JP2021066791A - 着色コート層用塗料およびその塗装方法 - Google Patents
着色コート層用塗料およびその塗装方法 Download PDFInfo
- Publication number
- JP2021066791A JP2021066791A JP2019192423A JP2019192423A JP2021066791A JP 2021066791 A JP2021066791 A JP 2021066791A JP 2019192423 A JP2019192423 A JP 2019192423A JP 2019192423 A JP2019192423 A JP 2019192423A JP 2021066791 A JP2021066791 A JP 2021066791A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- paint
- coating
- colored
- molecule
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
なお、本発明において、着色コート層用塗料は、ベース塗料およびクリア塗料などの上塗り塗料をいう。
1分子中に1個以上のカルボキシ基を有する樹脂は、具体的には、分子中にカルボキシ基と水酸基とを有するアクリル系共重合体である。前記アクリル系共重合体は、アクリル系単量体を主成分とし、該アクリル系単量体と、カルボキシ基を有する単量体と、水酸基を有する単量体とを共重合して得られる。
1分子中に1個以上のカルボキシ基を有する樹脂と、1分子中に1個以上のエポキシ基を有する樹脂とで、一方の平均分子量をやや大きくして、他方の平均分子量をやや小さくしてもよい。これにより、アクリル樹脂の相溶性を高め、両樹脂の相互の架橋反応が良好に進行する。
着色コート層用塗料中の着色顔料の濃度(pwc)は、通常1〜20質量%、好ましくは2〜10質量%である。
なお、「pwc」とは、Pigment Weight Concentration(顔料重量濃度)のことであり、塗料固形分に対する顔料の質量濃度をいう。
被塗装物は、例えば、鉄板、鋼鉄板、アルミニウムおよびステンレス鋼等である。例えば、被塗装物が自動車の鉄板等である場合、該鉄板上に予めプライマー層を形成してもよい。プライマー層は、電着塗装により車体の表面に形成する塗料や樹脂の膜であり、防食性や中塗り塗装膜との密着性を確保する役割を有する。
なお、被塗装物に着色コート層用塗料を塗布する方法は、限定されるものではなく、刷毛塗り塗装、ロール塗装、またはスプレー塗装等、公知の方法を用いることができる。
なお、中塗り塗装膜は、衝撃吸収の役割を有する。また、クリア塗装膜を補完する役割を併せ持っていてもよい。
〔実施例1〕
多官能性樹脂、分散剤および顔料の合計に対して、溶剤を10質量%添加して均一に混合した着色コート層用塗料を調製した。
多官能性樹脂、分散剤、顔料および溶剤は下記に示すとおりである。
(i)多官能性樹脂
数平均分子量(Mn)が4000、酸価が150mgKOH/gのカルボキシ基含有化合物溶液50%と、数平均分子量(Mn)が3000、エポキシ基含有量が2.5mmol/gのポリエポキシド樹脂溶液50%との混合物
なお、前記カルボキシ基含有化合物溶液および前記ポリエポキシド樹脂溶液は、それぞれ、カルボキシ基含有化合物およびポリエポキシド樹脂にソルベント100(ソルベントナフサ;三協化学(株)製)を添加して、均一に混合した10%溶液である。
(ii)分散剤
塩基性ポリアクリル酸樹脂、リン酸エステル塩
(iii)顔料
カーボンブラック
実施例1において、分散剤として、酸性ポリアクリル酸樹脂、硫酸エステル塩を使用したこと以外は、実施例1と同様にして、着色コート層用塗料を調製した。
実施例1において、顔料を使用しなかったこと以外は、実施例1と同様にして、コート層用塗料を調製した。
(1)耐酸性雨性
前記着色コート層用塗料を、電着塗装された基板上に塗布した後、乾燥させて、15cm×7cmの大きさの試験片を作製した。前記試験板にpH1.0の硫酸500μLを垂らし、IHオーブンにて80℃で30分間、加熱して塗膜を形成した後、塗膜のエッチング深さを表面粗さ計サーフテストSJ210((株)ミツトヨ製)を用いて評価した。
実施例1では、エッチング深さは0μmであり、比較例1では、エッチング深さは0.6μmであった。実施例1の着色コート層用塗料では、分散剤として、塩基性ポリアクリル酸樹脂のリン酸エステル塩が使用されたため、該分散剤と多官能性樹脂との間に形成された酸エポキシ結合中にカーボンブラックが取り込まれて均一性が向上し、耐酸性雨を含む耐候性が向上したものと考えられる。一方、比較例1の着色コート層用塗料は、カーボンブラックの分散性に劣るために、試験片に着色コート層用塗料が疎らに塗布されることとなり、耐酸性雨が不充分であった。
参考例1の顔料を含まない塗料(基準)と、実施例1の顔料を混合した塗料を60℃で16時間放置した後、それぞれの塗料の粘度変化率を評価した。粘度はJIS5600−2−2に規定されたストマー粘度計法を用いてKU値(コンシステンシーを示す数値)を算出した。
基準塗料に対して、増粘の程度が10%以下のとき、問題なしと判断した。
参考例1および実施例1ともに、経時的に粘度が上昇していたが、実施例1は、参考例1と比較し粘度の増加率が10%以下であった。
Claims (3)
- 1分子中に1個以上のカルボキシ基を有する樹脂と、1分子中に1個以上のエポキシ基を有する樹脂とからなる多官能性樹脂、または、1分子中にカルボキシ基とエポキシ基とをそれぞれ1個以上を有する多官能性樹脂と、
顔料と、
1分子中にカルボキシ基とエポキシ基とをそれぞれ1個以上を有する分散剤とを含有することを特徴とする着色コート層用塗料。 - 被塗装物上に着色トップコート層を形成する塗装方法において、
前記着色トップコート層が、
1分子中に1個以上のカルボキシ基を有する樹脂と、1分子中に1個以上のエポキシ基を有する樹脂とからなる多官能性樹脂、または、1分子中にカルボキシ基とエポキシ基とをそれぞれ1個以上を有する多官能性樹脂と、
顔料と、
1分子中にカルボキシ基とエポキシ基とをそれぞれ1個以上を有する分散剤とを含有する着色コート層用塗料を用いて形成されることを特徴とする塗装方法。 - 前記被塗装物上の一部に前記着色コート層用塗料を塗布して着色トップコート層を形成する工程1と、
前記被塗装物上の一部に形成した前記着色トップコート層上にマスキング層を形成する工程2と、
前記マスキング層上および前記マスキング層を形成していない前記被塗装物上に第2着色塗料を塗布して第2着色層を形成する工程3と、
前記第2着色層上にトップクリア層を形成する工程4と、
前記マスキング層の設けられた部分を剥離することにより、ツートーン塗装を完成する工程5と、
を有することを特徴とする請求項2に記載の塗装方法。