curb installed along this road surface (long). I found (about 40 cm).
The weeds were pulled out, soil and sand were removed with a broom, and the boundary depression and the surrounding surface were cleaned. Here, a primer agent (manufactured by Shin-Etsu Chemical Co., Ltd., Primer MT) was applied to a thickness of about 200 g / m 2 and naturally dried to form a primer layer (thickness about 0.2 mm).
Next, a commercially available paste made of uncured condensation-curable silicone was applied around the recess to a thickness of about 5 mm or more, and the surface was leveled with a sponge spatula. As a result, a base treatment material was formed to fill the depression and the unevenness of the surrounding asphalt surface.
Subsequently, a sheet made of uncured condensation-curable silicone (Polymer Ace PA, manufactured by Shin-Etsu Polymer Co., Ltd.) was attached so as to cover a part of the primer layer formed over the base treatment material and a wider area, and the installation surface was attached. I pressed it so that it would fit in.
By the above method, a weed germination prevention structure similar to the weed germination prevention structure 10A of FIGS. 1 and 2 was installed. The silicone member (base treatment material and sheet) constituting this weed germination prevention structure became rubbery from the surface after installation and was completely cured.
When the weed germination prevention structure installed above was observed for 6 months, it was maintained stable without any change even though it was exposed to wind and rain and was exposed to direct sunlight.

［実施例２］
実施例１において、未硬化の縮合硬化型シリコーンからなるペーストに、遮光材としてカーボンブラックを数グラム添加し、よく混ぜ合わせて黒色のペーストにしてから使用したこと以外は、実施例１と同様に雑草発芽防止構造を設置した。この下地処理材５の全光線透過率は約２０％であった。 [Example 2]
Similar to Example 1, except that a few grams of carbon black was added as a light-shielding material to a paste made of uncured condensation-curable silicone and mixed well to make a black paste before use. A weed germination prevention structure was installed. The total light transmittance of the base treatment material 5 was about 20%.

［比較例１］
アクリル樹脂系粘着剤層を有する市販の透明粘着テープを、実施例１の雑草発芽防止構造の近傍に貼付した。すなわち、アスファルト面と縁石の境界にある雑草が生えた窪みを掃除し、土や砂を除去して清浄化した後、この表面に透明粘着テープ（幅約５ｃｍ、長さ約３０ｃｍ）を貼付した。しかし、貼付する表面が粗く、実質的に接着している面積は少なかった。
以上で設置した透明粘着テープを観察したところ、風雨に曝され、直射日光を受ける時間が長引くほど、容易に劣化していることが明らかであり、２週間が経過するまでに剥離した。 [Comparative Example 1]
A commercially available transparent adhesive tape having an acrylic resin-based pressure-sensitive adhesive layer was attached in the vicinity of the weed germination prevention structure of Example 1. That is, after cleaning the weed-grown dents on the boundary between the asphalt surface and the curb, removing soil and sand to clean it, a transparent adhesive tape (width about 5 cm, length about 30 cm) was attached to this surface. .. However, the surface to which it was attached was rough, and the area where it was substantially adhered was small.
When the transparent adhesive tape installed as described above was observed, it was clear that the longer the time of exposure to wind and rain and the longer the time of direct sunlight, the easier the deterioration was, and the tape was peeled off by the lapse of two weeks.

１０Ａ，１０Ｂ 雑草発芽防止構造
１ 車道の舗装面
２ 縁石
３ 歩道の舗装面
４ プライマー層
５ 下地処理材
６ シート（雑草発芽防止シート） 10A, 10B Weed germination prevention structure 1 Roadway pavement 2 Curb 3 Sidewalk pavement 4 Primer layer 5 Base treatment material 6 sheets (weed germination prevention sheet)

Claims (11)

道路の舗装面と、その他の構造物との境界に設置された、雑草発芽防止構造であって、
前記雑草発芽防止構造は、プライマー層、硬化型シリコーンからなる下地処理材、及び、硬化型シリコーンからなるシートから選択される少なくとも一つであることを特徴とする雑草発芽防止構造。 A weed germination prevention structure installed at the boundary between the paved surface of the road and other structures.
The weed germination prevention structure is characterized in that the weed germination prevention structure is at least one selected from a primer layer, a base treatment material made of curable silicone, and a sheet made of curable silicone. 前記境界には滞留部が形成されており、
前記滞留部は、土埃が溜まり得る溝、窪み、段差、隙間又は目地からなり、
前記滞留部及びその周囲を構成する面は、アスファルト面、コンクリート面又はモルタル面からなる、請求項１記載の雑草発芽防止構造。 A retention portion is formed at the boundary.
The stagnant portion is composed of grooves, depressions, steps, gaps or joints where dust can collect.
The weed germination prevention structure according to claim 1, wherein the retaining portion and the surfaces constituting the retaining portion are composed of an asphalt surface, a concrete surface or a mortar surface. 前記下地処理材及び前記シートのうち少なくとも一方が遮光材を含有する、請求項１に記載の雑草発芽防止構造。 The weed germination prevention structure according to claim 1, wherein at least one of the base treatment material and the sheet contains a light-shielding material. 前記下地処理材及び前記シートのうち少なくとも一方の全光線透過率が３０％以下である、請求項１〜３の何れか一項に記載の雑草発芽防止構造。 The weed germination prevention structure according to any one of claims 1 to 3, wherein the total light transmittance of at least one of the base treatment material and the sheet is 30% or less. 前記下地処理材及び前記シートのうち少なくとも一方が、黒色もしくは灰色である、請求項１〜４の何れか一項に記載の雑草発芽防止構造。 The weed germination prevention structure according to any one of claims 1 to 4, wherein at least one of the base treatment material and the sheet is black or gray. 前記その他の構造物が、縁石または柱である、請求項１〜５の何れか一項に記載の雑草発芽防止構造。 The weed germination prevention structure according to any one of claims 1 to 5, wherein the other structure is a curb or a pillar. 前記下地処理材および前記シートの少なくとも一方に発芽防止剤または防草剤を含有する請求項１〜６何れか一項に記載の雑草発芽防止構造。 The weed germination prevention structure according to any one of claims 1 to 6, wherein at least one of the base treatment material and the sheet contains a germination inhibitor or a herbicide. 道路の舗装面と、その他の構造物との境界にある滞留部に、雑草発芽防止構造を設置する方法であって、
前記滞留部は、土埃が溜まり得る溝、窪み、段差、隙間又は目地からなり、
前記滞留部及びその周囲を構成するアスファルト面、コンクリート面又はモルタル面の表面を清浄にする工程と、
前記表面にプライマー剤を塗布し、乾燥することによりプライマー層を形成する工程と、
前記プライマー層が形成された前記滞留部に未硬化シリコーンからなるペーストを塗布し、前記滞留部の少なくとも一部を充填することにより下地処理材を形成する工程と、
前記下地処理材及び前記プライマー層の少なくとも一部を覆う、未硬化シリコーンからなるシートを貼付する工程と、
を有することを特徴とする雑草発芽防止構造の設置方法。 It is a method of installing a weed germination prevention structure at the retention part at the boundary between the paved surface of the road and other structures.
The stagnant portion is composed of grooves, depressions, steps, gaps or joints where dust can collect.
A step of cleaning the surface of the asphalt surface, concrete surface or mortar surface constituting the stagnant portion and its surroundings, and
A step of applying a primer agent to the surface and drying it to form a primer layer, and
A step of applying a paste made of uncured silicone to the retaining portion on which the primer layer is formed and filling at least a part of the retaining portion to form a base treatment material.
A step of attaching a sheet made of uncured silicone that covers at least a part of the base treatment material and the primer layer, and
A method of installing a weed germination prevention structure, which is characterized by having. 前記プライマー剤の塗布量が、１００ｇ／ｍ２〜５００ｇ／ｍ２である、請求項８に記載の雑草発芽防止構造の設置方法。 The coating amount of the primer agent is 100g / m 2 ~500g / m 2 , the installation method of weed germination prevention structure of claim 8. 前記舗装面を上方から見て、前記プライマー剤を塗布する領域が湾曲または屈曲している、請求項８または９に記載の雑草発芽防止構造の設置方法。 The method for installing a weed germination prevention structure according to claim 8 or 9, wherein the area to which the primer is applied is curved or bent when the pavement surface is viewed from above. 未硬化の硬化型シリコーンからなるシートであり、
請求項８〜１０の何れか一項に記載の雑草発芽防止構造の設置方法にて、
前記下地処理材及び前記プライマー層の少なくとも一部を覆う用途で使用される、雑草発芽防止シート。 A sheet made of uncured curable silicone,
According to the method for installing a weed germination prevention structure according to any one of claims 8 to 10.
A weed germination prevention sheet used for covering at least a part of the base treatment material and the primer layer.
JP2019214093A 2019-11-27 2019-11-27 Weed germination prevention structure and its installation method, and weed germination prevention sheet Active JP7341039B2 (en)